KR20090092167A - Method for manufacturing metal nano powders coated by carbon and metal nano powders coated by carbon using the same - Google Patents
Method for manufacturing metal nano powders coated by carbon and metal nano powders coated by carbon using the sameInfo
- Publication number
- KR20090092167A KR20090092167A KR1020080017515A KR20080017515A KR20090092167A KR 20090092167 A KR20090092167 A KR 20090092167A KR 1020080017515 A KR1020080017515 A KR 1020080017515A KR 20080017515 A KR20080017515 A KR 20080017515A KR 20090092167 A KR20090092167 A KR 20090092167A
- Authority
- KR
- South Korea
- Prior art keywords
- metal
- nano powder
- carbon
- gas
- metal nano
- Prior art date
Abstract
Description
본 발명은 탄소 코팅된 금속 나노 분말 제조 방법 및 그를 이용하여 제조된 탄소 코팅된 금속 나노 분말에 관한 것이다.The present invention relates to a carbon coated metal nano powder production method and a carbon coated metal nano powder prepared using the same.
현대 산업기술의 급속한 발달로 극도의 미세한 부품 및 이를 이용한 기기들의 요구에 부합하여 새로운 재료의 필요성이 대두되고 있다. 이에 따라, 최근에는 수십 내지 수백 나노미터 이하의 크기를 갖는 금속 나노 분말의 제조 및 그 응용에 관한 연구에 관심이 집중되고 있다.The rapid development of modern industrial technology has led to the need for new materials to meet the needs of extremely fine components and devices using them. Accordingly, in recent years, attention has been focused on the preparation of metal nanopowders having sizes of several tens to several hundred nanometers and their applications.
그런데, 상기 금속 나노 분말은 높은 표면에너지의 영향으로 활성이 대단히 강하고 대기중에서 급격히 산화되는 경향이 있으므로, 그 취급 안전성 및 보관 용이성이 떨어지는 문제점이 있다.However, since the metal nanopowder has a very strong activity under the influence of high surface energy and tends to be rapidly oxidized in the air, there is a problem in that its handling safety and storage ease are inferior.
이에 따라, 금속 나노 분말의 산화를 방지할 수 있는 방법이 요구되고 있다. 상기 금속 나노 분말의 산화를 방지하기 위한 방법에는 크게 두 가지가 있다. 첫째는, 금속 나노 분말 표면에 산화막을 형성시켜 금속 나노 분말이 그 이상 산화되는 것을 방지하는 방법이며, 둘째는, 금속 나노 분말 표면에 내산화성이 큰 헥산 등을 코팅하는 방법이다.Accordingly, there is a demand for a method capable of preventing oxidation of the metal nanopowder. There are two main methods for preventing oxidation of the metal nanopowder. First, a method of forming an oxide film on the surface of the metal nanopowder to prevent further oxidation of the metal nanopowder, and second, a method of coating hexane or the like having high oxidation resistance on the surface of the metal nanopowder.
그러나, 첫번째 방법의 경우, 금속 나노 분말 중에서 산화막이 차지하는 비율이 크고, 순수한 금속상의 성질을 이용하려 할 때 상기 산화막은 쓸모없는 층(dead layer)으로 작용한다. 즉, 금속 나노 분말 중에서 금속상 비율이 상대적으로 감소함과 동시에 그 효율이 떨어지는 문제점이 있다.However, in the first method, the oxide film occupies a large proportion of the metal nanopowders, and the oxide film serves as a dead layer when attempting to use pure metal properties. That is, there is a problem that the ratio of the metal phase in the metal nanopowder is relatively decreased and its efficiency is lowered.
그리고, 두번째 방법의 경우, 헥산의 강한 휘발성으로 인하여 코팅 이후에 헥산이 휘발될 가능성이 높으므로, 헥산이 코팅된 금속 나노 분말의 장기 보관을 위해 헥산의 휘발을 방지할 수 있는 부가적인 장치 내지는 후속 공정이 필요하다는 문제점이 있다.In the second method, since hexane is highly likely to be volatilized after coating due to the strong volatility of hexane, an additional device or subsequent device capable of preventing volatilization of hexane for long-term storage of hexane coated metal nanopowders. There is a problem that a process is required.
따라서, 본 발명이 해결하고자 하는 과제는 금속 나노 분말의 표면을 내산화성이 큰 탄소로 코팅함으로써 금속 나노 분말의 산화를 방지할 수 있는 탄소 코팅된 금속 나노 분말 제조 방법 및 그를 이용하여 제조된 탄소 코팅된 금속 나노 분말을 제공한다.Accordingly, the problem to be solved by the present invention is a method of producing a carbon-coated metal nanopowder and a carbon coating prepared using the same, which can prevent oxidation of the metal nanopowder by coating the surface of the metal nanopowder with carbon having high oxidation resistance Metal nanopowder.
또한, 본 발명이 해결하고자 하는 다른 과제는 금속 나노 분말의 산화를 방지하기 위해 금속 나노 분말의 표면을 내산화성이 큰 탄소로 코팅시, 부가적인 장치 내지는 후속 공정이 필요치 않은 탄소 코팅된 금속 나노 분말 제조 방법 및 그를 이용하여 제조된 탄소 코팅된 금속 나노 분말을 제공한다.In addition, another problem to be solved by the present invention is to prevent the oxidation of the metal nano-powder, when coating the surface of the metal nano-powder with a high oxidation resistance carbon, carbon coated metal nano powder that does not require additional devices or subsequent processes It provides a manufacturing method and a carbon coated metal nano powder prepared using the same.
