KR102176356B1 - Sealing tape composition and product comprisign the same - Google Patents

Sealing tape composition and product comprisign the same Download PDF

Info

Publication number
KR102176356B1
KR102176356B1 KR1020180166290A KR20180166290A KR102176356B1 KR 102176356 B1 KR102176356 B1 KR 102176356B1 KR 1020180166290 A KR1020180166290 A KR 1020180166290A KR 20180166290 A KR20180166290 A KR 20180166290A KR 102176356 B1 KR102176356 B1 KR 102176356B1
Authority
KR
South Korea
Prior art keywords
weight
sealing tape
less
styrene
filler
Prior art date
Application number
KR1020180166290A
Other languages
Korean (ko)
Other versions
KR20200077103A (en
Inventor
박광수
Original Assignee
주식회사 오아시스
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 오아시스 filed Critical 주식회사 오아시스
Priority to KR1020180166290A priority Critical patent/KR102176356B1/en
Publication of KR20200077103A publication Critical patent/KR20200077103A/en
Application granted granted Critical
Publication of KR102176356B1 publication Critical patent/KR102176356B1/en

Abstract

본 발명은 실링테이프 조성물에 관한 것으로써, 보다 상세하게는, 충진제, 발포제, 알루미늄 및 아연을 일정성분비로 포함함으로써, 테이프의 유연성 및 난연성이 증가되고, 대상물의 부식을 방지하는 실링테이프 조성물에 관한 것이다. The present invention relates to a sealing tape composition, and more particularly, to a sealing tape composition that increases the flexibility and flame retardancy of the tape and prevents corrosion of the object by including a filler, a foaming agent, aluminum and zinc in a constant component ratio. will be.

Description

실링테이프 조성물 및 이를 포함하는 성형품{SEALING TAPE COMPOSITION AND PRODUCT COMPRISIGN THE SAME} Sealing tape composition and molded article comprising the same TECHNICAL FIELD

본 발명은 실링테이프 조성물 및 성형품에 관한 것으로써, 보다 상세하게는, 충진제, 발포제, 알루미늄 및 아연을 일정성분비로 포함함으로써, 테이프의 유연성 및 난연성이 증가되고, 대상물의 부식을 방지하는 실링테이프 조성물 및 성형품에 관한 것이다. The present invention relates to a sealing tape composition and a molded article, and more particularly, by including a filler, a foaming agent, aluminum and zinc in a constant component ratio, the flexibility and flame retardancy of the tape is increased, and the sealing tape composition to prevent corrosion of the object And a molded article.

실링제에 사용되는 바인더는 다양한 수지군으로부터 선택되어지며, 그 예로 우레탄계 실링제, 설파이드계 실링제 및 실리콘계 실링제 등이 다양하게 알려져 있으며, 특히 우레탄계 실링제가 유용하게 사용되고 있는 실정이다. The binder used for the sealing agent is selected from various resin groups, for example, a urethane-based sealing agent, a sulfide-based sealing agent, and a silicone-based sealing agent are variously known, and in particular, a urethane-based sealing agent is usefully used.

이러한 실링제는 다양한 분야 구체적으로, 건축, 자동차 및 전자 산업 등에 다양하게 사용되고 있는 바, 각각의 분야에 따라 실링제에 요구되는 물성이 상이하다. 이중, 건축 구체적으로 건축물에 차양막을 설치하는 경우 리벳팅(볼팅, 피스)의 작업 후 종래 통상적으로 사용되는 실리콘계 실러 또는 우레탄계 실러 등을 사용하고 있다. 그러나, 이의 실링제를 사용하는 경우 외부 온도차에 의한 수축 및 팽창이 반복적으로 수행되어 사용된 실링제와 건축구조물간에 박리가 일어나거나 시간이 지남에 따라 균열, 잔금, 또는 표면이 딱딱해지는 현상이 발생하여 누수의 문제를 일으켜 왔으며, 이러한 누수는 건축물 자체의 기능 및 수명을 저해하는 요인으로 작용하고 있는 실정이다. These sealing agents are used in various fields, specifically, in the construction, automobile, and electronic industries, and the like, and physical properties required for the sealing agent are different according to each field. Among them, in the case of installing a sunshade on a building, specifically, a silicone-based sealer or a urethane-based sealer, which is conventionally used after riveting (bolting, piece) work, is used. However, when its sealing agent is used, shrinkage and expansion are repeatedly performed due to external temperature difference, and peeling occurs between the used sealing agent and the building structure, or cracks, residues, or surface hardening occur over time. As a result, it has caused a problem of water leakage, and this leakage is acting as a factor that hinders the function and life of the building itself.

이와 관련해서 수축 및 팽창에 의해 물성이 변형되지 않는 실링테이프 조성물이 필요한 실정이다. In this regard, there is a need for a sealing tape composition that does not deform physical properties due to contraction and expansion.

