JPH0965946A - Panel - Google Patents
PanelInfo
- Publication number
- JPH0965946A JPH0965946A JP24530395A JP24530395A JPH0965946A JP H0965946 A JPH0965946 A JP H0965946A JP 24530395 A JP24530395 A JP 24530395A JP 24530395 A JP24530395 A JP 24530395A JP H0965946 A JPH0965946 A JP H0965946A
- Authority
- JP
- Japan
- Prior art keywords
- organic
- base material
- transfer
- binder
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、表面に絵柄を有する化
粧板に関するもので、詳しくは、印刷による美麗な装飾
と、堅牢性、耐汚染性、耐久性、難燃性を併せ持つ意匠
性の高い化粧板に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a decorative plate having a pattern on its surface, and more specifically, it has a design that combines beautiful decoration by printing with fastness, stain resistance, durability and flame retardancy. It is about a high veneer.
【０００２】[0002]
【従来の技術】従来、住宅等の外装や内装用として各種
化粧板が使用されている。2. Description of the Related Art Conventionally, various decorative boards have been used for exteriors and interiors of houses and the like.
【０００３】例えば、外装用途としては、窯業系サイデ
ィングやＡＬＣといった無機系の建材が使われるように
なってきたが、近年の高級化、高意匠化の傾向ととも
に、表面にエンボスを設けた製品が好まれるようになっ
てきた。特に外壁材として非常に高級感のあるレンガや
タイルを模した窯業系サイディングは、実際のレンガや
タイルの施工を行うよりもはるかに簡便で且つ安価な施
工を行うことができる。[0003] For example, for exterior applications, inorganic building materials such as ceramic siding and ALC have come to be used, but with the recent trend toward higher grades and higher designs, products with embossed surfaces are being used. It has become popular. In particular, ceramic siding that imitates bricks and tiles with a very high-grade appearance as outer wall materials can be performed much more simply and cheaper than actual bricks and tiles.
【０００４】しかし、この窯業系サイディングはエンボ
スによる装飾を主な目的として製造されているため、カ
ラーデザインについては立ち遅れているのが現状であ
る。すなわち、ほとんどの製品は全面単色の塗料を塗装
するか、あるいは目地部分に異なる色を用いた２色の塗
装を行うに過ぎない。また、最近ではダイレクトグラビ
ア方式を用いた意匠性の高い製品も販売されているが、
この方法で得られる意匠効果は限られたものであり、本
物のレンガやタイルと比べるとあまり満足のいくもので
はなかった。However, since this ceramic siding is manufactured mainly for the purpose of embossing decoration, the color design is currently behind. In other words, most products are painted with a single-color paint on the entire surface, or simply painted with two colors using different colors at joints. In addition, recently, products with high designability using the direct gravure method are also sold,
The design effect obtained with this method was limited and not very satisfactory compared to real bricks and tiles.
【０００５】また、最近では、外装用途であることに鑑
み、堅牢性、耐汚染性、耐久性に富む無機系の塗料によ
る仕上げを行った窯業系サイディングも販売されている
が、塗装であるが故に、色調については単調なものであ
り、あくまでその機能性を重点においたものである。Further, recently, in view of its use as an exterior, ceramic siding finished by using an inorganic paint having high robustness, stain resistance, and durability is also on sale. Therefore, the color tone is monotonous, and its functionality is emphasized.
【０００６】一方、内装用途に関しては、物性的には外
装ほどの耐久性を要求されていないため、使用目的、使
用部位、意匠性などから様々な種類の化粧板が知られて
いる。例えば、紙あるいは合成樹脂フィルムに印刷を施
したもの、紙に印刷を施し合成樹脂を含浸させたもの、
あるいは天然木を薄くスライスしたものを基材に貼り合
わせたもの、等が化粧板として使用されている。また、
合成樹脂に顔料を練り込み硬化させ、それ自体を化粧板
とするものもある。On the other hand, for interior applications, since the physical properties are not required to be as durable as the exterior, various types of decorative boards are known in terms of purpose of use, site of use, designability and the like. For example, paper or synthetic resin film printed, paper printed and impregnated with synthetic resin,
Alternatively, a thin slice of natural wood, which is attached to a base material, or the like is used as a decorative board. Also,
There is also one in which a pigment is kneaded into a synthetic resin and cured to form a decorative board itself.
【０００７】これら内装用途の化粧板の中で、内装制限
の対象となる住宅の台所やビル等、不燃性、難燃性を必
要とされるものの場合には、繊維強化セメント板のよう
な無機系の基材が主に使用されている。これらの基材に
印刷による意匠性を持たせるために、従来では印刷を施
した紙やフィルムを接着剤により基材と貼り合わせるこ
とが行われているが、そういった印刷物自体には不燃性
や難燃性がない場合がほとんどである。そのため、印刷
物に不燃性や難燃性を付与するためには、材質の改良や
難燃剤の添加などを行う必要があった。Among these decorative veneers for interior applications, in the case of non-combustible and flame-retardant materials such as kitchens and buildings of houses subject to interior restriction, inorganic materials such as fiber reinforced cement boards are used. The base material of the system is mainly used. In order to give these substrates a design effect by printing, conventionally, printed paper or film is attached to the substrate with an adhesive, but such printed matter itself is nonflammable and difficult. In most cases, it is not flammable. Therefore, in order to impart nonflammability and flame retardancy to the printed matter, it is necessary to improve the material and add a flame retardant.
【０００８】また、内装用途の無機系の化粧板も、最近
の高級化、高意匠化の流れから、表面にエンボスを施し
た製品が販売されている。しかし、無機系の基材自体に
エンボスを施した場合には、前述の窯業系サイディング
同様、単色の塗装によるものがほとんどであり、意匠性
に乏しかった。As for inorganic decorative sheets for interior use, products having embossed surfaces are now on the market due to the recent trend toward higher grades and higher designs. However, when the inorganic base material itself is embossed, it is mostly painted by a single color like the above-mentioned ceramic siding, and the design is poor.
【０００９】また、スクリーン印刷法によりレリーフ調
の盛り上げ印刷を行った製品もあるが、この方法による
と、加工が煩雑な上、連続諧調の絵柄が出来ないなどの
制限があった。Further, there is a product in which relief printing is carried out by screen printing, but this method has a limitation in that processing is complicated and a continuous tone pattern cannot be formed.
【００１０】[0010]
【発明が解決しようとする課題】本発明は、上記従来の
問題点に鑑み為されたもので、その目的とするところ
は、表面に印刷による美麗な装飾と、堅牢性、耐汚染
性、耐久性、難燃性を併せ持つ意匠性の高い化粧板を提
供することにある。SUMMARY OF THE INVENTION The present invention has been made in view of the above-mentioned problems of the prior art. The object of the present invention is to make a beautiful decoration by printing on the surface and to provide fastness, stain resistance and durability. It is to provide a decorative plate having high designability that has both properties and flame retardancy.
【００１１】[0011]
【課題を解決するための手段】上記目的を達成するため
に、本発明の化粧板は、基材に所望の転写装飾模様を施
した化粧板であって、基材に有機無機複合高分子をバイ
ンダーとする塗料を塗布して下地層を形成し、この上
に、予めバインダーと顔料とを少なくとも含むインキを
用いて転写基体上に所望の絵柄を形成した転写シートを
圧着して絵柄を付与した後、表面に有機無機複合高分子
からなる透明保護層を設けたことを特徴としている。In order to achieve the above object, the decorative board of the present invention is a decorative board in which a desired transfer decorative pattern is applied to a base material, and an organic-inorganic composite polymer is applied to the base material. A coating material as a binder is applied to form a base layer, and a transfer sheet on which a desired pattern is formed on a transfer substrate using an ink containing at least a binder and a pigment in advance is pressure-bonded on the transfer sheet. After that, a transparent protective layer made of an organic-inorganic composite polymer is provided on the surface.
