KR100352643B1 - natural antiseptic substance made from mixture of natural mugwort and silver - Google Patents
natural antiseptic substance made from mixture of natural mugwort and silver Download PDFInfo
- Publication number
- KR100352643B1 KR100352643B1 KR1019990054667A KR19990054667A KR100352643B1 KR 100352643 B1 KR100352643 B1 KR 100352643B1 KR 1019990054667 A KR1019990054667 A KR 1019990054667A KR 19990054667 A KR19990054667 A KR 19990054667A KR 100352643 B1 KR100352643 B1 KR 100352643B1
- Authority
- KR
- South Korea
- Prior art keywords
- natural
- silver
- mugwort
- extract
- present
- Prior art date
Abstract
본 발명은 천연 쑥과 금속 은(Ag)의 혼합에 의해 제조되는 천연방부제에 관한 것으로, 상기 천연쑥은 화학처리에 의한 추출용액이고, 상기 은(Ag)은 이온상태의 콜로이드 용액으로 이루어지도록 한다. 그리고, 상기 천연쑥 추출물은, 에틸아세테이트 용액내에 용해후 여액의 에틸아세테이트를 증발시켜 중간 쑥추출물을 획득하고 에탄올 용해후 활성탄에 혼합 교반한 후 원심분리에 의해 생성된 상등액을 이용하는 것이 좋으며, 상기 천연쑥추출물은 3%농도 이상으로 이루어지고, 상기 은이온콜로이드의 농도는 10ppm이상으로 이루어지도록 하는 것이 바람직하다. 따라서 본 발명은 기존의 화학 합성방부제가 인체에 대하여 나타내는 부작용을 전혀 나타내지 않으면서 방부능력이 보다 우수한 새로운 천연방부제를 제공하는 효과가 있다.The present invention relates to a natural preservative prepared by mixing natural mugwort and metallic silver (Ag), wherein the natural mugwort is an extraction solution by chemical treatment, and the silver (Ag) is made of a colloidal solution in an ionic state. . The natural mugwort extract is obtained by dissolving ethyl acetate in the filtrate after dissolving in ethyl acetate solution to obtain an intermediate mugwort extract, and mixing and stirring the activated mugwort with activated carbon after dissolving ethanol, using the supernatant produced by centrifugation. Mugwort extract is made of more than 3% concentration, the concentration of the silver ion colloid is preferably made to be more than 10ppm. Therefore, the present invention has an effect of providing a new natural preservative having better antiseptic ability without exhibiting any side effects of the conventional chemical synthetic preservatives to the human body.
Description
본 발명은 천연방부제에 관한 것으로, 보다 상세하게는 천연 쑥과 금속 은(Ag)의 혼합에 의해 제조되는 천연방부제에 관한 것이다.The present invention relates to a natural preservative, and more particularly to a natural preservative prepared by mixing natural mugwort and metal silver (Ag).
일반적으로 우리 생활주변에서 널리 이용되는 식품 및 화장품 등에는 내부물성의 변화를 방지하고 일정한 기간동안 보존을 위해서 인체에 무익한 방부제를 첨가하게 된다. 상기 방부제는 세균 및 곰팡이 등의 이물질들의 작용을 효과적으로 저해하여 식품 및 화장품 등이 변성되는 것을 막아주게 되며, 이러한 방부기능을 가지는 방부제로는 천연으로 산출되는 물질들도 있으나, 대개는 제조의 편의상 또는 대량생산 등에 적용하기 위하여 화학적으로 합성한 인공물질들을 이용하게 된다.In general, food and cosmetics widely used around our lives are added to the human body to prevent the change of internal properties and to preserve for a certain period of time to use a preservative. The preservative effectively inhibits the action of foreign substances such as bacteria and fungi to prevent the degeneration of food and cosmetics, etc., and preservatives having such antiseptic function, there are some substances produced naturally, but usually for convenience of manufacture or Artificial materials synthesized chemically will be used for mass production.
