KR101545210B1 - Resin composition for being used to manufacture funtional resin articles - Google Patents
Resin composition for being used to manufacture funtional resin articles Download PDFInfo
- Publication number
- KR101545210B1 KR101545210B1 KR1020150093201A KR20150093201A KR101545210B1 KR 101545210 B1 KR101545210 B1 KR 101545210B1 KR 1020150093201 A KR1020150093201 A KR 1020150093201A KR 20150093201 A KR20150093201 A KR 20150093201A KR 101545210 B1 KR101545210 B1 KR 101545210B1
- Authority
- KR
- South Korea
- Prior art keywords
- resin
- resin composition
- weight
- kaolinite
- present
- Prior art date
Abstract
Description
본 발명은 향균력, 탈취력, 원적외선 방사율, 유해전자파 차단 등의 기능성을 지닌 기능성 수지 제품 제조용 수지 조성물에 관한 것이다.The present invention relates to a resin composition for the production of a functional resin product having functionality such as antimicrobial activity, deodorizing power, far infrared ray emissivity, harmful electromagnetic wave shielding, and the like.
일반적으로, 수지 제품은 필름, 섬유, 성형품, 파이프, 기계 부품 등을 포함하여 그 용도를 한정하기 어려울 정도로 매우 다양하다.In general, resin products are extremely diverse, including films, fibers, molded articles, pipes, mechanical parts, and the like, so that it is difficult to limit their use.
상기와 같이 수지 제품이 다양한 분야에서 사용되고 있기 때문에 차별화된 수지 제품을 개발하기 위해 수지 제품 관련 업체에서는 수지 제품에 기능성을 부여하려는 연구 개발이 이루어지고 있다.Since resin products are used in various fields as described above, in order to develop differentiated resin products, research and development is being carried out in the companies related to resin products to give functionality to resin products.
이러한 연구 개발에 일환으로 개발된 기술로 대표적인 예로는 2개 이상의 알코올성 히드록실기를 갖는 산화 방지제를 포함하는 산화 방지 기능성 수지 조성물과 카테킨류 등의 식물유래 성분, 미분판상 광물 및 세라믹 성분을 포함시켜 탈취성, 향미생물성 등의 기능성을 갖는 기능성 수지 조성물, 합성수지에 천연광물질의 함유를 통해 기능성을 향상시킨 기능성 수지 조성물 등을 들 수 있다.As a technology developed as a part of such research and development, typical examples include an antioxidant functional resin composition containing an antioxidant having two or more alcoholic hydroxyl groups, a plant-derived component such as catechins, a microparticulate mineral and a ceramic component A functional resin composition having functionalities such as deodorizing property and flavor microbial property, and a functional resin composition in which the functionality is improved through the addition of natural minerals to a synthetic resin.
특히, 합성수지에 천연광물질을 함유시키는 기능성 수지 조성물을 제조하는 기술은 합성수지를 기 설정된 온도(예컨대 150℃∼230℃)에서 융용시키는 가열 단계에서 기능이 추가되는 미분쇄된 천연광물질을 함유시키고, 블로윙(blowing) 및 냉각 단계를 거쳐 제조하는 공법으로 합성수지에 기능성을 부여할 수 있다.In particular, a technique for producing a functional resin composition containing natural minerals in a synthetic resin contains finely divided natural minerals, which are added during the heating step of melting the synthetic resin at a predetermined temperature (for example, 150 to 230 ° C) (blowing) and a cooling step, the functional property can be given to the synthetic resin.
그러나, 종래의 천연광물질을 이용한 기능성 수지 조성물에 함유되는 천연광물질은 그 비중이 높기 때문에 천연광물질이 함유된 수지 조성물을 이용하여 제품을 제조할 경우 기존의 합성수지를 이용한 제품의 생산량과 차이가 최소 10%에서 최대 20%까지 차이가 날 수 있다. 이러한 생산량의 차이로 인하여 천연광물질이 함유된 수지 조성물을 이용한 제품의 가격이 합성수지를 이용한 제품의 가격보다 2배 이상 높게 형성되기 때문에 천연광물질이 함유된 수지 조성물은 실제 제품에 제조에 이용되지 못하고 있다.However, since natural minerals contained in functional resin compositions using natural minerals have a high specific gravity, when a product is manufactured using a resin composition containing natural minerals, the difference in production amount of products using existing synthetic resins is at least 10 % To a maximum of 20%. Because the price of the product using the natural mineral-containing resin composition is more than twice that of the product using the synthetic resin due to the difference in the production amount, the resin composition containing the natural mineral is not used in the actual product .
본 발명의 목적은, 합성수지에 첨가제로 비중이 낮은 고령토 도석을 미분쇄가공 처리한 물질과 옻 나무의 분말 가루를 함유시켜 합성수지에 기능성을 부여함으로써, 합성수지의 향균력, 탈취력, 원적외선 방사율 및 유해전자파 차단 기능을 향상시킬 수 있는 기능성 수지 제품 제조용 수지 조성물을 제공하는데 있다.It is an object of the present invention to provide a synthetic resin which is obtained by finely grinding kaolinite having a low specific gravity as an additive in a synthetic resin and powdered powder of lacquer tree to impart functionality to the synthetic resin to improve the antimicrobial activity, deodorization power, far infrared ray emissivity, And to provide a resin composition for the production of a functional resin product capable of improving the function.
본 발명의 다른 목적은, 합성수지에 첨가제로 고령토 도석을 미분쇄가공 처리한 물질, 옻나무의 액상 및 활성탄을 합성수지에 기능성을 부여함으로써, 합성수지의 탈취력 및 향균력을 극대화시킬 수 있는 기능성 수지 제품 제조용 수지 조성물을 제공하는데 있다.Another object of the present invention is to provide a resin composition for functional resin products which can maximize the deodorizing power and the antimicrobial power of a synthetic resin by imparting functionality to the synthetic resin in the form of a material obtained by finely grinding kaolin with an additive to synthetic resin, .
