KR101463646B1 - 반도체 자기 조성물-전극접합체의 제조 방법 - Google Patents
반도체 자기 조성물-전극접합체의 제조 방법 Download PDFInfo
- Publication number
- KR101463646B1 KR101463646B1 KR1020107019265A KR20107019265A KR101463646B1 KR 101463646 B1 KR101463646 B1 KR 101463646B1 KR 1020107019265 A KR1020107019265 A KR 1020107019265A KR 20107019265 A KR20107019265 A KR 20107019265A KR 101463646 B1 KR101463646 B1 KR 101463646B1
- Authority
- KR
- South Korea
- Prior art keywords
- tio
- composition
- semiconductor
- baco
- hours
- Prior art date
Abstract
본 발명은, 발명자들에 의해 제안된 BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물에 관하여, 실온 저항율이 100Ω·㎝ 이하로 낮고, 통전에 의한 경시변화를 작게 한 반도체 자기 조성물-전극접합체를 제공하는 것을 목적으로 한다.
BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물에 전극을 접합한 반도체 자기 조성물-전극접합체이고, 전극접합 후, 100℃ 이상 600℃ 이하에서 0.5시간 이상 24시간 이하의 열처리를 행하는 반도체 자기 조성물-전극접합체의 제조 방법.
BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물에 전극을 접합한 반도체 자기 조성물-전극접합체이고, 전극접합 후, 100℃ 이상 600℃ 이하에서 0.5시간 이상 24시간 이하의 열처리를 행하는 반도체 자기 조성물-전극접합체의 제조 방법.
Description
본 발명은 PTC 써미스터, PTC 히터, PTC 스위치, 온도검지기 등에 사용되는 양의 저항온도를 갖는 반도체 자기 조성물-전극접합체의 제조 방법에 관한 것이다.
종래, PTCR 특성(양의 비저항온도계수: Positive Temperature Coefficient of Resistivity)을 나타내는 재료로서, BaTiO3에 각종 반도체화 원소를 첨가한 조성물이 제안되어 있다. 이들의 조성물은 큐리온도가 120℃ 전후이다. 또, 이들 조성물은 용도에 따라 큐리온도를 시프트시키는 것이 필요하다.
예를 들면, BaTiO3에 SrTiO3을 첨가하는 것에 의해, 큐리온도를 시프트시키는 것이 제안되어 있지만, 이 경우, 큐리온도는 음의 방향으로만 시프트하고, 양의 방향으로는 시프트하지 않는다. 현재, 큐리온도를 양의 방향으로 시프트시키는 첨가 원소로서 알려져 있는 것은 PbTiO3이다. 그러나, PbTiO3은 환경오염을 야기하는 원소를 함유하기 때문에, 근래, PbTiO3을 사용하지 않는 재료가 요망되고 있다.
PTC 재료에 있어서의 큰 특징은, PTC 재료의 비저항값이 큐리점에서 급격하게 높아지는 것(점프 특성=저항온도계수(α))에 있는데, 이것은, 결정입계에 형성된 저항(쇼트키장벽에 의한 저항)이 증대하기 때문에 일어나는 것으로 보인다. PTC 재료의 특성으로서는, 이 비저항값의 점프 특성이 높은 것이 요구되고 있다.
특허문헌 1과 같은 Pb를 함유하지 않는 PTC 재료는, 점프 특성이 우수한 것은 실온 비저항이 높고, 점프 특성이 떨어지는 것은 실온 비저항이 너무 낮아지는 경향이 있어, 안정된 실온 비저항과 우수한 점프 특성을 양립할 수 없는 문제가 있었다.
발명자들은, 상술한 종래의 BaTiO3계 반도체 자기의 문제를 해결하기 위하여, Pb를 사용하지 않고, 큐리온도를 양의 방향으로 시프트할 수 있음과 함께, 실온 저항율을 대폭 낮추면서도 우수한 점프 특성을 나타내는, BaTiO3의 Ba의 일부를 Bi-Na로 치환한 재료로서, BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물에 있어서 조성식을 [(BiNa)x(Ba1 - yRy)1-x]TiO3으로 나타내고(단, R은 희토류 원소 중의 적어도 1종), 0<x≤0.3, 0<y≤0.02를 만족하는 반도체 자기 조성물, 및 [(BiNa)xBa1 -x][Ti1 - zMz]O3으로 나타내고(단, M은 Nb, Sb 중의 적어도 1종), 0<x≤0.3, 0<z≤0.005를 만족하는 반도체 자기 조성물을 제안하였다(특허문헌 2).
이들 반도체 자기 조성물은, Pb를 사용하지 않고 큐리온도를 양의 방향으로 시프트켜, 실온 저항율을 낮추면서도 우수한 특성을 나타내지만, 히터 재료로서 사용하다 보면 재료의 전기저항율이 변화되는, 이른바 경시변화의 문제가 있었다. 이들의 BaTiO3계 반도체 자기 조성물은 함유 산소량이 변하면 캐리어 농도가 변화하여 전기저항율이 변화되는 것이 알려져 있고, 상기 재료는 불활성분위기 중에서 소결하기 때문에 산소가 결손된 상태에서 소결되어, 대기 중에서 사용하면 산소의 결손량이 변화하여 저항율이 변화되기 쉽다. 특히, 히터 재료로서 전극을 접합한 상태에서 통전하면, 재료가 50℃∼120℃의 고온으로 되었을 때, 대기 중의 산소나, 반도체 자기 조성물-전극 사이에서 산소의 교류가 일어나, 실온 저항율이 변화하여 버린다. 특허문헌 1 : 일본 공개특허 s56-169301호 공보 특허문헌 2 : 일본 공개특허 2007-333528호
본 발명은 발명자들에 의해 제안된 BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물에 관하여, 실온 저항율이 100Ω·㎝ 이하로 낮고, 통전에 의한 경시변화를 작게 한 반도체 자기 조성물-전극접합체를 제공하는 것을 목적으로 한다.
