KR101932703B1 - Antimicrobial composition consisting main of zinc oxide, functional film using the same - Google Patents
Antimicrobial composition consisting main of zinc oxide, functional film using the same Download PDFInfo
- Publication number
- KR101932703B1 KR101932703B1 KR1020160117826A KR20160117826A KR101932703B1 KR 101932703 B1 KR101932703 B1 KR 101932703B1 KR 1020160117826 A KR1020160117826 A KR 1020160117826A KR 20160117826 A KR20160117826 A KR 20160117826A KR 101932703 B1 KR101932703 B1 KR 101932703B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- antimicrobial composition
- zinc oxide
- parts
- antimicrobial
- Prior art date
Abstract
인체 유해성이 적고 항균효과가 우수하며 태양광 등에 무관하게 항균효과를 발생할 수 있도록 산화아연을 주성분으로 하는 항균 조성물 및 이를 적용한 기능성 필름이 개시된다. 이를 위하여 바인더 95 내지 99 중량%, 및 산화아연 분말 1 내지 5 중량%를 포함하는 항균 조성물을 포함하는 항균 조성물을 제공한다. 또한, 상기 항균 조성물이 0.1 내지 100 ㎛의 두께로 도포된 고분자 필름을 포함하는 기능성 필름을 제공한다. 본 발명에 의하면, 최근 인체 위해성이 제기되고 있는 은나노 물질 등의 합성 화학물질을 기반으로 하는 항균 제품을 대체하여 항균 시트지나 필름 등의 사용이 어려운 구석진 곳, 굴곡진 표면을 가지는 제품에 항균력을 부여할 수 있다.Disclosed is an antimicrobial composition comprising zinc oxide as a main component and a functional film using the same, so as to produce an antimicrobial effect irrespective of sunlight and the like. To this end, there is provided an antimicrobial composition comprising an antimicrobial composition comprising 95 to 99% by weight of a binder and 1 to 5% by weight of a zinc oxide powder. The present invention also provides a functional film comprising the polymer film coated with the antibacterial composition at a thickness of 0.1 to 100 탆. According to the present invention, an antimicrobial product based on a synthetic chemical substance such as a silver nano substance, which has recently been exposed to a human risk, is substituted, and a antibacterial power is imparted to a product having a curved surface or a corner where the antibacterial sheet or film is difficult to use can do.
Description
본 발명은 인체에 무해한 산화아연을 주성분으로 하는 항균 조성물 및 이를 적용한 기능성 필름에 관한 것으로, 보다 상세하게는 다양한 제품에 범용적으로 적용할 수 있고, 사용 편의성 및 내구성이 향상되며, 인체에 대한 유해성이 적은 산화아연을 주성분으로 하는 항균 조성물 및 이를 적용한 기능성 필름에 관한 것이다.The present invention relates to an antimicrobial composition containing zinc oxide as a main component, which is harmless to the human body, and a functional film to which the composition is applied. More specifically, the present invention can be applied to various products in general, This invention relates to an antimicrobial composition comprising zinc oxide as a main component and a functional film using the same.
미생물은 우리 주변에 항상 존재하고 있는 생명체로서, 인간에게 도움을 주는 유익한 미생물도 존재하지만, 한편으로는 질병을 유발하고 악취를 만들며, 미관상 혐오감을 주는 등의 문제를 일으키는 해로운 미생물도 존재한다. Microorganisms are living organisms that always exist around us, and there are beneficial microorganisms that help human beings, but harmful microorganisms exist which cause problems such as illness, odor, and aesthetics.
특히 곰팡이의 경우에는 습기가 많은 지하나 밀폐된 공간(예로, 옷장, 신발장 등)에서 서식하며 악취를 만들고, 물건을 변형시키며 미관상 혐오스러울 뿐만 아니라 질병을 일으킨다. 고온다습한 장마철의 경우에는 실내에서 벽지 등에 서식하여 위에서 설명한 문제점들을 일으킨다.In the case of molds, it is damp, but it lives in an enclosed space (for example, a closet, a shoe box, etc.). It produces odors, transforms objects, and causes illness as well as aesthetics. In the case of hot and humid rainy season, it is living in a room, wall paper, etc., and causes the problems described above.
최근에는 이와 같은 미생물에 의한 비위생적인 환경을 개선하고자 하는 위생관리용품들에 대한 관심이 높아지고 있다. 특히 2000년대 이후 사스(Severe Acute Respiratory Syndrome : SARS), 조류독감, 신종플루 등의 유행병 발발로 인해 세균과 바이러스 감염방지에 도움을 주는 위생관리 용품에 대한 관심이 높아지고 있다.In recent years, there has been a growing interest in sanitary ware products intended to improve the unsanitary environment caused by such microorganisms. Particularly since 2000, there has been a growing interest in hygiene products that help prevent bacterial and viral infections due to epidemics such as Severe Acute Respiratory Syndrome (SARS), avian influenza and swine flu.
이에 따라, 미생물에 의한 비위생적인 환경을 개선하고자 하는 항균 관련 제품들도 다수 제조 및 판매되고 있다. 그러나, 일반적으로 항균제로 화학물질을 사용하고 있고, 많은 경우에 있어서 이들 화학물질은 저분자량 물질이므로 안전성 및 지속성에 있어서 문제가 되고 있다. Accordingly, a number of antimicrobial-related products which are intended to improve an unsanitary environment due to microorganisms have been produced and sold. However, in general, chemical substances are used as antimicrobial agents, and in many cases, these chemical substances are low molecular weight substances, and therefore, they are problematic in terms of safety and persistence.
또한, 저분자량의 합성물들은 휘발되기 때문에 항균 지속성이 떨어지는 단점을 지니고 있다. 이외에도 합성 화합물이나 무기물질은 항균성은 있으나 유기용매에 녹이거나 분산시키는 방법으로 에어로졸 스프레이를 제조해야만 하는 불편한 점이 있으며, 실내에서 냄새가 좋지 않은 단점도 있다. In addition, low-molecular-weight compounds are volatilized and thus have a disadvantage of poor antimicrobial persistence. In addition, synthetic compounds and inorganic materials have antimicrobial properties, but they are inconvenient to manufacture aerosol sprays by dissolving or dispersing them in organic solvents, and there is also a disadvantage in that the odor is not good in the room.
