JPWO2018110465A1 - ウインドシールド、ウインドシールド用ガラス製品及び防曇部材 - Google Patents
ウインドシールド、ウインドシールド用ガラス製品及び防曇部材 Download PDFInfo
- Publication number
- JPWO2018110465A1 JPWO2018110465A1 JP2018556646A JP2018556646A JPWO2018110465A1 JP WO2018110465 A1 JPWO2018110465 A1 JP WO2018110465A1 JP 2018556646 A JP2018556646 A JP 2018556646A JP 2018556646 A JP2018556646 A JP 2018556646A JP WO2018110465 A1 JPWO2018110465 A1 JP WO2018110465A1
- Authority
- JP
- Japan
- Prior art keywords
- water
- film
- absorbing film
- water absorbing
- relative humidity
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
車外の情報を取得するために車内へと入射する光を受ける情報取得装置の配置に適したウインドシールドであって、
ガラス板と、
前記ガラス板に対する前記情報取得装置の固定と、前記車内を前記光が通過する光路を含む光路空間と前記車内の乗車空間との間との遮光と、から選ばれる少なくとも一つの機能を担うための固定及び/又は遮光用部材と、を備え、
前記ガラス板と前記固定及び/又は遮光用部材とから選ばれる少なくとも一つの前記光路空間に接する表面に、吸水性膜が配置され、
前記吸水性膜の膜単位面積当たりの飽和吸水量Wsが1g/m2以上であり、
相対湿度が横軸に示され、吸着した水蒸気量が縦軸に示され、前記飽和吸水量の値が原点よりも前記縦軸の上方に位置する直交座標系において、前記吸水性膜の水蒸気の吸着等温線が、前記相対湿度20〜90%の区間において下方に凸となる曲線となる、との条件A1と、
前記吸水性膜の水蒸気の吸着等温線において、相対湿度を70%から95%に上昇させたときの前記吸水性膜の吸水量の増加をAbHとしたときに、前記吸水量の増加AbHが前記飽和吸水量Wsの35%よりも大きい、との条件B1、とから選ばれる少なくとも一つを満たす、
ウインドシールド、を提供する。
ガラス板と、前記ガラス板の表面に配置された吸水性膜を備えたウインドシールド用ガラス製品であって、
前記吸水性膜の膜単位面積当たりの飽和吸水量Wsが1g/m2以上であり、
相対湿度が横軸に示され、吸着した水蒸気量が縦軸に示され、前記飽和吸水量の値が原点よりも前記縦軸の上方に位置する直交座標系において、前記吸水性膜の水蒸気の吸着等温線が、前記相対湿度20〜90%の区間において下方に凸となる曲線となる、との条件A1と、
前記吸水性膜の水蒸気の吸着等温線において、相対湿度を70%から95%に上昇させたときの前記吸水性膜の吸水量の増加をAbHとしたときに、前記吸水量の増加AbHが前記飽和吸水量Wsの35%よりも大きい、との条件B1、とから選ばれる少なくとも一つを満たす、
ウインドシールド用ガラス製品、を提供する。
基材と、前記基材の第1表面に担持された吸水性膜と、前記第1表面の反対側の前記基材の第2表面に形成された粘着剤層と、を備えた防曇部材とであって、
前記吸水性膜の膜単位面積当たりの飽和吸水量Wsが1g/m2以上であり、
