CN108707242A - A kind of band fragrance fingerprint proof membrane and preparation method thereof - Google Patents
A kind of band fragrance fingerprint proof membrane and preparation method thereof Download PDFInfo
- Publication number
- CN108707242A CN108707242A CN201810597887.5A CN201810597887A CN108707242A CN 108707242 A CN108707242 A CN 108707242A CN 201810597887 A CN201810597887 A CN 201810597887A CN 108707242 A CN108707242 A CN 108707242A
- Authority
- CN
- China
- Prior art keywords
- fingerprint
- fragrance
- resin
- coating
- masking liquid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of band fragrance fingerprint proof membranes and preparation method thereof.A kind of band fragrance fingerprint proof membrane includes base material, fragrance coating and anti-fingerprint coating successively;The fragrance coating is mainly formed by following component is mixing cured:By weight percentage, resin 10%~40%, fragrance 5%~20%, organic solvent 40%~85% can be recoated;The anti-fingerprint coating is mainly formed by following component is mixing cured:By weight percentage, anti-fingerprint resin 20%~50%, pore creating material 2%~10%, organic solvent 40%~72%.The product of the present invention has the effect of fragrance and anti-fingerprint simultaneously, and shows on the traditional performances such as adherence, translucency, wearability and hardness superior.
Description
Technical field
The present invention relates to field of material technology, more particularly, to a kind of band fragrance fingerprint proof membrane and preparation method thereof.
Background technology
With the fast development of science and technology and the increasingly raising of living standards of the people, the utilization rate of smart electronics communication equipment is got over
Come it is higher, also have more and more commodity for consumer select, when selecting commodity, consumer is not concerned only with cost performance, and
Also the specific function of commodity is increasingly paid close attention to.And one layer of stiffened protective film with fragrance is pasted on electronic communication equipment surface, it can be with
The specific fragrance of commodity is assigned, can allow experience of the consumer by smell, its desire to buy is stimulated, to increase the pin of product
Amount.In addition, intelligent display screen is during use, surface is easy to latent prints, cause its surface dirty, and is swiping
Meanwhile a large amount of scuffings are easy tod produce, the appearance and normal use to electronic product can make a big impact.
In processing film field, it is thin that Chinese patent application CN201310610406.7 discloses a kind of dulcet plastics of tool
The preparation method of film is added by realizing that surface layer, middle layer, the three-decker of inner layer prepare polyethylene film in middle layer
Fragrance microcapsule penetrates surface layer by fragrance emission to air to release fragrance particle, to realize the fragrance of film, but
The film does not have the function of anti-fingerprint.
In view of this, special propose the present invention.
Invention content
The first object of the present invention is to provide a kind of band fragrance fingerprint proof membrane, which has perfume (or spice) simultaneously
The effect of taste and anti-fingerprint, and show on the traditional performances such as adherence, translucency, wearability and hardness superior.
The second object of the present invention is to provide the above-mentioned preparation method with fragrance fingerprint proof membrane, preparation method flow letter
It is single, it is not related to complex device, binder, therefore easily industrialization promotion is added without additional;In addition photocurable resin is used
When solvent volatile quantity it is few, environmental pollution is small.
In order to achieve the goal above, the present invention provides following technical schemes.
A kind of band fragrance fingerprint proof membrane includes base material, fragrance coating and anti-fingerprint coating successively;
The fragrance coating is mainly formed by following component is mixing cured:By weight percentage, resin 10% can be recoated
~40%, fragrance 5%~20%, organic solvent 40%~85%;
The anti-fingerprint coating is mainly formed by following component is mixing cured:By weight percentage, anti-fingerprint resin
20%~50%, pore creating material 2%~8%, surplus is organic solvent.
Has the effect of fragrance and anti-fingerprint with fragrance fingerprint proof membrane more than provided by the invention, however the present invention not will
Conventional dulcet resin and anti-fingerprint resin simple superposition, but the coating of two kinds of effects must use formula as above,
Can reach can be fragrant, and stabilization distributes two months or more, and the effect of energy anti-fingerprint, this crucial institute exactly of the invention
.In other words, the formula of fragrance coating of the invention and the formula of anti-fingerprint coating act synergistically, could be not only fragrant, but also
Anti-fingerprint.
