KR20130090521A - Sand for cats and cats sand manufacturing method - Google Patents

Sand for cats and cats sand manufacturing method Download PDF

Info

Publication number
KR20130090521A
KR20130090521A KR1020120011731A KR20120011731A KR20130090521A KR 20130090521 A KR20130090521 A KR 20130090521A KR 1020120011731 A KR1020120011731 A KR 1020120011731A KR 20120011731 A KR20120011731 A KR 20120011731A KR 20130090521 A KR20130090521 A KR 20130090521A
Authority
KR
South Korea
Prior art keywords
weight
raw material
mixing
sand
zeolite
Prior art date
Application number
KR1020120011731A
Other languages
Korean (ko)
Other versions
KR101356232B1 (en
Inventor
이학섭
Original Assignee
이학섭
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 이학섭 filed Critical 이학섭
Priority to KR1020120011731A priority Critical patent/KR101356232B1/en
Publication of KR20130090521A publication Critical patent/KR20130090521A/en
Application granted granted Critical
Publication of KR101356232B1 publication Critical patent/KR101356232B1/en

Abstract

PURPOSE: Sand for pet cats and a manufacturing method thereof are provided to minimize dust generated in the use of sand for pet cats, to prevent various diseases induced by the dust, and to offer pleasant surrounding environment. CONSTITUTION: Sand for pet cats comprises a main material composed of zeolite in the form of powder, a supplementary material composed of bentonite and montmorillonite, and an additive composed of baking soda and cellulose, which are mixed, kneaded, rolled, and dried to take a granular form. The main material is the mixture of a first material which is made by mixing 30 wt% zeolite in the form of powder and 5 wt% water to take a granular form with a size of 1 to 2 mm; and 40 wt% of the second material which is composed of crushed zeolite in a granular form with a size of 1 to 2 mm. The supplementary material is the mixture of 5 wt% bentonite in a granular form and 15 wt% montmorillonite. The additive is the mixture of 3% baking soda, 2 wt% cellulose, and 5 wt% polyacrylamide.

Description

애완용 모래 및 그 제조방법{sand for cats and cats sand manufacturing method}Sand for cats and its manufacturing method {sand for cats and cats sand manufacturing method}

본 발명은 애완용 모래 및 그 제조방법에 관한 것으로서, 보다 상세하게는 애완용으로 고양이를 사육함에 있어서, 발생되는 대,소변 등의 분비물을 간편·용이하게 처리할 수 있도록 함은 물론, 대,소변에 의한 악취 탈취, 항균, 음이온, 원적외선 등의 기능성이 부각된 애완용 모래 및 이를 제조하기 위한 제조방법에 관한 것이다.The present invention relates to a sand for pets and a method for manufacturing the same, and more particularly, to facilitate the easy and easy treatment of secretions, such as feces, urine, etc. generated in breeding cats for pets, The present invention relates to a pet sand having a high odor, antibacterial effect, anion, and far infrared rays, and a manufacturing method for manufacturing the same.

또한, 본 발명은 고양이를 사육함에 있어, 분비물 특히, 액체상태로 분비되는 소변을 흡수 응고시켜 덩어리형태로 이루어지도록 하여 배출되는 소변 후처리 작업을 사용자가 쉽고 편리하게 행 할 수 있는 것이다.In addition, the present invention in the breeding of cats, the user can easily and conveniently carry out the urine post-treatment work is discharged by absorbing and coagulate the secretion, in particular in the liquid state to form a lump form.

일반적으로, 사람이 살아가기 위한 의식주(衣食住)가 기본적인 필수요소이며, 현대사회는 산업과 문명의 발달로 인해 도시화되어 자연에서 벗어나 인공적인 환경에서 살아가고 있다.In general, consciousness for man's life is a basic necessity, and modern society is urbanized due to the development of industry and civilization, living out of nature and living in an artificial environment.

도시화된 인공적인 환경에서도 인간의 본능은 환경친화적이며 자연에 속하여 자연으로 돌아가고 싶은 욕구가 절실하며, 핵가족화와 고령화에 따른 사회적 외면과 고독함과 외로움에 따른 우울증 등의 경제발전에 따른 사회적 모순이 점점 심화되고 있다.Even in the urbanized artificial environment, human instincts are environmentally friendly and the desire to return to nature is urgently needed, and social contradictions due to economic development such as social externality due to nuclear family age and aging and depression due to loneliness and loneliness are gradually increasing. It is deepening.

예전의 농경사회에서는 개, 고양이는 물론, 햄스터, 고슴도치, 토끼 등과 같은 중소형 동물은 부족한 식(食)을 위해 사육되거나 또는, 매매를 목적으로 사육하였으나, 현재는 단순한 동물이 아닌 가족의 일원으로 인식되고 있다.In the old farming society, small and medium-sized animals such as hamsters, hedgehogs, rabbits, as well as dogs and cats were raised for lack of food or for sale, but are now recognized as part of a family rather than just animals. It is becoming.

도심속에서 자연과 동물의 친근함을 얻고 교감을 통해 자연을 알고 삶의 질을 높이기 위한 수단을 애완용 동물이 확대되고 있으며, 동물애호가나 마니아에 의해 다각적으로 애완동물에 대한 수요가 점증적으로 높아지고 있다.In the city center, pets are expanding as a means of gaining familiarity with nature and sympathy and improving nature and improving the quality of life.As animal lovers and enthusiasts, the demand for pets is gradually increasing. have.

현재, 다종의 애완동물이 일반가정이나 영업소 및 동물원이나 농장 등에서 사육되고 있으며, 특히, 고양이나 햄스터, 고슴도치, 토끼 등과 같은 중소형 동물은 동물이라는 개념을 넘어 가족이며 인생의 동반자의 역할로 자리 잡고 있는 추세이다.Currently, many kinds of pets are raised in general homes, business offices, zoos and farms. In particular, small and medium-sized animals such as cats, hamsters, hedgehogs, rabbits, etc. are not only animals, but also family and life partners. It is a trend.

고양이나 햄스터, 고슴도치, 토끼 등과 같은 중소형 동물을 키우기 위해서는 사람과 마찬가지로 집과 음식 및 기타 도구가 필수적으로 요구되며, 음식과 동물 우리의 경우에는 동물의 특성에 따라 다양한 형태의 사료와 우리가 널리 보급되어 사용되고 있다.In order to raise small and medium-sized animals such as cats, hamsters, hedgehogs, rabbits, etc., homes, food, and other tools are indispensable, just like humans. It is used.

상기와 같이, 애완동물을 가족의 일원으로 생각하고 함께 살아가는 동반자로 취급되고 있으므로, 애완동물용 용품이 다각도로 개발되어 사용되고 있으며, 특히, 동물우리라는 개념이 단순히 가둬 기르고 잠자리를 위해 수단이 아니라, 인간과 마찬가지로 각종 놀이기구와 위생적이고 청결한 환경에서 살아갈 수 있도록 화장실 공간, 사료공간, 잠자리 공간 등의 각종 편의시설이 구성되어 있다.As mentioned above, because pets are considered as members of the family and are treated as companions living with them, pet supplies have been developed and used in various angles, and in particular, the concept of animal cages is not simply a means of raising and sleeping, Like humans, various facilities such as toilet space, feed space, and dragonfly space are provided to live in various play equipment and sanitary and clean environment.

