KR102559620B1 - Construction putty composition - Google Patents

Construction putty composition Download PDF

Info

Publication number
KR102559620B1
KR102559620B1 KR1020230003293A KR20230003293A KR102559620B1 KR 102559620 B1 KR102559620 B1 KR 102559620B1 KR 1020230003293 A KR1020230003293 A KR 1020230003293A KR 20230003293 A KR20230003293 A KR 20230003293A KR 102559620 B1 KR102559620 B1 KR 102559620B1
Authority
KR
South Korea
Prior art keywords
putty composition
rubber
weight
construction
styrene
Prior art date
Application number
KR1020230003293A
Other languages
Korean (ko)
Inventor
장성주
장진호
Original Assignee
주식회사 스페이스인코
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 스페이스인코 filed Critical 주식회사 스페이스인코
Priority to KR1020230003293A priority Critical patent/KR102559620B1/en
Application granted granted Critical
Publication of KR102559620B1 publication Critical patent/KR102559620B1/en

Abstract

본 발명의 실시예에 따라 건축용 퍼티 조성물이 제공된다. 상기 건축용 퍼티 조성물은, 탄소나노튜브; 불소계 수지; 아크릴 에멀젼; 및 고무 에멀젼을 포함하고, 상기 건축용 퍼티 조성물은, 상기 건축용 퍼티 조성물 총 중량 기준으로 탄소나노튜브 15 내지 28 중량％를 포함할 수 있다.According to an embodiment of the present invention, a putty composition for construction is provided. The putty composition for construction may include carbon nanotubes; fluorine-based resins; acrylic emulsion; and a rubber emulsion, and the constructional putty composition may include 15 to 28% by weight of carbon nanotubes based on the total weight of the constructional putty composition.

Description

건축용 퍼티 조성물{CONSTRUCTION PUTTY COMPOSITION}Construction putty composition {CONSTRUCTION PUTTY COMPOSITION}

본 발명은 건축용 퍼티 조성물에 관한 것이다.The present invention relates to a putty composition for construction.

건축용 퍼티는 도장재 마감 공정 시 도장재의 시공 품질을 향상시킬 수 있는 마감재를 의미한다. 이러한 건축용 퍼티는 일반적으로 도장재 시공 전에 건축, 토목 구조물 등의 외벽 또는 내벽의 크랙, 덴트 등을 보수하거나, 도장재의 색상이 선명하고 고르게 도포되도록 하기 위하여 외벽 또는 내벽에 전처리된다.Construction putty refers to a finishing material that can improve the construction quality of a painting material during a painting material finishing process. Such construction putty is generally pretreated on the outer or inner wall in order to repair cracks, dents, etc. of the outer or inner wall of a building, civil engineering structure, etc.

그런데 기존의 건축용 퍼티는 부착력 또는 내수성이 떨어지기 때문에 건축물의 도장층에 발생하는 수분 침투, 결로 현상에 의하여 퍼티가 도장층으로부터 박리되는 현상이 발생한다는 문제가 있었다. 또한, 기존의 건축용 퍼티는 탄성력 또는 강도가 떨어지기 때문에 온도 변화에 따른 신축성 또는 내구성이 저하된다는 단점 역시 존재하였다.However, since the existing putty for construction has poor adhesion or water resistance, there is a problem in that the putty is peeled off from the paint layer due to moisture penetration and condensation occurring in the paint layer of the building. In addition, since the existing construction putty has low elasticity or strength, there is also a disadvantage that elasticity or durability according to temperature change is lowered.

본 발명은 상기 문제점을 해결하기 위한 건축용 퍼티 조성물을 제공하는 것을 그 목적으로 한다.An object of the present invention is to provide a putty composition for construction to solve the above problems.

본 발명의 기술적 과제들은 이상에서 언급한 기술적 과제들로 제한되지 않으며, 언급되지 않은 또 다른 기술적 과제들은 아래의 기재들로부터 당업자에게 명확하게 이해될 수 있을 것이다.The technical problems of the present invention are not limited to the technical problems mentioned above, and other technical problems not mentioned will be clearly understood by those skilled in the art from the description below.

본 발명의 실시예에 따라, 건축용 퍼티 조성물이 제공된다. 상기 건축용 퍼티 조성물은, 탄소나노튜브; 불소계 수지; 아크릴 에멀젼; 및 고무 에멀젼을 포함하고, 상기 건축용 퍼티 조성물은, 상기 건축용 퍼티 조성물 총 중량 기준으로 탄소나노튜브 15 내지 28 중량％를 포함할 수 있다.According to an embodiment of the present invention, a putty composition for construction is provided. The putty composition for construction may include carbon nanotubes; fluorine-based resins; acrylic emulsion; and a rubber emulsion, and the constructional putty composition may include 15 to 28% by weight of carbon nanotubes based on the total weight of the constructional putty composition.

또한, 상기 건축용 퍼티 조성물은, 상기 건축용 퍼티 조성물 총 중량 기준으로 불소계 수지 15 내지 25 중량％를 포함할 수 있다.In addition, the constructional putty composition may include 15 to 25% by weight of a fluorine-based resin based on the total weight of the constructional putty composition.

또한, 상기 불소계 수지는, 폴리비닐리덴플루오라이드(Polyvinylidene Fluoride; PVDF), 폴리테트라플루오로에틸렌(Polytetrafluoroethylene; PTFE), 폴리클로로트리플루오르에틸렌(Polychlorotrifluoroethylene; PCTFE), 폴리비닐리덴플루오라이드-헥사플루오로프로필렌 공중합체(Poly(vinyliden fluoride-co-hexafluoropropylene); PVDF-HFP), 폴리비닐리덴플루오라이드-트라이플루오르에틸렌 공중합체(Poly(vinylidene fluoride-co-trifluoroethylene); PVDF-TrFE) 및 폴리비닐리덴플루오라이드-클로로트리플루오르에틸렌 공중합체(Poly(vinylidene fluoride-co-chlorotrifluoroethylene); PVDF-CTFE)로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다.In addition, the fluorine-based resin, polyvinylidene fluoride (PVDF), polytetrafluoroethylene (PTFE), polychlorotrifluoroethylene (PCTFE), polyvinylidene fluoride-hexafluoropropylene copolymer (Poly (vinylidene fluoride-co-hexafluoropropylene); PVDF-HFP), polyvinylidene fluoride-trifluoroethylene At least one selected from the group consisting of a copolymer (Poly (vinylidene fluoride-co-trifluoroethylene); PVDF-TrFE) and a polyvinylidene fluoride-chlorotrifluoroethylene copolymer (Poly (vinylidene fluoride-co-chlorotrifluoroethylene); PVDF-CTFE) may be included.

또한, 상기 건축용 퍼티 조성물은, 상기 건축용 퍼티 조성물 총 중량 기준으로 아크릴 에멀젼 15 내지 35 중량％을 포함할 수 있다.In addition, the architectural putty composition may include 15 to 35% by weight of the acrylic emulsion based on the total weight of the architectural putty composition.

