JPH101900A - Highly oil absorbing absorbent paper for makeup and its production - Google Patents
Highly oil absorbing absorbent paper for makeup and its productionInfo
- Publication number
- JPH101900A JPH101900A JP8154272A JP15427296A JPH101900A JP H101900 A JPH101900 A JP H101900A JP 8154272 A JP8154272 A JP 8154272A JP 15427296 A JP15427296 A JP 15427296A JP H101900 A JPH101900 A JP H101900A
- Authority
- JP
- Japan
- Prior art keywords
- paper
- absorbing
- layer
- highly oil
- makeup
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【発明の属する技術分野】この発明は、高吸化粧用脂取
り紙及びその製造方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a high-absorbency cosmetic absorbent paper and a method for producing the same.
【0002】[0002]
【従来の技術】人間の顔面、特に鼻、頬、額、眉毛間等
は皮脂の分泌が盛んで油っぽくなり易く、従って、その
部分では化粧崩れを起こし易い。一般に皮脂が浮いたま
ま化粧をすると、皮膚に化粧料が馴染まないため、顔面
の脂分を化粧用脂取り紙にて取り除いてから化粧し、効
果を上げている。これは化粧直しの場合も同様である。
従来の化粧用脂取り紙は古くから箔打紙が使われてお
り、名塩紙が有名である。この紙は、西宮市名塩産で、
三椏、楮、雁皮に特殊な泥、例えば、金箔打ちには東久
保土と呼ぶ白色のもの、銀箔打ちには蛇豆土という茶褐
色のものを混入して漉いた紙である。2. Description of the Related Art The face of a human, particularly between the nose, cheeks, forehead, and eyebrows, tends to become greasy due to the secretion of sebum, and the makeup tends to be lost in that part. In general, if makeup is applied while sebum is floating, cosmetics do not fit into the skin. Therefore, makeup is applied after removing fat on the face with a cosmetic fat removing paper. This is the same in the case of makeup correction.
Foiled paper has been used for a long time as the conventional degreasing paper for makeup, and Meisho paper is famous. This paper is from Nishinomiya City
It is a paper made by mixing mitsumata, mulberry, and goosepicks with special mud, for example, gold-foiled with a white thing called Higashikubo soil, and silver-foiled with a dark brown thing called snake bean soil.
【0003】又、箔打紙は箔打ちを15回ほど使用する
と、箔を打ちを延ばす働きがなくなり、これを女性の脂
取り化粧紙として用いられている。名塩紙は箱打ち後、
密度が0.94kg/cm3 と非常に高くなり、これを
脂取り化粧紙として用いると、顔面の油脂分が除かれ、
風呂に浴したようになるので、またの名を風呂屋紙とし
て早くから用いられてきた。When the foil punching paper is used about 15 times for foil punching, it loses the function of extending the foil punching and is used as a female degreasing decorative paper. After salting paper,
The density is as high as 0.94 kg / cm 3, and when this is used as a grease-removing decorative paper, the grease on the face is removed,
Since he started to take a bath, his name has been used as a bathhouse paper for a long time.
【0004】[0004]
【発明が解決しようとする課題】従来の技術で使用され
ている、化粧用脂取り紙は手漉きのため量産するには限
界があり、最近では靭皮繊維に特殊な無機填料、例え
ば、クレー、タルク、カオリン、炭酸カルシウム、酸化
チタン等を混合させた後、特殊な定着剤を投入した後、
抄紙し更に化粧紙として使用後の透明性を上げるため、
名塩紙のような高密度になるようにキャレンダー等によ
り処理を行い、量産使用されている。The cosmetic fat removing paper used in the prior art has a limit in mass production due to hand-making, and recently, a special inorganic filler such as clay, After mixing talc, kaolin, calcium carbonate, titanium oxide, etc., after adding a special fixing agent,
In order to increase transparency after making paper and using it as decorative paper,
It is used in mass production after being processed by a calender etc. so that it has a high density like Nao Shio.
【0005】しかし現行の化粧用脂取り紙では、使用後
の透明性が高く油脂分が取れた様に見えるが、2回、3
回と繰り返しても完全に顔面の油脂分が取れない問題点
がある。[0005] However, with the current cosmetic fat removing paper, the transparency after use is high and it seems that oil and fat are removed.