그러나, 애완동물이 가족의 일원이며 동반자 역할을 수행한다고는 하지만, 지능이 낮고 동물의 본능에 충실하게 생활하게 되므로, 동물 특유의 세균과 냄새를 풍기게 되며, 대,소변이나 분비물에 의한 악취가 발생하게 되고, 분비물을 스스로 처리할 수 없으므로, 실내에서 사육되는 경우 각종 악취를 발생시키게 되어 청결한 위생관리가 이루어지지 못하고 있는 실정이다.However, although pets are part of the family and act as companions, they are low in intelligence and faithful to the animal's instincts, resulting in bacteria and odors that are unique to the animals. It is generated, and can not process the secretion itself, when breeding indoors will cause various odors, the situation is not clean hygiene management.

일반가정의 실내에서 고양이, 강아지, 햄스터, 고슴도치, 토끼 등과 같은 애완동물을 우리에 가둬 기르는 과정에서, 우리 바닥에는 볏짚이나 갈대, 나무 톱밥 또는 모래, 펄프 모래 등으로 구성된 베딩이 사용되고 있다.In the process of keeping pets such as cats, puppies, hamsters, hedgehogs, rabbits, etc. in our homes, we use beddings made of rice straw, reeds, wood sawdust or sand, and pulp sand.

특히, 고양이의 경우에는 대,소변을 처리하기 위한 수단으로 일명 '고양이 모래'가 사용되고 있다.In particular, in the case of cats, so-called 'cat sand' is used as a means for treating urine and urine.

이하, 본 발명에서는 일반적으로 사용되고 있는 '고양이 모래'라는 단어를 '애완용 모래'로 통칭하여 사용하기로 한다. Hereinafter, in the present invention, the term 'cat sand' which is generally used will be referred to collectively as 'pet sand'.

상기와 같은 종래의 고양이 모래는 단순히 바닥을 구분하고 배설물을 은폐하기 위해 사용될 뿐, 기능성이 없고 장시간 사용하게 되면, 건조로 인해 부스러져 미세한 입자가 발생되고, 바람에 쉽게 날려 실내공기를 오염시키는 주원인을 제공하고 있다.The conventional cat sand as described above is simply used to separate the floor and conceal the excrement, and if it is not functional and used for a long time, it is broken by the drying, fine particles are generated, it is easily blown by the wind to contaminate indoor air To provide.

또한, 기존의 고양이 모래는 분진에 의한 피해가 크고, 배설물에 대한 기능 즉, 악취에 대한 탈취기능을 거의 없으므로 배설물에서 발생되는 악취에 무방비한 상태로 악취에 대한 탈취가 요구되고 있는 실정이다.In addition, the existing cat sand has a large damage caused by dust, and there is almost no function for excretion, that is, a deodorization function for odors, so that the deodorization of odors is required in a state in which defense is not performed against odors generated from excrement.

상기와 같은 종래의 애완용 모래는 10-2010-7012940(동물용 화장실 모래, 이하 선행특허라 칭함)에 의해 기출원되어 있으며, 선행특허는 복수의 입상물을 포함하는 동물용 화장실 모래로서, 복수의 입상물 각각은, 무기 다공질 재료로 이루어지는 입자군과, 실리카겔과, 이 입자군 및 이 실리카겔을 일체적으로 고정하는 무기 바인더를 포함하는 것인바, 상기 무기 바인더가 시멘트이거나 시멘트와 비시멘트계 고화제와의 혼합물로 구성된 것이다.The conventional pet sand as described above is filed by 10-2010-7012940 (animal toilet sand, hereinafter referred to as a prior patent), the prior patent is an animal toilet sand containing a plurality of granular materials, a plurality of Each of the granular materials includes a particle group made of an inorganic porous material, silica gel, and an inorganic binder for integrally fixing the particle group and the silica gel, wherein the inorganic binder is cement or cement and non-cement-based solidifying agent; It consists of a mixture of 상기 비시멘트계 고화제는 황산칼슘 및 산화마그네슘을 주성분으로 하는 수경화성 고화제이고, 상기 무기 다공질 재료가 제올라이트, 아타풀자이트, 세피올라이트, 규조토 및 규조혈암으로 이루어지는 군으로부터 선택되는 1종 이상인 구성을 갖는다.The non-cement-based solidifying agent is a hydraulic hardening agent mainly composed of calcium sulfate and magnesium oxide, and the inorganic porous material is at least one member selected from the group consisting of zeolite, attapulgite, sepiolite, diatomaceous earth, and diatomaceous shale rock. Has 상기 시멘트가 저알칼리 시멘트이고, 상기 복수의 입상물은, 상기 무기 바인더의 함유량이 5 질량%∼30질량%이고, 상기 실리카겔의 함유량이 3 질량%∼20질량%인 것이다.The said cement is a low alkali cement, and the said some granular thing is 5 mass%-30 mass% of content of the said inorganic binder, and content of the said silica gel is 3 mass%-20 mass%. 그러나, 상기와 같은 선행특허에서 사용되는 실리카겔(silicagel, SiO2ㆍ2H2O)은 수분에 대한 흡수성이 우수하여 방습 및 흡수제로 사용되는 것으로서, 애완동물의 수변 흡수력은 우수하지만 응고력이 떨어지고 탈취기능이 현저하게 떨어지며, 무기 바인더로 사용되는 시멘트는 인체와 환경에 유해한 석면 등의 발암물질을 함유하고 있으므로 눈병이나 피부질환 등의 질병원인을 제공하는 폐단을 갖고 있다.However, the silica gel (silicagel, SiO2.2H2O) used in the prior patent as described above is used as a moisture-proof and absorbent due to its excellent water absorption, and has excellent water absorption ability of pets, but the coagulation power is low and the deodorizing function is remarkable. Falling, the cement used as an inorganic binder contains carcinogens, such as asbestos, which are harmful to the human body and the environment, and thus have a defect that provides a cause of diseases such as eye diseases and skin diseases. 한편, 본 발명은 본 출원인에 의해 기출원되어 등록된 특허 제 837528호(악취 탈취제 조성물, 이하 선등록 특허라 칭함)와 특허출원 10-2010-44758(천연재료를 이용한 애완용 모래와 그 제조방법, 이하, 선출원특허라 칭함)되어 있다.On the other hand, the present invention is a patent application issued by the applicant No. 837528 (odor odor deodorant composition, referred to as a pre-registered patent) and patent application 10-2010-44758 (the sand for pets using natural materials and a method of manufacturing the same, Hereinafter referred to as a prior application patent). 이러한, 선등록 특허는 분말상태의 제올라이트 50∼90중량%, 식품첨가제 1∼5중량%, 벤토나이트 5∼35중량%를 혼합 및 반죽과정, 압축과정, 절단 및 롤링과정, 건조과정에 의해 탈취제 조성물을 구성함에 있어서, 상기 분말상태의 제올라이트에는 부원료로 식물성 섬유제인 펄프를 3~5중량%로 혼합하여 점도가 없는 제올라이트를 서로 결합시키는 충전제 역할을 하게 되며, 천연 향신료가 1중량%의 혼합비율로 첨가된 구성으로 이루어진 것이다.Such, the registered patent is 50 to 90% by weight of powdered zeolite, 1 to 5% by weight of food additives, 5 to 35% by weight of bentonite by mixing and kneading process, compression process, cutting and rolling process, drying process In the composition, the powdered zeolite is mixed with 3 to 5% by weight of pulp, which is a vegetable fiber, as a raw material, and serves as a filler to bind the zeolites without viscosity to each other, and the natural spices are mixed in an amount of 1% by weight. It consists of an added configuration. 선출원 특허는 고양이나 햄스터, 고슴도치, 토끼 등의 중소동물을 사육하는 과정에서, 바닥재로 사용되는 모래를 구성함에 있어서, 분말상태의 주원료인 제올라이트 45중량%와 벤토나이트 40중량%로 구성하고, 첨가제인 토르말린 3중량%로 구성하며, 정제수 12중량%의 비율로 혼합 및 반죽하고, 혼합 반죽된 원료를 롤링시켜 0.5~1mm이하의 과립형태와, 1~3mm이하의 과립형태, 3~7mm이하의 과립형태로 구성되는 것이다.Prior application patent consists of 45% by weight of zeolite, which is the main raw material in powder form, and 40% by weight of bentonite, in forming sand used for flooring in the process of raising small animals such as cats, hamsters, hedgehogs and rabbits. It is composed of 3% by weight of tourmaline, mixed and kneaded at a rate of 12% by weight of purified water, and rolled the mixed and kneaded raw material to granules of 0.5 ~ 1mm, granules of 1 ~ 3mm, granules of 3 ~ 7mm It is composed of the form. 선출원 특허는 애완동물의 바닥재로 사용되는 과립형태의 모래를 제조함에 있어서, 천연재료의 제올라이트, 벤토나이트, 토르말린, 편백나무 분말 및 정제수를 제올라이트 45중량%와 벤토나이트를 40중량%로 구성하고, 첨가제인 토르말린 3중량%로 구성하며, 정제수 12중량%의 비율로 혼합기에서 혼합 및 반죽하는 단계; 혼합기의 개폐실린더 작동단계; 원료가 배출되어 제 1이송 콘베이어에 의해 이송되는 단계; 이송된 원료가 롤링부의 회전통에 공급되는 단계; 롤링부의 회전통이 회전되어 원료가 롤링되며 구형상으로 성형되는 단계; 롤링부의 회전통에 의해 성형된 원료가 배출되어 제 2이송콘베이어에 의해 건조부로 이송되는 단계; 건조부의 열풍히터에 의해 원료가 이송되면서 건조되는 단계; 건조된 원료가 선별부에 공급되는 단계; 선별부의 제 1, 2, 3선별체에 의한 선별단계; 각각의 제 1, 2, 3선별체에 의해 선별된 원료가 수집되는 단계; 선별 수집된 원료를 정량공급기에 투입하는 단계; 정량공급기에 의해 정량 포장되는 단계로 구성된다.Prior application patent is made in the production of granular sand used as a pet flooring material, composed of zeolite, bentonite, tourmaline, cypress powder and purified water of 45% by weight of zeolite and 40% by weight of bentonite, and additives 3% by weight of tourmaline, mixing and kneading in a mixer at a ratio of 12% by weight of purified water; Opening and closing cylinder operation of the mixer; Discharging the raw material and transporting the raw material by the first conveying conveyor; Supplying the transferred raw material to the rotating barrel of the rolling unit; Rotating the rolling unit of the rolling unit to roll the raw material and to form a spherical shape; Discharging the raw material formed by the rotating cylinder of the rolling unit and transporting the raw material to the drying unit by the second transfer conveyor; Drying the raw material while being transferred by the hot air heater of the drying unit; Supplying the dried raw material to the sorting unit; A selection step by the first, second and third sorting units of the selection unit; Collecting raw materials selected by each of the first, second and third sorting bodies; Inputting the sorted and collected raw materials into the metering feeder; It is composed of the steps of quantitative packaging by the metering feeder.