Connection type between each layer of the present invention is unrestricted, can both be connected by being coated with additional binder, and also might be used
Directly to bond.
The base material material and thickness of the present invention is unrestricted, can be arbitrary, such as PET, TAC, PMMA, PC, COP base
Any one of film or other achievable materials, thickness select 25~250 μm, 50~200 μm, or according to demand and
Fixed other sizes.
The hardness of the film of the present invention is unrestricted, depending on purposes, such as can make widely used hardening
Film or the mantle in other a small number of fields.
The present invention above technical scheme can also be further improved, with improve other traditional performances or enhancing anti-fingerprint,
Flavouring effect, it is specific as follows.
By weight percentage, the content of resin can be recoated in the fragrance coating can choose appointing in 10%~40%
Meaning value, such as 10%, 15%, 20%, 25%, 30%, 35%, 40% etc.;The content of fragrance can be chosen in 5%~20%
Arbitrary value, such as 5%, 10%, 15%, 20% etc.;The content of organic solvent can choose the arbitrary value in 40%~85%, example
Such as 40%, 45%, 50%, 55%, 60%, 65%, 70%, 75%, 80%, 85%.
Wherein it is preferred to which the fragrance coating is mainly formed by following component is mixing cured:By weight percentage, may be used
Recoat resin 10%~30%, fragrance 10%~20%, organic solvent 50%~80%;
Preferably, the fragrance coating is mainly formed by following component is mixing cured:By weight percentage, tree can be recoated
Fat 20%~30%, fragrance 5%~20%, organic solvent surplus.
By weight percentage, the content of the anti-fingerprint resin in the anti-fingerprint coating can be chosen in 20%~50%
Arbitrary value, such as 20%, 25%, 30%, 35%, 40%, 45%, 50% etc.;The content of pore creating material can choose 2%~
Arbitrary value in 8%, such as 2%, 3%, 4%, 5%, 6%, 7%, 8% etc..
Wherein it is preferred to which the anti-fingerprint coating is mainly formed by following component is mixing cured:By weight percentage,
Anti-fingerprint resin 30%~50%, pore creating material 2%~5%, organic solvent 45%~68%;
Preferably, the anti-fingerprint coating is mainly formed by following component is mixing cured:By weight percentage, anti-fingerprint
Resin 30%~40%, pore creating material 5%~8%, organic solvent 52%~65%.
Preferably, it is described recoat resin be heat reactive resin or light-cured resin, preferably phenolic resin, polyester resin,
It is one or more in polyamide, polyethylene, polyvinyl chloride, polystyrene and polypropylene.
Preferably, the fragrance mixes for one or both of natural perfume material and synthetic perfume, and preferably synthetic fragrance is excellent
Select hydro carbons, alcohols, ethers, acids, esters, lactone, aldehydes, ketone, acetals, ketal class, nitrile, phenols and heterocyclic fragrant
It is one or more in material.
Preferably, the anti-fingerprint resin is the heat reactive resin or light-cured resin of anti-fingerprint, the preferably phenol of anti-fingerprint
It is one or more in urea formaldehyde, polyester resin, polyamide, polyethylene, polyvinyl chloride, polystyrene and polypropylene.
Preferably, the pore creating material is NCO type curing agent, preferably one kind in monoisocyanates and polyisocyanates or two
Person mixes, and preferably one or both of toluene di-isocyanate(TDI) and methyl diphenylene diisocyanate mix.
The above pore creating material can be reacted with active H releases CO2Gas, to achieve the effect that pore-creating.
Preferably, the organic solvent in the fragrance coating is one or more in alcohol, ketone, ether and ester, preferably acetic acid
Ethyl ester, butyl acetate, butanone, methylisobutylketone, propylene glycol monomethyl ether, propylene glycol methyl ether acetate, isopropanol, ethyl alcohol, n-butanol,
It is one or more in isobutanol;
Preferably, the organic solvent in the anti-fingerprint coating is one or more in alcohol, ketone, ether and ester, preferably second
Acetoacetic ester, butyl acetate, butanone, methylisobutylketone, propylene glycol monomethyl ether, propylene glycol methyl ether acetate, isopropanol, ethyl alcohol, positive fourth
It is one or more in alcohol, isobutanol.
