KR102272170B1 - Recyclable packaging paper - Google Patents

Recyclable packaging paper Download PDF

Info

Publication number
KR102272170B1
KR102272170B1 KR1020190065675A KR20190065675A KR102272170B1 KR 102272170 B1 KR102272170 B1 KR 102272170B1 KR 1020190065675 A KR1020190065675 A KR 1020190065675A KR 20190065675 A KR20190065675 A KR 20190065675A KR 102272170 B1 KR102272170 B1 KR 102272170B1
Authority
KR
South Korea
Prior art keywords
layer
polypropylene
based resin
resin film
wrapping paper
Prior art date
Application number
KR1020190065675A
Other languages
Korean (ko)
Other versions
KR20200139326A (en
Inventor
이상진
Original Assignee
주식회사 피엔디엔
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 피엔디엔 filed Critical 주식회사 피엔디엔
Priority to KR1020190065675A priority Critical patent/KR102272170B1/en
Publication of KR20200139326A publication Critical patent/KR20200139326A/en
Application granted granted Critical
Publication of KR102272170B1 publication Critical patent/KR102272170B1/en

Abstract

본 발명의 실시예들에 따른 폴리프로필렌계 수지 소재를 포함하는 포장대상물을 포장하는 재활용 포장지에 있어서, 무연신 폴리프로필렌계 수지로 구성되는 접착필름을 포함하고, 포장대상물에 인접하는 제1층; 제1층의 상층에 배치되는 폴리프로필렌계 수지 필름을 포함하는 제2층; 제2층의 상층에 배치되는 폴리프로필렌계 수지 필름을 포함하는 제3층; 제1층과 제2층의 사이에 배치되고, 유기계 소재를 포함하는 베리어 코팅층; 및 제2층과 제3층의 사이에 배치되고, 잉크가 인쇄된 인쇄층을 포함하는 재활용 포장지를 제공하고자 한다.In the recycled wrapping paper for packaging a packaging object comprising a polypropylene-based resin material according to embodiments of the present invention, comprising: an adhesive film made of a non-stretched polypropylene-based resin, the first layer adjacent to the packaging object; a second layer comprising a polypropylene-based resin film disposed on an upper layer of the first layer; a third layer comprising a polypropylene-based resin film disposed on the second layer; a barrier coating layer disposed between the first layer and the second layer and including an organic material; And disposed between the second layer and the third layer, to provide a recycled wrapping paper comprising a printed layer on which ink is printed.

Description

재활용 가능한 포장지{RECYCLABLE PACKAGING PAPER}Recyclable packaging paper {RECYCLABLE PACKAGING PAPER}

본 발명에 따른 재활용 포장지는 재활용이 용이한 포장지에 관한 것으로서, 구체적으로, 복수 개의 필름이 적층되어 형성되는 포장지를 구성하는 각각의 기능성 층들이 유사한 소재로 조성되어 재활용이 용이한 재활용 포장지에 관한 것이다.The recycled wrapping paper according to the present invention relates to a packaging paper that is easy to recycle, and specifically, it relates to a recycled wrapping paper that is easy to recycle because each functional layer constituting the wrapping paper formed by stacking a plurality of films is composed of a similar material. .

식품 포장지는 식품이 상하지 않도록 저장하고, 식품 용기의 마케팅 향상을 위한 것으로서, 식품 판매에 중요한 역할을 담당한다. 따라서, 식품 포장지는 식품의 신선도 및 보존성을 유지하기 위해서는 기체 및 수분의 차단성이 우수해야 할뿐만 아니라, 시각적으로도 우수해야 한다. 나아가, 현재 환경오염에 대한 관심이 커지고 있는 추세에서 재활용의 중요성이 강조되어, 재활용 가능한 단일 소재의 포장지의 필요성이 대두되고 있는 시점이다.Food packaging paper is used to store food so that it does not spoil and to improve marketing of food containers, and plays an important role in food sales. Therefore, in order to maintain the freshness and preservation of food, the food wrapping paper must have excellent gas and moisture barrier properties as well as visually excellent. Furthermore, the importance of recycling is emphasized in the current trend of increasing interest in environmental pollution, and the need for packaging paper made of a single recyclable material is emerging.

일반적으로, 기존의 식품 용기의 포장지는 산소 차단을 위해 알루미늄과 같은 금속재질을 포함한 이종소재로 구성된 다층필름이 적층된 제품이 다수 있었다. 그런데, 알루미늄과 같은 금속재질을 포함한 이종소재로 구성된 다층필름 포장지는 재활용이 어렵고, 재활용을 한다고 해도 환경에 유해한 물질의 배출을 막기 어려운 문제점이 있었다.In general, there have been many products in which a multilayer film composed of a different material including a metal material such as aluminum is laminated for the packaging paper of the existing food container to block oxygen. However, the multilayer film wrapping paper composed of dissimilar materials including metal materials such as aluminum is difficult to recycle, and even if recycled, it is difficult to prevent the discharge of substances harmful to the environment.

또한, 다층필름 포장지는 각 식품용기의 외형에 알맞게 가공하는 단계에서 포장지의 각 층을 이루는 조성물의 상이한 장력 특성으로 인해 말려들어가게 되어 포장지의 보관 및 대상 용기에 부착하는 것이 어려워지는 불편함이 있었다.In addition, the multilayer film wrapping paper was rolled up due to the different tensile properties of the composition constituting each layer of the wrapping paper in the step of processing it to suit the appearance of each food container, making it difficult to store the wrapping paper and attach it to the target container.

대한민국 등록실용신안공보 제20-0305978호(발명의 명칭: 인쇄층을 가지는 블리스터 투명 포장지)Republic of Korea Registered Utility Model Publication No. 20-0305978 (Title of the invention: transparent blister packaging paper having a printed layer)

본 발명에 따른 재활용 포장지는 상술한 문제점을 해결하기 위하여, 보편적인 재활용 식품 용기와 유사한 단일 소재로 형성되어, 식품 용기에서 따로 제거할 필요 없이 용이하게 재활용이 가능한 재활용 포장지를 제공하고자 한다.In order to solve the above-mentioned problems, the recycled wrapping paper according to the present invention is formed of a single material similar to a universal recycled food container, and it is intended to provide a recycled wrapping paper that can be easily recycled without separately removing it from the food container.

본 발명의 실시예들에 따른 폴리프로필렌계 수지 소재를 포함하는 포장대상물을 포장하는 재활용 포장지에 있어서, 무연신 폴리프로필렌계 수지로 구성되는 접착필름을 포함하고, 포장대상물에 인접하는 제1층; 제1층의 상층에 배치되는 폴리프로필렌계 수지 필름을 포함하는 제2층; 제2층의 상층에 배치되는 폴리프로필렌계 수지 필름을 포함하는 제3층; 제1층과 제2층의 사이에 배치되고, 유기계 소재를 포함하는 베리어 코팅층; 및 제2층과 제3층의 사이에 배치되고, 잉크가 인쇄된 인쇄층을 포함하는 재활용 포장지를 제공하고자 한다.In the recycled wrapping paper for packaging a packaging object comprising a polypropylene-based resin material according to embodiments of the present invention, comprising: an adhesive film made of a non-stretched polypropylene-based resin, the first layer adjacent to the packaging object; a second layer comprising a polypropylene-based resin film disposed on an upper layer of the first layer; a third layer comprising a polypropylene-based resin film disposed on the second layer; a barrier coating layer disposed between the first layer and the second layer and including an organic material; And disposed between the second layer and the third layer, to provide a recycled wrapping paper comprising a printed layer on which ink is printed.

