JPWO2016204105A1 - Composition for producing metal nanoparticles - Google Patents

Composition for producing metal nanoparticles Download PDF

Info

Publication number
JPWO2016204105A1
JPWO2016204105A1 JP2017525210A JP2017525210A JPWO2016204105A1 JP WO2016204105 A1 JPWO2016204105 A1 JP WO2016204105A1 JP 2017525210 A JP2017525210 A JP 2017525210A JP 2017525210 A JP2017525210 A JP 2017525210A JP WO2016204105 A1 JPWO2016204105 A1 JP WO2016204105A1
Authority
JP
Japan
Prior art keywords
composition
metal
metal nanoparticles
acid
mol
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP2017525210A
Other languages
Japanese (ja)
Other versions
JP6673352B2 (en
Inventor
謙輔 川村
謙輔 川村
崇充 森
崇充 森
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Osaka Soda Co Ltd
Original Assignee
Osaka Soda Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Osaka Soda Co Ltd filed Critical Osaka Soda Co Ltd
Publication of JPWO2016204105A1 publication Critical patent/JPWO2016204105A1/en
Application granted granted Critical
Publication of JP6673352B2 publication Critical patent/JP6673352B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

(A)シュウ酸金属塩、(B)アミン化合物、及び(C)ヒドロキシ脂肪酸を含む金属ナノ微粒子製造用組成物を加熱反応に供することにより金属ナノ微粒子が得られる。この金属ナノ微粒子は、極性溶媒又は極性溶媒の比率が高い溶媒混合物に分散させ易いものである。Metal nanoparticles can be obtained by subjecting the composition for producing metal nanoparticles containing (A) metal oxalate, (B) amine compound, and (C) hydroxy fatty acid to a heating reaction. The metal nanoparticles are easily dispersed in a polar solvent or a solvent mixture having a high ratio of polar solvents.

Description

本発明は、電子部品の配線形成等に用いられる導電性ペースト又はインクの材料である金属ナノ微粒子を製造するための組成物に関するものである。   The present invention relates to a composition for producing metal nano-particles which are materials of conductive paste or ink used for wiring formation of electronic parts.

近年、従来のめっき法や蒸着−フォトリソグラフィー法に代わる新たな回路形成(パターニング)方法であり、印刷によって直接回路を形成する技術である「プリンテッドエレクトロニクス」が、次世代の産業基盤として注目されている。この技術は、導電性ペースト又は導電性インクを用いて基板に所望の回路パターンを形成するものであり、薄膜トランジスタ、抵抗、インダクター、コンデンサー等の基本的な回路部品から、電池、ディスプレイ、センサー、RFID (Radio Frequency Identification)、太陽電池等の多数の応用製品まで広く応用が可能である。プリンテッドエレクトロニクスの採用により、エレクトロニクス関連製品の製造工程が、劇的に簡便になり、時間が短縮され、省資源及び省エネルギーが促進されることが期待されている。   In recent years, “printed electronics”, which is a new circuit formation (patterning) method that replaces the conventional plating method and vapor deposition-photolithography method and directly forms circuits by printing, has attracted attention as the next-generation industrial base. ing. This technology uses a conductive paste or conductive ink to form a desired circuit pattern on a substrate. From basic circuit components such as thin film transistors, resistors, inductors, and capacitors, batteries, displays, sensors, RFID (Radio Frequency Identification), many application products such as solar cells can be widely applied. The adoption of printed electronics is expected to dramatically simplify the manufacturing process of electronics-related products, reduce time, and promote resource and energy savings.

プリンテッドエレクトロニクスには、ガラス基材及びポリマーフィルムの何れも用いることができるが、広い範囲から基板材料を選択できるように、比較的低い温度での熱処理によって十分な導電性、基材との密着性が得られる導電性ペースト又は導電性インクの開発が求められている。   Although both glass substrates and polymer films can be used for printed electronics, heat treatment at a relatively low temperature ensures sufficient conductivity and adhesion to the substrate so that substrate materials can be selected from a wide range. There is a demand for the development of conductive pastes or conductive inks that can provide good properties.

この要求を満たす材料として、ナノサイズの金属ナノ微粒子を含む導電性ペースト又はインクが有望視されている。特に貴金属のナノ微粒子は、高い電気伝導性を有し、かつ、表面エネルギーの増大に起因するナノサイズ効果によって溶融温度がバルク金属よりも顕著に低下する。
しかし、平均粒子径の小さなナノ微粒子は、表面エネルギーの増加により不安定となり容易に凝集してしまうことから、ナノ微粒子の製造時、及び各種導電性インク又は導電性ペーストに配合した後に、凝集して固液分離が生じるという問題がある。
As a material that satisfies this requirement, a conductive paste or ink containing nano-sized metal nanoparticles is promising. In particular, the noble metal nanoparticles have high electrical conductivity, and the melting temperature is significantly lower than that of the bulk metal due to the nanosize effect resulting from the increase in surface energy.
However, nanoparticles with a small average particle size become unstable and easily aggregate due to an increase in surface energy. Therefore, they aggregate during the production of nanoparticles and after blending into various conductive inks or conductive pastes. Therefore, there is a problem that solid-liquid separation occurs.

この問題を解決するため、各種の保護層でナノ微粒子を被覆することが提案されている。保護層は、導電性ペースト又はインク中では安定に金属ナノ微粒子に結合して微粒子の凝集を防ぐと共に、回路形成時の焼結により容易に金属ナノ微粒子表面から脱離することが求められる。   In order to solve this problem, it has been proposed to coat the nanoparticles with various protective layers. The protective layer is required to be stably bonded to the metal nanoparticles in the conductive paste or ink to prevent the aggregation of the particles and to be easily detached from the surface of the metal nanoparticles by sintering at the time of circuit formation.

例えば、特許文献1は、シュウ酸銀と、沸点が100〜250℃のアルキルアミンと、沸点が100〜250℃のアルキルジアミンとを含む組成物を加熱反応させることにより得られる被覆金属ナノ微粒子が、保存中に凝集し難く、かつ低温焼結により容易に脱離することを教えている(段落0022)。   For example, Patent Document 1 discloses coated metal nanoparticles obtained by heating and reacting a composition containing silver oxalate, an alkylamine having a boiling point of 100 to 250 ° C., and an alkyl diamine having a boiling point of 100 to 250 ° C. Teaches that they are less likely to agglomerate during storage and are easily desorbed by low temperature sintering (paragraph 0022).

また、特許文献2は、アルコール系溶媒中、炭素数8以上の脂肪酸及び炭素数8以上の脂肪族アミンの共存下で、アルコール系溶媒に不溶な金属塩を還元させることにより得られる被覆金属ナノ微粒子が、焼結後の微粒子表面の脂肪族アミンの残存が少ないことを教えている(段落0010)。
金属塩としては、金属の炭酸塩、水酸化塩、硫酸塩等を使用している(実施例)。
炭素数8以上の脂肪酸としては、オレイン酸、オクタン酸、デカン酸、ドデカン酸、ステアリン酸等が例示されている(段落0030)。
また、得られた被覆金属ナノ微粒子を含むペースト中にヒドロキシ脂肪酸を配合する場合は、ヒドロキシ脂肪酸の親水基と疎水基の存在により、ペースト中に被覆金属ナノ微粒子を分散させ易くなることを教えている(段落0046)。
Patent Document 2 discloses a coated metal nanoparticle obtained by reducing a metal salt insoluble in an alcohol solvent in the presence of a fatty acid having 8 or more carbon atoms and an aliphatic amine having 8 or more carbon atoms in an alcohol solvent. The fine particles teach that there is little residual aliphatic amine on the surface of the fine particles after sintering (paragraph 0010).
Examples of metal salts include metal carbonates, hydroxides, sulfates, and the like (Examples).
Examples of fatty acids having 8 or more carbon atoms include oleic acid, octanoic acid, decanoic acid, dodecanoic acid, stearic acid and the like (paragraph 0030).
In addition, when blending hydroxy fatty acids in the paste containing the coated metal nanoparticles obtained, teach that the presence of the hydrophilic and hydrophobic groups of the hydroxy fatty acids makes it easier to disperse the coated metal nanoparticles in the paste. (Paragraph 0046).

しかし、これらの方法で得られる金属ナノ微粒子の保護層は、金属ナノ粒子との結合性に優れるが、疎水性が強いため、極性溶媒を含むインク又はペーストへの分散性が悪い。
例えば、ポリマーを含む導電性インク又はペーストの場合は、広い範囲からポリマーを選択できるように極性溶媒にも分散させ易い金属ナノ微粒子が求められる。また、例えば、インクジェット用のインクは極性の高い溶媒を用いるため、極性溶媒にも分散させ易い金属ナノ微粒子が求められる。
However, the protective layer of metal nanoparticles obtained by these methods is excellent in binding property to metal nanoparticles, but has a strong hydrophobicity, and therefore has a poor dispersibility in an ink or paste containing a polar solvent.
For example, in the case of a conductive ink or paste containing a polymer, metal nanoparticles that are easily dispersed in a polar solvent are required so that the polymer can be selected from a wide range. In addition, for example, since ink for inkjet uses a highly polar solvent, metal nanoparticles that are easily dispersed in a polar solvent are required.

この点に関し、特許文献3は、硝酸銀とオレイルアミンを含む組成物を加熱して被覆銀微粒子を得た後、この被覆銀微粒子とヒドロキシ酸の一種であるリシノール酸とを含む組成物を加温して、保護層を置換する方法を開示しており(実施例4)、これにより、テキサノールやテルピネオール等の極性有機溶媒への分散性が良い被覆銀微粒子が得られることを教えている(段落0007)。
しかし、特許文献3の方法で得られる被覆銀微粒子の極性溶媒への分散性は実用上十分ではない。
In this regard, Patent Document 3 heats a composition containing silver nitrate and oleylamine to obtain coated silver fine particles, and then heats the composition containing the coated silver fine particles and ricinoleic acid which is a kind of hydroxy acid. Thus, a method for replacing the protective layer is disclosed (Example 4), which teaches that coated silver fine particles having good dispersibility in polar organic solvents such as texanol and terpineol can be obtained (paragraph 0007). ).
However, the dispersibility of the coated silver fine particles obtained by the method of Patent Document 3 in a polar solvent is not sufficient in practice.

特許第5574761号公報Japanese Patent No. 5574761 特開2012−46779号公報JP 2012-46779 A 特開2013−151753号公報JP 2013-151753 A

本発明は、加熱反応により、極性溶媒又は極性溶媒の比率が高い溶媒混合物に分散させ易い金属ナノ微粒子が得られる組成物を提供することを課題とする。   This invention makes it a subject to provide the composition from which the metal nanoparticle which is easy to disperse | distribute to the solvent mixture with a high ratio of a polar solvent or a polar solvent is obtained by heat reaction.

上記課題を解決するために本発明者は研究を重ね、(A)シュウ酸金属塩、(B)アミン化合物、及び(C)ヒドロキシ脂肪酸を含む組成物を加熱反応させることにより得られる金属ナノ微粒子が、アルコール系溶媒、エステル系溶媒等の極性の高い溶媒にも分散させ易いことを見出した。
本発明は、上記知見に基づき完成されたものであり、下記の金属ナノ微粒子製造用組成物、金属ナノ微粒子の製造方法、導電性インク又はペースト、及び配線又は電極などを提供する。
In order to solve the above-mentioned problems, the present inventor has repeatedly researched and obtained metal nanoparticles obtained by heating and reacting a composition containing (A) a metal salt of oxalate, (B) an amine compound, and (C) a hydroxy fatty acid. However, it has been found that it is easy to disperse even in highly polar solvents such as alcohol solvents and ester solvents.
The present invention has been completed based on the above findings, and provides the following composition for producing metal nanoparticles, a method for producing metal nanoparticles, a conductive ink or paste, and a wiring or electrode.

