JPH1129756A - Adhesive and filter element formed using this adhesive - Google Patents

Abstract

PROBLEM TO BE SOLVED: To obtain an adhesive with improved sealing and adhesion abilities, and a filter element showing strong sealing and adhesion of a filter paper and an end plate at the attachment point, in which the decrease in the filter area of the filter medium is suppressed. SOLUTION: The adhesive 10 has an epoxy adhesive with a comparatively low viscosity of 500 to 100,000 cp as a base 10a. This base 10a is added with a hydrophilic, extremely fine fiber 10b which has 0.1 to 1 denier in gauge and 1 to 10 mm in length. The amount of this fiber 10b added to the base 10a is 0.1 to 1 wt.%. This adhesive 10 is used to attach an end plate 3 to the bottom surface of a rosette shaped filter medium 5. This reduces the absorption of the base 10a to the filter medium 5.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、気体、液体等の濾
過用のフィルターエレメントの形成に有効である接着剤
に関するとともに、この接着剤を用いて形成されたフィ
ルタエレメントに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an adhesive effective for forming a filter element for filtering gas, liquid, and the like, and to a filter element formed by using the adhesive.

【０００２】[0002]

【従来の技術】気体、液体等の流体を濾過するためのフ
ィルタエレメントに用いられる濾材としては、その濾過
面積をできる限り大きくするため、板状の濾紙を所定の
幅でプリーツ状に形成した後、全体形状が略円筒状とな
るように形成した菊花状エレメントと称されるフィルタ
エレメントが多く用いられている。2. Description of the Related Art As a filter medium used for a filter element for filtering a fluid such as a gas or a liquid, in order to increase the filtration area as much as possible, a plate-like filter paper is formed into a pleated shape with a predetermined width. A filter element called a chrysanthemum flower element formed so as to have a substantially cylindrical shape as a whole is often used.

【０００３】このような菊花状エレメントにおいては、
プリーツ状に形成された濾紙の上下端部にエンドプレー
トを接着することにより濾材の円筒形状を保持するよう
にしている。この接着のために用いられる接着剤には、
濾紙とエンドプレートとの接着性のみならず、濾紙とエ
ンドプレートとの間のシール性も要求される。In such a chrysanthemum flower-like element,
By attaching end plates to the upper and lower ends of the pleated filter paper, the cylindrical shape of the filter medium is maintained. The adhesive used for this bonding includes
Not only adhesiveness between the filter paper and the end plate, but also sealing performance between the filter paper and the end plate are required.

【０００４】ここで、濾紙とエンドプレートとのシール
性を維持するためには、接着剤の量を多くするのみなら
ず、粘度の高い接着剤を使用する必要がある。すなわ
ち、シール剤として一般的に用いられているパテのよう
な性質を有する接着剤を用いることが好ましい。Here, in order to maintain the sealing property between the filter paper and the end plate, it is necessary not only to increase the amount of the adhesive but also to use an adhesive having a high viscosity. That is, it is preferable to use an adhesive having properties like putty generally used as a sealant.

【０００５】しかしながら、接着剤は一般的に粘度が低
くなると接着力が高くなる傾向にあるため、粘度の高い
接着剤を用いた場合、シール性は向上するが接着力が低
下するとともに、濾紙およびエンドプレートの接着面に
対する馴染み（接着性）が低下する。このため、プリー
ツ状に折り曲げた濾紙の折り曲げ部に隙間（気泡）が生
じやすくなり、ピンホールができる原因となる。However, adhesives generally have a tendency to increase in adhesive strength when the viscosity decreases. Therefore, when an adhesive having a high viscosity is used, the sealing property is improved but the adhesive strength is reduced, and the adhesive strength is reduced. The familiarity (adhesion) of the end plate to the adhesive surface is reduced. For this reason, gaps (bubbles) are likely to be formed in the bent portion of the filter paper folded in a pleated shape, which causes pinholes.

【０００６】そこで、接着剤として粘度の低いものを使
うことが考えられる。しかしながら、図５（Ａ）に示す
ように、粘度の低い接着剤２０をエンドプレート（図５
においては、下側エンドプレート３のみ表している）上
に充填し、この接着剤２０の上に濾紙５を載置すると、
（Ｂ）に示すように濾紙５において生ずる毛細管現象に
よって、接着剤２０が硬化する前に濾紙５に吸い上げら
れてしまう。Therefore, it is conceivable to use an adhesive having a low viscosity as an adhesive. However, as shown in FIG. 5A, an adhesive 20 having a low viscosity is applied to an end plate (FIG. 5).
, Only the lower end plate 3 is shown), and the filter paper 5 is placed on the adhesive 20.
As shown in (B), the adhesive 20 is sucked up by the filter paper 5 before the adhesive 20 hardens due to the capillary phenomenon that occurs in the filter paper 5.

