KR101885363B1 - Manufacturing method of functional fabric having thermal insulation and waterproof function - Google Patents
Manufacturing method of functional fabric having thermal insulation and waterproof function Download PDFInfo
- Publication number
- KR101885363B1 KR101885363B1 KR1020170045356A KR20170045356A KR101885363B1 KR 101885363 B1 KR101885363 B1 KR 101885363B1 KR 1020170045356 A KR1020170045356 A KR 1020170045356A KR 20170045356 A KR20170045356 A KR 20170045356A KR 101885363 B1 KR101885363 B1 KR 101885363B1
- Authority
- KR
- South Korea
- Prior art keywords
- fabric
- adhesive
- waterproof
- waterproof fabric
- manufacturing
- Prior art date
Abstract
Description
본 발명은 보온 및 방수 기능을 갖는 기능성 원단에 관한 것으로, 더 상세하게는 접착제에 의해 통기성 방수 원단과 보온 원단을 합착(合着)시 주름 없이 매끄럽고 뒤틀림이 발생하지 않도록 합착 됨은 물론 합착 후에는 두 원단 간에 박리현상도 발생하지 않도록 한 보온 및 방수 기능을 갖는 기능성 원단의 제조방법에 관한 것이다. More particularly, the present invention relates to a functional fabric having an insulating and waterproof function. More specifically, the present invention relates to a functional fabric having an insulating and waterproof function, and more particularly, And a method of manufacturing a functional fabric having a thermal insulation function and a waterproof function so as not to cause peeling between cloths.
일반적으로 우의나 잠수복은 방수를 목적으로 제작된 의류의 일종으로, 전자인 우의는 우천시 의복의 위에 걸칠 수 있도록 제작되거나 작업장의 작업자, 어업 종사자, 레저용 등 다양한 분야에서 사용된다. In general, Wu's wetsuit is a kind of clothing made for the purpose of waterproofing, and the electronic wu is used in various fields such as worker in the workshop, fishermen, leisure, etc.
종래 통상적인 우의는 비닐재질로 제조되어 쉽게 찢어지는 등 그 내구성에 문제를 가지며, 피부와 직접 접촉하면서 온도차에 의해 내측 면에 습기를 발생시킴에 따라 오히려 옷이나 피부를 적시게 됨은 물론 체온을 떨어뜨리는 단점을 가진다. Conventionally, the right side is made of a vinyl material and is easily torn due to its durability. In addition, since it is in direct contact with the skin and generates moisture on the inner side due to a temperature difference, it moistens clothes and skin, It has a drawback.
이러한, 우의에서 가지는 문제점을 개선하기 위한 종래 선행기술에는 대한민국 등록실용신안 제20-0274654호(이하 '선행기술문헌 1'이라 한다)에 게시된 바와 같이 우의의 내피에 습기가 생기는 것을 막아 의복이 젖거나 피부에 달라붙는 것을 방지할 수 있어 활동성이 좋을 뿐만 아니라 보온성을 유지할 수 있어 장시간 사용시 오한이나 추위를 막을 수 있으며, 내피의 박리현상과 찢어짐 현상을 막아 우의의 내구성을 향상시킬 수 있는 부직포가 부착된 우의와 같은 기술이 제안된 바 있다. Conventional prior art for improving the problems of the above-mentioned problems has been disclosed in Korean Utility Model Registration No. 20-0274654 (hereinafter referred to as " Prior Art 1 ") to prevent moisture from forming on the inner surface of the human body, It is possible to prevent wetting or sticking to the skin, so that not only the activity but also the warmth can be maintained, it is possible to prevent chills and cold when used for a long time and to prevent the peeling of the inner skin and the tearing phenomenon and to improve the durability of the non- A technique similar to that of the attached technique has been proposed.
