KR102554716B1 - Beeswax coated paper manufacturing method the same - Google Patents
Beeswax coated paper manufacturing method the same Download PDFInfo
- Publication number
- KR102554716B1 KR102554716B1 KR1020230022913A KR20230022913A KR102554716B1 KR 102554716 B1 KR102554716 B1 KR 102554716B1 KR 1020230022913 A KR1020230022913 A KR 1020230022913A KR 20230022913 A KR20230022913 A KR 20230022913A KR 102554716 B1 KR102554716 B1 KR 102554716B1
- Authority
- KR
- South Korea
- Prior art keywords
- paper
- beeswax
- coated
- coated paper
- hanji
- Prior art date
Abstract
본 발명은 종이 준비 단계(S10), 밀랍 용융 단계(S20), 제1 종이에 상기 S20 단계에서 용융된 밀랍을 도포하는 단계(S30), 상기 S30 단계에서 밀랍이 도포된 상기 제1 종이의 양면에 각각 제2 종이의 일면을 맞닿게 배치하는 단계(S40), 상기 제2 종이의 타면을 60℃ 이상의 온도로 압착하는 단계(S50), 상기 제1 종이 양면에서 상기 제2 종이를 분리하는 단계(S60), 상기 S60 단계를 완료한 상기 제1 종이를 구기는 단계(S80), 상기 S80 단계를 완료한 상기 제1 종이에 용융된 밀랍을 도포하는 단계(S90), 상기 S90 단계를 완료한 상기 제1종이의 양면에 각각 제3종이의 일면을 맞닿게 배치하는 단계(S100), 상기 제3 종이의 타면을 60℃ 이상의 온도로 압착하는 단계(S110), 상기 제1 종이와 상기 제3 종이를 분리하는 단계(S120), 및 상기 S120 단계를 수행한 상기 제1 종이로 밀랍 코팅 종이를 완성하는 단계(S140)를 포함하는 밀랍 코팅 종이 제조 방법을 제공한다.The present invention includes a paper preparation step (S10), a beeswax melting step (S20), a step of applying the beeswax melted in the step S20 to the first paper (S30), and both sides of the first paper to which the beeswax is applied in the step S30. placing one side of the second paper in contact with each other (S40), pressing the other side of the second paper at a temperature of 60 ° C. or higher (S50), separating the second paper from both sides of the first paper (S60), crumpling the first paper after completing step S60 (S80), applying molten beeswax to the first paper after completing step S80 (S90), completing step S90 Placing one side of the third paper to be in contact with both sides of the first paper (S100), pressing the other side of the third paper at a temperature of 60 ° C. or higher (S110), the first paper and the third paper Provided is a method for manufacturing beeswax-coated paper comprising separating paper (S120) and completing beeswax-coated paper with the first paper having performed the step S120 (S140).
Description
본 발명은 밀랍 코팅 종이 제조 방법 및 그를 이용하여 제작된 밀랍 코팅 종이 및 베개커버에 관한 것이다.The present invention relates to a method for manufacturing beeswax-coated paper, and to beeswax-coated paper and pillow covers manufactured using the same.
우리 민족은 예로부터 한지 위에서 태어나 평생을 그 속에서 살며 지내다가 결국은 한지에 싸여 어머니 품속 같은 포근한 정을 받으며 다시 자연의 흙으로 돌아간다. 한지 위에 태어나는 것은 한지 장판지 위에서 태어남을 말함이며, 그 속에서 산다는 것은 한지 벽지韓紙壁紙와 문창호지門窓戶紙에 싸여 생활하는 것을 말하는 것이다. 그것을 만진다는 것은 한지 위에 쓰여 지고 인쇄된 서책을 가까이하는 생활을 말하는 것이고 그것에 싸여 간다는 것은 죽음을 맞이하여 염습殮襲할 때 한지에 싸여 다시금 자연으로 돌아간다는 뜻이다.Our nation was born on Hanji from ancient times, lived and lived in it for the rest of its life, and eventually returned to the soil of nature wrapped in Hanji and receiving the warm affection of a mother's arms. Being born on hanji means being born on hanji linoleum, and living in it means living wrapped in hanji wallpaper and door paper. Touching it refers to a life of being close to a book written and printed on Korean paper, and being wrapped in it means to return to nature wrapped in Korean paper when you die and get wet.
과연 세계 어느 민족이 우리 민족처럼 방바닥에 장판지라는 노란 종이 카펫carpet을 깔고 불까지 때가며 한지로 옷을 입고 살아 본 적이 있었을까? 비바람 몰아치는 황야에 유둔지油芚紙로 군용 천막을 만들고, 전시戰時에는 갑의지甲衣紙로 화살을 막는 한지 갑옷을 만들어 입었다. 종이요강, 종이 신, 종이 우의, 종이 옷장, 종이 책장, 종이로 만든 촛대, 종이 수통을 만들어 사용하였고, 집안에 사소한 방문이나 창호 손잡이 근처에도 부분 손상을 막거나 운치를 더하기 위해 단풍잎, 댓잎 등을 넣고 그 위에 창호지를 덧발라 생활 속 모든 곳에서 한지를 사용하였다. 우리민족처럼 모든 생활용품을 한지로 만들어 쓴 민족은 인류 역사상 그 유례를 찾아보기 힘들 것이다.Has there ever been a time when any people in the world had a yellow paper carpet called linoleum spread on the floor of a room and even lit a fire and dressed in Hanji like our people? Military tents were made with Yudunji (油芚紙) in the rain and windy wilderness, and during wartime, Korean paper armor was made and worn to block arrows with Gapuiji (甲衣紙). Paper baskets, paper shoes, paper raincoats, paper closets, paper bookshelves, paper candlesticks, and paper canteens were made and used, and maple leaves and bamboo leaves were used to prevent partial damage or add flavor to small visits or window handles in the house. Korean paper was used everywhere in daily life by applying window paper over it. It would be difficult to find a precedent in human history for a nation that used Korean paper to make all daily necessities like ours.
