JPH09291248A - Recording liquid - Google Patents
Recording liquidInfo
- Publication number
- JPH09291248A JPH09291248A JP4243797A JP4243797A JPH09291248A JP H09291248 A JPH09291248 A JP H09291248A JP 4243797 A JP4243797 A JP 4243797A JP 4243797 A JP4243797 A JP 4243797A JP H09291248 A JPH09291248 A JP H09291248A
- Authority
- JP
- Japan
- Prior art keywords
- acrylic
- recording liquid
- acrylate
- methacrylate
- styrene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【発明の属する技術分野】本発明は油性顔料インキに関
するものである。さらに詳しくは、毛細管現象を利用し
た吐出機構を有する筆記具に適した流動性を有し、かつ
分散安定性に優れ、フェルト製ペン先、繊維ペン先、プ
ラスチックペン先などで目詰まりが生じない特性を有す
る筆記具用ならびにやスタンプなどに用いられる油性顔
料インキに関する。TECHNICAL FIELD The present invention relates to an oil-based pigment ink. More specifically, it has a fluidity suitable for writing instruments that have a discharge mechanism that utilizes the capillary phenomenon, has excellent dispersion stability, and does not cause clogging with felt nibs, fiber nibs, plastic nibs, etc. The present invention relates to an oil-based pigment ink used for writing instruments and having a stamp.
【０００２】[0002]
【従来の技術】油性タイプのインキは、紙、布などのイ
ンキ吸収材やプラスチック、ガラス、金属などのインキ
非吸収材のどちらの表面にも筆記が可能で、しかも速乾
性であることから広く筆記具用油性インキとして使用さ
れている。特に、着色材として顔料を用いたインキは、
筆跡堅牢性が優れていることから、一般にペイントマー
カーとして知られ、家庭や学校、オフィスばかりでなく
様々な産業用途にも利用されている。そして、黒色イン
キの顔料としてはカーボンブラックが用いられている。2. Description of the Related Art Oil-based inks can be written on both ink-absorbing materials, such as paper and cloth, and non-ink-absorbing materials, such as plastics, glass, and metals. Used as oil-based ink for writing instruments. In particular, inks using pigments as coloring materials
Due to its excellent handwriting durability, it is generally known as a paint marker and is used not only at home, school and office but also in various industrial applications. Carbon black is used as the pigment of the black ink.
【０００３】しかしながら、このカーボンブラックを用
いた油性顔料インキは、粘度が高いために毛細管現象を
利用した吐出機構を有する筆記具においては十分な吐出
量が得られず筆記カスレを生じるため、ペイントマーカ
ーでは弁機構を採用して吐出量を得ている。また上記イ
ンキは長期間使用するとカーボンブラックの凝集や沈降
といった現象が発生し、流動性が悪くなり、ペン先の目
詰まりが発生する。そのために従来のペイントマーカー
は、インキ収納部にインキと共に金属球などの撹拌部材
を入れて、再分散する方法をとっており、弁構造と絡み
合わせて複雑な構造を有しているので、部品点数が多
く、組み立て作業工程も複雑でコストが高いという問題
点があった。However, since the oil-based pigment ink using this carbon black has a high viscosity, a writing instrument having an ejection mechanism utilizing the capillary phenomenon cannot provide a sufficient ejection amount to cause a writing blur, and therefore a paint marker is used. A valve mechanism is used to obtain the discharge amount. In addition, when the above ink is used for a long period of time, phenomena such as aggregation and sedimentation of carbon black occur, the fluidity deteriorates, and clogging of the pen tip occurs. For this reason, conventional paint markers use a method of redispersing by putting a stirring member such as a metal ball together with ink in the ink storage unit, and have a complicated structure intertwined with the valve structure, so parts There were problems that the number of points was large, the assembly work process was complicated, and the cost was high.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、従来のペイ
ントマーカーのような複雑な構造を採用しなくてもよい
筆記具用油性顔料インキを得ることを目的とする。すな
わち、毛細管現象を利用した吐出機構を有する筆記具に
適した流動性を有し、かつ、分散安定性に優れ、フェル
ト製ペン先、繊維ペン先、プラスチックペン先などで目
詰まりが生じない特性を有する筆記具用油性顔料インキ
を得ることを目的としたものである。SUMMARY OF THE INVENTION It is an object of the present invention to obtain an oil-based pigment ink for writing instruments which does not require a complicated structure such as a conventional paint marker. That is, it has a fluidity suitable for a writing instrument having a discharge mechanism utilizing a capillary phenomenon, and has excellent dispersion stability, and a characteristic that a clogging does not occur in a felt nib, a fiber nib, a plastic nib, etc. The purpose is to obtain the oily pigment ink for writing instruments.