또한, 대한민국 등록실용신안 제20-0422177호(이하 '선행기술문헌 2'라 한다)에 게시된 바와 같이 비닐수지 또는 방수천 등으로 이루어진 우의의 내측에 보온성과 방습성, 활동성 등이 뛰어난 안감용 직물을 구비시킴으로써 피부와 접촉하는 우의의 내부에 습기발생을 차단하는 동시에 보온성을 높이고, 습기에 의한 우의의 피부접착을 방지하여 우의 착용시 그 활동성을 향상시키는 것은 물론 우의의 내구성을 증대시키도록 구성되는 우의와 같은 기술도 제안된 바 있다. In addition, as disclosed in Korean Utility Model Registration No. 20-0422177 (hereinafter referred to as "Prior Art Document 2"), a lining fabric excellent in warmth, moisture resistance and activity is formed on the inner side of a right side made of vinyl resin or waterproof cloth It is possible to prevent the moisture from being generated in the inside of the human body in contact with the skin, to increase the warmth, to prevent the skin adhesion of the human body due to moisture, to improve the activity when the human body is worn and to increase the durability of the human body Techniques such as Woojin have also been proposed.
한편, 후자인 잠수복은 수중에서 작업을 할 때 체온의 방열을 억제하고, 어류 등으로부터 잠수자의 신체를 보호하기 위한 목적으로 사용된다. On the other hand, the latter wet suit is used for the purpose of suppressing the heat radiation of the body temperature when working underwater and protecting the body of the diver from fishes and the like.
이러한 잠수복과 관련된 선행기술에는 대한민국 공개특허 제10-2016-0096414호(이하 '선행기술문헌 3'이라 한다)에 게시된 바와 같이 외부의 물은 내부로 유입되지 못하게 하고, 인체에서 배출되는 땀 등은 수증기 형태로 외부로 배출이 가능하게 함은 물론 특히, 수심이 깊은 곳에서 잠수를 수행하는 경우 수압이 증가하여도 착용감을 안정적으로 유지할 수 있도록 하면서, 체온을 유지하는 성능이 향상되어 잠수가능 시간을 연장할 수 있는 방한용 기능성 잠수복과 같은 기술이 제안된 바 있다. Prior art related to such a wet suit is disclosed in Korean Patent Laid-Open No. 10-2016-0096414 (hereinafter referred to as "Prior Art Document 3"), which prevents external water from flowing into the inside, It is possible to discharge water to the outside in the form of water vapor, and in particular, when performing diving in a deep water depth, it is possible to maintain a comfortable feeling even if the water pressure increases, Such as a functional wetsuit for winter, which is capable of extending the wetsuit.
아울러, 상기와 같이 보온 기능을 가지면서 방수 기능을 갖도록 하는 선행기술에는 대한민국 등록특허 제10-1399659호(이하 '선행기술문헌 4'라 한다)에 게시된 바와 같이 순수 알루미늄 호일을 사용하여 열을 차단 및 단열 보온효과를 가져오며 성형 강화재와 순수 알루미늄 호일을 접착하여 의류, 제화, 침구 또는 레저에 사용하기 위한 단열, 보온, 통풍 및 투습 기능을 구비한 원단과 같은 기술도 제안된 바 있다. In addition, as described above in the prior art which has a water-retaining function and has a waterproof function as described above, pure aluminum foil is used for heat treatment as disclosed in Korean Patent No. 10-1399659 (hereinafter referred to as 'Prior Art Document 4' Techniques such as insulation, insulation, ventilation, and moisture-proofing fabrics have been proposed for use in clothing, shoes, bedding or leisure by adhering a molding reinforcement and a pure aluminum foil to provide insulation and thermal insulation.
그러나 선행기술문헌 1 내지 2는 보온성이 저하됨은 물론 피부와 접촉시 꺼끌꺼끌 한 단점을 가진다. However, the prior art documents 1 and 2 have a disadvantage in that the warmth is deteriorated and the skin is in contact with the skin.