상기 과제를 해결하는 제 1의 발명은, BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물에 전극을 접합한 반도체 자기 조성물-전극접합체이고, 반도체 자기 조성물에 전극을 접합한 후, 100℃ 이상 600℃ 이하의 온도에서 0.5시간 이상 24시간 이하의 열처리를 행하는 것을 특징으로 하는 반도체 자기 조성물-전극접합체의 제조 방법이다. 전극이 접합된 상태에서 열처리를 행하는 것에 의해, 통전시 소자가 고온으로 되었을 때의 반도체 자기 조성물-대기 사이, 및 반도체 자기 조성물-전극 사이에 있어서의 산소의 화학적 평형상태로 미리 접근시켜 놓고, 통전시에 시료가 50∼120℃의 고온으로 되어도 반도체 자기 조성물에 대해 산소의 교류가 거의 일어나지 않게 되고, 실온 저항변화를 억제할 수 있다. 이 열처리의 분위기는 대기 중이어도 좋고 산소 중이어도 좋다. 이 열처리를 전극접합 전에 행하면, 반도체 자기 조성물-대기 사이의 산소의 화학적 평형상태로는 전근시킬 수 있지만, 전극접합 후에도 전극-반도체 자기 조성물 사이에서의 산소의 교류가 일어나기 때문에, 실온 저항율 변화를 억제하는 효과가 작다. 또한, 100℃보다 낮은 열처리 온도에서는 산소의 화학적 평형상태로 할 수 없고, 600℃보다 높은 온도에서의 열처리에서는 반도체 자기 조성물이 고온에 의해 변질되어 실온 저항율이 100Ω·㎝ 이상으로 되어, PTC 히터 등에 적용하기 어려워지기 때문에 바람직하지 않다. 또한, 0.5시간보다 짧으면 산소의 화학적 평형상태로 접근시킬 수 없고, 24시간을 넘으면 제조상 비용이 너무 많이 들기 때문에 바람직하지 않다.
또한, 바람직하게는, 상기 반도체 자기 조성물의 조성식을 [(BiNa)x(Ba1 -yRy)1-x]TiO3으로 나타내고(단, R은 희토류 원소 중의 적어도 1종), 0<x≤0.3, 0<y≤0.02를 만족하는 것이 바람직하다. x는 (BiNa)의 성분범위를 나타내고, x가 0이면 큐리온도를 고온측으로 시프트할 수 없고, 0.3을 넘으면 실온 저항율이 102Ω·㎝에 근접하여, PTC 히터 등에 적용하기 어려워지기 때문에 바람직하지 않다.
상기 R은 희토류 원소 중의 적어도 1종이며 La가 가장 바람직하다. 조성식 중, y는 R의 성분범위를 나타내고, y가 0이면 조성물이 반도체화되지 않고, 0.02를 넘으면 실온 저항율이 커지기 때문에 바람직하지 않다. x, y를 상기 범위의 조성으로 하는 것에 의해, 실온 저항율이 더욱 작고, 점프 특성에 우수한 자기 조성물을 얻을 수 있고, 이 반도체 자기 조성물에 전극을 접합한 것을 100℃ 이상 600℃ 이하의 온도에서, 0.5시간 이상 24시간 이하의 열처리를 행하는 것에 의해, 경시변화에 우수하고, 실온 저항이 100Ω·㎝ 이하로 낮고, 점프 특성에 우수한 자기 조성물-전극접합체를 얻을 수 있다.
또한, 청구항 1의 반도체 자기 조성물의 조성식을 [(BiNa)xBa1 -x][Ti1 - zMz]O3으로 나타내고(단, M은 Nb, Sb 중의 적어도 1종), 0<x≤0.3, 0<z≤0.005를 만족하는 것이 바람직하다. x는 (BiNa)의 성분범위를 나타내고, x가 0이면 큐리온도를 고온측으로 시프트할 수 없고, 0.3을 넘으면 실온 저항율이 102Ω·㎝에 근접하여, PTC 히터 등에 적용하기 어려워지기 때문에 바람직하지 않다.
또한, M은 Nb, Sb 중의 적어도 1종이고, 그중에서도 Nb가 바람직하다. 조성식 중 z는 M의 성분범위를 나타내고, z가 0이면 원자가 제어를 행할 수 없고, 조성물이 반도체화되지 않고, 0.005를 넘으면 실온 저항율이 103Ω·㎝를 넘기 때문에 바람직하지 않다. x, z를 상기 범위의 조성으로 하는 것에 의해, 실온 저항율이 더욱 작고, 점프 특성에 우수한 자기 조성물을 얻을 수 있고, 이 반도체 자기 조성물에 전극을 접합한 것을 100℃ 이상 600℃ 이하의 온도에서, 0.5시간 이상 24시간 이하의 열처리를 행하는 것에 의해, 경시변화에 우수하고, 실온 저항이 100Ω·㎝ 이하로 낮고, 점프 특성에 우수한 자기 조성물-전극접합체를 얻을 수 있다.
