JPS6344469A - Multilayer sheet for thermoforming packaging vessel - Google Patents
Multilayer sheet for thermoforming packaging vesselInfo
- Publication number
- JPS6344469A JPS6344469A JP15973087A JP15973087A JPS6344469A JP S6344469 A JPS6344469 A JP S6344469A JP 15973087 A JP15973087 A JP 15973087A JP 15973087 A JP15973087 A JP 15973087A JP S6344469 A JPS6344469 A JP S6344469A
- Authority
- JP
- Japan
- Prior art keywords
- layer
- container
- multilayer sheet
- multilayer
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。(57) [Abstract] This bulletin contains application data before electronic filing, so abstract data is not recorded.
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明はこれにより得られた包装容器の易開封性を可能
にする包装容器熱成形用多層シートに関するものである
。さらに詳しくいえば、本発明は、蓋材とのヒートシー
ル条件範囲が広く密封性に優れるとともに、開封が容易
で、開封力が安定している上に、開封後の剥離面の外観
が良好であり、しかもボイルやレトルト処理に優れる易
開封性包装容器の製造に好適に用いられる多層シートに
関するものである。DETAILED DESCRIPTION OF THE INVENTION [Industrial Field of Application] The present invention relates to a multilayer sheet for thermoforming packaging containers, which enables the resulting packaging containers to be easily opened. More specifically, the present invention has excellent sealing performance over a wide range of heat sealing conditions with the lid, is easy to open, has stable opening force, and has a good appearance on the peeled surface after opening. The present invention relates to a multilayer sheet suitable for manufacturing easy-to-open packaging containers that are excellent in boiling and retort processing.
従来、容器本体フランジ部に蓋材をヒートシールする容
器は食品の包装に多用されている。この場合、容器の密
封性を高めるためにヒートシール強度を高くすると、使
用時の開封性が悪くなり実用的でない、この問題の解決
のためにシール層の樹脂の組み合わせや樹脂のブレンド
の選定で対応することが試みられている。しかしながら
、この相反する要求を満足するものは得られていない。Conventionally, containers in which a lid material is heat-sealed to the flange of the container body have been frequently used for food packaging. In this case, increasing the heat-sealing strength to improve the sealability of the container would make it difficult to open the container during use, making it impractical.To solve this problem, the combination of resins and resin blends for the sealing layer should be selected. Attempts are being made to address this. However, nothing that satisfies these contradictory demands has yet to be obtained.
これはヒートシール強度が樹脂そのものによる以外に、
シール時の温度、圧力、時間などのシール条件や充填物
などの夾雑物による影響等によりシール性が大きく左右
されるからである。This is because the heat seal strength is not only due to the resin itself.
This is because sealing performance is greatly influenced by sealing conditions such as temperature, pressure, and time during sealing, and by the influence of impurities such as fillers.
他方、近時、食品のボイル、レトルト殺菌が行われるよ
うになり、より高い密封性、耐熱性が必要となり、これ
に対応した易開封性包装容器とこの容器の製造に適した
多層シートが待望されている。On the other hand, in recent years, boiling and retort sterilization of food products has become a necessity, and higher sealing performance and heat resistance are required.Easy-to-open packaging containers and multilayer sheets suitable for manufacturing such containers are long-awaited. has been done.
本発明は、成形して多層容器とし、蓋材とヒートシール
して包装容器とした場合に、包装容器を開封するにあた
り、開封が容易で、開封力が安定している上に、蓋材の
剥離面の外観が良好であり、しかもボイルやレトルト処
理に優れる耐熱性が良好な全く新しい開封方法により開
封を行う易開封性包装容器を製造するのに適する多層シ
ートの提供を目的とするものである。According to the present invention, when the packaging container is formed by molding into a multilayer container and heat-sealing it with a lid material, the packaging container is easy to open, the opening force is stable, and the lid material is The object of the present invention is to provide a multilayer sheet suitable for producing easy-to-open packaging containers that have a good appearance on the peeling surface, excellent heat resistance for boiling and retort processing, and can be opened using a completely new opening method. be.
