KR20030025832A - Reflection sheet and backlight unit using the same - Google Patents

Reflection sheet and backlight unit using the same Download PDF

Info

Publication number
KR20030025832A
KR20030025832A KR1020020056850A KR20020056850A KR20030025832A KR 20030025832 A KR20030025832 A KR 20030025832A KR 1020020056850 A KR1020020056850 A KR 1020020056850A KR 20020056850 A KR20020056850 A KR 20020056850A KR 20030025832 A KR20030025832 A KR 20030025832A
Authority
KR
South Korea
Prior art keywords
ultraviolet
sheet
layer
absorbing layer
ultraviolet absorber
Prior art date
Application number
KR1020020056850A
Other languages
Korean (ko)
Other versions
KR100523204B1 (en
Inventor
나카노쇼지
Original Assignee
케이와 인코포레이티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 케이와 인코포레이티드 filed Critical 케이와 인코포레이티드
Publication of KR20030025832A publication Critical patent/KR20030025832A/en
Application granted granted Critical
Publication of KR100523204B1 publication Critical patent/KR100523204B1/en

Abstract

PURPOSE: To provide a reflecting sheet capable of preventing secular deterioration such as yellowing and a back light unit capable of increasing a brightness by using the reflecting sheet and capable of preventing the secular deterioration of quality. CONSTITUTION: This reflecting sheet for back light unit capable of reducing the diffusion of light beam comprises a white synthetic resin base material sheet layer 2 and an ultraviolet absorbing layer 3 stacked on the front surface of the base material sheet layer 2. The ultraviolet absorbing layer 3 comprises a base material polymer 4 containing ultraviolet absorbing agent or a base material polymer 4 having ultraviolet absorbing groups connected to molecular chains. The ultraviolet absorbing layer 3 may be formed of a base material polymer 4 containing ultraviolet stabilizing agent or a base material polymer 4 having ultraviolet stabilizing groups in the molecular chains.

Description

반사시트 및 이것을 이용한 백라이트 유닛{REFLECTION SHEET AND BACKLIGHT UNIT USING THE SAME}Reflective sheet and backlight unit using the same {REFLECTION SHEET AND BACKLIGHT UNIT USING THE SAME}

본 발명은, 광선의 방산을 저감하는 백라이트 유닛용의 반사시트, 및 이 반사시트를 이용한 백라이트 유닛에 관한 것이다.The present invention relates to a reflective sheet for a backlight unit which reduces light emission and a backlight unit using the reflective sheet.

액정표시장치는, 액정층을 배면에서 비추어 발광시키는 백라이트 방식이 보급되어, 액정층의 하면측에 에지라이트형, 직하형 등의 백라이트 유닛이 장비되어 있다. 이러한 에지라이트형의 백라이트 유닛(4O)은, 일반적으로는 도 5에 도시한 바와 같이, 광원으로서의 봉상의 램프(41)와 이 램프(41)에 단부가 따르도록 배치되는 사각형 판상의 도광판(43)과, 이 도광판(43)의 표면측에 적층된 복수매의 광학시트(42)와, 도광판(43)의 이면측에 적층된 반사시트(46)를 장비하고 있다. 이 광학시트(42)는, 각각, 굴절, 확산 등의 특정의 광학적 성질을 가지는 것이고, 구체적으로는, 도광판(43)의 표면측에 배열설치되는 광확산시트(44), 광확산시트(44)의 표면측에 배열설치되는 프리즘시트(45) 등이 해당된다.BACKGROUND ART In the liquid crystal display device, a backlight system that emits light by illuminating the liquid crystal layer from the back is widespread, and a backlight unit such as an edge light type or a direct type is provided on the lower surface side of the liquid crystal layer. As shown in FIG. 5, such an edge light type backlight unit 40 is a rod-shaped lamp 41 as a light source and a rectangular plate-shaped light guide plate 43 disposed so that an end portion thereof follows the lamp 41. ), A plurality of optical sheets 42 stacked on the front side of the light guide plate 43, and a reflective sheet 46 stacked on the back side of the light guide plate 43 are provided. Each of the optical sheets 42 has specific optical properties such as refraction and diffusion, and specifically, the light diffusion sheet 44 and the light diffusion sheet 44 arranged on the surface side of the light guide plate 43. The prism sheet 45 etc. which are arrange | positioned at the surface side of () are corresponded.

이 백라이트 유닛(4O)의 기능을 설명하면, 우선, 램프(41)로부터 도광판(43)에 입사한 광선은, 도광판(43) 이면의 반사도트(도시생략) 및 각 측면에서 반사되어, 도광판(43) 표면으로부터 출사된다. 도광판(43)으로부터 출사된 광선은 광 확산시트(44)에 입사하고, 확산되어, 광 확산시트(44) 표면으로부터 출사된다. 그 후, 광 확산시트(44)로부터 출사된 광선은, 프리즘시트(45)에 입사하고, 프리즘시트(45)의 표면에 형성된 프리즘부(45a)에 의해서, 약 법선방향으로 피크를 나타내는 분포의 광선으로서 출사된다. 이와 같이, 램프(41)로부터 출사된 광선이, 광 확산시트(44)에 의해서 확산되고, 또 프리즘시트(45)에 의해서 약 법선방향으로 피크를 나타내도록 굴절되고, 다시 상방의 도시하지않은 액정층 전면을 조명하는 것이다.Referring to the function of the backlight unit 40, first, light rays incident on the light guide plate 43 from the lamp 41 are reflected from the reflection dots (not shown) and the respective side surfaces of the light guide plate 43, and the light guide plate ( 43) Emitted from the surface. Light rays emitted from the light guide plate 43 enter the light diffusion sheet 44, are diffused, and are emitted from the light diffusion sheet 44 surface. Thereafter, the light rays emitted from the light diffusing sheet 44 enter the prism sheet 45, and the prism portions 45a formed on the surface of the prism sheet 45 exhibit peaks in the normal direction. It is emitted as a light beam. In this way, the light rays emitted from the lamp 41 are diffused by the light diffusion sheet 44 and refracted by the prism sheet 45 to show a peak in the approximately normal direction, and again the liquid crystal (not shown) To illuminate the front of the floor.

한편, 액정화면이 번쩍이지않을 정도로 도광판(43) 이면에서 방산되는 광선을 표면측에 반사시켜서 휘도의 향상을 도모하는 것(반사성), 백라이트 유닛(4O) 의 이면측에 배열설치되는 장치, 프레임 등이 확인되는 것을 방지하는 것(은폐성)을 목적으로 하여, 도광판(43)의 이면측에는 반사시트(46)가 배열설치되어 있다.On the other hand, to improve the brightness by reflecting light rays emitted from the rear surface of the light guide plate 43 to the surface side such that the liquid crystal screen does not flash (reflective), the device arranged on the rear side of the backlight unit 40, frame The reflective sheet 46 is arranged on the rear surface side of the light guide plate 43 for the purpose of preventing the back from being confirmed (hidden).

이러한 반사시트(46)로서는, 종래, (a) 합성 수지제의 시트 중에 산화티탄 등의 백색안료가 분산된 것, (b) 합성 수지제의 시트 중에 빛을 산란시키기 위한 보이드(기포)가 분산된 것, (c) 시트표면이 매트상으로 형성된 것 등이 사용되고 있다.As such a reflective sheet 46, conventionally, (a) a white pigment such as titanium oxide is dispersed in a sheet made of synthetic resin, and (b) a void (bubble) for scattering light is dispersed in a sheet made of synthetic resin. And (c) a sheet surface formed into a mat shape is used.

상기 종래의 반사시트(46)를 이용한 백라이트 유닛(4O)을 사용하면, 경시적으로 반사시트(46)에 황변 등이 생기고, 이것에 수반하여 백라이트 화면이 황색을 띠고, 휘도가 저하되는 등의 품질의 저하를 초래하고 있다.When the backlight unit 40 using the conventional reflecting sheet 46 is used, yellowing or the like occurs in the reflecting sheet 46 with time, and thus the backlight screen becomes yellow and luminance decreases. It causes the deterioration of quality.

본 발명은 이들의 문제를 감안하여 이루어진 것으로, 황변 등의 경시적인 열화를 일으키지 않는 반사시트, 및, 이러한 반사시트를 이용하여 휘도의 향상 및 경시적인 품질 저하의 방지를 도모할 수 있는 백라이트 유닛의 제공을 목적으로 하는 것이다.SUMMARY OF THE INVENTION The present invention has been made in view of these problems, and includes a reflection sheet which does not cause deterioration over time such as yellowing, and a backlight unit capable of improving luminance and preventing deterioration of quality over time using such a reflection sheet. It is for the purpose of providing.

도 1은 본 발명의 일실시형태에 관한 반사시트를 나타내는 모식적 단면도이다.BRIEF DESCRIPTION OF THE DRAWINGS It is typical sectional drawing which shows the reflecting sheet which concerns on one Embodiment of this invention.

도 2는 도 1의 반사시트와는 다른 형태의 반사시트를 나타내는 모식적 단면도이다.FIG. 2 is a schematic cross-sectional view showing a reflection sheet different from that of FIG. 1.

도 3은 도 1 및 도 2의 반사시트와는 다른 형태의 반사시트를 나타내는 모식적 단면도이다.3 is a schematic cross-sectional view showing a reflective sheet different from the reflective sheets of FIGS. 1 and 2.

도 4는 도 1, 도 2 및 도 3의 반사시트와는 다른 형태의 반사시트를 나타내는 모식적 단면도이다.4 is a schematic cross-sectional view illustrating a reflective sheet different from the reflective sheets of FIGS. 1, 2, and 3.

도 5는 일반적인 에지라이트형의 백라이트 유닛을 나타내는 모식적 사시도이다.5 is a schematic perspective view showing a general edge light type backlight unit.

