KR100851660B1 - Metal ultra thin plate for a switch button device and preparing method the same - Google Patents

Metal ultra thin plate for a switch button device and preparing method the same Download PDF

Info

Publication number
KR100851660B1
KR100851660B1 KR1020080024690A KR20080024690A KR100851660B1 KR 100851660 B1 KR100851660 B1 KR 100851660B1 KR 1020080024690 A KR1020080024690 A KR 1020080024690A KR 20080024690 A KR20080024690 A KR 20080024690A KR 100851660 B1 KR100851660 B1 KR 100851660B1
Authority
KR
South Korea
Prior art keywords
metal sheet
switch button
metal
silver
elastic
Prior art date
Application number
KR1020080024690A
Other languages
Korean (ko)
Inventor
박성제
박철민
Original Assignee
박성제
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 박성제 filed Critical 박성제
Priority to KR1020080024690A priority Critical patent/KR100851660B1/en
Application granted granted Critical
Publication of KR100851660B1 publication Critical patent/KR100851660B1/en
Priority to CN2009801090271A priority patent/CN101978448A/en
Priority to PCT/KR2009/001165 priority patent/WO2009116739A2/en

Abstract

A thin metal plate for a switch button device and a manufacturing method thereof are provided to improve quality of the switch button device by firmly plating nickel or silver on a surface thereof. A manufacturing method of a thin metal plate for a switch button device includes the steps of: forming a metal sheet by rolling a metal hot coil; forming an elastic metal sheet by performing heat treatment at 450 to 520 degrees centigrade for removing internal stress of the metal sheet and for providing the metal sheet with elasticity; washing surface of the elastic metal sheet and washing the elastic metal sheet with acid material for forming a thin film oxide on the surface of the elastic metal sheet; forming a coating layer by electro-plating nickel or silver on the surface of the elastic metal sheet; and slitting the elastic metal sheet into pieces of regular size.

Description

스위치 버튼 소자용 금속박판 및 그 제조 방법{METAL ULTRA THIN PLATE FOR A SWITCH BUTTON DEVICE AND PREPARING METHOD THE SAME}Metal plate for switch button element and manufacturing method therefor {METAL ULTRA THIN PLATE FOR A SWITCH BUTTON DEVICE AND PREPARING METHOD THE SAME}

본 발명은 각종 전자기기의 스위치 버튼에 사용되는 소자의 기재인 금속박판에 관한 것으로, 상세하게는 금속박판의 표면에 니켈 또는 은이 전해도금되어 강력하게 결착되므로, 금속박판을 프레스 가공하여 소자를 형성할 때 니켈 또는 은이 탈리되지 않기 때문에 소자의 품질이 대폭 향상되고, 탈리되는 니켈 또는 은분말로 인한 금형 또는 프레스 장치의 손상을 방지할 수 있는 스위치 버튼 소자용 금속박판 및 그 제조 방법에 관한 것이다.BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a metal thin plate, which is a base material of a device used in switch buttons of various electronic devices. Specifically, nickel or silver is electroplated and bound strongly on the surface of the metal thin plate, so that the metal thin plate is pressed to form an element. When the nickel or silver is not detached when the quality of the device is significantly improved, and a metal sheet for a switch button element that can prevent damage to the mold or press device due to the nickel or silver powder is removed and a method for manufacturing the same.

근래에 휴대폰, 리모컨, 디지털카메라, MP3, 네비게이션 등과 같은 각종 정보통신기기류나 의료장비, 정밀 공작기기 등과 같은 각종 업무용 기기류 뿐만 아니라, TV, 냉장고 등과 같은 일반 가전기기류에서도 다기능화가 진전됨에 따라서, 이러한 기기류에 설치되어야 하는 스위치 버튼의 수효가 지속적으로 증가되고 있으며, 스위치 버튼 자체의 크기도 소형화되고 있는 추세이다.In recent years, as the multifunctionalization of not only various information and communication devices such as mobile phones, remote controllers, digital cameras, MP3, navigation devices, medical equipment, precision machine tools, but also general household appliances such as TVs and refrigerators, The number of switch buttons that need to be installed on the wall is constantly increasing, and the size of the switch button itself is also becoming smaller.