項1. (A)シュウ酸金属塩、(B)アミン化合物、及び(C)ヒドロキシ脂肪酸を含む金属ナノ微粒子製造用組成物。
項2. (C)ヒドロキシ脂肪酸が、リシノール酸、及び12−ヒドロキシステアリン酸からなる群より選ばれる少なくとも1種である項1に記載の組成物。
項3. (A)シュウ酸金属塩が、シュウ酸銀である項1又は2に記載の組成物。
項4. (B)アミン化合物が、第1級アミンの1種以上、ジアミン化合物の1種以上、又は第1級アミンの1種以上とジアミン化合物の1種以上との組み合わせである項1〜3の何れかに記載の組成物。
項5. (C)ヒドロキシ脂肪酸の含有量が、(A)シュウ酸金属塩の1molに対して、0.001〜1molである項1〜4の何れかに記載の組成物。
項6. (A)シュウ酸金属塩の含有量が、組成物の全量に対して、20〜70重量%である項1〜5の何れかに記載の組成物。
項7. (B)アミン化合物の含有量が、(A)シュウ酸金属塩の1molに対して、0.4〜10molである項1〜5の何れかに記載の組成物。
項8. 項1〜7の何れかに記載の組成物を加熱反応させる工程を含む、金属ナノ微粒子の製造方法。
項9. 加熱反応温度が50〜240℃である項8に記載の方法。
項10. 金属ナノ微粒子の平均粒子径が10〜200nmである項8又は9に記載の方法。
項11. 項8〜10の何れかに記載の方法により得られる金属ナノ微粒子を含む導電性インク又はペースト。
項12. 項1〜7の何れかに記載の組成物を加熱反応させて金属ナノ微粒子を得る工程と、この金属ナノ微粒子を極性有機溶媒を含む有機溶媒に分散させる工程とを含む、導電性インク又はペーストの製造方法。
項13. 項11に記載の導電性インク又はペーストを用いて形成された回路又は電極。
項14. 項1〜7の何れかに記載の組成物を加熱反応させて金属ナノ微粒子を得る工程と、この金属ナノ微粒子を極性有機溶媒を含む有機溶媒に分散させて導電性インク又はペーストを得る工程と、この導電性インク又はペーストを用いて基板上に回路又は電極を印刷する工程とを含む、回路又は電極の形成方法。
項15. (A)シュウ酸金属塩、(B)アミン化合物、及び(C)ヒドロキシ脂肪酸を含む組成物の、金属ナノ微粒子の製造のための使用。
項16. (A)シュウ酸金属塩、(B)アミン化合物、及び(C)ヒドロキシ脂肪酸の、金属ナノ微粒子の製造のための組み合わせ使用。
Item 1. A composition for producing metal nanoparticles comprising (A) a metal oxalate salt, (B) an amine compound, and (C) a hydroxy fatty acid.
Item 2. (C) The composition according to item 1, wherein the hydroxy fatty acid is at least one selected from the group consisting of ricinoleic acid and 12-hydroxystearic acid.
Item 3. (A) The composition of claim | item 1 or 2 whose oxalate metal salt is silver oxalate.
Item 4. (B) Any one of Items 1 to 3, wherein the amine compound is one or more primary amines, one or more diamine compounds, or a combination of one or more primary amines and one or more diamine compounds. A composition according to claim 1.
Item 5. Item 5. The composition according to any one of Items 1 to 4, wherein the content of (C) hydroxy fatty acid is 0.001 to 1 mol with respect to 1 mol of (A) metal oxalate.
Item 6. (A) The composition according to any one of Items 1 to 5, wherein the content of the metal oxalate salt is 20 to 70% by weight based on the total amount of the composition.
Item 7. Item 6. The composition according to any one of Items 1 to 5, wherein the content of the (B) amine compound is 0.4 to 10 mol relative to 1 mol of the metal oxalate (A).
Item 8. Item 8. A method for producing metal nanoparticles, comprising a step of subjecting the composition according to any one of Items 1 to 7 to a heat reaction.
Item 9. Item 9. The method according to Item 8, wherein the heating reaction temperature is 50 to 240 ° C.
Item 10. Item 10. The method according to Item 8 or 9, wherein the metal nanoparticles have an average particle size of 10 to 200 nm.
Item 11. Item 11. A conductive ink or paste containing metal nanoparticles obtained by the method according to any one of Items 8 to 10.
Item 12. Item 8. A conductive ink or paste comprising a step of heating the composition according to any one of 1 to 7 to obtain metal nanoparticles, and a step of dispersing the metal nanoparticles in an organic solvent containing a polar organic solvent. Manufacturing method.
Item 13. Item 12. A circuit or electrode formed using the conductive ink or paste according to Item 11.
Item 14. The step of heat-reacting the composition according to any one of Items 1 to 7 to obtain metal nanoparticles, and the step of dispersing the metal nanoparticles in an organic solvent containing a polar organic solvent to obtain a conductive ink or paste; And a step of printing a circuit or an electrode on a substrate using the conductive ink or paste.
Item 15. Use of a composition comprising (A) a metal oxalate salt, (B) an amine compound, and (C) a hydroxy fatty acid for the production of metal nanoparticles.
Item 16. Use of (A) metal oxalate, (B) amine compound, and (C) hydroxy fatty acid in combination for the production of metal nanoparticles.

本発明によれば、極性溶媒への分散性が優れる金属ナノ微粒子が得られる。また、この金属ナノ微粒子は、導電性インク又はペーストの材料として従来汎用されている疎水性溶媒への分散性にも優れる。
また、この金属ナノ微粒子は、導電性インク又はペースト中で保護層が脱離し難く、即ち、保存性に優れる。
According to the present invention, metal nanoparticles having excellent dispersibility in a polar solvent can be obtained. In addition, the metal nanoparticles are excellent in dispersibility in a hydrophobic solvent that has been conventionally widely used as a material for conductive ink or paste.
In addition, the metal nano-particles are not easily detached from the protective layer in the conductive ink or paste, that is, they have excellent storage stability.

実施例1、比較例4で得られた金属微粒子のTg(熱重量)測定の重量変化を示す。The weight change of Tg (thermogravimetry) measurement of the metal fine particles obtained in Example 1 and Comparative Example 4 is shown.

以下、本発明を詳細に説明する。
(1)金属ナノ微粒子製造用組成物
本発明の金属ナノ微粒子製造用組成物は、(A)シュウ酸金属塩、(B)アミン化合物、及び(C)ヒドロキシ脂肪酸を含む。
Hereinafter, the present invention will be described in detail.
(1) Composition for producing metal nanoparticles The composition for producing metal nanoparticles of the present invention comprises (A) a metal oxalate salt, (B) an amine compound, and (C) a hydroxy fatty acid.

(A)シュウ酸金属塩
シュウ酸金属塩としては、シュウ酸金、シュウ酸銀、シュウ酸銅、シュウ酸白金、シュウ酸パラジウム、シュウ酸ニッケル、シュウ酸アルミニウム等を例示できる。中でも、加熱反応により導電性に優れる金属ナノ微粒子が効率よく生成する点で、シュウ酸銀、シュウ酸銅が好ましく、シュウ酸銀がより好ましい。
シュウ酸金属塩は、1種を単独で、又は2種以上を組み合わせて使用できる。
(A) Metal oxalate salt Examples of the metal oxalate salt include gold oxalate, silver oxalate, copper oxalate, platinum oxalate, palladium oxalate, nickel oxalate, and aluminum oxalate. Among these, silver oxalate and copper oxalate are preferable, and silver oxalate is more preferable in that metal nanoparticles having excellent conductivity can be efficiently generated by heating reaction.
Oxalic acid metal salts can be used singly or in combination of two or more.

組成物中のシュウ酸金属塩の含有量は、組成物の全量に対して、20重量%以上が好ましく、25重量%以上がより好ましく、30重量%以上がさらにより好ましい。この範囲であれば、加熱反応により金属ナノ微粒子が効率良く生成する。
また、組成物中のシュウ酸金属塩の含有量は、組成物の全量に対して、70重量%以下が好ましく、65重量%以下がより好ましく、60重量%以下がさらにより好ましい。この範囲であれば、加熱反応により金属ナノ微粒子が効率よく生成する。
組成物中のシュウ酸金属塩の含有量としては、組成物の全量に対して、20〜70重量%、20〜65重量%、20〜60重量%、25〜70重量%、25〜65重量%、25〜60重量%、30〜70重量%、30〜65重量%、30〜60重量%等の範囲が挙げられる。
The content of the metal oxalate salt in the composition is preferably 20% by weight or more, more preferably 25% by weight or more, and still more preferably 30% by weight or more based on the total amount of the composition. If it is this range, a metal nanoparticle will produce | generate efficiently by heating reaction.
Moreover, 70 weight% or less is preferable with respect to the whole quantity of a composition, content of the metal oxalate salt in a composition has more preferable 65 weight% or less, and 60 weight% or less is still more preferable. If it is this range, a metal nanoparticle will produce | generate efficiently by heat reaction.
The content of the metal oxalate salt in the composition is 20 to 70 wt%, 20 to 65 wt%, 20 to 60 wt%, 25 to 70 wt%, 25 to 65 wt% with respect to the total amount of the composition. %, 25-60 wt%, 30-70 wt%, 30-65 wt%, 30-60 wt%, and the like.

(B)アミン化合物
アミン化合物は、(A)シュウ酸金属塩と結合でき、かつ生成した金属ナノ微粒子の表面上で保護層を形成できるものであれば、制限なく使用できる。
例えば、アンモニアの3個の水素原子のうち、1個を直鎖、分岐、または環状の炭化水素で置換した化合物である第1級アミン(b‐1)、2個を同様に置換した第2級アミン(b‐2)、及び3個を同様に置換した第3級アミン(b‐3)を例示できる。
中でも、(A)シュウ酸金属塩と結合する能力が高く、また、得られた金属ナノ微粒子を用いた導電性インク又はペーストを基板上に塗布した後、比較的低温(例えば、PET基板を用いる際に求められる120℃以下の温度)での熱処理によって金属ナノ微粒子表面から容易に脱離する点で、第1級アミン(b‐1)が好ましい。
(B) Amine Compound The amine compound can be used without limitation as long as it can bind to (A) the metal oxalate and can form a protective layer on the surface of the generated metal nanoparticles.
For example, a primary amine (b-1), which is a compound in which one of the three hydrogen atoms of ammonia is substituted with a linear, branched, or cyclic hydrocarbon, two of which are substituted in the same manner. Examples thereof include a tertiary amine (b-2) and a tertiary amine (b-3) in which three are similarly substituted.
Among them, (A) the ability to bind to the metal oxalate is high, and after applying the conductive ink or paste using the obtained metal nanoparticles on the substrate, the temperature is relatively low (for example, using a PET substrate). The primary amine (b-1) is preferable in that it is easily detached from the surface of the metal nanoparticle by a heat treatment at a temperature of 120 ° C. or less).

第1級アミン(b‐1)としては、エチルアミン、n−プロピルアミン、イソプロピルアミン、1,2−ジメチルプロピルアミン、n−ブチルアミン、イソブチルアミン、sec−ブチルアミン、tert−ブチルアミン、イソアミルアミン、tert−アミルアミン、3−ペンチルアミン、n−アミルアミン、n−ヘキシルアミン、n−ヘプチルアミン、n−オクチルアミン、2−オクチルアミン、tert−オクチルアミン、2−エチルヘキシルアミン、n−ノニルアミン、n−アミノデカン、n−アミノウンデカン、n−ドデシルアミン、n−トリデシルアミン、2−トリデシルアミン、n−テトラデシルアミン、n−ペンタデシルアミン、n−ヘキサデシルアミン、n−ヘプタデシルアミン、n−オクタデシルアミン、n−オレイルアミン、3−メトキシプロピルアミン、3−エトキシプロピルアミン、3−プロポキシプロピルアミン、3−イソプロポキシプロピルアミン、3−ブトキシプロピルアミン、3−(2−エチルヘキシルオキシ)プロピルアミン、N‐エチル‐1,3‐プロパンジアミン、N‐ラウリル-プロパンジアミン等の直鎖又は分岐炭化水素基を有するアミン等を例示できる。
また、脂環式アミンであるシクロプロピルアミン、シクロブチルアミン、シクロプロピルアミン、シクロヘキシルアミン、シクロヘプチルアミン、シクロオクチルアミンや、芳香族アミンであるアニリン等も例示できる。
また、3−イソプロポキシプロピルアミン、イソブトキシプロピルアミン等のエーテルアミンも例示できる。
Examples of the primary amine (b-1) include ethylamine, n-propylamine, isopropylamine, 1,2-dimethylpropylamine, n-butylamine, isobutylamine, sec-butylamine, tert-butylamine, isoamylamine, tert- Amylamine, 3-pentylamine, n-amylamine, n-hexylamine, n-heptylamine, n-octylamine, 2-octylamine, tert-octylamine, 2-ethylhexylamine, n-nonylamine, n-aminodecane, n -Aminoundecane, n-dodecylamine, n-tridecylamine, 2-tridecylamine, n-tetradecylamine, n-pentadecylamine, n-hexadecylamine, n-heptadecylamine, n-octadecylamine, n-oleylami , 3-methoxypropylamine, 3-ethoxypropylamine, 3-propoxypropylamine, 3-isopropoxypropylamine, 3-butoxypropylamine, 3- (2-ethylhexyloxy) propylamine, N-ethyl-1,3 Examples thereof include amines having a linear or branched hydrocarbon group such as -propanediamine and N-lauryl-propanediamine.
Moreover, cyclopropylamine, cyclobutylamine, cyclopropylamine, cyclohexylamine, cycloheptylamine, cyclooctylamine which are alicyclic amines, aniline which is an aromatic amine, and the like can be exemplified.
Moreover, ether amines, such as 3-isopropoxypropylamine and isobutoxypropylamine, can also be illustrated.