본 발명에 의하면, Pb를 사용하지 않고 실온 저항율을 100Ω·㎝ 이하로 낮게 유지하면서, 13V, 5000시간의 통전에 따른 경시변화를 10% 이하 억제한 반도체 자기 조성물-전극접합체를 제공할 수 있다.
도 1은 본 발명에 따른 반도체 자기 조성물의 주사형 커패시턴스 현미경에 의한 관찰 이미지의 조직 사진을 나타내는 도면.
도 2는 본 발명에 따른 반도체 자기 조성물의 주사형 커패시턴스 현미경에 의한 관찰 이미지의 조직 사진을 나타내는 도면.
도 3은 본 발명에 따른 반도체 자기 조성물의 주사형 커패시턴스 현미경에 의한 관찰 이미지의 조직 사진을 나타내는 도면.
도 4는 본 발명에 따른 반도체 자기 조성물의 주사형 커패시턴스 현미경에 의한 관찰 이미지의 조직 사진을 나타내는 도면.
도 5는 본 발명에 따른 반도체 자기 조성물의 주사형 커패시턴스 현미경에 의한 관찰 이미지의 조직 사진을 나타내는 도면.
도 2는 본 발명에 따른 반도체 자기 조성물의 주사형 커패시턴스 현미경에 의한 관찰 이미지의 조직 사진을 나타내는 도면.
도 3은 본 발명에 따른 반도체 자기 조성물의 주사형 커패시턴스 현미경에 의한 관찰 이미지의 조직 사진을 나타내는 도면.
도 4는 본 발명에 따른 반도체 자기 조성물의 주사형 커패시턴스 현미경에 의한 관찰 이미지의 조직 사진을 나타내는 도면.
도 5는 본 발명에 따른 반도체 자기 조성물의 주사형 커패시턴스 현미경에 의한 관찰 이미지의 조직 사진을 나타내는 도면.
본 발명에 따른 반도체 자기 조성물은, BaTiO3의 Ba의 일부를 Bi-Na로 치환한 조성을 포함하는 조성이면 모두 채용할 수 있지만, 조성식을 [(BiNa)x(Ba1 - yRy)1-x]TiO3으로 나타내고(단, R은 희토류 원소 중의 적어도 1종), 0<x≤0.3, 0<y≤0.02를 만족하는 조성, 또는 조성식을 [(BiNa)xBa1 -x][Ti1 - zMz]O3으로 나타내고(단, M은 Nb, Sb 중의 적어도 1종), 0<x≤0.3, 0<z≤0.005를 만족하는 조성이 바람직하다. 이하, 본 발명을 실시예에 의해 구체적으로 설명하지만, 이들의 실시예에 의해 본 발명이 한정되지 않는다.
본 발명의 특징은, 상기 BaTiO3의 Ba의 일부를 Bi-Na로 치환한 반도체 자기 조성물에 있어서, 결정입계에 P형 반도체가 존재하는 것을 특징으로 한다.
P형 반도체의 존재는, 예를 들면, 반도체 자기 조성물의 임의의 면을 주사형 커패시턴스 현미경으로 관찰하는 것에 의해, 확인할 수 있다. 도 1∼도 5는 본 발명에 따른 반도체 자기 조성물의 평면을 주사형 커패시턴스 현미경으로 관찰한 조직 사진을 나타내는 도면이다. 각 도면에 있어서, 흰색으로 표시되어 있는 부분이 본 조성물의 주결정, 회색으로 표시되어 있는 부분이 결정입계, 회색보다 검게 표시되어 있는 부분이 P형 반도체이다. 도 1∼도 5로부터 명백한 바와 같이, P형 반도체는 결정입계에 존재하고 있다.
이하, 본 발명에 따른 반도체 자기 조성물을 얻기 위한 제조 방법의 일례를 설명한다.
우선, 본 발명에 있어서는, BaTiO3의 Ba의 일부를 Bi-Na로 치환한 반도체 자기 조성물의 제조에 있어서, (BaR)TiO3 가소분(반도체 자기 조성물이 조성식 [(BiNa)x(Ba1-yRy)1-x]TiO3 인 경우) 또는 Ba(TiM)O3 가소분(반도체 자기 조성물이 조성식 [(BiNa)xBa1 -x][Ti1 - zMz]O3 인 경우)으로 이루어지는 BT 가소분과, (BiNa)TiO3 가소분으로 이루어지는 BNT 가소분을 별도로 준비하고, 당해 BT 가소분과 BNT 가소분을 각각에 대응한 적정온도로 가소하는 분할가소법을 채용한다.
상기 분할가소법을 이용하는 것에 의해, BNT 가소분의 Bi의 휘산(揮散)이 억제되고, Bi-Na의 조성 차이를 방지하여 이상(異相)의 생성을 억제할 수 있고, 이들의 가소분을 혼합하여, 성형, 소결하는 것에 의해, 실온 저항율이 낮고, 큐리온도의 불규칙이 억제된 반도체 자기 조성물을 얻을 수 있다.