【０００７】このため、下エンドプレート３上の接着剤
２０の表面に凹凸を生じたり、極端な場合には下エンド
プレート３上の接着剤２０が無くなってしまうこともあ
る。これにより、濾紙５と下エンドプレート３との間に
隙間ができたり、接着部にピンホールができる原因とな
る。For this reason, the surface of the adhesive 20 on the lower end plate 3 may be uneven, or in extreme cases, the adhesive 20 on the lower end plate 3 may be lost. This causes a gap between the filter paper 5 and the lower end plate 3 or a pinhole in the bonding portion.

【０００８】[0008]

【発明が解決しようとする課題】すなわち、既存の接着
剤を用いて濾紙とエンドプレートとを接着することによ
ってフィルタエレメントを形成すると、接着剤の粘度の
高い場合および低い場合のいずれの場合においても、各
々の粘度における特性に基づく原因により、接着部にピ
ンホールができやすく、ピンホールができると、接着性
が低下するとともに濾過すべき流体の漏れが生じるとい
う問題がある。また、粘度の低い接着剤を用いた場合、
ピンホールが生じなくても、接着剤２０が濾材５に吸い
上げられることにより、濾材５の実効濾過面積が小さく
なってしまうという問題もある。That is, when a filter element is formed by bonding a filter paper and an end plate with an existing adhesive, the filter element can be formed regardless of whether the viscosity of the adhesive is high or low. Due to the cause based on the characteristics of the respective viscosities, a pinhole is likely to be formed in the bonding portion, and if the pinhole is formed, there is a problem that the adhesiveness is reduced and the fluid to be filtered leaks. Also, when using a low viscosity adhesive,
Even if a pinhole does not occur, there is also a problem that the effective filtration area of the filter medium 5 is reduced by the suction of the adhesive 20 into the filter medium 5.

【０００９】さらに、図６に示すような渦巻型フィルタ
エレメント１１においては、スペーサ材１９（右端にお
いてはスペーサ材１７）の端面に面したコーキング用溝
１５ｃに接着剤２０を詰め込んで、このスペーサ材１
７，１９の端面を閉塞する。この接着剤２０として既存
の接着剤を用いて閉塞しようとすると、前記と同様の原
因により閉塞部にピンホールができやすいという問題が
あるとともに、粘度の低い接着剤を用いた場合、接着剤
２０が濾材１６，１８やスペーサ材１７，１９に吸い上
げられることにより、濾材１６，１８の実効濾過面積が
小さくなってしまうという問題もある。Further, in the spiral filter element 11 as shown in FIG. 6, an adhesive 20 is packed in a caulking groove 15c facing an end face of a spacer material 19 (spacer material 17 at the right end). 1
The end faces of 7, 19 are closed. When an existing adhesive is used as the adhesive 20 for closing, there is a problem that a pinhole is easily formed in the closed portion due to the same reason as described above, and when an adhesive having a low viscosity is used, the adhesive 20 is used. Is sucked up by the filter media 16 and 18 and the spacer materials 17 and 19, so that the effective filtration area of the filter media 16 and 18 is reduced.

【００１０】本発明はこのような問題に鑑みてなされた
ものであり、シール性および接着性を向上させることが
できる接着剤を提供することを目的とするとともに、濾
紙とエンドプレートとの接着部や、濾材とスペーサ材と
の閉塞部におけるシール性および接着性がよく、且つ、
濾材の濾過面積の減少を抑えることができるフィルタエ
レメントを提供することを目的としている。[0010] The present invention has been made in view of the above problems, and has as its object to provide an adhesive capable of improving the sealing property and the adhesive property, and to provide an adhesive portion between a filter paper and an end plate. Also, the sealing property and adhesion at the closed portion between the filter medium and the spacer material are good, and
It is an object of the present invention to provide a filter element capable of suppressing a decrease in a filtration area of a filter medium.

【００１１】[0011]

【課題を解決するための手段】このような目的を達成す
るために、本発明の接着剤は、粘度が５００〜１０００
００ｃｐと比較的低粘度のエポキシ系接着剤に、親水性
を有する繊維を混入させている。この繊維は、太さが
０.１〜１デニールで長さが１〜１０ｍｍのいわゆる極
細繊維であり、その混入量は０.１〜１重量％とするこ
とが好ましい。In order to achieve the above object, the adhesive of the present invention has a viscosity of 500 to 1000.
An epoxy adhesive having a relatively low viscosity of 00 cp is mixed with fibers having hydrophilicity. These fibers are so-called ultrafine fibers having a thickness of 0.1 to 1 denier and a length of 1 to 10 mm, and the amount of the fibers is preferably 0.1 to 1% by weight.