There is a problem that the oil and fat on the face cannot be completely removed even if it is repeated many times.
【0006】この発明は1回の使用で真の皮脂の高吸収
性があり更に使用後の透明性が高い特性が得られる高吸
油化粧用脂取り紙及びその製造方法を提供することにあ
る。SUMMARY OF THE INVENTION An object of the present invention is to provide a highly oil-absorbing cosmetic fat-absorbing paper, which has a high absorbency of true sebum in one use and a property of high transparency after use, and a method for producing the same.
【0007】[0007]
【課題を解決するための手段】上記の目的を達成するた
めに、この請求項1の発明においては、植物繊維を主成
分とする原料からなり、抄紙時の抄網、ダンディロー
ル、或いはエンボスロール等の凹凸形成部材で片面又は
両面に凹凸層を設けたことを特徴とする高吸油化粧用脂
取り紙をその要旨としている。In order to achieve the above object, according to the first aspect of the present invention, there is provided a raw material mainly composed of vegetable fibers, a papermaking net, a dandy roll or an embossing roll at the time of paper making. The gist of the present invention is a highly oil-absorbing cosmetic fat-absorbing paper characterized in that an uneven layer is provided on one surface or both surfaces of the uneven member.
【0008】この発明での植物繊維は、マニラ麻、亜
麻、黄麻、サイザル麻、ケナフ、雁皮、楮、バナナ繊
維、或は三椏からなる靱皮繊維又は木材パルプから選ば
れた少なくとも一種をいい、主成分とは、前記植物繊維
を50重量部%以上を含むことをいう。[0008] The plant fiber in the present invention refers to at least one selected from bast fiber or wood pulp composed of Manila hemp, flax, jute, sisal, kenaf, ganpi, kozo, banana fiber, mitsumata, Means that the plant fiber is contained at 50% by weight or more.
【0009】凹凸層がない脂取り紙の場合、紙の厚さ方
向のみで吸油するため、紙の厚さにより吸油量が制限さ
れる。又、使用時の肌触り・強度(使用時破けにくい)
・使い易さより、紙の坪量は15〜25g/m2 の範囲
であり、使用時の吸油量には制限があり、特に顔面等の
皮脂の多い場合一枚のみの使用では十分に取れないた
め、2〜3枚使用する場合も生ずる。紙の片面又は両面
に凹凸層がある場合には、その凹部に皮脂が吸収され、
凹凸層面の表層部並びに紙の厚さ方向にて吸油され高い
吸油量が得られるため、特に顔面等の皮脂の多い場合一
枚のみの使用でも十分な効果が得られる。In the case of a degreased paper having no concavo-convex layer, oil is absorbed only in the thickness direction of the paper, so the oil absorption amount is limited by the thickness of the paper. Also, feel and strength when used (hard to break when used)
- from ease of use, the basis weight of the paper is in the range of 15~25g / m 2, there is a limit to the amount of oil absorption during use, enough to take not particularly with the use of only one case a lot of sebum such as facial Therefore, it may occur when two or three sheets are used. If there is an uneven layer on one or both sides of the paper, sebum will be absorbed in the recesses,
Since the oil is absorbed in the surface layer portion of the uneven layer surface and in the thickness direction of the paper and a high oil absorption is obtained, a sufficient effect can be obtained even when only one sheet is used, particularly when the face or the like has a large amount of sebum.
【0010】請求項2の発明は、請求項1において、前
記凹凸層は一層又は二層抄き合わせ抄紙からなることを
その要旨としている。前記凹凸層は、抄紙の段階で抄紙
機のシリンダーワイヤー上に金網又はプラスチックワイ
ヤー又はシリンダーワイヤー上に部分的に目止めを行う
ことにより、一層又は二層から形成される。A second aspect of the present invention is characterized in that, in the first aspect, the concavo-convex layer is made of a single-layer or double-layer laminated paper. The concavo-convex layer is formed of one layer or two layers by partially sealing the metal wire or the plastic wire on the cylinder wire of the paper machine or the cylinder wire at the stage of papermaking.