선행기술문헌 3 내지 4는 제조과정이 상당히 번거롭고 불편한 단점을 가진다. The prior art documents 3 to 4 have a disadvantage that the manufacturing process is considerably cumbersome and inconvenient.
아울러, 선행기술문헌 1 내지 4는 무엇보다도 외피와 내피 또는 외피와 내피 사이에 다른 부재를 개재시켜 부착하는 과정에서 각 부재 간에 매끄럽고 평평하게 부착되는 것이 아니라 어느 하나 이상의 부재에 주름이 발생하는 단점을 가진다. In addition, the prior art documents 1 to 4 have a disadvantage in that wrinkles are generated in one or more members rather than being smoothly and flatly attached to each other in the course of attaching the other members between the outer skin and the inner skin or between the outer skin and the inner skin I have.
또, 각 부재 간에 박리현상 또한 쉽게 발생하는 단점도 가진다. In addition, there is a disadvantage in that peeling phenomenon easily occurs between the members.
상기와 같은 종래의 제반 문제점을 해결하기 위한 본 발명의 주된 해결과제는 접착제에 의해 통기성 방수 원단과 보온 원단을 합착(合着)시 주름 없이 매끄럽고 뒤틀림이 발생하지 않도록 합착 됨은 물론 합착 후에는 두 원단 간에 박리현상도 발생하지 않도록 한 보온 및 방수 기능을 갖는 기능성 원단의 제조방법을 제공하는 데 있다. The main object of the present invention is to provide an air-permeable waterproof fabric and an insulating fabric which are adhered to each other so as not to be twisted smoothly without wrinkles, And a method of manufacturing a functional fabric having a thermal insulation function and a waterproof function so that the peeling phenomenon does not occur.
본 발명의 다른 해결과제는 통기성 방수 원단을 주름이 발생하지 않도록 평평하게 펼쳐질 수 있도록 하는 데 있다. Another object of the present invention is to provide a breathable waterproof fabric which can be flatly spread without wrinkles.
상기와 같은 기술적 과제를 해결하기 위한 본 발명의 해결수단은 보온과 방수 기능을 갖는 기능성 원단을 제조하는 방법으로서, 합착하고자 하는 통기성 방수 원단의 일면에 접착제를 균일하게 도포하는 단계; 상기 통기성 방수 원단에 도포된 접착제의 표면을 건조하는 단계; 상기 접착제의 표면이 건조된 통기성 방수 원단을 평판 상에 접착제가 도포된 면이 상부로 위치하면서 주름 없이 펼쳐지도록 중량 추에 의해 펼치는 단계; 및 상기 펼쳐진 통기성 방수 원단의 접착제가 도포된 면으로 합착하고자 하는 보온 원단을 주름지지 않게 고르게 펼친 후 소정 온도로 히팅 된 히팅 롤러를 이동시켜 합착하는 단계;를 포함한다. According to an aspect of the present invention, there is provided a method of manufacturing a functional fabric having a thermal insulation function and a waterproof function, the method comprising: uniformly applying an adhesive to one surface of a breathable waterproof fabric to be adhered; Drying the surface of the adhesive applied to the breathable waterproof fabric; Exposing the breathable waterproof fabric having the surface of the adhesive to weight by weight so that the adhesive coated surface is spread on the flat plate without wrinkles; And a step of uniformly spreading the heat-insulating fabric to be adhered to the surface of the stretched breathable waterproof fabric with the adhesive applied thereon so as not to corrugate, and then moving the heating roller heated to a predetermined temperature to coalesce.
상기 도포된 접착제의 표면을 건조는 송풍방식에 의해 건조한다. The surface of the applied adhesive is dried by a blowing method.
상기 중량 추에 의해 통기성 방수 원단을 펼치는 방식은 통기성 방수 원단의 서로 마주보는 양단 또는 서로 마주보는 양단 및 서로 마주보는 각 측단을 각 중량 추에 의해 주름 없이 펼치도록 한다. In the method of spreading the breathable waterproof fabric by the weight, the opposite ends of the breathable waterproof fabric, opposite ends of the waterproof fabric, facing each other, and opposite sides of the breathable waterproof fabric are spread without wrinkles by each weight weight.