이러한 소형 스위치 버튼은 내장된 고탄성 금속 재질의 소자가 기기류의 포인트 접점에 착탈되므로써 상기 기기류의 작동을 ON/Off하거나 컨트롤하도록 구성되며, 상기 소자는 450∼520 ℃의 열처리에 의해 고탄성력이 제공된 금속 재질의 테이프를 프레스 장치에 세트하고 금형에서 프레스 가공하여 이루어진다.The small switch button is configured to turn on / off or control the operation of the device by detaching a built-in high elastic metal element at a point contact of the device, and the device is a metal provided with high elasticity by heat treatment at 450 to 520 ° C. It is made by placing a tape of material in a press apparatus and pressing in a mold.

그런데, 스위치 버튼 소자를 제조하기 위한 금속박판은 스위치 버튼 소자에 요구되는 전기적 특성을 향상시키기 위하여, 스테인레스 스틸, 인동청 등과 같은 금속재료를 두께 0.025 ∼ 0.08 ㎜의 쉬트 형태로 가공하고 탄성이 제공되도록 450∼520 ℃로 열처리하여 형성된 기재의 표면에 니켈 또는 은을 코팅 가공하는 것이 필수적인 요구사항이라고 할 수 있다. 상기와 같은 요구사항을 충족하기 위하여, 종래에는 열처리되어 탄성이 제공된 기재인 두께 0.025 ∼ 0.08 ㎜의 금속 쉬트의 일측 또는 양측 표면에 금속 분말을 분사하여 코팅 가공한 후에, 후가공 공정을 거쳐서 스위치 버튼 소자용 금속박판을 제조하였다. However, in order to improve the electrical characteristics required for the switch button element, the metal thin plate for manufacturing the switch button element is processed into a sheet material having a thickness of 0.025 to 0.08 mm and elasticity is provided so as to provide elasticity. It is an essential requirement to coat nickel or silver on the surface of the substrate formed by heat treatment at 450 to 520 캜. In order to meet the above requirements, the switch button element is conventionally subjected to a post-processing process after spraying metal powder on one or both surfaces of a metal sheet having a thickness of 0.025 to 0.08 mm, which is heat-treated to provide elasticity. A metal thin plate was prepared.

상기와 같이 기재인 금속 쉬트의 표면에 금속 분말을 분사하여 코팅시켜서 형성된 종래의 스위치 버튼 소자용 금속박판은 비록 생산이 용이하기는 하지만, 기재인 금속 쉬트와 코팅된 금속 분말 사이의 결착력이 매우 취약하기 때문에, 소자를 제조하기 위하여 스위치 버튼 소자용 금속박판을 프레스 장치에 세트하고 금형에서 프레스 가공하여 스위치 버튼 소자를 제조할 때, 상기 금속박판로부터 금속 분말이 쉽게 탈리된다. 스위치 버튼 소자용 금속박판로부터 금속 분말이 탈리되면, 제조되는 스위치 버튼 소자의 품질이 크게 저하될 뿐만 아니라, 탈리되어 금형 또는 소자에 달라붙은 금속 분말을 제거하기 위한 별도의 시간과 노력이 소요되어 스위치 버튼 소자 제조의 작업효율이 매우 저하된다는 문제점이 있다. 게다가, 상기 스위치 버튼 소자용 금속박판로부터 탈리된 금속 분말이 소자를 제조하는 금형을 손상시킬 뿐만 아니라, 프레스 장치에까지 악영향을 미쳐서 상기 프레스 장치의 고 장을 유발하거나 수명을 단축시킬 수 있다는 문제점이 있다.The conventional metal sheet for switch button elements formed by spraying and coating metal powder on the surface of the metal sheet as the substrate as described above is very weak in binding force between the metal sheet as the substrate and the coated metal powder, although it is easy to produce. Therefore, in order to manufacture the device, when the metal sheet for switch button elements is placed in a press apparatus and pressed in a mold to produce the switch button element, the metal powder is easily detached from the metal sheet. When the metal powder is detached from the metal thin plate for the switch button element, not only the quality of the switch button element manufactured is greatly reduced, but also a separate time and effort is required to remove the metal powder detached and stuck to the mold or the element. There is a problem that the work efficiency of button element manufacturing is very low. In addition, there is a problem that the metal powder detached from the thin metal plate for the switch button element not only damages the mold for manufacturing the device, but also adversely affects the press device, causing failure of the press device or shortening the lifespan. .