일 실시예에 있어서, 제2층의 폴리프로필렌계 수지 필름은 연신 폴리프로필렌계 수지 필름이고, 제3층의 폴리프로필렌계 수지 필름은 연신 폴리프로필렌계 수지 필름인, 재활용 포장지를 제공할 수 있다.In one embodiment, the polypropylene-based resin film of the second layer is a stretched polypropylene-based resin film, and the polypropylene-based resin film of the third layer is a stretched polypropylene-based resin film, recycled wrapping paper may be provided.

다른 실시예에 있어서, 제2층의 폴리프로필렌계 수지 필름은 무연신 폴리프로필렌계 수지 필름이고, 제3층의 폴리프로필렌계 수지 필름은 연신 폴리프로필렌계 수지 필름인, 재활용 포장지를 제공할 수 있다.In another embodiment, the polypropylene-based resin film of the second layer is an unstretched polypropylene-based resin film, and the polypropylene-based resin film of the third layer is a stretched polypropylene-based resin film, recycled wrapping paper may be provided. .

또 다른 실시예에 있어서, 제2층의 폴리프로필렌계 수지 필름은 연신 폴리프로필렌계 수지 필름이고, 제3층의 폴리프로필렌계 수지 필름은 무연신 폴리프로필렌계 수지 필름인, 재활용 포장지를 제공할 수 있다.In another embodiment, the polypropylene-based resin film of the second layer is a stretched polypropylene-based resin film, and the polypropylene-based resin film of the third layer is an unstretched polypropylene-based resin film, recycled wrapping paper can be provided. have.

또 다른 실시예에 있어서, 제2층의 폴리프로필렌계 수지 필름은 무연신 폴리프로필렌계 수지 필름이고, 제3층의 폴리프로필렌계 수지 필름은 무연신 폴리프로필렌계 수지 필름인, 재활용 포장지를 제공할 수 있다.In another embodiment, the polypropylene-based resin film of the second layer is an unstretched polypropylene-based resin film, and the polypropylene-based resin film of the third layer is a non-stretched polypropylene-based resin film, to provide a recycled wrapping paper can

실시예들에 있어서, 제1층의 두께는 제2층의 두께 및 제3층의 두께보다 얇게 형성되는, 재활용 포장지를 제공할 수 있다.In embodiments, the thickness of the first layer is formed to be thinner than the thickness of the second layer and the thickness of the third layer, it is possible to provide a recycled wrapping paper.

변형된 실시예들에 있어서, 베리어 코팅층은 제1층 상에 건식 적층되는, 재활용 포장지를 제공할 수 있다.In modified embodiments, the barrier coating layer may provide a recyclable wrapper that is dry laminated on the first layer.

실시예들에 있어서, 포장대상물에 면접하는 일측면 및 타측면 중 어느 하나에 형성되는 요홈부를 포함하고, 요홈부는 베리어 코팅층에 침투되지 않는 깊이로 형성되는, 재활용 포장지를 제공할 수 있다.In embodiments, it is possible to provide a recycled wrapping paper, including a groove formed on any one of the one side and the other side facing the packaging object, the groove portion is formed to a depth that does not penetrate the barrier coating layer.

변형된 실시예들에 있어서, 요홈부가 타측면에 형성되는 경우에, 요홈부는 제3층에 형성되고, 요홈부의 깊이는 제2층의 두께, 인쇄층의 두께 및 제3층의 두께를 합한 깊이 이하로 형성되는, 재활용 포장지를 제공할 수 있다.In modified embodiments, when the recess is formed on the other side, the recess is formed in the third layer, and the depth of the recess is the sum of the thickness of the second layer, the thickness of the printed layer, and the thickness of the third layer. Formed below, it is possible to provide a recycled wrapping paper.

변형된 실시예들에 있어서, 요홈부는 인쇄층 및 제2층에 더 형성되고, 요홈부의 깊이는 인쇄층 및 제3층의 두께를 합한 깊이 이상으로 형성되는, 재활용 포장지를 제공할 수 있다.In modified embodiments, the concave portion is further formed in the printed layer and the second layer, and the depth of the concave portion is formed to be greater than or equal to the sum of the thicknesses of the printed layer and the third layer, it is possible to provide a recycled wrapping paper.

변형된 실시예들에 있어서, 요홈부는 일측면 및 타측면 중 어느 하나의 측면에 격자무늬 패턴으로 형성되는, 재활용 포장지를 제공할 수 있다.In modified embodiments, the concave portion is formed in a lattice pattern on any one side of one side and the other side, it is possible to provide a recycled wrapping paper.

변형된 실시예들에 있어서, 제1층의 두께는 10μm 이상 70μm 이하로 형성되고, 제2층의 두께는 40μm 이상 100μm 이하로 형성되고, 제3층의 두께는 40μm 이상 100μm 이하로 형성되는, 재활용 포장지를 제공할 수 있다.In modified embodiments, the first layer has a thickness of 10 μm or more and 70 μm or less, the second layer has a thickness of 40 μm or more and 100 μm or less, and the third layer has a thickness of 40 μm or more and 100 μm or less. Recycled wrapping paper can be provided.

본 발명에 따른 재활용 포장지는 폴리프로필렌계 수지 소재로 형성되는 식품 용기 형태의 포장대상물에 사용되며, 복수 개의 폴리프로필렌계 수지 소재의 필름이 적층된 구조로 형성되어, 포장대상물을 재활용하기 위해 분리배출 및 가공할 때 포장지를 따로 제거할 필요가 없어서 재활용이 용이해지는 효과가 있다.The recycling wrapping paper according to the present invention is used for packaging objects in the form of food containers made of polypropylene-based resin materials, and is formed in a structure in which a plurality of polypropylene-based resin films are laminated, and separated and discharged to recycle the packaging objects And since there is no need to separately remove the wrapping paper during processing, recycling is facilitated.

또한, 본 발명에 따른 재활용 포장지는 인장력이 높은 소재의 필름이 배치된 일측면에 요홈부를 형성하여, 필름 간의 인장력 차이로 인하여 포장지가 말려들어가는 현상을 방지할 수 있는 효과가 있다.In addition, the recycled wrapping paper according to the present invention has an effect that can prevent the wrapping paper from being rolled up due to the difference in tensile force between the films by forming a recess in one side where the film of the material having high tensile force is disposed.

