KR100947655B1 - Method for resurfacing of concrete pavement using remitar - Google Patents
Method for resurfacing of concrete pavement using remitar Download PDFInfo
- Publication number
- KR100947655B1 KR100947655B1 KR1020090053421A KR20090053421A KR100947655B1 KR 100947655 B1 KR100947655 B1 KR 100947655B1 KR 1020090053421 A KR1020090053421 A KR 1020090053421A KR 20090053421 A KR20090053421 A KR 20090053421A KR 100947655 B1 KR100947655 B1 KR 100947655B1
- Authority
- KR
- South Korea
- Prior art keywords
- concrete
- remittal
- mixed
- pavement
- laying
- Prior art date
Abstract
Description
본 발명은 레미탈을 이용한 콘크리트 포장의 재포장 공법에 관한 것으로서, 더욱 상세하게는 초속경 시멘트와 건조모래를 혼합한 레미탈이 포함된 혼합 콘크리트를 혼합장비를 통해 공급하여 효율적으로 콘크리트 도로면을 재포장하는 레미탈을 이용한 콘크리트 포장의 재포장 공법에 관한 것이다.The present invention relates to a repaving method of concrete pavement using remittal, and more specifically, to provide a concrete road surface by supplying a mixed concrete containing remittal mixed cemented carbide and dry sand through the mixing equipment The present invention relates to a repaving method of concrete pavement using remittal repacking.
고속국도, 국도, 공항 활주로 등에 건설된 시멘트 콘크리트 도로의 포장은 설계 수명이 약 20년 내외로서 현재 많은 도로의 공용년수가 20년을 초과하여, 이용 차량이 안전하고 쾌적하게 주행할 수 있는 도로 포장의 적절성을 나타내는 도로 포장의 공용성이 현저히 저하되어 시멘트 콘크리트 포장을 전면보수 또는 재포장을 해야 할 필요성이 요구되고 있다.Cement concrete roads built on high-speed national highways, national roads, airport runways, etc. have a design life of about 20 years, and many roads now have more than 20 years of common road use. The pavement of road pavement, which shows the adequacy of the pavement, is significantly reduced, requiring the necessity to completely repair or repackage the cement concrete pavement.
시멘트 콘크리트 포장을 재포장할 때에 일반화된 공법은 접착식 콘크리트 덧씌우기 공법(Bonded Concrete Overlay)과 비접착식 콘크리트 덧씌우기 공 법(Unbonded Concrete Overlay) 이 있다.Generalized methods for resurfacing cement concrete pavement include Bonded Concrete Overlay and Unbonded Concrete Overlay.
- 접착식 콘크리트 덧씌우기 공법(Bonded Concrete Overlay): 덧씌우려는 포장층을 기존 시멘트 콘크리트 포장층에 완전히 접착시키는 공법으로 먼저 노후화된 콘크리트 표면을 약간 깎아내고 경계면에 시멘트 그라우트 등의 접착제를 살포한 후 약 15㎝ 정도의 얇은 콘크리트로 덧씌우기를 하여 기존 콘크리트 슬래브와 일치되도록 하는 방법이다.Bonded Concrete Overlay: A method that completely bonds the pavement layer to be overlaid with the existing cement concrete pavement, first scrapping away the aged concrete surface and spraying an adhesive such as cement grout on the interface. It is a method of overlapping with existing concrete slab by overlaying it with thin concrete of about ㎝.
- 비접착식 콘크리트 덧씌우기 공법(Unbonded Concrete Overlay): 덧씌우기 포장층을 기존 포장면으로부터 완전히 분리시킴으로써 기존포장 결합부가 덧씌우기층의 거동에 영향을 주지 않도록 하는 공법으로 기존의 노후화된 콘크리트 슬래브에 분리층을 아스팔트 콘크리트 등으로 약 5㎝ 정도 설치하고, 그 위에 접착식 콘크리트 덧씌우기보다 두꺼운 콘크리트로 덧씌우기를 하는 방법이다. 일반적으로 기존 포장의 파손상태가 심하여 접착식 콘크리트 덧씌우기 공법으로 시공하기에 부적절한 경우에 사용하는 공법으로서 두께가 접착식 콘크리트 덧씌우기 공법에 비해 두껍게 시공을 하며 포장 두께는 약 20~25㎝ 정도로 시공한다.-Unbonded Concrete Overlay: A method that separates the overlaid pavement layer from the existing pavement surface so that the existing pavement joint does not affect the behavior of the overlaid layer. Is installed about 5cm by asphalt concrete, etc., and is overlaid with thick concrete rather than adhesive concrete overlay. Generally, when the damage of existing pavement is so severe that it is unsuitable for construction with adhesive concrete overlaying method, it is thicker than adhesive concrete overlaying method and the thickness is about 20 ~ 25㎝.
