KR101808828B1 - Sheath composite for electric cable and elcetric cable using the same - Google Patents
Sheath composite for electric cable and elcetric cable using the same Download PDFInfo
- Publication number
- KR101808828B1 KR101808828B1 KR1020160098497A KR20160098497A KR101808828B1 KR 101808828 B1 KR101808828 B1 KR 101808828B1 KR 1020160098497 A KR1020160098497 A KR 1020160098497A KR 20160098497 A KR20160098497 A KR 20160098497A KR 101808828 B1 KR101808828 B1 KR 101808828B1
- Authority
- KR
- South Korea
- Prior art keywords
- parts
- weight
- polyolefin
- maleic anhydride
- base resin
- Prior art date
Abstract
Description
본 발명은 전선용 시스 조성물 이를 포함하는 전선에 관한 것으로, 보다 상세하게는 친환경적이고, 내열성 및 물리적 특성이 향상된 전선용 시스 조성물 및 이를 포함하는 전선에 관한 것이다. TECHNICAL FIELD The present invention relates to a wire containing a wire for a wire, and more particularly, to a sheath composition for a wire having improved environmental friendliness, heat resistance and physical properties, and a wire containing the wire.
가교 폴리올레핀계 수지는 우수한 가공 특성, 내약품성, 내후성, 기계적 강도를 가지고 있어 가정용 전기제품, 건축자재, 내부 장식재, 자동차 부품 등의 분야에서 폭넓게 사용되고 있으며, 전선 재료로도 사용됨으로써 점차 그 응용 범위를 확대해 가고 있다. 그러나 이러한 가교 폴리올레핀계 수지는 난연에 매우 취약한 단점이 있어, 난연 특성을 얻기 위해 각종 유기계 또는 무기계 난연제를 첨가하여 사용하고 있다. Since the crosslinked polyolefin resin has excellent processing characteristics, chemical resistance, weather resistance and mechanical strength, it is widely used in household electric appliances, building materials, interior decoration materials, automobile parts and the like. It is expanding. However, such a crosslinked polyolefin-based resin is disadvantageous in that it is very vulnerable to flame retardancy, and various organic or inorganic flame retardants are added to obtain flame retardant properties.
상기 가교 폴리올레핀계 수지와 같은 고분자 수지의 난연성은 난연제의 종류에 따라 크게 좌우되는데, 종래 기술은 주로 염소, 브롬과 같은 할로겐을 함유하는 난연제를 사용하였으며, 이 경우 고분자 수지는 할로겐 원소들이 연소시 활성화된 고분자의 분해물을 안정화 시킴으로써 난연성을 얻을 수 있었다. The flame retardancy of the polymer resin such as the crosslinked polyolefin resin greatly depends on the kind of the flame retardant. In the prior art, a halogen-containing flame retardant such as chlorine or bromine is used. In this case, The flame retardancy was obtained by stabilizing the decomposition product of the polymer.
그러나, 할로겐계 화합물은 가교 폴리올레핀계 수지에 첨가됨으로써, 가공 및 연소시 인체에 유해한 유독 기체를 생성하고, 설비의 부식을 초래하는 독성 가스를 발생시켜 환경 문제를 일으키는 문제점이 있다. However, the halogen-containing compound is added to the crosslinked polyolefin-based resin, thereby generating poisonous gas harmful to the human body during processing and combustion, and generating toxic gas causing corrosion of the equipment, thereby causing environmental problems.
이러한 문제를 해결하기 위하여 비할로겐계 금속 난연제를 대체하여 사용하는 기술이 개발되었지만, 인장강도를 포함한 물리적 특성이 급격히 저하되는 문제가 있다. In order to solve such a problem, a technique of using a non-halogenated metal flame retardant instead of the halogen flame retardant has been developed. However, there is a problem that the physical properties including the tensile strength are rapidly deteriorated.
또한, 가교 올레핀계 수지는 가교 이후 재사용이나 처리 방법이 어려운 문제점이 있어 비가교 올리핀계 수지로 대체하여 사용하고 있지만, 비가교 올레핀을 사용하는 경우 내열성이 현저히 하락하여 전선에 사용하기 부적합한 문제가 있어, 본 발명은 이러한 문제를 해결하기 위하여 안출된 것이다. In addition, the crosslinked olefin resin is used in place of a non-crosslinked olefin resin because of problems such as difficulty in reuse and treatment after crosslinking. However, when non-crosslinkable olefin is used, the heat resistance is significantly lowered, , The present invention has been made in order to solve such a problem.