【００１２】このような接着剤によれば、低粘度のエポ
キシ系接着剤（以下、「基剤」と称する）は、極細繊維
に浸透することによって分散することがなく集合状態が
保たれる。このため、基剤の有する高い接着力を保持し
つつ、接着対象物が濾紙のような基剤を吸い込みやすい
材質であっても接着対象物への吸込量を少なくすること
ができることから、接着部における接着剤の減少を防止
することができる。According to such an adhesive, a low-viscosity epoxy-based adhesive (hereinafter, referred to as a "base") does not disperse by penetrating into ultrafine fibers, and is kept in an aggregated state. For this reason, while maintaining the high adhesive force of the base, the amount of suction into the bonding target can be reduced even when the bonding target is a material that easily absorbs the base, such as filter paper. Can be prevented from being reduced in the adhesive.

【００１３】さらに、基剤に混入された極細繊維によっ
て、接着部に細かい凹凸が形成されるため、接着対象物
が基剤を吸い込まない円滑な表面を有する材質であって
も、高い接着力（保持力）を得ることができる。Further, since fine irregularities are formed in the bonding portion by the ultrafine fibers mixed in the base material, even if the object to be bonded is a material having a smooth surface that does not absorb the base material, a high adhesive strength ( Holding power) can be obtained.

【００１４】なお、基剤に混入する極細繊維としては、
ポリエステル有機繊維を用いることが好ましく、ポリエ
ステル有機繊維を混入させることにより、基剤の集合状
態をよりよく保つことができる。The ultrafine fibers mixed into the base include:
It is preferable to use polyester organic fibers, and by mixing the polyester organic fibers, it is possible to keep the base in a better assembled state.

【００１５】また、前記の目的を達成するために、本発
明のフィルタエレメントは、いわゆる菊花状の濾材と、
この濾材の上下端面にそれぞれ接着するエンドプレート
とを上記の接着剤を用いて接着することとしている。こ
れにより、濾材への基剤の吸い込みを減少させることが
できるため、濾材の濾過面積が減少することがない。ま
た、基剤が比較的低粘度であるため濾材とエンドプレー
トとの間に気泡が生じにくく、極細繊維によって保持さ
れることから接着剤の量が減少することがない。また、
エンドプレートにおける接着面が沿滑であっても、極細
繊維によって形成された細かい凹凸により、濾材とエン
ドプレートとの接着力を向上させることができる。Further, in order to achieve the above object, a filter element of the present invention comprises a so-called chrysanthemum-shaped filter medium,
The end plates that are respectively bonded to the upper and lower end surfaces of the filter medium are bonded using the above-mentioned adhesive. Thereby, the suction of the base material into the filter medium can be reduced, so that the filtration area of the filter medium does not decrease. In addition, since the base material has a relatively low viscosity, air bubbles are hardly generated between the filter medium and the end plate, and the amount of the adhesive does not decrease because the base material is held by the ultrafine fibers. Also,
Even if the adhesive surface of the end plate is smooth, the adhesive force between the filter medium and the end plate can be improved by the fine irregularities formed by the ultrafine fibers.

【００１６】また、前記の目的を達成するために、本発
明のフィルタエレメントは、２枚のスペーサ材のうち一
方のスペーサ材の端部を開放して流体の入口とするとと
もに他方のスペーサ材の端部を本発明の接着剤により閉
塞している。これにより、スペーサ材および濾材への基
剤の吸い込みを減少させることができるため、濾材の濾
過面積が減少することがない。また、基剤が比較的低粘
度であるためスペーサ材と濾材との間に気泡が生じにく
く、極細繊維によって保持されることから接着剤の量が
減少することがない。従って、接着剤によって閉塞した
部分にピンホールが生じることなく、閉塞部分からの流
体の漏れを防止することができる。また、極細繊維によ
って形成された細かい凹凸により、スペーサ材と濾材と
の接着力を向上させることができる。In order to achieve the above object, a filter element according to the present invention provides a fluid inlet by opening an end of one of the two spacer members, and at the same time, the other spacer member. The end is closed by the adhesive of the present invention. Thereby, the suction of the base material into the spacer material and the filter material can be reduced, so that the filtration area of the filter material does not decrease. In addition, since the base material has a relatively low viscosity, bubbles are hardly generated between the spacer material and the filter material, and the amount of the adhesive does not decrease since the base material is held by the ultrafine fibers. Therefore, it is possible to prevent leakage of fluid from the closed portion without generating a pinhole in the portion closed by the adhesive. Moreover, the adhesive force between the spacer material and the filter material can be improved by the fine irregularities formed by the ultrafine fibers.