현재, 일반적으로 애완용 모래 특히, 고양이 모래로 사용되고 있는 모래는 자연상태의 나트륨 벤토나이트(sodiumbentonite)를 작은 입자로 파쇄하여 사용하는 것으로서, 나트륨계열의 특성을 이용하여 소변을 응고시키는 기능을 갖는다.Currently, sand, which is generally used as pet sand, in particular cat sand, is used by crushing natural sodium bentonite into small particles, and has a function of coagulating urine using sodium-based properties. 그러나, 상기와 같이, 자연상태의 나트륨 벤토나이트는 천연광물로 이루어져 환경친화적이기는 하나, 파쇄된 상태의 작은 입자로 구성되어 있으므로, 사용시 많은 양의 분진이 발생되어 주변환경을 오염시키는 단점을 작고 있으며, 또한, 나트륨계 벤토나이트는 국내에서는 생산되지 않고, 미국이나 중국 등에서만 생산이 가능하므로 유통되고 있는 제품의 99%이상 대부분이 수입에 의존하고 있는 실정이므로 가격이 고가이고 수급이 원활하지 못한 폐단을 갖고 있다.However, as mentioned above, natural sodium bentonite is made of natural minerals, but is environmentally friendly, but is composed of small particles in a crushed state, so that a large amount of dust is generated when using it, thereby contaminating the surrounding environment. In addition, sodium-based bentonite is not produced domestically, but can be produced only in the United States or China. Since more than 99% of the products in circulation depend on imports, the price is high and the supply and demand is not smooth. have.

본 발명은 애완용 동물을 기르는 과정에서 발생되는 대,소변 등의 이물질 특히, 고양이 소변을 응고시켜 후처리에 따른 편리성을 제공하고, 악취탈취율을 향상시켜 쾌적한 주변 환경을 조성하며, 천연재료를 이용하여 환경친화적임은 물론, 국내에서 채취 및 생산이 가능 재료를 이용하여 제품을 국산화할 수 있도록 하여 수입 의존도를 낮출 수 있고, 저렴한 가격으로 고품질의 제품을 제공함으로써, 소비자 만족도를 높일 수 있도록 된 새로운 형태의 애완용 모래를 제공하고자 하는 것이다.The present invention provides convenience for post-treatment by coagulating foreign substances such as urine and urine, especially cat urine, which is generated in the process of raising pet animals, improves the odor deodorization rate, creates a pleasant surrounding environment, and uses natural materials. It is not only environmentally friendly, but also localizes products using materials that can be collected and produced in Korea, thereby reducing dependence on imports and providing high-quality products at low prices, thereby enhancing customer satisfaction. To provide a pet sand in the form.

본 발명은 애완용 모래를 제조함에 있어, 혼합, 믹싱, 롤링, 건조, 선별 등의 단계를 거쳐 분말상태가 아닌 입상의 모래형태를 이루도록 하여 애완용 모래 사용시 발생되는 분진을 최소화 하며, 분진에 의해 발생되는 각종 질병을 방지함과 동시에 쾌적한 주변 환경을 조성할 수 있도록 된 애완용 모래를 제공하고자 하는 것이다.The present invention in the production of pet sand, by mixing, mixing, rolling, drying, screening, etc. to form a granular sand form, not a powder state to minimize the dust generated when using pet sand, and is generated by dust It is to provide a pet sand that can prevent various diseases and at the same time create a comfortable environment.

본 발명은 분말상태의 제올라이트로 이루어진 주원료와, 벤토나이트와 백토로 이루어진 보조원료와, 베이킹소다 및 셀룰로우즈로 이루어진 첨가제가 혼합 및 반죽, 롤링, 건조되어 입상으로 구성된 애완용 모래에 있어서,In the present invention, the main raw material consisting of powdered zeolite, auxiliary raw material consisting of bentonite and white clay, and additives consisting of baking soda and cellulose are mixed and kneaded, rolled and dried to form granular pet sand.