상기 히팅 롤러의 히팅 온도는 20~35℃의 온도를 유지한다. The heating temperature of the heating roller is maintained at 20 to 35 ° C.
본 발명은 접착제에 의해 통기성 방수 원단과 보온 원단을 합착(合着)시 주름 없이 매끄럽고 뒤틀림이 발생하지 않도록 합착 됨은 물론 합착 후에는 두 원단 간에 박리현상도 발생하지 않도록 함으로써, 제작하고자 하는 우의나 잠수복 등 또한 매끄럽고 맵시 있게 제작할 수 있는 효과와 함께 착용자로 하여금 항시 따뜻하게 체온을 유지할 수 있는 효과를 가진다. In the present invention, the breathable waterproof cloth and the warm cloth are adhered to each other so as not to be twisted smoothly without wrinkles when the breathable waterproof cloth and the warm cloth are adhered by the adhesive, And the effect that the wearer can keep the body temperature warm at all times with the effect that the clothes can be made smoothly and elegantly.
또한, 통기성 방수 원단을 주름이 발생하지 않도록 평평하게 펼쳐질 수 있도록 함으로써, 보온 원단을 부착시 주름이나 뒤틀림 없이 원활하게 부착할 수 있는 효과도 가진다. Further, the breathable waterproof fabric can be flatly spread so as not to generate wrinkles, so that it is possible to smoothly attach the heat insulation fabric without wrinkles or warping when attached.
도 1은 본 발명의 제조방법을 설명하기 위한 블록도,
도 2는 본 발명의 제조 과정을 설명하기 위한 순서도이다. 1 is a block diagram for explaining a manufacturing method of the present invention;
2 is a flow chart for explaining the manufacturing process of the present invention.
이하, 본 발명의 바람직한 실시 예를 첨부된 도면을 참고하여 좀 더 상세하게 설명하면 다음과 같으며, 본 발명이 실시 예에 의해 제한되거나 한정되는 것은 아니다. Hereinafter, preferred embodiments of the present invention will be described in more detail with reference to the accompanying drawings. The present invention is not limited to the embodiments.
도 1은 본 발명의 제조방법을 설명하기 위한 블록도이며, 도 2는 본 발명의 제조 과정을 설명하기 위한 순서도이다. FIG. 1 is a block diagram for explaining a manufacturing method of the present invention, and FIG. 2 is a flowchart for explaining a manufacturing process of the present invention.
도시된 바와 같이 본원에서의 기능성 원단은 우의 또는 잠수복에 적용되는 것으로, 착용시 보온성을 가지면서 습기나 땀 등의 방출이 원활하게 이루어짐은 물론 얇은 두께로 활동성 또한 뛰어날 수 있도록 한다. As shown in the drawing, the functional fabric of the present invention is applicable to a right or wet suit, and it has a warmth at the time of wearing, smoothly discharges moisture and sweat, and is also excellent in activity with a thin thickness.
본 발명은 접착제에 의해 통기성 방수 원단과 보온 원단을 합착(合着)시 주름 없이 매끄럽고 뒤틀림이 발생하지 않도록 합착 됨은 물론 합착 후에는 두 원단 간에 박리현상도 발생하지 않도록 하는 데 있다. The present invention is intended to prevent adhesion between an air permeable waterproof fabric and an insulating fabric due to adhesiveness so as not to be twisted smoothly without wrinkles, and also to prevent peeling between two fabrics after adhesion.
