JPS60127093A - ろう材 - Google Patents
ろう材Info
- Publication number
- JPS60127093A JPS60127093A JP23389583A JP23389583A JPS60127093A JP S60127093 A JPS60127093 A JP S60127093A JP 23389583 A JP23389583 A JP 23389583A JP 23389583 A JP23389583 A JP 23389583A JP S60127093 A JPS60127093 A JP S60127093A
- Authority
- JP
- Japan
- Prior art keywords
- weight
- brazing material
- wax
- total
- brazing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
本発明は、Ag−Cu−Pd系のろう祠の改良に関する
。
。
Ag−Cu−Pd系のろう相は、F’e、Co。
Ni基合金及びステンレス鋼などに対してAr。
H2又は真空中でろう付するとAgろうよりも濡れ性が
良いことが知られている。例示すると、J[S、BSの
パラジウムろう (Pd4.5〜25.5%、 A g
51.5〜69%、 Cu 19.5〜32%)、特
公昭57−61516号のろう材(Pd25%以上、A
g2〜25%、Cu2〜40%、Ni8〜40%)があ
る。
良いことが知られている。例示すると、J[S、BSの
パラジウムろう (Pd4.5〜25.5%、 A g
51.5〜69%、 Cu 19.5〜32%)、特
公昭57−61516号のろう材(Pd25%以上、A
g2〜25%、Cu2〜40%、Ni8〜40%)があ
る。
然し乍ら、上記Ag−Cu−Pd系のろう祠は、高温で
の強度が低く、高温での耐酸化性が劣るものである。ま
たろうの流動性が悪く、しかも醐;点が高いので、ろう
イ」作業が厄介である。
の強度が低く、高温での耐酸化性が劣るものである。ま
たろうの流動性が悪く、しかも醐;点が高いので、ろう
イ」作業が厄介である。
本発明は斯かる問題を解決すべくなされたものであり、
ろうの濡れ性が良いことは勿論のこと、高温での強度が
高く、且つ耐酸化性に優れ、またろうの流動性が良くし
かも融点が低くて、ろう付作業が容易なろう祠を提供せ
んとするものである。
ろうの濡れ性が良いことは勿論のこと、高温での強度が
高く、且つ耐酸化性に優れ、またろうの流動性が良くし
かも融点が低くて、ろう付作業が容易なろう祠を提供せ
んとするものである。
本発明のろう材の1つは、Pd2〜3(13%。
Ag45〜90重量%、Mn、Nf、Co(7)少なく
とも1種を合計で0.5〜9重量%、残部Cu及び0.
3重量%以下の不可避不純物より成る。
とも1種を合計で0.5〜9重量%、残部Cu及び0.
3重量%以下の不可避不純物より成る。
本発明のろう材の他の1つは、Pd2〜30重量%、A
g45〜90重量%、Mn、Ni、Coの少なくとも1
種を合計で0.5〜9重量%、In、S’nの少なくと
も1種を合計で0.5〜10重量%、残部Ou及び0.
3重量%以下の不可避不純物より成る。
g45〜90重量%、Mn、Ni、Coの少なくとも1
種を合計で0.5〜9重量%、In、S’nの少なくと
も1種を合計で0.5〜10重量%、残部Ou及び0.
3重量%以下の不可避不純物より成る。
本発明のろう祠の更に他の1つは、Pd2〜30■i
Ed % 、 A g 45〜90i 1i % 、
Mn、 Ni、 Co の少なくとも1種を合計で0.
5〜9重量%、L i O,05〜2市(i%、残部C
u及び0.3重量%以下の不可避不純物より成る。
Ed % 、 A g 45〜90i 1i % 、
Mn、 Ni、 Co の少なくとも1種を合計で0.
5〜9重量%、L i O,05〜2市(i%、残部C
u及び0.3重量%以下の不可避不純物より成る。
本発明のろう祠の更に他の1つは、Pd2〜301[【
量%、 Δ g 45−90重fJ %、Mn、Ni、
Co の少なくとも1種を合計で0.5〜9重量%、I
n。
量%、 Δ g 45−90重fJ %、Mn、Ni、
Co の少なくとも1種を合計で0.5〜9重量%、I
n。
S nの少なくとも1種を合計で0.5〜10重量%。
l i 0.05〜2 F、M%、残部CI!及び0.