도 1은 종래의 다양한 식품 용기 포장지를 보여주는 도면이다.
도 2는 본 발명의 일 실시예에 따른 재활용 포장지를 보여주는 측단면도이다.
도 3은 본 발명의 다른 실시예들에 따른 재활용 포장지를 보여주는 측단면도이다.
도 4는 본 발명의 변형된 실시예에 따른 재활용 포장지를 보여주는 측단면도이다.
도 5는 종래의 재활용 포장지 및 본 발명의 변형된 실시예에 따른 재활용 포장지를 보여주는 측단면도이다.
도 6은 본 발명의 변형된 실시예에 따른 재활용 포장지의 요홈부의 다양한 실시형태를 보여주는 도면이다.
도 7은 본 발명의 변형된 실시예에 따른 재활용 포장지의 요홈부의 활용형태를 보여주는 도면이다.1 is a view showing a conventional packaging for various food containers.
2 is a side cross-sectional view showing a recycled wrapping paper according to an embodiment of the present invention.
3 is a side cross-sectional view showing a recycled wrapping paper according to other embodiments of the present invention.
4 is a side cross-sectional view showing a recycled wrapping paper according to a modified embodiment of the present invention.
5 is a side cross-sectional view showing a conventional recycled wrapping paper and a recycled wrapping paper according to a modified embodiment of the present invention.
6 is a view showing various embodiments of the groove portion of the recycled wrapping paper according to a modified embodiment of the present invention.
7 is a view showing the utilization form of the recessed portion of the recycled wrapping paper according to a modified embodiment of the present invention.

아래에서는 첨부한 도면을 참조하여, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예를 상세히 설명한다. 그러나, 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다. 그리고, 도면에서 본 발명을 명확하게 설명하기 위해서 설명과 관계없는 부분은 생략하였으며, 명세서 전체를 통하여 유사한 부분에 대해서는 유사한 도면 부호를 붙였다.Hereinafter, with reference to the accompanying drawings, embodiments of the present invention will be described in detail so that those of ordinary skill in the art can easily carry out the present invention. However, the present invention may be embodied in many different forms and is not limited to the embodiments described herein. And, in order to clearly explain the present invention in the drawings, parts irrelevant to the description are omitted, and similar reference numerals are attached to similar parts throughout the specification.

명세서 전체에서, 어떤 부분이 다른 부분과 "연결"되어 있다고 할 때, 이는 "직접적으로 연결"되어 있는 경우뿐만 아니라, 그 중간에 다른 소자를 사이에 두고 "전기적으로 연결"되어 있는 경우도 포함한다. 또한, 어떤 부분이 어떤 구성요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성요소를 제외하는 것이 아니라 다른 구성요소를 더 포함할 수 있는 것을 의미한다.Throughout the specification, when a part is "connected" to another part, this includes not only the case of being "directly connected" but also the case of being "electrically connected" with another element interposed therebetween. . In addition, when a part "includes" a certain component, it means that other components may be further included, rather than excluding other components, unless otherwise stated.

이하에서는, 본 발명의 일 실시예에 따른 재활용 포장지에 대하여 상세히 설명하기로 한다.Hereinafter, the recycled packaging paper according to an embodiment of the present invention will be described in detail.

도 1은 종래의 다양한 식품 용기 포장지를 보여주는 도면이다.1 is a view showing a conventional packaging for various food containers.

도 1을 참조하면, 종래의 식품 용기 포장지는 일반적으로 식품 용기 내부로 유입되는 기체를 차단하여 식품의 신선도를 유지하기 위해 기체 차단 성능이 우수한 알루미늄 등의 금속으로 형성된 필름을 포함하는 복수 개의 필름들이 적층되어 형성되었다. 이러한 포장지는 유기계 수지, 금속 등의 다양한 소재가 혼합되어 있어서 분리 및 재활용이 어렵다는 문제점이 있었다.Referring to FIG. 1 , a conventional food container wrapper is generally made of a plurality of films including a film formed of a metal such as aluminum having excellent gas barrier performance in order to block the gas flowing into the food container to maintain the freshness of the food. laminated and formed. Such packaging paper has a problem in that it is difficult to separate and recycle it because various materials such as organic resin and metal are mixed.

상술한 문제점을 해결하기 위하여, 본 발명의 일 실시예에 따른 재활용 포장지(1)는 알루미늄 등의 금속 필름을 포함하지 않고 유기계 필름으로 구성되어 재활용이 용이한 포장지를 제공하고자 한다. 본 발명의 일 실시예에 따른 재활용 포장지(1)는 식품 용기 등의 포장대상물을 포장하기 위한 포장지일 수 있다. 여기에서, 포장대상물은 유기계 소재로 형성될 수 있으며, 바람직하게 폴리프로필렌계(Polypropylene)의 단일 소재로 형성될 수 있다. 폴리프로필렌은 견고하면서도 재활용이 용이하다는 특징이 있다.In order to solve the above-described problems, the recycled wrapping paper 1 according to an embodiment of the present invention is composed of an organic film without including a metal film such as aluminum, so that it is intended to provide a wrapping paper that is easy to recycle. The recycled wrapping paper 1 according to an embodiment of the present invention may be a wrapping paper for packaging a packaging object such as a food container. Here, the packaging object may be formed of an organic material, preferably of a single material of polypropylene. Polypropylene is characterized by being strong and easy to recycle.

도 2는 본 발명의 일 실시예에 따른 재활용 포장지(1)를 보여주는 측단면도이다.2 is a side cross-sectional view showing a recycled wrapping paper 1 according to an embodiment of the present invention.

도 2를 참조하면 본 발명의 일 실시예에 따른 재활용 포장지(1)는 제1층(11), 제2층(12), 제3층(13), 베리어 코팅층(14), 인쇄층(15)을 포함할 수 있다.Referring to FIG. 2 , the recycled wrapping paper 1 according to an embodiment of the present invention has a first layer 11 , a second layer 12 , a third layer 13 , a barrier coating layer 14 , and a printing layer 15 . ) may be included.

제1층(11)은 포장대상물에 인접하게 배치되어 포장대상물에 면접 및 부착되는 필름을 포함하는 층일 수 있다. 제1층(11)은 무연신 폴리프로필렌계(CPP: Casting Polypropylene) 수지 필름, 연신 호모폴리머 폴리프로필렌(Homopolymer OPP), 연신 코폴리머 폴리프로필렌(Copolymer OPP) 수지 필름 및 연신 터폴리머 폴리프로필렌(Terpolymer OPP) 수지 필름 중 적어도 어느 하나의 접착필름(Adhesive Film)을 포함할 수 있다. 다만, 이러한 종류의 연신 폴리프로필렌(OPP)만으로 본 발명의 구성이 한정되는 것은 아니다.The first layer 11 may be a layer including a film disposed adjacent to the packaging object and attached to the surface and attached to the packaging object. The first layer 11 is a non-stretched polypropylene-based (CPP: Casting Polypropylene) resin film, a stretched homopolymer polypropylene (Homopolymer OPP), a stretched copolymer polypropylene (Copolymer OPP) resin film, and a stretched terpolymer polypropylene (Terpolymer). OPP) may include at least one adhesive film of the resin film (Adhesive Film). However, the configuration of the present invention is not limited only to this type of stretched polypropylene (OPP).