닥나무 껍질은 섬유화해 대발로 물속에서 건져 햇빛을 이용해 말리면 자연이 우리에게 주는 한지가 된다. 전통 한지의 색은 그 자체가 자연이며 자연의 기본색이다. 이런 순수한 바탕색을 우리는 소색素色이라 부른다. 소색은 흰색이 아니라 자연에서 만들어진 순수한 바탕색이며 물체마다 지니고 있는 아무것도 가공되지 않은 자연의 색을 말하는 것이다. 한지를 만들 때 아무런 오염이나 인체에 해로운 물질을 첨가하지 않고 자연의 힘만을 이용하여 황갈색의 닥나무를 하얀 소색 한지로 만들어 낸다. 한지의 소색은 자연 자체의 산물이며 햇빛, 물, 바람, 불, 시간이라는 자연의 힘이 만들어낸 또 다른 자연의 색인 것이다. 한지의 모든 것은 자연 속에서 자연을 이용하여 만들어져 다시 자연 속으로 돌아간다.The bark of the paper mulberry tree is fibrous, taken out of the water on a drainboard, and dried in the sunlight to become Korean paper that nature gives us. The color of traditional Korean paper itself is natural and is the basic color of nature. We call such a pure background color the disappearing color. Discoloration is not white, but a pure background color made in nature, and refers to the color of nature that has not been processed into anything that each object has. When making Korean paper, no pollution or substances harmful to the human body are added, and only the power of nature is used to make yellowish-brown mulberry paper into white discolored Korean paper. The discoloration of Hanji is a product of nature itself and is another natural color created by the natural forces of sunlight, water, wind, fire, and time. Everything in Hanji is made in nature using nature and returns to nature again.
옛날에는 전통 한지를 백지百紙라고도 하였다. 한지를 만들 때, ‘닥나무를 베고, 찌고, 삶고, 말리고, 벗기고, 삶고, 두들기고, 고르게 섞고, 뜨고…’ 마무리 하는데 까지 백 번이라는 과정을 거쳐야만 한지가 만들어진다고 하여 백지百紙라고 한 것이다. 우리 전통한지 제작의 시작은 추수가 끝나고 찬바람이 불기 시작하는 11월에서 2월까지 닥나무를 베는 작업부터 시작 된다. 닥나무는 1년생 햇닥을 사용하는데, 햇닥은 섬유가 여리고 부드러워 종이뜨기에 좋기 때문이다. 닥나무 베는 작업이 끝나면 닥나무에서 종이의 원료가 되는 껍질을 벗기기 위해 닥솥에 닥나무를 채우고 증기가 새어나가지 않도록 밀폐한 후 불을 지펴 끓이는 닥무지라는 과정을 거치게 된다. 훈증과 열기가 가득한 닥솥에서 푹 쪄낸 닥나무는 껍질을 벗겨낸다. 벗겨낸 닥나무 껍질은 흑피 또는 피닥 이라고 하는데, 피닥을 다시 찬물에 담가 불린 후 닥칼을 이용해 겉껍질을 벗겨 백피를 만든다. 이렇게 얻은 백피를 햇볕에 널어 잘 말리면 전통한지의 기본 원료가 된다. 백피를 섬유로 만들기 위해서는 잿물에 삶아야 한다. 잿물은 짚, 메밀대, 콩대 등을 태운 재에 80도 정도의 따뜻한 물을 내려서 만든다. 이때 잿물은 변색을 일으키고 내구성을 떨어뜨리는 껍질 속의 불순물을 제거 해준다. 잿물에 네다섯 시간을 삶으면 백피보다 순수한 상태의 원료가 된다. 그 다음 잿물을 씻어내고 물속에서 햇볕을 쪼이는 과정을 거쳐 껍질에 있는 티를 골라내는 작업을 한다. 티가 적을수록 종이의 품질이 좋아지기 때문이다. 그런 다음 백피가 곤죽이 될 때까지 두드려 짧은 섬유질로 만드는 고해 작업을 하게 되는데, 이 과정이 끝나면 비로소 종이를 뜰 수 있는 원료가 완성된다. 그 다음 고해과정을 마친 닥 원료를 물에 넣고 힘차게 저어 섬유가 골고루 퍼지게 한 후, 황촉규 뿌리를 치대어 얻어낸 끈끈한 점액 닥풀을 첨가한다. 닥풀은 물이 흐르는 속도를 조절해 종이두께에 영향을 준다.In the past, traditional Korean paper was also called white paper. When making hanji, ‘paper mulberry is cut, steamed, boiled, dried, peeled, boiled, beaten, evenly mixed, steamed… ’ It is called blank paper because it is said that Hanji is made only after going through the process of 100 times until it is finished. Our traditional Korean paper production begins with the cutting of mulberry trees from November to February, when the harvest is over and the cold wind begins to blow. For the mulberry tree, one-year-old hetdak is used because it is good for making paper because the fiber is soft and soft. After cutting the mulberry tree, in order to peel the skin from the mulberry tree, which is the raw material for paper, the mulberry pot is filled with mulberry trees, sealed to prevent steam from escaping, and then heated and boiled. The bark of the mulberry tree is peeled off after being steamed in a mulberry pot full of fumigation and heat. The peeled mulberry bark is called millipede or pidak, and after soaking the mulberry in cold water again, it is soaked, and then peeled off the outer bark using a mulberry knife to make white skin. When the white skin obtained in this way is dried in the sun, it becomes a basic raw material for traditional Korean paper. To make white skin into fiber, it must be boiled in lye. Lye is made by pouring warm water of about 80 degrees into the ashes of burned straw, buckwheat stalks, and bean stalks. At this time, the lye removes impurities in the shell that cause discoloration and decrease durability. If you boil it in lye for four or five hours, it becomes a purer raw material than white skin. After that, the lye is washed off, and through the process of being exposed to the sun in the water, the work is done to pick out the tea in the skin. This is because the fewer the tees, the better the quality of the paper. Then, the white skin is beaten until it becomes a porridge and made into short fibers. After this process is over, the raw material for making paper is completed. Then, put the beaten mulberry raw material into water, stir vigorously to spread the fibers evenly, and then add the sticky mucus mulberry grass obtained by kneading the root of Hwang Chokgyu. The mulberry tree affects the thickness of the paper by controlling the speed at which the water flows.
