KR20040051494A - 원적외선이 방사되는 유리의 제조방법 - Google Patents
원적외선이 방사되는 유리의 제조방법 Download PDFInfo
- Publication number
- KR20040051494A KR20040051494A KR1020030077108A KR20030077108A KR20040051494A KR 20040051494 A KR20040051494 A KR 20040051494A KR 1020030077108 A KR1020030077108 A KR 1020030077108A KR 20030077108 A KR20030077108 A KR 20030077108A KR 20040051494 A KR20040051494 A KR 20040051494A
- Authority
- KR
- South Korea
- Prior art keywords
- glass
- photocatalyst
- less
- sericite
- borax
- Prior art date
Abstract
본 발명은 항균력이 우수하고 원적외선을 방사하는 유리의 제조방법에 관한 것으로, 88-96중량%의 세리사이트에, 각각 1-3 중량%의 소석회, 수산화나트륨, 붕사, 광촉매를 혼합하고 1300℃ 이상으로 24시간 이상 가열하여 용해시킨 다음, 성형하는 것을 특징으로 한다.
본 발명의 방법에 의해 제조된 유리는 원적외선 방사성이 매우 뛰어나 인체의 뼈 이식용 바이오그라스, 식 생활용 그릇 등으로 매우 폭넓게 이용할 수 있다.
Description
본 발명은 항균력이 우수하고 원적외선을 방사하는 유리의 제조방법에 관한 것이다.
각종의 모양과 형태의 생활유리, 판유리 및 각종의 유리 제품들은 일반적으로 출발물질을 규사(SiO2) 및 납석 등으로 하여 제조되고 있으며, 유리의 조색제로서 여러 금속분말을 이용하여 사용하고 있다.
이들이 갖고 있는 성질은 투명성에는 매우 뛰어나서 매우 오래전부터 현재에 이르기까지 커다란 변화없이 사용되어 지고있는 물질이다.
그러나 특별한 기능, 즉 원적외선 방사, 항균력 등의 기능을 가진 유리에 대한 이렇다 할 만한 개발이 되지 않고 있으며 이에 대한 진척은 한계에 머무르고 있었다.
우리 인간이 사용하는 유리는 아주 다양하며 또한 이를 이용하는 분야는 매우 넓지만, 특별한 기능을 제외하고는 여러의 기능중에서 특히 우리 생활용으로 사용하고 있는 용기들 중에서 인체에 유익성을 주는 원적외선과 항균력이라 할 수 있겠다.
따라서, 본 발명의 목적은 천연 광물질에서 갖고 있는 특성들을 이용하여 상온에서도 원적외선이 방사량이 많으면서 항균력을 갖는 유리의 제조방법을 제공하는 것이다.
상기 본 발명의 목적은 88-96중량%의 세리사이트에, 각각 1-3 중량%의 소석회, 수산화나트륨, 붕사, 광촉매를 혼합하고 1300℃ 이상으로 24시간 이상 가열하여 용해시킨 다음, 성형하는 것을 특징으로 하는 유리의 제조방법에 의해 달성된다.
광촉매는 이산화티탄 광촉매를 사용하며, 세리사이트, 소석회, 붕사의 입자크기는 30mm 이하, 수산화나트륨의 입자크기는 43㎛ 이하, 광촉매의 입자크기는 0.5㎛ 이하인 것이 바람직하다.
본 발명을 실시예에 의거 더욱 상세히 설명하면 다음과 같다.
실시예 1 ;
천연 무기 광물질인 세리사이트(Sericite)를 윤활성과 진주의 광택의 색상을 갖고 있는 물질만 엄선하는 작업의 공정을 거친 것을 크락샤에 넣은후 3메쉬(30mm)입자크기로 잘게 분쇄하였다.
입자크기 3메쉬(Mesh) 순도 99％이상의 소석회를 엄선하여 3중량％을 혼합기에 넣고, 입자크기 325메쉬(43㎛) 순도 99.9％이상인 수산화 나트륨(NaOH)을 엄선한후 중량3％를 혼합기에 넣고, 입자크기 3메쉬의 붕사를 순도 99％ 이상의 붕사를 엄선하여 2중량％ 혼합기에 넣었다.
무기질항균제인 광촉매제를 입자크기 0.5㎛이하, 순도 99.9％이상의 것으로 고온에서도 항균력이 떨어지지 않는 소재를 엄선하여 2중량％ 혼합기에 넣은 다음, 90중량％의 세리사이트(Sericite)를 혼입하여 재료들을 10분간 100RPM속도로 교반시켰다.
위의 공정에서 얻어진 혼합 파우더를 1.300℃의 용해로에 넣어 24시간동안 충분하게 용해를 시키고 상기에서 얻어진 용융된 유리물을 그라스 형틀에 주입시켜 이를 다시 600℃온도에서 30분간 서냉을 시키어 유리 성형물을 얻었다.
위의 상기 공정에서 얻어진 유리의 원적외선 방사도는 40℃에서 측정한 결과 91％이상의 방사도를 얻을 수 있었으며 항균력은 곰팡이균 테스트에서는 전혀자라지 못하였고, 황색포도상구균 ; 99.8%, 폐렴쌍구균 ; 98.9%, 대장균 ; 99.9%의 사멸효과를 나타내 98％이상의 항균력 결과를 얻었다.
본 발명의 제조방법에 의해 제조된 유리는 우리의 주변에서 흔하게 구할 수 있는 소재를 사용하고 나노입자를 이용하여 상온에서도 우수한 원적외선 방사량을얻을 수 있으며, 항균효과가 우수하다.
이들은 흔하게 사용하고 있는 유기질 고분자에 컴파운딩을 하여 주거나 혹은 무기질 모재(Matrix)에 합첨제로서도 널리 사용할 수 있다.
특히 우리의 생활 주변에서 흔하게 보이는 유리 제품들에 기능성을 부여하여 다용도로 적용이 가능하다.
본 발명에 의해 제조된 유리는 내열성 유리 그릇, 유리물잔, 생체물의 뼈 이식용 바이오그라스, 식 생활용 그릇 등 매우 폭넓게 이용할 수 있다.
Claims (3)
- 88-96중량%의 세리사이트에, 각각 1-3 중량%의 소석회, 수산화나트륨, 붕사, 광촉매를 혼합하고 1300℃ 이상으로 24시간 이상 가열하여 용해시킨 다음, 성형하는 것을 특징으로 하는 원적외선 방사 유리의 제조방법.
- 제 1 항에 있어서, 세리사이트, 소석회, 붕사의 입자크기는 30mm 이하, 수산화나트륨의 입자크기는 43㎛ 이하, 광촉매의 입자크기는 0.5㎛ 이하인 것을 특징으로 하는 원적외선 방사 유리의 제조방법.
- 제 1 항에 있어서, 상기 광촉매는 광촉매는 이산화티탄인 것을 특징으로 하는 원적외선 방사 유리의 제조방법.