위의 두 가지 공법은 미국 등에서 주로 사용하는 공법으로서 공용 중인 기존도로를 장기간 교통제한을 하여야 하는 단점이 있고, 도로면이 높아짐에 따라 갓길의 돋움, 다이크의 재설치, 가드레일 등 차량방책의 재설치, 교량접속부에서의 단차처리, 터널 전후의 단차처리, 중앙분리대 방호벽의 재설치 등 많은 부수적인 문제점이 수반되고 공사비도 고가인 문제점이 있다.The above two methods are mainly used in the United States, and have the disadvantage of restricting traffic on existing roads for long periods of time, and as the road surface increases, the reinforcement of shoulders, reinstallation of dykes, guardrails, etc. There are a number of side problems, such as the stepped processing at the bridge connection, the stepped before and after the tunnel, and the reinstallation of the central partition barrier, and the construction cost is expensive.
국내 고속국도 및 국도 시멘트 콘크리트 포장 보수의 경우는 전술한 두 가지 공법의 적용은 장기간의 도로 폐쇄, 고가의 공사비 등의 문제로 적용이 현실적으로 곤란하고 적용사례도 없다.In the case of the high speed national highway and national cement concrete pavement repair, the application of the above two methods is difficult to apply due to problems such as long-term road closure and expensive construction cost, and there is no application case.
그래서 기존 노후된 시멘트 콘크리트 도로의 포장 일부 두께를 약 5㎝ 내외로 절삭 제거한 후에 두께 8~10㎝의 아스팔트 콘크리트로 새로 포장하는 방법으로 보수하거나, 소규모 보수인 경우에는 초속경 폴리머 콘크리트로 보수하고 있다.Therefore, after removing some of the thickness of the existing pavement of cement concrete road to about 5cm and removing it, it is repaired by newly paving with asphalt concrete of 8 ~ 10cm thickness, or in the case of small-scale repair, it is repaired by superhard polymer concrete.
상기와 같이 시멘트 콘크리트 도로 포장 위에 아스팔트 포장으로 보수를 하는 것은 시공이 용이하고 공사비가 저렴하지만, 재포장한 도로 포장이 조기에 파손되고 소성변형에 취약하여 3~4년마다 새롭게 보수를 해야 하는 등의 기술적으로 많은 문제점을 내포하고 있음이 잘 알려져 있다.Repairing with asphalt pavement on cement concrete pavement as described above is easy to construct and inexpensive to construct, but the repaved pavement is damaged early and vulnerable to plastic deformation. It is well known that there are many technical problems.
또한 현재 국내에 일부 적용되고 있는 고무질계 개질 콘크리트(LMC: Latex Modified Concrete)에 의한 보수는 공사비가 고가이고, 1일 시공능력이 소량이며 반드시 습윤양생을 해야 하는 등 대규모 포장 보수의 경우에는 적용하기 어려운 문제점이 있다.In addition, repairs by latex modified concrete (LMC), which are partially applied in Korea, are expensive in terms of construction cost, have a small amount of construction capability per day, and must be cured. There is a difficult problem.
이에 본 발명은 상기와 같은 종래의 제반 문제점을 해결하기 위해 제안된 것으로, 본 발명의 목적은 콘크리트 도로면을 재포장함에 있어서 초속경 시멘트와 건조모래를 혼합한 레미탈을 이용하여 강도의 조기발현, 부착 강도의 확보, 모재와의 친화성, 동결융해 저항성, 내화학적 안정성을 향상시키는 데에 있다.Accordingly, the present invention has been proposed to solve the conventional problems as described above, and an object of the present invention is the early expression of strength by using a cementitized cemented carbide and dry sand in resurfacing concrete road surfaces In order to secure adhesion strength, affinity with the base metal, freeze-thawing resistance, and chemical stability.
본 발명의 다른 목적은 레미탈과 혼합 재료를 혼합하고 공급하는 혼합장비를 통하여 효율적인 콘크리트 도로를 재포장하는 데에 있다.Another object of the present invention is to repave an efficient concrete road through a mixing device for mixing and supplying a remittal and a mixed material.
