JPH11107153A - Packaging material comprising conjugate filament nonwoven fabric - Google Patents

Packaging material comprising conjugate filament nonwoven fabric

Info

Publication number
JPH11107153A
JPH11107153A JP9264704A JP26470497A JPH11107153A JP H11107153 A JPH11107153 A JP H11107153A JP 9264704 A JP9264704 A JP 9264704A JP 26470497 A JP26470497 A JP 26470497A JP H11107153 A JPH11107153 A JP H11107153A
Authority
JP
Japan
Prior art keywords
nonwoven fabric
packaging material
long
component
hot water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP9264704A
Other languages
Japanese (ja)
Inventor
Takeshi Chizuka
健史 千塚
Fumio Matsuoka
文夫 松岡
Keiko Sakota
恵子 迫田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Unitika Ltd
Original Assignee
Unitika Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Unitika Ltd filed Critical Unitika Ltd
Priority to JP9264704A priority Critical patent/JPH11107153A/en
Publication of JPH11107153A publication Critical patent/JPH11107153A/en
Pending legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain a packaging material free from deterioration of a polymer in conjugate spinning or heat sealing of components having different melting points. SOLUTION: This packaging material comprises a conjugate filament nonwoven fabric in which filaments are melted in dot-like state by softening or melting of sheath component of a core-sheath type conjugate filament using a polypropylene-based polymer as a core component and using a polyethylene- based polymer having lower melting point than the core component as a sheath component. The conjugate filament nonwoven fabric simultaneously satisfies formula I and formula II. The formula I:HWD<=0. 04% and the formula II : HWS<=8%, wherein HWD represents elution ratio of hot water soluble component in subjecting the filament nonwoven fabric to hot water treatment for 10 min by using 98 deg.C hot water in a bath ratio of 1:100 and HWS represents area shrinkage factor of the filament nonwoven fabric in a hot water treatment.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【０００１】[0001]

【発明の属する技術分野】本発明は、複合長繊維不織布
からなる包材に関し、特にコーヒーや紅茶等のためのい
わゆるティーバッグ形式の食品包材に好適に使用できる
複合長繊維不織布からなる包材に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a wrapping material made of a composite long-fiber non-woven fabric, and more particularly to a packaging material made of a composite long-fiber non-woven fabric which can be suitably used as a so-called tea bag type food wrapping material for coffee or tea. About.

【０００２】[0002]

【従来の技術】従来より、靴やバッグ等の皮革製品や電
化製品等の袋状包装材料や食料品の包装材料といった包
材として用いられる不織布としては、ポリエチレン系重
合体を鞘成分とし、前記鞘成分よりも融点の高いポリプ
ロピレン系重合体を芯成分とする芯鞘型の複合長繊維か
らなる不織布が知られている。2. Description of the Related Art Conventionally, a nonwoven fabric used as a packaging material such as a bag-like packaging material such as leather products such as shoes and bags and electric appliances and a packaging material for foodstuffs has a polyethylene-based polymer as a sheath component. 2. Description of the Related Art Nonwoven fabrics made of a core-sheath composite long fiber having a polypropylene-based polymer having a higher melting point than the sheath component as a core component are known.

【０００３】このような不織布を構成する複合長繊維
は、低融点成分と高融点成分とを同時に複合紡糸するこ
とによって得られるが、その際の紡糸温度は、一般に高
融点成分に適した紡糸温度を適用する。しかし、高融点
成分に合わせた紡糸温度では、低融点成分には高すぎる
ため低融点成分はポリマー劣化を生じることとなる。ポ
リマー劣化が生じると、低融点成分中の低分子量成分が
揮発ガスと化して紡糸口金面を汚すことから、紡糸口金
面の汚れを取り除くために操業中に清掃したり、時には
紡糸パックの交換が必要となり、操業性が悪く、コスト
が高くなるという問題点があった。また、複合紡糸され
た繊維には糸曲りが発生して、糸切れ等が生じやすいと
いう問題もあった。さらに、ポリマー劣化が生じると、
複合長繊維の低融点成分中や繊維表面には低分子量成分
が存在するようになるため、このような複合長繊維から
なる不織布を熱水や溶剤等に浸漬すると低分子量成分が
溶出するようになる。また、芯成分を構成するポリプロ
ピレン系重合体は、鞘成分を構成するポリエチレン系重
合体よりは高い融点を有するものの、比較的融点の低い
物質であるため、紡糸温度によってはポリマー劣化をお
こしやすく、上述のように低分子量成分を生じやすい。
従って、このような不織布を成形してコーヒー、紅茶、
お茶、漢方薬等のためのティーバッグ形式の食品包材と
して用いた場合には、低分子量成分が熱水のなかに溶出
して異様な味や異臭がして、コーヒーや紅茶等が本来具
備している風味が生かされないという問題があった。[0003] Composite filaments constituting such a nonwoven fabric can be obtained by simultaneously spinning a low-melting component and a high-melting component at the same time. The spinning temperature at that time is generally a spinning temperature suitable for the high-melting component. Apply However, the spinning temperature adjusted to the high melting point component is too high for the low melting point component, so that the low melting point component causes polymer deterioration. When polymer degradation occurs, low-molecular-weight components in the low-melting-point components are converted into volatile gas and contaminate the spinneret surface.Therefore, it is necessary to clean the spinneret surface during operation to remove dirt, and sometimes replace the spin pack. However, there is a problem that operability is poor and cost is high. In addition, there has been a problem that the yarn spun in the composite spun fiber is liable to be broken and the like. Furthermore, when polymer degradation occurs,
Since the low molecular weight component is present in the low melting point component of the composite long fiber and on the fiber surface, when the nonwoven fabric made of such a composite long fiber is immersed in hot water or a solvent, the low molecular weight component is eluted. Become. In addition, the polypropylene-based polymer constituting the core component has a higher melting point than the polyethylene-based polymer constituting the sheath component, but is a substance having a relatively low melting point. As described above, low molecular weight components are easily generated.
Therefore, such a non-woven fabric is formed into coffee, tea,
When used as a tea bag-type food packaging material for tea, herbal medicine, etc., low molecular weight components elute into hot water and give off strange tastes and odors, and coffee and tea etc. are originally provided. There was a problem that the flavor that was used could not be used.

【０００４】また、包材として用いられる不織布として
は、天然繊維層と熱可塑性繊維層とからなる積層不織布
が提案されているが、このような積層不織布はヒートシ
ール性に劣り、成形性に劣るものであった。そのため、
ヒートシール性を改良するものとして外層に高融点成分
からなる不織布を配置し、内層に低融点成分の短繊維か
らなる不織布を配置した３層からなる積層不織布が実用
新案登録第２５１３１５３号公報に提案されている。し
かしながら、このような積層不織布は、上記芯鞘型の複
合長繊維からなる不織布に比べてコストが高くなり、ま
た、ヒートシール時には高融点成分に適した温度でヒー
トシール処理を行うため、内層の低融点成分はポリマー
劣化を生じ、上述のようにコーヒー、紅茶等のためのテ
ィーバッグ形式の食品包材には不適であるという問題が
あった。As a nonwoven fabric used as a packaging material, a laminated nonwoven fabric comprising a natural fiber layer and a thermoplastic fiber layer has been proposed, but such a laminated nonwoven fabric is inferior in heat sealability and inferior in moldability. Was something. for that reason,
To improve the heat sealing property, a three-layer laminated non-woven fabric in which a non-woven fabric composed of a high melting point component is disposed in an outer layer and a non-woven fabric composed of short fibers having a low melting point component is disposed in an inner layer is proposed in Utility Model Registration No. 251153. Have been. However, the cost of such a laminated nonwoven fabric is higher than that of a nonwoven fabric made of the core-sheath composite long fiber, and the heat sealing process is performed at a temperature suitable for the high melting point component. The low-melting-point component causes polymer deterioration, and as described above, there is a problem that it is unsuitable for a tea bag-type food packaging material for coffee, tea and the like.

【０００５】[0005]

【発明が解決しようとする課題】本発明は、前記問題を
解決し、融点の異なる成分の複合紡糸時やヒートシール
時におけるポリマー劣化のない複合長繊維不織布からな
る包材を提供し、特にコーヒー、紅茶、お茶、漢方薬等
のためのティーバッグ形式の食品包材に好適に使用でき
る複合長繊維不織布からなる包材を提供するものであ
る。SUMMARY OF THE INVENTION The present invention solves the above-mentioned problems and provides a packaging material comprising a composite long-fiber non-woven fabric which is free from polymer deterioration during composite spinning and heat sealing of components having different melting points. The present invention provides a packaging material comprising a composite long-fiber nonwoven fabric that can be suitably used as a food packaging material in the form of a tea bag for black tea, tea, herbal medicine, and the like.

【０００６】[0006]

【課題を解決するための手段】本発明者らは，前記問題
点を解決すべく鋭意検討した結果、本発明に到達したも
のである。すなわち、本発明は、ポリプロピレン系重合
体を芯成分とするとともに、この芯成分よりも融点が低
いポリエチレン系重合体を鞘成分とした芯鞘型の複合長
繊維の鞘成分の軟化あるいは溶融により長繊維相互間が
散点状に融着された複合長繊維不織布からなり、かつ、
前記複合長繊維不織布は下記式及び式を同時に満た
すことを特徴とする複合長繊維不織布からなる包材を要
旨とするものである。なお、下記式及び式において
ＨＷＤは、１：１００の浴比で、９８℃の熱水を用いて
長繊維不織布を１０分間熱水処理した際の熱水可溶成分
の溶出率を表し、ＨＷＳは前記熱水処理時における複合
長繊維不織布の面積収縮率を表すものである。Means for Solving the Problems The present inventors have made intensive studies to solve the above-mentioned problems, and as a result, have reached the present invention. That is, the present invention uses a polypropylene-based polymer as a core component and softens or melts a sheath component of a core-sheath type composite continuous fiber having a polyethylene-based polymer having a lower melting point than the core component as a sheath component. It consists of a composite long-fiber nonwoven fabric in which the fibers are fused in a scattered manner, and
The composite long-fiber nonwoven fabric satisfies the following formulas and the following formulas at the same time. In the following formulas and formulas, HWD represents the elution rate of hot water-soluble components when the long-fiber nonwoven fabric is treated with hot water at 98 ° C. for 10 minutes in a bath ratio of 1: 100, and HWS Represents the area shrinkage rate of the composite long-fiber nonwoven fabric during the hot water treatment.

【０００７】 ＨＷＤ≦０．０４％ ・・・ ＨＷＳ≦８％ ・・・ このように本発明によれば、ポリプロピレン系重合体を
芯成分とし、この芯成分よりも融点が低いポリエチレン
系重合体を鞘成分とした芯鞘型の複合長繊維を用いるこ
とで、ヒートシール性の良い複合長繊維不織布を得るこ
とができる。HWD ≦ 0.04% HWS ≦ 8% As described above, according to the present invention, a polyethylene-based polymer having a polypropylene polymer as a core component and a melting point lower than the core component is used. By using a core-sheath composite long fiber as a sheath component, a composite long-fiber nonwoven fabric having good heat sealability can be obtained.

【０００８】また、前記複合長繊維の鞘成分の軟化ある
いは溶融により長繊維相互間が散点状に融着されるので
あるが、その融着区域では、鞘成分は軟化あるいは溶融
しているものの、芯成分はそのままの状態あるいは若干
変形した状態で繊維形態を維持しているため、前記不織
布は形態保持性や不織布の曲げ易さやハンドリングが良
く、包材として好適に使用できるものとなる。In addition, the sheath components of the composite filaments are fused or melted in a scattered manner by the softening or melting of the sheath components. In the fusion zone, the sheath components are softened or melted. Since the core component maintains the fiber form as it is or is slightly deformed, the nonwoven fabric has good shape retention, easy bending of the nonwoven fabric, and good handling, and can be suitably used as a packaging material.

【０００９】また、この複合長繊維不織布の熱水可溶成
分の溶出率ＨＷＤを０．０４％以下となるように調整す
ることで、熱水中や溶剤中へのポリプロピレン系重合体
およびポリエチレン系重合体の低分子量成分の溶出をほ
とんど無くし、コーヒーや紅茶等のためのティーバッグ
等のように熱水中で使用する食品包材に用いてもポリエ
チレン系重合体特有の異臭がすることがなくなる。さら
に、熱水処理時における複合長繊維不織布の面積収縮率
ＨＷＳを８％以下とすることで、収縮による破損やそれ
に伴う内容物の露出や破損等も解消される。Further, by adjusting the elution rate HWD of the hot water-soluble component of the composite continuous fiber nonwoven fabric to 0.04% or less, the polypropylene-based polymer and the polyethylene-based polymer in hot water or a solvent can be used. Eliminates the elution of low molecular weight components of the polymer, and eliminates the peculiar smell of polyethylene-based polymers even when used in food packaging used in hot water such as tea bags for coffee and tea . Further, by setting the area shrinkage HWS of the composite long-fiber nonwoven fabric at the time of hot water treatment to 8% or less, breakage due to shrinkage and accompanying exposure or breakage of contents are also eliminated.