본 발명자는, 상기 과제를 해결하기위해 예의연구를 거듭한 결과, 상술의 반사시트의 황변 등의 경시적인 열화는, 램프로부터 발생되는 광선에 포함되는 미량의 자외선이 그 주요인인 것을 발견하였다.MEANS TO SOLVE THE PROBLEM As a result of earnestly researching in order to solve the said subject, it discovered that the time-dependent deterioration, such as yellowing of the above-mentioned reflective sheet, is the main thing that the trace amount of ultraviolet rays contained in the light beam which a lamp produces.

그 결과, 상기 과제를 해결하기 위해 이루어진 발명은, 광선의 방산을 저감하는 백라이트 유닛용의 반사시트로서, 백색합성 수지제의 기재 시트층과, 이 기재 시트층의 표면측에 적층되는 자외선 흡수층을 구비하고 있는 것을 특징으로 하는 것이다.As a result, the invention made to solve the above problems is a reflection sheet for a backlight unit which reduces light emission, and includes a base sheet layer made of white synthetic resin and an ultraviolet absorbing layer laminated on the surface side of the base sheet layer. It is characterized by being provided.

당해 반사시트에 의하면, 기재 시트층의 표면측에 적층되는 자외선 흡수층에 의해서 램프로부터 발생되는 미량의 자외선을 흡수하여, 상기 황변 등의 경시적인 열화를 방지할 수가 있다.According to the said reflection sheet, the ultraviolet-ray absorption layer laminated | stacked on the surface side of a base material sheet layer can absorb the trace amount of ultraviolet-ray generate | occur | produced from a lamp, and can prevent deterioration with time such as yellowing.

상기 자외선 흡수층은, 기재 폴리머와, 이 기재 폴리머 중에 포함되는 자외선 흡수제를 가지면 좋다. 이 수단에 의하면, 자외선 흡수층이 내부에 함유하는 자외선 흡수제에 의해서 자외선 흡수기능을 유효하게 발휘할 수가 있다. 또, 자외선 흡수제가 기재 폴리머 중에 함유되어, 보호되고 있기때문에, 당해 반사시트의 보존 운반시, 백라이트 유닛의 조립 작업시 또는 사용시에 있어서의 자외선 흡수제의 결락 등을 방지할 수 있다.The said ultraviolet absorbing layer should just have a base polymer and the ultraviolet absorber contained in this base polymer. According to this means, the ultraviolet absorber can be effectively exhibited by the ultraviolet absorber contained in the ultraviolet absorber layer. In addition, since the ultraviolet absorber is contained and protected in the base polymer, it is possible to prevent the lack of the ultraviolet absorber during storage and transportation of the reflective sheet, during assembly of the backlight unit, or during use.

상기 자외선 흡수제의 기재 폴리머에 대한 함유량으로서는 O.1질량% 이상 1O 질량% 이하가 바람직하다. 자외선 흡수층을 구성하는 기재 폴리머에 대하여 자외선 흡수제를 이 정도 배합함으로써, 반사시트의 상기 황변 방지작용을 효과적으로 이룰 수가 있다.As content with respect to the base polymer of the said ultraviolet absorber, 0.1 mass% or more and 10 mass% or less are preferable. By incorporating an ultraviolet absorber in this amount with respect to the base polymer constituting the ultraviolet absorbing layer, it is possible to effectively achieve the above-described yellowing action of the reflective sheet.

상기 자외선 흡수제로서는, 살리실산계 자외선 흡수제, 벤조페논계 자외선 흡수제, 벤조트리아졸계 자외선 흡수제 및 시아노아크릴레이트계 자외선 흡수제로 이루어지는 군에서 선택되는 1종 또는 2종 이상의 것을 이용하면 좋다. 이들의 자외선 흡수제는, 자외선 흡수기능이 높고, 폴리머와의 상용성이나 열적 안정성도 양호하기때문에, 당해 반사시트의 광 열화, 특히 황변의 방지에 적합하다.As said ultraviolet absorber, 1 type, or 2 or more types chosen from the group which consists of a salicylic acid type ultraviolet absorber, a benzophenone type ultraviolet absorber, a benzotriazole type ultraviolet absorber, and a cyanoacrylate type ultraviolet absorber may be used. Since these ultraviolet absorbers have a high ultraviolet absorbing function and good compatibility with the polymer and also have good thermal stability, they are suitable for preventing light deterioration, particularly yellowing, of the reflective sheet.

또, 상기 자외선 흡수층은, 분자쇄에 자외선 흡수기가 결합된 기재 폴리머를 가지면 좋다. 이 수단에 의하면, 자외선 흡수층을 구성하는 기재 폴리머의 분자쇄에 결합된 자외선 흡수기에 의해서 자외선이 흡수되어, 상기 황변 등의 경시적인 열화를 방지할 수가 있다. 또, 자외선 흡수기능을 가지는 것이 관능기로서 기재 폴리머의 분자쇄에 편입되어 있기때문에, 자외선 흡수기능의 지속성이 현격하게 향상한다.The ultraviolet absorbing layer may have a base polymer having an ultraviolet absorber bonded to a molecular chain. According to this means, ultraviolet rays are absorbed by the ultraviolet absorber bonded to the molecular chain of the base polymer constituting the ultraviolet absorbing layer, thereby preventing deterioration over time such as yellowing. Moreover, since the thing which has an ultraviolet absorption function is incorporated in the molecular chain of a base polymer as a functional group, the persistence of an ultraviolet absorption function improves remarkably.

또한, 상기 자외선 흡수층 중에 자외선 안정제 또는 분자쇄에 자외선 안정기가 결합된 기재 폴리머를 가져도 좋다. 이 수단에 의하면, 자외선에 의해서 발생하는 래디컬, 활성산소 등이 자외선 흡수층 중에 가지는 자외선 안정제 또는 자외선 안정기에 의해 불활성화(분해, 포착 등)되어, 자외선 흡수층 나아가서는 당해 반사시트 열화를 저감할 수가 있다.Moreover, you may have the base polymer which the ultraviolet stabilizer couple | bonded with the ultraviolet stabilizer or molecular chain in the said ultraviolet absorber layer. According to this means, radicals, active oxygen, etc. generated by ultraviolet rays are inactivated (decomposed, trapped, etc.) by an ultraviolet stabilizer or an ultraviolet stabilizer in the ultraviolet absorbing layer, and thus the degradation of the reflecting sheet can be reduced. .

상기 자외선 안정제 또는 자외선 안정기로서는 힌더드아민계 자외선 안정제 또는 힌더드아민계 자외선 안정기가 적합하다. 이 힌더드아민계의 자외선 안정제 또는 흡수기는, 상기 자외선 안정기능이 높고, 또한, 그 지속성도 높기때문에, 당해 반사시트의 내구성 및 내후성을 현격히 향상시킬 수가 있다.As said ultraviolet stabilizer or ultraviolet stabilizer, a hindered amine ultraviolet stabilizer or a hindered amine ultraviolet stabilizer is suitable. This hindered amine-based ultraviolet stabilizer or absorber has a high ultraviolet stabilizing function and a high persistence, and thus can significantly improve the durability and weather resistance of the reflective sheet.

또, 당해 반사시트에 있어서, 상기 자외선 흡수층 중에 더욱이 연질 엘라스토머 재료제의 비드를 분산 함유하면 좋다. 이 수단에 의하면, 당해 반사시트의 표면에 비드에 의한 연질의 볼록형상부를 형성할 수가 있다. 그 때문에, 백라이트 유닛에 있어서 당해 반사시트는 그 표면측에 배열설치되는 도광판의 이면에 상기비드에 의한 연질의 볼록형상부에서 산점적(散点的)으로 맞닿고, 그 결과, 도광판의 이면에의 손상을 방지할 수가 있다. 또, 자외선 흡수층 중에 분산 함유되는 비드에 의해서 광 확산성을 부여할 수 있고, 이러한 자외선 흡수층의 광 확산성에 의해 반사시트의 반사성 및 은폐성을 촉진할 수가 있다.The reflective sheet may further contain, in the ultraviolet absorbing layer, a dispersion made of a soft elastomer material. According to this means, a soft convex portion formed by beads can be formed on the surface of the reflective sheet. Therefore, in the backlight unit, the reflecting sheet abuts against the back surface of the light guide plate arranged on the front surface side of the light guide plate at the soft convex shape due to the beads, and as a result, to the back surface of the light guide plate. Damage can be prevented. In addition, light diffusion can be imparted by the beads dispersed in the ultraviolet absorbing layer, and the reflectivity and concealability of the reflective sheet can be promoted by the light diffusing property of the ultraviolet absorbing layer.

상기 비드로서는, 유리전이 온도가 비교적 낮고, 또한 내용제성, 내열성 등이 우수한 연질 우레탄 비드가 바람직하다.As the beads, soft urethane beads having a relatively low glass transition temperature and excellent solvent resistance, heat resistance and the like are preferable.

한편, 당해 반사시트에 있어서, 상기 자외선 흡수층 중에 더욱 기포를 분산 함유하면 좋다. 이 수단에 의하면, 자외선 흡수층 중에 분산되는 기포에 의해서 표면에 미세한 연질의 볼록형상부가 형성되고, 분산 함유되는 상기 비드와 마찬가지로 도광판 이면에의 손상 방지성을 이룰 수 있고, 또한, 반사성 및 은폐성을 촉진할 수가 있다.On the other hand, in the said reflection sheet, what is necessary is to disperse | distribute foam | bubble further in the said ultraviolet absorbing layer. According to this means, a fine soft convex portion is formed on the surface by bubbles dispersed in the ultraviolet absorbing layer, and similarly to the above-mentioned beads contained in the dispersion, damage can be prevented on the back surface of the light guide plate. I can promote it.