예를 들어 현재 사용되는 화장품은 고분자성 지질이나 물을 주성분으로 하여 기타 여러가지 물질들이 혼합되어 이루어진다. 상기 화장품을 이루는 물질들중 미생물의 탄소원이 되는 글리세린이나 솔비톨 등이 함유되어 있고, 질소원으로는 아미노산 유도체 및 단백질 등이 배합된 것이 많다. 따라서 상기 탄소원 및 질소원을 매개체로 하는 세균 곰팡이 등이 번식되어 쉽게 오염이 이루어진다. 한편, 상기 화장품은, 일반적으로 식품과 비교하면, 사용기간이 극히 길기 때문에 식품에서 보다 방부제 처리에 더욱 더 많은 문제점이 있다. 이러한 화장품의 특성에 의해 고려되어야 하는 방부제의 기본조건으로는 모든 미생물에 대한 항균효과를 가지며, 사용 및 제조하기가 용이해야하고, 피부에 대한 자극이 없어야 한다. 또한, 상기조건이외에도 범용적으로 사용가능하기 위해서는 제품의 pH에 영향을 받지않고, 제품성분의 효과를 저하시키지 않으며 다루기가 용이해야 한다.For example, currently used cosmetics are made up of a mixture of various substances based on polymeric lipids or water. Among cosmetic substances, glycerin or sorbitol, which is a carbon source of microorganisms, is contained, and as a nitrogen source, many amino acid derivatives and proteins are incorporated. Therefore, bacterial fungi, which are mediated by the carbon source and the nitrogen source, are multiplied and easily polluted. On the other hand, the cosmetics, compared with the food in general, because the use period is extremely long, there are more problems in the preservative treatment than in food. Basic conditions for preservatives to be considered by the characteristics of these cosmetics should be antimicrobial effect on all microorganisms, easy to use and manufacture, and no skin irritation. In addition, to be usable universally in addition to the above conditions, it should be easy to handle without being affected by the pH of the product, without degrading the effect of the product components.
이러한 조건을 충족시키기 위해 현재 일반적인 화장품에 사용되고 있는 방부제로는, 파라옥시안식향산 에스텔과 파라벤류가 주로 쓰이고 있으며, 살균의 목적으로 염화벤잘코늄, 글리콘산 클로로헥시딘 및 트리클로로 카르바닐드 등이 쓰이고 있다. 현재 기존 제품에 사용되는 상술한 물질들은 화학합성을 통해 제조되어 방부제로의 기능을 수행하고 있으나, 이러한 화학물질들은 피부에 자극을 주게되어 피부의 부종발생이나 알러지증상을 유발하게 되어 사용자의 피부건강을 해치는 문제점이 있다.In order to satisfy these conditions, preservatives currently used in general cosmetics, paraoxybenzoic acid esters and parabens are mainly used, and for the purpose of sterilization, benzalkonium chloride, chlorohexidine glyconate and trichlorocarbanil This is used. Currently, the above-mentioned materials used in existing products are manufactured through chemical synthesis to perform functions as preservatives, but these chemicals cause skin irritation and cause skin edema or allergy symptoms. There is a problem that hurts.
따라서, 기존의 이러한 화학합성방부제가 가지는 부작용을 해결하기 위해 최근에는 천연으로 제조되어 자연친화적인 천연방부제의 연구가 활발히 이루어지고 있다. 본 발명자는 이러한 천연방부제의 우수한점을 연구하던 중 예전부터 민간에서 널리 사용되는 천연 쑥과 은(Ag)금속이 방부능력이 있음을 알 수 있었으며, 보다 나은 방부능력을 위해 연구하던 중 천연 쑥의 추출물과 금속 은(Ag)의 이온상태 콜로이드 혼합물이 방부능력이 탁월함을 알 수 있었고, 이러한 제조방법에 의한 천연방부제를 개발하게 되었다.Therefore, in order to solve the side effects of the conventional chemical synthetic preservatives, the researches on natural preservatives that are made naturally and are made in nature have been actively conducted in recent years. The inventors of the present invention have been able to find out that natural mugwort and silver (Ag) metals widely used in folklore have antiseptic properties while studying the superiority of such natural preservatives. It was found that the ionic colloid mixture of the extract and the metal silver (Ag) was excellent in preservative ability, and developed a natural preservative by this manufacturing method.
따라서 본 발명은 기존의 화학 합성방부제가 인체에 대하여 나타내는 부작용을 전혀 나타내지 않으면서 방부능력이 보다 우수한 새로운 천연방부제를 제공하는 것을 목적으로 한다.Accordingly, an object of the present invention is to provide a new natural preservative having better antiseptic ability without exhibiting any side effects of the conventional chemical synthetic preservative.
도 1 - 본 발명에 의한 천연방부제의 제조과정을 나타난 도.Figure 1-Figure showing the manufacturing process of natural preservatives according to the present invention.
도 2 - 본 발명에 의한 천연방부제의 구성물질은 은콜로이드를 생산하기 위한 장치를 개략적으로 보인 도.Figure 2 is a schematic of a device for producing silver colloids of the natural preservatives according to the present invention.
도 3 - 본 발명에 의한 천연방부제의 구성물질인 천연 쑥의 항균활성을 나타낸 도.Figure 3-Figure showing the antimicrobial activity of natural mugwort as a component of natural preservatives according to the present invention.
도 4 - 본 발명에 의한 천연방부제의 구성물질은 은콜로이드의 항균활성을 나타낸 도.Figure 4 is a component of the natural preservative according to the present invention showing the antimicrobial activity of silver colloid.