すなわち、本発明の包装容器熱成形用用多層シートは、
多層容器に熱成形され、蓋材とヒートシールされて包装
容器となる多層シートであって、蓋材を多層容器から剥
離する際に、従来のように蓋材と容器を剥離して開封す
るのではな（、包装容器の開封が多層容器の層間剥離か
ら開始されるように構成されている剥離性表面層とこれ
に接する層とからなる包装容器熱成形用多層シートに関
する。That is, the multilayer sheet for thermoforming packaging containers of the present invention is
A multilayer sheet that is thermoformed into a multilayer container and heat-sealed with a lid material to become a packaging container. The present invention relates to a multilayer sheet for thermoforming packaging containers, which comprises a peelable surface layer and a layer in contact with the peelable surface layer, which is configured such that opening of the packaging container starts from delamination between the layers of the multilayer container.
以下、本発明を図面に基づいて詳細に説明する。Hereinafter, the present invention will be explained in detail based on the drawings.
第１図は本発明の易開封性包装容器用多層シートの断面
図であり、２は剥離性表面層、１はこれに接する層であ
る。FIG. 1 is a cross-sectional view of the multilayer sheet for easy-open packaging containers of the present invention, where 2 is a peelable surface layer and 1 is a layer in contact with this.
剥離性表面層は、蓋材とヒートシール可能な樹脂層であ
り、剥離性表面層には剥離強度が１．５ ｋｇ／ １５
ｔｍ （引張速度３００＋ｎ／ｍ ｉ ｎ）以下にな
るようにこれに接する樹脂層が一体多層化されている。The peelable surface layer is a resin layer that can be heat-sealed to the lid material, and the peelable surface layer has a peel strength of 1.5 kg/15
The resin layers in contact with this are integrally multilayered so that the tensile speed is less than tm (tensile speed 300+n/min).
剥離性表面層は多層シートがフランジ部を有する多層容
器に成形されたときに、フランジ部において蓋材と通常
、２．０ｋｇ／１５ｍ以上、好ましくは２．５ｋｇ／１
５ｍ以上の強度でヒートシール可能な材質からなってい
る。そして、この剥離性表面層とこれに接する層との剥
離強度は１゜５ｋｇ／１５鶴以下、好ましくは１．３ｋ
ｇ／１５ｍｍ以下で、蓋材と剥離性表面層の剥離強度よ
り小さくなっており、蓋材を容器から剥離する際には剥
離性表面層とこれに接する層の間で剥離するようになっ
ている。When the multilayer sheet is formed into a multilayer container having a flange, the releasable surface layer is usually 2.0 kg/15 m or more, preferably 2.5 kg/1, with the lid material at the flange.
It is made of a material that can be heat-sealed with a strength of over 5m. The peel strength between this releasable surface layer and the layer in contact with it is 1°5 kg/15 tsuru or less, preferably 1.3 k.
g/15 mm or less, which is lower than the peel strength between the lid material and the removable surface layer, and when the lid material is peeled off from the container, it will peel between the removable surface layer and the layer in contact with it. There is.
この剥離性表面層とこれに接する石は多層シートの最内
層（以下、多層容器となったときに容器の内側となる層
を内層とする）とこれに接する層とすることが好ましい
が、容器から蓋材を剥離する場合、多層シートで剥離を
おこなって開封する本発明の特徴を有する限り、容器最
内層の内側に必要に応じて、シール層などの他の層を最
内層に設けてもよい。This peelable surface layer and the stones in contact with it are preferably the innermost layer of the multilayer sheet (hereinafter, the layer that becomes the inside of the container when it becomes a multilayer container is referred to as the inner layer) and the layer in contact with this. When peeling off the lid material from the container, as long as the feature of the present invention is to perform peeling and opening using a multilayer sheet, other layers such as a sealing layer may be provided as necessary inside the innermost layer of the container. good.