우리나라의 장판지, 창호지 등 저피楮皮를 원료로 하여 만들어진 한지는 모두 강하다는 특징을 갖고 있다. 그래서 우수한 보존성을 지니고 있다. 종이는 인간의 보존 욕구가 만들어낸 대표 산물이기도 하다. 이러한 종이의 뛰어난 보존성을 잘 표현해준 말이 “지紙 천 년, 견絹 오백”이다. 둘째, 한지는 일찍이 부드럽고 자연스러우며 질긴 성질 덕분에 다양한 미술 재료로 사용되어왔다. 동양의 미술 재료는 서양의 미술 재료와는 달리 모두 친수성親水性을 가지고 있다. 특히 전통 한지는 물을 빨아들일 때 옆으로 번지기보다는 밑으로 잘 스며드는 특성이 있다. 또한 기름과도 잘 어울려져 기름을 사용한 종이가 있는데, 대표적인 것이 장판지이다. 장판지는 기름을 쓰되 식물성 수지 성분 기름을 사용하여 물은 투과시키지 않고 공기만을 투과시키는 장점이 있다. 셋째, 동양 고유의 품격을 지닌다는 것이다. 규격화된 서양 종이에 비해 우아한 아름다움을 갖는 한지는 크기를 갖되 일정한 크기를 갖지 않고 각 장마다 같으면서도 다른 모습을 하고 있다. 넷째, 한지는 섬유 사이에 적당한 공간을 가지고 있다. 창문에 바른 창호지는 외부 공간과 내부 공간을 잇는 틈을 유지함으로써 계절에 따라 민감하게 반응해 방 안 습도를 자동으로 조절하는 기능을 가지고 있다(문화재청 홈페이지 한지 소개).Korean hanji, such as linoleum and shoji paper, made with low skin as a raw material, has the characteristic of being strong. Therefore, it has excellent preservability. Paper is also a representative product created by human desire for preservation. A phrase that well expresses the excellent preservation of such paper is “a thousand years of paper, five hundred silk.” Second, Hanji has been used as a variety of art materials early on thanks to its soft, natural and tough properties. Unlike Western art materials, Eastern art materials are all hydrophilic. In particular, when traditional hanji absorbs water, it has the characteristic of permeating underneath rather than spreading to the side. In addition, there is paper that uses oil because it goes well with oil, and the representative one is linoleum. Floorboard uses oil, but it has the advantage of permeating only air without permeating water by using vegetable resin component oil. Third, it has the unique dignity of the East. Compared to standardized Western paper, Hanji, which has an elegant beauty, has a size but does not have a fixed size, and each sheet has the same yet different appearance. Fourth, Hanji has appropriate spaces between fibers. The shoji paper applied to the window has the function of automatically adjusting the humidity in the room by reacting sensitively to the season by maintaining a gap between the external and internal spaces (Introduction of Hanji on the website of the Cultural Heritage Administration).
상기와 같이 다양한 장점을 가지는 한지는 물을 빨아들이는 성질을 가지고 있어, 때가 탈 경우 이를 물로 닦아내기 어려운 문제점이 있고, 물을 흡수할 경우 변형되는 문제점이 있다.Hanji, which has various advantages as described above, has a property of absorbing water, so it is difficult to wipe it off with water when it is burned, and there is a problem that it is deformed when it absorbs water.
본 발명은 밀랍 코팅 종이 제조 방법 및 그를 이용하여 제작된 밀랍 코팅 종이 및 베개 커버를 제공하는 것을 목적으로 한다.An object of the present invention is to provide a method for producing beeswax-coated paper and a beeswax-coated paper and pillow cover produced using the same.
본 발명은, The present invention,
종이 준비 단계(S10), Paper preparation step (S10),
밀랍 용융 단계(S20), Beeswax melting step (S20),
제1 종이에 상기 S20 단계에서 용융된 밀랍을 도포하는 단계(S30), Applying the beeswax melted in step S20 to the first paper (S30);
상기 S30 단계에서 밀랍이 도포된 상기 제1 종이의 양면에 각각 제2 종이의 일면을 맞닿게 배치하는 단계(S40), Placing one side of the second paper in contact with both sides of the first paper to which the beeswax is applied in the step S30 (S40);
상기 제2 종이의 타면을 60℃ 이상의 온도로 압착하는 단계(S50), Pressing the other surface of the second paper at a temperature of 60 ° C. or higher (S50);
상기 제1 종이 양면에서 상기 제2 종이를 분리하는 단계(S60),Separating the second paper from both sides of the first paper (S60);
상기 S60 단계를 완료한 상기 제1 종이를 구기는 단계(S80),Crumpling the first paper after completing the step S60 (S80);
상기 S80 단계를 완료한 상기 제1 종이에 용융된 밀랍을 도포하는 단계(S90),Applying molten beeswax to the first paper upon completion of the step S80 (S90);
상기 S90 단계를 완료한 상기 제1종이의 양면에 각각 제3종이의 일면을 맞닿게 배치하는 단계(S100),Disposing one side of the third paper to be in contact with both sides of the first paper after the step S90 has been completed (S100);
상기 제3 종이의 타면을 60℃ 이상의 온도로 압착하는 단계(S110), Pressing the other side of the third paper at a temperature of 60 ° C. or higher (S110);
상기 제1 종이와 상기 제3 종이를 분리하는 단계(S120), 및 Separating the first paper and the third paper (S120), and
상기 S120 단계를 수행한 상기 제1 종이로 밀랍 코팅 종이를 완성하는 단계(S140)를 포함하는 밀랍 코팅 종이 제조 방법을 제공한다.Provides a method for manufacturing beeswax-coated paper comprising the step (S140) of completing beeswax-coated paper with the first paper having performed the step S120.
상기 제1 종이, 상기 제2 종이, 및 상기 제3 종이는 한지, 노루지, 크라프트지, 신문용지 중 선택된 어느 하나인 것을 특징으로 한다.The first paper, the second paper, and the third paper are characterized in that any one selected from hanji, norruji, kraft paper, and newsprint.