第2級アミン(b‐2)としては、N,N−ジプロピルアミン、N,N−ジブチルアミン、N,N−ジペンチルアミン、N,N−ジヘキシルアミン、N,N−ジペプチルアミン、N,N−ジオクチルアミン、N,N−ジノニルアミン、N,N−ジデシルアミン、N,N−ジウンデシルアミン、N,N−ジドデシルアミン、N,N−ジステアリルアミン、N−メチル−N−プロピルアミン、N−エチル−N−プロピルアミン、N−プロピル−N−ブチルアミン等のジアルキルモノアミン、及びピペリジン等の環状アミンを例示することができる。   As the secondary amine (b-2), N, N-dipropylamine, N, N-dibutylamine, N, N-dipentylamine, N, N-dihexylamine, N, N-dipeptylamine, N, N -Dioctylamine, N, N-dinonylamine, N, N-didecylamine, N, N-diundecylamine, N, N-didodecylamine, N, N-distearylamine, N-methyl-N-propylamine, N Examples include dialkyl monoamines such as ethyl-N-propylamine and N-propyl-N-butylamine, and cyclic amines such as piperidine.

第3級アミン(b‐3)としては、トリエチルアミン、トリブチルアミン、トリヘキシルアミン、ジメチルオクチルアミン、ジメチルデシルアミン、ジメチルラウリルアミン、ジメチルミリスチルアミン、ジメチルパルミチルアミン、ジメチルステアリルアミン、ジラウリルモノメチルアミン等を例示できる。   Tertiary amine (b-3) includes triethylamine, tributylamine, trihexylamine, dimethyloctylamine, dimethyldecylamine, dimethyllaurylamine, dimethylmyristylamine, dimethylpalmitylamine, dimethylstearylamine, dilaurylmonomethylamine Etc. can be illustrated.

さらに、本発明では、ひとつの化合物中に2つのアミノ基を有するジアミン化合物(b‐4)も用いることができる。ジアミン化合物(b‐4)としては、エチレンジアミン、N,N−ジメチルエチレンジアミン、N,N’−ジメチルエチレンジアミン、N,N−ジエチルエチレンジアミン、N,N’−ジエチルエチレンジアミン、1,3−プロパンジアミン、2,2−ジメチル−1,3−プロパンジアミン、N,N−ジメチル‐1,3‐プロパンジアミン、N,N‐ジブチル‐1,3‐プロパンジアミン、N,N‐ジイソブチル‐1,3‐プロパンジアミン、N,N’‐ジメチル−1,3−プロパンジアミン、N,N−ジエチル−1,3−プロパンジアミン、N,N’−ジエチル−1,3−プロパンジアミン、1,4−ブタンジアミン、N,N−ジメチル−1,4−ブタンジアミン、N,N’−ジメチル−1,4−ブタンジアミン、N,N−ジエチル−1,4−ブタンジアミン、N,N’−ジエチル−1,4−ブタンジアミン、1,5−ペンタンジアミン、1,5−ジアミノ−2−メチルペンタン、1,6−ヘキサンジアミン、N,N−ジメチル−1,6−ヘキサンジアミン、N,N’−ジメチル−1,6−ヘキサンジアミン、1,7−ヘプタンジアミン、1,8−オクタンジアミン等を例示できる。   Furthermore, in the present invention, a diamine compound (b-4) having two amino groups in one compound can also be used. Examples of the diamine compound (b-4) include ethylenediamine, N, N-dimethylethylenediamine, N, N′-dimethylethylenediamine, N, N-diethylethylenediamine, N, N′-diethylethylenediamine, 1,3-propanediamine, , 2-Dimethyl-1,3-propanediamine, N, N-dimethyl-1,3-propanediamine, N, N-dibutyl-1,3-propanediamine, N, N-diisobutyl-1,3-propanediamine N, N′-dimethyl-1,3-propanediamine, N, N-diethyl-1,3-propanediamine, N, N′-diethyl-1,3-propanediamine, 1,4-butanediamine, N , N-dimethyl-1,4-butanediamine, N, N′-dimethyl-1,4-butanediamine, N, N-diethyl-1,4-butane Diamine, N, N′-diethyl-1,4-butanediamine, 1,5-pentanediamine, 1,5-diamino-2-methylpentane, 1,6-hexanediamine, N, N-dimethyl-1,6 -Hexanediamine, N, N'-dimethyl-1,6-hexanediamine, 1,7-heptanediamine, 1,8-octanediamine and the like can be exemplified.

ジアミン化合物(b‐4)の中でも、アミンの一方が第1級アミン、他方が第3級アミンであるジアミン化合物は、(A)シュウ酸金属塩との結合能に優れ、金属ナノ微粒子が生成した際に、金属ナノ微粒子の表面上で保護層を形成し易い点で好ましい。
一方が第1級アミン、他方が第3級アミンであるジアミン化合物としては、N,N−ジメチルエチレンジアミン、N,N−ジエチルエチレンジアミン、N,N−ジメチル−1,3-プロパンジアミン、N,N−ジエチル−1,3−プロパンジアミン、N,N−ジメチル−1,4−ブタンジアミン、N,N−ジエチル−1,4−ブタンジアミン、N,N−ジメチル−1,6−ヘキサンジアミン等を例示できる。
Among the diamine compounds (b-4), a diamine compound in which one of the amines is a primary amine and the other is a tertiary amine is excellent in the ability to bind to (A) metal oxalate and form metal nanoparticles. When it does, it is preferable at the point which forms a protective layer easily on the surface of a metal nanoparticle.
Examples of diamine compounds in which one is a primary amine and the other is a tertiary amine include N, N-dimethylethylenediamine, N, N-diethylethylenediamine, N, N-dimethyl-1,3-propanediamine, and N, N. -Diethyl-1,3-propanediamine, N, N-dimethyl-1,4-butanediamine, N, N-diethyl-1,4-butanediamine, N, N-dimethyl-1,6-hexanediamine and the like. It can be illustrated.

上述したアミン化合物の中でも、導電性インク又はペースト中での金属ナノ微粒子での分散安定性、及び回路形成時に低温の熱処理で容易に脱離可能な点で、n‐プロピルアミン、イソプロピルアミン、シクロプロピルアミン、n‐ブチルアミン、イソブチルアミン、sec‐ブチルアミン、tert‐ブチルアミン、シクロブチルアミン、n‐アミルアミン、n‐ヘキシルアミン、シクロヘキシルアミン、n‐オクチルアミン、2‐エチルヘキシルアミン、n‐ドデシルアミン、n‐オレイルアミン、3−メトキシプロピルアミン、3−エトキシプロピルアミン、3−プロポキシプロピルアミン、3−イソプロポキシプロピルアミン、N,N−ジメチル‐1,3‐プロパンジアミン、N,N‐ジブチル‐1,3‐アミノプロパンが好ましく、n‐ブチルアミン、n‐ヘキシルアミン、シクロヘキシルアミン、n‐オクチルアミン、n‐ドデシルアミン、N,N−ジメチル‐1,3‐プロパンジアミン、N,N‐ジブチル‐1,3‐アミノプロパン、3−メトキシプロピルアミン、3−エトキシプロピルアミンがより好ましく、n−ブチルアミン、n−ヘキシルアミン、シクロヘキシルアミン、n−オクチルアミン、n−ドデシルアミン、3−メトキシプロピルアミン、3−エトキシプロピルアミン、N,N−ジメチル−1,3−プロパンジアミンがさらにより好ましい。   Among the amine compounds mentioned above, n-propylamine, isopropylamine, cyclohexane, and the like are stable in dispersion with metal nanoparticles in conductive ink or paste, and can be easily detached by low-temperature heat treatment during circuit formation. Propylamine, n-butylamine, isobutylamine, sec-butylamine, tert-butylamine, cyclobutylamine, n-amylamine, n-hexylamine, cyclohexylamine, n-octylamine, 2-ethylhexylamine, n-dodecylamine, n- Oleylamine, 3-methoxypropylamine, 3-ethoxypropylamine, 3-propoxypropylamine, 3-isopropoxypropylamine, N, N-dimethyl-1,3-propanediamine, N, N-dibutyl-1,3- Aminopropane is preferred, n Butylamine, n-hexylamine, cyclohexylamine, n-octylamine, n-dodecylamine, N, N-dimethyl-1,3-propanediamine, N, N-dibutyl-1,3-aminopropane, 3-methoxypropyl More preferred are amines and 3-ethoxypropylamine, n-butylamine, n-hexylamine, cyclohexylamine, n-octylamine, n-dodecylamine, 3-methoxypropylamine, 3-ethoxypropylamine, N, N-dimethyl. -1,3-propanediamine is even more preferred.

(B)アミン化合物は、1種を単独で、又は2種以上を組み合わせて用いることができる。具体的には、(b‐1)、(b‐2)、(b‐3)、(b‐4)の中の1つ以上を使用することができ、特に、(b‐1)のみ、(b‐4)のみ、及び(b‐1)と(b‐4)との組み合わせが好ましい。さらに、(b‐1)、(b‐2)、(b‐3)、(b‐4)の各群の中でも1種以上を使用することができる。   (B) An amine compound can be used individually by 1 type or in combination of 2 or more types. Specifically, one or more of (b-1), (b-2), (b-3), (b-4) can be used, in particular, only (b-1), Only (b-4) and a combination of (b-1) and (b-4) are preferred. Furthermore, 1 or more types can be used among each group of (b-1), (b-2), (b-3), (b-4).

組成物中の(B)アミン化合物の含有量は、組成物の全量に対して、5重量%以上が好ましく、10重量%以上がより好ましく、20重量%以上がさらにより好ましい。この範囲であれば、シュウ酸金属塩と良好な結合を形成し、かつ生成した金属ナノ微粒子の表面上で保護層を形成することができる。
また、組成物中の(B)アミン化合物の含有量は、組成物の全量に対して、55重量%以下が好ましく、50重量%以下がより好ましく、45重量%以下がさらにより好ましい。この範囲であれば、シュウ酸金属塩と良好な結合を形成し、かつ生成した金属ナノ微粒子の表面上で保護層を形成することができる。
組成物中の(B)アミン化合物の含有量としては、組成物の全量に対して、5〜55重量%、5〜50重量%、5〜45重量%、10〜55重量%、10〜50重量%、10〜45重量%、20〜55重量%、20〜50重量%、20〜45重量%等の範囲が挙げられる。
The content of the (B) amine compound in the composition is preferably 5% by weight or more, more preferably 10% by weight or more, and still more preferably 20% by weight or more based on the total amount of the composition. Within this range, it is possible to form a good bond with the metal oxalate and form a protective layer on the surface of the generated metal nanoparticles.
Further, the content of the (B) amine compound in the composition is preferably 55% by weight or less, more preferably 50% by weight or less, and even more preferably 45% by weight or less based on the total amount of the composition. Within this range, it is possible to form a good bond with the metal oxalate and form a protective layer on the surface of the generated metal nanoparticles.
As content of (B) amine compound in a composition, it is 5-55 weight%, 5-50 weight%, 5-45 weight%, 10-55 weight%, 10-50 with respect to the whole quantity of a composition. The range of weight%, 10-45 weight%, 20-55 weight%, 20-50 weight%, 20-45 weight% etc. is mentioned.

組成物中の(B)アミン化合物の含有量は、シュウ酸金属塩の1molに対して、0.4mol以上が好ましく、0.6mol以上がより好ましく、1mol以上がさらにより好ましい。この範囲であれば、シュウ酸金属塩と良好な結合を形成し、かつ生成した金属ナノ微粒子の表面上で保護層を形成することができる。
また、組成物中の(B)アミン化合物の含有量は、シュウ酸金属塩の1molに対して、10mol以下が好ましく、8mol以下がより好ましく、6mol以下がさらにより好ましい。この範囲であれば、シュウ酸金属塩と良好な結合を形成し、かつ生成した金属ナノ微粒子の表面上で保護層を形成することができる。
シュウ酸金属塩の1molに対する(B)アミン化合物の量としては、0.4〜10mol、0.4〜8mol、0.4〜6mol、0.6〜10mol、0.6〜8mol、0.6〜6mol、1〜10mol、1〜8mol、1〜6mol等の範囲が挙げられる。
The content of the (B) amine compound in the composition is preferably 0.4 mol or more, more preferably 0.6 mol or more, and even more preferably 1 mol or more with respect to 1 mol of the metal oxalate salt. Within this range, it is possible to form a good bond with the metal oxalate and form a protective layer on the surface of the generated metal nanoparticles.
In addition, the content of the (B) amine compound in the composition is preferably 10 mol or less, more preferably 8 mol or less, and even more preferably 6 mol or less with respect to 1 mol of the metal oxalate salt. Within this range, it is possible to form a good bond with the metal oxalate and form a protective layer on the surface of the generated metal nanoparticles.
The amount of the (B) amine compound relative to 1 mol of the metal oxalate is 0.4 to 10 mol, 0.4 to 8 mol, 0.4 to 6 mol, 0.6 to 10 mol, 0.6 to 8 mol, 0.6 The range of -6 mol, 1-10 mol, 1-8 mol, 1-6 mol, etc. is mentioned.