또한, 당해 반사시트에 있어서, 상기 기재 시트층의 이면측에 적층되는 고은폐층을 더욱 구비하고, 이 고은폐층을 백색안료를 함유하는 도료의 도공에 의해 형성하면 좋다. 이 수단에 의하면, 기재 시트층의 이면측에 적층되는 고은폐층에 의해서 당해 반사시트의 반사성 및 은폐성을 현격히 향상시킬 수가 있다.The reflective sheet may further include a high concealment layer laminated on the back side of the base sheet layer, and the high concealment layer may be formed by coating a paint containing a white pigment. According to this means, the reflective and concealable properties of the reflective sheet can be remarkably improved by the highly concealed layer laminated on the back side of the base sheet layer.

따라서 (a) 선상의 램프와, (b) 이 램프를 따르도록 배열설치되고, 램프로부터 발생되는 광선을 표면측으로 유도하는 도광판과, (c) 이 도광판의 표면측에 배열설치되고, 상기 도광판으로부터 출사된 광선을 대략 균일하게 확산하고 또한 법선방향측으로 굴절시키는 광학시트와, (d) 상기 도광판의 이면측에 배열설치되는 상기 본 발명의 반사시트를 장비하는 액정표시 장치용의 백라이트 유닛은, 상술과같이 당해 반사시트가 경시적인 황변 방지작용을 이루기때문에, 백라이트 화면이 경시적으로 황색을 띠는 것 및 휘도가 저하하는 것을 방지할 수 있어, 품질을 향상시킬 수가 있다. 또, 당해 반사시트가 이루는 도광판 이면의 손상이 방지성에 의해서, 도광판 이면에의 손상에 의한 휘도의 저하 및 휘도얼룩의 발생을 방지할 수 있고, 또, 조립 등의 작업성을 개선할 수가 있다.Therefore, (a) a linear lamp, (b) is arranged so as to follow the lamp, a light guide plate for guiding light rays generated from the lamp to the surface side, and (c) is arranged on the surface side of the light guide plate, The backlight unit for a liquid crystal display device equipped with the optical sheet which spreads the emitted light beam substantially uniformly and refracts to the normal direction side, and (d) the reflection sheet of this invention arrange | positioned at the back surface side of the said light-guide plate is mentioned above. As described above, since the reflective sheet has a yellowing prevention effect over time, yellowing of the backlight screen over time and deterioration of luminance can be prevented, and the quality can be improved. In addition, damage to the back surface of the light guide plate formed by the reflective sheet can be prevented, so that the lowering of the brightness and the occurrence of the brightness stain due to the damage to the back surface of the light guide plate can be prevented, and workability such as assembly can be improved.

바람직한 구체예의 설명Description of Preferred Embodiments

이하, 적절한 도면을 참조하면서 본 발명의 실시형태를 상세히 설명한다.EMBODIMENT OF THE INVENTION Hereinafter, embodiment of this invention is described in detail, referring an appropriate drawing.

도 1의 반사시트(1)는, 기재 시트층(2)과, 이 기재 시트층(2)의 표면에 적층되는 자외선 흡수층(3)을 구비하고 있다.The reflective sheet 1 of FIG. 1 includes a base sheet layer 2 and an ultraviolet absorbing layer 3 laminated on the surface of the base sheet layer 2.

이 기재 시트층(2)은, 백색합성 수지로 형성되어 있다. 이 백색합성 수지는, 상술한 바와 같이 백색안료나 미소 기포를 분산 함유하는 합성수지이다. 이 기재 시트층(2)에 사용 가능한 합성수지로서는, 특별히 한정되는 것은 아니고, 예를 들면 폴리에틸렌 테레프탈레이트, 폴리에틸렌 나프탈레이트, 아크릴수지, 폴리카보네이트, 폴리스티렌, 폴리올레핀, 셀룰로오스 아세테이트, 내후성 염화비닐 등을 들 수 있다. 그 중에서도, 내열성이 우수한 폴리에틸렌 테레프탈레이트가 바람직하다.This base material sheet layer 2 is formed of white synthetic resin. This white synthetic resin is a synthetic resin which disperse | distributes a white pigment and a micro bubble as mentioned above. The synthetic resin usable for the base sheet layer 2 is not particularly limited, and examples thereof include polyethylene terephthalate, polyethylene naphthalate, acrylic resin, polycarbonate, polystyrene, polyolefin, cellulose acetate, weather resistant vinyl chloride, and the like. have. Especially, the polyethylene terephthalate excellent in heat resistance is preferable.

이 기재 시트층(2)의 두께는, 특별히 한정되지 않지만, 예를 들면 50㎛ 이상 25O㎛이하가 된다. 기재 시트층(2)의 두께가 상기 범위 미만이면, 자외선 흡수층(3)을 형성하는 수지 조성물을 도공했을 때에 컬이 발생하기 쉬워져버리는 경우가 있다. 반대로, 기재 시트층(2)의 두께가 상기 범위를 초과하면, 액정표시장치의 휘도가 저하되어 버리는 일이 있고, 또 백라이트 유닛의 두께가 커져서 액정표시장치의 박형화의 요구에도 반하게 된다.Although the thickness of this base material sheet layer 2 is not specifically limited, For example, they are 50 micrometers or more and 250 micrometers or less. When the thickness of the base sheet layer 2 is less than the above range, curling may easily occur when the resin composition for forming the ultraviolet absorbing layer 3 is coated. On the contrary, when the thickness of the base sheet layer 2 exceeds the above range, the luminance of the liquid crystal display device may be lowered, and the thickness of the backlight unit may be increased to counter the demand for thinning the liquid crystal display device.

또한, 함유하는 백색안료로서는, 종래의 반사시트와 동일하고, 구체적으로는 산화티탄(티탄백), 산화아연(아연화), 탄산연(연백), 황산바륨, 탄산칼슘(백악) 등을 이용할 수가 있다. 그 중에서도, 은폐성 향상효과가 큰 산화티탄이 바람직하다. 또, 분산 함유하는 기포에 관해서도, 종래의 반사시트와 동일하다.As the white pigment to be contained, it is the same as the conventional reflective sheet, and specifically, titanium oxide (titanium bag), zinc oxide (zinc oxide), lead carbonate (light white), barium sulfate, calcium carbonate (chalk) or the like can be used. have. Especially, titanium oxide with a large concealment improvement effect is preferable. In addition, the bubbles contained in the dispersion are the same as in the conventional reflective sheet.

자외선 흡수층(3)은, 기재 폴리머(4)와, 이 기재 폴리머(4) 중에 함유되는 자외선 흡수제로 형성되어 있다. 또한, 이 자외선 흡수층(3)의 두께는 특별히 한정되지 않지만, 예를 들면 3㎛ 이상 3O㎛ 이하 정도로 되어 있다.The ultraviolet absorbing layer 3 is formed of the base polymer 4 and the ultraviolet absorber contained in the base polymer 4. In addition, although the thickness of this ultraviolet absorbing layer 3 is not specifically limited, For example, they are about 3 micrometers or more and 30 micrometers or less.

이 기재 폴리머(4)에 이용하는 재료로서는, 특별히 한정되는 것은 아니고, 예를 들면 아크릴계 수지, 폴리우레탄, 폴리에스테르, 플루오르계 수지, 실리콘계 수지, 폴리아미드이미드, 에폭시수지 등을 이용할 수가 있다. 또, 이 기재 폴리머(4) 중에는, 상기의 폴리머 외, 예를 들면 가소제, 안정화제, 열화 방지제, 분산제, 대전 방지제 등이 배합되어도 좋다. 이 기재 폴리머(4)는, 일반적으로는 투명으로 되어 있는데, 기재 시트층(2)과 마찬가지로 반사성 및 은폐성을 부여하기위해, 백색안료나 기포를 분산시켜도 좋다.The material used for the base polymer 4 is not particularly limited, and for example, acrylic resins, polyurethanes, polyesters, fluorine resins, silicone resins, polyamideimide, epoxy resins and the like can be used. In addition, in the base polymer 4, a plasticizer, a stabilizer, a deterioration inhibitor, a dispersant, an antistatic agent and the like other than the above polymer may be blended. Although the base polymer 4 is generally transparent, a white pigment or bubbles may be dispersed in order to provide reflectivity and concealment like the base sheet layer 2.

자외선 흡수층(3)에 포함되는 자외선 흡수제로서는, 자외선을 흡수하고, 효율좋게 열에너지로 변환할 수 있는 것이고, 또한, 빛에 대하여 안정한 화합물이면 특별히 한정되는 것은 아니고 공지의 것을 사용할 수가 있다. 그 중에서도, 자외선 흡수기능이 높고, 상기 기재 폴리머(4)와의 상용성이 양호하며, 기재 폴리머(4)중에 안정되게 존재하는 살리실산계 자외선 흡수제, 벤조페논계 자외선 흡수제, 벤조트리아졸계 자외선 흡수제 및 시아노아크릴레이트계 자외선 흡수제가 바람직하고, 이들의 군으로부터 선택되는 1종 또는 2종 이상의 것을 이용하면 좋다.As a ultraviolet absorber contained in the ultraviolet absorbing layer 3, if it is a compound which absorbs an ultraviolet-ray, can be converted into heat energy efficiently, and is stable with respect to light, a well-known thing can be used. Especially, the salicylic acid type ultraviolet absorber, the benzophenone type ultraviolet absorber, the benzotriazole type ultraviolet absorber, and the cyan which have a high ultraviolet absorbing function, are compatible with the said base polymer 4, and exist in the base polymer 4 stably. A noacrylate ultraviolet absorber is preferable, and 1 type, or 2 or more types chosen from these group may be used.