또한, 상기 아크릴 에멀젼은, 에틸헥실아크릴레이트(Ethylhexyl Acrylate), 부틸아크릴레이트(Butyl Acrylate), 에폭시아크릴레이트(Epoxy Acrylate), 메틸메타크릴레이트(Methyl Methacrylate) 및 우레탄아크릴레이트(Urethane Acrylate)로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다.In addition, the acrylic emulsion may include at least one selected from the group consisting of ethylhexyl acrylate, butyl acrylate, epoxy acrylate, methyl methacrylate, and urethane acrylate.

또한, 상기 건축용 퍼티 조성물은, 상기 건축용 퍼티 조성물 총 중량 기준으로 고무 에멀젼 10 내지 30 중량％을 포함할 수 있다.In addition, the constructional putty composition may include 10 to 30% by weight of the rubber emulsion based on the total weight of the constructional putty composition.

또한, 상기 고무 에멀젼은, 클로로프렌고무(Chloroprene Rubber; CR), 스타이렌-부타디엔-스타이렌 공중합체(Styrene-Butadiene-Styrene Copolymer; SBS), 스타이렌-부타디엔 공중합체(Styrene-Butadiene Copolymer, SB), 스타이렌-아이스프렌-스타이렌 공중합체(Styrene-Isoprene-Styrene Copolymer; SIS), 부타디엔고무(Butadiene Rubber; BR), 스타이렌-부타디엔고무(Styrene-Butadiene Rubber; SBR), 니트릴-부타디엔 고무(Nitrile-Butadiene Rubber; NBR) 및 천연고무(Natural Rubber; NR)로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다.In addition, the rubber emulsion, Chloroprene Rubber (CR), Styrene-Butadiene-Styrene Copolymer (SBS), Styrene-Butadiene Copolymer (SB), Styrene-Isoprene-Styrene Copolymer (SIS), butadiene rubber (Butadiene Rubber; BR), styrene-butadiene rubber (SBR), nitrile-butadiene rubber (NBR), and natural rubber (Natural Rubber; NR).

또한, 에틸렌비닐아세테이트(Ethylene-Vinyl Acetate; EVA)를 더 포함할 수 있다.In addition, ethylene-vinyl acetate (EVA) may be further included.

또한, 상기 건축용 퍼티 조성물은, 상기 건축용 퍼티 조성물 총 중량 기준으로 에틸렌비닐아세테이트 5 내지 18 중량％을 포함할 수 있다.In addition, the constructional putty composition may include 5 to 18% by weight of ethylene vinyl acetate based on the total weight of the constructional putty composition.

또한, 소포제, 분산제, 충진제 및 증점제 중 1종 이상을 더 포함할 수 있다.In addition, one or more of a defoaming agent, a dispersing agent, a filler, and a thickening agent may be further included.

본 발명에 따르면, 탄소나노튜브 및 불소계 수지를 포함함으로써, 탄성력, 강도, 인장력 및 부착력이 우수하여 건축물의 도장면으로부터의 박리 현상이 방지될 수 있고, 온도 변화에 따른 신축성 또는 내구성이 향상될 수 있다.According to the present invention, by including the carbon nanotubes and the fluorine-based resin, elasticity, strength, tensile force, and adhesion are excellent, so that peeling from the painted surface of the building can be prevented, and elasticity or durability according to temperature change can be improved.

또한, 본 발명에 따르면, 아크릴 에멀젼 및 고무 에멀젼을 포함함으로써, 우수한 내수성을 제공할 수 있으며, 외부 방수, 천정 방수 또는 실내 방수 등 다양한 시공 부위에 적용할 수 있다.In addition, according to the present invention, by including an acrylic emulsion and a rubber emulsion, excellent water resistance can be provided, and it can be applied to various construction sites such as external waterproofing, ceiling waterproofing, or indoor waterproofing.

또한, 본 발명에 따르면, 휘발성 유기 화합물 및 유기 용제를 실질적으로 포함하지 않음으로써, 환경에 친화적일 수 있다.In addition, according to the present invention, since it does not substantially contain volatile organic compounds and organic solvents, it can be environmentally friendly.

다른 식으로 정의되지 않는 한, 본 명세서에서 사용된 모든 기술적 및 과학적 용어들은 본 발명이 속하는 기술 분야에서 숙련된 전문가에 의해서 통상적으로 이해되는 것과 동일한 의미를 갖는다. 일반적으로, 본 명세서에서 사용된 명명법은 본 기술분야에서 잘 알려져 있고 통상적으로 사용되는 것이다. 또한, 본 발명의 실시예를 설명함에 있어, 관련된 공지 구성 또는 기능에 대한 구체적인 설명이 본 발명의 실시예에 대한 이해를 방해한다고 판단되는 경우에는 그 상세한 설명은 생략한다. 또한, 이하에서 본 발명의 실시예들을 설명할 것이나, 본 발명의 기술적 사상은 이에 한정되거나 제한되지 않고 당업자에 의해 변형되어 다양하게 실시될 수 있다.Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. In general, the nomenclature used herein is one well known and commonly used in the art. In addition, in describing an embodiment of the present invention, if it is determined that a detailed description of a related known configuration or function hinders understanding of the embodiment of the present invention, the detailed description will be omitted. In addition, embodiments of the present invention will be described below, but the technical idea of the present invention is not limited or limited thereto and can be modified and implemented in various ways by those skilled in the art.

본 명세서에서 어떤 부분이 어떤 구성요소를 포함한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다. 본 명세서에서, 및/또는 이라는 용어는 복수의 관련된 항목들의 조합 또는 복수의 관련된 항목들 중의 어느 하나의 항목을 포함한다.In the present specification, when a part includes a certain component, this means that it may further include other components without excluding other components unless otherwise stated. In this specification, the terms and/or include a combination of a plurality of related items or any one of a plurality of related items.

본 발명의 실시예에 따라, 건축용 퍼티 조성물이 제공된다.According to an embodiment of the present invention, a putty composition for construction is provided.

건축용 퍼티 조성물은 탄소나노튜브; 불소계 수지; 아크릴 에멀젼; 및 고무 에멀젼을 포함할 수 있다.The putty composition for construction includes carbon nanotubes; fluorine-based resins; acrylic emulsion; and rubber emulsions.

탄소나노튜브는, 조성물의 부착력, 기계적 강도, 내구성 또는 내열성 등을 향상시키는 역할을 할 수 있다. 또한, 탄소나노튜브는 소량으로 포함되더라도 조성물의 강도를 현저하게 증진시킬 수 있으며, 나노 입자로서 조성물의 점도를 적절하게 조절할 수 있다. 예를 들어, 탄소나노튜브는 5 내지 20 nm의 평균 입자 직경을 가질 수 있고, 바람직하게는 5 내지 15 nm의 평균 입자 직경을 가질 수 있으나, 이에 한정되는 것은 아니다.Carbon nanotubes may serve to improve adhesion, mechanical strength, durability or heat resistance of the composition. In addition, even if the carbon nanotubes are included in a small amount, the strength of the composition can be remarkably improved, and the viscosity of the composition can be appropriately controlled as nanoparticles. For example, carbon nanotubes may have an average particle diameter of 5 to 20 nm, preferably 5 to 15 nm, but are not limited thereto.