상술한 분할가소법을 이용하여, 본 발명에 따른 반도체 자기 조성물을 얻기 위해서는, 하기에 나타내는 3가지 방법을 채용할 수 있다. (1) 분할가소법에 있어서 BT 가소분을 준비할 때, BT 가소분 중에 BaCO3 및 TiO2가 일부 잔존하도록 조제하는 방법(이하 "잔존법"이라 한다), (2) 분할가소법으로 제작한 BT 가소분 및/또는 BNT 가소분에 BaCO3 및/또는 TiO2를 첨가하는 방법(이하 "첨가법"이라 한다), (3) 분할가소법으로 제작한 BT 가소분과 BNT 가소분을 소결할 때, BT와 BNT를 완전히 고용시키지 않고 소결하는 방법(이하 "불완전소결법"이라 한다)이다. 이하, 차례로 설명한다.
(1) 잔존법 분할가소법에 있어서는, BT 가소분을 준비함에 있어서, BaCO3, TiO2와 반도체화 원소의 원료분말, 예를 들면, La2O3이나 Nb2O5를 혼합하여 혼합원료분말을 제작하고, 가소하는데, 종래에는, 완전한 단일상을 형성시키기 위하여, 가소온도를 900℃∼1300℃의 범위에서 실시하고 있었다. 이에 대해, 잔존법은, 이 가소온도를 종래보다 낮은 900℃ 이하에서 실시하고, (BaR)TiO3 또는 Ba(TiM)O3을 완전히 형성시키지 않고, 가소분 중에 BaCO3, TiO2를 일부 잔존시킨다.
잔존법에 의한 BaCO3, TiO2를 일부 잔존시킨 BT 가소분과, 별도로 준비한 BNT 가소분을 혼합하고, 혼합가소분을 성형, 소결하는 것에 의해, 본 발명에 따른 BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물을 얻을 수 있다.
BT 가소분 중의 BaCO3 및 TiO2의 잔존량을 변화시키기 위해서는, BT 가소분을 준비하는 공정에 있어서, 가소온도를 900℃ 이하로 변화시키거나, 가소시간을 변화시키거나, 또는 BT 가소분의 배합 조성을 변화시키는 것에 의해, BT 가소분 중의 BaCO3 및 TiO2의 잔존량을 변화시킬 수 있고, 이에 의해 P형 반도체의 존재 비율을 제어할 수 있다.
상기 잔존법에 있어서, 가소온도가 900℃를 넘으면 (BaR)TiO3 또는 Ba(TiM)O3이 과잉 형성되어, BaCO3, TiO2를 잔존시킬 수 없게 되기 때문에 바람직하지 않다. 가소시간은 0.5시간∼10시간이 바람직하고, 2∼6시간이 더욱 바람직하다.
BT 가소분 중의 BaCO3 및 TiO2의 잔존량은, (BaR)TiO3 또는 Ba(TiM)O3과, BaCO3 및 TiO2의 합계를 100mol%로 한 경우, BaCO3이 30mol% 이하, TiO2가 30mol% 이하인 것이 바람직하다.
BaCO3의 잔존량을 30mol% 이하로 한 것은, 30mol%를 넘으면 BaCO3 이외의 이상이 생성되어 실온 비저항이 상승하기 때문이다. 또한, 소결공정에 있어서 CO2 가스가 발생하고, 소결체에 크랙이 생기기 때문에 바람직하지 않다. TiO2의 잔존량을 30mol% 이하로 한 것은, 30mol%를 넘으면 BaCO3 이외의 이상이 생성되어 실온 비저항이 상승하기 때문이다.
BaCO3 및 TiO2의 잔존량의 상한은 BaCO3이 30mol%, TiO2가 30mol%인 합계 60mol%, 하한은 0 이상의 양이 되지만, BaCO3이 20mol%를 넘는 경우, TiO2가 10mol% 미만으로 되면 BaCO3 이외의 이상이 생성되어 실온 비저항이 상승하기 때문에 바람직하지 않다. TiO2가 20mol%를 넘고, BaCO3이 10mol% 미만으로 되는 경우도 마찬가지로 바람직하지 않다. 따라서, BaCO3 또는 TiO2의 어느 하나가 20mol%를 넘는 경우, 다른 하나를 10mol% 이상으로 하도록 가소온도나 온도, 배합 조성 등을 조정하는 것이 바람직하다.
상술한 BaCO3 및 TiO2가 일부 잔존하는 BT 가소분과 혼합하는, (BiNa)TiO3 가소분으로 이루어지는 BNT 가소분을 준비하는 공정은, 우선, 원료분말이 되는 Na2CO3, Bi2O3, TiO2를 혼합하여 혼합원료분말을 제작한다. 이때, Bi2O3을 과잉으로(예를 들면, 5mol% 이상) 첨가하면, 가소 때에 이상을 생성하고, 실온 비저항이 상승하기 때문에 바람직하지 않다.
다음으로, 상기 혼합원료분말을 가소한다. 가소온도는 700℃∼950℃의 범위가 바람직하다. 가소시간은 0.5시간∼10시간이 바람직하고, 2시간∼6시간이 더욱 바람직하다. 가소온도가 700℃ 미만 또는 가소시간이 0.5시간 미만에서는 미반응 Na2CO3이나 분해하여 생성된 NaO가 분위기의 수분, 또는 습식 혼합의 경우 그 용매와 반응하여, 조성 차이나 특성의 불규칙을 일으키기 때문에 바람직하지 않다. 또한, 가소온도가 950℃를 넘거나 또는 가소시간이 10시간을 넘으면, Bi의 휘산이 진행되어, 조성 차이를 일으키고, 이상의 생성이 촉진되기 때문에 바람직하지 않다.