본 발명의 또 다른 목적은 콘크리트 도로를 재포장함에 있어서 기존 도로의 차량 통행에 문제가 없도록 하여 안전하게 작업할 수 있는 효과가 있다.Another object of the present invention is to re-paved the concrete road there is no effect on the traffic of the vehicle of the existing road has the effect that can work safely.
본 발명인 레미탈을 이용한 콘크리트 포장의 재포장 공법은 재포장할 도로면을 절삭 제거한 후 절삭면을 청소하는 절삭 및 청소단계, 초속경 시멘트와 건조모래를 혼합한 레미탈을 제조하는 레미탈 제조단계, 혼합장비를 이용하여 상기 레미탈과, 자갈, 아크릴 중합체 분산제, 물 및 혼화제를 혼합하여 혼합 콘트리트를 제조하는 혼합 콘크리트 제조단계, 상기 혼합 콘크리트를 포설장비를 이용하여 상기 절삭면에 포설하는 포설단계, 상기 포설단계 후 조면 마무리 장비를 이용하여 조면 마무리하는 조면 마무리단계, 상기 조면 마무리 단계 후 양생제를 사용하지 않고 대기 중에서 양생하는 양생단계, 상기 양생단계 후 줄눈을 시공하는 줄눈시공단계를 포함하여 이루어진다.The repaving method of concrete pavement using the present invention remittal cutting and cleaning step of cleaning the cutting surface after cutting off the road surface to be repaved, the remittal manufacturing step of manufacturing a remittal mixed cemented carbide and dry sand Preparing a mixed concrete by mixing the remittal, gravel, acrylic polymer dispersant, water and admixture using a mixing equipment, and installing the mixed concrete on the cutting surface using a laying equipment. Including a rough finishing step to finish the rough finish using the rough finishing equipment after the laying step, curing step in the air without using a curing agent after the finishing finish step, including a joint construction step for constructing the joint after the curing step Is done.
본 발명은 콘크리트 도로면을 재포장함에 있어서 초속경 시멘트와 건조모래를 혼합한 레미탈을 이용하여 강도의 조기발현, 부착 강도의 확보, 모재와의 친화성, 동결융해 저항성, 내화학적 안정성을 향상시키는 효과가 있다.The present invention improves the early expression of strength, securing the adhesion strength, affinity with the base metal, freeze-thawing resistance, and chemical resistance by using a remittal mixed with cemented carbide and dry sand in resurfacing the concrete road surface. It is effective to let.
또한 레미탈과 혼합 재료를 혼합하고 공급하는 혼합장비를 통하여 공사비용 및 작업시간을 줄일 수 있는 효과가 있다.In addition, there is an effect that can reduce the construction cost and work time through the mixing equipment for mixing and supplying the remittal and mixed materials.
또한 특수하게 설계된 재포장용 장비를 사용하여 포장함으로써 도로에 통행 중인 차량이 원활하게 소통될 수 있도록 하는 효과가 있다.In addition, by using specially designed repackaging equipment, there is an effect that the vehicles on the road can communicate smoothly.
본 발명에 의한 레미탈을 이용한 콘크리트 포장의 재포장 공법의 바람직한 실시예를 첨부한 도면에 의거하여 상세히 설명하면 다음과 같다.When described in detail on the basis of the accompanying drawings a preferred embodiment of the re-packaging method of concrete pavement using the remittal according to the present invention.
하기에서 본 발명을 설명함에 있어 관련된 공지 기능 또는 구성에 대한 구체적인 설명이 본 발명의 요지를 불필요하게 흐릴 수 있다고 판단되는 경우에는 그 상세한 설명을 생략할 것이다. 그리고 후술되는 용어들은 본 발명에서의 기능을 고려하여 정의된 용어들로서, 이는 사용자, 운용자의 의도 또는 판례 등에 따라 달라질 수 있으며, 이에 따라 각 용어의 의미는 본 명세서 전반에 걸친 내용을 토대로 해석되어야 할 것이다.In the following description of the present invention, detailed descriptions of well-known functions or configurations will be omitted if it is determined that the detailed description of the present invention may unnecessarily obscure the subject matter of the present invention. In addition, terms to be described below are terms defined in consideration of functions in the present invention, which may vary according to intention or precedent of a user or an operator, and thus, the meaning of each term should be interpreted based on the contents throughout the present specification. will be.