【００１０】従って、ヒートシール性が良くて成形性に
優れた複合長繊維不織布からなるうえに、融点の異なる
成分の複合紡糸時やヒートシール時におけるポリマー劣
化を無くした包材を提供でき、このため低分子量成分の
熱水への溶出の問題が解消されるため、コーヒー、紅茶
等のためのティーバッグ形式の食品包材に好適に使用で
きる複合長繊維不織布からなる包材を提供することがで
きる。[0010] Accordingly, it is possible to provide a packaging material which is made of a composite long-fiber non-woven fabric having excellent heat sealability and excellent moldability, and which is free from polymer deterioration during composite spinning and heat sealing of components having different melting points. Therefore, since the problem of elution of low molecular weight components into hot water is solved, it is possible to provide a packaging material made of a composite long-fiber nonwoven fabric that can be suitably used for a tea bag type food packaging material for coffee, tea, and the like. it can.

【００１１】[0011]

【発明の実施の形態】次に、本発明を詳細に説明する。
本発明における複合長繊維からなる包材は、芯鞘型複合
長繊維を構成繊維とするものである。前記芯鞘型複合長
繊維は、芯成分にはポリプロピレン系重合体が用いら
れ、鞘成分としては、このポリプロピレン成分よりも融
点の低いポリエチレン系重合体が用いられる。このよう
な成分からなる芯鞘型の複合長繊維であれば、その断面
形状は芯成分と鞘成分とが同心であっても偏芯であって
もよい。このような芯鞘型複合長繊維を熱処理して低融
点成分である鞘成分を軟化あるいは溶融させることによ
り長繊維相互間を散点状に融着して複合長繊維不織布が
形成される。Next, the present invention will be described in detail.
The packaging material made of the composite long fiber according to the present invention has a core-sheath type composite long fiber as a constituent fiber. In the core-sheath type composite long fiber, a polypropylene-based polymer is used as a core component, and a polyethylene-based polymer having a lower melting point than the polypropylene component is used as a sheath component. As long as it is a core-sheath composite long fiber composed of such components, the cross-sectional shape may be such that the core component and the sheath component are concentric or eccentric. Such a core-sheath type composite filament is heat-treated to soften or melt the sheath component, which is a low melting point component, so that the filaments are fused in a scattered manner to form a composite filament nonwoven fabric.

【００１２】前記複合長繊維からなる不織布は、１：１
００の浴比で、９８℃の熱水を用いて長繊維不織布を１
０分間熱水処理した際の熱水可溶成分の溶出率ＨＷＤが
０．０４％以下である必要があり、好ましくは、０．０
２％以下、より好ましくは０．０１％以下、さらに好ま
しくは、０．００８％以下とすることが望ましい。熱水
可溶成分の溶出率ＨＷＤが０．０４％を超えると、前記
複合長繊維からなる不織布を、例えばコーヒーや紅茶等
のティーバッグのように熱水中で使用する食品包材に用
いた場合に、低融点成分中の低分子量成分が熱水中に溶
出して異臭等を発し、コーヒーや紅茶等の風味や香り等
を損なうこととなる。また、前記熱水処理時における面
積収縮率ＨＷＳは８％以下である必要があり、好ましく
は、７％以下、より好ましくは６％以下、さらに好まし
くは、５％以下であることが望ましい。熱水処理時にお
ける複合長繊維不織布の面積収縮率ＨＷＳが８％を超え
ると、熱水中で使用した場合に大きく収縮してしまい、
前記と同様にコーヒーや紅茶等のティーバッグとして用
いた場合には、内容物の流動によるエキスの抽出が不完
全となったり、時には包材が収縮に伴って破損して、内
容物が露出したり飛び散ったりするという問題が生じ
る。なお本発明における複合長繊維不織布は、熱水可溶
成分の溶出率ＨＷＤおよび面積収縮率ＨＷＳの値が上記
範囲を同時に満たす必要がある。[0012] The non-woven fabric composed of the composite filaments is 1: 1.
In a bath ratio of 00, the long-fiber nonwoven fabric is heated to 1 using hot water of 98 ° C.
The elution rate HWD of the hot water-soluble component after the hot water treatment for 0 minute needs to be 0.04% or less, preferably 0.04% or less.
It is desirable that the content be 2% or less, more preferably 0.01% or less, and still more preferably 0.008% or less. When the elution rate HWD of the hot water-soluble component exceeds 0.04%, the nonwoven fabric made of the composite long fiber is used for a food packaging material used in hot water such as a tea bag for coffee or tea. In this case, the low-molecular-weight component in the low-melting-point component is eluted into the hot water and emits an unusual odor, which impairs the flavor and aroma of coffee and tea. Further, the area shrinkage HWS during the hot water treatment needs to be 8% or less, preferably 7% or less, more preferably 6% or less, and further preferably 5% or less. If the area shrinkage ratio HWS of the composite long-fiber nonwoven fabric during hot water treatment exceeds 8%, the nonwoven fabric shrinks greatly when used in hot water,
When used as a tea bag for coffee or black tea as described above, the extraction of the extract due to the flow of the contents becomes incomplete, and sometimes the packaging material is damaged due to shrinkage, and the contents are exposed. Or splatters. In the composite long-fiber nonwoven fabric according to the present invention, the elution rate HWD and the area shrinkage rate HWS of the hot water-soluble component must satisfy the above ranges at the same time.

【００１３】前記複合長繊維からなる不織布の熱水可溶
成分の溶出率ＨＷＤ及び面積収縮率ＨＷＳを本発明の範
囲とするためには、複合紡糸時やヒートシール時におけ
る低融点成分のポリマー劣化を防止することが必要とな
る。本発明においては、低融点成分のポリマー劣化を防
止するために、前記複合長繊維不織布を構成する芯鞘型
複合長繊維の少なくとも鞘成分には、酸化防止を目的と
して融点が１４０℃以上のフェノール系添加剤を添加
し、触媒等を不活性化させる目的で中和剤を添加するこ
とが好ましい。このように前記フェノール系添加剤が配
合されると、ポリマーの酸化分解が抑制されて耐熱性が
向上し、前記中和剤が添加されると、ポリマー重合時の
触媒等に起因する残存酸性物質が不活性化するため、ポ
リマー劣化を抑制することができる。また、芯成分を構
成するポリプロピレン系重合体は鞘成分を構成するポリ
エチレン系重合体よりは高い融点を有するものの、比較
的融点の低い物質であるため、鞘成分だけでなく芯成分
にも前記フェノール系添加剤と中和剤とを添加すること
で、より一層ポリマー劣化が抑制されて耐熱性が向上す
るため、コーヒーや紅茶等のためのティーバッグ等のよ
うに熱水中で使用する食品包材に用いても、ポリマー劣
化により生じた低分子量成分が熱水中に溶出して異臭等
を発生することが無くなる。すなわち、芯鞘型複合長繊
維の少なくとも鞘成分に、融点が１４０℃以上のフェノ
ール系添加剤と中和剤とを添加することで、溶融紡糸中
の高い温度履歴や不織布形態を保持させるための熱接着
工程においてもポリマーの酸化劣化が防止され、さらに
触媒等に起因する残存酸性物質が不活性化されて、ポリ
マー劣化により生じる低分子量成分が減少するため、熱
安定性が向上し、熱水や溶剤中においても低融点成分中
の低分子量成分が溶出されないようにすることができ
る。フェノール系添加剤の融点が１４０℃未満である
と、溶融紡糸時に、紡糸口金からポリマー糸条として開
放された際に添加剤がほどんど気化してしまい、その後
の工程においてポリマーの酸化防止を行うことができな
くなり、ポリマー劣化が生じやすくなる。また、中和剤
が配合されないと、ポリマー重合時に使用した触媒の完
全中和が不可能となり、残存触媒に起因する酸性物質を
不活性化することができなくなり、ポリマー劣化を生じ
やすくなる。従って、いずれの場合もコーヒーや紅茶等
のためのティーバッグ等のように熱水中で使用する食品
包材として用ると、低分子量成分の熱水中への溶出が起
こりやすくなり、好適に使用できなくなることもある。In order to make the dissolution rate HWD and the area shrinkage rate HWS of the hot water-soluble component of the nonwoven fabric composed of the composite filaments fall within the scope of the present invention, the polymer degradation of the low melting point component during composite spinning or heat sealing. Must be prevented. In the present invention, in order to prevent deterioration of the polymer of the low melting point component, at least the sheath component of the core-sheath type conjugate long fiber constituting the conjugate long fiber nonwoven fabric has a phenol having a melting point of 140 ° C or higher for the purpose of preventing oxidation. It is preferable to add a neutralizing agent for the purpose of adding a system additive and inactivating a catalyst or the like. When the phenolic additive is blended in this way, the oxidative decomposition of the polymer is suppressed and the heat resistance is improved, and when the neutralizing agent is added, the residual acidic substance due to a catalyst or the like at the time of polymerizing the polymer. Is inactivated, so that polymer deterioration can be suppressed. Further, although the polypropylene polymer constituting the core component has a higher melting point than the polyethylene polymer constituting the sheath component, it is a substance having a relatively low melting point, so that not only the sheath component but also the phenol is contained in the core component. By adding a system additive and a neutralizing agent, the deterioration of the polymer is further suppressed and the heat resistance is improved, so that a food package used in hot water such as a tea bag for coffee or tea etc. Even when used as a material, low molecular weight components generated by polymer deterioration do not elute into hot water and generate no odor or the like. That is, by adding a phenolic additive having a melting point of 140 ° C. or more and a neutralizing agent to at least the sheath component of the core-sheath type composite filament, a high temperature history during melt spinning and a nonwoven fabric form are retained. Also in the heat bonding step, the polymer is prevented from being oxidized and degraded, and the residual acidic substances caused by the catalyst and the like are inactivated, and the low molecular weight components generated by the polymer degradation are reduced. It is possible to prevent the low-molecular-weight component in the low-melting-point component from being eluted even in a solvent or a solvent. If the melting point of the phenolic additive is lower than 140 ° C., the additive is almost vaporized when being released from the spinneret as a polymer yarn during melt spinning, and the polymer is prevented from being oxidized in a subsequent step. And deterioration of the polymer is likely to occur. Further, if the neutralizing agent is not blended, complete neutralization of the catalyst used at the time of polymer polymerization becomes impossible, so that it becomes impossible to inactivate the acidic substance caused by the remaining catalyst, and the polymer is easily deteriorated. Therefore, in any case, when used as a food packaging material used in hot water such as a tea bag for coffee or black tea, the low-molecular weight components easily elute into the hot water, and are preferably used. You may not be able to use it.

【００１４】また、さらにポリマー劣化が起こりにくく
するために、前記複合長繊維不織布を構成する芯鞘型複
合長繊維の鞘成分には、パーキンエルマー社製の熱重量
計（型番ＴＧＡ−７）を用いて、昇温速度が２０℃／分
で２３０℃の空気中の雰囲気下で測定した熱減量率が５
％以下であるポリエチレン系重合体を用いることが好ま
しい。この熱減量率は少ないほど包材として適してお
り、食品用包材としては３％以下であることが望まし
い。Further, in order to further prevent polymer deterioration, a thermogravimeter (model number TGA-7) manufactured by PerkinElmer Co., Ltd. is used as a sheath component of the core-sheath type composite long fiber constituting the nonwoven fabric. The rate of heat loss measured in an atmosphere of air at 230 ° C. at a rate of temperature increase of 20 ° C./min was 5
% Is preferably used. The smaller the heat loss rate is, the more suitable it is as a packaging material, and it is desirable that it is 3% or less for a food packaging material.

【００１５】ポリエチレン系重合体の熱減量率を５％以
下とすることで、上述のように複合紡糸時やヒートシー
ル時におけるポリマー劣化が起こりにくくなり、紡糸口
金面の汚染や糸曲りの派生による糸切れを解消し、また
コーヒー、紅茶等のためのティーバッグ形式の食品包材
として用いても低分子量成分の熱水中への溶出が解消さ
れることとなる。熱減量率が５％を超えると、複合紡糸
時やヒートシール時にポリマー劣化が起こり、コーヒ
ー、紅茶等のティーバッグ形式の食品包材としては不向
きとなる。By setting the heat loss rate of the polyethylene polymer to 5% or less, deterioration of the polymer during composite spinning and heat sealing hardly occurs as described above, resulting in contamination of the spinneret surface and derivation of yarn bending. Even when used as a food bag in the form of a tea bag for coffee, black tea, etc., elution of low molecular weight components into hot water is eliminated. When the heat loss rate exceeds 5%, the polymer deteriorates at the time of composite spinning or heat sealing, and is not suitable for a tea bag type food packaging material such as coffee and black tea.

【００１６】上記のように構成された芯鞘型複合長繊維
からなる不織布は、縦方向の不織布の強力が（以下「引
張強力ＭＤ」と称す。）５ｋｇ／５ｃｍ幅以上、横方向
（以下「引張強力ＣＤ」と称す。）の不織布の強力が１
ｋｇ／５ｃｍ幅以上であることが好ましい。ここで、引
張強力ＭＤと引張強力ＣＤは、不織布の縦方向と横方向
の最大強力値を示すものである。引張強力ＭＤが５ｋｇ
／５ｃｍ幅より小さいと、包装した際の強力不足が生じ
て内容物が飛散する場合がある。また、引張強力ＣＤは
引張強力ＭＤよりも低くてよいが、１ｋｇ／５ｃｍ幅よ
り小さいと不織布の横方向で伸長されることが少なくな
り、包装される内容物が破れて出てくることとなる。そ
のため、好ましくは引張強力ＭＤが７ｋｇ／５ｃｍ幅以
上、さらに好ましくは９ｋｇ／５ｃｍ幅以上であること
が望ましい。また引張強力ＣＤについては、好ましくは
２ｋｇ／５ｃｍ幅以上、さらに好ましくは３ｋｇ／５ｃ
ｍ幅以上であることが望ましい。In the nonwoven fabric composed of the core-sheath composite long fibers constituted as described above, the strength of the nonwoven fabric in the longitudinal direction (hereinafter referred to as "tensile strength MD") is 5 kg / 5 cm or more in width and the transverse direction (hereinafter referred to as "tensile strength MD"). The tensile strength of the nonwoven fabric is 1).
Preferably, the width is at least kg / 5 cm. Here, the tensile strength MD and the tensile strength CD indicate the maximum strength values in the machine direction and the transverse direction of the nonwoven fabric. Tensile strength MD is 5kg
If the width is smaller than / 5 cm, there is a case where the content is scattered due to insufficient strength at the time of packaging. Further, the tensile strength CD may be lower than the tensile strength MD, but if it is smaller than 1 kg / 5 cm width, the nonwoven fabric is less likely to be stretched in the lateral direction, and the packaged contents will be broken. . Therefore, it is desirable that the tensile strength MD is preferably 7 kg / 5 cm width or more, more preferably 9 kg / 5 cm width or more. The tensile strength CD is preferably 2 kg / 5 cm width or more, more preferably 3 kg / 5 c.
It is desirable that the width is not less than m width.