【００１７】[0017]

【発明の実施の形態】以下、図面に基づいて本発明の好
ましい実施形態である接着剤を用いてフィルタエレメン
トを形成する場合について、図１および図２を参照して
説明する。このフィルタエレメント１は、菊花状エレメ
ントと称され、それぞれ円形開口を有した円盤状の上下
エンドプレート２，３と、多数の小孔が打ち抜き成形さ
れたパンチングメタルからなる円筒状の内筒４と、この
内筒４の外周を覆って配設される濾材５とからなる。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS A preferred embodiment of the present invention in which a filter element is formed using an adhesive will be described below with reference to FIGS. 1 and 2. FIG. The filter element 1 is referred to as a chrysanthemum-shaped element, and has disk-shaped upper and lower end plates 2 and 3 each having a circular opening, and a cylindrical inner cylinder 4 made of a punching metal formed by punching and forming a number of small holes. And a filter medium 5 arranged to cover the outer periphery of the inner cylinder 4.

【００１８】この濾材５は、内筒４の外周面に当接接触
するように円筒状に形成されているが、板状の濾紙を所
定の幅でプリーツ状に形成した後、全体形状が略円筒状
となるように形成されている。これにより、軸方向と直
角な断面形状が菊花状を有して形成され、内周面（菊花
状の内側の稜線）が内筒４に当接することとなる。The filter medium 5 is formed in a cylindrical shape so as to be in contact with the outer peripheral surface of the inner cylinder 4. After the plate-shaped filter paper is formed into a pleated shape with a predetermined width, the overall shape is substantially equal. It is formed so as to be cylindrical. Thereby, the cross-sectional shape perpendicular to the axial direction is formed to have a chrysanthemum flower shape, and the inner peripheral surface (the inner ridge line of the chrysanthemum flower) comes into contact with the inner cylinder 4.

【００１９】このような菊花状エレメント１において
は、図１に示すように、濾材５の円筒形状を保持するた
めに濾材５の上下端部にエンドプレート（図３において
は下エンドプレート３のみを示している）を接着してい
る。この接着を行う場合には、まず下エンドプレート３
の内側空間３ａ内に均一に接着剤１０を充填しておき、
その後、（Ａ）に示すように、接着剤１０上に円筒状に
形成した濾材５を載置する。In such a chrysanthemum-shaped element 1, as shown in FIG. 1, an end plate (in FIG. 3, only the lower end plate 3 is attached) at the upper and lower ends of the filter medium 5 in order to maintain the cylindrical shape of the filter medium 5. (Shown) is adhered. When performing this bonding, first, the lower end plate 3
Adhesive 10 is uniformly filled in the inner space 3a of
Thereafter, as shown in (A), the filter medium 5 formed in a cylindrical shape on the adhesive 10 is placed.

【００２０】接着剤１０は、５００〜１０００００ｃｐ
の比較的低粘度のエポキシ系接着剤を基剤１０ａとし、
この基剤１０ａに、０.１〜１デニールの太さで１〜１
０ｍｍの長さの親水性のポリエステル極細有機繊維（以
下、「極細繊維」と称する）１０ｂを、０.１〜１重量
％混合させることによって作られている。The adhesive 10 has a thickness of 500 to 100,000 cp.
A relatively low-viscosity epoxy adhesive as a base 10a,
The base material 10a has a thickness of 0.1 to 1 denier and a thickness of 1 to 1
It is made by mixing 0.1 to 1% by weight of a hydrophilic polyester ultrafine organic fiber (hereinafter referred to as "ultrafine fiber") 10b having a length of 0 mm.

【００２１】このように作られた接着剤１０において
は、接着剤１０上に濾材５を載置しても、接着剤１０内
には濾材５を構成する濾紙よりも親水性（浸透性）が高
い極細繊維１０ｂが混合されているため、接着剤１０に
濾材５が浸されてもこの濾材５によって基剤１０ａが分
散されることなく、集合が保たれる。In the adhesive 10 thus produced, even if the filter medium 5 is placed on the adhesive 10, the adhesive 10 has a hydrophilicity (permeability) in the adhesive 10 higher than that of the filter paper constituting the filter medium 5. Since the high ultrafine fibers 10b are mixed, even if the filter medium 5 is immersed in the adhesive 10, the base 10a is not dispersed by the filter medium 5 and the assembly is maintained.