多層シートを構成する剥離性表面層とこれに接する層の
材質としては、特に制限されず、ポリオレフィン系樹脂
、ポリスチレン系樹脂、ポリアミド系樹脂、ポリエステ
ル系樹脂、またはこれらの混合物、もしくはこれらとエ
ラストマーとの混合物などを組み合わせて用いることが
できる。さらに必要により、樹脂層中に種々の添加剤を
加えることもできる。ポリオ゛レフイン樹脂系樹脂層の
組み合わせからなる具体的な例としては、（イ）ポリプ
ロピレン系樹脂とポリエチレン系樹脂との混合樹脂層と
（ロ）高密度ポリエチレン樹脂層の組み合わせとするの
が好ましい。The materials of the releasable surface layer and the layer in contact with the multilayer sheet are not particularly limited, and may include polyolefin resins, polystyrene resins, polyamide resins, polyester resins, or mixtures thereof, or combinations of these and elastomers. A mixture of these can be used in combination. Furthermore, various additives can be added to the resin layer if necessary. A specific example of a combination of polyolefin resin layers is preferably a combination of (a) a mixed resin layer of polypropylene resin and polyethylene resin and (b) a high-density polyethylene resin layer.
この混合樹脂層に用いられるポリプロピレン系樹脂とし
ては、高結晶性のプロピレン単独重合体のほかに、エチ
レン、ブテン−１１ペンテン−１，３−メチルブテン−
１，４−メチルペンテン−１などのα−オレフィンとの
ランダム共重合体や、これらの混合物などが挙げられる
。なお、ランダム共重合体としては多段重合で得られる
ホモポリプロピレンとの混合物であってもよい。前記共
重合体においては、共重合モノマーの割合が１０モル％
以下のものが好ましい。また、これらのポリプロピレン
系樹脂は、メルトインデックスが０．１〜２０の範囲に
あるものが好適である。In addition to highly crystalline propylene homopolymer, the polypropylene resin used in this mixed resin layer includes ethylene, butene-11pentene-1,3-methylbutene-
Examples include random copolymers with α-olefins such as 1,4-methylpentene-1, and mixtures thereof. Note that the random copolymer may be a mixture with homopolypropylene obtained by multistage polymerization. In the copolymer, the proportion of copolymerized monomers is 10 mol%.
The following are preferred. Further, these polypropylene resins preferably have a melt index in the range of 0.1 to 20.
一方、該混合樹脂層に用いられるポリエチレン系樹脂と
しては、低密度（高圧法低密度ポリエチレン、直鎖状低
密度ポリエチレンなど）、中密度および高密度ポリエチ
レンのいずれも使用することができ、また、エチレン単
独重合体のほかに、プロピレンや、ブテン−１、ペンテ
ン−１，３−メチルブテン−１，４−メチルペンテン−
１などのα−オレフィンまたは酢酸ビニルとのランダム
またはブロック共重合体、あるいはこれらの混合物など
も使用することができる。前記共重合体においては、共
重合モノマーの割合は１０モル％以下のものが好ましい
、また、これらのポリエチレン系樹脂は、メルトインデ
ックスが０．０２〜５０の範囲にあり、かつ密度が０．
９００〜０．９７５ｇ／Ｊの範囲にあるものが好適であ
る。On the other hand, as the polyethylene resin used for the mixed resin layer, any of low density (high pressure low density polyethylene, linear low density polyethylene, etc.), medium density and high density polyethylene can be used, and In addition to ethylene homopolymer, propylene, butene-1, pentene-1,3-methylbutene-1,4-methylpentene-
Random or block copolymers with α-olefins such as 1 or vinyl acetate, or mixtures thereof can also be used. In the copolymer, the proportion of the copolymerized monomer is preferably 10 mol % or less, and these polyethylene resins have a melt index in the range of 0.02 to 50 and a density of 0.
Preferably, the amount is in the range of 900 to 0.975 g/J.