상기 주원료는 분말상태의 제올라이트 30중량%에 5중량%의 수분을 혼합 믹싱하여 1~2mm크기를 갖는 입상의 1차 원료와, 파쇄된 1~2mm 크기 입자형태의 입상의 제올라이트로 이루어진 2차 원료 40중량%로 혼합 구성되고,The main raw material is a secondary raw material consisting of granular primary raw material having a size of 1 ~ 2mm and crushed granular zeolite of 1 ~ 2mm size by mixing and mixing 5% by weight of water in 30% by weight of powdered zeolite 30% by weight Composed of 40% by weight,

상기 보조원료는 분말상태의 벤토나이트 5중량%와 백토 15중량%로 혼합 구성되며,The auxiliary material is composed of 5% by weight of powdered bentonite and 15% by weight of clay,

상기 첨가제는 베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드(polyacryiamide) 5중량%로 혼합 구성된 것을 특징으로 하는 애완용 모래.The additive is a pet sand, characterized in that consisting of 3% by weight of baking soda, 2% by weight of cellulose, 5% by weight of polyacryiamide.

이와 같은 본 발명에서, 상기 주원료는 제올라이트로 이루어진 1차 원료 40중량%와 2차 원료 45중량%로 혼합 구성되고, 상기 보조원료는 백토 8중량%로 구성되며, 상기 첨가제는 폴리아크릴아미드(polyacryiamide) 7중량%로 혼합 구성된 특징을 갖는다.In the present invention, the main raw material is composed of 40% by weight of the primary raw material made of zeolite and 45% by weight of the secondary raw material, the auxiliary raw material is composed of 8% by weight of clay, the additive is polyacryiamide ) 7% by weight of the mixed features.

본 발명은 주원료인 제올라이트와, 보조원료인 벤토나이트 및 백토와, 첨가제인 베이킹소다, 셀룰로우즈, 폴리아크릴아미드를 혼합 구성하여 애완용모래를 제조함에 있어서, 상기 주원료인 분말상태의 제올라이트 40중량%에 5중량%의 수분을 혼합하여 믹싱하여 1~2mm 크기의 입상형태의 1차 원료를 구성하는 단계;The present invention is a mixture of zeolite as a main raw material, bentonite and white clay as an auxiliary raw material, baking soda, cellulose, and polyacrylamide as additives to prepare a sand for pets, wherein 40 wt% of the powdered zeolite as the main raw material is used. Mixing 5% by weight of moisture to mix to form a primary raw material having a granular shape of 1 to 2 mm in size;

1차 원료를 전기히터를 이용하여 건조하는 단계;Drying the primary raw material using an electric heater;

건조된 1차원료 30중량%에 2차원료 40중량%를 혼합 롤링하는 단계;Mixing and rolling 40% by weight of the two-dimensional material to 30% by weight of the dried one-dimensional material;

1, 2차 원료가 혼합 롤링되는 과정에서 수분을 분무하여 5%의 수분을 갖도록 하고, 보조원료인 벤토나이트 5중량%와 백토 10중량%를 투입하여 혼합 롤링하는 단계;Spraying water in the process of mixing and rolling the first and second raw materials to have 5% moisture, and mixing and rolling 5 wt% of bentonite and 10 wt% of white clay as auxiliary materials;

주원료와 보조 원료가 혼합 롤링되는 과정에서, 첨가제인 베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드(polyacryiamide) 5중량%로 투입하여 혼합 롤링하는 단계에 의해 제조되는 특징을 갖는다.In the process of mixing and rolling the main raw material and the auxiliary raw material, it is prepared by mixing and rolling by adding 3% by weight of baking soda as an additive, 2% by weight of cellulose, and 5% by weight of polyacryiamide.

이와 같은 본 발명에서, 상기 보조원료 투입 단계에서 백토 8중량% 만을 투입하고, 첨가제 투입단계에서는 폴리아크릴아미드(polyacryiamide) 7중량% 만을 투입하여 혼합 롤링하는 단계로 구성된다.In the present invention as described above, in the auxiliary raw material input step only 8% by weight of clay, in the additive input step is composed of a step of mixing by rolling only 7% by weight of polyacrylamide (polyacryiamide).

이와 같이, 본 발명에 따른 애완용 모래를 이용함에 따라, 애완동물 특히, 고양이와 같이, 모래가 요구되는 애완용 동물을 사육함에 있어, 대,소변에 의한 악취를 탈취함과 동시에, 대,소변 후처리에 따른 편리함을 제공할 수 있으며, 수입에 의존하고 있는 애완용 모래를 국산화함에 따라, 고품질의 제품을 저렴한 가격으로 제공할 수 있어 소비에 대한 부담감을 줄일 수 있어 경제적이며, 더 나아가서는 수입에 따른 외화낭비를 줄일 수 있을 뿐만 아니라, 애완동물 시장에 대한 경쟁력을 확보할 수 있는 매우 파급적인 산업과 경제적 효과를 얻을 수 있는 것이다.As such, according to the use of the pet sand according to the present invention, in breeding pet animals requiring sand, such as pets, especially cats, while deodorizing odor due to large and urine, at the same time, after the urine and urine treatment It can provide convenience according to the localization of pet sand, which is dependent on imports, and can provide high-quality products at a low price, thereby reducing the burden on consumption. Not only can you reduce waste, but you also get a very disruptive industry and economic impact that will give you a competitive edge in the pet market.

도 1은 본 발명에 따른 애완용 모래를 나타내는 공정도,
도 2는 본 발명에 따른 애완용 모래를 나내는 사진,
도 3은 본 발명에 따른 애완용 모래의 실시에를 나타내는 사진이다.1 is a process chart showing the pet sand according to the present invention,
Figure 2 is a photo out of the pet sand according to the invention,
3 is a photograph showing an embodiment of pet sand according to the present invention.

이하, 본 발명을 첨부된 도면에 의해 보다 상세하게 설명하면 다음과 같다.DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, the present invention will be described in more detail with reference to the accompanying drawings.

도 1은 본 발명에 따른 애완용 모래를 나타내는 공정도로서, 본 발명의 애완용 모래 제조공정은 주원료인 분말상태의 제올라이트 40중량%에 5중량%의 수분을 혼합하여 믹싱하여 1~2mm 크기의 입상형태의 1차 원료를 구성하는 단계(S10); 1차 원료를 전기히터를 이용하여 건조하는 단계(S20); 건조된 1차원료 30중량%에 2차원료 40중량%를 혼합 롤링하는 단계(S30); 1, 2차 원료가 혼합 롤링되는 과정에서 수분을 분무하여 5%의 수분을 갖도록 하고, 보조원료인 벤토나이트 5중량%와 백토 10중량%를 투입하여 혼합 롤링하는 단계(S40); 주원료와 보조 원료가 혼합 롤링되는 과정에서, 첨가제인 베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드(polyacryiamide) 5중량%로 투입하여 혼합 롤링하는 단계(S50)에 의해 제조되는 것이다.1 is a process chart showing the pet sand according to the present invention, the pet sand manufacturing process of the present invention by mixing 5% by weight of moisture mixed with 40% by weight of the powdered zeolite of the main raw material of the granular form of 1 ~ 2mm size Constructing a primary raw material (S10); Drying the primary raw material using an electric heater (S20); Mixing and rolling 40% by weight of the two-dimensional material to 30% by weight of the dried one-dimensional material (S30); Spraying moisture in the process of mixing and rolling the first and second raw materials to have 5% moisture, and mixing and rolling 5 wt% of bentonite and 10 wt% of clay as auxiliary materials (S40); In the process of mixing and rolling the main raw material and the auxiliary raw material, it is prepared by mixing and rolling in an amount of 3% by weight of baking soda, 2% by weight of cellulose, and 5% by weight of polyacryliamide (S50). .

