KR101697514B1 - Silicone material composition having good maintenance effect of freshness, and extruded product thereof - Google Patents
Silicone material composition having good maintenance effect of freshness, and extruded product thereof Download PDFInfo
- Publication number
- KR101697514B1 KR101697514B1 KR1020150099193A KR20150099193A KR101697514B1 KR 101697514 B1 KR101697514 B1 KR 101697514B1 KR 1020150099193 A KR1020150099193 A KR 1020150099193A KR 20150099193 A KR20150099193 A KR 20150099193A KR 101697514 B1 KR101697514 B1 KR 101697514B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- freshness
- material composition
- raw material
- present
- Prior art date
Abstract
Description
본 발명은 신선도 유지 기능이 부여된 실리콘 원료 조성물에 관한 것으로, 더욱 상세하게는 미러블형 실리콘 고무를 주재료로 사용하되 이에 식물유래 천연항균제, 광물질 혼합분말, 소디움계 첨가제, 유기산 및 천연유 성분을 소정량 함께 배합함으로써, 항균, 신선도 연장, 탈취 및 원적외선 방출의 기능을 동시에 구현하고 인체에도 무해하며 필요에 따라 각종 다양한 용도에 효율적으로 적용될 수 있는 친환경적인 실리콘 원료 조성물과 이의 압출성형품에 관한 것이다.
The present invention relates to a silicone raw material having a freshness-retaining function, and more particularly, to a silicone rubber composition comprising a silicone rubber as a main ingredient and a natural antimicrobial agent, a mineral mixture powder, a sodium additive, The present invention also relates to an environmentally friendly silicone raw material composition and an extrusion molded article thereof which can be effectively applied to various uses as needed, by simultaneously realizing functions of antibacterial, freshness extension, deodorization and far infrared ray emission by blending together a fixed amount.
환경의 변화에 따라 인체에 유해한 바이러스, 박테리아 등 인간의 건강을 위협하는 세균, 곰팡이류의 확산을 효과적으로 차단하고자 하는 노력이 지속되고 있다.Efforts to effectively prevent the spread of bacteria and fungi that threaten human health such as viruses and bacteria harmful to the human body due to changes in the environment are continuing.
예를 들어, 산업화에 따른 경제성장으로 식생활 문화가 변화함에 따라 포장식품에 대한 선호도가 증가하고 건강 및 웰빙에 대한 관심이 높아지고 있는 상황에서, 포장을 이용하여 신선도 연장 등 식품의 상품성을 지속적으로 유지시키기 위한 기능성 포장재에 관한 연구가 활발히 진행되고 있다.For example, as the food culture has changed due to the economic growth due to industrialization, the preference for packaged foods has increased and the interest in health and well-being has been increasing. Therefore, Researches on functional packaging materials have been actively carried out.
기능성 포장이란 "포장재의 여러 성질 중 최소한 한 가지 이상의 특수한 성질을 활용할 수 있는 포장재료"를 말하는 것인데, 식품의 경우 저장 유통기간을 연장시키고 상품성 확보를 위하여 포장 내에 어떤 목적을 가진 첨가제를 넣는 포장을 의미한다. 이러한 기능성 포장은 포장재의 특성에 따라서 그 기능을 세분화할 수 있으며 원재료가 가지고 있는 특성에 따라 포장 용도를 구체적으로 설정할 수 있다.Functional packaging refers to "a packaging material that can utilize at least one of the various properties of the packaging material." In the case of food, packaging for adding a certain purposeful additive into the package it means. These functional packages can be divided into functions according to the characteristics of the packaging materials and the packaging usage can be specifically set according to the characteristics of the raw materials.
다만, 국내에서 기능성 포장재는 선진국에 비해 아직까지 낮은 기술력을 보유하고 있는바, 현재 포장의 1차원적 단계에서 벗어나 기능성을 부여하는 포장 기술의 개발을 위해 투자 증가와 더불어 기술력 성장을 위한 활발한 노력이 진행되고 있다.However, in Korea, functional packaging materials still have low technological capabilities compared to advanced countries. In order to develop packaging technology that gives functionality beyond the one-dimensional stage of packaging, active efforts for technology growth along with investment increase It is progressing.
상기 기능성 포장재를 비롯한 각종 기능성 제품들은 주로 생활에 자주 사용되는 고분자 화합물인 플라스틱을 주원료로 하여 이에 기능성 성분을 소정량 첨가하는 방식으로 제조된다.Various functional products such as the above-mentioned functional packaging materials are prepared by adding a predetermined amount of a functional ingredient to a plastic material as a main material, which is a polymer compound frequently used in daily life.
구체적으로, 최근까지 플라스틱 제품에 무기계 항균제로서 은(Ag) 나노입자를 첨가 내지 분산시켜 항균 기능을 부여하려는 시도가 지속되고 있다.Specifically, until now, attempts have been made to add antimicrobial functions by adding or dispersing silver (Ag) nanoparticles as inorganic antibacterial agents in plastic products.
그러나, 은 나노입자는 항균력은 우수하지만 자체 위해성, 환경 위험성 및 고가의 재료로 인한 경제성 결여 등으로 실제 제품에는 제한적으로만 적용되는 수준에 그치고 있다. 또한 은 나노입자는 이를 플라스틱에 첨가하여 필름이나 PET 등의 실을 제조했을 경우 사용시 은의 색상이 변질되어 상품가치가 떨어지는 단점이 있다.However, silver nanoparticles are excellent in antibacterial activity, but they are limited to practical products due to their inherent risks, environmental risks and lack of economics due to expensive materials. Also, silver nanoparticles have a disadvantage in that, when they are added to plastics to produce a film such as a film or PET, the color of the silver is changed and the product value is lowered.
이러한 단점을 극복하기 위해, 자외선 차단제로 광범위하게 사용되어온 물질인 산화아연을 은 대신 사용하여 항균성을 부여하려는 기술이 제안된바 있다.To overcome these disadvantages, there has been proposed a technique for imparting antimicrobial properties by using zinc oxide, which is a substance widely used as a sunscreen agent, instead of silver.
그러나, 은과 비교했을 때 산화아연의 항균력은 만족할만한 수준에 이르지 못하고 있다. 또한 최근 선크림 등에 함유된 산화아연 성분이 자외선과 만나면 활성산소 분자를 방출시키게 되어 오히려 피부세포 및 DNA를 파괴한다는 연구결과가 보도된바 있고, 나노입자 산화아연을 흡입시 폐에 염증을 유발할 수 있다는 견해도 제시된바 있다(미국 미주리주립대학 연구진, SCCS 등). 즉 산화아연을 플라스틱에 첨가하여 항균제로서 사용하기에는 충분한 항균 기능 부여 및 인체 위해성과 관련하여 상당한 리스크가 존재하는 것이다.However, compared with silver, the antimicrobial activity of zinc oxide has not reached a satisfactory level. In addition, recently, zinc oxide contained in sunscreen and the like has been reported to cause the release of active oxygen molecules and ultimately destroys skin cells and DNA, and it has been reported that nanoparticle zinc oxide may cause lung inflammation Opinions were also presented (University of Missouri State University researchers, SCCS, etc.). That is, there is a considerable risk associated with imparting sufficient antimicrobial functions and harmful effects on the human body to use zinc oxide as an antimicrobial agent.
이에, 인체에 무해한 천연 물질을 기본으로 하되, 항균력이 매우 우수하여 식품 등의 신선도를 장기간 유지할 수 있고 기능성 포장재를 비롯한 다양한 제품에 광범위하게 다용도로 적용될 수 있는 친환경적인 고분자 기반 원료에 대한 개발이 요구되고 있다.