【００２２】これにより、図１（Ｂ）に示すように、濾
材５と下エンドプレート３とが接着された状態において
は、接着剤１０内の極細繊維１０ｂが濾材５の下に圧縮
されて残っており、この極細繊維１０ｂによって基剤１
０ａが下エンドプレート３上に残って保持される。従っ
て、濾材５への基剤１０ａの吸い上げ量（浸透量）が少
なくなるため、下エンドプレート３上の接着剤１０の量
が少なくなることがない。このため、濾材５と下エンド
プレート３との間に隙間やピンホールを発生させること
なく、濾材５と下エンドプレート３とをしっかりと接着
することができる。Thus, as shown in FIG. 1B, in a state where the filter medium 5 and the lower end plate 3 are bonded, the ultrafine fibers 10b in the adhesive 10 are compressed under the filter medium 5 and remain. The base material 1 is formed by the ultrafine fibers 10b.
0a remains on the lower end plate 3 and is held. Accordingly, the amount of the base material 10a sucked into the filter medium 5 (permeation amount) is reduced, so that the amount of the adhesive 10 on the lower end plate 3 is not reduced. For this reason, the filter medium 5 and the lower end plate 3 can be firmly bonded without generating a gap or a pinhole between the filter medium 5 and the lower end plate 3.

【００２３】なお、本発明に係る接着剤１０は、基剤１
０ａの粘度が５００ｃｐ〜１０００００ｃｐの範囲であ
り、極細繊維１０ｂの太さが０.１〜１デニールで長さ
が１〜１０ｍｍであるとともに、極細繊維１０ｂの重量
の割合が０.１〜１％の範囲であればよいが、基剤１０
ａの粘度や極細繊維１０ｂの状態（形状・太さ・長さ）
および割合は、濾材５や下エンドプレート３の材質、形
状等に応じて、上記の各範囲内において適宜変更される
ものである。また、極細繊維１０ｂは、必ずしも親水性
のポリエステル極細有機繊維に限られるものではなく、
親水性のガラス繊維等を用いてもよい。The adhesive 10 according to the present invention comprises the base 1
0a is in the range of 500 cp to 100,000 cp, the thickness of the ultrafine fiber 10b is 0.1 to 1 denier, the length is 1 to 10 mm, and the weight ratio of the ultrafine fiber 10b is 0.1 to 1%. The base 10
The viscosity of a and the state of the ultrafine fiber 10b (shape, thickness, length)
The ratio and the ratio are appropriately changed within the above-described ranges according to the material, shape, and the like of the filter medium 5 and the lower end plate 3. The ultrafine fibers 10b are not necessarily limited to hydrophilic polyester ultrafine organic fibers,
You may use hydrophilic glass fiber etc.

【００２４】さらに、本発明に係る接着剤は、必ずしも
上記のようなフィルタエレメントの形成、すなわち、濾
材とエンドプレートの接着を行うためだけに用いられる
ものではなく、他の用途においても用いることができる
のはむろんである。Furthermore, the adhesive according to the present invention is not necessarily used only for forming the filter element as described above, that is, for bonding the filter medium to the end plate, but may be used for other purposes. You can do it.

【００２５】以下、本発明の好ましい実施形態である接
着剤を用いて異なる構成のフィルタエレメントを形成す
る場合について、図３および図４を参照して説明する。
このフィルタエレメント１１は、いわゆる渦巻型フィル
タエレメントと称されるフィルタエレメントである。Hereinafter, a case of forming a filter element having a different configuration using an adhesive according to a preferred embodiment of the present invention will be described with reference to FIGS.
The filter element 11 is a so-called spiral filter element.

【００２６】このフィルタエレメント１１は、渦巻状の
チューブ１４と、このチューブ１４の外周に巻き付けら
れる濾過部材１５とから構成されている。チューブ１４
は、長方形の板材を渦巻状に丸めて形成したものであ
り、濾過部材１５は、２枚の濾材（第１濾材１６および
第２濾材１８）と２枚のスペーサ材（第１スペーサ材１
７および第２スペーサ材１９）とを交互に重ね合わせて
４層に形成されている。The filter element 11 includes a spiral tube 14 and a filter member 15 wound around the outer periphery of the tube 14. Tube 14
Is formed by spirally rolling a rectangular plate material. The filter member 15 includes two filter materials (first filter material 16 and second filter material 18) and two spacer materials (first spacer material 1).
7 and the second spacer material 19) are alternately overlapped to form four layers.