무연신 폴리프로필렌계 수지는 연신공정을 통하지 않고 생산되는 폴리프로필렌계 수지로서, 투명성 및 방습성이 우수하고, 표면 경도가 높으며, 연신 폴리프로필렌계 필름과 대비하여 열봉합성이 우수하다는 특징이 있다. 따라서, 무연신 폴리프로필렌계 수지 필름은 포장지의 가장 아래층에 배치되며 포장대상물에 면접된 상태로 열처리되어서 포장대상물과 포장지를 접착하는 역할을 수행할 수 있다.The non-stretched polypropylene-based resin is a polypropylene-based resin produced without a stretching process, and has excellent transparency and moisture-proof properties, high surface hardness, and excellent heat-sealability compared to a stretched polypropylene-based film. Therefore, the non-stretched polypropylene-based resin film is disposed on the lowermost layer of the wrapping paper and is heat-treated in a state in which the packaging object is face-to-face to perform a role of adhering the packaging object and the wrapping paper.

코폴리머는 모노머 2종류 이상을 공중합하여 구성되는 중합체이며, 터폴리머는 모노머 3종류 이상을 공중합하여 구성되는 중합체일 수 있다. 코폴리머 및 터폴리머 폴리프로필렌 수지는 내충격강도가 호모폴리머 폴리프로필렌 수지보다 높을 수 있다. 또한, 코폴리머 및 터폴리머 폴리프로필렌 수지는 호모폴리머 폴리프로필렌 수지보다 내열성이 약할 수 있다. 따라서, 제1층의 하면을 코폴리머 및 터폴리머 폴리프로필렌 수지로 구성하고, 이에 열을 가하면, 제1층의 하면과 면접하는 포장대상물에 접착을 용이하게 수행할 수 있는 효과가 있다.The copolymer may be a polymer constituted by copolymerizing two or more types of monomers, and the terpolymer may be a polymer constituted by copolymerizing three or more kinds of monomers. Copolymer and terpolymer polypropylene resins may have higher impact strength than homopolymer polypropylene resins. In addition, copolymer and terpolymer polypropylene resins may have weaker heat resistance than homopolymer polypropylene resins. Therefore, when the lower surface of the first layer is composed of copolymer and terpolymer polypropylene resins and heat is applied thereto, there is an effect that adhesion can be easily performed to the packaging object in contact with the lower surface of the first layer.

제2층(12)은 제1층(11)의 상층에 배치되는 폴리프로필렌계 수지 필름을 포함하는 층일 수 있다. 제2층(12)이 제1층(11)의 윗면에 직접적으로 부착될 수도 있지만, 제1층(11)과 제2층(12) 사이에 다양한 기능성 층들이 배치될 수도 있다. 제2층(12)은 연신 폴리프로필렌계(OPP: Oriented Polypropylene) 수지 필름을 포함할 수 있다. 연신 폴리프로필렌계 수지는 투명성, 방습성, 표면 광택도가 우수하고, 비중이 낮으며 무연신 폴리프로필렌에 대비하여 인장강도, 충격강도 등의 기계적 강도가 우수하다는 특징이 있다.The second layer 12 may be a layer including a polypropylene-based resin film disposed on an upper layer of the first layer 11 . Although the second layer 12 may be directly attached to the upper surface of the first layer 11 , various functional layers may be disposed between the first layer 11 and the second layer 12 . The second layer 12 may include an oriented polypropylene (OPP) resin film. Stretched polypropylene-based resins are characterized by excellent transparency, moisture resistance, surface gloss, low specific gravity, and mechanical strength such as tensile strength and impact strength compared to unstretched polypropylene.

제3층(13)은 제2층(12)의 상층에 배치되는 폴리프로필렌계 수지 필름을 포함하는 층일 수 있다. 제3층(13)이 제2층(12)의 윗면에 직접적으로 부착될 수도 있지만, 제2층(12)과 제3층(13) 사이에 다양한 기능성 층들이 배치될 수도 있다. 제3층(13)은 연신 폴리프로필렌계(OPP: Oriented Polypropylene) 수지 필름을 포함할 수 있다.The third layer 13 may be a layer including a polypropylene-based resin film disposed on an upper layer of the second layer 12 . Although the third layer 13 may be directly attached to the upper surface of the second layer 12 , various functional layers may be disposed between the second layer 12 and the third layer 13 . The third layer 13 may include an oriented polypropylene (OPP) resin film.

베리어 코팅층(14)은 제1층(11)과 제2층(12) 사이에 배치되며, 기체 및 수분의 투과를 방지하기 위한 층일 수 있다. 베리어 코팅층(14)은 유기계 소재를 포함하여 형성될 수 있다. 바람직하게, 베리어 코팅층(14)은 폴리프로필렌계(PP: Polypropylene) 수지를 포함할 수 있으며, 방습성 향상을 위해 무기계 소재를 더 포함할 수 있다. 베리어 코팅층(14)은 0μm 초과 5μm 이하의 두께를 가질 수 있다. 기체차단성 향상을 위해 베리어 코팅층(14)의 두께 두꺼운 것이 유리하지만, 두께가 5 μm를 초과하면, 가공이 어렵고, 재활용 수율이 떨어질 수 있다. 따라서, 대기압 하에서 충분한 방습성 및 기체 차단성을 제공하면서, 가공성 및 재활용 수율 확보를 위해 베리어 코팅층(14)의 두께는 5μm이하인 것이 바람직하며, 무기계 소재를 첨가하여 기체차단성을 향상시키는 것도 가능하다.The barrier coating layer 14 is disposed between the first layer 11 and the second layer 12 , and may be a layer for preventing the permeation of gas and moisture. The barrier coating layer 14 may include an organic material. Preferably, the barrier coating layer 14 may include a polypropylene-based (PP: Polypropylene) resin, and may further include an inorganic material to improve moisture resistance. The barrier coating layer 14 may have a thickness greater than 0 μm and less than or equal to 5 μm. Although it is advantageous to have a thick barrier coating layer 14 to improve gas barrier properties, if the thickness exceeds 5 μm, processing may be difficult, and recycling yield may be reduced. Therefore, while providing sufficient moisture resistance and gas barrier properties under atmospheric pressure, the thickness of the barrier coating layer 14 is preferably 5 μm or less in order to secure processability and recycling yield, and it is also possible to improve the gas barrier property by adding an inorganic material.