Therefore, it is necessary to develop eco-friendly polymer-based raw materials which can be widely applied to various products including functional packaging materials, which can maintain freshness of foods and the like for a long time by using natural substances harmless to human body, .
본 발명은 상기와 같은 종래기술의 문제점을 해결하고자 한 것으로, 항균, 신선도 유지, 탈취 및 원적외선 방출 등의 기능을 조화롭게 구현할 수 있고 인체에 무해하며 다양한 용도의 제품에 광범위하게 적용될 수 있는 새로운 형태의 실리콘 고무 기반 원료 조성물을 제공하는 것을 기술적 과제로 한다.
Disclosure of Invention Technical Problem [8] Accordingly, the present invention has been made keeping in mind the above problems occurring in the prior art, and it is an object of the present invention to provide a new type of device capable of harmoniously implementing functions such as antibacterial, freshness, deodorization and far infrared ray emission, It is a technical object to provide a silicone rubber-based raw material composition.
상기한 기술적 과제를 달성하고자, 본 발명은 (A) 식물유래 천연항균제 1.0~5.0 중량%; (B) 고령토, 규조토, 맥반석, 몬모릴로나이트, 밀러라이트, 백운모, 붕산석, 석영, 연옥, 운기석, 장석, 질석, 카펠레나이트, 펜틀란다이트, 해부석 및 활석 중에서 선택된 2종 이상으로서, Si, Fe, Ni, Al, B, K, Ca, Na 및 Mg를 함유하는 광물질 혼합분말 0.24~1.40 중량%; (C) 아황산수소나트륨(NaHSO3), 과탄산소다(2Na2CO3), 중탄산소다(NaHCO3), 염화나트륨(NaCl), 메타규산소다(Na2SiO3), 사붕산나트륨(Na2B4O7), 붕사(Na2B4O7·10H2O) 및 소다회(Na2CO3) 중에서 선택된 소디움계 첨가제 0.10~0.80 중량%; (D) 사과산, 말산, 구연산, 말레산, 아세트산, 호박산 및 푸마르산 중에서 선택된 유기산 0.14~1.40 중량%; (E) 신남알데히드(Cinnam aldehyde)를 함유하는 계피유(Cinnamon oil), 알릴이소티오시아네이트(Allyl isothiocyanate)를 함유하는 겨자유(Mustard oil), 유제놀 및 바닐린을 함유하는 정향유(Clove oil), 및 캡사이신(Capsaicin)을 함유하는 고추기름(Red pepper oil) 중에서 선택된 2종 이상의 천연유 0.02~1.40 중량%; 및 (F) 미러블형 실리콘 고무 90.0~98.5 중량%;를 포함하는 신선도 유지 기능이 부여된 실리콘 원료 조성물을 제공한다.In order to achieve the above technical object, the present invention provides a method of producing a microorganism, which comprises (A) 1.0 to 5.0% by weight of a plant-derived natural antibacterial agent; (B) at least two selected from kaolin, diatomaceous earth, elvanite, montmorillonite, millerite, muscovite, borate, quartz, nephrite, calcite, feldspar, vermiculite, capellenite, fterlandite, 0.24 to 1.40 wt% of a mineral mixed powder containing Fe, Ni, Al, B, K, Ca, Na and Mg; (C) sodium bisulfite (NaHSO 3), and sodium carbonate (2Na 2 CO 3), bicarbonate (NaHCO 3), sodium chloride (NaCl), meta-sodium silicate (Na 2 SiO 3), four sodium borate (Na 2 B 4 O 7), borax (Na 2 B 4 O 7 · 10H 2 O) and soda ash (Na 2 CO 3) sodium-based additive selected from the group consisting of 0.10 ~ 0.80% by weight; (D) from 0.14 to 1.40% by weight of an organic acid selected from malic acid, malic acid, citric acid, maleic acid, acetic acid, succinic acid and fumaric acid; (E) Cinnamon oil containing Cinnam aldehyde, Mustard oil containing Allyl isothiocyanate, Clove oil containing eugenol and vanillin, and 0.02 to 1.40% by weight of at least two natural oils selected from red pepper oil containing capsaicin; And (F) 90.0 to 98.5% by weight of a mirrorblock type silicone rubber.
아울러, 상기 (A) 식물유래 천연항균제는 허브 추출물, 방향유, 자몽 추출물, 피톤치드, 달맞이꽃 추출물, 향나무잎 추출물, 대나무잎 추출물, 소나무잎 추출물 및 가죽나무잎 추출물 중에서 선택된 1종 이상인 것을 특징으로 하는 신선도 유지 기능이 부여된 실리콘 원료 조성물을 제공한다.The natural antimicrobial agent derived from plant (A) is at least one selected from the group consisting of herb extract, aromatic oil, grapefruit extract, phytoncide, evening primrose extract, bamboo leaf extract, bamboo leaf extract, pine leaf extract, Thereby providing a silicon raw material composition having a holding function.
또한, 본 발명의 다른 측면으로, 상기 신선도 유지 기능이 부여된 실리콘 원료 조성물을 이용한 압출성형품을 제공한다.
According to another aspect of the present invention, there is provided an extrusion molded article using the silicone raw material composition having the freshness maintaining function.
본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물은 항균성(및 선택적 살균성)이 매우 우수하여 식품 등의 신선도 유지 기간을 크게 연장시킬 수 있다.The silicone raw material composition having the freshness-retaining function of the present invention is very excellent in antimicrobial activity (and selective bactericidal activity), and can greatly prolong the freshness maintenance period of foods and the like.
또한, 방사율 0.9 내외의 강력한 원적외선을 방출하며, 포름알데히드(HCHO), 톨루엔, 자일렌, VOCs 및 냄새 성분 등의 C-H 체인을 절단하여 우수한 탈취(방취) 기능을 발휘할 수 있다.In addition, it emits a strong far-infrared ray with an emissivity of about 0.9 and cuts C-H chains such as formaldehyde (HCHO), toluene, xylene, VOCs and odor components, and can exert excellent deodorizing function.
또한, 4대 중금속이 포함되지 않은 무독성 원료로서 인체에 무해하고 친환경적이며, 소정의 산화 생분해제를 첨가하면 사용 후 폐기시 자연계에서 생분해될 수 있는 장점이 있다.In addition, as a non-toxic raw material containing no 4 heavy metals, it is harmless to the human body and is eco-friendly. When a predetermined oxidative biodegradation agent is added, it can be biodegraded in the natural world when it is disposed of after use.
이를 토대로, 다양한 용도의 실리콘 고무 제품에 원하는 형태로 유연하게 적용될 수 있다.
Based on this, it can be flexibly applied to silicone rubber products of various applications in a desired form.
도 1은 본 발명에 따른 실리콘 원료 조성물을 사용하여 제조된 신선도 용기로 과채류를 포장한 경우, 저장시간에 따른 중량감소율 변화를 대조구와 비교하여 나타낸 그래프이다.
도 2는 본 발명에 따른 실리콘 원료 조성물을 사용하여 제조된 필름 형태 성형품의 항균력을 대조구와 비교하여 나타낸 도면이다.FIG. 1 is a graph showing a change in the weight loss rate with time of storage when the fruit and vegetables are packaged in a fresh container prepared using the silicone material composition according to the present invention, in comparison with a control.
2 is a view showing the antibacterial activity of a film-form molded article produced using the silicone raw material composition according to the present invention, in comparison with a control.
이하, 본 발명에 대해 상세히 설명한다.
Hereinafter, the present invention will be described in detail.