따라서, 본 발명은 상기와 같은 문제를 해결하기 위하여, 친환경적이면서도 동시에 내열성 및 물리적 특성이 우수한 전선용 시스 조성물 및 이를 포함하는 전선을 제공하는 것을 목적으로 한다. SUMMARY OF THE INVENTION Accordingly, it is an object of the present invention to provide a wire sheath composition that is eco-friendly, excellent in heat resistance and physical properties, and a wire including the wire sheath composition.
상기 과제를 해결하기 위하여, 본 발명의 일 측면에 따르면, 베이스 수지 및 무기 난연제를 포함하는 전선용 시스 조성물에 있어서, In order to solve the above problems, according to one aspect of the present invention, there is provided a wire sheath composition comprising a base resin and an inorganic flame retardant,
상기 베이스 수지가 비가교 폴리올레핀, 스티렌 공중합체 및 무수말레산 개질 폴리올레핀을 포함하고, Wherein the base resin comprises an uncrosslinked polyolefin, a styrene copolymer and a maleic anhydride modified polyolefin,
상기 베이스 수지 100 중량부에 대하여, 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 함량은 각각 독립적으로 10 중량부 내지 90 중량부이고, 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 총합은 70 내지 95 중량부인 것을 특징으로 하는 전선용 시스 조성물을 제공한다. The content of the non-crosslinkable polyolefin and the maleic anhydride-modified polyolefin is 10 to 90 parts by weight, and the total amount of the non-crosslinkable polyolefin and the maleic anhydride-modified polyolefin is 70 to 95 By weight based on the total weight of the composition.
상기 베이스 수지 100 중량부에 대하여, 상기 비가교 폴리올레핀의 함량은 20 내지 70 중량부일 수 있다. The amount of the non-crosslinkable polyolefin may be 20 to 70 parts by weight based on 100 parts by weight of the base resin.
상기 베이스 수지 100 중량부에 대하여, 상기 무기 난연제의 함량은 50 중량부 내지 150 중량부일 수 있다. The inorganic flame retardant may be contained in an amount of 50 to 150 parts by weight based on 100 parts by weight of the base resin.
상기 전선용 시스 조성물은 난연보조제, 안정제, 산화방지제, 및 가공조제 중 적어도 어느 하나를 더 포함할 수 있다. The wire sheath composition may further include at least one of a flame retardant aid, a stabilizer, an antioxidant, and a processing aid.
상기 무기 난연제가 수산화알루미늄, 수산화마그네슘, 하이드로마그네사이트 및, 하이드로탈사이트로 이루어진 군에서 선택되는 어느 하나 또는 둘 이상의 비할로겐계 금속 산화물을 포함할 수 있다. The inorganic flame retardant may include any one or two or more non-halogenated metal oxides selected from the group consisting of aluminum hydroxide, magnesium hydroxide, hydro-magneite, and hydrotalcite.
상기 무수말레산 개질 폴리올레핀이 폴리올레핀 100 중량부에 대하여, 무수말레산 0.5 내지 5 중량부를 포함일 수 있다. The maleic anhydride-modified polyolefin may include 0.5 to 5 parts by weight of maleic anhydride relative to 100 parts by weight of the polyolefin.
상기 베이스 수지 100 중량부에 대하여, 상기 난연보조제의 함량은 1 내지 10 중량부일 수 있다. The content of the flame-retardant auxiliary may be 1 to 10 parts by weight based on 100 parts by weight of the base resin.
상기 베이스 수지 100 중량부에 대하여, 상기 안정제, 산화방지제 및 가공조제의 함량은 각각 독립적으로 0.1 내지 10 중량부일 수 있다.The content of the stabilizer, the antioxidant and the processing aid may be independently 0.1 to 10 parts by weight based on 100 parts by weight of the base resin.
또한, 본 발명의 다른 일 측면에 따르면, 전술한 전선용 시스 조성물을 포함하는 전선이 제공된다. According to another aspect of the present invention, there is also provided an electric wire including the above-described sheath composition for a wire.
본 발명에 따른 열가소성 폴리올레핀, 스티렌 공중합체 및 무수말레산 개질 폴리올레핀이 최적의 중량비된 혼합된 베이스 수지와 무기 난연제를 함께 사용함으로써, 고온의 발명 조건에서도 견딜 수 있는 우수한 내열성을 가지며, 인장강도, 신장율 등의 물리적 물성 및 난연성이 우수하면서도 친환경적인 전선용 시스 조성물을 제공할 수 있는 이점이 있다. By using the thermoplastic polyolefin, styrene copolymer and maleic anhydride-modified polyolefin according to the present invention together with an inorganic flame retardant in combination with an optimal weight ratio of the mixed base resin and the inorganic flame retardant, it has excellent heat resistance that can withstand high temperature inventive conditions, Which is excellent in physical properties and flame retardancy as well as being environmentally friendly, can be provided.