(C)ヒドロキシ脂肪酸
ヒドロキシ脂肪酸としては、炭素数3〜24で、かつ水酸基を1個以上(例えば、1個)有する化合物を使用できる。ヒドロキシ脂肪酸として、例えば、2−ヒドロキシデカン酸、2−ヒドロキシドデカン酸、2−ヒドロキシテトラデカン酸、2−ヒドロキシヘキサデカン酸、2−ヒドロキシオクタデカン酸、2−ヒドロキシエイコサン酸、2−ヒドロキシドコサン酸、2−ヒドロキシトリコサン酸、2−ヒドロキシテトラコサン酸、3−ヒドロキシヘキサン酸、3−ヒドロキシオクタン酸、3−ヒドロキシノナン酸、3−ヒドロキシデカン酸、3−ヒドロキシウンデカン酸、3−ヒドロキシドデカン酸、3−ヒドロキシトリデカン酸、3−ヒドロキシテトラデカン酸、3−ヒドロキシヘキサデカン酸、3−ヒドロキシヘプタデカン酸、3−ヒドロキシオクタデカン酸、ω−ヒドロキシ−2−デセン酸、ω−ヒドロキシペンタデカン酸、ω−ヒドロキシヘプタデカン酸、ω−ヒドロキシエイコサン酸、ω−ヒドロキシドコサン酸、6−ヒドロキシオクタデカン酸、リシノール酸、12−ヒドロキシステアリン酸、[R−(E)]−12−ヒドロキシ−9−オクタデセン酸等が挙げられる。中でも、炭素数4〜18で、かつω位以外(特に、12位)に1個の水酸基を有するヒドロキシ脂肪酸が好ましく、リシノール酸、12-ヒドロキシステアリン酸がより好ましい。
ヒドロキシ脂肪酸は、1種を単独で、又は2種以上を組み合わせて使用できる。
(C) Hydroxy fatty acid As the hydroxy fatty acid, a compound having 3 to 24 carbon atoms and having one or more hydroxyl groups (for example, one) can be used. Examples of hydroxy fatty acids include 2-hydroxydecanoic acid, 2-hydroxydodecanoic acid, 2-hydroxytetradecanoic acid, 2-hydroxyhexadecanoic acid, 2-hydroxyoctadecanoic acid, 2-hydroxyeicosanoic acid, 2-hydroxydocosanoic acid, 2-hydroxytricosanoic acid, 2-hydroxytetracosanoic acid, 3-hydroxyhexanoic acid, 3-hydroxyoctanoic acid, 3-hydroxynonanoic acid, 3-hydroxydecanoic acid, 3-hydroxyundecanoic acid, 3-hydroxydodecanoic acid, 3-hydroxytridecanoic acid, 3-hydroxytetradecanoic acid, 3-hydroxyhexadecanoic acid, 3-hydroxyheptadecanoic acid, 3-hydroxyoctadecanoic acid, ω-hydroxy-2-decenoic acid, ω-hydroxypentadecanoic acid, ω-hydroxy Heptade Acid, ω-hydroxyeicosanoic acid, ω-hydroxydocosanoic acid, 6-hydroxyoctadecanoic acid, ricinoleic acid, 12-hydroxystearic acid, [R- (E)]-12-hydroxy-9-octadecenoic acid, etc. Can be mentioned. Among these, hydroxy fatty acids having 4 to 18 carbon atoms and having one hydroxyl group other than the ω position (particularly the 12th position) are preferable, and ricinoleic acid and 12-hydroxystearic acid are more preferable.
A hydroxy fatty acid can be used individually by 1 type or in combination of 2 or more types.

組成物中の(C)ヒドロキシ脂肪酸の含有量は、組成物の全量に対して、0.01重量%以上が好ましく、0.05重量%以上がより好ましく、0.1重量%以上がさらにより好ましい。この範囲であれば、極性溶媒への分散性が実用上十分である金属ナノ微粒子が得られる。
また、組成物中のヒドロキシ脂肪酸の含有量は、組成物の全量に対して、15重量%以下が好ましく、10重量%以下がより好ましく、8重量%以下がさらにより好ましい。この範囲であれば、極性溶媒への分散性が実用上十分である金属ナノ微粒子が得られる。
組成物中のヒドロキシ脂肪酸の含有量としては、組成物の全量に対して、0.01〜15重量%、0.01〜10重量%、0.01〜8重量%、0.05〜15重量%、0.05〜10重量%、0.05〜8重量%、0.1〜15重量%、0.1〜10重量%、0.1〜8重量%等が挙げられる。
The content of (C) hydroxy fatty acid in the composition is preferably 0.01% by weight or more, more preferably 0.05% by weight or more, and even more preferably 0.1% by weight or more based on the total amount of the composition. preferable. Within this range, metal nanoparticles having practically sufficient dispersibility in polar solvents can be obtained.
Further, the content of hydroxy fatty acid in the composition is preferably 15% by weight or less, more preferably 10% by weight or less, and still more preferably 8% by weight or less based on the total amount of the composition. Within this range, metal nanoparticles having practically sufficient dispersibility in polar solvents can be obtained.
As content of the hydroxy fatty acid in a composition, it is 0.01-15 weight%, 0.01-10 weight%, 0.01-8 weight%, 0.05-15 weight% with respect to the whole quantity of a composition. %, 0.05 to 10% by weight, 0.05 to 8% by weight, 0.1 to 15% by weight, 0.1 to 10% by weight, 0.1 to 8% by weight, and the like.

組成物中の(C)ヒドロキシ脂肪酸の含有量は、シュウ酸金属塩の1molに対して、0.001mol以上が好ましく、0.005mol以上がより好ましく、0.01mol以上がさらにより好ましい。この範囲であれば、極性溶媒への分散性が実用上十分である金属ナノ微粒子が得られる。
また、組成物中のヒドロキシ脂肪酸の含有量は、シュウ酸金属塩の1molに対して、1mol以下が好ましく、0.5mol以下がより好ましく、0.25mol以下がさらにより好ましい。この範囲であれば、極性溶媒への分散性が実用上十分である金属ナノ微粒子が得られる。
シュウ酸金属塩の1molに対するヒドロキシ脂肪酸の量としては、0.001〜1mol、0.001〜0.5mol、0.001〜0.25mol、0.005〜1mol、0.005〜0.5mol、0.005〜0.25mol、0.01〜1mol、0.01〜0.5mol、0.01〜0.25mol等が挙げられる。
The content of (C) hydroxy fatty acid in the composition is preferably 0.001 mol or more, more preferably 0.005 mol or more, and still more preferably 0.01 mol or more with respect to 1 mol of the metal oxalate salt. Within this range, metal nanoparticles having practically sufficient dispersibility in polar solvents can be obtained.
Moreover, 1 mol or less is preferable with respect to 1 mol of oxalic acid metal salts, as for content of the hydroxy fatty acid in a composition, 0.5 mol or less is more preferable, and 0.25 mol or less is further more preferable. Within this range, metal nanoparticles having practically sufficient dispersibility in polar solvents can be obtained.
The amount of hydroxy fatty acid relative to 1 mol of the metal oxalate is 0.001 to 1 mol, 0.001 to 0.5 mol, 0.001 to 0.25 mol, 0.005 to 1 mol, 0.005 to 0.5 mol, 0.005-0.25 mol, 0.01-1 mol, 0.01-0.5 mol, 0.01-0.25 mol, etc. are mentioned.

有機溶媒(S)
本発明の組成物は、有機溶媒を含むことができる。有機溶媒は、20℃の水に対して約1g/L以上溶解するものが好ましく、約10g/L以上溶解するものがより好ましい。中でも、エーテル結合及びヒドロキシル基を有する化合物を有機溶媒として好適に使用できる。
Organic solvent (S)
The composition of the present invention may contain an organic solvent. The organic solvent is preferably one that dissolves about 1 g / L or more in water at 20 ° C., and more preferably one that dissolves about 10 g / L or more. Especially, the compound which has an ether bond and a hydroxyl group can be used conveniently as an organic solvent.

有機溶媒としては、ベンゼン、ベンゾニトリル等の芳香族化合物、アセトン、アセチルアセトン、メチルエチルケトン等のケトン類、酢酸エチル、酢酸ブチル、酪酸エチル、蟻酸エチル等の脂肪酸エステル類、ジエチルエーテル、ジプロピルエーテル、ジブチルエーテル、テトラヒドロフラン、1,4−ジオキサン等のエーテル類、ジクロロメタン、クロロホルム、ジクロロエタン等のハロゲン化炭化水素類、1,2−プロパンジオール、1,2−ブタンジオール、1,3−ブタンジオール、1,4−ブタンジオール、2,3−ブタンジオール、1,2−ヘキサンジオール、1,6−ヘキサンジオール、1,2−ペンタンジオール、1,5−ペンタンジオール、2−メチル−2,4−ペンタンジオール、3−メチル−1,5−ペンタンジオール等のジオール類、炭素数1〜7の直鎖又は分岐アルキルを有するアルコール、シクロヘキサノール、3−メトキシ−3−メチル−1−ブタノール、3−メトキシ−1−ブタノール、2−(2−エチルヘキシルオキシ)エタノール等のアルコール類、ポリエチレングリコール、トリエチレングリコールモノメチルエーテル、テトラエチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールジメチルエーテル、トリエチレングリコールジメチルエーテル、テトラエチレングリコールジメチルエーテル、3−メトキシブチルアセテート、エチレングリコールモノブチルエーテル、エチレングリコールモノブチルエーテルアセテート、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノメチルエーテルアセテート、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテルアセテート、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノブチルエーテル、ジプロピレングリコールモノメチルエーテル、ジプロピレングリコールモノエチルエーテル、ジプロピレングリコールモノプロピルエーテル、ジプロピレングリコールモノブチルエーテル、トリプロピレングリコールモノメチルエーテル、トリプロピレングリコールモノエチルエーテル、トリプロピレングリコールモノプロピルエーテル、トリプロピレングリコールモノブチルエーテル等のグリコールもしくはグリコールエーテル類、メチル-n-アミルケトン、メチルエチルケトンオキシム、トリアセチン、γ-ブチロラクトン、2-ピロリドン、N-メチルピロリドン、アセトニトリル、N,N-ジメチルホルムアミド、N-(2-アミノエチル)ピペラジン、ジメチルスルホキシド、及びテルピネオール等のテルペン類、等を例示することができる。
有機溶媒は、1種を単独で用いてもよく、2種以上を混合して用いてもよい。
Examples of the organic solvent include aromatic compounds such as benzene and benzonitrile, ketones such as acetone, acetylacetone, and methyl ethyl ketone, fatty acid esters such as ethyl acetate, butyl acetate, ethyl butyrate, and ethyl formate, diethyl ether, dipropyl ether, and diethyl ether. Ethers such as butyl ether, tetrahydrofuran, 1,4-dioxane, halogenated hydrocarbons such as dichloromethane, chloroform, dichloroethane, 1,2-propanediol, 1,2-butanediol, 1,3-butanediol, 1, 4-butanediol, 2,3-butanediol, 1,2-hexanediol, 1,6-hexanediol, 1,2-pentanediol, 1,5-pentanediol, 2-methyl-2,4-pentanediol 3-methyl-1,5-pentanedioe Diols such as C1-C7 linear or branched alkyl, cyclohexanol, 3-methoxy-3-methyl-1-butanol, 3-methoxy-1-butanol, 2- (2-ethylhexyloxy) ) Alcohols such as ethanol, polyethylene glycol, triethylene glycol monomethyl ether, tetraethylene glycol monomethyl ether, ethylene glycol monoethyl ether, diethylene glycol monoethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, 3-methoxybutyl Acetate, ethylene glycol monobutyl ether, ethylene glycol monobutyl ether acetate, diethylene glycol Monomethyl ether, diethylene glycol monomethyl ether acetate, diethylene glycol monoethyl ether, diethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether, diethylene glycol monobutyl ether acetate, propylene glycol monopropyl ether, propylene glycol monobutyl ether, dipropylene glycol monomethyl ether, dipropylene glycol monoethyl Ether, dipropylene glycol monopropyl ether, dipropylene glycol monobutyl ether, tripropylene glycol monomethyl ether, tripropylene glycol monoethyl ether, tripropylene glycol monopropyl ether, tripropylene glycol monobutyl ether Glycols such as tilether or glycol ethers, methyl-n-amyl ketone, methyl ethyl ketone oxime, triacetin, γ-butyrolactone, 2-pyrrolidone, N-methylpyrrolidone, acetonitrile, N, N-dimethylformamide, N- (2-aminoethyl) Examples include terpenes such as piperazine, dimethyl sulfoxide, and terpineol.
An organic solvent may be used individually by 1 type, and 2 or more types may be mixed and used for it.