신선도 유지 기능이 부여된 실리콘 원료 조성물Silicone raw material composition having freshness keeping function
본 발명에 따른 신선도 유지 기능이 부여된 실리콘 원료 조성물은,The silicon raw material composition to which the freshness-retaining function according to the present invention is imparted,
(A) 식물유래 천연항균제 1.0~5.0 중량%;(A) 1.0 to 5.0% by weight of a plant-derived natural antibacterial agent;
(B) 고령토, 규조토, 맥반석, 몬모릴로나이트, 밀러라이트, 백운모, 붕산석, 석영, 연옥, 운기석, 장석, 질석, 카펠레나이트, 펜틀란다이트, 해부석 및 활석 중에서 선택된 2종 이상으로서, Si, Fe, Ni, Al, B, K, Ca, Na 및 Mg를 함유하는 광물질 혼합분말 0.24~1.40 중량%;(B) at least two selected from kaolin, diatomaceous earth, elvanite, montmorillonite, millerite, muscovite, borate, quartz, nephrite, calcite, feldspar, vermiculite, capellenite, fterlandite, 0.24 to 1.40 wt% of a mineral mixed powder containing Fe, Ni, Al, B, K, Ca, Na and Mg;
(C) 아황산수소나트륨(NaHSO3), 과탄산소다(2Na2CO3), 중탄산소다(NaHCO3), 염화나트륨(NaCl), 메타규산소다(Na2SiO3), 사붕산나트륨(Na2B4O7), 붕사(Na2B4O7·10H2O) 및 소다회(Na2CO3) 중에서 선택된 소디움계 첨가제 0.10~0.80 중량%;(C) sodium bisulfite (NaHSO 3), and sodium carbonate (2Na 2 CO 3), bicarbonate (NaHCO 3), sodium chloride (NaCl), meta-sodium silicate (Na 2 SiO 3), four sodium borate (Na 2 B 4 O 7), borax (Na 2 B 4 O 7 · 10H 2 O) and soda ash (Na 2 CO 3) sodium-based additive selected from the group consisting of 0.10 ~ 0.80% by weight;
(D) 사과산, 말산, 구연산, 말레산, 아세트산, 호박산 및 푸마르산 중에서 선택된 유기산 0.14~1.40 중량%;(D) from 0.14 to 1.40% by weight of an organic acid selected from malic acid, malic acid, citric acid, maleic acid, acetic acid, succinic acid and fumaric acid;
(E) 신남알데히드(Cinnam aldehyde)를 함유하는 계피유(Cinnamon oil), 알릴이소티오시아네이트(Allyl isothiocyanate)를 함유하는 겨자유(Mustard oil), 유제놀 및 바닐린을 함유하는 정향유(Clove oil), 및 캡사이신(Capsaicin)을 함유하는 고추기름(Red pepper oil) 중에서 선택된 2종 이상의 천연유 0.02~1.40 중량%; 및(E) Cinnamon oil containing Cinnam aldehyde, Mustard oil containing Allyl isothiocyanate, Clove oil containing eugenol and vanillin, and 0.02 to 1.40% by weight of at least two natural oils selected from red pepper oil containing capsaicin; And
(F) 미러블형 실리콘 고무 90.0~98.5 중량%;(F) 90.0 to 98.5% by weight of a mirror-bladed silicone rubber;
를 포함하는 것이다..
즉, 미러블형 실리콘 고무에 다양한 기능을 갖는 특정 성분들을 소정 함량으로 최적 배합한 것으로서, 이를 통해 항균, 신선도 연장, 탈취 및 원적외선 방출 등의 기능을 극대화할 수 있고, 다방면의 용도로 활용가능한 기능성 실리콘 고무를 원료 형태로 제공할 수 있다.
That is, it is possible to maximize functions such as antimicrobial, freshness, deodorization and far infrared ray emission through the use of a specific content of specific components having various functions in a mirrorblock type silicone rubber, The rubber can be provided in the form of raw material.
(A) 식물유래 천연항균제는 본 발명의 실리콘 원료 조성물에 항균 기능을 부여하는 주된 성분으로서, 모두 자연에서 유래된 인체에 무해한 친환경적인 성분이다.(A) The plant-derived natural antimicrobial agent is an eco-friendly ingredient harmless to the human body derived from nature as a main component that imparts an antimicrobial function to the silicone raw material composition of the present invention.
바람직한 일 구체예에서, 상기 식물유래 천연항균제로는 허브 추출물, 방향유(Essential oil), 자몽 추출물(특히, 자몽종자 추출물), 피톤치드(특히, 편백추출물에 포함되어 있는 피톤치드), 달맞이꽃 추출물, 향나무잎 추출물, 대나무잎 추출물, 소나무잎 추출물 및 가죽나무잎 추출물을 단독으로 또는 2종 이상 혼합하여 사용할 수 있다.In one preferred embodiment, the plant-derived natural antimicrobial agent is selected from the group consisting of herb extract, essential oil, grapefruit extract (especially grapefruit seed extract), phytoncide (especially phytoncide contained in the cottonseed extract), evening primrose oil, Extract, bamboo leaf extract, pine leaf extract and leather tree leaf extract may be used singly or in combination of two or more kinds.
상기 식물유래 천연항균제는 실리콘 원료 조성물 총 중량(= (A) 내지 (F) 성분의 총 중량; 이하 같음)에 대하여 1.0~5.0 중량%(예컨대, 2 중량%) 포함된다. 그 함량이 1.0 중량% 미만이면 항균성 부여 정도가 미미해질 수 있으며, 5.0 중량%를 초과하면 미러블형 실리콘 고무 등 기본 성분의 상대적 함량 감소로 제품에 기본적으로 요구되는 물성을 확보하기 어려워질 수 있다.
The plant-derived natural antimicrobial agent is contained in an amount of 1.0 to 5.0% by weight (e.g., 2% by weight) based on the total weight of the silicone raw material composition (= the total weight of the components (A) to (F)). When the content is less than 1.0% by weight, the degree of imparting antimicrobial properties may be insignificant. If the content is more than 5.0% by weight, the relative content of basic components such as the mirror-bladed silicone rubber may decrease.
본 발명에 있어서, (B) 내지 (E) 성분은 선도 유지제로서 기능하며, 실리콘 원료 조성물 총 중량에 대해 0.5~5.0 중량%(예컨대, 1 중량%) 포함된다.In the present invention, the components (B) to (E) function as a lead retention agent and are contained in an amount of 0.5 to 5.0% by weight (e.g., 1% by weight) based on the total weight of the silicone raw material composition.
(B) 광물질 혼합분말은 Si, Fe, Ni, Al, B, K, Ca, Na 및 Mg를 모두 함유하는 광물질 조합체로서, 항균(살균 기능 병행), 신선도 유지/연장, 탈취(방취, 악취제거) 및 원적외선 방출 기능을 발휘하게 하는 성분이다. 또한 천연 유래 물질로서 인체 및 생물체에 안전하며, 상온에서 장기 보관시에도 변질되지 않아 그 기능성을 지속적으로 유지할 수 있는 성분이다.(B) Mineral mixed powder is a mineral combination containing Si, Fe, Ni, Al, B, K, Ca, Na and Mg as antibacterial ) And a component that emits far-infrared radiation. It is a naturally derived material, safe for human and living organisms, and does not deteriorate even when stored at room temperature for a long period of time.