이하, 본 발명에 대하여 상세히 설명하기로 한다. 이에 앞서 본 명세서 및 청구범위에 사용된 용어 또는 단어는 통상적이거나 사전적인 의미로 한정되어 해석 되어서는 안되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 따라서, 본 명세서상에 기재된 실시예와 도면에 도시된 구성은 본 발명의 가장 바람직한 일 실시예에 불과할 뿐이고, 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서, 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있음을 이해하여야 한다. Hereinafter, the present invention will be described in detail. The terms or words used in the present specification and claims should not be construed to be limited to ordinary or dictionary terms and the inventor should appropriately define the concept of terms in order to describe his invention in the best way The present invention should be construed in accordance with the meaning and concept consistent with the technical idea of the present invention. Therefore, the embodiments described in the present specification and the configurations shown in the drawings are only the most preferred embodiments of the present invention, and not all of the technical ideas of the present invention are described. Therefore, at the time of the present application, It should be understood that there are numerous equivalents and variations that can be made.
본 발명의 베이스 수지 및 무기 난연제를 포함하는 전선용 시스 조성물은 베이스 수지가 비가교 폴리올레핀, 스티렌 공중합체 및 무수말레산 개질 폴리올레핀을 포함하고, 상기 베이스 수지 100 중량부에 대하여, 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 함량은 각각 독립적으로 10 중량부 내지 90 중량부이고, 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 총합은 70 내지 95 중량부이다. The sheath composition for a wire comprising the base resin and the inorganic flame retardant of the present invention is characterized in that the base resin comprises an uncrosslinked polyolefin, a styrene copolymer and a maleic anhydride modified polyolefin, and the amount of the non- The content of the maleic anhydride-modified polyolefin is independently 10 parts by weight to 90 parts by weight, and the total amount of the non-cross-linked polyolefin and the maleic anhydride-modified polyolefin is 70 to 95 parts by weight.
상기 베이스 수지에 사용되는 비가교 폴리올레핀은 당해 기술분야에서 화학적 변화를 일으키지 않는 비가교 폴리올레핀이라면 제한없이 사용할 수 있고, 그 예로는 폴리에틸렌, 폴리프로필렌, 폴리부틸렌 등의 호모폴리머 또는 코폴리머 등이 있으며, 상세하게는 호모폴리프로필렌, 폴리프로필렌-에틸렌 코폴리머 등이 있을 수 있다. The non-crosslinked polyolefin used in the base resin is not particularly limited as long as it is a non-crosslinked polyolefin which does not cause any chemical change in the related art. Examples thereof include homopolymers or copolymers such as polyethylene, polypropylene and polybutylene , Specifically, homopolypropylene, polypropylene-ethylene copolymer, and the like.
또한, 상기 비가교 폴리올레핀은 용융지수(M.I.)가 0.5 내지 10 g/10min(230℃, 2.16kg), 상세하게는 0.7 내지 5 g/10min(230℃, 2.16kg), 더 상세하게는 1 내지 3 g/10min(230℃, 2.16kg)인 물질을 사용할 수 있으며, 용융지수가 이러한 범위를 만족하는 경우, 베이스 수지의 생산이 용이하고, 인장 강도가 우수하고, 흐름성이 제어되어 압출 가공성이 개선될 수 있다.The non-crosslinked polyolefin preferably has a melt index (MI) of 0.5 to 10 g / 10 min (230 DEG C, 2.16 kg), more specifically 0.7 to 5 g / 10 min (230 DEG C, 2.16 kg) 3 g / 10 min (230 ° C, 2.16 kg) can be used. When the melt index satisfies this range, the base resin is easily produced, the tensile strength is excellent, the flowability is controlled, Can be improved.
상기 무수말레산 개질 폴리올레핀은 무수말레산이 극성기로서 폴리올레핀에 그래프트된 형태로, 비할로겐계 금속수산화물 난연제와 첨가제, 다른 수지와의 혼화성을 증가시키고, 인장강도를 향상시키는 물질이며, 당해 기술분야에서 이러한 역할을 하는 물질은 제한없이 사용할 수 있으며, 비제한적인 예로는 바람직하게는 폴리프로필렌-그래프트-무수말레산일 수 있다. The maleic anhydride-modified polyolefin is a material in which maleic anhydride is grafted to a polyolefin as a polar group, and improves the compatibility of the non-halogenated metal hydroxide flame retardant with additives and other resins, and improves the tensile strength. Materials that act in this way may be used without limitation, and a non-limiting example is polypropylene-graft-maleic anhydride, preferably.