【００１２】また、本発明の化粧板は、前記インキのバ
インダーとして、有機無機複合高分子を用いたことを特
徴としている。The decorative board of the present invention is characterized in that an organic-inorganic composite polymer is used as a binder for the ink.
【００１３】また、本発明の化粧板は、前記有機無機複
合高分子が、（I）一般式 ＲnＳｉ（ＯＲ’）4-n［式
中、Ｒは炭素数１〜８の有機基、Ｒ’は炭素数１〜５の
有機基、ｎは０〜２の整数を示す。］で表されるアルコ
キシシランの加水分解縮合物、又は、（II）シリル基含
有ビニル系樹脂、或いはこれらの混合物であることを特
徴としている。In the decorative board of the present invention, the organic-inorganic composite polymer is (I) a general formula R n Si (OR ') 4-n [wherein R is an organic group having 1 to 8 carbon atoms, R ′ represents an organic group having 1 to 5 carbon atoms, and n represents an integer of 0 to 2. ] Hydrolyzed condensate of alkoxysilane represented by the above formula, or (II) silyl group-containing vinyl resin, or a mixture thereof.
【００１４】さらに、本発明の化粧板は、前記基材とし
て、窯業系基材を用いることを特徴としている。Further, the decorative board of the present invention is characterized in that a ceramic base material is used as the base material.
【００１５】以下、本発明をさらに詳しく説明する。The present invention will be described in more detail below.
【００１６】本発明の化粧板は、次のような構成を有す
る。The decorative board of the present invention has the following structure.
【００１７】すなわち、化粧基材の装飾面に、後述する
有機無機複合高分子を主体成分とする塗料を塗布するこ
とにより下地層を形成する。That is, a base layer is formed by applying a coating material containing an organic-inorganic composite polymer described later as a main component on the decorative surface of the decorative base material.
【００１８】一方、有機無機複合高分子等のバインダー
と顔料からなる絵柄層を基体シート上に剥離可能に設け
た転写シートを用意しておき、上記下地層の上に圧着一
体化する。次いで、上記基体シートを剥離することによ
り、絵柄層の転移された化粧板を得る。この上にさら
に、有機無機複合高分子をバインダーとする透明保護層
を設ける。これによって、印刷絵柄層による美麗な装飾
と、堅牢性、耐汚染性、耐久性を併せ持つ化粧板が出来
上がる。また、基材に窯業系基材を用いた場合、基材及
び塗膜自体が難燃性であることから、難燃性の化粧板が
得られる。On the other hand, a transfer sheet is provided in which a pattern layer composed of a binder such as an organic-inorganic composite polymer and a pigment is removably provided on a base sheet, and pressure-bonded integrally on the above-mentioned base layer. Then, the base sheet is peeled off to obtain a decorative plate to which the pattern layer is transferred. A transparent protective layer having an organic-inorganic composite polymer as a binder is further provided thereon. As a result, a decorative board having beautiful decoration with a printed pattern layer, and having robustness, stain resistance, and durability is completed. When a ceramic base material is used as the base material, a flame-retardant decorative board can be obtained because the base material and the coating film itself are flame-retardant.
【００１９】本発明では、上記のように、有機無機複合
高分子をバインダーとする塗料を用いることを特徴とし
ている。As described above, the present invention is characterized by using the coating material containing the organic-inorganic composite polymer as a binder.
【００２０】本発明に好適に用いられる有機無機複合高
分子としては、例えば、アルコキシシランの加水分解縮
合物並びにシリル基含有ビニル系樹脂が挙げられる。以
下に、本発明に好適に用いられる有機無機複合高分子で
ある、アルコキシシランの加水分解縮合物並びにシリル
基含有ビニル系樹脂について説明する。Examples of the organic-inorganic composite polymer preferably used in the present invention include a hydrolysis-condensation product of an alkoxysilane and a silyl group-containing vinyl resin. Hereinafter, the hydrolysis-condensation product of alkoxysilane and the silyl group-containing vinyl resin, which are organic-inorganic composite polymers suitably used in the present invention, will be described.
【００２１】上記のアルコキシシランは、ＲnＳｉ（Ｏ
Ｒ’）4-nで表される化合物であり、ｎは０〜２の整数
であるが、特にｎが０もしくは１であるアルコキシシラ
ンを主成分とするものが、耐クラック性、耐候性に優れ
ているので好ましい。Ｒは炭素数１〜８、好ましくは１
〜３の有機基であり、具体的には、メチル基、エチル
基、ｎ−プロピル基、ｉ−プロピル基などのアルキル
基、γ−クロロプロピル基、ビニル基、トリクロロプロ
ピル基、γ−グリシドキシプロピル基、γ−メタクリル
オキシプロピル基、γ−メルカプトプロピル基、フェニ
ル基、エポキシシクロヘキシルエチル基、γ−アミノプ
ロピル基などが代表的なものとして挙げられる。また、
Ｒ’は炭素数１〜５、好ましくは１〜４の有機基であ
り、具体的には、メチル基、エチル基、ｎ−プロピル
基、ｉ−プロピル基、ｎ−ブチル基、ｓｅｃ−ブチル
基、ｔｅｒｔ−ブチル基等のアルキル基や、アセチル基
等のアシル基などが代表的なものとして挙げられる。The above-mentioned alkoxysilane is R n Si (O
R ′) 4-n is a compound represented by n , and n is an integer of 0 to 2, and particularly, a compound mainly containing an alkoxysilane in which n is 0 or 1 is excellent in crack resistance and weather resistance. It is preferable because it is excellent. R has 1 to 8 carbon atoms, preferably 1
To 3 organic groups, specifically, alkyl groups such as methyl group, ethyl group, n-propyl group, i-propyl group, γ-chloropropyl group, vinyl group, trichloropropyl group, γ-glycid Representative examples include a xypropyl group, a γ-methacryloxypropyl group, a γ-mercaptopropyl group, a phenyl group, an epoxycyclohexylethyl group, and a γ-aminopropyl group. Also,
R'is an organic group having 1 to 5 carbon atoms, preferably 1 to 4 carbon atoms, and specifically, methyl group, ethyl group, n-propyl group, i-propyl group, n-butyl group, sec-butyl group. Representative examples thereof include an alkyl group such as a tert-butyl group and an acyl group such as an acetyl group.
【００２２】上記アルコキシシランとして具体的には、
テトラメトキシシラン、テトラエトキシシラン、テトラ
プロポキシシラン、テトラブトキシシラン、メチルトリ
メトキシシラン、メチルトリエトキシシラン、エチルト
リメトキシシラン、プロピルトリメトキシシラン、プロ
ピルトリエトキシシラン、クロロプロピルトリメトキシ
シラン、ビニルトリメトキシシラン、トリクロロプロピ
ルトリメトキシシラン、γ−グリシドキシプロピルトリ
メトキシシラン、γ−メタクリルオキシプロピルトリエ
トキシシラン、フェニルトリメトキシシラン、γ−アミ
ノプロピルトリメトキシシラン、エポキシシクロヘキシ
ルエチルトリメトキシシラン、フェニルメチルジメトキ
シシラン、ジメチルジメトキシシラン、γ−グリシドキ
シプロピルメチルジメトキシシランなどが代表的なもの
として挙げられる。Specifically as the above-mentioned alkoxysilane,
Tetramethoxysilane, tetraethoxysilane, tetrapropoxysilane, tetrabutoxysilane, methyltrimethoxysilane, methyltriethoxysilane, ethyltrimethoxysilane, propyltrimethoxysilane, propyltriethoxysilane, chloropropyltrimethoxysilane, vinyltrimethoxy Silane, trichloropropyltrimethoxysilane, γ-glycidoxypropyltrimethoxysilane, γ-methacryloxypropyltriethoxysilane, phenyltrimethoxysilane, γ-aminopropyltrimethoxysilane, epoxycyclohexylethyltrimethoxysilane, phenylmethyldimethoxy Typical examples include silane, dimethyldimethoxysilane, and γ-glycidoxypropylmethyldimethoxysilane.