구체적으로, 상기 광물질 혼합분말은 식품 등의 드립 현상 및 스펀지 현상의 원인이 되는 에틸렌(C2H4) 가스를 제거(분해)하여 신선도 유지 기간을 크게 연장시킨다. 또한 상기 광물질 혼합분말은 강력한 원적외선을 방출(방사율(5∼20㎛, 37℃): 0.9 내외)하는데, 이러한 유익 진동파(예컨대, 6~12㎛)의 방출을 통해 유해 미생물 및 바이러스는 사멸시키는 반면, 발효균 등 유익균에 대해서는 성장촉진 및 활동성을 부여하는 선택적 살균(항균) 작용을 하게 된다. 아울러 상기 광물질 혼합분말은 포름알데히드(HCHO), 톨루엔, 자일렌, VOCs, 냄새 성분 등의 C-H 체인을 절단하는바 탁월한 탈취 기능을 발휘하게 한다.Specifically, the mineral mixed powder significantly removes (decomposes) ethylene (C 2 H 4 ) gas, which causes dripping and sponge of foods and the like, and greatly prolongs the freshness maintenance period. In addition, the mineral mixed powder emits a strong far infrared ray (emissivity (5 to 20 mu m, 37 DEG C): about 0.9). The harmful microorganisms and viruses are killed through the release of such beneficial vibration waves (for example, 6 to 12 mu m) On the other hand, beneficial bacteria such as fermenting bacteria are selectively sterilized (antibacterial) to promote growth and activity. In addition, the mineral mixed powder cleaves CH chains such as formaldehyde (HCHO), toluene, xylene, VOCs, and odor components, thereby exhibiting an excellent deodorizing function.
상기 광물질 혼합분말은 고령토, 규조토, 맥반석, 몬모릴로나이트, 밀러라이트, 백운모, 붕산석, 석영, 연옥, 운기석, 장석, 질석, 카펠레나이트, 펜틀란다이트, 해부석 및 활석 중 2종 이상을 분말화하고 이를 균일하게 혼합(예컨대, 같은 중량비율로 혼합)함으로써 구비될 수 있다. 여기서, 다공성인 광물질을 포함하여 혼합분말을 구성하면 에틸렌 가스의 분해와 더불어 흡수 또한 가능해지는바 에틸렌 가스를 더욱 효과적으로 빠르게 제거할 수 있다. 또한 붕소(B) 원소를 부여하기 위한 광물로서 상기 붕산석 및 카펠레나이트 이외에 다토석, 댄버라이트, 듀모르티에석, 뤼네부르자이트, 마난도나이트, 베이커라이트, 부석, 세렌디바이트, 시알레사이드, 전기석, 하이알로테카이트, 호밀라이트 등을 사용할 수 있다.Wherein the mineral mixed powder is at least two kinds of powders selected from the group consisting of kaolin, diatomaceous earth, elvanite, montmorillonite, millerite, muscovite, borate, quartz, nephrite, ungas, feldspar, vermiculite, capellanite, And mixing them uniformly (for example, mixing them at the same weight ratio). Here, when the mixed powder including the porous inorganic material is constituted, it is possible to absorb the ethylene gas as well as the decomposition, so that the ethylene gas can be removed more effectively and quickly. In addition to the boron oxide and capelenite as the mineral for imparting the boron (B) element, it is also possible to use, in addition to the boron oxide and capelenite, Reside, tourmaline, hyaluronic acid, rye light and the like can be used.
상기 광물질 혼합분말의 크기는 배합되는 다른 성분들의 구체적인 종류에 따라 적절히 조절될 수 있으며, 예를 들어 1nm~10㎛ 정도의 크기로 각 광물질을 분쇄 및 혼합하여 사용할 수 있다.The size of the mineral mixed powder can be appropriately adjusted according to the specific kind of the other components to be mixed. For example, each of the minerals may be pulverized and mixed with a size of about 1 nm to 10 탆.
상기 광물질 혼합분말은 실리콘 원료 조성물 총 중량에 대하여 0.24~1.40 중량% 포함된다. 그 함량이 0.24 중량% 미만이면 전술한 신선도 유지 기능 등이 충분히 부여되지 않아 본 발명이 추구하는 목적을 달성하기 어려워지며, 1.40 중량%를 초과하면 성형품의 외관 등에 좋지 않은 영향을 미칠 수 있다.The mineral mixed powder is contained in an amount of 0.24 to 1.40 wt% based on the total weight of the silicone raw material composition. If the content is less than 0.24% by weight, the above-described freshness-retaining function and the like are insufficiently imparted, so that it is difficult to achieve the object pursued by the present invention, and if it exceeds 1.40% by weight, appearance and the like of the molded article may be adversely affected.
상기 광물질 혼합분말에는 필요에 따라 다른 층상규산염 광물인 엽랍석, 사문석, 온석면, 흑운모, 어안석, 녹니석 등이 추가로 포함될 수 있는바, 이러한 다공질 광물의 추가에 따라 에틸렌 가스의 흡착을 더욱 촉진시킬 수 있다.
The mineral mixed powder may further contain other layered silicate minerals such as leaf clay, serpentinite, zeolite, biotite, ophthalmic stone, chlorite and the like. If the porous mineral is further added, the adsorption of ethylene gas can be further promoted have.
(C) 소디움계 첨가제는 세균, 잔류 환경유해 물질 및 냄새 제거 기능을 보완하는 성분으로서, 산을 중화시켜 pH를 적절히 조절하고, 제품의 독성을 완화하며, 조성물의 원활한 배합을 보조하며, 유색 첨가제 투입에 따라 실리콘 고무 고유의 색상이 과도하게 변질되는 것을 방지하는 역할도 일부 수행하는 성분이다.(C) The sodium-based additive is a component that complements bacteria, residual environmental harmful substances and deodorizing function. It neutralizes the acid to appropriately adjust the pH, alleviate the toxicity of the product, assists in the smooth composition of the composition, It is also a component that performs some of the role of preventing excessive color change of inherent silicone rubber according to input.
본 발명에서는, 상기 소디움계 첨가제로서 아황산수소나트륨(Sodium hydrogensulfite; NaHSO3), 과탄산소다(Sodium percarbonate; 2Na2CO3 또는 2Na2CO3-3H2O2), 중탄산소다(Sodium bicarbonate; NaHCO3), 염화나트륨(NaCl), 메타규산소다(Na2SiO3), 사붕산나트륨(Na2B4O7), 붕사(Na2B4O7·10H2O) 또는 소다회(Soda ash; Na2CO3)를 사용한다.In the present invention, as the sodium-based additive, sodium hydrogensulfite (NaHSO 3 ), sodium percarbonate (2Na 2 CO 3 or 2Na 2 CO 3 -3H 2 O 2 ), sodium bicarbonate (NaHCO 3), sodium chloride (NaCl), meta-sodium silicate (Na 2 SiO 3), four sodium borate (Na 2 B 4 O 7) , borax (Na 2 B 4 O 7 · 10H 2 O) or soda ash (soda ash; Na 2 CO 3 ) is used.
상기 소디움계 첨가제는 실리콘 원료 조성물 총 중량에 대하여 0.10~0.80 중량% 포함된다. 그 함량이 0.10 중량% 미만이면 항균 및 탈취 기능을 극대화하기 어렵거나 다른 유색 성분의 상대적 함량 증가에 따라 제품의 상품성이 저하될 수 있으며, 0.80 중량%를 초과하면 원치않는 과도한 발포 현상 등으로 인해 작업에 불리한 영향을 미치거나 세포조직에 자극을 줄 수 있다.