【０００５】[0005]
【課題を解決するための手段】本発明者は、前記課題を
解決すべく種々検討を重ねた結果、アルコール系溶剤お
よびグリコールエーテル系溶剤からなる群から選ばれた
少なくとも一種の溶剤とアクリル系樹脂を用いることに
より、カーボンブラックを用いた場合でも筆記具に適し
た流動性を有し、かつ、分散安定性に優れ、フェルト製
ペン先、繊維ペン先、プラスチックペン先などで目詰ま
りが生じない特性を有する筆記具用油性顔料インキ得る
ことに成功し、本発明を完成するに至った。As a result of various studies to solve the above problems, the present inventor has found that at least one solvent selected from the group consisting of alcohol solvents and glycol ether solvents and an acrylic resin. By using, it has fluidity suitable for writing instruments even when carbon black is used, and has excellent dispersion stability, and does not cause clogging with felt nibs, fiber nibs, plastic nibs, etc. It succeeded in obtaining the oil-based pigment ink for writing instruments which has the following, and came to complete the present invention.
【０００６】すなわち、本発明の筆記具用油性顔料イン
キは、アルコール系溶剤およびグリコールエーテル系溶
剤からなる群から選ばれた少なくとも一種の溶剤、顔
料、および少なくともスチレン及びカルボキシル基を有
するアクリル系モノマーを含む混合単量体または少なく
ともスチレン及びアミノ基を有するアクリル系モノマー
を含む混合単量体を共重合したアクリル系樹脂を含むこ
とからなる。好ましくは、顔料がカーボンブラックであ
り、アクリル系樹脂が、重量平均分子量が５００００以
下の共重合体である。That is, the oil-based pigment ink for a writing instrument of the present invention contains at least one solvent selected from the group consisting of alcohol solvents and glycol ether solvents, a pigment, and at least styrene and an acrylic monomer having a carboxyl group. It comprises an acrylic resin obtained by copolymerizing a mixed monomer or a mixed monomer containing at least styrene and an acrylic monomer having an amino group. Preferably, the pigment is carbon black and the acrylic resin is a copolymer having a weight average molecular weight of 50,000 or less.
【０００７】[0007]
【発明の実施の形態】本発明のインキに用いる顔料とし
てはカーボンブラックが好ましく、そのカーボンブラッ
クは、限定されることはなく、市販のものが使用できる
が、特に一次粒子径が８０ｎｍ以下のものがインキの黒
色度、流動性の点で好ましい。BEST MODE FOR CARRYING OUT THE INVENTION As the pigment used in the ink of the present invention, carbon black is preferable, and the carbon black is not limited, and commercially available ones can be used, but those having a primary particle diameter of 80 nm or less are particularly preferable. Is preferable in terms of blackness and fluidity of the ink.