상술한 각각의 가소분을 준비하는 공정에 있어서는, 원료분말의 혼합 때에, 원료분말의 입도에 상응하여 분쇄를 시행하여도 좋다. 또한, 혼합, 분쇄는 순수(純水)나 에탄올을 이용한 습식 혼합·분쇄 또는 건식 혼합·분쇄 중의 어느 것이어도 좋지만, 건식 혼합·분쇄를 행하면, 조성 차이를 더욱 방지할 수 있어 바람직하다. 또, 상기에 있어서는, 원료분말로서, BaCO3, Na2CO3, TiO2 등을 예로 들었지만, 그 외의 Ba 화합물, Na 화합물 등을 이용하여도 좋다.
상기한 바와 같이, BaCO3, TiO2가 일부 잔존하는 BT 가소분과 BNT 가소분을 별도로 준비하고, 각 가소분을 소정의 량으로 배합한 후, 혼합한다. 혼합은 순수나 에탄올을 이용한 습식 혼합 또는 건식 혼합 중의 어느 것이어도 좋지만, 건식 혼합을 행하면, 조성 차이를 더욱 방지할 수 있어 바람직하다. 또한, 가소분의 입도에 상응하여, 혼합한 후에 분쇄, 또는 혼합과 분쇄를 동시에 행하여도 좋다. 혼합, 분쇄 후의 혼합가소분의 평균 입도는, 0.5㎛∼2.5㎛가 바람직하다.
상술한, BT 가소분을 준비하는 공정 및/또는 BNT 가소분을 준비하는 공정, 또는 각 가소분을 혼합하는 공정에 있어서, Si 산화물을 3.0mol% 이하, Ca 산화물 또는 Ca 탄산염을 4.0mol% 이하 첨가하면, Si 산화물은 결정입의 이상성장을 억제함과 함께 저항율의 컨트롤을 쉽게 할 수 있고, Ca 산화물 또는 Ca 탄산염은 저온에서의 소결성을 향상시킬 수 있고, 또한 환원성을 컨트롤할 수 있어 바람직하다. 어느 것이나 상기 한정량을 넘어 첨가하면, 조성물이 반도체화를 나타내지 않게 되기 때문에 바람직하지 않다. 첨가는, 각 공정에 있어서의 혼합 전에 행하는 것이 바람직하다.
BT 가소분과 BNT 가소분을 혼합하는 공정에 의해 얻어진 혼합가소분은, 원하는 성형수단에 의해 성형한다. 성형 전에 필요에 따라 분쇄분을 조립(造粒)장치에 의해 조립하여도 좋다. 성형 후의 성형체 밀도는 2.5∼3.5g/㎤가 바람직하다.
소결은, 대기 중, 또는 환원 분위기 중, 또는 저산소농도의 불활성 가스 분위기에서 행할 수 있지만, 특히, 산소농도 1% 미만의 질소 또는 아르곤 분위기 중에서 소결하는 것이 바람직하다. 소결온도는 1250℃∼1380℃가 바람직하다. 소결시간은 1시간∼10시간이 바람직하고, 2시간∼6시간이 더욱 바람직하다. 어느 것이나 바람직한 조건에서 벗어남에 따라, 실온 비저항이 상승하고, 점프 특성이 저하하기 때문에 바람직하지 않다.
다른 소결공정으로서, 온도 1290℃∼1380℃, 산소농도 1% 미만의 분위기 중에서, (1) 4시간 미만의 소결시간으로 실행하거나, 또는 (2) 식:△T≥25t(t=소결시간(hr), △T=소결 후의 냉각속도(℃/hr))를 만족하는 소결시간으로 실행되고, 그 다음, 상기 식을 만족하는 냉각속도로 소결 후의 냉각을 실행하는 것에 의해, 실온 비저항을 낮게 유지한 채로, 고온영역(큐리온도 이상)에서 저항온도계수를 향상시킨 반도체 자기 조성물을 얻을 수 있다.
(2) 첨가법 첨가법에 있어서, BT 가소분을 준비함에 있어서, BaCO3, TiO2와 반도체화 원소의 원료분말, 예를 들면, La2O3이나 Nb2O5를 혼합하여 혼합원료분말을 제작하고, 가소한다. 가소온도는 1000℃ 이상이 바람직하다. 가소온도가 1000℃ 미만에서는 (BaR)TiO3 또는 Ba(TiM)O3이 완전한 단일상이 형성되지 않기 때문에 바람직하지 않다. 완전한 단일상이 형성되지 않으면 미반응 BaCO3, TiO2가 잔존하게 되고, BaCO3분(粉) 및/또는 TiO2분(粉)의 첨가를 전제로 하므로 그 첨가량의 예측이 어려워지기 때문이지만, 약간의 BaCO3이나 TiO2의 잔존은 허용할 수 있다. 바람직한 가소온도는 1000℃∼1300℃이다. 가소시간은 0.5시간∼10시간이 바람직하고, 2∼6시간이 더욱 바람직하다.
첨가법에 있어서, BNT 가소분을 준비하는 공정, BT 가소분과 BNT 가소분의 혼합(분쇄)공정 등에 관해서는, 상술한 잔존법과 동일하다.