【００２７】第１濾材１６と第２濾材１８は、極細繊維
にて高密度に作られた濾紙からなり、帯状にカットされ
ている。第１スペーサ材１７および第２スペーサ材１９
は、荒い目の網（ポリエステル製の網や金網等）を濾材
１６，１８よりも小さな幅（高さ）で帯状にカットさ
れ、複数枚重ねられたものである。このように各スペー
サ材１７，１９を、網を複数枚重ねて厚みを持たせた構
造とすることにより、所要の強度を確保するとともに、
濾材１６，１８同士の密着を防ぎ、内部をオイル等の流
体が流通しやすいようにしている。The first filter medium 16 and the second filter medium 18 are made of filter paper made of ultra-fine fibers at a high density, and are cut into strips. First spacer material 17 and second spacer material 19
Is obtained by cutting a coarse mesh (such as a polyester mesh or a wire mesh) into a band shape with a width (height) smaller than that of the filter media 16 and 18 and stacking a plurality of the meshes. In this way, by forming the spacer members 17 and 19 into a structure in which a plurality of nets are stacked to have a thickness, the required strength is ensured, and
The filter media 16 and 18 are prevented from adhering to each other so that a fluid such as oil can easily flow through the interior.

【００２８】そして、各スペーサ材１７，１９は、これ
らの上下端が各濾材１６，１８の上下端からそれぞれほ
ぼ同じ高さだけ離れるように配置される。このため、濾
過部材１５がチューブ１４に巻き付けられたときには、
第１スペーサ材１７と第２スペーサ材１９の上下に、濾
材１６，１８により挟まれるコーキング用溝１５ｃが形
成される。The spacer members 17 and 19 are arranged such that their upper and lower ends are separated from the upper and lower ends of each of the filter media 16 and 18 by substantially the same height. For this reason, when the filtering member 15 is wound around the tube 14,
Above and below the first spacer member 17 and the second spacer member 19, a caulking groove 15c sandwiched between the filter members 16 and 18 is formed.

【００２９】このように構成された濾過部材１５は、４
層をまとめてチューブ１４に巻き付けられる。濾過部材
１５のチューブ１４への巻き付けを完了した後は、濾過
部材１５の軸方向一端（図では右端）における第１スペ
ーサ材１７の端面に面したコーキング用溝１５ｃに接着
剤１０を詰め込んで、この第１スペーサ材１７の端面を
閉塞する。なお、第２スペーサ材１９の端面は開放して
おく。一方、濾過部材１５の軸方向他端（図では左端）
における第２スペーサ材１９の端面に面したコーキング
用溝１５ｃに接着剤１０を詰め込んで、この第２スペー
サ材１９の端面を閉塞する。なお、第１スペーサ材１７
の端面は開放しておく。The filtering member 15 thus configured is
The layers are wrapped around tube 14 together. After the winding of the filter member 15 around the tube 14 is completed, the adhesive 10 is packed into the coking groove 15c facing the end surface of the first spacer member 17 at one axial end (right end in the figure) of the filter member 15, The end face of the first spacer member 17 is closed. Note that the end face of the second spacer member 19 is left open. On the other hand, the other axial end of the filtering member 15 (the left end in the figure)
The adhesive 10 is packed in the caulking groove 15c facing the end face of the second spacer material 19 in the above, and the end face of the second spacer material 19 is closed. The first spacer material 17
The end face is left open.

【００３０】こうして濾過部材１５の接着剤１０による
閉塞処理（コーキング）を行った後、濾過部材１５の左
端に第一保持プレート１３ａを取り付け、右端には第二
保持プレート１３ｂを取り付ける。このようにして作ら
れた渦巻型フィルタエレメント１１は、本体１２ａおよ
び蓋１２ｂからなるフィルタケース１２内に配置され
る。After the filtering member 15 is closed (caulked) with the adhesive 10, the first holding plate 13a is attached to the left end of the filtering member 15 and the second holding plate 13b is attached to the right end. The spiral filter element 11 thus produced is disposed in a filter case 12 composed of a main body 12a and a lid 12b.

【００３１】フィルタケース１２の流入口１２ｃからフ
ィルタケース１２内に流入したオイルは、図３中に矢印
で示すように、入口空間ＥＳ内に流入する。このオイル
は、第２スペーサ材１９における右端開口（入口）から
濾過部材１５内に流入する。第２スペーサ材１９内に流
入したオイルは、第２スペーサ材１９を軸方向に流れる
が、左端が接着剤１０によって閉塞されているので、こ
れに隣合う第１・第２濾材１６，１８を通って濾過され
ながら第１スペーサ材１７内に流入する。そして、第１
スペーサ材１７内に流入したオイルは、この第１スペー
サ材１７の右端が接着剤１０によって閉塞されているた
め、左端開口（出口）から流通路ＲＳに流出する。The oil that has flowed into the filter case 12 from the inlet 12c of the filter case 12 flows into the inlet space ES as indicated by the arrow in FIG. This oil flows into the filtering member 15 from the right end opening (inlet) of the second spacer member 19. The oil that has flowed into the second spacer member 19 flows in the second spacer member 19 in the axial direction. However, since the left end is closed by the adhesive 10, the first and second filter members 16 and 18 adjacent to the oil are removed. It flows into the first spacer member 17 while being filtered. And the first
The oil that has flowed into the spacer material 17 flows out of the left end opening (exit) into the flow passage RS because the right end of the first spacer material 17 is closed by the adhesive 10.