실시예에서, 탄소나노튜브는 건축용 퍼티 조성물 총 중량 기준으로 15 내지 28 중량％로 포함될 수 있고, 바람직하게는 17 내지 27 중량％로 포함될 수 있다. 탄소나노튜브가 상기 함량 범위로 포함됨에 따라 조성물의 기계적 강도가 극대화될 수 있다. 다만 이에 한정되는 것은 아니다.In an embodiment, the carbon nanotubes may be included in an amount of 15 to 28% by weight, preferably 17 to 27% by weight, based on the total weight of the construction putty composition. As the carbon nanotubes are included within the above content range, mechanical strength of the composition may be maximized. However, it is not limited thereto.

불소계 수지는, 불소계 고분자 화합물로서, 조성물의 내수성, 내충격성, 내열성, 내약품성 또는 전기 절연성 등을 향상시키는 역할을 할 수 있다. 예를 들어, 불소계 수지는 폴리비닐리덴플루오라이드(Polyvinylidene Fluoride; PVDF), 폴리테트라플루오로에틸렌(Polytetrafluoroethylene; PTFE), 폴리클로로트리플루오르에틸렌(Polychlorotrifluoroethylene; PCTFE), 폴리비닐리덴플루오라이드-헥사플루오로프로필렌 공중합체(Poly(vinyliden fluoride-co-hexafluoropropylene); PVDF-HFP), 폴리비닐리덴플루오라이드-트라이플루오르에틸렌 공중합체(Poly(vinylidene fluoride-co-trifluoroethylene); PVDF-TrFE) 및 폴리비닐리덴플루오라이드-클로로트리플루오르에틸렌 공중합체(Poly(vinylidene fluoride-co-chlorotrifluoroethylene); PVDF-CTFE)로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다. 다만 이에 한정되는 것은 아니다.The fluorine-based resin is a fluorine-based polymer compound and can play a role in improving water resistance, impact resistance, heat resistance, chemical resistance or electrical insulation of the composition. For example, fluorine-based resins include polyvinylidene fluoride (PVDF), polytetrafluoroethylene (PTFE), polychlorotrifluoroethylene (PCTFE), polyvinylidene fluoride-co-hexafluoropropylene (PVDF-HFP), polyvinylidene fluoride-trifluoroethylene At least one selected from the group consisting of a copolymer (Poly (vinylidene fluoride-co-trifluoroethylene); PVDF-TrFE) and a polyvinylidene fluoride-chlorotrifluoroethylene copolymer (Poly (vinylidene fluoride-co-chlorotrifluoroethylene); PVDF-CTFE) may be included. However, it is not limited thereto.

실시예에서, 불소계 수지는 건축용 퍼티 조성물 총 중량 기준으로 15 내지 25 중량％로 포함될 수 있고, 바람직하게는 17 내지 23 중량％로 포함될 수 있다. 불소계 수지가 상기 함량 범위로 포함됨에 따라 조성물의 내충격성이 극대화될 수 있다. 다만 이에 한정되는 것은 아니다. In an embodiment, the fluorine-based resin may be included in 15 to 25% by weight, preferably 17 to 23% by weight based on the total weight of the construction putty composition. As the fluorine-based resin is included within the above content range, the impact resistance of the composition may be maximized. However, it is not limited thereto.

아크릴 에멀젼은, 수용성으로서 조성물의 부착력, 신장률, 인열 성능 또는 내약품성 등을 향상시키는 역할을 할 수 있다. 예를 들어, 아크릴 에멀젼은 에틸헥실아크릴레이트(Ethylhexyl Acrylate), 부틸아크릴레이트(Butyl Acrylate), 에폭시아크릴레이트(Epoxy Acrylate), 메틸메타크릴레이트(Methyl Methacrylate) 및 우레탄아크릴레이트(Urethane Acrylate)로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다. 다만 이에 한정되는 것은 아니다.The acrylic emulsion, being water-soluble, may play a role in improving adhesion, elongation, tear performance or chemical resistance of the composition. For example, the acrylic emulsion may include at least one selected from the group consisting of ethylhexyl acrylate, butyl acrylate, epoxy acrylate, methyl methacrylate, and urethane acrylate. However, it is not limited thereto.

실시예에서, 아크릴 에멀젼은 건축용 퍼티 조성물 총 중량 기준으로 15 내지 35 중량％로 포함될 수 있고, 바람직하게는 15 내지 30 중량％로 포함될 수 있다. 아크릴 에멀젼이 상기 함량 범위로 포함됨에 따라, 조성물의 부착력이 극대화될 수 있다. 다만 이에 한정되는 것은 아니다.In an embodiment, the acrylic emulsion may be included in 15 to 35% by weight, preferably 15 to 30% by weight based on the total weight of the construction putty composition. As the acrylic emulsion is included in the content range, the adhesion of the composition may be maximized. However, it is not limited thereto.

고무 에멀젼은, 내후성, 내오존성, 내열성, 내약품성 또는 내노화성 등이 우수하다는 성질이 있어, 조성물의 인장력, 신장률, 접착성, 응집성 또는 혼화성 등을 향상시키는 역할을 할 수 있다. 예를 들어, 고무 에멀젼은 클로로프렌고무(Chloroprene Rubber; CR), 스타이렌-부타디엔-스타이렌 공중합체(Styrene-Butadiene-Styrene Copolymer; SBS), 스타이렌-부타디엔 공중합체(Styrene-Butadiene Copolymer, SB), 스타이렌-아이스프렌-스타이렌 공중합체(Styrene-Isoprene-Styrene Copolymer; SIS), 부타디엔고무(Butadiene Rubber; BR), 스타이렌-부타디엔고무(Styrene-Butadiene Rubber; SBR), 니트릴-부타디엔 고무(Nitrile-Butadiene Rubber; NBR) 및 천연고무(Natural Rubber; NR)로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있고, 바람직하게는 클로로프렌고무일 수 있다. 다만 이에 한정되는 것은 아니다.Rubber emulsions have properties such as excellent weather resistance, ozone resistance, heat resistance, chemical resistance, or aging resistance, and can play a role in improving tensile strength, elongation, adhesiveness, cohesiveness, or miscibility of the composition. For example, rubber emulsions include Chloroprene Rubber (CR), Styrene-Butadiene-Styrene Copolymer (SBS), Styrene-Butadiene Copolymer (SB), Styrene-Isoprene-Styrene Copolymer (SIS), and Butadiene Rubber. (Butadiene Rubber; BR), styrene-butadiene rubber (SBR), nitrile-butadiene rubber (NBR), and natural rubber (NR) may include at least one selected from the group consisting of, preferably chloroprene rubber. However, it is not limited thereto.

