KR100764945B1 - 강의 연속주조방법 - Google Patents
강의 연속주조방법 Download PDFInfo
- Publication number
- KR100764945B1 KR100764945B1 KR1020057019223A KR20057019223A KR100764945B1 KR 100764945 B1 KR100764945 B1 KR 100764945B1 KR 1020057019223 A KR1020057019223 A KR 1020057019223A KR 20057019223 A KR20057019223 A KR 20057019223A KR 100764945 B1 KR100764945 B1 KR 100764945B1
- Authority
- KR
- South Korea
- Prior art keywords
- magnetic field
- molten steel
- mold
- steel
- mass
- Prior art date
Abstract
Description
Claims (26)
- 연속주조용 주형의 장변방향에 따라 3개 이상의 전자석을 나란히 배열하여, 진동자계를 발생시키면서 상기 진동자계의 피크위치를 상기 장변방향에 따라 이동시키는 것을 특징으로 하는 강의 연속주조방법.
- 제 1항에 있어서,상기 3개 이상의 전자석 중, 서로 이웃하는 전자석에 장착되는 코일의 위상이, n, 2n, n 또는 n, 3n, 2n의 배열부분을 가지는 것을 특징으로 하는 강의 연속주조방법.
- 제 1항에 있어서,상기 진동자계에 더하여, 직류자계를 주편의 두께방향으로 중첩하는 것을 특징으로 하는 강의 연속주조방법.
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 제 2항에 있어서,상기 진동자계에 더하여, 직류자계를 주편의 두께방향으로 중첩하는 것을 특징으로 하는 강의 연속주조방법.
- 제 1항 내지 제 3항, 제10항 중 어느 한 항에 있어서,상기 주형 내의 미응고 용강의 개재물을 저융점화하는 것에 의해, 상기 용강을 상기 주형으로 공급하는 노즐의 폐색을 방지하여, 상기 노즐로부터 불활성 가스를 불어넣지 않고 연속주조를 행하는 것을 특징으로 하는 강의 연속주조방법.
- 제 11항에 있어서,상기 용강이, 용강 100질량%중에, C ≤ 0.020질량%, Si ≤ 0.2질량%, Mn ≤ 1.0질량%, S ≤ 0.050질량%, Ti ≥ 0.010질량%를 포함하고, Al ≤ [질량%Ti] / 5의 조건을 만족하는 조성으로 된 극저탄소 Ti 탈산강인 것을 특징으로 하는 강의 연속주조방법.
- 제 12항에 있어서,상기 용강을 제조하는 데에 있어, 상기 용강을 우선 진공 탈가스장치에 의해 탈탄처리한 후, Ti 함유합금에 의해 탈산하고, 그 후, 탈산용강 중에 Ca ≥ 10질량% 및 REM ≥ 5질량%의 1종류 또는 2종류와 Fe, Al, Si 및 Ti 중에서 선택된 1종류 또는 2종류 이상을 함유하는 산화물 조성조정용 합금을 첨가하는 것에 의해, 상기 용강 중의 산화물 조성은 그 산화물 조성 100질량%에 대하여, CaO 및 REM 산화물로부터 선택되는 1종류 이상의 함유량이 10질량% 이상 50질량% 이하이고, 또한 Ti 산화물의 함유량이 90질량% 이하, Al2O3의 함유량이 70질량% 이하로 하는 것을 특징으로 하는 강의 연속주조방법.
- 제 13항에 있어서,상기 탈탄처리 후의 용강을, 상기 Ti 함유합금에 의한 탈산처리에 앞서, Al, Si, Mn 중 어느 하나에 의해 예비탈산함으로써, 용강 중의 용존산소농도를 미리 200ppm 이하로 하는 것을 특징으로 하는 강의 연속주조방법.
- 제 1항 내지 제 3항 중 어느 한 항에 있어서,상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 5000(N/m3) 이상 13000(N/m3) 이하로 하는 것을 특징으로 하는 강의 연속주조방법.
- 제 11항에 있어서,상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 5000(N/m3) 이상 13000(N/m3) 이하로 하는 것을 특징으로 하는 강의 연속주조방법.
- 제 12항에 있어서,상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 5000(N/m3) 이상 13000(N/m3) 이하로 하는 것을 특징으로 하는 강의 연속주조방법.
- 제 13항에 있어서,상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 5000(N/m3) 이상 13000(N/m3) 이하로 하는 것을 특징으로 하는 강의 연속주조방법.
- 제 14항에 있어서,상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 5000(N/m3) 이상 13000(N/m3) 이하로 하는 것을 특징으로 하는 강의 연속주조방법.
- 제 1항 내지 제 3항 중 어느 한 항에 있어서,상기 주형 내의 미응고 용강의 유속을 V(m/s)로 하고, 상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 Fmax(N/m3)으로 할 때, V × Fmax가 3000(N/(s·m2)) 이상으로 되도록 조정하는 것을 특징으로 하는 강의 연속주조방법.
- 제 11항에 있어서,상기 주형 내의 미응고 용강의 유속을 V(m/s)로 하고, 상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 Fmax(N/m3)으로 할 때, V × Fmax가 3000(N/(s·m2)) 이상으로 되도록 조정하는 것을 특징으로 하는 강의 연속주조방법.
- 제 12항에 있어서,상기 주형 내의 미응고 용강의 유속을 V(m/s)로 하고, 상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 Fmax(N/m3)으로 할 때, V × Fmax가 3000(N/(s·m2)) 이상으로 되도록 조정하는 것을 특징으로 하는 강의 연속주조방법.
- 제 13항에 있어서,상기 주형 내의 미응고 용강의 유속을 V(m/s)로 하고, 상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 Fmax(N/m3)으로 할 때, V × Fmax가 3000(N/(s·m2)) 이상으로 되도록 조정하는 것을 특징으로 하는 강의 연속주조방법.
- 제 14항에 있어서,상기 주형 내의 미응고 용강의 유속을 V(m/s)로 하고, 상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 Fmax(N/m3)으로 할 때, V × Fmax가 3000(N/(s·m2)) 이상으로 되도록 조정하는 것을 특징으로 하는 강의 연속주조방법.
- 제 15항에 있어서,상기 주형 내의 미응고 용강의 유속을 V(m/s)로 하고, 상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 Fmax(N/m3)으로 할 때, V × Fmax가 3000(N/(s·m2)) 이상으로 되도록 조정하는 것을 특징으로 하는 강의 연속주조방법.
- 제 16항 내지 제19항 중 어느 한 항에 있어서,상기 주형 내의 미응고 용강의 유속을 V(m/s)로 하고, 상기 진동자계에 의해 구동되는 로렌츠력의 최대값을 Fmax(N/m3)으로 할 때, V × Fmax가 3000(N/(s·m2)) 이상으로 되도록 조정하는 것을 특징으로 하는 강의 연속주조방법.