【００２３】これらアルコキシシランの加水分解縮合物
は、例えばアルコール等の溶液中で必要量の水及び酸触
媒を用いて反応させることにより得られるもので、分子
量は、ポリスチレン換算重量平均分子量（以下同様）１
０００〜１０００００、好ましくは３０００〜３０００
０のものが適当である。The hydrolyzed condensates of these alkoxysilanes are obtained, for example, by reacting with a necessary amount of water and an acid catalyst in a solution of alcohol or the like, and the molecular weight is the polystyrene-reduced weight average molecular weight (the same applies hereinafter). ) 1
000 to 100,000, preferably 3000 to 3000
A value of 0 is appropriate.
【００２４】一方、前記シリル基含有ビニル系樹脂とし
ては、 ［式中、Ｘはハロゲン、アルコキシ、アシルオキシ、ケ
トキシメート、アミノ、酸アミド、アミドオキシ、メル
カプト、アルケニルオキシ、フェノキシ等の加水分解性
基を示し、Ｒ1及びＲ2はそれぞれ、水素原子又は炭素数
１〜１０のアルキル基、アリール基、アラルキル基等の
１価の炭化水素基を示し、ｎは１〜３の整数を示す。］
で表されるシリル基を分子中に少なくとも１つ以上有す
る、分子量が１０００〜５００００の樹脂が好ましい。On the other hand, as the silyl group-containing vinyl resin, [In the formula, X represents a hydrolyzable group such as halogen, alkoxy, acyloxy, ketoximate, amino, acid amide, amidooxy, mercapto, alkenyloxy, and phenoxy, and R 1 and R 2 are each a hydrogen atom or a carbon number of 1 10 represents a monovalent hydrocarbon group such as an alkyl group, an aryl group and an aralkyl group, and n represents an integer of 1 to 3. ]
A resin having at least one silyl group represented by and having a molecular weight of 1,000 to 50,000 is preferable.
【００２５】該樹脂は、 ［式中、Ｘ、Ｒ1、ｎはそれぞれ前述と同様のものを示
す。］で表されるヒドロシラン化合物と炭素−炭素二重
結合を有するビニル系樹脂を触媒存在下で反応させるこ
とにより製造される。The resin is [In the formula, each of X, R 1 and n is the same as described above. ] It manufactures by making the hydrosilane compound and the vinyl resin which have a carbon-carbon double bond react with the presence of a catalyst.
【００２６】ここで、上記ヒドロシラン化合物として具
体的には、メチルジクロロシラン、メチルジエトキシシ
ラン、メチルジアセトキシシラン、メチルジアミノキシ
シラン等が代表的なものとして挙げられる。なお、ヒド
ロシラン化合物量は、ビニル系樹脂中に含まれる炭素−
炭素二重結合に対し、０．５〜２倍モル量の使用が適当
である。Specific examples of the hydrosilane compound include methyldichlorosilane, methyldiethoxysilane, methyldiacetoxysilane, and methyldiaminoxysilane. The amount of the hydrosilane compound is the amount of carbon contained in the vinyl resin.
It is suitable to use 0.5 to 2 times the molar amount of the carbon double bond.
【００２７】上記ビニル系樹脂は、（メタ）アクリル酸
のメチル、エチル、ｎ−ブチル、イソブチル、ｔ−ブチ
ル、２−エチルヘキシル、ベンジル、ｎ−プロピル、イ
ソプロピル等のアルキルエステル；（メタ）アクリル
酸、イタコン酸、無水マレイン酸等のカルボン酸あるい
は酸無水物；グリシジル（メタ）アクリレート等のエポ
キシ化合物；（メタ）アクリルアミド等のアミド化合
物；アクリロニトリル、スチレン、酢酸ビニル等のその
他の化合物等からなる群から選ばれるビニル系モノマー
の共重合体である。該共重合体製造時に、（メタ）アク
リル酸アリルやジアリルフタレート等をラジカル共重合
させることにより、ビニル系樹脂中にヒドロシリル化反
応のための炭素−炭素二重結合の導入が可能である。The vinyl resin is an alkyl ester of (meth) acrylic acid such as methyl, ethyl, n-butyl, isobutyl, t-butyl, 2-ethylhexyl, benzyl, n-propyl and isopropyl; (meth) acrylic acid. Carboxylic acids or acid anhydrides such as itaconic acid and maleic anhydride; epoxy compounds such as glycidyl (meth) acrylate; amide compounds such as (meth) acrylamide; other compounds such as acrylonitrile, styrene, vinyl acetate, etc. It is a copolymer of vinyl monomers selected from By radically copolymerizing allyl (meth) acrylate, diallyl phthalate or the like during the production of the copolymer, it is possible to introduce a carbon-carbon double bond into the vinyl resin for the hydrosilylation reaction.
【００２８】また、シリル基含有ビニル系樹脂のその他
の製造方法として、前記ビニル系モノマーとビニルトリ
クロルシラン、ビニルトリエトキシシラン、ビニルトリ
メトキシシラン、ビニルトリス（β−メトキシエトキ
シ）シラン、γ−メタクリロキシプロピルトリメトキシ
シラン、ビニルトリアセトキシシラン等のビニル基含有
シリル化合物とをラジカル重合させる方法もある。As another method for producing a silyl group-containing vinyl resin, the above vinyl monomer and vinyltrichlorosilane, vinyltriethoxysilane, vinyltrimethoxysilane, vinyltris (β-methoxyethoxy) silane, γ-methacryloxy are used. There is also a method of radically polymerizing a vinyl group-containing silyl compound such as propyltrimethoxysilane and vinyltriacetoxysilane.
【００２９】図１、図２及び図３はそれぞれ本発明に用
いられる転写シートの構成例を示す断面図である。FIGS. 1, 2 and 3 are sectional views showing an example of the structure of a transfer sheet used in the present invention.
【００３０】図１は、ポリ塩化ビニル樹脂フィルム１１
及びポリオレフィン樹脂フィルム１２からなる基体シー
ト１３の表面に絵柄層１４を設けた構成となっている。FIG. 1 shows a polyvinyl chloride resin film 11
The base sheet 13 composed of the polyolefin resin film 12 and the pattern layer 14 is provided on the surface of the base sheet 13.
【００３１】基体シート１３の作製方法は、２種のフィ
ルムを接着剤を介して貼り合わせるドライラミネート
法、熱可塑性樹脂フィルムにポリオレフィン樹脂フィル
ムを溶融させて貼り合わせるエクストルージョン法など
公知の技術を用いればよい。As the method for producing the base sheet 13, known techniques such as a dry laminating method in which two kinds of films are bonded together via an adhesive and an extrusion method in which a polyolefin resin film is melted and bonded to a thermoplastic resin film are used. Good.
【００３２】最近はポリ塩化ビニル樹脂を主体とし、Ａ
ＢＳ等の樹脂を若干加えた３次元成形用のフィルムも市
販されており、このようなフィルムをポリ塩化ビニル樹
脂フィルムの代用に使用してもよい。また、ポリオレフ
ィン樹脂フィルムとしてはポリエチレン樹脂フィルムや
ポリプロピレン樹脂フィルム等を使用することが出来
る。なお、ポリ塩化ビニル樹脂フィルム単体では、絵柄
層のインキに対する剥離機能を有さないことから、剥離
ワニスや離型コート層を設ける必要がある。Recently, mainly polyvinyl chloride resin
A film for three-dimensional molding to which a resin such as BS is added is also commercially available, and such a film may be used as a substitute for the polyvinyl chloride resin film. A polyethylene resin film, a polypropylene resin film, or the like can be used as the polyolefin resin film. Since the polyvinyl chloride resin film alone does not have a peeling function for the ink of the pattern layer, it is necessary to provide a peeling varnish or a release coat layer.
【００３３】図２は、紙２１とポリプロピレンフィルム
２２からなる基体シート２３（一般にＰＰラミネート紙
と呼ばれている）の表面に絵柄層２４を設けた構成とな
っている。In FIG. 2, a pattern layer 24 is provided on the surface of a base sheet 23 (generally called PP laminated paper) consisting of paper 21 and polypropylene film 22.