이에 대한 대안으로서 항균, 소취능이 있는 무기물질을 이용한 무기계 항균제품이 제조되고 있다. 이러한 무기계 항균제품으로서는 항균능이 있는 금속을 용매에 분산시킨 형태, 다공성 지지체에 금속을 결합시킨 후 사용하는 형태의 제품이 있다. As an alternative, an inorganic antibacterial product using an inorganic substance having antibacterial and deodorizing ability has been produced. As such an inorganic antibacterial product, there is a product in which a metal having antimicrobial activity is dispersed in a solvent, or a product in which a metal is bonded to a porous support and then used.
그 일 예로서 제올라이트, 실리카, 알루미나 등의 무기 담체에 은(Ag), 구리(Cu), 망간(Mn), 아연(Zn) 등과 같이 항균성이 뛰어난 금속이온을 치환시킨 항균제품은, 미세한 기공을 가진 3차원의 골격구조를 지니기 때문에 비표면적이 크고 내열성이 우수하다는 장점을 가진다. An example of such an antimicrobial product is an inorganic antibacterial product in which an inorganic carrier such as zeolite, silica or alumina is substituted with a metal ion having excellent antimicrobial properties such as silver (Ag), copper (Cu), manganese (Mn) Dimensional skeleton structure and thus has a large specific surface area and excellent heat resistance.
무기 항균제에 대해 더 설명하면, 무기 항균제는 미생물에 대한 살균기능 또는 증식억제기능을 갖는 중금속이온 중에서 인체에 안전한 은이온, 구리이온, 아연이온 등을 무기산화물인 세라믹에 이온교환 또는 담지시킨 것이다. 여기서 구리이온, 아연이온, 은이온 중, 구리이온은 독성 및 산화에 의한 변색의 문제로 인해 통상 건자재 등에만 적용되고 있다.More specifically, inorganic antibacterial agents are ion exchanged or supported on inorganic oxides such as silver ions, copper ions, and zinc ions, which are safe for human body among heavy metal ions having sterilizing function or antiproliferative function against microorganisms. Here, among copper ions, zinc ions, and silver ions, copper ions are usually applied to construction materials and the like due to toxicity and discoloration due to oxidation.
따라서 무기 항균제에 사용되는 금속이온은 실제적으로 은이온이 주를 이루고 있으며, 이러한 은이온은 향균 효과도 높은 동시에 항균 대상인 세균의 종류도 다양하다.Therefore, metal ions used in inorganic antimicrobial agents are mainly composed of silver ions. These silver ions have a high antibacterial effect as well as various kinds of bacteria which are antimicrobial targets.
그러나, 상기와 같이 종래의 무기 항균제는 대부분 은이온을 사용하는데, 은나노 물질은 최근 OECD 연구 등에서 특유의 작은 크기로 인해 몸속에 침투할 경우 유해인자로 작용할 가능성이 높은 물질로 보고됐다. 이 밖에도 지난 2011년 폐 손상 증상을 유발한 '가습기 살균제' 사건 등 예상치 못한 인체 위해물질에 대한 불안감이 높아지고 있는 실정이다. However, as described above, most conventional inorganic antibacterial agents use silver ions, and silver nano materials have recently been reported to be a harmful agent when they penetrate into the body due to a unique small size in OECD research. In addition, anxiety about unexpected harmful substances such as the 'humidifier disinfectant' that caused the lung injury symptoms in 2011 is increasing.
따라서, 은이온이 포함되어 있지 않더라도 은이온을 주성분으로 하는 무기 항균제와 대등한 기능을 발휘할 수 있는 항균제의 제공이 요구되는 상황이다.Therefore, it is required to provide an antimicrobial agent capable of exerting a function equivalent to that of an inorganic antimicrobial agent containing silver ions as a main component even if silver ions are not contained therein.
한편, 스프레이형 항균 조성물을 제공하기 위해서는 1) 소량의 항균제로도 높은 항균 활성이 있어야 하고, 2) 피부 및 눈에 강한 자극성이 없어야 하며, 3) 잔류 활성이 강하여야 한다는 요건들이 구비되어야 한다.On the other hand, in order to provide a spray-type antimicrobial composition, it is required that 1) a small amount of antimicrobial agent should have a high antimicrobial activity, 2) have no irritation to the skin and eyes, and 3) have a strong residual activity.
따라서, 따라서, 본 발명의 제1 목적은 도포 후 항균성, 살균성, 항곰팡이성, 탈취성, 친수성이 기존 은이온을 주성분으로 하는 무기 항균제와 비등(比等)한 작용을 할 수 있으며, 안전성이 개선된 항균 조성물을 제공하는데 있다.Accordingly, it is a first object of the present invention to provide an antimicrobial agent that can act as a boiling (ratio or the like) antimicrobial agent, bactericidal agent, antifungal agent, deodorant, And to provide an improved antimicrobial composition.
또한, 본 발명의 제2 목적은 고분자 필름에 도포하여 필름형태로 제조함으로써 항균성, 살균성, 항곰팡이성, 탈취성, 친수성을 부여할 수 있는 기능성 필름을 제공하는데 있다.A second object of the present invention is to provide a functional film capable of imparting antimicrobial activity, bactericidal activity, antifungal property, deodorization property, and hydrophilicity by coating the film on a polymer film.
상술한 본 발명의 제1 목적을 달성하기 위하여, 본 발명의 일 실시예에서는 바인더 95 내지 99 중량%, 및 산화아연 분말 1 내지 5 중량%를 포함하는 항균 조성물을 포함하는 항균 조성물을 제공한다. In order to achieve the first object of the present invention, there is provided an antimicrobial composition comprising an antimicrobial composition comprising 95 to 99% by weight of a binder and 1 to 5% by weight of a zinc oxide powder in an embodiment of the present invention.
또한, 본 발명의 제2 목적을 달성하기 위하여, 본 발명의 일 실시예 에서는 고분자 필름, 및 상기 고분자 필름 상에 0.01 내지 100 ㎛의 두께로 도포된 항균 조성물을 포함하는 기능성 필름에 있어서, 상기 항균 조성물은 바인더 95 내지 99 중량%와 산화아연 분말 1 내지 5 중량%의 혼합물, 및 상기 혼합물의 100 중량부를 기준으로 10 내지 900 중량부의 분산제가 포함된 기능성 필름을 제공한다.In order to achieve the second object of the present invention, in an embodiment of the present invention, there is provided a functional film comprising a polymer film and an antimicrobial composition coated on the polymer film in a thickness of 0.01 to 100 탆, The composition provides a functional film comprising 10 to 900 parts by weight of a dispersing agent based on 100 parts by weight of a mixture of 95 to 99% by weight of the binder and 1 to 5% by weight of the zinc oxide powder.