Preparation method with fragrance fingerprint proof membrane described above generally includes to be coated with and cures two steps, and each layer is pressed
Sequence is coated with successively, specifically includes the following steps:
Step A:It is coated with fragrance masking liquid in the substrate surface, then cures, forms fragrance coating;
Step B:It is coated with the anti-fingerprint masking liquid on the surface of fragrance coating, then cures, forms anti-fingerprint coating.
Fragrance masking liquid and anti-fingerprint masking liquid are prepared respectively according to the formula of the fragrance coating and the anti-fingerprint coating
It forms.
In above method, cured mode and condition are depending on the type of resin.Coating method is arbitrary, such as is scraped
Blade, atomizing, roll-type, slit etc..
In addition, in actual product, according to different needs, can also increase after step with before step B together with apply
The process of cloth binder.
In order to improve the feasibility of coating, reducing operation difficulty or reduce wastage of material rate, it is preferable that the fragrance masking liquid
Solid content be 10~40wt%, preferably 15~35wt%, more preferable 20~35wt%.
Preferably, the solid content of the anti-fingerprint masking liquid be 20~50wt%, preferably 25~45wt%, more preferable 30~
45wt%.
Preferably, the resin that recoats is ultraviolet-curing resin, and the curing in the step A is:First heating is dry
It is dry, rear ultraviolet radiation-curable;
Preferably, the anti-fingerprint resin is ultraviolet-curing resin, and the curing in the step B is:First heating is dry
It is dry, rear ultraviolet radiation-curable.
On the one hand heating can accelerate solvent to volatilize, reduce solidification difficulty, on the one hand can also reinforce pore creating material in masking liquid
In chemical reaction, improve anti-fingerprint effect.
To sum up, compared with prior art, invention achieves following technique effects:
(1) not only solve the problem of can not taking into account fragrance and anti-fingerprint, and improve the adherence of film, translucency,
The performances such as wearability and hardness;
(2) binder between each layer is saved, technique is simplified;
(3) resin for selecting photocuring reduces the pollution that solvent volatilizees to environment;
(4) retention period of fragrance is improved, holding two months or more can be at least stablized;
(5) preparation method flow of the invention is simple, is not related to complex device, therefore easily industrialization promotion.
Description of the drawings
It, below will be to specific in order to illustrate more clearly of the specific embodiment of the invention or technical solution in the prior art
Embodiment or attached drawing needed to be used in the description of the prior art are briefly described, it should be apparent that, in being described below
Attached drawing is some embodiments of the present invention, for those of ordinary skill in the art, before not making the creative labor
It puts, other drawings may also be obtained based on these drawings.
Fig. 1 is the structural schematic diagram of cured film provided by the invention;
Fig. 2 is that the fragrance of cured film provided by the invention changes over time tendency chart.
Specific implementation mode
Technical scheme of the present invention is clearly and completely described below in conjunction with the drawings and specific embodiments, but
Be it will be understood to those of skill in the art that it is following described embodiments are some of the embodiments of the present invention, rather than it is whole
Embodiment is merely to illustrate the present invention, and is not construed as limiting the scope of the invention.Based on the embodiments of the present invention, ability
The every other embodiment that domain those of ordinary skill is obtained without making creative work, belongs to guarantor of the present invention
The range of shield.The person that is not specified actual conditions in embodiment, carries out according to conventional conditions or manufacturer's recommended conditions.Agents useful for same
Or production firm person is not specified in instrument, is the conventional products that can be obtained by commercially available purchase.