【００３２】このように、コーキング用溝１５ｃに詰め
込まれた接着剤１０は、極細繊維１０ｂによって基剤１
０ａがコーキング用溝１５ｃ内に残って保持される。従
って、濾材１６，１８やスペーサ材１７，１９への基剤
１０ａの吸い上げ量（浸透量）が少なくなるため、コー
キング用溝１５ｃ内における接着剤１０の量が少なくな
ることがない。このため、コーキング用溝１５ｃ内にお
いて隙間やピンホールを発生させることなく、濾材１
６，１８やスペーサ材１７，１９を漏れの無いようにし
っかりと接着することができる。As described above, the adhesive 10 packed in the caulking groove 15c is made of the base material 1 by the ultrafine fibers 10b.
0a remains in the caulking groove 15c and is held. Therefore, the amount of the base material 10a sucked up (permeated) into the filter materials 16 and 18 and the spacer materials 17 and 19 is reduced, so that the amount of the adhesive 10 in the caulking groove 15c is not reduced. For this reason, the filter medium 1 does not generate a gap or a pinhole in the caulking groove 15c.
6, 18 and the spacer members 17, 19 can be firmly bonded without leakage.

【００３３】[0033]

【発明の効果】以上説明したように、本発明の接着剤
は、いわゆる低粘度のエポキシ系接着剤に、親水性を有
する極細繊維が混入されている。このため、低粘度のエ
ポキシ系接着剤の有する本来の接着力を低下させること
なく、接着対象物が濾材等の接着剤を吸い込みやすい材
質であっても、接着対象物への吸込量を減少させること
ができる。また、両接着対象物の間に極細繊維に浸透し
たエポキシ系接着剤が分散されることなく保持されるた
め、接着対象物上の接着剤の量が減少することがなく、
接着に必要な量を確保することができるとともに、接着
剤が部分的に少なく（薄く）なってしまうこともない。As described above, in the adhesive of the present invention, a so-called low-viscosity epoxy adhesive is mixed with ultrafine fibers having hydrophilicity. For this reason, even if the object to be bonded is a material such as a filter medium that easily absorbs the adhesive, the amount of suction to the object to be bonded is reduced without lowering the original adhesive strength of the low-viscosity epoxy adhesive. be able to. In addition, since the epoxy-based adhesive that has permeated the microfibers is held between the two bonding objects without being dispersed, the amount of the adhesive on the bonding object does not decrease,
The amount required for the bonding can be ensured, and the amount of the adhesive does not partially decrease (thin).

【００３４】さらに、接着対象物の間に残って保持され
た接着剤内には、極細繊維が圧縮されて残っているた
め、接着対象物との接着面が細かい凹凸を有することと
なり、接着対象物の表面が円滑であっても高い接着力を
得ることができる。Furthermore, since the ultrafine fibers are compressed and remain in the adhesive that is left and held between the objects to be bonded, the surface to be bonded to the object to be bonded has fine irregularities. High adhesive strength can be obtained even if the surface of the object is smooth.

【００３５】従って、このような接着剤を用いて濾材と
エンドプレートとの接着を行ったり、スペーサ材の端部
の閉塞を行うことによりフィルタエレメントを形成した
場合には、濾材とエンドプレート接着部や、スペーサ材
の端部に形成されたコーキング溝においてピンホールが
生じたり、隙間が生じたりすることがないため、濾過す
べき流体の漏れが発生することがない。また、濾材やス
ペーサ材に吸い上げられる接着剤の量が少ないため、濾
材の実効濾過面積が小さくなってしまうこともない。Therefore, when the filter element is formed by bonding the filter medium to the end plate by using such an adhesive or by closing the end of the spacer material, the filter medium and the end plate bonding section Also, since no pinholes or gaps are formed in the caulking groove formed at the end of the spacer material, leakage of the fluid to be filtered does not occur. Further, since the amount of the adhesive sucked up by the filter material and the spacer material is small, the effective filtration area of the filter material does not decrease.

