KR101658184B1 - Polymer film, film for protecting photovoltaic panel and photovoltaic apparatus comprising same - Google Patents
Polymer film, film for protecting photovoltaic panel and photovoltaic apparatus comprising same Download PDFInfo
- Publication number
- KR101658184B1 KR101658184B1 KR1020150057376A KR20150057376A KR101658184B1 KR 101658184 B1 KR101658184 B1 KR 101658184B1 KR 1020150057376 A KR1020150057376 A KR 1020150057376A KR 20150057376 A KR20150057376 A KR 20150057376A KR 101658184 B1 KR101658184 B1 KR 101658184B1
- Authority
- KR
- South Korea
- Prior art keywords
- layer
- resin
- bonding force
- polyester resin
- weight
- Prior art date
Abstract
Description
실시예는 폴리머 필름, 태양 전지 패널 보호 필름 및 이를 포함하는 태양광 발전 장치에 관한 것이다.
Embodiments relate to a polymer film, a solar cell panel protective film, and a photovoltaic device including the same.
PVDF(폴리비닐리덴 플루오라이드)는 우수한 내후성, 내방사선성, 내약품성 및 내스크래치성을 가질 뿐만 아니라 광택 있는 외관을 제공할 수 있어, 제품 또는 재료를 보호하는 피복재료로 널리 사용되며, 특히 폴리에스테르 층과 적층된 형태로 태양 전지 패널 보호 필름(이면 보호 필름)으로서 유용하게 사용된다.PVDF (polyvinylidene fluoride) is widely used as a coating material for protecting a product or a material because it can provide a glossy appearance as well as excellent weather resistance, radiation resistance, chemical resistance and scratch resistance, And it is usefully used as a solar cell panel protective film (back protection film) in a laminated form with an ester layer.
따라서, PVDF 필름으로 다양한 종류의 물체를 코팅하는 경우가 많아, 상기 PVDF 필름에는 상술한 물성 이외에도 다양한 물성들이 추가로 필요로 된다. 즉, 코팅 대상 물체(기판)에 대한 우수한 접착성 및 온화하지 않은 기후상태 또는 고온 공정에의 노출에 견딜 수 있는 우수한 내열성이 필요로 되며, 필름이 물체 위에 놓여졌을 때, 더 나아가 그 물체가 예를 들어 연신(drawing)될 경우 발생하는 기계적 압력을 견딜 수 있는 높은 강도와 유연성이 필요로 된다.Therefore, in many cases, various kinds of objects are coated with PVDF film, and thus various physical properties besides the above-mentioned properties are additionally required to the PVDF film. That is, there is a need for excellent adhesion to an object (substrate) to be coated and an excellent heat resistance that can withstand a mild climate or exposure to a high temperature process, and when the film is placed on an object, A high strength and flexibility that can withstand the mechanical pressure that occurs when drawing is required.
이에, 한국 공개특허공보 제 10-2011-0118736 호는 양호한 유연성과 고강도를 나타내는 PVDF 기재 필름을 개시하며, PET 또는 PEN 시트와 상기 PVDF 기재 필름이 조합된 다층 구조의 필름을 개시한다.Korean Patent Laid-Open Publication No. 10-2011-0118736 discloses a PVDF base film which exhibits good flexibility and high strength, and discloses a multilayered film in which a PET or PEN sheet and the PVDF base film are combined.
그러나 상기 한국 공개특허공보 제 10-2011-0118736 호에 개시된 PVDF 기재 필름을 비롯한 기존의 불소계 고분자 필름을 구성하는 불소계 고분자 수지는 PET 수지 등과 공압출될 경우 서로 혼합되지 않아(immiscible) 박리(delamination)를 일으키는 문제가 있었다.However, when the fluoropolymer resin constituting the conventional fluoropolymer film including the PVDF base film disclosed in Korean Patent Laid-Open No. 10-2011-0118736 is co-extruded with a PET resin or the like, the film is immiscible and is not delaminated, . ≪ / RTI >
이에, 공압출하는 대신 라미네이션(lamination) 또는 오프라인(off-line) 코팅을 수행하여 불소계 고분자 층/폴리에스테르 층의 적층체를 제조하는 경우가 많았으나, 이 경우 제조비용이 높아지는 단점이 있었다.
Thus, in many cases, a laminated body of fluoropolymer layer / polyester layer is produced by performing lamination or off-line coating instead of pneumatic shipment, but in this case, manufacturing cost is increased.
실시예는 향상된 박리 강도를 가지며 용이하게 제조될 수 있는 폴리머 필름, 태양 전지 패널 보호 필름 및 이를 포함하는 태양광 발전 장치를 제공하고자 한다.
Embodiments provide a polymer film, a solar cell panel protective film, and a photovoltaic power generation device including the polymer film, which have improved peel strength and can be easily manufactured.
일 실시예에 따르면,According to one embodiment,
폴리에스테르 수지를 포함하는 제1 층; 및 A first layer comprising a polyester resin; And
상기 제1 층의 일면 또는 양면에 형성된 제2 층을 포함하되, 상기 제1 층과 제2 층이 공압출된 구조를 가지며,And a second layer formed on one or both sides of the first layer, wherein the first layer and the second layer are co-extruded,
상기 제2 층이 50 중량% 초과 내지 90 중량% 이하의 불소계 수지 및 5 내지 25 중량%의 접합력 향상 수지를 포함하고, 상기 접합력 향상 수지 및 상기 폴리에스테르 수지 사이의 접합력이 상기 불소계 수지 및 상기 폴리에스테르 수지 사이의 접합력보다 더 큰, 폴리머 필름을 제공한다.Wherein the second layer comprises a fluorine resin in an amount of more than 50% by weight to 90% by weight and a bonding force improving resin in an amount of 5 to 25% by weight, and the bonding force between the bonding force improving resin and the polyester resin is higher than the bonding strength between the fluorine resin and the poly Is greater than the bond strength between the polyester resin and the ester resin.