상기 S50 단계 또는 상기 제 110 단계에서 60℃ 내지 80℃ 에서 선택된 어느 하나의 온도의 열판으로 압착하는 것을 특징으로 한다.It is characterized in that the compression is performed with a hot plate at any one temperature selected from 60 ° C to 80 ° C in the step S50 or the step 110.
항기 S60 단계 또는 상기 S120 단계를 수행한 후, 상기 제1 종이를 60℃ 이상의 열판을 통과시키는 열처리 과정을 수행하는 것을 특징으로 한다.After performing the step S60 or the step S120, a heat treatment process of passing the first paper through a hot plate of 60 ° C. or higher is characterized in that it is performed.
한편, 본 발명의 실시예에 따른 밀랍 코팅 종이 제조 방법에 의해 제작된 밀랍 코팅 종이를 제공할 수 있다.On the other hand, it is possible to provide a beeswax-coated paper produced by the method for manufacturing beeswax-coated paper according to an embodiment of the present invention.
또한, 본 발명의 실시예에 따른 밀랍 코팅 종이 제조 방법에 의해 제작된 밀랍 코팅 종이로 제작된 베개커버, 의자 헤드레스트, 모자, 종이가방, 또는 우산 원단을 제공할 수 있다. In addition, pillow covers, chair headrests, hats, paper bags, or umbrella fabrics made of beeswax-coated paper produced by the method for manufacturing beeswax-coated paper according to an embodiment of the present invention can be provided.
상기와 같이 구성된 본 발명의 실시예에 따르면, 한지에 흡수 가능한 밀랍으로 코팅된 밀랍 코팅 종이를 제조할 수 있다.According to the embodiment of the present invention configured as described above, beeswax-coated paper coated with beeswax capable of being absorbed into Korean paper can be manufactured.
본 발명의 실시예에 따르면 밀랍 코팅 후에도 바스락 거리는 소리가 나지 않는 밀랍 코팅 종이 및 그를 이용한 밀랍 코팅 종이 베개를 제조할 수 있다.According to an embodiment of the present invention, it is possible to manufacture a beeswax-coated paper and a beeswax-coated paper pillow using the same that do not make a rustling sound even after being coated with beeswax.
도 1 은 본 발명의 실시예에 따른 밀랍 코팅 종이 제조 방법을 나타내는 흐름도이다.
도 2 는 밀랍으로 1차 코팅된 한지의 사진이다.
도 3 은 1차 코팅된 한지에 구김 공정을 실시한 사진이다.
도 4 는 본 발명의 실시예에 따른 밀랍 코팅 종이 제조 방법에 따라 제조된 밀랍 코팅 한지를 나타낸 사진이다.
도 5 는 본 발명의 실시예에 따른 밀랍 코팅 종이 베개 제조 방법에 따라 제조된 베개 커버를 나타낸 사진이다.
도 6 은 본 발명의 실시예에 따른 밀랍 코팅 종이 제조 방법을 적용하여 신문 용지로 제작한 밀랍 코팅 종이를 나타낸 사진이다.
도 7 은 본 발명의 실시예에 따른 밀랍 코팅 종이 제조 방법을 적용하여 크래프트지로 제작한 밀랍 코팅 종이를 나타낸 사진이다.1 is a flowchart showing a method for manufacturing beeswax-coated paper according to an embodiment of the present invention.
2 is a photograph of Korean paper first coated with beeswax.
3 is a photograph of a first-coated Korean paper subjected to a crumpling process.
4 is a photograph showing beeswax-coated Korean paper manufactured according to the method for manufacturing beeswax-coated paper according to an embodiment of the present invention.
5 is a photograph showing a pillow cover manufactured according to a method for manufacturing a beeswax-coated paper pillow according to an embodiment of the present invention.
6 is a photograph showing beeswax-coated paper made of newsprint by applying the method for manufacturing beeswax-coated paper according to an embodiment of the present invention.
7 is a photograph showing beeswax-coated paper made of kraft paper by applying the method for manufacturing beeswax-coated paper according to an embodiment of the present invention.
이하 본 발명에 따른 항균 방수 기능성 밀랍 종이 제조 방법에 대해 상세히 설명한다. 이때, 사용되는 기술 용어 및 과학 용어에 있어서 다른 정의가 없다면, 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명 및 첨부 도면에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 설명은 생략한다.Hereinafter, a method for manufacturing antibacterial and waterproof functional beeswax paper according to the present invention will be described in detail. At this time, unless there is another definition in the technical terms and scientific terms used, they have meanings commonly understood by those of ordinary skill in the art to which this invention belongs, and the gist of the present invention in the following description and accompanying drawings Descriptions of well-known functions and configurations that may be unnecessarily obscure are omitted.
본 발명은, 용융된 밀랍으로 종이를 균일하게 코팅하는 밀랍 코팅 종이를 제조하는 방법에 관한 것이다.The present invention relates to a method for producing beeswax-coated paper that uniformly coats the paper with molten beeswax.
도 1 은 본 발명의 실시예에 따른 밀랍 코팅 종이 제조 방법을 나타내는 흐름도이다. 도시되는 바와 같이, 본 발명의 실시예에 따른 밀랍 코팅 종이 제조 방법은 종이 준비 단계(S10), 밀랍 용융 단계(S20), 제1 종이에 상기 S20 단계에서 용융된 밀랍을 도포하는 단계(S30), 상기 S30 단계에서 밀랍이 도포된 상기 제1 종이의 양면에 제2 종이의 일면을 각각 맞닿게 배치하는 단계(S40), 상기 제2 종이의 타면을 60℃ 이상의 열판으로 압착하는 단계(S50), 상기 제1 종이와 상기 제2 종이를 분리하는 단계(S60), 상기 제1 종이를 열처리하는 단계(S70), 상기 S70 단계를 완료한 제1 종이를 구김 효과가 나도록 구기는 단계(S80), 상기 S80 단계를 완료한 상기 제1종이의 양면에 용융된 밀랍을 도포하는 단계(S90), 상기 S90 단계를 완료한 상기 제1 종이의 양면에 제3종이의 일면을 맞닿게 배치하는 단계(S100), 상기 제3종이의 타면을 60℃ 이상의 열판으로 압착하는 단계(S110), 상기 제1 종이와 상기 제3 종이를 분리하는 단계(S120), 상기 제1 종이를 열처리하는 단계(S130), 및 상기 제1 종이로 밀랍 코팅 종이를 완성하는 단계(S140)를 포함한다. 1 is a flowchart showing a method for manufacturing beeswax-coated paper according to an embodiment of the present invention. As shown, the method for manufacturing beeswax-coated paper according to an embodiment of the present invention includes a paper preparation step (S10), a beeswax melting step (S20), and applying the molten beeswax in the step S20 to the first paper (S30). , Placing one side of the second paper in contact with both sides of the first paper coated with beeswax in step S30 (S40), pressing the other side of the second paper with a hot plate at 60 ° C or higher (S50) , Separating the first paper from the second paper (S60), heat-treating the first paper (S70), and crumpling the first paper after completing the step S70 to have a creasing effect (S80) , applying molten beeswax to both sides of the first paper that has completed the step S80 (S90), placing one side of the third paper in contact with both sides of the first paper that has completed the step S90 ( S100), pressing the other side of the third paper with a hot plate at 60 ° C or higher (S110), separating the first paper and the third paper (S120), heat-treating the first paper (S130) , and completing a beeswax-coated paper with the first paper (S140).