Embodiment 1
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 10 parts by weight and recoating for 30 parts by weight
UV-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 60 parts by weight, stirs 30min, shape
At masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 40 parts by weight and 5 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into the butanone of 55 parts by weight and isopropanol (isometric ratio) mix it is molten
In agent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.Structure such as Fig. 1, successively include base material 1,
Fragrance coating 2, anti-fingerprint coating 3, fragrance coating 2 contain perfume particles 5, and anti-fingerprint coating 3 forms mesoporous containing pore creating material
4。
Embodiment 2
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 20 parts by weight and recoating for 10 parts by weight
UV-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 70 parts by weight, stirs 30min, shape
At masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 50 parts by weight and 8 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into 42 parts by weight butanone and isopropyl alcohol mixed solvent it is (isometric
Than) in, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.Structure such as Fig. 1, successively include base material 1,
Fragrance coating 2, anti-fingerprint coating 3, fragrance coating 2 contain perfume particles 5, and anti-fingerprint coating 3 forms mesoporous containing pore creating material
4。
Embodiment 3
Masking liquid can be recoated:The fragrance of 5 parts by weight (rose is provided according to human relations chemical industry) and 40 parts by weight are recoated into purple
Outer light-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 55 parts by weight, is stirred 30min, is formed
Masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 30 parts by weight and 2 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into 68 parts by weight butanone and isopropyl alcohol mixed solvent it is (isometric
Than) in, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.Structure such as Fig. 1, successively include base material 1,
Fragrance coating 2, anti-fingerprint coating 3, fragrance coating 2 contain perfume particles 5, and anti-fingerprint coating 3 forms mesoporous containing pore creating material
4。
Embodiment 4
It is different that its differing only in from embodiment 1 can recoat the type of resin and solvent in masking liquid, specially:
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 10 parts by weight and recoating for 30 parts by weight
UV-cured resin PCP-001 (Natoco offers) is dissolved into respectively in the ethyl acetate solvent of 60 parts by weight, stirring
30min, formation can recoat masking liquid;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 40 parts by weight and 5 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into the butanone of 55 parts by weight and isopropanol (isometric ratio) mix it is molten
In agent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.Structure such as Fig. 1, successively include base material 1,
Fragrance coating 2, anti-fingerprint coating 3, fragrance coating 2 contain perfume particles 5, and anti-fingerprint coating 3 forms mesoporous containing pore creating material
4。
Embodiment 5
Its from embodiment 1 to differ only in the type of resin and solvent in anti-fingerprint masking liquid different, specially:
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 10 parts by weight and recoating for 30 parts by weight
UV-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 60 parts by weight, stirs 30min, shape
At masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MD002 (Natoco offers) of 40 parts by weight and 5 parts by weight
ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into ethyl acetate and n-butanol (isometric ratio) mixing of 55 parts by weight
In solvent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.Structure such as Fig. 1, successively include base material 1,
Fragrance coating 2, anti-fingerprint coating 3, fragrance coating 2 contain perfume particles 5, and anti-fingerprint coating 3 forms mesoporous containing pore creating material
4。
Embodiment 6
It is different from the type for differing only in pore creating material in anti-fingerprint masking liquid of embodiment 1, by ADD-3275 curing agent
Replace with CAA-004 curing agent (Changzhou Chinese mugwort card provides).
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 10 parts by weight and recoating for 30 parts by weight
UV-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 60 parts by weight, stirs 30min, shape
At masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 40 parts by weight and 5 weight
The CAA-004 curing agent (Changzhou Chinese mugwort card provides) of part is dissolved into the butanone and isopropanol (isometric to compare) mixed solvent of 55 parts by weight
In, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.Structure such as Fig. 1, successively include base material 1,
Fragrance coating 2, anti-fingerprint coating 3, fragrance coating 2 contain perfume particles 5, and anti-fingerprint coating 3 forms mesoporous containing pore creating material
4。
Embodiment 7
It is different that its differing only in from embodiment 1 can recoat the composition of masking liquid, is:Fragrance (the rose fragrant of 5 parts by weight
Material is provided according to human relations chemical industry), 20 parts by weight recoat UV-cured resin MA003 (vertical big chemical industry provides), 75 parts by weight
Butanone.
Masking liquid can be recoated:The fragrance of 5 parts by weight (rose is provided according to human relations chemical industry) and 20 parts by weight are recoated into purple
Outer light-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 75 parts by weight, is stirred 30min, is formed
Masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 40 parts by weight and 5 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into the butanone of 55 parts by weight and isopropanol (isometric ratio) mix it is molten
In agent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.Structure such as Fig. 1, successively include base material 1,
Fragrance coating 2, anti-fingerprint coating 3, fragrance coating 2 contain perfume particles 5, and anti-fingerprint coating 3 forms mesoporous containing pore creating material
4。
Embodiment 8
It is different from the composition for differing only in anti-fingerprint masking liquid of embodiment 1, is:The anti-fingerprint ultraviolet light of 20 parts by weight
Solidified resin MA001 (vertical big chemical industry provides), the ADD-3275 curing agent (vertical big chemical industry provides) of 8 parts by weight, 72 parts by weight
Butanone and isopropyl alcohol mixed solvent (isometric ratio).