본 발명에 따른 보온과 방수 기능을 갖는 기능성 원단을 제조하는 방법은 합착하고자 하는 통기성 방수 원단(10)의 일면에 접착제(B)를 균일하게 도포하는 단계(S1)를 행한다. 이때, 통기성 방수 원단은 비교적 신축성 없는 원단이다. A method of manufacturing a functional fabric having a thermal insulation and a waterproof function according to the present invention comprises the step (S1) of uniformly applying an adhesive (B) to one surface of a breathable waterproof fabric (10) to be adhered. At this time, the breathable waterproof fabric is relatively non-elastic fabric.
즉, 통기성 방수 원단은 일반적으로 고어텍스(Gore-tex)와 같이 테프론계 물질로 만들어진 기능성 섬유로 제작되는 것들을 말한다. 통기성 방수 원단은 액체의 통과는 차단되고 액체보다 입자가 매우 작은 기체의 통과만을 허용하는 섬유이다. 따라서 본 발명에서 사용되는 통기성 방수 원단은 빗물이나 해수는 내부로 침투되는 것을 방지하고, 내부의 땀과 같은 액체는 체온에 의해 기화된 상태에서 외부로의 배출이 가능한 것이다. 즉, 통기성 방수 원단은 알려진 바와 같이 방수성과 투습성이라는 상반된 특성을 동시에 지닌 소재로 고어텍스 이외에도 많은 제품이 개발되어 있고, 등산뿐만 아니라 모든 아웃도어 용품에 널리 쓰이고 있는 것으로서, 우의, 텐트, 재킷, 등산화, 장갑, 게이터, 침낭커버, 모자, 오버 트라우저 등의 소재로 보편화되어 있다. That is, breathable waterproof fabrics are generally made of functional fibers made of a Teflon-based material such as Gore-Tex. Breathable waterproof fabrics are fibers that block the passage of liquids and allow passage of very small particles than liquids. Therefore, the breathable waterproof fabric used in the present invention prevents rainwater or seawater from penetrating into the inside, and liquid such as sweat inside can be discharged to the outside in a state of being vaporized by body temperature. In other words, as it is known, breathable waterproof fabric is a material that has the opposite characteristics of waterproofness and moisture permeability, and many products other than Gore-Tex have been developed and widely used in all outdoor products as well as mountain climbing. , Gloves, gaiters, sleeping bag covers, hats and overtrailers.
통기성 방수 원단은 섬유의 표면을 방수성 수지로 가공하여 표면에 물 입자는 통과할 수 없는 많은 수의 작은 구멍이 생긴 엷은 막이 형성된 것이 특징이다. 물입자가 통과하지 못하는 작은 구멍은 1제곱인치당 90억 개 이상이 형성되는 것이 일반적이고, 이 작은 구멍들로 우의나 잠수복 내부의 땀은 수증기 형태로 빠져나갈 수 있다. The breathable waterproof fabric is characterized in that the surface of the fiber is made of a waterproof resin and a thin film is formed with a large number of small pores that can not pass water particles on the surface. It is common for small holes that water particles can not penetrate to form more than 9 billion per square inch, and these small holes allow the sweat inside the wet or wet suit to escape in the form of water vapor.
접착제는 공지된 스프레이 도포방식이나 롤 브러쉬 도포방식 등에 의해 어느 일부분으로 편중되지 않고 고르게 분포되면서 얇게 도포한다. 상기 접착제는 일반적인 접착제를 사용할 경우, 딱딱하게 경화됨에 따라 착용시 불편함을 유발할 수 있다. 그에 따라 유연성을 가질 수 있는 접착제, 즉 통상적인 폴리우레탄 접착제에 아세트산 에틸(Acetate Ethyl)을 적정 비율로 혼합한 접착제를 사용함으로써, 통기성 방수 원단과 후술하는 보온 원단이 긴밀하게 접착되어 박리되지 않을 뿐만 아니라 착용시에도 유연성으로 인한 불편함이 없도록 하는 것이 바람직하다. The adhesive is applied in a thin manner while being uniformly distributed in a part by a known spray application method or roll brush application method or the like. When the general adhesive is used, the adhesive hardens and may cause inconvenience when worn. Accordingly, by using an adhesive capable of having flexibility, that is, an adhesive obtained by mixing ethyl acetate (Acetate Ethyl) in an appropriate ratio with a conventional polyurethane adhesive, the breathable waterproof fabric and the insulation fabric to be described later are tightly adhered to each other But it is desirable to avoid inconvenience due to flexibility even when worn.