The sodium based additive is included in an amount of 0.10 to 0.80% by weight based on the total weight of the silicone raw material composition. If the content is less than 0.10% by weight, it is difficult to maximize the antibacterial and deodorizing function, or the merchantability of the product may deteriorate due to the increase of the relative content of other colored components. If the content exceeds 0.80% by weight, Lt; RTI ID = 0.0 > cell tissue. ≪ / RTI >
(D) 유기산(예컨대, 구연산)은 탈취 효과를 극대화하는 성분으로서, 유색 첨가제 투입에 따라 실리콘 고무 고유의 색상이 과도하게 변질되는 것을 방지하는 역할도 일부 수행하는 성분이다.(D) The organic acid (for example, citric acid) is a component that maximizes the deodorizing effect, and is a component that partially prevents the intrinsic color of the silicone rubber from being altered by the addition of the coloring additive.
본 발명에서는, 상기 유기산으로서 사과산, 말산, 구연산, 말레산, 아세트산, 호박산 또는 푸마르산을 사용한다.In the present invention, malic acid, citric acid, maleic acid, acetic acid, succinic acid or fumaric acid is used as the organic acid.
상기 유기산은 실리콘 원료 조성물 총 중량에 대하여 0.14~1.40 중량% 포함된다. 그 함량이 0.14 중량% 미만이면 탈취 기능을 극대화하기 어려워질 수 있으며, 1.40 중량%를 초과하면 pH 저하 및 광물질 혼합분말 등 다른 성분들의 상대적 함량 감소에 따른 불이익이 발생할 수 있다.
The organic acid is contained in an amount of 0.14 to 1.40 wt% based on the total weight of the silicone raw material composition. If the content is less than 0.14% by weight, it may become difficult to maximize the deodorizing function. If the content is more than 1.40% by weight, a decrease in pH and a decrease in the relative content of other components such as a mineral mixture powder may occur.
(E) 천연유는 전술한 광물질 혼합분말과의 조합을 통한 상승적 작용에 따라 실리콘 원료 조성물의 항균성 및 신선도 유지성을 더욱더 높이게 하는 천연유래 기름 성분이다.(E) Natural oil is a natural-derived oil component that further enhances the antimicrobial and freshness-retaining properties of the silicone raw material composition in accordance with synergistic action through combination with the above-mentioned mineral mixed powder.
본 발명에서는, 상기 천연유로서 신남알데히드(Cinnam aldehyde)를 함유하는 계피유(계피 정유; Cinnamon oil), 알릴이소티오시아네이트(Allyl isothiocyanate)를 함유하는 겨자유(Mustard oil), 유제놀 및 바닐린을 함유하는 정향유(정향 정유; Clove oil), 및 캡사이신(Capsaicin)을 함유하는 고추기름(Red pepper oil)을 2종 이상 혼합하여 사용한다. 여기서, 혼합비율은 천연유 100 중량부를 기준으로 계피유 20~50 중량부, 겨자유 10~30 중량부, 정향유 0~40 중량부 및 고추기름 0~40 중량부 정도가 바람직하다.In the present invention, it is preferable that cinnamon oil, cinnamon oil, allyl isothiocyanate, mustard oil, eugenol and vanillin containing cinnamaldehyde are used as the natural oil, And red pepper oil containing capsaicin are mixed with each other and used. The blending ratio is preferably 20 to 50 parts by weight of cinnamon oil, 10 to 30 parts by weight of mustard oil, 0 to 40 parts by weight of clove oil and 0 to 40 parts by weight of red pepper oil based on 100 parts by weight of natural oil.
상기 천연유는 실리콘 원료 조성물 총 중량에 대하여 0.02~1.40 중량% 포함된다. 그 함량이 0.02 중량% 미만이면 항균성 및 신선도 유지성을 극대화하기 어려워질 수 있으며, 1.40 중량%를 초과하면 충분한 항균성이 부여된 상태에서 불필요하게 제조비용만 증가하거나 향이 강하여 제품 자체에 이취감이 생기거나 식품 포장의 경우 향이 전이되어 식품 고유의 풍미를 흐릴 수 있다.
The natural oil is contained in an amount of 0.02 to 1.40 wt% based on the total weight of the silicone raw material composition. When the content is less than 0.02% by weight, it may be difficult to maximize the antimicrobial activity and freshness retention. If the content is more than 1.40% by weight, the product is unnecessarily increased in the state of sufficient antimicrobial activity, In the case of food packaging, the fragrance may be transferred and the original flavor of the food may be blurred.
(F) 미러블형 실리콘 고무(Millable silicone rubber; HCR)는 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물을 구성하는 베이스 고분자 재료로서, 내열성이 탁월하고 내한성, 내약품성 및 내유성 등의 특성이 우수하며, 무독성 소재라는 장점이 있다.(F) Millable silicone rubber (HCR) is a base polymer material constituting a silicone raw material composition having a freshness-retaining function of the present invention, and is excellent in heat resistance, excellent in cold resistance, chemical resistance and oil resistance It has the advantage of non-toxic material.
상기 미러블형 실리콘 고무는 고온경화용(열가교형) 실리콘 고무의 일종으로, 실록산 단위 5,000~10,000 정도의 고중합도를 갖는 선상 폴리오가노실록산을 주원료로 하여 실리카계의 보강성 충전제 및 각종 특성을 부여하기 위한 첨가제를 배합하여 베이스 컴파운드를 제조한 후, 가교제를 첨가하여 가열 경화하는 형태의 고무이다.The mirror-bladed silicone rubber is a type of high-temperature curing (heat-crosslinkable) silicone rubber, and is composed of a linear polyorganosiloxane having a high degree of polymerization of about 5,000 to 10,000 in terms of siloxane units as a main raw material, To prepare a base compound, and then adding a cross-linking agent to heat and cure the rubber.
본 발명에 있어서, 상기 미러블형 실리콘 고무로는 시중에 통상적으로 유통되는 종류의 것을 특별한 제한없이 입수하여 사용할 수 있다.In the present invention, the above-mentioned mirror-bladed silicone rubber can be used without any particular limitation, and can be used by being commercially available in the market.
상기 미러블형 실리콘 고무는 실리콘 원료 조성물 총 중량에 대하여 90.0~98.5 중량%(예컨대, 97 중량%) 포함된다. 그 함량이 90.0 중량% 미만이면 최종 제품의 내열성, 내한성, 내후성, 탄성 등 기본적인 요구물성 저하를 유발할 수 있으며, 98.5 중량%를 초과하면 상기 (A) 내지 (E) 성분의 첨가량 감소로 본 발명이 목적으로 하는 기능성을 부여하기 어려워질 수 있다.
The mirror-bladed silicone rubber comprises 90.0-98.5 wt% (e.g., 97 wt%) based on the total weight of the silicone raw composition. If the content is less than 90.0% by weight, basic properties such as heat resistance, cold resistance, weather resistance and elasticity of the final product may be deteriorated. If the content exceeds 98.5% by weight, the addition amount of the components (A) to (E) It may be difficult to impart the desired functionality.
또한, 본 발명에서는 상기 미러블형 실리콘 고무가 고온에서 원활히 경화되도록 가교제(경화제) 역할을 하는 유기 과산화물 성분, 특히 디큐밀 퍼옥사이드를 추가로 포함할 수 있다.In addition, the present invention may further comprise an organic peroxide component, in particular, dicumyl peroxide, which acts as a crosslinking agent (hardening agent) so that the mirror-bladed silicone rubber can be cured smoothly at a high temperature.
상기 디큐밀 퍼옥사이드는 미러블형 실리콘 고무 100 중량부에 대하여 0.01~1 중량부 정도 포함되는 것이 바람직하다. 디큐밀 퍼옥사이드의 함량이 0.01 중량부 미만이면 미러블형 실리콘 고무의 원활한 가교가 있어나지 않을 수 있으며, 1 중량부를 초과하면 필요한 정도를 넘어 불필요한 제조비용 상승을 불러올 수 있다.
