KR101991672B1 - Eco frendry hybride bees wax sheet for Waterproof and anti-virus and manufacturing method thereof - Google Patents
Eco frendry hybride bees wax sheet for Waterproof and anti-virus and manufacturing method thereof Download PDFInfo
- Publication number
- KR101991672B1 KR101991672B1 KR1020170012338A KR20170012338A KR101991672B1 KR 101991672 B1 KR101991672 B1 KR 101991672B1 KR 1020170012338 A KR1020170012338 A KR 1020170012338A KR 20170012338 A KR20170012338 A KR 20170012338A KR 101991672 B1 KR101991672 B1 KR 101991672B1
- Authority
- KR
- South Korea
- Prior art keywords
- waterproof
- sheet
- antimicrobial
- wax
- present
- Prior art date
Abstract
본 발명은 마이크로크리스탈린 왁스, 밀랍, 로진 및 목분을 포함하는 항균 방수 기능성 친환경 시트에 관한 것으로, 본 발명에 의한 항균 방수 기능성 친환경 시트는 방수뿐만 아니라 항균효과를 나타내어 기능성 건축용 내장재로 사용이 가능한 장점이 있다. The present invention relates to an antimicrobial waterproof functional environmentally friendly sheet comprising microcrystalline wax, beeswax, rosin and wood powder. The antimicrobial waterproof functional environmentally friendly sheet according to the present invention is not only waterproof, but also exhibits an antibacterial effect and can be used as a functional building interior material. .
Description
본 발명은 마이크로크리스탈린 왁스, 밀납, 로진 및 목분을 포함하는 방수, 항균기능을 지니는 친환경 복합시트 및 이의 제조방법에 관한 것이다.The present invention relates to an environmentally friendly composite sheet having a waterproof, antibacterial function including microcrystalline wax, beeswax, rosin and wood flour, and a process for producing the same.
기술 발전과 함께 합성소재의 발달로 시공이 용이하고 가격이 저렴한 건축물 내장재가 다양하게 개발되었다. 그러나 최근 아토피, 새집증후군 등과 같이 합성소재를 이용한 건축용 내장재의 사용으로 인한 여러 가지 증상들을 호소하는 경우가 많아짐에 따라, 이러한 합성소재들의 유해성에 대해 다양한 연구가 지속적으로 수행되고 있다. With the development of technology, various kinds of interior materials of building which are easy to construct and cheap are developed by the development of synthetic materials. Recently, however, various studies on the harmfulness of such synthetic materials have been continuously carried out because of the increasing incidence of various symptoms due to the use of building interior materials using synthetic materials such as atopy and sick house syndrome.
구체적으로, 건축용 내장재로 다수 이용되던 석고보드의 경우 라돈가스를 방출하여 인체에 여러 가지 질병을 유발하며, 석고보드뿐만 아니라 합성 소재에 포함된 접착제 또는 유기용제 등이 장기간 공기 중에 노출되면서, 일부분이 기화하여 공기중으로 유입되고, 결과적으로 유해한 실내공기를 형성하는 문제점이 발생하게 된다. 이러한 유해한 실내공기는 인체에 치명적인 위협이 될 수 있으며, 특히 유아나 청소년 등의 건강에 치명적일 수 있어, 개선이 필요하다. Specifically, the gypsum board, which has been widely used as a building interior material, emits lardon gas to induce various diseases in the human body, and not only the gypsum board but also the adhesive or organic solvent contained in the synthetic material are exposed in the air for a long time, Vaporized and introduced into the air, resulting in the formation of harmful indoor air. Such harmful indoor air can be a fatal threat to the human body, and it may be particularly fatal to infants and young people, and improvement is needed.
이러한 문제점을 해결하기 위하여 천연소재를 이용한 건축용 내장재에 대해 다양한 연구가 수행되고 있으나, 내장재의 접착성 등에 문제가 발생하거나, 천연소재들이 균일하게 혼합되기 어려워 균질한 조성을 나타내지 않는 등의 문제가 발생하기도 한다. In order to solve such problems, various studies have been conducted on building interior materials using natural materials. However, problems such as adhesiveness of interior materials and the like are difficult to uniformly mix with natural materials, do.
대한민국 공개특허공보 10-2016-0023253호 에서도 코르크를 이용한 건축용 내장재에 대해서 소개하고 있으나, 코르크의 탄성, 신축성 등과 같은 우수한 물리적 특성에도 불구하고 수분에 약한 문제점이 있으며, 접착성이 낮은 문제점이 있다. Korean Patent Laid-Open Publication No. 10-2016-0023253 also discloses an interior material for building using cork. However, it has a problem in that it is weak in moisture and low in adhesiveness, despite excellent physical properties such as elasticity and stretchability of cork.
