KR102421804B1 - Pre-lithiation method for negative electrode of lithium secondary battery, and lithium metal for pre-lithiation for negative electrode of lithium secondary battery - Google Patents
Pre-lithiation method for negative electrode of lithium secondary battery, and lithium metal for pre-lithiation for negative electrode of lithium secondary battery Download PDFInfo
- Publication number
- KR102421804B1 KR102421804B1 KR1020170134135A KR20170134135A KR102421804B1 KR 102421804 B1 KR102421804 B1 KR 102421804B1 KR 1020170134135 A KR1020170134135 A KR 1020170134135A KR 20170134135 A KR20170134135 A KR 20170134135A KR 102421804 B1 KR102421804 B1 KR 102421804B1
- Authority
- KR
- South Korea
- Prior art keywords
- negative electrode
- lithium metal
- lithium
- secondary battery
- lithiation
- Prior art date
Abstract
본 발명은 리튬 이차전지용 음극과 리튬 금속을 접촉시켜 상기 리튬 금속으로부터 상기 음극에 리튬을 공급하는 과정을 포함하고, 상기 리튬 금속은 복수개의 관통홀을 포함하는 리튬 금속판이고, 상기 전리튬화를 통해 상기 음극에서 발생되는 가스는 상기 관통홀을 통해 배출되는 리튬 이차전지용 음극의 전리튬화 방법, 및 이에 사용되는 리튬 이차전지용 음극의 전리튬화용 리튬 금속에 관한 것이다.The present invention includes a process of supplying lithium from the lithium metal to the negative electrode by contacting a negative electrode for a lithium secondary battery with a lithium metal, wherein the lithium metal is a lithium metal plate including a plurality of through holes, and through the prelithiation The gas generated from the negative electrode relates to a method of pre-lithiation of an anode for a lithium secondary battery discharged through the through hole, and a lithium metal for pre-lithiation of a negative electrode for a lithium secondary battery used therein.
Description
본 발명은 리튬 이차전지용 음극의 전리튬화 방법 및 리튬 이차전지용 음극의 전리튬화용 리튬 금속에 관한 것이다.The present invention relates to a method for pre-lithiation of a negative electrode for a lithium secondary battery and a lithium metal for pre-lithiation of a negative electrode for a lithium secondary battery.
모바일 기기에 대한 기술 개발과 수요가 증가함에 따라 에너지원으로서의 이차전지에 대한 수요가 급격히 증가하고 있고, 그러한 이차전지 중에서도 높은 에너지 밀도와 작동 전위를 나타내고, 사이클 수명이 길며, 자기방전율이 낮은 리튬 이차전지가 상용화되어 널리 사용되고 있다.As technology development and demand for mobile devices increase, the demand for secondary batteries as an energy source is rapidly increasing, and among such secondary batteries, lithium secondary batteries exhibiting high energy density and operating potential, long cycle life, and low self-discharge rate. Batteries have been commercialized and widely used.
한편, 리튬 이차 전지의 양극을 구성하는 양극 활물질로서는 LiCoO2, LiMnO2, LiMn2O4 또는 LiCrO2와 같은 금속 산화물이 이용되고 있으며, 음극을 구성하는 음극 활물질로서는 금속 리튬(metal lithium), 흑연(graphite) 또는 활성탄(activated carbon) 등의 탄소계 물질(carbon based meterial), 또는 산화실리콘(SiOx) 등의 물질이 사용되고 있다. 상기 음극 활물질 중에서도 초기에는 금속 리튬이 주로 사용되었으나 충전 및 방전 사이클이 진행됨에 따라 금속 리튬 표면에 리튬 원자가 성장하여 분리막을 손상시켜 전지를 파손시키는 현상이 발생하여 최근에는 탄소계 물질이 주로 사용되고 있다. 그러나, 탄소계 물질의 경우 이론 용량이 약 400 mAh/g에 불과하여 용량이 작다는 단점을 지니고 있어, 음극 활물질로서 높은 이론 용량(4,200 mAh/g)을 가지는 실리콘(silicon, Si)을 이용하여 상기 탄소계 물질을 대체하려는 다양한 연구가 진행되어 왔다.On the other hand, a metal oxide such as LiCoO 2 , LiMnO 2 , LiMn 2 O 4 or LiCrO 2 is used as a positive active material constituting the positive electrode of a lithium secondary battery, and as a negative active material constituting the negative electrode, metal lithium, graphite (Graphite) or a carbon-based material such as activated carbon (activated carbon), or a material such as silicon oxide (SiO x ) is used. Among the anode active materials, metallic lithium was mainly used in the beginning, but as the charging and discharging cycle proceeds, lithium atoms grow on the surface of metallic lithium to damage the separator and damage the battery. Recently, carbon-based materials are mainly used. However, in the case of a carbon-based material, since the theoretical capacity is only about 400 mAh/g, it has a disadvantage that the capacity is small. Various studies have been conducted to replace the carbon-based material.
상기 리튬 이차전지는 양극의 양극 활물질의 리튬 이온이 음극의 음극활물질로 삽입(intercadlation)되고 탈리(deintercalation)되는 과정을 반복하면서 충방전이 진행된다. The lithium secondary battery is charged and discharged while repeating the process in which lithium ions of the positive active material of the positive electrode are intercalated into the negative active material of the negative electrode and deintercalated.
이론적으로는 음극 활물질 내로의 리튬 삽입 및 탈리 반응이 완전히 가역적이지만, 실제로는 음극 활물질의 이론 용량보다 더 많은 리튬이 소모되며, 이중 일부만이 방전시 회수된다. 따라서, 두번째 사이클 이후에는 보다 적은 양의 리튬 이온이 충전시 삽입되게 되나 방전시에는 삽입된 거의 대부분의 리튬 이온이 탈리된다. 이와 같이 첫번째 충전 및 방전 반응에서 나타나는 용량의 차이를 비가역 용량 손실이라 하며, 상용화된 리튬 이차전지에서는 리튬 이온이 양극에서 공급되고 음극에는 리튬이 없는 상태로 제조되므로, 초기 충전 및 방전에서 비가역 용량 손실을 최소화하는 것이 중요하다. Theoretically, lithium intercalation and desorption reactions into the negative active material are completely reversible, but in practice, more lithium than the theoretical capacity of the negative active material is consumed, and only a part of it is recovered during discharge. Accordingly, after the second cycle, a smaller amount of lithium ions are inserted during charging, but most of the inserted lithium ions are desorbed during discharging. As described above, the difference in capacity that appears in the first charge and discharge reaction is called irreversible capacity loss. In commercial lithium secondary batteries, lithium ions are supplied from the positive electrode and lithium is not present in the negative electrode. It is important to minimize
이러한 초기 비가역 용량 손실은 대부분 음극 활물질 표면에서의 전해질 분해(electrolyte decomposition) 반응에 기인하는 것으로 알려져 있으며, 상기 전해질 분해를 통한 전기화학 반응에 의해 음극 활물질 표면 위에 SEI막(고체 전해질막, Solid Electrolyte Interface)이 형성된다. 이러한 SEI 막 형성에는 많은 리튬 이온이 소모되기 때문에 비가역 용량 손실을 유발시키는 문제점이 있지만, 충전 초기에 형성된 SEI 막은 충방전 중 리튬 이온과 음극 또는 다른 물질과의 반응을 막아주며, 이온 터널(Ion Tunnel)의 역할을 수행하여 리튬 이온만을 통과시키는 기능을 하므로 더 이상의 전해질 분해반응을 억제하여 리튬 이차전지의 사이클 특성 향상에 기여한다. It is known that this initial irreversible capacity loss is mostly due to an electrolyte decomposition reaction on the surface of the anode active material, and an SEI film (solid electrolyte membrane, Solid Electrolyte Interface) on the surface of the anode active material by an electrochemical reaction through the electrolyte decomposition. ) is formed. Since many lithium ions are consumed in the formation of the SEI film, there is a problem of causing irreversible capacity loss. ), which allows only lithium ions to pass through, thereby suppressing further electrolyte decomposition reactions and contributing to the improvement of cycle characteristics of lithium secondary batteries.