The dicumyl peroxide is preferably contained in an amount of 0.01 to 1 part by weight based on 100 parts by weight of the mirror-bladed silicone rubber. When the content of the dicumyl peroxide is less than 0.01 part by weight, the mirror-bladed silicone rubber may not be smoothly crosslinked. If the content is more than 1 part by weight, the unnecessary manufacturing cost may be increased.
이외에도, 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물에는 가공성, 제품 안정성, 제품의 성능 등을 향상시키기 위하여 첨가제로 사용될 수 있는 널리 알려진 다양한 성분들이 소정의 양으로 첨가될 수 있다. 예를 들어, 접합력을 강화시키고 반발력을 감소시키기 위해 표면처리제를 소정의 양으로 첨가할 수 있으며, 또한 제품의 사용기간 중 고분자의 물리적, 화학적 성질을 유지하여 분해되지 않도록 하기 위하여 안정제를 소정의 양으로 첨가할 수 있다.In addition, in the silicone raw material composition having the freshness-retaining function of the present invention, various well-known various ingredients that can be used as additives for improving processability, product stability, product performance and the like can be added in predetermined amounts. For example, a surface treatment agent may be added in a predetermined amount to enhance bonding strength and reduce repulsion, and a stabilizer may be added in a predetermined amount so as to maintain the physical and chemical properties of the polymer during use, . ≪ / RTI >
또한, 화합물의 변형 및 탄화를 방지하여 기계적 물성 및 가공 안정성을 유지하기 위해 분자량이 2,000 미만인 선형 유기 열안정제 및 산화방지제(irganox 1010 또는 1076 계열)를 통상의 방법에 따라 소정의 양으로 첨가하는 것 또한 바람직하다.Further, in order to prevent deformation and carbonization of the compound to maintain mechanical properties and processing stability, a linear organic thermal stabilizer and an antioxidant (irganox 1010 or 1076 series) having a molecular weight of less than 2,000 are added in a predetermined amount according to a conventional method It is also preferred.
아울러, 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물에는 본 발명의 목적을 벗어나지 않는 범위 안에서 필요에 따라 수용성 금속염이 소량 첨가될 수 있다. 이러한 수용성 금속염의 첨가는 항균 기능의 보조, 포장재에 존재할 수 있는 독성 물질의 분해 및 원적외선 발생의 원활화 등에 도움을 줄 수 있다.In addition, a small amount of a water-soluble metal salt may be added to the silicone raw material composition to which the freshness-retaining function of the present invention is applied, as needed, without departing from the object of the present invention. The addition of such a water-soluble metal salt can assist in antimicrobial function, decomposition of toxic substances present in the packaging material, and facilitation of generation of far-infrared rays.
상기 수용성 금속염으로는 염화마그네슘, 염화알루미늄, 염화금, 탄산칼륨, 붕사 및 염화제일철을 단독으로 또는 2종 이상 혼합하여 사용할 수 있다.As the water-soluble metal salt, magnesium chloride, aluminum chloride, chloride, potassium carbonate, borax and ferrous chloride may be used alone or in combination of two or more.
상기 수용성 금속염은 (A) 내지 (F) 성분 100 중량부에 대하여 0.01~0.05 중량부 첨가되는 것이 적절하다. 그 함량이 0.01 중량부 미만이면 이의 첨가에 따라 구현하고자 하는 효과가 미미해질 수 있으며, 0.05 중량부를 초과하면 광물질 혼합분말, 천연유와 같은 본 발명의 주요 기능성 성분들의 상대적 함량 감소에 따라 원치않는 효과가 발생할 수 있다.The water-soluble metal salt is suitably added in an amount of 0.01 to 0.05 part by weight based on 100 parts by weight of the components (A) to (F). If the content is less than 0.01 part by weight, the effect to be achieved may be insignificant depending on the addition thereof. If the content is more than 0.05 part by weight, the relative content of the main functional ingredients of the present invention such as mineral powder, May occur.
또한, 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물에는 본 발명의 목적을 벗어나지 않는 범위 안에서 자외선 차단제, 대전방지제, 유연제, 흡수제, 흡습제, 탈취제, 발수제, 방오재, 방염재 등이 더욱 첨가(예컨대, (A) 내지 (F) 성분 100 중량부에 대하여 0.01~0.05 중량부)될 수 있다.The silicone raw material composition to which the freshness-retaining function of the present invention is imparted may further contain additives such as a sunscreen agent, an antistatic agent, a softener, an absorbent, a hygroscopic agent, a deodorant, a water repellent agent, For example, 0.01 to 0.05 part by weight based on 100 parts by weight of the components (A) to (F).
아울러, 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물에는 탄산칼슘(예컨대, 2~5㎛ 크기), 왁스(예컨대, PE 왁스) 및 지방산(예컨대, 스테아린산칼슘, 리놀레산 및 미리스트올레산)이 더욱 첨가될 수 있다. 여기서, 상기 탄산칼슘은 제품의 내구성을 강화시키는 역할, 상기 지방산은 미러블형 실리콘 고무의 분해를 가속화하고 열분해 및 광분해를 촉진시키는 역할 내지 재료의 흐름성을 좋게 하여 원활한 생산을 가능하게 하는 활제 역할을 할 수 있다.
In addition, calcium carbonate (for example, having a size of 2 to 5 mu m), wax (e.g., PE wax), and fatty acids (e.g., calcium stearate, linoleic acid and misteriolenoic acid) Can be added. Here, the calcium carbonate serves to enhance the durability of the product. The fatty acid accelerates the decomposition of the mirror-type silicone rubber, promotes thermal decomposition and photodegradation, improves the flow of the material, and serves as a lubricant enabling smooth production can do.
본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물을 제조하는 방법은 특별히 제한되지 않으며, 소정의 분쇄기 및 믹서 등을 이용해 전술한 성분들을 (필요시 2~5㎛ 정도로 분쇄한 다음) 정해진 배합비로 투입한 후 교반하면서 균일하게 혼합하여 압출성형을 위한 조성물(혼합물)을 제조할 수 있다.
The method of producing the silicone raw material composition having the freshness-retaining function of the present invention is not particularly limited, and the above-mentioned components may be pulverized to a particle size of about 2 to 5 탆 by using a predetermined pulverizer and a mixer, (Mixture) for extrusion molding can be produced by uniformly mixing with stirring.
신선도 유지 기능이 부여된 실리콘 원료 조성물을 이용한 압출성형품Extrusion molding product using silicone raw material composition having freshness keeping function
본 발명의 다른 측면에 따르면, 전술한 신선도 유지 기능이 부여된 실리콘 원료 조성물의 압출성형품이 제공된다.According to another aspect of the present invention, there is provided an extrusion molded article of a silicone raw material composition having the freshness keeping function as described above.
본 발명에 따른 신선도 유지 기능이 부여된 실리콘 원료 조성물을 압출성형하는 방법은 특별히 제한되지 않으며, 예를 들어 준비된 조성물을 압출기(예컨대, 트윈 익스트루더)를 이용하여 압출한 후 송풍 건조하여 수행할 수 있다.The method of extruding the silicone raw material composition having the freshness-retaining function according to the present invention is not particularly limited. For example, the prepared composition is extruded using an extruder (for example, twin extruder) .
