JPS5947034B2 - 防錆剤 - Google Patents

防錆剤

Info

Publication number
JPS5947034B2
JPS5947034B2 JP57013527A JP1352782A JPS5947034B2 JP S5947034 B2 JPS5947034 B2 JP S5947034B2 JP 57013527 A JP57013527 A JP 57013527A JP 1352782 A JP1352782 A JP 1352782A JP S5947034 B2 JPS5947034 B2 JP S5947034B2
Authority
JP
Japan
Prior art keywords
parts
rust
rust preventive
water
acid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
JP57013527A
Other languages
English (en)
Other versions
JPS58133381A (ja
Inventor
紳一 熊谷
達夫 真鍋
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ITSUHOSHA YUSHI KOGYO KK
Original Assignee
ITSUHOSHA YUSHI KOGYO KK
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ITSUHOSHA YUSHI KOGYO KK filed Critical ITSUHOSHA YUSHI KOGYO KK
Priority to JP57013527A priority Critical patent/JPS5947034B2/ja
Priority to US06/428,719 priority patent/US4466902A/en
Publication of JPS58133381A publication Critical patent/JPS58133381A/ja
Publication of JPS5947034B2 publication Critical patent/JPS5947034B2/ja
Expired legal-status Critical Current

Description

【発明の詳細な説明】 本発明は、防錆性および低気泡性に優れる新規な防錆剤
に関するものである。
従来、防錆剤としてはクロム酸塩、リノ酸塩、亜硝酸ソ
ーダなどの無機系化合物、およびアルキルアミン、アル
キルポリアミン、脂肪酸とポリアルキレンポリアミンと
の縮合物、アルキレンオキサイドとアミン類との付加物
などの有機系化合物が主として用いられている。
このうち無機系のものは一般に潤滑性が悪いうえに、ク
ロム系は毒性があり、リン系のものは排水の富栄養化を
もたらし、また亜硝酸系のものは発ガン性の懸念のある
ニトロソアミンに変化する等公害上の問題から使用が規
制されはじめ、次第に有機系のものに移りつつある。
しかし、現在用いられている有機系防錆剤の防錆効果は
いまだ十分なものではなく、主として亜硝酸ソーダなど
の無機系化合物を混入して用いている。もつとも、上記
各無機系防錆剤自体夫々単独では防錆効果が十分でなく
、用途に合わせて各種の有機・無機化合物を混入して用
いているのが現状である。しかも、従来の有機系防錆剤
は、水溶性防錆剤として用いられる場合泡立ちが激しく
、そのため工業的利用において操作性に劣るなどの問題
があり、低起泡性で防錆効果の優れた有機系防錆剤の出
現が強く望まれている。そこで本発明者等は上記問題を
解決するべく鋭意研究した結果、少量の使用でしかも他
の無機系化合物と混用しなくても優れた防錆効果を示し
、且つ低起泡性の有機防錆剤を開発した。
即ち、本発明の防錆剤は、一般式〔Ｉ〕 ＨＯＯＣＲ３ト■（Ｃｏ−Ｘ−Ｃ０ＮＨＲ２ＣＯＯＨ・
・・〔工〕で示されるカルボン酸類の塩を必須成分とす
る防錆剤である。
伺式〔Ｉ〕中、Ｘは芳香族系炭化水素基であり、Ｒ、、