【００３４】また、図３はポリプロピレン樹脂フィルム
からなる基体シート３１の表面に絵柄層３２を設けた構
成となっている。Further, in FIG. 3, a pattern layer 32 is provided on the surface of a base sheet 31 made of a polypropylene resin film.
【００３５】その他に基体シートとしては、ポリエチレ
ンテレフタレート樹脂フィルム等も使用することが出来
る。基体シートは転写を行う基材の形状により適当な材
質のものを適宜選択すればよい。例えば、基材の表面が
エンボス形状の場合は、転写時の熱によって基材表面の
凹凸に追随することが可能な熱可塑性樹脂フィルムであ
るポリ塩化樹脂フィルムと、インキに対して剥離機能を
有するポリオレフィン樹脂フィルムとの積層フィルム、
あるいはポリプロピレンフィルム等が好適である。In addition, a polyethylene terephthalate resin film or the like can be used as the base sheet. The base sheet may be made of an appropriate material depending on the shape of the base material to be transferred. For example, when the surface of the base material has an embossed shape, it has a peeling function from the polychlorinated resin film, which is a thermoplastic resin film that can follow the irregularities of the base material surface by the heat at the time of transfer, and the ink. Laminated film with polyolefin resin film,
Alternatively, a polypropylene film or the like is suitable.
【００３６】また、積層フィルムの場合、転写を行う基
材の凹凸の程度、転写温度との兼ね合いからフィルムの
厚みの組み合わせを適宜選択すればよいが、本発明者ら
の実験によれば、例えば、１４０℃〜１８０℃の転写温
度、６〜５０ｋｇ／ｃｍの転写圧力では、厚み５０〜１
００μｍのポリ塩化ビニル樹脂フィルムと１０〜３０μ
ｍのポリエチレン樹脂フィルムとの積層フィルムが良好
な結果が得られる。In the case of a laminated film, a combination of film thicknesses may be appropriately selected in consideration of the degree of unevenness of the base material to be transferred and the transfer temperature. According to the experiments conducted by the present inventors, for example, At a transfer temperature of 140 ° C to 180 ° C and a transfer pressure of 6 to 50 kg / cm, a thickness of 50 to 1
00μm polyvinyl chloride resin film and 10-30μ
Good results can be obtained with a laminated film of m of polyethylene resin film.
【００３７】また、ポリオレフィン樹脂フィルムの場合
は、耐熱性の問題から転写温度が１４０℃未満で行える
構成の場合に使用することが出来る。本発明者らの実験
によれば、例えば、１００℃〜１４０℃の転写温度、６
〜５０ｋｇ／ｃｍの転写圧力では、厚み５０〜１００μ
ｍのポリプロピレンフィルムで良好な結果が得られる。Further, the polyolefin resin film can be used when the transfer temperature is less than 140 ° C. due to heat resistance. According to experiments by the present inventors, for example, a transfer temperature of 100 ° C. to 140 ° C., 6
At a transfer pressure of -50 kg / cm, the thickness is 50-100 μm.
Good results are obtained with a polypropylene film of m.
【００３８】一方、転写を行う基材形状がフラットであ
る場合には、転写時の基材形状への追随適性を特に考慮
する必要がないことから、例えば紙とポリオレフィンフ
ィルムとの積層シート、あるいは厚み６〜２５μｍのポ
リエチレンテレフタレート樹脂フィルム等を用いること
がコスト的にも有利である。この場合は基体シートの耐
熱温度が高いため、転写温度１００℃〜２３０℃の範囲
での使用が可能である。具体的には、坪量５２．３ｇ／
ｍ2の上質紙にポリプロピレン樹脂を２０μｍの厚さに
積層したシートでは、１６０℃〜２００℃の転写温度、
６〜５０ｋｇ／ｃｍの転写圧力で良好な結果が得られ
る。On the other hand, when the base material to be transferred has a flat shape, it is not necessary to consider the adaptability to the shape of the base material at the time of transfer. Therefore, for example, a laminated sheet of paper and a polyolefin film, or It is advantageous in terms of cost to use a polyethylene terephthalate resin film having a thickness of 6 to 25 μm. In this case, since the heat resistant temperature of the base sheet is high, the transfer temperature can be used in the range of 100 ° C to 230 ° C. Specifically, the basis weight is 52.3 g /
For a sheet obtained by laminating polypropylene resin on a high-quality paper of m 2 to a thickness of 20 μm, a transfer temperature of 160 ° C. to 200 ° C.,
Good results are obtained with a transfer pressure of 6 to 50 kg / cm.
【００３９】基体シートの表面に設ける絵柄層を形成す
る方法は、グラビア印刷、スクリーン印刷、オフセット
印刷などの公知の印刷方法を適用すればよい。As a method for forming the pattern layer provided on the surface of the base sheet, known printing methods such as gravure printing, screen printing and offset printing may be applied.
【００４０】本発明で絵柄層を形成するために使用する
インキは、バインダー、着色顔料及び有機溶剤等からな
り、さらに必要に応じて体質顔料や硬化促進剤、分散
剤、増粘剤、成膜助剤、紫外線吸収剤等の各種添加剤を
配合することも可能である。上記バインダーとしては、
有機無機複合高分子や有機高分子などが使用可能であ
る。有機無機複合高分子としては、前述のアルコキシシ
ランの加水分解縮合物やシリル基含有ビニル系樹脂又は
これらの混合物などである。有機高分子としては、フッ
素樹脂、アクリル樹脂、スチレン樹脂、アルキッド樹
脂、ポリアミド樹脂、ポリ塩化ビニル樹脂、ポリ酢酸ビ
ニル樹脂、又はこれらの混合物などである。The ink used for forming the pattern layer in the present invention comprises a binder, a coloring pigment, an organic solvent and the like, and further, if necessary, an extender pigment, a curing accelerator, a dispersant, a thickener and a film formation. It is also possible to mix various additives such as an auxiliary agent and an ultraviolet absorber. As the binder,
Organic-inorganic composite polymers and organic polymers can be used. The organic-inorganic composite polymer is, for example, the above-mentioned hydrolysis-condensation product of alkoxysilane, silyl group-containing vinyl resin, or a mixture thereof. Examples of the organic polymer include fluororesin, acrylic resin, styrene resin, alkyd resin, polyamide resin, polyvinyl chloride resin, polyvinyl acetate resin, and mixtures thereof.
【００４１】インキのバインダーとしては、特にアルコ
キシシランの加水分解縮合物とシリル基含有ビニル系樹
脂との混合割合が、５０：５０〜０：１００（重量比）
のものが、耐候性、顔料分散性、基材との追随性などの
点で好ましい。As a binder for the ink, the mixing ratio of the hydrolyzed condensate of alkoxysilane and the silyl group-containing vinyl resin is 50:50 to 0: 100 (weight ratio).
Those having the above properties are preferable in terms of weather resistance, pigment dispersibility, conformability with a substrate, and the like.
【００４２】上記着色顔料としては、酸化チタン、カー
ボンブラック、ベンガラ等の通常の塗料用あるいはイン
キ用の着色顔料が特に制限なく使用可能である。As the above-mentioned color pigment, a usual color pigment for paint or ink such as titanium oxide, carbon black, red iron oxide, etc. can be used without particular limitation.
【００４３】上記有機溶剤としては、メチルアルコー
ル、エチルアルコール、イソプロピルアルコール、エチ
レングリコール、エチレングリコールモノメチルエーテ
ル等のアルコールもしくはその誘導体；アセトン、メチ
ルエチルケトン等のケトン類；酢酸メチル、酢酸ブチル
等のエステル類；キシレン、トルエン等の炭化水素類な
どが挙げられる。Examples of the organic solvent include alcohols such as methyl alcohol, ethyl alcohol, isopropyl alcohol, ethylene glycol and ethylene glycol monomethyl ether or derivatives thereof; ketones such as acetone and methyl ethyl ketone; esters such as methyl acetate and butyl acetate; Hydrocarbons such as xylene and toluene are included.