【0011】請求項3の発明は、請求項2において、二
層抄き合わせで一層はフラットで他の層に凹凸層がある
ことをその要旨としている。請求項4の発明は、請求項
1乃至請求項3のうちいずれかにおいて、凹凸層に填料
が混在することをその要旨としている。[0011] The invention of claim 3 is based on claim 2, and the gist is that two layers are laminated and one layer is flat and another layer has an uneven layer. The gist of the invention of claim 4 is that, in any one of claims 1 to 3, the filler is mixed in the uneven layer.
【0012】填料とは、クレー、タルク、カオリン、炭
酸カルシウム、酸化チタン、あるいはホワイトカーボン
等の填料をいい、この填料が混在することにより、高吸
油し、更に使用後透明性が上がるものをいう。The filler refers to a filler such as clay, talc, kaolin, calcium carbonate, titanium oxide, white carbon, or the like. When the filler is mixed, the filler has a high oil absorption and further increases the transparency after use. .
【0013】請求項5の発明は、請求項1乃至請求項4
のうちいずれかにおいて、紙密度が0.7〜1.2g/
cm3 であることをその要旨としている。0.7〜1.
2g/cm3 の範囲であると、高吸油し、更に使用後非
常に透明性が上がる。紙密度が0.7g/cm3 未満の
場合は、使用後の透明性が悪くなり、1.2g/cm3
を越えると、生産が困難となるため好ましくない。[0013] The invention of claim 5 is the invention of claims 1 to 4.
Paper density is 0.7 to 1.2 g /
The gist is cm 3 . 0.7-1.
When the content is in the range of 2 g / cm 3 , the oil absorption is high, and the transparency is extremely increased after use. When the paper density is less than 0.7 g / cm 3 , the transparency after use becomes poor, and the paper density becomes 1.2 g / cm 3.
Exceeding the range is not preferred because production becomes difficult.
【0014】請求項6の発明は、請求項1乃至請求項5
のうちいずれかにおいて、紙の表面層に金粉を混在させ
たことをその要旨としている。金粉を化粧用脂取り紙の
表面に点在させることによりに高級な名塩紙の様に金箔
工程を通した様な意匠性のある化粧用脂取り紙を得るこ
とができる。The invention according to claim 6 is any one of claims 1 to 5.
In any of the above, the gist is that gold powder is mixed in the surface layer of the paper. By scattering the gold powder on the surface of the cosmetic fat removing paper, it is possible to obtain a decorative fat removing paper having a design like a high-grade salt paper through a gold foil process.
【0015】請求項7の発明は、抄紙時の抄網で線経
0.1〜1 .0mmで5〜40メッシュを使用して凹凸
層を形成した化粧用脂取り紙を要旨としている。線径
0.1mmから1 .0mmの範囲で、かつ5メッシュ〜
40メッシュの範囲の抄網を使用すると、凹凸層による
吸油量及び紙層形成の点で好ましい。0.1mm未満の
線径では、吸油量が増加しないため好ましくなく、1.
0mmを越すと、紙層形成及び強度の点でよくない。
又、5メッシュ未満では、吸油量の点で好ましくなく、
40メッシュを越えると、凹凸層が形成できず好ましく
ない。The invention according to claim 7 is a method for producing a paper net having a meridian of 0.1 to 1. The gist of this invention is a grease-absorbing paper for cosmetics in which an uneven layer is formed using 5 to 40 mesh at 0 mm. Wire diameter 0.1mm to 1. In the range of 0 mm, and 5 mesh ~
It is preferable to use a netting in the range of 40 mesh in terms of the oil absorption by the uneven layer and the formation of the paper layer. A wire diameter of less than 0.1 mm is not preferable because the oil absorption does not increase.
If it exceeds 0 mm, it is not good in terms of paper layer formation and strength.
Further, if the mesh size is less than 5 mesh, it is not preferable in terms of oil absorption,
If it exceeds 40 mesh, an uneven layer cannot be formed, which is not preferable.
【0016】請求項8は植物繊維を主成分とする原料を
抄紙機にて抄紙し、前記抄紙機の抄網で片面又は両面に
凹凸層を形成することを特徴とする高吸油化粧用脂取り
紙の製造方法をその要旨としている。In a preferred embodiment of the invention, the raw material mainly composed of vegetable fiber is made by a paper machine, and an uneven layer is formed on one or both sides of the net by the paper making machine. The gist is a paper manufacturing method.