종이 준비 단계(S10)에서, 한지, 색한지, 노루지, 크라프트지, 신문용지 중 하나를 채택할 수 있다. 종이는 식물의 섬유를 물에 풀어 평평하면서 얇게 서로 엉기도록하여 물을 빼고 말린 것을 말하는 데, 크게 한지(韓紙)와 양지(洋紙)로 나누며, 한지는 수록지(手질紙)와 기계지(機械紙)로, 양지는 종이(좁은 뜻의)와 판지(板紙)로 다시 나눈다. 양지의 주된 원료는 목재펄프이며, 한지는 닥·삼·마 등의 인피섬유(靭皮纖維)를 원료로 하여 사람의 힘으로 제조되었으나, 근래에 와서 목재펄프를 섞어서 기계를 사용하여 만들기도 한다. 따라서, 양지와 한지의 구별은 점차 애매하게 되어 가며, 제품의 외관으로 구별할 수밖에 없게 되었다. 양지의 종이는 섬유를 단층으로 조성하여 만들며, 판지는 지층을 여러 겹을 조성하여 물을 머금은 상태에서 압착함으로써 섬유가 서로 엉겨 붙도록 하여 만든다. 그러나 종이의 두꺼운 것과 판지를 외관상으로 정확하게 구별하기가 곤란한 경우가 얼마든지 있다. 종이의 두께는 g/㎡로 표시하는데, 이는 1×1m짜리를 저울에 달았을 때의 결과값을 말한다.(두산백과 두피디아, 두산백과) In the paper preparation step (S10), one of hanji, colored hanji, noruji, kraft paper, and newsprint may be adopted. Paper refers to a product made by dissolving plant fibers in water so that they are flat and thinly congealed, drained of water, and then dried.紙), and Yangji is further divided into paper (in a narrow sense) and cardboard (板紙). The main raw material of Yangji is wood pulp, and Hanji is made by human power using bast fibers such as mulberry, hemp, and hemp as a raw material, but in recent years, it is also made using machines by mixing wood pulp. Therefore, the distinction between Western paper and Korean paper has gradually become ambiguous, and there is no choice but to distinguish them by the appearance of the product. Yangji paper is made by composing fibers into a single layer, and cardboard is made by forming several layers of paper layers and pressing them in a water-soaked state so that the fibers stick together. However, there are many cases in which it is difficult to accurately distinguish between thick paper and cardboard by appearance. The thickness of paper is expressed in g/㎡, which is the result when a 1×1m piece is weighed on a scale. (Doosan Encyclopedia, Dupedia, Doosan Encyclopedia)
닥나무 한지는 닥나무를 잘라 찐 후에 껍질을 벗겨낸 후 다듬고 말려 백피를 준비하고, 백피를 물에 불려 솥에 넣어 잿물에 삶고, 삶은 후 표백하고, 방망이 등으로 두드려 섬유가 부드럽게 분산되도록 한 후, 닥풀(황촉규액)을 물에 넣고 섬유소를 풀어준 후 발로 떠서 말리면 닥나무 한지가 완성된다. 상기와 같이 제조된 한지 중 21g/㎡ 내지 55g/㎡ 규격의 한지를 사용하는 것이 바람직하다. 특히, 제1 종이로부터 밀랍을 흡수할 제2종이와 제3 종이는 21g/㎡ 이상의 두께를 가진 한지를 사용하는 것이 바람직하다. 제1, 제2, 및 제3 종이는 동일한 종류로 사용하는 것이 바람직하다. 제1, 제2, 및 제3 종이는 한지에 한정되지는 않는다. Paper mulberry Hanji is made by cutting the mulberry tree, steaming it, peeling it, trimming and drying it to prepare white skin, soaking the white skin in water, putting it in a pot, boiling it in lye, bleaching it after boiling, beating it with a bat so that the fibers are gently dispersed, and then mulberry paste ( Hwangchokgyuaek) is put in water, the fibers are released, and mulberry paper is completed by scooping it up with your feet and drying it. Among the Korean paper prepared as described above, it is preferable to use Korean paper having a standard of 21 g/m2 to 55 g/m2. In particular, it is preferable to use Korean paper having a thickness of 21 g/m 2 or more as the second paper and the third paper to absorb beeswax from the first paper. The first, second, and third papers are preferably of the same type. The first, second, and third papers are not limited to Korean paper.