따라서 이러한 문제점을 해결하기위해 친환경 소재를 이용한 새로운 소재의 개발에 많은 관심이 집중되고 있다.Therefore, much attention has been focused on the development of new materials using environmentally friendly materials to solve these problems.
벌집 즉 밀납은 꿀벌의 번식을 위해 병충해로부터 서식조건을 완벽하게 하기 위하여 왁스성분의 벌집에 프로폴리스와 같은 항균물질을 코팅하여 무균상태로 부화하는 특성이 있다. The honeycomb, or wax, has the property of hatching in an aseptic state by coating an antimicrobial substance such as propolis in a honeycomb honeycomb to perfect habitat conditions from insect pests for the breeding of bees.
그러나 현재 약 250만군에 이르는 양봉 농가에서는 꿀을 채취후 밀납으로 재조된 소초와 함께 버려지는 밀납이 년간 약 2∼300톤에 이르는 막대한 양으로 자원의 낭비가 심각한 실정이다. 또한 벌통 및 양봉자재 제작 부산물인 톱밥 등의 부산물이 발생하여 이의 처리가 시급한 실정이다.However, at present, about 2.5 million farmers have wasted resources with an enormous amount of about 2 to 300 tons of waxy wastes that are discarded with soybeans, which are harvested after harvesting honey. In addition, by-products such as beehive and sawdust, which are by-products of beekeeping material production, are generated, and their disposal is urgent.
따라서 본 발명에서는 밀납과 양봉자재 부산물의 재활용을 위하여 이들의 장점 즉 밀납의 항균, 방수특성과 톱밥의 미생물에 의한 분해특성을 이용하여 이들을 간단한 압출 또는 칼렌더링, 압축공정을 통하여 친환경 밀납 항균 시트의 제조에 관한 것이다.Therefore, in the present invention, by utilizing the advantage of these advantages, namely, antibacterial and waterproof properties of beeswax and decomposition characteristics of sawdust by microorganisms for recycling of wax and beekeeping by-products, they are subjected to simple extrusion, .
본 발명의 목적은 밀납 및 양봉자재 생산 부산물을 이용한 방수, 발수 및 항균 등 다양한 기능이 있는 친환경 시트를 제조하는 것이다.It is an object of the present invention to produce an eco-friendly sheet having various functions such as waterproof, water repellent and antibacterial using beeswax and beekeeping material by-products.
본 발명의 다른 목적은 조성이 균질한 건축용 항균 기능성 친환경 시트를 제공하는 것이다. Another object of the present invention is to provide an antimicrobial functional eco-friendly sheet for construction which is homogeneous in composition.
본 발명에 의한 항균 방수 기능성 친환경 시트는 마이크로크리스탈린 왁스, 밀랍, 로진 및 목분을 포함한다.The antimicrobial waterproof functional environmentally friendly sheet according to the present invention includes microcrystalline wax, beeswax, rosin and wood flour.
본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트는 마이크로크리스탈린 왁스를 30 내지 60 중량% 포함할 수 있다. The antimicrobial and waterproof functional eco-friendly sheet according to an embodiment of the present invention may contain 30 to 60% by weight of microcrystalline wax.
본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트는 활성탄, 제올라이트, 광촉매, 맥반석 및 활성알루미나에서 선택되는 어느 하나 이상의 탈취제를 더 포함할 수 있다. The antibacterial and waterproof functional eco-friendly sheet according to an embodiment of the present invention may further include at least one deodorant selected from activated carbon, zeolite, photocatalyst, elvan, and activated alumina.
본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트 의 제조방법은 a) 마이크로크리스탈린 왁스, 밀랍, 로진 및 목분을 포함하는 원재료를 가열 및 혼련하여 왁스반죽을 형성하는 단계;A method for producing an antibacterial and waterproof functional environmentally friendly sheet according to an embodiment of the present invention comprises the steps of: a) heating and kneading a raw material including microcrystalline wax, beeswax, rosin and wood powder to form a wax dough;
b) 상기 왁스 반죽을 압출 하고 엠보싱 롤을 통과시켜 패턴이 형성된 압출시트를 형성하는 단계; 및b) extruding the wax dough and passing it through an embossing roll to form a patterned extruded sheet; And
c) 상기 압출시트를 컷팅하는 단계;를 포함할 수 있다.and c) cutting the extruded sheet.