먼저 본 발명인 레미탈을 이용한 콘크리트 포장의 재포장 공법은 재포장할 도로면을 절삭 제거한 후 절삭면을 청소하는 절삭 및 청소단계, 초속경 시멘트와 건조모래를 혼합한 레미탈을 제조하는 레미탈 제조단계, 혼합장비를 이용하여 상기 레미탈과, 자갈, 아크릴 중합체 분산제, 물 및 혼화제를 혼합하여 혼합 콘트리트를 제조하는 혼합 콘크리트 제조단계, 상기 혼합 콘크리트를 포설장비를 이용하여 상기 절삭면에 포설하는 포설단계, 상기 포설단계 후 조면 마무리 장비를 이용하여 조면 마무리하는 조면 마무리단계, 상기 조면 마무리 단계 후 양생제를 사용하지 않고 대기 중에서 양생하는 양생단계, 상기 양생단계 후 줄눈을 시공하는 줄눈시공단계를 포함하여 이루어진다.First, the repaving method of concrete pavement using the present invention, the re-packing method of cutting and cleaning the cutting surface after removing the road surface to be repaved, the manufacturing of the remittal manufacturing a remixed cemented carbide and dry sand Step, a mixed concrete manufacturing step of producing a mixed concrete by mixing the remittal, gravel, acrylic polymer dispersant, water and admixture using a mixing equipment, laying the mixed concrete on the cutting surface using a laying equipment Step, the rough finishing step to finish the rough surface using the rough finishing equipment after the laying step, curing step in the air without using the curing agent after the rough finish step, including the joint construction step for constructing the joint after the curing step It is done by
본 발명의 다른 실시예로 상기 레미탈은 레미탈의 총중량을 기준으로 하여 초속경 시멘트는 30~40 중량%, 건조모래는 60~70 중량%인 것이 바람직하다.In another embodiment of the present invention, the cemented cement is 30 to 40% by weight, and the dry sand is 60 to 70% by weight based on the total weight of the resin.
본 발명의 또 다른 실시예로 상기 혼합장비에서 혼합하는 혼합 콘크리트는 레미탈이 1000~1200㎏일 때를 기준으로 하여 자갈은 900~1100㎏, 아크릴 중합체 분산제는 50~80㎏, 물은 80~120㎏, 혼화제는 0.01~0.5㎏의 중량으로 혼합되는 것이 바람직하다.In another embodiment of the present invention, the mixed concrete to be mixed in the mixing equipment is based on when the remital is 1000 ~ 1200kg gravel 900 ~ 1100kg, acrylic polymer dispersant 50 ~ 80kg, water 80 ~ It is preferable that 120 kg and a admixture are mixed by the weight of 0.01-0.5 kg.
본 발명의 또 다른 실시예로 상기 혼합장비는 레미탈 저장 사일로, 자갈 저장 빈, 아크릴 중합체 분산제 탱크, 물탱크, 혼화제 저장통, 믹서, 혼합 콘크리트의 혼합재료를 중량으로 계량하는 계량장치, 제어장치를 포함하여 구성될 수 있다.In another embodiment of the present invention, the mixing device is a remitter storage silo, gravel storage bin, acrylic polymer dispersant tank, water tank, admixture reservoir, mixer, a metering device, the control device for weighing the mixed material of mixed concrete by weight It can be configured to include.
본 발명의 또 다른 실시예로 상기 혼합장비는 자주식으로 작업현장으로 이동이 가능하고, 이동 중에도 연속적인 작업이 가능한 것이 바람직하다.In another embodiment of the present invention, the mixing equipment can be moved to a work site on an independent basis, and it is preferable that continuous work can be performed during the movement.
본 발명의 또 다른 실시예로 상기 포설장비는 호퍼, 벨트 컨베이어, 무한궤도식 4트랙의 후방에 위치하고 콘크리트를 고르게 펴주는 스프레딩 장치, 콘크리트 다짐용 바이브레이터, 포설마무리 장치를 포함하여 구성될 수 있다.In another embodiment of the present invention, the installation equipment may be configured to include a spreading device, a concrete compacting vibrator, a laying and finishing device located at the rear of the hopper, belt conveyor, trackless four tracks.
본 발명의 또 다른 실시예로 상기 포설마무리 장치의 도로점유폭은 4m 이하인 것으로 구성될 수 있다.In still another embodiment of the present invention, the road occupancy width of the laying finishing device may be configured to be 4 m or less.