본 발명에 의하면, 최근 인체 위해성이 제기되고 있는 합성 화학물질을 기반으로 하는 항균 제품을 대체할 수 있으며, 인체에 무해한 소재를 사용하여 상기 항균 제품에 대등한 항균력을 제공할 수 있다.According to the present invention, an antimicrobial product based on a synthetic chemical substance, which has recently been exposed to a human risk, can be substituted, and the antibacterial activity equivalent to that of the antibacterial product can be provided by using a material harmless to human body.
또한, 본 발명은 스프레이 형태로 사용하는 경우, 항균 시트지나 필름 등의 사용이 어려운 구석진 곳, 굴곡진 표면을 가지는 제품에도 간편하게 적용할 수 있다. Further, when the present invention is used in the form of a spray, it can be easily applied to products having curved surfaces or curved surfaces which are difficult to use such as antibacterial sheets or films.
아울러, 본 발명은 티타늄 등과 달리 태양광 등 주변 환경에 무관하게 효과를 발휘하므로, 환경에 관계없이 우수한 항균효과를 제공할 수 있다. In addition, unlike titanium or the like, the present invention exerts an effect irrespective of the surrounding environment such as sunlight, so that an excellent antibacterial effect can be provided regardless of the environment.
이와 같이, 불특정 다수가 사용하는 물체나 건축물에 적용하면, 해당 물체나 건축물에 항균력과 살균력을 부여함으로써, 손이나 발 등의 접촉을 통해 세균이 번식되는 것을 방지할 수 있으므로, 별도의 공중위생 활동 없이도 세균의 번식을 억제할 수 있다.As described above, when applied to an object or building used by an unspecified number of people, it is possible to prevent the propagation of bacteria through contact with a hand or a foot by applying the antibacterial power and the sterilizing power to the object or building, It is possible to suppress the propagation of bacteria.
이하, 본 발명의 바람직한 실시예들에 의한 산화아연을 주성분으로 하는 항균 조성물 및 이를 적용한 기능성 필름(이하, "항균 조성물"이라 한다) 및 이를 이용한 기능성 필름을 상세하게 설명한다.Hereinafter, an antimicrobial composition containing zinc oxide as a main component according to preferred embodiments of the present invention, a functional film (hereinafter referred to as "antimicrobial composition") and a functional film using the same will be described in detail.
본 발명의 일 실시예에 의한 항균 조성물은 바인더, 및 산화아연 분말을 포함하며, 선택적으로 분산제를 더 포함할 수 있다. An antimicrobial composition according to an embodiment of the present invention includes a binder and zinc oxide powder, and may further include a dispersant.
이러한, 항균 조성물은 건축물에 적용하여 각종 세균 등으로부터 안전하게 사용자를 보호하는 역할을 수행한다. 예컨대, 본 발명의 항균 조성물은 탄성코트의 대용으로 베란다에 도포되어 사용되거나, 타일 줄눈제로 사용될 수 있다.Such an antimicrobial composition is applied to a building to safely protect a user from various bacteria and the like. For example, the antimicrobial composition of the present invention may be applied to a veranda as a substitute for an elastic coat, or used as a tile joint agent.
또한, 상기 항균 조성물은 스마트폰을 비롯하여 은행과 증권사의 ATM기기, 관공서에서 사용되는 민원발급기 등에 사용되는 TFT-LCD 등의 터치패널, 쇼핑카트의 손잡이, 키보드의 키스킨 등의 표면부에 적용하여 각종 세균 등으로부터 안전하게 표면부를 유지하도록 하는 역할도 수행할 수 있다. In addition, the antimicrobial composition is applied to a surface portion of a touch panel such as a TFT-LCD, a handle of a shopping cart, and a keyboard of a keyboard, which are used for an ATM device of a bank, a securities company, It can also function to keep the surface portion safely from bacteria and the like.
이러한 각각의 성분들은 서로 화학적인 작용을 통하여 공동으로 기능을 수행할 수도 있는데, 이는 화학 물질의 특성상 당연한 것이다. 따라서, 본 발명은 특정 기능 성분에만 의존 한다기보다는 여러 조성의 조합과 그 조합량에 특이성이 있다고 할 수 있다. 특히, 본 발명은 살균 및 항균 효과가 뛰어나지만 인체에 침투할 경우 유해인자로 작용할 가능성이 높은 은나노 물질을 첨가하지 않더라도 은나노 물질이 첨가된 항균 조성물에 대등한 항균력을 제공하는 항균 조성물을 발명하는데 그 기술적 의의가 존재한다.Each of these components may function jointly with each other through a chemical action, which is natural in the nature of the chemical. Therefore, the present invention can be said to have a specific combination of various composition combinations and combinations thereof, rather than depending only on a specific functional ingredient. In particular, the present invention relates to an antimicrobial composition which provides antimicrobial activity comparable to antimicrobial compositions to which silver nanomaterials are added even when silver nanomaterials which are excellent in sterilization and antimicrobial effects but are likely to act as harmful agents when they are infiltrated into human body are not added. Technical significance exists.
먼저, 본 발명의 일 실시예에 의한 항균 조성물은 바인더를 포함한다.First, the antimicrobial composition according to one embodiment of the present invention includes a binder.
상기 바인더는 항균 조성물이 분무되는 대상물에 항균 조성물의 유효성분을 고정시키는 역할을 하는 것으로, 열경화성수지, UV경화성수지, 열 및 UV 동시 경화성수지, 습기경화성수지 또는 이들을 2 이상 혼합한 수지를 사용할 수 있다. 예컨대, 바인더로는 폴리우레탄, 폴리우레아, 아크릴, 에폭시, 폴리프로필렌, 폴리에틸렌, 폴리설폰(polysulfone), 폴리스티렌, 폴리염화비닐, 폴리에틸렌테레프탈레이트, 폴리에스테르, 나일론 및 실리콘수지 중 어느 하나를 사용하는 것이 바람직하다.The binder serves to fix the active ingredient of the antimicrobial composition to an object to which the antibacterial composition is sprayed. The binder may be a thermosetting resin, a UV curable resin, a heat and UV curable resin, a moisture curable resin, or a resin obtained by mixing two or more thereof have. For example, the binder may be any one of polyurethane, polyurea, acrylic, epoxy, polypropylene, polyethylene, polysulfone, polystyrene, polyvinyl chloride, polyethylene terephthalate, polyester, nylon and silicone resin desirable.
구체적으로, 상기 열경화성수지로는 에폭시수지, 우레탄수지, 아크릴수지, 불소수지 등을 사용하는 것이 바람직하지만, 이들에 한정되지 않는다.Specifically, as the thermosetting resin, an epoxy resin, a urethane resin, an acrylic resin, a fluororesin or the like is preferably used, but not limited thereto.