相対湿度が横軸に示され、吸着した水蒸気量が縦軸に示され、前記飽和吸水量の値が原点よりも前記縦軸の上方に位置する直交座標系において、前記吸水性膜の水蒸気の吸着等温線が、前記相対湿度20〜90%の区間において下方に凸となる曲線となる、との条件A1と、
前記吸水性膜の水蒸気の吸着等温線において、相対湿度を70%から95%に上昇させたときの前記吸水性膜の吸水量の増加をAbHとしたときに、前記吸水量の増加AbHが前記飽和吸水量Wsの35%よりも大きい、との条件B1、とから選ばれる少なくとも一つを満たす、
防曇部材、を提供する。
(第1形態)
図1及び図2に示すように、本実施形態に係るウインドシールド1は、車体の前方において車内と車外とを画するガラス板5を備えている。ガラス板5は、車外側の表面が斜め上方を向くように傾斜した状態で車体に設置されている。ウインドシールド1の部材としてのガラス板5としては、通常、複数のガラス単板を樹脂中間膜により接合した合わせガラスが使用される。合わせガラスは、典型的には、2枚のガラス単板と2枚のガラス単板を接合する1枚の樹脂中間膜とを備えている。
本発明に係るウインドシールド1の別の実施形態を図3に示す。この形態は、防曇部材8が、ガラス板5上にではなく、固定及び/又は遮光用部材、具体的にはカバー62上に配置されている点で第1形態と相違するが、これ以外の点は第1形態と同一である。吸水性膜の特性を含め、第1形態と同一である事項に関しては説明を省略する。
本発明に係るウインドシールド1のまた別の実施形態を図4に示す。この形態では、防曇部材8又は吸水性膜81が、遮蔽膜7の開口71oの端部の全周に接するように配置されている点で第1形態と相違するが、これ以外の点は第1形態と同一である。ここでも第1形態と同一である事項に関しては説明を省略する。この形態は、吸水性膜81をガラス板5の表面に単層膜として形成する場合に特に適している。
本発明に係るウインドシールド1のさらに別の実施形態を図5に示す。この形態では、吸水性膜81が、遮蔽膜7の開口71oの上方端を乗り越えて遮蔽膜7の一部を覆うように形成されている点で第3形態と相違するが、これ以外の点は第3形態と同一である。ここでも既に説明した事項に関しては説明を省略する。
ウインドシールド用ガラス製品は、例えば、上記各形態で説明したウインドシールド1から、固定及び/又は遮光用部材61、62を除いた各部材により構成される。このガラス製品は、例えば、ガラス板5と、ガラス板5の表面に形成された遮蔽膜7と、遮蔽膜7の開口71o又は後退部71r内に配置された吸水性膜81とを備えている。吸水性膜81に代えてこの膜を含む防曇部材8を用いてもよい。上記各形態を参照すればウインドシールド用ガラス製品の実施形態を容易に理解できるから、同製品についてはこれ以上の説明を省略する。
図6に防曇部材8の一形態を配置した状態の断面を示す。防曇部材8は、基材85と、基材85の表面(第1表面)に担持された吸水性膜81と、基材85の反対側の表面(第2表面)に形成された粘着剤層82とを備えている。吸水性膜81は、積層体である防曇部材8の最上層に位置し、光路空間41に露出している。粘着剤層82は、ガラス板5の車内側表面、又はカバー62等の部材の表面に固定され、これによって防曇部材8はガラス板5等の表面に貼りつけられている。
<ガラス板/合わせガラス>
ウインドシールドを構成するガラス板としては、通常、合わせガラスが使用される。合わせガラスは、一般に、内側ガラス板及び外側ガラス板を備え、これらのガラス板がその間に配置された樹脂製中間膜により互いに接合されている。ガラス板は、公知のガラス板、例えばクリアガラス、グリーンガラス、UVグリーンガラス等と呼ばれるガラス板であってよい。ただし、ガラス板の組成は、合わせガラス5の可視光透過率が各国の規格(例えば70%以上、あるいは75%以上)を満たすように選択する必要がある。