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 10 parts by weight and recoating for 30 parts by weight
UV-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 60 parts by weight, stirs 30min, shape
At masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 20 parts by weight and 8 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into the butanone of 72 parts by weight and isopropanol (isometric ratio) mix it is molten
In agent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.Structure such as Fig. 1, successively include base material 1,
Fragrance coating 2, anti-fingerprint coating 3, fragrance coating 2 contain perfume particles 5, and anti-fingerprint coating 3 forms mesoporous containing pore creating material
4。
Comparative example 1
Masking liquid can be recoated:The fragrance of 3 parts by weight (rose is provided according to human relations chemical industry) and 9 parts by weight are recoated into purple
Outer light-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 88 parts by weight, is stirred 30min, is formed
Masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 40 parts by weight and 5 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into the butanone of 55 parts by weight and isopropanol (isometric ratio) mix it is molten
In agent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.
Comparative example 2
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 10 parts by weight and recoating for 30 parts by weight
UV-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 60 parts by weight, stirs 30min, shape
At masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 60 parts by weight and 10 weights
The ADD-3275 curing agent (vertical big chemical industry provides) for measuring part is dissolved into butanone and isopropanol (isometric ratio) mixing of 30 parts by weight
In solvent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.
Comparative example 3
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 30 parts by weight and recoating for 30 parts by weight
UV-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 40 parts by weight, stirs 30min, shape
At masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 40 parts by weight and 10 weights
The ADD-3275 curing agent (vertical big chemical industry provides) for measuring part is dissolved into butanone and isopropanol (isometric ratio) mixing of 50 parts by weight
In solvent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.
Comparative example 4
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 10 parts by weight and recoating for 30 parts by weight
UV-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 60 parts by weight, stirs 30min, shape
At masking liquid can be recoated;
Anti-fingerprint masking liquid:The anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 50 parts by weight is dissolved into
Butanone and isopropanol (isometric ratio) in the mixed solvent of 50 parts by weight, stirring 30min form anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain an anti-fingerprint cured film.
Comparative example 5
Masking liquid can be recoated:The UV-cured resin MA003 (vertical big chemical industry provides) that recoats of 30 parts by weight is dissolved into
In the butanone solvent of 70 parts by weight, 30min is stirred, formation can recoat masking liquid;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 40 parts by weight and 5 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into the butanone of 55 parts by weight and isopropanol (isometric ratio) mix it is molten
In agent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, cured film can be recoated by obtaining one;Again will
Anti-fingerprint masking liquid, which is coated on, to be recoated on cured film, be placed in 80 DEG C of cycle baking oven dry 2min, about via dosage later
500mJ/cm2Ultraviolet light, obtain an anti-fingerprint cured film.
Comparative example 6
Masking liquid can be recoated:By the fragrance (rose is provided according to human relations chemical industry) of 10 parts by weight and recoating for 30 parts by weight
UV-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 60 parts by weight, stirs 30min, shape
At masking liquid can be recoated;
Ordinary hardening masking liquid:By the general ultraviolet light-cured resin OA001 (vertical big chemical industry provides) of 40 parts by weight and 5 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into the butanone of 55 parts by weight and isopropanol (isometric ratio) mix it is molten
In agent, stirring 30min formation can the Ordinary hardening coating fluid of pore-creating;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Ordinary hardening masking liquid, which is coated on, again to recoat on cured film, be placed in 80 DEG C of cycle baking oven dry 2min, later via
Dosage about 500mJ/cm2Ultraviolet light, obtain one band the Ordinary hardening film of fragrance.