따라서, 상기 SEI 막의 형성 등으로 유발되는 초기 비가역을 개선하기 위한 방법이 필요하며, 그 한가지 방법으로서 리튬 이차전지 제작 전에 전 리튬화(pre-lithiation)를 실시하여 첫번째 충전시 발생되는 부반응을 미리 겪게 하는 방법을 들 수 있다. 이와 같이, 전 리튬화(pre-lithiation)를 실시할 경우, 실제 제조된 이차전지에 대해 충방전을 실시했을 때 그만큼 비가역이 감소된 상태에서 첫번째 사이클이 진행되어 초기 비가역이 감소될 수 있는 장점이 있다. Therefore, there is a need for a method for improving the initial irreversibility caused by the formation of the SEI film, etc., and as one of the methods, pre-lithiation is performed before manufacturing a lithium secondary battery to undergo a side reaction that occurs during the first charge. how to do it As such, when pre-lithiation is performed, the first cycle proceeds in a state in which irreversibility is reduced as much as when charging and discharging of the actually manufactured secondary battery is performed, which has the advantage that the initial irreversibility can be reduced. have.
음극의 전리튬화 방법으로는 예컨대 음극 표면에 리튬을 증착한 후, 전지를 조립하여 전해액을 주액함으로써 웨팅(wetting) 공정에서 리튬화를 시키는 방법, 및 음극을 전해액에 침지하여 웨팅 시킨 후, 음극과 리튬을 직접 접촉시키는 방법을 들 수 있다. 이 중, 음극을 전해액에 침지하여 웨팅 시킨 후, 음극과 리튬을 직접 접촉시키는 방법의 경우, 전리튬화시 리튬금속과 음극의 접촉면에서 전해액의 부반응이 발생하여 가스가 발생하게 되며, 발생된 가스가 리튬금속과 음극 사이에서 빠져나가지 못하면서 접촉을 저하시켜 전리튬화를 방해하게 된다.As a method of pre-lithiation of the negative electrode, for example, after depositing lithium on the surface of the negative electrode, assembling a battery and injecting an electrolyte to lithiate in a wetting process, the negative electrode is wetted by immersing the negative electrode in the electrolyte and a method of directly bringing lithium into contact. Among these, in the case of the method of directly contacting the negative electrode and lithium after wetting the negative electrode in the electrolyte, a side reaction of the electrolyte occurs at the contact surface of the lithium metal and the negative electrode during pre-lithiation to generate gas, As lithium metal cannot escape between the lithium metal and the negative electrode, the contact is lowered, preventing prelithiation.
이에 따라, 보다 효과적인 전 리튬화가 이루어질 수 있는 새로운 리튬 이차전지용 음극의 전리튬화 방법의 개발이 요구된다.Accordingly, there is a need to develop a new method for pre-lithiation of a negative electrode for a lithium secondary battery capable of more effective pre-lithiation.
본 발명의 해결하고자 하는 과제는 전리튬화시 전해액의 부반응에 따라 발생하는 가스를 효과적으로 제거하여 균일한 전리튬화가 이루어질 수 있는 리튬 이차전지용 음극의 전리튬화 방법을 제공하는 것이다. An object of the present invention is to provide a method for pre-lithiation of a negative electrode for a lithium secondary battery in which uniform pre-lithiation can be achieved by effectively removing a gas generated according to a side reaction of an electrolyte during pre-lithiation.
본 발명의 다른 해결하고자 하는 과제는 상기 리튬 이차전지용 음극의 전리튬화에서 사용될 수 있는 리튬 이차전지용 음극의 전리튬화용 리튬 금속을 제공하는 것이다.Another object of the present invention to be solved is to provide a lithium metal for pre-lithiation of a negative electrode for a lithium secondary battery that can be used in the pre-lithiation of the negative electrode for a lithium secondary battery.
상기 과제를 해결하기 위하여, 본 발명은 In order to solve the above problems, the present invention
리튬 이차전지용 음극과 리튬 금속을 접촉시켜 상기 리튬 금속으로부터 상기 음극에 리튬을 공급하는 과정을 포함하는, 리튬 이차전지용 음극의 전리튬화 방법으로서, 상기 리튬 금속은 복수개의 관통홀을 포함하는 리튬 금속판이고, 상기 전리튬화를 통해 상기 음극에서 발생되는 가스는 상기 관통홀을 통해 배출되는, 리튬 이차전지용 음극의 전리튬화 방법을 제공한다. A method of prelithiation of a negative electrode for a lithium secondary battery, comprising the step of supplying lithium from the lithium metal to the negative electrode by contacting the negative electrode for a lithium secondary battery with lithium metal, wherein the lithium metal includes a plurality of through holes. and, the gas generated from the negative electrode through the pre-lithiation is discharged through the through hole, and provides a method for pre-lithiation of the negative electrode for a lithium secondary battery.
또한, 본 발명은 상기 또 다른 과제를 해결하기 위하여, 리튬 이차전지용 음극과 리튬 금속을 접촉시켜 상기 음극을 전리튬화하기 위한 리튬 금속으로서, 상기 리튬 금속은 복수개의 관통홀을 포함하는 리튬 금속판인, 리튬 이차전지용 음극의 전리튬화용 리튬 금속을 제공한다.In addition, the present invention is a lithium metal for prelithiation of the negative electrode by contacting a negative electrode for a lithium secondary battery and a lithium metal in order to solve the another problem, wherein the lithium metal is a lithium metal plate including a plurality of through holes. , to provide a lithium metal for all-lithiation of an anode for a lithium secondary battery.
본 발명에 따른 리튬 이차전지용 음극의 전리튬화 방법은 전리튬화시 리튬금속과 음극의 접촉면에서 전해액의 부반응에 따라 발생하는 가스를 효과적으로 제거하여 음극에 균일하게 전리튬화가 이루어질 수 있다.The method for pre-lithiation of a negative electrode for a lithium secondary battery according to the present invention effectively removes a gas generated according to a side reaction of the electrolyte at the contact surface of the lithium metal and the negative electrode during pre-lithiation, so that the negative electrode can be uniformly pre-lithiated.
도 1은 본 발명의 일례에 따른 리튬 이차전지용 음극의 전리튬화용 리튬 금속의 개략적인 정면도이다.
도 2는 실시예 1 및 비교예 1에서 전리튬화가 이루어진 후의 음극 표면을 나타낸 사진이다.
도 3 및 4는 본 발명의 일례에 따른 복수개의 오목부를 포함하는 음극 활물질층을 포함하는 음극의 개략적인 정면도(a) 및 단면의 측면도(b)이다. 1 is a schematic front view of a lithium metal for pre-lithiation of a negative electrode for a lithium secondary battery according to an example of the present invention.
FIG. 2 is a photograph showing the surface of the anode after prelithiation in Example 1 and Comparative Example 1. FIG.
3 and 4 are schematic front views (a) and cross-sectional side views (b) of a negative electrode including a negative active material layer including a plurality of concave portions according to an example of the present invention.
이하, 본 발명에 대한 이해를 돕기 위해 본 발명을 더욱 상세하게 설명한다.Hereinafter, the present invention will be described in more detail to help the understanding of the present invention.
본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.The terms or words used in the present specification and claims should not be construed as being limited to their ordinary or dictionary meanings, and the inventor may properly define the concept of the term in order to best describe his invention. Based on the principle that there is, it should be interpreted as meaning and concept consistent with the technical idea of the present invention.
본 발명에 따른 리튬 이차전지용 음극의 전리튬화 방법은 리튬 이차전지용 음극과 리튬 금속을 접촉시켜 상기 리튬 금속으로부터 상기 음극에 리튬을 공급하는 과정을 포함하는 것으로, 상기 리튬 금속은 복수개의 관통홀을 포함하는 리튬 금속판이고, 상기 전리튬화를 통해 상기 음극에서 발생되는 가스는 상기 관통홀을 통해 배출된다. The method for prelithiation of a negative electrode for a lithium secondary battery according to the present invention includes the step of supplying lithium from the lithium metal to the negative electrode by contacting the negative electrode for a lithium secondary battery with a lithium metal, wherein the lithium metal has a plurality of through holes. a lithium metal plate including, and the gas generated from the negative electrode through the prelithiation is discharged through the through hole.
본 발명에 일례에 따른 리튬 이차전지용 음극의 전리튬화 방법은 리튬 이차전지용 음극과 리튬 금속을 접촉시켜 상기 리튬 금속으로부터 상기 음극에 리튬을 공급하는 과정을 포함하며, 이때 상기 음극은 상기 리튬 금속과의 접촉전에 전해액에 침지시켜 웨팅(wetting)된 것일 수 있다. 상기 음극은 음극 집전체 및 상기 음극 집전체 상에 형성된 음극 활물질층을 포함하는 것일 수 있고, 상기 음극을 전해액에 웨팅시킨 후, 상기 음극을 리튬 금속과 접촉시킬 경우, 상기 리튬 금속에 포함된 리튬이 상기 음극의 음극 활물질층에 확산되어 포함됨으로써 전리튬화(pre-lithiation)가 이루어질 수 있다. The method of prelithiation of a negative electrode for a lithium secondary battery according to an example of the present invention includes a step of supplying lithium from the lithium metal to the negative electrode by contacting the negative electrode for a lithium secondary battery with a lithium metal, wherein the negative electrode is the lithium metal and It may be wetted by being immersed in an electrolyte before contacting. The negative electrode may include a negative electrode current collector and a negative electrode active material layer formed on the negative electrode current collector, and after wetting the negative electrode in an electrolyte solution, when the negative electrode is brought into contact with lithium metal, lithium contained in the lithium metal Pre-lithiation may be achieved by being diffused and included in the anode active material layer of the anode.