또한, 상기 보조원료 투입 단계(S40)에서는 벤토나이트 5중량%는 첨가하지 않고 백토 8중량% 만을 투입하는 단계(S41)과, 첨가제 투입단계(S50)에서는 첨가제 중에서 폴리아크릴아미드(polyacryiamide) 7중량% 만을 투입하여 혼합 롤링하는 단계(S51)에 의해 제조되는 것이다.In addition, in the auxiliary raw material input step (S40), 5 wt% of bentonite is not added, but only 8 wt% of clay is added (S41), and in the additive addition step (S50), 7% by weight of polyacrylamide (polyacryiamide) in the additive. It is manufactured by the step (S51) of mixing and rolling only by putting.

상기 1차원료에 사용되는 제올라이트는 0.1mm 입자크기의 분말상태이고, 분말 제올라이트 40중량% 대비 5중량%에 해당하는 수분을 혼합하여 믹싱하여 1~2mm 크기의 입상형태로 구성되며, 2차원료의 제올라이트는 파쇄되어 1~2mm 입자크기로 구성된다.The zeolite used in the one-dimensional material is in a powder state of 0.1mm particle size, and mixed by mixing water corresponding to 5% by weight with respect to 40% by weight of the powdered zeolite, and composed in a granular form having a size of 1 to 2mm. Zeolite is crushed and composed of 1 ~ 2mm particle size.

본 발명에서 애완용 모래를 제조하기 위한 혼합 롤링은 통상적으로 사용되는 혼합기 또는 원통형태로 회전되는 롤링기를 이용하게 되며, 1차 원료의 건조는 전기히터 또는 가스히터에 의한 건조기 및 건조로를 이용하게 되는 것으로서, 이는 통상적으로 사용되는 것이므로 이에 대한 도면표기 및 상세한 설명은 생략한다.Mixed rolling for producing pet sand in the present invention is to use a conventionally used mixer or a rolling mill rotated in a cylindrical shape, the drying of the primary raw material is to use a dryer and a drying furnace by an electric heater or gas heater as This is commonly used, so the drawing and detailed description thereof will be omitted.

상기 보조원료 투입 단계(S40)에서는 벤토나이트 5중량%와 백토 10중량%를 주원료에 투입하여 혼합 롤링되도록 하거나 또는, 단계(S41)과 같이, 보조원료로 사용되는 백토 8중량% 만을 선택하여 투입할 수 있는 것이다.In the auxiliary material input step (S40), 5% by weight of bentonite and 10% by weight of white clay are added to the main raw material to be rolled or mixed, or as in step S41, only 8% by weight of white clay used as the auxiliary raw material is selected and added. It can be.

상기 첨가제 투입 단계(S50)에서는 베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드(polyacryiamide) 5중량%로 투입하거나 또는, 단계(S51)과 같이, 첨가제 중 베이킹소다 3중량%, 셀룰로우즈 2중량%는 제외하고 폴리아크릴아미드(polyacryiamide) 7중량%만을 선택하여 투입할 수 있는 것이다.In the additive addition step (S50), 3% by weight of baking soda, 2% by weight of cellulose, 5% by weight of polyacryiamide, or 3% by weight of baking soda as an additive, as in step S51, Excluding 2% by weight of cellulose, only 7% by weight of polyacrylamide may be selected.

본 발명에서, 보조원료와 첨가제는 모두 0.05~0.1mm 입자크기의 미세한 분말상태이며, 애완모래 제조시 분말에 의한 분진을 최소화하기 위해서는 위에서 언급한 주원료 중 분말상태의 1차 원료를 입상형태로 가공하는 공정과 마찬가지로 제조하여 입상화하여 사용할 수 있는 것이다.In the present invention, the auxiliary raw material and the additive are both in the fine powder state of 0.05 ~ 0.1mm particle size, in order to minimize the dust by the powder in the production of pet sand to process the primary raw material in the powder state of the above-mentioned main raw material in a granular form It can manufacture and granulate like a process to use.

도 2는 본 발명에 따른 애완용 모래를 나내는 사진으로서, 본 발명에 따른 애완용 모래는 분말상태의 제올라이트로 이루어진 주원료와, 벤토나이트와 백토로 이루어진 보조원료와, 베이킹소다 및 셀룰로우즈로 이루어진 첨가제가 혼합 및 반죽, 롤링, 건조되어 입상으로 구성되는 것으로서, 상기 주원료는 분말상태의 제올라이트 30중량%에 5중량%의 수분을 혼합 믹싱하여 1~2mm크기를 갖는 입상의 1차 원료와, 파쇄된 1~2mm 크기 입자형태의 입상의 제올라이트로 이루어진 2차 원료 40중량%로 혼합 구성되고, 상기 보조원료는 분말상태의 벤토나이트 5중량%와 백토 15중량%로 혼합 구성되며, 상기 첨가제는 베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드(polyacryiamide) 5중량%로 혼합 구성되는 것이다.Figure 2 is a picture out of the pet sand according to the present invention, the pet sand according to the present invention is a main raw material made of a powdered zeolite, an auxiliary raw material made of bentonite and white earth, and additives made of baking soda and cellulose Mixing and kneading, rolling, and dried to form a granule, the main raw material is a granular primary raw material having a 1 ~ 2mm size by mixing and mixing 5% by weight of water with 30% by weight of powdered zeolite The secondary raw material is composed of 40% by weight of the secondary raw material consisting of granular zeolite in the form of particles of 2 mm size, and the auxiliary raw material is mixed with 5% by weight of bentonite in powder form and 15% by weight of white clay, and the additive is 3% by weight of baking soda. %, Cellulose 2% by weight, polyacryiamide (polyacryiamide) 5% by weight of the mixture.

이때, 상기 주원료는 제올라이트로 이루어진 1차 원료 40중량%와 2차 원료 45중량%로 혼합 구성되고, 상기 보조원료는 백토 8중량%로 구성되며, 상기 첨가제는 폴리아크릴아미드(polyacryiamide) 7중량%로 혼합 구성된다.At this time, the main raw material is composed of a mixture of 40% by weight of the primary raw material made of zeolite and 45% by weight of the secondary raw material, the auxiliary raw material is composed of 8% by weight of clay, the additive is polyacryiamide 7% by weight It is composed of mixed.

도 3은 본 발명에 따른 애완용 모래의 실시에를 나타내는 사진으로서, 본 발명의 애완용 모래에 의해 고양이 소변이 납짝한 형태로 응고되어 덩어리 형태로 뭉친 것을 나타내는 것이다.3 is a photograph showing an embodiment of the pet sand according to the present invention, which shows that the cat urine is solidified in a flat form and aggregated in a lump form by the pet sand of the present invention.