실시예에서, 고무 에멀젼은 건축용 퍼티 조성물 총 중량 기준으로 10 내지 30 중량％로 포함될 수 있고, 바람직하게는 10 내지 25 중량％로 포함될 수 있다. 고무 에멀젼이 상기 함량 범위로 포함됨에 따라, 조성물의 내후성, 접착성, 신장률이 극대화될 수 있다. 다만 이에 한정되는 것은 아니다.In an embodiment, the rubber emulsion may be included in an amount of 10 to 30% by weight, preferably 10 to 25% by weight, based on the total weight of the construction putty composition. As the rubber emulsion is included in the above content range, weather resistance, adhesiveness, and elongation of the composition may be maximized. However, it is not limited thereto.

실시예에서, 건축용 퍼티 조성물은 에틸렌비닐아세테이트(Ethylene-Vinyl Acetate; EVA)를 더 포함할 수 있다. In an embodiment, the putty composition for construction may further include ethylene-vinyl acetate (EVA).

에틸렌비닐아세테이트는, 에틸렌(Ethylene)과 비닐아세테이트(Vinyl Acetate)의 공중합체로서, 조성물의 부착력, 작업성, 유연성, 탄성력 또는 내구성 등을 향상시키는 역할을 할 수 있다. Ethylene vinyl acetate is a copolymer of ethylene and vinyl acetate, and may serve to improve adhesion, workability, flexibility, elasticity or durability of the composition.

실시예에서, 에틸렌비닐아세테이트는 건축용 퍼티 조성물 총 중량 기준으로 5 내지 18 중량％로 포함될 수 있고, 바람직하게는 7 내지 17 중량％로 포함될 수 있다. 에틸렌비닐아세테이트가 상기 함량 범위로 포함됨에 따라, 조성물의 작업성, 탄성이 극대화될 수 있다. 다만 이에 한정되는 것은 아니다.In an embodiment, ethylene vinyl acetate may be included in an amount of 5 to 18% by weight, preferably 7 to 17% by weight, based on the total weight of the construction putty composition. As ethylene vinyl acetate is included in the above content range, workability and elasticity of the composition can be maximized. However, it is not limited thereto.

실시예에서, 건축용 퍼티 조성물은 소포제, 분산제, 충진제 및 증점제 중 1종 이상을 더 포함할 수 있다. 예를 들어, 건축용 퍼티 조성물은 건축용 퍼티 조성물 총 중량 기준으로 소포제 0.01 내지 5 중량％, 분산제 0.01 내지 5 중량％, 충진제 1 내지 30 중량％ 및 증점제 0.1 내지 5 중량％를 포함할 수 있다. 다만 이에 한정되는 것은 아니다.In an embodiment, the construction putty composition may further include at least one of a defoaming agent, a dispersing agent, a filler, and a thickening agent. For example, the constructional putty composition may include 0.01 to 5% by weight of an antifoamer, 0.01 to 5% by weight of a dispersant, 1 to 30% by weight of a filler, and 0.1 to 5% by weight of a thickener based on the total weight of the constructional putty composition. However, it is not limited thereto.

소포제는, 조성물 내에 형성되는 거품을 제거하거나, 거품, 기포, 핀홀 등의 발생을 최소화하는 역할을 할 수 있다. 예를 들어, 소포제는 폴리실록산계 소포제, 실리콘계 소포제, 지방산 에스테르계 소포제, 알코올계 소포제 및 인산 에스테르계 소포제로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있고, 바람직하게는 폴리실록산계 소포제를 포함할 수 있다. 다만 이에 한정되는 것은 아니다.The antifoaming agent may play a role of removing bubbles formed in the composition or minimizing the occurrence of bubbles, bubbles, pinholes, and the like. For example, the antifoaming agent may include at least one selected from the group consisting of a polysiloxane-based antifoaming agent, a silicone-based antifoaming agent, a fatty acid ester-based antifoaming agent, an alcohol-based antifoaming agent, and a phosphoric acid ester-based antifoaming agent, and preferably includes a polysiloxane-based antifoaming agent. However, it is not limited thereto.

분산제는, 조성물의 각종 구성을 조성물 내에 균일하게 분산시켜 균일한 물성으로 구현되도록 하는 역할을 할 수 있다. 예를 들어, 분산제는 폴리카르복실릭산 폴리머(Polycarboxylic acid polymer)계 분산제, 아크릴계 분산제, 우레탄계 분산제, 폴리카보네이트계 분산제, 폴리에스테르계 분산제 및 폴리올레핀계 분산제로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있고, 바람직하게는 폴리카르복실릭산 폴리머계 분산제를 포함할 수 있고, 더욱 바람직하게는 저분자량 폴리카르복실릭산 폴리머의 알킬 암모늄염 용액을 포함할 수 있다. 다만 이에 한정되는 것은 아니다.The dispersant may play a role of uniformly dispersing various components of the composition into the composition to realize uniform physical properties. For example, the dispersing agent may include at least one selected from the group consisting of a polycarboxylic acid polymer-based dispersing agent, an acrylic-based dispersing agent, a urethane-based dispersing agent, a polycarbonate-based dispersing agent, a polyester-based dispersing agent, and a polyolefin-based dispersing agent, preferably a polycarboxylic acid polymer-based dispersing agent, and more preferably an alkyl ammonium salt solution of a low molecular weight polycarboxylic acid polymer. However, it is not limited thereto.

충진제는, 내구성, 내열성, 경도 등과 같이 기계적, 열적, 전기적 특성, 가공성 등을 개선하기 위한 역할을 할 수 있다. 예를 들어, 충진제는 탄산칼슘, 고로 슬래그, 플라이애쉬, 탈크, 고무칩(폐타이어가루 등) 및 벤토나이트로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있고, 바람직하게는 탄산칼슘을 포함할 수 있다. 다만 이에 한정되는 것은 아니다.The filler may serve to improve mechanical, thermal, and electrical properties, processability, and the like, such as durability, heat resistance, and hardness. For example, the filler may include at least one selected from the group consisting of calcium carbonate, blast furnace slag, fly ash, talc, rubber chips (waste tire powder, etc.), and bentonite, and may preferably include calcium carbonate. However, it is not limited thereto.

실시예에서, 탄산칼슘은 분말 제형일 수 있다. 부가적으로, 분말 제형의 탄산칼슘은 30 내지 60 ㎛의 평균 입자 직경을 가질 수 있으며, 바람직하게는 30 내지 50 ㎛의 평균 입자 직경을 가질 수 있다. 다만 이에 한정되는 것은 아니다.In an embodiment, the calcium carbonate may be in a powder formulation. Additionally, the calcium carbonate in the powder formulation may have an average particle diameter of 30 to 60 μm, preferably 30 to 50 μm. However, it is not limited thereto.

증점제는, 조성물의 점도를 적절하게 조절하여 조성물의 접착력을 향상시키는 역할을 할 수 있다. 예를 들어, 증점제는 알칼리 증점제, 우레탄계 증점제 및 CMC(Carboxymethyl Cellulose)계 증점제로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다. 다만 이에 한정되는 것은 아니다.The thickener may serve to improve the adhesion of the composition by appropriately adjusting the viscosity of the composition. For example, the thickener may include at least one selected from the group consisting of alkali thickeners, urethane-based thickeners, and CMC (Carboxymethyl Cellulose)-based thickeners. However, it is not limited thereto.