【0017】(製造方法)原料は、マニラ麻、亜麻、黄
麻、サイザル麻、ケナフ、雁皮、楮、バナナ繊維あるい
は三椏から成る靭皮繊維又は木材パルプから選ばれた少
なくとも一種を50重量部%以上を用いることが望まし
い。50重量部%を下回ると、使用時の脂の取れ方の点
で好ましくない。(Production method) The raw material is at least 50% by weight of at least one selected from bast fiber or wood pulp composed of manila hemp, flax, jute, sisal, kenaf, ganpi, kozo, banana fiber or mitsumata. It is desirable to use. If the amount is less than 50 parts by weight, it is not preferable in terms of removing fats during use.
【0018】ビー夕ー等の叩解機にて所定の叩解度に調
成し、更にタルク等の無機質填料を0.5〜40重量部
混合して均一分散する。そして、そのまま抄紙すると、
繊維への填料定着が悪く、排水の問題並びに工程の汚れ
が発生するため、その後定着剤としてファイレックスR
C104及びファイレックスM(ともに、明成化学工業
株式会社製)等を用い、繊維への定着性を向上する。そ
の後、丸網抄紙機、短網抄紙機、長網抄紙機等の抄き網
であって、線径0.1〜1 .0mmで5〜40メッシュ
のものを使用して網目模様にて一層の凹凸紙を形成す
る、又は抄き網に部分的に金網の目を詰めることにより
その部分は原料が乗らず一層の凹凸紙を形成できる。The mixture is adjusted to a predetermined beating degree with a beating machine such as a beader, and 0.5 to 40 parts by weight of an inorganic filler such as talc is mixed and uniformly dispersed. And if you make the paper as it is,
The filler fixation to the fiber is poor, causing drainage problems and process contamination.
Using C104 and Filex M (both manufactured by Meisei Chemical Industry Co., Ltd.), etc., the fixability to fibers is improved. After that, a wire-making machine such as a round-net paper machine, a short-net paper machine, or a fourdrinier paper machine having a wire diameter of 0.1 to 1. One layer of corrugated paper is formed by forming a layer of corrugated paper in a mesh pattern using 5 mm to 40 mesh of 0 mm, or by partially filling the mesh of the paper making net with no raw material. Can be formed.
【0019】更に二層の場合は抄き漕を2本として一層
と同様、図1(a)に示すように表層と裏層に凹凸層2
0を形成する。又、二層抄き合わせの場合は第一抄き漕
は金網60〜120メッシュを使用して凹凸層のない層
(平滑層)22を形成し、更に第二抄き漕は線径0.1
〜1 .0mmで5〜40メッシュを使用又は部分的に金
網の目を詰めることにより凹凸層21を形成し、坪量1
5〜25g/m2 の紙を抄造する(図1(b)を参
照)。Further, in the case of two layers, two sheeting tanks are used, and as in the case of one layer, as shown in FIG.
0 is formed. In the case of two-layer mixing, the first tank uses a wire mesh of 60 to 120 mesh to form a layer (smooth layer) 22 without an uneven layer. 1
~ 1. The uneven layer 21 is formed by using 5 to 40 mesh with 0 mm or partially filling the mesh of the wire mesh, and the basis weight is 1
Paper of 5 to 25 g / m 2 is made (see FIG. 1 (b)).
【0020】坪量15g/m2 未満の場合、紙の強度が
なく、使用時に破けを生じ易く、又、25g/m2 を越
えると柔軟性がなくなり、使用時肌との馴染みが悪く違
和感があり、さらには、使用時の透明性にもかけるため
25g/m2 以下が好ましい。In the case of less than the basis weight 15 g / m 2, without the strength of the paper, tend to cause torn during use, also eliminates the flexibility exceeds 25 g / m 2, familiar poor incompatibility with when using skin Yes, and more preferably 25 g / m 2 or less in order to increase transparency during use.
【0021】なお、使用される無機質填料はクレー、タ
ルク、カオリン、炭酸カルシウム、酸化チタンあるいは
ホワイトカーボンの中から選ばれたものが使用できる
が、皮脂の吸油量を多くするには、マイクロタルクを使
用し平均粒子径2.5μ以下で表面積13.0 BET
m2 /g以上のものが望ましい。The inorganic filler used can be selected from clay, talc, kaolin, calcium carbonate, titanium oxide and white carbon. To increase the oil absorption of sebum, use micro talc. Used, average particle size 2.5μ or less, surface area 13.0 BET
Those having m 2 / g or more are desirable.