상기 리튬 이차전지용 음극과 리튬 금속을 접촉시키는 과정은 상기 리튬 금속을 상기 음극과 서로 대면하여 밀착시키는 과정을 통해 이루어질 수 있다. 이를 위해 상기 리튬 금속은 평면 상의 리튬 금속판으로 이루어질 수 있다. 상기 리튬 금속판은 상기 음극과 동일하거나 약간 더 큰 면적을 가질 수 있으며, 두께는 상기 음극의 비가역을 보충할 수 있는 양의 리튬을 포함할 수 있는 두께이면 특별히 한정되지 않고 적절히 조절될 수 있다. The process of contacting the negative electrode for a lithium secondary battery with the lithium metal may be performed through a process of bringing the lithium metal into close contact with the negative electrode to face each other. To this end, the lithium metal may be formed of a flat lithium metal plate. The lithium metal plate may have the same or slightly larger area as the negative electrode, and the thickness is not particularly limited as long as it can contain an amount of lithium capable of supplementing the irreversibility of the negative electrode, and may be appropriately adjusted.
상기 리튬 금속은 복수개의 관통홀을 포함하며, 상기 리튬화를 통해 상기 음극에서 발생되는 가스는 상기 관통홀을 통해 배출된다. 상기 음극은 상기 리튬 금속과의 접촉 전에 전해액에 침지되어 웨팅(wetting)될 수 있으며, 이 과정에서 상기 음극의 음극 활물질과 전해액간의 부반응을 통해 가스가 발생될 수 있다. 이와 같이 가스가 발생되는 상태에서 상기 음극과 상기 리튬 금속이 서로 대면하면서 밀착될 경우, 상기 가스가 빠져나갈 수 있는 공간이 없다면 상기 가스가 상기 음극과 상기 리튬 금속의 계면에 포집될 수 있다. 이와 같이, 상기 음극과 상기 리튬 금속의 계면에 포집될 수 있는 가스는 상기 관통홀을 통해 밖으로 배출될 수 있으므로, 상기 음극과 상기 리튬 금속이 더욱 긴밀히 접촉되어 더욱 효과적으로 전리튬화가 이루어질 수 있다. The lithium metal includes a plurality of through-holes, and the gas generated from the negative electrode through the lithiation is discharged through the through-holes. The negative electrode may be wetted by being immersed in the electrolyte before contact with the lithium metal, and in this process, gas may be generated through a side reaction between the negative electrode active material of the negative electrode and the electrolyte. When the anode and the lithium metal are in close contact while facing each other in a state in which the gas is generated as described above, the gas may be collected at the interface between the anode and the lithium metal if there is no space through which the gas can escape. In this way, since the gas that can be collected at the interface between the negative electrode and the lithium metal can be discharged out through the through hole, the negative electrode and the lithium metal are in more intimate contact with each other to more effectively prelithiate.
도 1에는 본 발명의 일례에 따른 리튬 이차전지용 음극의 전리튬화용 리튬 금속이 모식적으로 도시되어 있다. 도 1을 참조하면 리튬금속(100)의 면에는 복수개의 관통홀(110)이 형성되어 있다. 1 schematically shows a lithium metal for pre-lithiation of a negative electrode for a lithium secondary battery according to an example of the present invention. Referring to FIG. 1 , a plurality of through
상기 관통홀은 상기 리튬 금속판 1 cm2 당 1개 내지 200개 포함될 수 있고, 구체적으로 1 cm2 당 4개 내지 100개, 더욱 구체적으로 1 cm2 당 10개 내지 20개 포함될 수 있다. 상기 관통홀이 상기 리튬 금속판 1 cm2 당 상기 범위의 개수만큼 포함되므로, 상기 음극에서 발생된 가스가 상기 음극과 상기 리튬 금속의 계면의 일부 영역에 편중되더라도 상기 관통홀을 통해 적절히 빠져나갈 수 있으며, 상기 관통홀에 해당하는 영역만큼 상기 음극과 상기 리튬 금속이 접촉하지 못하여도 리튬이 상기 음극의 음극활물질층에서 적절히 확산하여 효과적으로 전리튬화가 이루어질 수 있다.The through-holes may be included in 1 to 200 per 1 cm 2 of the lithium metal plate, specifically 4 to 100 per 1 cm 2 , more specifically, 10 to 20 per 1 cm 2 may be included. Since the number of the through-holes per 1 cm 2 of the lithium metal plate is included in the above range, even if the gas generated from the negative electrode is biased in a partial region of the interface between the negative electrode and the lithium metal, it can properly escape through the through hole, , even if the negative electrode and the lithium metal do not contact as much as the region corresponding to the through hole, lithium is appropriately diffused in the negative electrode active material layer of the negative electrode, so that prelithiation can be effectively achieved.
상기 관통홀은 30 ㎛ 내지 3,000 ㎛의 직경을 가질 수 있고, 구체적으로 100 ㎛ 내지 2,000 ㎛의 직경을 가질 수 있으며, 더욱 구체적으로 500 ㎛ 내지 1,000 ㎛의 직경을 가질 수 있다. 상기 관통홀이 너무 작으면 상기 음극에서 발생된 가스의 배출이 원활하지 못할 수 있으며, 상기 관통홀이 상기 범위의 직경을 가질 경우 상기 음극에서 발생된 가스가 효과적으로 배출될 수 있다. 한편, 상기 관통홀이 상기 범위의 직경을 가질 경우 상기 관통홀에 해당하는 영역만큼 상기 음극과 상기 리튬 금속이 접촉하지 못하여도 리튬이 상기 음극의 음극활물질층에서 적절히 확산하여 효과적으로 전리튬화가 이루어질 수 있다.The through hole may have a diameter of 30 μm to 3,000 μm, specifically 100 μm to 2,000 μm, and more specifically 500 μm to 1,000 μm. If the through hole is too small, the gas generated from the cathode may not be smoothly discharged, and when the through hole has a diameter within the above range, the gas generated from the cathode may be effectively discharged. On the other hand, when the through-hole has a diameter in the above range, even if the negative electrode and the lithium metal do not contact as much as the area corresponding to the through-hole, lithium is properly diffused in the negative electrode active material layer of the negative electrode, so that all-lithiation can be effectively achieved. have.
상기 복수개의 관통홀의 총 면적은 상기 리튬 금속판의 총 면적 대비 0.1 면적% 내지 20 면적%일 수 있고, 구체적으로 1 면적% 내지 10 면적%일 수 있으며, 더욱 구체적으로 3 면적% 내지 7 면적%일 수 있다. 상기 복수개의 관통홀의 총 면적이 너무 작으면 상기 음극에서 발생된 가스가 효과적으로 배출되기 어렵고, 상기 복수개의 관통홀의 총 면적이 너무 크면 상기 전리튬화에 시간이 오래걸리거나, 상기 음극에 균일한 전리튬화가 이루어지지 않을 수 있다. 따라서, 상기 복수개의 관통홀의 총 면적은 상기 리튬 금속판의 총 면적 대비 상기 범위의 비율을 가질 수 있다. The total area of the plurality of through-holes may be 0.1 area% to 20 area%, specifically 1 area% to 10 area%, more specifically 3 area% to 7 area%, based on the total area of the lithium metal plate. can If the total area of the plurality of through-holes is too small, it is difficult for the gas generated from the cathode to be effectively discharged. Lithation may not occur. Accordingly, the total area of the plurality of through holes may have a ratio of the above range to the total area of the lithium metal plate.
상기 음극의 음극 활물질층의 두께에 따라 전해액과의 부반응에 의한 가스 발생량에 차이가 있을 수 있으므로, 상기 관통홀의 1 cm2 당 면적은 상기 음극의 음극 활물질층의 두께에 따라 적절히 조절될 수 있다. Since there may be a difference in the amount of gas generated due to a side reaction with the electrolyte depending on the thickness of the negative active material layer of the negative electrode, the area per 1 cm 2 of the through hole may be appropriately adjusted according to the thickness of the negative electrode active material layer of the negative electrode.