본 발명이 해결하고자 하는 또 다른 과제들은 이상에서 언급한 과제들로 제한되지 않으며, 언급되지 않은 또 다른 과제들은 아래의 기재로부터 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 명확하게 이해될 수 있을 것이다.Further objects to be solved by the present invention are not limited to the above-mentioned objects, and other objects not mentioned will be clearly understood by those skilled in the art from the following description. Could be.
상기 해결하고자 하는 과제를 달성하기 위한 본 발명에 따른 탄소 코팅된 금속 나노 분말 제조 방법은 반응 챔버 내부로 불활성 가스 및 탄소 함유 가스를 포함하는 혼합 가스를 공급하는 단계; 상기 반응 챔버 내부로 금속 와이어를 공급하는 단계; 및 상기 공급된 금속 와이어를 전기폭발(Pulsed Wire Evaporation: PWE)시킴으로써, 표면이 탄소로 코팅된 금속 나노 분말을 형성하는 단계를 포함한다.Carbon-coated metal nanopowder manufacturing method according to the present invention for achieving the object to be solved comprises the steps of supplying a mixed gas containing an inert gas and a carbon containing gas into the reaction chamber; Supplying a metal wire into the reaction chamber; And forming metal nano-powder coated with carbon by surface-evaporating the supplied metal wire by Pulsed Wire Evaporation (PWE).
한편, 상기 해결하고자 하는 과제를 달성하기 위한 본 발명에 따른 탄소 코팅된 금속 나노 분말은 상기한 바에 의해 제조되고, 금속코어부; 및 상기 금속코어부의 표면에 1 내지 20nm의 두께를 갖도록 형성된 탄소층을 포함한다.On the other hand, the carbon-coated metal nanopowder according to the present invention for achieving the problem to be solved is prepared by the above, the metal core portion; And a carbon layer formed on the surface of the metal core part to have a thickness of 1 to 20 nm.
본 발명에 따르면, 반응 챔버 내부로 불활성 가스 및 탄소 함유 가스를 포함하는 혼합 가스를 공급하고, 반응 챔버 내부로 금속 와이어를 공급한 후, 그 금속 와이어를 전기폭발시킴으로써, 금속 나노 분말 표면을 내산화성이 큰 탄소로 코팅할 수 있다. 이러한 탄소 코팅은 금속 나노 분말의 형성과 동시에 이루어질 수 있으므로, 금속 나노 분말의 산화를 근본적으로 방지할 수 있다. 이를 통해, 금속 나노 분말의 취급 안정성 및 보관 용이성을 확보할 수 있다. 아울러, 금속 나노 분말의 산화를 방지하기 위한 별도의 장치 내지는 후속 공정의 제거가 가능하다.According to the present invention, a mixed gas containing an inert gas and a carbon-containing gas is supplied into the reaction chamber, a metal wire is supplied into the reaction chamber, and the metal wire is electroexploded, thereby oxidizing the metal nano powder surface. It can be coated with large carbon. This carbon coating can be made simultaneously with the formation of the metal nanopowder, thereby fundamentally preventing the oxidation of the metal nanopowder. Through this, it is possible to secure the handling stability and storage ease of the metal nano powder. In addition, it is possible to remove a separate device or subsequent process for preventing the oxidation of the metal nanopowder.
도 1은 실시예 1을 통해 제조된 구리 금속 나노 분말의 주사전자현미경 사진이다.1 is a scanning electron micrograph of the copper metal nano powder prepared in Example 1.
도 2는 실시예 1을 통해 제조된 구리 금속 나노 분말의 투과전자현미경 사진이다.Figure 2 is a transmission electron micrograph of the copper metal nano powder prepared in Example 1.
도 3은 실시예 1을 통해 제조된 구리 금속 나노 분말의 제조 직후 및 열처리후의 X선 회절도이다.3 is an X-ray diffraction diagram immediately after preparation and after heat treatment of the copper metal nanopowder prepared in Example 1. FIG.
도 4는 비교예 1을 통해 제조된 구리 금속 나노 분말의 주사전자현미경 사진이다.Figure 4 is a scanning electron micrograph of the copper metal nano powder prepared through Comparative Example 1.
도 5는 비교예 1을 통해 제조된 구리 금속 나노 분말의 제조 직후 및 열처리후의 X선 회절도이다.5 is an X-ray diffraction diagram immediately after the preparation and after the heat treatment of the copper metal nanopowder prepared in Comparative Example 1. FIG.
도 6은 실시예 2를 통해 제조된 구리-니켈 합금 나노 분말의 주사전자현미경 사진이다.FIG. 6 is a scanning electron micrograph of the copper-nickel alloy nanopowder prepared in Example 2. FIG.
도 7은 실시예 2를 통해 제조된 구리-니켈 합금 나노 분말의 투과전자현미경 사진이다.FIG. 7 is a transmission electron micrograph of the copper-nickel alloy nanopowder prepared in Example 2. FIG.