따라서, 본 발명의 목적은 스위치 버튼 소자용 금속박판의 표면에 니켈 또는 은이 전해도금에 의해 강력하게 결착되어 상기 금속박판을 프레스 가공하여 소자를 형성할 때, 표면에서 니켈 또는 은이 탈리되지 않는 스위치 버튼 소자용 금속박판 및 그 제조 방법을 제공하는데 있다.Therefore, an object of the present invention is a switch button that does not detach nickel or silver from the surface when the nickel or silver is strongly bound to the surface of the metal thin plate for switch button elements by electroplating to form a device by press working the metal thin plate. It is to provide a metal thin plate for the device and a method of manufacturing the same.

상기와 같은 과제를 해결하기 위하여, 본 발명에서는 금속 핫코일을 압연하여 형성된 금속 쉬트가 일정한 온도로 열처리되고, 산 세정되고, 그 표면이 니켈 또는 은이 전해도금되어 코팅층이 형성되고, 일정한 사이즈로 슬리팅되어 이루어지는 스위치 버튼 소자용 금속박판이 제공된다.In order to solve the above problems, in the present invention, a metal sheet formed by rolling a metal hot coil is heat-treated at a constant temperature, acid-cleaned, and a surface thereof is electroplated with nickel or silver to form a coating layer, and slitting to a constant size. A metal thin plate for a switch button element is provided.

또한, 본 발명에서는 금속 핫코일을 압연하여 금속 쉬트를 형성하는 단계: 상기 금속 쉬트의 내부응력을 제거하고 탄성을 제공하도록 일정한 온도로 열처리하여 탄성 금속 쉬트를 형성하는 단계; 상기 탄성 금속 쉬트의 표면을 세정하고 산화피막을 형성하도록 산 세정하는 단계; 상기 산 세정된 탄성 금속 쉬트의 표면에 니켈 또는 은을 전해도금하여 코팅층을 형성하는 단계; 상기 코팅층이 형성된 탄성 금속 쉬트를 일정한 사이즈로 슬리팅하는 단계를 포함하는 스위치 버튼 소자용 금속박판의 제조 방법이 제공된다.In addition, the present invention comprises the steps of forming a metal sheet by rolling a metal hot coil: forming an elastic metal sheet by heat treatment at a constant temperature to remove the internal stress of the metal sheet and to provide elasticity; Cleaning the surface of the elastic metal sheet and acid cleaning to form an oxide film; Forming a coating layer by electroplating nickel or silver on the surface of the acid-cleaned elastic metal sheet; Provided is a method of manufacturing a metal sheet for a switch button element comprising the step of slitting an elastic metal sheet having a coating layer formed in a predetermined size.