한국공개특허 제10-1997-0042918호Korean Patent Publication No. 10-1997-0042918

본 발명은 상술된 문제점을 해결하기 위해 안출된 것으로, 본 발명의 목적은, 충진제 및 발포제를 추가하여 스티렌-부타디엔-스티렌(SBS) 내부 공간을 확보하여 온도차에 의해 수축 및 팽창될 수 있는 공간 확보 가능한 실링테이프 조성물 및 성형품을 제공하는 것이다. The present invention was conceived to solve the above-described problems, and an object of the present invention is to secure a space that can shrink and expand due to a temperature difference by securing an internal space of styrene-butadiene-styrene (SBS) by adding a filler and a foaming agent. It is to provide a possible sealing tape composition and molded article.

또한, 본 발명의 목적은, 발포제를 더 추가하여 실링테이프의 유연성을 증가시킬 수 있는 실링테이프 조성물 및 성형품을 제공하는 것이다. In addition, an object of the present invention is to provide a sealing tape composition and a molded article capable of increasing the flexibility of the sealing tape by further adding a foaming agent.

또한, 본 발명의 목적은, 알루미늄 및 아연을 포함하여 불/열에 형태가 변형되는 것을 방지하고 대상물의 부식을 방지할 수 있는 실링테이프 조성물 및 성형품을 제공하는 것이다. In addition, it is an object of the present invention to provide a sealing tape composition and a molded article capable of preventing the object from being deformed by fire/heat, including aluminum and zinc, and preventing corrosion of an object.

본 발명의 일 실시예에 따른 실링테이프 조성물은 스티렌-부타디엔-스티렌 중합체(SBS), 염소화폴리에틸렌(Chlorinated Polyethylene, CPE), 디부틸히드록시톨루엔(Butylated Hydroxytoluene, BHT), 탄산칼슘, MGO, 충진제, 스테아린산(Stearic Acid), 폴리에틸렌왁스, 이산화타이타늄(TiO2) 및 디이소노닐 프탈레이트(DINP)를 포함하는 것을 특징으로 한다. Sealing tape composition according to an embodiment of the present invention is styrene-butadiene-styrene polymer (SBS), chlorinated polyethylene (CPE), dibutylhydroxytoluene (Butylated Hydroxytoluene, BHT), calcium carbonate, MGO, filler, It characterized in that it comprises stearic acid (Stearic Acid), polyethylene wax, titanium dioxide (TiO 2 ) and diisononyl phthalate (DINP).

일 실시예에서, 스티렌-부타디엔-스티렌 중합체(SBS) 16~35중량%, 염소화폴리에틸렌(CPE) 7~12중량%, 디부틸히드록시톨루엔(BHT) 1중량% 이하, 탄산칼슘 17~38중량%, MGO 1~2.5중량%, 충진제 70중량% 이하, 스테아린산(Stearic Acid) 0.6중량% 이하, 폴리에틸렌왁스 0.6중량% 이하, 이산화타이타늄(TiO2) 1.5중량% 이하 및 디이소노닐프탈레이트(DINP) 1~8중량%인 것을 특징으로 한다. In one embodiment, styrene-butadiene-styrene polymer (SBS) 16 to 35% by weight, chlorinated polyethylene (CPE) 7 to 12% by weight, dibutylhydroxytoluene (BHT) 1% by weight or less, calcium carbonate 17 to 38% by weight %, MGO 1 to 2.5 wt%, filler 70 wt% or less, stearic acid 0.6 wt% or less, polyethylene wax 0.6 wt% or less, titanium dioxide (TiO 2 ) 1.5 wt% or less and diisononylphthalate (DINP) It is characterized in that 1 to 8% by weight.

일 실시예에서, 상기 충진제는, 클레이(CLAY) 및 탈크(TALC) 중 어느 하나 이상을 포함하는 것을 특징으로 한다. In one embodiment, the filler is characterized in that it contains any one or more of clay (CLAY) and talc (TALC).

일 실시예에서, 상기 충진제는, 클레이(CLAY) 4~42중량% 및 탈크(TALC) 26중량% 이하인 것을 특징으로 한다. In one embodiment, the filler is characterized in that 4 to 42% by weight of clay (CLAY) and 26% by weight of talc (TALC) or less.

일 실시예에서, 발포제, 알루미늄 및 아연 중 어느 하나 이상을 더 포함하는 것을 특징으로 한다. In one embodiment, it is characterized in that it further comprises any one or more of a blowing agent, aluminum and zinc.

일 실시예에서, 발포제 0.5중량% 이하, 알루미늄 1중량% 이하 및 아연 1중량% 이하인 것을 특징으로 한다. In one embodiment, it is characterized in that the blowing agent is 0.5% by weight or less, aluminum 1% by weight or less and zinc 1% by weight or less.

본 발명의 일 실시예에 따른 실링테이프 조성물을 이용하여 제조된 실링테이프 성형품은 본 발명에 따른 실링테이프 조성물을 포함하는 것을 특징으로 한다. The sealing tape molded article manufactured by using the sealing tape composition according to an embodiment of the present invention is characterized in that it comprises the sealing tape composition according to the present invention.

일 실시예에서, 3중굴곡 형태로 제공되는 것을 특징으로 한다. In one embodiment, it is characterized in that it is provided in the form of a triple bend.