이때, 상기 무수말레산 개질 폴리올레핀은 폴리올레핀 100 중량부에 대하여, 극성기로 작용하는 무수말레산 0.5 내지 5 중량부를 포함할 수 있으며, 상기 범위를 만족하는 경우 다른 베이스 수지와 상용성이 우수하여, 인장강도 향상 효과를 극대화할 수 있다.The maleic anhydride-modified polyolefin may include 0.5 to 5 parts by weight of maleic anhydride acting as a polar group, based on 100 parts by weight of the polyolefin. When the content of the maleic anhydride modified polyolefin is within the above range, The strength improvement effect can be maximized.
전술한 바와 같이, 상기 베이스 수지 100 중량부에 대하여, 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 함량은 각각 독립적으로 10 중량부 내지 90 중량부이고, 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 총합은 70 내지 95 중량부이다.As described above, the content of the non-crosslinkable polyolefin and the maleic anhydride-modified polyolefin is preferably 10 parts by weight to 90 parts by weight, respectively, based on 100 parts by weight of the base resin, and the content of the non-crosslinkable polyolefin and the maleic anhydride- The total amount is 70 to 95 parts by weight.
구체적으로, 상기 비가교 폴리올레핀의 함량은 베이스 수지 100 중량부에 대하여, 10 중량부 내지 90 중량부, 상세하게는 20 내지 70 중량부, 더 상세하게는 30 내지 60 중량부일 수 있으며, 이러한 범위를 만족하는 경우, 유연성과 신장율, 가공성이 개선되고, 인장강도가 향상될 수 있다. Specifically, the amount of the non-crosslinking polyolefin may be 10 parts by weight to 90 parts by weight, specifically 20 to 70 parts by weight, more specifically 30 to 60 parts by weight, based on 100 parts by weight of the base resin. When satisfied, flexibility and elongation rate, workability can be improved and tensile strength can be improved.
또한, 상기 무수말레산 개질 폴리올레핀의 함량은 상기 베이스 수지 100 중량부에 대하여, 10 중량부 내지 90 중량부, 상세하게는 20 내지 70 중량부, 더 상세하게는 30 내지 60 중량부일 수 있으며, 이러한 범위를 만족하는 경우, 인장강도가 향상되고, 압출 가공성이 개선되며, 비가교 폴리올레핀 내에 무기 난연제의 분산성 및 상호 결합성을 증대시키는 역할을 하여 시스 조성물의 난연 효과를 높일 수 있다. The maleic anhydride-modified polyolefin may be used in an amount of 10 to 90 parts by weight, more preferably 20 to 70 parts by weight, and more preferably 30 to 60 parts by weight, based on 100 parts by weight of the base resin. , The tensile strength is improved, the extrusion workability is improved, the dispersibility of the inorganic flame retardant in the non-crosslinked polyolefin and the mutual bonding property are increased, and the flame retarding effect of the sheath composition can be enhanced.
상기 스티렌 공중합체는 비할로겐계 금속산화물 난연제와 상용성을 높여주며 신장율을 항샹시킬 수 있는 물질로서, 당해 기술분야에서 이러한 역할을 하는 스티렌 공중합체라면 제한 없이 사용할 수 있다. 이러한 스티렌 공중합체로서 상세하게는 스티렌/에틸렌-부틸렌 공중합체일 수 있으며, 이때 상기 공중합체에서 스티렌 반복단위:에틸렌-부틸렌 반복단위 총합의 중량비가 20:80 내지 80:40일 수 있고, 에틸렌 반복단위:부틸렌 반복단위의 중량비는 9:1 내지 1:9 일 수 있다. The styrene copolymer improves the compatibility with the non-halogenated metal oxide flame retardant and can increase the elongation. Any styrene copolymer having such a role in the art can be used without limitation. The styrene copolymer may be a styrene / ethylene-butylene copolymer, and the weight ratio of the styrene repeating unit: ethylene-butylene repeating unit sum in the copolymer may be 20:80 to 80:40, The weight ratio of ethylene repeat unit: butylene repeat unit may be from 9: 1 to 1: 9.
본 발명의 일 실시예에 따르면, 상기 스티렌 공중합체의 함량은 상기 베이스 수지에서 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 총합을 제외한 함량이 될 수 있다, 예를 들어, 상기 베이스 수지 100 중량부에 대하여 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 총합이 70 내지 95 중량부인 경우, 상기 스티렌 공중합체의 함량은 5 내지 30 중량부일 수 있다. According to an embodiment of the present invention, the content of the styrene copolymer may be the content of the base resin excluding the total amount of the non-crosslinkable polyolefin and the maleic anhydride-modified polyolefin. For example, , The total content of the non-crosslinkable polyolefin and the maleic anhydride-modified polyolefin is 70 to 95 parts by weight, and the content of the styrene copolymer may be 5 to 30 parts by weight.