【0022】使用後の透明性を上げるには密度を0.7
〜1.2g/cm3 と高密度化する必要があり、所定の
寸法に裁断した後、箔打ち工程で数百回〜数千回の処理
を行う。なお、箔打ち工程の代りにスーパーキャレンダ
ー及び高圧プレス等により紙の密度を向上する方法もあ
る。To increase the transparency after use, the density should be 0.7.
It is necessary to increase the density to 1.21.2 g / cm 3, and after cutting to a predetermined size, several hundred to several thousand treatments are performed in the foiling step. There is also a method of improving the density of the paper by using a super calender, a high-pressure press or the like instead of the foil stamping step.
【0023】[0023]
【実施例】以下、実施例及び比較例について説明する。 (実施例1)実施例1では、下記の紙料、無機填料、及
び定着剤を使用した。EXAMPLES Examples and comparative examples will be described below. (Example 1) In Example 1, the following paper material, inorganic filler, and fixing agent were used.
【0024】 マニラ麻 叩解度SR30゜ 100部 マイクロタルク 平均粒子径 1.7μ 20部 表面積 16.0 BETm2 /g 定着剤 ファィレックスRC−104 0.5% ファイレックスM 0.3% すなわち、マニラ麻をビーターにて所定の叩解度に調成
し、マイクロタルクを20.0重量部を混合して均一分
散とした。そして、その後、定着剤としてファイレック
スRC−104及びファイレックスM(ともに、明成化
学工業株式会社製)を用いて、繊維へ定着させ、その
後、丸網抄紙機にて抄造した。Manila hemp Beating degree SR 30 ° 100 parts Micro talc Average particle size 1.7 μ 20 parts Surface area 16.0 BETm 2 / g Fixing agent Filex RC-104 0.5% Phyrex M 0.3% That is, Manila hemp is beater Was adjusted to a predetermined beating degree, and 20.0 parts by weight of microtalc was mixed to obtain a uniform dispersion. Then, using Firex RC-104 and Firex M (both manufactured by Meisei Chemical Industry Co., Ltd.) as fixing agents, the fibers were fixed to the fiber, and then the paper was formed by a round mesh paper machine.
【0025】丸網抄紙機の抄き網は線径0.2mmで1
6メッシュのものを使用し、1本バットにて坪量22g
/m2 で片面側に凹凸層を抄紙した後、スーパーキャレ
ンダーにて密度1.0g/cm3 にして化粧用脂取り紙
とした。The net of the round net paper machine has a wire diameter of 0.2 mm and a diameter of 1 mm.
Use 6 mesh, one bat basis weight 22g
/ M 2 , after making a concavo-convex layer on one side with a density of 1.0 g / cm 3 using a super calender, to obtain a cosmetic grease-absorbing paper.
【0026】(比較例1)比較例1では、実施例1と同
一の原料・薬品にてスラリーを調成し、抄き網は線径0
.132mmで90メッシュを使用し、1本バットに
て坪量22g/m2で両面ともに凹凸層のない紙を抄紙
した後、スーパーキャレンダーにて密度1.0g/cm
3 の化粧用脂取り紙とした。(Comparative Example 1) In Comparative Example 1, a slurry was prepared with the same raw materials and chemicals as in Example 1, and the papermaking net had a wire diameter of 0.
. A 90 mm mesh with 132 mm is used, and with a single bat, paper having a basis weight of 22 g / m 2 and no uneven layer on both sides is made, and then the density is 1.0 g / cm with a super calender.
3 was used as a degreasing paper for makeup.