실시예에서, 건축용 퍼티 조성물은 동결방지제, 미세균열 방지제 및 안료 중 1종 이상을 더 포함할 수 있다. 예를 들어, 건축용 퍼티 조성물은 건축용 퍼티 조성물 총 중량 기준으로 동결방지제 0.01 내지 5 중량％, 미세균열 방지제 0.1 내지 5 중량％ 및 안료 0.1 내지 10 중량％를 포함할 수 있다. 다만 이에 한정되는 것은 아니다.In an embodiment, the construction putty composition may further include at least one of an antifreeze agent, a microcrack inhibitor, and a pigment. For example, the architectural putty composition may include 0.01 to 5% by weight of an antifreezing agent, 0.1 to 5% by weight of a microcrack inhibitor, and 0.1 to 10% by weight of a pigment based on the total weight of the architectural putty composition. However, it is not limited thereto.

동결방지제는, 저온에서도 조성물이 얼지 않고 우수한 단열성, 방수성 등을 제공하거나, 조성물이 적절한 물성을 유지하도록 하는 역할을 할 수 있다. 예를 들어, 동결방지제는 에틸렌글라이콜(Ethylene Glycol), 프로필렌글리콜(Propylene Glycol), 다이에틸렌글라이콜(Diethylene Glycol) 및 글리세린(Glycerin)으로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있다. 다만 이에 한정되는 것은 아니다.The anti-freezing agent may serve to prevent the composition from freezing even at low temperatures and to provide excellent thermal insulation and waterproof properties, or to maintain appropriate physical properties of the composition. For example, the antifreezing agent may include at least one selected from the group consisting of ethylene glycol, propylene glycol, diethylene glycol, and glycerin. However, it is not limited thereto.

미세균열 방지제는, 외부 자극에 의하여 발생되는 균열, 미세균열을 방지하거나 최소화하는 역할을 할 수 있다. 예를 들어, 미세균열 방지제는 폴리부텐(Polybutene)을 포함할 수 있다. 폴리부텐은 미세균열 방지력 뿐만 아니라, 결합력 또는 접착력 등을 향상시킬 수 있다. 다만 이에 한정되는 것은 아니다.The microcrack inhibitor may serve to prevent or minimize cracks and microcracks generated by external stimuli. For example, the microcrack inhibitor may include polybutene. Polybutene can improve not only micro-crack prevention, but also bonding strength or adhesive strength. However, it is not limited thereto.

안료는, 조성물의 색채, 명암을 조절하고 커버력 또는 착색력을 조절하는 역할을 할 수 있다. 예를 들어, 안료는 화이트 안료를 포함할 수 있으며, 화이트 안료는 이산화티탄, 산화아연, 황화아연, 황산바륨 및 산화납으로 이루어진 군에서 선택되는 1종 이상을 포함할 수 있고, 바람직하게는 이산화티탄을 포함할 수 있다. 다만 이에 한정되는 것은 아니다.The pigment may play a role in adjusting the color and contrast of the composition and adjusting the covering power or coloring power. For example, the pigment may include a white pigment, and the white pigment may include at least one selected from the group consisting of titanium dioxide, zinc oxide, zinc sulfide, barium sulfate, and lead oxide, and may preferably include titanium dioxide. However, it is not limited thereto.

실시예에 따라, 건축용 퍼티 조성물은 휘발성 유기 화합물 및/또는 유기 용제를 포함하지 않아 친환경적일 수 있다. 이는 휘발성 유기 화합물 및/또는 유기 용제가 전혀 포함되지 않은 것뿐만 아니라, 당업계에서 통상적으로 인정할 수 있는 정도의 유효한 양, 즉 유효성분으로서 포함되지 않은 것을 포함하는 의미로 해석될 수 있다. 구체적으로, 휘발성 유기 화합물 및/또는 유기 용제가 조성물 총 중량 대비 1 중량％, 0.5 중량％, 0.1 중량％, 0.05 중량％, 0.01 중량％ 또는 0.001 중량％ 미만으로 포함하는 경우, 휘발성 유기 화합물 및/또는 유기 용제를 포함하지 않은 것으로 간주할 수 있다.According to embodiments, the construction putty composition may be environmentally friendly as it does not contain a volatile organic compound and/or an organic solvent. This may be interpreted as meaning not only that volatile organic compounds and/or organic solvents are not included at all, but also those that are not included as active ingredients in an effective amount commonly recognized in the art. Specifically, when the volatile organic compound and / or organic solvent is included in less than 1% by weight, 0.5% by weight, 0.1% by weight, 0.05% by weight, 0.01% by weight or 0.001% by weight based on the total weight of the composition, the volatile organic compound and / or organic solvent can be regarded as not included.

실시예에 따라, 건축용 퍼티 조성물은 전처리제로 사용될 수 있다. 예를 들어, 건축용 퍼티 조성물이 외벽에 발생한 크랙, 덴트 등에 도포되어 외벽을 하자 보수하거나, 건축용 퍼티 조성물이 외벽에 도포된 후 유성 또는 수성 페인트 등의 도장재가 퍼티 조성물의 상부에 도포될 수 있다. 다만, 이에 한정되는 것은 아니고, 건축용 퍼티 조성물은 건축, 토목 구조물의 외부 방수, 지하구조물의 옹벽 내지 천정 방수와 화장실, 욕실, 베란다 등의 실내 방수를 위해서 사용되거나, 타일 시공을 위해서도 사용될 수 있다.Depending on the embodiment, the construction putty composition may be used as a pretreatment agent. For example, the construction putty composition is applied to the outer wall to repair cracks or dents, or the construction putty composition is applied to the outer wall, and then a coating material such as oil or water-based paint is applied on top of the putty composition. However, it is not limited thereto, and the architectural putty composition is used for external waterproofing of construction and civil engineering structures, waterproofing of retaining walls or ceilings of underground structures, and indoor waterproofing of toilets, bathrooms, verandas, etc., or for tile construction.

[실험예][Experimental example]

이하에서, 본 발명을 더욱 구체적으로 설명하기 위한 실시예를 다음과 같이 나타내었으나, 본 발명이 이에 한정되는 것은 아니다.Hereinafter, examples for explaining the present invention in more detail are shown as follows, but the present invention is not limited thereto.

실시예 및 비교예의 제조Preparation of Examples and Comparative Examples

하기 표 1에 기재되어 있는 성분을 이용하여, 본 발명에 따른 조성물의 실시예 및 비교예를 제조하였다. 표 1 성분 함량의 단위는 중량％이다.Using the components listed in Table 1 below, examples and comparative examples of the composition according to the present invention were prepared. Table 1 The unit of component content is % by weight.