본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트의 제조방법에서 상기 왁스 반죽은 활성탄, 제올라이트, 광촉매, 맥반석 및 활성알루미나에서 선택되는 어느 하나 이상의 탈취제를 더 포함할 수 있다. In the method for producing an environmentally friendly antimicrobial and waterproof sheet according to an embodiment of the present invention, the wax paste may further include at least one deodorant selected from activated carbon, zeolite, photocatalyst, elvan, and activated alumina.
본 발명에 의한 항균, 방수 기능성 친환경 시트는 밀랍을 포함하여 단일층만으로 항균 및 방수기능을 나타내는 장점이 있다. The antimicrobial and waterproof functional eco-friendly sheet according to the present invention is advantageous in that it has antimicrobial and waterproof functions with only a single layer including beeswax.
본 발명에 의한 항균, 방수 기능성 친환경 시트는 밀납, 로진, 마이크로크리스탈린 왁스를 포함하여 항균 기능성과 향취, 소취 기능성을 갖는 균질한 조성을 가지는 장점이 있다. The antibacterial and waterproof functional environmentally friendly sheet according to the present invention has an advantage of having a homogeneous composition having antimicrobial function, flavor and deodorizing function including wax, rosin and microcrystalline wax.
이하 본 발명에 따른 항균 방수 기능성 친환경 시트는 시트 및 이의 제조방법에 대해 상세히 설명한다. 이때, 사용되는 기술 용어 및 과학 용어에 있어서 다른 정의가 없다면, 이 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 통상적으로 이해하고 있는 의미를 가지며, 하기의 설명 및 첨부 도면에서 본 발명의 요지를 불필요하게 흐릴 수 있는 공지 기능 및 구성에 대한 설명은 생략한다. Hereinafter, the antimicrobial and waterproof functional environmentally friendly sheet according to the present invention will be described in detail. Hereinafter, the technical and scientific terms used herein will be understood by those skilled in the art without departing from the scope of the present invention. Descriptions of known functions and configurations that may be unnecessarily blurred are omitted.
본 발명은,According to the present invention,
마이크로크리스탈린 왁스, 밀랍, 로진 및 목분을 포함하는 항균 방수 기능성 친환경 시트에 관한 것이다. 본 발명에 의한 항균 방수 기능성 친환경 시트는를 건축용 내장재로 이용할 경우, 방수성뿐만 아니라 항균성 및 항곰팡이성을 띠는 특징이 있다. Microcrystalline wax, beeswax, rosin and wood flour. The antimicrobial and waterproof functional environmentally friendly sheet according to the present invention is characterized not only in water resistance but also in antibacterial and antifungal properties when used as a building interior material.
본 발명에 의한 항균 방수 기능성 친환경 시트는 밀랍을 포함한다. 밀랍을 포함함으로써 방수성을 확보하고, 광택을 내는 것은 물론이며, 벌이 벌집을 짓는 과정에서 로열젤리 등의 보호를 위해 만들어내는 천연 물질인 프로폴리스를 일정량 포함하고 있어, 항균성을 띠는 장점이 있다. 이러한 장점에 의해, 밀랍으로부터 별도로 프로폴리스를 분리하는 공정을 거치지 않으면서도 방수 시트의 항균성을 확보하여 결과적으로 방수 시트의 생산단가를 현저히 낮출 수 있는 장점이 있다. 이는 종래 항균 방수 기능성 친환경 시트에서 통상적으로 고분자 수지를 이용하는 점과 차별성을 띠며, 이러한 고분자 수지를 포함하지 않고도 천연재료인 밀랍을 이용하여 건축용에 적합한 방수효율을 나타내면서도 항균성을 나타낼 수 있는 장점이 있다. The antimicrobial waterproof functional environmentally friendly sheet according to the present invention includes beeswax. By including beeswax, it secures waterproofness and luster. It also contains a certain amount of propolis, which is a natural substance for protection of royal jelly in the process of making a honeycomb, and has an advantage of being antibacterial. By virtue of these advantages, the antibacterial property of the waterproof sheet can be ensured without the step of separating the propolis separately from the beeswax, and as a result, the production cost of the waterproof sheet can be remarkably lowered. This is different from the conventional method of using a polymer resin in an antimicrobial and waterproof functional eco-friendly sheet, and it has an advantage of exhibiting antimicrobial properties while exhibiting a waterproof efficiency suitable for construction by using beeswax, which is a natural material, without including such a polymer resin .
이러한 밀랍은 항균 방수 기능성 친환경 시트 중 5 내지 20 중량% 포함될 수 있다. 밀랍이 상기 범위보다 적게 첨가되는 경우 제조되는 시트가 방수성을 나타내기 어려운 문제점이 있으며, 밀랍이 상기 범위 보다 다량 첨가되는 경우 제조되는 시트의 유연성을 담보하기 어려운 문제점이 있다. Such beeswax may comprise 5 to 20% by weight of the antimicrobial water-resistant eco-friendly sheet. When the beeswax is added in an amount less than the above range, there is a problem that the sheet to be produced is difficult to exhibit waterproof property, and when the beeswax is added in a larger amount than the above range, the flexibility of the sheet to be produced is difficult to be secured.