본 발명에 따르면, 충진제 및 발포제를 추가하여 스티렌-부타디엔-스티렌(SBS) 내부 공간을 확보하여 온도에 따라 실링테이프가 수축 및 팽창할 수 있는 공간을 확보하여 실링테이프에 균열, 잔금 또는 표면이 딱딱해지는 현상을 방지하는 효과가 발생하게 된다. According to the present invention, by adding a filler and a foaming agent to secure an internal space of styrene-butadiene-styrene (SBS), a space for the sealing tape to shrink and expand depending on temperature is secured, and the sealing tape is cracked, left behind, or the surface is hard. The effect of preventing the falling phenomenon occurs.

또한, 발포제를 더 추가하여 실링테이프의 유연성을 증가시킬 수 있는 효과가 발생하게 된다. In addition, by adding a foaming agent, the effect of increasing the flexibility of the sealing tape occurs.

또한, 본 발명의 목적은, 알루미늄 및 아연을 포함하여 불/열에 형태가 변형되는 것을 방지하고 대상물의 부식을 방지할 수 있는 효과가 발생하게 된다. In addition, it is an object of the present invention to produce an effect of preventing the object from being deformed by fire/heat including aluminum and zinc and preventing corrosion of the object.

본 발명을 첨부된 도면을 참조하여 상세히 설명하면 다음과 같다. 여기서, 반복되는 설명, 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 상세한 설명은 생략한다. 본 발명의 실시형태는 당 업계에서 평균적인 지식을 가진 자에게 본 발명을 완전하게 설명하기 위해서 제공되는 것이다. 따라서, 도면에서의 요소들의 형상 및 크기 등은 보다 명확한 설명을 위하여 과장될 수 있다. The present invention will be described in detail with reference to the accompanying drawings as follows. Here, repeated descriptions and detailed descriptions of known functions and configurations that may unnecessarily obscure the subject matter of the present invention will be omitted. Embodiments of the present invention are provided to completely explain the present invention to those with average knowledge in the art. Accordingly, the shapes and sizes of elements in the drawings may be exaggerated for clearer explanation.

명세서 전체에서, 어떤 부분이 어떤 구성 요소를 "포함"한다고 할 때, 이는 특별히 반대되는 기재가 없는 한 다른 구성 요소를 제외하는 것이 아니라 다른 구성 요소를 더 포함할 수 있는 것을 의미한다. Throughout the specification, when a part "includes" a certain component, it means that other components may be further included rather than excluding other components unless otherwise stated.

이하, 본 발명의 이해를 돕기 위하여 바람직한 실시예를 제시한다. 그러나 하기의 실시예는 본 발명을 보다 용이하게 이해하기 위하여 제공되는 것일 뿐, 실시예에 의해 본 발명의 내용이 한정되는 것은 아니다. Hereinafter, a preferred embodiment is presented to aid the understanding of the present invention. However, the following examples are only provided to more easily understand the present invention, and the contents of the present invention are not limited by the examples.

<< 실링테이프Sealing tape 조성물> Composition>

본 발명에 따른 실링테이프 조성물은 스티렌-부타디엔-스티렌 중합체(Styrene-Butadiene-Styrene, SBS), 염소화폴리에틸렌(Chlorinated Polyethylene, CPE), 디부틸히드록시톨루엔(Butylated Hydroxytoluene, BHT), 탄산칼슘, MGO, 충진제, 스테아린산(Stearic Acid), 폴리에틸렌왁스, 이산화 타이타늄(TiO2) 및 디이소노닐 프탈레이트(DINP)를 포함할 수 있다. The sealing tape composition according to the present invention is a styrene-butadiene-styrene polymer (Styrene-Butadiene-Styrene, SBS), chlorinated polyethylene (CPE), dibutylhydroxytoluene (BHT), calcium carbonate, MGO, Fillers, stearic acid, polyethylene wax, titanium dioxide (TiO2), and diisononyl phthalate (DINP) may be included.

스티렌-부타디엔-스티렌은 스티렌과 부타디엔 두 가지 단량체를 가지고 만들어지는 열가소성 탄성체로 플라스틱과 고무의 성질을 동시에 발현하는 특성이 있다. 그래서 플라스틱 개질제, 아스팔트 개질제, 접착제 등의 용도로 사용될 수 있다. Styrene-butadiene-styrene is a thermoplastic elastomer made of two monomers, styrene and butadiene, and has the property of simultaneously expressing the properties of plastic and rubber. So, it can be used for plastic modifiers, asphalt modifiers, and adhesives.

본 발명에 따른 실링테이프 조성물은 스티렌-부타디엔-스티렌 중합체가 16~35중량% 포함될 수 있다. 16중량% 미만 포함될 경우, 경도 및 강도가 낮아 가공성이 저하되는 등 실링테이프의 물성이 감소되며, 35중량% 초과일 경우, 경도 및 강도가 지나치게 증가하여 취성점이 높아지는 문제가 발생할 수 있다. The sealing tape composition according to the present invention may contain 16 to 35% by weight of a styrene-butadiene-styrene polymer. If it is included in less than 16% by weight, the physical properties of the sealing tape are reduced, such as lowering of workability due to low hardness and strength, and when it is more than 35% by weight, the hardness and strength may be excessively increased, resulting in a problem of increasing brittleness.