자외선 흡수층(3)에 있어서, 상기 자외선 흡수제의 기재 폴리머(4)에 대한 함유량의 하한으로서는 O.1질량%, 특히 1질량%, 더욱이 3질량%가 바람직하고, 자외선 흡수제의 상기 함유량의 상한으로서는 1O질량%, 특히 8질량%, 더욱이 5질량%가 바람직하다. 이것은, 자외선 흡수층을 구성하는 기재 폴리머(4)에 대하여 자외선 흡수제의 배합량이 상기 하한보다 작으면, 반사시트(1)의 상기 황변 등의 방지작용을 효과적으로 이룰 수 없기 때문이고, 반대로, 자외선 흡수제의 배합량이 상기 상한을 초과하면, 기재 폴리머(4)에 악영향을 미쳐서, 자외선 흡수층(3)의 강도, 내구성 등의 저하를 초래하기때문이다.In the ultraviolet absorber layer 3, the lower limit of the content of the ultraviolet absorber with respect to the base polymer 4 is 0.1% by mass, in particular 1% by mass, more preferably 3% by mass, and as the upper limit of the content of the ultraviolet absorber 10 mass%, especially 8 mass%, Furthermore, 5 mass% is preferable. This is because, when the compounding quantity of the ultraviolet absorber with respect to the base polymer 4 constituting the ultraviolet absorbing layer is smaller than the lower limit, it is not possible to effectively prevent the yellowing or the like of the reflective sheet 1, and conversely, This is because when the blending amount exceeds the above upper limit, the base polymer 4 is adversely affected, leading to a decrease in the strength, durability and the like of the ultraviolet absorbing layer 3.

당해 반사시트(1)의 제조방법으로서는, (a) 기재 폴리머(4)에 자외선 흡수제를 혼합함으로써 자외선 흡수층(3)용 수지 조성물을 조정하는 공정과, 도공 등의 방법으로 이 수지 조성물을 기재 시트층(2)의 표면에 적층하고, 자외선 흡수층(3)을 형성하는 공정으로 이루어지는 제법이나, (b) 도공 등의 방법으로 기재 폴리머(4)를 구성하는 수지 조성물을 기재 시트층(2)의 표면에 적층하는 공정과, 이 공정에서 형성된 적층층에 자외선 흡수제를 함침시킴으로써 자외선 흡수층(3)을 형성하는 공정으로 이루어지는 제법 등이 가능하다.As the manufacturing method of the said reflection sheet 1, (a) the resin composition for ultraviolet absorbing layer 3 is adjusted by mixing a ultraviolet absorber with the base material polymer 4, and a base material sheet is used for this resin composition by methods, such as coating. The resin composition which comprises the base material polymer 4 by the manufacturing method which consists of a process of laminating | stacking on the surface of the layer 2 and forming the ultraviolet-ray absorption layer 3, (b) coating, etc. of the base material sheet layer 2 The manufacturing method etc. which consist of the process of laminating | stacking on the surface and the process of forming the ultraviolet absorbing layer 3 by impregnating an ultraviolet absorber in the laminated layer formed at this process are possible.

당해 반사시트(1)에 의하면, 백색합성 수지제의 기재 시트층(2)에 의해 종래의 반사시트와 동일한 반사성과 은폐성을 이루고, 또한 기재 시트층(2)의 표면측에적층되는 자외선 흡수층(3)에 의해서 램프로부터 발생되는 자외선을 흡수하여, 황변 등의 경시적인 열화를 방지할 수가 있다. 즉, 종래의 반사시트와 동일한 기재 시트층(2)을 이용하여, 그 표면에 상기 자외선 흡수층(3)을 적층함으로써, 용이하고도 확실하게 반사시트(1)의 경시적인 황변 등을 방지할 수가 있다.According to the said reflection sheet 1, the ultraviolet absorbing layer laminated | stacked on the surface side of the base material sheet layer 2 by the base material sheet layer 2 made of white synthetic resin achieves the same reflectivity and concealment as the conventional reflection sheet. By (3), ultraviolet rays generated from the lamp can be absorbed, and the deterioration over time such as yellowing can be prevented. That is, by laminating the ultraviolet absorbing layer 3 on the surface thereof using the same base sheet layer 2 as in the conventional reflecting sheet, it is possible to easily and reliably prevent the yellowing of the reflecting sheet 1 over time. have.

또한, 자외선 흡수층(3)은, 분자쇄에 자외선 흡수기를 가지는 기재 폴리머(예를 들면, (주) 니혼 쇼쿠바이의 「유더블 UV」시리즈 등)로 형성하는 것도 가능하다. 이와 같이, 자외선 흡수층(3)에 분자쇄에 자외선 흡수기를 가지는 기재 폴리머를 이용함으로써, 자외선 흡수제의 블리드아웃 등에 의한 자외선 흡수기능의 열화를 방지할 수가 있다. 또, 이 자외선 흡수기가 결합된 기재 폴리머 중에 또한 자외선 흡수제를 함유함으로써, 자외선 흡수층(3)의 자외선 흡수기능을 보다 향상시킬 수가 있다.Moreover, the ultraviolet absorbing layer 3 can also be formed from the base polymer (for example, "Ultra UV" series of Nippon Shokubai Co., Ltd.) which has an ultraviolet absorber in a molecular chain. Thus, by using the base polymer which has an ultraviolet absorber in a molecular chain for the ultraviolet absorbing layer 3, deterioration of the ultraviolet absorbing function by the bleeding-out of an ultraviolet absorber can be prevented. Moreover, the ultraviolet absorber of the ultraviolet absorber layer 3 can be improved further by containing a ultraviolet absorber further in the base polymer which this ultraviolet absorber couple | bonded.

도 2의 반사시트(11)는, 상기 도 1의 반사시트(1)와 마찬가지로, 기재 시트층(2)과, 이 기재 시트층(2)의 표면에 적층되는 자외선 흡수층(12)을 구비하고 있다. 이 기재 시트층(2)은 상기 도 1의 반사시트(1)와 동일하다.The reflective sheet 11 of FIG. 2 is provided with the base material sheet layer 2 and the ultraviolet absorbing layer 12 laminated | stacked on the surface of this base material sheet layer 2 similarly to the said reflective sheet 1 of FIG. have. This base sheet layer 2 is the same as the reflective sheet 1 of FIG.

이 자외선 흡수층(12)은, 상기 반사시트(1)의 자외선 흡수층(3)과 마찬가지로, 기재 폴리머(4)와 이 기재 폴리머(4) 중에 함유되는 자외선 흡수제로 형성되어 있다. 이 기재 폴리머(4), 자외선 흡수제, 및 그 배합량은 상기 반사시트(1)와 동일하다. 당해 자외선 흡수층(12)은, 기재 폴리머(4) 중에 또한 연질 엘라스토머 재료제의 비드(13)를 분산 함유하고 있다. 이 비드(13)의 상단부가 기재 폴리머(4) 외면으로부터 돌출하는 것 등에 의해, 당해 반사시트(1)의 표면에는 매끄럽게 만곡한 연질의 볼록형상부(14)가 형성되어 있다. 따라서, 백라이트 유닛에 있어서, 당해 반사시트(11)의 표면측에 배열설치되는 도광판에 대하여, 당해 반사시트(1)가 연질의 볼록형상부(14)에서 산점적으로 맞닿아, 도광판 이면에의 손상이 저감된다.This ultraviolet absorbing layer 12 is formed of the base polymer 4 and the ultraviolet absorber contained in the base polymer 4 similarly to the ultraviolet absorbing layer 3 of the reflection sheet 1. This base polymer 4, an ultraviolet absorber, and the compounding quantity are the same as that of the said reflection sheet 1. The ultraviolet absorbing layer 12 further contains and contains a bead 13 made of a soft elastomeric material in the base polymer 4. An upper end of the bead 13 protrudes from the outer surface of the base polymer 4, for example, and a soft convex portion 14 that is smoothly curved is formed on the surface of the reflective sheet 1. Therefore, in the backlight unit, the reflective sheet 1 scatters abutting on the soft convex portion 14 with respect to the light guide plate arranged on the surface side of the reflective sheet 11, and damages to the back surface of the light guide plate. This is reduced.

이 자외선 흡수층(12)의 표면 거칠기(Ra)의 하한으로서는, 5㎛, 특히 7㎛, 더욱이 9㎛이 바람직하다. 한편, 상기 표면 거칠기(Ra)의 상한으로서는, 2O㎛, 특히 17㎛, 더욱이 14㎛이 바람직하다. 이것은, 자외선 흡수층(12)의 표면 거칠기(Ra)가 상기 하한보다 작으면, 상술과 같은 도광판 이면에의 산점적 맞닿음에 의한 손상 방지성을 효과적으로 이루는 것이 곤란해지고, 반대로, 표면 거칠기(Ra)가 상기 상한을 초과하면, 거친 볼록형상부(14)에 의해서 반대로 도광판 이면에 상처를 내버릴 우려가 있기때문이다. 상기「표면 거칠기(Ra)」는, 컷오프 값 8㎜, 평가 길이 4Omm의 값이다.As a minimum of the surface roughness Ra of this ultraviolet absorbing layer 12, 5 micrometers, especially 7 micrometers, Furthermore, 9 micrometers is preferable. On the other hand, as an upper limit of the said surface roughness Ra, 20 micrometers, especially 17 micrometers, 14 micrometers are preferable. When the surface roughness Ra of the ultraviolet absorbing layer 12 is smaller than the lower limit, it becomes difficult to effectively prevent damage due to scattered contact with the back surface of the light guide plate as described above, and conversely, the surface roughness Ra This is because when the upper limit exceeds the upper limit, the rough convex portion 14 may damage the back surface of the light guide plate. Said "surface roughness Ra" is a value of a cutoff value of 8 mm and an evaluation length of 40 mm.