본 발명의 또 다른 목적은, 합성수지에 첨가제로 이용되는 천연광물질의 함유량을 25 중량 % 이하로 사용함으로써, 수지를 가공하는 사출성형제조 기계의 스쿠류 마모에 영향을 주지 아니하도록 하는 기능성 수지 제품 제조용 수지 조성물을 제공하는데 있다.It is still another object of the present invention to provide a functional resin product manufacturing resin which does not affect the squeal wear of an injection molding machine for processing a resin by using a content of natural minerals used as an additive in a synthetic resin of 25 wt% Compositions.
상기한 본 발명의 목적들은 수지와, 첨가제로 고령석 도석 및 옻 나무 분말을 포함하는 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물에 의해 달성된다.The above objects of the present invention are achieved by a resin composition for the production of a functional resin article, which comprises a resin and an additive comprising an aged stones and an lacquer powder.
또한, 본 발명의 기능성 수지 제품 제조용 수지 조성물은 상기 첨가제로 활성탄을 더 포함하는 것을 특징으로 한다.Further, the resin composition for producing a functional resin product of the present invention is characterized by further containing activated carbon as the additive.
또한, 상기 수지 제품은 물품의 포장용 필름 또는 보관 용기인 것을 특징으로 한다.Further, the resin product is a film for packaging the article or a storage container.
또한, 상기 기능성은 향균성, 탈취성, 유해전자파 차단성 및 원적외선 방사성으로 이루어진 군에서 선택되는 하나 이상인 것을 특징으로 한다.Further, the functionalities are characterized by being at least one selected from the group consisting of antibacterial, deodorizing, harmful electromagnetic wave shielding, and far-infrared radiation.
본 발명의 목적들은 폴리프로필렌 75 중량 %, 고령토 도석 23.5-24 중량 % 및 옻 분말 1-1.5 중량 %을 포함하는 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물에 의해 달성된다.The objects of the present invention are achieved by a resin composition for the production of a functional resin article, which comprises 75% by weight of polypropylene, 23.5-24% by weight of kaolinite and 1-1.5% by weight of lacquer powder.
본 발명의 목적들은 폴리프로필렌 75 중량 %, 고령토 도석 22.5-23 중량 %, 옻 분말 1-1.5 중량 % 및 활성탄 0.5-1 중량 %를 포함하는 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물에 의해 달성된다.The object of the present invention is achieved by a resin composition for the production of a functional resin article, which comprises 75% by weight of polypropylene, 22.5-23% by weight of kaolinite, 1-1.5% by weight of lacquer powder and 0.5-1% by weight of activated carbon .
본 발명의 목적들은 옥수수 전분을 포함한 공폴리에스테스(Copolyester) 74 중량 %, 고령토 도석 25 중량 %, 옻 분말 1 %중량을 포함하는 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물에 의해 달성된다.The object of the present invention is achieved by a resin composition for the production of a functional resin article, which comprises 74 wt% of a copolyester containing corn starch, 25 wt% of kaolinite, and 1 wt% of a lacquer powder.
본 발명의 수지 조성물에 따르면, 고령토 도석과 천연식물성원료를 정재처리한 미분쇄 옻 분말 가루를 합성수지에 첨가하여 표면처리를 하여 줌으로서 항균기능, 원적외선 기능 및 탈취력을 극대화시킬 수 있다. 이에 따라, 식료품포장지와 같은 제품의 내 보관 물질의 신선도 및 보관 물질의 부패에 대한 냄새제거를 향상시킬 수 있다. According to the resin composition of the present invention, it is possible to maximize antimicrobial function, far-infrared ray function and deodorizing power by adding the ground powder of kaolinite and natural vegetable raw material to the synthetic resin for surface treatment. Thus, it is possible to improve the freshness of the storage material of a product such as a food package and the removal of odor due to storage material spoilage.
또한, 본 발명에 따른 수지 조성물을 의료용수지원료로 사용할 경우 의료용수지원료로 제조된 제품의 향균력, 원적외선방사성 등을 향상시킬 수 있다.In addition, when the resin composition according to the present invention is used as a raw material for medical resins, the antimicrobial activity, far-infrared radiation and the like of a product made of a medical resin raw material can be improved.
본 발명에 따르면, 합성수지에 첨가제로 이용되는 천연광물질인 고령토 도석의 함유량을 25 중량 % 이하로 사용함으로써, 수지를 가공하는 사출성형제조 기계의 스쿠류 마모에 영향을 주지 않기 때문에 기존 제조 기계의 변경 없이 기능성 수지 제품을 생산할 수 있다.According to the present invention, by using the content of kaolinite, which is a natural mineral used as an additive in synthetic resin, to 25 wt% or less, it does not affect the squeal wear of the injection molding machine for processing the resin. Functional resin products can be produced.
도 1은 시간 경과에 다른 탈취율, 블랭크 농도 및 샘플 농도의 변화를 도시한 그래프
도 2는 원적외선량 변화에 따른 본 발명의 수지 조성물의 방사량 변화를 도시한 그래프
도 3은 원적외선량 변화에 따른 본 발명의 수지 조성물의 방사 에너지 변화를 도시한 그래프1 is a graph showing changes in deodorization rate, blank concentration and sample concentration,
Fig. 2 is a graph showing changes in the amount of radiation of the resin composition of the present invention depending on the change in far-infrared ray amount
FIG. 3 is a graph showing the change in radiant energy of the resin composition of the present invention according to the change in far-infrared ray amount
일 측면에 있어서, 본 발명은 기능성 수지 제품 제조용 수지 조성물에 관한 것이다.In one aspect, the present invention relates to a resin composition for producing a functional resin product.