【0027】(実施例2)実施例2では実施例1と同一
の原料・薬品にてスラリーを調成し、1本目のバットの
抄き網は線径0 .132mm、90メッシュを使用して
凹凸のない層を形成、11g/m2 にし、更に2本目の
バットの抄き網は線径0.2mmで16メッシュを使用
し、片面側に凹凸層を11g/m2 にして坪量22g/
m2 の紙を抄き合わせ抄紙した後、スーパーキャレンダ
ーにて密度1.0g/cm3 にし化粧用脂取り紙とし
た。(Example 2) In Example 2, a slurry was prepared with the same raw materials and chemicals as in Example 1, and the papermaking net of the first vat had a wire diameter of 0. A layer having no irregularities is formed by using a 90 mm mesh of 132 mm, and the mesh is made 11 g / m 2 , and the mesh of the second bat is 16 mm with a wire diameter of 0.2 mm, and an irregular layer of 11 g is formed on one side. / M 2 and basis weight 22g /
After the paper combined paper making a paper m 2, and the density of 1.0g / cm 3 in the super calender was cosmetic oil blotting paper.
【0028】比較例1並びに実施例1及び実施例2の化
粧用脂取り紙を使用して下記試験方法にて吸油量を測定
した。 (試験方法) 1.試験片は5cm × 5cmにする。Using the degreasing paper for makeup of Comparative Example 1 and Examples 1 and 2, the oil absorption was measured by the following test method. (Test method) The test piece is 5 cm × 5 cm.
【0029】2.調湿後(JISP8111の条件)の
試験片の重量を測定する。 3.容器の中に入れた亜麻仁油の中に試験片をどぶ漬け
して5分間浸漬する。 4.試験片の一角をピンセットでつかみ、つかんだ角の
対角以外の対角線が平衡となるようにして5分間つる
す。2. The weight of the test piece after humidity adjustment (JISP8111 condition) is measured. 3. The test piece is dipped in flaxseed oil placed in a container and immersed for 5 minutes. 4. Grasp one corner of the test piece with tweezers and suspend for 5 minutes so that the diagonal lines other than the diagonal of the gripped corner are in equilibrium.
【0030】5.5分間つるし終わった試験片を、カッ
プ容器に入れて計量する。 6.下式にて吸油率を演算する。 吸油率(%)= 吸油量(g)/ 吸油前試験片重量
(g)× 100 なお、吸油量(g)は、吸油後試験片重量(g)から吸
油前試験片重量 (g)の差にて求める。The test specimen which has been suspended for 5.5 minutes is put into a cup container and weighed. 6. Calculate the oil absorption by the following formula. Oil absorption rate (%) = Oil absorption amount (g) / Pre-oil absorption test piece weight (g) x 100 The oil absorption amount (g) is the difference between the post-absorption test piece weight (g) and the pre-oil absorption test piece weight (g). Ask for.
【0031】(試験結果)試験結果を表1に示す。(Test Results) The test results are shown in Table 1.
【0032】[0032]
【表1】 上記の表1のごとく比較例1に対して実施例1の方が吸
油率が35.9%も向上した、又実施例2の方では吸油
率が23.4%の向上が認められた。[Table 1] As shown in Table 1 above, the oil absorption rate of Example 1 was improved by 35.9% as compared with Comparative Example 1, and the oil absorption rate of Example 2 was improved by 23.4%.
【0033】(実施例3)この実施例3では、二層抄き
合わせの実施例である。すなわち、実施例3では、図2
に示すように、少なくとも2個の円網12を備えた抄き
合わせ抄紙機3を使用した。又、抄紙機3のプレスロー
ル前に湿紙全幅に流下できるカーテンコータ10を設置
し、第1円網1では実施例1と同じ紙料、無機填料、及
び定着剤を使用したスラリー6から11g/m2 に相当
する湿紙8を形成してフェルト5でピックアップさせ
た。すなわち、前記第1円網1は金網90メッシュを使
用して凹凸層のない層を形成するのである。(Embodiment 3) This embodiment 3 is an embodiment of two-layer papermaking. That is, in the third embodiment, as shown in FIG.
As shown in FIG. 2, a combined paper machine 3 equipped with at least two cylinders 12 was used. Further, a curtain coater 10 capable of flowing down to the full width of the wet paper is installed in front of the press roll of the paper machine 3, and in the first cylinder 1, slurry 6 to 11 g using the same paper material, inorganic filler, and fixing agent as in Example 1 is used. / M 2 was formed and picked up by the felt 5. That is, the first circular mesh 1 forms a layer having no uneven layer by using a wire mesh of 90 mesh.