비드(13)는, 유리전이 온도가 낮은 연질 엘라스토머 재료로 형성된 것을 이용한다. 이러한 연질 엘라스토머 재료제의 비드(13)에 의해 자외선 흡수층(12)의 표면에 형성되는 볼록형상부(14)의 경도가 비교적 작아져, 상기 도광판 이면에 대한 손상 방지성이 효과적으로 이루어진다.The beads 13 are formed of a soft elastomer material having a low glass transition temperature. The soft elastomer beads 13 make the hardness of the convex portion 14 formed on the surface of the ultraviolet absorbing layer 12 relatively small, thereby effectively preventing damage to the back surface of the light guide plate.

이 연질 엘라스토머 재료의 구체적인 유리전이 온도의 하한으로서는 -1OO℃, 특히 -8O℃, 더욱이 -6O℃가 바람직하고, 그 상한으로서는 3O℃, 특히 25℃, 더욱이 2O℃가 바람직하다. 이것은, 비드(13)를 구성하는 연질 엘라스토머 재료의 유리전이 온도가 상기 상한을 초과하면, 당해 반사시트(11) 표면의 볼록형상부(14)의경도가 커져서, 상기 도광판 이면에 대한 손상 방지성을 효과적으로 발휘할 수 없게 되어 버리고, 반대로, 당해 연질 엘라스토머 재료의 유리전이 온도가 상기 하한보다 작으면, 당해 반사시트(11) 표면의 볼록형상부(14)가 찌그러져, 자외선 흡수 층(12) 표면이 도광판 이면에 맞닿아, 상기 손상 방지성을 효과적으로 이룰 수 없게 되어 버리기때문이다.As a minimum of the specific glass transition temperature of this soft elastomer material, -10 degreeC, especially -80 degreeC, Furthermore, -60 degreeC is preferable, As an upper limit, 30 degreeC, especially 25 degreeC, Furthermore, 20 degreeC is preferable. This is because when the glass transition temperature of the soft elastomeric material constituting the bead 13 exceeds the upper limit, the hardness of the convex portion 14 on the surface of the reflective sheet 11 increases, preventing damage to the back surface of the light guide plate. On the contrary, when the glass transition temperature of the said soft elastomeric material is less than the said minimum, the convex part 14 of the surface of the said reflective sheet 11 will be crushed, and if the surface of the ultraviolet absorbing layer 12 is a light guide plate, This is because the damage preventing property cannot be effectively achieved.

비드(13)에 사용가능한 구체적인 연질 엘라스토머 재료로서는, 예를 들면, 폴리우레탄, 실리콘고무, 폴리스티렌, 열가소성 폴리에스테르 등을 들 수 있고, 그 중에서도 내용제성, 내열성 등에서 연질 우레탄 비드가 바람직하다.Specific soft elastomeric materials usable for the beads 13 include, for example, polyurethane, silicone rubber, polystyrene, thermoplastic polyester, and the like. Among them, soft urethane beads are preferred in terms of solvent resistance and heat resistance.

비드(13)의 평균 입자직경의 하한으로서는, 3㎛, 특히 5㎛, 더욱이 7㎛이 바람직하고, 그 상한으로서는 4O㎛, 특히 3O㎛, 더욱이 2O㎛이 바람직하다. 이것은, 비드(13)의 평균 입자직경이 상기 하한 미만이면, 비드(13)를 기재 폴리머(4)로부터 돌출시켜서 볼록형상부(14)를 형성하는 것이 곤란해져, 자외선 흡수층(12)의 표면 거칠기(Ra)를 상기 범위로 할 수 없기때문이고, 반대로, 비드(13)의 평균 입자직경이 상기 상한을 초과하면, 자외선 흡수층(12)의 표면 거칠기(Ra)가 상기 범위를 초과하여 손상 방지성이 저감하는 것, 및, 수지 조성물의 도공 등에 의한 자외선 흡수층(12)의 형성이 곤란해져 버리기때문이다.As a minimum of the average particle diameter of the bead 13, 3 micrometers, especially 5 micrometers, Furthermore, 7 micrometers is preferable, As an upper limit, 40 micrometers, especially 30 micrometers, Furthermore, 20 micrometers is preferable. This makes it difficult to protrude the beads 13 from the base polymer 4 to form the convex portions 14 when the average particle diameter of the beads 13 is less than the lower limit, so that the surface roughness of the ultraviolet absorbing layer 12 ( On the contrary, if the average particle diameter of the bead 13 exceeds the upper limit, the surface roughness Ra of the ultraviolet absorbing layer 12 exceeds the above range and the damage prevention property It is because it becomes difficult to reduce and to form the ultraviolet absorbing layer 12 by coating of a resin composition.

기재 폴리머(4)의 폴리머분 1OO부에 대한 비드(13)의 배합량의 하한으로서는, O.1부, 특히 5부, 더욱이 1O부가 바람직하다. 한편, 비드(13)의 상기 배합량의 상한으로서는, 5OO부, 특히 3OO부, 더욱이 1OO부가 바람직하다. 여기서, 「부」로 나타내는 수치는 질량을 기준으로 하는 비를 의미한다. 이것은, 비드(13)의배합량이 상기 하한미만이면, 자외선 흡수층(12)의 표면 거칠기(Ra)를 상기 범위로 할 수 없기 때문이고, 반대로, 상기 상한을 초과하면, 수지 조성물의 도공 등에 의한 자외선 흡수층(12)의 형성이 곤란해져 버리기 때문이다.As a minimum of the compounding quantity of the bead 13 with respect to 100 parts of polymer powders of the base polymer 4, 0.1 part, especially 5 parts, and 10 parts are preferable. On the other hand, as an upper limit of the said compounding quantity of the bead 13, 5OO parts, especially 3OO parts, Furthermore, 100 parts are preferable. Here, the numerical value represented by "part" means the ratio based on mass. This is because the surface roughness Ra of the ultraviolet absorbing layer 12 cannot be within the above range if the blending amount of the beads 13 is less than the above lower limit. On the contrary, if the upper limit is exceeded, ultraviolet rays due to coating of the resin composition or the like This is because the formation of the absorbing layer 12 becomes difficult.

비드(13)로서는 투명, 특히 무색투명이 바람직하다. 이와 같이 투명한 비드(13)를 이용함으로써, 자외선 흡수층(12)에 광 확산성을 부여할 수 있고, 그 결과, 기재 시트층(2)등에서의 반사 등에 의해서 표면측으로 출사되는 광선을 확산하여, 은폐성을 촉진할 수가 있다.As the beads 13, transparent, especially colorless and transparent, is preferable. By using the transparent beads 13 in this manner, light diffusing property can be imparted to the ultraviolet absorbing layer 12, and as a result, light rays emitted to the surface side by the reflection in the substrate sheet layer 2 or the like are diffused and concealed. It can promote sex.

당해 반사시트(11)의 제조방법으로서는, 기본적으로는, 기재 폴리머(4)에 자외선 흡수제 및 비드(13)를 혼합함으로써 자외선 흡수층(12)용 수지 조성물을 조정하는 공정과, 도공 등의 방법으로 이 수지 조성물을 기재 시트층(2)의 표면에 적층하여, 자외선 흡수층(12)을 형성하는 공정으로 이루어진다.As a manufacturing method of the said reflection sheet 11, the process of adjusting the resin composition for the ultraviolet absorbing layers 12 by mixing the ultraviolet absorber and the bead 13 with the base polymer 4 basically, and a method, such as coating, etc. This resin composition is laminated | stacked on the surface of the base material layer 2, and the process of forming the ultraviolet absorbing layer 12 is carried out.

당해 반사시트(11)에 의하면, 상기 반사시트(1)와 마찬가지로, 백색합성 수지제의 기재 시트층(2)에 의해 종래의 반사시트와 동일한 반사성과 은폐성을 이루고, 기재 시트층(2)의 표면측에 적층되는 자외선 흡수층(12)에 의해서 램프로부터 발생되는 자외선을 흡수하여, 황변 등의 경시적인 열화를 방지할 수가 있다. 또, 당해 반사시트(11)에 의하면, 자외선 흡수층(12) 표면의 연질의 볼록형상부(14)에 의해서 표면측에 배열설치되는 도광판 이면에의 손상을 방지할 수가 있다. 또한, 당해 반사시트(11)는, 자외선 흡수층(12)의 비드(13)에 의해서 표면에 요철이 형성되기때문에, 표면측으로의 반사성, 나아가서는 은폐성을 높일 수가 있다.According to the reflection sheet 11, similar to the reflection sheet 1, the base sheet layer 2 made of white synthetic resin achieves the same reflectivity and concealment as the conventional reflection sheet, and the base sheet layer 2 Ultraviolet rays generated from the lamps can be absorbed by the ultraviolet absorbing layer 12 laminated on the surface side of the substrate, and the deterioration over time such as yellowing can be prevented. Moreover, according to the said reflection sheet 11, the damage to the back surface of the light guide plate arrange | positioned at the surface side by the soft convex part 14 of the surface of the ultraviolet absorbing layer 12 can be prevented. Moreover, since the unevenness | corrugation is formed in the surface by the bead 13 of the ultraviolet-ray absorption layer 12, the said reflective sheet 11 can improve the reflectivity to a surface side, and also the concealability.

도 3의 반사시트(21)는, 상기 도 1의 반사시트(1)와 마찬가지로, 기재 시트층(2)과, 이 기재 시트층(2)의 표면에 적층되는 자외선 흡수층(22)을 구비하고 있다. 이 기재 시트층(2)은, 상기 반사시트(1)와 동일하다.The reflective sheet 21 of FIG. 3 is provided with the base material sheet layer 2 and the ultraviolet absorbing layer 22 laminated | stacked on the surface of this base material sheet layer 2 similarly to the said reflective sheet 1 of FIG. have. This base sheet layer 2 is the same as the said reflective sheet 1.