【００４４】これらの構成成分の配合割合は、バインダ
ー１０〜６０重量％、好ましくは耐候性、基材との追随
性等から２５〜４０重量％、顔料（着色及び体質顔料）
５〜３５重量％、好ましくは隠蔽性、乾燥性等から５〜
３０重量％、添加剤０〜１５重量％、有機溶剤２０〜７
５重量％、好ましくは作業性から３５〜６５重量％が適
当である。The mixing ratio of these components is 10 to 60% by weight of the binder, preferably 25 to 40% by weight from the viewpoint of weather resistance, conformability with the substrate, etc., pigment (coloring and extender pigment).
5 to 35% by weight, preferably 5 to 5 in terms of hiding property, drying property, etc.
30% by weight, additives 0 to 15% by weight, organic solvents 20 to 7
5% by weight, preferably 35 to 65% by weight from the viewpoint of workability.
【００４５】このように構成された転写シートを基材へ
転写する方式については、柔軟なロールを用いて転写す
るロール転写方式、シート状の弾性体と平プレスを用い
て転写する平プレス方式等があり、転写を行う基材に応
じて選択すればよい。As for the method of transferring the transfer sheet thus constructed to the substrate, a roll transfer method of transferring using a flexible roll, a flat press method of transferring using a sheet-like elastic body and a flat press, etc. Therefore, it may be selected according to the substrate to be transferred.
【００４６】図４は、転写方式の一例としてロール転写
方式を示す模式図である。FIG. 4 is a schematic view showing a roll transfer system as an example of the transfer system.
【００４７】同図に示すように、転写による装飾を施す
基材４１（表面にエンボス面を有している）のエンボス
面に、前述の有機無機複合高分子をバインダーとするベ
ース塗料を塗工して、下地層（図示せず）を形成した
後、前述の構成に係る転写シート４２を絵柄層面を基材
側にして重ね合わせ、表面よりゴムロール４３で押圧し
て、絵柄の転写を行う。As shown in the figure, the embossed surface of a base material 41 (having an embossed surface on the surface) to be decorated by transfer is coated with a base paint using the above-mentioned organic-inorganic composite polymer as a binder. Then, after forming a base layer (not shown), the transfer sheet 42 having the above-mentioned configuration is superposed with the pattern layer surface as the base material side, and the rubber roll 43 is pressed from the surface to transfer the pattern.
【００４８】本発明で下地層を形成するために使用する
ベース塗料は、前述の如く、有機無機複合高分子からな
るバインダーと、着色顔料及び有機溶剤とからなり、さ
らに必要に応じて体質顔料や硬化促進剤、分散剤、増粘
剤、成膜助剤、紫外線吸収剤等の各種添加剤を配合する
ことも可能である。The base paint used for forming the underlayer in the present invention comprises, as described above, a binder composed of an organic-inorganic composite polymer, a coloring pigment and an organic solvent, and if necessary, an extender pigment or an organic pigment. It is also possible to mix various additives such as a curing accelerator, a dispersant, a thickener, a film forming aid, and an ultraviolet absorber.
【００４９】有機無機複合高分子としては、前述のアル
コキシシランの加水分解縮合物やシリル基含有ビニル系
樹脂又はこれらの混合物などが使用され、具体的には前
に詳しく述べたとおりである。As the organic-inorganic composite polymer, a hydrolyzed condensate of the above-mentioned alkoxysilane, a silyl group-containing vinyl resin, or a mixture thereof is used, which is specifically as described above in detail.
【００５０】ベース塗料のバインダーとしては、特にア
ルコキシシランの加水分解縮合物とシリル基含有ビニル
系樹脂との混合割合が、７０：３０〜０：１００（重量
比）のものが、耐候性、基材との密着性などの点で好ま
しい。As the binder of the base paint, a binder having a mixing ratio of the hydrolysis-condensation product of alkoxysilane and the vinyl resin containing a silyl group of 70:30 to 0: 100 (weight ratio) has a weather resistance and a base property. It is preferable in terms of adhesion with the material.
【００５１】上記着色顔料としては、酸化チタン、カー
ボンブラック、ベンガラ等の通常の塗料用の着色顔料が
特に制限なく使用可能である。As the above color pigment, color pigments for ordinary paints such as titanium oxide, carbon black and red iron oxide can be used without particular limitation.
【００５２】上記有機溶剤としては、メチルアルコー
ル、エチルアルコール、イソプロピルアルコール、エチ
レングリコール、エチレングリコールモノメチルエーテ
ル等のアルコールもしくはその誘導体；アセトン、メチ
ルエチルケトン等のケトン類；酢酸メチル、酢酸ブチル
等のエステル類；キシレン、トルエン等の炭化水素類な
どが挙げられる。Examples of the organic solvent include alcohols such as methyl alcohol, ethyl alcohol, isopropyl alcohol, ethylene glycol and ethylene glycol monomethyl ether or derivatives thereof; ketones such as acetone and methyl ethyl ketone; esters such as methyl acetate and butyl acetate; Hydrocarbons such as xylene and toluene are included.
【００５３】これらの構成成分の配合割合は、バインダ
ー１５〜４０重量％、好ましくは耐候性、基材との密着
性等から２０〜３０重量％、顔料（着色及び体質顔料）
１０〜５０重量％、好ましくは隠蔽性、乾燥性等から１
５〜４０重量％、添加剤０〜１０重量％、有機溶剤２０
〜５０重量％、好ましくは塗工作業性等から３０〜４０
重量％が適当である。The blending ratio of these components is 15 to 40% by weight of the binder, preferably 20 to 30% by weight from the viewpoint of weather resistance, adhesion to the substrate, etc., pigment (coloring and extender pigment).
10 to 50% by weight, preferably 1 because of hiding and drying properties
5-40% by weight, additives 0-10% by weight, organic solvent 20
〜50% by weight, preferably 30-40 from the viewpoint of coating workability
Weight percent is suitable.
【００５４】転写温度については、エンボス面を有する
基材への転写であれば、転写シートを基材形状に追随さ
せる目的から、少なくとも転写シートのガラス転移点以
上の温度であることが望ましい。なお、上限について
は、本発明者らの行った実験によれば、ゴムロールを使
用する場合はその耐熱性から２２０℃以下が望ましい。Regarding the transfer temperature, in the case of transfer to a substrate having an embossed surface, it is desirable that the temperature is at least the glass transition point of the transfer sheet or higher in order to make the transfer sheet follow the shape of the substrate. According to an experiment conducted by the present inventors, the upper limit is preferably 220 ° C. or lower in terms of heat resistance when a rubber roll is used.
【００５５】転写圧については、基材の形状により適宜
決定される。例えば、基材表面の凹凸形状の大きなもの
については、転写シートをその形状に追随させる意味か
ら転写圧を高くすればよいが、基材や転写ロールの強
度、駆動するモーターの容量を考慮すると、５０ｋｇ／
ｃｍ以下が望ましい。The transfer pressure is appropriately determined depending on the shape of the base material. For example, for large irregularities on the surface of the base material, the transfer pressure may be increased in the sense that the transfer sheet follows the shape, but considering the strength of the base material and the transfer roll, and the capacity of the driving motor, 50 kg /
cm or less is desirable.
【００５６】なお、転写方式としては、前記のロール転
写方式が連続的に転写を行うことが可能であり、生産面
からも有利である。ロール転写に用いるロールの材質と
しては、通常ゴムやスポンジ等が使用されるが、耐久性
や耐熱性を考慮すると、具体的にはシリコンゴム、シリ
コンスポンジ、ニトリルゴム、エチレンプロピレンゴ
ム、フッ素ゴム等が望ましい。As the transfer method, the above-mentioned roll transfer method can continuously perform the transfer, which is also advantageous in terms of production. Normally, rubber or sponge is used as the material of the roll used for roll transfer, but considering durability and heat resistance, specifically, silicone rubber, silicon sponge, nitrile rubber, ethylene propylene rubber, fluororubber, etc. Is desirable.