상기와 같이 하여 준비한 BT 가소분 또는 BNT 가소분 또는 그들의 혼합가소분에, BaCO3 및/또는 TiO2를 첨가하는 것이 첨가법의 특징이다. 첨가 후의 혼합가소분을 성형, 소결하는 것에 의해, 본 발명에 따른 BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물을 얻을 수 있다.
BaCO3 및/또는 TiO2의 첨가량은, (BaR)TiO3 또는 Ba(TiM)O3과, BaCO3 및/또는 TiO2의 합계를 100mol%로 한 경우, BaCO3이 30mol% 이하, TiO2가 30mol% 이하인 것이 바람직하다. 이 첨가량을 변화시키는 것에 의해, P형 반도체의 존재 비율을 제어할 수 있다. 특히, 첨가법에 의하면, 첨가량을 정확하게 조정할 수 있기 때문에, 극히 높은 정밀도로 실온 저항율을 컨트롤할 수 있는 효과도 갖는다.
BaCO3의 첨가량을 30mol% 이하로 한 것은, 30mol%를 넘으면 BaCO3 이외의 이상이 생성되어 실온 비저항이 상승하기 때문이다. 또한, 소결공정에 있어서 CO2 가스가 발생하고, 소결체에 크랙이 생기기 때문에 바람직하지 않다. TiO2의 첨가량을 30mol% 이하로 한 것은, 30mol%를 넘으면 BaCO3 이외의 이상이 생성되어 실온 비저항이 상승하기 때문이다.
BaCO3과 TiO2를 모두 포함하는 경우, 첨가량의 상한은 BaCO3이 30mol%, TiO2가 30mol%인 합계 60mol%, 하한은 0 이상의 양이 되지만, BaCO3이 20mol%를 넘는 경우, TiO2가 10mol% 미만이 되면 BaCO3 이외의 이상이 생성되어 실온 비저항이 상승하기 때문에 바람직하지 않다. TiO2가 20mol%를 넘고, BaCO3이 10mol% 미만으로 되는 경우에도 마찬가지로 바람직하지 않다. 따라서, BaCO3 또는 TiO2 중의 어느 하나가 20mol%를 넘는 경우에는, 다른 하나를 10mol% 이상으로 하는 것이 바람직하다.
또, BT 가소분으로서 (BaR)TiO3 또는 Ba(TiM)O3과의 완전한 단일상이 형성되어 있는 것이 바람직한 것은, 상술한 바와 동일하지만, 완전한 단일상이 형성된 BT 가소분의 일부를 상술한 잔존법에 의한 BaCO3, TiO2가 잔존하는 BT 가소분으로 치환하고, 나아가, BaCO3 및/또는 TiO2를 소정의 량으로 첨가하는 것에 의해, 첨가량을 변화시킬 수도 있다.
첨가법에서는, 상기한 바와 같이, BT 가소분과 BNT 가소분을 별도로 준비한 후, 당해 BT 가소분 또는 BNT 가소분 또는 그들의 혼합가소분에 BaCO3 및/또는 TiO2를 첨가한다. 그 다음, 각 가소분을 소정의 량으로 배합한 후, 혼합한다. 혼합은, 순수나 에탄올을 이용한 습식 혼합 또는 건식 혼합 중의 어느 것이어도 좋지만, 건식 혼합을 행하면, 조성 차이를 방지할 수 있어 바람직하다. 또한, 가소분의 입도에 상응하여, 혼합한 후에 분쇄, 또는 혼합과 분쇄를 동시에 행하여도 좋다. 혼합, 분쇄 후의 혼합가소분의 평균 입도는 0.5㎛∼2.5㎛가 바람직하다.
상술한, BT 가소분을 준비하는 공정 및/또는 BNT 가소분을 준비하는 공정, 또는 이들의 가소분을 혼합하는 공정에 있어서, Si 산화물을 3.0mol% 이하, Ca 산화물 또는 Ca 탄산염을 4.0mol% 이하 첨가하면, Si 산화물은 결정입의 이상성장을 억제함과 함께 저항율의 컨트롤을 쉽게 할 수 있고, Ca 산화물 또는 Ca 탄산염은 저온에서의 소결성을 향상시킬 수 있고, 또한 환원성을 컨트롤할 수 있어 바람직하다. 어느 것이나 상기 한정량을 넘어 첨가하면, 조성물이 반도체화를 나타내지 않게 되기 때문에 바람직하지 않다. 첨가는, 각 공정에 있어서의 혼합 전에 행하는 것이 바람직하다.
BT 가소분과 BNT 가소분을 혼합하는 공정 이후의, 성형, 소결 등의 공정은 상술한 잔존법과 동일하다.
(3) 불완전소결법 불완전소결법에 있어서, BT 가소분을 준비하는 공정, BNT 가소분을 준비하는 공정, BT 가소분과 BNT 가소분을 혼합(분쇄)하는 공정, 성형공정에 대해서는, 상술한 첨가법과 동일하다.
불완전소결법에서는, BT 가소분과 BNT 가소분과의 혼합가소분을 소결할 때에, BT와 BNT를 완전히 고용시키지 않고 소결하는 것이 특징이다. 이에 의해, 본 발명에 따른 BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물을 얻을 수 있다.