본 발명의 일례에 따른 리튬 이차전지용 음극의 전리튬화 방법에 있어서, 상기 음극과 리튬 금속을 접촉시키는 과정은 감압 하에서 이루어질 수 있다. 전리튬화 과정 중 상기 음극과 리튬 금속을 접촉시키는 과정이 감압 하에서 이루어질 경우, 상기 음극에서 발생된 가스가 상기 관통홀을 더욱 더 효과적으로 배출될 수 있다. 상기 감압은 10-10 Torr 내지 102 Torr 의 압력으로 이루어질 수 있고, 구체적으로 10-5 Torr 내지 10 Torr의 압력으로 이루어질 수 있다. In the prelithiation method of the negative electrode for a lithium secondary battery according to an example of the present invention, the process of contacting the negative electrode with the lithium metal may be performed under reduced pressure. When the process of contacting the negative electrode with the lithium metal during the prelithiation process is performed under reduced pressure, the gas generated from the negative electrode may be more effectively discharged through the through hole. The decompression may be performed at a pressure of 10 −10 Torr to 10 2 Torr, and specifically, a pressure of 10 −5 Torr to 10 Torr.
한편, 상기 음극은 음극 집전체 및 상기 음극 집전체 상에 형성된 음극 활물질층을 포함하고, 상기 음극 활물질층은 복수개의 오목부를 포함할 수 있다. 상기 오목부는 상기 음극 활물질층에 포함되어 있는 홈 또는 구멍(hole) 등일 수 있으며, 상기 음극 활물질층을 관통하고 있지 않은 오목한 구멍일 수 있고, 상기 음극 활물질층을 관통하고 있는 음극 관통홀일 수도 있다. Meanwhile, the negative electrode may include a negative electrode current collector and a negative electrode active material layer formed on the negative electrode current collector, and the negative electrode active material layer may include a plurality of concave portions. The concave portion may be a groove or hole included in the anode active material layer, may be a concave hole that does not penetrate the anode active material layer, or may be a cathode through hole penetrating the anode active material layer.
도 3 및 4에는 복수개의 오목부를 포함하는 음극 활물질층을 포함하는 음극의 일례가 도시되어 있다. 도 3 및 4에서 (a)는 음극의 정면도이고, (b)는 음극 단면의 측면도이다. 3 and 4 illustrate an example of a negative electrode including a negative active material layer including a plurality of concave portions. 3 and 4, (a) is a front view of the cathode, (b) is a side view of a cross-section of the cathode.
도 3을 참조하면, 음극 활물질층(200)에는 복수개의 오목부(210)가 형성되어 있고, 복수개의 오목부(210)는 음극 활물질층(200)을 관통하지 않아 음극 집전체(200)상에는 모두 음극 활물질층(200)이 덮여있는 형태일 수 있다. Referring to FIG. 3 , a plurality of
도 4를 참조하면, 음극 활물질층(201)에는 복수개의 음극 관통홀(211)이 형성되어 있고, 복수개의 음극 관통홀(211)은 음극 활물질층(200)을 관통하여 음극 집전체(200)까지 연결된 형태일 수 있다. Referring to FIG. 4 , a plurality of negative through-
상기 오목부는 상기 음극이 전해액에 침지되어 웨팅됐을 때 음극활물질 층에서 발생하는 가스를 보다 효과적으로 음극활물질층의 표면으로 전달할 수 있는 통로로서의 역할을 할 수 있다. The concave portion may serve as a passage through which the gas generated from the anode active material layer can be more effectively transferred to the surface of the anode active material layer when the anode is immersed in the electrolyte and wetted.
상기 오목부는 상기 음극과 리튬 금속을 접촉시키는 과정에서 리튬 금속판의 관통홀과 서로 접하여 연결됨으로써 연장될 수 있다. 상기 오목부가 상기 리튬 금속판의 관통홀과 연장될 경우, 상기 음극활물질 층에서 발생하는 가스가 보다 효과적으로 외부로 배출될 수 있다. The concave portion may be extended by contacting and connecting the through hole of the lithium metal plate in the process of bringing the negative electrode into contact with the lithium metal. When the concave portion extends from the through hole of the lithium metal plate, the gas generated in the anode active material layer may be more effectively discharged to the outside.
또한, 본 발명의 일례에 따른 리튬 이차전지용 음극의 전리튬화 방법에 있어서, 상기 음극 집전체는 복수개의 음극 집전체 관통홀을 포함할 수 있다. 상기 음극 집전체가 복수개의 음극 집전체 관통홀을 포함할 경우, 상기 음극이 전해액에 침지되어 웨팅됐을 때 음극활물질 층에서 발생하는 가스가 상기 음극 집전체 관통홀을 통해서 빠져나갈 수 있으므로, 상기 음극과 상기 리튬 금속의 계면에 위치할 수 있는 가스의 양이 줄어들어 보다 효과적으로 전리튬화가 이루어질 수 있다. In addition, in the method for prelithiation of a negative electrode for a lithium secondary battery according to an example of the present invention, the negative electrode current collector may include a plurality of negative electrode current collector through-holes. When the negative electrode current collector includes a plurality of negative current collector through-holes, when the negative electrode is immersed in the electrolyte and wetted, the gas generated from the negative electrode active material layer can escape through the negative electrode collector through-hole, so that the negative electrode The amount of gas that can be located at the interface between the lithium metal and the lithium metal is reduced, so that all-lithiation can be performed more effectively.
한편, 본 발명의 일례에 따른 리튬 이차전지용 음극의 전리튬화 방법에 있어서, 상기 음극 집전체 관통홀은 상기 오목부와 연장되고, 상기 오목부는 상기 음극과 리튬 금속을 접촉시키는 과정에서 서로 대면하는 리튬 금속판의 관통홀과 서로 연장될 수 있다. 이 경우, 상기 음극 집전체, 상기 음극활물질층의 오목부, 및 상기 리튬 금속의 관통홀이 서로 연결되므로, 상기 음극활물질 층에서 발생하는 가스가 더욱 효과적으로 빠져나갈 수 있다. On the other hand, in the prelithiation method of the negative electrode for a lithium secondary battery according to an example of the present invention, the negative electrode current collector through-hole extends with the concave portion, and the concave portion faces each other in the process of contacting the negative electrode with the lithium metal The through hole of the lithium metal plate may extend to each other. In this case, since the negative electrode current collector, the concave portion of the negative electrode active material layer, and the through hole of the lithium metal are connected to each other, the gas generated in the negative electrode active material layer can be more effectively discharged.
또한, 본 발명은 상기 리튬 이차전지용 음극의 전리튬화 방법에 사용될 수 있는, 리튬 이차전지용 음극의 전리튬화용 리튬 금속을 제공한다. In addition, the present invention provides a lithium metal for pre-lithiation of a negative electrode for a lithium secondary battery, which can be used in the method for pre-lithiation of the negative electrode for a lithium secondary battery.
본 발명의 리튬 이차전지용 음극의 전리튬화용 리튬 금속은 리튬 이차전지용 음극과 리튬 금속을 접촉시켜 상기 음극을 전리튬화하기 위한 리튬 금속으로서, 상기 리튬 금속은 복수개의 관통홀을 포함하는 리튬 금속판이다. The lithium metal for pre-lithiation of the negative electrode for a lithium secondary battery of the present invention is a lithium metal for pre-lithiation of the negative electrode by contacting the negative electrode for a lithium secondary battery with lithium metal, wherein the lithium metal is a lithium metal plate including a plurality of through holes. .
상기 관통홀은 상기 리튬 금속판 1 cm2 당 1개 내지 200개 포함될 수 있고, 구체적으로 1 cm2 당 4개 내지 100개, 더욱 구체적으로 1 cm2 당 10개 내지 20개 포함될 수 있다. The through-holes may be included in 1 to 200 per 1 cm 2 of the lithium metal plate, specifically 4 to 100 per 1 cm 2 , more specifically, 10 to 20 per 1 cm 2 may be included.
상기 관통홀은 30 ㎛ 내지 3,000 ㎛의 직경을 가질 수 있고, 구체적으로 100 ㎛ 내지 2,000 ㎛의 직경을 가질 수 있으며, 더욱 구체적으로 500 ㎛ 내지 1,000 ㎛의 직경을 가질 수 있다. The through hole may have a diameter of 30 μm to 3,000 μm, specifically 100 μm to 2,000 μm, and more specifically 500 μm to 1,000 μm.