또한, 상기 스티렌 공중합체는 융용지수가 3 내지 8g/10min(230℃, 2.16kg)인 물질일 수 있으며, 용융지수가 이러한 범위를 만족하는 경우, 압출 가공성이 개선되며, 물리적 특성이 향상될 수 있다. The styrene copolymer may be a material having a number of sheets of jute paper of 3 to 8 g / 10 min (230 DEG C, 2.16 kg). When the melt index satisfies the range, extrusion processability is improved and physical properties have.
본 발명의 일 실시예에 따른 복합수지 조성물은 난연성을 발현하기 위해 무기 난연제를 포함하며, 종래 유독 기체를 발생하던 할로겐의 문제점을 해결하기 위하여 비할로겐계 물질인 금속산화물을 사용할 수 있다. The composite resin composition according to an embodiment of the present invention includes an inorganic flame retardant to exhibit flame retardancy and a metal oxide that is a non-halogen based material can be used to solve the problem of halogen which has conventionally generated toxic gases.
상기 비할로겐계 금속산화물은 당해 기술분야에서 유독 기체를 발생하기 않으면서 난연성이 발휘되는 물질은 제한 없이 적용할 수 있으며, 비제한적인 예로는 수산화알루미늄, 수산화마그네슘, 하이드로마그네사이트 및 하이드로탈사이트 중 어느 하나 또는 둘 이상을 혼합하여 사용할 수 있다. 또한, 필요에 따라 실란커플링제 또는 지방산으로 표면 처리된 것을 사용할 수 있으며, 이때, 상기 표면 처리는 금속수산화물 100 중량부에 대하여 0.01 내지 3 중량부가 포함되도록 할 수 있다. The non-halogenated metal oxide can be applied without limitation to materials which exhibit flame retardancy without generating a toxic gas in the related art, and examples thereof include aluminum hydroxide, magnesium hydroxide, hydro-magneite and hydrotalcite One or two or more may be mixed and used. If necessary, a surface treated with a silane coupling agent or a fatty acid may be used. In this case, the surface treatment may include 0.01 to 3 parts by weight based on 100 parts by weight of the metal hydroxide.
또한, 상기 비할로겐계 금속산화물의 함량은 비가교 폴리올레핀 100 중량부에 대하여 20 내지 500 중량부, 상세하게는 70 내지 180 중량부일 수 있다. 상기 비할로겐계 금속산화물의 함량이 이러한 범위를 만족하는 경우, 난연성의 저하를 방지하고, 신장율의 급격한 저하 및 가공 과정에서 기계적 과부하의 문제가 해소될 수 있어, 난연성과 기계적 특성을 동시에 만족할 수 있다. The content of the non-halogenated metal oxide may be 20 to 500 parts by weight, specifically 70 to 180 parts by weight based on 100 parts by weight of the non-crosslinkable polyolefin. When the content of the non-halogenated metal oxide satisfies the above range, it is possible to prevent deterioration of the flame retardancy, to drastically decrease the elongation percentage and to solve the problem of mechanical overload during processing, and to simultaneously satisfy the flame retardancy and mechanical characteristics .
본 발명의 일 실시예에 따른 전선용 시스 조성물은 난연보조제, 안정제, 산화방지제, 가공 조제 등을 물성을 향상시키는 첨가제를 더 포함할 수 있다. The wire sheath composition according to an embodiment of the present invention may further include an additive for improving physical properties such as a flame retardant aid, a stabilizer, an antioxidant, a processing aid, and the like.
상기 난연보조제는 난연제와 혼용하여 사용하여 난연성을 보완해주고 기계적 특성의 하락을 최소화할 수 있으며, 당해 기술분야에서 사용되는 물질은 제한없이 사용할 수 있으며, 비제한적인 예로는 적색인, 실리콘계 화합물 등을 사용할 수 있다. The flame retardant adjuvant may be used in combination with a flame retardant to complement the flame retardancy and minimize the deterioration of the mechanical properties. Materials used in the technical field may be used without limitation, and examples thereof include red phosphorus, Can be used.