상기 UV경화성수지로는 어떠한 UV경화성수지를 사용하여도 무방하지만, 바람직하게는 폴리우레탄아크릴레이트 25 내지 35 중량%, 반응성 모노머 희석제 10 내지 27 중량%, 접착촉진제 1 내지 3 중량%, 메틸에틸케톤(methyl ethyl ketone : 이하 "MEK"라 한다.) 15 내지 20 중량%, 톨루엔 20 내지 25 중량%로 이루어진 혼합물을 사용하는 것이 좋다. 이때, 상기 UV경화성수지에는 기타용제 5 내지 27 중량%가 더 포함될 수 있다. 여기서, 상기 반응성 모노머 희석제로는 단관능 아크릴레이트모노머, 삼관능 아크릴레이트모노머 또는 이들의 혼합물을 사용하는 것이 바람직하다.As the UV curable resin, any UV curable resin may be used, but preferably 25 to 35% by weight of a polyurethane acrylate, 10 to 27% by weight of a reactive monomer diluent, 1 to 3% by weight of an adhesion promoter, 15 to 20% by weight of methyl ethyl ketone (hereinafter referred to as "MEK"), and 20 to 25% by weight of toluene. At this time, the UV curable resin may further contain 5 to 27% by weight of other solvent. The reactive monomer diluent may be a monofunctional acrylate monomer, a trifunctional acrylate monomer, or a mixture thereof.
또한, 상기 UV경화성수지로는 폴리우레탄아크릴레이트 25 내지 35 중량%, 반응성 모노머 희석제 15 내지 40 중량%, 접착촉진제 1 내지 3 중량%, 광개시제 8 내지 14 중량%, 레벨링제 0.5 내지 1.5 중량%, MEK 15 내지 20 중량%, 톨루엔 20 내지 25 중량% 및 부틸아세테이트 1 내지 10 중량%로 이루어진 혼합물을 사용할 수도 있다.The UV curable resin may further contain 25 to 35 wt% of a polyurethane acrylate, 15 to 40 wt% of a reactive monomer diluent, 1 to 3 wt% of an adhesion promoter, 8 to 14 wt% of a photoinitiator, 0.5 to 1.5 wt% of a leveling agent, Mixtures of 15 to 20% by weight of MEK, 20 to 25% by weight of toluene and 1 to 10% by weight of butyl acetate may also be used.
필요에 따라, 상기 바인더로는 주제(主劑)와 경화제를 혼합하여 제조한 2액형(二液型) 바인더를 사용할 수 있다. 예컨대, 바인더로는 주재로 폴리올(polyol)과 경화제로 이소시아네이트 수지를 사용한 폴리우레탄을 사용할 수 있으며, 주재로 아민계 수지와 경화제로 이소시아네이트 트리폴리머(lsocyante Trepolymer)를 사용한 폴리우레아를 사용할 수 있다. 이때, 산화아연 분말은 주재나 경화제 중 어느 한 곳에 미리 혼합된 형태로 포함될 수도 있다.If necessary, the binder may be a two-pack type binder prepared by mixing a main agent and a curing agent. For example, as the binder, polyol using polyol and isocyanate resin as a curing agent can be used, and polyurea mainly using amine resin and isocyanate triopolymer (lsocyante Trepolymer) as a curing agent can be used. At this time, the zinc oxide powder may be preliminarily mixed with any one of the host material and the curing agent.
한편, 본 발명에 따른 항균 조성물에 포함되는 바인더는 항균 조성물 100 중량%를 기준으로 95 내지 99 중량%가 사용된다. 이때, 항균 조성물에 포함되는 바인더의 함량이 95 중량% 미만이면 경화속도가 느려지고, 피착면에 접착력이 떨어지는 문제가 발생되며, 항균 조성물의 유효성분이 피착면에 일정기간(최소 6개월) 이상 부착된 상태를 유지할 수 없게 된다. 또한, 바인더의 함량이 99 중량%를 초과하면 전체 조성에서 산화아연 분말제의 첨가량이 감소하여 항균성이 저하될 수 있다. Meanwhile, the binder contained in the antimicrobial composition according to the present invention is used in an amount of 95 to 99% by weight based on 100% by weight of the antimicrobial composition. If the content of the binder contained in the antimicrobial composition is less than 95% by weight, the curing rate is slowed, the adhesive strength to the surface of the adhesive layer is lowered, and the effective ingredient of the antimicrobial composition adheres to the surface of the adhesive layer for at least 6 months The state can not be maintained. If the content of the binder is more than 99% by weight, the amount of the zinc oxide powder to be added may decrease in the whole composition and the antibacterial property may be lowered.
본 발명의 일 실시예에 의한 항균 조성물은 산화아연 분말을 포함한다.The antimicrobial composition according to an embodiment of the present invention includes zinc oxide powder.
상기 산화아연 분말은 항균 조성물이 사용되어 항균력, 살균력을 부여하는 것으로서, 항곰팡이성, 탈취성이 우수하다. 이러한 산화아연은 바이러스나 박테리아의 신진대사를 저해시킴으로써 이를 고사시켜 제거하는 메커니즘을 통해 항균력 및 살균력을 부여한다. 특히, 나노사이즈의 산화아연은 비표면적이 증가하여 벌크 재료가 구비하지 못한 표면효과를 가지며, 항균 조성물이 도포된 모체가 공기 중의 수분과 접촉하게 될 때, 모체의 표면에 존재하는 산화아연의 아연 금속 성분이 이온화되어 용출되면서 박테리아 등의 유해균에 항균제로서 작용하게 된다.The zinc oxide powder is used as an antimicrobial composition to impart antibacterial and disinfecting power, and is excellent in anti-mold and deodorant properties. These zinc oxide inhibits the metabolism of viruses and bacteria, thereby giving them antimicrobial and sterilizing power through a mechanism to eliminate them. Particularly, the zinc oxide of nano size has a surface area that is not provided by the bulk material due to an increase in specific surface area. When the host coated with the antimicrobial composition comes into contact with moisture in the air, zinc oxide The metal component ionizes and elutes and acts as an antimicrobial agent against harmful bacteria such as bacteria.