【００５７】以上のようにして、基材の表面に所望の絵
柄を転写により付与した後、その表面には透明保護層が
形成されるが、本発明で透明保護層を形成するために使
用するクリアー塗料は、有機無機複合高分子からなるバ
インダーと、有機溶剤とからなり、さらに必要に応じて
硬化促進剤、分散剤、増粘剤、成膜助剤、紫外線吸収剤
等の各種添加剤を配合することも可能である。After a desired pattern is transferred and applied to the surface of the substrate as described above, a transparent protective layer is formed on the surface, which is used in the present invention to form the transparent protective layer. The clear paint is composed of a binder composed of an organic-inorganic composite polymer and an organic solvent, and if necessary, various additives such as a curing accelerator, a dispersant, a thickener, a film-forming aid and an ultraviolet absorber. It is also possible to mix.
【００５８】有機無機複合高分子としては、前述のアル
コキシシランの加水分解縮合物やシリル基含有ビニル系
樹脂又はこれらの混合物などが使用され、具体的には前
に詳しく述べたとおりである。As the organic-inorganic composite polymer, the above-mentioned hydrolyzed condensate of alkoxysilane, silyl group-containing vinyl resin, or a mixture thereof is used, which is specifically as described above in detail.
【００５９】クリアー塗料のバインダーとしては、特に
アルコキシシランの加水分解縮合物とシリル基含有ビニ
ル系樹脂との混合割合が、１００：０〜７０：３０（重
量比）のものが、耐候性、耐熱性、耐水性、耐汚染性な
どの点で好ましい。As the binder of the clear paint, the one having a mixing ratio of the hydrolysis-condensation product of the alkoxysilane and the silyl group-containing vinyl resin in the range of 100: 0 to 70:30 (weight ratio) is particularly weather resistant and heat resistant. It is preferable from the viewpoints of resistance, water resistance and stain resistance.
【００６０】上記有機溶剤としては、メチルアルコー
ル、エチルアルコール、イソプロピルアルコール、エチ
レングリコール、エチレングリコールモノメチルエーテ
ル等のアルコールもしくはその誘導体；アセトン、メチ
ルエチルケトン等のケトン類；酢酸メチル、酢酸ブチル
等のエステル類；キシレン、トルエン等の炭化水素類な
どが挙げられる。Examples of the organic solvent include alcohols such as methyl alcohol, ethyl alcohol, isopropyl alcohol, ethylene glycol and ethylene glycol monomethyl ether or derivatives thereof; ketones such as acetone and methyl ethyl ketone; esters such as methyl acetate and butyl acetate; Hydrocarbons such as xylene and toluene are included.
【００６１】これらの構成成分の配合割合は、バインダ
ー１５〜４０重量％、添加剤０〜５重量％、有機溶剤６
０〜８０重量％としたものが、塗膜物性、塗工作業性、
乾燥性等の点から適当である。The mixing ratio of these constituent components is such that the binder is 15 to 40% by weight, the additive is 0 to 5% by weight, and the organic solvent is 6%.
The content of 0 to 80% by weight means coating film physical properties, coating workability,
It is suitable in terms of drying property.
【００６２】透明保護層の塗工方法としては、スプレー
法、フローコート法、ロールコート法など既存の方法を
用いればよい。As a method for applying the transparent protective layer, an existing method such as a spray method, a flow coating method or a roll coating method may be used.
【００６３】図５は、本発明の化粧板の構成を示す断面
図である。これによれば、基材５１上に、下地層５２、
絵柄層５３、透明保護層５４が積層された構成である。FIG. 5 is a sectional view showing the structure of the decorative plate of the present invention. According to this, the base layer 52,
This is a structure in which the pattern layer 53 and the transparent protective layer 54 are laminated.
【００６４】次に、本発明の化粧板の製造方法の具体例
について説明する。Next, a specific example of the method for manufacturing a decorative board of the present invention will be described.
【００６５】まず、予めプライマー処理をした例えばセ
メント系の無機基材を必要に応じて表面温度約３０〜６
０℃に予熱し、前述のベース塗料を例えば１８〜１２０
ｇ／ｍ2（ｗｅｔ）程度にフローコート法、スプレー法
等の手段を用いて塗工する。次いで、８０〜１２０℃の
温度で４〜１０分間強制乾燥させて下地層を形成させ
る。なお、該下地層の乾燥膜厚は約２０〜５０μｍ程度
が適当である。First, for example, a cement-based inorganic base material which has been preliminarily treated with a primer is preliminarily subjected to a surface temperature of about 30-6.
Preheat to 0 ° C and apply the above-mentioned base paint to, for example, 18 to 120
The coating is carried out to a degree of g / m 2 (wet) using a method such as a flow coating method or a spraying method. Then, the base layer is formed by forced drying at a temperature of 80 to 120 ° C. for 4 to 10 minutes. It is suitable that the dry film thickness of the underlayer is about 20 to 50 μm.
【００６６】次に、上記下地層を形成した基材に絵柄の
転写を行う。転写シートは前述の構成に係るものを基材
の形状や転写条件等から適宜選択する。その転写シート
を、絵柄層を基材の下地層に接するように設置した後、
例えばロール転写法により、しかるべき転写条件で転写
を行い、基体シートを剥離する。Next, the pattern is transferred to the base material on which the base layer is formed. The transfer sheet having the above-mentioned structure is appropriately selected from the shape of the base material, the transfer conditions and the like. After placing the transfer sheet so that the pattern layer is in contact with the base layer of the base material,
For example, by a roll transfer method, transfer is performed under appropriate transfer conditions, and the base sheet is peeled off.
【００６７】次いで、絵柄が転写された基材を必要に応
じて表面温度約３０〜５０℃に予熱し、前述のクリヤー
塗料を例えば３２〜６５ｇ／ｍ2（ｗｅｔ）程度にフロ
ーコート法、スプレー法等の手段を用いて塗工する。次
いで、１００〜１５０℃の温度で１５〜３０分間加熱し
て透明保護層を形成させ、化粧板が出来上がる。なお、
該透明保護層の乾燥膜厚は約５〜１５μｍ程度が適当で
ある。Next, the substrate on which the pattern has been transferred is preheated to a surface temperature of about 30 to 50 ° C., if necessary, and the above-mentioned clear paint is applied by, for example, a flow coating method or spraying to about 32 to 65 g / m 2 (wet). Apply using a method such as a method. Then, the transparent protective layer is formed by heating at a temperature of 100 to 150 ° C. for 15 to 30 minutes to complete the decorative plate. In addition,
A suitable dry film thickness of the transparent protective layer is about 5 to 15 μm.
【００６８】[0068]
【作用】以上のような本発明によれば、基材に所望の転
写装飾模様を施すとともに、各種物性に優れた有機無機
複合高分子をバインダーとする塗料を用いることによ
り、表面に印刷による美麗な装飾が施され、しかも堅牢
性、耐汚染性、耐久性、難燃性に優れた意匠性の高い化
粧板を提供することが出来る。According to the present invention as described above, a desired transfer decorative pattern is applied to a substrate and a coating material having an organic-inorganic composite polymer as a binder, which is excellent in various physical properties, is used to make the surface beautiful by printing. It is possible to provide a decorative plate which is highly decorated and has excellent durability, stain resistance, durability and flame retardancy.
【００６９】[0069]
【実施例】以下、実施例を示して、本発明をさらに具体
的に説明する。なお、実施例中の「部」、「％」は重量
基準で示す。 （ベース塗料の調製）下記表１に示す成分を混合し、ベ
ース塗料（１）、（２）を調製した。EXAMPLES The present invention will be described more specifically by showing examples. In addition, "part" and "%" in the examples are shown by weight. (Preparation of Base Paint) The components shown in Table 1 below were mixed to prepare base paints (1) and (2).