도 8은 비교예 2를 통해 제조된 구리-니켈 합금 나노 분말의 주사전자현미경 사진이다.8 is a scanning electron micrograph of the copper-nickel alloy nanopowder prepared in Comparative Example 2.
이하, 본 발명에 따른 탄소 코팅된 금속 나노 분말 제조 방법 및 그를 이용하여 제조된 탄소 코팅된 금속 나노 분말에 대하여 상세히 설명한다.Hereinafter, a carbon coated metal nanopowder manufacturing method and a carbon coated metal nanopowder prepared using the same according to the present invention will be described in detail.
본 발명에 따른 탄소 코팅된 금속 나노 분말은 금속 와이어를 사용한 전기폭발(Pulsed Wire Evaporation: PWE)법을 통해 제조될 수 있다. 상기 전기폭발법은 고밀도 전류가 금속 와이어를 통과할 때, 상기 금속 와이어가 미세한 입자나 증기 형태로 폭발하는 현상을 이용하는 방법으로서, 구체적인 입자 형성 원리는 다음과 같다. 먼저, 두 전극 사이에 위치한 금속 와이어에 강력한 충격 전류를 인가하면, 상기 금속 와이어는 저항 발열에 의해 용융된다. 그리고, 계속적인 온도 상승에 따라 금속 와이어 표면은 주위의 매개체에 의해 냉각되는 반면, 금속 와이어 내부는 액적(droplet)을 형성하여 액적 간에 방전이 일어나서 기화된다. 그 기화된 금속 가스는 핀치 효과와 관성의 법칙때문에 금속 와이어 내부에 구속되어 있다가 금속 와이어 내부 압력이 임계값 이상으로 도달되면 순간적으로 팽창하여 충격파를 형성하고 금속 미립자와 가스가 고속으로 분출되어 미세한 입자를 형성하게 된다.Carbon-coated metal nanopowder according to the present invention can be prepared through the Pulsed Wire Evaporation (PWE) method using a metal wire. The electroexplosion method uses a phenomenon in which the metal wire explodes in the form of fine particles or vapor when a high density current passes through the metal wire, and the specific particle formation principle is as follows. First, when a strong impact current is applied to a metal wire located between two electrodes, the metal wire is melted by resistance heating. As the temperature rises steadily, the surface of the metal wire is cooled by the surrounding medium, while the inside of the metal wire forms droplets to discharge and vaporize between the droplets. The vaporized metal gas is confined inside the metal wire due to the pinch effect and the law of inertia, and when the pressure inside the metal wire reaches a threshold or higher, it instantly expands to form a shock wave, and the metal particles and gas are ejected at high speed to produce fine particles. Will form particles.
상기 전기폭발법을 위해 본 발명에서는, 예를 들어, 반응 챔버, 펄스 발생부, 와이어 공급부, 가스 공급부 및 분말 포집부를 포함하는 전기폭발장치가 사용될 수 있으나, 본 발명은 상기 전기폭발장치의 구성에 의해 한정되지 않는다. 여기서, 상기 반응 챔버 내부에 전기폭발을 위한 두 전극이 구비되어 있어서 상기 반응 챔버 내부에서는 전기폭발이 일어날 수 있다. 또한, 상기 펄스 발생부는 상기 두 전극 중에서 적어도 일 전극에 소정의 펄스 전압을 공급할 수 있으며, 상기 와이어 공급부는 상기 반응 챔버 내부로 금속 와이어를 공급할 수 있다. 또한, 상기 가스 공급부는 상기 반응 챔버 내부로 소정 가스, 예를 들어, 불활성 가스 및 탄소 함유 가스를 포함하는 혼합 가스를 공급할 수 있다. 또한, 상기 분말 포집부는 제조된 금속 나노 분말을 포집할 수 있다.In the present invention for the electroexplosion method, for example, an electroexplosion apparatus including a reaction chamber, a pulse generator, a wire supply unit, a gas supply unit and a powder collecting unit may be used, but the present invention is directed to the configuration of the electroexplosion apparatus. It is not limited by. Here, two electrodes for electric explosion are provided in the reaction chamber, and thus, the electric explosion may occur in the reaction chamber. The pulse generator may supply a predetermined pulse voltage to at least one of the two electrodes, and the wire supply unit may supply a metal wire into the reaction chamber. In addition, the gas supply unit may supply a mixed gas including a predetermined gas, for example, an inert gas and a carbon-containing gas, into the reaction chamber. In addition, the powder collecting unit may collect the prepared metal nano powder.