일 실시예에 따르면, According to one embodiment,
폴리에스테르 수지를 포함하는 제1 층; 및 A first layer comprising a polyester resin; And
상기 제1 층의 일면 또는 양면에 형성된 제2 층을 포함하되, 상기 제1 층과 제2 층이 공압출된 구조를 가지며,And a second layer formed on one or both sides of the first layer, wherein the first layer and the second layer are co-extruded,
상기 제2 층이 50 중량% 초과 내지 90 중량% 이하의 불소계 수지 및 5 내지 25 중량%의 접합력 향상 수지를 포함하고, 상기 접합력 향상 수지 및 상기 폴리에스테르 수지 사이의 접합력이 상기 불소계 수지 및 상기 폴리에스테르 수지 사이의 접합력보다 더 큰, 태양 전지 패널 보호 필름을 제공한다.Wherein the second layer comprises a fluorine resin in an amount of more than 50% by weight to 90% by weight and a bonding force improving resin in an amount of 5 to 25% by weight, and the bonding force between the bonding force improving resin and the polyester resin is higher than the bonding strength between the fluorine resin and the poly Wherein the adhesive force between the ester resin and the ester resin is larger than the bonding force between the ester resin and the ester resin.
일 실시예에 따르면, According to one embodiment,
태양 전지 패널; 및 상기 태양 전지 패널의 적어도 일면에 배치되는 상기 보호 필름을 포함하는 태양광 발전 장치를 제공한다.
Solar panel; And a protective film disposed on at least one side of the solar cell panel.
실시예에 따른 폴리머 필름은 불소계 수지(제2 층)와 폴리에스테르 수지(제1 층)와의 공압출에 의해 형성되는데, 상기 불소계 수지를 접합력 향상 수지와 함께 사용함으로써, 공압출시 상기 제1 층과 상기 제2 층 사이의 접합력이 향상된다.The polymer film according to the embodiment is formed by co-extrusion of a fluorine resin (second layer) and a polyester resin (first layer). By using the fluorine resin together with the bonding force improving resin, The bonding strength between the second layers is improved.
이에 따라서, 상기 제1 층과 상기 제2 층은 공압출될 경우에도 서로 박리되지 않고 강하게 접합되어 하나의 적층 필름을 형성할 수 있다.Accordingly, even when the first layer and the second layer are co-extruded, they can be strongly bonded without being separated from each other to form a laminated film.
따라서, 불소계 수지 필름 및 폴리에스테르계 수지 필름을 따로 형성하여 라미네이션하지 않아도, 실시예는 서로 간에 향상된 박리 강도를 갖는 불소계 수지층 및 폴리에스테르 수지층을 원하는 두께로 한번의 공압출에 의해 용이하게 형성할 수 있다.
Therefore, even if the fluororesin film and the polyester resin film are separately formed and laminated, the embodiment can easily form the fluororesin layer and the polyester resin layer having desired peel strengths to each other to a desired thickness by one coextrusion can do.
도 1은 일 실시예에 따른 태양 전지 패널 보호 필름의 일 단면을 도시한 도면이다.
도 2는 일 실시예에 따른 태양광 발전 장치의 일 단면을 도시한 도면이다.1 is a cross-sectional view of a solar cell panel protective film according to an embodiment.
2 is a cross-sectional view of a photovoltaic device according to an embodiment.
실시예의 설명에 있어서, 각 필름, 막, 패널, 또는 층 등이 각 필름, 막, 패널, 또는 층 등의 "상(on)" 또는 "하(under)"에 형성되는 것으로 기재되는 경우에 있어, "상(on)"과 "하(under)"는 "직접(directly)" 또는 "다른 구성요소를 개재하여(indirectly)" 형성되는 것을 모두 포함한다. 또한 각 구성요소의 상/하에 대한 기준은 도면을 기준으로 설명한다. 도면에서의 각 구성요소들의 크기는 설명을 위하여 과장될 수 있으며, 실제로 적용되는 크기를 의미하는 것은 아니다.In the description of the embodiments, in the case where each film, film, panel or layer is described as being formed "on" or "under" of each film, film, panel, , "On" and "under" all include being formed "directly" or "indirectly" through "another element". In addition, the upper and lower standards for each component are described with reference to the drawings. The size of each component in the drawings may be exaggerated for the sake of explanation and does not mean the size actually applied.
도 1은 일 실시예에 따른 태양 전지 패널 보호 필름의 일 단면을 도시한 도면이다.1 is a cross-sectional view of a solar cell panel protective film according to an embodiment.
도 1을 참조하면, 일 실시예에 따른 태양 전지 패널 보호 필름은 제1 층(100), 제2 층(200) 및 제3 층(300)을 포함한다.Referring to FIG. 1, a solar cell panel protective film according to one embodiment includes a
상기 제1 층은 폴리에스테르 수지를 포함한다. 더 자세하게, 상기 제1 층은 적어도 하나의 폴리에스테르 수지를 포함한다. 상기 폴리에스테르 수지는 단일 중합 폴리에스테르 또는 공중합 폴리에스테르 일 수 있다.The first layer comprises a polyester resin. More specifically, the first layer comprises at least one polyester resin. The polyester resin may be a single polymerized polyester or a copolymerized polyester.
상기 제1 층은 상기 폴리에스테르 수지를 약 80 중량% 이상의 함량으로 포함할 수 있다. 더 자세하게, 상기 제1 층은 상기 폴리에스테르 수지를 약 90 중량% 이상의 함량으로 포함할 수 있다. 더 자세하게, 상기 제1 층은 상기 폴리에스테르 수지를 약 95 중량% 이상의 함량으로 포함할 수 있다. 더 자세하게, 상기 제1 층은 상기 폴리에스테르 수지를 약 99 중량% 이상의 함량으로 포함할 수 있다.The first layer may contain the polyester resin in an amount of about 80% by weight or more. More specifically, the first layer may comprise the polyester resin in an amount of about 90% by weight or more. More specifically, the first layer may comprise the polyester resin in an amount of about 95% by weight or more. More specifically, the first layer may comprise the polyester resin in an amount of about 99% by weight or more.
상기 폴리에스테르 수지는 디올 성분 및 디카르복실산 성분을 포함한다. 더 자세하게, 상기 폴리에스테르 수지는 전체적으로 상기 디올 성분 및 상기 디카르복실산 성분으로 이루어질 수 있다. 더 자세하게, 상기 폴리에스테르 수지는 상기 디올 성분 및 상기 디카르복실산 성분을 약 95 몰% 이상 포함할 수 있다.The polyester resin includes a diol component and a dicarboxylic acid component. More specifically, the polyester resin may consist entirely of the diol component and the dicarboxylic acid component. More specifically, the polyester resin may contain about 95 mol% or more of the diol component and the dicarboxylic acid component.