본 발명은 하기 실시예 및 실험예에서 확인되는 바와 같이 합성수지에 첨가제로, 고령토 도석 분말 및 옻나무의 분말 가루를 함께 넣어 수지 제품을 제조하고, 그 수지 제품을 이용하여 향균력, 탈취력(소취력 또는 방취력), 원적외선 방사율, 유해전자파 차단 기능을 살펴 본 결과, 그 효과가 매우 뛰어남을 확인할 수 있었다. The present invention is characterized in that a resin product is prepared by putting powdered kaolin powder and Rhus verniciflua powder as an additive into a synthetic resin as shown in the following Examples and Experimental Examples, and using the resin product, antimicrobial activity, deodorizing power Power, far - infrared ray emittance, and harmful electromagnetic wave shielding function.
또한, 본 발명은 하기 실시예 및 실험예에서 고령토 도석 분말, 옻나무의 분말 가루 및 활성탄을 함께 넣어 수지 제품을 제조하고, 그 수지 제품을 이용하여 향균력, 탈취력(소취력 또는 방취력), 원적외선 방사율, 유해전자파 차단 기능을 살펴 본 결과, 그 효과가 매우 뛰어남을 확인할 수 있었다. The present invention also provides a resin product prepared by putting kaolin powder, powdered Rhus powder and activated carbon together in the following Examples and Experimental Examples. Using the resin product, antimicrobial activity, deodorizing power (deodorizing power or deodorizing power) , The harmful electromagnetic wave shielding function was examined, and it was confirmed that the effect is excellent.
본 발명은 이러한 실험 결과에 기초하여 제공 되어지는 것이다.The present invention is provided based on the results of these experiments.
그러므로 본 발명의 기능성 수지 제품 제조용 수지 조성물은 수지와 첨가제로서 고령토 도석 분말 및 옻나무의 분말 가루가 포함하거나 고령토 도석 분말, 옻나무의 분말 가루 및 활성탄을 포함하는 것을 특징으로 한다.Therefore, the resin composition for the production of a functional resin product of the present invention is characterized in that it contains a powder of kaolinite powder and Rhus verniciflua powder as a resin and an additive, powdered kaolin powder, powder of Rhus verniciflua, and activated carbon.
한편, 청구범위를 포함하는 본 명세서에서 상기 "기능성"이란 향균성, 탈취성, 원적외선 방사성, 정화성, 항균성 및/또는 유해전자파 차단성을 포함하는 의미로서 정의된다.On the other hand, in the present specification including claims, the above-mentioned "functional" is defined as meaning including antibacterial, deodorizing, far infrared radiation, purification, antibacterial and / or harmful electromagnetic wave shielding.
"기능성"이 이와 같이 정의되어지는 한, 어떠한 수지 조성물이 수지와 첨가제로서 고령토 도석 분말 및 옻나무의 분말 가루가 포함하거나 운기석 분말, 옻나무의 분말 가루 및 활성탄을 포함하고, 또 그것이 상기 정화성, 항균성 및/또는 탈취성을 갖는/요하는 수지 제품의 제조에 사용될 수 있다면, 그러한 수지 조성물은 모두 본 발명의 기능성 수지 제품 제조용 수지 조성물에 포함되는 것으로 이해되어져야 한다.As long as "functional" is defined as such, any resin composition contains powdered powder of kaolinite powder and Rhus verniciflua powder as a resin and an additive, or powdered powder of fenugreek powder, Rhus verniciflua powder and activated carbon, All such resin compositions should be understood to be included in the resin composition for the production of a functional resin product of the present invention, if they can be used in the production of a resin product requiring / having antibacterial and / or deodorizing properties.
한편, 청구범위를 포함하는 본 명세서에서, "첨가제로 포함한다"는 것의 의미는 수지보다 실질적으로 적은 양으로 포함한다는 의미이면서 또한 전술하는 바의 기능성을 나타낼 수 있을 만큼의 양으로 포함한다는 의미로서 정의될 수 있다. 특히, 본 발명에 따른 기능성 수지 제품 제조용 수지 조성물의 경우 첨가제인 천연광물질에 해당하는 고령토 도석이 기존의 사출성형제조기계의 스쿠류 마모에 영향을 주지 않는 범위, 예컨대 25 중량 %를 넘지 않는 범위의 양으로 정의될 수 있다.In the present specification including the claims, the meaning of "comprising as an additive" means that it contains substantially less amount of resin than resin, and also includes in an amount sufficient to exhibit the above-mentioned functionality Can be defined. In particular, in the case of the resin composition for the production of a functional resin product according to the present invention, kaolin stones corresponding to natural minerals which are additives are added in such a range as not to affect the squeal wear of the conventional injection molding machine, . ≪ / RTI >
당업자라면 본 출원의 출원시를 기준으로 당업계에 공지된 기술과 본 발명의 하기 실시예 및 실험예에 기초하는 한 그의 통상의 능력 범위 내에서 전술하는 바의 기능성을 나타낼 수 있는(그 기능성의 정도에 있어서는 차이는 있더라도) 수지 제품의 제조에 적합한 수지와 첨가제의 비율을 결정할 수 있을 것이다.Those skilled in the art will appreciate that, based on the time of the filing of the present application, those skilled in the art will be able to demonstrate the foregoing functionality within the scope of ordinary skill in the art based on techniques known in the art and the following Examples and Experimental Examples of the invention The ratio of resin and additive suitable for the production of the resin product may be determined.