불완전소결법에 있어서의 소결온도, 소결시간은, BT 가소분의 가소온도에 따라 상이하지만, 예를 들면, BT 가소분의 가소온도가 700℃∼1200℃의 경우, 소결온도는 1250℃∼1380℃, 소결시간은 2.5시간 이하가 바람직한 범위다. 단, 소결온도가 비교적 낮을 경우(예를 들면, 1300℃인 경우)의 바람직한 소결시간은 3.5시간 이하라도 좋고, 소결온도가 비교적 높을 경우(예를 들면, 1380℃인 경우)의 바람직한 소결시간은 2시간 이하가 된다. 소결온도가 높을 경우(예를 들면, 1400℃ 이상인 경우)이나 소결온도가 낮아도 소결시간이 긴 경우(예를 들면, 5시간 이상인 경우)는, BT와 BNT가 완전히 고용해버리기 때문에 바람직하지 않다.
상기한 바와 같이, 소결온도와 소결시간을 제어하는 것에 의해, BT와 BNT의 고용도를 변화시킬 수 있고, 이에 의해 P형 반도체의 존재 비율을 제어할 수 있다. [실시예]
(실시예 1) 잔존법을 이용하여 다음과 같이 하여 반도체 자기 조성물을 얻었다. BaCO3, TiO2, La2O3의 원료분말을 준비하고, (Ba0 .994La0 .006)TiO3이 되도록 배합하고, 순수로 혼합하였다. 얻어진 혼합원료분말을 900℃에서, 4시간 대기 중에서 가소하여, BT 가소분을 준비하였다.
Na2CO3, Bi2O3, TiO2의 원료분말을 준비하고, (Bi0 .5Na0 .5)TiO3이 되도록 배합하고, 에탄올 중에서 혼합하였다. 얻어진 혼합원료분말을 900℃에서, 2시간 대기 중으로 가소하여, BNT 가소분을 준비하였다.
준비한 BT 가소분과 BNT 가소분을 몰비로 73:7이 되도록 배합하고, 순수를 매체로 하여 포트밀(Pot Mill)에 의해, 혼합가소분의 중심 입경이 1.0㎛∼2.0㎛가 될 때까지 혼합, 분쇄한 후, 건조시켰다. 당해 혼합가소분의 분쇄분에 PVA를 첨가하고 혼합한 후, 조립(造粒)장치에 의해 조립하였다. 얻어진 조립분을 1축 프레스장치로 성형하고, 상기 성형체를 700℃에서 탈 바인더 후, 1360℃에서 4시간 유지하고 질소 중에서 소결하여, 소결체를 얻었다.
얻어진 소결체를 10㎜×10㎜×1㎜의 판 형상으로 가공하여 시험편을 제작하고, NAMICS CORPORATION이 제조한 오믹전극(모델번호: SR5051)을 도포하고, 나아가 NAMICS CORPORATION이 제조한 커버전극(모델번호: SR5080)을 도포하여 180℃에서 건조시킨 후 600℃에서 10분 유지하고 베이킹하여 전극을 형성하였다. 그 후, 대기 중에서 100℃에서 0.5시간의 열처리를 행하여 반도체 자기 조성물-전극접합체를 얻었다. 얻어진 반도체 자기 조성물의 25℃에서의 전기저항율을 측정하고, 알루미늄 핀을 갖는 히터에 도입하여, 풍속 4m/s로 냉각하면서 13V, 5000시간의 통전시험을 행하였다. 이때 핀의 온도는 70℃였다. 통전시험 후의 25℃에서의 전기저항율을 측정하고, 통전시험 전과 비교하여 저항변화율을 구하고, 경시변화를 조사하였다. 얻어진 결과를 표 1에 나타낸다. 열처리 후의 실온 저항율은 50Ω·㎝, 5000시간 통전 후의 실온 저항율은 54.5Ω·㎝, 저항변화율은 9%로 되었다.
실시예 2∼12는 열처리 온도와 열처리 시간을 다르게 한 예이다. 그외의 반도체 자기 조성물-전극접합체의 제작 방법이나 평가 방법은 실시예 1과 동일한 방법으로 행하였다. 얻어진 결과를 표 1에 나타낸다.
실시예 13∼17은 BT 가소분과 BNT 가소분의 몰비를 변화시킨 예이다. 그외의 반도체 자기 조성물-전극접합체의 제작 방법이나 평가 방법은 실시예 1과 동일한 방법으로 행하였다. 얻어진 결과를 표 1에 나타낸다.
실시예 18은 Ti의 일부를 Nb으로 치환한 예이다. (실시예 18) BaCO3, TiO2, Nb2O3의 원료분말을 준비하고, Ba(Ti0 .997Nb0 .003)O3이 되도록 배합하고, 순수로 혼합하였다. 얻어진 혼합원료분말을 900℃에서 4시간 대기 중에서 가소하여, BT 가소분을 준비하였다.
Na2CO3, Bi2O3, TiO2의 원료분말을 준비하고, (Bi0 .5Na0 .5)TiO3이 되도록 배합하고, 에탄올 중에서 혼합하였다. 얻어진 혼합원료분말을 900℃에서, 2시간 대기 중에서 가소하여, BNT 가소분을 준비하였다.