【０００８】カーボンブラックとしては、例えばＣａｂ
ｏｔ社製の”Ｒｅｇａｌ ４１５Ｒ”、”Ｒｅｇａｌ
２５０Ｒ”、”Ｒｅｇａｌ ３５０Ｒ”、”Ｍｏｎａｒ
ｃｈ４６０”、”Ｍｏｇｕｌ−Ｌ”など、Ｄｅｇｕｓｓ
ａ社製の”Ｐｒｉｎｔｅｘ２５”、”Ｐｒｉｎｔｅｘ
３５”、”Ｐｒｉｎｔｅｘ ４５”、”Ｓｐｅｃｉａｌ
Ｂｌａｃｋ ２５０”、”Ｓｐｅｃｉａｌ Ｂｌａｃ
ｋ ３５０”など、三菱化学（株）製の”＃４５
Ｌ”、”＃５０”、”＃９００”、”＃９８０”、”＃
２３００”、”ＭＡ７”、”ＭＡ１１”、”ＭＣＦ８
８”などを挙げることができる。これらを単独もしくは
二種以上混合して使用することができる。その使用量は
３〜２０重量％が好ましい。As carbon black, for example, Cab
OT's "Regal 415R", "Regal
250R "," Regal 350R "," Monar "
ch460 ”,“ Mogul-L ”, Deguss
"Printex 25", "Printex" manufactured by a company
35 "," Printex 45 "," Special
Black 250 "," Special Blac
"# 45" manufactured by Mitsubishi Chemical Corporation, such as "k 350"
L ","# 50 ","# 900 ","# 980 ","#
2300 "," MA7 "," MA11 "," MCF8 "
8 "and the like. These may be used alone or in combination of two or more kinds. The amount used is preferably 3 to 20% by weight.
【０００９】本発明のインキに用いるアクリル系樹脂
は、少なくともスチレン及びカルボキシル基を有するア
クリル系モノマー、又は、少なくともスチレン及びアミ
ノ基を有するアクリル系モノマー含む混合単量体の共重
合からなる重量平均分子量が５００００以下の共重合体
である。特に、カルボキシル基を有するアクリル系モノ
マーを含む混合単量体から得られる共重合体には、一次
粒子径８０ｎｍ以下のカーボンブラックを用いるのが好
ましい。本発明においてアクリル系樹脂は、カーボンブ
ラックの分散剤、沈降防止剤およびバインダーとして効
果を示す。The acrylic resin used in the ink of the present invention is a weight average molecular weight obtained by copolymerizing an acrylic monomer having at least styrene and a carboxyl group, or a mixed monomer containing an acrylic monomer having at least styrene and an amino group. Is 50,000 or less. In particular, it is preferable to use carbon black having a primary particle diameter of 80 nm or less for a copolymer obtained from a mixed monomer containing an acrylic monomer having a carboxyl group. In the present invention, the acrylic resin is effective as a dispersant for carbon black, an anti-settling agent and a binder.
【００１０】カルボキシル基を有するアクリル系モノマ
ー及びアミノ基を有するアクリル系モノマーの役割は定
かではないが、主にアルコール系溶剤もしくはグリコー
ルエーテル系溶剤への溶解性を助けるものであると考え
られる。カルボキシル基を有するアクリル系モノマーと
しては、例えば、アクリル酸、メタクリル酸、アクリル
酸２−サクシノイルオキシエチル、アクリル酸ー２フタ
ロイルオキシエチル、アクリル酸ー２フタロイルオキシ
プロピル、アクリル酸２−ヘキサヒドロフタロイルオキ
シエチル、メタクリル酸２−サクシノイルオキシエチ
ル、メタクリル酸ー２フタロイルオキシエチル、メタク
リル酸ー２フタロイルオキシプロピル、メタクリル酸２
−ヘキサヒドロフタロイルオキシエチルなどを挙げるこ
とができる。The roles of the acrylic monomer having a carboxyl group and the acrylic monomer having an amino group are not clear, but it is considered that they mainly aid solubility in an alcohol solvent or a glycol ether solvent. Examples of the acrylic monomer having a carboxyl group include acrylic acid, methacrylic acid, 2-succinoyloxyethyl acrylate, 2-phthaloyloxyethyl acrylate, 2-phthaloyloxypropyl acrylate, 2-hexaacrylic acid. Hydrophthaloyloxyethyl, 2-succinoyloxyethyl methacrylate, 2 phthaloyloxyethyl methacrylate, 2 phthaloyloxypropyl methacrylate, 2 methacrylic acid
-Hexahydrophthaloyloxyethyl etc. can be mentioned.