【００１７】本発明における芯鞘型複合長繊維の鞘成分
に用いるポリエチレン系重合体としては、ポリエチレン
あるいはエチレンを主体とする共重合体が挙げられる。
ポリエチレンとしては、線状低密度ポリエチレン、中密
度ポリエチレン、高密度ポリエチレン等が挙げられ、Ａ
ＳＴＭ−Ｄ−１２３８Ｅに記載の方法で測定したメルト
インデックス値が１０〜８０ｇ／１０分であることが好
ましい。メルトインデックス値が１０ｇ／１０分より小
さいと溶融粘度が高過ぎて高速製糸性が得られず、ま
た、メルトインデックス値が８０ｇ／１０分を超えると
溶融粘度が低過ぎてヌメリ感が発生したり、繊維の冷却
が十分行われず繊維同士が密着して芯鞘型の長繊維が得
られなくなる。The polyethylene polymer used for the sheath component of the core-sheath type composite long fiber in the present invention includes polyethylene or a copolymer mainly composed of ethylene.
Examples of the polyethylene include linear low-density polyethylene, medium-density polyethylene, and high-density polyethylene.
The melt index value measured by the method described in STM-D-1238E is preferably 10 to 80 g / 10 minutes. If the melt index value is less than 10 g / 10 minutes, the melt viscosity is too high to obtain high-speed spinning properties, and if the melt index value exceeds 80 g / 10 minutes, the melt viscosity is too low and a slimy feeling may occur. In addition, the fibers are not sufficiently cooled, and the fibers adhere to each other, so that a core-sheath type long fiber cannot be obtained.

【００１８】芯成分に用いるポリプロピレン系重合体と
しては、ポリプロピレンあるいはプロピレンを主体とす
るポリプロピレン系重合体が挙げられる。ポリプロピレ
ンの粘度としては、ＡＳＴＭ−Ｄ−１２３８Ｌに記載の
方法で測定したメルトフローレート値が２０〜７０ｇ／
１０分であることが好ましい。メルトフローレート値が
２０ｇ／１０分未満であると溶融粘度が高過ぎて高速製
糸性が得られず、また、メルトフローレート値が７０ｇ
／１０分を超えると溶融粘度が低過ぎて、ヌメリ感が発
生したり、繊維の冷却が利かず密着を生じるためであ
る。Examples of the polypropylene polymer used for the core component include polypropylene or a polypropylene polymer mainly composed of propylene. As the viscosity of the polypropylene, the melt flow rate measured by the method described in ASTM-D-1238L is 20 to 70 g /
Preferably, it is 10 minutes. If the melt flow rate value is less than 20 g / 10 minutes, the melt viscosity is too high to obtain high-speed spinning properties, and the melt flow rate value is 70 g.
If the time exceeds / 10 minutes, the melt viscosity is too low, and a slimy feeling is generated, and the cooling of the fiber is not effective, resulting in adhesion.

【００１９】なお、上記鞘成分を構成するポリエチレン
や芯成分を構成するポリプロピレン中には、必要に応じ
て、艶消し剤、顔料、光り安定剤、熱安定剤、酸化防止
剤、結晶化促進剤等の各種添加剤を本発明の目的を損な
わない範囲で添加してもよい。In the polyethylene constituting the sheath component and the polypropylene constituting the core component, if necessary, a matting agent, a pigment, a light stabilizer, a heat stabilizer, an antioxidant, a crystallization accelerator may be used. And the like may be added within a range that does not impair the purpose of the present invention.

【００２０】上記鞘成分を構成するポリエチレンと芯成
分を構成するポリプロピレンとを複合紡糸する際の芯成
分と鞘成分との重量比は、芯成分１に対して鞘成分が
０．１〜５重量部であるのが好ましく、特に０．２〜４
重量部であることが好ましい。鞘成分は、融着区域にお
いて複合長繊維相互間を融着させる成分であるため、そ
の重量割合が０．１重量部未満になると、融着が不十分
となり、不織布の引張強力が低くなる。一方鞘成分が５
重量部を超えると、融着区域における融着が激しくなっ
て、融着区域中において繊維形態を維持している箇所の
割合が少なくなり、風合いが硬くなると共に不織布強力
が低下する。The weight ratio of the core component to the sheath component in the composite spinning of the polyethylene constituting the sheath component and the polypropylene constituting the core component is such that the ratio of the sheath component to the core component is 0.1 to 5% by weight. Part, especially 0.2-4
It is preferably in parts by weight. Since the sheath component is a component for fusing between the composite long fibers in the fusion zone, if the weight ratio is less than 0.1 part by weight, fusion will be insufficient and the tensile strength of the nonwoven fabric will be low. On the other hand, the sheath component is 5
When the amount is more than the weight part, the fusion in the fusion zone becomes severe, the proportion of the portion maintaining the fiber form in the fusion zone decreases, the hand becomes hard and the strength of the nonwoven fabric decreases.

【００２１】上述のように、本発明に用いられる融点が
１４０℃以上のフェノール系添加剤は、ポリマーや複合
長繊維の酸化分解を抑制して耐熱性を向上させる作用を
有するものである。詳細に説明すると、一般的に、ポリ
マーは溶融時や成形加工時や実使用時の各種条件下にお
いて劣化が進行しやすく、このポリマー劣化は、熱や紫
外線などによって誘発される自動酸化により生じる。こ
のようなポリマーの酸化劣化を防止するためには、ラジ
カルの発生を防ぎ、ラジカルを補足して自動酸化のサイ
クルを停止させることが重要となる。そのため本発明に
おいては、この酸化劣化を抑えるために各種の酸化防止
剤を適用することも可能であるが、酸化分解反応の抑制
効果を高めるために、特に融点が１４０℃以上のフェノ
ール系添加剤を用いる。フェノール系添加剤の融点が１
４０℃よりも低い場合には、防止口金からポリマー糸条
が開放された際に殆ど気化されて、それ以降の工程では
殆ど存在しないため、ポリマーの酸化分解を抑制するこ
とが難しくなる。As described above, the phenolic additive having a melting point of 140 ° C. or more used in the present invention has an effect of suppressing the oxidative decomposition of a polymer or a composite filament and improving the heat resistance. More specifically, in general, a polymer tends to deteriorate under various conditions during melting, molding, and actual use, and the polymer deterioration is caused by autoxidation induced by heat, ultraviolet rays, and the like. In order to prevent such a polymer from being oxidized and degraded, it is important to prevent the generation of radicals and stop the autoxidation cycle by capturing the radicals. Therefore, in the present invention, various antioxidants can be applied to suppress the oxidative degradation, but in order to enhance the effect of suppressing the oxidative decomposition reaction, in particular, a phenol additive having a melting point of 140 ° C. or higher. Is used. Melting point of phenolic additive is 1
When the temperature is lower than 40 ° C., the polymer yarn is almost vaporized when the prevention spinneret is opened and hardly exists in the subsequent steps, so that it becomes difficult to suppress the oxidative decomposition of the polymer.

【００２２】上述のような融点が１４０℃以上のフェノ
ール系添加剤としては、具体的には、１，３，５−トリ
メチル−２，４，６−トリス（３，５−ジ−ｔ−ブチル
−４−ヒドロキシベンジル）ベンゼン（融点２４０℃）
やトリス（３，５−ジ−ｔ−ブチル−４−ヒドロキシベ
ンジル）−イソシアヌレート（融点２２０℃）及び１，
３，５−トリス（４−ｔ−ブチル−３−ヒドロキシ−
２，６−ジメチルベンジル）イソシアヌル酸（融点１５
０℃）等が挙げられる。中でも、１，３，５−トリス
（４−ｔ−ブチル−３−ヒドロキシ−２，６−ジメチル
ベンジル）イソシアヌル酸（融点１５０℃）が酸化劣化
を防止する観点から最も好適に使用できる。Examples of the above-mentioned phenolic additives having a melting point of 140 ° C. or more include 1,3,5-trimethyl-2,4,6-tris (3,5-di-t-butyl). -4-Hydroxybenzyl) benzene (melting point 240 ° C)
And tris (3,5-di-t-butyl-4-hydroxybenzyl) -isocyanurate (melting point 220 ° C.) and 1,
3,5-tris (4-t-butyl-3-hydroxy-
2,6-dimethylbenzyl) isocyanuric acid (mp 15
0 ° C.). Among them, 1,3,5-tris (4-t-butyl-3-hydroxy-2,6-dimethylbenzyl) isocyanuric acid (melting point 150 ° C.) can be most preferably used from the viewpoint of preventing oxidative deterioration.

【００２３】また、上述のように本発明に用いられる中
和剤は、ポリマー重合時に使用したチーグラーナッタ触
媒等に起因するポリマー中の残存酸性物質に作用してこ
れを不活性化させるものである。一般的に用いることが
できる中和剤としては、ステアリン酸（融点５０℃）、
ビス（２−フェノキシプロピオニルハイドラザイド）イ
ソフタル酸（融点２２５℃）、３−（Ｎ−サリシロイ
ル）アミノ１，２，４トリアゾール（融点３２５℃）、
ＮＮ’−ビス［３−（３，５−ジ−ｔ−ブチル−４−ヒ
ドロキシフェニル）プロピオニル］ヒドラジン（融点２
２７℃）等が挙げられるが、本発明においては、無機系
の中和剤が好適に使用できる。無機系の中和剤はポリマ
ー中の残存酸性物質を不活性化させる作用が高く、ま
た、融点を保持していないため溶融紡糸時やそれ以降の
熱加工工程等やその他各種の条件下においても溶融する
ことがなく、中和剤としての効果を十二分に発揮するこ
とができる。このような効果を奏する無機系の中和剤と
しては、ハイドロタルサイトやこれを合成したハイドロ
タルサイト類化合物が挙げられ、ハイドロタルサイトと
しては天然鉱物であるMg6Al2(OH)16CO3・4H2Oが、ハイド
ロタルサイト類化合物としてはMg4.5Al2(OH)13CO3・3.5H
2Oが好適に使用できる。Further, as described above, the neutralizing agent used in the present invention acts on the remaining acidic substance in the polymer caused by the Ziegler-Natta catalyst or the like used at the time of polymer polymerization and inactivates it. . Commonly used neutralizing agents include stearic acid (melting point 50 ° C.),
Bis (2-phenoxypropionyl hydrazide) isophthalic acid (melting point 225 ° C.), 3- (N-salicyloyl) amino 1,2,4 triazole (melting point 325 ° C.),
NN'-bis [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionyl] hydrazine (melting point 2
27 ° C.). In the present invention, an inorganic neutralizing agent can be suitably used. The inorganic neutralizing agent has a high effect of inactivating residual acidic substances in the polymer, and does not maintain a melting point, so that it can be used during melt spinning, a subsequent thermal processing step, and other various conditions. Without melting, the effect as a neutralizing agent can be sufficiently exhibited. Examples of the inorganic neutralizing agent having such an effect include hydrotalcite and hydrotalcite compounds synthesized therefrom, and hydrotalcite is a natural mineral such as Mg 6 Al 2 (OH) 16 CO 3 · 4H 2 O, and examples of the hydrotalcite compound Mg 4.5 Al 2 (OH) 13 CO 3 · 3.5H
2 O can be suitably used.

【００２４】フェノール系添加剤と中和剤とのポリエチ
レン系重合体またはポリプロピレン系重合体に対する配
合割合は、それぞれ２００ｐｐｍ〜１０００ｐｐｍの範
囲であることが好ましく、その重量比は、（フェノール
系添加剤）／（中和剤）＝１／２〜２／１とすることが
好ましい。前記範囲において、フェノール系添加剤の配
合割合が２００ｐｐｍより少なくなると、ポリエチレン
系重合体およびポリプロピレン系重合体の耐熱効果が低
下する傾向にあり、また、フェノール系添加剤の配合割
合が１０００ｐｐｍを超えると、フェノール系添加剤の
熱分解による紡糸中の発煙が多くなり、紡糸環境を汚す
こととなる。また、中和剤の配合量が２００ｐｐｍより
少なくなると、重合時に用いられる触媒から派生する酸
成分の中和ができなくなり、紡糸ラインや熱圧着工程で
のロールの腐食、あるいは包材形成工程での機材の腐食
が生じる。また、中和剤の配合量が１０００ｐｐｍを超
えると、製糸性が低下したり、コストが高くなるために
操業性や経済性の面からも好ましくない。The mixing ratio of the phenolic additive and the neutralizing agent to the polyethylene polymer or the polypropylene polymer is preferably in the range of 200 ppm to 1000 ppm, and the weight ratio thereof is (phenolic additive). / (Neutralizer) = 1/2 to 2/1 In the above range, when the blending ratio of the phenolic additive is less than 200 ppm, the heat resistance effect of the polyethylene polymer and the polypropylene polymer tends to decrease, and when the blending ratio of the phenolic additive exceeds 1000 ppm. In addition, smoke generated during spinning due to thermal decomposition of the phenolic additive increases, and the spinning environment is polluted. On the other hand, if the amount of the neutralizing agent is less than 200 ppm, it becomes impossible to neutralize the acid component derived from the catalyst used during the polymerization, and the corrosion of the roll in the spinning line or the thermocompression bonding process, or in the packaging material forming process. Corrosion of equipment occurs. On the other hand, when the compounding amount of the neutralizing agent exceeds 1000 ppm, the spinning property is lowered and the cost is increased, which is not preferable in terms of operability and economic efficiency.