상기 폴리에스테르 수지는 상기 디올 성분 및 상기 디카르복실산 성분을 에스테르 교환 반응한 후 중합하여 형성될 수 있다.The polyester resin may be formed by transesterifying the diol component and the dicarboxylic acid component followed by polymerization.
상기 디올 성분의 구체적인 예로는 에틸렌글리콜, 1,4-시클로헥산디메탄올(1,4-cyclohexanedimethanol), 1,3-프로판디올, 1,2-옥탄디올, 1,3-옥탄디올, 2,3-부탄디올, 1,3-부탄디올, 1,4-부탄디올, 1,5-펜탄디올, 2,2-디메틸-1,3-프로판디올(네오펜틸 글리콜), 2-부틸-2-에틸-1,3-프로판디올, 2,2-디에틸-1,5-펜탄디올, 2,4-디에틸-1,5-펜탄디올, 3-메틸-1,5-펜탄디올, 1,1-디메틸-1,5-펜탄디올, 스피로글리콜(spiroglycol, 3,9-비스(1,1-디메틸-2-히드록시에틸)-2,4,8,10-테트라옥사스피로[5.5]운데칸), 디에틸렌글리콜(2-(2-히드록시에톡시)에탄-1-올) 및 이들의 혼합물을 들 수 있다. 상기 디올 성분은 약 20 몰% 내지 약 97 몰%의 에틸렌글리콜을 포함하고, 네오펜틸글리콜, 1,4-시클로헥산디메탄올, 디에틸렌글리콜 및 스피로글리콜 중 적어도 하나를 약 3 몰% 내지 약 80 몰%의 함량으로 포함할 수 있다. Specific examples of the diol component include ethylene glycol, 1,4-cyclohexanedimethanol, 1,3-propanediol, 1,2-octanediol, 1,3-octanediol, 2,3 Butanediol, 1,3-butanediol, 1,4-butanediol, 1,5-pentanediol, 2,2-dimethyl-1,3-propanediol (neopentyl glycol) 1,3-propanediol, 2,2-diethyl-1,5-pentanediol, 2,4-diethyl-1,5-pentanediol, 3- 1,5-pentanediol, spiroglycol, 3,9-bis (1,1-dimethyl-2-hydroxyethyl) -2,4,8,10-tetraoxaspiro [5.5] undecane, Ethylene glycol (2- (2-hydroxyethoxy) ethan-1-ol) and mixtures thereof. Wherein the diol component comprises from about 20 mole% to about 97 mole% ethylene glycol and at least one of neopentyl glycol, 1,4-cyclohexanedimethanol, diethylene glycol, and spiroglycol from about 3 mol% to about 80 Mol%.
또한, 상기 디카르복실산 성분의 구체적인 예로는 테레프탈산, 디메틸테레프탈산, 이소프탈산, 나프탈렌디카복실산, 오르토프탈산 등의 방향족 디카르복실산; 아디프산, 아젤라산, 세바스산, 데칸디카르복실산 등의 지방족 디카르복실산; 지환식 디카르복실산; 이들의 에스테르화물; 및 이들의 혼합물을 들 수 있다. 더 자세하게, 상기 디카르복실산 성분은 약 80 몰% 이상의 방향족 디카르복실산을 포함할 수 있다. 더 자세하게, 상기 디카르복실산 성분은 약 20 몰% 내지 약 97 몰%의 테레프탈산 및 약 3 몰% 내지 약 80 몰%의 이소프탈산을 포함할 수 있다.Specific examples of the dicarboxylic acid component include aromatic dicarboxylic acids such as terephthalic acid, dimethylterephthalic acid, isophthalic acid, naphthalene dicarboxylic acid and orthophthalic acid; Aliphatic dicarboxylic acids such as adipic acid, azelaic acid, sebacic acid and decanedicarboxylic acid; Alicyclic dicarboxylic acid; Esters thereof; And mixtures thereof. More specifically, the dicarboxylic acid component may comprise at least about 80 mole% aromatic dicarboxylic acid. More specifically, the dicarboxylic acid component may comprise from about 20 mol% to about 97 mol% terephthalic acid and from about 3 mol% to about 80 mol% isophthalic acid.
상기 제2 층은 상기 제1 층에 직접 접한다. 더 자세하게, 상기 제2 층은 상기 제1 층의 상면 및/또는 하면에 직접 접할 수 있다. 더 자세하게, 상기 제2 층은 상기 제1 층의 상면 및/또는 하면에 전체적으로 직접 접촉될 수 있다.The second layer directly contacts the first layer. More specifically, the second layer may directly contact the upper surface and / or the lower surface of the first layer. More specifically, the second layer may be entirely in direct contact with the upper surface and / or the lower surface of the first layer.
상기 제2 층은 불소계 수지 및 접합력 향상 수지를 포함한다. 상기 불소계 수지 및 상기 접합력 향상 수지는 서로 혼합된다. 즉, 상기 제2 층은 상기 불소계 수지 및 상기 접합력 향상 수지의 혼합물을 포함한다.The second layer includes a fluorine resin and a bonding force improving resin. The fluorine resin and the bonding force improving resin are mixed with each other. That is, the second layer includes a mixture of the fluorine resin and the bonding force improving resin.
상기 불소계 수지는 불소를 포함하는 폴리머일 수 있다. The fluororesin may be a fluorine-containing polymer.
상기 불소계 수지의 구체적인 예로는 에틸렌-테트라플루오로에틸렌 공중합체(ETFE), 폴리비닐리덴플루오라이드(PVDF), 테트라플루오로에틸렌-헥사플루오로프로필렌 공중합체(FEP), 테트라플루오로에틸렌-헥사플루오로프로필렌-비닐리덴플루오라이드 공중합체(THV), 이들의 공중합체, 및 이들의 혼합물을 들 수 있다. 그 중에서도, 에틸렌-테트라플루오로에틸렌 공중합체(ETFE), 폴리비닐리덴플루오라이드(PVDF) 및 테트라플루오로에틸렌-헥사플루오로프로필렌 공중합체(FEP)로 이루어진 군으로부터 선택될 수 있다.Specific examples of the fluororesin include ethylene-tetrafluoroethylene copolymer (ETFE), polyvinylidene fluoride (PVDF), tetrafluoroethylene-hexafluoropropylene copolymer (FEP), tetrafluoroethylene-hexafluoro Propylene-vinylidene fluoride copolymer (THV), copolymers thereof, and mixtures thereof. Among them, it may be selected from the group consisting of ethylene-tetrafluoroethylene copolymer (ETFE), polyvinylidene fluoride (PVDF) and tetrafluoroethylene-hexafluoropropylene copolymer (FEP).