【００１１】また、アミノ基を有するアクリル系モノマ
ーとしては、例えば、アクリル酸ジメチルアミノエチ
ル、アクリル酸ジエチルアミノエチル、メタクリル酸ジ
メチルアミノエチル、メタクリル酸ジエチルアミノエチ
ルなどが使用できる。これらのアクリル系モノマーは、
共重合成分（混合単量体）中に５〜８０モル％好ましく
は、１０〜７０モル％の割合で使用される。スチレンの
役割も定かではないが、主にカーボンブラックの分散性
を引き出すものであると考えられ、共重合成分中に５〜
７０モル％好ましくは１０〜６０モル％の割合で含まれ
るように混合される。As the acrylic monomer having an amino group, for example, dimethylaminoethyl acrylate, diethylaminoethyl acrylate, dimethylaminoethyl methacrylate, diethylaminoethyl methacrylate and the like can be used. These acrylic monomers are
It is used in an amount of 5 to 80 mol%, preferably 10 to 70 mol% in the copolymerization component (mixed monomer). The role of styrene is not clear, but it is thought that it is mainly to bring out the dispersibility of carbon black.
It is mixed so as to be contained in a proportion of 70 mol%, preferably 10 to 60 mol%.
【００１２】また、これ以外に共重合成分中にアクリル
酸メチル、アクリル酸エチル、アクリル酸ｎ−ブチル、
アクリル酸２−エチルヘキシルなどの非官能性アクリル
酸エステル、メタクリル酸メチル、メタクリル酸エチ
ル、メタクリル酸ｎ−ブチル、メタクリル酸２−エチル
ヘキシルなどの非官能性メタクリル酸エステルを必要に
応じて適宜含ませることができる。In addition to the above components, methyl acrylate, ethyl acrylate, n-butyl acrylate,
Non-functional acrylic acid ester such as 2-ethylhexyl acrylate, non-functional methacrylic acid ester such as methyl methacrylate, ethyl methacrylate, n-butyl methacrylate, and 2-ethylhexyl methacrylate should be appropriately contained as necessary. You can
【００１３】一方、毛細管現象を利用した吐出機構を有
する筆記具に適したインキの粘度は、２０ｍＰａ・ｓ以
下（２５℃）であるので、前記アクリル系樹脂の重量平
均分子量は５００００以下が好ましく、その使用量は、
重量平均分子量などにより異なるものの１〜２０重量％
が好ましい。On the other hand, since the viscosity of the ink suitable for a writing instrument having a discharge mechanism utilizing the capillary phenomenon is 20 mPa · s or less (25 ° C.), the weight average molecular weight of the acrylic resin is preferably 50,000 or less. The usage is
1 to 20% by weight, depending on the weight average molecular weight
Is preferred.
【００１４】本発明のインキに用いる溶剤は、アルコー
ル系溶剤およびグリコールエーテル系溶剤からなる群か
ら選ばれた少なくとも一種である。アルコール系溶剤と
しては、メタノール、エタノール、ｎ−プロピルアルコ
ール、イソプロピルアルコール、ｎ−ブチルアルコー
ル、ｓｅｃ−ブチルアルコール、ｔｅｒｔ−ブチルアル
コール、ｎ−アミルアルコール、イソアミルアルコー
ル、ｓｅｃ−アミルアルコール、ｎ−ヘキサノールなど
をあげることができる。グリコールエーテル系溶剤とし
ては、メチルセロゾルブ、エチルセロゾルブ、イソプロ
ピルセロゾルブ、ブチルセロゾルブ、プロピレングリコ
ールモノメチルエーテルなどがあげられる。The solvent used in the ink of the present invention is at least one selected from the group consisting of alcohol solvents and glycol ether solvents. Examples of alcohol solvents include methanol, ethanol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol, n-amyl alcohol, isoamyl alcohol, sec-amyl alcohol, and n-hexanol. Can be raised. Examples of the glycol ether solvent include methyl cellosolve, ethyl cellosolve, isopropyl cellosolve, butyl cellosolve, propylene glycol monomethyl ether and the like.