압출시에는 압출기(예컨대, 트윈 익스트루더)를 통한 반응온도 100~300℃, 스크류 회전속도 300~800RPM의 조건에서 수행하는 것이 적절하다. 반응온도가 100℃ 미만이면 미러블형 실리콘 고무의 고온가교가 원활히 진행되지 않을 수 있으며, 300℃를 초과하면 식물유래 천연항균제 등 첨가 성분의 기능성 저하를 유발할 수 있다. 또한 스크류 회전속도가 300RPM 미만이면 생산성이 나쁠 뿐만 아니라 충분한 혼합 및 반응이 어려워질 수 있으며, 800RPM을 초과하면 스크류 내부 압력이 상승하고 압력에 의한 온도 상승으로 인해 식물유래 천연항균제, 천연유 등 자연 유래 첨가 성분의 기능성 저하를 유발할 수 있다.At the time of extrusion, it is appropriate to carry out the extrusion through a extruder (for example, twin extruder) at a reaction temperature of 100 to 300 ° C and a screw rotation speed of 300 to 800 RPM. If the reaction temperature is less than 100 ° C, the high-temperature crosslinking of the mirror-bladed silicone rubber may not proceed smoothly. If the reaction temperature exceeds 300 ° C, the functionality of the added components such as natural antimicrobial agents derived from plants may be lowered. In addition, when the rotational speed of the screw is less than 300 RPM, productivity may be poor, and sufficient mixing and reaction may become difficult. If the screw rotation speed is higher than 800 RPM, the internal pressure of the screw rises and the temperature rises due to pressure. It may cause a decrease in functionality of the additive component.
또한, 제조되는 성형품에 특별한 컬러를 부여하고자 하는 경우 호퍼에 염료나 안료 또는 이를 함유하는 마스터 배치를 함께 투입한 후 생산할 수 있으며, 그 함량은 원하는 색상 구현에 따라 적절히 조절하여 투입할 수 있다.
When a special color is to be imparted to a molded article to be produced, the hopper may be produced by adding a dye or a pigment or a master batch containing the same to the hopper, and the content thereof may be appropriately adjusted according to the desired color implementation.
이렇게 제조된 본 발명의 압출성형품은 항균성이 우수한 천연 성분이 다량 함유되어 있어 신선도 유지 기능 및 탈취 기능이 매우 뛰어나며, 내열성, 탄성 등 성형품의 물성 또한 우수한 특성을 나타낸다. 또한 시트, 용기, 케이스, 식기 등 다양한 용도의 실리콘 고무 최종 제품으로 탄생할 수 있다. 예를 들어, 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물은 신선식품, 조리된 음식, 김밥, 과채류, 발효식품, 쌀 등의 포장재; 바이오 위생백, 위생장갑, 롤백, 신선도 봉투 등; 주방용, 유아용 등의 다양한 제품; 코팅제; 펄프 몰드; 자동차 내장재, 시트 등의 코팅재; 환경호르몬 저감형 접착제; 건축 및 토목 분야의 내장재, 바닥재; 등의 제조 원료로서 매우 적합하게 사용될 수 있다.
The extrusion molded article of the present invention thus produced exhibits excellent properties of moldability such as heat resistance and elasticity because it contains a large amount of natural components having excellent antimicrobial properties and is excellent in freshness retaining function and deodorizing function. In addition, it can be produced as a final product of silicone rubber for various purposes such as sheets, containers, cases and tableware. For example, the silicone raw material composition having the freshness-retaining function of the present invention can be used as a packaging material for fresh foods, cooked foods, kimbap, fruit and vegetables, fermented foods, and rice; Bio hygienic bags, sanitary gloves, roll bags, freshness bags, etc .; Various products such as kitchens, infants, etc; Coating agents; Pulp mold; Coating materials such as automobile interior materials and sheets; Environmental hormone-reducing adhesives; Interior and floor coverings for construction and civil engineering; And the like can be suitably used.
이하, 실시예를 통해 본 발명을 보다 구체적으로 설명한다. 그러나 이들 실시예는 본 발명의 이해를 돕기 위한 것일 뿐 어떠한 의미로든 본 발명의 범위가 이들 실시예로 한정되는 것은 아니다.
Hereinafter, the present invention will be described more specifically by way of examples. However, these examples are provided only for the understanding of the present invention, and the scope of the present invention is not limited to these examples in any sense.
실시practice 예 1: 신선도 유지 기능이 부여된 실리콘 원료 조성물Example 1: Silicone raw material composition having freshness maintaining function 을 이용한 압출성형품 제조For extrusion molding
(A) 시판의 허브 추출물 천연항균제 2.0 중량%; (B) 규조토, 장석, 운기석, 펜틀란다이트(니켈 광물) 및 붕산석(붕소 광물) 분말이 동일한 중량비율로 포함된 광물질 혼합분말 0.6 중량%; (C) 중탄산소다(NaHCO3) 0.1 중량%; (D) 구연산 0.2 중량%; (E) 계피유, 겨자유 및 고추기름이 4:3:3의 중량비율로 포함된 천연유 0.1 중량%; 및 (F) 시판의 미러블형 실리콘 고무 97.0 중량%;에 디큐밀 퍼옥사이드를 미러블형 실리콘 고무 100 중량부 기준 0.01 중량부 첨가하여, 고속 교반기에 투입한 후 400RPM으로 교반하여 혼합물을 생성하였다.(A) 2.0% by weight of commercially available herb extract natural antibacterial agent; (B) 0.6% by weight of a mineral mixed powder containing diatomite, feldspar, unguicite, feldramite (nickel mineral) and borate (boron mineral) powder in the same weight ratio; (C) sodium bicarbonate (NaHCO 3) 0.1% by weight; (D) 0.2% by weight citric acid; (E) 0.1% by weight natural oil containing cinnamon oil, mustard oil and pepper oil in a weight ratio of 4: 3: 3; And (F) 97.0% by weight of a commercially available mirror-bladed silicone rubber; 0.01 parts by weight of dicumyl peroxide based on 100 parts by weight of a mirror-bladed silicone rubber was added to a high-speed stirrer and stirred at 400 RPM to produce a mixture.
(* 상기 모든 "중량%"는 (A) 내지 (F) 성분의 중량 총합을 100 중량%로 보았을 때의 수치임.)(* All "weight%" is a value when the weight sum of the components (A) to (F) is taken as 100% by weight)
얻어진 혼합물을 색상 구현을 위한 소정량의 염료와 함께 호퍼에 투입한 후 220℃의 조건으로 압출성형하여, 캡과 본체로 구성된 식품 포장용 밀폐 용기를 제조하였다.
The resulting mixture was put into a hopper together with a predetermined amount of dye for color implementation, and extruded at 220 ° C to prepare a sealed container for food packaging consisting of a cap and a body.
실시예 2: 신선도 유지 기능이 부여된 실리콘 원료 조성물을 이용한 압출 필름 제조Example 2: Production of an extruded film using a silicone raw material composition having a freshness maintaining function
얻어진 혼합물을 압출성형(160~180℃)하여 필름 형태로 얇게 제조한 점을 제외하고는, 실시예 1과 동일하다.
Except that the obtained mixture was extrusion-molded (160 to 180 占 폚) and made thin as a film.
비교예 1: 종래의 범용 식품 포장 PP 용기Comparative Example 1: Conventional general-purpose food packaging PP container
시중의 범용 식품 포장 PP 용기를 입수하여, 대조구로 삼았다.
Commercially available food packaging PP containers were obtained and used as a control.
비교예 2: 종래의 범용 식품 포장 PE 필름Comparative Example 2: Conventional general-purpose food packaging PE film
시중의 범용 식품 포장 PE 필름을 입수하여, 대조구로 삼았다.
A commercially available food packaging PE film was obtained and used as a control.
실험예 1: 독성 테스트Experimental Example 1: Toxicity test
실시예 1의 식품 포장용 용기에 대해 "식품공전 제 7. 기구 및 용기포장의 기준 및 규격"에 의거하여 독성 테스트를 하고, 그 결과를 하기 표 1에 나타내었다.The food packaging container of Example 1 was subjected to the toxicity test according to " Standards and Specifications of the Food and Drug Administration 7. Apparatus and Container Packaging ", and the results are shown in Table 1 below.