예컨대, 수지가 폴리프로필렌(PP : Polypropylene)인 경우, 수지 조성물은 75 중량 %의 폴리프로필렌에 23.5 ∼ 24 중량 %의 고령토 도석 분말을 첨가시키고, 향균력의 상승과 원적외 방사율을 증가시키기 위해 천연식품연료인 정제된 옻 분말 가루를 1 ∼1.5 중량 % 첨가시켜 제조하는 것을 바람직하다.For example, when the resin is polypropylene (PP), the resin composition is prepared by adding 23.5 to 24% by weight of kaolinite powder to 75% by weight of polypropylene, It is preferable to add 1 to 1.5 wt% of refined octanoic powder powder as a fuel.
한편, 본원발명의 고령토 도석은 SiO2, MgO, CaO, Al2O3, TiO2, K2O, Na2O, Fe2O2, L.O.I 및 Ge가 함유된 미분쇄 분말이고, 그 비중이 수지, 예컨대 폴리프로필렌의 비중 이상이 되지 않는 광물질인 고령토 도석을 의미할 수 있다.On the other hand, the kaolinite of the present invention is a fine powder containing SiO 2 , MgO, CaO, Al 2 O 3 , TiO 2 , K 2 O, Na 2 O, Fe 2 O 2 , LOI and Ge, It may mean kaolinite, which is a mineral that does not exceed the specific gravity of resin, such as polypropylene.
또한, 본원발명의 수지는 PP(Polypropylene). PE(Polyethylense), SAN(Styrene AcryloNitrile), ABS(Acrylonitrile Butadiene Styrene), POM(polyacetal), PET(Polyethylene Terephthalate), PES(Poly Ether Sulfone), PVC(Polyvinyl Chloride), PU(Polyurethane), PC(PolyCarbonate), EVA(Ethylene Vinyl Acetate), 우레탄(urethane) 및 공폴리에스테스(Copolyester) 등을 포함할 수 있으나, 첨가제로서 포함되는 고령토 도석 분말, 옻 나무 분말, 활성탄이 전술한 바의 기능성을 나타내는 것을 방해하지 않는다면 의도하는 용도에 따라 당업계에 공지된 임의의 수지를 사용할 수도 있다.The resin of the present invention is PP (Polypropylene). (Polyethylene), SAN (Styrene Acrylonitrile), ABS (Acrylonitrile Butadiene Styrene), POM (Polyacetal), PET (Polyethylene Terephthalate), PES (Polyether Sulfone), PVC (Polyvinyl Chloride), PU ), EVA (Ethylene Vinyl Acetate), urethane, and copolyester, but it does not exhibit the above-mentioned functionalities of kaolin powder, lacquer powder and activated carbon contained as additives It is possible to use any resin known in the art depending on the intended use.
상기 예시한 바의 수지 이외에도, 폴리염화비닐, 폴리염화비닐리덴 등의 폴리할로겐화비닐류, 할로겐화 폴리에틸렌, 할로겐화 폴리프로필렌 등의 단일 중합체와, 염화비닐/아세트산비닐 공중합체, 염화비닐/에틸렌 공중합체, 염화비닐/프로필렌 공중합체, 염화비닐/스티렌 공중합체, 염화비닐/이소부틸렌 공중합체, 염화비닐/염화비닐리덴 공중합체, 염화비닐/스티렌/아크릴로니트릴 공중합체, 염화비닐/부타디엔 공중합체, 염화비닐/염소화프로필렌 공중합체, 염화비닐/염화비닐리덴/아세트산비닐 공중합체, 염화비닐/말레산 에스테르 공중합체, 염화비닐/메타크릴산 에스테르 공중합체, 염화비닐/아크릴로니트릴 공중합체, 에틸렌/프로필렌 공중합체, 에틸렌/부텐 공중합체, 에틸렌/펜텐 공중합체, 에틸렌/헥센 공중합체, 에틸렌/헵텐 공중합체, 에틸렌/옥텐 공중합체, 에틸렌/프로필렌 공중합체, 에틸렌/1-부텐 공중합체, 에틸렌/4-메틸-1-펜텐공중합체, 에틸렌/아크릴산 공중합체, 에틸렌/메틸메타크릴레이트 공중합체 등의 공중합체 등이 단독으로 2종 이상 혼합되어 본 발명의 기능성 수지 제품 제조용 수지 조성물에 사용될 수 있다.In addition to the above-exemplified resins, it is also possible to use homopolymers such as polyvinyl chloride, polyvinyl halides such as polyvinylidene chloride, halogenated polyethylene and halogenated polypropylene, vinyl chloride / vinyl acetate copolymer, vinyl chloride / ethylene copolymer, Vinyl chloride / vinylidene chloride copolymer, vinyl chloride / styrene / acrylonitrile copolymer, vinyl chloride / butadiene copolymer, chlorinated vinyl chloride / butadiene copolymer, vinyl chloride / Vinyl chloride / vinyl chloride / vinyl acetate copolymer, vinyl chloride / maleic acid ester copolymer, vinyl chloride / methacrylic acid ester copolymer, vinyl chloride / acrylonitrile copolymer, ethylene / propylene copolymer Ethylene / butene copolymer, ethylene / pentene copolymer, ethylene / hexene copolymer, ethylene / heptene copolymer, ethyl A copolymer of an ethylene / 1-butene copolymer, an ethylene / 4-methyl-1-pentene copolymer, an ethylene / acrylic acid copolymer, and an ethylene / methyl methacrylate copolymer May be used alone or in combination of two or more in the resin composition for the production of the functional resin product of the present invention.