이러한 산화아연 분말은 100 내지 150㎚의 평균 입경을 가지는 것이 바람직하다. 여기서, 평균 입경이란 전체 부피를 100%로 한 입도의 누적분포 곡선에서 50부피%에 해당하는 누적 평균입경을 의미한다. 예를 들어, 입도 분석기(Particle size analyzer)로 측정하거나, TEM 또는 SEM 사진으로부터 측정할 수도 있다. 다른 방법으로는, 동적광산란법(dynamic Light-scattering)을 이용한 측정장치를 이용하여 측정한 후, 데이터 분석을 실시하여 각각의 사이즈 범위에 대하여 입자수가 카운팅 되며, 이로부터 계산을 통하여 평균 입경을 쉽게 얻을 수 있다.The zinc oxide powder preferably has an average particle diameter of 100 to 150 nm. Here, the average particle diameter means a cumulative average particle diameter corresponding to 50% by volume in the cumulative distribution curve of the particle size at 100% of the total volume. For example, it can be measured with a particle size analyzer, or measured from a TEM or SEM photograph. Alternatively, the measurement is performed using a dynamic light-scattering measuring device, and data analysis is performed. The number of particles is counted for each size range, and the average particle size is easily calculated Can be obtained.
이때, 항균 조성물에 포함되는 산화아연의 평균 입경이 100㎚ 미만이면 분산제가 첨가된 항균 조성물을 1개월 등의 비교적 짧은 기간 이내에 사용하는 경우에는 문제가 없으나, 보관 기간이 증가되는 경우에는 분산제가 첨가된 항균 조성물이 액상으로 보관되는 특성 상 산화아연 미립자가 특정 부분에 집중되어 항균 조성물로 형성된 코팅면이 균일한 항균력을 나타내지 못하는 문제가 발생될 수 있다. 또한, 산화아연의 평균 입경이 150㎚를 초과하면 항균 조성물이 코팅된 모체의 환경에 따라 효과적인 표면효과를 나타내기 어려운 문제가 발생될 수 있다. If the average particle diameter of the zinc oxide contained in the antimicrobial composition is less than 100 nm, there is no problem when the antimicrobial composition containing the dispersing agent is used within a relatively short period such as one month. However, when the storage period is increased, The zinc oxide fine particles are concentrated in a specific part, and the coated surface formed with the antimicrobial composition may not exhibit a uniform antibacterial activity. If the average particle diameter of zinc oxide is more than 150 nm, there may arise a problem that it is difficult to exhibit an effective surface effect depending on the environment of the coated body of the antimicrobial composition.
또한, 상기 산화아연은 인체유해성이 적고 티타늄 등과 달리 태양광과 무관하게 항균효과를 나타낼 수 있다. In addition, zinc oxide has little harmfulness to humans and can exhibit an antibacterial effect regardless of sunlight, unlike titanium and the like.
본 발명에 따른 항균 조성물에 포함되는 산화아연 분말은 항균 조성물 100 중량%를 기준으로 1 내지 5 중량%가 사용된다. 이때, 항균 조성물에 포함되는 산화아연 분말의 함량이 1 중량% 미만이면 항균 조성물의 코팅 대상면(피착면)에 항균력을 제공할 수 없다. 또한, 산화아연 분말의 함량이 5 중량%를 초과하면 항균력에 대한 효과의 향상은 미미하며 제조비용이 증가되는 문제가 발생될 수 있다.The zinc oxide powder contained in the antimicrobial composition according to the present invention is used in an amount of 1 to 5% by weight based on 100% by weight of the antimicrobial composition. At this time, if the content of the zinc oxide powder contained in the antimicrobial composition is less than 1% by weight, the antimicrobial activity can not be provided on the coated surface (coated surface) of the antimicrobial composition. If the content of the zinc oxide powder exceeds 5% by weight, the effect on the antibacterial activity is insignificant and the manufacturing cost may increase.
본 발명의 일 실시예에 의한 항균 조성물은 분산제를 더 포함할 수 있다. The antimicrobial composition according to an embodiment of the present invention may further include a dispersing agent.
상기 분산제는 항균 조성물에 포함된 바인더와 산화아연 분말을 균일하게 분산시키는 것으로, 물이나 유기용제 또는 물과 유기용제의 혼합물을 사용할 수 있다. The dispersing agent is used to uniformly disperse the binder and the zinc oxide powder contained in the antimicrobial composition, and water, an organic solvent, or a mixture of water and an organic solvent may be used.
구체적으로 상기 분산제로는 물, 알코올, 케톤류(아세톤, 메틸에틸케톤, 메틸이소부틸케톤, 시클로헥사논 등), 에테르류(메틸셀루솔브, 에틸셀루솔브, 부틸셀루솔브 등), 에스테르류(에틸아세테이트, 부틸아세테이트 등), 디메틸포름아마이드(dimethylformamide), n-메틸피로리딘, 프로필렌 글리콜모노메틸 에테르 아세테이트, 디베이직 에스테르, 디메틸카보네이트, 또는 톨루엔 등을 사용할 수 있으며, 이들을 2 이상 혼합하여 사용할 수도 있다. 필요에 따라, 상기 분산제로는 메틸에틸케톤(MEK)을 일부 첨가하여 사용할 수 있다.Specific examples of the dispersing agent include water, alcohols, ketones (such as acetone, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone), ethers (methyl cellosolve, ethyl cellosolve, butyl cellosolve, etc.) Dimethylformamide, n-methylpyrrolidine, propylene glycol monomethyl ether acetate, dibasic ester, dimethyl carbonate, or toluene. These solvents may be used in combination of two or more thereof . If necessary, methyl ethyl ketone (MEK) may be added in part as the dispersing agent.
본 발명에 따른 분산제는 바인더 및 산화아연 분말의 혼합물 100 중량부를 기준으로 10 내지 900 중량부가 포함된다. 이때, 항균 조성물에 포함되는 분산제의 함량이 바인더 및 산화아연 분말의 혼합물 100 중량부를 기준으로 10중량부 미만이면 항균 조성물을 코팅 대상물 또는 필름에 도포하거나 필름 제조 시에 바인더와 산화아연 분말이 균일하게 분산시키는데 어려움이 발생될 수 있다. 특히, 분산제의 함량이 바인더 및 산화아연 분말의 혼합물 100 중량부를 기준으로 100중량부 미만이면 항균 조성물의 점성이 높아져 스프레이로 사용하기 어려운 문제가 발생될 수 있다. The dispersant according to the present invention contains 10 to 900 parts by weight based on 100 parts by weight of the mixture of the binder and the zinc oxide powder. If the content of the dispersant contained in the antimicrobial composition is less than 10 parts by weight based on 100 parts by weight of the mixture of the binder and the zinc oxide powder, the antimicrobial composition is applied to the coating object or film, or the binder and the zinc oxide powder are uniformly Difficulties may arise in dispersing. Particularly, if the content of the dispersing agent is less than 100 parts by weight based on 100 parts by weight of the mixture of the binder and the zinc oxide powder, the viscosity of the antimicrobial composition becomes high, which may make it difficult to use as a spray.