前記のポリプロピレン系樹脂とポリエチレン系樹脂との
割合は、好ましくは重量基準で５０：５０ないし９７：
３、さらに好ましくは６０ ： ４０ないし９５：５の
範囲で選ばれる。The ratio of the polypropylene resin to the polyethylene resin is preferably 50:50 to 97: by weight.
3, more preferably in the range of 60:40 to 95:5.
さらに、この樹脂混合物には、所望に応じ、その相溶性
を改善するために第３の樹脂成分を配合することができ
る。このような第３樹脂成分としては、例えば不飽和カ
ルボン酸またはその誘導体により変性された変性ポリオ
レフィン、エチレン−酢酸ビニル共重合体、エチレン−
アクリレート共重合体、エチレン−プロピレンゴム、エ
チレン−プロピレン−ジエン系ゴム、ポリブテン、ポリ
イソブチレン、ポリブタジェン系ゴム、ポリイソプレン
系ゴム、アタクチックポリ−４−メチルペンテン−１、
スチレン−ブタジェンゴム、アクリロニトリル−ブタジ
ェンゴム、イオン架橋オレフィン共重合体（アイオノマ
ー）などが挙げられ、これらはそれぞれ単独で用いても
よいし、２種以上組み合わせて用いてもよい。これらの
第３成分はポリプロピレン系樹脂１００重量部あたり、
３０重量部以下の量で用いることが好ましい。Furthermore, a third resin component can be added to this resin mixture, if desired, in order to improve its compatibility. Examples of such a third resin component include a modified polyolefin modified with an unsaturated carboxylic acid or a derivative thereof, an ethylene-vinyl acetate copolymer, and an ethylene-vinyl acetate copolymer.
Acrylate copolymer, ethylene-propylene rubber, ethylene-propylene-diene rubber, polybutene, polyisobutylene, polybutadiene rubber, polyisoprene rubber, atactic poly-4-methylpentene-1,
Examples include styrene-butadiene rubber, acrylonitrile-butadiene rubber, and ionically crosslinked olefin copolymers (ionomers), each of which may be used alone or in combination of two or more. These third components are per 100 parts by weight of polypropylene resin,
It is preferable to use it in an amount of 30 parts by weight or less.
本発明の多層シートのもう一つの層の高密度ポリエチレ
ン樹脂層に用いられる高密度ポリエチレン樹脂としては
、エチレン単独重合体のほかに、プロピレンや、ブテン
−１、ペンテン−１，３−メチルブテン−１，４−メチ
ルペンテン−１などのα−オレフィンとの共重合体など
が挙げられる。The high-density polyethylene resin used for the other high-density polyethylene resin layer of the multilayer sheet of the present invention includes, in addition to ethylene homopolymer, propylene, butene-1, pentene-1,3-methylbutene-1 , and copolymers with α-olefins such as 4-methylpentene-1.
この共重合体においては、共重合モノマーの割合は１０
モル％以下のものが好ましい、この高密度ポリエチレン
樹脂は、密度が０．９４０〜０．９７５ｇ／−の範囲に
あるものが好ましく、また、密度や分子量分布の異なる
ものの混合物であってもよい。In this copolymer, the proportion of copolymerized monomers is 10
This high-density polyethylene resin, which is preferably less than mol %, preferably has a density in the range of 0.940 to 0.975 g/-, and may be a mixture of resins having different densities and molecular weight distributions.
この（イ）（ロ）の樹脂層からなる多層シートはそのま
ま用いて容器本体を構成してもよいが、ガスバリヤ−性
の向上や、容器の変形を少なくする目的で、他の材料を
用いた三層以上の多層シートとして用いてもよい、他の
層としては、例えばエチレン−ビニルアルコール共重合
体、ポリ塩化ビニリデン、ナイロン、ポリエチレンテレ
フタレートなどの樹脂層やアルミ蒸着層などのガスバリ
ヤ−性に優れたものが挙げられる。また、無機充填剤１
０〜８０重量％を含有する樹脂層を設けたものであって
もよい。The multilayer sheet consisting of the resin layers in (a) and (b) may be used as is to construct the container body, but in order to improve the gas barrier properties and reduce the deformation of the container, other materials may be used. Other layers that may be used as a multilayer sheet of three or more layers include resin layers such as ethylene-vinyl alcohol copolymer, polyvinylidene chloride, nylon, and polyethylene terephthalate, and resin layers with excellent gas barrier properties such as aluminum vapor-deposited layers. There are many things that can be mentioned. In addition, inorganic filler 1
A resin layer containing 0 to 80% by weight may be provided.