본 발명의 또 다른 실시예로 상기 줄눈시공단계는 재포장한 콘크리트의 압축 강도가 8~12㎫에 도달하면 쏘컷터를 이용하여 줄눈을 시공하는 것이 바람직하다.In another embodiment of the present invention, in the joint construction step, when the compressive strength of the repacked concrete reaches 8 to 12 MPa, it is preferable to construct the joint using a saw cutter.
이하 본 발명의 바람직한 일실시예를 설명하기로 한다. 하기 설명은 일실시예일 뿐이고 본 발명은 이것에 국한되지 않는다.Hereinafter, a preferred embodiment of the present invention will be described. The following description is only one example and the present invention is not limited thereto.
본 발명은 대규모의 콘크리트 포장 재포장에도 적용이 가능한 보다 저렴하고, 시공성이 있는 콘크리트 포장의 재포장(ReSurfacing of Concrete Pavement, 이하 RSCP 공법이라 한다.) 공법이다.The present invention is a cheaper, constructible concrete pavement resurfacing (hereinafter referred to as RSCP method) method that can be applied to large-scale concrete pavement resurfacing.
RSCP 공법에 사용되는 시멘트 콘크리트의 요구조건은 다음과 같다.The requirements for cement concrete used in the RSCP process are as follows.
RSCP용 시멘트 콘크리트는 포설완료 후 3시간 만에 21㎫의 압축강도를 가지는 강도의 신속한 발현, 비건조수축(Non drying Shrinkage), 1종 포틀랜드 시멘트 콘크리트 부착강도의 3.0배 정도인 양호한 부착강도, 기존 콘크리트와 유사한 탄성계수와 열팽창계수를 가짐에 따른 모재(Substrate)와의 상호 친화성(Compatibility: 온도, 하중에 의한 변형을 같게 하여 일체로 거동함으로써 유해한 응력발생을 제거하여 내구성 확보), 동결융해저항성(Resistance to Freeze-thaw), 염화칼슘(CaCl2), 소금(NaCl) 등의 제설제에 대한 내화학적 안정성 등이 확보되어야 한다.Cement concrete for RSCP has a rapid development of strength with a compressive strength of 21 MPa after 3 hours of laying, non drying shrinkage, good adhesion strength of 3.0 times that of one Portland cement concrete, Compatibility with the substrate due to the elasticity and thermal expansion coefficient similar to concrete (Compatibility: ensures durability by eliminating harmful stresses by acting integrally by equal deformation by temperature and load), freeze-thawing resistance ( Resistance to freeze-thaw, calcium chloride (CaCl 2 ), and salt (NaCl), etc., should be secured against chemical stability.
보수재료(Repair Material)로서의 시멘트 콘크리트에 대한 필요조건은 국제 콘크리트 보수협회 (ICRI: International Concrete Repair Institute)에서 발행된 콘크리트 보수지침(Concrete Repair Mannual)에 기술되어 있다.Requirements for cement concrete as repair materials are described in the Concrete Repair Mannual issued by the International Concrete Repair Institute (ICRI).
따라서 본 발명에 사용되는 콘크리트는 상기와 같은 요구조건을 만족할 수 있다.Therefore, the concrete used in the present invention can satisfy the above requirements.
먼저 재포장할 콘크리트 도로면 포장의 일부 두께를 노면절삭기(Road Cutter)를 통해 절삭 제거한 후 재포장할 절삭면을 청소를 위한 솔을 장착한 스키드로우더(Skid Loader)와 고압분사기(High pressure water jet)로 잔재물을 제거하고, 일부 열화부위를 깨끗이 청소한다(ST1).First, a part of the thickness of the concrete pavement to be repaved is cut through a road cutter, and then a skid loader and a high pressure water jet equipped with a brush for cleaning the cut to be repaved. ) To remove the residue and to clean some deterioration areas (ST1).
본 발명은 작업현장에서 초속경으로 콘크리트가 제조되어야 하기 때문에 초속경 시멘트와 건조모래를 혼합하여 혼합물을 제조한다(ST2). 상기 혼합물은 이하 레미탈(Remitar)라고 한다.In the present invention, since the concrete should be manufactured with a cemented carbide at the work site, the cemented cement and the dry sand are mixed to produce a mixture (ST2). This mixture is hereinafter referred to as Remitar.