본 발명의 기능성 수지 조성물에 의해 제조되는 수지 제품으로는 높은 향균력이 요구되고, 부패된 냄새를 억제하는 탈취력이 요구되는 1회용 용기, 식품 용기 등의 프레스 금형 사출 제품, 음식물의 보존기간을 향균력과 원적외선 방사율로 인하여 기존의 부패율을 감소시키고, 음식물의 부패된 냄새를 억제하는 탈취력이 요하는 수출용 김치 포장지, 식품 비닐 포장지 등의 포장용 비닐 포장지, 의료용 수지 원료 제품 등을 포함할 수 있다.Resin products manufactured by the functional resin composition of the present invention are required to have a high antimicrobial power and to be used in a disposable container requiring a deodorizing power for suppressing a decayed odor, a press mold injection product such as a food container, Kimchi wrapping paper for export, plastic wrapping paper for packaging such as food plastic wrapping paper, and medical resin raw material product, which require a deodorizing power to reduce the decay rate of the food due to the far-infrared emissivity and reduce the decaying odor of foodstuffs.
본 발명의 수지 조성물이 상기와 같은 1회용 용기, 식품 용기, 포장지 등의 수지 제품에 이용될 경우에, 용기 및 포장지는 향균 효과, 탈취 효과, 원적외선 방사 효과, 유해전자파 차단 효과를 지닌다는 점에서 포장지 및 용기 등에 담긴 물질에 의한 냄새를 억제시킬 수 있을 뿐만 아니라 물질의 부패를 억제시키는데 유용하게 사용될 수 있다.When the resin composition of the present invention is used for a resin product such as a disposable container, a food container, a packaging paper, etc., the container and the packaging paper have an antibacterial effect, a deodorizing effect, a far infrared radiation effect, It can be used not only to suppress the odor due to the material contained in the wrapping paper and the container but also to suppress the decay of the material.
또한, 수지 조성물이 의료용 수지 원료 제품에 사용되거나 자연 생분해가 가능한 친환경 에코젠 수지 제품의 제조에 이용될 경우에, 의료용 수지 원료 제품은 수지 조성물의 높은 향균력을 발휘할 수 있으며, 에코젠 수지 제품은 다른 첨가제를 함유한 에코젠 수지 제품에 비해 기능성면에서 향상될 수 있다.Further, when the resin composition is used in the production of an eco-friendly echogen resin product which can be used for raw materials for medical resin production or can be biodegraded naturally, the medical resin raw material product can exert a high antimicrobial effect of the resin composition, Can be improved in terms of functionality compared to an ezogen resin product containing an additive.
본 발명의 기능성 수지 제품 제조용 수지 조성물에 함유된 활성탄은 참나무, 소나무, 밤나무, 대나무 등에 의해 생성된 숯에 수증기 또는 약품을 사용하여 표면적을 증가시킨 소재를 의미할 수 있다.The activated carbon contained in the resin composition for producing a functional resin product of the present invention may be a material having increased surface area by using water vapor or chemicals on charcoal produced by oak, pine, chestnut, bamboo, and the like.
본 발명은 다른 측면에서 전술한 바와 같은 기능성 수지 제품 제조용 수지 조성물의 제조 방법에 관한 것이다.In another aspect, the present invention relates to a method for producing a resin composition for producing a functional resin product as described above.
본 발명의 기능성 수지 조성물 제조 방법은 표면 처리, 열처리, 성형 가공 단계를 포함하는 것을 특징으로 한다.The method for producing a functional resin composition of the present invention is characterized by including a surface treatment, a heat treatment, and a molding and processing step.
본 발명의 성형 가공 단계는 제조되는 제품의 용도에 따라 당업계에 알려진 방법을 사용할 수 있다. 예컨대, 수지 제품이 필름인 경우 인플레이션법, 캘린더법, T다이법, 블로운(blown)필름압출법, 플랫다이(flat die)압출법 등을 사용할 수 있다. 수지 제품이 보관 용기나 파이프인 경우에는 중공 성형법 등을 사용할 수 있다.The molding step of the present invention can be carried out by a method known in the art depending on the use of the product to be produced. For example, when the resin product is a film, an inflation method, a calendar method, a T-die method, a blown film extrusion method, a flat die extrusion method, or the like can be used. When the resin product is a storage container or a pipe, a blow molding method or the like can be used.
한편, 본 발명의 기능성 수지 조성물을 이용한 제품의 제조 방법에 있어서, 기능성 수지 제품 제조용 수지 조성물을 성형 가공하여 수지 제품을 제조하기 이전에 그 수지 조성물을 융용 혼련하는 단계를 포함할 수 있다.On the other hand, in the method for producing a product using the functional resin composition of the present invention, it may include a step of melt kneading the resin composition before the resin product is manufactured by molding the resin composition for manufacturing the functional resin product.
이러한 용융 혼련 방법은 당업계에 공지된 방법을 사용하여 수행될 수 있으며, 그러한 방법으로서 밴버리 혼합기, 가압 혼련기 등을 사용한 방법 등이 예시될 수 있다.Such a melt-kneading method can be carried out using a method known in the art, and examples of such methods include a Banbury mixer, a method using a pressure kneader, and the like.
이하 본 발명을 실시예를 참조하여 설명한다. 그러나 이러한 실시예가 본 발명의 범위를 제한하는 것은 아니다.Hereinafter, the present invention will be described with reference to examples. However, these examples do not limit the scope of the present invention.
