KR100467780B1 - 열가소성 수지 조성물 및 이의 제조방법 - Google Patents
열가소성 수지 조성물 및 이의 제조방법 Download PDFInfo
- Publication number
- KR100467780B1 KR100467780B1 KR10-2002-0059553A KR20020059553A KR100467780B1 KR 100467780 B1 KR100467780 B1 KR 100467780B1 KR 20020059553 A KR20020059553 A KR 20020059553A KR 100467780 B1 KR100467780 B1 KR 100467780B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- compound
- parts
- thermoplastic resin
- methacrylic acid
- Prior art date
Abstract
Description
구분 | 실시예 | 비교예 | ||||||
1 | 2 | 3 | 4 | 5 | 1 | 2 | 3 | |
D│n1-n2│ | 0 | 0.005 | 0.01 | 0 | 0 | 0.015 | 0 | 0 |
MX-PMI103-L (중량부) | 20 | 20 | 20 | 30 | 40 | 20 | 3 | 65 |
투과율 | 89 | 88 | 87 | 89 | 89 | 78 | 89 | 89 |
투명도 | 3.1 | 3.3 | 3.5 | 3.1 | 3.1 | 10 | 2.7 | 3.3 |
충격강도(1/4") | 15 | 15 | 15 | 11 | 10 | 11 | 15 | 4 |
MFR(240 ℃) | 20 | 20 | 20 | 16 | 15 | 20 | 30 | 10 |
[주] D│n1-n2│: 스티렌계 수지와 내열성 공중합체의 굴절율 차MX-PMI103-L : N-페닐 말레이미드/메타크릴산 에스테르/방향족 비닐계 내열성공중합체(일본촉매(Nippon shokubai) 제품) |
Claims (8)
- 열가소성 수지 조성물에 있어서,a)ⅰ) 폴리부타디엔 고무라텍스 15 내지 50 중량부;ⅱ) 메타크릴산 알킬에스테르 화합물 또는 아크릴산 알킬 에스테르화합물 30 내지 60 중량부;ⅲ) 방향족 비닐 화합물 5 내지 25 중량부; 및ⅳ) 비닐시안 화합물 1 내지 20 중량부를 포함하는 스티렌계 수지 95 내지 40 중량%; 및b) N-페닐 말레이드/메타크릴산 에스테르/방향족 비닐계 내열성 공중합체 5 내지 60 중량%를 포함하는 열가소성 수지 조성물.
- 제1항에 있어서,상기 b)의 N-페닐 말레이미드/메타크릴산 에스테르/방향족 비닐계 내열성 공중합체는 상기 a)의 스티렌계 수지와의 굴절율 차이가 하기 수학식 1을 만족하는 열가소성 수지 조성물:[수학식 1]상기 수학식 1의 식에서,n1은 스티렌계 수지의 굴절율이고,n2는 N-페닐 말레이미드/메타크릴산 에스테르/방향족 비닐계 내열성 공중합체의 굴절율이다.
- 제1항에 있어서,상기 a)ⅰ)의 폴리부타디엔 고무라텍스는 입경이 2500 내지 5000 Å이고, 겔 함량이 60 내지 95 %이고, 팽윤지수가 12 내지 40인 열가소성 수지 조성물.
- 제1항에 있어서,상기 a)ⅰ)의 폴리부타디엔 고무라텍스가 1,3-부타디엔, 유화제, 중합개시제, 전해질, 분자량조절제, 및 이온교환수를 일괄투여하여 중합시키는 방법으로 제조되는 열가소성 수지 조성물.
- 제1항에 있어서,상기 a)ⅱ)의 메타크릴산 알킬에스테르 화합물이 메틸메타크릴레이트 또는 그 유도체인 열가소성 수지 조성물.
- 제1항에 있어서,상기 a)ⅲ)의 방향족 비닐 화합물이 스티렌, α-메틸스티렌, ο-에틸스티렌, ρ-에틸스티렌, 및 비닐톨루엔으로 이루어지는 군으로부터 1 종 이상 선택되는 화합물 또는 이들의 유도체인 열가소성 수지 조성물.
- 제1항에 있어서,상기 a)ⅳ)의 비닐시안 화합물이 아크릴로니트릴, 메타크릴로니트릴, 및 에타크릴로니트릴로 이루어지는 군으로부터 1 종 이상 선택되는 화합물 또는 이들의 유도체인 열가소성 수지 조성물.
- 열가소성 수지의 제조방법에 있어서,a) 폴리부타디엔 고무라텍스를 제공하는 단계;b) 상기 a)단계의 폴리부타디엔 고무라텍스에ⅰ) 메타크릴산 알킬에스테르 화합물 또는 아크릴산 알킬 에스테르화합물;ⅱ) 방향족 비닐 화합물; 및ⅲ) 비닐시안 화합물을 유화중합으로 그라프트 공중합시켜 스티렌계 수지를 제조하는단계; 및c) 상기 b)단계의 스티렌계 수지에 N-페닐 말레이드/메타크릴산 에스테르/방향족 비닐계 내열성 공중합체를 가하여 혼합하는 단계를 포함하는 열가소성 수지의 제조방법.