CN103571289A - Research and development of scrubbing-resistant odor-removal paint for internal walls - Google Patents
Research and development of scrubbing-resistant odor-removal paint for internal walls Download PDFInfo
- Publication number
- CN103571289A CN103571289A CN201310553449.6A CN201310553449A CN103571289A CN 103571289 A CN103571289 A CN 103571289A CN 201310553449 A CN201310553449 A CN 201310553449A CN 103571289 A CN103571289 A CN 103571289A
- Authority
- CN
- China
- Prior art keywords
- scrubbing
- development
- internal wall
- paint
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to research and development of scrubbing-resistant odor-removal paint for internal walls. The paint comprises the following ingredients in percentage by weight: 20-26% of emulsion, 18-22% of water, 4-6% of 1.5% cellulose ether solution, 0.6-0.7% of disperser, 0.09-0.11% of wetting agent, 0.9-1.5% of propylene glycol, 0.3-0.5% of defoaming agent, 0.6-0.7% of finished film, 0.1-0.3% of sterile agent, 13-14% of ground calcium carbonate, 5-7% of titanium dioxide, 7-9% of kaolin, 8-10% of diatomaceous earth, 0.1-0.14% of PH regulator, and 3-5% of thickener. The paint is proper in viscosity and thickness, cannot be clustered after being stored for a long time, can effectively remove harmful gases of formaldehyde, benzene, ammonia and the like indoors, release negative ions and regulate the air humidity. The paint has good property of easily scrubbing the contamination on a wall surface, is excellent in aspiration function, strong in fire resistance, capable of better effectively eliminating bacteria, and mould-proof and odor-proof, and antistatic. Through high-concentration air negative ions, the interior living environment can be tremendously improved to keep fresh and health life.
Description
Technical field the present invention relates to a kind of coating, and particularly the clean taste coating of scrubbing-tolerant internal wall, is a kind of advanced person's environmentally friendly functional materials, belongs to chemistry painting industry technical field.
Background technology is well-known, and people 70% time tides over indoor, so the degree of cleaning of room air will directly have influence on people's health.In recent years, along with living standards of the people improve constantly, living environment is constantly improved, when indoor decorating is increasingly luxurious, attractive in appearance, the problem that affects HUMAN HEALTH because fitting up the indoor pollution causing gets more and more, investigation shows: 68% disease cause is relevant with the pollution of room air, and 80% cancer is relevant with living environment, and metope is with the passing of time easily infected with spot.Therefore, high-efficient and lasting ground purifies indoor harmful gas, the target that keeps life, the Working environment of pure and fresh health to become people more and more urgently to pursue.Therefore to have the clean taste coating of scrubbing-tolerant internal wall significant in research.
Summary of the invention the object of this invention is to provide a kind of interior wall coating, and this coating viscosity is moderate, and long-term storage is not reunited, and can effectively remove the obnoxious flavoures such as indoor formaldehyde, benzene, ammonia, while anion releasing, adjusting air humidity.There is fabulous easy scouring metope spot performance, excellent respiratory function, fire protection flame retarding is strong, more can effectively remove bacterium, mildew-resistant deodorizing, anti-electrostatic.High density negative aeroion, can significantly improve indoor living environment, keeps the life of pure and fresh health.
The development of the clean taste coating of scrubbing-tolerant internal wall is by weight ratio:
Emulsion: 20-26%; Water: 18-22%; 1.5% ether of cellulose solution: 4-6%; Dispersion agent: 0.6-0.7%; Wetting agent: 0.09-0.11%; Propylene glycol: 0.9-1.5%; Defoamer: 0.3-0.5%; Film forming: 0.6-0.7%; Sterilant: 0.1-0.3%; Coarse whiting: 13-14%; Titanium dioxide: 5-7%; Kaolin: 7-9%; Diatomite: 8-10%; PH value conditioning agent: 0.1-0.14%; Thickening material: 3-5%.
Vinyl acetate between to for plastic/butyl acrylate copolymer that the emulsion that the present invention uses is softening agent, solids content is 48 ± 2%, minimum film-forming temperature is at 12 ℃.Can improve paint film smoothness, and there is good water-fast, fabulous scrub performance.
The Gonak that the ether of cellulose solution that the present invention uses is 1.5%, molecular weight is 55000.Have excellent water-retentivity, good temperature stability, improves putty application property, improves cohesive strength.
The diatomite that the present invention uses is that the remains deposition institute by unicellular waterplant diatom is formed, the free silica that the special performance of this diatom is to absorb in water forms its anatomy, deposition after its life finishes forms Diatomite Deposit under certain geologic condition.It has some unique performances, porousness, lower concentration, larger specific surface area, relative incompressibility and chemical stability, by the manufacturing procedures such as the pulverizing of original soil, sorting, calcining, air classification, impurity elimination are changed after the distribution and surface properties of its granularity, applicable to multiple industrial requirements such as paint of coating additives.Its feature is that absorption property is strong, unit weight is light, and fineness is even, and pH value neutrality is nontoxic, and mixing uniformity is good.It is neutral that pH value belongs to, and nontoxic, unit weight is light by 0.35, and it is good that powder carefully should play mixing uniformity, and SiO267% impels the effect of HUMAN HEALTH.Along with the raising of living standards of the people, the enhancing of health perception must be applied nontoxic smokeless mosquito-repellent incense, and diatomite can play combustion-supporting, smokeless, nontoxic, receives praises from customers.