본 발명에 의하여 제조되는 스위치 버튼 소자용 금속박판은 그 표면에 니켈 또는 은이 전해도금에 의해 강력하게 결착되어 상기 금속박판을 프레스 가공하여 소자를 형성할 때 표면에서 니켈 또는 은이 탈리되지 않기 때문에 제조된 스위치 버튼 소자의 품질이 크게 향상되며, 탈리되어 금형 또는 소자에 달라붙은 금속 분말을 제거하기 위한 별도의 시간과 노력이 소요되지 않아서 스위치 버튼 소자 제조의 작업효율이 크게 개선되는 효과를 지니고 있다.The metal thin plate for the switch button element manufactured according to the present invention is manufactured because nickel or silver is strongly bound to its surface by electroplating, and thus nickel or silver does not detach from the surface when the metal thin plate is pressed to form an element. The quality of the switch button element is greatly improved, and since it takes no time and effort to remove metal powder attached to the mold or the element due to detachment, the work efficiency of the switch button element manufacturing is greatly improved.

또한, 본 발명의 스위치 버튼 소자용 금속박판은 표면에서 탈리되는 니켈 또는 은 분말로 인한 금형 또는 프레스 장치의 손상을 방지할 수 있다.In addition, the metal thin plate for the switch button element of the present invention can prevent damage to the mold or press apparatus due to nickel or silver powder detached from the surface.

본 발명에 의한 스위치 버튼 소자용 금속박판에 대하여 실시예를 참조하여 상세하게 설명한다.The thin metal plate for switch button elements according to the present invention will be described in detail with reference to Examples.

본 발명의 스위치 버튼 소자용 금속박판은 기재인 금속 쉬트의 표면에 금속 분말이 분사되어 코팅층이 형성되는 것이 아니라, 니켈 또는 은이 전해도금되어 코팅층이 형성되는 것을 기술적인 특징으로 하고 있다.The metal thin plate for the switch button element of the present invention has a technical feature that the coating layer is formed by electroplating nickel or silver, instead of the metal powder being sprayed on the surface of the metal sheet serving as the base material.

우선, 스테인레스 스틸, 인동청 등의 금속 핫코일이 일정한 두께로 압연되어 스위치 버튼 소자용 금속박판의 베이스인 금속 쉬트가 형성된다. First, metal hot coils, such as stainless steel and phosphor bronze, are rolled to a certain thickness to form a metal sheet which is a base of the metal sheet for switch button elements.

금속 핫코일이 압연 가공되어 형성된 금속 쉬트는 내부 응력이 발생하여 경화된 상태이므로, 금속 쉬트를 사용하여 스위치 버튼 소자용 금속박판을 구성하려면, 상기 금속 쉬트의 내부응력을 제거하고 탄성을 부여해야 한다.Since the metal sheet formed by rolling the metal hot coil is in a hardened state due to internal stress, the internal stress of the metal sheet must be removed and elasticity must be applied to the metal sheet for the switch button element using the metal sheet.

이를 위하여, 이미 공지된 바와 같이 금속 쉬트가 450∼520 ℃로 열처리되어 상기 금속 쉬트의 내부응력이 제거되고 탄성이 부여된 탄성 금속 쉬트가 형성된다.To this end, as already known, the metal sheet is heat-treated at 450 to 520 ° C. to thereby remove the internal stress of the metal sheet and form an elastic metal sheet provided with elasticity.

그런데, 상기에서 기술된 바와 같이 금속 쉬트를 450∼520 ℃로 열처리하게 되면, 상기 금속 쉬트에 탄성이 부여되는 대신, 상기 금속 쉬트의 표면에는 스케일이 발생하게 된다. 상기와 같이 탄성 금속 쉬트의 표면에 스케일이 발생하게 되면, 상기 스케일로 인하여 탄성 금속 쉬트를 전체적으로 균일하게 전해도금하는 것이 곤란하게 되며, 이것은 결국 스위치 버튼 소자용 금속박판의 품질 및 내구성 저하로 연결된다.However, as described above, when the metal sheet is heat-treated at 450 to 520 ° C., elasticity is applied to the metal sheet, and scale is generated on the surface of the metal sheet. When the scale is generated on the surface of the elastic metal sheet as described above, it is difficult to uniformly electroplat the elastic metal sheet as a whole due to the scale, which leads to the deterioration of quality and durability of the metal sheet for switch button element .