베리어 코팅층(14)은 제1층(11) 상에 건식 적층될 수 있다. 여기서 건식 적층이란, 유기용제에 녹인 접착제를 필름에 도포한 후 건조기에서 건조시킨 후 다른 기재를 붙여 합치는 방법일 수 있다. 구체적으로, 본 발명의 일 실시예에 따른 베리어 코팅층(14)은 유기계 소재로 형성되므로 이를 액상으로 가공한 후에 제1층(11) 상에 도포하는 방식으로 제1층(11)의 윗면을 코팅하고, 건조된 상태의 베리어 코팅층(14)의 상층에 제2층(12)이 적층되는 것으로서 건식 적층이 수행될 수 있는 것이다. The barrier coating layer 14 may be dry laminated on the first layer 11 . Here, the dry lamination may be a method in which an adhesive dissolved in an organic solvent is applied to a film, dried in a dryer, and then another substrate is attached to the film. Specifically, since the barrier coating layer 14 according to an embodiment of the present invention is formed of an organic material, the upper surface of the first layer 11 is coated by applying it on the first layer 11 after processing it in a liquid phase. And, as the second layer 12 is laminated on the upper layer of the barrier coating layer 14 in a dried state, dry lamination can be performed.

인쇄층(15)은 제2층(12)과 제3층(13) 사이에 배치되고, 잉크가 인쇄된 층일 수 있다. 예를 들어, 인쇄층(15)은 프라이머(Primer) 소재의 베이스 상에 다양한 색상의 잉크가 인쇄된 층일 수 있다. 인쇄층(15)은 제2층(12)과 제3층(13) 사이에 적층될 수 있다. 이로써, 인쇄층(15)의 윗면에 제3층(12)이 배치되어 인쇄층(14)이 외부와 차단되므로 인쇄된 잉크가 손상되는 것을 방지할 수 있는 효과가 있다.The printed layer 15 is disposed between the second layer 12 and the third layer 13, and may be a layer on which ink is printed. For example, the printing layer 15 may be a layer in which inks of various colors are printed on a base of a primer material. The printed layer 15 may be laminated between the second layer 12 and the third layer 13 . Accordingly, since the third layer 12 is disposed on the upper surface of the printed layer 15 and the printed layer 14 is blocked from the outside, it is possible to prevent damage to the printed ink.

이하에서는, 본 발명의 다른 실시예들에 따른 재활용 포장지에 대하여 상세히 설명하기로 한다.Hereinafter, the recycled packaging paper according to other embodiments of the present invention will be described in detail.

도 3은 본 발명의 다른 실시예들에 따른 재활용 포장지를 보여주는 측단면도이다.3 is a side cross-sectional view showing a recycled wrapping paper according to other embodiments of the present invention.

도 3의 (a)를 참조하면, 본 발명의 다른 실시예에 따른 재활용 포장지(2)는 무연신 폴리프로필렌계 수지 필름으로 구성된 제1층(21) 상에 유기계 소재를 포함하는 베리어 코팅층(24)이 적층될 수 있다. 베리어 코팅층(24)의 상층에는 무연신 폴리프로필렌계 수지 필름을 포함하는 제2층(22)이 적층될 수 있다. 제2층(22)의 상층에는 인쇄층(25)이 적층될 수 있다. 인쇄층(25)의 상층에는 연신 폴리프로필렌계 수지 필름을 포함하는 제3층(23)이 적층될 수 있다.Referring to FIG. 3 (a), the recycled wrapping paper 2 according to another embodiment of the present invention is a barrier coating layer 24 including an organic material on the first layer 21 made of a non-stretched polypropylene-based resin film. ) can be stacked. A second layer 22 including a non-stretched polypropylene-based resin film may be laminated on an upper layer of the barrier coating layer 24 . A printed layer 25 may be stacked on an upper layer of the second layer 22 . A third layer 23 including a stretched polypropylene-based resin film may be laminated on the upper layer of the print layer 25 .

도 3의 (b)를 참조하면, 본 발명의 또 다른 실시예에 따른 재활용 포장지(3)는 무연신 폴리프로필렌계 수지 필름을 포함하는 제1층(31) 상에 베리어 코팅층(34)이 적층될 수 있다. 베리어 코팅층(34) 상에 연신 폴리프로필렌계 수지 필름을 포함하는 제2층(32)이 적층될 수 있다. 제2층(32) 상에 인쇄층(35)이 적층될 수 있다. 인쇄층(35) 상에 무연신 폴리프로필렌계 수지 필름을 포함하는 제3층(33)이 적층될 수 있다.Referring to FIG. 3 (b), in the recycled wrapping paper 3 according to another embodiment of the present invention, the barrier coating layer 34 is laminated on the first layer 31 including the non-stretched polypropylene-based resin film. can be A second layer 32 including a stretched polypropylene-based resin film may be laminated on the barrier coating layer 34 . A printed layer 35 may be laminated on the second layer 32 . A third layer 33 including a non-stretched polypropylene-based resin film may be laminated on the print layer 35 .

도 3의 (c)를 참조하면, 본 발명의 또 다른 실시예에 따른 재활용 포장지(4)는 무연신 폴리프로필렌계 수지 필름을 포함하는 제1층(41) 상에 베리어 코팅층(44)이 적층될 수 있다. 베리어 코팅층(44) 상에 연신 폴리프로필렌계 수지 필름을 포함하는 제2층(42)이 적층될 수 있다. 제2층(42) 상에 인쇄층(45)이 적층될 수 있다. 인쇄층(45) 상에 무연신 폴리프로필렌계 수지 필름을 포함하는 제3층(43)이 적층될 수 있다.Referring to (c) of Figure 3, in the recycled wrapping paper 4 according to another embodiment of the present invention, the barrier coating layer 44 is laminated on the first layer 41 including the non-stretched polypropylene-based resin film. can be A second layer 42 including a stretched polypropylene-based resin film may be laminated on the barrier coating layer 44 . A printed layer 45 may be laminated on the second layer 42 . A third layer 43 including a non-stretched polypropylene-based resin film may be laminated on the print layer 45 .

이하에서는, 본 발명의 변형된 실시예에 따른 재활용 포장지(1')에 대하여 상세히 설명하기로 한다.Hereinafter, the recycled wrapping paper 1' according to a modified embodiment of the present invention will be described in detail.

도 4는 본 발명의 변형된 실시예에 따른 재활용 포장지를 보여주는 측단면도이다. 도 5는 종래의 재활용 포장지 및 본 발명의 변형된 실시예에 따른 재활용 포장지를 보여주는 측단면도이다.4 is a side cross-sectional view showing a recycled wrapping paper according to a modified embodiment of the present invention. 5 is a side cross-sectional view showing a conventional recycled wrapping paper and a recycled wrapping paper according to a modified embodiment of the present invention.