준비한 BT 가소분과 BNT 가소분을 몰비로 73:7이 되도록 배합하고, 순수를 매체로 하여 포트밀에 의해, 혼합가소분의 중심입경이 1.0㎛∼2.0㎛가 될 때까지 혼합, 분쇄한 후, 건조시켰다. 당해 혼합가소분의 분쇄분에 PVA를 첨가하고 혼합한 후, 조립(造粒)장치에 의해 조립하였다. 얻어진 조립분을 1축 프레스장치로 성형하고, 상기 성형체를 700℃에서 탈 바인더 후, 1360℃에서 4시간 유지하고 질소 중에서 소결하여, 소결체를 얻었다. 얻어진 소결체를 실시예 1과 동일한 방법으로 전극을 형성하고, 300℃에서 3시간 대기 중에서 열처리를 행하여 반도체 자기 조성물-전극접합체를 얻었다. 평가 방법은 실시예 1과 동일한 방법으로 행하였다. 얻어진 결과를 표 1에 나타낸다.
실시예 19∼23은 Ti의 일부를 Nb로 치환하고, 열처리 조건을 다르게 한 예이다. 그외의 반도체 자기 조성물-전극접합체의 제작 방법이나 평가 방법은 실시예 18과 동일한 방법으로 행하였다. 얻어진 결과를 표 1에 나타낸다.
실시예 24는 Ti의 일부를 Sb로 치환한 예이다. Nb2O3 대신 Sb2O3을 사용한 이외에는 실시예 18과 동일한 방법으로 시료를 제작하고, 특성평가를 하였다. 얻어진 결과를 표 1에 나타낸다.
비교예 1은 전극을 형성한 후 열처리를 행하지 않는 예이다. 열처리를 행하지 않는 이외에는 실시예 1과 동일한 제작 방법으로 시료를 얻고, 특성평가를 하였다. 얻어진 결과를 표 1에 나타낸다.
비교예 2∼5는 열처리 조건을 본 발명의 범위 외에서 행한 예이다. 열처리 조건 이외에는 실시예와 동일한 제작 방법으로 시료를 얻고, 특성평가를 하였다. 얻어진 결과를 표 1에 나타낸다.
비교예 6은 열처리를 전극의 접합 전에 행한 예이다. (비교예 6) 실시예 1과 동일한 방법으로 반도체 자기 조성물을 소결한 후, 300℃에서 3시간의 열처리를 행하였다. 그 후, 실시예 1과 동일한 방법으로 전극을 형성하고, 특성평가를 하였다. 얻어진 결과를 표 1에 나타낸다.
표 1을 참조로, 본 발명의 실시예에 의하면 어느 한 구성이어도 실온 저항율이 100Ω·㎝ 이하로 낮고, 13V, 5000시간 통전 후의 경시변화가 10% 이하로 낮게 억제된 반도체 자기 조성물-전극접합체를 얻을 수 있음을 알 수 있다. 또한, 실시예 1과 비교예 2를 참조로, 열처리 온도가 100℃ 이상이 아니면 5000시간의 통전시험 후의 경시변화를 10% 이하로 억제할 수 없고, 실시예 10과 비교예 3을 참조로, 열처리 온도가 600℃보다 높아지면 실온 저항율이 100Ω·㎝ 이상으로 너무 높아져 버리는 것을 알 수 있다. 또한, 실시예 5∼8과 비교예 4를 비교하면, 열처리 시간은 0.5시간 이상이면 바람직하다는 것을 알 수 있다. 단, 열처리 시간이 24시간을 넘으면 제조상 비용이 너무 많이 들기 때문에 바람직하지 않다. 또한, 비교예 6을 참조로, 전극의 접합 전에 열처리를 행하여도 경시변화를 억제하는 효과가 작다는 것을 알 수 있다.
모든 실시예와 비교예에 있어서, 얻어진 열처리 후의 반도체 자기 조성물은 결정입계에 P형 반도체를 갖고, 그 면적농도는 0.01∼10%의 범위 내였다.
본 발명을 상세하게, 또한 특정 실시예를 참조하여 설명하였지만, 본 발명의 정신과 범위를 벗어나지 않고 다양한 변경이나 수정을 더할 수 있음은, 당업자에 있어서 자명하다. 본 출원은 2008년 3월 27일로 출원된 일본 특허출원(특원 2008-082669)에 근거하는 것으로서, 그 내용은 여기에 참조로서 도입된다.
본 발명에 의해 얻어지는 반도체 자기 조성물-전극접합체는 PTC 써미스터, PTC 히터, PTC 스위치, 온도검지기 등의 재료로서 최적이다.
Claims (3)
- BaTiO3의 Ba의 일부가 Bi-Na로 치환되어, 결정입계에 P형 반도체를 갖는 반도체 자기 조성물에 전극을 접합한 반도체 자기 조성물-전극접합체이고,
상기 반도체 자기 조성물은, 조성식을 [(BiNa)x(Ba1-yRy)1-x]TiO3으로 나타내고(단, R은 희토류 원소 중의 적어도 1종), 0<x≤0.3, 0<y≤0.02를 만족하거나, [(BiNa)xBa1-x][Ti1-zMz]O3으로 나타내고(단, M은 Nb, Sb 중의 적어도 1종), 0<x≤0.3, 0<z≤0.005를 만족하는 것이고,
상기 반도체 자기 조성물을 산소농도 1% 미만인 질소 또는 아르곤 분위기 중에서 소결하여, 얻어진 소결체에 전극을 접합한 후, 대기 중 또는 산소 중에서 300℃ 이상 600℃ 이하에서 0.5시간 이상 24시간 이하의 열처리를 행하는 것을 특징으로 하는 반도체 자기 조성물-전극접합체의 제조 방법. - 삭제
- 삭제