이러한 과제를 해결하기 위하여, 탄성 금속 쉬트의 표면 스케일을 제거하는 동시에, 전해도금을 촉진하는 산화피막을 형성하도록 상기 탄성 금속 쉬트를 산으로 세정한다.In order to solve this problem, the elastic metal sheet is washed with an acid to remove the surface scale of the elastic metal sheet and to form an oxide film which promotes electroplating.

탄성 금속 쉬트를 산으로 세정하게 되면, 상기 탄성 금속 쉬트의 표면에서 전해도금을 방해하는 스케일이 제거되는 반면, 전해도금을 촉진하는 산화피막이 생성된다.When the elastic metal sheet is washed with an acid, a scale that prevents electroplating is removed from the surface of the elastic metal sheet, while an oxide film that promotes electroplating is produced.

상기와 같이 탄성 금속 쉬트의 표면에 산화피막이 형성된 상태에서, 상기와 같이 탄성 금속 쉬트를 니켈 또는 은으로 전해도금되어 니켈 또는 은 재질의 코팅층이 형성된다.In the state where the oxide film is formed on the surface of the elastic metal sheet as described above, the elastic metal sheet is electroplated with nickel or silver as described above to form a coating layer of nickel or silver.

탄성 금속 쉬트를 니켈 또는 은으로 전해도금하여 니켈 또는 은 재질의 코팅층을 형성하게 되면, 상기 전해도금된 코팅층이 탄성 금속 쉬트에 강력하게 결착되므로, 상기 탄성 금속 쉬트를 사용하여 구성된 스위치 버튼 소자용 금속박판을 프레스 가공하여 스위치 버튼 소자를 형성할 때, 상기 금속박판로부터 니켈 또는 은이 전혀 탈리되지 않는다는 특성을 지니게 된다.When the electroplated elastic metal sheet with nickel or silver forms a coating layer made of nickel or silver, the electroplated coating layer is strongly bound to the elastic metal sheet, so that the switch button element metal is constructed using the elastic metal sheet. When the thin plate is pressed to form a switch button element, it has a characteristic that no nickel or silver is detached from the metal thin plate at all.

상기와 같이 표면에 니켈 또는 은 재질의 코팅층이 형성된 탄성 금속 쉬트가 일정한 사이즈로 슬리팅되고, 릴에 권취되어 본 발명의 스위치 버튼 소자용 금속박판이 구성된다.As described above, an elastic metal sheet having a nickel or silver coating layer formed on the surface is slit to a certain size and wound on a reel to constitute a metal thin plate for a switch button element of the present invention.

상기 스위치 버튼 소자용 금속박판을 프레스 장치에 세트하고 금형에서 프레스 가공하여 스위치 버튼 소자를 제조한다. 스위치 버튼 소자용 금속박판을 사용하여 스위치 버튼 소자를 제조하는 과정에서, 상기 스위치 버튼 소자용 금속박판로부터 니켈 또는 은이 전혀 탈리되지 않기 때문에, 제조된 스위치 버튼 소자의 품질이 크게 향상되며, 탈리되어 금형 또는 소자에 달라붙은 금속 분말을 제거하기 위한 별도의 시간과 노력이 소요되지 않아서 스위치 버튼 소자 제조의 작업효율이 크게 개선된다.The thin metal plate for the switch button element is set in a press device and pressed in a mold to manufacture the switch button element. In the process of manufacturing the switch button element using the metal thin plate for the switch button element, since no nickel or silver is detached from the metal thin plate for the switch button element at all, the quality of the manufactured switch button element is greatly improved, and the mold Alternatively, no time and effort is required to remove the metal powder stuck to the device, thereby greatly improving the work efficiency of the switch button device manufacturing.

