JPS5829842A - Propylene polymer composition having improved coatability - Google Patents
Propylene polymer composition having improved coatabilityInfo
- Publication number
- JPS5829842A JPS5829842A JP12819281A JP12819281A JPS5829842A JP S5829842 A JPS5829842 A JP S5829842A JP 12819281 A JP12819281 A JP 12819281A JP 12819281 A JP12819281 A JP 12819281A JP S5829842 A JPS5829842 A JP S5829842A
- Authority
- JP
- Japan
- Prior art keywords
- propylene polymer
- propylene
- styrene
- block copolymer
- polymer composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【発明の詳細な説明】
本発明は、塗装性の改良されたプロピレン重合体組成物
に関する。DETAILED DESCRIPTION OF THE INVENTION The present invention relates to propylene polymer compositions with improved paintability.
プロピレン重合体は、入手が容易で、市場の要求性能を
ある程度溝たす物性を有するので、汎用樹脂として各分
野で利用されているが、分子構造上極性がないのて塗装
性が不良であることが欠点の一つとなっている。Propylene polymer is easy to obtain and has physical properties that meet market requirements to some extent, so it is used in various fields as a general-purpose resin, but it has poor paintability because its molecular structure has no polarity. This is one of the drawbacks.
この欠点を解消するために、エラス)w−を添加する方
法が知られているが、プロピレン重合体との相溶性に問
題があシ、また剛性が低下するので、更に無機質フィラ
ーを添加する方法が行なわれている。In order to overcome this drawback, a method of adding elas) w- is known, but there is a problem with compatibility with the propylene polymer and the rigidity decreases, so a method of further adding an inorganic filler is known. is being carried out.
しかし、エラストマーおよびフィラーを多tK配合する
ことは、プロピレン重合体の持つ低密度、光沢、肌触り
感を損ねることになり好ましくない。However, blending an elastomer and a filler with a high tK is not preferable because it impairs the low density, gloss, and texture of the propylene polymer.
また、プロピレン重合体にエチレン−プロピレン共重合
体ゴム(KPM)またはエチレン−プロピレン−非共役
ジエン三元共重合体ゴム(EPDM)をブレンドする方
法も知られているが、この方法はプロピレン単独重合体
(PP)には有効であるが、エチレン−プロピレンブロ
ック共重合体(EPP)には効果が低い。Also known is a method of blending propylene polymer with ethylene-propylene copolymer rubber (KPM) or ethylene-propylene-nonconjugated diene terpolymer rubber (EPDM); Although it is effective for copolymer (PP), it is less effective for ethylene-propylene block copolymer (EPP).
更にプロピレン重合体くスチレン−ブタジェンブロック
共重合体をブレンドする方法も知られているが、PPK
は効果が低く、またプロピレン重合体との相溶性が悪く
、層状剥離することがある。Furthermore, a method of blending a propylene polymer with a styrene-butadiene block copolymer is also known, but PPK
is less effective and has poor compatibility with propylene polymers, resulting in delamination.
本発明は、これらの欠点を解決するものであシ、少量の
スチレン−イソプレンブロック共重合体を配合すること
によってプロピレン重合体の塗装性を改良でき、市場か
らの要求性能の高度化に対応できる塗装性を有し、成形
品の表面処理を施さなくても十分効果があるプロピレン
重合体組成物を提供することを目的とし、その要旨とす
るところは、プロピレン重合体にスイレンーイソプレン
ブUツク共重合体を両成分の総和に対してW〜薗型重量
配合したことを特徴とする塗装性の改良されたプロピレ
ン重合体組成物に存する。The present invention solves these drawbacks, and by blending a small amount of styrene-isoprene block copolymer, the paintability of propylene polymer can be improved, and it can meet the increasingly sophisticated performance demands from the market. The purpose is to provide a propylene polymer composition that has paintability and is sufficiently effective without surface treatment of molded products. The present invention provides a propylene polymer composition with improved paintability, characterized in that a copolymer is blended in a proportion of W to 100% by weight based on the total of both components.