도 5 - 본 발명에 의한 천연방부제의 구성물질은 천연 쑥과 은콜로이드의 다양한 혼합비를 나타낸 도.Figure 5-The composition of the natural preservatives according to the present invention is showing the various mixing ratios of natural mugwort and silver colloid.
도 6 - 본 발명에 의한 천연방부제의 항균활성의 상승을 나타낸 도.Figure 6 is a diagram showing the rise of the antimicrobial activity of the natural preservative according to the present invention.
상기와 같은 목적을 달성하기 위한 본 발명에 의한 천연방부제는, 천연쑥과 금속 은(Ag)의 혼합물로 이루어지는 천연 쑥과 은(Ag)을 이용한 천연방부제를 제공하는 것이다. 바람직하기로는 상기 천연쑥은 화학처리에 의한 추출용액이고, 상기은(Ag)은 이온상태의 콜로이드 용액으로 이루어지도록 한다.The natural preservative according to the present invention for achieving the above object is to provide a natural preservative using natural mugwort and silver (Ag) consisting of a mixture of natural mugwort and metal silver (Ag). Preferably, the natural mugwort is an extraction solution by chemical treatment, and the silver (Ag) is made of a colloidal solution in an ionic state.
그리고, 상기 천연쑥추출물은, 에틸아세테이트 용액내에 용해후 여액의 에틸아세테이트를 증발시켜 중간 쑥추출물을 획득하고 에탄올 용해후 활성탄에 혼합 교반한 후 원심분리에 의해 생성된 상등액을 이용하는 것이 좋으며, 상기 천연쑥추출물은 3%농도 이상으로 이루어지고, 상기 은이온콜로이드의 농도는 10ppm이상으로 이루어지도록 하는 것이 바람직하다.The natural mugwort extract is obtained by dissolving ethyl acetate in the filtrate after dissolving in ethyl acetate solution to obtain an intermediate mugwort extract, and mixing and stirring the activated mugwort with activated carbon after dissolving ethanol, using the supernatant produced by centrifugation. Mugwort extract is made of more than 3% concentration, the concentration of the silver ion colloid is preferably made to be more than 10ppm.
다음, 상기와 같은 구성을 갖는 본 발명에 의한 천연방부제의 특징 및 적용은 하기의 설명을 통하여 명백하게 나타날 것이며, 이하 도시한 도면을 참조하여 천연방부제 및 그 제조방법을 자세히 설명하기로 한다.Next, the features and applications of the natural preservative according to the present invention having the above configuration will be apparent through the following description, and the natural preservative and its manufacturing method will be described in detail with reference to the accompanying drawings.
기본적으로 본 발명은 천연방부제로서의 기능을 수행하기 위하여 천연 쑥 추출물과 금속 은(Ag)으로부터 전기분해에 의해 은(Ag)콜로이드를 얻고 이를 혼합하여 제조하였다. 먼저, 천연 쑥으로 부터 방부능력을 가지는 물질을 추출하는 과정을 도시한 도 1을 참조하여 설명하기로 한다.Basically, the present invention was prepared by obtaining a silver (Ag) colloid by electrolysis from natural mugwort extract and metal silver (Ag) in order to perform the function as a natural preservative. First, it will be described with reference to Figure 1 showing the process of extracting a substance having antiseptic properties from natural mugwort.
본 발명의 재료로 사용되는 천연 쑥은 강화도에서 채취된 것을 사용하였고, 채취쑥을 말려서 사용하였다. 제일 먼저, 마른 강화 쑥을 분쇄기로 분쇄하여 입자를 잘게 부순다.(Ⅰ) 이는 후술하는 바와 같이 본발명에서는 천연 쑥의 추출물을 원료로 사용하므로 원료의 추출을 용이하게 하기위하여 잘게부수게 되며, 이러한 분쇄는 일반적인 분쇄기를 이용하면 되므로 이하 자세한 설명은 생략하기로 한다.Natural mugwort used as the material of the present invention was obtained from Ganghwado, and used to dry the mugwort. First, the dry reinforced mugwort is crushed by a grinder to crush the particles. (I) In the present invention, since the extract of natural mugwort is used as a raw material in the present invention, it is crushed to facilitate the extraction of raw materials. Since the pulverization may be performed using a general pulverizer, detailed description thereof will be omitted.
다음, 상기 분쇄된 천연쑥의 유효성분을 추출한다.(Ⅱ) 즉, 상기 마른 천연 쑥을 에틸아세테이트에 담가두고 1 내지 2일간 둔다. 상기 에틸아세테이트 용액내에 담겨진 천연쑥은 시간이 지남에 따라 유효성분이 에틸아세테이트 용액속에 녹아나게 된다.Next, the active ingredient of the ground natural mugwort is extracted. (II) That is, the dried natural mugwort is soaked in ethyl acetate and left for 1 to 2 days. Natural mugwort contained in the ethyl acetate solution is the active ingredient is dissolved in the ethyl acetate solution over time.