본 발명에 따른 탄소 코팅된 금속 나노 분말은 반응 챔버 내부로 불활성 가스 및 탄소 함유 가스를 포함하는 혼합 가스를 공급하는 단계, 상기 반응 챔버 내부로 금속 와이어를 공급하는 단계 및 상기 공급된 금속 와이어를 전기폭발시킴으로써, 표면이 탄소로 코팅된 금속 나노 분말을 형성하는 단계를 거쳐 제조될 수 있으며, 이후 추가적으로 상기 금속 나노 분말을 포집할 수 있다. 여기서, 상기 혼합 가스 및 상기 금속 와이어의 공급 순서는 무관하다. 즉, 상기 혼합 가스 및 상기 금속 와이어를 동시에 공급하거나, 또는 상기 혼합 가스를 공급한 후에 상기 금속 와이어를 공급하거나, 또는 상기 금속 와이어를 공급한 후에 상기 혼합 가스를 공급할 수 있다.The carbon-coated metal nanopowder according to the present invention comprises the steps of supplying a mixed gas containing an inert gas and a carbon-containing gas into the reaction chamber, supplying a metal wire into the reaction chamber and the supplied metal wire By exploding, the surface may be prepared by the step of forming a metal nanopowder coated with carbon, and then the metal nanopowder may be additionally collected. Here, the supply order of the mixed gas and the metal wire is irrelevant. That is, the mixed gas and the metal wire may be simultaneously supplied, or the mixed gas may be supplied after the mixed gas is supplied, or the mixed gas may be supplied after the metal wire is supplied.
이하에서는, 본 발명에 따른 탄소 코팅된 금속 나노 분말 제조 방법을 각 단계별로 구체적으로 설명한다.Hereinafter, the carbon coated metal nano powder manufacturing method according to the present invention will be described in detail for each step.
먼저, 상기 혼합 가스 공급시 상기 불활성 가스 및 탄소 함유 가스는 공급전 미리 혼합된 상태, 또는 공급전 미리 혼합되지 않고 각각 독립적으로 유량 조절이 가능한 상태로 상기 반응 챔버 내부로 공급될 수 있다.First, when the mixed gas is supplied, the inert gas and the carbon-containing gas may be supplied into the reaction chamber in a pre-mixed state before supplying or in a state in which the flow rate can be adjusted independently without pre-mixing before supplying.
상기 불활성 가스는 전기폭발시 상기 반응 챔버 내부에 구비되는 두 전극에 인가되는 전기에너지에 의해 가스 이온이 될 수 있는데, 이러한 가스 이온은 금속 가스를 응축시키는 역할을 한다.The inert gas may be gas ions by electrical energy applied to two electrodes provided in the reaction chamber during the electroexplosion, and these gas ions serve to condense metal gas.
상기 불활성 가스로는 헬륨, 네온, 아르곤 및 질소 가스를 단독으로, 또는 2종 이상으로 혼합하여 사용할 수 있다. 예를 들어, 상기 불활성 가스로 아르곤 가스 단독 또는 질소 가스 단독을 사용할 수 있으나, 상기 아르곤 가스 및 질소 가스를 혼합하여 사용하여도 무방하다. 단원자인 상기 아르곤 가스는 이원자 분자인 상기 질소 가스보다 상대적으로 낮은 전기에너지에 의해 가스 이온이 될 수 있다. 이 때문에, 만약, 같은 전기에너지에 의해 가스 이온화가 발생하는 경우, 가스 이온의 농도는 아르곤 가스의 경우가 질소 가스보다 높다. 따라서, 아르곤 가스 분위기에서 보다 쉽게 금속 가스의 응축이 발생할 수 있으므로, 최종적으로 제조되는 금속 나노 분말의 입경을 작게 할 수 있다. 한편, 상기 질소 가스는 아르곤 가스보다 상대적으로 낮은 기압에서 높은 과열도(super heat)를 얻을 수 있다. 여기서, 상기 과열도가 높다는 것은 상기 두 전극에 인가된 전기에너지가 효과적으로 금속 와이어의 폭발에너지로 작용할 수 있다는 것을 의미한다.As said inert gas, helium, neon, argon, and nitrogen gas can be used individually or in mixture of 2 or more types. For example, argon gas alone or nitrogen gas alone may be used as the inert gas, but the argon gas and the nitrogen gas may be mixed and used. The argon gas, which is a monoatomic member, may be a gas ion by electric energy relatively lower than the nitrogen gas, which is a diatomic molecule. For this reason, if gas ionization occurs by the same electrical energy, the concentration of gas ions is higher than that of nitrogen gas in the case of argon gas. Therefore, since the condensation of the metal gas may occur more easily in the argon gas atmosphere, the particle diameter of the metal nanopowder finally produced can be reduced. On the other hand, the nitrogen gas can obtain a high super heat at a lower pressure than argon gas (super heat). Here, the high degree of superheat means that the electrical energy applied to the two electrodes can effectively act as the explosion energy of the metal wire.
상기 탄소 함유 가스는 전기폭발시 상기 두 전극에 의해 인가되는 전기에너지에 의해 단원자 상태로 분해될 수 있다. 그 중에서, 탄소 원자는 금속 증기가 냉각 및 응축하는 과정 중에 금속 증기와 반응하거나, 또는 금속 증기와 촉매 작용 등과 같은 상호 작용을 통해 금속 나노 분말의 표면을 코팅할 수 있다. 이를 통해 형성된 탄소층은 금속 증기가 더욱 응축하여 자라나거나 응집에 의해 입자가 성장하는 것을 차단할 수 있기 때문에, 불활성 가스만을 이용하여 제조한 금속 나노 분말에 비해 상대적으로 작은 크기의 금속 나노 분말을 제조할 수 있으며, 아울러 외부 열에너지에 의한 입자의 성장을 막아주는 역할을 할 수 있다.The carbon-containing gas may be decomposed into a monoatomic state by electrical energy applied by the two electrodes during the electrical explosion. Among them, the carbon atoms may react with the metal vapor during the cooling and condensation of the metal vapor, or may coat the surface of the metal nanopowder through interaction such as catalysis with the metal vapor. Since the carbon layer formed thereon may further prevent condensation and growth of the metal vapor, the particles may be prevented from growing, and thus, metal nanopowders having a relatively small size may be prepared compared to metal nanopowders prepared using only inert gas. In addition, it may also play a role in preventing the growth of particles by external thermal energy.