자외선 흡수층(22)은, 상기 반사시트(1)의 자외선 흡수층(3)과 마찬가지로, 기재 폴리머(4)와 기재 폴리머(4)중에 함유되는 자외선 흡수제로 형성되어 있고, 더하여 기재 폴리머(4)중에 기포(23)를 분산 함유하고 있다. 이 기포(23)의 분산에 의해서 표면에 볼록형상부(24)가 대략 균일하게 다수 형성되어 있다. 이와 같이, 당해 반사시트(21) 표면의 볼록형상부(24)는, 기포(23)가 내재하고 있기때문에, 탄력이 있고 연질이며, 매끄럽게 만곡하고 있다. 그 때문에, 백라이트 유닛에 있어서 당해 반사시트(21)의 표면측에 배열설치되는 도광판에 대하여, 당해 반사시트(21)가 연질의 볼록형상부(24)에서 산점적으로 맞닿아, 도광판 이면에의 손상이 저감된다. 또한, 이 자외선 흡수층(22)의 표면 거칠기(Ra)는, 상기 도 2의 반사시트(11)와 동일하다.The ultraviolet absorbing layer 22 is formed of the ultraviolet absorbing agent contained in the base polymer 4 and the base polymer 4 similarly to the ultraviolet absorbing layer 3 of the reflection sheet 1, and furthermore, in the base polymer 4. The bubble 23 is dispersed and contained. By the dispersion | distribution of this bubble 23, many convex-shaped parts 24 are formed in the surface substantially uniformly. Thus, since the bubble 23 is inherent, the convex portion 24 on the surface of the reflection sheet 21 is elastic, soft and smoothly curved. Therefore, the reflective sheet 21 is scattered on the soft convex portion 24 in contact with the light guide plate arranged on the surface side of the reflective sheet 21 in the backlight unit, and damage to the back surface of the light guide plate is caused. This is reduced. In addition, the surface roughness Ra of this ultraviolet absorbing layer 22 is the same as that of the reflective sheet 11 of FIG.

이 기포(23)는, 기재 폴리머(4) 중에 존재하는 어떠한 기체를 포함하는 미소 부분으로, 그 형상은 특별히 한정되지 않고, 예를 들면 구상, 입상, 다면체상, 별사탕형상, 랜덤형상, 방추상 등 각종의 형상이 가능하다. 단, 기포(23)의 형상으로서는 구상의 독립기포가, 연질의 볼록형상부(24)의 형성의 용이함 및 높은 광 확산성에 의한 은폐성의 촉진의 점에서 바람직하다. 또, 기포(23)는, 원칙으로서 기재 폴리머(4)의 내부에 존재하는데, 기재 폴리머(4)의 표면에 개구한 개구 기포가 존재하여도 좋고, 이 개구 기포에 의해 볼록형상부(24)의 형성성 및 광 확산성이 촉진된다.The bubble 23 is a micro part containing any gas present in the base polymer 4, and the shape thereof is not particularly limited, and for example, spherical, granular, polyhedral, star candy, random, room, etc. Various shapes such as abstraction are possible. However, as the shape of the bubble 23, a spherical independent bubble is preferable in terms of ease of formation of the soft convex portion 24 and promotion of concealability due to high light diffusivity. In addition, although the bubble 23 exists in the inside of the base polymer 4 as a general rule, the opening bubble opened to the surface of the base polymer 4 may exist, and this opening bubble of the convex-shaped part 24 Formability and light diffusivity are promoted.

기포(23)에 포함되는 기체는, 기포(23)의 형성방법에 의해 결정되고, 특별히 한정되는 것은 아니다. 예를 들면, 후술하는 바와 같이 발포제를 이용한 경우, 발포제의 종류에 의해 공기, 질소가스, 이산화탄소, 암모니아 가스 등이 충전된다.The gas contained in the bubble 23 is determined by the formation method of the bubble 23, and is not specifically limited. For example, when a foaming agent is used as described later, air, nitrogen gas, carbon dioxide, ammonia gas, etc. are filled by the kind of blowing agent.

기포(23)의 평균직경의 하한으로서는 O.5㎛, 특히 1㎛, 더욱이 5㎛이 바람직하고, 그 평균직경의 상한으로서는 5O㎛, 특히 4O㎛, 더욱이 3O㎛이 바람직하다. 이것은, 기포(23)의 평균직경이 상기 하한보다 작으면, 볼록형상부(24)를 형성하는것이 곤란해져, 자외선 흡수층(22)의 표면 거칠기(Ra)를 상기 범위로 할 수 없기 때문이고, 반대로, 평균직경이 상기 상한을 초과하면, 자외선 흡수층(22)의 강도가 저하하기 때문이다.As a minimum of the average diameter of the bubble 23, 0.5 micrometer, especially 1 micrometer, Furthermore, 5 micrometers is preferable, As an upper limit of the average diameter, 50 micrometers, especially 40 micrometers, Furthermore, 30 micrometers are preferable. This is because if the average diameter of the bubbles 23 is smaller than the lower limit, it is difficult to form the convex portion 24, and the surface roughness Ra of the ultraviolet absorbing layer 22 cannot be within the above range. It is because the intensity | strength of the ultraviolet absorbing layer 22 will fall when an average diameter exceeds the said upper limit.

기재 폴리머(4)에 대한 기포(23)의 체적비의 하한으로서는 1vol%, 특히 1Ovol%, 더욱이 2Ovol%가 바람직하고, 그 체적비의 상한으로서는 8Ovol%, 특히 7Ovol%, 더욱이 6Ovol%가 바람직하다. 이것은, 기포(23)의 체적비가 상기 하한보다 작으면, 볼록형상부(24)에 의한 자외선 흡수층(22)의 표면 거칠기(Ra)를 바람직한 상기 범위로 하는 것이 곤란해지고, 또 광 확산성에 의한 은폐성을 촉진하는 효과도 작아지기때문이고, 반대로, 기포(23)의 체적비가 상기 상한을 초과하면, 자외선 흡수층(22)의 강도 및 내구성이 저하하기때문이다.The lower limit of the volume ratio of the bubbles 23 to the base polymer 4 is preferably 1 vol%, in particular 10 vol%, more preferably 20 vol%, and the upper limit of the volume ratio is preferably 8 vol%, particularly 7 vol%, further 6 volvol. If the volume ratio of the bubbles 23 is smaller than the lower limit, it becomes difficult to set the surface roughness Ra of the ultraviolet absorbing layer 22 by the convex portion 24 to the desired range, and the concealability due to light diffusivity. This is because the effect of promoting the pressure decreases. On the contrary, when the volume ratio of the bubbles 23 exceeds the upper limit, the strength and durability of the ultraviolet absorbing layer 22 decrease.

당해 반사시트(21)의 제조방법으로서는, 기본적으로는, 기재 폴리머(4)를 구성하는 수지 조성물(열경화성 수지를 주 폴리머로 한다)중에 발포제 및 자외선 흡수제를 첨가·혼련함으로서, 자외선 흡수층(22)용 수지 조성물을 조정하는 공정과, 이 수지 조성물을 기재 시트층(2)의 표면에 코팅하는 공정과, 가열함으로써 기재폴리머(4)를 열경화시킴과 동시에 발포제를 발포시켜서 기포(23)가 분산된 자외선 흡수층(22)을 적층하는 공정으로 이루어진다.As the manufacturing method of the said reflection sheet 21, the ultraviolet absorbing layer 22 is added basically by adding and kneading a foaming agent and an ultraviolet absorber in the resin composition which comprises the base polymer 4 (a thermosetting resin is used as a main polymer). The process of adjusting the resin composition for resin, the process of coating this resin composition on the surface of the base sheet layer 2, and heat-setting the base polymer 4 by heating, foaming a foaming agent, and foaming | bubble 23 disperse | distributing It consists of a process of laminating | stacking the obtained ultraviolet absorbing layer 22.

당해 반사시트(21)에 의하면, 상기 반사시트(1)와 마찬가지로, 백색합성 수지제의 기재 시트층(2)에 의해 종래의 반사시트와 동일한 반사성과 은폐성을 이루고, 기재 시트층(2)의 표면측에 적층되는 자외선 흡수층(22)에 의해서 램프로부터 발생되는 자외선을 흡수하여, 황변 등의 경시적인 열화를 방지할 수 있다. 또, 당해 반사시트(21)는, 상기 반사시트(11)와 마찬가지로, 자외선 흡수층(22) 표면의 연질의 볼록형상부(14)에 의해서 표면측에 배열설치되는 도광판 이면에의 손상을 방지할 수 있다. 또한, 당해 반사시트(21)는, 자외선 흡수층(22)의 기포(23)에 의해서 표면에 요철이 형성되기 때문에, 표면측으로의 반사성, 나아가서는 은폐성을 높일 수가 있다.According to the reflection sheet 21, similarly to the reflection sheet 1, the base sheet layer 2 made of white synthetic resin achieves the same reflectivity and concealment as the conventional reflection sheet, and the base sheet layer 2 Ultraviolet rays generated from the lamps can be absorbed by the ultraviolet absorbing layer 22 laminated on the surface side of the substrate, and the deterioration over time such as yellowing can be prevented. In addition, the reflective sheet 21, like the reflective sheet 11, can prevent damage to the rear surface of the light guide plate arranged on the surface side by the soft convex portions 14 on the surface of the ultraviolet absorbing layer 22. have. Moreover, since the unevenness | corrugation is formed in the surface by the bubble 23 of the ultraviolet absorber layer 22, the said reflective sheet 21 can improve the reflectivity to a surface side, and also the concealment property.