【0034】又、第2円網2では、実施例1と同じ紙
料、無機填料、定着剤を使用したスラリーにさらに抗菌
填料としてのゼオライト系抗菌填料(ゼオライト、銀、
亜鉛からなる抗菌填料)0.5部を添加したスラリー4
から11g/m2 に相当する湿紙7を形成させて抄き合
わせを行う。なお、この第2円網2は線径0 .3mmで
20メッシュの金網を使用している。従って、この第2
円網2において、凹凸層が形成される。そして、カーテ
ンコーター10から金粉の懸濁液を流下させて、湿紙7
の抗菌填料含有層面に金粉を付着させた。次にヤンキー
ドライヤー(図示しない)で乾燥し、ついで熱キャレン
ダー(図示しない)を用いて処理し、抗菌性を有する重
さ22g/m2 の抗菌化粧紙を得た。なお、図2中、9
は回転ロール、11はカーテンコーター10から流下し
た懸濁液をうけるサクションボックスである。In the second mesh 2, a slurry containing the same paper material, inorganic filler, and fixing agent as in Example 1 is further added to a zeolite-based antibacterial filler (zeolite, silver,
Slurry 4 containing 0.5 part of antibacterial filler composed of zinc)
To form a wet paper 7 corresponding to 11 g / m 2 . The second circular net 2 has a wire diameter of 0. A wire mesh of 3 mm and 20 mesh is used. Therefore, this second
In the circular net 2, an uneven layer is formed. Then, the suspension of the gold powder is allowed to flow down from the curtain coater 10 and the wet paper 7
Gold powder was adhered to the surface of the antibacterial filler-containing layer. Next, it was dried with a Yankee dryer (not shown) and then treated with a thermal calender (not shown) to obtain an antibacterial decorative paper having an antibacterial property and having a weight of 22 g / m 2 . In addition, in FIG.
Is a rotating roll, and 11 is a suction box for receiving the suspension flowing down from the curtain coater 10.
【0035】この化粧紙は抗菌填料配合表面が凹凸層が
形成されるとともに金粉も表面側に偏在することにな
る。この化粧紙を裁断後重ねて箔打ち機にて処理し、表
裏面とも平滑してから製本した。In this decorative paper, the surface containing the antibacterial filler is formed with an uneven layer, and the gold powder is also unevenly distributed on the surface side. The decorative paper was cut, stacked and processed by a foiling machine, and the front and back surfaces were smoothed before binding.
【0036】この実施例では、金粉が表面側に偏在して
いるため、貴重で有用な資源の消費が節減された抗菌化
粧紙となる。 (実施例4)この実施例4は両面が凹凸層のものの実施
例である。In this embodiment, since the gold powder is unevenly distributed on the surface side, the antibacterial decorative paper has a reduced consumption of valuable and useful resources. (Embodiment 4) This embodiment 4 is an embodiment in which both surfaces are uneven layers.
【0037】実施例4 では、実施例1と同一の原料・薬
品にてスラリーを調成し、図2に示すように少なくとも
2個の円網1,2を備えた抄き合わせ抄紙機3を使用し
た。抄紙機3の抄き網は2個の円網1,2とも線径0.
2mmで20メッシュの金網を使用して各坪量11g/m2に
て湿紙形成し、抄き合わせにて両面凹凸層がある22g/
m2の紙を抄紙した。In Example 4, a slurry was prepared from the same raw materials and chemicals as in Example 1, and as shown in FIG. 2, a papermaking machine 3 provided with at least two circular meshes 1 and 2 was used. used. The paper net of the paper machine 3 has a wire diameter of 0.2 for both the two circular nets 1 and 2.
Wet paper is formed at a basis weight of 11 g / m 2 using a 20-mm wire mesh at 2 mm, and the two- sided uneven layer is formed at 22 g / m 2 by laminating.
the paper of m 2 and paper making.
【0038】次いで熱キャレンダーを用い密度1.0g/
cm3 にして化粧用脂取り紙とした。この化粧用脂取り紙
の吸油量を上記実施例1と同様の測定方法にて測定した
結果、表1の通りとなった。Then, using a thermal calender, the density is 1.0 g /
It was made into cm 3 to make a degreasing paper for makeup. The oil absorption of the cosmetic grease-absorbing paper was measured by the same measuring method as in Example 1 above.