본 발명에 의한 항균 방수 기능성 친환경 시트는 또한 마이크로크리스탈린 왁스를 더 포함한다. 이때 마이크로크리스탈린 왁스는 석유로부터 분리되는 이소파라핀을 포함하는 고형 탄화수소류를 의미하며, 이러한 마이크로크리스탈린 왁스는 접착성을 띨 뿐만 아니라, 목분의 분산성을 향상시키는 장점이 있다. 구체적으로, 밀랍과 목분이 혼합되는 경우, 광택도를 나타내면서도 단열효과를 도모할 수 있는 장점이 있으나, 목분과 밀랍은 균질하게 혼합되기 어려워 대면적으로 제작이 어려운 문제점이 있었다. 그러나, 본원발명과 같이 밀랍과 목분을 동시에 포함하는 조성물이 마이크로크리스탈린왁스를 더 포함하는 경우, 마이크로크리스탈린 왁스의 접착성으로 인해 방수 시트에 접착력을 확보하면서도, 목분의 분산성을 향상시켜 대면적에서도 균질한 혼합비를 나타내며, 결과적으로 방수 특성 또한 균일하게 나타나는 장점이 있다. The antimicrobial waterproof functional environmentally friendly sheet according to the present invention further comprises microcrystalline wax. In this case, microcrystalline wax means a solid hydrocarbon containing isoparaffin separated from petroleum. Such microcrystalline wax has an advantage of not only sticking but also improving the dispersibility of wood powder. Specifically, when beeswax is mixed with wood, there is an advantage that the heat insulating effect can be achieved while exhibiting glossiness, but the wood and beeswax are difficult to be homogeneously mixed, so that it is difficult to manufacture the beeswax with a large area. However, when the composition including wax and wood powder at the same time further includes microcrystalline wax as in the present invention, adhesion of microcrystalline wax is secured, thereby improving the dispersibility of wood powder while securing adhesion to the waterproof sheet It shows homogeneous mixture ratio even in the area, and as a result, waterproof property is also uniformly displayed.
이러한 마이크로크리스탈린 왁스는 전체 항균 방수 기능성 친환경 시트 중 30 내지 60 중량% 포함될 수 있다. 마이크로크리스탈린 왁스가 상기 범위 보다 소량 첨가되는 경우, 제조되는 시트에서 균질한 조성을 기대하기 어려우며, 마이크로크리스탈린 왁스가 다량 첨가되는 경우 제조되는 시트의 방수성 및 항균성을 도모하기 어려운 문제점이 있다. 나아가, 마이크로크리스탈린 왁스가 상기 범위 내로 포함되는 경우, 제조되는 항균 방수 기능성 친환경 시트가 유연성을 띠어 보관, 이동 및 시공이 용이할 뿐만 아니라, 건축용으로 시공 시 콘크리트 벽 등과의 높은 결착력을 띨 수 있는 장점이 있다.Such microcrystalline wax may be contained in an amount of 30 to 60% by weight of the entire antimicrobial waterproof functional eco-friendly sheet. When a microcrystalline wax is added in a smaller amount than the above range, it is difficult to expect a homogeneous composition in a sheet to be produced, and when the microcrystalline wax is added in a large amount, it is difficult to achieve waterproof and antimicrobial properties of a sheet to be produced. Further, when the microcrystalline wax is contained within the above-mentioned range, the antimicrobial waterproof functional environmentally friendly sheet to be produced is flexible and easy to store, move and install, and can have a high binding force with a concrete wall There are advantages.
상술한 바와 같이, 본 발명에 의한 항균 방수 기능성 친환경 시트는 목분을 더 포함한다. 이때 목분이라 함은 통상적인 의미에서 이용되는 목분일 수 있으나, 더욱 구체적으로는 소나무, 은행나무, 향나무, 편백나무, 측백나무, 계피나무 또는 잣나무를 건조 후 분쇄하여 제조된 것일 수 있으며, 이러한 목분은 입자의 크기가 0.05 내지 1 ㎜일 수 있다. 이러한 목분을 포함함으로써, 시트에 목재의 질감을 나타내어 본 발명에 의한 항균 방수 기능성 친환경 시트가 건축 내장재로 사용 시 심미감을 살릴 수 있는 장점이 있다. 나아가, 이러한 목분의 혼합에 의해 제조되는 시트의 기계 강도를 향상시킬 수 있는 장점이 있다. As described above, the antimicrobial and waterproof functional environmentally friendly sheet according to the present invention further comprises wood flour. The wood flour may be used in a conventional manner, but more specifically, it may be one prepared by drying and then pulverizing pine, ginkgo, juniper, cottonwood, cinnamon or pine wood, The size of the silver particles may be 0.05 to 1 mm. By including such wood powder, the wood has a texture on the sheet, which is advantageous in that the antimicrobial and waterproof functional eco-friendly sheet according to the present invention can provide aesthetics when used as a building interior material. Further, there is an advantage that the mechanical strength of the sheet produced by mixing such wood powder can be improved.