도 4의 반사시트(31)는, 기재 시트층(2)과, 이 기재 시트층(2)의 표면에 적층되는 자외선 흡수층(12)을 구비하고 있는 점에서, 상기 도 2의 반사시트(11)와 동일하기때문에, 동일 번호를 붙이고 설명을 생략한다. 또한, 당해 반사시트(21)는, 기재 시트층(2)의 이면에 적층되는 고은폐층(32)을 구비하고 있다.Since the reflective sheet 31 of FIG. 4 is provided with the base material sheet layer 2 and the ultraviolet absorbing layer 12 laminated | stacked on the surface of this base material layer 2, the reflective sheet 11 of FIG. Are the same, and the description is omitted. In addition, the reflective sheet 21 is provided with the high concealment layer 32 laminated | stacked on the back surface of the base material sheet layer 2. As shown in FIG.

고은폐층(32)은, 은폐성 및 반사성을 이루는 것으로, 구체적으로는 기재 시트층(2)의 이면에 백색안료(33)를 함유하는 도료(34)를 도공함으로써 형성된다. 또한, 이 고은폐층(32)에 사용되는 도료(34)로서는, 특별히 한정되는 것은 아니고, 일반적인 것이 사용된다. 또, 백색안료(33)로서는, 특별히 한정되는 것은 아니고, 상기 기재 시트층(2) 중에 포함되는 상기 백색안료와 동일한 것이 사용된다.The high concealment layer 32 achieves concealability and reflectivity, and is specifically formed by coating a paint 34 containing a white pigment 33 on the back surface of the substrate sheet layer 2. In addition, the coating material 34 used for this high concealment layer 32 is not specifically limited, A general thing is used. The white pigment 33 is not particularly limited, and the same one as the white pigment contained in the base sheet layer 2 is used.

도료(34)의 고형분에 대한 백색안료(33)의 배합량의 하한으로서는, 7O질량%가 바람직하고, 8O질량%가 특히 바람직하다. 한편, 상기 배합량의 상한으로서는, 95질량%가 바람직하고, 9O질량%가 특히 바람직하다. 이것은, 백색안료(33)의 배합량이 상기 하한보다 작으면, 고은폐층(32)에 의한 상기 반사성 및 은폐성의 향상효 과가 작아지고, 반대로, 백색안료(33)의 배합량이 상기 상한을 초과하면, 도료(34)의 도공이 곤란해지기 때문이다.As a minimum of the compounding quantity of the white pigment 33 with respect to solid content of the coating material 34, 70 mass% is preferable and 80 mass% is especially preferable. On the other hand, as an upper limit of the said compounding quantity, 95 mass% is preferable and 90 mass% is especially preferable. This means that, when the compounding amount of the white pigment 33 is smaller than the lower limit, the effect of improving the reflectivity and hiding property by the high concealment layer 32 becomes small. On the contrary, the compounding amount of the white pigment 33 exceeds the upper limit. This is because coating of the paint 34 becomes difficult.

도료(34)의 도공량(고형분 환산)의 하한으로서는, 1g/㎡, 특히 5g/㎡, 더욱이 1Og/㎡이 바람직하다. 한편, 상기 도공량(고형분 환산)의 상한으로서는, 5Og/㎡, 특히 45g/㎡, 더욱이 4Og/㎡이 바람직하다. 이것은, 도료(34)의 도공량이 상기 하한보다 작으면, 고은폐층(32)에 의한 상기 반사성 및 은폐성의 향상효과가 작아지고, 반대로, 도료(34)의 도공량이 상기 상한을 초과하면, 고은폐층(32)의 두께가 증대하고, 백라이트 유닛의 박형화의 요청에 반하는 것, 및, 고은폐층(32)의 강도의 저하를 초래하기때문이다.As a minimum of coating amount (solid content conversion) of the coating material 34, 1 g / m <2>, especially 5 g / m <2>, and 10 g / m <2> are preferable. On the other hand, as an upper limit of the said coating amount (solid content conversion), 50 g / m <2>, 45 g / m <2>, especially 40 g / m <2> are preferable. This means that if the coating amount of the paint 34 is smaller than the lower limit, the improvement effect of the reflectivity and concealability by the high concealment layer 32 becomes small. On the contrary, if the coating amount of the paint 34 exceeds the upper limit, This is because the thickness of the concealment layer 32 increases, which is contrary to the request for thinning of the backlight unit, and causes a decrease in the strength of the high concealment layer 32.

백색안료(33)의 입자직경(평균 입자직경)은, 10Onm 이상 3O㎛ 이하가 바람직하고, 2OOnm 이상 2O㎛ 이하가 특히 바람직하다. 이것은, 백색안료(33)의 입자직경이 상기 범위보다 작으면, 상기 은폐성을 효과적으로 이루는 것이 곤란해지고, 반대로, 백색안료(33)의 입자직경이 상기 범위를 초과하면, 도료(34) 중에 균일하게 분산되는 것이 곤란해지고, 또 당해 반사시트(31)의 이면이 거칠어져 버리기 때문이다.As for the particle diameter (average particle diameter) of the white pigment 33, 100 micrometers or less are preferable, and 20 micrometers or less and 20 micrometers or less are especially preferable. This means that if the particle diameter of the white pigment 33 is smaller than the above range, it is difficult to achieve the concealability effectively. On the contrary, if the particle diameter of the white pigment 33 exceeds the above range, it is uniform in the paint 34. It is because it becomes difficult to disperse | distribute easily, and the back surface of the said reflection sheet 31 becomes rough.

당해 반사시트(31)의 제조방법으로서는, 기본적으로는, 기재 폴리머(4)에 자외선 흡수제 및 비드(13)를 혼합함으로써 자외선 흡수층(12)용 수지 조성물을 조정하는 공정과, 이 수지 조성물을 기재 시트층(2)의 표면에 적층함으로써 자외선 흡 수층(12)을 형성하는 공정과, 도료(34)에 백색안료(33)를 배합하는 공정과, 이 도료(34)를 기재 시트층(2)의 이면에 도공함으로써 고은폐층(32)을 적층하는 공정으로 이루어진다.As a manufacturing method of the said reflection sheet 31, the process of adjusting the resin composition for ultraviolet absorbing layers 12 by mixing the ultraviolet absorber and the bead 13 with the base material polymer 4 basically, and this resin composition are described The process of forming the ultraviolet-ray absorption layer 12 by laminating | stacking on the surface of the sheet layer 2, the process of mix | blending the white pigment 33 with the paint 34, and this paint 34 are used as the base sheet layer 2 The coating is made on the back surface of the layer to form the high concealment layer 32.

당해 반사시트(31)에 의하면, 상기 반사시트(1)와 마찬가지로, 백색합성 수지제의 기재 시트층(2)에 의해 종래의 반사시트와 동일한 반사성과 은폐성을 이루고, 기재 시트층(2)의 표면측에 적층되는 자외선 흡수층(12)에 의해서 황변 등의 경시적인 열화를 방지할 수가 있다. 또, 상기 반사시트(11)와 마찬가지로, 자외선 흡수층(12)의 비드(13)에 의해서 표면측에 배열설치되는 도광판 이면에의 손상을 방지할 수 있고, 자외선 흡수층(12) 표면의 요철 및 비드(13)의 광 확산성에 의해 표면측으로의 반사성 및 은폐성을 높일 수가 있다. 당해 반사시트(31)에 의하면, 또한, 기재 시트층(2)의 이면의 고은폐층(32)에 의해서 반사성 및 은폐성을 현격히 향상시킬 수가 있다.According to the reflecting sheet 31, similar to the reflecting sheet 1, the base sheet layer 2 made of white synthetic resin achieves the same reflectivity and concealment as the conventional reflecting sheet, and the base sheet layer 2 The ultraviolet absorbing layer 12 laminated on the surface side of the film can prevent deterioration over time such as yellowing. In addition, similar to the reflection sheet 11, damage to the back surface of the light guide plate arranged on the surface side by the bead 13 of the ultraviolet absorbing layer 12 can be prevented, and the unevenness and the bead on the surface of the ultraviolet absorbing layer 12 are prevented. By the light diffusing property of (13), the reflectivity and hiding property to the surface side can be improved. According to the reflection sheet 31, the high hiding layer 32 on the back surface of the base sheet layer 2 can significantly improve the reflectivity and the hiding property.

따라서, 도 5에 도시한 바와 같은 에지라이트형의 백라이트 유닛(4O)에 있어서, 반사시트(46)로서 상기 반사시트(1, 11, 21, 31)를 사용하면, 당해 반사시트(1) 등이 상술과 같이 황변 등의 열화 방지효과를 가지기때문에, 백라이트 화면이 황색을 띠는 것 및 휘도가 저하되는 것을 방지할 수가 있다. 특히, 표면에 연질의 볼록형상부(14, 24)를 가지는 반사시트(11, 21) 및 (31)을 이용하면, 당해 반사시트(11) 등이 상술의 손상 방지성을 이루기때문에, 도광판(43)의 이면에의 손상에 의한 휘도얼룩의 발생을 방지할 수 있고, 또, 백라이트 유닛(4O)의 조립작업이 용이해진다. 또, 이면측에 고은폐층(32)을 구비하는 반사시트(31)를 이용하면, 고은폐층(32)의 높은 은폐성 및 반사성에 의해서 이면측으로부터 방산되는 광선 로스를 저감할 수 있어, 휘도를 향상시킬 수가 있고, 또, 이면측에 배열설치되는 프레임 등이 화면으로부터 확인되는 것을 방지할 수 있어, 휘도얼룩의 발생방지를 촉진할 수가 있다.Therefore, in the edge light type backlight unit 40 as shown in FIG. 5, when the reflecting sheets 1, 11, 21, 31 are used as the reflecting sheet 46, the reflecting sheet 1 and the like. As described above, since it has a deterioration prevention effect such as yellowing, it is possible to prevent the backlight screen from becoming yellow and deteriorating luminance. In particular, when the reflective sheets 11, 21 and 31 having the soft convex portions 14 and 24 on the surface are used, since the reflective sheet 11 and the like achieve the above-mentioned damage prevention property, the light guide plate 43 The occurrence of the luminance unevenness due to the damage to the back surface of the can be prevented, and the assembling work of the backlight unit 40 becomes easy. In addition, by using the reflective sheet 31 having the high concealment layer 32 on the back surface side, it is possible to reduce the light loss emitted from the back surface side by the high concealability and reflectivity of the high concealment layer 32, The luminance can be improved, and the frames and the like arranged on the back side can be prevented from being confirmed from the screen, and the prevention of the occurrence of the luminance stain can be promoted.