또한 상기 난연보조제는 베이스 수지 100 중량부에 대하여 1 내지 10 중량부 사용하는 것이 바람직한데, 이러한 범위를 만족하는 경우, 사용하는 효과가 있으면서, 블루밍(blooming) 현상을 방지할 수 있다.The flame-retardant aid is preferably used in an amount of 1 to 10 parts by weight based on 100 parts by weight of the base resin. When the range is satisfied, blooming can be prevented while using the flame-retardant.
상기 산화방지제의 비제한적인 예로는 페놀계 산화방지제, 인계 산화방지제, 황계 산화방지제등을 사용하며 하나 또는 둘 이상의 복합산화방지제를 사용할 수 있으며, 베이스 수지 100 중량부에 대하여 0.1 내지 10 중량부로 사용할 수 있다. Examples of the antioxidant include phenol-based antioxidants, phosphorus-based antioxidants, sulfur-based antioxidants, etc. One or more complex antioxidants may be used, and 0.1 to 10 parts by weight per 100 parts by weight of the base resin .
상기 가공조제로는 탄화수소계인 파라핀 왁스(paraffin wax) 또는 지방산계 왁스(stearic acid) 및 몬탄왁스(Montan wax), 실리콘계 왁스(sillicon wax) 등을 사용하며, 하나 또는 둘 이상의 혼합물을 사용할 수 있고, 베이스 수지 100 중량부에 대하여 0.1 내지 10 중량부로 사용할 수 있다. As the processing aid, a hydrocarbon type paraffin wax, fatty acid wax (stearic acid), Montan wax, sillicon wax and the like may be used, and one or a mixture of two or more thereof may be used, May be used in an amount of 0.1 to 10 parts by weight based on 100 parts by weight of the base resin.
또한, 본 발명의 다른 일 실시예에 따라 전술한 전선용 시스 조성물을 포함하는 전선이 제공된다. Further, according to another embodiment of the present invention, there is provided a wire including the above-described sheath composition for a wire.
이하, 본 발명을 구체적으로 설명하기 위하여 실시예를 들어 상세히 설명하기로 한다. 그러나 본 발명에 따른 실시예들은 여러 가지 다른 형태로 변형될 수 있으며, 본 발명의 범위가 아래에서 서술하는 실시예들에 한정되는 것으로 해석되어서는 안 된다. 본 발명의 실시예들은 당업계에서 평균적인 지식을 가지는 자에게 본 발명을 보다 완전하게 설명하기 위해 제공되는 것이다.BEST MODE FOR CARRYING OUT THE INVENTION Hereinafter, the present invention will be described in detail with reference to examples. However, the embodiments according to the present invention may be modified into various other forms, and the scope of the present invention should not be construed as being limited to the embodiments described below. Embodiments of the present invention are provided to more fully describe the present invention to those skilled in the art.
[실시예 1 내지 5][Examples 1 to 5]
비가교 폴리올레핀으로 열가소성 폴리올레핀(호모 폴리프로필렌) (Basell사 CA-7441A) (용융지수: 0.88g/10min), 스티렌 공중합체로 SEBS (폴리스티렌-에틸렌-부틸렌, polyStyrene-Ethylene-Butylene) (스티렌 반복단위: 에틸렌 반복단위: 부틸렌 반복단위 (중량비) = 30:35:35 (Asahi사, H1041), 무수말레산 개질 폴리올레핀으로 무수말레산이 1.5 중량부 그래프트된 무수말레산-그래프트-폴리프로필렌을 하기 표 1과 같은 중량부를 포함하도록 베이스 수지 100 중량부를 제조하였으며, 난연제로 1 중량부의 실란이 코팅된 수산화마그네슘, 난연 보조제로 적색인, 산화방지제로 페놀계 산화방지제와 인계 산화방지제의 혼합물, 가공조제로 실리콘계 화합물을 하기 표 1과 같은 중량부로 첨가하여 제조된 복합수지 조성물을 제조하여, 도체 외측을 감싸는 2mm 두께의 전선 피복층을 형성하였으며, 이때, 상기 도체는 0.05mm 직경이면서, 마그네슘-아연(Mg-Zn) 합금 재질을 사용하였다. (Homopolypropylene) (Basell, CA-7441A) (melt index: 0.88 g / 10 min) as the noncrosslinked polyolefin, SEBS (polystyrene-ethylene-butylene) Unit: ethylene repeating unit: butylene repeating unit (weight ratio) = 30:35:35 (Asahi, H1041), 1.5 parts by weight of maleic anhydride-modified maleic anhydride modified polyolefin, grafted maleic anhydride-grafted-polypropylene 100 parts by weight of a base resin was prepared so as to include the same parts by weight as shown in Table 1, and magnesium hydroxide coated with 1 part by weight of silane as a flame retardant, a mixture of phenol antioxidant and phosphorus antioxidant as red antioxidant as a flame- To prepare a composite resin composition prepared by adding the silicone-based compound as shown in Table 1 below to form a 2-mm-thick wire covering layer surrounding the outside of the conductor And that, this time, the conductor diameter of 0.05mm, yet, magnesium was used zinc (Mg-Zn) alloy.