そして本発明のプロピレン重合体組成物の用途としては
、自動車、家電、容器、雑貨等の広い分野での利用が可
能である。The propylene polymer composition of the present invention can be used in a wide range of fields such as automobiles, home appliances, containers, and miscellaneous goods.
本発明で用いるプロピレン重合体は、プロピレン単独結
晶性重合体:エチレン、ブテン−11ペンテン−11ヘ
キセン−1%番−メチルペンテン−1等信のa−オレフ
ィンまたは酢酸ビニに勢のビニルエステルと過半重量の
プロピレンからなるランダムないしブロック共重合体ニ
アクリル酸、メタクリル酸、マレイン酸、イタコン酸等
の不飽和有機酸類(エステル、アミン、アミド、塩、無
水物岬誘導体も含む)またはビニルトリメトキシシラン
等のビニルシランなどでプロピレン重合体をグラフト処
理したもの等である。The propylene polymer used in the present invention is a propylene homocrystalline polymer: ethylene, a-olefin such as butene-11pentene-11hexene-1%-methylpentene-1, or a vinyl ester such as vinyl acetate. Random or block copolymers of propylene, unsaturated organic acids such as nialic acid, methacrylic acid, maleic acid, and itaconic acid (including esters, amines, amides, salts, and anhydride derivatives), or vinyltrimethoxysilane, etc. These include those obtained by grafting a propylene polymer with vinyl silane or the like.
中テモ、プロピレン単独重合体、他のα−オレフィンを
雪〜美重i1−含有したプロピレン−σ−オレフインブ
ロック共重合体が良く、とりわけエチレンを2〜20重
量%含有し、MFRo、5〜40fA紛のプロピレン−
エチレンブロック共重合体が好ましい。A propylene-σ-olefin block copolymer containing medium-sized, propylene homopolymer, and other α-olefins is good, especially containing 2 to 20% by weight of ethylene, MFRo, 5 to 40 fA Propylene powder
Ethylene block copolymers are preferred.
このようなプロピレン重合体は通常市販のものから適宜
選択することができる。Such propylene polymers can be appropriately selected from commercially available products.
また、本発明で用いるスチレン−イソプレンブロック共
重合体(SIS)は、公知の方法(例えば特公昭42−
1749鱒公報)で得られるスチレンとイソプレンがブ
ロック状に共重合したゴム状物質であり、スチレンとイ
ソプレンの比率(X量比)は1o790〜40μOOも
のである。In addition, the styrene-isoprene block copolymer (SIS) used in the present invention can be prepared by a known method (for example,
It is a rubber-like substance obtained by copolymerizing styrene and isoprene in a block shape, and the ratio of styrene to isoprene (X amount ratio) is 10790 to 40 μOO.
トリわけ、スチレンとイソプレンの比率(重量比)が1
2/88〜zs/75のものが好ましい。SISの配合
割合は全組成中10〜30重〜−1好ましくはi〜5〜
量−である。10チ未満では塗装性改良効果が不十分で
あり、30チを越えると組成物の剛性が低下して実用的
でなくなる。The ratio (weight ratio) of styrene and isoprene is 1.
Preferably, it has a value of 2/88 to zs/75. The blending ratio of SIS is 10 to 30 weights to -1, preferably i to 5 weight in the whole composition.
The amount is -. If it is less than 10 inches, the effect of improving paintability is insufficient, and if it exceeds 30 inches, the rigidity of the composition decreases and it becomes impractical.
なお、本発明の効果を損なわない範囲で、他の熱可塑性
樹脂、無機充填剤、各種安定剤、着色剤郷を添加しても
よい。Note that other thermoplastic resins, inorganic fillers, various stabilizers, and colorants may be added to the extent that the effects of the present invention are not impaired.