【００１５】その他必要に応じて界面活性剤、分散助
剤、防錆剤、潤滑剤などを必要に応じて適宜選択して使
用することができる。Other surfactants, dispersion aids, rust preventives, lubricants and the like can be appropriately selected and used as required.
【００１６】本発明のインキの製造方法としては、従来
公知の方法が採用できる。上述した各成分をホモミキサ
ー、ボールミル、ビーズミル、ホモジナイザー、サンド
ミル、ロールミルなどの分散機にて混練分散することに
より容易に得ることができる。As a method for producing the ink of the present invention, a conventionally known method can be adopted. The above components can be easily obtained by kneading and dispersing the above components with a dispersing machine such as a homomixer, a ball mill, a bead mill, a homogenizer, a sand mill, and a roll mill.
【００１７】本発明の筆記具用油性顔料インキは、なぜ
流動性がよく分散性に優れ、かつ、ペン先での目詰まり
が発生しないかは定かでないが、特定の共重合体を用い
ることによりカーボンブラック表面への樹脂の吸着作用
が特に強く、その結果、分散性、沈降防止の効果が発現
するために流動性および分散安定性に優れ、かつ、長期
保存においてもカーボンブラックが沈降することなく、
ペン先での目詰まりが発生しないものと考えられる。Although it is not clear why the oil-based pigment ink for a writing instrument of the present invention has good fluidity and excellent dispersibility and does not cause clogging at the pen tip, it is possible to use carbon by using a specific copolymer. The adsorption of the resin on the black surface is particularly strong, and as a result, the dispersibility and the effect of preventing sedimentation are excellent, so that the fluidity and dispersion stability are excellent, and carbon black does not sediment even during long-term storage,
It is considered that clogging at the pen tip does not occur.
【００１８】[0018]
【実施例】以下、実施例、比較例により本発明を詳細に
説明するが、本発明はこれらの実施例によりなんら限定
されるものではない。The present invention will be described in detail below with reference to Examples and Comparative Examples, but the present invention is not limited to these Examples.
【００１９】実施例、比較例で得られたインキについて
下記の試験を行った。 流動性：コーンプレート型回転粘度計により、２５℃に
て測定した粘度の値から評価した。２０ｍＰａ・ｓ以下
のものが優れた流動性を示す。 分散性：インキ中に分散されたカーボンブラックの平均
粒子径をレーザー散乱式粒度分布測定機を用いて測定
し、得られた値から評価した。平均粒子径が小さいもの
特に１５０ｎｍ以下のものが分散性が優れている。 長期保存性：インキをアクリル樹脂製繊維ペン先を有す
るサインペンに充填し、３ケ月放置した後に筆記を行
い、その状態の目視判定から評価した。 ○ ：目詰まりなく良好な筆跡。 × ：目詰まりが発生し筆跡がかすれる。The following tests were conducted on the inks obtained in the examples and comparative examples. Flowability: Evaluated from the viscosity value measured at 25 ° C. with a cone-plate type rotary viscometer. Those having a pressure of 20 mPa · s or less show excellent fluidity. Dispersibility: The average particle size of the carbon black dispersed in the ink was measured using a laser scattering type particle size distribution measuring device, and the obtained value was evaluated. Those having a small average particle size, particularly those having a particle size of 150 nm or less, have excellent dispersibility. Long-term storability: The ink was filled in a felt-tip pen having a fiber nib made of an acrylic resin, left for 3 months, then written, and evaluated by visual judgment of the state. ○: Good handwriting without clogging. X: Clogging occurs and the handwriting is faint.