상기 복수개의 관통홀의 총 면적은 상기 리튬 금속판의 총 면적 대비 0.1 면적% 내지 20 면적%일 수 있고, 구체적으로 1 면적% 내지 10 면적%일 수 있으며, 더욱 구체적으로 3 면적% 내지 7 면적%일 수 있다.The total area of the plurality of through-holes may be 0.1 area% to 20 area%, specifically 1 area% to 10 area%, more specifically 3 area% to 7 area%, based on the total area of the lithium metal plate. can
이와 같은 본 발명의 일례에 따른 리튬 이차전지용 음극의 전리튬화용 리튬 금속은 상기 복수개의 관통홀이 전리튬화 과정에서 음극에서 발생되는 가스를 효과적으로 배출시킬 수 있으면서도, 음극에 균일한 전리튬화가 이루어지도록 할 수 있다. The lithium metal for pre-lithiation of the negative electrode for a lithium secondary battery according to an example of the present invention can effectively discharge the gas generated from the negative electrode during the pre-lithiation process through the plurality of through-holes, and uniform pre-lithiation is achieved on the negative electrode. can make it go away
본 발명의 일례에 따른 리튬 이차전지용 음극의 전리튬화 방법에서, 상기 음극은 음극 활물질로서 실리콘계 음극 활물질을 포함하는 것일 수 있다. 상기 실리콘계 음극 활물질로는, 예컨대 Si, 실리콘 산화물 입자(SiOx, 0<x≤2), 및 Si-금속합금, 이루어진 군으로부터 선택된 1종 이상을 포함하는 것을 들 수 있고, 상기 실리콘 산화물 입자는 결정형 SiO2 및 비정형 Si로 구성된 복합물(SiOx, 0<x<2)일 수 있다. 상기 실리콘계 음극 활물질은 충방전시 부피 변화가 크고, 초기 충방전시 표면 부작용이 심하여 비가역 용량이 크므로, 전리튬화(pre-lithiation)를 실시함에 따른 효용이 더욱 크다. In the method for prelithiation of a negative electrode for a lithium secondary battery according to an example of the present invention, the negative electrode may include a silicon-based negative electrode active material as an anode active material. The silicon-based negative active material may include, for example, Si, silicon oxide particles (SiO x , 0<x≤2), and Si-metal alloy, and one or more selected from the group consisting of, the silicon oxide particles are It may be a composite (SiO x , 0<x<2) composed of crystalline SiO 2 and amorphous Si. Since the silicon-based anode active material has a large volume change during charging and discharging, and a large irreversible capacity due to a severe surface side effect during initial charging and discharging, the utility due to pre-lithiation is greater.
또한, 상기 음극 활물질은 상기 실리콘계 음극 활물질 이외에 통상적으로 리튬 이온이 흡장 및 방출될 수 있는 탄소재, 리튬 금속 또는 주석 등을 함께 포함할 수 있다. 상기 탄소재로는 저결정 탄소 및 고결정성 탄소 등이 모두 사용될 수 있고, 상기 저결정성 탄소로는 연화탄소(soft carbon) 및 경화탄소(hard carbon)가 대표적이며, 상기 고결정성 탄소로는 천연 흑연, 키시흑연(kish graphite), 열분해 탄소(pyrolytic carbon), 액정피치계 탄소섬유(mesophase pitch based carbon fiber), 탄소 미소구체(meso-carbon microbeads), 액정피치(mesophase pitches) 및 석유와 석탄계 코크스 (petroleum or coal tar pitch derived cokes) 등의 고온 소성탄소가 대표적이다.In addition, the negative active material may include, in addition to the silicon-based negative active material, a carbon material, lithium metal, or tin in which lithium ions can be occluded and released. As the carbon material, both low crystalline carbon and high crystalline carbon may be used, and as the low crystalline carbon, soft carbon and hard carbon are representative, and the high crystalline carbon is natural. Graphite, kish graphite, pyrolytic carbon, mesophase pitch based carbon fiber, meso-carbon microbeads, mesophase pitches, and petroleum and coal-based coke High-temperature calcined carbon such as (petroleum or coal tar pitch derived cokes) is a representative example.
상기 음극은 당 분야에 통상적으로 알려져 있는 방법에 따라 제조될 수 있으며, 예컨대 상기 음극 활물질 및 바인더 및 도전재 등의 첨가제들을 혼합 및 교반하여 음극 활물질 슬러리를 제조한 후, 이를 음극 집전체에 도포하고 건조한 후 압축하여 제조할 수 있다.The negative electrode may be manufactured according to a method commonly known in the art, for example, by mixing and stirring the negative electrode active material and additives such as a binder and a conductive material to prepare a negative electrode active material slurry, and then applying it to the negative electrode current collector, It can be prepared by compression after drying.
상기 음극 활물질 층은 10 ㎛ 내지 100 ㎛의 두께를 가질 수 있고, 구체적으로 50 ㎛ 내지 80 ㎛의 두께를 가질 수 있다. The negative active material layer may have a thickness of 10 μm to 100 μm, specifically, a thickness of 50 μm to 80 μm.
상기 음극에 사용되는 바인더 및 도전재는 당 분야에 통상적으로 사용될 수 있는 것을 사용할 수 있다. The binder and the conductive material used for the negative electrode may be those that can be commonly used in the art.
상기 음극을 형성하기 위한 용매로는 N-메틸 피롤리돈(NMP), 디메틸 포름아미드(DMF), 아세톤, 디메틸 아세트아미드 등의 유기 용매 또는 물 등이 있으며, 이들 용매는 단독으로 또는 2종 이상을 혼합하여 사용할 수 있다. 용매의 사용량은 슬러리의 도포 두께, 제조 수율을 고려하여 상기 음극 활물질, 바인더, 도전재를 용해 및 분산시킬 수 있는 정도이면 충분하다.Examples of the solvent for forming the negative electrode include organic solvents such as N-methyl pyrrolidone (NMP), dimethyl formamide (DMF), acetone, and dimethyl acetamide or water, and these solvents are used alone or in two or more types. can be mixed and used. The amount of the solvent used is sufficient as long as it is capable of dissolving and dispersing the negative electrode active material, the binder, and the conductive material in consideration of the application thickness of the slurry and the production yield.
상기 바인더로는 폴리비닐리덴플루오라이드-헥사플루오로프로필렌 코폴리머(PVDF-co-HFP), 폴리비닐리덴플루오라이드(polyvinylidenefluoride), 폴리아크릴로니트릴(polyacrylonitrile), 폴리메틸메타크릴레이트(polymethylmethacrylate), 폴리비닐알코올, 카르복시메틸셀룰로오스(CMC), 전분, 히드록시프로필셀룰로오스, 재생 셀룰로오스, 폴리비닐피롤리돈, 테트라플루오로에틸렌, 폴리에틸렌, 폴리프로필렌, 폴리아크릴산, 에틸렌-프로필렌-디엔 모노머(EPDM), 술폰화 EPDM, 스티렌 부타디엔 고무(SBR), 불소 고무, 폴리 아크릴산(poly acrylic acid) 및 이들의 수소를 Li, Na 또는 Ca 등으로 치환된 고분자, 또는 다양한 공중합체 등의 다양한 종류의 바인더 고분자가 사용될 수 있다.As the binder, polyvinylidene fluoride-hexafluoropropylene copolymer (PVDF-co-HFP), polyvinylidenefluoride, polyacrylonitrile, polymethylmethacrylate, Polyvinyl alcohol, carboxymethyl cellulose (CMC), starch, hydroxypropyl cellulose, regenerated cellulose, polyvinyl pyrrolidone, tetrafluoroethylene, polyethylene, polypropylene, polyacrylic acid, ethylene-propylene-diene monomer (EPDM), Sulfonated EPDM, styrene butadiene rubber (SBR), fluororubber, polyacrylic acid, and a polymer in which hydrogen is substituted with Li, Na or Ca, or the like; or Various types of binder polymers such as various copolymers may be used.
상기 도전재는 당해 전지에 화학적 변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되는 것은 아니며, 예컨대 천연 흑연이나 인조 흑연 등의 흑연; 아세틸렌 블랙, 케첸 블랙, 채널 블랙, 파네스 블랙, 램프 블랙, 서멀 블랙 등의 카본블랙; 탄소 섬유나 금속 섬유 등의 도전성 섬유; 탄소 나노 튜브 등의 도전성 튜브; 플루오로카본, 알루미늄, 니켈 분말 등의 금속 분말; 산화아연, 티탄산 칼륨 등의 도전성 위스커; 산화 티탄 등의 도전성 금속 산화물; 폴리페닐렌 유도체 등의 도전성 소재 등이 사용될 수 있다.The conductive material is not particularly limited as long as it has conductivity without causing a chemical change in the battery, for example, graphite such as natural graphite or artificial graphite; carbon black such as acetylene black, Ketjen black, channel black, farness black, lamp black, and thermal black; conductive fibers such as carbon fibers and metal fibers; conductive tubes such as carbon nanotubes; metal powders such as fluorocarbon, aluminum, and nickel powder; conductive whiskers such as zinc oxide and potassium titanate; conductive metal oxides such as titanium oxide; Conductive materials such as polyphenylene derivatives may be used.