次に、遮蔽膜7について説明する。遮蔽膜7は、しばしばセラミックプリントと呼ばれ、車外からの視線を遮るマスクとして機能する。遮蔽膜7は、セラミックペーストを所定のパターンに印刷し、印刷したセラミックペーストを焼成することにより形成することができる。セラミックペーストは、例えば、黒色顔料と、ガラス板と熱融着して機械的強度を発現するためのガラスフリットと、焼成により除去可能な有機バインダと、スクリーン印刷に適した粘性を持たせるためのパインオイル等の有機溶剤との混合物である。セラミックペーストの焼成は、ガラス板の曲げ成形時の加熱によって同時に進めることができる。
吸水性膜81は、撥水基と金属酸化物成分とを含むことが好ましく、吸水性樹脂をさらに含むことが好ましい。吸水性膜は、必要に応じ、その他の機能成分をさらに含んでいてもよい。吸水性樹脂は、水を吸収して保持できる樹脂であればその種類を問わず、吸水性膜の飽和吸水量を増加させる。撥水基は、吸水性樹脂その他の成分と組み合わせることにより、吸水性膜の吸水特性が高湿度域において発揮されやすくする。後述するとおり、撥水基は、吸水性膜の内部にまで水蒸気を取り込むことに寄与し、高湿度域における吸水特性を改善していると考えられる。撥水基は、撥水基を有する金属化合物(撥水基含有金属化合物)から吸水性膜に供給することができる。金属酸化物成分は、撥水基含有金属化合物その他の金属化合物、金属酸化物微粒子等から吸水性膜に供給することができる。以下、各成分について説明する。
吸水性樹脂としては、ウレタン樹脂、エポキシ樹脂、アクリル樹脂、ポリビニルアセタール樹脂、及びポリビニルアルコール樹脂からなる群から選ばれる少なくとも1種を例示できる。ウレタン樹脂としては、ポリイソシアネートとポリオールとで構成されるポリウレタン樹脂が挙げられる。ポリオールとしては、アクリルポリオール及びポリオキシアルキレン系ポリオールが好ましい。エポキシ系樹脂としては、グリシジルエーテル系エポキシ樹脂、グリシジルエステル系エポキシ樹脂、グリシジルアミン系エポキシ樹脂、環式脂肪族エポキシ樹脂が挙げられる。好ましいエポキシ樹脂は、環式脂肪族エポキシ樹脂である。以下、好ましい吸水性樹脂であるポリビニルアセタール樹脂(以下、単に「ポリアセタール」)について説明する。
撥水基は、吸水性膜の強度と防曇性との両立を容易にすると共に、膜の表面を疎水性として水滴が形成されたとしても入射する光の直進性を確保することに貢献する。撥水基による効果を十分に得るためには、撥水性が高い撥水基を用いることが好ましい。好ましい撥水基は、(1)炭素数3〜30の鎖状又は環状のアルキル基、及び(2)水素原子の少なくとも一部をフッ素原子により置換した炭素数1〜30の鎖状又は環状のアルキル基(以下、「フッ素置換アルキル基」ということがある)から選ばれる少なくとも1種である。
撥水基を吸水性膜に配合するためには、撥水基を有する金属化合物(撥水基含有金属化合物)、特に撥水基と加水分解可能な官能基又はハロゲン原子とを有する金属化合物(撥水基含有加水分解性金属化合物)又はその加水分解物を、膜を形成するための塗布液に添加するとよい。言い換えると、撥水基は、撥水基含有加水分解性金属化合物に由来するものであってもよい。撥水基含有加水分解性金属化合物としては、以下の式(I)に示す撥水基含有加水分解性シリコン化合物が好適である。