상기 S20 단계에서 밀랍을 가열하여 용융하되, 60℃ 내지 80℃ 까지 가열하는 것이 바람직하다. 밀랍 (蜜蠟)은 일벌의 배 아래쪽에서 분비하는 노란색 천연 왁스이다. 일벌은 이것으로 꿀을 모으고, 알을 낳아두며, 벌집을 만든다. 밀랍은 벌집에서 가열압착법·용제추출법 등에 의해 채취하는 동물성 고체랍으로 주성분은 멜리실알코올의 팔미트산 에스터와 세로트산이다. 점착성이 있는 비결정성 물질로 화장품, 전기의 절연제, 마룻바닥의 도료, 양초 등의 원료로 사용된다. 밀납이라고도 하며, 주성분은 멜리실알코올의 팔미트산 에스터와 세로트산이고, 이 밖에 여러 가지 지방산·알코올 및 고급탄화수소 등이 함유되어 있다. 녹는점 62~63℃, 비중 0.961~0.973, 굴절률 1.456~1.459, 비누화값 86~93, 아이오딘값 8~14이다. 밀랍은 약간의 점착성이 있는 비결정성 물질이다.(두산백과 두피디아, 두산백과) In the step S20, the beeswax is heated and melted, but it is preferable to heat it to 60 ° C to 80 ° C. Beeswax (蜜蠟) is a yellow natural wax secreted from the lower abdomen of worker bees. Worker bees use it to collect nectar, lay eggs, and build beehives. Beeswax is animal solid wax collected from beehives by hot pressing and solvent extraction, and its main components are palmitic acid ester and cerotic acid of melissyl alcohol. It is an amorphous substance with adhesiveness and is used as a raw material for cosmetics, electrical insulation, floor paint, and candles. It is also called beeswax, and its main components are palmitic acid ester and cerotic acid of melissyl alcohol, and it also contains various fatty acids, alcohols, and higher hydrocarbons. Melting point 62~63℃, specific gravity 0.961~0.973, refractive index 1.456~1.459, saponification value 86~93, iodine value 8~14. Beeswax is an amorphous substance with some adhesive properties. (Doosan Baekwa Dupedia, Doosan Baekwa)
S20 단계에서 용융된 밀랍을 상기 제1 종이에 도포한다(S30). 제1 종이의 양면에 붓 롤러 등을 이용하여 도포하거나, 제1 종이를 용융된 밀랍에 침지시켜 도포할 수 있다. 즉, S20 단계에서 60℃ 내지 80℃의 스테인리스 욕조에 밀랍을 용융시키고 제1 종이를 투입해서 일면에 용융된 밀랍이 도포되도록 할 수 있다. The beeswax melted in step S20 is applied to the first paper (S30). It may be applied to both sides of the first paper using a brush roller or the like, or it may be applied by dipping the first paper into molten beeswax. That is, in step S20, beeswax may be melted in a stainless steel tub at 60° C. to 80° C., and a first paper may be introduced so that the melted beeswax is applied to one surface.
한지에 도포된 밀랍은 공기와 접촉하면 바로 굳는다. 한지에 완전히 스며들지 못한 밀랍 잔여량은 사용 시 사용자의 피부나 옷 등에 묻어나오고 두껍게 굳은 영역에서 건조되어 수시로 떨어지는 문제점이 있다. 도 2 는 밀랍으로 1차 코팅된 한지의 사진이다. 밀랍으로 1차 코팅된 종이는 방수 효과를 가지지만 단단히 굳어 뻣뻣하고 굳은 밀랍은 종이를 구부리거나 접으면 떨어질 수 있고, 결에 따라 찢어지기 용이한 문제점이 있다. The beeswax applied to Korean paper hardens as soon as it comes into contact with air. The remaining amount of beeswax that has not completely permeated into the Korean paper comes off the user's skin or clothes when used, and is dried in a thick hardened area and often falls off. 2 is a photograph of Korean paper first coated with beeswax. Paper coated primarily with beeswax has a waterproof effect, but stiff and hardened beeswax can fall off when the paper is bent or folded, and there is a problem that it is easy to tear along the texture.
이와 같은 밀랍이 도포된 제1 종이의 양면에 제2 종이를 배치한 그 다음 상기 제2 종이의 타면을 60℃ 이상으로 압착하는 S50 단계에서 밀랍이 제1 종이에 완전히 스며들고, 스며들지 못한 잔여량은 제2 종이에 스며들게 되어 상기와 같은 문제점을 해결할 수 있다. In step S50 of placing a second paper on both sides of the first paper coated with such beeswax and then pressing the other side of the second paper at 60° C. or higher, the beeswax completely permeates the first paper, and the remaining amount that is not permeated Silver permeates into the second paper to solve the above problems.
S50 단계에서 제2 종이의 타면을 60℃ 내지 80℃의 스테인리스 판으로 누르거나, 60℃ 내지 80℃의 금속 롤러로 제2 종이의 타면을 문질러 제1 종이에 스며들지 못한 밀랍이 제2 종이로 흡수되도록 한다. 제1 종이에 흡수되지 못한 밀랍이 제2종이로 흡수되므로 제1 종이에는 스며든 밀랍만 남게 되고, 나머지 밀랍이 흡수되지 못한 상태에서 굳은 후 접촉 시 떨어지거나 피부에 묻는 현상이 발생하는 것을 방지할 수 있게 된다.In step S50, the other side of the second paper is pressed with a stainless steel plate at 60 ° C to 80 ° C, or the other side of the second paper is rubbed with a metal roller at 60 ° C to 80 ° C so that the beeswax that has not penetrated into the first paper is transferred to the second paper. to be absorbed. Since the beeswax that was not absorbed in the first paper is absorbed into the second paper, only the soaked wax remains in the first paper, and after the remaining wax is hardened in a state where it is not absorbed, it is possible to prevent the occurrence of falling off when in contact or sticking to the skin. be able to
그 다음 상기 제1 종이에서 제2 종이를 분리하고(S60), S60 단계를 완료한 제 1 종이를 열판 위를 통시키는 열처리를 수행한다(S70). 제1 종이를 60℃ 내지 80℃의 스테인리스 판 3cm 이격된 위치를 통과시켜 열처리되도록 한다. 열처리 단계(S70)를 거칠 경우 종이에서 바스락 거리는 소리가 잡혀 베개 커버나 헤드레스트 커버로 사용하기에 좋다. Then, the second paper is separated from the first paper (S60), and heat treatment is performed by passing the first paper over a hot plate after completing the step S60 (S70). The first paper is heat treated by passing it through a stainless steel plate at 60° C. to 80° C. at a distance of 3 cm. When going through the heat treatment step (S70), the sound of rustling paper is caught and it is good to use it as a pillow cover or a headrest cover.