이러한 목분은 전체 항균 방수 기능성 친환경 시트는 시트 중 20 내지 50 중량% 포함될 수 있으며, 목분이 상기 범위로 포함되는 경우, 제조되는 항균 방수 기능성 친환경 시트가 단열효과를 나타낼 수 있는 장점이 있다. 나아가, 상기 범위로 목분이 포함되는 경우 기계강도를 향상시키면서도 제조되는 시트의 방수성 저하를 예방할 수 있는 장점이 있다. The whole antimicrobial waterproof functional eco-friendly sheet may contain 20 to 50% by weight of the whole antimicrobial waterproof functional eco-friendly sheet. If the wood is in the above range, the antimicrobial waterproof functional eco-friendly sheet can exhibit a heat insulating effect. Further, when the wood is included in the above range, there is an advantage that the water resistance of the manufactured sheet can be prevented from deteriorating while improving the mechanical strength.
본 발명에 의한 항균 방수 기능성 친환경 시트는 로진을 더 포함한다. 이때 로진이라 함은 소나무의 송진에서 테르펜유를 추출하고 남은 잔류물을 의미하며, 이러한 로진이 본 발명에 의한 방수 시트에 포함됨으로써 항균성을 더욱 강화할 수 있다. 나아가, 이러한 로진은 상술한 목분과 혼합되어 결착됨으로써 방수 시트의 결착력을 더욱 향상시킬 수 있는 장점이 있다. 이러한 로진은 전체 항균 방수 기능성 친환경 시트 중 1 내지 12 중량% 포함될 수 있다. 로진이 상기 범위로 포함되는 경우, 지나치게 다량의 로진에 의해 피부자극이 일어나는 것을 예방하면서도, 항균성을 더욱 강화하여 주거용 내장재로 이용이 더욱 적합한 장점이 있다. The antimicrobial and waterproof functional environmentally friendly sheet according to the present invention further comprises rosin. In this case, the term "rosin" refers to residues remaining after extracting terpene oil from the pine rosin. The rosin is included in the waterproof sheet according to the present invention to further enhance antimicrobial activity. Furthermore, such rosin is advantageous in that it can further improve the binding force of the waterproof sheet by mixing with the above-mentioned wood. Such rosin may comprise 1 to 12% by weight of the total antimicrobial and waterproof functional eco-friendly sheet. When the rosin is included in the above range, it is advantageous to further enhance its antimicrobial activity and to use it as a residential interior material, while preventing skin irritation from occurring due to an excessive amount of rosin.
본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트는 활성탄, 제올라이트, 광촉매, 맥반석 및 활성알루미나에서 선택되는 어느 하나 이상의 탈취제를 더 포함한다. 이러한 탈취제를 포함함으로써 제조되는 항균 방수 기능성 친환경 시트가 탈취의 기능성을 나타낼 수 있는 장점이 있다. 이러한 탈취제는 입경이 100 내지 3000 ㎛, 구체적으로는 100 내지 1000 ㎛인 것을 이용할 수 있으며, 탈취제에 형성된 기공의 평균 직경은 300 내지 1500 ㎚일 수 있다. 탈취제의 입자크기 및 평균 기공의 직경이 상기 범위를 만족하는 경우, 방수 시트의 제조를 위한 방수 시트용 조성물에 혼합 시 균일하게 분산될 뿐만 아니라 일정한 기공의 크기를 확보하여 탈취효율을 나타내면서도 상술한 마이크로크리스탈린 왁스와 결착되어 추후 물리적 충격 등에 의해 탈취제가 유실되는 것을 예방할 수 있다. The antibacterial and waterproof functional eco-friendly sheet according to an embodiment of the present invention further includes at least one deodorant selected from activated carbon, zeolite, photocatalyst, elvan, and activated alumina. The antibacterial and waterproof functional environment-friendly sheet produced by including such a deodorant has an advantage that it can exhibit the function of deodorization. Such a deodorant may have a particle size of 100 to 3000 탆, specifically 100 to 1000 탆, and the average diameter of the pores formed in the deodorant may be 300 to 1500 nm. When the particle size of the deodorant and the diameter of the average pore satisfy the above range, not only uniformly dispersed in the composition for a waterproof sheet for producing a waterproof sheet but also securing a certain pore size, The microcrystalline wax can be combined with the microcrystalline wax to prevent the deodorant from being lost due to physical shock or the like.