ここで、Rは、撥水基、すなわち水素原子の少なくとも一部がフッ素原子により置換されていてもよい炭素数1〜30の鎖状又は環状のアルキル基であり、Yは加水分解可能な官能基又はハロゲン原子であり、mは1〜3の整数である。加水分解可能な官能基は、例えば、アルコキシル基、アセトキシ基、アルケニルオキシ基及びアミノ基から選ばれる少なくとも1種であり、好ましくはアルコキシ基、特に炭素数1〜4のアルコキシ基である。アルケニルオキシ基は、例えばイソプロペノキシ基である。ハロゲン原子は、好ましくは塩素である。なお、ここに例示した官能基は、以降に述べる「加水分解可能な官能基」としても使用することができる。mは好ましくは1〜2である。
RmSiO(4-m)/2 (II)
ここで、R及びmは、上述したとおりである。加水分解及び重縮合の後、式(II)により示される化合物は、実際には、吸水性膜中において、シリコン原子が酸素原子を介して互いに結合したネットワーク構造を形成する。
吸水性膜は、金属酸化物成分を含んでいてもよい。金属酸化物成分は、例えば、Si、Ti、Zr、Ta、Nb、Nd、La、Ce及びSnから選ばれる少なくとも1種の元素の酸化物成分であり、好ましくはSiの酸化物成分(シリカ成分)である。吸水性樹脂を含む場合、吸水性膜は、吸水性樹脂100質量部に対し、0.01質量部以上、好ましくは0.1質量部以上、より好ましくは0.2質量部以上、さらに好ましくは1質量部以上、特に好ましくは5質量部以上、場合によっては7質量部以上、必要であれば10質量部以上、また、60質量部以下、特に50質量部以下、好ましくは40質量部以下、さらに好ましくは30質量部以下、特に好ましくは20質量部以下、場合によっては18質量部以下となるように、金属酸化物成分を含むことが好ましい。金属酸化物成分は、膜の強度、特に耐擦傷性を確保するために必要な成分であるが、その含有量が過多となると膜の防曇性が低下する。
吸水性膜は、金属酸化物成分の少なくとも一部として金属酸化物微粒子をさらに含んでいてもよい。金属酸化物微粒子を構成する金属酸化物は、例えば、Si、Ti、Zr、Ta、Nb、Nd、La、Ce及びSnから選ばれる少なくとも1種の元素の酸化物であり、好ましくはシリカ微粒子である。シリカ微粒子は、例えば、コロイダルシリカを添加することにより膜に導入できる。金属酸化物微粒子は、吸水性膜に加えられた応力を膜を支持する透明物品に伝達する作用に優れ、硬度も高い。したがって、金属酸化物微粒子の添加は、吸水性膜の耐摩耗性及び耐擦傷性を向上させる観点から有利である。また、吸水性膜に金属酸化物微粒子を添加すると、微粒子が接触又は近接している部位に微細な空隙が形成され、この空隙から膜中に水蒸気が取り込まれやすくなる。このため、金属酸化物微粒子の添加は、防曇性の向上に有利に作用することもある。金属酸化物微粒子は、吸水性膜を形成するための塗布液に予め形成した金属酸化物微粒子を添加することにより、吸水性膜に供給することができる。
吸水性膜は、撥水基を有しない加水分解性金属化合物(撥水基非含有加水分解性化合物)に由来する金属酸化物成分を含んでいてもよい。好ましい撥水基非含有加水分解性金属化合物は、撥水基を有しない加水分解性シリコン化合物である。撥水基を有しない加水分解性シリコン化合物は、例えば、シリコンアルコキシド、クロロシラン、アセトキシシラン、アルケニルオキシシラン及びアミノシランから選ばれる少なくとも1種のシリコン化合物(ただし、撥水基を有しない)であり、撥水基を有しないシリコンアルコキシドが好ましい。なお、アルケニルオキシシランとしては、イソプロペノキシシランを例示できる。
上述したとおり、Yは、加水分解可能な官能基であって、好ましくはアルコキシル基、アセトキシ基、アルケニルオキシ基、アミノ基及びハロゲン原子から選ばれる少なくとも1つである。