본 발명의 일 실시예에 따르면, 상기 음극은 점도조절을 위해 증점제를 더 포함할 수 있다. 상기 증점제는 셀룰로오스계 화합물일 수 있으며, 예를 들어 카르복시 메틸 셀룰로오스(CMC), 하이드록시 메틸셀룰로오스, 하이드록시 에틸 셀룰로오스 및 하이드록시 프로필 셀룰로오스로 이루어진 군에서 선택된 1 종 이상일 수 있고, 구체적으로 카르복시 메틸 셀룰로오스(CMC)일 수 있으며, 상기 음극 활물질 및 바인더를 증점제와 함께 물에 분산시켜 음극에 적용할 수 있다.According to an embodiment of the present invention, the negative electrode may further include a thickener for viscosity control. The thickener may be a cellulose-based compound, for example, may be at least one selected from the group consisting of carboxymethyl cellulose (CMC), hydroxy methyl cellulose, hydroxy ethyl cellulose and hydroxy propyl cellulose, specifically carboxy methyl cellulose (CMC), and may be applied to the negative electrode by dispersing the negative electrode active material and the binder in water together with a thickener.
상기 전리튬화에서 상기 음극을 웨팅시키기 위한 전해액은 이차 전지용 전해액에 통상적으로 사용되는 전해질 및 유기 용매를 제한 없이 포함할 수 있다. In the prelithiation, the electrolyte for wetting the negative electrode may include, without limitation, an electrolyte and an organic solvent commonly used in an electrolyte for a secondary battery.
본 발명에서 사용되는 전해질로서 포함될 수 있는 리튬염은 리튬 이차전지용 전해질에 통상적으로 사용되는 것들이 제한 없이 사용될 수 있으며, 예컨대 상기 리튬염의 음이온으로는 F-, Cl-, Br-, I-, NO3 -, N(CN)2 -, BF4 -, ClO4 -, PF6 -, (CF3)2PF4 -, (CF3)3PF3 -, (CF3)4PF2 -, (CF3)5PF-, (CF3)6P-, CF3SO3 -, CF3CF2SO3 -, (CF3SO2)2N-, (FSO2)2N-, CF3CF2(CF3)2CO-, (CF3SO2)2CH-, (SF5)3C-, (CF3SO2)3C-, CF3(CF2)7SO3 -, CF3CO2 -, CH3CO2 -, SCN- 및 (CF3CF2SO2)2N-로 이루어진 군에서 선택된 어느 하나일 수 있다. Lithium salts that may be included as the electrolyte used in the present invention may be used without limitation, those commonly used in electrolytes for lithium secondary batteries, for example, as an anion of the lithium salt, F - , Cl - , Br - , I - , NO 3 - , N(CN) 2 - , BF 4 - , ClO 4 - , PF 6 - , (CF 3 ) 2 PF 4 - , (CF 3 ) 3 PF 3 - , (CF 3 ) 4 PF 2 - , (CF 3 ) 5 PF - , (CF 3 ) 6 P - , CF 3 SO 3 - , CF 3 CF 2 SO 3 - , (CF 3 SO 2 ) 2 N - , (FSO 2 ) 2 N - , CF 3 CF 2 (CF 3 ) 2 CO - , (CF 3 SO 2 ) 2 CH - , (SF 5 ) 3 C - , (CF 3 SO 2 ) 3 C - , CF 3 (CF 2 ) 7 SO 3 - , CF 3 CO 2 - , CH 3 CO 2 - , SCN - and (CF 3 CF 2 SO 2 ) 2 N - may be any one selected from the group consisting of.
상기 전해액에 포함되는 유기 용매로는 이차 전지용 전해액에 통상적으로 사용되는 것들이 제한 없이 사용될 수 있으며, 대표적으로 프로필렌 카보네이트(propylene carbonate, PC), 에틸렌 카보네이트(ethylene carbonate, EC), 디에틸 카보네이트(diethyl carbonate, DEC), 디메틸 카보네이트(dimethyl carbonate, DMC), 에틸메틸 카보네이트(EMC), 메틸프로필 카보네이트, 디프로필 카보네이트, 디메틸 설퍼옥사이드, 아세토니트릴, 디메톡시에탄, 디에톡시에탄, 비닐렌 카보네이트, 설포란, 감마-부티로락톤, 프로필렌 설파이트 및 테트라하이드로푸란으로 이루어진 군에서 선택되는 어느 하나 또는 이들 중 2종 이상의 혼합물 등이 대표적으로 사용될 수 있다. 구체적으로, 상기 카보네이트계 유기용매 중 고리형 카보네이트인 에틸렌 카보네이트 및 프로필렌 카보네이트는 고점도의 유기용매로서 유전율이 높아 전해질 내의 리튬염을 잘 해리시키므로 바람직하게 사용될 수 있으며, 이러한 고리형 카보네이트에 디메틸 카보네이트 및 디에틸 카보네이트와 같은 저점도, 저유전율 선형 카보네이트를 적당한 비율로 혼합하여 사용하면 높은 전기 전도율을 갖는 전해액을 만들 수 있어 더욱 바람직하게 사용될 수 있다.As an organic solvent included in the electrolyte, those commonly used in electrolytes for secondary batteries may be used without limitation, and representatively, propylene carbonate (PC), ethylene carbonate (EC), diethyl carbonate (diethyl carbonate) , DEC), dimethyl carbonate (DMC), ethylmethyl carbonate (EMC), methylpropyl carbonate, dipropyl carbonate, dimethyl sulfuroxide, acetonitrile, dimethoxyethane, diethoxyethane, vinylene carbonate, sulfolane, Any one selected from the group consisting of gamma-butyrolactone, propylene sulfite, and tetrahydrofuran, or a mixture of two or more thereof may be typically used. Specifically, among the carbonate-based organic solvents, ethylene carbonate and propylene carbonate, which are cyclic carbonates, are highly viscous organic solvents and have a high dielectric constant, so they can be preferably used because they dissociate lithium salts in the electrolyte well, and in these cyclic carbonates, dimethyl carbonate and di When a low-viscosity, low-dielectric constant linear carbonate such as ethyl carbonate is mixed in an appropriate ratio, an electrolyte having a high electrical conductivity can be prepared, which can be more preferably used.
선택적으로, 본 발명에 따라 저장되는 전해액은 통상의 전해액에 포함되는 과충전 방지제 등과 같은 첨가제를 더 포함할 수 있다.Optionally, the electrolyte stored according to the present invention may further include additives such as an overcharge inhibitor included in a conventional electrolyte.
실시예Example
이하, 본 발명을 구체적으로 설명하기 위해 실시예 및 실험예를 들어 더욱 상세하게 설명하나, 본 발명이 이들 실시예 및 실험예에 의해 제한되는 것은 아니다. 본 발명에 따른 실시예는 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 상술하는 실시예에 한정되는 것으로 해석되어서는 안 된다. 본 발명의 실시예는 당업계에서 평균적인 지식을 가진 자에게 본 발명을 보다 완전하게 설명하기 위해서 제공되는 것이다.Hereinafter, examples and experimental examples will be described in more detail to describe the present invention in detail, but the present invention is not limited by these examples and experimental examples. Embodiments according to the present invention may be modified in various other forms, and the scope of the present invention should not be construed as being limited to the embodiments described below. The embodiments of the present invention are provided to more completely explain the present invention to those of ordinary skill in the art.
실시예 1Example 1
<음극의 제조><Production of cathode>
음극 활물질로서 (흑연:SiO=7:3) 92 중량%, Denka black(도전제) 3 중량% 및 SBR(결합제) 3.5 중량%, 및 CMC(증점제) 1.5 중량%를 물에 첨가하여 음극 혼합물 슬러리를 제조하였다. 구리 집전체의 일면에 상기 제조된 음극 혼합물 슬러리를 50 ㎛ 두께로 코팅하고, 이를 건조 및 압연한 후 가로 3 cm, 세로 4 cm로 타발하였다. 제조된 음극의 음극 활물질층의 두께는 40 ㎛였다.As a negative electrode active material (graphite:SiO=7:3) 92% by weight, Denka black (conductive agent) 3% by weight and SBR (binder) 3.5% by weight, and CMC (thickener) 1.5% by weight were added to water to slurry the negative electrode mixture was prepared. The prepared negative electrode mixture slurry was coated on one surface of a copper current collector to a thickness of 50 μm, dried and rolled, and then punched out to a width of 3 cm and a length of 4 cm. The thickness of the negative active material layer of the prepared negative electrode was 40 μm.