【００７０】[0070]
【表１】 注1) メチルトリメトキシシランを主成分とするオルガノアルコキシシラン の加水分解縮合物７０部とシリル基含有ビニル系樹脂３０部との混合 溶液（加熱残分３８％） 注2) Ｔｇ：２６℃、数平均分子量：１１４００、加熱残分４８％ （インキの調製その１）下記表２に示す成分を混合し、
有機無機複合高分子をバインダーとするインキ４色
（墨、藍、黄土、茶）を調製した。[Table 1] Note 1) A mixed solution of 70 parts of hydrolyzed condensate of organoalkoxysilane containing methyltrimethoxysilane as a main component and 30 parts of vinyl resin containing silyl group (heating residue 38%) Note 2) Tg: 26 ° C Number average molecular weight: 11400, heating residue 48% (Preparation of ink 1) The components shown in Table 2 below are mixed,
Four inks (ink, indigo, ocher, brown) were prepared using the organic-inorganic composite polymer as a binder.
【００７１】[0071]
【表２】 注3) 注2)と同様 （インキの調製その２）下記表３に示す成分を混合し、
有機高分子をバインダーとするインキ４色（墨、藍、黄
土、茶）を調製した。[Table 2] Note 3) Same as Note 2) (Ink preparation 2) Mix the components shown in Table 3 below,
Four colors of ink (ink, indigo, ocher, and brown) were prepared using an organic polymer as a binder.
【００７２】[0072]
【表３】 （クリヤー塗料の調製）下記表４に示す成分を混合し、
クリヤー塗料（I）、（II）を調製した。[Table 3] (Preparation of clear paint) Mix the components shown in Table 4 below,
Clear paints (I) and (II) were prepared.
【００７３】[0073]
【表４】 注4) メチルトリメトキシシランを主成分とするオルガノアルコキシシラン の加水分解縮合物溶液（加熱残分２０％） 注5) 注1)と同様 （実施例１）厚さ７０μｍの半硬質塩化ビニルシート上
に、Ｔダイ押し出し成形によりポリエチレン樹脂フィル
ムを２０μｍの厚さに積層し、基体シートを作製した。
そして、この基体シートのポリエチレン樹脂フィルム側
に前記表２の構成からなる４色のインキを使用してグラ
ビア方式により、煉瓦柄の転写シートを作製した。[Table 4] Note 4) Hydrolyzed condensate solution of organoalkoxysilane containing methyltrimethoxysilane as the main component (heating residue 20%) Note 5) Same as Note 1) (Example 1) Semi-rigid vinyl chloride sheet with a thickness of 70 μm A polyethylene resin film having a thickness of 20 μm was laminated thereon by T-die extrusion molding to prepare a base sheet.
Then, a transfer sheet having a brick pattern was produced on the polyethylene resin film side of this base sheet by the gravure method using the four color inks having the constitution shown in Table 2 above.
【００７４】予めプライマー処理（湿気硬化型ウレタン
樹脂系塗料を塗装し、次いでアクリルウレタン樹脂系塗
料を塗装）をした多孔質石綿スレート板を表面温度約４
５℃に予熱し、エアースプレーを用いて前記表１のベー
ス塗料（１）を１００ｇ／ｍ2で塗工し、８０℃の温度
で４分間強制乾燥させ、膜厚４０μｍの下地層を形成さ
せ、基材とした。The surface temperature of a porous asbestos slate plate which had been subjected to a primer treatment (a moisture-curable urethane resin-based paint and then an acrylic urethane resin-based paint) was approximately 4
Preheat to 5 ° C., apply the base paint (1) shown in Table 1 at 100 g / m 2 using an air spray, and force-dry at 80 ° C. for 4 minutes to form a base layer having a thickness of 40 μm. , As a base material.
【００７５】次に、上記の転写シートを上記基材の上に
設置し、表面から表面温度１５０℃、ゴム硬度３０°、
肉厚２０ｍｍ、ロール径２００ｍｍのシリコンロールで
押圧し、基体シートを剥離した。このときの転写速度は
１０ｍ／分、転写圧力は２０ｋｇ／ｃｍとした。Next, the above-mentioned transfer sheet was placed on the above-mentioned substrate, and the surface temperature was 150 ° C. from the surface, the rubber hardness was 30 °,
The base sheet was peeled off by pressing with a silicon roll having a wall thickness of 20 mm and a roll diameter of 200 mm. The transfer speed at this time was 10 m / min, and the transfer pressure was 20 kg / cm.
【００７６】次いで、この絵柄の転写された基材を表面
温度約４０℃に予熱し、エアースプレーを用いて前記表
４のクリヤー塗料（I）を４３ｇ／ｍ2で塗工し、１５０
℃の温度で２０分間焼き付けし、表面に膜厚１０μｍの
透明保護層を形成させた。Then, the substrate having the transferred pattern was preheated to a surface temperature of about 40 ° C., and the clear paint (I) shown in Table 4 was applied at 43 g / m 2 using an air spray,
It was baked at a temperature of ° C for 20 minutes to form a transparent protective layer having a film thickness of 10 µm on the surface.
【００７７】こうして得られた化粧板について、塗膜外
観、耐候性、耐水性、密着性、耐汚染性の試験を行っ
た。その結果を下記表５に示した。 （実施例２〜４）前記表１〜４に示す各塗料、インキを
使用して上記実施例１と同様にして化粧板を作製し（使
用した塗料、インキは表５参照）、それらについて、実
施例１と同様の試験を行い、その結果を表５に示した。 （比較例１、２）実施例１の積層フィルムからなる基体
シートのポリエチレン樹脂フィルム側に前記表３の構成
からなる４色のインキを使用して、実施例１と同様の煉
瓦柄をグラビア方式により印刷した転写シートを作製し
た。The decorative plate thus obtained was tested for coating film appearance, weather resistance, water resistance, adhesion and stain resistance. The results are shown in Table 5 below. (Examples 2 to 4) Decorative plates were prepared in the same manner as in Example 1 using the paints and inks shown in Tables 1 to 4 (see Table 5 for the paints and inks used). The same test as in Example 1 was conducted, and the results are shown in Table 5. (Comparative Examples 1 and 2) The same brick pattern as in Example 1 was gravure-processed by using the four color inks having the constitution shown in Table 3 on the polyethylene resin film side of the base sheet made of the laminated film of Example 1. To produce a transfer sheet printed by.
【００７８】予めプライマー処理（実施例１と同様）を
した多孔質石綿スレート板を表面温度約４５℃に予熱
し、エアースプレーを用いてベース塗料（アクリルウレ
タン樹脂系）を１００ｇ／ｍ2で塗工し、８０℃の温度
で４分間強制乾燥させ、膜厚４０μｍの下地層を形成さ
せ、基材とした。A porous asbestos slate plate which had been subjected to a primer treatment (as in Example 1) in advance was preheated to a surface temperature of about 45 ° C., and the base paint (acrylic urethane resin type) was applied at 100 g / m 2 using an air spray. And forcibly dried at a temperature of 80 ° C. for 4 minutes to form a base layer having a film thickness of 40 μm, which was used as a base material.
【００７９】次に、上記の転写シートを上記基材の上に
設置し、表面から表面温度１５０℃、ゴム硬度３０°、
肉厚２０ｍｍ、ロール径２００ｍｍのシリコンロールで
押圧し、基体シートを剥離した。このときの転写速度は
１０ｍ／分、転写圧力は２０ｋｇ／ｃｍとした。Next, the above-mentioned transfer sheet was placed on the above-mentioned substrate, and the surface temperature was 150 ° C. from the surface, the rubber hardness was 30 °,
The base sheet was peeled off by pressing with a silicon roll having a wall thickness of 20 mm and a roll diameter of 200 mm. The transfer speed at this time was 10 m / min, and the transfer pressure was 20 kg / cm.