3重量%以下の不可避不純物より成る。
3重量%以下の不可避不純物より成る。
これら本発明のろう祠に於いて、]) d 2〜30重
量%、Ag45〜90重量%とじたのは、残部Cuとに
よるA g−C’u −P d系のろう材として優れた
特性、即ちFe、Co、N+基合金及びステンレス鋼な
どに対してAr、t(z又は真空中でろうイ4した際の
濡れ性を備えさせる為で、Pd、Agか前記の重量比の
範囲を逸脱するとろう材としての濡れ性が著しく劣下す
るものである。
量%、Ag45〜90重量%とじたのは、残部Cuとに
よるA g−C’u −P d系のろう材として優れた
特性、即ちFe、Co、N+基合金及びステンレス鋼な
どに対してAr、t(z又は真空中でろうイ4した際の
濡れ性を備えさせる為で、Pd、Agか前記の重量比の
範囲を逸脱するとろう材としての濡れ性が著しく劣下す
るものである。
Mn、Ni、Coの少なくとも1種を合計で0.5〜9
重量%としたのは、Ag−Cu−Pd系のろう材の高温
中での強度を高め、且つ高温での耐酸化性を向上させる
為で、・0.5重量%未満ではその目的を達成させるこ
とができす、9重量%を超えるとろうの融点が上がり、
ろう流れが悪くなる。
重量%としたのは、Ag−Cu−Pd系のろう材の高温
中での強度を高め、且つ高温での耐酸化性を向上させる
為で、・0.5重量%未満ではその目的を達成させるこ
とができす、9重量%を超えるとろうの融点が上がり、
ろう流れが悪くなる。
In、Snの少なくとも1種を合計で0.5〜10重量
%とじたのは、Ag−Cu−Pd系のろう祠に於けるろ
うの流動性、ろうイzJ性を良好にし、且つ融点を低く
して、ろう付作業を容易ならしめる為で、0.5N量%
未満ではろうの流動性が良くな上記表−2の結果で明ら
かなように実施例1〜4のろう+4は、従来例のろう祠
と同様にろうの濡れ性に優れていることは勿論のこと、
従来例のろう祠では劣っていた高温での強度、耐酸化性
に優れていることが判る。また実施例2.4のろう(、
(についてはろうの流動性が従来例のろう+Aに比べて
優れ、しかも実施例2.4のろう材は従来例のろう材よ
りも著しく融点が低いことが判る。
%とじたのは、Ag−Cu−Pd系のろう祠に於けるろ
うの流動性、ろうイzJ性を良好にし、且つ融点を低く
して、ろう付作業を容易ならしめる為で、0.5N量%
未満ではろうの流動性が良くな上記表−2の結果で明ら
かなように実施例1〜4のろう+4は、従来例のろう祠
と同様にろうの濡れ性に優れていることは勿論のこと、
従来例のろう祠では劣っていた高温での強度、耐酸化性
に優れていることが判る。また実施例2.4のろう(、
(についてはろうの流動性が従来例のろう+Aに比べて
優れ、しかも実施例2.4のろう材は従来例のろう材よ
りも著しく融点が低いことが判る。
以」二の説明で判るように本発明による各ろう材は、ろ
うの濡れ性が良く、高温での強度が高<■」。
うの濡れ性が良く、高温での強度が高<■」。
つ耐酸化性に優れており、またIn、Snのいずれか1
種を合計で0.5〜10市景%添加した本発明の特許請
求の範囲2,4のろう材は、更にろうの流動性に優れし
かも融点が著しく低くてろう付作業が容易であるので、
Fe、Co、Ni基合金及びステンレス鋼などに対する
ろう(=Jのろう祠としては従来のろう祠にとって代わ
ることのできる画期的なものと云える。
種を合計で0.5〜10市景%添加した本発明の特許請
求の範囲2,4のろう材は、更にろうの流動性に優れし
かも融点が著しく低くてろう付作業が容易であるので、
Fe、Co、Ni基合金及びステンレス鋼などに対する
ろう(=Jのろう祠としては従来のろう祠にとって代わ
ることのできる画期的なものと云える。
出願人 ロJ中貴金属工業株式会社
Claims (1)
- 【特許請求の範囲】 1 ) l) d 2〜30ffi1%、Ag45〜9
0重量%、Mn。 Ni、Coの少なくとも1種を合計で0.5〜9重II
t%、残部Ou及び不可避不純物より成るろう材。 2)Pd2〜30重量%、Δg45〜90重量%、Iv
ln。 Ni、Coの少なくとも1種を合計で0.5〜9重早%
、In、Snの少なくとも1種を合計で0,5〜10市
掛%、残部CLI及び不可避不純物より成るろう祠。 3 > p d2−3offl[%、Ag45〜90重
量%、Mn。 Ni、Coの少なくとも1種を合計で0.5〜9重1t
%、1、i 0.05〜2重量%、残部Cu及び不可避
不純物、1、り成るろう利。 4) P d 2〜30i1[%、Ag45〜90重量
%、Mn。 Ni、Coの少なくとも1種を合計で0.5〜9重量%
、In、Snの少なくとも1種を合計で0.5〜10i
11Rff1%、 I−i 0.05〜2重量%、残部
Cu及び不可避不純物より成るろう材。