역할role 성분ingredient 실시예 1Example 1 실시예 2Example 2 실시예 3Example 3 비교예 1Comparative Example 1 비교예 2Comparative Example 2 비교예 3Comparative Example 3 비교예 4Comparative Example 4 비교예 5Comparative Example 5 비교예 6Comparative Example 6 비교예 7Comparative Example 7 비교예 8Comparative Example 8 비교예 9Comparative Example 9 탄소나노튜브carbon nanotube 2020 2727 2020 -- 2020 1313 3030 2020 2020 2020 2020 2020 불소계 수지Fluorine resin 폴리비닐리덴플루오라이드polyvinylidene fluoride 2020 2020 2020 2020 -- 2020 2020 1313 2727 2020 2020 2020 아크릴 에멀젼acrylic emulsion 에틸헥실아크릴레이트ethylhexyl acrylate 2020 2020 2020 2020 2020 2020 2020 2020 2020 2020 2020 2020 고무 에멀젼rubber emulsion 클로로프렌고무Chloroprene rubber 1515 1515 1515 1515 1515 1515 1515 1515 1515 1515 1515 1515 에틸렌비닐아세테이트Ethylene Vinyl Acetate 1010 1010 1717 1010 1010 1010 1010 1010 1010 -- 33 2020 소포제antifoam 폴리실록산polysiloxane 0.30.3 0.30.3 0.30.3 0.30.3 0.30.3 0.30.3 0.30.3 0.30.3 0.30.3 0.30.3 0.30.3 0.30.3 분산제dispersant 폴리카르복실릭산 폴리머의 암모늄염 용액Ammonium salt solution of polycarboxylic acid polymer 0.50.5 0.50.5 0.50.5 0.50.5 0.50.5 0.50.5 0.50.5 0.50.5 0.50.5 0.50.5 0.50.5 0.50.5 동결방지제cryoprotectant 프로필렌글라이콜propylene glycol 0.20.2 0.20.2 0.20.2 0.20.2 0.20.2 0.20.2 0.20.2 0.20.2 0.20.2 0.20.2 0.20.2 0.20.2 미세균열 방지제anti-crack agent 폴리부텐polybutene 22 22 22 22 22 22 22 22 22 22 22 22 충진제filler 탄산칼슘calcium carbonate 1010 33 33 3030 3030 1717 -- 1717 33 2020 1717 -- 안료pigment 이산화티탄titanium dioxide 1One 1One 1One 1One 1One 1One 1One 1One 1One 1One 1One 1One 증점제thickener 셀룰로오스검cellulose gum 1One 1One 1One 1One 1One 1One 1One 1One 1One 1One 1One 1One 계total 100100 100100 100100 100100 100100 100100 100100 100100 100100 100100 100100 100100

구체적인 제조방법은 다음과 같다.The specific manufacturing method is as follows.

아크릴 에멀젼, 고무 에멀젼, 에틸렌비닐아세테이트 및 불소계 수지를 혼합한 뒤, 23 ℃의 온도에서 600 rpm의 속도로 20분 동안 균일하게 교반하고, 동일한 조건에서 소포제, 분산제, 동결방지제 및 미세균열 방지제를 순차적으로 첨가한 뒤 10분 동안 균일하게 교반하였다. 이후, 충진제 및 탄소나노튜브를 순차적으로 첨가한 뒤, 23 ℃의 온도에서 950 rpm의 저속에서의 교반, 1700 rpm의 고속에서의 교반 및 950 rpm의 저속에서의 교반을 15분 동안 순차적으로 수행하였다. 이후, 안료를 첨가한 뒤 23 ℃의 온도에서 1700 rpm의 속도로 10분 동안 균일하게 교반하고, 증점제를 첨가한 뒤 2250 rpm의 속도로 15분 동안 균일하게 교반하였다.After mixing the acrylic emulsion, rubber emulsion, ethylene vinyl acetate and fluorine-based resin, the mixture was uniformly stirred for 20 minutes at a temperature of 23 ° C. at a speed of 600 rpm, and an antifoaming agent, a dispersing agent, an anti-freeze agent and a microcrack inhibitor were sequentially added under the same conditions, followed by uniform stirring for 10 minutes. Thereafter, after sequentially adding the filler and the carbon nanotubes, stirring at a low speed of 950 rpm, stirring at a high speed of 1700 rpm, and stirring at a low speed of 950 rpm were sequentially performed at a temperature of 23 °C for 15 minutes. Thereafter, the mixture was uniformly stirred for 10 minutes at a speed of 1700 rpm at a temperature of 23 °C after adding the pigment, and after the addition of a thickener, the mixture was stirred uniformly for 15 minutes at a speed of 2250 rpm.

실험예: 부착 강도, 인장 강도, 파단 시 신장률, 인열 성능 및 투수압 실험Experimental Example: Bond strength, tensile strength, elongation at break, tear performance and water permeability test

실시예 및 비교예에 대하여 KS F 3211 표준의 실험 방법에 따라 부착 강도, 인장 강도, 파단 시 신장률, 인열 성능 및 투수압 실험을 진행하여, 그 결과를 표 2에 나타내었다.For Examples and Comparative Examples, adhesion strength, tensile strength, elongation at break, tear performance, and water permeability were tested according to the KS F 3211 standard test method, and the results are shown in Table 2.

부착 강도 실험의 경우, 시험용 밑판의 표면에 상기 실시예 및 비교예의 샘플을 각각 도포하고 표준 상태에서 168시간 동안 양생한 후, 상기 샘플에 대하여 2 mm/min의 인장 속도로 인장하여 최대 하중을 구한 뒤, 샘플의 단면적에 대한 최대 하중의 값을 부착 강도로 산출하였다. 부착 강도 실험은 총 3번 진행하여 이에 대한 평균값을 산출하였다.In the case of the adhesion strength test, the samples of the Examples and Comparative Examples were each applied to the surface of the test base plate and cured for 168 hours in a standard state, and then the sample was stretched at a tensile rate of 2 mm/min to obtain a maximum load. Then, the value of the maximum load for the cross-sectional area of the sample was calculated as the adhesion strength. The adhesion strength test was conducted a total of three times, and the average value was calculated.

인장 강도 및 파단 시 신장률 실험의 경우, 시험용 밑판의 표면에 상기 실시예 및 비교예의 샘플을 각각 도포하고 표준 상태에서 168시간 동안 양생한 후, 인장 시험기에 물림 간격이 60 mm가 되도록 샘플을 부착시키고, 500 mm/min의 인장 속도로 샘플이 파단될 때까지 인장하였다. 샘플의 단면적에 대한 최대 하중의 값을 인장 강도로 산출하고, 최초 눈금 사이 거리에 대한 파단 시의 눈금 사이 거리의 백분율을 파단 시 신장률로 산출하였다. 각 실험은 총 3번 진행하여 이에 대한 평균값을 산출하였다.In the case of the tensile strength and elongation at break test, the samples of Examples and Comparative Examples were respectively applied to the surface of the test base plate and cured for 168 hours in a standard state, and then the sample was attached to a tensile tester so that the gap between bites was 60 mm, and the sample was stretched at a tensile rate of 500 mm / min until the sample broke. The value of the maximum load for the cross-sectional area of the sample was calculated as the tensile strength, and the percentage of the distance between the scales at break to the distance between the initial scales was calculated as the elongation at break. Each experiment was conducted a total of 3 times and the average value was calculated.