<직접 접촉법을 이용한 전리튬화><All-lithiation using direct contact method>
상기에서 제작한 음극을 에틸렌 카보네이트(EC), 에틸메틸 카보네이트(DEC)를 50:50의 부피비로 혼합한 용매에 1M LiPF6가 용해된 전해액에 담가두고 5시간 동안 웨팅(wetting) 시켜준 후 도 1에 나타낸 본 발명의 일례에 따른 리튬 이차전지용 음극의 전리튬화용 리튬 금속과 같이 가스 방출을 위한 관통홀(직경 500 ㎛, 리튬메탈 1 cm2당 10 개, 관통홀의 면적 1.96 면적%)을 형성시킨 리튬메탈을 1.5cm2 당 1 kgf의 힘으로 30 분 동안 음극에 눌러주었다. 이렇게 직접 접촉을 마친 전극은 디메틸카보네이트(DMC)를 이용해 세척하고 건조시켜 주었다.The anode fabricated above was immersed in an electrolyte solution in which 1M LiPF6 was dissolved in a solvent in which ethylene carbonate (EC) and ethylmethyl carbonate (DEC) were mixed in a volume ratio of 50:50, followed by wetting for 5 hours. Like the lithium metal for pre-lithiation of the negative electrode for a lithium secondary battery according to an example of the present invention shown in Lithium metal was pressed against the negative electrode at a force of 1 kgf per 1.5 cm 2 for 30 minutes. The electrode after direct contact was washed with dimethyl carbonate (DMC) and dried.
<리튬 이차전지의 제조><Manufacture of lithium secondary battery>
양극활물질로 LiCoO2 94 중량%, 도전제로 카본 블랙(carbon black) 3 중량%, 결합제로 PVdF 3 중량%를 용제인 N-메틸-2 피롤리돈(NMP)에 첨가하여 양극 혼합물 슬러리를 제조하였다. 상기 양극 혼합물 슬러리를 두께 20 ㎛ 정도의 양극 집전체인 알루미늄(Al) 박막에 도포 및 건조를 통하여 양극을 제조한 후 롤 프레스(roll press)를 실시하였다.A cathode mixture slurry was prepared by adding 94 wt% of LiCoO 2 as a cathode active material, 3 wt% of carbon black as a conductive agent, and 3 wt% of PVdF as a binder to N-methyl-2 pyrrolidone (NMP) as a solvent. . The positive electrode mixture slurry was applied to an aluminum (Al) thin film, which is a positive electrode current collector, having a thickness of about 20 μm, and dried to prepare a positive electrode, and then roll press was performed.
상기에서 전리튬화를 마친 음극과 상기 제조된 양극 사이에 폴리올레핀 세퍼레이터를 개재시킨 후 에틸렌 카보네이트(EC) 및 디에틸 카보네이트(DEC)를 30:70의 부피비로 혼합한 용매에 1M LiPF6가 용해된 전해질을 주입하여 코인형 리튬 이차전지를 제조하였다. 1M LiPF 6 was dissolved in a solvent in which ethylene carbonate (EC) and diethyl carbonate (DEC) were mixed in a volume ratio of 30:70 after interposing a polyolefin separator between the negative electrode after prelithiation and the prepared positive electrode A coin-type lithium secondary battery was manufactured by injecting electrolyte.
실시예 2 내지 4Examples 2 to 4
상기 실시예 1에서 전리튬화시 각각 하기 표 1에 나타낸 바와 같이 가스 방출을 위한 관통홀의 개수 및 직경을 달리한 리튬 메탈을 사용한 것을 사용한 것을 제외하고는 실시예 1과 마찬가지의 방법으로 음극을 제조하고, 전리튬화를 실시한 다음, 리튬 이차전지를 제조하였다. An anode was manufactured in the same manner as in Example 1, except that lithium metal having different numbers and diameters of through-holes for gas emission was used during prelithiation in Example 1, respectively, as shown in Table 1 below. and prelithiation was performed, and then a lithium secondary battery was manufactured.
실시예 5Example 5
상기 실시예 1에서 제조된 음극 표면에 바늘(needle)을 이용하여 직경 500 ㎛, 음극활물질층 1 cm2당 10 개가 되도록 홀을 형성하였다. 상기 홀이 형성된 음극을 사용한 것을 제외하고는, 실시예 1과 마찬가지의 방법으로 전리튬화를 실시한 다음, 리튬 이차전지를 제조하였다. Holes were formed on the surface of the negative electrode prepared in Example 1 so as to have a diameter of 500 μm and 10 per cm 2 of the negative electrode active material layer using a needle. All-lithiation was performed in the same manner as in Example 1, except that the negative electrode having the hole was used, and then a lithium secondary battery was manufactured.
비교예 1Comparative Example 1
상기 실시예 1에서 제조된 음극을 가스 방출 홀이 없는 리튬메탈을 사용하여 전리튬화한 것을 제외하고는, 실시예 1과 마찬가지의 방법으로 리튬 이차전지를 제조하였다. A lithium secondary battery was manufactured in the same manner as in Example 1, except that the negative electrode prepared in Example 1 was prelithiated using lithium metal without a gas release hole.
비교예 2Comparative Example 2
상기 실시예 1에서 전리튬화시 각각 하기 표 1에 나타낸 바와 같이 가스 방출을 위한 관통홀의 개수 및 직경을 달리한 리튬 메탈을 사용한 것을 사용한 것을 제외하고는 실시예 1과 마찬가지의 방법으로 음극을 제조하고, 전리튬화를 실시한 다음, 리튬 이차전지를 제조하였다. An anode was manufactured in the same manner as in Example 1, except that lithium metal having different numbers and diameters of through-holes for gas emission was used during prelithiation in Example 1, respectively, as shown in Table 1 below. and prelithiation was performed, and then a lithium secondary battery was manufactured.
실험예 1 : 전리튬화 전극의 표면 균일도Experimental Example 1: Surface uniformity of pre-lithiated electrode
상기 실시예 1 및 비교예 1에서 제조된 음극의 표면을 도 2에 나타내었다. 실시예 1의 경우 전극 표면에 얼룩이 존재하지 않아 전체적으로 전리튬화가 균일하게 된 것을 확인할 수 있었다. 한편, 전리튬화가 된 부분과 전리튬화가 이루어지지 않은 부분간에는 두께 차이 및 색상 차이가 발생하므로, 비교예 1의 경우 전극 표면에 얼룩을 존재한다는 것을 통해 전리튬화가 균일하게 되지 않았다는 것을 확인할 수 있다. 실시예 1의 경우 리튬금속과 음극의 접촉시 전해액 부반응으로 발생한 가스(수소가스, 메탄가스 등)가 가스 방출 홀을 통해 방출되어 리튬금속과 음극사이에 접촉이 잘 유지될 수 있으므로 균일하게 전리튬화가 이루어진 것으로 판단된다. 반면, 비교예 1의 경우 리튬금속과 음극의 접촉시 전해액 부반응으로 발생한 가스가 빠져나가지 못해 리튬금속과 음극 사이에 남게되어 그 사이의 접촉을 방해하게 되어 접촉이 되지 않은 면은 전리튬화가 이루어지지 않기 때문에 전체적으로 균일하지 않게 전리튬화가 된 것으로 판단된다.The surfaces of the negative electrodes prepared in Example 1 and Comparative Example 1 are shown in FIG. 2 . In the case of Example 1, there was no stain on the electrode surface, and it was confirmed that the total lithiation was uniform. On the other hand, since a difference in thickness and color occurs between the prelithiated portion and the non-lithiated portion, in Comparative Example 1, it can be confirmed that the prelithiation is not uniform through the presence of stains on the electrode surface. . In the case of Example 1, the gas (hydrogen gas, methane gas, etc.) generated as a side reaction of the electrolyte solution when the lithium metal and the negative electrode is in contact is released through the gas release hole, so that the contact between the lithium metal and the negative electrode can be maintained well, so that all lithium anger is considered to have occurred. On the other hand, in the case of Comparative Example 1, when the lithium metal and the negative electrode are in contact, the gas generated due to the side reaction of the electrolyte cannot escape, so that it remains between the lithium metal and the negative electrode, which prevents the contact between the lithium metal and the negative electrode. Therefore, it is judged that the overall lithiation is not uniform.