상기 탄소 함유 가스로는 특별히 한정되지 않지만, 예를 들어, 탄화수소 가스를 사용할 수 있다. 상기 탄화수소 가스로는, 예를 들어, 메탄, 에탄, 에틸렌, 프로판, 프로필렌, 부탄 또는 부틸렌 가스를 단독으로, 또는 2종 이상 혼합하여 사용할 수 있다. 그 중에서, 상대적으로 낮은 전기에너지에 의해 분해될 수 있는 메탄 가스를 사용할 수 있다.Although it does not specifically limit as said carbon containing gas, For example, hydrocarbon gas can be used. As said hydrocarbon gas, methane, ethane, ethylene, propane, propylene, butane or butylene gas can be used individually or in mixture of 2 or more types, for example. Among them, methane gas that can be decomposed by relatively low electrical energy can be used.
상기 혼합 가스 내 상기 탄소 함유 가스의 함량은 1 내지 80부피%일 수 있다. 상기 탄소 함유 가스 함량이 1부피% 미만이면, 가스 함량이 작아 탄소 코팅이 원하는 두께만큼 이루어지지 않을 수 있고, 80부피%를 초과하면, 상대적으로 낮은 함량의 불활성 가스로 인해 금속 증기의 응축이 원활히 이루어지지 않을 수 있다.The content of the carbon-containing gas in the mixed gas may be 1 to 80% by volume. When the carbon-containing gas content is less than 1% by volume, the gas content may be small so that the carbon coating may not be achieved by a desired thickness. When the carbon content is more than 80% by volume, the relatively low content of the inert gas may facilitate the condensation of the metal vapor. It may not be done.
상기 탄소 함유 가스의 최소 함량에 대한 계산을 메탄 가스를 예로 들어 설명한다. 상기 메탄 가스의 함량은 하기 수학식 1 내지 6을 통해 계산될 수 있다. 여기서, 하기 수학식 1 내지 6에 의해 결정된 메탄 가스의 함량은 목적하는 탄소층의 두께를 얻기 위한 최소한의 양을 나타내므로, 하기 수학식에 의해 결정된 메탄 가스의 함량보다는 높은 함량에서 제조함이 바람직하다.The calculation for the minimum content of the carbon containing gas will be described taking methane gas as an example. The content of the methane gas may be calculated through the following Equations 1 to 6. Here, since the content of methane gas determined by the following Equations 1 to 6 represents the minimum amount for obtaining the desired carbon layer thickness, it is preferable to prepare at a higher content than the content of methane gas determined by the following equation. Do.
여기서, MC(g)는 전기폭발시 생성되는 금속 나노 분말 1g을 코팅하기 위한 탄소의 질량을 의미하며, S(104*cm2/g)는 탄소 코팅이 되기 전 금속 나노 분말 1g에 대한 비표면적을 의미하며, h(10-7*cm)는 목적하는 탄소층의 두께를 의미하며, γC(g/cm3)는 탄소의 밀도를 의미한다.Here, M C (g) refers to the mass of carbon for coating 1 g of the metal nanopowder generated during electroexplosion, and S (10 4 * cm 2 / g) refers to 1 g of the metal nanopowder before carbon coating. The specific surface area, h (10 -7 * cm) refers to the thickness of the target carbon layer, γ C (g / cm 3 ) means the density of the carbon.
여기서, M1(g)는 1회 전기폭발시 생성되는 금속 나노 분말의 질량을 의미하며, L(cm)은 전기폭발에 기여하는 금속 와이어의 길이를 의미하며, Φ(cm)는 금속 와이어의 직경을 의미하며, γM(g/cm3)은 금속 와이어의 밀도를 의미하며, k는 금속 와이어를 전기폭발하여 나노 분말화할 때의 수율을 의미한다.Here, M 1 (g) refers to the mass of the metal nanopowder generated during one electrical explosion, L (cm) refers to the length of the metal wire to contribute to the electrical explosion, Φ (cm) of the metal wire Γ M (g / cm 3 ) refers to the density of the metal wire, and k refers to the yield when the metal wire is electroexploded and nanopowdered.
여기서, MN(g)은 N회 전기폭발시 생성되는 금속 나노 분말의 질량을 의미하며, N은 전기폭발 회수를 의미하며, 나머지는 상기 수학식 2와 동일하다.Here, M N (g) refers to the mass of the metal nanopowder generated during N times of electroexplosion, N means the number of electroexplosion, and the rest is the same as Equation (2).
여기서, ∑MC(g)는 N회 전기폭발시 생성되는 금속 나노 분말 MN을 코팅하기 위한 탄소의 총질량을 의미하며, 나머지는 상기 수학식 1 및 2와 동일하다.Here,? M C (g) means the total mass of carbon for coating the metal nanopowder M N generated during N electroexplosion, and the rest is the same as Equations 1 and 2 above.