本発明組成物を製造する方法は、ロール、バンバリーミ
キサ−、プラベンダープラストグラフ、二軸押出機等通
常の混線機で、両成分(必要に応じ他の成分を加えて)
を混練することによシ行なわれる。The method for producing the composition of the present invention is to use a common mixer such as a roll, Banbury mixer, Prabender Plastograph, or twin screw extruder to produce both components (with other components added if necessary).
This is done by kneading.
混練機としては、混線効果の大きなものが好ましいが、
各種成形機に所要成分を直接フィードして本発明組成物
を製造することもできる。As a kneading machine, it is preferable to use one with a large crosstalk effect.
The composition of the present invention can also be produced by directly feeding the necessary components into various molding machines.
次に実施例によって本発明を更に具体的に説明する。Next, the present invention will be explained in more detail with reference to Examples.
実施例11比較例1
2種類のプロピレン重合体にそれぞれ各種ゴムを謳重量
%添加し、し勺=6の2軸押出機により混錬し、これを
ペレットにした。このペレットを射出成形機で2−厚の
シートに成形し、塗装試験に供した。Example 11 Comparative Example 1 Two types of propylene polymers were each added with various rubbers in an amount of % by weight, and kneaded using a twin-screw extruder with a pressure of 6 to form pellets. The pellets were molded into a 2-thick sheet using an injection molding machine and subjected to a coating test.
塗装試験は、カシュー社製のポリオレフィン用塗料マイ
クロンφ3000および同φ4000 をそれぞれ上
記シートに厚み約加μになるように吹付は塗装し、80
℃で(資)分間乾燥後に、塗装面に縦横それぞれ11間
隔で1−角が10個ずつ、すなわち合計100個になる
ようにナイフ刃で基盤目を入れ、セ;テープを接着させ
て急激に剥離を行ない、塗料が剥離せずに残つ良計の数
を数えた。結果を第1表に示す。In the coating test, polyolefin paint Micron φ3000 and Micron φ4000 manufactured by Cashew Co., Ltd. were sprayed onto the above sheet to a thickness of approximately 80 μm.
After drying at ℃ for minutes, make base marks on the painted surface with a knife blade so that there are 10 1-angles at 11 intervals vertically and horizontally, that is, 100 pieces in total. Peeling was performed and the number of good samples that remained without the paint peeling was counted. The results are shown in Table 1.
オ 五 表
Cυ本本玉三菱油化社製ポリプロピレン本2 同上
エチレン−プロピレンブロック共重合体本3シエ
ル化学社製 スチレン−イソプレンブロック共重合体ネ
4 同上 スチレン−ブタジェンプルツク共
重合体本5旭化成社製 同上
率6日本イービーラバー社製 エチレン−プロピレン共
重合体ゴム(EPM)
実施例2、比較例2
実験例ム■のゴム含量を変えて同様に塗装試験を行なっ
た。結果を第2表に示す。E 5 Table Cυ Honhontama Polypropylene book manufactured by Mitsubishi Yuka Co., Ltd. 2 Same as above
Ethylene-propylene block copolymer 3 Made by Ciel Chemical Co., Ltd. Styrene-isoprene block copolymer 4 Same as above Styrene-butadiene Plutsch copolymer 5 Made by Asahi Kasei Co., Ltd. Same as above 6 Ethylene-propylene copolymer made by Nippon E-B Rubber Co., Ltd. Combined Rubber (EPM) Example 2, Comparative Example 2 A coating test was conducted in the same manner as in Experimental Example M (2) with different rubber contents. The results are shown in Table 2.
((転)本7一部基材の表層剥離が起こった。((Transformed) Book 7 The surface layer of the base material peeled off in some parts.
Claims (1)
合体を両成分の総和量に対して1O−(9)重量−配合
したことを特徴とする塗装性の改良されたプロピレン重
合体組成物。A propylene polymer composition with improved paintability, characterized in that a styrene-isogrene block copolymer is blended with a propylene polymer in an amount of 10-(9) weight based on the total amount of both components.