그리고 바인더 및 산화아연 분말의 혼합물 100 중량부를 기준으로 분산제의 함량이 900 중량부를 초과하면 나머지 다른 구성은 원활하게 분산시킬 수 있으나 도포면을 따라 항균 조성물이 흘러내리는 문제가 발생될 수 있다.If the content of the dispersing agent exceeds 900 parts by weight based on 100 parts by weight of the mixture of the binder and the zinc oxide powder, the other components may be dispersed smoothly, but the antibacterial composition may flow along the coated surface.
본 발명의 일 실시예에 의한 항균 조성물은 소포제를 더 포함할 수 있다. The antimicrobial composition according to an embodiment of the present invention may further include a defoaming agent.
상기 소포제는 항균 조성물을 스프레이용 조성물로 사용하는 경우 첨가되는 것으로, 항균 조성물을 스프레이 방식으로 대상물(모체)에 도포하는 경우 도포된 대상물의 표면에 발생하는 기포 등을 제거하는 기능을 제공한다. 특히, 소포제는 기포발생에 의해 도포면이 굴곡지게 변형되는 것을 방지함으로써 항균 조성물의 상품성을 높이는 역할을 한다. The antifoaming agent is added when the antimicrobial composition is used as a composition for spraying. When the antimicrobial composition is applied to an object (mother body) by spraying, the antifungal agent provides a function of removing air bubbles or the like generated on the surface of the applied object. In particular, the antifoaming agent serves to enhance the commerciality of the antimicrobial composition by preventing the coated surface from being deformed by bending.
본 발명에 따른 소포제는 바인더 및 산화아연 분말 혼합물의 100 중량부를 기준으로 2 내지 3 중량부가 포함된다. 이때, 바인더 및 산화아연 분말 혼합물의 100 중량부에 첨가되는 소포제의 함량이 2 중량부 미만이면 항균 조성물에 포함된 소포제의 함량이 낮아서 항균 조성물이 대상물의 표면에 도포되는 경우에 기포발생을 억지하지 못하여 도포면이 굴곡지게 변형되는 문제가 발생될 수 있다. 그리고 바인더 및 산화아연 분말 혼합물의 100 중량부에 첨가되는 분산제의 함량이 3 중량부를 초과하면 기포를 제거하는 이외의 추가적인 효과가 나타나지 않고 제조비용이 증가하는 문제가 발생될 수 있다. The antifoaming agent according to the present invention contains 2 to 3 parts by weight based on 100 parts by weight of the binder and the zinc oxide powder mixture. If the amount of the antifoaming agent added to 100 parts by weight of the binder and the zinc oxide powder mixture is less than 2 parts by weight, the content of the antifoaming agent contained in the antimicrobial composition is low so that bubbles are not inhibited There is a problem that the application surface is bent and deformed. If the content of the dispersant added to 100 parts by weight of the mixture of the binder and the zinc oxide powder exceeds 3 parts by weight, no additional effect other than bubble removal may be exhibited and the manufacturing cost may increase.
본 발명의 일 실시예에 의한 항균 조성물은 첨가제를 더 포함할 수 있다.The antimicrobial composition according to an embodiment of the present invention may further include an additive.
상기 첨가제로는 필름에 부착증진을 위하여 실란 커플링 첨가제를 사용할 수 있다. 이때, 실란 커플링 첨가제로는 비닐관능기의 트리메톡시 실란, 클로로 프로필 트리메톡시 실란, 글리시딜 에테르 관능기의 트리메톡시 실란, 메타아크릴레이트 관능기의 트리메톡시 실란, 1급 아민 관능기 및 2관능 아민 관능기의 트리메톡시 실란, 머캅토 프로필 트리메톡시 실란, 양이온 스터럴 트리메톡시 실란, 크로스링커 트리메톡시 실란 등을 사용할 수 있다.As the additive, a silane coupling additive may be used for adhesion enhancement to the film. Examples of the silane coupling additive include trimethoxysilane of vinyl functional group, chloropropyltrimethoxysilane, trimethoxysilane of glycidyl ether functional group, trimethoxysilane of methacrylate functional group, primary amine functional group and 2 Trifunctional amine functional groups such as trimethoxy silane, mercaptopropyl trimethoxy silane, cationic stearyl trimethoxy silane, cross linker trimethoxy silane, and the like can be used.
또한, 상기 첨가제로는 필름 표면의 전기 저항을 작게 하여 정전기의 발생을 방지함으로써 먼지의 흡착을 막기 위해 대전방지제를 사용할 수 있다. 이러한 대전방지제는 바인더 및 산화아연 분말 혼합물의 100 중량부를 기준으로 1 내지 5 중량부가 포함된다. 이때, 바인더 및 산화아연 분말 혼합물의 100 중량부에 첨가되는 대전방지제의 함량이 1 중량부 미만이면 필름 제조 시에 대전효과를 달성할 수 없으며, 대전방지제의 함량이 5 중량부를 초과하면 사용량 증가에 따른 효과의 향상은 미비하지만 생산비가 증가된다.As the additive, an antistatic agent may be used to prevent the adsorption of dust by preventing the generation of static electricity by reducing the electric resistance of the film surface. Such an antistatic agent is contained in an amount of 1 to 5 parts by weight based on 100 parts by weight of the binder and the zinc oxide powder mixture. If the content of the antistatic agent added to 100 parts by weight of the mixture of the binder and the zinc oxide powder is less than 1 part by weight, the charging effect can not be obtained at the time of producing the film. If the antistatic agent content exceeds 5 parts by weight, But the production cost is increased.
아울러, 상기 첨가제로는 탈취효과, 항균 성분에 의한 악취 발생 원인균 억제를 통한 소취효과를 나타낼 수 있도록 향료를 사용할 수 있다. 이때, 향료로는 악취를 마스킹함으로써 뛰어난 소취효과를 달성 할 수 있도록 잔향성이 우수한 향료를 사용하는 것이 좋다. 이러한 향료는 바인더 및 산화아연 분말의 혼합물 100 중량부를 기준으로 0.01 내지 0.1 중량부가 포함된다.In addition, as the additive, fragrance can be used so as to exhibit a deodorizing effect and a deodorizing effect by suppressing odor generating bacteria caused by an antibacterial component. At this time, as the fragrance, it is preferable to use a fragrance excellent in reverberation so as to achieve an excellent deodorizing effect by masking the odor. Such a perfume is contained in an amount of 0.01 to 0.1 part by weight based on 100 parts by weight of the mixture of the binder and the zinc oxide powder.