【００２５】芯鞘型複合繊維の単糸繊度は、１〜１５デ
ニールの範囲であることが好ましい。単糸繊度が１５デ
ニールを超えると長繊維の剛性が高くなり、包材として
使用する場合に粗硬感が強くなり、その用途が限定され
てしまう。また溶融紡糸工程において、紡出糸条の冷却
固化に支障を来すこともあるため好ましくない。また、
単糸繊度が１デニールより小さいと、紡糸操業性が低下
してコスト高になるため好ましくない。The single-filament fineness of the core-sheath type composite fiber is preferably in the range of 1 to 15 denier. If the single-fiber fineness exceeds 15 denier, the rigidity of the long fiber becomes high, and when used as a packaging material, the coarse and hard feeling becomes strong, and its use is limited. In addition, in the melt spinning step, it is not preferable because cooling and solidification of the spun yarn may be hindered. Also,
If the single-filament fineness is smaller than 1 denier, the spinning operability is lowered and the cost is increased.

【００２６】なお、長繊維を紡糸するときの単孔吐出量
と牽引速度とをコントロールすることによって、本発明
の面積収縮率の範囲内で長繊維の単糸繊度及び包材の目
の詰まり具合を任意に設定することができる。By controlling the single hole discharge amount and the drawing speed when spinning the long fiber, the fineness of the single fiber of the long fiber and the degree of clogging of the packaging material are controlled within the range of the area shrinkage of the present invention. Can be set arbitrarily.

【００２７】芯鞘型複合長繊維に熱処理を施した際に形
成される、鞘成分の軟化あるいは溶融による長繊維相互
間の散点状の融着区域の形状は、丸型、楕円型、スリッ
ト型、十字型、十葉型、三角型、三葉型、四角、五角、
六角、八角型、ひし形、Ｔ型、井型、長方形四葉、五
葉、六葉、八葉型、卍型等の任意の形態のもので良く、
この散点状に多数設けられた融着区域の模様は、走査型
電子顕微鏡を用いて不織布の小片を拡大撮影することに
より測定される。前記走査型電子顕微鏡を用いて測定さ
れた最小繰返単位の面積に対して点圧着されている部分
の面積の総和の比率を個々に１０回測定したときの平均
値を圧着面積率といい、本発明における不織布の圧着面
積率は３〜５０％であることが好ましい。圧着面積率が
３％より小さいと不織布の柔軟性は向上するが不織布強
力が低下し、不織布が擦れた場合に毛羽立ちが発生し易
くなり実用的な面で問題がある。また、圧着面積率が５
０％を超えると、不織布自体が極めて硬くなりハンドリ
ングが悪くなる。従ってより好ましくは、圧着面積率が
５〜４０％である。The shape of the scattered fusion zone between the long fibers formed by softening or melting of the sheath component formed when the core-sheath type composite long fiber is subjected to heat treatment is round, elliptical, or slit. Type, cross, ten leaf, triangle, three leaf, square, pentagon,
Hex, octagon, diamond, T, well, rectangular four-leaf, five-leaf, six-leaf, eight-leaf, swastika, etc.
The pattern of the fused areas provided in a large number of scattered points is measured by enlarging and photographing a small piece of the nonwoven fabric using a scanning electron microscope. The average value when the ratio of the sum of the areas of the parts that are point-pressed to the area of the minimum repeating unit measured using the scanning electron microscope is individually measured 10 times is referred to as the press-bonding area ratio, The non-woven fabric according to the present invention preferably has a compression area ratio of 3 to 50%. When the compression area ratio is less than 3%, the flexibility of the nonwoven fabric is improved, but the strength of the nonwoven fabric is reduced, and when the nonwoven fabric is rubbed, fluffing is likely to occur, which is problematic in practical terms. In addition, the crimping area ratio is 5
If it exceeds 0%, the nonwoven fabric itself becomes extremely hard and handling becomes poor. Therefore, more preferably, the compression area ratio is 5 to 40%.

【００２８】また各融着区域の大きさは、０．１〜２．
０ｍｍ2 程度であることが好ましい。個々の融着区域が
０．１ｍｍ2 より小さいと、不織布強力が低下したり、
毛羽立ちが発生し易くなり、個々の融着区域が２．０ｍ
ｍ2 より大きいと、不織布の柔軟性が低下するため好ま
しくない。The size of each fusion zone is from 0.1 to 2.
It is preferably about 0 mm 2 . And individual fusion zone 0.1 mm 2 smaller than lowered nonwoven strength,
Fuzz is likely to occur, and the individual fused area is 2.0 m
If it is larger than m 2 , the flexibility of the nonwoven fabric is undesirably reduced.

【００２９】また、本発明における不織布の圧着部の存
在する密度は、６〜１５０個／ｃｍ 2 程度であることが
好ましい。圧着部の密度が６個／ｃｍ2 未満であると不
織布の柔軟性は向上するが不織布強力の低下や、不織布
が擦れた場合に毛羽立ちが発生し易くなって実用面から
問題が生じる。また、圧着部の密度が１５０個／ｃｍ 2
を超えると不織布自体が極めて硬くなり、ハンドリング
が悪くなる。従ってより好ましくは、圧着部の密度は、
８〜１２０個／ｃｍ2 がよい。In the present invention, the presence of the pressure-bonded portion of the nonwoven fabric
Existing density is 6-150 pieces / cm TwoTo be about
preferable. The density of the crimping part is 6 pieces / cmTwoIf it is less than
The flexibility of the woven fabric increases, but the strength of the nonwoven fabric decreases,
Fraying is likely to occur when the surface is rubbed.
Problems arise. In addition, the density of the crimping part is 150 pieces / cm. Two
If it exceeds, the nonwoven fabric itself becomes extremely hard and
Gets worse. Therefore, more preferably, the density of the crimped portion is
8 to 120 pieces / cmTwoIs good.

【００３０】本発明における不織布の目付は、包材とし
てのハンドリングが好適に行えるように目付けを１００
ｇ／ｍ2 以下とすることが好ましい。特に食品包材とし
て用いる際には、４０ｇ／ｍ2 〜１５ｇ／ｍ2 とするこ
とで好適に使用できる。The basis weight of the nonwoven fabric in the present invention is 100% so that handling as a packaging material can be suitably performed.
g / m 2 or less. In particular, when used as food packaging materials can be suitably used by a 40g / m 2 ~15g / m 2 .

【００３１】本発明の複合長繊維不織布からなる包材
は、例えば次の方法により製造することができる。すな
わち、鞘成分がポリエチレン系重合体によって構成され
るとともに芯成分が鞘成分よりも融点の高いポリプロピ
レン系重合体によって構成された芯鞘型の長繊維によっ
てスパンボンド法により形成した長繊維不織ウェブに、
エンボス加工を施して長繊維不織布とし、前記長繊維不
織布をヒートシールすることにより包材として加工する
ものである。The wrapping material made of the composite long-fiber nonwoven fabric of the present invention can be produced, for example, by the following method. That is, a long-fiber nonwoven web formed by a spunbond method using a core-sheath type long fiber in which a sheath component is constituted by a polyethylene polymer and a core component is constituted by a polypropylene polymer having a higher melting point than the sheath component. To
The long-fiber nonwoven fabric is embossed, and the long-fiber nonwoven fabric is heat-sealed to be processed as a packaging material.

【００３２】詳細には、まず複合長繊維ウェブをスパン
ボンド法で製造する。その際には、できあがった糸条に
おいて、上述のようにポリエチレン系重合体が鞘成分を
形成し、ポリプロピレン系重合体が芯成分を形成するよ
うに、溶融したポリエチレン系重合体とポリプロピレン
系重合体とを個別計量した後、通常の芯鞘型複合口金装
置を使用して複合紡糸する。引き続いて、紡出された複
合繊維を吹付装置で冷却固化した後にエアーサッカーで
牽引し、開繊器によって開繊して、移動するコンベアー
ネット上に堆積させて長繊維ウェブとなし、熱エンボス
加工機で点圧着した後、捲取機で巻き取って不織布とす
るものである。Specifically, a composite continuous fiber web is first produced by a spunbond method. At that time, in the completed yarn, the polyethylene-based polymer forms a sheath component as described above, and the polypropylene-based polymer and the polypropylene-based polymer melted such that the polypropylene-based polymer forms a core component. Are individually weighed, and then composite spinning is performed using an ordinary core-sheath composite spinneret. Subsequently, the spun conjugate fiber is cooled and solidified by a spraying device, pulled by air soccer, opened by an opener, deposited on a moving conveyor net to form a long fiber web, and heat embossed After being point-pressed by a machine, the film is wound up by a winding machine to form a nonwoven fabric.

【００３３】本発明の方法において、繊維糸条のエアー
サッカーによる牽引は糸切れが生じない範囲内でできる
だけ高紡速、具体的には２０００ｍ／分程度以上にする
ことが望ましい。このようにすることで、繊維の配向を
高めて熱収縮性を抑えるとともに不織布物性の向上を図
ることができる。すなわち、高紡糸速度にすることは、
生産性の観点からも好ましく、かつ、繊維の結晶配向度
を高める点からも好ましく、また、熱収縮特性も低下す
るため耐熱性や寸法安定性も向上する。さらに、繊維自
体の強度も保持されるために不織布強力も高くなる。こ
れに対し、２０００ｍ／分程度よりも低い紡糸速度で
は、不織布の寸法安定性が低下したり、粗硬感が発生す
るため余りよくない。In the method of the present invention, the pulling of the fiber yarn by air soccer is desirably performed at a spinning speed as high as possible within a range in which yarn breakage does not occur, specifically, about 2000 m / min or more. By doing so, it is possible to increase the orientation of the fibers, suppress the heat shrinkage, and improve the physical properties of the nonwoven fabric. In other words, to achieve a high spinning speed,
It is preferable from the viewpoint of productivity, and is also preferable from the viewpoint of increasing the degree of crystal orientation of the fiber. In addition, heat resistance and dimensional stability are improved because the heat shrinkage property is reduced. Further, the strength of the nonwoven fabric is increased because the strength of the fiber itself is maintained. On the other hand, if the spinning speed is lower than about 2000 m / min, the dimensional stability of the nonwoven fabric is reduced, and a rough feeling is generated, which is not so good.

【００３４】上記製造方法では、点圧着により不織布の
形態を保持するためにエンボス加工法を用いたが、エン
ボス加工機としては、現在乾式不織布用に使用されてい
る公知の熱エンボス加工機や超音波溶着機等を適用する
ことができる。In the above-described manufacturing method, an embossing method is used to maintain the shape of the nonwoven fabric by point compression. However, as the embossing machine, a known hot embossing machine currently used for dry nonwoven fabrics or a super embossing machine may be used. A sonic welding machine or the like can be applied.

【００３５】例えば、熱エンボス加工機を適用した場合
の加工温度は、鞘成分の融点よりも５℃から５０℃低い
温度とすることが好ましい。加工温度が前記範囲よりも
高くなると、風合いが硬く、ハンドリングが悪く、引張
強力の低い不織布となる。また、加工温度をさらに上げ
ると、長繊維ウェブが彫刻ロールあるいは、金属製の平
滑ロールに取られて操業性が悪くなる。加工温度が鞘成
分の融点よりも５０℃以上低くなると、長繊維ウェブが
熱圧着されなくなり不織布の形態保持性が低下する。更
に加工温度が低くなると長繊維ウェブが彫刻ロールに取
られてしまい、操業性が悪くなる。このように加工温度
が融点以下であっても、鞘成分の軟化点がその加工温度
範囲内にあり、彫刻ロールの圧着ポイント部での圧力が
付与されることにより、確実に融着された状態となる。For example, when a hot embossing machine is applied, the processing temperature is preferably 5 to 50 ° C. lower than the melting point of the sheath component. If the processing temperature is higher than the above range, the hand becomes hard, the handling is poor, and the nonwoven fabric has a low tensile strength. Further, when the processing temperature is further increased, the long fiber web is taken up by an engraving roll or a metal smooth roll, and the operability deteriorates. When the processing temperature is lower than the melting point of the sheath component by 50 ° C. or more, the long fiber web is not thermocompression-bonded, and the shape retention of the nonwoven fabric is reduced. Further, when the processing temperature is lowered, the long fiber web is taken up by the engraving roll, and the operability is deteriorated. Thus, even if the processing temperature is below the melting point, the softening point of the sheath component is within the processing temperature range, and the pressure is applied at the pressure bonding point portion of the engraving roll, so that the sheath is securely fused. Becomes

【００３６】また、不織布を製造する上では、点圧着の
模様が不織布強力、柔軟性、風合いに影響するため重要
であり、この彫刻ロールの彫刻面積、形状が一つのポイ
ントである。彫刻面積の基準は、熱圧着させる時の圧着
面積率で示すことができ、本発明の不織布を得るための
圧着面積率としては、３〜５０％が好ましい。３％未満
では風合はソフトであるが強力が不十分である。逆に圧
着面積率が５０％を超えると強力は高くなるが、硬い不
織布となり本発明では好ましくない。In the production of a nonwoven fabric, the point compression pattern is important because it affects the strength, flexibility and texture of the nonwoven fabric, and the engraving area and shape of this engraving roll is one point. The standard of the engraving area can be indicated by the compression area ratio at the time of thermocompression, and the compression area ratio for obtaining the nonwoven fabric of the present invention is preferably 3 to 50%. If it is less than 3%, the feeling is soft but the strength is insufficient. Conversely, if the compression area ratio exceeds 50%, the strength increases, but a hard nonwoven fabric is not preferred in the present invention.