그리고 나서, 상기 통기성 방수 원단(10)에 도포된 접착제(B)의 표면을 건조하는 단계(S2)를 수행한다. 이때, 건조하는 방식은 통상적인 송풍기를 사용한 송풍방식에 의해 접착제의 표면만 건조될 수 있도록 한다. Then, a step (S2) of drying the surface of the adhesive (B) applied to the breathable waterproof fabric (10) is performed. At this time, the drying method allows only the surface of the adhesive to be dried by a blowing method using a conventional blower.
접착제의 표면을 건조하는 것은 접착제의 끈적이는 성질을 감소시켜 이후 작업공정 시 접착제가 묻어나는 것을 최소화할 수 있도록 함은 물론 취급이 편리할 수 있도록 하면서 후술하는 보온 원단과 부착시 그 보온 원단의 표면까지 접착제가 올라오지 않도록 하기 위한 것이다. Drying the surface of the adhesive reduces the stickiness of the adhesive thereby minimizing the appearance of glue during the subsequent working process. It also makes it convenient to handle, So that the adhesive does not come up.
그런 다음 상기 접착제(B)의 표면이 건조된 통기성 방수 원단(10)을 통상적인 평판 상에 접착제가 도포된 면이 상부로 위치하면서 주름 없이 펼쳐지도록 중량 추(15)에 의해 펼치는 단계(S3)를 행한다. Thereafter, the step (S3) of spreading the breathable waterproof fabric (10) with the surface of the adhesive (B) by the weight (15) so that the adhesive coated surface is spread on the conventional flat plate without wrinkles, .
다시 말해서, 접착제가 도포된 통기성 방수 원단을 펼칠 때 주름이 발생하지 않고 평평하게 펼쳐질 수 있도록 상기 통기성 방수 원단의 테두리에 중량 추를 구비하여 펼친다. 이때, 상기 중량 추에 의해 통기성 방수 원단을 펼치는 방식은 통기성 방수 원단의 서로 마주보는 양단 또는 서로 마주보는 양단 및 서로 마주보는 각 측단을 각 중량 추에 의해 주름 없이 펼치도록 한다. 상기 중량 추는 통상적인 클램프 등에 의해 통기성 방수 원단의 테두리에 고정한다. In other words, the breathable waterproof fabric is spread out with a weight on the rim of the breathable waterproof fabric so that when the breathable waterproof fabric is spread, the wrinkle does not occur and spreads flat. At this time, in the method of expanding the breathable waterproof fabric by the weight, the opposite ends of the breathable waterproof fabric, opposite ends of the waterproof fabric, or opposite sides and opposite sides of the breathable waterproof fabric are spread without wrinkles by each weight. The weight is secured to the rim of the breathable waterproof fabric by a conventional clamp or the like.
그로 인해 평판 상에서 통기성 방수 원단이 주름 없이 평평하게 펼쳐질 수 있는 것이다. So that the breathable waterproof fabric on the flat surface can be spread flat without wrinkles.