The dispersion agent that the present invention uses is low molecular weight sodium polyacrylate dipersant, can significantly improve concentration and the stability thereof of fillers dispersed slurry, by this dispersion agent, can surround a layer charge on filler particles surface, make repulsion mutually between particle, thereby reach the effect of stable slurry.
The titanium dioxide that the present invention uses is anatase titanium dioxide, and kaolin is 1250 orders, and coarse whiting is 800 orders, and fine particle calcium carbonate is 800 orders.
During use, coating is stirred and just can carry out roller coating or spraying at the construction field (site).
Below embodiment, be one embodiment of the present of invention.
The development of the clean taste coating of scrubbing-tolerant internal wall by weight component is calculated as:
26 parts of emulsions; 16 parts of deionized waters; 7 part of 1.5% ether of cellulose solution E R30M; 0.65 part of dispersion agent; 0.48 part of wetting agent; 1.5 parts of propylene glycol; 0.45 part of defoamer; 0.6 part of film forming; 0.2 part of sterilant; 13 parts of coarse whitings; 13 parts of titanium dioxides; 7 parts of kaolin; 10 parts of diatomite; 0.12 part of pH value conditioning agent; 4 parts of thickening materials.
Production technique of the present invention is: after weighing in the ratio of formula under stirring at low speed, water, dispersion agent, wetting agent, defoamer, pH value conditioning agent, various powder added and mixed, and high speed dispersion half an hour, then add remaining mixing.
Its indices of interior wall coating of making according to the present invention all reaches GB/T9756-2009 about the requirement of interior wall coating defined, this coating viscosity is moderate, and long-term storage is not reunited, and can effectively remove the obnoxious flavoures such as indoor formaldehyde, benzene, ammonia, while anion releasing, adjusting air humidity.Not only there is excellent purifying air property, also there is stronger respiratory function, adjustable humidity.Have more fire protection flame retarding, high temperature resistant, do not burn, not combustion-supporting.Can effectively remove bacterium, mildew-resistant deodorizing.Metope is difficult for absorbing dust, anti-electrostatic, and used water is cleaned metope spot.Practicality is high, energy-conserving and environment-protective.High density negative aeroion, can significantly improve indoor living environment, keeps the life of pure and fresh health.
Claims (6)
1. concrete component and the part by weight of the Development Techniques of the clean taste coating of scrubbing-tolerant internal wall of the present invention are:
Emulsion: 20-26%; Water: 18-22%; 1.5% ether of cellulose solution: 4-6%; Dispersion agent: 0.6-0.7%; Wetting agent: 0.09-0.11%; Propylene glycol: 0.9-1.5%; Defoamer: 0.3-0.5%; Film forming: 0.6-0.7%; Sterilant: 0.1-0.3%; Coarse whiting: 13-14%; Titanium dioxide: 5-7%; Kaolin: 7-9%; Diatomite: 8-10%; PH value conditioning agent: 0.1-0.14%; Thickening material: 3-5%.
2. the development of the clean taste coating of a kind of scrubbing-tolerant internal wall according to claim 1, is characterized in that said emulsion is the vinyl acetate between to for plastic/butyl acrylate copolymer of softening agent, and solids content is 48 ± 2%, and minimum film-forming temperature is at 12 ℃.Can improve paint film smoothness, and there is good water-fast, fabulous scrub performance.
3. the development of the clean taste coating of a kind of scrubbing-tolerant internal wall according to claim 1, is characterized in that said ether of cellulose solution has excellent water-retentivity, and good temperature stability, improves putty application property, improves cohesive strength.
4. the development of the clean taste coating of a kind of scrubbing-tolerant internal wall according to claim 1, is characterized in that its feature of said diatomite is that absorption property is strong, unit weight is light, and fineness is even, and pH value neutrality is nontoxic, and mixing uniformity is good.It is neutral that pH value belongs to, and nontoxic, unit weight is light by 0.35, and it is good that powder carefully should play mixing uniformity, and SiO267% impels the effect of HUMAN HEALTH.
5. the development of the clean taste coating of a kind of scrubbing-tolerant internal wall according to claim 1, it is characterized in that said dispersion agent is low molecular weight sodium polyacrylate dipersant, can significantly improve concentration and the stability thereof of fillers dispersed slurry, by this dispersion agent, can surround a layer charge on filler particles surface, make repulsion mutually between particle, thereby reach the effect of stable slurry.
6. the development of the clean taste coating of a kind of scrubbing-tolerant internal wall according to claim 1, is characterized in that said titanium dioxide is anatase titanium dioxide, and kaolin is 1250 orders, and coarse whiting is 800 orders, and fine particle calcium carbonate is 800 orders.