中でも、沸点が高いため扱い易く、また組成物中で各成分を良好に分散することができる点で、2−(2−エチルヘキシルオキシ)エタノール、3−メトキシ−1−ブタノール、3−メトキシ−3−メチル−1−ブタノールのようなアルコキシ基を有するアルコール類、エチレングリコールモノエチルエーテル、エチレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノエチルエーテル、ジプロピレングリコールモノエチルエーテル、トリエチレングリコールモノエチルエーテル等のグリコールエーテル類が好ましい。   Among these, 2- (2-ethylhexyloxy) ethanol, 3-methoxy-1-butanol, and 3-methoxy-3 are easy to handle because they have a high boiling point and can disperse each component well in the composition. -Alcohols having an alkoxy group such as methyl-1-butanol, ethylene glycol monoethyl ether, ethylene glycol monobutyl ether, diethylene glycol monobutyl ether, diethylene glycol monoethyl ether, dipropylene glycol monoethyl ether, triethylene glycol monoethyl ether, etc. The glycol ethers are preferred.

有機溶媒を使用する場合、組成物中の有機溶媒の含有量は、シュウ酸金属塩100重量部に対して、5重量部以上が好ましく、10重量部以上がより好ましく、30重量部以上がさらにより好ましい。この範囲であれば、組成物中の各成分を均一に混合できる。
また、組成物中の有機溶媒の含有量は、シュウ酸金属塩100重量部に対して、1000重量部以下が好ましく、500重量部以下が好ましく、300重量部以下が好ましい。この範囲であれば、反応液が希薄になりすぎて反応が長くなったり、回収コストが増大するという事態が避けられる。
組成物中の有機溶媒の含有量としては、シュウ酸金属塩100重量部に対して、5〜1000重量部、5〜500重量部、5〜300重量部、10〜1000重量部、10〜500重量部、10〜300重量部、30〜1000重量部、30〜500重量部、30〜300重量部等が挙げられる。
When the organic solvent is used, the content of the organic solvent in the composition is preferably 5 parts by weight or more, more preferably 10 parts by weight or more, and further preferably 30 parts by weight or more with respect to 100 parts by weight of the metal oxalate salt. More preferred. If it is this range, each component in a composition can be mixed uniformly.
In addition, the content of the organic solvent in the composition is preferably 1000 parts by weight or less, preferably 500 parts by weight or less, and preferably 300 parts by weight or less with respect to 100 parts by weight of the metal oxalate salt. Within this range, it is possible to avoid situations where the reaction solution becomes too dilute and the reaction becomes longer or the recovery cost increases.
As content of the organic solvent in a composition, 5-1000 weight part, 5-500 weight part, 5-300 weight part, 10-1000 weight part, 10-500 with respect to 100 weight part of oxalic acid metal salts. Parts by weight, 10 to 300 parts by weight, 30 to 1000 parts by weight, 30 to 500 parts by weight, 30 to 300 parts by weight, and the like.

本発明の組成物は、本発明の効果に影響を与えない範囲で、プリンテッドエレクトロニクスに適用される金属微粒子製造用組成物に使用される添加剤の1種又は2種以上を含有できる。
このような添加剤として、脂肪酸(炭素数3〜18以下の脂肪酸、例えば、酢酸、プロピオン酸、酪酸、吉草酸、カプロン酸、カプリル酸、2−エチルヘキサン酸、カプリン酸、ラウリン酸、ミリスチン酸、パルミチン酸、ステアリン酸、オレイン酸、リノール酸、α−リノレン酸、シクロヘキサンカルボン酸等)、粘度調製剤、導電助剤、チョーキング防止剤、酸化防止剤、pH調製剤、乾燥防止剤、密着付与剤、防腐剤、消泡剤、レベリング剤、界面活性剤等が挙げられる。
The composition of this invention can contain the 1 type (s) or 2 or more types of additive used for the composition for metal fine particle manufacture applied to printed electronics in the range which does not affect the effect of this invention.
Examples of such additives include fatty acids (fatty acids having 3 to 18 carbon atoms such as acetic acid, propionic acid, butyric acid, valeric acid, caproic acid, caprylic acid, 2-ethylhexanoic acid, capric acid, lauric acid, myristic acid. , Palmitic acid, stearic acid, oleic acid, linoleic acid, α-linolenic acid, cyclohexanecarboxylic acid, etc.), viscosity adjuster, conductive aid, anti-choking agent, antioxidant, pH adjuster, anti-drying agent, adhesion imparting Agents, preservatives, antifoaming agents, leveling agents, surfactants and the like.

組成物の調製方法
本発明の組成物は、各成分を混合することにより調製できる。混合は、メカニカルスターラー、マグネティックスターラー、ボルテックスミキサー、遊星ミル、ボールミル、三本ロール、ラインミキサー、プラネタリーミキサー、ディゾルバー等の汎用の装置で行える。
混合時の溶解熱、摩擦熱等の影響で組成物の温度が上昇し、金属ナノ微粒子の熱分解反応が開始することを回避するために、組成物の温度を、例えば60℃以下、特に40℃以下に抑えながら混合することが好ましい。
Preparation Method of Composition The composition of the present invention can be prepared by mixing each component. Mixing can be performed by a general-purpose apparatus such as a mechanical stirrer, a magnetic stirrer, a vortex mixer, a planetary mill, a ball mill, a triple roll, a line mixer, a planetary mixer, and a dissolver.
In order to avoid that the temperature of the composition rises due to the influence of heat of dissolution, frictional heat, etc. during mixing and the thermal decomposition reaction of the metal nanoparticles is started, the temperature of the composition is, for example, 60 ° C. or less, particularly 40 ° C. It is preferable to mix while keeping the temperature below ℃.

(2)金属ナノ微粒子の製造方法
反応工程
上記説明した本発明の金属ナノ微粒子製造用組成物を、反応容器内で反応、通常は加熱による反応に供することにより、金属化合物の熱分解反応が起こり、金属ナノ微粒子が生成する。反応に当たっては、予め加熱しておいた反応容器内に組成物を導入してもよく、組成物を反応容器内に導入した後に加熱してもよい。
(2) Method for producing metal nanoparticles
Reaction Step By subjecting the composition for producing metal nanoparticles of the present invention described above to a reaction in a reaction vessel, usually a reaction by heating, a metal compound undergoes a thermal decomposition reaction to produce metal nanoparticles. In the reaction, the composition may be introduced into a previously heated reaction vessel, or may be heated after the composition is introduced into the reaction vessel.

反応温度は、熱分解反応が進行し、金属ナノ微粒子が生成する温度であればよく、例えば50℃以上、好ましくは100℃以上、より好ましくは120℃以上が挙げられる。この範囲であれば、金属ナノ微粒子が効率よく生成する。また、反応温度は、250℃以下であればよく、240℃以下が好ましく、200℃以下がより好ましい。この範囲であれば、保護層構成成分の揮発が抑えられて、金属ナノ微粒子表面に効率よく保護層を形成できる。
反応温度としては、50〜250℃、100〜250℃、120〜250℃、50〜240℃、100〜240℃、120〜240℃、50〜200℃、100〜200℃、120〜200℃等が挙げられる。
上記温度は、加熱反応開始時の反応液の温度である。
また、反応時間は、所望する平均粒子径の大きさや、それに応じた組成物の組成に合せて、適宜選択すればよい。反応時間としては、例えば1分間〜100時間、好ましくは1分間〜10時間が挙げられる。
The reaction temperature may be a temperature at which the thermal decomposition reaction proceeds and metal nanoparticles are generated. Examples thereof include 50 ° C. or higher, preferably 100 ° C. or higher, and more preferably 120 ° C. or higher. If it is this range, a metal nanoparticle will produce | generate efficiently. Moreover, the reaction temperature should just be 250 degrees C or less, 240 degrees C or less is preferable and 200 degrees C or less is more preferable. If it is this range, volatilization of a protective layer structural component will be suppressed and a protective layer can be efficiently formed in the metal nanoparticle surface.
As reaction temperature, 50-250 degreeC, 100-250 degreeC, 120-250 degreeC, 50-240 degreeC, 100-240 degreeC, 120-240 degreeC, 50-200 degreeC, 100-200 degreeC, 120-200 degreeC etc. Is mentioned.
The said temperature is the temperature of the reaction liquid at the time of a heating reaction start.
Further, the reaction time may be appropriately selected according to the desired average particle size and the composition of the composition corresponding thereto. Examples of the reaction time include 1 minute to 100 hours, preferably 1 minute to 10 hours.

精製工程
熱分解反応により生成した金属ナノ微粒子は、未反応原料を含む混合物として得られるため、金属ナノ微粒子を精製することが好ましい。
精製方法としては、固液分離方法、金属ナノ微粒子と有機溶媒等の未反応原料との比重差を利用した沈殿方法等が挙げられる。固液分離方法としては、フィルター濾過、遠心分離、サイクロン式、又はデカンタ等の方法が挙げられる。精製時の取り扱いを容易にするために、アセトン、メタノール等の低沸点溶媒で金属ナノ微粒子を含有する混合物を希釈して、その粘度を調整してもよい。
Since the metal nanoparticle produced | generated by the refinement | purification process pyrolysis reaction is obtained as a mixture containing an unreacted raw material, it is preferable to refine | purify a metal nanoparticle.
Examples of the purification method include a solid-liquid separation method and a precipitation method using a difference in specific gravity between the metal nanoparticle and an unreacted raw material such as an organic solvent. Examples of the solid-liquid separation method include filter filtration, centrifugal separation, cyclone type, and decanter methods. In order to facilitate handling during purification, the viscosity of the mixture may be adjusted by diluting a mixture containing metal nanoparticles with a low-boiling solvent such as acetone or methanol.

金属ナノ微粒子の粒径
金属ナノ微粒子製造用組成物の組成や反応条件を調整することにより、得られる金属ナノ微粒子の平均粒子径を調整できる。上記説明した組成物を用い、上記説明した反応を行うことにより、平均粒子径が10〜200nm、特に10〜150nm、特に10〜100nm、特に10〜50nmの金属ナノ微粒子が得られる。
本発明において、平均粒子径は、走査型電子顕微鏡で観察される画像中の20個の微粒子の長辺の長さの平均値である。
By adjusting the composition and reaction conditions the particle size metal nanoparticles composition for the preparation of metal nanoparticles, it is possible to adjust the average particle size of the resulting metal nanoparticles. By performing the above-described reaction using the above-described composition, metal nanoparticles having an average particle diameter of 10 to 200 nm, particularly 10 to 150 nm, particularly 10 to 100 nm, and particularly 10 to 50 nm are obtained.
In the present invention, the average particle diameter is an average value of the lengths of the long sides of 20 fine particles in an image observed with a scanning electron microscope.

(3)導電性インク又はペースト
本発明の導電性インク又はペーストは、上記説明した本発明の製造方法により得られる金属ナノ微粒子と、極性有機溶媒を含む有機溶媒とを含む。有機溶媒は、極性有機溶媒の他に、非極性又は疎水性溶媒を含むことができる。
(3) Conductive ink or paste The conductive ink or paste of the present invention contains metal nanoparticles obtained by the production method of the present invention described above and an organic solvent containing a polar organic solvent. Organic solvents can include non-polar or hydrophobic solvents in addition to polar organic solvents.