염소화폴리에틸렌은 HDPE powder의 염소화를 통해 제조되는 고무재료로서, 내후성, 내오존성 및 내약품성이 뛰어나고 난연성과 절연성이 좋다는 특성을 가지고 있다. 이같은 특성 때문에 CPE는 주로 PVC 충격보강제, 고무전선용 소재 및 난연 ABS용으로 적용되었다. Chlorinated polyethylene is a rubber material manufactured through chlorination of HDPE powder, and has excellent weather resistance, ozone resistance and chemical resistance, and good flame retardancy and insulation. Because of these characteristics, CPE was mainly applied for PVC impact modifiers, rubber wire materials, and flame-retardant ABS.

본 발명에 따른 실링테이프 조성물은 염소화 폴리에틸렌을 7~12중량% 포함될 수 있다. 염소화 폴리에틸렌이 7중량% 미만일 경우, 내후성, 내오존성, 내약품성 및 난연성이 떨어져 열, 불, 오존 및 약품에 취약해지는 문제가 발생할 수 있다. 그리고, 염소화 폴리에틸렌 함량이 12중량% 초과일 경우, 실링테이프의 형태 변형이 용이하지 않은 문제가 발생할 수 있다. The sealing tape composition according to the present invention may contain 7 to 12% by weight of chlorinated polyethylene. If the chlorinated polyethylene is less than 7% by weight, weather resistance, ozone resistance, chemical resistance, and flame retardancy are poor, which may lead to problems of being vulnerable to heat, fire, ozone and chemicals. In addition, when the chlorinated polyethylene content exceeds 12% by weight, a problem in which the sealing tape is not easily deformed may occur.

디부틸히드록시톨루엔은 스티렌-부타디엔-스티렌 중합체 및 염소화 폴리에틸렌의 산화를 방지하는 노화방지제(혹은 산화방지제)로 노화 현상의 주요 인자인 산소에 의해서 자동산화되는 연쇄반응을 정지시키는 작용을 할 수 있다. 그리고, 디부틸히드록시톨루엔은 고무에 대한 용해도가 크고, 휘발성이 작으며 고부에 대하여 비활성 성질을 가지고 있다. Dibutylhydroxytoluene is an antioxidant (or antioxidant) that prevents oxidation of styrene-butadiene-styrene polymers and chlorinated polyethylene, and can stop chain reactions that are automatically oxidized by oxygen, a major factor in aging. . In addition, dibutylhydroxytoluene has high solubility in rubber, low volatility, and has inert properties with respect to high parts.

본 발명에 따른 실링테이프 조성물은 디부틸히드록시톨루엔을 1중량% 이하 포함하고 있다. 디부틸히드록시톨루엔이 1중량% 초과가 포함될 경우, 오히려 노화방지제(산화방지제)의 표면 이동에 의한 외관 오염을 유발할 수 있다. The sealing tape composition according to the present invention contains 1% by weight or less of dibutylhydroxytoluene. When dibutylhydroxytoluene is contained in an amount of more than 1% by weight, it may cause appearance contamination due to surface migration of an anti-aging agent (antioxidant).

충진제는 강도나 각종 성질의 개량을 위하여 혹은 원가절감을 위하여 첨가되는 불활성의 물질로, 실링테이프의 기계적 특성을 향상시킬 수 있다. 충진제는 45~64중량% 포함될 수 있는데, 45중량% 미만 포함될 경우 기계적 특성 개선 효과가 저하될 수 있고, 유동 현상이 발생할 수 있으며, 체적형성이 어려운 문제가 발생할 수 있다. The filler is an inert material added to improve strength or various properties or to reduce cost, and can improve the mechanical properties of the sealing tape. The filler may be contained in an amount of 45 to 64% by weight, and if it is contained in an amount of less than 45% by weight, the effect of improving mechanical properties may be deteriorated, a flow phenomenon may occur, and a problem in which volume formation may be difficult may occur.

64중량% 초과될 경우 실링테이프의 접착력 및 기재에 대한 밀착력이 저하되고, 마모성이 저하되는 문제가 발생할 수 있다. If it exceeds 64% by weight, the adhesive strength of the sealing tape and the adhesion to the substrate may be lowered, and a problem of lowering abrasion may occur.

본 발명의 실링테이프 조성물 중 충진제은 탄산칼슘, 클레이(CLAY) 및 탈크(TALC) 중 어느 하나 이상을 포함하고 있다. 그리고, 실링테이프 조성물에 포함되는 충진제의 총 중량%가 100중량% 일 때, 탄산칼슘 17~38중량%, 클레이(CLAY) 4~42중량% 및 탈크(TALC) 26중량% 이하인 것을 특징으로 한다. The filler in the sealing tape composition of the present invention contains at least one of calcium carbonate, clay (CLAY), and talc (TALC). And, when the total weight% of the filler contained in the sealing tape composition is 100% by weight, it is characterized in that it is 17 to 38% by weight of calcium carbonate, 4 to 42% by weight of clay, and 26% by weight of talc (TALC). .