또한, 본 발명의 반사시트는 상기 실시형태에 한정되는 것이 아니고, 예를 들면 자외선 흡수제를 함유하는 자외선 흡수층(3, 12, 22)을 구비하지 않고, 기재 시트층(2)을 구성하는 수지 중에 자외선 흡수제를 함유하는 것도 가능하고, 마찬가지로 황변 등의 열화 방지효과를 이룰 수가 있다.In addition, the reflecting sheet of this invention is not limited to the said embodiment, For example, in the resin which comprises the base-sheet sheet layer 2, without providing the ultraviolet absorber layers 3, 12, and 22 containing a ultraviolet absorber. It is also possible to contain a ultraviolet absorber, and similarly it can achieve the deterioration prevention effect, such as yellowing.

또, 자외선 흡수층은, 자외선 안정제를 함유하는 기재 폴리머(4) 또는 분자쇄에 자외선 안정기가 결합된 기재 폴리머(4)로 형성하는 것도 가능하다. 이 자외선 안정제 또는 자외선 안정기에 의해, 자외선에서 발생하는 래디컬, 활성산소 등이 불활성화되고, 자외선 흡수층 나아가서는 당해 반사시트의 자외선 안정성, 내후성 등을 향상시킬 수가 있다. 이 자외선 안정제 또는 자외선 안정기로서는, 자외 선에 대한 안정성이 높은 힌더드아민계 자외선 안정제 또는 힌더드아민계 자외선 안정기가 적합하게 사용된다. 또한, 자외선 흡수층은, 이 자외선 안정제 또는 자외선 안정기와 상기 자외선 흡수제 또는 자외선 안정기를 병유하는 것도 가능하고, 이 병유에 의해 자외선에 의한 열화방지 및 내후성이 현격히 향상한다.Moreover, the ultraviolet absorbing layer can also be formed of the base polymer 4 containing the ultraviolet stabilizer or the base polymer 4 in which the ultraviolet stabilizer is bonded to the molecular chain. By this ultraviolet stabilizer or ultraviolet stabilizer, radicals, active oxygen, etc. generated in the ultraviolet ray are inactivated, and the ultraviolet ray absorbing layer and further, the ultraviolet stability, weather resistance and the like of the reflective sheet can be improved. As this ultraviolet stabilizer or ultraviolet stabilizer, a hindered amine ultraviolet stabilizer or a hindered amine ultraviolet stabilizer having high stability to ultraviolet rays is suitably used. In addition, the ultraviolet absorbing layer can also use this ultraviolet stabilizer or ultraviolet stabilizer together with the said ultraviolet absorber or ultraviolet stabilizer, and this disease prevention significantly improves the prevention of deterioration and weather resistance by ultraviolet rays.

본 발명의 반사시트는 황변등의 경시적인 열화를 일으키지 않으며, 이러한 반사시트를 이용한 백라이트 유닛은 휘도의 향상 및 경시적인 품질 저하의 방지를 도모할 수 있다.The reflective sheet of the present invention does not cause the deterioration of yellowing or the like over time, and the backlight unit using the reflective sheet can improve the luminance and prevent the deterioration of quality over time.

Claims (12)

광선의 방산을 저감하는 백라이트 유닛용의 반사시트로서,As a reflection sheet for a backlight unit which reduces light emission, 백색합성 수지제의 기재 시트층과, 이 기재 시트층의 표면측에 적층되는 자외선 흡수층을 구비하고 있는 것을 특징으로 하는 반사시트.A base sheet layer made of white synthetic resin and an ultraviolet absorbing layer laminated on the surface side of the base sheet layer are provided. 제 1 항에 있어서, 상기 자외선 흡수층이 기재 폴리머와 이 기재 폴리머 중에 포함되는 자외선 흡수제를 가지고 있는 것을 특징으로 하는 반사시트.The reflective sheet according to claim 1, wherein the ultraviolet absorbing layer has a base polymer and an ultraviolet absorber contained in the base polymer. 제 2 항에 있어서, 상기 자외선 흡수제의 기재 폴리머에 대한 함유량이 O.1질량% 이상 1O질량% 이하인　것을 특징으로 하는 반사시트.The reflection sheet according to claim 2, wherein the ultraviolet absorber has a content of 0.1 mass% or more and 10 mass% or less with respect to the base polymer. 제 2 항에 있어서, 상기 자외선 흡수제로서, 살리실산계 자외선 흡수제, 벤조페논계 자외선 흡수제, 벤조트리아졸계 자외선 흡수제 및 시아노아크릴레이트계 자외선 흡수제로 이루어지는 군으로부터 선택되는 1종 또는 2종 이상의 것이 사용되고 있는 것을 특징으로 하는 반사시트.The said ultraviolet absorber is used the 1 type (s) or 2 or more types chosen from the group which consists of a salicylic acid type ultraviolet absorber, a benzophenone type ultraviolet absorber, a benzotriazole type ultraviolet absorber, and a cyanoacrylate type ultraviolet absorber. Reflective sheet, characterized in that. 제 1 항에 있어서, 상기 자외선 흡수층이 분자쇄에 자외선 흡수기가 결합된 기재 폴리머를 가지고 있는 것을 특징으로 하는 반사시트.The reflective sheet according to claim 1, wherein the ultraviolet absorbing layer has a base polymer having an ultraviolet absorber bonded to a molecular chain. 제 1 항에 있어서, 상기 자외선 흡수층 중에 자외선 안정제 또는 분자쇄에 자외선 안정기가 결합된 기재 폴리머를 가지고 있는 것을 특징으로 하는 반사시트.The reflection sheet according to claim 1, wherein the ultraviolet absorption layer has a base polymer having an ultraviolet stabilizer or an ultraviolet stabilizer bonded to a molecular chain. 제 6 항에 있어서, 상기 자외선 안정제 또는 자외선 안정기로서 힌더드아민계 자외선 안정제 또는 힌더드아민계 자외선 안정기가 사용되고 있는 것을 특징으로 하는 반사시트.The reflection sheet according to claim 6, wherein a hindered amine ultraviolet stabilizer or a hindered amine ultraviolet stabilizer is used as the ultraviolet stabilizer or the ultraviolet stabilizer. 제 1 항에 있어서, 상기 자외선 흡수층 중에 연질 엘라스토머 재료제의 비드를 분산 함유하는 것을 특징으로 하는 반사시트.The reflective sheet according to claim 1, wherein the ultraviolet absorber contains dispersed beads of a soft elastomeric material. 제 8 항에 있어서, 상기 비드가 연질 우레탄 비드인 것을 특징으로 하는 반사시트.The reflective sheet of claim 8, wherein the beads are soft urethane beads. 제 1 항에 있어서, 상기 자외선 흡수층 중에 기포를 분산 함유하는 것을 특징으로 하는 반사시트.The reflective sheet according to claim 1, wherein bubbles are dispersed in said ultraviolet absorbing layer. 제 1 항에 있어서, 상기 기재 시트층의 이면측에 적층되는 고은폐층을 더욱 구비하고 있고,The method of claim 1, further comprising a high hiding layer laminated on the back side of the base sheet layer, 이 고은폐층이, 백색안료를 함유하는 도료를 도공함으로써 형성되어 있는 것을 특징으로 하는 반사시트.The high hiding layer is formed by coating a coating material containing a white pigment. 선상의 램프와,With lamps on board, 이 램프를 따르도록 배열설치되고, 램프로부터 발생되는 광선을 표면측으로 유도하는 도광판과,A light guide plate arranged to follow this lamp, for guiding light rays generated from the lamp toward the surface; 이 도광판의 표면측에 배열설치되고, 상기 도광판으로부터 출사된 광선을 대략 균일하게 확산하고 또한 법선방향측으로 굴절시키는 광학시트와,An optical sheet which is arranged on the surface side of the light guide plate and diffuses light rays emitted from the light guide plate substantially uniformly and refracts to the normal direction; 상기 도광판의 이면측에 배열설치되고, 광선의 방산을 저감하는 반사시트를 장비하는 액정표시 장치용의 백라이트 유닛으로서,A backlight unit for a liquid crystal display device, which is arranged on the rear surface side of the light guide plate and is equipped with a reflection sheet which reduces light emission. 상기 반사시트가, 백색합성 수지제의 기재 시트층과, 이 기재 시트층의 표 면측에 적층되는 자외선 흡수층을 구비하고 있는 것을 특징으로 하는 액정표시 장치용의 백라이트 유닛.The said reflective sheet is equipped with the base material sheet layer made from white synthetic resin, and the ultraviolet absorbing layer laminated | stacked on the surface side of this base material sheet layer, The backlight unit for liquid crystal display devices characterized by the above-mentioned.
KR10-2002-0056850A 2001-09-20 2002-09-18 Reflection sheet and backlight unit using the same KR100523204B1 (en)