본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트에서 이러한 탈취제는 1 내지 12 중량% 포함될 수 있다. 탈취제가 상기 범위로 포함되는 경우, 탈취효과를 확보하면서도 제조되는 시트의 접착성 저하를 막을 수 있는 장점이 있다. In the antimicrobial waterproof functional eco-friendly sheet according to an embodiment of the present invention, the deodorant may be contained in an amount of 1 to 12 wt%. When the deodorant is included in the above-mentioned range, there is an advantage that the deterioration effect can be ensured and the deterioration of the adhesiveness of the sheet to be produced can be prevented.
이러한 항균 방수 기능성 친환경 시트의 두께는 이용되는 용도 등에 따라 달라질 수 있으나, 일반적으로 3 내지 30 ㎜의 두께로 제조될 수 있다. 나아가, 본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트는 콘크리트 벽, 타일, 벽지, 가구 등의 표면에 시공하거나, 장식용 시트 등에 이용 등 각종 건축용 내외장재의 표면에 도입할 수 있으며, 더욱 구체적으로는 방수를 필요로 하는 베란다 등의 벽면에 시공하는 건축용 방수시트로 이용하여 방수와 단열을 함께 도모할 수 있다. The thickness of the antimicrobial waterproof functional eco-friendly sheet may vary depending on the intended use and the like, but may be generally 3 to 30 mm. Further, the antimicrobial and waterproof functional environmentally friendly sheet according to the embodiment of the present invention can be introduced to the surface of concrete wall, tile, wallpaper, furniture, etc., or to the surface of various building interior and exterior materials such as a decorative sheet, Is used as a waterproof sheet for construction that is installed on a wall surface of a veranda or the like that requires waterproofing, so that waterproofing and insulation can be achieved together.
본 발명은 또한 마이크로크리스탈린 왁스, 밀랍, 로진 및 목분을 포함하는 항균 방수 기능성 친환경 시트의 제조방법을 제공한다. 본 발명에 의한 항균 방수 기능성 친환경 시트 의 제조방법은 The present invention also provides a process for producing an antimicrobial waterproof functional environmentally friendly sheet comprising microcrystalline wax, beeswax, rosin and wood flour. The method for producing an antibacterial and waterproof functional environmentally friendly sheet according to the present invention comprises
a) 마이크로크리스탈린 왁스, 밀랍, 로진 및 목분을 포함하는 원재료를 가열 및 혼련하여 왁스반죽을 형성하는 단계;a) heating and kneading a raw material including microcrystalline wax, beeswax, rosin and wood powder to form a wax dough;
b) 상기 왁스 반죽을 압출 하고 엠보싱 롤을 통과시켜 패턴이 형성된 압출시트를 형성하는 단계; 및b) extruding the wax dough and passing it through an embossing roll to form a patterned extruded sheet; And
c) 상기 압출시트를 컷팅하는 단계;를 포함한다. and c) cutting the extruded sheet.
나아가 본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트는 일면에 종이, 부직포 또는 필름에서 선택되는 하나 이상의 표면층을 형성하는 단계를 더 포함할 수 있다. Further, the antibacterial and waterproof functional eco-friendly sheet according to an embodiment of the present invention may further include forming at least one surface layer selected from a paper, a nonwoven fabric or a film on one side.
이때, 상기 a) 단계는 70-90℃, 구체적으로 80℃ 내지 85℃ 에서 수행될 수 있으며, 상기 온도 범위에서 재료를 혼련하는 경우, 고열에 의한 조성물의 화학적 변화를 예방할 수 있으면서도, 조성물을 균일하게 혼련할 수 있다. 이러한 상기 a) 단계는 5 분 내지 30 분 동안 수행될 수 있으나, 조성물을 균일하게 혼련할 수 있는 범위 내인 경우 제한이 없다.In this case, the step a) may be carried out at a temperature of 70-90 ° C., specifically 80 ° C. to 85 ° C. When the material is kneaded in the temperature range, it is possible to prevent the chemical change of the composition due to high temperature, . The step a) may be carried out for 5 minutes to 30 minutes, but there is no limitation as long as the composition can be uniformly kneaded.