該多層シートの作成方法としては、通常の共押出成形法
の他、ラミネート加工に慣用されている方法、例えばエ
キストルージョンラミネート、ホットメルトラミネート
、ドライラミネート、ウェットラミネートなどの方法を
用いることができる。As a method for producing the multilayer sheet, in addition to the usual coextrusion molding method, methods commonly used for lamination processing, such as extrusion lamination, hot melt lamination, dry lamination, and wet lamination, can be used.
該混合樹脂層、高密度ポリエチレン樹脂層の厚さは、通
常、１０〜１０００μｍ１好ましくは２０〜５００μｍ
の範囲にあることが好ましい。The thickness of the mixed resin layer and high density polyethylene resin layer is usually 10 to 1000 μm, preferably 20 to 500 μm.
It is preferable that it is in the range of .
多層シートの層構成は、蓋材のシーラント層樹脂により
適宜選定すればよいが、蓋材が例えばポリエチレン系シ
ーラント層の場合、高密度ポリエチレン層を多層シート
の最内層とすることが好ましい。The layer structure of the multilayer sheet may be appropriately selected depending on the sealant layer resin of the lid material, but when the lid material is, for example, a polyethylene sealant layer, it is preferable to make the high-density polyethylene layer the innermost layer of the multilayer sheet.
第２図は本発明の多層シートを用いて製造した易開封性
包装容器の一実施例の部分断面図である。FIG. 2 is a partial sectional view of an embodiment of an easy-to-open packaging container manufactured using the multilayer sheet of the present invention.
Ａは多層構造を有する多層容器本体で、２は多層容器本
体の最内層蘭１はこれに接する層である。A is a multilayer container main body having a multilayer structure, 2 is the innermost layer of the multilayer container main body, and 1 is a layer in contact with this.
この多層容器本体は、通常、共押出等により前記多層シ
ートを得て、これを真空成形、圧空成形などの熱成形し
て得られるものである。This multilayer container body is usually obtained by obtaining the multilayer sheet by coextrusion or the like, and then thermoforming this by vacuum forming, pressure forming, or the like.
Ｂは容器の蓋材で、多層容器本体の最内層２と易ヒート
シール性を有するシーラント層３と基材４を有するもの
である。５はヒートシール部で、容器本体と蓋材とは容
器本体開口フランジ部で環状に難剥離ヒートシールされ
ている。容器の形状は特に限定されるものではなく、通
常、円、四角などであり、この形状のフランジ部に沿っ
て環状にヒートシールされている。B is a lid material for a container, which has an innermost layer 2 of a multilayer container body, a sealant layer 3 having easy heat-sealability, and a base material 4. Reference numeral 5 denotes a heat-sealing portion, in which the container body and the lid material are heat-sealed in an annular shape at the opening flange portion of the container body so as to be difficult to peel off. The shape of the container is not particularly limited, and is usually circular, square, etc., and is heat-sealed in an annular shape along the flange portion of this shape.
蓋材Ｂは図では２層フィルムとなっているが、単層フィ
ルムであっても多層フィルムであってもいずれでもよく
、特に制限はない。２層フィルムを用いた場合について
説明すると、プラスチックの単層フィルム、多層フィル
ム、紙、アルミ箔、またはこれらの複合材料等からなる
基材４と、ポリエチレン、ポリプロピレン、エチレン−
α−オレフィン共重合体、エチレン−酢酸ビニル共重合
体等からなる容器本体の最内層２との易ヒートシール性
を有する樹脂からなるシーラント層３とからなっている
。Although the lid material B is a two-layer film in the figure, it may be a single-layer film or a multi-layer film, and is not particularly limited. To explain the case where a two-layer film is used, the base material 4 is made of a plastic single-layer film, multi-layer film, paper, aluminum foil, or a composite material thereof, and the base material 4 is made of a plastic single-layer film, multi-layer film, paper, aluminum foil, or a composite material of these materials, and
It consists of an innermost layer 2 of the container body made of an α-olefin copolymer, an ethylene-vinyl acetate copolymer, etc., and a sealant layer 3 made of a resin that is easily heat-sealable.