여기서, VCH4(L)은 N회 전기폭발시 생성되는 금속 나노 분말을 코팅하기 위한 메탄 가스의 부피를 의미하며, ∑MC(g)는 상기 수학식 4와 동일하다.Here, V CH4 (L) refers to the volume of methane gas for coating the metal nano-powder generated during N-explosion, ∑M C (g) is the same as Equation 4.
여기서, CCH4(부피%)는 압력 P에서 N회 전기폭발시에 생성되는 금속 나노 분말을 코팅하기 위한 메탄 가스의 함량을 의미하며, Vtotal(L)은 압력 P일 때 충진되는 혼합 가스의 부피를 의미하며, P(bar)는 반응 챔버 내에 충진되는 혼합 가스의 압력을 의미하며, Vsystem(L)은 반응 챔버와 금속 나노 분말이 내부에서 순환되는 연결관 전체의 부피를 의미하며, VCH4는 상기 수학식 5와 동일하다.Here, C CH4 (% by volume) refers to the content of methane gas for coating the metal nanopowder generated during N-explosion at pressure P, and V total (L) is the content of the mixed gas filled at pressure P. P (bar) refers to the pressure of the mixed gas filled in the reaction chamber, V system (L) refers to the volume of the entire connecting tube through which the reaction chamber and the metal nanopowder circulated therein, V CH4 is the same as Equation 5 above.
상기 혼합 가스는 0.5 내지 5bar의 압력으로 공급될 수 있다. 상기 혼합 가스의 압력이 0.5bar 미만이면, 목적하는 과열도를 얻기 힘들고, 5bar를 초과하면, 불활성 가스 및 탄소 함유 가스가 필요 이상으로 공급되어 원료비가 증가하는 문제점이 있다.The mixed gas may be supplied at a pressure of 0.5 to 5 bar. If the pressure of the mixed gas is less than 0.5bar, it is difficult to obtain the desired degree of superheat, if it exceeds 5bar, the inert gas and carbon-containing gas is supplied more than necessary to increase the raw material cost.
상기 혼합 가스를 공급한 후에 상기 반응 챔버 내부로 금속 와이어를 공급할 수 있는데, 상기 금속 와이어로는, 특별히 한정되지는 않지만, 예를 들어, 구리, 니켈, 알루미늄, 철, 금 또는 은 금속 단독, 이들의 합금 또는 이들의 혼합물을 사용할 수 있다. 상기 금속 와이어의 직경은, 예를 들어, 0.1 내지 1mm일 수 있으며, 그 길이는 특별히 한정되지 않는다.After supplying the mixed gas, a metal wire may be supplied into the reaction chamber. The metal wire is not particularly limited, but for example, copper, nickel, aluminum, iron, gold, or silver metal alone, these Alloys or mixtures thereof may be used. The diameter of the metal wire may be, for example, 0.1 to 1 mm, the length is not particularly limited.
다음으로, 상기 반응 챔버 내부에서 금속 와이어를 전기폭발시킨다. 상기 전기 폭발은 상기 두 전극을 이용하여 상기 금속 와이어에, 예를 들어, N회(N은 자연수)의 펄스 전압을 인가함으로써 발생될 수 있다. 여기서, 상기 N은 특별히 한정되지 않는다. 상기 펄스 전압은, 예를 들어, 0.5 내지 10초의 주기로 인가될 수 있으며, 상기 범위 내에서 상기 펄스 전압의 주기는 일정하거나, 또는 가변될 수 있다. 또한, 상기 펄스 전압은, 예를 들어, 10 내지 40kV일 수 있으며, 상기 범위 내에서 일정하거나, 또는 가변될 수 있다. 상기와 같은 금속 와이어의 전기폭발을 통해 표면이 탄소로 코팅된 금속 나노 분말을 형성할 수 있다.Next, the metal wire is electroexploded in the reaction chamber. The electrical explosion may be generated by applying, for example, N pulses (N is a natural number) to the metal wire using the two electrodes. Here, N is not particularly limited. The pulse voltage may be applied at, for example, a period of 0.5 to 10 seconds, and the period of the pulse voltage may be constant or variable within the range. In addition, the pulse voltage may be, for example, 10 to 40 kV, and may be constant or variable within the above range. Through the electrical explosion of the metal wire as described above it is possible to form a metal nano-powder coated with a surface of carbon.
상술한 바에 따라 제조된 본 발명의 탄소 코팅된 금속 나노 분말은 금속으로 이루어진 금속코어부; 및 상기 금속코어부의 표면에 1 내지 20nm의 두께를 갖도록 형성된 탄소층을 포함한다. 여기서, 상기 금속코어부는 구리, 니켈, 알루미늄, 철, 금 또는 은 금속 단독, 이들의 합금 또는 이들의 혼합물을 포함할 수 있다. 또한, 상기 탄소 코팅된 금속 나노 분말의 입경은 특별히 한정되지 않으나, 대략 100nm 또는 그 이하의 입자 크기일 수 있으며, 상기 100nm 보다 커도 무방하다. 예를 들어, 상기 금속 나노 분말은 입경은 5 내지 150nm일 수 있다.Carbon coated metal nano powder of the present invention prepared according to the above is made of a metal core portion made of a metal; And a carbon layer formed on the surface of the metal core part to have a thickness of 1 to 20 nm. Here, the metal core portion may include copper, nickel, aluminum, iron, gold or silver metal alone, alloys thereof, or mixtures thereof. In addition, the particle diameter of the carbon-coated metal nanopowder is not particularly limited, but may be about 100 nm or less in particle size, and may be larger than 100 nm. For example, the metal nano powder may have a particle diameter of 5 to 150 nm.