吸水性膜は、架橋剤、好ましくは有機ホウ素化合物、有機チタン化合物及び有機ジルコニウム化合物から選ばれる少なくとも1種の架橋剤、に由来する架橋構造を含んでいてもよい。架橋構造の導入は、吸水性膜の耐摩耗性、耐擦傷性、耐水性を向上させる。別の観点から述べると、架橋構造の導入は、吸水性膜の防曇性能を低下させることなくその耐久性を改善することを容易にする。
吸水性膜にはその他の添加剤を配合してもよい。添加剤としては、防曇性を改善する機能を有するグリセリン、エチレングリコール等のグリコール類が挙げられる。添加剤は、界面活性剤、レベリング剤、紫外線吸収剤、着色剤、消泡剤、防腐剤等であってもよい。
吸水性膜81の膜厚は、要求される吸水特性その他に応じて適宜調整すればよい。吸水性膜81の好ましい膜厚は、1〜20μm、好ましくは2〜15μm、特に3〜10μmである。
吸水性膜81は、吸水性膜81を形成するための塗布液をガラス板(合わせガラス)上に塗布し、塗布した塗布液を乾燥させ、必要に応じてさらに高温高湿処理等を実施することにより、成膜することができる。塗布液の調製に用いる溶媒、塗布液の塗布方法は、従来から公知の材料及び方法を用いればよい。塗布液の塗布に際しては、吸水性膜81の膜厚及びその分布の調整のために、合わせガラスの姿勢を適切に制御し、必要に応じて、塗布しながら、あるいは塗布した後に、その姿勢を変更してもよい。
a)吸水性樹脂100質量部に対し、金属酸化物成分を0.1〜60質量部、撥水基を0.05〜10質量部含む、吸水性膜。
b)撥水基は、炭素数1〜8、特に4〜8の鎖状アルキル基であり、撥水基は、金属酸化物成分を構成する金属原子に直接結合しており、金属原子がシリコンである、吸水性膜。
c)金属酸化物成分の少なくとも一部が、吸水性膜を形成するための塗布液に添加された、加水分解性金属化合物又は加水分解性金属化合物の加水分解物に由来する金属酸化物成分であって、加水分解性金属化合物は、撥水基を有する加水分解性金属化合物、及び撥水基を有しない加水分解性金属化合物から選ばれる少なくとも1種である、吸水性膜。
d)撥水基を有しない加水分解性金属化合物が、テトラアルコキシシラン及びシランカップリング剤から選ばれる少なくとも1種を含む、c)の吸水性膜。
防曇部材8を構成する基材85は、樹脂フィルムが好適である。樹脂フィルムを構成する材料としては、ポリエチレン、ポリプロピレン等のポリオレフィン、ポリエチレンテレフタレート等のポリエステル、ポリカーボネート、ポリイミド、トリアセテート、ポリテトラフルオロエチレン等のフッ素樹脂等を例示できる。基材85の好ましい厚さ及び熱伝導率については上述したとおりである。上述した好ましい熱伝導率を具備する樹脂フィルムとしては、ポリエステルフィルムである東洋紡社「コスモシャインA4300」が挙げられる。
防曇部材8を構成する粘着剤層82を構成する粘着剤としては、ゴム系粘着剤、アクリル系粘着剤、シリコーン系粘着剤、ウレタン系粘着剤等の各種粘着剤を使用できる。ガラス板5の表面に貼りつける防曇部材8の粘着剤層82には、透明性に優れたアクリル系粘着剤が適している。粘着剤層82の厚みは、特に制限はなく、粘着剤の種類等に応じて適宜設定すればよいが、例えば1〜500μm、特に10〜100μmである。
サンプルの透明性及びクラックの有無を目視で観察し、下記の基準で評価した。
○:良好
△:僅かに白濁が認められる。
×:膜中にムラ、白濁、クラック等が認められ、実用上問題がある。
サンプルを、室温20℃、相対湿度50%の環境下に1時間放置した後、KLA Tencor社製の表面形状測定器α-Step500を用いて吸水性膜の膜厚を測定した。