[비교예 1 내지 7][Comparative Examples 1 to 7]
비가교 폴리올레핀으로 열가소성 폴리올레핀(호모 폴리프로필렌) (Bassel사 CA-7441A) (용융지수: 0.88g/10min), 스티렌 공중합체로 SEBS (폴리스티렌-에틸렌-부틸렌, polyStyrene-Ethylene-Butylene) (스티렌: 에틸렌: 부틸렌 (중량비) = 30:35:35) (Asahi사, H1041), 무수말레산 개질 폴리올레핀으로 무수말레산이 1.5 중량부 그래프트된 무수말레산-그래프트-폴리프로필렌을 하기 표 2와 같은 중량부를 포함하도록 베이스 수지 100 중량부를 제조하였으며, 난연제로 1 중량부의 실란이 코팅된 수산화마그네슘, 난연 보조제로 적색인, 산화방지제로 페놀계 산화방지제와 인계 산화방지제의 혼합물, 가공조제로 실리콘계 화합물을 하기 표 2와 같은 중량부로 첨가하여 제조된 복합수지 조성물을 제조하여, 도체 외측을 감싸는 2mm 두께의 전선 피복층을 형성하였으며, 이때, 상기 도체는 0.05mm 직경이면서, 마그네슘-아연(Mg-Zn) 합금 재질을 사용하였다.(Homopolypropylene) (Bassel's CA-7441A) (melt index: 0.88 g / 10 min) as a non-crosslinkable polyolefin, SEBS (polystyrene-ethylene-butylene) Maleic anhydride-modified polyolefin, 1.5 parts by weight of maleic anhydride-modified polyolefin, and the grafted maleic anhydride-graft-polypropylene as the following Table 2 (weight ratio) 100 parts by weight of a base resin was prepared so as to include a part of the base resin, 1 part by weight of silane-coated magnesium hydroxide as a flame retardant, a mixture of phenol antioxidant and phosphorus antioxidant as an antioxidant which is red as a flame retardant auxiliary agent, The composite resin composition prepared by adding the same weight parts as shown in Table 2 was prepared to form a 2-mm-thick wire covering layer surrounding the outside of the conductor, A magnesium-zinc (Mg-Zn) alloy material with a diameter of .05 mm was used.
폴리올레핀Thermoplastic
Polyolefin
성능평가Performance evaluation
1. 인장강도 및 신장율1. Tensile strength and elongation
IEC 60811-1-1에 따라 인장강도 및 신장율을 측정하여 인장강도는 1.5kgf/mm2, 신장율은 300%를 초과하여야 한다.Tensile strength and elongation shall be measured in accordance with IEC 60811-1-1. The tensile strength shall be 1.5 kgf / mm2 and the elongation shall be more than 300%.
2. 한계산소지수2. Limit oxygen index
ASTM D 3683에 따라 시험하여 그 값은 25이상이여야 한다. Tested in accordance with ASTM D 3683, the value shall not be less than 25.
3. 난연성 3. Flammability
UL 1581에 따라 시험하여 V0등급 이상을 만족하여야 한다. It shall be tested according to UL 1581 and satisfy V0 grade or higher.
4. 내열성4. Heat resistance
UL 105 ㅀC등급(136℃ X 168hr)의 노화 시험 조건하에 노화시험을 진행하여 IEC 60811-1-1에 따라 인장강도 및 신장율을 측정하여 인장잔율 및 신장잔율이 각각 75~125% 이내에 있어야 한다.Under aging test conditions of UL 105 Class C (136 ° C x 168hr), the tensile strength and elongation shall be measured according to IEC 60811-1-1, and the tensile residual rate and elongation percentage shall be within 75 to 125%, respectively .
상기 성능 평가 방식을 기준으로 측정한 값을 하기 표 3 및 표 4에 도시하였다. Values measured based on the performance evaluation method are shown in Tables 3 and 4 below.
상기 표 3과 같이 본 발명의 일 실시예에 따른 베이스 수지 함량을 포함하는 전선은 측정된 성능 평가 항목 모두 소정의 범위를 만족하는 것을 확인할 수 있다. As shown in Table 3, it can be seen that the wires including the base resin content according to one embodiment of the present invention all satisfy the predetermined range of the measured performance evaluation items.