Comparative example 7
Masking liquid can be recoated:The fragrance of 10 parts by weight (rose is provided according to human relations chemical industry) and 5 parts by weight are recoated into purple
Outer light-cured resin MA003 (vertical big chemical industry provides) is dissolved into respectively in the butanone solvent of 85 parts by weight, is stirred 30min, is formed
Masking liquid can be recoated;
Anti-fingerprint masking liquid:By the anti-fingerprint UV-cured resin MA001 (vertical big chemical industry provides) of 40 parts by weight and 5 weight
Part ADD-3275 curing agent (vertical big chemical industry provide) be dissolved into the butanone of 55 parts by weight and isopropanol (isometric ratio) mix it is molten
In agent, stirring 30min formation can pore-creating anti-fingerprint coating fluid;
It first will can recoat masking liquid to be coated on the PET transparent bases (South Korea Cologne U43R) of 100 μm of thickness, be placed in 80 DEG C
Dry 2min in baking oven is recycled, later via dosage about 400mJ/cm2Ultraviolet light, obtain one band fragrance can recoat hardening
Film;Anti-fingerprint masking liquid, which is coated on, again to recoat on cured film, dry 2min is placed in 80 DEG C of cycle baking oven, later via agent
Measure about 500mJ/cm2Ultraviolet light, obtain one band fragrance anti-fingerprint cured film.
The properties of the above cured film are as shown in table 1.
Table 1
Note:
The present invention is according to K7105~1981 JIS《The test method of plastic optics performance》Standard, test its full light
Transmitance and mist degree.
According to K5400~1990 JIS《The measurement of powdery paints coating adhesion energy》Standard, test its pencil hardness.
According to GB 1720~1979《Paint film adhesion measuring method》Standard, test HC adhesive force, wherein 100/100 generation
Table not demoulding completely, 90/100 represents and falls off 10%.
According to HG/T 4303~2012《Surface hardened layer polyester film wearability assay method》The abrasion performance of testing film
Can, using 0000# steel wool, 1000gf/cm2It bears a heavy burden, by detecting the abrasion resistance limit of the membrane surface without scuffing, to judge
The abrasion resistant effect of film, abrasion resistance is higher, and effect is better.
According to GB/T 30693~2014《The measurement of plastic film and water contact angle》Standard, the water on testing film surface
Contact angle, water contact angle is higher, illustrates that hydrophobicity is better, anti-fingerprint effect is better.Fingerprint residues test method is as follows:In diaphragm
On leave fingerprint, with 200gf/cm2It bears a heavy burden, non-dust cloth is tied up on abrasion performance instrument, it is round-trip to wipe diaphragm 5 times, see fingerprint residues
Situation.
According to GB/T 14454.2~2008《Fragrance aroma rating method》Standard, the fragrance of material is judged, wherein zero generation
Table fragrance is apparent, and representative generation fragrance is slight, × represent British plain spirits.
The formula that masking liquid can be recoated in table refers to the weight ratio of fragrance, resin and solvent, and the formula of anti-fingerprint masking liquid refers to
The weight ratio of resin, curing agent and solvent.
Data are shown in table, and the present invention can form adherence, translucency, mist degree, hardness, anti-finger on PET base material surface
Line and the hardening coat for having fragrance.The material advantages are:Not only it ensure that the excellent anti-fingerprint function of material, but also imparted
The certain fragrance of material, and fragrance can continue two months or more.Fig. 2 shows the fragrance of 1 cured film of embodiment of the present invention guarantors
Trend is held, fragrance level is measured using GC-MS.
In addition, the flavor concentration with fragrance anti-fingerprint cured film in the present invention can pass through the additive amount of fragrance and pore creating material
It adjusts, fragrance additive amount is very few, and material fragrance is very slight, but fragrance additive amount is excessive, can reduce the anti-fingerprint performance of material.
The addition of pore creating material can reduce the wearability of material, but influence in a certain range it is not too large, if exceed optimum range, it is resistance to
Mill property declines to a great extent, and adhesive force can be made to decline.
Finally it should be noted that:The above embodiments are only used to illustrate the technical solution of the present invention., rather than its limitations;To the greatest extent
Present invention has been described in detail with reference to the aforementioned embodiments for pipe, it will be understood by those of ordinary skill in the art that:Its according to
So can with technical scheme described in the above embodiments is modified, either to which part or all technical features into
Row equivalent replacement;And these modifications or replacements, various embodiments of the present invention technology that it does not separate the essence of the corresponding technical solution
The range of scheme.
Claims (10)
1. a kind of band fragrance fingerprint proof membrane, which is characterized in that include base material, fragrance coating and anti-fingerprint coating successively;
The fragrance coating is mainly formed by following component is mixing cured:By weight percentage, can recoat resin 10%~
40%, fragrance 5%~20%, organic solvent 40%~85%;
The anti-fingerprint coating is mainly formed by following component is mixing cured:By weight percentage, anti-fingerprint resin 20%~
50%, pore creating material 2%~8%, surplus is organic solvent.