인열 성능 실험의 경우, 시험용 밑판의 표면에 상기 실시예 및 비교예의 샘플을 각각 도포하고 표준 상태에서 168시간 동안 양생한 후, 상기 샘플에 대하여 500 mm/min의 인장 속도로 샘플이 파단될 때까지 인장하여 최대 하중을 구한 뒤, 샘플의 두께에 대한 최대 하중의 값을 인열 성능으로 산출하였다. 인열 성능 실험은 총 3번 진행하여 이에 대한 평균값을 산출하였다.In the case of the tear performance test, the samples of the Examples and Comparative Examples were respectively applied to the surface of the test base plate, cured for 168 hours in a standard state, and then the sample was pulled at a tensile rate of 500 mm/min until the sample broke. After obtaining the maximum load, the value of the maximum load for the thickness of the sample was calculated as the tear performance. The tear performance test was conducted a total of three times and the average value was calculated.

투수압 실험의 경우, 시험용 밑판의 표면에 상기 실시예 및 비교예의 샘플을 각각 도포하고 168시간 동안 양생한 후, 0.3 N/mm2의 투수압을 가하여 시험용 밑판의 하측에 압력수가 투수되는지 여부를 관측하였다.In the case of the water permeability experiment, the samples of the Examples and Comparative Examples were each applied to the surface of the test bottom plate and cured for 168 hours, and then a water permeability pressure of 0.3 N / mm 2 was applied to the lower side of the test bottom plate. It was observed whether or not the pressure water permeated.

구분division 부착 강도(N/mm2)Adhesion strength (N/mm 2 ) 인장 강도(N/mm2)Tensile strength (N/mm 2 ) 파단 시 신장률(％)Elongation at break (%) 인열 성능(N/mm)Tear performance (N/mm) 투수 여부pitcher 실시예 1Example 1 1One 2.32.3 500500 1515 투수 안됨no pitcher 실시예 2Example 2 1.31.3 22 450450 1414 투수 안됨no pitcher 실시예 3Example 3 1One 2.22.2 495495 1414 투수 안됨no pitcher 비교예 1Comparative Example 1 0.70.7 2.32.3 490490 1313 투수 됨pitched 비교예 2Comparative Example 2 1.21.2 1.71.7 400400 1010 투수 됨pitched 비교예 3Comparative Example 3 0.70.7 2.12.1 470470 1313 투수 안됨no pitcher 비교예 4Comparative Example 4 1.21.2 1.91.9 435435 1313 투수 안됨no pitcher 비교예 5Comparative Example 5 1One 1.51.5 410410 1111 투수 됨pitched 비교예 6Comparative Example 6 0.70.7 2.32.3 490490 1515 투수 안됨no pitcher 비교예 7Comparative Example 7 0.90.9 2.12.1 450450 1212 투수 됨pitched 비교예 8Comparative Example 8 0.90.9 22 430430 1313 투수 됨pitched 비교예 9Comparative Example 9 0.80.8 1.81.8 485485 1313 투수 안됨no pitcher

실험 결과, 실시예 1 내지 3은 모두 부착 강도, 인장 강도, 파단 시 신장률 및 인열 성능이 모두 높은 값으로 측정되고, 투수압 인가 시 압력수가 투수되지 않았는 바, 부착 성능, 인장 성능, 탄성 및 방수 성능이 모두 우수함을 확인할 수 있었다.As a result of the experiment, Examples 1 to 3 were all measured as high values in adhesion strength, tensile strength, elongation at break, and tear performance, and no pressure water was permeated when water pressure was applied, so it was confirmed that all excellent adhesion performance, tensile performance, elasticity and waterproof performance were obtained.

한편, 탄소나노튜브 또는 불소계 수지가 제외된 비교예 1 및 2는 투수압 인가 시 압력수가 투수되었는 바, 방수 성능이 매우 좋지 않은 것을 알 수 있었다. 비교예 1은 부착 강도가 낮은 값으로 측정되어 부착 성능 또한 좋지 않은 것을 알 수 있었고, 비교예 2는 인장 강도, 파단 시 신장률 및 인열 성능이 매우 낮은 값으로 측정되어 인장 성능 및 탄성 또한 매우 좋지 않은 것을 확인하였다.On the other hand, Comparative Examples 1 and 2, in which carbon nanotubes or fluorine-based resins were excluded, were permeated with pressure water when water permeation pressure was applied, and thus it was found that the waterproof performance was not very good. In Comparative Example 1, the adhesive strength was measured at a low value, indicating that the adhesive performance was also poor, and in Comparative Example 2, the tensile strength, elongation at break, and tear performance were measured at very low values, indicating that the tensile performance and elasticity were also very poor.

또한, 탄소나노튜브가 소량으로 포함된 비교예 3은 부착 강도가 낮은 값으로 측정되어 부착 성능이 좋지 않은 것을 알 수 있었고, 탄소나노튜브가 과량으로 포함된 비교예 4는 인장 강도 및 파단 시 신장률이 낮은 값으로 측정되어 인장 성능 및 탄성이 좋지 않은 것을 확인하였다.In addition, in Comparative Example 3 containing a small amount of carbon nanotubes, the adhesion strength was measured at a low value, indicating poor adhesion performance, and in Comparative Example 4, which contained an excessive amount of carbon nanotubes, the tensile strength and elongation at break were measured at low values, confirming that the tensile performance and elasticity were poor.

또한, 불소계 수지가 소량으로 포함된 비교예 5는 투수압 인가 시 압력수가 투수되어 방수 성능이 매우 좋지 않은 것을 알 수 있었고, 불소계 수지가 과량으로 포함되는 비교예 6은 부착 강도가 낮은 값으로 측정되어 부착 성능이 좋지 않은 것을 알 수 있었다.In addition, Comparative Example 5 containing a small amount of fluorine-based resin was found to have very poor waterproof performance because pressure water was permeated when the water permeability pressure was applied, and Comparative Example 6 containing an excessive amount of fluorine-based resin had a low adhesive strength. It was found that the adhesion performance was not good.

또한, 에틸렌비닐아세테이트가 제외된 비교예 7 및 에틸렌비닐아세테이트가 소량으로 포함된 비교예 8은 투수압 인가 시 압력수가 투수되어 방수 성능이 매우 좋지 않은 것을 알 수 있었다. 비교예 8은 파단 시 신장률이 매우 낮은 값으로 측정되어 인장 성능 또한 매우 좋지 않은 것을 확인하였다. In addition, Comparative Example 7 in which ethylene vinyl acetate was excluded and Comparative Example 8 in which ethylene vinyl acetate was included in a small amount were found to have very poor waterproof performance because pressure water was permeated when permeation pressure was applied. In Comparative Example 8, the elongation at break was measured at a very low value, confirming that the tensile performance was also very poor.

또한, 에틸렌비닐아세테이트가 과량으로 포함된 비교예 9는 부착 강도 및 인장 강도가 낮은 값으로 측정되어 부착 성능 및 인장 성능이 좋지 않은 것을 확인하였다.In addition, Comparative Example 9 containing an excessive amount of ethylene vinyl acetate was measured at low values of adhesive strength and tensile strength, confirming that the adhesive performance and tensile performance were poor.