고양이의 소변이 애완용 모래와 접촉하게 되면, 주원료와 보조원료에 의해 단시간에 흡수되고, 주원료와 보조 원료에 의해 흡수됨과 동시에 혼합된 첨가제에 의해 응고되어 덩어리 형태로 뭉치게 되며, 소변에서 발생되는 암모니아 등의 악취는 제올라이트와 베이킹소다에 의해 흡입되어 탈취되는 것이다.When the cat's urine comes into contact with pet sand, it is absorbed by the main and auxiliary raw materials in a short time, and is absorbed by the main and auxiliary raw materials and coagulated by the mixed additives to form agglomerates. Odors such as back are sucked and deodorized by zeolite and baking soda.

본 발명에서 주원료로 사용되는 제올라이트와 보조 원료로 사용되는 벤토나이트의 화학적 성분은 아래 표 1과 같다.In the present invention, the chemical components of the zeolite used as the main raw material and the bentonite used as the auxiliary raw material are shown in Table 1 below.


품명
Product Name

규산

Silicic acid

알루미나
Alumina
철
iron
마그네슘
magnesium
칼슘
calcium
나트륨
salt
칼륨
potassium
제올라이트
Zeolite

65.01%
65.01%
19.5%
19.5%
2.84%
2.84%
1.27%
1.27%
2.30%
2.30%
0.49%
0.49%
2.22%
2.22%
벤토나이트
Bentonite

68.01%
68.01%
17.5%
17.5%
2.94%
2.94%
1.20%
1.20%
2.30%
2.30%
0.49%
0.49%
2.22%
2.22%

백토(terra alba)는 백선토, 백악이라고도 하며 백색의 점토로 도자기를 만드는데 쓰는 흙으로 주원료는 카올리나이트와 할로이사이트이다.The terra alba, also known as white clay and chalk, is the clay used to make pottery from white clay. The main ingredients are kaolinite and halosite.

첨가제로 사용되는 베이킹소다는 화학적 팽창제의 한 종류로 중탄산나트륨의 단점을 보완하기 위해 중탄산나트륨, 한 종류 이상의 산염 또는 산 생성물질과 전분을 혼합한 것이다. Baking soda, used as an additive, is a type of chemical swelling agent that combines starch with sodium bicarbonate, one or more types of acid salts, or acid products to compensate for the shortcomings of sodium bicarbonate.

셀롤로우즈는(cellulose)는 식물체의 세포벽 골격을 형성하는 주성분. D-글루코오스가 β-1,4 결합한 곧은사슬상의 다당류로서, 길이는 2000㎛이고, 두께는 35㎛이며, PH는 6.5이며, 화학적 기호는 표 2와 같다.Cellulose is the main component that forms the cell wall skeleton of plants. It is a straight chain polysaccharide which D-glucose couple | bonded with (beta) -1,4, length is 2000 micrometers, thickness is 35 micrometers, PH is 6.5, and chemical symbols are shown in Table 2.

Figure pat00001
Figure pat00001

폴리아크릴아미드(polyacryiamide)는 응집제로 사용되는 것으로서, 화학적 기호는 표 3과 같다.Polyacrylamide is used as a flocculant, and the chemical symbols are shown in Table 3.

Figure pat00002
Figure pat00002

본 발명에서, 주원료, 보조원료 및 첨가제의 혼합비율 즉, 중량%는 혼합과정에서 100중량%를 초과하지 않는 범위내에서 상호간에 2중량%의 오차 허용범위를 유지한다.In the present invention, the mixing ratio, that is, the weight percentage of the main raw material, the auxiliary raw material, and the additive maintains an error tolerance of 2% by weight within the range not exceeding 100% by weight in the mixing process.

이와 같은 본 발명에 따른 애완용 모래 및 제조방법에 따른 실시예를 설명하면 다음과 같다.Referring to the embodiment according to the pet sand and the manufacturing method according to the present invention as follows.

본 발명의 애완용 모래는 주원료인 분말상태의 제올라이트 40중량%에 5중량%의 수분을 혼합하여 믹싱하여 1~2mm 크기의 입상형태의 1차 원료를 구성하는 단계(S10); 1차 원료를 전기히터를 이용하여 건조하는 단계(S20); 건조된 1차원료 30중량%에 2차원료 40중량%를 혼합 롤링하는 단계(S30); 1, 2차 원료가 혼합 롤링되는 과정에서 수분을 분무하여 5%의 수분을 갖도록 하고, 보조원료인 벤토나이트 5중량%와 백토 10중량%를 투입하여 혼합 롤링하는 단계(S40); 주원료와 보조 원료가 혼합 롤링되는 과정에서, 첨가제인 베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드(polyacryiamide) 5중량%로 투입하여 혼합 롤링하는 단계(S50)에 의해 제조되는 것으로서, 애완용 모래 10kg을 제조하기 위해서는 먼저, 분말상태의 제올라이트 30중량%에 해당되는 3kg과 5중량%의 수분 즉, 500g을 혼합기에 투입하여 혼합 믹싱하게 되면, 1~2mm크기를 갖는 입상의 1차 원료가 가공되며, 1차 원료를 전기히터를 이용하여 건조시키게 되면, 애완용 모래를 제조하기 위한 1차원료 가공이 이루어지게 되는 것이다.Pet sand of the present invention comprises mixing 5% by weight of water in the powdered zeolite 40% by weight of the main raw material to form a primary raw material of the granular form of 1 ~ 2mm size (S10); Drying the primary raw material using an electric heater (S20); Mixing and rolling 40% by weight of the two-dimensional material to 30% by weight of the dried one-dimensional material (S30); Spraying moisture in the process of mixing and rolling the first and second raw materials to have 5% moisture, and mixing and rolling 5 wt% of bentonite and 10 wt% of clay as auxiliary materials (S40); In the process of mixing and rolling the main raw material and the auxiliary raw material, it is prepared by the step of mixing and rolling (S50) by adding 3% by weight of baking soda as an additive, 2% by weight of cellulose, and 5% by weight of polyacryiamide. To prepare 10 kg of pet sand, first, 3 kg corresponding to 30% by weight of the powdered zeolite and 5% by weight of water, that is, 500 g are mixed and mixed in a mixer, the primary granule having a size of 1 to 2 mm When the raw material is processed, and the primary raw material is dried using an electric heater, a one-dimensional material processing for producing pet sand is made.

이와 같이, 애완용 모래를 구성하는 주원료 중 1차원료가 가공되면, 파쇄된 1~2mm 크기 입자형태의 제올라이트 2차 원료를 1차 원료와 혼합 롤링하게 되는 바, 이때, 2차 원료는 혼합비율 40중량%에 해당하는 4kg이 혼합된다.As such, when the primary raw material constituting the pet sand is processed, the crushed zeolite secondary raw material in the form of 1 to 2 mm size particles is mixed and rolled with the primary raw material, wherein the secondary raw material has a mixing ratio of 40 4 kg of the weight percent is mixed.

이 과정에서, 1차원료 가공을 위해 공급된 수분 5중량%는 건조과정에서 99%정도 증발되어 소멸되고, 1, 2차 원료 혼합 롤링과정에서 추가적인 수분 5중량%에 해당하는 공급이 이루어지게 되므로 주원료의 혼합 비율 중량%는 허용범위 2중량%내에서 유지되는 것이다.In this process, 5% by weight of moisture supplied for the one-dimensional material processing is evaporated and extinguished by 99% in the drying process, and an additional 5% by weight of moisture is provided in the first and second raw material mixing rolling process. The mixing ratio weight percentage of the main raw material is maintained within the allowable range of 2% by weight.