탄산칼슘은 석회석을 분쇄하여 만든 초미립 분말로서 상온에서 안정한 백색의 알칼리성 성분이다. 그리고, 탄산칼슘은 백색도가 높고 독성이 없기 때문에 주로 플라스틱, 도료, 고무 등의 분야에서 충진제로 많이 사용되고, 백색도, 무광 및 점도조절을 하기 위한 조성물로 사용될 수 있다. Calcium carbonate is a white, alkaline component that is stable at room temperature as an ultra-fine powder made by crushing limestone. And, because calcium carbonate has high whiteness and is not toxic, it is mainly used as a filler in the fields of plastics, paints, and rubber, and can be used as a composition for controlling whiteness, matte, and viscosity.

따라서, 탄산칼슘이 17중량% 미만 포함될 경우, 백색도, 무광 및 점도조절의 효과를 기대하기 어려운 문제가 있다. 그리고, 38중량% 초과일 경우, 점도 조절이 어렵고 가사 시간이 짧아지며 접착제의 탄성을 잃어 딱딱해지는 문제가 있다. Therefore, if less than 17% by weight of calcium carbonate is included, there is a problem that it is difficult to expect the effects of whiteness, matte and viscosity control. And, when it exceeds 38% by weight, it is difficult to control the viscosity, the pot life is shortened, and there is a problem that the elasticity of the adhesive is lost and hardened.

그리고, 클레이는 천연함수규산 알루미늄 광물로 엽납석을 주성분으로 하고, 카올린광물, 세리사이트 및 석영을 수반할 수 있다. 클레이는 실링테이프의 점도조절을 하는 조성물로 4중량% 미만 포함될 경우, 유동 현상이 발생할 수 있으며, 체적형성이 어려운 문제가 발생할 수 있다. 그리고, 42중량% 초과일 경우, 점도 조절이 어렵고 가사 시간이 짧아지며 접착제의 탄성을 잃어 딱딱해지는 문제가 있다. In addition, clay is a natural hydrous aluminum silicate mineral containing pyrophyllite as a main component, and may include kaolin mineral, sericite, and quartz. Clay is a composition that adjusts the viscosity of the sealing tape, and when it is included in less than 4% by weight, a flow phenomenon may occur, and a problem in which volume formation may be difficult may occur. And, when it exceeds 42% by weight, it is difficult to control the viscosity, the pot life is shortened, and there is a problem that the adhesive loses elasticity and becomes hard.

탈크는 천연으로 산출되는 광석 중 가장 경도가 낮은 물질로 활석분이라고 부르기도 한다. 탈크는 연한 광물이므로 충전제로 사용했을 때, 초지용 망의 마모가 적다. 또한, 탈크는 판상결정이므로 인쇄성이 높고 실온 및 고온하에서 높은 강성과 크리프 저항을 나타내는 특징이 있다. Talc is a material with the lowest hardness among natural ores and is sometimes called talc powder. Since talc is a soft mineral, when used as a filler, there is little abrasion of the papermaking net. In addition, since talc is a plate-shaped crystal, it has high printability and exhibits high rigidity and creep resistance at room temperature and high temperature.

본 발명에 따른 실링테이프 조성물의 탈크 함유량이 26중량% 초과일 경우, 실온 및 고온에서 실링테이프의 연성이 낮고 크리프 저항이 높아 외부 압력에 의해 쉽게 손상될 수 있다. When the talc content of the sealing tape composition according to the present invention is more than 26% by weight, the sealing tape has low ductility and high creep resistance at room temperature and high temperature, so that it can be easily damaged by external pressure.

스테아린산 금속 양이온에 부착될 수 있는 극성 머리 부분과 유기 용매에 용해성을 가진 비극성 사슬의 양친매적인 성질을 가지고 있다. 이러한 양친자성으로 인해 계면활성제 및 연화제로 사용될 수 있다. 따라서, 실링테이프에서 스테아린산은 가류촉진제로 가류온도를 낮추고 가류시간을 단축시킬 수 있다. It has the amphiphilic nature of a polar head that can be attached to a stearic acid metal cation and a non-polar chain that is soluble in organic solvents. Due to this amphiphilic nature, it can be used as a surfactant and an emollient. Therefore, stearic acid in the sealing tape is a vulcanization accelerator, which can lower the vulcanization temperature and shorten the vulcanization time.

스테아린산이 0.6중량% 초과일 경우, 실링테이프의 접착 조성물 내에 배합함에 있어서 가공 및 분산시 불양이 발생되고 계면의 물성이 너무 높아지는 문제가 발생하게 된다. When stearic acid is more than 0.6% by weight, defects occur during processing and dispersion in blending into the adhesive composition of the sealing tape, and the physical properties of the interface become too high.

폴리에틸렌왁스는 공기층의 산소에 의한 중합 금지 효과를 차단하기 위하여 사용되는 성분으로서, 이를 함유시키면 표면경화성 및 내오염성이 향상되는 효과가 발생할 수 있다. Polyethylene wax is a component used to block the effect of inhibiting polymerization due to oxygen in the air layer, and when it is contained, the effect of improving the surface hardening property and stain resistance may occur.

따라서, 폴리에틸렌왁스가 0.6중량%를 초과할 경우, 표면경화성이 지나치게 증가하여 실링테이프의 연성이 감소되는 문제가 발생할 수 있다. Therefore, when the polyethylene wax exceeds 0.6% by weight, the surface hardenability is excessively increased, and thus the ductility of the sealing tape may be reduced.