多層容器本体のフランジ部には環状ヒートシール部より
内側に環状の切り込み６が設けられている。切り込みは
通常、環状刃を有する押型などにより設けられ、蓋材を
剥がすときに剥離層を容易に切断できるものであればよ
く、その形状、深さは特に限定されない、剥離層の一部
だけ切り込まれていてもよい。また、環状の切り込みは
、全周にわたってつけてもよいし、一部は残しておいて
もよい。蓋材の一部を剥がさずについたまま残すような
場合には、そこの部分だけ切り込みを入れないようにす
る。An annular cut 6 is provided in the flange portion of the multilayer container body on the inner side of the annular heat seal portion. The incision is usually made by a pressing die with an annular blade, etc., and it is sufficient that the release layer can be easily cut when the lid material is peeled off.The shape and depth of the cut are not particularly limited. It may be included. Further, the annular cut may be made all around the circumference, or a portion may be left. If a part of the lid material is to be left on without being removed, do not make a cut in that part.
図に示した包装容器には、ヒートシール部の内側端と切
り込みとの間に間隔が設けられている。In the illustrated packaging container, there is a gap between the inner edge of the heat-sealed portion and the notch.
この間隔の長さｔは通常、０．５８〜Ｌｏｗ、好ましく
は１．５〜５ｆｌとする。この長さが０．５ ｗ未満だ
と容器内側からの剥離強度が外側からの剥離強度よりそ
れほど大きくならず、１０ｍを越えると実用的でなくな
る。The length t of this interval is usually 0.58 to Low, preferably 1.5 to 5 fl. If this length is less than 0.5 W, the peel strength from the inside of the container will not be much greater than the peel strength from the outside, and if it exceeds 10 m, it will not be practical.
蓋材の外縁を多層容器本体より外側にはみ出させたつま
み部７を設けておくと、蓋をあけて剥離する際につまみ
やすいので好ましい。It is preferable to provide a knob portion 7 in which the outer edge of the lid material protrudes outside the multilayer container body, since this makes it easier to grip when opening and peeling off the lid.
本発明の多層シートを用いて製造した容器に商品を封入
し、蓋材Ｂをヒートシールしたものを開封するときは以
下のような動作で簡単に開封することができる。When a product is sealed in a container manufactured using the multilayer sheet of the present invention and a lid material B is heat-sealed, the container can be easily opened by the following operation.
例えば、第２図において、つまみ部７を上方にもちあげ
る、すると多層容器本体Ａの最内層２とこれに接する層
１の間で剥離し、切り込み６のところまで最内層が剥離
する。以後引き続いて層１、層２間で剥離が進行し、蓋
材が剥がされる。従って、蓋材と多層容器本体が難剥離
ヒートシールされていても容易に開封できる。また、シ
ール面から剥離する従来法に比べて、シール端部の不完
全シールによるノツチ効果、シール条件の差、夾雑物の
影響などがな（、開封力の安定が図れる。特に蓋材をヒ
ートシールする場合に剥離性をまったく考慮する必要が
ない、したがって、高いヒートシール強度が得られるよ
うに蓋材の選択やシール条件を選定できるためシールが
容易となる。For example, in FIG. 2, when the grip portion 7 is lifted upward, the innermost layer 2 of the multilayer container main body A and the layer 1 in contact therewith are separated, and the innermost layer is separated up to the notch 6. Thereafter, peeling continues between layer 1 and layer 2, and the lid material is peeled off. Therefore, even if the lid material and the multilayer container body are heat-sealed to prevent peeling, the container can be easily opened. In addition, compared to the conventional method of peeling from the seal surface, there is no notch effect due to incomplete sealing at the seal end, differences in sealing conditions, and the influence of foreign substances (and the opening force can be stabilized. In particular, the lid material is heated When sealing, there is no need to consider releasability at all, and therefore, the lid material and sealing conditions can be selected so as to obtain high heat-sealing strength, making sealing easy.