이때 상기 레미탈은 레미탈의 총중량을 기준으로 하여 초속경 시멘트는 30~40 중량%, 건조모래는 60~70 중량%인 것이 바람직하고, 더욱 바람직하게는 초속경 시멘트는 36 중량%, 건조모래는 64 중량%이다.In this case, the remittal is preferably based on the total weight of the remittal cemented carbide cement is 30 to 40% by weight, dry sand is 60 to 70% by weight, more preferably cemented carbide cement 36% by weight, dry sand is 64 weight percent.
상기 레미탈을 제조공장에서 제조하여 별도의 장비를 이용하여 작업현장으로 운반을 한다. 상기 장비는 후술한다.The remittal is manufactured in a manufacturing plant and transported to a work site using separate equipment. The equipment will be described later.
본 발명의 콘크리트를 위한 혼합재료는 상기 레미탈과, 자갈, 아크릴 중합체 분산제, 물 및 혼화제를 포함하여 구성된다.The mixed material for the concrete of the present invention comprises the remittal, gravel, acrylic polymer dispersant, water and admixture.
상기 자갈은 Ø13~19㎜ 정도의 크기가 바람직하다.The gravel is preferably a size of about 13 ~ 19㎜.
상기 아크릴 중합체 분산제를 사용하는 목적은 그동안 널리 보급된 스티렌 부타디엔 라텍스를 사용하는 고무질계 개질 콘크리트(LMC: Latex Modified Concrete)를 사용할 경우 포설 후 양생 시 반드시 습윤 양생포(Wet Burlap)와 폴리 에틸렌 필름 등으로 덮는 습윤양생(Wet Curing)을 하여야 하는데, 대규모 면적의 경우 소요재료, 소요인력, 소요시간의 측면에서 현실적으로 불가능하고 불합리한 문제점이 있다. 하지만 아크릴 중합체 분산제를 사용한 콘크리트는 미국에서의 이용사례와 미국콘크리트협회 위원회 548(ACI Committee 548) 문헌에서 알려진 바와 같이 대기중 양생(Air Curing)이 가능하고, 또한 상기 스티렌 부타디엔 라텍스보다 콘크리트 1㎥ 당 투입량이 절반 정도만 소요되어 경제적으로도 훨씬 유리하다. 또한 강도의 조기발현, 부착 강도의 확보, 모재와의 친화성, 동결융해 저항성, 내화학적 안정성을 향상시키는 효과가 있다.The purpose of using the acrylic polymer dispersant is that when using rubber-based modified concrete (LMC: Latex Modified Concrete) using styrene butadiene latex, which has been widely used, it is necessary to wet wet lap (Wet Burlap) and polyethylene film during curing. Wet Curing should be covered with, but in the case of a large area, there is a practically impossible and unreasonable problem in terms of required materials, required labor, and required time. However, concrete using acrylic polymer dispersant is capable of air curing as known in the US and ACI Committee 548, and also per cubic meter of concrete than the styrene butadiene latex. Only half the input is economically advantageous. In addition, there is an effect of improving the early expression of strength, securing the adhesion strength, affinity with the base material, resistance to freezing and thawing, and chemical stability.
본 발명은 상기 혼합재료를 혼합하여 초속경 혼합 콘크리트를 생산하기 위하여 일반적으로 사용되는 용적측정의 이동식믹서(Volumetric Mobile Mixer)를 사용하지 않고, 엄격한 품질관리와 비용절감을 위해 별도의 혼합장비를 이용하여 제조한다(ST3).The present invention does not use a volumetric mobile mixer (Volumetric Mobile Mixer) generally used to produce the cemented carbide mixed concrete by mixing the mixed material, using a separate mixing equipment for strict quality control and cost reduction To prepare (ST3).
상기 혼합장비는 이동식 콘크리트 배치 플랜트(MCBP: Mobile Concrete Batch Plant)로 불리며, 이하 MCBP라 한다.The mixing equipment is called a mobile concrete batch plant (MCBP), hereinafter referred to as MCBP.