サンプルを、室温20℃、相対湿度50%の環境下に1時間放置した後、協和界面科学社製の接触角計(CA-A)を用いて約4μL(=4mg)の水滴を吸水性膜の表面に滴下し、吸水性膜の表面におけるその水滴の接触角を測定した。
サンプルを、室温20℃、相対湿度30%の環境下に1時間放置した。一方で、恒温水槽に水温を40℃に保持した温水を収容し、その温水の上方にサンプルを吸水性膜が水蒸気に晒されるように配置し、吸水性膜に曇りが認められるまでの時間を測定した。なお、吸水性膜を設けていないガラス板(ソーダライムガラス板)では、10秒以下で曇りが確認された。曇りが形成されるまでの時間を下記の基準で評価した。
◎:85秒超で曇りが確認された。
○:60秒超85秒以下で曇りが確認された。
△:30秒超60秒以下で曇りが確認された。
×:30秒以下で曇りが確認された。
マイクロトラックベル株式会社の蒸気吸着量測定装置「BELSORP−18PLUS HT」を用い、定容量法により、サンプルについて、水蒸気の吸脱着特性を測定した。測定温度は10℃とした。この測定により、各相対湿度における吸着等温線上の吸水量(例えば相対湿度70%の吸水量A70)、脱着等温線上の吸水量(例えば相対湿度70%の吸水量D70)、及び飽和吸水量を得た。
ポリビニルアセタール樹脂含有溶液(積水化学工業社製「エスレックKX−5」、固形分8質量%、アセタール化度9モル%、ベンズアルデヒドに由来するアセタール構造を含む)87.5質量%、n−ヘキシルトリメトキシシラン(HTMS、信越シリコーン社製「KBM−3063」)0.26質量%、3−グリシドキシプロピルトリメトキシシラン(GPTMS、信越シリコーン社製「KBM−403」)0.10質量%、テトラエトキシシラン(TEOS、信越シリコーン社製「KBE−04」)1.39質量%、アルコール溶媒(日本アルコール工業製「ソルミックスAP−7」)7.86質量%、精製水2.87質量%、酸触媒として塩酸0.01質量%、レベリング剤(信越シリコーン社製「KP−341」)0.01質量%をガラス製容器に入れ、室温(25℃)で3時間撹拌することにより、吸水性膜形成用塗布液を調製した。
表1の組成となるように、実施例1と同様の手順で吸水性膜形成用塗布膜を調製し、サンプルを作製した。
Claims (13)
- 車外の情報を取得するために車内へと入射する光を受ける情報取得装置の配置に適したウインドシールドであって、
ガラス板と、
前記ガラス板に対する前記情報取得装置の固定と、前記車内を前記光が通過する光路を含む光路空間と前記車内の乗車空間との間との遮光と、から選ばれる少なくとも一つの機能を担うための固定及び/又は遮光用部材と、を備え、
前記ガラス板と前記固定及び/又は遮光用部材とから選ばれる少なくとも一つの前記光路空間に接する表面に、吸水性膜が配置され、
前記吸水性膜の膜単位面積当たりの飽和吸水量Wsが1g/m2以上であり、
相対湿度が横軸に示され、吸着した水蒸気量が縦軸に示され、前記飽和吸水量の値が原点よりも前記縦軸の上方に位置する直交座標系において、前記吸水性膜の水蒸気の吸着等温線が、前記相対湿度20〜90%の区間において下方に凸となる曲線となる、との条件A1と、
前記吸水性膜の水蒸気の吸着等温線において、相対湿度を70%から95%に上昇させたときの前記吸水性膜の吸水量の増加をAbHとしたときに、前記吸水量の増加AbHが前記飽和水蒸気量Wsの35%よりも大きい、との条件B1、とから選ばれる少なくとも一つを満たす、
ウインドシールド。
ただし、前記飽和吸水量、前記吸着等温線、及び前記吸水量の測定温度は10℃とする。 - 前記吸水性膜が、少なくとも前記条件A1を満たす、請求項1に記載のウインドシールド。
- 前記吸水性膜が、