【００３７】また、超音波溶着機としては、彫刻ロール
と超音波溶着機構をもった支持体との間で前記ウェブを
通布し、２０ｋＨｚ程度の超音波を発振すればよい。溶
着状態を変更する場合には、用いる素材によって超音波
の波長すなわち周波数を適宜変更する。この場合の線圧
としては、熱エンボス加工機と異なって０．５〜２ｋｇ
／ｃｍ程度を用いることが好ましい。また、圧着面積率
としては、４〜５０％が好ましい。As the ultrasonic welding machine, the web may be passed between an engraving roll and a support having an ultrasonic welding mechanism, and an ultrasonic wave of about 20 kHz may be oscillated. When changing the welding state, the wavelength, that is, the frequency of the ultrasonic wave is appropriately changed depending on the material used. In this case, the linear pressure is 0.5 to 2 kg unlike the hot embossing machine.
/ Cm is preferably used. Further, the compression area ratio is preferably 4 to 50%.

【００３８】この超音波溶着による点圧着を施した不織
布は点圧着部以外の繊維が殆ど熱の影響を受けないた
め、風合いが硬くならず、熱エンボス加工よりも好適に
使用できる。In the nonwoven fabric subjected to the point compression by the ultrasonic welding, since the fibers other than the point compression part are hardly affected by heat, the texture does not become hard and can be used more favorably than the hot embossing.

【００３９】上述のように形成された複合長繊維不織布
を包材として用いる方法としては、一般的には、超音波
ウェルダーを用いたり、ヒートシーラーを用いて袋状に
ヒートシールすれば良い。超音波ウェルダー加工は、彫
刻ロールと超音波溶着機構をもった支持体との間で前記
長繊維不織布を通布し、２０ｋＨｚ程度の超音波を発振
すればよい。溶着状態を変更する場合には、用いる素材
によって、超音波の波長を適宜変更すればよい。この場
合の線圧としては、０．５〜２ｋｇ／ｃｍ程度を用いれ
ばよい。As a method of using the composite long-fiber nonwoven fabric formed as described above as a packaging material, generally, an ultrasonic welder or a heat sealer may be used for heat sealing in a bag shape. The ultrasonic welding may be performed by passing the long-fiber nonwoven fabric between an engraving roll and a support having an ultrasonic welding mechanism and oscillating an ultrasonic wave of about 20 kHz. When changing the welding state, the wavelength of the ultrasonic wave may be appropriately changed depending on the material used. In this case, a linear pressure of about 0.5 to 2 kg / cm may be used.

【００４０】ヒートシーラーは不織布を構成する低融点
成分が溶着できる温度に設定すればよく、一般的には不
織布を構成する低融点成分が軟化接着温度から不織布を
構成する高融点成分の軟化が始まるまでの温度で加工す
れば良い。この場合の線圧としては、０．５〜２ｋｇ／
ｃｍ程度であることが好ましい。The heat sealer may be set at a temperature at which the low-melting-point component constituting the non-woven fabric can be welded. Generally, the low-melting-point component constituting the non-woven fabric softens, and the high-melting-point component constituting the non-woven fabric begins to soften from the bonding temperature. Processing may be performed at temperatures up to. The linear pressure in this case is 0.5 to 2 kg /
cm.

【００４１】なお、本発明に係る包材中には、芯鞘型複
合繊維以外の他の繊維又は短繊維が若干混入していても
差し支えがない。It should be noted that the packaging material according to the present invention may contain a small amount of other fibers or short fibers other than the core-sheath composite fibers.

【００４２】[0042]

【実施例】次に、実施例に基づいて本発明を具体的に説
明するが、本発明はこれらの実施例のみに限定されるも
のではない。なお、実施例における各種物性値の測定
は、以下の方法により実施した。Next, the present invention will be specifically described based on examples, but the present invention is not limited to only these examples. The measurement of various physical property values in the examples was performed by the following methods.

【００４３】（１）融点（℃）：パーキンエルマー社製
の示差走査型熱量計ＤＳＣ−２型を用いて、昇温速度２
０℃／分で測定し、得られた融解吸熱曲線において極値
を与える温度を融点とした。(1) Melting point (° C.): Using a differential scanning calorimeter DSC-2 manufactured by Perkin Elmer Co., Ltd.
The temperature was measured at 0 ° C./min, and the temperature at which an extreme value was obtained in the obtained melting endothermic curve was defined as the melting point.

【００４４】（２）メルトインデックス（ｇ／１０
分）：ＡＳＴＭ−Ｄ−１２３８Ｅに記載の方法に準じて
測定した。(2) Melt index (g / 10
Min): Measured according to the method described in ASTM-D-1238E.

【００４５】（３）メルトフローレート（ｇ／１０
分）：ＡＳＴＭ−Ｄ−１２３８Ｌに記載の方法に準じて
測定した。(3) Melt flow rate (g / 10
Min): Measured according to the method described in ASTM-D-1238L.

【００４６】（４）重合体の熱減量率：パーキンエルマ
ー社製の熱重量計（型番ＴＧＡ−７）を用い、昇温速度
２０℃／分で、空気中で２３０℃に到達してからその温
度を保持し、１０分後の雰囲気下での熱減量率である。(4) Thermal loss of polymer: Using a thermogravimeter (model number TGA-7) manufactured by PerkinElmer, at a heating rate of 20 ° C./min, the temperature reached 230 ° C. in the air. It is a heat loss rate in an atmosphere after 10 minutes while maintaining the temperature.

【００４７】（５）不織布の引張強力（ｋｇ／５ｃｍ
幅）及び引張伸度（％）：ＪＩＳ−Ｌ−１０９６に記載
のストリップ法に準じて測定した。すなわち、試料長が
１５ｃｍ、試料幅が５ｃｍの試料片を不織布の縦方向
（ＭＤ）及び横方向（ＣＤ）にそれぞれ１０点作成し、
各試料片毎に、不織布のＭＤ方向及びＣＤ方向につい
て、定速伸長型引張試験機（東洋ボールドウィン社製テ
ンシロンＵＴＭ−４−１−１００）を用い、試料の掴み
間隔１０ｃｍとし、引張速度１０ｃｍ／分で伸長した。
そして、得られた切断時荷重値（ｋｇ／５ｃｍ幅）の平
均値を引張強力とした。また、その時の最大伸度の平均
値を不織布の引張伸度とした。(5) Tensile strength of nonwoven fabric (kg / 5cm
Width) and tensile elongation (%): Measured according to the strip method described in JIS-L-1096. That is, 10 pieces of sample pieces each having a sample length of 15 cm and a sample width of 5 cm are created in the machine direction (MD) and the transverse direction (CD) of the nonwoven fabric, respectively.
For each sample piece, in the MD direction and CD direction of the nonwoven fabric, using a constant-speed elongation type tensile tester (Tensilon UTM-4-1-100 manufactured by Toyo Baldwin Co., Ltd.), the gripping interval of the sample was 10 cm, and the tensile speed was 10 cm / Extended in minutes.
Then, the average value of the obtained load values at cutting (kg / 5 cm width) was defined as the tensile strength. The average value of the maximum elongation at that time was defined as the tensile elongation of the nonwoven fabric.

【００４８】（６）不織布の熱水可溶成分の溶出率［Ｈ
ＷＤ］（％）：長さ１ｍ、幅１ｍの試験片を作成し、９
８℃の熱水に浴比１：１００で１０分間浸漬させ、その
後純水で更に洗浄したあと脱水し、６０℃で１時間乾燥
した際の熱水可溶成分の溶出率（％）を求めた。(6) Elution rate of hot water soluble component of nonwoven fabric [H
WD] (%): A test piece having a length of 1 m and a width of 1 m was prepared, and 9
Immersion in hot water at 8 ° C. for 10 minutes at a bath ratio of 1: 100, followed by further washing with pure water, dehydration, and determination of the elution rate (%) of hot water-soluble components when dried at 60 ° C. for 1 hour. Was.

【００４９】（７）不織布の熱水面積収縮率［ＨＷＳ］
（％）：長さ１ｍ、幅１ｍの試験片に、不織布の縦方向
が５ｃｍ、横方向が５ｃｍの枠を４か所記載した後、９
８℃の熱水に浴比１：１００で１０分間浸漬させ、その
後純水で更に洗浄したあと脱水し、６０℃で１時間乾燥
した際の個々の長さを測定し、最初に記載した面積に対
する熱水処理後の面積の割合を面積収縮率（％）として
算出し、その平均値を不織布の熱水面積収縮率とした。(7) Hot water area shrinkage of nonwoven fabric [HWS]
(%): After placing four frames each having a length of 5 cm and a width of 5 cm on a test piece of 1 m in length and 1 m in width, 9
Immerse in hot water of 8 ° C. for 10 minutes at a bath ratio of 1: 100, then wash with pure water, dehydrate, measure the length when dried at 60 ° C. for 1 hour, and measure the area described first. Was calculated as the area shrinkage (%), and the average value was defined as the hot water area shrinkage of the nonwoven fabric.

【００５０】（８）製袋性：通常のヒートシール機を用
いて、適性温度条件で５０個の包材を作成し、製袋性を
調査し下記のごとく判定した。 ◎ 全く問題が無く、良好であった。(8) Bag-making properties: Using an ordinary heat sealing machine, 50 packaging materials were prepared under appropriate temperature conditions, and the bag-making properties were examined and judged as follows. ◎ There was no problem at all and it was good.

【００５１】 ○ おおむね良好であった。 △ やや問題であった。 × 不良である。○ Generally good. △ It was a little problem. X: defective.

【００５２】（９）実用性：ヒートシール機を用いて長
繊維不織布をティーバッグ型の包材に作製した。そして
市販のブラジル産コーヒー豆の粉砕物を１０ｇ計量し
て、前記包材中に封入し、コーヒーバッグを作製した。
作製されたコーヒーバッグを９８℃の熱水２００ｃｃ中
に投入して１分間抽出処理を行った後、パネラー５人に
よる試飲を含めたモニター試験を行い、下記の如く実用
性の評価を行った。(9) Practicality: A long-fiber nonwoven fabric was produced in a tea bag type packaging material using a heat sealing machine. Then, 10 g of commercially available ground coffee beans from Brazil were weighed and sealed in the packaging material to prepare a coffee bag.
The prepared coffee bag was put into 200 cc of hot water at 98 ° C. and subjected to an extraction treatment for one minute. Then, a monitor test including tasting by five panelists was performed, and the practicality was evaluated as follows.

【００５３】 ◎ 全く問題が無く、良好であった。 ○ おおむね良好であった。 △ やや問題であった。A: There was no problem at all and it was good. ○ Generally good. △ It was a little problem.

【００５４】× 不良である。× Bad.

【００５５】実施例１ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、鞘成分として融点が１３２℃で密度が０．９５８ｇ
／ｃｍ3 、ＡＳＴＭのＤ−１２３８Ｅで測定されるメル
トインデックス値が２０ｇ／１０分で、２３０℃におけ
る重合体の熱減量率が２．０％のポリエチレンを用い
た。また、芯成分には、融点が１６２℃で、ＡＳＴＭの
Ｄ−１２３８Ｌで測定されるメルトフローレート値が３
０ｇ／１０分、２３０℃における重合体の熱減量率が
１．６％のポリプロピレンを用いた。前記鞘成分を構成
するポリエチレンおよび前記芯成分を構成するポリプロ
ピレンには、フェノール系添加剤として、１，３，５−
トリス（４−ｔ−ブチル−３−ヒドロキシ−２，６−ジ
メチルベンジル）イソシアヌル酸を５００ｐｐｍ、無機
系の中和剤として、ハイドロタルサイト類化合物３００
ｐｐｍをそれぞれに同量づつ配合した。Example 1 In forming a core-sheath type long fiber constituting a composite long-fiber nonwoven fabric, a melting point of 132 ° C. and a density of 0.958 g were used as a sheath component.
/ Cm 3 , a polyethylene having a melt index value measured by ASTM D-1238E of 20 g / 10 min and a loss on heat of the polymer at 230 ° C. of 2.0% was used. The core component has a melting point of 162 ° C. and a melt flow rate measured by ASTM D-1238L of 3%.
A polypropylene having 0 g / 10 min and a heat loss rate of the polymer at 230 ° C. of 1.6% was used. The polyethylene constituting the sheath component and the polypropylene constituting the core component include 1,3,5-
500 ppm of tris (4-t-butyl-3-hydroxy-2,6-dimethylbenzyl) isocyanuric acid, hydrotalcite compound 300 as an inorganic neutralizing agent
ppm was blended in the same amount.