일반적으로 콘크리트 제조를 위한 재료의 공급 시 모래, 자갈을 각각을 적재한 덤프트럭에서 굴삭기(Back Hoe)를 이용하여 콘크리트 믹서(Concrete Mixer)에 재료를 투입하는데, 상기 덤프트럭을 교대로 계속하여 굴삭기에 접근시키면서 작업해야 하기 때문에 작업 효율은 매우 저하되고, 또한 모래의 경우 보관 상태와 일기에 따라 함수비가 크게 변하여 균일한 품질의 콘크리트를 생산하는데 장애가 될 뿐만 아니라 협소한 작업 공간에서 작업하는 경우 안전에 매우 취약한 문제점이 있 다.In general, when supplying materials for manufacturing concrete, a dump truck loaded with sand and gravel is used to input materials to a concrete mixer using a back hoe, and the dump trucks are alternately continued. The work efficiency is very low because the work must be done in close proximity to the sand, and in the case of sand, the water content varies greatly depending on the storage conditions and weather conditions, which not only prevents the production of concrete of uniform quality, but also the safety of working in a narrow work space. There is a very weak problem.
따라서 본 발명의 MCBP는 레미탈 저장 사일로, 자갈저장빈, 아크릴 중합체 분산제 탱크, 물탱크, 혼화제 저장통, 믹서(Mixer), 혼합 콘크리트의 혼합재료를 중량으로 계량하는 계량장치, 믹서로 보내주는 벨트 컨베이어, 스크류 컨베이어, 파이프, 에어 컴프레셔, 제너레이터, 컴퓨터 제어 패널 등을 포함하여 구성된다.Therefore, the MCBP of the present invention is a belt conveyor to send a remitter storage silo, gravel storage bin, acrylic polymer dispersant tank, water tank, admixture reservoir, mixer (Mixer), a weighing device for mixing the mixed material of mixed concrete by weight , Including screw conveyors, pipes, air compressors, generators, computer control panels and the like.
상기 MCBP는 견인차(Tractor)가 견인하는 로우베드 트레일러(Low-bed Trailer) 위에 장착되고 자주식으로 작업현장으로 이동할 수 있고, 연속적으로 이동하면서 작업이 가능한 장점이 있다.The MCBP is mounted on a low-bed trailer pulled by a tractor and can move to a work site on an autonomous basis.
상기 MCBP는 시간당 약 30㎥의 혼합 콘크리트 생산능력을 가지며 혼합하여 배출된 콘크리트는 포설장비의 호퍼(Hopper)로 투입된다.The MCBP has a mixed concrete production capacity of about 30㎥ per hour and the concrete discharged by mixing is put into a hopper (Hopper) of the installation equipment.
상기 MCBP에서 혼합되는 혼합 콘크리트는 레미탈이 1000~1200㎏일 때를 기준으로 하여 자갈은 900~1100㎏, 아크릴 중합체 분산제는 50~80㎏, 물은 80~120㎏, 혼화제는 0.01~0.5㎏의 중량으로 혼합되는 것이 바람직하다.The mixed concrete to be mixed in the MCBP is based on when the remittal is 1000 ~ 1200kg gravel 900 ~ 1100kg, acrylic polymer dispersant 50 ~ 80kg, water 80 ~ 120kg, admixture 0.01 ~ 0.5kg It is preferable to mix by weight of.
상기 혼합 콘크리트를 제조하면 포설장비를 통하여 도로면에 포설한다(ST4).When the mixed concrete is manufactured, it is laid on the road surface through the laying equipment (ST4).
일반적으로 콘크리트 도로면의 포장에 사용되는 기존 포장 장비는 신설도로 포장 작업에 적합하며, 공용 중인 기존 도로에서 재포장시 사용하기에는 포설작업의 폭원으로 인하여 차량 통행 및 시공상에 문제점이 있다.In general, the existing paving equipment used for paving concrete road surfaces is suitable for paving new roads, and there is a problem in vehicle traffic and construction due to the width of the paving work for repaving on existing roads in common use.
따라서 본 발명은 별도의 포설장비를 사용하며 상기 포설장비는 스프레딩 장치를 무한궤도 4트랙의 후방에 구성하여 장비의 점유폭을 4m로 축소 설계함에 따라 기존 도로의 차량 통행에 문제가 없도록 하여 안전하게 작업할 수 있는 장점이 있 다.Therefore, the present invention uses a separate laying equipment and the laying equipment is designed to reduce the occupancy of the equipment to 4m by configuring the spreading device to the rear of the track 4 tracks so that there is no problem in the traffic of the existing road There is an advantage to working.
상기 무한궤도 4트랙은 무한궤도 트랙이 앞뒤 각각 2개씩으로 구성되어 각 트랙이 개별적으로 작동한다.The track 4 tracks are composed of two track tracks, each of which is operated separately.