도 4 및 도 5를 참조하면, 일반적으로 식품 포장지는 복수개의 대면적의 포장용 필름을 권출하여 적층시키고, 이를 포장대상물의 포장하려는 부위에 맞는 크기 및 형상으로 펀칭하여 제조된다. 이러한 공정에서, 펀칭된 포장지는 권출됨에 따라 한쪽 면으로 말리거나, 각각 인장력 등의 물성이 다른 소재의 필름이 적층된 구조를 가지므로, 인장력이 낮은 소재의 필름(11)은 확장되고, 인장력이 높은 소재의 필름(13)이 배치된 쪽으로 수축되어 말려들어가는 문제점이 있었다(도 5의 (a) 참조). 이를 해결하기 위하여, 본 발명의 변형된 실시예에 따른 재활용 포장지는 요홈부(16)를 포함할 수 있다.4 and 5, in general, food packaging paper is manufactured by unwinding a plurality of large-area packaging films, stacking them, and punching them in a size and shape suitable for the part to be packaged of the packaging object. In this process, the punched wrapping paper is rolled on one side as it is unwound, or has a structure in which films made of materials with different physical properties such as tensile force are laminated, respectively, so the film 11 made of a material with low tensile force is expanded, and the tensile force is There was a problem in that the high material film 13 was shrunk to the side where it was arranged (see Fig. 5 (a)). In order to solve this, the recycled wrapping paper according to a modified embodiment of the present invention may include a recess 16 .

요홈부(16)는 포장지의 평평한 표면 상에 오목하게 형성되는 홈일 수 있다. 요홈부(16)는 포장대상물에 면접하는 포장지의 일측면 또는 이와 반대측에 배치되는 타측면 중 어느 하나에 형성될 수 있다. 예를 들어, 상기 포장지의 타측면은 인장력이 높은 소재의 필름이 배치된 부분일 수 있다. 요홈부(16)는 포장지의 타측면 상에 칼집을 내는 반칼 가공을 통해 형성될 수 있다.The concave portion 16 may be a groove formed concavely on the flat surface of the wrapping paper. The concave portion 16 may be formed on either one side of the wrapping paper that faces the packaging object or the other side disposed on the opposite side. For example, the other side of the wrapping paper may be a portion on which a film made of a material having high tensile force is disposed. The concave portion 16 may be formed through half-knife processing to make a cut on the other side of the wrapping paper.

요홈부(16)는 베리어 코팅층(14)에 침투되지 않는 깊이로 형성될 수 있다. 요홈부(16)는 제3층(13) 상에 형성되며, 그 깊이는 제3층(51)의 두께 이하일 수 있다. 또한 요홈부(16)는, 인쇄층(15) 및 제2층(12)에 더 형성되고, 요홈부(16)의 깊이는 인쇄층(15) 및 제3층(13)의 두께를 합한 깊이 이상이고, 제2층(12)의 두께, 인쇄층(15)의 두께, 및 제3층(13)의 두께를 합한 깊이 이하로 형성될 수 있다(도 5의 (b) 참조). 이로써, 요홈부(16)는 제1층(11)의 상층에 배치되는 베리어 코팅층(14)에는 형성되지 않을 수 있고, 포장지의 방습 및 기체차단 효과가 유지될 수 있다.The concave portion 16 may be formed to a depth that does not penetrate into the barrier coating layer 14 . The concave portion 16 is formed on the third layer 13 , and the depth thereof may be less than or equal to the thickness of the third layer 51 . In addition, the recessed portion 16 is further formed in the printed layer 15 and the second layer 12 , and the depth of the recessed portion 16 is the sum of the thicknesses of the printed layer 15 and the third layer 13 . above, the thickness of the second layer 12 , the thickness of the printed layer 15 , and the thickness of the third layer 13 may be formed to a depth equal to or less than the sum (see (b) of FIG. 5 ). Accordingly, the concave portion 16 may not be formed in the barrier coating layer 14 disposed on the upper layer of the first layer 11 , and the moisture-proof and gas barrier effect of the wrapping paper may be maintained.

본 발명의 일 실시예에 따른 재활용 포장지(1)의 두께는 90μm 이상 270μm 이하일 수 있다. 포장지는 너무 두꺼우면 가공이 어려워지고 제조 비용이 높아지는 단점이 있고, 너무 얇으면 기체 차단 성능이 낮아지고 파손이 용이해지는 단점이 있다. 따라서 포장지의 두께는 90μm 이상 270μm 이하인 것이 소형 일회용 용기에 사용되는 경우에 있어서, 우수한 기체 차단 성능 및 내구성이 보장되고, 가공이 용이하다는 장점이 있다. 나아가, 제1층(11)의 두께는 10μm 이상 70μm 이하로 형성되고, 제2층(12)의 두께는 40μm 이상 100μm 이하로 형성되고, 제3층(13)의 두께는 40μm 이상 100μm 이하로 각각 형성되는 것이 가공성을 향상시킬 수 있다. 바람직하게 제1층(11)의 두께는 30μm로 형성되고, 제2층(12)과 제3층(13)의 두께는 60μm로 형성될 수 있다. 이로써, 제1층(11)의 두께는 제2층(12)의 두께 및 제3층(13)의 두께보다 얇게 형성될 수 있다.The thickness of the recycled wrapping paper 1 according to an embodiment of the present invention may be 90 μm or more and 270 μm or less. If the wrapping paper is too thick, processing is difficult and manufacturing cost is high, and if it is too thin, gas barrier performance is lowered and breakage is easy. Therefore, when the thickness of the wrapping paper is 90 μm or more and 270 μm or less is used for a small disposable container, excellent gas barrier performance and durability are guaranteed, and processing is easy. Furthermore, the thickness of the first layer 11 is formed to be 10 μm or more and 70 μm or less, the second layer 12 has a thickness of 40 μm or more and 100 μm or less, and the thickness of the third layer 13 is 40 μm or more and 100 μm or less. Forming each can improve workability. Preferably, the thickness of the first layer 11 may be formed to be 30 μm, and the thickness of the second layer 12 and the third layer 13 may be formed to be 60 μm. Accordingly, the thickness of the first layer 11 may be formed to be thinner than the thickness of the second layer 12 and the thickness of the third layer 13 .

요홈부(16)의 깊이는 15μm 이상, 재활용 포장지(1)의 두께의 70% 이하일 수 있다. 예를 들어, 재활용 포장지(1)의 두께가 90μm인 경우 요홈부(16)의 깊이는 15μm 이상 63μm 이하일 수 있다. 또한, 재활용 포장지(1)의 두께가 270μm인 경우 요홈부(16)의 깊이는 15μm 이상 189μm 이하일 수 있다. 또한, 재활용 포장지(1)의 두께가 150μm인 경우, 요홈부(16)의 깊이는 15μm 이상 105μm 이하일 수 있다. The depth of the recessed portion 16 may be 15 μm or more, and 70% or less of the thickness of the recycled wrapping paper 1 . For example, when the thickness of the recycled wrapping paper 1 is 90 μm, the depth of the recess 16 may be 15 μm or more and 63 μm or less. In addition, when the thickness of the recycled wrapping paper 1 is 270 μm, the depth of the recess 16 may be 15 μm or more and 189 μm or less. In addition, when the thickness of the recycled wrapping paper 1 is 150 μm, the depth of the recess 16 may be 15 μm or more and 105 μm or less.