본 발명은 상기 항균 조성물이 고분자 필름에 적용된 기능성 필름을 제공한다. The present invention provides a functional film wherein the antimicrobial composition is applied to a polymer film.
본 발명에 따른 항균 조성물은 필름형태로 제작된 고분자 필름 표면에 0.01 내지 100 ㎛의 두께로 도포되어 기능성 필름을 제작하는데 사용될 수 있다. The antimicrobial composition according to the present invention may be applied to the surface of a polymer film prepared in the form of a film in a thickness of 0.01 to 100 탆 to prepare a functional film.
상기 고분자 필름은 1 내지 300 ㎛ 두께의 폴리프로필렌, 폴리에틸렌, 폴리에틸렌테레프탈레이트, 폴리우레탄, 폴리스티렌, 폴리염화비닐, 폴리비닐부티랄, 에틸렌비닐아세테이트, 폴리카보네이트, 또는 나일론 소재의 필름이거나, 이러한 각각의 고분자 필름 제조를 위한 원료물질을 복수 개 혼합하여 제작한 복합소재의 필름이 사용될 수 있지만, 이에 한정되지는 않는다.The polymer film may be a film of 1 to 300 탆 thick polypropylene, polyethylene, polyethylene terephthalate, polyurethane, polystyrene, polyvinyl chloride, polyvinyl butyral, ethylene vinyl acetate, polycarbonate, or nylon, A film of a composite material prepared by mixing a plurality of raw materials for producing a polymer film may be used, but is not limited thereto.
이러한 기능성 필름은 고분자 필름의 표면에 0.01 내지 100 ㎛ 두께로 전술한 항균 조성물을 도포하는 단계와, 상기 고분자 필름에 300 내지 500 mJ/㎠의 자외선(UV) 광량을 제공하는 동시에 70 내지 80℃로 2분 동안 건조하는 단계를 통하여 제조할 수 있다.The functional film may be formed by applying the above-described antimicrobial composition to the surface of the polymer film in a thickness of 0.01 to 100 탆, and providing the polymer film with an ultraviolet (UV) light quantity of 300 to 500 mJ / Followed by drying for 2 minutes.
특정 양태로서, 본 발명에 따른 기능성 필름은 30 내지 70 ㎛ 두께의 제 2 고분자 필름, 상기 제 2 고분자 필름의 상부에 구비된 제 1 실리콘 압력밀봉접착제(Pressure Sealing Adhesive: PSA) 점착층, 상기 제 1 실리콘 PSA 점착층의 상부에 구비된 1 내지 300 ㎛ 두께의 고분자 필름, 상기 고분자 필름 상부에 구비된 본 발명의 항균 조성물, 상기 항균 조성물 상부에 구비된 제 2 실리콘 PSA 점착층, 및 상기 제 2 실리콘 PSA 점착층의 상부에 구비된 30 내지 70 ㎛ 두께의 제 3 고분자 필름을 포함할 수 있다. 여기서, 제 2 고분자 필름과 제 3 고분자 필름은 상기 고분자 필름과 동일한 소재를 사용하는 것이 바람직하다.In a specific embodiment, the functional film according to the present invention comprises a second polymer film having a thickness of 30 to 70 탆, a first silicone pressure-sensitive adhesive (PSA) adhesive layer provided on the second polymer film, 1 < / RTI > silicone PSA adhesive layer, a second silicone PSA adhesive layer provided on the antimicrobial composition, and a second silicone PSA adhesive layer provided on the second polymeric film, And a third polymer film having a thickness of 30 to 70 mu m provided on the upper portion of the silicon PSA adhesive layer. Here, it is preferable that the second polymer film and the third polymer film use the same material as the polymer film.
이와 같이, 제 2 고분자 필름 및 제 3 고분자 필름이 구비된 기능성 필름은 제품에 사용하는 시점에, 제 1 실리콘 PSA 점착층으로부터 제 2 고분자 필름을 분리시키고, 제 2 실리콘 PSA 점착층으로부터 제 3 고분자 필름을 분리시켜 사용할 수 있다.As described above, the functional film provided with the second polymer film and the third polymer film is obtained by separating the second polymer film from the first silicone PSA adhesive layer at the time of use in the product and separating the second polymer film from the second silicone PSA adhesive layer, The film may be used separately.
즉, 상기 제 2 고분자 필름 및 제 3 고분자 필름은 임의적으로 분리시킬 수 있도록 구비되어 항균 조성물이 도포된 고분자 필름의 사용성을 향상시킨다. That is, the second polymer film and the third polymer film can be separated arbitrarily, thereby improving usability of the polymer film coated with the antimicrobial composition.
이하, 본 발명을 바람직한 일 실시예를 참조하여 다음에서 구체적으로 상세하게 설명한다. 단, 다음의 실시예는 본 발명을 구체적으로 예시하기 위한 것이며, 이것만으로 한정하는 것은 아니다.Hereinafter, the present invention will be described in detail with reference to the preferred embodiments. It should be noted, however, that the present invention is not limited to the following examples.
<실시예><Examples>
1. 폴리우레탄 192g, 산화아연 분말 8g, 분산제 800g을 1시간 동안 균일하게 혼합하여 항균 조성물을 수득하였다.1. 192 g of polyurethane, 8 g of zinc oxide powder and 800 g of dispersant were uniformly mixed for 1 hour to obtain an antimicrobial composition.
2. 100 ㎛ PET 필름의 상부에 상기 항균 조성물을 도포한 후 자외선 광량을 400mJ/㎠로 하여 온도 75℃하에서 2분 동안 건조하여 기능성 필름을 제조하였다. 2. The antimicrobial composition was coated on the top of a 100 탆 PET film and dried at 75 캜 for 2 minutes under ultraviolet light intensity of 400 mJ / cm 2 to prepare a functional film.
<비교예><Comparative Example>
1. UV경화성수지 400g, 은나노 콜로이드 용액 30g, 수용성 실리케이트 화합물 50g, 산화주석 미립자 100g을 1시간 동안 균일하게 혼합하여 항균 조성물을 수득하였다.1. An antimicrobial composition was obtained by mixing 400 g of the UV curable resin, 30 g of the silver nano-colloidal solution, 50 g of the water-soluble silicate compound and 100 g of the tin oxide fine particles uniformly for 1 hour.
2. 100 ㎛ PET 필름의 상부에 상기 항균 조성물을 도포한 후 자외선 광량을 400mJ/㎠로 하여 온도 75℃하에서 2분 동안 건조하여 기능성 필름을 제조하였다. 2. The antimicrobial composition was coated on the top of a 100 탆 PET film and dried at 75 캜 for 2 minutes under ultraviolet light intensity of 400 mJ / cm 2 to prepare a functional film.