더 자세하게, 상기 불소계 수지는 단일 중합 폴리비닐리덴플루오라이드 또는 공중합 폴리비닐리덴플루오라이드일 수 있다.More specifically, the fluororesin may be a single-polymerized polyvinylidene fluoride or a copolymerized polyvinylidene fluoride.
PVDF가 공중합 수지일 경우, 비닐리덴플루오라이드(VF2) 및 공단량체가 50:50 내지 99:1의 중량비로 공중합된 수지인 것이 바람직하다.When PVDF is a copolymer resin, it is preferable that vinylidene fluoride (VF2) and a comonomer are resins copolymerized in a weight ratio of 50:50 to 99: 1.
공중합될 수 있는 공단량체로는 불소화된 단량체가 바람직한데, 예를 들어, 불화비닐; 트리플루오로에틸렌(VF3); 클로로트리플루오로에틸렌(CTFE); 1,2-디플루오로에틸렌; 테트라플루오로에틸렌(TFE); 헥사플루오로프로필렌(HFP); 퍼플루오로(메틸비닐)에테르(PMVE), 퍼플루오로(에틸비닐)에테르(PEVE) 및 퍼플루오로(프로필비닐)에테르(PPVE) 등의 퍼플루오로(알킬비닐)에테르; 퍼플루오로(1,3-디옥솔); 및 퍼플루오로(2,2-디메틸-1,3-디옥솔)(PDD)로 이루어진 군으로부터 선택되는 하나 이상일 수 있다. 이 중에서도, 클로로트리플루오로에틸렌(CTFE), 헥사플루오로프로필렌(HFP), 트리플루오로에틸렌(VF3) 또는 테트라플루오로에틸렌(TFE)인 것이 바람직하다.The comonomer which can be copolymerized is preferably a fluorinated monomer such as vinyl fluoride; Trifluoroethylene (VF3); Chlorotrifluoroethylene (CTFE); 1,2-difluoroethylene; Tetrafluoroethylene (TFE); Hexafluoropropylene (HFP); Perfluoro (alkyl vinyl) ethers such as perfluoro (methyl vinyl) ether (PMVE), perfluoro (ethyl vinyl) ether (PEVE) and perfluoro (propyl vinyl) ether (PPVE); Perfluoro (1,3-dioxol); And perfluoro (2,2-dimethyl-1,3-dioxole) (PDD). Among these, chlorotrifluoroethylene (CTFE), hexafluoropropylene (HFP), trifluoroethylene (VF3), or tetrafluoroethylene (TFE) are preferable.
PVDF는, 압출 및 사출 성형에 적합하기 위해서, 전단속도 100s-1 및 230℃의 조건으로 모세관 유량계에 의해 측정한 점도가 100 내지 2,500 Pa·s인 것이 바람직하며, 500 내지 2,000 Pa·s인 것이 더욱 바람직하다. In order to be suitable for extrusion and injection molding, the PVDF preferably has a viscosity of 100 to 2,500 Pa · s as measured by a capillary flow meter at a shear rate of 100 s -1 and 230 ° C., preferably 500 to 2,000 Pa · s More preferable.
PVDF의 함량은, 상기 제2 층의 중량을 기준으로 50 중량% 초과이면서 90 중량%, 특히 60 내지 80 중량%인 것이 바람직하다. PVdF의 함량이 50 중량% 이하인 경우에는 충분한 내후성 발현에 한계가 있을 수 있고, 90 중량%를 초과하는 경우에는 필요 이상의 물성이 발현되거나 제조원가가 상승할 수 있다. The content of PVDF is preferably more than 50% by weight and 90% by weight, particularly preferably 60 to 80% by weight, based on the weight of the second layer. When the content of PVdF is 50% by weight or less, sufficient weatherability may be limited. When the content of PVdF is more than 90% by weight, physical properties more than necessary may be produced or the production cost may increase.
상기 접합력 향상 수지는 상기 제1 층과 향상된 접합력을 갖는다. 더 자세하게, 상기 접합력 향상 수지는 상기 폴리에스테르 수지와 향상된 접합력을 갖는다. 더 자세하게, 상기 접합력 향상 수지와 상기 제1 층에 포함된 폴리에스테르 수지 사이의 접합력은 상기 불소계 수지와 상기 폴리에스테르 수지 사이의 접합력보다 더 크다. 더 자세하게, 상기 폴리에스테르 수지에 대하여, 상기 접합력 향상 수지의 접합력은 상기 불소계 수지의 접합력보다 약 1.3배 이상 더 클 수 있다. 더 자세하게, 상기 폴리에스테르 수지에 대하여, 상기 접합력 향상 수지의 접합력은 상기 불소계 수지의 접합력보다 약 1.5배 이상 더 클 수 있다. 더 자세하게, 상기 폴리에스테르 수지에 대하여, 상기 접합력 향상 수지의 접합력은 상기 불소계 수지의 접합력보다 약 3배 이상 더 클 수 있다.The bonding force improving resin has an improved bonding force with the first layer. More specifically, the bonding force improving resin has an improved bonding force with the polyester resin. More specifically, the bonding force between the bonding force improving resin and the polyester resin contained in the first layer is greater than the bonding force between the fluororesin and the polyester resin. More specifically, the bonding force of the bonding force improving resin with respect to the polyester resin may be about 1.3 times or more greater than the bonding force of the fluororesin. More specifically, with respect to the polyester resin, the bonding force of the bonding force improving resin may be about 1.5 times or more greater than the bonding force of the fluorine resin. More specifically, the bonding force of the bonding force improving resin with respect to the polyester resin may be about three times or more larger than the bonding force of the fluorine resin.
상기 접합력 향상 수지는 아크릴계 수지일 수 있다. 더 자세하게, 상기 접합력 향상 수지는 치환되거나 비치환된 폴리메틸메타크릴레이트(PMMA) 수지일 수 있다. 더 자세하게, 상기 접합력 향상 수지는 메틸메타크릴레이트 단량체의 단일 수지이거나 다른 공단량체와의 공중합 수지일 수 있다. The bonding force improving resin may be an acrylic resin. More specifically, the bonding force improving resin may be a substituted or unsubstituted polymethyl methacrylate (PMMA) resin. More specifically, the bonding force improving resin may be a single resin of a methyl methacrylate monomer or a copolymer resin with other comonomers.