<실시예><Examples> 기능성 수지 제품 제조용 수지 조성물 제조 Manufacture of resin composition for manufacturing functional resin products
<실시예 1> 기능성 수지 제품 제조용 수지 조성물의 제조예 1≪ Example 1 > Preparation Example 1 of a resin composition for producing a functional resin product
합성수지인 폴리프로필렌 75 중량 %에 23.5 ∼ 24 중량 %의 천연광물질인 고령토 도석과 천연식물원료인 옻 나무 분말 가루 1 ∼ 1.5 중량 %를 첨가제로 함유시켜 표면 처리, 및 기 설정된 온도, 예컨대 200-220도에서 가열시켜 블로윙, 압축 및 압출 공정을 실시하여 향균력, 탈취력, 원적외선 방사율이 높은 기능성 수지 조성물을 제조하였다. 이후, 제조된 기능성 수지 조성물을 옻 나무 분말 가루로 표면 처리하여 그 기능을 극대화시켰다. 75% by weight of polypropylene, which is a synthetic resin, contains 23.5 to 24% by weight of kaolin stones, which are natural minerals, and 1 to 1.5% by weight of lacquer powder as a raw material of natural plants, as surface additives, And then subjected to a blowing, compression and extrusion process by heating in a mold to prepare a functional resin composition having high antimicrobial activity, deodorizing power, and far infrared ray emissivity. Thereafter, the functional resin composition thus prepared was surface-treated with powder of lacquer wood powder to maximize its function.
소정의 실시예1에서, 고령토 도석은 아래의 표 1과 같은 성분을 가지고 있다In certain Example 1, kaolinite has the components listed in Table 1 below
상기와 같은 방법으로 제조된 기능성 수지 조성물은 고령토 도석에 의해 1차적으로 향균력, 탈취력, 원적외선 방사율 및 유해전자파 차단율을 높이고, 2차적으로 옻 분말의 우루시올에 의해 향균력과 살균력을 더욱더 높일 수 있다.The functional resin composition prepared by the above method can enhance the antimicrobial activity, deodorization power, far infrared ray emissivity and harmful electromagnetic wave shielding rate primarily by kaolinite, and further enhance the antimicrobial activity and sterilization power by urushiol of the lacquer powder.
<실시예 2> 기능성 수지 제품 제조용 수지 조성물의 제조예 2Example 2 Production Example 2 of Resin Composition for Manufacturing Functional Resin Product
합성수지인 폴리프로필렌 75 중량 %에 22.5∼ 23 중량 %의 천연광물질인 고령토 도석, 천연식물원료인 옻분말 가루 1-1.5% 및 활성탄 가루 0.5 ∼ 1 중량 %를 첨가제로 함유시켜 표면 처리, 및 기 설정된 온도, 예컨대 200-220도에서 가열시켜 블로윙, 압축 및 압출 공정을 실시하여 향균력, 탈취력, 원적외선 방사율이 높은 기능성 수지 조성물을 제조하였다.The present invention relates to a synthetic resin composition comprising 75% by weight of polypropylene which is a synthetic resin, 22.5 to 23% by weight of kaolin stones made of natural minerals, 1-1.5% of powder of natural plant raw material, and 0.5 to 1% And then subjected to a blowing, compression and extrusion process by heating at a temperature of, for example, 200-220 ° C. to produce a functional resin composition having high antimicrobial activity, deodorizing power, and far infrared ray emissivity.
<실시예 3> 기능성 수지 제품 제조용 조성물의 제조예 3≪ Example 3 > Preparation Example 3 of Composition for Preparing Functional Resin Product
옥수수 전분을 포함한 에코젠 74 중량 %에 25 중량 %의 천연광물질인 천연식물원료인 옻 나무 분말 가루 1 중량 %를 첨가제로 함유시켜 친환경 기능성 수지 조성물을 제조하였다.An eco-friendly functional resin composition was prepared by adding 1 wt% of lacquer powder as a natural plant material, which is a natural mineral material, to 25 wt% of 74 wt% ecozone containing corn starch as an additive.
<실시예><Examples> 기능성 수지 제품 제조용 수지 조성물을 이용한 제품 제조 Production of products using resin composition for manufacturing functional resin products
<실시예 1> 기능성 수지 제품 제조용 조성물을 이용한 플라스틱 제조Example 1 Preparation of Plastic Using Composition for Functional Resin Product
천연광물질인 고령토 도석과 함께 미분쇄한 옻 나무 분말을 합성수지, 예컨대 폴리프로필렌과 혼합하여 제조한 기능성 수지 조성물의 펠릿으로 플라스틱 제품을 제조하였다.A plastic product was prepared from pellets of a functional resin composition prepared by mixing finely pulverized lacquer wood powder with a natural mineral such as kaolinite, synthetic resin such as polypropylene.
<실시예 2> 기능성 수지 제품 제조용 수지 조성물을 이용한 식품 밀폐 용기 제조Example 2 Production of Food-Closed Container Using Resin Composition for Manufacturing Functional Resin Product
천연광물질인 고령토 도석과 함께 미분쇄한 옻 나무 분말을 합성수지, 예컨대 폴리프로필렌과 혼합하여 제조한 기능성 수지 조성물의 펠릿으로 식품 밀폐 용기를 제조하였다.A food sealed container was prepared by pelletizing a functional resin composition prepared by mixing finely pulverized lacquer wood powder with a natural mineral such as kaolinite, synthetic resin such as polypropylene.