나아가, 본 발명의 일 실시예에 의한 상기 왁스 반죽은 활성탄, 제올라이트, 광촉매, 맥반석 및 활성알루미나에서 선택되는 어느 하나이상의 탈취제를 더 포함할 수 있다. 이러한 탈취제를 더 포함하는 경우, 본 발명의 일 실시예에 의해 제조되는 항균 방수 기능성 친환경 시트가 방수, 항균뿐만 아니라 탈취의 기능성을 더 확보할 수 있으며, 상술한 마이크로크리스탈린 왁스와 긴밀하게 결착하여 제조되는 시트의 기계강도를 강화할 수 있는 장점이 있다. Further, the wax paste according to an embodiment of the present invention may further include at least one deodorant selected from activated carbon, zeolite, photocatalyst, elvan, and activated alumina. When such deodorant is further contained, the antibacterial and waterproof functional environmentally friendly sheet produced according to one embodiment of the present invention can secure waterproof, antibacterial as well as deodorizing function, and can be firmly adhered to the microcrystalline wax There is an advantage that the mechanical strength of the sheet to be manufactured can be enhanced.
본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트의 제조방법에서 상기 b) 단계는 상기 왁스 반죽을 압출하고 엠보싱 롤을 통과시켜 패턴을 형성하는 단계일 수 있다. 엠보싱 롤을 통과시켜 형성되는 패턴은 제조되는 시트의 양면 또는 일면에 형성될 수 있으나, 시공과정에서 접착력을 확보하기 위하여 일면에만 패턴을 형성할 수 있다. 상기 b) 단계를 통해 형성되는 시트의 두께는 2 내지 100 ㎜일수 있으나, 사용용도 및 사용 환경 등을 고려하여 적절히 조절될 수 있다. In the method for manufacturing an antibacterial and waterproof functional environmentally friendly sheet according to an embodiment of the present invention, the step b) may be a step of extruding the wax dough and passing the wax dough through an embossing roll to form a pattern. The pattern formed by passing through the embossing roll may be formed on both sides or one side of the sheet to be manufactured, but a pattern may be formed only on one side in order to secure an adhesive force during the construction process. The thickness of the sheet formed through the step b) may be 2 to 100 mm, but may be suitably adjusted in consideration of the intended use and the use environment.
본 발명의 일 실시예에 의한 상기 왁스 반죽은 활성탄, 제올라이트, 광촉매, 맥반석 및 활성알루미나에서 선택되는 어느 하나이상의 탈취제를 더 포함할 수 있으며, 이러한 탈취제는 상기 왁스반죽 중 1 내지 12 중량% 포함되어, 기계적 물성을 확보하면서도 접착성 및 탈취효과를 담보할 수 있다. The wax dough according to an embodiment of the present invention may further include at least one deodorant selected from activated carbon, zeolite, photocatalyst, elvan, and activated alumina, and the deodorant includes 1 to 12 wt% of the wax dough , Adhesion and deodorizing effect can be secured while ensuring mechanical properties.
본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트는, 상술한 조성물을 조합함으로써 단층만으로 항균 방수 기능성 친환경 시트로 이용할 수 있는 장점이 있다. 구체적으로, 종래 통상적으로 이용되던 방수용 시트는 여러 층을 형성하여 각 층이 방수기능 및 항균, 소취, 유해물질 제거 등의 기능을 띨 수 있도록 하는 것이 일반적이었다. 그러나 이러한 경우, 다층구조에 의해 생산 단계가 복잡해지고, 기능성을 나타내는 층이 내부에 포함됨으로써, 종래 의도한 기능을 충분히 발휘하지 못하는 문제점이 있었다. 그러나, 본 발명의 일 실시예에 의한 항균 방수 기능성 친환경 시트는 밀랍, 마이크로크리스탈린 왁스, 로진 및 목분을 혼합함으로써 다층구조의 형성 없이, 단층구조만으로 형성이 가능하여 생산비용을 절감하면서도 효율적으로 방수 및 항균과 같은 기능성을 나타낼 수 있는 장점이 있다. The antibacterial and waterproof functional eco-friendly sheet according to an embodiment of the present invention has an advantage that it can be used as an antimicrobial waterproof functional eco-friendly sheet only with a single layer by combining the above-described compositions. Specifically, the waterproof sheet conventionally used conventionally has a plurality of layers formed so that each layer can function as waterproof, antibacterial, deodorant, and harmful substances. However, in such a case, the production step becomes complicated due to the multilayer structure, and the layer exhibiting the functionality is contained therein, so that the conventional functions can not be sufficiently exhibited. However, the antimicrobial and waterproof functional eco-friendly sheet according to an embodiment of the present invention can be formed only by a single layer structure without mixing multi-layer structure by mixing beeswax, microcrystalline wax, rosin and wood powder, ≪ / RTI > and antibacterial activity.