이산화타이타늄은 테이프 상에 도체의 접착성을 제공하는 결합제로서의 역할을 할 수 있다. 그리고, 소성하는 동안 테이프 상에 응력을 최소화하기 위해 도체의 소결 속도를 조정할 수 있으며, 인터페이스(interface)에 이산화타이타늄이 존재하거나 테이프 중으로 미량의 이산화타이타늄이 확산되어 테이프의 기계적 강도를 증진시킬 수 있다. Titanium dioxide can serve as a binder providing adhesion of the conductor onto the tape. In addition, during firing, the sintering rate of the conductor can be adjusted to minimize stress on the tape, and the presence of titanium dioxide at the interface or a trace amount of titanium dioxide can diffuse into the tape, thereby improving the mechanical strength of the tape. .

아울러, 이산화타이타늄은 색상 발현을 위해서 사용하는 성분으로 1.5중량% 이하 범위에서 사용가능하고, 상기 범위 외의 성분 함량 조절에 따라 밝은 회색에서 어두운 회색까지 제품의 색상을 구현할 수 있다. In addition, titanium dioxide is a component used for color expression and can be used in the range of 1.5% by weight or less, and the color of the product from light gray to dark gray can be realized by adjusting the content of components outside the above range.

디이소노닐프탈레이트는 가소제 종류의 하나로 실링테이프의 유연성과 탄성을 향상시키는 역할을 할 수 있다. 여기서, 디이소노닐프탈레이트 ?t량이 1중량% 미만이면 실링테이프의 가소화가 미비하여 발포율의 저하 및 조성물의 배합 작업성이 저하될 수 있고, 8중량% 초과이면 실링테이프의 과도한 가소로 인하여 마모성이 저하되는 문제가 발생할 수 있다. Diisononylphthalate is one of a kind of plasticizer and can improve the flexibility and elasticity of the sealing tape. Here, if the amount of diisononylphthalate ?t is less than 1% by weight, plasticization of the sealing tape may be insufficient, resulting in a decrease in the foaming rate and the blending workability of the composition.If it exceeds 8% by weight, abrasion resistance due to excessive plasticization of the sealing tape This deterioration can cause problems.

본 발명에 따른 실링테이프 조성물은 발포제, 알루미늄 및 아연 중 어느 하나 이상을 더 포함할 수 있고, 발포제 0.5 중량% 이하, 알루미늄 1 중량% 이하 및 아연 1 중량% 이하인 것을 특징으로 한다. The sealing tape composition according to the present invention may further include any one or more of a foaming agent, aluminum and zinc, and is characterized in that the foaming agent is 0.5% by weight or less, aluminum 1% by weight or less, and zinc 1% by weight or less.

발포제는 원료에 혼합하여 스스로 열분해 등의 반응을 일으켜 다량의 기체를 발생시켜 제품 속에 거품을 일으키는 물질로, 본 발명에서는 스티렌-부타디엔-스티렌 중합체를 발포시켜 내부 공간을 만들어 실링테이프를 유연하게 만들어 실링테이프가 대상물에 접착 시 형태 변형을 용이하게 할 수 있다. The foaming agent is a substance that causes a reaction such as thermal decomposition on its own by mixing it with the raw material to generate a large amount of gas to create foam in the product.In the present invention, the styrene-butadiene-styrene polymer is foamed to create an inner space to make the sealing tape flexible to seal. When the tape is adhered to the object, it can be easily deformed.

발포제가 0.5중량% 초과로 포함될 경우, 원료의 기체발생이 과도하여 실링테이프의 기계적 물성이 감소되는 문제가 발생될 수 있다. When the blowing agent is included in an amount of more than 0.5% by weight, there may be a problem in that the mechanical properties of the sealing tape are reduced due to excessive gas generation of the raw material.

알루미늄은 무기계의 대표적인 난연제로, 무독성(비할로겐), 저발연성으로 가공기계의 부식이 적고, 전기 절연성이 우수한 효과가 있다. Aluminum is a representative inorganic flame retardant. It is non-toxic (non-halogen) and has low smoke, so it has less corrosion of processing machines and has excellent electrical insulation properties.

또한, 알루미늄은 실링테이프의 성형성을 증가시키는 효과가 있지만, 알루미늄 함량이 1중량% 초과하면 실링테이프의 기계적 물성이 감소되는 문제가 발생할 수 있다. In addition, although aluminum has an effect of increasing the formability of the sealing tape, when the aluminum content exceeds 1% by weight, a problem of reducing the mechanical properties of the sealing tape may occur.