PMMA가 공중합 수지일 경우, 메틸메타크릴레이트(MMA) 및 공단량체가 50:50 내지 99:1의 중량비로 공중합된 수지인 것이 바람직하다.When PMMA is a copolymer resin, it is preferable that methyl methacrylate (MMA) and a comonomer are resins copolymerized in a weight ratio of 50:50 to 99: 1.
공중합될 수 있는 공단량체의 예로는, 알킬 (메트)아크릴레이트, 아크릴로니트릴, 부타디엔, 스티렌, 이소프렌 및 이들의 혼합물을 들 수 있다. 상기 알킬 (메트)아크릴레이트는 문헌[Kirk-Othmer Encyclopedia of Chemical Technology, 4th Edition, Vol. 1, p. 292~293 & Vol. 16, p. 475~478]에 기재되어 있다. Examples of comonomers which can be copolymerized include alkyl (meth) acrylates, acrylonitrile, butadiene, styrene, isoprene, and mixtures thereof. The alkyl (meth) acrylate is described in Kirk-Othmer Encyclopedia of Chemical Technology, 4th Edition, Vol. 1, p. 292-293 & 16, p. 475-478.
바람직하게는, 상기 공중합 수지는 메틸 아크릴레이트 및/또는 에틸 아크릴레이트 공단량체가 1 내지 20 중량%, 특히 5 내지 15 중량%의 함량으로 공중합된 것일 수 있다. Preferably, the copolymer resin may be copolymerized with methyl acrylate and / or ethyl acrylate comonomer in an amount of 1 to 20% by weight, particularly 5 to 15% by weight.
PMMA는 관능화될 수 있는데, 예를 들어 산, 산 염화물, 알코올 또는 무수물 관능기를 함유할 수 있고, 이들 관능기는 그라프트(graft) 또는 공중합의 방식으로 도입될 수 있다. 이 중에서도, 아크릴산 공중합 수지에 의해 제공되는 산 관능기인 것이 바람직하다. 관능기의 함량비율은, 관능기를 함유하는 PMMA의 중량을 기준으로 0 내지 15 중량%일 수 있다. PMMA can be functionalized, for example, containing an acid, acid chloride, alcohol or anhydride functionality, and these functional groups can be introduced by graft or copolymerization. Among these, an acid functional group provided by an acrylic acid copolymer resin is preferable. The content of the functional group may be 0 to 15% by weight based on the weight of the PMMA containing the functional group.
2개의 인접한 아크릴산 관능기는 물을 상실하여 하기 화학식 1 또는 2와 같은 무수물을 형성하기도 한다. 이들 무수물은, PMMA의 취약한 충격강도를 강화시키거나, PVDF와의 블렌딩 이후 PVDF의 결정거동을 완화시킴으로써, 보다 부드러운 연질구조를 발현시키는 작용을 할 수 있다:
Two adjacent acrylic acid functional groups lose water and form anhydrides such as the following formula (1) or (2). These anhydrides can act to enhance the soft impact structure of the PMMA, or to soften the soft structure by alleviating the crystalline behavior of the PVDF after blending with PVDF:
즉, 실시예에 사용되는 PMMA는 내충격특성을 갖는 개질된 폴리메틸메타크릴레이트일 수 있다.That is, the PMMA used in the embodiment may be a modified polymethyl methacrylate having an impact resistance property.
PMMA의 MVI(용융체적지수)는 3.8kg의 하중하에서 230℃의 온도로 측정하였을 때, 4 내지 6 ㎤/10분일 수 있다. The MVI (melt volume index) of PMMA can be 4 to 6 cm < 3 > / 10 min when measured at 230 DEG C under a load of 3.8 kg.
PMMA의 함량은, 상기 제2 층을 기준으로 5 내지 25 중량%, 특히 10 내지 20 중량%인 것이 바람직하다. The content of PMMA is preferably 5 to 25% by weight, particularly 10 to 20% by weight based on the second layer.
상기 제1 층 및 제2 층 중 적어도 한 층은 안료 또는 염료를 한 층 총 중량을 기준으로 1 내지 40 중량%, 바람직하게는 5 내지 20 중량%의 양으로 추가로 포함할 수 있다.At least one of the first layer and the second layer may further comprise a pigment or dye in an amount of 1 to 40% by weight, preferably 5 to 20% by weight, based on the total weight of one layer.
상기 안료는 티타늄 옥사이드(TiO2) 입자일 수 있으며, TiO2 입자는 빛의 투과율, 반사율, 색상 등의 광학적 특성은 물론, 마찰계수, 표면조도 및 미세한 촉감을 조절하는 역할을 한다. The pigment may be a titanium oxide (TiO 2 ) particle, and the TiO 2 particle serves to control not only the optical characteristics such as light transmittance, reflectance and color, but also friction coefficient, surface roughness and fine touch.
TiO2는 컴파운딩 방식으로 첨가하는 것이 바람직하며, 입경은 0.1 내지 0.7 ㎛인 것이 좋고, 특히 0.2 내지 0.35 ㎛ 범위인 것이 바람직하다. The TiO 2 is preferably added in a compounding manner, and the particle diameter is preferably 0.1 to 0.7 탆, and more preferably 0.2 to 0.35 탆.
상기 제3 층은 상기 제1 층의 일면에 제2 층이 형성될 경우 제1 층의 타면에 직접 접할 수 있고, 상기 제1 층의 양면에 제2 층이 형성될 경우 제2 층의 표면에 직접 접할 수 있다.When the second layer is formed on one side of the first layer, the third layer may directly contact the other side of the first layer. When the second layer is formed on both sides of the first layer, You can contact them directly.
상기 제3 층은 폴리올레핀계 수지를 포함할 수 있다. 상기 폴리올레핀계 수지로는 당업계에서 통상적으로 사용되는 것을 사용할 수 있다. 제3 층은 봉지재로서 사용되는 에틸렌비닐아세테이트(EVA)와의 이접착성을 위한 것이다.The third layer may comprise a polyolefin-based resin. As the polyolefin-based resin, those conventionally used in the art can be used. The third layer is for this adhesion with ethylene vinyl acetate (EVA) used as an encapsulant.