상술한 바와 같이, 본 발명에 따르면, 반응 챔버 내부로 불활성 가스 및 탄소 함유 가스를 포함하는 혼합 가스를 공급하고, 반응 챔버 내부로 금속 와이어를 공급한 후, 금속 와이어를 전기폭발시킴으로써, 표면이 내산화성이 큰 탄소로 코팅된 금속 나노 분말을 제조할 수 있다. 이러한 탄소 코팅은 동일한 반응 챔버 내에서 금속 나노 분말의 형성과 동시에 이루어질 수 있으므로, 금속 나노 분말의 산화를 근본적으로 방지할 수 있다. 이를 통해, 금속 나노 분말의 취급 안정성 및 보관 용이성을 확보할 수 있다. 아울러, 금속 나노 분말의 산화를 방지하기 위한 별도의 장치 내지는 후속 공정의 제거가 가능하다.As described above, according to the present invention, after supplying a mixed gas containing an inert gas and a carbon-containing gas into the reaction chamber, supplying a metal wire into the reaction chamber, and then electroexploding the metal wire, the surface Metal nano powder coated with oxidative carbon can be prepared. This carbon coating can be made simultaneously with the formation of the metal nanopowder in the same reaction chamber, thereby essentially preventing the oxidation of the metal nanopowder. Through this, it is possible to secure the handling stability and storage ease of the metal nano powder. In addition, it is possible to remove a separate device or subsequent process for preventing the oxidation of the metal nanopowder.
이하, 본 발명에 따른 탄소 코팅된 금속 나노 분말의 제조를 실시예를 통하여 구체화하지만, 이는 본 발명의 이해를 돕기 위하여 제시되는 것일 뿐 본 발명이 하기 실시예에 한정되는 것은 아니다.Hereinafter, the preparation of the carbon-coated metal nanopowder according to the present invention will be embodied through examples, but this is only presented to aid the understanding of the present invention and the present invention is not limited to the following examples.
[실시예]EXAMPLE
실시예 1Example 1
구리 와이어(직경 0.4mm, 길이 91mm)를 1.5bar의 아르곤/메탄 가스(20부피%)로 이루어진 혼합 가스 분위기에서 2초당 1회의 주기로 25kV의 펄스 전압을 인가하여 전기폭발시킴으로써, 탄소 코팅된 구리 금속 나노 분말을 제조하였으며, 그 주사전자현미경 사진을 도 1에, 그 투과전자현미경 사진을 도 2에 나타내었다. 이후, 상기 구리 금속 나노 분말을 공기중에서 10일 가량 방치한 후, 아르곤 가스 분위기하의 600℃에서 1시간동안 열처리하였으며, 상기 구리 금속 나노 분말 제조 직후 및 열처리후의 X선 회절도를 측정하여 도 3에 나타내었다.Copper-coated copper metal by electroexploding copper wire (0.4 mm diameter, 91 mm length) by applying a pulse voltage of 25 kV at a cycle of once every 2 seconds in a mixed gas atmosphere consisting of 1.5 bar of argon / methane gas (20% by volume). Nano powder was prepared, the scanning electron micrograph is shown in Figure 1, the transmission electron microscope picture is shown in Figure 2. Thereafter, the copper metal nano powder was left in the air for about 10 days, and then heat-treated at 600 ° C. under an argon gas atmosphere for 1 hour. The X-ray diffractograms of the copper metal nano powders immediately after and after the heat treatment were measured, and FIG. Indicated.
실시예 2Example 2
구리-니켈(10%) 합금 와이어(직경 0.4mm, 길이 87mm)를 1.5bar의 아르곤/메탄 가스(20부피%)로 이루어진 혼합 가스 분위기에서 2초당 1회의 주기로 25kV의 펄스 전압을 인가하여 전기폭발시킴으로써, 탄소 코팅된 구리-니켈(10%) 합금 나노 분말을 제조하였으며, 그 주사전자현미경 사진을 도 6에, 그 투과전자현미경 사진을 도 7에 나타내었다.Electroexplosion by applying a pulse voltage of 25 kV at a rate of once every 2 seconds in a mixed-gas atmosphere consisting of 1.5 bar of argon / methane gas (20% by volume) of copper-nickel (10%) alloy wire (0.4 mm in diameter and 87 mm in length). By doing so, a carbon-coated copper-nickel (10%) alloy nanopowder was prepared, and the scanning electron micrograph is shown in FIG. 6, and the transmission electron micrograph is shown in FIG. 7.