아연은 철의 부식 속도보다 느리다. 철과 아연(전위가 낮아 이온화 경향이 높음)을 전기적으로 접촉시키면, 아연은 철보다 더 활성적인 금속이 되므로 전위가 낮아 양극으로 작용하고 철은 음극이 된다. 그러므로 아연은 양극 반응(Zn -> Zn2 + + 2e-)을 통해 전자는 음극인 철로 운반되어 철 표면에서 음극 반응으로 소모된다. 즉, 아연은 철에 전기적으로 접촉하기 전보다 더 빠르게 부식되는 반면, 철은 음극 보호를 받아 부식이 매우 느리게 일어나거나 거의 일어나지 않는다. 이러한 원리를 바탕으로 테이프의 점착층에 희생양극 작용을 하는 금속을 첨가해서 테이프 손상시 쉽게 발생하는 녹에 대한 저항성을 가지도록 한다. Zinc is slower than iron's corrosion rate. When iron and zinc (low potential and high ionization tendency) are electrically contacted, zinc becomes a more active metal than iron, so it has a lower potential and acts as an anode, and iron becomes a cathode. Therefore, zinc is transported to the cathode iron through the anodic reaction (Zn -> Zn 2 + + 2e-) and is consumed by the cathode reaction on the iron surface. In other words, zinc corrodes faster than before electrical contact with iron, whereas iron is cathodic protected, so that corrosion occurs very slowly or rarely. Based on this principle, a metal that acts as a sacrificial anode is added to the adhesive layer of the tape so that it has resistance to rust that is easily generated when the tape is damaged.

아연이 1중량% 초과로 포함될 경우, 실링테이프로부터 박리되는 현상이 발생하여 대상물의 방식에 대한 신뢰성이 현저하게 저하되는 문제점이 있다. When zinc is included in an amount of more than 1% by weight, there is a problem in that the reliability of the corrosion of the object is remarkably deteriorated due to the occurrence of peeling from the sealing tape.

<< 실링테이프Sealing tape 성형품> Molded product>

본 발명에 따른 실링테이프 조성물을 이용하여 제조된 실링테이프 성형품은 3중 굴곡 형태를 유지하여 차량패널의 곡선 부위에 부착 시 밀착력이 증가될 수 있다. 즉, 성형품의 일측 표면을 3개의 볼록부를 포함하는 형태로 제공될 수 있다. The sealing tape molded article manufactured using the sealing tape composition according to the present invention maintains a triple bent shape so that adhesion may increase when attached to a curved portion of a vehicle panel. That is, one surface of the molded article may be provided in a form including three convex portions.

아울러, 본 발명에 따른 성형품은 실링테이프 조성물이 발포제를 첨가함으로써 성형품 내부 공간 및 유연성이 증가되어 실링테이프 성형품의 형태변형이 용이하고 차량패널과 밀착력을 증가시키는 효과가 발생될 수 있다. In addition, in the molded article according to the present invention, by adding a foaming agent to the sealing tape composition, the interior space and flexibility of the molded article are increased, so that the shape of the molded article of the sealing tape is easily deformed, and the effect of increasing the adhesion to the vehicle panel may occur.

<비교예><Comparative Example>

기존 실링테이프를 이용하여 경도계 및 비중값을 측정하였다. The hardness tester and specific gravity values were measured using the existing sealing tape.

<실시예><Example>

본 발명에 따른 실링테이프 조성물을 포함하는 성형품을 제조하여 경도계 및 비중값을 측정하였다. A molded article including the sealing tape composition according to the present invention was prepared, and a hardness meter and a specific gravity value were measured.

실시예는 스티렌-부타디엔-스티렌 중합체(SBS) 34.66중량%, 염소화폴리에틸렌(CPE) 7.06중량%, 디부틸히드록시톨루엔(BHT) 1.03중량%, MGO 4.11중량%, 충진제 34.71중량%, 스테아린산(Stearic Acid) 0.51중량%, 폴리에틸렌왁스 0.51 중량%, 이산화타이타늄(TiO2) 1.03 중량%, 디이소노닐프탈레이트(DINP) 2.94 중량%, 발포제 0.12중량%, 알루미늄 12.3중량% 및 아연 1.03중량%를 포함하는 실링테이프 조성물을 포함하는 성형품이다. Examples are styrene-butadiene-styrene polymer (SBS) 34.66 wt%, chlorinated polyethylene (CPE) 7.06 wt%, dibutylhydroxytoluene (BHT) 1.03 wt%, MGO 4.11 wt%, filler 34.71 wt%, stearic acid (Stearic acid) Acid) 0.51 wt%, polyethylene wax 0.51 wt%, titanium dioxide (TiO 2 ) 1.03 wt%, diisononylphthalate (DINP) 2.94 wt%, blowing agent 0.12 wt%, aluminum 12.3 wt%, and zinc 1.03 wt% It is a molded article containing a sealing tape composition.

이때, 충진제는 탄산칼슘 15.3중량%, 클레이(CLAY) 16.47중량% 및 탈크(TALC) 2.94중량%를 포함할 수 있다. In this case, the filler may include 15.3 wt% of calcium carbonate, 16.47 wt% of clay, and 2.94 wt% of talc.

비교예Comparative example 실시예Example 경도Hardness 6262 5454 비중importance 1.3351.335 1.881.88

경도는 물질의 단단함과 무른 정도를 나타내는 값이다. 상기 경도는 쇼어경도시험기로 측정하였는데, 쇼어경도시험기는 추를 h0높이에서 떨어뜨리고, 튀어 오른 높이를 h라하면, 쇼어경도 Hs는 H0(10,000/65)*(h/h0)로 표시된다. Hardness is a measure of the hardness and softness of a material. The hardness was measured with a shore hardness tester, and the shore hardness tester drops the weight from the height h0, and if the bounced height is h, the shore hardness Hs is expressed as H0(10,000/65)*(h/h0).