이후, 상기 펼쳐진 통기성 방수 원단(10)의 접착제(B)가 도포된 면으로 합착하고자 하는 통상적인 보온 원단(20)을 주름지지 않게 고르게 펼친 후 소정 온도로 히팅 된 히팅 롤러(16)를 이동시켜 가압에 의해 합착하는 단계(S4);를 포함한다. 상기 히팅 롤러(16)의 히팅 온도는 비교적 낮은 20~35℃의 온도를 유지한다. 이때, 히팅 롤러의 온도를 20℃ 이하일 경우에는 접착제로의 열 전달이 늦어져, 히팅 롤러의 이동 속도 또한 더 느려지게 되어 작업 효율성이 저하된다. 또, 히팅 롤러의 온더가 35℃ 이상일 때에는 접착제로 열은 신속하게 전달되나 성분이 변형될 우려가 있어, 상기한 온도를 유지하는 것이 바람직하다. Thereafter, the conventional
보온 원단은 감촉이 우수하면서 착용감 또한 뛰어난 통상적인 기모 처리된 기모 원단은 물론 방습성 및 흡습성은 물론 활동성과 보온성이 뛰어나면서 내구성이 우수한 섬유질의 직물을 사용하는 것이 바람직한 것으로, 예를 들어, 레이온이나 폴리에스테르섬유 등이 단독으로 제작되거나 또는 혼합된 형태의 직물을 사용하여도 무방하다. 또, 털 원단 등도 포함할 수 있다. 이때, 상기 보온 원단은 그 특성상 신축성을 가진다. It is preferable to use a fibrous fabric having excellent durability with excellent moisture and hygroscopicity as well as moisture-proof and hygroscopicity as well as ordinary brushed brushed fabrics having excellent feel and excellent comfort, and for example, rayon or poly Ester fiber, or the like may be used alone or in the form of a mixed fabric. In addition, hair fabrics and the like can also be included. At this time, the insulating fabric has elastic properties in terms of its characteristics.
다시 말해서, 보온 원단을 펼친 후 통상적인 프레스 방식에 의해 상부에서 가압하게 되면 신축성을 가지는 보온 원단이 일정하게 부착되는 것이 아니라 우는 것과 같이 주름지거나 혹은 뒤틀림이나 늘어지는 현상이 발생하는 단점을 가진다. In other words, when the insulating fabric is spread and then pressed at the upper portion by a conventional pressing method, the stretchable insulating fabric is not fixedly attached but is wrinkled, wrinkled, twisted or stretched.
이러한 문제점을 감안하여, 통기성 방수 원단의 접착제가 도포된 상부로 보온 원단을 주름지지 않게 고르게 펼친 후, 이때 접착제의 표면 또한 건조된 상태이므로 보온 원단이 바로 접착되는 것이 아니라 주름지지 않게 고르게 펼칠 수 있는 것이다. In view of such problems, since the insulating fabric is spread evenly over the upper surface to which the adhesive of the breathable waterproof fabric is applied, the surface of the adhesive is also dried, so that the insulating fabric is not directly bonded but spread evenly will be.
이렇게, 보온 원단이 고르게 펼쳐지면 소정 온도로 히팅 된 히팅 롤러를 보온 원단의 상면에서 이동시킴으로써, 접착제는 소정 온도로 히팅 된 히팅 롤러의 열이 전달되면서 통기성 방수 원단과 보온 원단을 주름이 발생하지 않으면서 뒤틀리거나 늘어짐 없이 긴밀하게 접착시키게 된다. When the heat-insulating fabric is uniformly spread, the heating roller heated to a predetermined temperature is moved on the upper surface of the heat-insulating fabric so that the heat of the heating roller heated to a predetermined temperature is transferred to the adhesive, So that they are closely bonded without twisting or sagging.
즉, 보온 원단은 접착제 상에서 늘려지지 않고 주름지지 않게 고르게 펼쳐진 상태이므로 그 상부를 히팅 롤러가 그대로 이동하면서 접착시킴에 따라 신축성을 가지는 보온 원단이 주름지거나 뒤틀림과 늘어짐 없이 긴밀하게 접착이 이루어질 수 있는 것이다. That is, since the heat-insulating fabric is not stretched on the adhesive but is spread evenly so as not to be wrinkled, the heat-insulating fabric having stretchability can be wrinkled or tightly adhered without twisting or sagging .