이상으로 본 발명의 내용의 특정한 부분을 상세히 기술하였는 바, 당업계의 통상의 지식을 가진 자에게 있어서, 이러한 구체적 기술은 단지 바람직한 실시양태일 뿐이며, 이에 의해 본 발명의 범위가 제한되는 것이 아닌 점은 명백할 것이다. 따라서 본 발명의 실질적인 범위는 첨부된 청구항들과 그것들의 등가물에 의하여 정의된다고 할 것이다.As above, a specific part of the content of the present invention has been described in detail, to those skilled in the art, these specific descriptions are only preferred embodiments, and thereby the scope of the present invention is not limited. It will be clear. Accordingly, the substantial scope of the present invention will be defined by the appended claims and their equivalents.

Claims (10)

건축용 퍼티 조성물로서,
탄소나노튜브; 불소계 수지; 아크릴 에멀젼; 및 고무 에멀젼;을 포함하고,
상기 건축용 퍼티 조성물은, 상기 건축용 퍼티 조성물 총 중량 기준으로 탄소나노튜브 15 내지 28 중량％, 불소계 수지 15 내지 25 중량％, 아크릴 에멀젼 15 내지 35 중량％ 및 고무 에멀젼 10 내지 30 중량％를 포함하며,
상기 불소계 수지는 폴리비닐리덴플루오라이드(Polyvinylidene Fluoride; PVDF)를 포함하고,
상기 아크릴 에멀젼은 에틸헥실아크릴레이트(Ethylhexyl Acrylate)를 포함하고,
상기 고무 에멀젼은 클로로프렌고무(Chloroprene Rubber; CR)를 포함하는, 건축용 퍼티 조성물.As a putty composition for construction,
carbon nanotubes; fluorine-based resins; acrylic emulsion; and a rubber emulsion;
The constructional putty composition includes 15 to 28% by weight of carbon nanotubes, 15 to 25% by weight of a fluorine resin, 15 to 35% by weight of an acrylic emulsion and 10 to 30% by weight of a rubber emulsion based on the total weight of the constructional putty composition,
The fluorine-based resin includes polyvinylidene fluoride (PVDF),
The acrylic emulsion contains ethylhexyl acrylate,
The rubber emulsion is a construction putty composition comprising chloroprene rubber (CR). 삭제delete 제 1 항에 있어서,
상기 불소계 수지는 폴리테트라플루오로에틸렌(Polytetrafluoroethylene; PTFE), 폴리클로로트리플루오르에틸렌(Polychlorotrifluoroethylene; PCTFE), 폴리비닐리덴플루오라이드-헥사플루오로프로필렌 공중합체(Poly(vinyliden fluoride-co-hexafluoropropylene); PVDF-HFP), 폴리비닐리덴플루오라이드-트라이플루오르에틸렌 공중합체(Poly(vinylidene fluoride-co-trifluoroethylene); PVDF-TrFE) 및 폴리비닐리덴플루오라이드-클로로트리플루오르에틸렌 공중합체(Poly(vinylidene fluoride-co-chlorotrifluoroethylene); PVDF-CTFE)로 이루어진 군에서 선택되는 1종 이상을 더 포함하는, 건축용 퍼티 조성물.According to claim 1,
The fluorine-based resin is polytetrafluoroethylene (PTFE), polychlorotrifluoroethylene (PCTFE), polyvinylidene fluoride-hexafluoropropylene copolymer (Poly (vinylidene fluoride-co-hexafluoropropylene); PVDF-HFP), polyvinylidene fluoride-trifluoroethylene copolymer (Poly (vinylidene fluoride-co-trifluoroethylene); PVDF-Tr FE) and polyvinylidene fluoride-chlorotrifluoroethylene copolymer (Poly (vinylidene fluoride-co-chlorotrifluoroethylene); PVDF-CTFE) further comprising at least one selected from the group consisting of, construction putty composition. 삭제delete 제 1 항에 있어서,
상기 아크릴 에멀젼은 부틸아크릴레이트(Butyl Acrylate), 에폭시아크릴레이트(Epoxy Acrylate), 메틸메타크릴레이트(Methyl Methacrylate) 및 우레탄아크릴레이트(Urethane Acrylate)로 이루어진 군에서 선택되는 1종 이상을 더 포함하는, 건축용 퍼티 조성물.According to claim 1,
The acrylic emulsion further comprises at least one selected from the group consisting of Butyl Acrylate, Epoxy Acrylate, Methyl Methacrylate and Urethane Acrylate, Architectural putty composition. 삭제delete 제 1 항에 있어서,
상기 고무 에멀젼은 스타이렌-부타디엔-스타이렌 공중합체(Styrene-Butadiene-Styrene Copolymer; SBS), 스타이렌-부타디엔 공중합체(Styrene-Butadiene Copolymer, SB), 스타이렌-아이스프렌-스타이렌 공중합체(Styrene-Isoprene-Styrene Copolymer; SIS), 부타디엔고무(Butadiene Rubber; BR), 스타이렌-부타디엔고무(Styrene-Butadiene Rubber; SBR), 니트릴-부타디엔 고무(Nitrile-Butadiene Rubber; NBR) 및 천연고무(Natural Rubber; NR)로 이루어진 군에서 선택되는 1종 이상을 더 포함하는, 건축용 퍼티 조성물.According to claim 1,
The rubber emulsion is styrene-butadiene-styrene copolymer (SBS), styrene-butadiene copolymer (SB), styrene-isoprene-styrene copolymer (Styrene-Isoprene-Styrene Copolymer; SIS), butadiene rubber (BR), styrene-butadiene rubber (Styrene-Butadiene Rubber; SBR), nitrile-butadiene rubber (Nitrile-Butadiene Rubber; NBR) and natural rubber (Natural Rubber; NR) further comprising at least one selected from the group consisting of, construction putty composition. 제 1 항에 있어서,
에틸렌비닐아세테이트(Ethylene-Vinyl Acetate; EVA)를 더 포함하는, 건축용 퍼티 조성물.According to claim 1,
A construction putty composition further comprising ethylene-vinyl acetate (EVA). 제 8 항에 있어서,
상기 건축용 퍼티 조성물은, 상기 건축용 퍼티 조성물 총 중량 기준으로 에틸렌비닐아세테이트 5 내지 18 중량％을 포함하는, 건축용 퍼티 조성물.According to claim 8,
The architectural putty composition comprises 5 to 18% by weight of ethylene vinyl acetate based on the total weight of the architectural putty composition. 제 1 항에 있어서,
소포제, 분산제, 충진제 및 증점제 중 1종 이상을 더 포함하는, 건축용 퍼티 조성물.According to claim 1,
A putty composition for construction, further comprising at least one of a defoaming agent, a dispersing agent, a filler, and a thickening agent.
KR1020230003293A 2023-01-10 2023-01-10 Construction putty composition KR102559620B1 (en)