열처리 완료 후 제1 종이를 구겨 밀랍이 흡수된 제1 종이가 구김 효과 기법을 나타내게 된다(S70). 구김 효과 기법은 종이나 천에 일부러 구김을 만들어서 질감을 표현하는 기법으로 패션 디자인이나 직물 디자인 표현 기법의 하나이다. 도 3은 구김 공정을 종료한 종이를 나타낸다. 구김을 통해 밀랍의 찬성질이 없어지고 주름 사이 사이에 공기순환이나 부드러움을 더해주게 되고, 완제품 사용 시 구김이나 주름이 발생하는 문제점을 예방할 수 있게 된다.After the heat treatment is completed, the first paper is crumpled and the first paper absorbs the beeswax to show the crumpling effect technique (S70). The crease effect technique is a technique to express texture by deliberately creating wrinkles on paper or cloth, and is one of the techniques for expressing fashion design or textile design. 3 shows the paper after the crumpling process is completed. Through wrinkles, the positive quality of beeswax is lost, air circulation or softness is added between wrinkles, and the problem of wrinkles or wrinkles occurring when using the finished product can be prevented.
상기 S80 단계를 완료한 구김 효과 기법을 나타낸 1차 밀랍 코팅된 제1 종이의 양면에 용융된 밀랍을 도포하여 2차 밀랍 코팅을 수행한다(S90). S30 단계와 마찬가지로 붓이나 롤러를 사용하거나 밀랍 욕조에 침지하여 종이 양면에 밀랍이 도포되도록 한다. S90 단계를 완료한 제1 종이 양면에 제3 종이의 일면을 각각 맞닿게 배치하고(S100), 제3 종이의 타면을 60℃ 이상의 온도로 각각 압착하여 잔여 밀랍이 흡수되도록 한 후(S110), 제3 종이를 분리한다(S120). S110 공정은 S50 과 같이 60℃ 이상의 롤러 또는 60℃ 이상의 열판으로 제3 종이의 타면을 각각 압착하여 잔여 밀랍을 흡수시키는 공정이다. 2차 밀랍 코팅과 흡수 공정을 통해 주름 사이사이에 밀랍이 흡수되어 부드러우면서 종이를 질기게 만들어준다. A second beeswax coating is performed by applying molten beeswax to both sides of the first first beeswax-coated paper showing the wrinkle effect technique after completing the step S80 (S90). As in step S30, beeswax is applied to both sides of the paper by using a brush or roller or immersing in a beeswax bath. One side of the third paper is placed in contact with both sides of the first paper that has completed step S90 (S100), and the other side of the third paper is pressed at a temperature of 60 ° C or higher to absorb the remaining beeswax (S110), Separate the third paper (S120). Step S110 is a step of absorbing residual beeswax by compressing the other side of the third paper with a roller at 60° C. or higher or a hot plate at 60° C. or higher, as in S50. Through the secondary beeswax coating and absorption process, the beeswax is absorbed between the wrinkles, making the paper soft and tough.
2차 밀랍 코팅 흡수를 완료한 후 2차 열처리 공정을 수행한다. 2차 열처리 공정(S130)은 S70 1차 열처리 공정과 같이 열판 상을 제1 종이를 통과시켜 열처리 되도록 한다. 2차 열처리 공정을 통해 종이의 바스락 거리는 소리를 잡게 된다. 열처리 공정 후 제1 종이로 밀랍 코팅 종이를 완성한다(S140). After completing the absorption of the secondary beeswax coating, a secondary heat treatment process is performed. In the second heat treatment process (S130), the first paper is passed through the hot plate to be heat treated, like the first heat treatment process in S70. Through the secondary heat treatment process, the rustling sound of the paper is captured. After the heat treatment process, the wax-coated paper is completed with the first paper (S140).
도 4 는 완성된 밀랍 코팅 종이를 나타내는 사진이다. 1차 코팅 후 구김 공정을 수행한 다음 2차 코팅을 수행할 경우 구겨져 빈 공간에 밀랍이 투입되어 찢어지지 않고 부드러우며 바스락 거리는 소리가 나지 않는 밀랍 코팅 종이가 완성된다. 완성된 밀랍 코팅 종이는 세척도 가능하게 된다. 구김과 2차 밀랍 코팅과 열처리에 의해 완성된 밀랍 코팅 종이에서 밀랍의 찬성질을 빼주고 부드러움을 가지도록 한다.4 is a photograph showing the finished beeswax-coated paper. When the second coating is performed after the first coating and then the crumpling process, beeswax is injected into the crumpled empty space to complete beeswax-coated paper that is soft without tearing and does not make a rustling sound. The finished beeswax-coated paper can also be washed. The beeswax-coated paper, which is completed by wrinkles, secondary beeswax coating, and heat treatment, subtracts the favorable quality of beeswax and has softness.
상기와 같이 구성된 본 발명의 실시예에 따른 밀랍 코팅 종이는 밀랍으로 코팅되어 방수성을 확보하고, 광택을 가지며 프로폴리스를 포함하여 항균성을 지니게 된다. 밀랍의 특성을 이용할 수 있으면서도 부드럽고 찢어지지 않으며 방수성과 항균성 및 좋은 향기를 가지게된 본 발명의 실시예에 따라 제조된 밀랍 코팅 종이는 도 5에 도시되는 바와 같은 베개 커버로 활용될 수 있고, 벽지, 신발깔창, 마스크, 종이접기, 버스 기차 비행기 좌석의 헤드 레스트 커버 등으로 활용될 수 있다.The beeswax-coated paper according to the embodiment of the present invention configured as described above is coated with beeswax to ensure waterproofness, gloss, and antibacterial properties by including propolis. The beeswax-coated paper manufactured according to the embodiment of the present invention, which can use the characteristics of beeswax, is soft, does not tear, has waterproofness, antibacterial properties and good fragrance, and can be used as a pillow cover as shown in FIG. 5, wallpaper, It can be used as shoe insoles, masks, origami, and headrest covers for buses, trains, and airplane seats.