제1 층과 제2 층은 공압출되어 형성되며, 제3 층은 공압출되어 형성된 제1 층/제2 층 적층체 또는 제2 층/제1 층/제2 층 적층체의 일면에 인라인 코팅을 통해 적절한 두께로 형성될 수 있다.The first layer and the second layer are formed by co-extrusion, and the third layer is formed by co-extruding the first layer / second layer laminate or the second layer / first layer / Lt; RTI ID = 0.0 > thickness. ≪ / RTI >
실시예에 따른 폴리머 필름은 태양 전지 패널 보호 필름으로 사용되며, 25 내지 400 ㎛, 바람직하게는 125 내지 300 ㎛의 두께를 가질 수 있다. 이때 제1 층과 제2 층은 1~100 : 1의 두께비를 가질 수 있다. 더 자세하게, 제1 층과 제2 층은 1~50 : 1의 두께비를 가질 수 있다. 더 자세하게, 제1 층과 제2 층은 1~20 : 1의 두께비를 가질 수 있다.The polymer film according to the embodiment is used as a solar cell panel protective film and may have a thickness of 25 to 400 mu m, preferably 125 to 300 mu m. Here, the first layer and the second layer may have a thickness ratio of 1 to 100: 1. More specifically, the first layer and the second layer may have a thickness ratio of 1 to 50: 1. More specifically, the first layer and the second layer may have a thickness ratio of 1 to 20: 1.
제1 층을 구성하는 수지는 0.4 내지 0.9 cPs(centipoise), 바람직하게는 0.5 내지 0.7 cPs의 고유점도(IV, intrinsic viscosity)를 가질 수 있으며, 230 내지 280℃, 바람직하게는 250 내지 270℃의 온도에서 공압출될 수 있다.The resin constituting the first layer may have an intrinsic viscosity (IV) of 0.4 to 0.9 cPs (centipoise), preferably 0.5 to 0.7 cPs, and may have an intrinsic viscosity of 230 to 280 ° C, preferably 250 to 270 ° C Can be co-extruded at a temperature.
제2 층을 구성하는 수지는 230℃에서 2 내지 20 g/10분, 바람직하게는 5 내지 15 g/10분의 용융지수(MI, melting index)를 가질 수 있으며, 190 내지 260℃, 바람직하게는 220 내지 240℃의 온도에서 공압출될 수 있다.The resin constituting the second layer may have a melting index (MI) at 230 DEG C of 2 to 20 g / 10 min, preferably 5 to 15 g / 10 min, and preferably 190 to 260 DEG C May be co-extruded at a temperature of 220-240 < 0 > C.
실시예에 따른 폴리머 필름은 일축 또는 이축 연신된 것일 수 있으며, 적어도 한 방향으로 1.5 배 내지 6 배 연신된 것일 수 있다. 예컨대, 폴리머 필름은 길이 방향으로 약 2 배 내지 약 5 배 연신되고/연신되거나, 폭 방향으로 약 2 배 내지 약 5 배 연신된 것일 수 있다. 더 자세하게, 폴리머 필름은 길이 방향으로 약 2.5 배 내지 약 4 배 연신되고/연신되거나, 폭 방향으로 약 2.5 배 내지 약 4 배 연신된 것일 수 있다.The polymer film according to an embodiment may be uniaxially or biaxially stretched and may be stretched 1.5 to 6 times in at least one direction. For example, the polymer film may be stretched about 2 times to about 5 times in the length direction / stretched or about 2 times to about 5 times in the width direction. More specifically, the polymer film may be stretched about 2.5 to about 4 times in the length direction / stretched or about 2.5 to about 4 times in the width direction.
이와 같이, 실시예에 따른 폴리머 필름은 불소계 수지(제2 층)와 폴리에스테르 수지(제1 층)와의 공압출에 의해 형성되는데, 상기 불소계 수지를 접합력 향상 수지와 함께 사용함으로써, 공압출시 상기 제1 층과 상기 제2 층 사이의 접합력이 향상된다.As described above, the polymer film according to the embodiment is formed by co-extrusion of a fluorine resin (second layer) and a polyester resin (first layer). By using the fluorine resin together with the bonding force improving resin, The bonding force between the first layer and the second layer is improved.
이에 따라서, 상기 제1 층과 상기 제2 층은 공압출될 경우에도 서로 박리되지 않고 강하게 접합되어 하나의 적층 필름을 형성할 수 있다.Accordingly, even when the first layer and the second layer are co-extruded, they can be strongly bonded without being separated from each other to form a laminated film.
따라서, 불소계 수지 필름 및 폴리에스테르계 수지 필름을 따로 형성하여 라미네이션하지 않아도, 실시예는 서로 간에 향상된 박리 강도를 갖는 불소계 수지층 및 폴리에스테르 수지층을 원하는 두께로 한번의 공압출에 의해 용이하게 형성할 수 있다.Therefore, even if the fluororesin film and the polyester resin film are separately formed and laminated, the embodiment can easily form the fluororesin layer and the polyester resin layer having desired peel strengths to each other to a desired thickness by one coextrusion can do.
또한, 실시예에 따른 폴리머 필름은 550㎚ 파장에서 50 내지 99%의 반사율을 나타낼 수 있다.Further, the polymer film according to the embodiment can exhibit a reflectance of 50 to 99% at a wavelength of 550 nm.
도 2는 일 실시예에 따른 태양광 발전 장치의 일 단면을 도시한 도면이다.2 is a cross-sectional view of a photovoltaic device according to an embodiment.
도 2를 참조하면, 일 실시예에 따른 태양광 발전 장치는 태양 전지 패널(10); 및 상기 태양 전지 패널(10)의 양면에 배치되는 상기 보호 필름(20, 30)을 포함한다.
Referring to FIG. 2, the photovoltaic device according to one embodiment includes a
또한, 이상에서 실시예들에 설명된 특징, 구조, 효과 등은 본 발명의 적어도 하나의 실시예에 포함되며, 반드시 하나의 실시예에만 한정되는 것은 아니다. 나아가, 각 실시예에서 예시된 특징, 구조, 효과 등은 실시예들이 속하는 분야의 통상의 지식을 가지는 자에 의해 다른 실시예들에 대해서도 조합 또는 변형되어 실시 가능하다. 따라서 이러한 조합과 변형에 관계된 내용들은 본 발명의 범위에 포함되는 것으로 해석되어야 할 것이다.