본 발명에 의한 스위치 버튼 소자용 금속박판의 제조 방법에 대하여 실시예를 참조하여 상세하게 설명한다.The manufacturing method of the metal thin plate for switch button elements which concerns on this invention is demonstrated in detail with reference to an Example.

우선, 본 발명의 스위치 버튼 소자용 금속박판의 제조 방법은 금속 핫코일을 압연하여 금속 쉬트를 형성하는 단계가 포함된다(단계 S10).First, the manufacturing method of the metal thin plate for switch button elements of this invention includes the step of rolling a metal hot coil, and forming a metal sheet (step S10).

스테인레스 스틸, 인동청 등의 금속 핫코일을 일정한 두께로 압연 가공하여 스위치 버튼 소자용 금속박판의 베이스인 금속 쉬트를 형성한다.Metal hot coils, such as stainless steel and phosphor bronze, are rolled to a certain thickness to form a metal sheet that is the base of the metal sheet for switch button elements.

이러한 금속 쉬트를 베이스로 사용하여 스위치 버튼 소자용 금속박판을 제조한다.Using this metal sheet as a base, a metal sheet for switch button element is manufactured.

또한, 본 발명의 스위치 버튼 소자용 금속박판의 제조 방법은 상기 금속 쉬트의 내부응력을 제거하고 탄성을 제공하도록 450∼520 ℃로 열처리하여 탄성 금속 쉬트를 형성하는 단계가 포함된다(단계 S20).In addition, the method for manufacturing a metal sheet for a switch button element of the present invention includes the step of forming an elastic metal sheet by heat treatment at 450 ~ 520 ℃ to remove the internal stress of the metal sheet and provide elasticity (step S20).

상기 단계 S10에서 금속 핫코일을 압연 가공하여 형성된 금속 쉬트는 상기 압연에 의해 내부 응력이 발생하여 경화된 상태이므로, 금속 쉬트를 사용하여 스위치 버튼 소자용 금속박판을 구성하려면, 상기 금속 쉬트의 내부응력을 제거하고 탄성을 부여해야 한다.Since the metal sheet formed by rolling the metal hot coil in the step S10 is a state in which an internal stress is generated and hardened by the rolling, to construct a metal sheet for switch button element using the metal sheet, the internal stress of the metal sheet may be reduced. Should be removed and given elasticity.

이를 위하여, 금속 쉬트를 450∼520 ℃로 열처리하여 상기 금속 쉬트의 내부응력을 제거하고 스위치 버튼 소자에 요구되는 탄성을 부여한 탄성 금속 쉬트를 형성하는 것이다.To this end, the metal sheet is heat-treated at 450 to 520 ° C. to remove the internal stress of the metal sheet and form an elastic metal sheet provided with the elasticity required for the switch button element.

또한, 본 발명의 스위치 버튼 소자용 금속박판의 제조 방법은 상기 탄성 금속 쉬트의 표면을 세정하고 산화피막을 형성하도록 산 세정하는 단계가 포함된다(단계 S30).In addition, the method for producing a metal sheet for a switch button element of the present invention includes the step of cleaning the surface of the elastic metal sheet and the acid cleaning to form an oxide film (step S30).

상기 단계 S20에서 금속 쉬트를 450∼520 ℃로 열처리하게 되면, 상기 금속 쉬트에 탄성이 부여되는 대신, 상기 금속 쉬트의 표면에는 스케일이 발생한다. 상기와 같이 탄성 금속 쉬트의 표면에 전해도금을 방해하는 스케일이 발생하면, 상기 스케일로 인하여 탄성 금속 쉬트를 전체적으로 균일하게 전해도금하는 것이 곤란하게 되며, 이것은 결국 스위치 버튼 소자용 금속박판의 품질 및 내구성 저하로 연결된다.When the metal sheet is heat-treated at 450 to 520 ° C. in step S20, instead of providing elasticity to the metal sheet, scale is generated on the surface of the metal sheet. If a scale that interferes with electroplating occurs on the surface of the elastic metal sheet as described above, it is difficult to uniformly electroplat the elastic metal sheet as a whole due to the scale, which in turn results in the quality and durability of the metal sheet for switch button elements. Leads to degradation.