비교예 1Comparative Example 1
아르곤 가스 단독 분위기에서 전기폭발시킨 것을 제외하고는, 실시예 1과 동일한 과정을 통해 구리 금속 나노 분말을 제조하였으며, 그 주사전자현미경 사진을 도 4에 나타내었다. 이후, 실시예 1과 동일한 과정을 통해 구리 금속 나노 분말을 열처리하였으며, 상기 구리 금속 나노 분말 제조 직후 및 열처리후의 X선 회절도를 측정하여 도 5에 나타내었다.A copper metal nanopowder was prepared in the same manner as in Example 1, except that the particles were electroexploded in an argon gas atmosphere, and a scanning electron micrograph is shown in FIG. 4. Thereafter, the copper metal nano powder was heat-treated through the same process as in Example 1, and the X-ray diffractograms immediately after the copper metal nano powder preparation and after the heat treatment were measured, and are shown in FIG. 5.
비교예 2Comparative Example 2
아르곤 가스 단독 분위기에서 전기폭발시킨 것을 제외하고는 실시예 2와 동일한 과정을 통해 구리-니켈 합금 나노 분말을 제조하였으며, 그 주사전자현미경 사진을 도 8에 나타내었다.A copper-nickel alloy nanopowder was prepared in the same manner as in Example 2 except for the electroexplosion in an argon gas atmosphere, and a scanning electron micrograph is shown in FIG. 8.
상기 실시예 1을 통해 제조된 구리 금속 나노 분말(도 1 참조)은 그 입자 크기가 비교예 1을 통해 제조된 구리 금속 나노 분말(도 4 참조)에 비해 상당히 감소되었음을 알 수 있었다. 아울러, 실시예 1을 통해 제조된 구리 금속 나노 분말은, 도 2에 도시된 바와 같이, 구리 금속 나노 분말 표면에 탄소층이 잘 형성되어 있음을 확인할 수 있었다.Copper metal nano powder prepared in Example 1 (see FIG. 1) was found to be significantly reduced in particle size compared to copper metal nano powder prepared in Comparative Example 1 (see FIG. 4). In addition, the copper metal nano powder prepared through Example 1, as shown in Figure 2, it was confirmed that the carbon layer is well formed on the surface of the copper metal nano powder.
또한, 상기 실시예 1을 통해 제조된 구리 금속 나노 분말은, 도 3에 도시된 바와 같이, 그 제조 직후(As-pre) 뿐만 아니라 열처리(600℃) 후에도 전혀 산화물이 생성되지 않은, 즉, 순수한 단일상으로 존재함을 확인할 수 있었으며, 회절 피크의 선폭도 거의 변화하지 않았음을 알 수 있었다.In addition, as shown in FIG. 3, the copper metal nano powder prepared through Example 1 has no oxides formed immediately after its preparation (As-pre) as well as after heat treatment (600 ° C.), that is, pure It could be confirmed that it exists as a single phase, and that the line width of the diffraction peak was also hardly changed.
반면, 상기 비교예 1을 통해 제조된 구리 금속 나노 분말은, 도 5에 도시된 바와 같이, 그 제조 직후(As-pre)에는 산화물이 생성되지 않았지만, 열처리(600℃) 후에는 분말의 표면 산화층의 결정화로 인해 산화구리 상이 함께 존재하고 있었음을 확인할 수 있었다. 또한, 2θ 값이 대략 43˚인 주피크의 선폭이 크게 감소하였으며, 이를 통해 열처리후 분말들의 입자 크기가 증가되었음을 알 수 있었다.On the other hand, in the copper metal nano powder prepared through Comparative Example 1, as shown in Figure 5, the oxide is not produced immediately after the production (As-pre), but after the heat treatment (600 ℃) surface oxide layer of the powder It was confirmed that the copper oxide phase coexisted due to the crystallization of. In addition, the line width of the main peak having a 2θ value of approximately 43 ° was greatly reduced, and thus the particle size of the powders was increased after the heat treatment.
한편, 상기 실시예 2를 통해 제조된 구리-니켈 합금 나노 분말(도 6 참조)은 그 입자 크기가 비교예 2를 통해 제조된 구리-니켈 합금 나노 분말(도 8 참조)에 비해 상당히 감소되었음을 알 수 있었다. 아울러, 실시예 2를 통해 제조된 구리-니켈 합금 나노 분말은, 도 7에 도시된 바와 같이, 분말 표면에 탄소층이 잘 형성되어 있음을 확인할 수 있었다.Meanwhile, it can be seen that the copper-nickel alloy nanopowder prepared in Example 2 (see FIG. 6) was significantly reduced in size compared to the copper-nickel alloy nanopowder prepared in Comparative Example 2 (see FIG. 8). Could. In addition, the copper-nickel alloy nano powder prepared in Example 2, as shown in Figure 7, it was confirmed that the carbon layer is well formed on the surface of the powder.
이상 첨부된 도면들을 참조하여 본 발명의 실시예들을 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다.Although the embodiments of the present invention have been described above with reference to the accompanying drawings, those skilled in the art to which the present invention pertains can realize that the present invention can be implemented in other specific forms without changing the technical spirit or essential features. I can understand that.
따라서, 이상에서 기술한 실시예들은 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이므로, 모든 면에서 예시적인 것이며 한정적이 아닌 것으로 이해해야만 하며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다.Therefore, since the embodiments described above are provided to completely inform the scope of the invention to those skilled in the art, it should be understood that they are exemplary in all respects and not limited. The invention is only defined by the scope of the claims.
Claims (15)