[표 1][Table 1]
상기 표 1에서 보듯이, 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물로부터 제조된 용기는 4대 중금속이 검출되지 않았을 뿐만 아니라 "식품공전 제 7. 기구 및 용기포장의 기준 및 규격"을 모두 충족하여 인체에 무해함을 알 수 있다.
As shown in Table 1, not only the four heavy metals were detected in the container made from the silicone raw material composition having the freshness-retaining function of the present invention, but all of the standards and specifications of the food packing device And it is found that it is harmless to human body.
실험예 2: 신선도 연장 테스트Experimental Example 2: Freshness Extension Test
실시예 1 및 비교예 1의 식품 포장용 용기를 이용하여 사과 및 상추를 각각 진공포장한 후 저장시간 경과에 따른 중량감소율 변화를 측정하여, 그 결과를 도 1에 나타내었다.The packaged food containers of Example 1 and Comparative Example 1 were individually packaged in a vacuum packed state, and the changes in the weight loss rate with the passage of time were measured. The results are shown in FIG.
도 1에서 보듯이, 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물로부터 제조된 용기는 포장 이틀 경과 후에도 과채류 최초 중량의 95% 이상을 유지할 정도로 신선도 연장 효과가 우수하였다. 반면 비교예 1의 경우 저장시간 경과에 따라 과채류의 중량이 크게 감소하여 장시간 신선도를 유지할 수 없었다.
As shown in FIG. 1, the container prepared from the silicone raw material composition having the freshness-retaining function of the present invention was excellent in freshness extension effect to maintain 95% or more of the initial weight of the fruit-vegetables even after two days of packing. On the other hand, in the case of Comparative Example 1, the weight of the fruit vegetables was greatly decreased according to the storage time, and thus the freshness could not be maintained for a long time.
실험예 3: 항균력 테스트Experimental Example 3: Antimicrobial Test
실시예 2 및 비교예 2의 식품 포장용 필름에 대해 항균(살균) 시험을 실시하고, 그 결과를 도 2에 나타내었다.Antibacterial (sterilization) tests were conducted on the films for food packaging of Example 2 and Comparative Example 2, and the results are shown in Fig.
* 항균시험(JIS Z 2801: 필름 밀착법) : 세균 수/cm2, 항균 활성치 log* Antibacterial test (JIS Z 2801: film adhesion method): Number of bacteria / cm 2 , value of antibacterial activity log
도 2에서 보듯이, 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물로부터 제조된 필름의 경우 비교예 2 대비 항균력이 매우 우수함을 알 수 있다.
As shown in FIG. 2, it can be seen that the film prepared from the silicone raw material composition having the freshness-retaining function of the present invention exhibits excellent antibacterial activity compared to Comparative Example 2. [
실험예 4: 탈취 효과 및 원적외선 방출 테스트Experimental Example 4: Deodorizing Effect and Far Infrared Emission Test
실시예 1의 식품 포장용 용기에 대해 소정의 조건으로 탈취 효과를 시험한 결과, 불쾌한 냄새 성분을 분해시켜 탈취 효과가 90% 이상에 이르고, 공기 중의 미생물, 곰팡이 및 바이러스의 살균율 또한 90% 이상이며, 포름알데히드 및 VOCs 등 유해 가스 제거에도 효과가 있음을 확인하였다.
The deodorizing effect of the food packaging container of Example 1 was tested under predetermined conditions. As a result, it was found that the deodorizing effect was 90% or more by decomposing the unpleasant odor component, and the sterilization rate of microorganisms, fungi and viruses in the air was 90% , Formaldehyde, VOCs, and other hazardous gases.
또한, 실시예 1의 식품 포장용 용기에 대해 원적외선 방출 정도를 측정하고, 그 결과를 하기 표 2에 나타내었다.The degree of far-infrared emission was measured for the food packaging container of Example 1, and the results are shown in Table 2 below.
[표 2][Table 2]
상기 표 2에서 보듯이, 본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물로부터 제조된 용기는 0.9에 육박하는 매우 높은 원적외선 방사율을 나타내고, 방사에너지 또한 충분하였다.
As shown in Table 2, the container prepared from the silicone raw material composition having the freshness-maintaining function of the present invention exhibited a very high far-infrared emissivity close to 0.9, and sufficient radiant energy.
본 발명의 신선도 유지 기능이 부여된 실리콘 원료 조성물은 항균성이 요구되는 다양한 산업 분야의 고분자 제품 제조에 있어, 시트, 용기, 케이스, 필름, 코팅제, 접착제, 내장재, 바닥재, 보강재 등의 형태로 매우 광범위하게 적용될 수 있을 것이다.
The silicone raw material composition to which the freshness-retaining function of the present invention is imparted is very broad in the form of sheets, containers, cases, films, coatings, adhesives, interior materials, flooring materials and reinforcing materials in the production of polymer products in various industrial fields, .
Claims (3)
(B) Si, Fe, Ni, Al, B, K, Ca, Na 및 Mg를 모두 함유하는 광물질 혼합분말로서, 규조토, 장석, 운기석, 펜틀란다이트 및 붕산석 분말이 동일한 중량비율로 포함된 것 0.6 중량%;
(C) 소디움계 첨가제로서, 중탄산소다(NaHCO3) 0.1 중량%;
(D) 유기산으로서, 구연산 0.2 중량%;
(E) 천연유로서, 신남알데히드(Cinnam aldehyde)를 함유하는 계피유(Cinnamon oil), 알릴이소티오시아네이트(Allyl isothiocyanate)를 함유하는 겨자유(Mustard oil), 및 캡사이신(Capsaicin)을 함유하는 고추기름(Red pepper oil)이 4:3:3의 중량비율로 포함된 것 0.1 중량%; 및
(F) 미러블형 실리콘 고무 97.0 중량%;를 포함하고,
상기 미러블형 실리콘 고무 100 중량부를 기준으로 0.01 중량부의 디큐밀 퍼옥사이드가 첨가된 것이며,
상기 광물질 혼합분말은 원적외선을 방출하는 것으로서, 37℃에서의 원적외선 방사율이 0.885, 원적외선 방사파장이 6~12㎛, 원적외선 방사에너지가 3.57×102 W/m2인 것을 특징으로 하는,
신선도 유지 기능이 부여된 실리콘 원료 조성물.
(A) a plant-derived natural antimicrobial agent comprising 2.0% by weight of herbal extract;
(B) a mineral mixed powder containing all of Si, Fe, Ni, Al, B, K, Ca, Na and Mg, wherein diatomite, feldspar, 0.6% by weight;
(C) a sodium based additives, sodium bicarbonate (NaHCO 3) 0.1% by weight;
(D) 0.2% by weight citric acid as an organic acid;
(E) Natural oils include Cinnamon oil containing Cinnam aldehyde, Mustard oil containing Allyl isothiocyanate, and Capsicin containing pepper oil 0.1% by weight red pepper oil in a weight ratio of 4: 3: 3; And
(F) 97.0% by weight of a mirrorblock type silicone rubber,
0.01 part by weight of dicumyl peroxide is added based on 100 parts by weight of the mirror-bladed silicone rubber,
Wherein the mineral powder is mixed as to emit a far infrared ray, a far-infrared emissivity of 0.885 at 37 ℃, far-infrared radiation having a wavelength of 6 ~ 12㎛, wherein the far-infrared radiation energy of 3.57 × 10 2 W / m 2,
A silicone raw material composition having a freshness maintaining function.