여액의 에틸아세테이트를 증발시켜 쑥추출물을 획득한다.(Ⅲ) 즉, 상기 에틸아세테이트 용액을 0.45㎛여과지로 여과하고, 그 여액을 감압기를 이용하여 감압함으로써 에틸아세테이트를 증발시켜 중간추출물을 획득하게 되는데 이때, 상기 에틸아세테이트가 완전히 증발되면 젤상태의 중간 쑥추출물이 남게 된다.The ethyl acetate of the filtrate is evaporated to obtain a mugwort extract. (III) That is, the ethyl acetate solution is filtered through a 0.45 µm filter paper, and the filtrate is evaporated under reduced pressure using a pressure reducer to evaporate ethyl acetate to obtain an intermediate extract. At this time, when the ethyl acetate is completely evaporated, the middle mugwort extract in a gel state remains.
다음, 상기 젤상태의 추출물을 에틸아세테이트에 대하여 50중량%의 에탄올을 가하여 용해시킨다.(Ⅳ) 그리고, 상기 에탄올에 용해되지 않는 부분은 0.45㎛여과지를 이용하여 여과하여 걸러내고 여액을 수거한다.(Ⅴ) 상기 여액을 추출액의 50중량%이 활성탄에 혼합하고 하루동안 교반한 후, 약 1200rpm의 속도로 약 10분가량원심분리를 행한다.(Ⅵ) 상기 원심분리에 따라 상층부분에는 투명한 노란색의 분획물이 생성되고, 이러한 맑은 상등액을 분획하여 본 발명에 의한 쑥추출물을 획득한다.(Ⅶ)Next, the gel-like extract is dissolved by adding 50% by weight of ethanol to ethyl acetate. (IV) Then, the portion which is not dissolved in ethanol is filtered out using a 0.45 μm filter paper and the filtrate is collected. (V) 50% by weight of the extract is mixed with activated carbon and stirred for one day, followed by centrifugation for about 10 minutes at a speed of about 1200rpm. A fraction is produced, and this clear supernatant is fractionated to obtain wormwood extract according to the present invention.
다음, 도시한 도2의도면을 참조하여 본 발명에 의한 은(Ag)이온의 생성과정을 설명하기로 한다. 먼저, 금속 은(Ag)은 그 자체가 어느 정도 항균성이 있다는 것이 알려져 있다. 그러나, 본 발명에서 사용되는 화장품은 인체의 얼굴 손 등에 바르는 것이므로 금속 은(Ag)자체의 혼합도 가능하나, 이럴경우 금속 은(Ag)이 피부에 노출되어 미관상 곤란한 경우도 발생한다. 즉, 미세한 은(Ag)분말을 사용한다 할지라도 화장품내의 다른 성분과의 혼합이 곤란하고, 이에 따라 뭉쳐진 은이 피부에 도포되었을 경우 표시가 나므로 화장품에 그대로 혼합하는 것은 바람직하지않다. 따라서 본 발명자는 이러한 은(Ag) 금속 자체보다는 은(Ag)이온상태가 더욱 더 향균에 효과적임을 알 수 있었으며, 또한 화장품 내의 다른 성분과의 고른 혼합이 가능함을 알 수 있었다. 이하 이러한 은(Ag)이온의 제조과정을 설명하기로 한다.Next, a process of generating silver (Ag) ions according to the present invention will be described with reference to the drawing of FIG. 2. First, it is known that metal silver (Ag) has some antibacterial property per se. However, since the cosmetics used in the present invention are applied to the face, hands, and the like of the human body, the metal silver (Ag) may be mixed, but in this case, the metal silver (Ag) may be exposed to the skin, resulting in aesthetic difficulties. In other words, even if fine silver (Ag) powder is used, it is difficult to mix with other ingredients in the cosmetic, and thus, when the aggregated silver is applied to the skin, it is not preferable to mix it with the cosmetic as it is. Therefore, the present inventors found that silver (Ag) ion state was more effective for antibacterial than silver (Ag) metal itself, and it was also found that even mixing with other components in cosmetics was possible. Hereinafter, a manufacturing process of such silver (Ag) ions will be described.