상기 포설장비는 호퍼, 벨트 컨베이어, 무한궤도식 4트랙의 후방에 위치하고 콘크리트를 고르게 펴주는 스프레딩 장치, 콘크리트 다짐용 바이브레이터, 포설 마무리 장치를 포함하여 구성된다.The installation equipment includes a hopper, a belt conveyor, a spreading device for evenly spreading concrete, a concrete compacting vibrator, and a laying finishing device located at the rear of the track 4 track.
상기 콘크리트 포설 후에는 조면 마무리(Texturing) 시공을 한다(ST5).After the concrete installation is roughing (Texturing) construction (ST5).
상기 조면 마무리는 콘크리트 도로면의 신설포장 시와 동일한 방법으로 조면 마무리 장비(Texturing Machine)를 이용하여 횡방향 또는 종방향으로 타이닝(Tinning)을 한다.The rough finish is made in the same way as when paving concrete road surface using a roughing finishing machine (Texturing Machine) in the transverse direction or longitudinal direction (Tinning).
상기 조면 마무리 후에는 양생(Curing)을 한다(ST6).After finishing the rough surface, curing is performed (ST6).
상기 양생은 별도의 양생제 살포없이 대기 중에서 양생을 실시한다.The curing is carried out in the atmosphere without spraying a separate curing agent.
상기 양생 후에는 줄눈시공을 한다(ST7).After curing, joint construction is performed (ST7).
상기 줄눈시공은 본 발명인 혼합 콘크리트의 압축강도가 10㎫(약 1.5hr)에 도달하면 쏘컷터(Saw Cutter)와 인력을 사용하여 콘크리트 도로면의 신설포장의 경우와 같은 방법으로 줄눈을 시공하고, 교통 개방에 필요한 기준 강도(21㎫, 3,000psi)가 발현되면 교통제한을 해제하고 작업을 완료한다.When the joint construction of the present invention reaches a compressive strength of 10 MPa (about 1.5 hr) of the mixed concrete of the present invention, the joint is constructed in the same manner as in the case of the new pavement of the concrete road surface using a saw cutter and a manpower. When the standard strength (21 MPa, 3,000 psi) is required to open the traffic, lift the traffic restriction and complete the work.
상기와 같이 본 발명인 레미탈을 이용한 콘크리트 포장의 재포장 공법은 콘크리트 도로면을 재포장함에 있어서 초속경 시멘트와 건조모래를 혼합한 레미탈을 이용하여 강도의 조기발현, 부착강도의 확보, 모재와의 친화성, 동결융해 저항성, 내화학적 안정성을 향상시키고, 또한 레미탈과 혼합 재료를 혼합하고 공급하는 혼합장비를 통하여 공사비용 및 작업시간을 줄일 수 있으며, 기존 도로의 차량 통행에 문제가 없도록 하여 안전하게 작업할 수 있는 효과가 있다.As described above, the repaving method of concrete pavement using the remittal of the present invention uses the remittal mixed with cemented carbide and dry sand in resurfacing the concrete road surface. It improves the affinity, freeze-thawing resistance and chemical stability of the product, and also reduces the construction cost and working time through the mixing equipment that mixes and supplies the remittal and the mixed material. It has the effect of working safely.
이상과 같이 본 발명은 비록 한정된 실시예를 설명하였으나, 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정되어 해석되어서는 아니되며, 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다. 따라서 본 명세서에 기재된 실시 예와 도면에 도시된 구성은 본 발명의 일실시예에 불과할 뿐이고 본 발명의 기술적 사상을 모두 대변하는 것은 아니므로, 본 출원시점에 있어서 이들을 대체할 수 있는 다양한 균등물과 변형예들이 있을 수 있음을 이해하여야 한다.As described above, although the present invention has been described in a limited embodiment, the terms or words used in the specification and claims are not to be construed as being limited to ordinary or dictionary meanings, and meanings consistent with the technical spirit of the present invention. It must be interpreted as a concept. Therefore, the embodiments described in the specification and the drawings shown in the drawings are only one embodiment of the present invention and do not represent all of the technical idea of the present invention, and various equivalents that may be substituted for them at the time of the present application and It should be understood that there may be variations.
도 1은 본 발명의 제조 방법에 대해 단계별로 나타낸 흐름도.1 is a flow chart showing step by step for the manufacturing method of the present invention.
Claims (8)