또한, 표 4를 참조하면, 비교예 1 내지 7과 같이 본 발명에 따른 베이스 수지 조성물의 중량비율을 벗어나는 경우 인장 강도, 내열성 등의 물성이 하락하는 것을 확인할 수 있다.Also, referring to Table 4, it can be seen that the physical properties such as tensile strength, heat resistance and the like are deteriorated when the weight ratio of the base resin composition according to the present invention is deviated as in Comparative Examples 1 to 7.
이하, 본 발명의 비록 한정된 실시예에 의해 설명되었으나, 본 발명은 이것에 의해 한정되지 않으며, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자에 의해 본 발명의 기술 사상과 아래에 기재될 특허청구범위의 균등 범위 내에서 다양한 수정 및 변형이 가능함은 물론이다. Although the present invention has been described with reference to certain exemplary embodiments, it is to be understood that the present invention is not limited thereto and that various changes and modifications will be apparent to those skilled in the art. It is to be understood that various changes and modifications may be made without departing from the scope of the appended claims.
Claims (9)
상기 베이스 수지가 비가교 폴리올레핀, 스티렌 공중합체 및 무수말레산 개질 폴리올레핀을 포함하고,
상기 무기 난연제가 수산화알루미늄, 수산화마그네슘, 하이드로마그네사이트 및 하이드로탈사이트로 이루어진 군에서 선택되는 어느 하나 또는 둘 이상의 비할로겐계 금속산화물이며,
상기 베이스 수지 100 중량부에 대하여, 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 함량이 각각 독립적으로 10 중량부 내지 90 중량부이고, 상기 비가교 폴리올레핀 및 무수말레산 개질 폴리올레핀의 총합이 70 내지 95 중량부이고,
상기 베이스 수지 100 중량부에 대하여, 상기 무기 난연제의 함량이 50 중량부 내지 150 중량부인 것을 특징으로 하는 전선용 시스 조성물. A sheath composition for a wire comprising a base resin and an inorganic flame retardant,
Wherein the base resin comprises an uncrosslinked polyolefin, a styrene copolymer and a maleic anhydride modified polyolefin,
Wherein the inorganic flame retardant is any one or two or more halogen-free metal oxides selected from the group consisting of aluminum hydroxide, magnesium hydroxide, hydro-magne- site, and hydrotalcite,
Wherein the content of the non-crosslinkable polyolefin and the maleic anhydride-modified polyolefin are independently 10 parts by weight to 90 parts by weight, and the total amount of the non-crosslinkable polyolefin and the maleic anhydride-modified polyolefin is 70 to 95 parts by weight, Parts by weight,
Wherein the inorganic flame retardant is contained in an amount of 50 to 150 parts by weight based on 100 parts by weight of the base resin.
상기 베이스 수지 100 중량부에 대하여, 상기 비가교 폴리올레핀의 함량이 20 중량부 내지 70 중량부인 것을 특징으로 하는 전선용 시스 조성물. The method according to claim 1,
Wherein the amount of the non-crosslinkable polyolefin is 20 to 70 parts by weight based on 100 parts by weight of the base resin.
상기 전선용 시스 조성물이 난연보조제, 안정제, 산화방지제 및 가공조제 중 적어도 어느 하나를 더 포함하는 것을 특징으로 하는 전선용 시스 조성물. The method according to claim 1,
Wherein the wire sheath composition further comprises at least one of a flame retardant aid, a stabilizer, an antioxidant and a processing aid.
상기 무수말레산 개질 폴리올레핀이 폴리올레핀 100 중량부에 대하여, 무수말레산 0.5 내지 5 중량부를 포함하는 것을 특징으로 하는 전선용 시스 조성물. The method according to claim 1,
Wherein the maleic anhydride-modified polyolefin comprises 0.5 to 5 parts by weight of maleic anhydride relative to 100 parts by weight of the polyolefin.
상기 베이스 수지 100 중량부에 대하여, 상기 난연보조제의 함량이 1 내지 10 중량부인 것을 특징으로 하는 전선용 시스 조성물. 5. The method of claim 4,
Wherein the content of the flame-retardant auxiliary is 1 to 10 parts by weight based on 100 parts by weight of the base resin.
상기 베이스 수지 100 중량부에 대하여, 상기 안정제, 산화방지제 및 가공조제의 함량이 각각 독립적으로 0.1 내지 10 중량부인 것을 특징으로 하는 전선용 시스 조성물. 5. The method of claim 4,
Wherein the content of the stabilizer, the antioxidant, and the processing aid is independently 0.1 to 10 parts by weight based on 100 parts by weight of the base resin.