도 2에 도시된 바와 같이, 본 발명자는 간단하게 장치를 구현하여 은(Ag)이온을 콜로이드 상태로 제조하였다. 즉, 본체(10) 내부에 일정량의 증류수를 담아두고 순도 99.99%의 금속 순수 은(Ag)의 봉(14)을 전원의 양극에 설치하였다. 상기 본체의 표면(12)은 외부자외선을 차단하기 위하여 갈색으로 처리하였다. 그리고, 본체덮개(17)에 전원(16)을 연결하고, 외부에서 일정한 전류 및 전압을 가함으로서 은을 전기분해시켰다. 즉, 전원스위치(18)을 작동시킴에 따라 일정량의 전류와 전압(전압은 약 30볼트가 바람직함)이 순수한 은(pure silver 99.99%이상)에 가해짐으로서 은이온(Ag2+)가 방출되며, 이러한 은이온(Ag2+)을 증류수에 부유시켜 콜로이드화하는 것이며, 이러한 전원의 작동여부는 전원램프(15)에 의해 확인가능하다. 그리고, 보다 향상된 방법으로는 순수 증류수를 전기분해시켜 은이온의 방출속도를 가속화시켜 제조할 수도 있으며, 여하튼 은이온 콜로이드를 제조하는데 있어서 가장 적합한 것은 고품질의 증류수에 99.99%의 이상 순도를 가지는 은을 넣고 전극을 연결하는 것이다. 상기와 같이 제조된 은용액은 유도결합플라즈마 방출분광계에 의하여 분석한 결과 은이온(Ag2+)이 콜로이드 상태로 존재하는 것을 확인할 수 있었으며, 그 농도 또한 측정가능 하였다.상기와 같이 각각 별도로 제조된 쑥추출물 용액과 콜로이드 상태의 은이온용액을 단순히 물리적으로 혼합함으로써 본원발명에서 요구하는 천연방부제가 제조되는 것이다. 즉, 쑥추출물 용액과 은이온 용액을 혼합함으로써 각 개별의 은이온이 쑥추출물의 용액 내에 고루 분산이 이루어지게 된다. 상기 쑥추출물 용액과 은이온 용액의 혼합비는 여러가지 가능하겠으나, 본원발명에서 요구되는 방부제로써의 기능을 구현하기 위하여 하기 실험에서 나타난 바와 같이 최소한의 혼합비로 혼합하게 되는 것이다. 즉 본원발명에서 요구되는 천연방부제로의 기능을 구현하기 위하여 쑥추출물과 은이온 용액이 혼합됨에 따라 보다 상승된 작용을 나타내며 그 바람직한 혼합비는 은이온용액은 최소 10ppm 이상 그리고 쑥추출물은 3%농도 이상 혼합되는 것이 바람직하다.As shown in FIG. 2, the inventors simply implemented a device to prepare silver (Ag) ions in a colloidal state. That is, a predetermined amount of distilled water was contained in the main body 10, and a rod 14 of pure metallic silver (Ag) having a purity of 99.99% was installed at the anode of the power source. The surface 12 of the body was browned to block external ultraviolet rays. Then, the power source 16 was connected to the main body cover 17, and silver was electrolyzed by applying a constant current and voltage from the outside. That is, as the power switch 18 is operated, a certain amount of current and voltage (a voltage of about 30 volts is preferably applied) is applied to pure silver (more than 99.99% of pure silver), thereby releasing silver ions (Ag 2+ ). The silver ions (Ag 2+ ) are colloidalized by distillation in distilled water, and the operation of the power source can be confirmed by the power lamp 15. In addition, an improved method may be prepared by accelerating the release rate of silver ions by electrolyzing pure distilled water. Put and connect the electrodes. The silver solution prepared as described above was confirmed by the inductively coupled plasma emission spectrometer that silver ions (Ag 2+ ) were present in the colloidal state, and the concentration thereof was also measured. The natural preservative required by the present invention is prepared by simply physically mixing the mugwort extract solution and the colloidal silver ion solution. That is, by mixing the mugwort extract solution and the silver ion solution, each individual silver ion is uniformly dispersed in the solution of the mugwort extract. The mixing ratio of the mugwort extract solution and the silver ion solution may be various, but it is to be mixed at the minimum mixing ratio as shown in the following experiment to implement the function as a preservative required in the present invention. In other words, in order to realize the function as a natural preservative required in the present invention, as the mugwort extract and the silver ion solution are mixed, the synergistic effect is increased. It is preferable to mix.
다음, 상기와 같이 제조된 천연 쑥 추출물과 은이온 콜로이드를 이용하여 하기와 같은 실시예를 통하여 방부제의 실험을 수행하였다.Next, using the natural mugwort extract and silver ion colloid prepared as described above was carried out experiment of the preservative through the following examples.