베개 커버는 직사각형 밀랍 코팅 종이 2장의 가장자리에 접착제를 도포하여 접착하여 밀랍 코팅 종이 사이에 공간이 형성되도록 하여 제작할 수 있다. 밀랍 베개는 상기 공간에 쿠션재를 투입하여 제작할 수 있다. 2차 코팅된 밀랍 코팅 종이로 베개 커버를 제작할 경우 물로 세척이 가능하기 때문에 취침 중에 탈락되는 신체 분비물 들을 제거하여 다회용으로 사용할 수 있게 된다. 특히 한지를 이용하여 본 발명의 실시예에 따른 밀랍 코팅 종이 제조 방법을 이용하여 밀랍 코팅을 수행할 경우 천 대용으로 사용이 가능하게 된다. 부드럽고 질기며 쉽게 찢어지지 않게 된다.The pillow cover can be manufactured by applying an adhesive to the edges of two rectangular beeswax-coated papers and bonding them so that a space is formed between the beeswax-coated papers. A beeswax pillow can be manufactured by injecting a cushioning material into the space. When the pillow cover is made of beeswax-coated paper with a secondary coating, it can be washed with water, so it can be used multiple times by removing body secretions that fall off during sleep. In particular, when wax coating is performed using the method for manufacturing wax-coated paper according to an embodiment of the present invention using Korean paper, it can be used as a substitute for cloth. It is soft, tough, and does not tear easily.
창호지를 이용하여 밀랍 코팅 종이를 제작한 후, 문이나 창문을 바르는 데 밀랍 코팅 종이를 사용할 수 있다. 본 발명의 실시예에 따른 창호지 밀랍 코팅 종이를 사용할 경우 방수 방습이 가능하여 습한 날씨나 우기에도 비에 젖어 흘러니리지 않고 쉽게 찢어지지 않고 말리기만 하면 원상 복구가 가능해지는 장점이 있다.After making beeswax-coated paper using window paper, the beeswax-coated paper can be used to apply doors or windows. When using the beeswax-coated paper according to the embodiment of the present invention, it is waterproof and moisture-proof, so it does not flow wet from rain even in humid or rainy season, does not tear easily, and can be restored to its original state only by drying.
도 6은 신문 용지를 이용하여 제작된 밀랍 코팅 종이를 나타낸다. 신문 용지의 경우 1차 코팅 전에 구김 공정을 수행 한 후 도 1의 밀랍 코팅 종이 제조 방법의 흐름을 수행하는 것이 바람직하다. 신문 용지를 사용할 경우 재활용에 도움이 되는 장점이 있다.6 shows beeswax-coated paper produced using newsprint. In the case of newsprint, it is preferable to carry out the flow of the wax-coated paper manufacturing method of FIG. 1 after performing the crumpling process before the first coating. The advantage of using newsprint is that it helps in recycling.
도 7은 크래프트지를 이용하여 제작된 밀랍 코팅 종이를 나타낸다. 크래프트지 밀랍 코팅 종이는 한지보다 질기고 딱딱하여 보드판, 우산원단, 모자, 가방 등에 활용할 수 있다.7 shows beeswax-coated paper produced using kraft paper. Kraft paper, beeswax-coated paper is tougher and harder than Korean paper, so it can be used for board boards, umbrella fabric, hats, and bags.
Claims (5)
밀랍 용융 단계(S20),
제1 종이에 상기 S20 단계에서 용융된 밀랍을 도포하는 단계(S30),
상기 S30 단계에서 밀랍이 도포된 상기 제1 종이의 양면에 각각 제2 종이의 일면을 맞닿게 배치하는 단계(S40),
상기 제2 종이의 타면을 60℃ 이상의 온도로 압착하는 단계(S50),
상기 제1 종이 양면에서 상기 제2 종이를 분리하는 단계(S60),
상기 S60 단계를 완료한 상기 제1 종이를 구기는 단계(S80),
상기 S80 단계를 완료한 상기 제1 종이에 용융된 밀랍을 도포하는 단계(S90),
상기 S90 단계를 완료한 상기 제1종이의 양면에 각각 제3종이의 일면을 맞닿게 배치하는 단계(S100),
상기 제3 종이의 타면을 60℃ 이상의 온도로 압착하는 단계(S110),
상기 제1 종이와 상기 제3 종이를 분리하는 단계(S120), 및
상기 S120 단계를 수행한 상기 제1 종이로 밀랍 코팅 종이를 완성하는 단계(S140)를 포함하는 밀랍 코팅 종이 제조 방법.Paper preparation step (S10),
Beeswax melting step (S20),
Applying the beeswax melted in step S20 to the first paper (S30);
Placing one side of the second paper in contact with both sides of the first paper to which the beeswax is applied in the step S30 (S40);
Pressing the other surface of the second paper at a temperature of 60 ° C. or higher (S50);
Separating the second paper from both sides of the first paper (S60);
Crumpling the first paper after completing the step S60 (S80);
Applying molten beeswax to the first paper upon completion of the step S80 (S90);
Disposing one side of the third paper to be in contact with both sides of the first paper after the step S90 has been completed (S100);
Pressing the other side of the third paper at a temperature of 60 ° C. or higher (S110);
Separating the first paper and the third paper (S120), and
A method of manufacturing beeswax-coated paper comprising the step (S140) of completing a beeswax-coated paper with the first paper having performed the step S120.
상기 제1 종이, 상기 제2 종이, 및 상기 제3 종이는 한지, 색한지, 노루지, 크라프트지, 신문용지 중 선택된 어느 하나인 것을 특징으로 하는 밀랍 코팅 종이 제조 방법.According to claim 1,
The first paper, the second paper, and the third paper are beeswax-coated paper manufacturing method, characterized in that any one selected from hanji, colored hanji, noruji, kraft paper, newsprint.
상기 S20 단계에서 60℃ 내지 80℃ 의 온도로 용융시키고,
상기 S50 및 S100단계에서 60℃ 내지 80℃ 로 압착하는 것을 특징으로 하는 밀랍 코팅 종이 제조 방법.According to claim 1,
Melting at a temperature of 60 ℃ to 80 ℃ in the step S20,
A method for producing beeswax-coated paper, characterized in that the pressing at 60 ℃ to 80 ℃ in the steps S50 and S100.