상기 1,2차 원료를 혼합 롤링하는 과정에서 추가적인 수분 5중량%가 공급되는 것은 1, 2차원료가 롤링되는 과정에서 마찰로 인해 발생된 분진을 최소화하기 위한 것이며, 혼합 롤링 시간은 약 150초로 한다.The additional 5% by weight of moisture in the process of mixing and rolling the first and second raw materials is for minimizing the dust generated by the friction in the process of rolling the one and two-dimensional materials, and the mixing rolling time is about 150 seconds. do.

이와 같이, 주원료를 구성하는 1, 2차 중량%로 혼합 롤링한 상태에서, 보조 원료를 투입하여 혼합 롤링시키게 되는 바, 벤토나이트 5중량%에 해당되는 500g과 백토 15중량%에 해당되는 1,5kg의 혼합 롤링 시간은 약 60초로 한다.As such, in the state of mixing and rolling in the primary and secondary weight% constituting the main raw material, the auxiliary raw material is added and rolled, and the mixture is 500 g corresponding to 5 wt% bentonite and 1,5 kg corresponding to 15 wt% clay. Mixing rolling time is about 60 seconds.

이와 같이, 주원료와 보조 원료가 혼합되어 롤링된 상태에서, 첨가제를 투입하게 되는 바, 첨가제인 베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드(polyacryiamide) 5중량%로 투입하여 혼합 롤링하게 되는 것이다.As such, in the state where the main raw material and the auxiliary raw material are mixed and rolled, an additive is added. The additive is mixed with 3% by weight of baking soda, 2% by weight of cellulose, and 5% by weight of polyacryiamide. Rolling.

상기 첨가제의 공급량은 베이킹 소다는 300g이고, 셀룰로우즈는 200g이며, 폴리아크릴아미드는 500g이 된다.The feed amount of the additive is 300 g of baking soda, 200 g of cellulose, and 500 g of polyacrylamide.

이와 같이, 주원료인 제올라이트 1, 2차 원료 7kg, 보조 원료 2kg, 첨가제 1kg으로 구성된 애완용 모래가 완성되는 것이다.Thus, the pet sand consisting of the zeolite 1, the secondary raw material 7kg, the auxiliary raw material 2kg, the additive 1kg as the main raw material is completed.

상기 주원료인 제올라이트 1, 2차 원료 혼합시 공급된 5중량%의 물은 건조과정에서 일부 증발하고 보조원료와 첨가제의 혼합 롤링되는 과정에서 자연건조되어 증발하게 되므로, 전체적인 애완모래의 중량%에는 크게 영향을 미치지 않으며, 수분에 의한 중량% 허용범위인 2중량%내를 유지하게 된다.5% by weight of water supplied when mixing the first raw material and the second raw material, which is the main raw material, is partially evaporated in the drying process and naturally dried in the process of mixing and rolling of the auxiliary raw material and the additive, so that the total weight of the pet sand is large. It does not affect, and maintains within 2% by weight, which is an allowable weight percentage by moisture.

본 발명에 따른 애완용 모래는 주원료와 보조원료에 의해 고양이로부터 발생되는 분비물 즉, 대,소변을 흡수함과 동시에 암모니아 등의 악취원인이 되는 성분을 흡착하여 탈취가 이루어지게 되고, 첨가제로 사용되는 베이킹 소다에 의해 살균 및 세정효과를 갖게 되며, 셀룰로우즈와 폴리아크릴아미드에 의해 응고되어 덩어리형태로 뭉치게 되는 것이다.Pet sand according to the present invention by absorbing the secretion generated from the cat by the main raw material and the auxiliary raw material, that is, the urine, urine and at the same time adsorbs the components that cause odors such as ammonia deodorization is made, baking used as an additive It has a sterilization and cleaning effect by soda, and is solidified by cellulose and polyacrylamide to agglomerate in a lump form.

한편, 본 발명에 따른 애완용 모래를 제조하는 과정에서, 응고력을 높이기 위해서는 주원료와 보조원료 및 첨가제의 혼합 비율 즉, 혼합 중량%를 선택하여 조절하게 되는 것으로서, 먼저, 주원료인 제올라이트 1차 원료를 40중량% 즉, 4kg으로 하고, 2차 원료를 45중량% 즉, 4.5kg으로 혼합 구성되도록 하고, 보조원료는 백토 8중량% 즉, 800g을 투입하며, 첨가제는 폴리아크릴아미드(polyacryiamide) 7중량%에 해당되는 700g의 중량% 비율로 혼합 구성시킨다.On the other hand, in the process of manufacturing the pet sand according to the present invention, in order to increase the coagulation power is to adjust by adjusting the mixing ratio, that is, mixing weight% of the main raw material, auxiliary raw materials and additives, first, the zeolite primary raw material 40% by weight, that is 4kg, the secondary raw material is 45% by weight, that is to be composed of 4.5kg mixed, the auxiliary material is 8% by weight of clay, or 800g is added, the additive is 7% of polyacryiamide The composition is mixed at a weight percentage of 700 g corresponding to%.

이와 같이, 주원료와 보조 원료 및 첨가제의 혼합 비율을 다르게 구성하게 되면, 애완모래의 사용에 따른 특성 즉, 응고력이 우선적으로 요구되는 상황에 적합한 애완용 모래를 제공할 수 있고, 악취에 의한 탈취력이 우선적으로 요구되는 상황에 적합한 애완용 모래를 제공할 수 있는 것이다.In this way, if the mixing ratio of the main raw material, auxiliary raw materials and additives is different, it is possible to provide a pet sand suitable for the situation where the characteristics of the use of pet sand, that is, coagulation force is required first, and deodorizing power due to odor First of all, it is possible to provide pet sand suitable for the required situation.

본 발명에 따른 애완용 모래의 응고력에 대해 시간당 변화율을 백분율 %로 비교한 데이타는 아래 표 4와 같다.Data comparing the rate of change per hour with respect to the coagulation power of pet sand according to the present invention in percentage% is shown in Table 4 below.


구분
division

응고력/30초
Coagulation force / 30 seconds
응고력/60초
Coagulation Force / 60 seconds
응고력/90초
Coagulation Force / 90 seconds
주원료 70중량%
(1차원료 30중량%, 2차원료 40중량%)
보조원료 20중량%
(벤토나이트 5중량%, 백토 15중량%)
첨가제 10중량%
(베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드 5중량%)
70 wt% of main raw materials
(30% by weight of one-dimensional material, 40% by weight of two-dimensional material)
20% by weight of auxiliary raw materials
(5 wt% bentonite, 15 wt% clay)
10 wt% of additives
(3% by weight baking soda, 2% by weight cellulose, 5% by weight polyacrylamide)




70%



70%



90%



90%



98%



98%
주원료 85중량%
(1차원료 40중량%, 2차원료 45중량%)
보조원료 20중량%
(백토 8중량%)
첨가제 10중량%
(폴리아크릴아미드 7중량%)
85 wt% of main raw materials
(40% by weight of one-dimensional material, 45% by weight of two-dimensional material)
20% by weight of auxiliary raw materials
(8% by weight of clay)
10 wt% of additives
(7% by weight of polyacrylamide)



85%


85%


95%


95%


99%


99%

상기 표 2에 대한 응고력에 대한 백분율 기준은 별도의 측정기기를 이용한 측정이 불가능하므로, 인위적인 육안과 접촉에 의한 기준으로서, 통상적으로 굳기가 고형물형태를 이루고 흔들거나 굴림시 덩어리진 상태가 균열되어가 흩어져 탈리되지 않는 상태를 응고력 100%로 기준으로 하여 애완용 모래에 대한 응고력을 판단한 것이다.Since the percentage criteria for the coagulation force in Table 2 cannot be measured using a separate measuring device, as a reference by artificial visual contact, the solid state forms a solid form and cracks are formed when shaking or rolling. The coagulation power for the pet sand was determined based on the coagulation power of 100% based on the state that is not scattered.