2. band fragrance fingerprint proof membrane according to claim 1, which is characterized in that the fragrance coating is mainly by following component
It is mixing cured to form:By weight percentage, resin 10%~30%, fragrance 10%~20%, organic solvent 50% can be recoated
~80%;
Preferably, the fragrance coating is mainly formed by following component is mixing cured:By weight percentage, resin can be recoated
20%~30%, fragrance 5%~20%, organic solvent surplus.
3. band fragrance fingerprint proof membrane according to claim 1 or 2, which is characterized in that the anti-fingerprint coating mainly by with
Lower ingredient is mixing cured to be formed:By weight percentage, anti-fingerprint resin 30%~50%, pore creating material 2%~5%, You Jirong
Agent 45%~68%;
Preferably, the anti-fingerprint coating is mainly formed by following component is mixing cured:By weight percentage, anti-fingerprint resin
30%~40%, pore creating material 5%~8%, organic solvent 52%~65%.
4. band fragrance fingerprint proof membrane according to claim 1, which is characterized in that the resin that recoats is heat reactive resin
Or light-cured resin, preferably phenolic resin, polyester resin, polyamide, polyethylene, polyvinyl chloride, polystyrene and poly- third
It is one or more in alkene.
5. band fragrance fingerprint proof membrane according to claim 1, which is characterized in that the fragrance is that natural perfume material and synthesis are fragrant
The mixing of one or both of material, preferably synthetic fragrance, preferably hydro carbons, alcohols, ethers, acids, esters, lactone, aldehydes, ketone
It is one or more in class, acetals, ketal class, nitrile, phenols and heterocyclic fragrance.
6. band fragrance fingerprint proof membrane according to claim 1, which is characterized in that the anti-fingerprint resin is the heat of anti-fingerprint
Solidified resin or light-cured resin, the preferably phenolic resin, polyester resin, polyamide, polyethylene of anti-fingerprint, polychlorostyrene second
It is one or more in alkene, polystyrene and polypropylene.
7. band fragrance fingerprint proof membrane according to claim 1, which is characterized in that the pore creating material is NCO type curing agent, excellent
One or both of menu isocyanates and polyisocyanates mix, and preferably toluene di-isocyanate(TDI) and diphenyl methane two is different
One or both of cyanate mixes.
8. band fragrance fingerprint proof membrane according to claim 1, which is characterized in that the organic solvent in the fragrance coating is
It is one or more in alcohol, ketone, ether and ester, ethyl acetate, butyl acetate, butanone, methylisobutylketone, propylene glycol monomethyl ether,
It is one or more in propylene glycol methyl ether acetate, isopropanol, ethyl alcohol, n-butanol, isobutanol;
Preferably, the organic solvent in the anti-fingerprint coating is one or more in alcohol, ketone, ether and ester, preferably acetic acid second
It is ester, butyl acetate, butanone, methylisobutylketone, propylene glycol monomethyl ether, propylene glycol methyl ether acetate, isopropanol, ethyl alcohol, n-butanol, different
It is one or more in butanol.
9. preparation method of claim 1~8 any one of them with fragrance fingerprint proof membrane, which is characterized in that including following step
Suddenly:
Step A:It is coated with fragrance masking liquid in the substrate surface, then cures, forms fragrance coating;The fragrance masking liquid is according to institute
The formula for stating fragrance coating is formulated;
Step B:It is coated with anti-fingerprint masking liquid on the surface of the fragrance coating, then cures, forms anti-fingerprint coating;The anti-finger
Line masking liquid is formulated according to the formula of the anti-fingerprint coating.
10. preparation method according to claim 9, which is characterized in that the solid content of the fragrance masking liquid be 10~
40wt%, preferably 15~35wt%, more preferable 20~35wt%;
Preferably, the solid content of the anti-fingerprint masking liquid be 20~50wt%, preferably 25~45wt%, more preferable 30~
45wt%;
Preferably, the resin that recoats is ultraviolet-curing resin, and the curing in the step A is:First heat drying, after
Ultraviolet radiation-curable;
Preferably, the anti-fingerprint resin is ultraviolet-curing resin, and the curing in the step B is:First heat drying, after
Ultraviolet radiation-curable.