【００２０】実施例１ メタクリル酸ジメチルアミノエチル５０モル％、スチレ
ン４０モル％、アクリル酸−ブチル１０モル％の混合単
量体１０重量部を溶媒エチルアルコール８０重量部に投
入し、アゾビスジメチルバレロニトリルを触媒として溶
液重合し、重合平均分子量１３０００のアクリル系共重
合樹脂溶液を得た。この溶液９０重量部とカーボンブラ
ック”ＭＣＦ８８”〔三菱化学（株）製〕の１０重量部
とをサンドミルにて１時間、混練分散し、本発明の筆記
具用油性顔料インキを得た。インキの試験結果を表１に
示す。Example 1 10 parts by weight of a mixed monomer of 50 mol% of dimethylaminoethyl methacrylate, 40 mol% of styrene and 10 mol% of butyl acrylate was added to 80 parts by weight of a solvent ethyl alcohol, and azobisdimethyl valero was added. Solution polymerization was performed using nitrile as a catalyst to obtain an acrylic copolymer resin solution having a polymerization average molecular weight of 13,000. 90 parts by weight of this solution and 10 parts by weight of carbon black "MCF88" (manufactured by Mitsubishi Chemical Co., Ltd.) were kneaded and dispersed in a sand mill for 1 hour to obtain an oil-based pigment ink for a writing instrument of the present invention. The test results of the ink are shown in Table 1.
【００２１】実施例２〜４、比較例１〜４ 混合単量体とその混合比率、溶媒、カーボンブラック、
インキ配合比率を表１および表２に示す通りとし、実施
例１に準じて筆記具用油性顔料インキを調製した。得ら
れたインキの試験結果を表１および表２に示す。Examples 2 to 4, Comparative Examples 1 to 4 Mixed monomers and their mixing ratio, solvent, carbon black,
The ink composition ratios were as shown in Tables 1 and 2, and an oil-based pigment ink for a writing instrument was prepared according to Example 1. The test results of the obtained ink are shown in Tables 1 and 2.
【００２２】実施例５ アクリル酸３０モル％、スチレン４０モル％、アクリル
酸んｎ−ブチル３０％の混合単量体１０重量部を溶媒エ
チルアルコール８０％重量部に投入し、アゾビスジメチ
ルバレロニトリルを触媒として溶液重合し、重合平均分
子量１５０００のアクリル系共重合樹脂溶液を得た。こ
の溶液９０重量部とカーボンブラック”Ｒｅｇａｌ ４
１５Ｒ”（平均粒子径：２５ｎｍ）〔Ｃａｂｏｔ社製〕
の１０重量部とをサンドミルにて１時間、混練分散し、
本発明の筆記具用油性顔料インキを得た。インキの試験
結果を表３に示す。Example 5 10 parts by weight of a mixed monomer of 30% by mole of acrylic acid, 40% by mole of styrene, and 30% of n-butyl acrylate was added to 80% by weight of ethyl alcohol as a solvent, and azobisdimethylvaleronitrile was added. Was used as a catalyst to perform solution polymerization to obtain an acrylic copolymer resin solution having a polymerization average molecular weight of 15,000. 90 parts by weight of this solution and carbon black "Regal 4"
15R "(average particle size: 25 nm) [manufactured by Cabot]
Knead and disperse 10 parts by weight of
An oil-based pigment ink for writing instruments of the present invention was obtained. The ink test results are shown in Table 3.
【００２３】実施例６〜８、比較例５〜８ 混合単量体とその混合比率、溶媒、カーボンブラック、
インキ配合比率を表３および表４に示す通りとし、実施
例５に準じて筆記具用油性顔料インキを調製した。得ら
れたインキの試験結果を表３および表４に示す。Examples 6-8, Comparative Examples 5-8 Mixed monomers and their mixing ratios, solvents, carbon black,
The ink blending ratio was as shown in Tables 3 and 4, and an oil-based pigment ink for a writing instrument was prepared according to Example 5. The test results of the obtained ink are shown in Tables 3 and 4.