<실험예> 수지 조성물과 수지 제품의 정화 효과 실험, 항균 효과 실험 및 탈취 효과 실험EXPERIMENTAL EXAMPLES Experiments of purification effect, antibacterial effect and deodorization effect of resin composition and resin product
<실험예 1> 기능성 수지 제품 제조용 수지 조성물의 탈취 효과 실험Experimental Example 1 Deodorizing Effect Test of Resin Composition for Manufacturing Functional Resin Product
의뢰자가 제시한 시료, 즉 본 발명의 기능성 수지 제품 제조용 수지 조성물 20g을 5L 크기의 반응기에 넣고 시험 가스, 즉 초기 농도가 50μmol/mol인 암모니아(NH3)을 반응기에 주입한 후 30분, 60분, 90분 및 120분 간격으로 암모니아 농도를 측정하였다. 이때, 농도 측정 시험 중 온도는 23℃±5℃, 상대 습도는 50%±10%를 유지하였다. 상기의 반응기 내에서 측정된 시험 가스의 농도를 샘플(sample) 농도라고 정의한다.20 g of the resin composition for preparing a functional resin product of the present invention was injected into a reactor having a size of 5 L and ammonia (NH 3) having an initial concentration of 50 μmol / mol was injected into the reactor for 30 minutes and 60 minutes , 90 minutes and 120 minutes. At this time, the temperature was maintained at 23 ° C ± 5 ° C and the relative humidity was 50% ± 10% during the concentration measurement test. The concentration of the test gas measured in the reactor is defined as a sample concentration.
이와 별도로 시료가 없는 상태에서 상기의 온도 및 상대 습도가 유지된 상태에서 실험을 진행하고, 이때의 농도를 블랭크(blank) 농도라고 정의하였다. Separately, the experiment was carried out in a state in which the above temperature and relative humidity were maintained in the absence of the sample, and the concentration at this time was defined as a blank concentration.
상기의 각 시간대별로 시험 가스의 제거율(탈취율)을 아래의 수학식에 의해 계산하였다.The removal rate (deodorization rate) of the test gas for each time zone was calculated by the following equation.
상기의 같은 수학식 1에 의해 계산된 탈취율, 블랭크 농도 변화, 샘플 농도의 변화는 아래의 표 2와 같다.The change in deodorization rate, blank concentration, and sample concentration calculated by the above Equation 1 is shown in Table 2 below.
(mol/mol)Blank concentration
(mol / mol)
(mol/mol)Sample concentration
(mol / mol)
상기의 같은 수학식 1에 의해 계산된 탈취율, 블랭크 농도 및 샘플 농도의 시간 경과에 따른 변화는 도 1의 그래프와 같다. 구체적으로, 도 1에 도시된 바와 같이, 샘플 농도의 경우 시간이 경과될수록 낮아지고, 120분이 경과된 시점에서 샘플 농도가 "0"로 변화되지만, 블랭크 농도의 경우 시간과 무관하게 초기 농도를 계속 유지하는 것을 알 수 있다.The change in deodorization ratio, blank concentration, and sample concentration over time as calculated by the above Equation 1 is shown in the graph of FIG. Specifically, as shown in FIG. 1, the sample concentration decreases as the time elapses and the sample concentration changes to "0" at the time when 120 minutes have elapsed. However, in the case of the blank concentration, It can be seen that it maintains.
<실험예 2> 기능성 수지 제품 제조용 수지 조성물의 원적외선 방사 효과 실험<Experimental Example 2> Effect of far-infrared radiation effect of resin composition for functional resin product
37℃의 온도에서 FT-IR 분광계(spectrometer)를 이용하여 원적외선을 본 발명의 기능성 수지 제품 제조용 수지 조성물에 방사한 후 그 방사율과 방사 에너지를 측정하였습니다. 이러한 측정 결과는 아래의 표 3과 같다.Far-infrared rays were radiated to a resin composition for the production of the functional resin product of the present invention using an FT-IR spectrometer at a temperature of 37 ° C, and the emissivity and radiant energy thereof were measured. The results of these measurements are shown in Table 3 below.
(5∼20㎛)Emissivity
(5 to 20 占 퐉)
(W/㎡·㎛, 37℃)Radiant energy
(W / m 2 占 퐉, 37 占 폚)
37℃의 온도에서 FT-IR 분광계(spectrometer)를 이용하여 원적외선을 본 발명의 기능성 수지 제품 제조용 수지 조성물에 방사한 후 원적외선 방사량에 따른 그 방사율과 방사 에너지의 변화는 도 2 내지 도 3의 그래프와 같다. 구체적으로, 방사율은 도 2에 도시된 바와 같이, 원적외선 방사량의 변화에 무관하게 일정량을 유지하는 것을 알 수 있다. 또한, 방사 에너지는 도 3에 도시된 바와 같이, 원적외선 방사량의 변화에 따라 포물선 형태로 증가되는 것을 알 수 있다.Infrared radiation is radiated to the resin composition for producing a functional resin product of the present invention at a temperature of 37 ° C using an FT-IR spectrometer, the change in the emissivity and the radiant energy with respect to the far-infrared radiation amount is shown in the graphs of FIGS. 2 to 3 same. Specifically, as shown in FIG. 2, the emissivity is maintained at a certain level irrespective of the change in the far-infrared radiation dose. Further, as shown in Fig. 3, the radiant energy increases in a parabolic shape according to the variation of the far-infrared radiation dose.
<실험예 3> 기능성 수지 제품 제조용 수지 조성물을 이용한 밀폐 용기의 향균 효과 실험<Experimental Example 3> Antibacterial effect test of a sealed container using a resin composition for manufacturing a functional resin product
본 발명의 수지 조성물, 즉 고령토 도석과 옻 분말 가루를 기존의 합성수지, 예컨대 폴리프로필렌을 혼합하여 제조한 수지 조성물로 플라스틱 제품인 밀폐 용기를 제작한 후 향균 성능을 측정하기 위해 대장균 및 포도상구균을 제작된 밀폐 용기에 배양하였다. 그런 다음, 기 설정된 시간, 예컨대 24시간이 경과된 후 균의 증감 수지를 측정하였다. 그 결과는 아래의 표 4와 같다.The resin composition of the present invention, that is, a resin composition prepared by mixing kaolinite and lacquer powder with a conventional synthetic resin such as polypropylene, was prepared, and then a microcapsule was prepared from E. coli and Staphylococcus aureus And cultured in an airtight container. Then, after a lapse of a predetermined time, for example, 24 hours, the increase / decrease of bacteria was measured. The results are shown in Table 4 below.