각 실시예들을 설명하기에 앞서 본 발명에서 사용되는 각종 실험항목을 설명하기로 한다. 항균활성의 측정은 보사부 공시균주인 에스체리치아 콜라이 (Escherichia coli), 바실러스 서브틸리스(Bacillus subtilis) 그리고 스타필로코커스 아우레우스(Staphylococcus aureus)를 엘비(LB)배지에서 약 37℃의 온도로 약18시간 전배양 하였다. 그리고, 슈도모나스 에어로지노사(Pseudomonas aeruginosa)와 캔디다 알비칸스(Candida albicans)는 엘비(LB)배지에서 약 30℃의 온도로 약18시간 전배양하였다. 그 후,본 발명에 의해 제조된 은용액, 쑥추출물 그리고 은용액과 쑥추출물의 혼합액에 상술한 각 균주의 전 배양액을 분주 후 24시간동안 배양하여 생육도를 측정함으로써 항균활성을 알아보았다. 이하 각 실시예에서 이러한 본 발명에 의한 은용액과 쑥추출물의 혼합에 따른 본 발명에 의한 천연방부제를 구체적으로 설명하지만, 본 발명에 의한 개념이 하기의 실시예에 한정되는 것은 아님을 알 수 있다.Before describing each embodiment, various experimental items used in the present invention will be described. Antimicrobial activity was measured by escherichia coli, Bacillus subtilis and Staphylococcus aureus at 37 ° C in LB medium. It was preincubated for about 18 hours. Pseudomonas aeruginosa and Candida albicans were preincubated for about 18 hours at a temperature of about 30 ° C. in LB medium. Thereafter, the antimicrobial activity was examined by culturing the whole culture solution of the above-described strains for 24 hours after dispensing in the silver solution, wormwood extract prepared by the present invention and the mixed solution of silver solution and wormwood extract. Hereinafter, the natural preservatives according to the present invention according to the mixing of the silver solution and wormwood extract according to the present invention in each embodiment will be described in detail, but it can be seen that the concept according to the present invention is not limited to the following examples. .
실시예 1 강화약쑥의 항균효과Example 1 Antibacterial Effect of Fortified Wormwood
상술한 도 1의 방법에 의해 추출된 강화약쑥으로 배지를 만들었다. 본 배양 배지는 각각 1.6%, 3.3%, 5% 그리고 6.6%가 되도록 쑥추출물을 넣어 만들고 전배양된 균주를 접종하여 24시간 배양한 후, 생균수를 측정하여 항균활성을 알아 보았다. 그 결과를 도시한 도3에 나타내었다. 도시된 바와 같이, 에스체라치아 콜라이(Escherichia coli), 바실러스 서브틸리스(Bacillus subtilis) 그리고 스타필로코커스 아우레우스(Staphylococcus aureus)는 본 발명에 의한 강화약쑥 추출물의 최저농도인 1.6%에서도 모두 사멸됨을 알 수 있으나, 슈도모나스 에어로지노사(Pseudomonas aeruginosa)와 캔디다 알비칸스(Candida albicans)는 1.6%농도에서는 완전히 사멸되지는 않으나, 3.3%농도에서는 완전히 사멸된다. 따라서 본 발명에 의한 쑥추출물의 단독으로는 3.3% 이상의 농도가 적합함을 알 수 있다.The medium was made with the strengthened wormwood extracted by the method of FIG. 1 described above. The culture medium was prepared by adding mugwort extract to 1.6%, 3.3%, 5% and 6.6%, respectively, and inoculated with the precultured strains, and incubated for 24 hours. The result is shown in FIG. As shown, Esccherichia coli, Bacillus subtilis and Staphylococcus aureus were all killed at 1.6%, the lowest concentration of fortified wormwood extract according to the present invention. However, Pseudomonas aeruginosa and Candida albicans are not completely killed at 1.6% but are completely killed at 3.3%. Therefore, it can be seen that the concentration of 3.3% or more is suitable as the wormwood extract of the present invention alone.
실시예 2 은콜로이드의 항균효과Example 2 Antimicrobial Effect of Silver Colloid
상술한 도 2의 방법에 의해 제조된 은콜로이드를 넣어 농도가 각 10ppm,20ppm,30ppm,40ppm 그리고 50ppm이 되도록 만든 배지에 전배양된 각 균주를 접종하여 24시간 배양한다. 그 후, 600나노미터에서 흡광도를 측정하여 항균활성을 알아보았으며, 그 결과는 도4에 도시된 바와 같다. 상기 도4는 실험결과를 나타내며, 은콜로이드의 양이 많으면 많을 수록 효과적임을 알 수 있었으며, 단순히 최소의 은콜로이드양을 조사하였다. 도시된 바와 같이, 상술한 각 균주는 은콜로이드가 함유된 배지와 그렇지 못한 배지에서 명확한 차이가 나타나며, 콘트롤로 제공된 배지는 시간이 지날수록 점차 개체수가 증대하여 활성됨을 알 수 있다. 그러나, 캔디다 알비칸스는 10ppm하에서도 항균활성의 두드러진 저해가 보여지나 약 20ppm의 농도에서 항균활성이 거의 저해되었으며, 나머지 네가지 균주는 모두 10ppm하에서도 항균활성이 저해됨을 알 수 있었다.The silver colloid prepared by the method of FIG. 2 described above was inoculated with each strain preincubated in a medium made to have a concentration of 10ppm, 20ppm, 30ppm, 40ppm and 50ppm and incubated for 24 hours. Then, the absorbance was measured at 600 nanometers to determine the antimicrobial activity, and the results are shown in FIG. 4. Figure 4 shows the experimental results, it was found that the more the amount of the silver colloid is more effective, simply examined the minimum amount of silver colloid. As shown, each of the strains described above shows a clear difference in the medium containing the silver colloid and not the medium, it can be seen that the medium provided as a control is activated by increasing the population gradually over time. However, Candida albicans showed a significant inhibition of the antimicrobial activity even under 10ppm, the antimicrobial activity was almost inhibited at a concentration of about 20ppm, the remaining four strains were found to inhibit the antimicrobial activity even under 10ppm.