요홈부(16)의 깊이가 너무 깊으면 포장지의 내구성 및 기체 차단 성능이 낮아지는 단점이 있다. 요홈부(16)의 깊이가 너무 얕으면 포장지를 구성하는 복수 개의 필름 간의 인장력 차이로 인한 포장지가 말려들어가는 것을 방지하는 효과가 낮아질 수 있다. 따라서, 요홈부(16)의 깊이는 15μm 이상, 재활용 포장지(1)의 두께의 70% 이하인 것이, 소형 일회용 용기에 사용되는 경우에 있어서, 포장지의 우수한 기체 차단 성능 및 내구성을 확보하고, 포장지가 가공될 때 말려들어가는 것도 방지할 수 있다는 장점이 있다.If the depth of the concave portion 16 is too deep, there is a disadvantage in that the durability and gas barrier performance of the wrapping paper are lowered. If the depth of the concave portion 16 is too shallow, the effect of preventing the wrapping paper from being drawn in due to a difference in tensile force between a plurality of films constituting the wrapping paper may be lowered. Therefore, the depth of the recessed portion 16 is 15 μm or more and 70% or less of the thickness of the recycled wrapping paper 1, when used in a small disposable container, to ensure excellent gas barrier performance and durability of the wrapping paper, It also has the advantage of being able to prevent curling up during processing.

도 6은 본 발명의 변형된 실시예에 따른 재활용 포장지의 요홈부의 다양한 실시형태를 보여주는 도면이다. 도 7은 본 발명의 변형된 실시예에 따른 재활용 포장지의 요홈부의 활용형태를 보여주는 도면이다.6 is a view showing various embodiments of the groove portion of the recycled wrapping paper according to a modified embodiment of the present invention. 7 is a view showing the utilization form of the recessed portion of the recycled wrapping paper according to a modified embodiment of the present invention.

도 6 및 도 7을 참조하면, 요홈부(16a)는 포장지의 일측면 및 타측면 중 어느 하나의 측면에 격자무늬 패턴으로 형성될 수 있다(도 6의 (a) 참조). 이러한 형태의 요홈부(16a)는 일반적으로 직선의 패턴을 가지는 반칼 가공이 용이하다는 장점이 있다. 또한, 요홈부(16a)는 재활용 포장지(1')가 컵용기의 덮개로 사용되는 경우에 있어서, 재활용 표장지(1')의 표면에 복수 개의 홈이 파여져 있으므로 빨대(S)의 삽입을 용이하게 할 수 있다는 장점이 있다.Referring to FIGS. 6 and 7 , the concave portion 16a may be formed in a lattice pattern on any one of one side and the other side of the wrapping paper (see FIG. 6(a) ). The concave portion 16a of this type has the advantage of being easy to cut with a knife having a generally straight pattern. In addition, the recessed portion 16a facilitates insertion of the straw (S) because a plurality of grooves are dug in the surface of the recycled wrapping paper 1' when the recycled wrapping paper 1' is used as the cover of the cup container. There are advantages to being able to do it.

또한, 요홈부(16b)는 서로 다른 직경을 가지는 동심원 패턴으로 복수 개 형성될 수 있다(도 6의 (b) 참조). 예를 들어 원통형의 일회용 커피의 개방된 상부를 밀폐하기 위한 포장지는 원형으로 형성될 수 있고, 요홈부(16b)는 포장지의 형상에 대응하는 원형으로 형성될 수 있다. 나아가, 요홈부(16b)는 동심원 패턴으로 각각 다른 직경을 가지는 원형 라인의 형태로 복수 개가 형성될 수 있다. 상기 원형 라인은 상호 동일한 간격을 가지고 이격되어 배치될 수 있다. 이로써, 포장지의 모든 방향에서 작용되는 수축력 및 인장력을 흡수하여 포장지가 말려들어가는 것을 방지할 수 있는 효과가 있다.In addition, a plurality of recessed portions 16b may be formed in a concentric circle pattern having different diameters (see FIG. 6(b) ). For example, the wrapping paper for sealing the open upper part of the cylindrical disposable coffee may be formed in a circular shape, and the concave portion 16b may be formed in a circular shape corresponding to the shape of the wrapping paper. Furthermore, a plurality of recessed portions 16b may be formed in the form of circular lines having different diameters in a concentric circle pattern. The circular lines may be spaced apart from each other at the same distance. Thereby, there is an effect of absorbing the contractile and tensile forces acting in all directions of the wrapping paper to prevent the wrapping paper from being drawn in.

또한, 요홈부(16c)는 포장지의 일측면 상에 점선의 형태로 형성될 수 있다(도 6의 (c) 참조). 예를 들어, 포장지의 일측면 상에 동심원 패턴으로 각각 다른 직경을 가지는 원형 라인 상에 점선의 형태로 형성될 수 있다. 이로써, 직선 형태로 형성되는 요홈부(16c)보다 포장지의 내구성을 향상시킬 수 있는 효과가 있다.In addition, the concave portion 16c may be formed in the form of a dotted line on one side of the wrapping paper (see FIG. 6(c)). For example, it may be formed in the form of a dotted line on a circular line having a different diameter in a concentric circle pattern on one side of the wrapping paper. Accordingly, there is an effect that can improve the durability of the wrapping paper than the recessed portion 16c formed in a straight shape.

이상으로 설명한, 본 발명의 다양한 실시예들에 따른 재활용 포장지(1~4)는 폴리프로필렌계 수지 소재로 형성되는 식품 용기 형태의 포장대상물에 사용되며, 다수의 폴리프로필렌계 수지 소재의 필름이 적층 형성되어, 포장대상물을 재활용하기 위해 분리배출 및 가공할 때 포장지를 따로 제거할 필요가 없어서 재활용 작업이 수월해지는 효과가 있다.As described above, the recycled wrapping papers 1 to 4 according to various embodiments of the present invention are used for packaging objects in the form of food containers formed of polypropylene-based resin materials, and a plurality of polypropylene-based resin films are laminated. Formed, there is no need to separately remove the wrapping paper when discharging and processing to recycle the packaging object, thereby making recycling easier.

또한, 본 발명의 다양한 실시예들에 따른 재활용 포장지는 인장력이 높은 소재의 필름이 배치된 일측면에 요홈부(16)를 형성하여, 필름 간의 인장력 차이로 인하여 포장지가 말려들어가는 현상을 방지할 수 있는 효과가 있다.In addition, the recycled wrapping paper according to various embodiments of the present invention forms a recess 16 on one side where a film of a material having high tensile force is disposed, thereby preventing the wrapping paper from being rolled up due to a difference in tensile force between the films. there is an effect

이상의 설명은 본 발명의 기술적 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예는 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술적 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.The above description is merely illustrative of the technical idea of the present invention, and various modifications and variations will be possible without departing from the essential characteristics of the present invention by those skilled in the art to which the present invention pertains. Therefore, the embodiments disclosed in the present invention are not intended to limit the technical spirit of the present invention, but to explain, and the scope of the technical spirit of the present invention is not limited by these embodiments. The protection scope of the present invention should be construed by the following claims, and all technical ideas within the scope equivalent thereto should be construed as being included in the scope of the present invention.