In addition, the features, structures, effects and the like described in the embodiments are included in at least one embodiment of the present invention, and are not necessarily limited to only one embodiment. Furthermore, the features, structures, effects and the like illustrated in the embodiments can be combined and modified by other persons skilled in the art to which the embodiments belong. Therefore, it should be understood that the present invention is not limited to these combinations and modifications.
이하, 본 발명을 실시예에 의해 보다 상세히 설명한다. 단 하기 실시예는 본 발명을 예시하는 것일 뿐, 본 발명의 내용이 하기 실시예에 한정되는 것은 아니다.
Hereinafter, the present invention will be described in more detail by way of examples. The following examples are illustrative of the present invention, but the present invention is not limited to the following examples.
실시예Example 1 One
네오펜틸글리콜 18 몰%, 에틸렌글리콜 82 몰% 및 테레프탈산 100 몰%로부터 얻어진 코-PET 칩(SKC(주) 제품)을 제1 층 수지 조성물(0.6 cPs의 IV)로서 준비하였다. A co-PET chip (product of SKC) obtained from 18 mol% of neopentyl glycol, 82 mol% of ethylene glycol and 100 mol% of terephthalic acid was prepared as a first layer resin composition (IV of 0.6 cPs).
폴리비닐리덴플루오라이드(PVDF) 단일 중합 수지(Hylar, Solvay사) 65 중량%, 개질된 폴리메틸메타크릴레이트(PMMA) 수지(Arylpet, Mitsubishi사) 20 중량% 및 TiO2 입자(Ti-pure, Dupont사) 15 중량%를 혼합하여 제2 층 수지 조성물(230℃에서 10 g/10분의 MI)을 제조하였다.20% by weight of a modified polymethyl methacrylate (PMMA) resin (Arylpet, Mitsubishi), 65% by weight of TiO 2 particles (Ti-pure, Dupont) were mixed to prepare a second layer resin composition (MI of 10 g / 10 min at 230 캜).
상기 제1 층 수지 조성물을 260℃에서, 상기 제2 층 수지 조성물을 230℃에서 용융 공압출한 후, 약 20℃의 캐스팅롤에서 냉각하여, 미연신 시트를 제조하였다. 이렇게 얻어진 미연신 시트를 80℃로 예열한 후, 90℃에서 길이 방향으로 3.5배 연신하고 연속적으로 120℃에서 폭 방향으로 3.5배 연신하였다. 이후, 상기 연신된 시트를 235℃의 온도에서 약 1분 동안 열고정하여 두께 250 ㎛의 2층 폴리머 필름(제1 층:제2 층의 두께비 = 10:1)을 제조하였다.
The first layer resin composition was melt-co-extruded at 260 캜 at 230 캜 for the second layer resin composition, and then cooled on a casting roll at about 20 캜 to prepare an unoriented sheet. The thus-obtained unstretched sheet was preheated at 80 DEG C, stretched 3.5 times in the longitudinal direction at 90 DEG C, and subsequently stretched 3.5 times in the width direction at 120 DEG C successively. Then, the stretched sheet was heat-set at 235 캜 for about 1 minute to prepare a two-layer polymer film (first layer: thickness ratio of the second layer = 10: 1) having a thickness of 250 탆.
실시예Example 2 내지 15 및 2 to 15 and 비교예Comparative Example 1 내지 6 1 to 6
제2 층 수지 조성물을 구성하는 PVDF 단일 중합 수지, 개질된 PMMA 수지 및 TiO2 입자의 함량, 및/또는 제1 층과 제2 층의 두께비를 하기 표 1에 기재된 바와 같이 변화시킨 것을 제외하고는, 상기 실시예 1과 동일한 방법으로 두께 250 ㎛의 2층 폴리머 필름을 제조하였다.Except that the content of PVDF monopolymer resin, modified PMMA resin and TiO 2 particles constituting the second layer resin composition, and / or the thickness ratio of the first layer and the second layer were changed as described in the following Table 1 , A two-layer polymer film having a thickness of 250 mu m was prepared in the same manner as in Example 1 above.
상기 실시예 및 비교예에서 제조된 폴리머 필름의 박리 여부를 육안으로 관찰하여 하기 표 1에 함께 나타내었다.The peeling of the polymer films prepared in the above Examples and Comparative Examples was visually observed and shown in Table 1 below.
(제1층/
제2층)Thickness ratio
(First layer /
Second layer)
상기 표 1에서 보는 바와 같이, 실시예 1 내지 15의 2층 폴리머 필름은 공압출되었음에도 불구하고 제1 층과 제2 층 간에 서로 강하게 접합되어 박리를 일으키지 않으므로, 태양 전지 패널 보호 필름(이면 보호 필름)으로서 유용하게 사용될 수 있다.
As shown in Table 1, the two-layer polymer films of Examples 1 to 15 were strongly bonded to each other between the first layer and the second layer in spite of the co-extrusion, so that the solar cell panel protective film ). ≪ / RTI >
100: 제1 층
200: 제2 층
300: 제3 층
10: 태양 전지 패널
20, 30: 보호 필름100: 1st layer
200: Second layer
300: Third floor
10: Solar panel
20, 30: Protective film
Claims (16)
상기 제1 층의 일면 또는 양면에 형성된 제2 층을 포함하되, 상기 제1 층과 제2 층이 공압출되어 적층된 구조를 가지며,
상기 제2 층이 50 중량% 초과 내지 90 중량% 이하의 불소계 수지 및 10 내지 20 중량%의 접합력 향상 수지를 포함하고, 상기 접합력 향상 수지 및 상기 폴리에스테르 수지 사이의 접합력이 상기 불소계 수지 및 상기 폴리에스테르 수지 사이의 접합력보다 더 큰, 태양 전지 패널 보호 필름으로서,
상기 제1 층을 구성하는 폴리에스테르 수지가 0.4 내지 0.9 cps의 고유점도(IV, intrinsic viscosity)를 가지며 230 내지 280℃에서 공압출되고, 상기 제2 층을 구성하는 불소계 수지 및 접합력 향상 수지의 혼합물이 2 내지 20 g/10분의 용융지수(MI, melting index)를 가지며 190 내지 260℃에서 공압출된,
태양 전지 패널 보호 필름.