前記直交座標系において、前記吸水性膜の水蒸気の脱着等温線が、相対湿度20〜90%の区間において下方に凸となる曲線となる、との条件A2をさらに満たす、請求項2に記載のウインドシールド。 - 前記吸水性膜が、少なくとも前記条件B1を満たす、請求項1〜3のいずれか1項に記載のウインドシールド。
- 前記吸水性膜が、
前記吸水性膜の水蒸気の脱着等温線において、相対湿度を95%から70%に低下させたときの前記吸水性膜の吸水量の減少をDeHとしたときに、前記吸水量の減少DeHが前記飽和吸水量Wsの30%よりも大きい、との条件B2をさらに満たす、請求項4に記載のウインドシールド。 - 前記吸水性膜が、
前記直交座標系において、前記吸着等温線における相対湿度85%のときの前記吸水性膜の吸水量A85に相当する前記脱着等温線上の吸水量DA85が相対湿度75%以上に位置する、との条件Cをさらに満たす、請求項1〜5のいずれか1項に記載のウインドシールド。 - 前記吸水性膜と前記光路空間に接する前記表面との間に、前記吸水性膜を担持する第1表面を有する基材と、前記基材の前記第1表面と反対側の第2表面に接する粘着剤層とが介在している、請求項1〜6のいずれか1項に記載のウインドシールド。
- 前記吸水性膜が、少なくとも、前記固定及び/又は遮光用部材の前記光路空間に接する前記表面に配置されている、請求項1〜7のいずれか1項に記載のウインドシールド。
- 前記吸水性膜が、少なくとも、前記ガラス板の前記光路空間に接する前記表面に配置されている、請求項1〜8のいずれか1項に記載のウインドシールド。
- 前記吸水性膜が、前記ガラス板の前記光路空間に接する前記表面上に直接形成されている、請求項9に記載のウインドシールド。
- 前記吸水性膜の表面に4mgの水滴を滴下して測定した水の接触角が70度以上である、請求項1〜10のいずれか1項に記載のウインドシールド。
- ガラス板と、前記ガラス板の表面に配置された吸水性膜を備えたウインドシールド用ガラス製品であって、
前記吸水性膜の膜単位面積当たりの飽和吸水量Wsが1g/m2以上であり、
相対湿度が横軸に示され、吸着した水蒸気量が縦軸に示され、前記飽和吸水量の値が原点よりも前記縦軸の上方に位置する直交座標系において、前記吸水性膜の水蒸気の吸着等温線が、前記相対湿度20〜90%の区間において下方に凸となる曲線となる、との条件A1と、
前記吸水性膜の水蒸気の吸着等温線において、相対湿度を70%から95%に上昇させたときの前記吸水性膜の吸水量の増加をAbHとしたときに、前記吸水量の増加AbHが前記飽和水蒸気量Wsの35%よりも大きい、との条件B1、とから選ばれる少なくとも一つを満たす、
ウインドシールド用ガラス製品、
ただし、前記飽和吸水量、前記吸着等温線、及び前記吸水量の測定温度は10℃とする。 - 基材と、前記基材の第1表面に担持された吸水性膜と、前記第1表面の反対側の前記基材の第2表面に形成された粘着剤層と、を備えた防曇部材とであって、
前記吸水性膜の膜単位面積当たりの飽和吸水量Wsが1g/m2以上であり、
相対湿度が横軸に示され、吸着した水蒸気量が縦軸に示され、前記飽和吸水量の値が原点よりも前記縦軸の上方に位置する直交座標系において、前記吸水性膜の水蒸気の吸着等温線が、前記相対湿度20〜90%の区間において下方に凸となる曲線となる、との条件A1と、
前記吸水性膜の水蒸気の吸着等温線において、相対湿度を70%から95%に上昇させたときの前記吸水性膜の吸水量の増加をAbHとしたときに、前記吸水量の増加AbHが前記飽和水蒸気量Wsの35%よりも大きい、との条件B1、とから選ばれる少なくとも一つを満たす、
防曇部材。
ただし、前記飽和吸水量、前記吸着等温線、及び前記吸水量の測定温度は10℃とする。