極性有機溶媒としては、アセトン、アセチルアセトン、メチルエチルケトン等のケトン類;ジエチルエーテル、ジプロピルエーテル、ジブチルエーテル、テトラヒドロフラン、1,4−ジオキサン等のエーテル類;1,2−プロパンジオール、1,2−ブタンジオール、1,3−ブタンジオール、1,4−ブタンジオール、2,3−ブタンジオール、1,2−ヘキサンジオール、1,6−ヘキサンジオール、1,2−ペンタンジオール、1,5−ペンタンジオール、2−メチル−2,4−ペンタンジオール、3−メチル−1,5−ペンタンジオール、1,2−オクタンジオール、1,8−オクタンジオール、2−エチル−1,3−ヘキサンジオール等のジオール類;グリセロール;炭素数1〜5の直鎖又は分岐鎖のアルコール、シクロヘキサノール、3−メトキシ−3−メチル−1−ブタノール、3−メトキシ−1−ブタノール等のアルコール類;酢酸エチル、酢酸ブチル、酪酸エチル、蟻酸エチル等の脂肪酸エステル類;ポリエチレングリコール、トリエチレングリコールモノメチルエーテル、テトラエチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、ジエチレングリコールモノエチルエーテル、ジエチレングリコールジメチルエーテル、トリエチレングリコールジメチルエーテル、テトラエチレングリコールジメチルエーテル、3-メトキシブチルアセテート、エチレングリコールモノブチルエーテル、エチレングリコールモノブチルエーテルアセテート、エチレングリコールモノヘキシルエーテル、エチレングリコールモノオクチルエーテル、エチレングリコールモノ−2−エチルヘキシルエーテル、エチレングリコールモノベンジルエーテル、ジエチレングリコールモノメチルエーテル、ジエチレングリコールモノメチルエーテルアセテート、ジエチレングリコールモノエチルエーテル、ジエチレングリコールモノエチルエーテルアセテート、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテルアセテート、ポリプロピレングリコール、プロピレングリコールモノプロピルエーテル、プロピレングリコールモノブチルエーテル、ジプロピレングリコールモノメチルエーテル、ジプロピレングリコールモノエチルエーテル、ジプロピレングリコールモノプロピルエーテル、ジプロピレングリコールモノブチルエーテル、トリプロピレングリコールモノメチルエーテル、トリプロピレングリコールモノエチルエーテル、トリプロピレングリコールモノプロピルエーテル、トリプロピレングリコールモノブチルエーテル等のグリコール又はグリコールエーテル類;N,N−ジメチルホルムアミド;ジメチルスルホキシド;テルピネオール等のテルペン類;アセトニトリル;γ-ブチロラクトン;2-ピロリドン;N-メチルピロリドン;N-(2-アミノエチル)ピペラジン等が挙げられる。
中でも、炭素数3〜5の直鎖又は分岐鎖のアルコール、3-メトキシ-3-メチル-1-ブタノール、3-メトキシ-1-ブタノール、ジエチレングリコールモノブチルエーテル、ジエチレングリコールモノブチルエーテルアセテート、テルピネオールが好ましい。
Examples of polar organic solvents include ketones such as acetone, acetylacetone, and methyl ethyl ketone; ethers such as diethyl ether, dipropyl ether, dibutyl ether, tetrahydrofuran, and 1,4-dioxane; 1,2-propanediol, 1,2-butane Diol, 1,3-butanediol, 1,4-butanediol, 2,3-butanediol, 1,2-hexanediol, 1,6-hexanediol, 1,2-pentanediol, 1,5-pentanediol Diols such as 2-methyl-2,4-pentanediol, 3-methyl-1,5-pentanediol, 1,2-octanediol, 1,8-octanediol, 2-ethyl-1,3-hexanediol Glycerol; C1-C5 linear or branched alcohol, cyclohexa Alcohol, alcohols such as 3-methoxy-3-methyl-1-butanol and 3-methoxy-1-butanol; fatty acid esters such as ethyl acetate, butyl acetate, ethyl butyrate and ethyl formate; polyethylene glycol, triethylene glycol Monomethyl ether, tetraethylene glycol monomethyl ether, ethylene glycol monoethyl ether, diethylene glycol monoethyl ether, diethylene glycol dimethyl ether, triethylene glycol dimethyl ether, tetraethylene glycol dimethyl ether, 3-methoxybutyl acetate, ethylene glycol monobutyl ether, ethylene glycol monobutyl ether acetate, Ethylene glycol monohexyl ether, ethylene glycol monooctyl ether, Tylene glycol mono-2-ethylhexyl ether, ethylene glycol monobenzyl ether, diethylene glycol monomethyl ether, diethylene glycol monomethyl ether acetate, diethylene glycol monoethyl ether, diethylene glycol monoethyl ether acetate, diethylene glycol monobutyl ether, diethylene glycol monobutyl ether acetate, polypropylene glycol, propylene glycol mono Propyl ether, Propylene glycol monobutyl ether, Dipropylene glycol monomethyl ether, Dipropylene glycol monoethyl ether, Dipropylene glycol monopropyl ether, Dipropylene glycol monobutyl ether, Tripropylene glycol Glycol or glycol ethers such as methyl ether, tripropylene glycol monoethyl ether, tripropylene glycol monopropyl ether, tripropylene glycol monobutyl ether; N, N-dimethylformamide; dimethyl sulfoxide; terpenes such as terpineol; acetonitrile; Butyrolactone; 2-pyrrolidone; N-methylpyrrolidone; N- (2-aminoethyl) piperazine and the like.
Of these, linear or branched alcohols having 3 to 5 carbon atoms, 3-methoxy-3-methyl-1-butanol, 3-methoxy-1-butanol, diethylene glycol monobutyl ether, diethylene glycol monobutyl ether acetate, and terpineol are preferable.

非極性溶媒としては、ヘキサン、ヘプタン、オクタン、ノナン、デカン、2−エチルヘキサン、シクロヘキサン等の直鎖、分枝、又は環状の飽和炭化水素;炭素数6以上の直鎖又は分岐鎖のアルコール等のアルコール類;ベンゼン、トルエン、ベンゾニトリル等の芳香族化合物;ジクロロメタン、クロロホルム、ジクロロエタン等のハロゲン化炭化水素類;メチル−n−アミルケトン;メチルエチルケトンオキシム;トリアセチン等が挙げられる。
中でも、飽和炭化水素及び炭素数6以上の直鎖又は分岐鎖のアルコール類が好ましく、ヘキサン、オクタン、デカン、オクタノール、デカノール、ドデカノールがより好ましい。
溶媒は、1種を単独で、又は2種以上を混合して使用できる。
Examples of nonpolar solvents include linear, branched, or cyclic saturated hydrocarbons such as hexane, heptane, octane, nonane, decane, 2-ethylhexane, and cyclohexane; linear or branched alcohols having 6 or more carbon atoms, and the like. Alcohols such as benzene, toluene and benzonitrile; halogenated hydrocarbons such as dichloromethane, chloroform and dichloroethane; methyl-n-amyl ketone; methyl ethyl ketone oxime; and triacetin.
Of these, saturated hydrocarbons and linear or branched alcohols having 6 or more carbon atoms are preferable, and hexane, octane, decane, octanol, decanol, and dodecanol are more preferable.
A solvent can be used individually by 1 type or in mixture of 2 or more types.

極性溶媒と非極性溶媒との双方を含む場合、極性溶媒の比率は、溶媒の全量に対して、5容量%以上が好ましく、10容量%以上がより好ましく、15容量%以上がさらにより好ましい。また、60容量%以下とすることができ、55容量%以下とすることもでき、50容量%以下とすることもできる。
溶媒は極性溶媒からなるものとすることもできる。
本発明の導電性インク又はペーストは、このように極性溶媒を多く含む場合にも、金属ナノ微粒子の分散性が良い。
When both the polar solvent and the nonpolar solvent are included, the ratio of the polar solvent is preferably 5% by volume or more, more preferably 10% by volume or more, and even more preferably 15% by volume or more based on the total amount of the solvent. Moreover, it can be 60 volume% or less, can also be 55 volume% or less, and can also be 50 volume% or less.
The solvent can also consist of a polar solvent.
Even when the conductive ink or paste of the present invention contains a large amount of polar solvent, the dispersibility of the metal nanoparticles is good.

本発明の導電性インク又はペーストは、導電性インク又はペーストに通常含まれる、熱又は光硬化性樹脂、硬化剤、レベリング剤、増粘剤、沈殿防止剤、密着性向上のためのカップリング剤、消泡剤、充填剤、pH調整剤、被膜形成助剤、撥水剤等の1種又は2種以上を含むことができる。   The conductive ink or paste of the present invention includes a heat or photocurable resin, a curing agent, a leveling agent, a thickening agent, a suspending agent, and a coupling agent for improving adhesion, which are usually included in the conductive ink or paste. 1 type, or 2 or more types, such as an antifoamer, a filler, a pH adjuster, a film formation adjuvant, and a water repellent.

(4)回路・電極
上記説明した本発明の導電性インク又はペーストを用いて、回路ないしは配線又は電極を形成するに当たっては、基板上に、インクジェット印刷法、スクリーン印刷法、凸版反転印刷法、グラビアオフセット印刷法、オフセット印刷法、スピンコート法、スプレーコート法、バーコート法、ダイコート法、スリットコート法、ロールコート法、ディップコート法等の方法で、回路又は電極となるパターンを印刷すればよい。
次いで、例えば50℃以上、好ましくは80℃以上、より好ましくは100℃以上、また、例えば200℃以下、好ましくは150℃以下、より好ましくは120℃以下の温度で焼成することにより、回路又は電極が形成される。焼成は、オーブン、熱風式乾燥炉、赤外線乾燥炉、レーザー照射、フラッシュランプ照射、マイクロウェーブ等を用いて行える。
(4) Circuit / electrode In forming a circuit or wiring or electrode using the above-described conductive ink or paste of the present invention, an ink jet printing method, a screen printing method, a letterpress reverse printing method, a gravure are formed on a substrate. A pattern to be a circuit or an electrode may be printed by a method such as an offset printing method, an offset printing method, a spin coating method, a spray coating method, a bar coating method, a die coating method, a slit coating method, a roll coating method, or a dip coating method. .
Next, for example, by firing at a temperature of 50 ° C. or higher, preferably 80 ° C. or higher, more preferably 100 ° C. or higher, for example 200 ° C. or lower, preferably 150 ° C. or lower, more preferably 120 ° C. or lower, a circuit or electrode Is formed. Firing can be performed using an oven, a hot air drying furnace, an infrared drying furnace, laser irradiation, flash lamp irradiation, microwaves, or the like.

以下に実施例を挙げて、本発明をより詳細に説明する。但し、本発明はこれらに限定されない。   Hereinafter, the present invention will be described in more detail with reference to examples. However, the present invention is not limited to these.

(1)材料
実施例及び比較例の金属ナノ微粒子製造用組成物を構成する各成分を以下に示す。
(1) Each component which comprises the composition for metal nanoparticle manufacture of a material Example and a comparative example is shown below.

金属塩(A)
a1:シュウ酸銀((COOAg)
なお、シュウ酸銀は特許文献1(特許第5574761号公報)に記載の方法で合成した。
a2:硝酸銀(和光純薬工業株式会社製)
Metal salt (A)
a1: Silver oxalate ((COOAg) 2 )
Silver oxalate was synthesized by the method described in Patent Document 1 (Japanese Patent No. 5574761).
a2: Silver nitrate (Wako Pure Chemical Industries, Ltd.)

アミン化合物(B)
b1:n−オクチルアミン(和光純薬工業株式会社製)
b2:3−メトキシプロピルアミン(和光純薬工業株式会社製)
b3:N,N−ジメチル−1,3−プロパンジアミン(和光純薬工業株式会社製)
b4:オレイルアミン(東京化成工業株式会社製)
Amine compound (B)
b1: n-octylamine (manufactured by Wako Pure Chemical Industries, Ltd.)
b2: 3-methoxypropylamine (manufactured by Wako Pure Chemical Industries, Ltd.)
b3: N, N-dimethyl-1,3-propanediamine (manufactured by Wako Pure Chemical Industries, Ltd.)
b4: Oleylamine (manufactured by Tokyo Chemical Industry Co., Ltd.)

ヒドロキシ脂肪酸(C)、脂肪酸
c1:リシノール酸(東京化成工業株式会社製)
c2:12−ヒドロキシステアリン酸(東京化成工業株式会社製)
c3:オレイン酸(和光純薬工業株式会社製)
Hydroxy fatty acid (C), fatty acid c1: ricinoleic acid (manufactured by Tokyo Chemical Industry Co., Ltd.)
c2: 12-hydroxystearic acid (manufactured by Tokyo Chemical Industry Co., Ltd.)
c3: Oleic acid (Wako Pure Chemical Industries, Ltd.)

有機溶媒(S)
s1:2−(2−エチルヘキシルオキシ)エタノール(和光純薬工業株式会社製)
s2:2−オクタノール(和光純薬工業株式会社製)
Organic solvent (S)
s1: 2- (2-ethylhexyloxy) ethanol (Wako Pure Chemical Industries, Ltd.)
s2: 2-octanol (Wako Pure Chemical Industries, Ltd.)

以上の成分を用いて、後掲の表1、表2に示す組成の各組成物を調製した。アミン化合物(B)は、複数のアミン化合物を予め混合してから他成分と混合した。   Using the components described above, compositions having the compositions shown in Tables 1 and 2 below were prepared. The amine compound (B) was mixed with other components after previously mixing a plurality of amine compounds.