また、第２図のように間隔ｔを設けると、内側からの剥
離強度が外側からの剥離強度と比べて大きくなり、ボイ
ル、レトルト処理に耐える耐熱性が良好な容器となる。Furthermore, when the interval t is provided as shown in FIG. 2, the peel strength from the inside becomes greater than the peel strength from the outside, resulting in a container with good heat resistance that can withstand boiling and retort processing.
この理由はさだかではないが、内側から剥離したときに
は、図のＸ点に応力が集中し、Ｙ点からの剥離強度はＹ
Ｚ面の剪断力となるために、内側からの剥離強度が大に
なったものと思われる。The reason for this is not trivial, but when peeling from the inside, stress is concentrated at point X in the figure, and the peel strength from point Y is Y.
It is thought that the peel strength from the inside was increased due to the shearing force on the Z plane.
次に実施例により本発明をさらに詳細に説明するが、本
発明はこれらの例によってなんら限定されるものではな
い。EXAMPLES Next, the present invention will be explained in more detail with reference to examples, but the present invention is not limited to these examples in any way.
実施例１
第３図に示したような層構成からなる多層シートを共押
出成形により得た（ａ層厚み２００μｍ、ｂ層厚み５０
／Ｊｍ）。Example 1 A multilayer sheet having the layer structure shown in FIG.
/Jm).
ａ：ポリプロピレン樹脂〔出光石油化学■ 出光ポリプ
ロ Ｅ−１００Ｇ、密度 ０．９１ｇ／Ｓ−１Ｍ１
Ｏ，６ｇ／１０分〕８０重量部と低密度ポリエチレン樹
脂〔東洋曹達工業■、ベトロセン１７２、密度０．９２
ｇ／ｃｄ、、Ｍ Ｉ Ｏ，３ｇ／ １０分１２０重量
部との混合物
ｂ＝高密度ポリエチレン〔出光石油化学側、出光ポリエ
チレン ４４０Ｍ、密度０．９５４ｇ／ａＪ、Ｍｌ
０．９ｇ／１０分〕
この多層シートを成形可能な温度に加熱して真空、圧空
成形法により第２図に示すようなフランジ付多層容器本
体Ａを成形した。a: Polypropylene resin [Idemitsu Petrochemical ■ Idemitsu Polypro E-100G, density 0.91g/S-1M1
O, 6 g/10 minutes] 80 parts by weight and low density polyethylene resin [Toyo Soda Kogyo ■, Vetrocene 172, density 0.92
g/cd,, M I O, 3 g/10 min. Mixture b with 120 parts by weight = high density polyethylene [Idemitsu Petrochemical side, Idemitsu polyethylene 440M, density 0.954 g/aJ, Ml
0.9 g/10 minutes] This multilayer sheet was heated to a moldable temperature and molded into a flanged multilayer container main body A as shown in FIG. 2 by vacuum and pressure forming.
この多層容器のフランジ部にｔが２鶴、４ ｍｍとなる
ようにして、深さ７０μｍの切り込み６を入れた。A notch 6 with a depth of 70 μm was made in the flange portion of this multilayer container so that t was 2 mm and 4 mm.