상기의 표 4에서 알 수 있듯이, 본 발명의 밀폐 용기는 24시간 경과 후 99.9%로 대장균 및 포도상구균이 감소하는데 반해, 본 발명의 수지 조성물이 적용되지 않는 용기(블랭크)는 대장균의 경우 거의 감소되지 않고, 포도상구균의 경우 그 양이 더 증가하는 것을 알 수 있다.As can be seen from Table 4, the closed container of the present invention showed a decrease in the amount of Escherichia coli and Staphylococci by 99.9% after 24 hours, whereas the container (blank) to which the resin composition of the present invention was not applied decreased in the case of Escherichia coli And the amount of Staphylococcus aureus is further increased.
<실험예 4> 식품 밀폐 용기의 유해 중금속 검출 유무 실험<Experimental Example 4> Experiments on detection of harmful heavy metals in sealed food containers
본 발명의 수지 조성물, 즉 고령토 도석과 옻 분말 가루를 기존의 합성수지, 예컨대 폴리프로필렌을 혼합하여 제조한 수지 조성물로 플라스틱 제품인 밀폐 용기를 제작한 후 납 및 카드뮴과 같은 유해 중금속 검출 유무를 검사하였다. 구체적으로, 시료인 밀폐 용기를 산분해한 후 유도결합플라즈마-광학발광분광기를 이용하여 유해 중금속인 납과 카드뮴의 량을 분석하였다. 그 결과는 아래의 표 5와 같다.The resin composition of the present invention, that is, a resin composition prepared by mixing kaolinite and lacquer powder with a conventional synthetic resin such as polypropylene, was made into a closed container, and then the presence of harmful heavy metals such as lead and cadmium was detected. Specifically, the amount of lead and cadmium, which are harmful heavy metals, was analyzed using an inductively coupled plasma-optical emission spectroscope after acid decomposition of a sealed vessel as a sample. The results are shown in Table 5 below.
이상에서 본 발명의 대표적인 실시예들을 상세하게 설명하였으나, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 상술한 실시예에 대하여 본 발명의 범주에서 벗어나지 않는 한도 내에서 다양한 변형이 가능함을 이해할 것이다. 그러므로 본 발명의 권리범위는 설명된 실시예에 국한되어 정해져서는 안 되며, 후술하는 특허청구범위뿐만 아니라 이 특허청구범위와 균등한 것들에 의해 정해져야 한다.While the present invention has been particularly shown and described with reference to exemplary embodiments thereof, it is to be understood that the invention is not limited to the disclosed exemplary embodiments, but, on the contrary, . Therefore, the scope of the present invention should not be limited to the above-described embodiments, but should be determined by equivalents to the appended claims, as well as the appended claims.
Claims (7)
첨가제로 SiO2, MgO, CaO, Al2O3, K2O, Na2O, Fe2O2 및 Ge으로 이루어진 고령토 도석 및 옻 나무 분말을 포함하는 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물.
Resin,
Wherein the additive comprises kaolinite and lacquer powder consisting of SiO2, MgO, CaO, Al2O3, K2O, Na2O, Fe2O2 and Ge.
상기 첨가제로 활성탄을 더 포함하는 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물.
The method according to claim 1,
The resin composition for the production of a functional resin product, further comprising activated carbon as the additive.
상기 수지 제품은 물품의 포장용 필름 또는 보관 용기인 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물.
3. The method according to claim 1 or 2,
Wherein the resin product is a film for packaging the article or a storage container.
상기 기능성은 향균성, 탈취성, 유해전자파 차단성 및 원적외선 방사성으로 이루어진 군에서 선택되는 하나 이상인 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물.
3. The method according to claim 1 or 2,
Wherein the functional property is at least one selected from the group consisting of antibacterial property, deodorization property, harmful electromagnetic wave shielding property and far-infrared radiation property.
상기 고령토 도석은 SiO2, MgO, CaO, Al2O3, K2O, Na2O, Fe2O2 및 Ge으로 이루어진 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물.
75% by weight of polypropylene, 23.5-24% by weight of kaolinite and 1-1.5% by weight of lacquer powder,
Wherein the kaolinite is composed of SiO2, MgO, CaO, Al2O3, K2O, Na2O, Fe2O2 and Ge.
상기 고령토 도석은 SiO2, MgO, CaO, Al2O3, K2O, Na2O, Fe2O2 및 Ge으로 이루어진 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물.
75% by weight of polypropylene, 22.5-23% by weight of kaolinite, 1-1.5% by weight of lacquer powder and 0.5-1% by weight of activated carbon,
Wherein the kaolinite is composed of SiO2, MgO, CaO, Al2O3, K2O, Na2O, Fe2O2 and Ge.
상기 고령토 도석은 SiO2, MgO, CaO, Al2O3, K2O, Na2O, Fe2O2 및 Ge으로 이루어진 것을 특징으로 하는 기능성 수지 제품 제조용 수지 조성물.74% by weight of a copolyester resin containing corn starch, 25% by weight of kaolin stones and 1% by weight of lacquer powder,
Wherein the kaolinite is composed of SiO2, MgO, CaO, Al2O3, K2O, Na2O, Fe2O2 and Ge.