실시예 3 천연쑥추출물과 은콜로이드의 혼합비 결정Example 3 Determination of the Mixing Ratio of Natural Mugwort Extract and Silver Colloid
상술한 바와 같이, 천연쑥추출물과 은콜로이드 용액 각자는 항균활성을 나타내나, 두가지 혼합물이 더욱 항균활성에 대한 저해성이 우수함을 알 수 있으며, 이러한 항균활성의 최적 억제를 위한 혼합비를 실험해 보았다. 은콜로이드 10ppm에 천연쑥추출물의 농도를 각각 달리한 배지에 전배양된 각 균주를 접종하여 24시간 배양한다. 그 후, 생균수를 조사하여 항균활성을 알아보아 최적의 혼합비율을 결정하였다. 그 결과는 도 5에 나타내었는데, 도시된 바와 같이, 천연쑥의 약 3.5%농도가 최적임을 알 수 있다. 비록 도시되지는 않았지만 천연쑥의 농도가 점차로 증가할수록 항균활성의 억제능은 더 좋아짐을 알 수 있다. 그리고, 본 실험에서는 은콜로이드 농도를 10ppm으로 나타내었으나, 은콜로이드의 농도 역시 증가할 수록 항균활성이 더욱 억제됨은 자명하다.As described above, each of the natural mugwort extract and the silver colloidal solution exhibited antimicrobial activity, but the two mixtures showed more excellent antimicrobial activity, and the mixing ratio for optimum inhibition of the antimicrobial activity was tested. . Inoculate each strain precultured with silver colloid 10ppm in different concentrations of natural mugwort extract and incubate for 24 hours. Thereafter, the number of viable cells was examined to determine the antimicrobial activity to determine the optimum mixing ratio. The results are shown in Figure 5, as shown, it can be seen that the concentration of about 3.5% of the natural mugwort is optimal. Although not shown, it can be seen that as the concentration of natural mugwort gradually increases, the antimicrobial activity is inhibited. In the present experiment, the silver colloid concentration was represented as 10 ppm, but as the concentration of the silver colloid also increased, it was obvious that the antimicrobial activity was further suppressed.
실시예 4 은콜로이드, 천연쑥추출물 및 은콜로이드와 천연쑥추출물의 혼합액에 대한 항균활성 비교Example 4 Comparison of Antimicrobial Activity of Silver Colloid, Natural Mugwort Extract and Mixed Solution of Silver Colloid and Natural Mugwort Extract
실시예1, 실시예2 그리고 실시예3에 의한 은콜로이드의 항균활성,천연쑥추출물의 항균활성 그리고 이들 혼합액의 항균활성을 각각 비교하였으며, 이들의 결과는 도6과 같이 나타났다. 그리고 설명의 편의상 은콜로이드와 천연쑥추출물의 혼합액을 이하에서는 DASA(Dong-eui Amaranth Silver Artemisia)라고 칭하기로 한다. 도시된 바와 같이, 은콜로이드 및 천연쑥추출물의 단독 사용보다는 이들을 혼합한 DASA가 보다 효과적임을 알 수 있다.The antimicrobial activity of silver colloid, antibacterial activity of natural mugwort extract and the antimicrobial activity of these mixed solutions according to Examples 1, 2 and 3 were compared, respectively, and the results were shown in FIG. For convenience of explanation, a mixed solution of silver colloid and natural mugwort extract will be referred to as Dong-eui Amaranth Silver Artemisia (DASA). As shown, it can be seen that DASA mixed with them is more effective than the use of silver colloid and natural mugwort extract alone.
실시예 5 안정성Example 5 Stability
상술한 각 실시예1,2 및 3에 대한 은콜로이드, 천연쑥추출물 및 이들의 혼합액인 DASA에 대한 안정성은 1주일 간격으로 4주일 동안 측정하였다. 전배양된 다섯가지 균주를 고체 평판배지에 도말하고 그 위에 은콜로이드와 천연쑥을 분주하여 항균저지대의 면적으로 측정하였다. 표1은 은콜로이드의 항균활성 안정성을 나타내고, 표2는 천연쑥의 항균활성 안정성을 나타내고 있다.The stability of silver colloids, natural mugwort extracts and their mixed solution for DASA for each of Examples 1, 2 and 3 described above was measured for 4 weeks at weekly intervals. Five precultured strains were plated on a solid plate medium and silver colloid and natural mugwort were dispensed on it to measure the area of the antimicrobial zone. Table 1 shows the antimicrobial activity stability of silver colloid, Table 2 shows the antimicrobial activity stability of natural mugwort.