A first layer comprising a polyester resin; And
And a second layer formed on one or both surfaces of the first layer, wherein the first layer and the second layer are co-extruded and laminated,
Wherein the second layer contains a fluorine resin in an amount of more than 50% by weight to 90% by weight and a bonding force improving resin in an amount of 10 to 20% by weight, and the bonding force between the bonding force- Wherein the adhesive force between the ester resin and the ester resin is larger than the bonding force between the ester resin and the ester resin,
Wherein the polyester resin constituting the first layer has an intrinsic viscosity (IV) of 0.4 to 0.9 cps and is co-extruded at 230 to 280 DEG C, and a mixture of a fluorine resin constituting the second layer and a bonding force improving resin Extruded at 190 to 260 DEG C with a melting index (MI) of 2 to 20 g / 10 min,
Solar panel protective film.
상기 폴리에스테르 수지가 디올 성분으로서 네오펜틸글리콜, 1,4-시클로헥산디메탄올, 디에틸렌글리콜 및 스피로글리콜 중 적어도 하나를 3 몰% 내지 80 몰%의 양으로 포함하는, 태양 전지 패널 보호 필름.
The method according to claim 1,
Wherein the polyester resin comprises at least one of neopentyl glycol, 1,4-cyclohexanedimethanol, diethylene glycol and spiroglycol as a diol component in an amount of 3 mol% to 80 mol%.
상기 폴리에스테르 수지가 디카르복실산 성분으로서 이소프탈산을 3 몰% 내지 80 몰%의 양으로 포함하는, 태양 전지 패널 보호 필름.
The method according to claim 1,
Wherein the polyester resin contains isophthalic acid in an amount of 3 to 80 mol% as a dicarboxylic acid component.
상기 제2 층이 상기 불소계 수지를 60 내지 80 중량%의 양으로 포함하는, 태양 전지 패널 보호 필름.
The method according to claim 1,
And the second layer contains the fluorine resin in an amount of 60 to 80% by weight.
상기 불소계 수지가 단일 중합 또는 공중합 폴리비닐리덴플루오라이드인, 태양 전지 패널 보호 필름.
The method according to claim 1,
Wherein the fluorine-based resin is a single-polymerized or copolymerized polyvinylidene fluoride.
상기 접합력 향상 수지가 아크릴계 수지를 포함하는, 태양 전지 패널 보호 필름.
The method according to claim 1,
Wherein the bonding force improving resin comprises an acrylic resin.
상기 접합력 향상 수지가 치환되거나 비치환된 폴리메틸메타크릴레이트 수지인, 태양 전지 패널 보호 필름.
8. The method of claim 7,
Wherein the bonding force improving resin is a substituted or unsubstituted polymethyl methacrylate resin.
상기 제1 층 및 제2 층이 1~50 : 1의 두께비를 갖는, 태양 전지 패널 보호 필름.
The method according to claim 1,
Wherein the first layer and the second layer have a thickness ratio of 1 to 50: 1.
상기 제1 층 및 제2 층 중 적어도 한 층이 안료 또는 염료를 한 층 총 중량을 기준으로 1 내지 40 중량%의 양으로 추가로 포함하는, 태양 전지 패널 보호 필름.
The method according to claim 1,
Wherein at least one of the first and second layers further comprises a pigment or dye in an amount of 1 to 40 wt% based on the total weight of the one layer.
상기 안료가 티타늄 옥사이드(TiO2) 입자인, 태양 전지 패널 보호 필름.
11. The method of claim 10,
Wherein the pigment is a titanium oxide (TiO 2) particles having, solar panel-protective film.
상기 태양 전지 패널 보호 필름이 제1 층 또는 제2 층과 직접 접하는 제3 층을 추가로 포함하고,
상기 제 3 층은 폴리올레핀계 수지를 포함하는, 태양 전지 패널 보호 필름.
The method according to claim 1,
Wherein the solar cell panel protective film further comprises a third layer directly contacting the first or second layer,
Wherein the third layer comprises a polyolefin-based resin.
상기 태양 전지 패널 보호 필름이 적어도 한 방향으로 1.5배 내지 6배 연신된 것인, 태양 전지 패널 보호 필름.
The method according to claim 1,
Wherein the solar cell panel protective film is stretched 1.5 to 6 times in at least one direction.
상기 태양 전지 패널의 적어도 일면에 배치되는 보호 필름을 포함하는 태양광 발전 장치로서,
상기 보호 필름이
폴리에스테르 수지를 포함하는 제1 층; 및
상기 제1 층의 일면 또는 양면에 형성된 제2 층을 포함하되, 상기 제1 층과 제2 층이 공압출되어 적층된 구조를 가지며, 상기 제2 층이 50 중량% 초과 내지 90 중량% 이하의 불소계 수지 및 10 내지 20 중량%의 접합력 향상 수지를 포함하고, 상기 접합력 향상 수지 및 상기 폴리에스테르 수지 사이의 접합력이 상기 불소계 수지 및 상기 폴리에스테르 수지 사이의 접합력보다 더 크고, 상기 제1 층을 구성하는 폴리에스테르 수지가 0.4 내지 0.9 cps의 고유점도(IV, intrinsic viscosity)를 가지며 230 내지 280℃에서 공압출되고, 상기 제2 층을 구성하는 불소계 수지 및 접합력 향상 수지의 혼합물이 2 내지 20 g/10분의 용융지수(MI, melting index)를 가지며 190 내지 260℃에서 공압출된,
태양광 발전 장치.Solar panel; And
And a protective film disposed on at least one surface of the solar cell panel,
The protective film
A first layer comprising a polyester resin; And
And a second layer formed on one or both surfaces of the first layer, wherein the first layer and the second layer are co-extruded and laminated, and the second layer has a composition of more than 50 wt% to 90 wt% Based resin and a bonding force improving resin of 10 to 20% by weight, wherein the bonding force between the bonding force improving resin and the polyester resin is larger than the bonding force between the fluororesin and the polyester resin, Wherein the polyester resin is co-extruded at 230 to 280 DEG C with an intrinsic viscosity (IV) of 0.4 to 0.9 cps, and a mixture of the fluorine resin and the bonding force improving resin constituting the second layer is 2 to 20 g / Extruded at 190 to < RTI ID = 0.0 > 260 C < / RTI > with a melt index (MI)
Photovoltaic devices.