(2)金属ナノ微粒子製造用組成物を用いた金属ナノ微粒子の製造
(実施例1〜7、比較例1〜3)
磁気撹拌子を入れた50mLガラス製遠沈管に、アミン化合物(B)の混合物、ヒドロキシ脂肪酸(C)、及び有機溶媒(S)を、表1に示す量投入し、1分間程度攪拌したのち、シュウ酸金属塩(a1)を表1に示す量投入し、約10分間攪拌することで、金属ナノ微粒子製造用組成物を調製した。その後、アルミブロックを備えたホットスターラー(小池精密機器製作所製HHE-19G-U)上に、これらのガラス製遠沈管を立てて設置し、130℃で加熱を開始した。加熱開始から約10分後に反応が開始し、その後10分程度で反応が終了した。放冷後、磁気撹拌子を取り出し、各組成物にメタノール15gを添加してボルテックスミキサーで攪拌した後、遠心分離機(日立工機製CF7D2)にて3000rpm(約1600×G)で1分間の遠沈操作を実施し、遠沈管を傾けることにより上澄みを除去した。メタノール15gの添加、撹拌、遠心分離、及び上澄み除去の工程を2回繰り返し、製造された各金属ナノ微粒子を回収した。このようにして、実施例1〜7の金属ナノ粒子を得た。
また、表2に示す組成物を用いた以外は、上記と同様にして、比較例1〜3の金属ナノ微粒子を作成した。
(2) Production of metal nanoparticles using the composition for producing metal nanoparticles
(Examples 1-7, Comparative Examples 1-3)
In a 50 mL glass centrifuge tube containing a magnetic stir bar, the mixture of amine compound (B), hydroxy fatty acid (C), and organic solvent (S) were added in the amounts shown in Table 1 and stirred for about 1 minute. An amount of metal oxalate (a1) shown in Table 1 was added and stirred for about 10 minutes to prepare a composition for producing metal nanoparticles. Thereafter, these glass centrifuge tubes were set up on a hot stirrer (HIKE-19G-U, manufactured by Koike Seimitsu Seisakusho) equipped with an aluminum block, and heating was started at 130 ° C. The reaction started about 10 minutes after the start of heating, and the reaction was completed after about 10 minutes. After standing to cool, the magnetic stir bar was taken out, 15 g of methanol was added to each composition, and the mixture was stirred with a vortex mixer, and then centrifuged at 3000 rpm (about 1600 × G) for 1 minute with a centrifuge (CF7D2 manufactured by Hitachi Koki). A sedimentation operation was performed, and the supernatant was removed by tilting the centrifuge tube. The steps of adding 15 g of methanol, stirring, centrifuging, and removing the supernatant were repeated twice to collect each produced metal nanoparticle. In this way, metal nanoparticles of Examples 1 to 7 were obtained.
Moreover, the metal nanoparticle of Comparative Examples 1-3 was created like the above except having used the composition shown in Table 2.

(比較例4)
硝酸銀(a2)を原料とし、特許5441550号公報に記載の方法により金属ナノ微粒子を作成した。具体的には、表2に示す組成になるように各成分を混合して、硝酸銀が完全に溶解した液を作成し、この液100mLを還流器を備える容器に移し、メカニカルスターラー(東京理化器械製Z−2200)で撹拌(300rpm)しながら昇温させた。昇温速度は、120℃までは1.0℃/minとし、120℃を超えて140℃までは0.5℃/minとした。その後、上記撹拌状態を維持しながら、140℃で1時間反応させた。反応は、容器の気相部に窒素ガスを5mL/minの流量で供給しながら行った。反応終了後、室温まで冷却し、反応後のスラリーを3日間静置した後、上澄み液をデカントにより除去した。その際、還元された銀が全スラリーに対して20質量%となるように上澄みの除去量を調整した。上澄み液除去後、スラリーにイソプロパノールを、銀とイソプロパノールとの比率が銀:イソプロパノール=1:30(モル比)となる量添加して混合し、銀粒子を300rpmで1時間攪拌洗浄した。その後、遠心分離により銀粒子を含む固形分を回収した。
(Comparative Example 4)
Metal nanoparticles were prepared using silver nitrate (a2) as a raw material by the method described in Japanese Patent No. 5441550. Specifically, each component was mixed so as to have the composition shown in Table 2 to prepare a solution in which silver nitrate was completely dissolved, and 100 mL of this solution was transferred to a container equipped with a refluxer, and a mechanical stirrer (Tokyo Rika Instruments Co., Ltd.). The temperature was raised while stirring (300 rpm) with Z-2200). The heating rate was 1.0 ° C./min up to 120 ° C., and 0.5 ° C./min up to 120 ° C. up to 140 ° C. Then, it was made to react at 140 degreeC for 1 hour, maintaining the said stirring state. The reaction was performed while supplying nitrogen gas to the gas phase part of the container at a flow rate of 5 mL / min. After completion of the reaction, the reaction mixture was cooled to room temperature, and the slurry after the reaction was allowed to stand for 3 days, and then the supernatant was removed by decantation. At that time, the removal amount of the supernatant was adjusted so that the reduced silver was 20% by mass with respect to the total slurry. After removing the supernatant, isopropanol was added to the slurry in an amount such that the ratio of silver to isopropanol was silver: isopropanol = 1: 30 (molar ratio), and the silver particles were stirred and washed at 300 rpm for 1 hour. Thereafter, the solid content including silver particles was recovered by centrifugation.

回収した固形分にリシノール酸とイソプロパノールの混合溶媒(リシノール酸:イソプロパノール=0.02:1(モル比))を加え、液温40℃に保って、40℃で5時間撹拌し、未反応原料を除去することにより、固形分から銀粒子を回収した。得られたスラリーを3000rpmで5分間の遠心分離により固液分離した。その後、前記固形成分に、固形成分:メタノールが1:30(モル比)となるようにメタノールを加えて、前記固形成分を300rpmで30分攪拌洗浄した。メタノールによるこの洗浄をもう一度行い、その後固液分離を行い、固形成分を回収することにより銀ナノ微粒子を抽出した。   A mixed solvent of ricinoleic acid and isopropanol (ricinoleic acid: isopropanol = 0.02: 1 (molar ratio)) is added to the recovered solid content, the liquid temperature is kept at 40 ° C., and the mixture is stirred at 40 ° C. for 5 hours. Then, silver particles were recovered from the solid content. The obtained slurry was subjected to solid-liquid separation by centrifugation at 3000 rpm for 5 minutes. Thereafter, methanol was added to the solid component so that the solid component: methanol ratio was 1:30 (molar ratio), and the solid component was stirred and washed at 300 rpm for 30 minutes. This washing with methanol was performed once again, followed by solid-liquid separation, and silver nanoparticles were extracted by collecting the solid components.

溶媒を除去して得られた各金属ナノ微粒子を、分散用の溶媒(2−プロパノール)に、金属ナノ微粒子の最終濃度が1重量%となるよう投入し、金属ナノ微粒子を分散させることで分散性評価用インクを得た。
また、各金属ナノ微粒子を、分散用の溶媒(2−プロパノール)に、金属ナノ微粒子の最終濃度が50重量%となるよう投入し、金属ナノ微粒子を分散させることで導電性評価用及びSEM観察による平均粒子径評価用のインクを得た。
また、実施例1、及び比較例4の金属ナノ微粒子は、1時間減圧乾燥してTg測定用サンプルを調整し、このサンプルをTg測定に供した。
Each metal nanoparticle obtained by removing the solvent is added to a dispersion solvent (2-propanol) so that the final concentration of the metal nanoparticle is 1% by weight and dispersed by dispersing the metal nanoparticle. An ink for property evaluation was obtained.
Further, each metal nanoparticle is introduced into a dispersion solvent (2-propanol) so that the final concentration of the metal nanoparticle is 50% by weight, and the metal nanoparticle is dispersed to conduct conductivity evaluation and SEM observation. Ink for average particle size evaluation was obtained.
Further, the metal nanoparticles of Example 1 and Comparative Example 4 were dried under reduced pressure for 1 hour to prepare a sample for Tg measurement, and this sample was subjected to Tg measurement.

各実施例で使用した組成物の組成を表1に、各比較例で使用した組成物の組成を表2に、それぞれ示す。   The composition of the composition used in each example is shown in Table 1, and the composition of the composition used in each comparative example is shown in Table 2.

(3)低温焼結性の評価
実施例1及び比較例4で得た銀粒子について、Tg(熱重量)を、セイコーインスツルメンツ製 EXSTAR6000 TG/DTA6300を用いて、大気下、10℃/分で昇温させて、70〜200℃での重量変化を測定することにより、Tg(熱重量)を測定した。結果を図1に示す。図1の縦軸は、70℃でのTgを100としたときの各温度でのTgの比率を示す。
比較例4の銀粒子は昇温してもTgがほとんど変化しなかったが、実施例1の銀粒子は登温に伴いTgが低下した。これは、銀粒子の保護層成分が銀粒子から脱離したことを示しており、このことから、本願発明の組成物を用いれば、低温焼結により回路などを形成できる金属ナノ微粒子が得られることが分かる。
(3) Evaluation of low-temperature sinterability For the silver particles obtained in Example 1 and Comparative Example 4, Tg (thermoweight) was increased at 10 ° C./min in the atmosphere using EXSTAR6000 TG / DTA6300 manufactured by Seiko Instruments Inc. Tg (thermogravimetric) was measured by heating and measuring the weight change at 70-200 ° C. The results are shown in FIG. The vertical axis in FIG. 1 indicates the ratio of Tg at each temperature when Tg at 70 ° C. is 100.
Although the Tg of the silver particles of Comparative Example 4 hardly changed even when the temperature was increased, the Tg of the silver particles of Example 1 decreased with increasing temperature. This indicates that the protective layer component of the silver particles has been detached from the silver particles. From this, metal nanoparticles capable of forming a circuit or the like by low-temperature sintering can be obtained by using the composition of the present invention. I understand that.

(4)金属ナノ微粒子の分散性の評価
各実施例及び比較例で得た銀粒子を最終濃度1重量%含む上記の評価用インクを用い、動的光散乱法(DLS:Dynamic Light Scattering)(スペクトリス社製ゼータサイザーナノS)により、調製5分後及び60分後のZ(平均値の比)を求めた。調製から測定までの間は各インクを静置した。実施例の結果を表3に、比較例の結果を表4にそれぞれ示す。
通常、分散状態にある粒子は、次第に元の成分系に戻ろうとし、その過程で次第に凝集する。即ち、分散性が悪いほど、凝集するスピードが速い。DLSでは、凝集状態にある粒子は1つの粒子としてカウントされる。従って、表中の「DLS結果」のT1/T0が大きいことは、凝集状態の粗大な粒子が増えたことを示し、分散性が悪いことを意味する。
(4) Evaluation of Dispersibility of Metal Nanoparticles Using the above-mentioned ink for evaluation containing the silver particles obtained in each Example and Comparative Example at a final concentration of 1% by weight, a dynamic light scattering method (DLS: Dynamic Light Scattering) Z (average ratio) after 5 minutes and after 60 minutes of preparation was determined by Spectris Zeta Sizer Nano S). Each ink was allowed to stand between preparation and measurement. Table 3 shows the results of the examples and Table 4 shows the results of the comparative examples.
Usually, particles in a dispersed state gradually return to the original component system and gradually aggregate in the process. That is, the lower the dispersibility, the faster the aggregation speed. In DLS, particles in an aggregated state are counted as one particle. Therefore, a large T1 / T0 of the “DLS result” in the table indicates that the number of coarse particles in the aggregated state has increased, which means that the dispersibility is poor.

(5)導電性の評価
各実施例及び比較例で得た銀粒子を最終濃度50重量%含む上記の評価用インクをPETフィルム(東レ製ルミラーU483)上に滴下し、スピンコーター(アクテス社製ASC-4000、1500rpm)を用いて約200nmの厚さの金属薄膜を作製した。この金属薄膜をスピンコート後速やかに100℃で1時間熱処理し、熱処理金属薄膜の抵抗値を、四探針型導電率計(三菱化学アナリテック製ロレスターAX)を用いて測定した。実施例の結果を表3に、比較例の結果を表4にそれぞれ示す。
(5) Evaluation of conductivity The above-mentioned ink for evaluation containing 50% by weight of the silver particles obtained in each Example and Comparative Example was dropped on a PET film (Toray Lumirror U483), and a spin coater (manufactured by Actes) ASC-4000, 1500 rpm) was used to produce a metal thin film having a thickness of about 200 nm. This metal thin film was heat-treated immediately at 100 ° C. for 1 hour after spin coating, and the resistance value of the heat-treated metal thin film was measured using a four-probe conductivity meter (Lorestar AX manufactured by Mitsubishi Chemical Analytech). Table 3 shows the results of the examples and Table 4 shows the results of the comparative examples.