Ｒ２はそれぞれ炭素数１〜１８の炭化水素基でありそれ
ぞれは同じものでも異なつていてもよく、また直鎖状で
も分岐鎖状でもよい。更に場合により、炭化水素基に不
飽和結合があつても差支えない。本発明に使用されるカ
ルボン酸類としては、Ｎ、Ｎ’−テレフタロイルジグリ
シン、Ｎ、Ｎ’−テレフタロイルジアミノプロピオン酸
、Ｎ、Ｎ’−テレフタロイルジアミノカプロン酸、Ｎ、
Ｎ’−テレフタロイルジアラニン、Ｎ、Ｎ’−テレフタ
ロイルジザルコシンなど、更に例えば無水ピロメリット
酸とグリシン、ザルコシン及びアミノカプロン酸などの
アミノ酸との反応物などが用いられるが、これらに限定
するものではない。
そしてこれらのカルボン酸類は、塩化プタロールとアミ
ノ酸とから公知の方法で容易に合成できる（例えば、有
機化合物合成法、第３集第６６頁）。次に、カルボン酸
類と塩を構成する化合物としては、苛性ソーダ、苛性カ
リ、炭酸ソーダ、水酸化カルシウムなどのアルカリ金属
，アルカリ土類金属の塩のほか、アンモニウム塩、メチ
ルアミン、エチルアミン、モノエタノールアミン、ジエ
タノールアミン、トリエタノールアミン、シクロヘキシ
ルアミン等の低級アミン類等が好適に用いられる。
伺、カルボン酸類の塩（アルカリ塩）を製造するには、
両者を混合し、必要があれば加熱撹拌してもよい。
その際、反応溶媒として両成分を溶解させる有機溶剤ま
たは水、あるいはその両者の混合物を用いてもよい。ま
た、カルボン酸類とアルカリ（上記アルカリ金属、アル
カリ土類金属の塩やアミン類等）の混合割合は、当量か
もしくは一万が過剰でもよいが、一般的にアルカリ過剰
の方が水に対する溶解性が良好になる。本発明の防錆剤
は，その使用方法に｝いて特に限定されず、従来の防錆
剤と同様水、油，エマルジヨン液に溶解して使用される
。
次に、実施例により本発明を更に詳しく説明する。
向、実施例中の部は重量部を意味する。実施例 １コン
デンサーと攪拌装置のついた反応容器にアミノカプロン
酸４３部、水酸化ナトリウム２５９．水１４０部を人れ
混合攪拌し冷却しながら６塩化テレフタロイル３０部を
ジオキサン７０部に溶解したものを内温が３０℃以下に
保たれるよう徐々に滴下する。
滴下終了後３０℃にて更に３時間攪拌したのち、冷却し
ながら硫酸で中和する。生成した白色沈澱を濾過し、水
洗後イソプロピルアルコールにて精製し、Ｎ，Ｎ′−テ
レフタロイルジアミノカプロン酸を得る。次に、このＮ
，Ｎ′−テレフタロイルジアミノカプロン酸３０部、ト
リエタノールアミン２６部、水１３２部を加熱混合して
有効成分約３０％の防錆剤を得る。
実施例 ２ 実施例１で合成したＮ，Ｎ５−テレフタロイルジアミノ
カプロン酸１５部、苛性ソーダ３部、水４２部を加熱混
合して有効成分約３０（ｆｌ）の防錆剤を得る。
実施例 ３ 実施例１で合成したＮ，Ｎ′−テレフタロイルジアミノ
カプロン酸１５部、苛性カリ４．５部、水４５．５部を
加熱混合して有効成分約３００Ｉ）の防錆剤を得る。
実施例 ４ 実施例１で合成したＮ，Ｎ′−テレフタロイルジアミノ
カプロン酸１５部、ジエタノールアミン８部、水５４部
を加熱混合して有効成分約３０（ｆ）の防錆剤を得る。
実施例 ５ 実施例１で合成したＮ，Ｎ５−テレフタロイルジアミノ
カプロン酸１５部、メチルアミン４ｆ！ｆ）ｓ水４４部
を加熱混合して有効成分約３０％の防錆剤を得る。
実施例 ６ 実施例１で合成したＮ，Ｎ′−テレフタロイルジアミノ
カプロン酸１５部、モノエタノールアミン５部、水４７
部を加熱混合して有効成分約３００１）の防錆剤を得る
。
実施例 ７ 実施例１で合成したＮ，Ｎｌ−テレフタロイルジアミノ
カプロン酸１５部、シクロヘキシルアミン７部、水５１
部を加熱混合して有効成分約３０（ｆｌ）の防錆剤を得
る。
実施例 ８ 実施例１と同様な反応容器に、グリシン１６５部、水酸
化ナトリウム１７６部、水５１１部を入れ混合撹拌し、
冷却しながら塩化テレフタロイル３９６部をジオキサン
８００部に溶解したものを３０分〜６０分かけて内温が
３０℃以下に保たれるように注意しながら滴下する。
滴下終了後３０〜４０℃にて更に２時間攪拌を続けたの
ち、硫酸にて酸性にして生成したジカルボン酸を析出さ