실험예 2 : 수명 특성 평가Experimental Example 2: Lifespan characteristic evaluation
상기 실시예 1 내지 4, 및 비교예 1 및 2에서 제조된 전지를 각각 25℃에서 정전류/정전압(CC/CV) 조건으로 4.2V까지 1 C으로 충전한 다음, 정전류(CC) 조건으로 2.5V까지 1 C으로 방전하고, 그 방전 용량을 측정하였다. 이를 1 내지 100 사이클로 반복 실시하였다. 그 결과를 하기 표 2에 나타내었다. The batteries prepared in Examples 1 to 4 and Comparative Examples 1 and 2 were respectively charged at 25° C. to 4.2 V under constant current/constant voltage (CC/CV) conditions at 1 C, and then at 2.5 V under constant current (CC) conditions. Discharged at 1 C until the time of discharge, and the discharge capacity was measured. This was repeated for 1 to 100 cycles. The results are shown in Table 2 below.
(㎛)hole diameter
(μm)
표 1을 참조하면 실시예 1 내지 4의 리튬 이차전지는 100사이클 용량 유지율이 80% 이상으로 잘 유지되고 있음을 확인할 수 있다. 이는 전리튬화시 가스 방출 홀에 의해 적절히 가스가 배출되어 리튬화의 균일도가 높아 충방전시 리튬이온이 고르게 충전과 방전을 반복하기 때문으로 판단된다. Referring to Table 1, it can be seen that the lithium secondary batteries of Examples 1 to 4 are well maintained at a capacity retention rate of 80% or more for 100 cycles. This is considered to be because the gas is properly discharged by the gas discharge hole during all lithiation, and the uniformity of lithiation is high, so that the lithium ions repeat charging and discharging evenly during charging and discharging.
비교예 1의 100사이클 용량 유지율이 낮은 이유는 가스방출 홀이 없는 리튬 메탈을 이용하여 전리튬화를 실시하였으므로, 음극의 리튬화 균일도가 떨어져 음극에서 리튬이온의 충방전이 균일하게 일어나지 않아 사이클이 반복될 경우 음극 활물질층이 뒤틀려 탈리되기 때문으로 판단된다. The reason that the 100-cycle capacity retention rate of Comparative Example 1 was low is because all-lithiation was performed using lithium metal without a gas release hole, so the lithiation uniformity of the negative electrode was low, and the charge and discharge of lithium ions did not occur uniformly in the negative electrode. If it is repeated, it is considered that the anode active material layer is twisted and detached.
한편, 비교예 2와 같이 가스 홀의 면적이 일정수준 이상으로 넓어지게 되면 리튬메탈과 직접접촉되어 전리튬화되는 전극의 면적이 줄어들기 때문에 전리튬화가 적절히 이루어지 못하며 이러한 이유로 100사이클 용량유지율이 저하된 것으로 판단된다. On the other hand, as in Comparative Example 2, when the area of the gas hole is widened to a certain level or more, the area of the electrode that is in direct contact with lithium metal to be prelithiated is reduced, so prelithiation is not performed properly. is considered to have been
100: 리튬금속
110: 관통홀100: lithium metal
110: through hole
Claims (15)
상기 리튬 금속은 복수개의 관통홀을 포함하는 리튬 금속판이고,
상기 전리튬화를 통해 상기 음극에서 발생되는 가스는 상기 관통홀을 통해 배출되고,
상기 복수개의 관통홀의 총 면적은 상기 리튬 금속판의 총 면적 대비 0.1 면적% 내지 16 면적%인, 리튬 이차전지용 음극의 전리튬화 방법.
A method for prelithiation of a negative electrode for a lithium secondary battery, comprising the step of supplying lithium from the lithium metal to the negative electrode by contacting the negative electrode for a lithium secondary battery with lithium metal,
The lithium metal is a lithium metal plate including a plurality of through holes,
The gas generated from the cathode through the prelithiation is discharged through the through hole,
The total area of the plurality of through-holes is 0.1 area% to 16 area% based on the total area of the lithium metal plate.
상기 관통홀은 상기 리튬 금속판 1 cm2 당 1 내지 50개 포함되는, 리튬 이차전지용 음극의 전리튬화 방법.
The method of claim 1,
The method of prelithiation of the negative electrode for a lithium secondary battery, wherein the through-holes are included in 1 to 50 per 1 cm 2 of the lithium metal plate.
상기 관통홀은 1 ㎛ 내지 3,000 ㎛의 직경을 가지는, 리튬 이차전지용 음극의 전리튬화 방법.
The method of claim 1,
The through-hole has a diameter of 1 μm to 3,000 μm, a method of pre-lithiation of a negative electrode for a lithium secondary battery.
상기 음극과 리튬 금속을 접촉시키는 과정은 감압 하에서 이루어지는, 리튬 이차전지용 음극의 전리튬화 방법.
The method of claim 1,
The process of bringing the negative electrode into contact with the lithium metal is a pre-lithiation method of a negative electrode for a lithium secondary battery made under reduced pressure.
상기 감압은 10-10 Torr 내지 102 Torr의 압력으로 이루어지는, 리튬 이차전지용 음극의 전리튬화 방법.
6. The method of claim 5,
The reduced pressure is made of a pressure of 10 -10 Torr to 10 2 Torr, the all-lithiation method of a negative electrode for a lithium secondary battery.
상기 음극은 음극 집전체 및 상기 음극 집전체 상에 형성된 음극 활물질층을 포함하고,
상기 음극 활물질층은 복수개의 오목부를 포함하는, 리튬 이차전지용 음극의 전리튬화 방법.
The method of claim 1,
The negative electrode includes a negative electrode current collector and a negative electrode active material layer formed on the negative electrode current collector,
The anode active material layer includes a plurality of concave portions, a method of pre-lithiation of a negative electrode for a lithium secondary battery.
상기 오목부는 상기 음극 활물질층을 관통하는 음극 관통홀인, 리튬 이차전지용 음극의 전리튬화 방법.
8. The method of claim 7,
The concave portion is a negative electrode through-hole penetrating the negative electrode active material layer, a method of pre-lithiation of a negative electrode for a lithium secondary battery.
상기 오목부는 상기 음극과 리튬 금속을 접촉시키는 과정에서 리튬 금속판의 관통홀과 서로 연장되는, 리튬 이차전지용 음극의 전리튬화 방법.
8. The method of claim 7,
The concave portion extends from the through hole of the lithium metal plate in the process of contacting the negative electrode with the lithium metal.
상기 음극 집전체는 복수개의 음극 집전체 관통홀을 포함하는, 리튬 이차전지용 음극의 전리튬화 방법.
8. The method of claim 7,
The negative electrode current collector includes a plurality of negative electrode current collector through-holes, a method of pre-lithiation of a negative electrode for a lithium secondary battery.
상기 음극 집전체 관통홀은 음극 활물질층의 오목부와 연장되고,
상기 오목부는 상기 음극과 리튬 금속을 접촉시키는 과정에서 리튬 금속판의 관통홀과 서로 연장되는, 리튬 이차전지용 음극의 전리튬화 방법.
11. The method of claim 10,
The negative current collector through-hole extends with the concave portion of the negative electrode active material layer,
The concave portion extends from the through hole of the lithium metal plate in the process of contacting the negative electrode with the lithium metal.
상기 리튬 금속은 복수개의 관통홀을 포함하는 리튬 금속판이고,
상기 복수개의 관통홀의 총 면적은 상기 리튬 금속판의 총 면적 대비 0.1 면적% 내지 16 면적%인, 리튬 이차전지용 음극의 전리튬화용 리튬 금속.
As a lithium metal for prelithiation of the negative electrode by contacting the negative electrode for a lithium secondary battery with lithium metal,
The lithium metal is a lithium metal plate including a plurality of through holes,
The total area of the plurality of through-holes is 0.1 area% to 16 area% of the total area of the lithium metal plate.
상기 관통홀은 상기 리튬 금속판 1 cm2 당 1개 내지 50 개 포함되는, 리튬 이차전지용 음극의 전리튬화용 리튬 금속.
13. The method of claim 12,
The through-holes are included in 1 to 50 per 1 cm 2 of the lithium metal plate, lithium metal for pre-lithiation of a negative electrode for a lithium secondary battery.
상기 관통홀은 1 ㎛ 내지 3,000 ㎛의 직경을 가지는, 리튬 이차전지용 음극의 전리튬화용 리튬 금속.
13. The method of claim 12,
The through-hole has a diameter of 1 μm to 3,000 μm, a lithium metal for pre-lithiation of a negative electrode for a lithium secondary battery.