1: 재활용 포장지
11: 제1층
12: 제2층
13: 제3층
14: 베리어 코팅층
15: 인쇄층
16: 요홈부1: Recycled wrapping paper
11: 1st floor
12: 2nd floor
13: 3rd floor
14: barrier coating layer
15: print layer
16: groove

Claims (12)

폴리프로필렌계 수지 소재를 포함하는 포장대상물을 포장하는 재활용 포장지에 있어서,
무연신 폴리프로필렌계 수지로 구성되는 접착필름을 포함하고, 상기 포장대상물에 인접하는 제1층;
상기 제1층의 상층에 배치되는 폴리프로필렌계 수지 필름을 포함하는 제2층;
상기 제2층의 상층에 배치되는 폴리프로필렌계 수지 필름을 포함하는 제3층;
상기 제1층과 상기 제2층의 사이에 배치되고, 유기계 소재를 포함하는 베리어 코팅층; 및
상기 제2층과 상기 제3층의 사이에 배치되고, 잉크가 인쇄된 인쇄층을 포함하되,
상기 포장대상물에 면접하는 일측면 및 타측면 중 어느 하나에 형성되는 요홈부를 포함하고,
상기 요홈부는 상기 베리어 코팅층에 침투되지 않는 깊이로 형성되는 것이고,
상기 요홈부가 상기 타측면에 형성되는 경우에, 상기 요홈부는 상기 제3층에 형성되고, 상기 요홈부의 깊이는 상기 제2층의 두께, 상기 인쇄층의 두께 및 상기 제3층의 두께를 합한 깊이 이하로 형성되는 것이고,
상기 요홈부는 상기 인쇄층 및 상기 제2층에 더 형성되고, 상기 요홈부의 깊이는 상기 인쇄층 및 상기 제3층의 두께를 합한 깊이 이상으로 형성되는 것이고,
상기 요홈부는 상기 일측면 및 타측면 중 어느 하나의 측면에 격자무늬 패턴으로 형성되며, 상기 제1층 내지 제3층의 필름 간의 인장력 차이로 인해 상기 포장지가 가공될 때 말려들어가는 것을 방지하는 것인, 재활용 포장지.In the recycled packaging paper for packaging a packaging object containing a polypropylene-based resin material,
a first layer comprising an adhesive film made of a non-stretched polypropylene resin and adjacent to the packaging object;
a second layer including a polypropylene-based resin film disposed on an upper layer of the first layer;
a third layer including a polypropylene-based resin film disposed on an upper layer of the second layer;
a barrier coating layer disposed between the first layer and the second layer and including an organic material; and
It is disposed between the second layer and the third layer, comprising a printed layer printed with ink,
Containing a concave portion formed in any one of the one side and the other side to face the packaging object,
The concave portion is formed to a depth that does not penetrate into the barrier coating layer,
When the recess is formed on the other side, the recess is formed in the third layer, and the depth of the recess is the sum of the thickness of the second layer, the thickness of the printed layer, and the thickness of the third layer. is formed below,
The concave portion is further formed in the printed layer and the second layer, and the depth of the concave portion is formed to be greater than or equal to the sum of the thicknesses of the printed layer and the third layer,
The concave portion is formed in a lattice pattern on either side of the one side and the other side, and prevents the wrapping paper from being drawn in when processing due to the difference in tensile force between the films of the first layer to the third layer. , recycled wrapping paper. 제1항에 있어서,
상기 제2층의 상기 폴리프로필렌계 수지 필름은 연신 폴리프로필렌계 수지 필름이고,
상기 제3층의 상기 폴리프로필렌계 수지 필름은 연신 폴리프로필렌계 수지 필름인, 재활용 포장지.According to claim 1,
The polypropylene-based resin film of the second layer is a stretched polypropylene-based resin film,
The polypropylene-based resin film of the third layer is a stretched polypropylene-based resin film, recycled wrapping paper. 제1항에 있어서,
상기 제2층의 상기 폴리프로필렌계 수지 필름은 무연신 폴리프로필렌계 수지 필름이고,
상기 제3층의 상기 폴리프로필렌계 수지 필름은 연신 폴리프로필렌계 수지 필름인, 재활용 포장지.According to claim 1,
The polypropylene-based resin film of the second layer is an unstretched polypropylene-based resin film,
The polypropylene-based resin film of the third layer is a stretched polypropylene-based resin film, recycled wrapping paper. 제1항에 있어서,
상기 제2층의 상기 폴리프로필렌계 수지 필름은 연신 폴리프로필렌계 수지 필름이고,
상기 제3층의 상기 폴리프로필렌계 수지 필름은 무연신 폴리프로필렌계 수지 필름인, 재활용 포장지.According to claim 1,
The polypropylene-based resin film of the second layer is a stretched polypropylene-based resin film,
The polypropylene-based resin film of the third layer is a non-stretched polypropylene-based resin film, recycled wrapping paper. 제1항에 있어서,
상기 제2층의 상기 폴리프로필렌계 수지 필름은 무연신 폴리프로필렌계 수지 필름이고,
상기 제3층의 상기 폴리프로필렌계 수지 필름은 무연신 폴리프로필렌계 수지 필름인, 재활용 포장지.According to claim 1,
The polypropylene-based resin film of the second layer is an unstretched polypropylene-based resin film,
The polypropylene-based resin film of the third layer is a non-stretched polypropylene-based resin film, recycled wrapping paper. 제1항에 있어서,
상기 제1층의 두께는 상기 제2층의 두께 및 상기 제3층의 두께보다 얇게 형성되는, 재활용 포장지.According to claim 1,
The thickness of the first layer is formed thinner than the thickness of the second layer and the thickness of the third layer, recycled wrapping paper. 제1항에 있어서,
상기 베리어 코팅층은 상기 제1층 상에 건식 적층되는, 재활용 포장지.According to claim 1,
The barrier coating layer is dry laminated on the first layer, recycled wrapping paper. 삭제delete 삭제delete 삭제delete 삭제delete 제1항에 있어서,
상기 제1층의 두께는 10μm 이상 70μm 이하로 형성되고, 상기 제2층의 두께는 40μm 이상 100μm 이하로 형성되고, 상기 제3층의 두께는 40μm 이상 100μm 이하로 형성되는, 재활용 포장지.According to claim 1,
The first layer has a thickness of 10 μm or more and 70 μm or less, the second layer has a thickness of 40 μm or more and 100 μm or less, and the third layer has a thickness of 40 μm or more and 100 μm or less.
KR1020190065675A 2019-06-04 2019-06-04 Recyclable packaging paper KR102272170B1 (en)