(6)平均粒子径の測定
(5)で作製したスピンコート後熱処理を施さない金属薄膜を走査型電子顕微鏡(日立ハイテク製S-4500)で観察し、表面の粒子形状を観察することにより画像の粒子の長辺を計測して粒子径とした。さらに、20個の粒子の粒子径の平均値を平均粒子径とした。実施例の結果を表3に、比較例の結果を表4にそれぞれ示す。
(6) Measurement of average particle diameter The metal thin film not subjected to the post-spin coating heat treatment prepared in (5) was observed with a scanning electron microscope (S-4500, manufactured by Hitachi High-Tech), and the surface particle shape was observed to obtain an image. The long side of each particle was measured to obtain the particle diameter. Furthermore, the average value of the particle diameters of 20 particles was defined as the average particle diameter. Table 3 shows the results of the examples and Table 4 shows the results of the comparative examples.

実施例1及び2では、ヒドロキシ脂肪酸としてリシノール酸を用いた。実施例2では、実施例1と比較して保護層全体に占める割合を多くした。また、アミン化合物として、n−オクチルアミン及びN,N−ジメチル−1,3−プロパンジアミンを用いた。
DLSによる分散液調製5分後及び60分後の測定値の比による分散性評価は、実施例1がT1/T0=1.01と、ほぼ変化が無く、実施例2がT1/T0=0.93と、時間が経つにつれ逆に凝集構造が崩れ、分散性が向上するという結果が得られた。実施例1、2共に、実用的に十分な導電性が得られた。
In Examples 1 and 2, ricinoleic acid was used as the hydroxy fatty acid. In Example 2, compared with Example 1, the ratio which occupies for the whole protective layer was increased. Moreover, n-octylamine and N, N-dimethyl-1,3-propanediamine were used as amine compounds.
The dispersibility evaluation based on the ratio of the measured values after 5 minutes and 60 minutes after preparation of the dispersion by DLS was almost the same as T1 / T0 = 1.01 in Example 1, and T1 / T0 = 0 in Example 2. .93, the agglomeration structure collapsed over time, and the dispersibility was improved. In both Examples 1 and 2, practically sufficient conductivity was obtained.

実施例3、4、及び5では、アミン化合物として、実施例1で用いたN,N−ジメチル−1,3−プロパンジアミンを使用せず、3−メトキシプロピルアミンを使用した。その結果、分散性、導電性ともに実施例1、2と同様の傾向が見られた。   In Examples 3, 4, and 5, N, N-dimethyl-1,3-propanediamine used in Example 1 was not used as the amine compound, and 3-methoxypropylamine was used. As a result, the same tendency as in Examples 1 and 2 was observed in both dispersibility and conductivity.

実施例6及び7では、ヒドロキシ脂肪酸としてリシノール酸の代わりに12−ヒドロキシステアリン酸を用いた。その結果、分散性、導電性ともに、リシノール酸を用いた実施例1〜5と同様の結果が得られた。   In Examples 6 and 7, 12-hydroxystearic acid was used in place of ricinoleic acid as the hydroxy fatty acid. As a result, the same results as in Examples 1 to 5 using ricinoleic acid were obtained for both dispersibility and conductivity.

比較例1では、金属塩としてシュウ酸銀を用いたが、脂肪酸として水酸基を有しない脂肪酸であるオレイン酸を用いた。その結果、導電性は実施例1及び2と同等程度であったが、DLSによる分散性評価の結果は、60分後にはT1/T0が3.19となり、実施例1、2と比べて顕著に凝集が進行していた。なお、約10時間静置後には完全に銀粒子が沈降し分散液は透明になった。   In Comparative Example 1, silver oxalate was used as the metal salt, but oleic acid, which is a fatty acid having no hydroxyl group, was used as the fatty acid. As a result, the conductivity was almost the same as in Examples 1 and 2, but the result of the dispersibility evaluation by DLS showed that T1 / T0 was 3.19 after 60 minutes, which is remarkable compared to Examples 1 and 2. Aggregation had progressed. In addition, after leaving still for about 10 hours, silver particles completely settled and the dispersion became transparent.

比較例2では、金属塩としてシュウ酸銀を用いたが、脂肪酸として水酸基を有しない脂肪酸であるオレイン酸を用いた。その結果、実施例3、4、5と比較して導電性は同等程度であったが、DLSによる分散性評価の結果は、60分後にはT1/T0が1.48となり、実施例3、4、5と比べて顕著に凝集が進行していた。なお、約10時間静置後には完全に銀粒子が沈降し分散液は透明になった。   In Comparative Example 2, silver oxalate was used as the metal salt, but oleic acid, which is a fatty acid having no hydroxyl group, was used as the fatty acid. As a result, the conductivity was comparable to that of Examples 3, 4, and 5. However, as a result of the dispersibility evaluation by DLS, T1 / T0 became 1.48 after 60 minutes. Aggregation proceeded significantly compared to 4,5. In addition, after leaving still for about 10 hours, silver particles completely settled and the dispersion became transparent.

比較例3では、金属塩としてシュウ酸銀を用いたが、ヒドロキシ脂肪酸も脂肪酸も用いずに金属ナノ微粒子を作製した。その結果、導電性は実施例と比較して良好であったが、DLSによる分散性評価の結果は、60分後にはT1/T0が5.64となり、最も分散安定性が悪かった。このサンプルは3時間後には完全に沈降し分散液は透明になった。   In Comparative Example 3, silver oxalate was used as the metal salt, but metal nanoparticles were prepared without using hydroxy fatty acid or fatty acid. As a result, the electroconductivity was good as compared with the Examples, but the result of the dispersibility evaluation by DLS was that T1 / T0 was 5.64 after 60 minutes, and the dispersion stability was the worst. This sample was completely settled after 3 hours and the dispersion became transparent.

上記結果より、極性溶媒中での金属粒子の分散性は、金属ナノ微粒子の保護層中にヒドロキシ脂肪酸を含有させることで顕著に向上することが分かる。   From the above results, it can be seen that the dispersibility of the metal particles in the polar solvent is remarkably improved by including a hydroxy fatty acid in the protective layer of the metal nanoparticles.

比較例4では、金属塩としてシュウ酸銀以外のものを用いた。即ち、比較例4では硝酸銀を用いて、金属ナノ微粒子を作製した。その結果、いずれの金属ナノ微粒子も、DLSにおける分散性評価の結果は良好であったが、100℃、1時間の焼成によっては、十分な導電性が得られなかった。
この点に関して、図1に示すTg測定結果は、低温での重量変化、すなわち金属ナノ微粒子表面の保護層の低温焼結時の脱離性の差により、得られた銀粒子の導電性に差が出たことを示している。即ち、図1は、より低温で保護層が脱離する金属ナノ微粒子では、マイルドな焼成条件で金属ナノ微粒子同士の焼結が進行し、高い導電性が得られることを意味している。
In Comparative Example 4, a metal salt other than silver oxalate was used. That is, in Comparative Example 4, metal nanoparticles were prepared using silver nitrate. As a result, all the metal nanoparticles had good dispersibility evaluation results in DLS, but sufficient conductivity was not obtained by firing at 100 ° C. for 1 hour.
In this regard, the Tg measurement results shown in FIG. 1 are different in the conductivity of the obtained silver particles due to the change in weight at low temperature, that is, the difference in detachability during low-temperature sintering of the protective layer on the surface of the metal nanoparticles. Indicates that That is, FIG. 1 means that in the metal nanoparticle from which the protective layer is released at a lower temperature, the metal nanoparticle is sintered under mild firing conditions, and high conductivity is obtained.

本発明の金属ナノ微粒子製造用組成物を用いて製造される金属ナノ微粒子は、極性溶媒を多く含む導電性インク又はペースト中での分散性が良いため、広範囲の用途に使用できる。   The metal nanoparticles produced using the composition for producing metal nanoparticles of the present invention have good dispersibility in a conductive ink or paste containing a large amount of a polar solvent, and therefore can be used for a wide range of applications.

Claims (16)

(A)シュウ酸金属塩、(B)アミン化合物、及び(C)ヒドロキシ脂肪酸を含む金属ナノ微粒子製造用組成物。   A composition for producing metal nanoparticles comprising (A) a metal oxalate salt, (B) an amine compound, and (C) a hydroxy fatty acid. (C)ヒドロキシ脂肪酸が、リシノール酸、及び12−ヒドロキシステアリン酸からなる群より選ばれる少なくとも1種である請求項1に記載の組成物。   (C) The composition according to claim 1, wherein the hydroxy fatty acid is at least one selected from the group consisting of ricinoleic acid and 12-hydroxystearic acid. (A)シュウ酸金属塩が、シュウ酸銀である請求項1又は2に記載の組成物。   (A) The composition according to claim 1 or 2, wherein the metal oxalate salt is silver oxalate. (B)アミン化合物が、第1級アミンの1種以上、ジアミン化合物の1種以上、又は第1級アミンの1種以上とジアミン化合物の1種以上との組み合わせである請求項1〜3の何れかに記載の組成物。   (B) The amine compound is a combination of one or more primary amines, one or more diamine compounds, or a combination of one or more primary amines and one or more diamine compounds. The composition in any one. (C)ヒドロキシ脂肪酸の含有量が、(A)シュウ酸金属塩の1molに対して、0.001〜1molである請求項1〜4の何れかに記載の組成物。   (C) Content of hydroxy fatty acid is 0.001-1 mol with respect to 1 mol of (A) metal oxalate, The composition in any one of Claims 1-4. (A)シュウ酸金属塩の含有量が、組成物の全量に対して、20〜70重量%である請求項1〜5の何れかに記載の組成物。   (A) Content of metal oxalate salt is 20 to 70 weight% with respect to the whole quantity of a composition, The composition in any one of Claims 1-5. (B)アミン化合物の含有量が、(A)シュウ酸金属塩の1molに対して、0.4〜10molである請求項1〜5の何れかに記載の組成物。   (B) Content of an amine compound is 0.4-10 mol with respect to 1 mol of (A) metal oxalate, The composition in any one of Claims 1-5. 請求項1〜7の何れかに記載の組成物を加熱反応させる工程を含む、金属ナノ微粒子の製造方法。   The manufacturing method of a metal nanoparticle including the process of carrying out the heat reaction of the composition in any one of Claims 1-7. 加熱反応温度が50〜240℃である請求項8に記載の方法。   The method according to claim 8, wherein the heating reaction temperature is 50 to 240 ° C. 金属ナノ微粒子の平均粒子径が10〜200nmである請求項8又は9に記載の方法。   The method according to claim 8 or 9, wherein the metal nanoparticles have an average particle size of 10 to 200 nm. 請求項8〜10の何れかに記載の方法により得られる金属ナノ微粒子を含む導電性インク又はペースト。   The electroconductive ink or paste containing the metal nanoparticle obtained by the method in any one of Claims 8-10. 請求項1〜7の何れかに記載の組成物を加熱反応させて金属ナノ微粒子を得る工程と、この金属ナノ微粒子を極性有機溶媒を含む有機溶媒に分散させる工程とを含む、導電性インク又はペーストの製造方法。   A conductive ink comprising a step of heat-reacting the composition according to claim 1 to obtain metal nanoparticles, and a step of dispersing the metal nanoparticles in an organic solvent containing a polar organic solvent. Manufacturing method of paste. 請求項11に記載の導電性インク又はペーストを用いて形成された回路又は電極。   A circuit or electrode formed using the conductive ink or paste according to claim 11. 請求項1〜7の何れかに記載の組成物を加熱反応させて金属ナノ微粒子を得る工程と、この金属ナノ微粒子を極性有機溶媒を含む有機溶媒に分散させて導電性インク又はペーストを得る工程と、この導電性インク又はペーストを用いて基板上に回路又は電極を印刷する工程とを含む、回路又は電極の形成方法。   A step of heating the composition according to any one of claims 1 to 7 to obtain metal nanoparticles, and a step of dispersing the metal nanoparticles in an organic solvent containing a polar organic solvent to obtain a conductive ink or paste. And a step of printing a circuit or an electrode on a substrate using the conductive ink or paste. (A)シュウ酸金属塩、(B)アミン化合物、及び(C)ヒドロキシ脂肪酸を含む組成物の、金属ナノ微粒子の製造のための使用。   Use of a composition comprising (A) a metal oxalate salt, (B) an amine compound, and (C) a hydroxy fatty acid for the production of metal nanoparticles. (A)シュウ酸金属塩、(B)アミン化合物、及び(C)ヒドロキシ脂肪酸の、金属ナノ微粒子の製造のための組み合わせ使用。   Use of (A) metal oxalate, (B) amine compound, and (C) hydroxy fatty acid in combination for the production of metal nanoparticles.
JP2017525210A 2015-06-15 2016-06-13 Composition for producing metal nanoparticles Active JP6673352B2 (en)