이러한 과제를 해결하기 위하여, 탄성 금속 쉬트의 표면 스케일을 제거하는 동시에, 전해도금을 촉진하는 산화피막을 형성하도록 상기 탄성 금속 쉬트를 산으로 세정한다.In order to solve this problem, the elastic metal sheet is washed with an acid to remove the surface scale of the elastic metal sheet and to form an oxide film which promotes electroplating.

탄성 금속 쉬트를 산으로 세정하게 되면, 상기 탄성 금속 쉬트의 표면에서 전해도금을 방해하는 스케일이 제거되는 반면, 산화피막이 생성되어 상기 탄성 금속 쉬트의 전해도금을 촉진하는 것이다.When the elastic metal sheet is washed with an acid, the scale that prevents electroplating from the surface of the elastic metal sheet is removed, whereas an oxide film is generated to promote electroplating of the elastic metal sheet.

또한, 본 발명의 스위치 버튼 소자용 금속박판의 제조 방법은 상기 산 세정된 탄성 금속 쉬트의 표면에 니켈 또는 은을 전해도금하여 코팅층을 형성하는 단계가 포함된다(단계 S40).In addition, the method for manufacturing a metal sheet for a switch button element of the present invention includes a step of forming a coating layer by electroplating nickel or silver on the surface of the acid-cleaned elastic metal sheet (step S40).

상기 단계 S30에서 표면에 산화피막이 형성된 탄성 금속 쉬트를 니켈 또는 은으로 전해도금하여, 상기 탄성 금속 쉬트의 표면에 니켈 또는 은 재질의 코팅층을 형성한다.In step S30, the elastic metal sheet having the oxide film formed on the surface is electroplated with nickel or silver, thereby forming a coating layer of nickel or silver on the surface of the elastic metal sheet.

탄성 금속 쉬트를 니켈 또는 은으로 전해도금하여 니켈 또는 은 재질의 코팅층을 형성하게 되면, 상기 전해도금된 코팅층이 탄성 금속 쉬트에 강력하게 결착되므로, 상기 탄성 금속 쉬트를 사용하여 구성된 스위치 버튼 소자용 금속박판을 프레스 가공할 때, 상기 금속박판로부터 니켈 또는 은이 전혀 탈리되지 않는다는 특성을 지니게 된다.When the electroplated elastic metal sheet with nickel or silver forms a coating layer made of nickel or silver, the electroplated coating layer is strongly bound to the elastic metal sheet, so that the switch button element metal is constructed using the elastic metal sheet. When pressing a thin plate, it has the characteristic that no nickel or silver is detached from the metal plate at all.

또한, 본 발명의 스위치 버튼 소자용 금속박판의 제조 방법은 상기 코팅층이 형성된 탄성 금속 쉬트를 일정한 사이즈로 슬리팅하는 단계가 포함된다(단계 S50).In addition, the method for manufacturing a metal sheet for a switch button element of the present invention includes the step of slitting the elastic metal sheet formed with the coating layer to a predetermined size (step S50).

상기 단계 S40에서 표면에 니켈 또는 은 재질의 코팅층이 형성된 탄성 금속 쉬트를 일정한 사이즈로 슬리팅하고, 슬리팅된 탄성 금속 쉬트를 릴에 권취하여 본 발명의 스위치 버튼 소자용 금속박판을 제조한다.In step S40, the elastic metal sheet having a nickel or silver coating layer formed on the surface is slitted to a predetermined size, and the slitting elastic metal sheet is wound on a reel to manufacture a metal sheet for switch button element of the present invention.