【００８０】次いで、この絵柄の転写された基材を表面
温度約４０℃に予熱し、エアースプレーを用いてクリヤ
ー塗料（比較例１：フッ素樹脂系、比較例２：アクリル
ウレタン樹脂系）を１００ｇ／ｍ2で塗工し、８０℃の
温度で１０分間強制乾燥させ、表面に膜厚４０μｍの透
明保護層を形成させた。Then, the substrate having the transferred pattern was preheated to a surface temperature of about 40 ° C., and 100 g of a clear coating (Comparative Example 1: Fluorine resin type, Comparative Example 2: acrylic urethane resin type) was prepared by using an air spray. / M 2 and then forcedly dried at a temperature of 80 ° C. for 10 minutes to form a transparent protective layer having a film thickness of 40 μm on the surface.
【００８１】こうして得られた化粧板について、実施例
１と同様の試験を行い、その結果を下記表５に示した。The decorative board thus obtained was tested in the same manner as in Example 1, and the results are shown in Table 5 below.
【００８２】[0082]
【表５】 注6) 目視観察 注7) サンシャインウエザオメーター試験１０００時間後、塗膜外観を目視 観察 注8) ２０℃水中浸漬７日間後、塗膜外観を目視観察 注9) ４ｍｍ間隔ゴバン目セロハン粘着テープ剥離 注10) 油性マジック（赤、黒）で線を引き、２時間放置後、ウエスを用いて エタノールで拭き取り、塗膜外観目視観察 上記表５の結果からも明らかなとおり、本発明による化
粧板は、すべての評価項目において優れた塗膜物性を有
していた。[Table 5] Note 6) Visual observation Note 7) Visual observation of coating film after 1000 hours of sunshine weatherometer test Note 8) Visual observation of coating film after 7 days of immersion in 20 ° C water Note 9) 4 mm interval cellophane adhesive tape Peeling Note 10) A line was drawn with an oil-based marker (red, black), left for 2 hours, wiped off with ethanol using a waste cloth, and visually observed for the appearance of the coating film. Had excellent coating film physical properties in all evaluation items.
【００８３】これに対し、比較例１では耐汚染性が悪
く、比較例２では耐候性、耐汚染性が劣っていた。In contrast, Comparative Example 1 was poor in stain resistance, and Comparative Example 2 was inferior in weather resistance and stain resistance.
【００８４】[0084]
【発明の効果】以上詳細に説明したように、本発明の化
粧板によれば、基材に所望の転写装飾模様を施すととも
に、各種物性に優れた有機無機複合高分子をバインダー
とする塗料を用いることにより、表面に印刷による美麗
な装飾が施され、しかも堅牢性、耐汚染性、耐久性、難
燃性に優れた意匠性の高い化粧板を提供することが出来
るという優れた効果を奏する。As described above in detail, according to the decorative board of the present invention, a coating material having a desired transfer decorative pattern on the base material and using the organic-inorganic composite polymer excellent in various physical properties as a binder is provided. By using it, it has an excellent effect that it can be provided with a beautiful decoration by printing on the surface, and can provide a decorative sheet with high designability that is excellent in robustness, stain resistance, durability and flame retardancy. .
【図１】本発明に使用する転写シートの一構成例を示す
断面図である。FIG. 1 is a cross-sectional view showing one structural example of a transfer sheet used in the present invention.
【図２】本発明に使用する転写シートの他の構成例を示
す断面図である。FIG. 2 is a cross-sectional view showing another structural example of the transfer sheet used in the present invention.
【図３】本発明に使用する転写シートの別の構成例を示
す断面図である。FIG. 3 is a cross-sectional view showing another configuration example of the transfer sheet used in the present invention.
【図４】転写方式の一例としてロール転写方式を示す模
式図である。FIG. 4 is a schematic diagram showing a roll transfer system as an example of a transfer system.
【図５】本発明の化粧板の構成を示す断面図である。FIG. 5 is a cross-sectional view showing a configuration of a decorative board of the present invention.
１１ ポリ塩化樹脂フィルム １２ ポリオレフィン樹脂フィルム １３ 基体シート １４ 絵柄層 ２１ 紙 ２２ ポリプロピレンフィルム ２３ 基体シート ２４ 絵柄層 ３１ ポリプロピレン樹脂フィルム（基体シート） ３２ 絵柄層 ４１ 基材 ４２ 転写シート ４３ ゴムロール ５１ 基材 ５２ 下地層 ５３ 絵柄層 ５４ 透明保護層 11 Polychlorinated Resin Film 12 Polyolefin Resin Film 13 Base Sheet 14 Design Layer 21 Paper 22 Polypropylene Film 23 Base Sheet 24 Design Layer 31 Polypropylene Resin Film (Base Sheet) 32 Design Layer 41 Base Material 42 Transfer Sheet 43 Rubber Roll 51 Base Material 52 Bottom Stratum 53 Picture layer 54 Transparent protective layer
───────────────────────────────────────────────────── フロントページの続き (72)発明者 鈴木 幸雄 東京都台東区台東１丁目５番１号 凸版印 刷株式会社内 (72)発明者 佐野 誠治 東京都台東区台東１丁目５番１号 凸版印 刷株式会社内 (72)発明者 北野 智昭 栃木県大田原市下石上1382−12 大日本塗 料株式会社内 (72)発明者 島岡 宏 栃木県大田原市下石上1382−12 大日本塗 料株式会社内 (72)発明者 竹内 隆男 栃木県大田原市下石上1382−12 大日本塗 料株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Yukio Suzuki 1-5-1 Taito, Taito-ku, Tokyo Within Toppan Printing Co., Ltd. (72) Inventor Seiji Sano 1-5-1 Taito, Taito-ku, Tokyo Toppan Imprint Co., Ltd. (72) Inventor Tomoaki Kitano 1382-12 Shimoishigami, Otawara-shi, Tochigi Dai Nippon Paint Co., Ltd. (72) Inventor Hiroshi Shimaoka 1382-12 Shimoishigami, Otawara-shi, Tochigi Dainippon Paint Co., Ltd. (72) Inventor Takao Takeuchi 1382-12 Shimoishigami, Otawara-shi, Tochigi Dai Nippon Paint Co., Ltd.
Claims (4)
板であって、基材に有機無機複合高分子をバインダーと
する塗料を塗布して下地層を形成し、この上に、予めバ
インダーと顔料とを少なくとも含むインキを用いて転写
基体上に所望の絵柄を形成した転写シートを圧着して絵
柄を付与した後、表面に有機無機複合高分子からなる透
明保護層を設けたことを特徴とする化粧板。1. A decorative board in which a desired transfer decorative pattern is applied to a base material, wherein a base material is formed by applying a coating material having an organic-inorganic composite polymer as a binder to the base material, After applying a pattern by press-bonding a transfer sheet having a desired pattern formed on a transfer substrate using an ink containing at least a binder and a pigment, a transparent protective layer made of an organic-inorganic composite polymer was provided on the surface. A featured decorative board.
機複合高分子を用いたことを特徴とする請求項１記載の
化粧板。2. The decorative board according to claim 1, wherein an organic-inorganic composite polymer is used as a binder for the ink.
１〜８の有機基、Ｒ’は炭素数１〜５の有機基、ｎは０
〜２の整数を示す。］で表されるアルコキシシランの加
水分解縮合物、又は、 （II）シリル基含有ビニル系樹脂、或いはこれらの混合
物であることを特徴とする請求項１または２記載の化粧
板。3. The organic-inorganic composite polymer comprises: (I) a general formula R n Si (OR ′) 4-n [wherein R is an organic group having 1 to 8 carbon atoms and R ′ is 1 to 1 carbon atoms]. 5 organic groups, n is 0
2 to 2. ] The decorative board according to claim 1 or 2, which is a hydrolysis-condensation product of an alkoxysilane represented by the above formula, or (II) a silyl group-containing vinyl resin, or a mixture thereof.
とを特徴とする請求項１、２または３記載の化粧板。4. The decorative board according to claim 1, 2 or 3, wherein a ceramic base material is used as the base material.