【００５６】そしてポリエチレンは２２０℃で溶融し、
ポリプロピレンは２３０℃で溶融して１：１の重量比と
なるように個別溶融計量し、丸孔の口金孔を有する芯鞘
型複合紡糸用口金装置を用いて、単孔吐出量を１．０ｇ
／分として、２３０℃の温度で溶融紡糸を行った。The polyethylene melts at 220 ° C.
The polypropylene is melted at 230 ° C. and individually melted and weighed so as to have a weight ratio of 1: 1. Using a core-sheath type composite spinning die device having a round die hole, a single hole discharge amount is 1.0 g.
The melt spinning was performed at a temperature of 230 ° C./min.

【００５７】芯鞘型複合紡糸用口金装置より紡出された
糸条を冷却装置を介してエアーサッカーで牽引し、公知
の開繊器にて開繊させ、移動するコンベアーネット上に
堆積させて単糸繊度が３．０デニールの芯鞘型長繊維か
らなる長繊維ウェブを得た。この長繊維ウェブに引続き
熱圧接処理を施した。熱圧接処理に際しては、圧着面積
率１５％、圧着部密度２２個／ｃｍ2 、圧着部面積０．
７ｍｍ2 の彫刻ロールとフラットロールとからなる熱エ
ンボス加工機で、加工温度を１２３℃、ロール間の線圧
を４０ｋｇ／ｃｍとして点圧着し、目付が約２０ｇ／ｍ
2 の長繊維不織布を製造した。The yarn spun from the core-sheath type composite spinneret is pulled by an air soccer through a cooling device, opened by a known opening device, and deposited on a moving conveyor net. A long fiber web composed of a core-sheath type long fiber having a single fiber fineness of 3.0 denier was obtained. Subsequently, the heat-welding treatment was applied to the long fiber web. At the time of the heat-pressing treatment, the crimping area ratio is 15%, the crimping portion density is 22 pieces / cm 2 , and the crimping portion area is 0.1 mm.
With a hot embossing machine consisting of a 7 mm 2 engraving roll and a flat roll, point press bonding was performed at a working temperature of 123 ° C. and a linear pressure between the rolls of 40 kg / cm, and the basis weight was about 20 g / m.
Two long fiber nonwoven fabrics were produced.

【００５８】得られた長繊維不織布をヒートシール機を
用いて、温度１３５℃でヒートシール加工して、コーヒ
ーや紅茶やお茶等の食品包材として使用できるティーバ
ッグ型の包材を作製した。また、得られた包材の実用性
を調べるために前記包材の中に市販のブラジル産コーヒ
ー豆の粉砕物を封入してコーヒーバッグを作製した。The obtained long-fiber nonwoven fabric was heat-sealed at a temperature of 135 ° C. using a heat-sealing machine to prepare a tea bag-type packaging material that can be used as a food packaging material for coffee, black tea, tea and the like. Further, in order to examine the practicality of the obtained packaging material, a pulverized product of commercially available Brazilian coffee beans was enclosed in the packaging material to prepare a coffee bag.

【００５９】上記長繊維不織布と包材の物性等を表１に
示す。Table 1 shows the physical properties and the like of the long-fiber nonwoven fabric and the packaging material.

【００６０】[0060]

【表１】 [Table 1]

【００６１】実施例２ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、鞘成分として融点が１２６℃で密度が０．９３８ｇ
／ｃｍ3 、ＡＳＴＭのＤ−１２３８Ｅで測定されるメル
トインデックス値が２６ｇ／１０分で２３０℃における
重合体の熱減量率が２．２％の線状低密度ポリエチレン
を用いた。前記鞘成分を構成する線状低密度ポリエチレ
ンには実施例１と同様にフェノール系添加剤と無機系の
中和剤とを配合し、２１０℃で溶融した。そして、それ
以外は実施例１と同様にして芯鞘型長繊維を溶融紡糸
し、長繊維ウェブを作製した。Example 2 When forming a core-sheath type long fiber constituting a composite long-fiber nonwoven fabric, a melting point was 126 ° C. and a density was 0.938 g as a sheath component.
/ Cm 3, ASTM polymer thermal weight loss of at 230 ° C. The melt index value measured by D-1238E is at 26 g / 10 min was used 2.2% of the linear low density polyethylene. A phenolic additive and an inorganic neutralizing agent were blended into the linear low-density polyethylene constituting the sheath component in the same manner as in Example 1, and melted at 210 ° C. Other than that, the core-sheath type long fiber was melt-spun in the same manner as in Example 1 to produce a long fiber web.

【００６２】この長繊維ウェブに施した熱エンボス加工
における加工温度を１１０℃とした以外は実施例１と同
様にして熱圧接処理を施した。得られた長繊維不織布を
ヒートシール機を用いて、温度１３０℃でヒートシール
加工して、実施例１と同様にしてティーバッグ型の包材
とこの包材にブラジル産コーヒー粉末を封入したコーヒ
ーバッグとを作製した。A hot pressing treatment was performed in the same manner as in Example 1 except that the processing temperature in the hot embossing performed on the long fiber web was 110 ° C. The obtained long-fiber nonwoven fabric was heat-sealed at a temperature of 130 ° C. using a heat-sealing machine, and a tea bag-type packaging material and coffee in which Brazilian coffee powder was sealed in the packaging material in the same manner as in Example 1. And a bag.

【００６３】上記長繊維不織布と包材の物性等を表１に
示す。Table 1 shows the physical properties and the like of the long-fiber nonwoven fabric and the packaging material.

【００６４】実施例３ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、鞘成分として融点が１２５℃で密度が０．９３６ｇ
／ｃｍ3 、ＡＳＴＭのＤ−１２３８Ｅで測定されるメル
トインデックス値が４３ｇ／１０分で２３０℃における
重合体の熱減量率が３．２％の線状低密度ポリエチレン
を用いた。前記鞘成分を構成する線状低密度ポリエチレ
ンには、実施例１と同様にフェノール系添加剤と無機系
の中和剤とを配合した。また、芯成分には、融点が１６
２℃で、密度が０．９１８ｇ／ｃｍ3 、ＡＳＴＭのＤ−
１２３８Ｌで測定されるメルトフローレート値が５０ｇ
／１０分、２３０℃における重合体の熱減量率が５．３
％の市販のポリプロピレンを用いた。線状低密度ポリエ
チレンは２００℃で、ポリプロピレンは２３０℃で溶融
した。Example 3 When forming the core-sheath type long fiber constituting the composite long-fiber nonwoven fabric, the sheath component had a melting point of 125 ° C. and a density of 0.936 g.
A linear low-density polyethylene having a melt index value of 43 g / 10 min./cm 3 , measured by ASTM D-1238E, and a loss on heat of the polymer at 230 ° C. of 3.2% was used. The linear low-density polyethylene constituting the sheath component was mixed with a phenolic additive and an inorganic neutralizing agent in the same manner as in Example 1. The core component has a melting point of 16%.
At 2 ° C, the density is 0.918 g / cm 3 , ASTM D-
Melt flow rate value measured at 1238L is 50g
/ 10 min, the loss of heat of the polymer at 230 ° C. is 5.3.
% Commercial polypropylene was used. The linear low density polyethylene melted at 200 ° C and the polypropylene melted at 230 ° C.

【００６５】そしてそれ以外は実施例１と同様にして芯
鞘型長繊維を溶融紡糸し、長繊維ウェブを作製した。得
られた長繊維不織布をヒートシール機を用いて、温度１
３０℃でヒートシール加工して、実施例１と同様にして
ティーバッグ型の包材とこの包材にブラジル産コーヒー
粉末を封入したコーヒーバッグとを作製した。Other than that, the core-sheath type long fiber was melt-spun in the same manner as in Example 1 to produce a long fiber web. The obtained long-fiber nonwoven fabric was heated at a temperature of 1 using a heat sealing machine.
A heat-sealing process was performed at 30 ° C. to produce a tea bag-type packaging material and a coffee bag in which Brazilian coffee powder was sealed in the packaging material in the same manner as in Example 1.

【００６６】上記長繊維不織布と包材の物性等を表１に
示す。Table 1 shows the physical properties and the like of the long-fiber nonwoven fabric and the packaging material.

【００６７】実施例４ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、鞘成分を構成するポリエチレンに添加するフェノー
ル系添加剤を、融点が５２℃のｎ−オクタデシル−３−
（３’，５’−ジ−ｔ−ブチル４’−ヒドロキシフェニ
ル）−プロピオネートとし、前記鞘成分を構成するポリ
エチレンの熱減量率を６．４％とした。Example 4 In forming the core-sheath type long fiber constituting the composite long-fiber nonwoven fabric, a phenolic additive to be added to the polyethylene constituting the sheath component was added to n-octadecyl-3-melting point having a melting point of 52 ° C.
(3 ′, 5′-di-t-butyl 4′-hydroxyphenyl) -propionate, and the polyethylene constituting the sheath component had a heat loss rate of 6.4%.

【００６８】そして、それ以外は実施例１と同様にして
芯鞘型長繊維を溶融紡糸し、長繊維ウエブを作製した。
得られた長繊維不織布をヒートシール機を用いて温度１
３５℃でヒートシール加工して、ティーバッグ型の包材
とこの包材にブラジル産コーヒー粉末を封入したコーヒ
ーバッグとを作製した。Otherwise, the core-sheath type long fiber was melt-spun in the same manner as in Example 1 to produce a long fiber web.
The obtained long-fiber nonwoven fabric was heated at a temperature of 1 using a heat sealing machine.
Heat sealing was performed at 35 ° C. to produce a tea bag-type packaging material and a coffee bag in which Brazilian coffee powder was sealed in the packaging material.

【００６９】上記長繊維不織布と包材の物性等を表１に
示す。Table 1 shows the physical properties of the long-fiber nonwoven fabric and the packaging material.

【００７０】実施例５ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、鞘成分を構成するポリエチレンに添加する中和剤と
してステアリン酸カルシウムと、融点が２２７℃のＮ
Ｎ’−ビス［３−（３，５−ジ−ｔ−ブチル−４−ヒド
ロキシフェニル）プロピオニル］ヒドラジンとをそれぞ
れ２００ｐｐｍづつ配合し、前記鞘成分を構成するポリ
エチレンの熱減量率を４．８％とした。Example 5 In forming the core-sheath type long fiber constituting the composite long-fiber nonwoven fabric, calcium stearate as a neutralizing agent added to polyethylene constituting the sheath component and N having a melting point of 227 ° C.
N'-bis [3- (3,5-di-t-butyl-4-hydroxyphenyl) propionyl] hydrazine was added in an amount of 200 ppm, and the polyethylene constituting the sheath component was reduced by 4.8%. And

【００７１】そして、それ以外は実施例１と同様にして
芯鞘型長繊維を溶融紡糸し、長繊維ウエブを作製した。
得られた長繊維不織布をヒートシール機を用いて温度１
３５℃でヒートシール加工して、ティーバッグ型の包材
とこの包材にブラジル産コーヒー粉末を封入したコーヒ
ーバッグとを作製した。Other than that, the core-sheath type long fiber was melt-spun in the same manner as in Example 1 to produce a long fiber web.
The obtained long-fiber nonwoven fabric was heated at a temperature of 1 using a heat sealing machine.
Heat sealing was performed at 35 ° C. to produce a tea bag-type packaging material and a coffee bag in which Brazilian coffee powder was sealed in the packaging material.

【００７２】上記長繊維不織布と包材の物性等を表１に
示す。Table 1 shows the physical properties and the like of the long-fiber nonwoven fabric and the packaging material.

【００７３】実施例６ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、単孔吐出量を０．９ｇ／分に下げて、２３０℃の温
度で溶融紡糸を行った。また、芯鞘型複合紡糸用口金装
置より紡出された糸条を冷却装置を介してエアーサッカ
ーで牽引する際の牽引速度を下げて、実施例１のものと
同じ単糸繊度すなわち３．０デニールとなるものを得
た。また、熱エンボス加工時の加工温度を１２０℃とし
た。Example 6 At the time of forming the core-sheath type long fiber constituting the composite long-fiber nonwoven fabric, the single-hole discharge rate was reduced to 0.9 g / min, and melt spinning was performed at a temperature of 230 ° C. Further, the drawing speed at the time of drawing the yarn spun from the core-sheath type composite spinneret by the air soccer through the cooling device is reduced, and the same single yarn fineness as that of Example 1, namely 3.0. I got what would be denier. The processing temperature during hot embossing was set to 120 ° C.

【００７４】そして、それ以外は実施例１と同様にして
長繊維不織布を作製し、前記長繊維不織布をヒートシー
ル機を用いて温度１３５℃でヒートシール加工して、テ
ィーバッグ型の包材とこの包材にブラジル産コーヒー粉
末を封入したコーヒーバッグとを作製した。Otherwise, a long-fiber nonwoven fabric was prepared in the same manner as in Example 1, and the long-fiber nonwoven fabric was heat-sealed at a temperature of 135 ° C. using a heat-sealing machine to obtain a tea bag type packaging material. A coffee bag in which Brazilian coffee powder was enclosed in this packaging material was produced.

【００７５】上記長繊維不織布と包材の物性等を表１に
示す。Table 1 shows the physical properties and the like of the long-fiber nonwoven fabric and the packaging material.