この多層容器に水を充填した後、蓋材フィルムＢＨｅ：
ｄ：ｃ （配向ナイロン（ＯＮＹ）：ポリ塩化ビニリデ
ン（ＰＶＤＣ）：直鎖状低密度ポリエチレン（ＬＬＤＰ
Ｅ）＝１５ ： ２０ ： ４０ （ｍμ））を直鎖状
低密度ポリエチレン面をシール層として、温度１７０℃
、圧力１．５ｋｇ／ａｊ、１．５秒の条件下でヒートシ
ールし、１２０℃で３０分間のレトルト処理を行ったが
、破袋はまったくみられなかった。なおこの容器の開封
力はレトルト前、約０．９ｋｇ／１５ｗｍ、レトルト後
約０．６ ｋｇ／ １５ ｕｓであった。また、この包
装容器は蓋材を剥離するとフランジシール部の外端より
容器層間で容易に剥離し、剥離面もきれいであった。After filling this multilayer container with water, the lidding film BHe:
d:c (Oriented nylon (ONY): Polyvinylidene chloride (PVDC): Linear low density polyethylene (LLDP)
E)=15:20:40 (mμ)) with the linear low density polyethylene surface as the sealing layer, at a temperature of 170°C.
The bag was heat-sealed at a pressure of 1.5 kg/aj for 1.5 seconds and retorted at 120° C. for 30 minutes, but no bag breakage was observed. The opening force of this container was approximately 0.9 kg/15 wm before retorting, and approximately 0.6 kg/15 us after retorting. Furthermore, when the lid material of this packaging container was peeled off, it was easily peeled off between the container layers from the outer end of the flange seal portion, and the peeled surface was clean.
本発明の多層シートを用いて製造した易開封性包装容器
は、シール強度が高く、密封性に優れ、開封が容易で、
開封力が安定している上に、剥離面の外観が良好であり
、しかも容器内側からの剥離強度が外側からの剥離強度
より大きく、耐熱性が良好で、ボイルやレトルト処理が
可能であるなど、優れた特徴を有しており、特にレトル
ト食品やボイル食品などの食品包装容器として好適に用
いられる。The easy-to-open packaging container manufactured using the multilayer sheet of the present invention has high sealing strength, excellent sealing performance, and is easy to open.
In addition to stable opening force, the peel surface has a good appearance, the peel strength from the inside of the container is greater than the peel strength from the outside, it has good heat resistance, and can be boiled or retorted. It has excellent characteristics and is particularly suitable for use as food packaging containers for retort foods, boiled foods, and the like.
第１図は本発明の多層シートの一実施例の部分断面図で
あり、１は剥離性表面層に接する層１．２は剥離性表面
層である。第２図は本発明の多層シートを用いて製造し
た包装容器の一実施例の部分断面図であり、図中符号Ａ
は多層容器本体、Ｂは蓋材、１は多層容器本体の最内層
に接する層、２は多層容器本体の最内層、３はシーラン
ト層、４は基材、５はヒートシール部、６は切り込み、
７はつまみ部であるFIG. 1 is a partial cross-sectional view of an embodiment of the multilayer sheet of the present invention, where 1 is a layer 1 in contact with a releasable surface layer, and 2 is a releasable surface layer. FIG. 2 is a partial sectional view of one embodiment of a packaging container manufactured using the multilayer sheet of the present invention, and the reference numeral A in the figure is
is the multilayer container main body, B is the lid material, 1 is the layer in contact with the innermost layer of the multilayer container main body, 2 is the innermost layer of the multilayer container main body, 3 is the sealant layer, 4 is the base material, 5 is the heat seal part, 6 is the notch ,
7 is the knob part
Claims (1)
包装容器となる多層シートであって、少なくとも剥離性
表面層とこれに接する層とからなり、包装容器の開封が
該２層の層間剥離から開始されるように、該２層の層間
剥離強度を１．５ｋｇ／１５ｍｍ以下として包装容器熱
成形用多層シート。1. A multilayer sheet that is thermoformed into a multilayer container and heat-sealed with a lid material to become a packaging container, which consists of at least a peelable surface layer and a layer in contact with this layer, and when the packaging container is opened, there is a gap between the two layers. A multilayer sheet for thermoforming packaging containers in which the interlayer peel strength of the two layers is 1.5 kg/15 mm or less so as to start from peeling.