표 1Table 1
표 2TABLE 2
상기 데이터에 나타난 바와 같이, 한달동안 은콜로이드와 천연쑥추출물은 항균활성에 큰 차이를 보이지 않음을 알 수 있으며, 이는 안정하다고 볼수 있다. 그리고, 비록 도시하지는 않았지만 DASA역시 동일한 안정성을 나타낸다.As shown in the data, for one month, silver colloid and natural mugwort extract do not show a significant difference in antimicrobial activity, which can be seen as stable. And although not shown, DASA also shows the same stability.
실시예 6 인체적용 부작용테스트Example 6 Side Effects Test
20대부터 40까지의 여성 11명을 대상으로 하여 부작용에 대한 실험을 하였다. 인체의 겨드랑이 근처 팔안쪽에 은콜로이드와 천연쑥추출물, DASA 그리고 DASA를 첨가한 스킨을 바르고 48시간 후 변화를 관찰하였다. 이들 중 어느것에도 특별한 부작용이나 부어오름 등을 관찰할 수가 없었으며, 이러한 실험결과에 따르면 기존 화장품에 함유된 화학합성된 방부제보다는 보다 효과적임을 알 수 있다.Eleven women in their 20s to 40s were tested for side effects. Changes were observed 48 hours after the application of silver colloid, natural mugwort extract, DASA and DASA added to the arm near the armpit. None of them could observe special side effects or swelling, and these experimental results show that they are more effective than the chemically synthesized preservatives contained in conventional cosmetics.
실시예 7 : 제품에서 기존방부제와 DASA의 방부효과 비교Example 7 Comparison of Preservative Effects of Preservatives and DASA in Products
방부제를 제거한 것과 기존 방부제를 첨가한 것 그리고 DASA를 첨가한 제품을 만들어 방부효과를 비교하였다. 실험을 위하여 화장품은 소비자들이 널리 사용하는 스킨과 크림을 사용하였다. 스타필로코커스 아우레우스를 배양하여 스킨과 크림에 6.72 ×107/g으로 분주하여 4주동안 생균수의 측정으로 방부효과를 비교하였다. 스킨에서의 결과는 표3에 그리고 크림에서의 결과는 표4에 나타내었다.The preservative effect was compared by removing preservatives, adding preservatives, and adding DASA. For the experiment, cosmetics used skins and creams widely used by consumers. Staphylococcus aureus was cultured and dispensed into skin and cream at 6.72 × 10 7 / g to compare the preservative effect by measuring the viable cell count for 4 weeks. The results in the skin are shown in Table 3 and the results in the cream in Table 4.
표 3TABLE 3
표 4Table 4
상기 표에 나타난 바와 같이, 제품에 방부제를 제거하였을 경우, 균수가 처음에는 줄어들다가 점차적으로 늘어나는 현상 즉, 미생물의 번식에 의한 화장품의 변성이 나타남을 알 수 있으나, 기존 합성방부제와 DASA는 시간이 지날수록 균수가 줄어들어 4주일 후에는 살아있는 균을 발견할 수 없었다. 즉, 이는 기존합성방부제와 DASA의 방부능력은 거의 차이가 없음을 나타내며, DASA가 방부제로서의 적합함을 알 수 있다.As shown in the table, when the preservatives are removed from the product, the number of bacteria decreases initially and then gradually increases, that is, the degeneration of cosmetics due to the propagation of microorganisms appears, but the existing synthetic preservatives and DASA do not have time. As the number of bacteria passed, the live bacteria could not be found after 4 weeks. That is, it indicates that the preservative ability of the existing synthetic preservatives and DASA is almost no difference, it can be seen that DASA is suitable as a preservative.
이상에서 살펴본 바와 같이, 본 발명에 따르면, 기존의 방부제와 동일한 방부효능을 가지면서, 피부의 부어오름 및 간지럼증 등의 인체에 전혀 부작용이 발생되지 않으므로 알레르기에 대한 특이체질 뿐만 아니라 일반인들에게 안심하고 사용할 수 있는 천연방부제를 제공하는 효과가 있다.As described above, according to the present invention, while having the same antiseptic effect as the existing preservatives, no side effects occur in the human body such as skin swelling and tickling, so it is safe for the general public as well as specific constitution for allergy. It is effective in providing natural preservatives that can be used.
Claims (4)