【００７６】実施例１〜３は、いずれもポリプロピレン
系重合体を芯成分とし、この芯成分よりも融点が低いポ
リエチレン系重合体を鞘成分とした芯鞘型の複合長繊維
を用いているため、ヒートシール性が良く製袋性の良い
複合長繊維不織布が得られた。また、前記複合長繊維が
エンボス加工されて長繊維相互間が散点状に融着されて
いたため、不織布の引張強力や引張伸度にも優れてい
た。さらに熱水可溶成分の溶出率ＨＷＤが０．０４％以
下で、面積収縮率ＨＷＳが８％以下であったため、コー
ヒーバッグとして使用しても鞘成分を構成するポリエチ
レン系重合体の低分子量成分が熱水中に溶出して異臭が
したり、コーヒーバッグが収縮して中身のコーヒー粉末
が漏れたりすることがなく、コーヒーバッグとして好適
に使用できた。また、鞘成分中には、融点が１４０℃以
上のフェノール系添加剤と、無機系の中和剤とが添加さ
れていたため、複合紡糸時やヒートシール時におけるポ
リマー劣化がなく、低分子量成分の熱水中への溶出が解
消され、サイフォン抽出法で得たコーヒーと遜色ないブ
ラジル産コーヒーが本来の持つ香りが生かされ、味、コ
ク共に満足できる実用性の良いコーヒーバッグが得られ
た。また、実施例３は、芯成分に市販のポリプロピレン
を用いたため、芯成分の熱減量率がやや高くなったもの
の、上記のように包材としての実用性が良いものが得ら
れた。In each of Examples 1 to 3, a core-sheath composite long fiber having a polypropylene polymer as a core component and a sheath polymer of a polyethylene polymer having a lower melting point than the core component is used. Thus, a composite long-fiber nonwoven fabric having good heat sealing properties and good bag making properties was obtained. In addition, since the composite long fibers were embossed and fused between the long fibers in a scattered manner, the nonwoven fabric was excellent in tensile strength and tensile elongation. Further, since the elution rate HWD of the hot water-soluble component was 0.04% or less and the area shrinkage HWS was 8% or less, the low molecular weight component of the polyethylene polymer constituting the sheath component even when used as a coffee bag. Did not elute in hot water to give off-flavors, or the coffee bag shrank and the content of coffee powder leaked out, so that it could be suitably used as a coffee bag. In addition, since a phenolic additive having a melting point of 140 ° C. or higher and an inorganic neutralizing agent were added to the sheath component, there was no polymer deterioration during composite spinning or heat sealing, and the low molecular weight component Elution into hot water was eliminated, and the original aroma of Brazilian coffee comparable to coffee obtained by siphon extraction method was utilized, and a practical coffee bag with satisfactory taste and richness was obtained. Further, in Example 3, since commercially available polypropylene was used as the core component, although the heat loss rate of the core component was slightly increased, a material having good practicability as a packaging material was obtained as described above.

【００７７】実施例４は、フェノール系の添加剤の融点
が低いものを用いたため、鞘成分の熱劣化による溶出率
がやや大きくなり、コーヒー等のティーバッグのように
熱水中で使用する食品包材としては幾分風味に劣るもの
であったが実用上の問題はなかった。In Example 4, since the phenol-based additive having a low melting point was used, the dissolution rate due to thermal degradation of the sheath component was slightly increased, and the food used in hot water such as a tea bag for coffee or the like was used. Although the packaging material was somewhat inferior in flavor, there was no practical problem.

【００７８】実施例５は、無機系の中和剤の代わりに有
機系の中和剤を用いたため、鞘成分の熱劣化による溶出
率がやや大きくなったものの、その他の特性においては
上記実施例１〜３と同様に包材としての特性のよいもの
が得られた。In Example 5, since the organic neutralizing agent was used in place of the inorganic neutralizing agent, the elution rate due to the thermal degradation of the sheath component was slightly increased. As in the cases of Nos. 1 to 3, good packaging materials were obtained.

【００７９】実施例６は、牽引速度を落として長繊維不
織布を作製したため、長繊維不織布としての物性は、機
械的強力がやや低下する傾向にあり、熱収縮率もやや高
くなる傾向にあるが包材の製袋性には問題はなかった。
また、その実用性においては、コーヒーの抽出時間をや
や長めにかけることで良好な状態に改善された。In Example 6, since the long-fiber nonwoven fabric was manufactured at a reduced pulling speed, the physical properties of the long-fiber nonwoven fabric tended to slightly decrease in mechanical strength and slightly increased in heat shrinkage. There was no problem in the bag making property of the packaging material.
In addition, in terms of its practicality, it was improved to a good state by slightly extending the coffee extraction time.

【００８０】比較例１ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、鞘成分として融点が１３２℃で密度が０．９５８ｇ
／ｃｍ3 、ＡＳＴＭのＤ−１２３８Ｅで測定されるメル
トインデックス値が２０ｇ／１０分で２３０℃における
重合体の熱減量率が８．４％のポリエチレンを用いた。
前記鞘成分を構成するポリエチレンにはフェノール系添
加剤として、テトラキス−［メチレン−３−（３’，
５’−ジ−タート−ブチル−４’−ヒドロキシ−フェニ
ル）−プロピオネート］メタン（融点１２０℃）８００
ｐｐｍと中和剤としてステアリン酸カルシウム３００ｐ
ｐｍを配合し、２２０℃で溶融した。そして、それ以外
は実施例１と同様にして芯鞘型長繊維を溶融紡糸し、長
繊維ウェブを作製した。また、この長繊維ウェブには実
施例１と同様にして熱圧接処理を施して長繊維不織布を
作製した。Comparative Example 1 When forming the core-sheath type long fiber constituting the composite long-fiber nonwoven fabric, the sheath component had a melting point of 132 ° C. and a density of 0.958 g.
/ Cm 3 , a polyethylene having a melt index value measured by ASTM D-1238E of 20 g / 10 min and a heat loss rate of the polymer at 230 ° C. of 8.4% was used.
In the polyethylene constituting the sheath component, tetrakis- [methylene-3- (3 ′,
5'-di-tert-butyl-4'-hydroxy-phenyl) -propionate] methane (melting point 120 ° C) 800
ppm and calcium stearate 300p as neutralizer
pm was melted at 220 ° C. Other than that, the core-sheath type long fiber was melt-spun in the same manner as in Example 1 to produce a long fiber web. In addition, this long fiber web was subjected to a heat press treatment in the same manner as in Example 1 to produce a long fiber nonwoven fabric.

【００８１】得られた長繊維不織布をヒートシール機を
用いて、温度１４０℃でヒートシール加工して、実施例
１と同様にしてティーバッグ型の包材とブラジル産コー
ヒー粉末を封入したコーヒーバッグとを作製した。The obtained long-fiber nonwoven fabric was heat-sealed using a heat-sealing machine at a temperature of 140 ° C., and in the same manner as in Example 1, a tea bag-type packaging material and a coffee bag in which Brazilian coffee powder was enclosed. And were produced.

【００８２】上記長繊維不織布と包材の物性等を表２に
示す。Table 2 shows the physical properties of the long-fiber nonwoven fabric and the packaging material.

【００８３】[0083]

【表２】 [Table 2]

【００８４】比較例２ 融点が１２６℃で密度が０．９４５ｇ／ｃｍ3 、ＡＳＴ
ＭのＤ−１２３８Ｅで測定されるメルトインデックス値
が２５ｇ／１０分で２３０℃における重合体の熱減量率
が８．０％であるポリエチレンのみを用いた。前記ポリ
エチレンにはフェノール系添加剤として、ｎ−オクタデ
シル−３−（３’，５’−ジ−ｔ−ブチル４’−ヒドロ
キシフェニル）−プロピオネート（融点５２℃）５００
ｐｐｍと中和剤としてステアリン酸カルシウム３００ｐ
ｐｍを配合した。前記添加剤が配合されたポリエチレン
を、芯鞘型の紡糸口金ではない通常の単軸型溶融紡糸装
置に適用して、丸孔を有する紡糸用口金装置を用いて、
単孔吐出量が１．０ｇ／分で、紡糸温度を２３０℃とし
て溶融紡糸し、長繊維ウェブを作製した。Comparative Example 2 Melting point: 126 ° C., density: 0.945 g / cm 3 , AST
Only polyethylene having a melt index value measured by D-1238E of M of 25 g / 10 minutes and a loss on heat of the polymer at 230 ° C. of 8.0% was used. N-octadecyl-3- (3 ', 5'-di-t-butyl4'-hydroxyphenyl) -propionate (melting point 52 ° C) 500 as a phenolic additive in the polyethylene.
ppm and calcium stearate 300p as neutralizer
pm. The polyethylene compounded with the additive is applied to a normal single-axis type melt spinning device that is not a core-sheath type spinneret, using a spinneret device having a round hole,
Melt spinning was performed at a single hole discharge rate of 1.0 g / min and a spinning temperature of 230 ° C. to produce a long fiber web.

【００８５】この長繊維ウェブに施した熱エンボス加工
における加工温度を１０５℃とした以外は実施例１と同
様にして熱圧接処理を施した。得られた長繊維不織布を
ヒートシール機を用いて、温度１２３℃でヒートシール
加工して、実施例１と同様にしてティーバッグ型の包材
とこの包材にブラジル産コーヒー粉末を封入したコーヒ
ーバッグとを作製した。A hot press treatment was performed in the same manner as in Example 1 except that the processing temperature in the hot embossing performed on the long fiber web was 105 ° C. The obtained long-fiber nonwoven fabric was heat-sealed at a temperature of 123 ° C. using a heat-sealing machine, and in the same manner as in Example 1, a tea bag-type packaging material and coffee in which Brazilian coffee powder was sealed in the packaging material And a bag.

【００８６】上記長繊維不織布と包材の物性等を表２に
示す。Table 2 shows the physical properties of the long-fiber nonwoven fabric and the packaging material.

【００８７】比較例３ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、鞘成分として融点が１３２℃で密度が０．９５８ｇ
／ｃｍ3 、ＡＳＴＭのＤ−１２３８Ｅで測定されるメル
トインデックス値が２０ｇ／１０分で２３０℃における
重合体の熱減量率が９．０％のポリエチレンを用いた。
前記鞘成分を構成するポリエチレンにはフェノール系添
加剤を配合せず、中和剤として、ハイドロタルサイト類
化合物を３００ｐｐｍ配合した。Comparative Example 3 When forming the core-sheath type long fiber constituting the composite long-fiber nonwoven fabric, the sheath component had a melting point of 132 ° C. and a density of 0.958 g.
/ Cm 3 , a polyethylene having a melt index value measured by ASTM D-1238E of 20 g / 10 min and a polymer weight loss at 230 ° C. of 9.0%.
A phenolic additive was not added to the polyethylene constituting the sheath component, and 300 ppm of a hydrotalcite compound was added as a neutralizing agent.

【００８８】そして、それ以外は実施例１と同様にして
長繊維不織布を作製し、前記長繊維不織布をヒートシー
ル機を用いて温度１３５℃でヒートシール加工して、テ
ィーバッグ型の包材とこの包材にブラジル産コーヒー粉
末を封入したコーヒーバッグとを作製した。Otherwise, a long-fiber non-woven fabric was prepared in the same manner as in Example 1, and the long-fiber non-woven fabric was heat-sealed at a temperature of 135 ° C. using a heat-sealing machine to obtain a tea bag type packaging material. A coffee bag in which Brazilian coffee powder was enclosed in this packaging material was produced.

【００８９】上記長繊維不織布と包材の物性等を表２に
示す。Table 2 shows the physical properties of the long-fiber nonwoven fabric and the packaging material.

【００９０】比較例４ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、鞘成分として融点が１３２℃で密度が０．９５８ｇ
／ｃｍ3 、ＡＳＴＭのＤ−１２３８Ｅで測定されるメル
トインデックス値が２０ｇ／１０分で２３０℃における
重合体の熱減量率が８．５％のポリエチレンを用いた。
前記鞘成分を構成するポリエチレンにはフェノール系添
加剤の代わりに融点が１８３℃のリン系の酸化防止剤ト
リス（２，４−ジ−ｔ−ブチルフェニル）−フォスファ
イトを添加剤として８００ｐｐｍ配合し、中和剤として
は、ハイドロタルサイト類化合物を３００ｐｐｍ配合し
た。Comparative Example 4 When forming the core-sheath type long fiber constituting the composite long-fiber nonwoven fabric, the sheath component had a melting point of 132 ° C. and a density of 0.958 g.
/ Cm 3 , a polyethylene having a melt index value measured by ASTM D-1238E of 20 g / 10 min and a heat loss rate of the polymer at 230 ° C. of 8.5% was used.
800 ppm of tris (2,4-di-t-butylphenyl) -phosphite, a phosphorus-based antioxidant having a melting point of 183 ° C., was added to the polyethylene constituting the sheath component instead of the phenol-based additive as an additive. As a neutralizing agent, 300 ppm of a hydrotalcite compound was blended.

【００９１】そして、それ以外は実施例１と同様にして
長繊維不織布を作製し、前記長繊維不織布をヒートシー
ル機を用いて温度１３５℃でヒートシール加工してティ
ーバッグ型の包材とこの包材にブラジル産コーヒー粉末
を封入したコーヒーバッグとを作製した。Otherwise, a long-fiber non-woven fabric was prepared in the same manner as in Example 1, and the long-fiber non-woven fabric was heat-sealed at a temperature of 135 ° C. using a heat-sealing machine to form a tea bag type packaging material. A coffee bag in which Brazilian coffee powder was enclosed in a packaging material was produced.

【００９２】上記長繊維不織布と包材の物性等を表２に
示す。Table 2 shows the physical properties of the long-fiber nonwoven fabric and the packaging material.