따라서, 쇼어경도값은 그 값이 클수록 딱딱한 물질이고 작을수록 연한 물질이라고 생각될 수 있다. Accordingly, it can be considered that the larger the Shore hardness value is, the harder it is and the smaller it is, the softer it is.

표 1을 참고하면, 실시예가 비교예보다 경도값이 낮게 측정되었고, 따라서, 실시예는 종래 실링테이프보다 무른 성질을 가지고 있다고 판단될 수 있다. Referring to Table 1, the Example was measured to have a lower hardness value than the Comparative Example, and thus, it can be determined that the Example has a softer property than the conventional sealing tape.

그리고, 실시예는 무른 성질을 가지고 있어, 손으로 성형이 가능하고 이에 따라 부착 대상물과 밀착력이 증가되는 효과가 발생할 수 있다. In addition, since the embodiment has a soft property, it can be molded by hand, and accordingly, an effect of increasing adhesion to the object to be attached may occur.

상기에서는 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술 분야의 숙련된 당업자는 하기의 특허 청구의 범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. Although the above has been described with reference to preferred embodiments of the present invention, those skilled in the art will variously modify and change the present invention within the scope not departing from the spirit and scope of the present invention described in the following claims. You will understand that you can do it.

Claims (8)

스티렌-부타디엔-스티렌 중합체(Styrene-Butadiene-Styrene, SBS), 염소화폴리에틸렌(Chlorinated Polyethylene, CPE), 디부틸히드록시톨루엔(Butylated Hydroxytoluene, BHT), MgO, 충진제, 스테아린산(Stearic Acid), 폴리에틸렌왁스, 이산화타이타늄(TiO2) 및 디이소노닐프탈레이트(DINP)를 포함하는 실링테이프 조성물을 이용하여 제조되고, 3중 굴곡 형태로 제공되는,
실링테이프 성형품.
Styrene-Butadiene-Styrene (SBS), Chlorinated Polyethylene (CPE), Butylated Hydroxytoluene (BHT), MgO, Filler, Stearic Acid, Polyethylene Wax, Prepared by using a sealing tape composition comprising titanium dioxide (TiO2) and diisononylphthalate (DINP), and provided in a triple bent form,
Sealing tape molded product.
 제1항에 있어서,
상기 실링테이프 조성물은,
스티렌-부타디엔-스티렌 중합체(SBS) 16~35중량%, 염소화폴리에틸렌(CPE) 7~12중량%, 디부틸히드록시톨루엔(BHT) 1중량% 이하, MgO 1~2.5중량%, 충진제 45~64중량% 이하, 스테아린산(Stearic Acid) 0.6중량% 이하, 폴리에틸렌왁스 0.6 중량% 이하, 이산화타이타늄(TiO2) 1.5 중량% 이하 및 디이소노닐프탈레이트(DINP) 1~8 중량%인 것을 특징으로 하는, 실링테이프 성형품.
The method of claim 1,
The sealing tape composition,
Styrene-butadiene-styrene polymer (SBS) 16 to 35 wt%, chlorinated polyethylene (CPE) 7 to 12 wt%, dibutylhydroxytoluene (BHT) 1 wt% or less, MgO 1 to 2.5 wt%, filler 45 to 64 Sealing, characterized in that it is not more than 0.6% by weight of stearic acid, 0.6% by weight of polyethylene wax, 1.5% by weight or less of titanium dioxide (TiO2) and 1 to 8% by weight of diisononylphthalate (DINP) Tape moldings.
 제1항에 있어서,
상기 충진제는,
탄산칼슘, 클레이(CLAY) 및 탈크(TALC) 중 어느 하나 이상을 포함하는 것을 특징으로 하는, 실링테이프 성형품.
The method of claim 1,
The filler,
Calcium carbonate, clay (CLAY) and talc (TALC) characterized in that it comprises any one or more of, sealing tape molded article.
 제3항에 있어서,
상기 충진제의 총 중량%가 100중량%일 경우, 탄산칼슘 17~38중량%, 클레이(CLAY) 4~42중량% 및 탈크(TALC) 26중량% 이하인 것을 특징으로 하는, 실링테이프 성형품.
The method of claim 3,
When the total weight% of the filler is 100% by weight, characterized in that the calcium carbonate 17 to 38% by weight, clay (CLAY) 4 to 42% by weight, and talc (TALC) 26% by weight or less, molded sealing tape.
 제1항에 있어서,
상기 실링테이프 조성물은,
발포제, 알루미늄 및 아연 중 어느 하나 이상을 더 포함하는 것을 특징으로 하는, 실링테이프 성형품.
The method of claim 1,
The sealing tape composition,
Foaming agent, characterized in that it further comprises any one or more of aluminum and zinc, sealing tape molded article.
 제5항에 있어서,
발포제 0.5중량% 이하, 알루미늄 1중량% 이하 및 아연 1중량% 이하인 것을 특징으로 하는, 실링테이프 성형품.
The method of claim 5,
A foaming agent 0.5% by weight or less, aluminum 1% by weight or less, and zinc 1% by weight or less.
 삭제delete 삭제delete
KR1020180166290A 2018-12-20 2018-12-20 Sealing tape composition and product comprisign the same KR102176356B1 (en)