【0039】この実施例においても比較例よりも吸油率
が32%向上した。なお、この発明は、前記実施例に限
定されるものではなく、この発明から逸脱しない範囲で
任意に変更可能である。Also in this example, the oil absorption was improved by 32% as compared with the comparative example. It should be noted that the present invention is not limited to the above-mentioned embodiments, and can be arbitrarily modified without departing from the present invention.
【0040】[0040]
【発明の効果】以上詳述したようにこの発明は、化粧用
脂取り紙の片面又は両面に網目等の凹凸層を設けたこと
により、その凹部にて吸油量が大幅に増大し従来使用さ
れている化粧用脂取り紙に比べて真の皮脂量を増大し、
特に皮脂の発生量が多い場合の使用枚数を低減でき更に
使用後の透明感が非常に高いので使用後の満足感が得ら
れる化粧用脂取り紙とすることができる。As described above in detail, according to the present invention, the unevenness layer such as a mesh is provided on one side or both sides of the decorative fat-removing paper, so that the oil absorption in the concave portion is greatly increased, so that the present invention has been used conventionally. The amount of true sebum is increased compared to the existing degreasing paper for makeup,
In particular, when the amount of generated sebum is large, the number of sheets used can be reduced, and the transparency after use is very high.
【図1】(a)は両面に凹凸層を設けた化粧用脂取り上
の断面図、(b)は片面に凹凸層を設けた化粧用脂取り
紙の断面図。FIG. 1 (a) is a cross-sectional view of a makeup degreasing paper having a concavo-convex layer on both sides, and FIG.
【図2】実施例3及び実施例4の抄紙法の略体説明図。FIG. 2 is a schematic explanatory view of the paper making method of Examples 3 and 4.
1…第1円網、2…第2円網、3…抄紙機、4,6…ス
ラリー、5…フェルト、7,8…湿紙、9…回転ロー
ル、10…カーテンコータ、11…サクションボック
ス。DESCRIPTION OF SYMBOLS 1 ... 1st circular mesh, 2 ... 2nd circular mesh, 3 ... Paper machine, 4, 6 ... Slurry, 5 ... Felt, 7, 8 ... Wet paper, 9 ... Rotating roll, 10 ... Curtain coater, 11 ... Suction box .
Claims (8)
片面又は両面に凹凸層を設けたことを特徴とする高吸油
化粧用脂取り紙。1. A raw material containing vegetable fiber as a main component,
A highly oil-absorbing cosmetic fat-absorbing paper, characterized in that an uneven layer is provided on one or both sides.
紙からなる請求項1の高吸油化粧用脂取り紙。2. The high-oil-absorbing cosmetic fat-absorbing paper according to claim 1, wherein the uneven layer comprises a single-layer or two-layer laminated paper.
層に凹凸層がある請求項2に記載の高吸油化粧用脂取り
紙。3. The highly oil-absorbing cosmetic fat-absorbing paper according to claim 2, wherein two layers are laminated and one layer is flat and the other layer has an uneven layer.
求項3のうちいずれかに記載の高吸油化粧用脂取り紙。4. The highly oil-absorbing cosmetic degreasing paper according to claim 1, wherein a filler is mixed in the uneven layer.
求項1乃至請求項4のうちいずれかに記載の高吸油化粧
用脂取り紙。5. The highly oil-absorbing cosmetic fat removing paper according to claim 1, wherein the paper density is 0.7 to 1.2 g / cm 3 .
乃至請求項5のうちいずれかに記載の高吸油化粧用脂取
り紙。6. The paper according to claim 1, wherein gold powder is mixed in the surface layer of the paper.
A highly oil-absorbing cosmetic fat-absorbing paper according to any one of claims 1 to 5.
40メッシュの抄網にて凹凸層を形成した高吸油化粧用
脂取り紙。7. A paper having a line length of 0.1 to 1.0 mm and a paper making value of 5 to 5.
Highly oil-absorbing cosmetic grease-absorbing paper with an uneven layer formed by a 40-mesh net.
て抄紙し、前記抄紙機の抄網で片面又は両面に凹凸層を
形成することを特徴とする高吸油化粧用脂取り紙の製造
方法。8. A highly oil-absorbing decorative grease-absorbing paper, characterized in that a raw material mainly composed of vegetable fiber is made with a paper machine, and an uneven layer is formed on one or both sides with a paper making net of the paper machine. Production method.