상기 제조된 스위치 버튼 소자용 금속박판을 프레스 장치에 세트하고 금형에서 프레스 가공하여 스위치 버튼 소자를 제조한다. 스위치 버튼 소자용 금속박판을 사용하여 스위치 버튼 소자를 제조하는 과정에서, 상기 스위치 버튼 소자용 금속박판로부터 니켈 또는 은이 전혀 탈리되지 않기 때문에, 제조된 스위치 버튼 소자의 품질이 크게 향상되며, 탈리되어 금형 또는 소자에 달라붙은 금속 분말을 제거하기 위한 별도의 시간과 노력이 소요되지 않아서 스위치 버튼용 소자 제조의 작업효율을 크게 개선할 수 있다.The above-described metal sheet for switch button element is set in a press device, and pressed in a mold to manufacture a switch button element. In the process of manufacturing the switch button element using the metal thin plate for the switch button element, since no nickel or silver is detached from the metal thin plate for the switch button element at all, the quality of the manufactured switch button element is greatly improved, and the mold Alternatively, no time and effort is required to remove the metal powder stuck to the device, thereby greatly improving the work efficiency of device manufacturing for the switch button.

이상의 본 발명에 의한 스위치 버튼용 소자는 본 발명의 기술적 사상의 범위 내에서 다양한 형태로 변형 및 응용 가능하다. 따라서 상기 실시예는 발명의 내용을 상세하게 설명하기 위한 것일 뿐이며, 발명의 기술적 사상의 범위를 한정하고자 하는 것이 아니므로, 본 발명의 권리범위는 후술하는 청구범위 뿐만 아니라, 그와 균등한 범위를 포함하여 판단하여야 한다.The switch button element according to the present invention can be modified and applied in various forms within the scope of the technical idea of the present invention. Therefore, the above embodiments are only intended to describe the contents of the invention in detail, and are not intended to limit the scope of the technical idea of the invention, the scope of the present invention is not limited to the claims to be described later, the equivalent scope thereof Should be judged.

Claims (2)

금속 핫코일을 압연하여 형성된 금속 쉬트가 450∼520 ℃로 열처리되고, 산 세정되고, 그 표면이 니켈 또는 은이 전해도금되어 코팅층이 형성되고, 일정한 사이즈로 슬리팅되어 이루어지는 스위치 버튼 소자용 금속박판.A metal sheet formed by rolling a metal hot coil is heat-treated at 450 to 520 DEG C, acid-cleaned, and a surface thereof is electroplated with nickel or silver to form a coating layer, and is formed by slitting to a predetermined size. 금속 핫코일을 압연하여 금속 쉬트를 형성하는 단계:Rolling the metal hot coil to form a metal sheet: 상기 금속 쉬트의 내부응력을 제거하고 탄성을 제공하도록 450∼520 ℃로 열처리하여 탄성 금속 쉬트를 형성하는 단계;Forming an elastic metal sheet by heat-treating at 450 to 520 ° C. to remove internal stress of the metal sheet and to provide elasticity; 상기 탄성 금속 쉬트의 표면을 세정하고 산화피막을 형성하도록 산(酸) 세정하는 단계;Cleaning the surface of the elastic metal sheet and acid cleaning to form an oxide film; 상기 산 세정된 탄성 금속 쉬트의 표면에 니켈 또는 은을 전해도금하여 코팅층을 형성하는 단계;Forming a coating layer by electroplating nickel or silver on the surface of the acid-cleaned elastic metal sheet; 상기 코팅층이 형성된 탄성 금속 쉬트를 일정한 사이즈로 슬리팅하는 단계를 포함하는 스위치 버튼 소자용 금속박판의 제조 방법.Method of manufacturing a metal sheet for a switch button element comprising the step of slitting the elastic metal sheet formed with the coating layer to a predetermined size.
KR1020080024690A 2008-03-18 2008-03-18 Metal ultra thin plate for a switch button device and preparing method the same KR100851660B1 (en)