【００２４】[0024]
【表１】 [Table 1]
【００２５】[0025]
【表２】 [Table 2]
【００２６】[0026]
【表３】 [Table 3]
【００２７】[0027]
【表４】 [Table 4]
【００２８】表１〜表４の結果から明らかなように、本
発明の筆記具用油性顔料インキは、流動性、分散性に優
れ、かつ、長期保存においてもペン先で目詰まりが発生
しない優れたものである。As is clear from the results of Tables 1 to 4, the oil-based pigment ink for a writing instrument of the present invention is excellent in fluidity and dispersibility and is free from clogging of the pen tip even after long-term storage. It is a thing.
【００２９】[0029]
【発明の効果】本発明の油性顔料インキは、毛細管現象
を利用した吐出機構を有する筆記具に適している。また
従来のペイントマーカー構造の筆記具やスタンプ用にも
有効に使用できるものである。INDUSTRIAL APPLICABILITY The oil-based pigment ink of the present invention is suitable for a writing instrument having an ejection mechanism utilizing the capillary phenomenon. It can also be effectively used for writing instruments and stamps having a conventional paint marker structure.
Claims (6)
テル系溶剤からなる群から選ばれた少なくとも一種の溶
剤、顔料、および少なくともスチレン及びカルボキシル
基を有するアクリル系モノマーを含む混合単量体または
少なくともスチレン及びアミノ基を有するアクリル系モ
ノマーを含む混合単量体を共重合してなるアクリル系樹
脂を含む記録液。1. A mixed monomer containing at least one solvent selected from the group consisting of alcohol solvents and glycol ether solvents, a pigment, and at least styrene and an acrylic monomer having a carboxyl group, or at least styrene and an amino group. A recording liquid containing an acrylic resin obtained by copolymerizing a mixed monomer containing an acrylic monomer having
記載の記録液。2. The pigment is carbon black.
Recording liquid described.
００００以下のアクリル系樹脂である請求の範囲１〜２
のいずれか記載の記録液。3. The acrylic resin has a weight average molecular weight of 5
An acrylic resin having a viscosity of 0000 or less.
Recording liquid according to any one of 1.
マーが、アクリル酸、メタクリル酸、アクリル酸２−サ
クシノイルオキシエチル、アクリル酸２−フタロイルオ
キシエチル、アクリル酸２−フタロイルオキシプロピ
ル、アクリル酸２−ヘキサヒドロフタロイルオキシエチ
ル、メタクリル酸２−サクシノイルオキシエチル、メタ
クリル酸２−フタロイルオキシエチル、メタクリル酸２
−フタロイルオキシプロピルまたはメタクリル酸２−ヘ
キサヒドロフタロイルオキシエチルである請求の範囲１
〜３のいずれか記載の記録液。4. The acrylic monomer having a carboxyl group is acrylic acid, methacrylic acid, 2-succinoyloxyethyl acrylate, 2-phthaloyloxyethyl acrylate, 2-phthaloyloxypropyl acrylate, or acrylic acid 2. -Hexahydrophthaloyloxyethyl, 2-succinoyloxyethyl methacrylate, 2-phthaloyloxyethyl methacrylate, methacrylic acid 2
-Phthaloyloxypropyl or 2-hexahydrophthaloyloxyethyl methacrylate.
The recording liquid according to any one of 3 to 3.
が、アクリル酸ジメチルアミノエチル、アクリル酸ジエ
チルアミノエチル、メタクリル酸ジメチルアミノエチル
またはメタクリル酸ジエチルアミノエチルである請求の
範囲１〜３のいずれか記載の記録液。5. The recording liquid according to claim 1, wherein the acrylic monomer having an amino group is dimethylaminoethyl acrylate, diethylaminoethyl acrylate, dimethylaminoethyl methacrylate or diethylaminoethyl methacrylate. .
ノマー５〜８０％、スチレン５〜７０％を含むことを特
徴とする請求の範囲１〜５のいずれか記載の記録液。6. The recording liquid according to any one of claims 1 to 5, wherein the mixed monomer contains at least 5 to 80% of an acrylic monomer and 5 to 70% of styrene.