접착제 또한 소정 온도로 가열된 히팅 롤러로부터 전달되는 열에 의해 더욱더 높은 접착력을 가질 수 있게 됨으로써, 통기성 방수 원단과 보온 원단이 더욱더 긴밀하게 접착될 수 있는 조건을 가진다. The adhesive can also have a higher adhesive force by the heat transmitted from the heating roller heated to a predetermined temperature so that the breathable waterproof fabric and the insulating fabric can be more closely adhered to each other.
그로 인해 두 원단이 긴밀하게 접착됨으로써, 접착 후에는 두 원단이 박리되는 현상을 원천적으로 방지할 수 있게 된다. As a result, since the two fabric ends are closely adhered to each other, it is possible to fundamentally prevent the two fabric ends from being peeled off after bonding.
상기와 같이 본 발명에 의해 제조된 기능성 원단은 우의 또는 잠수복 이외에 필요로 하는 용도에 따라 제단과 봉제 과정을 거쳐 제작함으로써, 물과 접촉시에도 내부로 유입되지 않을 뿐만 아니라 뛰어난 보온성으로 인해 편안하고 안락하게 착용하여 사용할 수 있는 것이다. As described above, the functional fabric manufactured according to the present invention can be manufactured by sewing and sewing according to the needs of users other than the right or the wet suit, so that not only does not enter the inside even when it comes in contact with water, It can be used to wear.
10 : 통기성 방수 원단 15 : 중량 추
16 : 히팅 롤러 20 : 보온 원단10: Breathable waterproof fabric 15: Weight Chu
16: Heating roller 20: Insulating fabric
Claims (5)
합착하고자 하는 통기성 방수 원단의 일면에 폴리우레탄 접착제에 아세트산 에틸(Acetate Ethyl)이 혼합된 접착제를 균일하게 도포하는 단계;
상기 통기성 방수 원단에 도포된 접착제의 표면을 건조하는 단계;
상기 접착제의 표면이 건조된 통기성 방수 원단을 평판 상에 접착제가 도포된 면이 상부로 위치하면서 주름 없이 펼쳐지도록 중량 추에 의해 펼치는 단계; 및
상기 펼쳐진 통기성 방수 원단의 접착제가 도포된 면으로 합착하고자 하는 보온 원단을 주름지지 않게 고르게 펼친 후 20~35℃의 온도로 히팅 된 온도를 유지하는 히팅 롤러를 이동시켜 합착하는 단계;를 포함하되,
상기 중량 추에 의해 통기성 방수 원단을 펼치는 방식은 통기성 방수 원단의 서로 마주보는 양단 또는 서로 마주보는 양단 및 서로 마주보는 각 측단을 각 중량 추에 의해 주름 없이 펼치도록 하는 보온 및 방수 기능을 갖는 기능성 원단의 제조방법. A method of fabricating a functional fabric having thermal insulation and waterproof function,
Uniformly applying an adhesive mixed with ethyl acetate to a polyurethane adhesive on one side of a breathable waterproof fabric to be cemented;
Drying the surface of the adhesive applied to the breathable waterproof fabric;
Exposing the breathable waterproof fabric having the surface of the adhesive to weight by weight so that the adhesive coated surface is spread on the flat plate without wrinkles; And
A step of uniformly spreading the heat-insulating fabric to be adhered to the surface of the stretched breathable waterproof fabric with the adhesive coated thereon so as not to corrugate, and moving the heating roller to maintain the heated temperature at a temperature of 20 to 35 ° C,
In the method of spreading the breathable waterproof fabric by the weight, the ventilation waterproof fabric is provided with a function of maintaining both sides opposite to each other, opposite ends facing each other, and side edges facing each other without wrinkles by weight, ≪ / RTI >
상기 도포된 접착제의 표면을 건조는 송풍방식에 의해 건조하는 보온 및 방수 기능을 갖는 기능성 원단의 제조방법. The method according to claim 1,
Wherein the surface of the applied adhesive is dried by a blowing method.