<실험예><Experimental Example>
* 항균성 효과 시험 및 결과* Antimicrobial effect test and results
대장균(Escherichia coli ATCC 8739), 포도상구균(Staphylococcus aureus ATCC 6538P)을 대상으로 필름밀착법(JIZ Z 2801:2006)을 사용하여 기능성 필름의 항균력을 측정하였다.The antibacterial activity of the functional film was measured using Escherichia coli ATCC 8739 and Staphylococcus aureus ATCC 6538P using the film adhesion method (JIZ Z 2801: 2006).
이때, 표준필름은 Stomacher 400 poly-bag을 사용하였고, 시험균액을 35ㅁ 1℃, RH 90% 에서 24시간 정치 배양후 균수를 측정하였고, 그 결과는 표 1로 나타내었다.At this time, Stomacher 400 poly-bag was used as a standard film, and the bacterial counts were measured after culturing the test bacteria at 35 ° C and 1 ° C and RH 90% for 24 hours. The results are shown in Table 1.
상기 표 1에서 확인할 수 있는 바와 같이, 본 발명의 기능성 필름은 포도상구균과 대장균에 대해 2.0 이상의 항균활성치를 가지고 있는 것으로 나타났으며, 은나노 물질이 포함된 기능성 필름과 대등한 항균활성치를 가지고 있는 것으로 분석되었다. As can be seen in Table 1, the functional film of the present invention has an antibacterial activity value of not less than 2.0 against Staphylococcus aureus and Escherichia coli, and has an antibacterial activity equivalent to that of a functional film containing silver nanomaterials Respectively.
결과적으로, 본 발명에 따른 기능성 필름은 건축물의 유리창이나 터치패널, 자동판매기의 버튼이나 쇼핑카트의 손잡이에 사용되면, 우수한 세균 살균 효과를 얻을 수 있었다. As a result, when the functional film according to the present invention is used in a glass window of a building, a touch panel, a button of a vending machine, or a handle of a shopping cart, excellent bactericidal effect can be obtained.
이상에서 본 발명의 바람직한 실시예를 참조하여 설명하였지만, 해당 기술분야의 숙련된 당업자는 하기의 특허청구범위에 기재된 본 발명의 사상 및 영역으로부터 벗어나지 않는 범위 내에서 본 발명을 다양하게 수정 및 변경시킬 수 있음을 이해할 수 있을 것이다. It will be apparent to those skilled in the art that various modifications and variations can be made in the present invention without departing from the spirit and scope of the invention as defined in the appended claims. It can be understood that it is possible.
Claims (7)
상기 혼합물 100 중량부를 기준으로 메틸에틸케톤이 첨가된 분산제 10 내지 900 중량부; 및
상기 바인더 및 산화아연 분말의 혼합물 100 중량부를 기준으로 소포제 2 내지 3 중량부를 포함하는 항균 조성물.95 to 99% by weight of a two-component binder prepared by mixing a subject and a curing agent and a zinc metal component of zinc oxide existing on the surface of the mother when the mother coated with the antimicrobial composition comes into contact with moisture in the air is ionized and eluted 100 parts by weight of a mixture containing 1 to 5% by weight of a zinc oxide powder having an average particle diameter of 100 to 150 nm so as to act as an antibacterial agent against harmful bacteria;
10 to 900 parts by weight of a dispersant to which methyl ethyl ketone is added based on 100 parts by weight of the mixture; And
2 to 3 parts by weight of a defoaming agent based on 100 parts by weight of a mixture of the binder and the zinc oxide powder.
주재로 폴리올과 경화제로 이소시아네이트 수지를 사용한 폴리우레탄, 또는 주재로 아민계 수지와 경화제로 이소시아네이트 트리폴리머를 사용한 폴리우레아인 것을 특징으로 하는 항균 조성물.The image forming apparatus according to claim 1, wherein the two-component type binder
Wherein the polyurethane is polyurethane mainly using polyol and isocyanate resin as a curing agent, or polyurea mainly using an amine-based resin and an isocyanate tri polymer as a curing agent.
물 또는 유기용제인 것을 특징으로 하는 항균 조성물. The method of claim 1, wherein the dispersant
Wherein the antimicrobial composition is water or an organic solvent.
상기 항균 조성물은
주제와 경화제를 혼합하여 제조한 2액형 바인더 95 내지 99 중량%와 항균 조성물이 도포된 모체가 공기 중의 수분과 접촉하게 될 때 모체의 표면에 존재하는 산화아연의 아연 금속 성분이 이온화되어 용출되면서 유해균에 항균제로서 작용할 수 있도록 100 내지 150㎚의 평균 입경을 갖는 산화아연 분말 1 내지 5 중량%의 혼합물;
상기 혼합물의 100 중량부를 기준으로 메틸에틸케톤이 첨가된 분산제 10 내지 900 중량부; 및
상기 바인더 및 산화아연 분말의 혼합물 100 중량부를 기준으로 소포제 2 내지 3 중량부가 포함된 기능성 필름.1. A functional film comprising a polymer film and an antimicrobial composition coated on the polymer film in a thickness of 0.01 to 100 m,
The antimicrobial composition
When 95 to 99% by weight of a two-component binder prepared by mixing a base and a curing agent and a mother coated with the antimicrobial composition are brought into contact with moisture in the air, the zinc metal component present on the surface of the mother is ionized and eluted, 1 to 5% by weight of a zinc oxide powder having an average particle size of 100 to 150 nm so as to serve as an antimicrobial agent;
10 to 900 parts by weight of a dispersant to which methyl ethyl ketone is added based on 100 parts by weight of the mixture; And
A functional film comprising 2 to 3 parts by weight of a defoaming agent based on 100 parts by weight of a mixture of the binder and the zinc oxide powder.
폴리프로필렌, 폴리에틸렌, 폴리에틸렌테레프탈레이트, 폴리우레탄, 폴리스티렌, 폴리염화비닐, 폴리비닐부티랄, 에틸렌비닐아세테이트, 폴리카보네이트, 나일론 소재의 필름 또는 이들을 2 이상 혼합하여 제조한 필름인 것을 특징으로 하는 기능성 필름.The polymer film according to claim 6,
Wherein the film is a film made of polypropylene, polyethylene, polyethylene terephthalate, polyurethane, polystyrene, polyvinyl chloride, polyvinyl butyral, ethylene vinyl acetate, polycarbonate, nylon or a mixture of two or more thereof .