【００９３】比較例５ 複合長繊維不織布を構成する芯鞘型長繊維を形成する際
に、単孔吐出量を実施例６と同様に０．９ｇ／分とし
た。また、芯鞘型複合紡糸用口金装置より紡出された糸
条を冷却装置を介してエアーサッカーで牽引する際の牽
引速度を実施例６よりもさらに下げて、単糸繊度が４．
５デニールの芯鞘型長繊維からなる長繊維ウェブを得
た。この長繊維ウェブに加工温度を１１８℃として熱エ
ンボス加工を施した。Comparative Example 5 In forming the core-sheath type long fiber constituting the composite long-fiber nonwoven fabric, the single hole discharge amount was set to 0.9 g / min as in Example 6. Further, the pulling speed at the time of pulling the yarn spun from the core-sheath type composite spinning die device by air soccer through the cooling device is further lowered than in Example 6, and the single yarn fineness is 4.
A long-fiber web composed of 5 denier core-sheath type long fibers was obtained. The long fiber web was subjected to hot embossing at a processing temperature of 118 ° C.

【００９４】そして、それ以外は実施例１と同様にして
長繊維不織布を作製し、前記長繊維不織布をヒートシー
ル機を用いて温度１３５℃でヒートシール加工してティ
ーバッグ型の包材とこの包材にブラジル産コーヒー粉末
を封入したコーヒーバッグとを作製した。Otherwise, a long-fiber nonwoven fabric was prepared in the same manner as in Example 1, and the long-fiber nonwoven fabric was heat-sealed at a temperature of 135 ° C. using a heat-sealing machine to form a tea bag type packaging material. A coffee bag in which Brazilian coffee powder was enclosed in a packaging material was produced.

【００９５】上記長繊維不織布と包材の物性等を表２に
示す。Table 2 shows the physical properties of the long-fiber nonwoven fabric and the packaging material.

【００９６】比較例１は、ポリプロピレン系重合体を芯
成分とし、この芯成分よりも融点が低いポリエチレン系
重合体を鞘成分とした芯鞘型の複合長繊維を用いている
ため、ヒートシール性が良く製袋性の良い複合長繊維不
織布が得られたものの、鞘成分の熱減量率が本発明の上
限を超えており、複合紡糸時やヒートシール時にポリマ
ー劣化がおこりやすくなり、熱水中への低分子量成分の
溶出率が高くなり、コーヒーバッグとして用いるとコー
ヒーに異臭が生じ実用性に劣るものとなった。Comparative Example 1 uses a core-sheath composite long fiber having a polypropylene polymer as a core component and a polyethylene polymer having a lower melting point than the core component as a sheath component. Although a composite long-fiber nonwoven fabric with good bag-making properties was obtained, the heat loss rate of the sheath component exceeded the upper limit of the present invention, and polymer deterioration was liable to occur during composite spinning or heat sealing, resulting in hot water. The low-molecular-weight components eluted at high rates, and when used as a coffee bag, unpleasant odor was generated in the coffee, resulting in poor practicality.

【００９７】比較例２は、芯鞘型長繊維の替わりにポリ
エチレンの単一成分からなる長繊維を用いたため、得ら
れた長繊維不織布は引張強力ＭＤに劣り、また、単一成
分からなるためにヒートシール性に劣り、得られたコー
ヒーバッグにはヒートシール不良が２０％もあり製袋性
に劣るものであった。また、加工温度範囲が極めて狭
く、ヒートシール時の加工温度が５℃アップするとシー
ル部が全融してしまい操業性に劣るという問題もあっ
た。特に面積収縮率が高いために、コーヒーの抽出に要
する時間が２倍も長くなるという問題やコーヒーバッグ
の一部が破損して内容物が抽出液中に混入するという問
題も生じた。また、長繊維不織布の熱水中への溶出率が
高くなり、ブラジル産本来のコーヒーの香りが生かされ
ず、渋みのある味に変化して実用性にも劣るものとなっ
た。In Comparative Example 2, since a long fiber consisting of a single component of polyethylene was used instead of the core-sheath type long fiber, the obtained long-fiber nonwoven fabric was inferior in tensile strength MD and consisted of a single component. In addition, the obtained coffee bag had poor heat sealability as much as 20% and was inferior in bag making property. Further, the processing temperature range is extremely narrow, and if the processing temperature during heat sealing is increased by 5 ° C., there is also a problem that the seal portion is completely melted and the operability is poor. In particular, since the area shrinkage rate is high, the problem that the time required for coffee extraction is twice as long and the problem that a part of the coffee bag is damaged and the contents are mixed into the extract have arisen. In addition, the rate of dissolution of the long-fiber nonwoven fabric into hot water was increased, and the original flavor of Brazilian coffee was not used, and the taste changed to a bitter taste, resulting in poor practicality.

【００９８】比較例３は、フェノール系添加剤が配合さ
れていなかったため、溶融した際のポリマーは熱劣化が
大きく、長繊維不織布の物性面では、殆ど影響を示さな
いものの、溶出率が極端に高くなって、コーヒーバッグ
のように熱水中で使用する包材として使用するには全く
適さず、上記比較例１、２と同様に実用性に劣るものと
なった。In Comparative Example 3, since the phenol-based additive was not blended, the polymer when melted was greatly deteriorated by heat, and had little effect on the physical properties of the long-fiber nonwoven fabric, but the dissolution rate was extremely high. It became completely unsuitable for use as a packaging material used in hot water like a coffee bag, and was inferior in practicality as in Comparative Examples 1 and 2.

【００９９】比較例４は、フェノール系添加剤の代わり
にリン系の酸化防止剤を用いたため、添加剤の融点は高
いものの鞘成分の熱減量率は高くなり、不織布として成
形した際には溶出率が高くなり、上記比較例１、２と同
様に実用性に劣るものとなった。In Comparative Example 4, since the phosphorus-based antioxidant was used instead of the phenolic additive, the melting point of the additive was high, but the heat loss of the sheath component was high. As a result, the practicality was inferior as in Comparative Examples 1 and 2.

【０１００】比較例５は、糸条の牽引速度を低下させた
ため、長繊維不織布の面積収縮率が非常に高くなった。
ヒートシール温度を下げることにより包材の製袋性には
あまり問題が生じなかったが、コーヒーバッグとして用
いた場合には、不織布が収縮してコーヒーの抽出にかか
る時間が長くなり、コーヒー本来の味が薄いという問題
が生じたため実用性に劣るものとなった。In Comparative Example 5, the area shrinkage of the long-fiber nonwoven fabric was extremely high because the pulling speed of the yarn was reduced.
Lowering the heat-sealing temperature did not cause much problem with the bag-making properties of the packaging material, but when used as a coffee bag, the nonwoven fabric shrinks and the time it takes to extract the coffee becomes longer, and the original coffee Due to the problem of light taste, it became inferior in practical use.

【０１０１】[0101]

【発明の効果】このように本発明によれば、包材を構成
する複合長繊維不織布の熱水可溶成分の溶出率ＨＷＤを
０．０４％以下となるように調整することで、熱水中や
溶剤中へのポリエチレン系重合体の低分子量成分の溶出
を無くすことができる。また、熱水処理時における複合
長繊維不織布の面積収縮率ＨＷＳを８％より小さくする
ことで、熱水中で包材として使用しても収縮による破損
やそれに伴う内容物の露出等が無くなる。従って、特に
コーヒーや紅茶等のティーバッグ形式の食品包材のよう
に熱水中で使用する包材として用いた場合でも、ポリエ
チレン系重合体特有の異臭がすることがなく、収縮によ
る破損やそれに伴う内容物の露出等もないため、ティー
バッグ形式の食品包材として好適に使用できる包材が提
供できる。As described above, according to the present invention, by adjusting the dissolution rate HWD of the hot water-soluble component of the composite long-fiber nonwoven fabric constituting the packaging material to be 0.04% or less, the hot water It is possible to eliminate the elution of the low molecular weight component of the polyethylene polymer into the medium or into the solvent. Further, by setting the area shrinkage HWS of the composite long-fiber nonwoven fabric at the time of hot water treatment to be less than 8%, even when used as a packaging material in hot water, damage due to shrinkage and accompanying exposure of contents are eliminated. Therefore, even when used as a packaging material used in hot water, such as a tea bag type food packaging material such as coffee or tea, there is no peculiar smell peculiar to the polyethylene polymer, and damage due to shrinkage and Since there is no accompanying exposure of the contents, a packaging material that can be suitably used as a tea bag type food packaging material can be provided.

【０１０２】また、包材を構成する不織布は、芯鞘型複
合長繊維の鞘成分の軟化あるいは溶融により長繊維相互
間が散点状に融着されることにより形成されるため、不
織布強力が極めて高く、リントの発生が無く、形態保持
性や不織布の曲げ易さやハンドリングの良いものであ
り、しかも前記不織布は、ヒートシール性にも優れてい
るため、製袋性や実用性にも優れた複合長繊維からなる
包材を提供することができる。Further, the nonwoven fabric constituting the packaging material is formed by fusing the long fibers with each other in a scattered manner by softening or melting the sheath component of the core-sheath type composite long fiber. It is extremely high, does not generate lint, has good shape retention, easy bending of the nonwoven fabric, and good handling.Moreover, since the nonwoven fabric is excellent in heat sealability, it is also excellent in bag making and practicality. It is possible to provide a packaging material made of a composite long fiber.

【０１０３】従って、本発明における複合長繊維不織布
からなる包材は、上述のようなティーバッグ形式の食品
包材だけでなく、かつお節等煮出し用袋といった食品包
材や、靴やバック等の所謂皮革製品やカセットやレコー
ダーやラジオ等の弱電製品の袋状包装材料や、引っ越し
のために移動する物の保護材等幅広い分野で好適に使用
できる。Therefore, the packaging material of the present invention composed of the nonwoven fabric of a composite long fiber is not limited to the above-mentioned tea bag type food packaging material, but also a food packaging material such as a sushi bag or a so-called food such as shoes and bags. It can be suitably used in a wide range of fields, such as bag-like packaging materials for leather goods, cassettes, recorders, radios, and other weak electric appliances, and protective materials for moving objects for moving.

Claims (4)

【特許請求の範囲】[Claims] 【請求項1】 ポリプロピレン系重合体を芯成分とする
とともに、この芯成分よりも融点が低いポリエチレン系
重合体を鞘成分とした芯鞘型の複合長繊維の鞘成分の軟
化あるいは溶融により長繊維相互間が散点状に融着され
た複合長繊維不織布からなり、かつ、前記複合長繊維不
織布は下記式及び式を同時に満たすことを特徴とす
る複合長繊維不織布からなる包材。 ＨＷＤ≦０．０４％ ・・・ ＨＷＳ≦８％ ・・・ なお、上記ＨＷＤは、１：１００の浴比で、９８℃の熱
水を用いて長繊維不織布を１０分間熱水処理した際の熱
水可溶成分の溶出率を表し、ＨＷＳは前記熱水処理時に
おける長繊維不織布の面積収縮率を表す。1. A filament obtained by softening or melting a sheath component of a core-sheath type composite filament having a polypropylene polymer as a core component and a polyethylene polymer having a lower melting point than the core component as a sheath component. A packaging material comprising a composite long-fiber nonwoven fabric comprising a composite long-fiber nonwoven fabric fused to each other in a scattered manner, wherein the composite long-fiber nonwoven fabric simultaneously satisfies the following formulas. HWD ≤ 0.04% ... HWS ≤ 8% ... The above-mentioned HWD is obtained by treating the long-fiber nonwoven fabric with hot water at 98 ° C for 10 minutes using hot water at a bath ratio of 1: 100. HWS represents the elution rate of the hot water soluble component, and HWS represents the area shrinkage rate of the long fiber nonwoven fabric during the hot water treatment. 【請求項2】 少なくとも鞘成分のポリエチレン系重合
体には、融点が１４０℃以上のフェノール系添加剤と、
中和剤とが添加されていることを特徴とする請求項１記
載の複合長繊維不織布からなる包材。A phenolic additive having a melting point of at least 140 ° C.
The packaging material comprising a composite long-fiber nonwoven fabric according to claim 1, further comprising a neutralizing agent. 【請求項3】 パーキンエルマー社製の熱重量計（型番
ＴＧＡ−７）を用い、昇温速度が２０℃／分で２３０℃
の空気中の雰囲気下で測定した熱減量率が５％以下であ
るポリエチレン系重合体を鞘成分とすることを特徴とす
る請求項１又は２記載の複合長繊維不織布からなる包
材。3. A thermogravimeter (Model No. TGA-7) manufactured by Perkin Elmer Co., Ltd., which was heated at a heating rate of 20 ° C./min to 230 ° C.
The packaging material comprising a composite long-fiber nonwoven fabric according to claim 1 or 2, wherein the sheath component is a polyethylene-based polymer having a heat loss rate of 5% or less measured in an air atmosphere. 【請求項4】 不織布の強力が縦方向で５ｋｇ／５ｃｍ
幅以上、横方向で１ｋｇ／５ｃｍ幅以上であることを特
徴とする請求項１から３のいずれか１項記載の複合長繊
維不織布からなる包材。4. The strength of the nonwoven fabric is 5 kg / 5 cm in the vertical direction.
The packaging material comprising the composite long-fiber nonwoven fabric according to any one of claims 1 to 3, wherein the packaging material has a width of not less than 1 kg / 5 cm in a width direction.
JP9264704A 1997-09-30 1997-09-30 Packaging material comprising conjugate filament nonwoven fabric Pending JPH11107153A (en)