せ、濾過水洗してＮ，Ｎ５−テレフタロイルジグリシン
の白色粉末を得る。次にこのＮ，Ｎ′−テレフタロイル
ジグリシン５０部、トリエタノールアミン６０部、水２
５７部を混合攪拌して有効成分約３０％の防錆剤を得る
。
実施例 ９ 実施例１と同様な反応容器にＤＬ−アラニン８９部、水
酸化ナトリウム５０部、水２００部を入れ混合攪拌し、
冷却しながら塩化プタロール９５部をジオキサン１００
部に溶解したものを内温が３０℃以下に保たれるよう注
意しながら滴下する。
滴下終了後３０〜４０℃にて更に２時間攪拌 続けたの
ち、硫酸にて中和し、生成したジカルボン酸を濾過水洗
して．Ｎ，Ｎ５−プタロールビス（ＤＬ−アラニン）の
白色粉末を得る。次にこのＮ，Ｎ５−プタロールビス（
ＤＬ−アラニン）３０部、トリエタノールアミン４５部
、水１７５部を混合撹拌して有効成分約３００ｔ）の防
錆剤を得る。
比較例 １ 安息香酸１００部、トリエタノールアミン１１７音艮水
５０６部を加熱攪拌して有効成分約３００１）の防錆剤
を得る。
比較例 ２ オレイン酸１００部、トリエタノールアミン５１部、水
３５２部を混合攪拌して、有効成分約３０％の防錆剤を
得る。
これらの各実施例訃よび比較例に示す防錆剤から、夫々
有効成分１（ｆ）の水溶液をつくり、さび発生試験及び
起泡性テストを行なつた結果を表−１に示す。
さび発生試験はＪＩＳ−Ｋ−２２４６（さび止め油湿潤
試験）に準拠したもので、ＳＯＰＣ−１の鋼板（６０×
８１×１Ｖ．）を用い、湿潤箱中で４９±１℃、相対湿
度９５０１）以上、空気送入量８８６．５±１１０．５
１１／／Ｈｒの条件下でさび発生試験を行なつた。
さび発生度の判定はＪＩＳ−Ｋ−２２４６（さび止め油
さび発生度測定方法）に従つたが、本発明品は表−に示
すように極めて優れた防錆剤を示した。また、起泡性の
測定は、ロス・クラーク法に準拠した。
即ち，内径５０度、高さ１０００Ｖ．の円筒に有効成分
１％の防錆剤水溶液を２００ｍ２入れ．細孔の直径４０
〜５０μのガラスフイルタ一より、５００ｍｅ／Ｍｍの
空気を連続的に吹き込み、６０秒後の２０℃にかける泡
の高さを測定した。次に、表−にその結果を示すように
、切粉（鋳鉄粉）のさび発生度を上記各実施例むよび比
較例について行なつた。
この試験の方法及び判定基準は次の通りである。まずド
ライカツトした鋳鉄（ＦＣ−２０及びＦＣ−２５）の切
り削５ｙをトルエンで洗浄したのちつづいてメタノール
で洗浄し、夫々の試料液（有効成分１％の防錆剤水溶液
）中に１分間（常温）浸漬して液を切つたものを、濾紙
を敷いたシヤーレ（直径６０Ｖ．）に入れ、前記夫々の
試料液１ｍ２を加え、蓋をした後３０℃，８０（！）Ｒ
Ｈで保存する。そして発錆までの時間と、２４時間後の
さびの発生度を、濾紙についてＪＩＳ−Ｋ−２２４６に
準拠して測定した。但し、各試料液のＰＨはＮａＯＨ水
溶液にて９．５に調整したものを用いた。表−から切粉
に対して極めて優れた防錆性を示すことがわかる。周、
この両者を満足する防錆剤は極めて少ないとされている
。このように本発明の発明の防錆剤は、湿潤箱中の鉄板
と湿潤された切粉（鋳鉄粉）の両方の防錆を有効になし
得広範囲な防錆効果を有するとともに、低起泡性である
ため、エマルジヨンや水溶液に用いた場合泡立ちがなく
、発泡による防錆効果の減少や取扱いにくさがないこと
も大きな特徴である。
更に、本発明の防錆剤は、亜硝酸ソーダのような無機塩
を併用しなくても単独で優れた防錆効果をもたらすもの
であるが、場合訃よび用途によつては他の無機系あるい
は有機系の防錆剤と混合して用いることもできる。

Claims (1)

  1. 【特許請求の範囲】 １ 一般式 ＨＯＯＣＲ＿１ＮＨＣＯ−Ｘ−ＣＯＮＨＲ＿２ＣＯＯＨ
    で示されるカルボン酸類の塩を必須成分とする防錆剤。 （式中、Ｘは芳香族系炭化水素基であり、Ｒ＿１、Ｒ＿
    ２はそれぞれ炭素数１〜１８の炭化水素基であり同じで
    も異なつてもよく、直鎖状でも分岐状でもよい。 ）
JP57013527A 1982-01-31 1982-01-31 防錆剤 Expired JPS5947034B2 (ja)