본 발명에 따른 애완용 모래를 구성하는 주원료에 대한 탈취력은 아래 표 5과 같다.Deodorizing power for the main raw material constituting the pet sand according to the present invention is shown in Table 5 below.

Figure pat00003
Figure pat00003

*출처:한국생활환경시험연구원* Source: Korea Living Environment Research Institute

본 발명에 따른 애완용 모래는 도 2 및 도 3에서와 같이, 일반적으로 사용되는 고양이용 모래 용기(도면에 도시되지 않음)에 일정량의 애완용 모래를 넣어 사용하게 되며, 그림 1과 같이, 고양이가 용기에 소변을 보게 되면, 애완용 모래가 소변을 흡수하여 응고하여 그림 2와 같이, 덩어리 형태를 이루게 되는 것이다.Pet sand according to the present invention is used to put a certain amount of pet sand in a generally used cat sand container (not shown), as shown in Figure 2 and 3, as shown in Figure 1, the cat container When you urinate in, the pet sand absorbs the urine and coagulates, forming a lump, as shown in Figure 2.

이와 같이, 애완용 모래에 의해 소변이 흡수 응고돼어 덩어리 형태를 이루게 되면, 사용자가 응고되어 덩어리진 상태의 소변을 간편 용이하고 편리하게 처리할 수 있는 것이다.As such, when the urine is absorbed and solidified by the pet sand to form a lump, the user can easily and conveniently handle the urine in the solidified and lumped state.

Claims (4)

분말상태의 제올라이트로 이루어진 주원료와, 벤토나이트와 백토로 이루어진 보조원료와, 베이킹소다 및 셀룰로우즈로 이루어진 첨가제가 혼합 및 반죽, 롤링, 건조되어 입상으로 구성된 애완용 모래에 있어서,
상기 주원료는 분말상태의 제올라이트 30중량%에 5중량%의 수분을 혼합 믹싱하여 1~2mm크기를 갖는 입상의 1차 원료와, 파쇄된 1~2mm 크기 입자형태의 입상의 제올라이트로 이루어진 2차 원료 40중량%로 혼합 구성되고,
상기 보조원료는 분말상태의 벤토나이트 5중량%와 백토 15중량%로 혼합 구성되며,
상기 첨가제는 베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드(polyacryiamide) 5중량%로 혼합 구성된 것을 특징으로 하는 애완용 모래.In the pet sand composed of granules by mixing and kneading, rolling and drying the main raw material of powdered zeolite, auxiliary raw material of bentonite and white clay, and additives of baking soda and cellulose,
The main raw material is a secondary raw material consisting of granular primary raw material having a size of 1 ~ 2mm and crushed granular zeolite of 1 ~ 2mm size by mixing and mixing 5% by weight of water in 30% by weight of powdered zeolite 30% by weight Composed of 40% by weight,
The auxiliary material is composed of 5% by weight of powdered bentonite and 15% by weight of clay,
The additive is a pet sand, characterized in that consisting of 3% by weight of baking soda, 2% by weight of cellulose, 5% by weight of polyacryiamide. 제 1항에 있어서,
상기 주원료는 제올라이트로 이루어진 1차 원료 40중량%와 2차 원료 45중량%로 혼합 구성되고, 상기 보조원료는 백토 8중량%로 구성되며, 상기 첨가제는 폴리아크릴아미드(polyacryiamide) 7중량%로 혼합 구성된 것을 특징으로 하는 애완용 모래.The method of claim 1,
The main raw material is composed of 40% by weight of the primary raw material consisting of zeolite and 45% by weight of the secondary raw material, the auxiliary raw material is composed of 8% by weight of clay, the additive is mixed with 7% by weight of polyacryiamide Pet sand, characterized in that configured. 주원료인 제올라이트와, 보조원료인 벤토나이트 및 백토와, 첨가제인 베이킹소다, 셀룰로우즈, 폴리아크릴아미드를 혼합 구성하여 애완용모래를 제조함에 있어서,
상기 주원료인 분말상태의 제올라이트 40중량%에 5중량%의 수분을 혼합하여 믹싱하여 1~2mm 크기의 입상형태의 1차 원료를 구성하는 단계(S10);
1차 원료를 전기히터를 이용하여 건조하는 단계(S20);
건조된 1차원료 30중량%에 2차원료 40중량%를 혼합 롤링하는 단계(S30);
1, 2차 원료가 혼합 롤링되는 과정에서 수분을 분무하여 5%의 수분을 갖도록 하고, 보조원료인 벤토나이트 5중량%와 백토 10중량%를 투입하여 혼합 롤링하는 단계(S40);
주원료와 보조 원료가 혼합 롤링되는 과정에서, 첨가제인 베이킹소다 3중량%, 셀룰로우즈 2중량%, 폴리아크릴아미드(polyacryiamide) 5중량%로 투입하여 혼합 롤링하는 단계(S50)에 의해 제조되는 것을 특징으로 하는 애완용 모래 제조방법.In the production of pet sand by mixing zeolite as a main raw material, bentonite and white clay as an auxiliary raw material, baking soda, cellulose and polyacrylamide as additives,
Mixing 5% by weight of water with 40% by weight of the zeolite in powder form, which is the main raw material, to form a primary raw material having a granular shape of 1 to 2 mm in size (S10);
Drying the primary raw material using an electric heater (S20);
Mixing and rolling 40% by weight of the two-dimensional material to 30% by weight of the dried one-dimensional material (S30);
Spraying moisture in the process of mixing and rolling the first and second raw materials to have 5% moisture, and mixing and rolling 5 wt% of bentonite and 10 wt% of clay as auxiliary materials (S40);
In the process of mixing and rolling the main raw material and the auxiliary raw material, it is prepared by mixing and rolling (S50) by adding 3% by weight of baking soda as an additive, 2% by weight of cellulose, and 5% by weight of polyacryiamide. Pet sand production method characterized in that. 제 3항에 있어서,
상기 주원료는 1차원료를 40중량%와 2차원료 45중량%로 공급되고,
상기 보조원료 투입 단계(S40)에서는 백토 8중량% 만을 투입하는 단계(S41)와;
상기 첨가제 투입단계(S50)에서는 폴리아크릴아미드(polyacryiamide) 7중량% 만을 투입하는 단계(S51)가 포함되는 것을 특징으로 하는 애완용 모래 제조방법.The method of claim 3,
The main raw material is supplied in 40% by weight of one-dimensional material and 45% by weight of two-dimensional material,
In the auxiliary raw material input step (S40) and the step of adding only 8% by weight of clay (S41);
The additive injecting step (S50) is a method for producing pet sand, characterized in that the step of adding only 7% by weight of polyacrylamide (polyacryiamide) (S51).
KR1020120011731A 2012-02-06 2012-02-06 sand for cats and cats sand manufacturing method KR101356232B1 (en)