【図面の簡単な説明】[Brief description of the drawings]

【図１】本発明に係る接着剤を用いて濾材とエンドプレ
ートとを接着させることにより形成された本発明に係る
フィルタエレメントの部分断面図である。FIG. 1 is a partial cross-sectional view of a filter element according to the present invention formed by adhering a filter medium and an end plate using an adhesive according to the present invention.

【図２】上記のフィルターエレメントの斜視図である。FIG. 2 is a perspective view of the above filter element.

【図３】上記接着剤を用いてスペーサ材の端部を閉塞す
ることにより形成された本発明に係るフィルタエレメン
トの部分断面図である。FIG. 3 is a partial cross-sectional view of a filter element according to the present invention formed by closing an end of a spacer material using the adhesive.

【図４】上記のフィルターエレメントの断面図である。FIG. 4 is a sectional view of the filter element.

【図５】従来の接着剤を用いてフィルターエレメントを
形成した場合の部分断面図である。FIG. 5 is a partial cross-sectional view when a filter element is formed using a conventional adhesive.

【図６】従来の接着剤を用いて異なるフィルターエレメ
ントを形成した場合の部分断面図である。FIG. 6 is a partial cross-sectional view when a different filter element is formed using a conventional adhesive.

【符号の説明】[Explanation of symbols]

１，１１ フィルターエレメント ２ 上エンドプレート ３ 下エンドプレート ５ 濾材 １０ 接着剤 １０ａ 基剤 １０ｂ 極細繊維 １５ 濾過部材 １６，１８ 濾材 １７，１９ スペーサ材 DESCRIPTION OF SYMBOLS 1,11 Filter element 2 Upper end plate 3 Lower end plate 5 Filter medium 10 Adhesive 10a Base 10b Microfiber 15 Filtration member 16,18 Filter medium 17,19 Spacer material

Claims (4)

【特許請求の範囲】[Claims] 【請求項１】 粘度が５００〜１０００００ｃｐのエポ
キシ系接着剤に、 太さが０.１〜１デニールで長さが１〜１０ｍｍの親水
性を有する繊維を０.１〜１重量％混入させたことを特
徴とする接着剤。1. An epoxy adhesive having a viscosity of 500 to 100,000 cp is mixed with 0.1 to 1% by weight of a hydrophilic fiber having a thickness of 0.1 to 1 denier and a length of 1 to 10 mm. An adhesive characterized in that: 【請求項２】 前記繊維が、ポリエステル有機繊維であ
ることを特徴とする請求項１に記載の接着剤。2. The adhesive according to claim 1, wherein the fibers are polyester organic fibers. 【請求項３】 全体形状が略円筒状の濾材と、この濾材
の上下端面にそれぞれ接着されるエンドプレートとから
なり、 請求項１もしくは請求項２に記載の接着剤により前記濾
材と前記エンドプレートとが接着されていることを特徴
とするフィルタエレメント。3. A filter medium having a substantially cylindrical shape as a whole and end plates respectively bonded to upper and lower end surfaces of the filter medium, wherein the filter medium and the end plate are bonded by the adhesive according to claim 1 or 2. And a filter element, wherein the filter element is bonded to the filter element. 【請求項４】 円筒状に形成されたチューブと、 ２枚のシート状の濾材と２枚の流体を通すシート状のス
ペーサ材とを交互に重ねて４層に形成され、前記チュー
ブに渦巻状に巻き付けられる濾過部材とから構成される
渦巻型のフィルタエレメントであって、 前記濾過部材の軸方向一端において、前記２枚のスペー
サ材のうち一方のスペーサ材の端部を開放して流体の入
口とするとともに他方のスペーサ材の端部を請求項１も
しくは請求項２に記載の接着剤により閉塞し、 前記濾過部材の軸方向他端において、前記一方のスペー
サ材の端部を請求項１もしくは請求項２に記載の接着剤
により閉塞するとともに前記他方のスペーサ材の端部を
開放して流体の出口としたこと特徴とするフィルタエレ
メント。4. A tube formed in a cylindrical shape, and two sheet-like filter media and two sheet-like spacer materials through which two fluids are alternately stacked are formed in four layers, and the tube has a spiral shape. And a filter member wound around the filter member, wherein at one axial end of the filter member, one end of one of the two spacer members is opened to open a fluid inlet. 3. An end of the other spacer material is closed with the adhesive according to claim 1 or 2, and an end of the one spacer material at the other axial end of the filter member. 3. A filter element which is closed by the adhesive according to claim 2 and has an end of the other spacer material opened to form a fluid outlet.