이하 본 발명을 실시예에 의해 구체적으로 설명한다. 아래에서 설명하는 실시예는 발명의 이해를 돕기 위한 것일 뿐, 본 발명이 실시예에 한정되지 않는다.Hereinafter, the present invention will be described in detail with reference to examples. The embodiments described below are only for the understanding of the invention, and the present invention is not limited to the embodiments.
[실시예 1][Example 1]
밀랍 20 g, 마이크로크리스탈린 왁스(W-445, Witco 社) 20 g, 로진 5 g, 목분 50 g 및 활성탄 5 g을 80 ℃에서 20 분간 혼합하여 왁스 반죽을 제조한다, 이후, 이를 압출하고 엠보싱 롤러를 통과시켜 두께 5 ㎜의 시트를 형성한다. 20 g of beeswax, 20 g of microcrystalline wax (W-445, Witco), 5 g of rosin, 50 g of wood powder and 5 g of activated carbon were mixed at 80 DEG C for 20 minutes to prepare a wax dough. And passed through rollers to form a sheet having a thickness of 5 mm.
[비교예 1] [Comparative Example 1]
실시예 1과 같은 방법으로 제조하되, 마이크로크리스탈린 왁스 대신 파라핀왁스를 이용하여 항균 방수 기능성 친환경 시트를 제조하였다. An antimicrobial waterproof functional eco-friendly sheet was prepared in the same manner as in Example 1 except that paraffin wax was used instead of microcrystalline wax.
[제조되는 방수 시트의 접촉각 측정][Measurement of contact angle of waterproof sheet to be manufactured]
제조되는 항균 방수 기능성 친환경 시트의 조성이 균질한지 확인하기 위하여, 실시예 1 및 비교예 1의 시트를 가로 1.5 m * 세로 1 m로 제조하고, 상기 시트상에 임의로 지정된 30 개 지점에서 물과의 접촉각을 측정하고 평균 및 표준편차를 구하여 표 1로 나타내었다. In order to confirm that the composition of the antibacterial and waterproof functional environmentally friendly sheet to be produced was homogeneous, the sheets of Example 1 and Comparative Example 1 were manufactured to have a width of 1.5 m and a length of 1 m, The contact angles were measured and the mean and standard deviation were obtained and are shown in Table 1.
표 1을 참고하면, 마이크로크리스탈린 왁스 대신 파라핀왁스를 포함하는 경우, 평균 접촉각이 낮아질 뿐만 아니라, 표준편차의 크기가 커져 제조되는 방수 시트가 균일한 조성을 갖지 않는 것을 확인할 수 있다. Referring to Table 1, when the paraffin wax is contained in place of the microcrystalline wax, not only the average contact angle is lowered but also the size of the standard deviation is increased, and it can be confirmed that the waterproof sheet produced has no uniform composition.
Claims (5)
상기 항균 방수 기능성 친환경 시트는 활성탄, 제올라이트, 광촉매, 맥반석 및 활성알루미나에서 선택되는 어느 하나 이상의 탈취제를 더 포함하는 항균 방수 기능성 친환경 시트.The method according to claim 1,
The antimicrobial and waterproof functional eco-friendly sheet further comprises at least one deodorant selected from activated carbon, zeolite, photocatalyst, elvan, and activated alumina.
a) 마이크로크리스탈린 왁스, 밀랍, 로진 및 목분을 포함하는 원재료를 가열 및 혼련하여 왁스반죽을 형성하는 단계;
b) 상기 왁스 반죽을 압출 하고 엠보싱 롤을 통과시켜 패턴이 형성된 압출시트를 형성하는 단계; 및
c) 상기 압출시트를 컷팅하는 단계;
를 포함하는 항균 방수 기능성 친환경 시트의 제조방법.A process for producing an antibacterial and waterproof functional environmentally friendly sheet according to claim 1 or 3,
a) heating and kneading a raw material including microcrystalline wax, beeswax, rosin and wood powder to form a wax dough;
b) extruding the wax dough and passing it through an embossing roll to form a patterned extruded sheet; And
c) cutting the extruded sheet;
Wherein the method comprises the steps of:
상기 왁스 반죽은 활성탄, 제올라이트, 광촉매, 맥반석 및 활성알루미나에서 선택되는 어느 하나 이상의 탈취제를 더 포함하는 항균 방수 기능성 친환경 시트의 제조방법.5. The method of claim 4,
Wherein the wax paste further comprises at least one deodorant selected from activated carbon, zeolite, photocatalyst, elvan, and activated alumina.