JPH0924666A - Coating solution for medium to be recorded, its manufacture, and image-forming method using the manufacture - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide coating solution for a medium to be recorded capable of obtaining the medium to be recorded which is excellent in color reproducibility and its shelf life, excellent in an ink absorbing property, beading, and image density, and has high transparency and smoothness, its manufacture, and an image forming method using the coating solution. SOLUTION: In coating solution for a medium to be recorded having an ink accepting layer of alumina hydrate as main body, the coating solution making the ink accepting layer form, is composed of dispersion wherein the alumina hydrate is deflocculated with acid, and alkali is added thereto, and water-soluble high polymer molecule, and pH of the coating solution is 3-7.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【発明の属する技術分野】本発明は、水性インク用被記
録媒体に適した塗工液及びその製造方法、これを用いた
画像形成方法に関するものであり、特に分散性、経時安
定性に優れ、かつ形成されるインク受容層の透明性、画
像濃度、解像度が高く、インク吸収能力や皮膜性に優れ
た被記録媒体用塗工液及びその製造方法、これを用いた
画像形成方法に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a coating liquid suitable for a recording medium for water-based ink, a method for producing the same, and an image forming method using the same, and particularly excellent in dispersibility and stability over time. The present invention also relates to a coating liquid for a recording medium, which has high transparency, image density and resolution of an ink receiving layer to be formed and is excellent in ink absorbing ability and film forming property, a method for producing the same, and an image forming method using the same. .

【０００２】[0002]

【従来の技術】近年、インクジェット記録方式はインク
の微小液滴を種々の作動原理により飛翔させて、紙など
の被記録媒体に付着させ、画像、文字などの記録を行な
うものであるが、高速低騒音、多色化が容易、記録パタ
ーンの融通性が大きい、現像、定着が不要などの特徴が
あり、各種画像の記録装置として情報機器をはじめ各種
の用途において急速に普及している。さらに多色インク
ジェット方式により形成される画像は、製版方式による
多色印刷や、カラー写真方式による印画と比較して遜色
のない記録を得ることも可能であり、作成部数が少ない
場合には通常の多色印刷や印画によるよりも安価である
ことからフルカラー画像記録分野にまで広く応用されつ
つある。記録の高速化、高精細化、フルカラー化などの
記録特性の向上に伴って記録装置、記録方法の改良が行
われてきたが、被記録媒体に対しても高度な特性が要求
されるようになってきた。2. Description of the Related Art In recent years, an ink jet recording system is one in which minute droplets of ink are ejected according to various operating principles and adhered to a recording medium such as paper to record images, characters, etc. It is characterized by low noise, easy multicoloring, high flexibility in recording patterns, and no need for development and fixing, and is rapidly spreading in various applications including information devices as various image recording devices. Furthermore, images formed by the multi-color ink jet method can obtain multicolor printing by the plate-making method or a record comparable to printing by the color photographic method. Since it is cheaper than multicolor printing and printing, it is being widely applied to the field of full-color image recording. Recording devices and recording methods have been improved in line with improvements in recording characteristics such as higher recording speed, higher definition, and full color printing. It has become.

【０００３】かかる問題点を解決するために、従来から
多種多様の被記録媒体の形態が提案されてきた。例えば
特開昭５５−５８３０号公報には支持体表面にインク吸
収性の塗工層を設けたインクジェット記録用紙が開示さ
れ、特開昭５５−５１５８３号公報には被覆層中の顔料
として非晶質シリカを用いた例が開示され、特開昭５５
−１４６７８６号公報には水溶性高分子塗工層を用いた
例が開示されている。また近年、ベーマイト構造のアル
カリを用いた塗工層を有する被記録媒体が提案されてお
り、例えば、米国特許明細書第４８７９１６６号、同５
１０４７３０号、特開平２−２７６６７０号公報、同４
−３７５７６号公報、同５−３２０３７号公報に開示さ
れている。In order to solve such a problem, various forms of recording media have been conventionally proposed. For example, JP-A-55-5830 discloses an ink jet recording paper having an ink-absorptive coating layer provided on the surface of a support, and JP-A-55-51583 discloses amorphous as a pigment in a coating layer. An example using a high-quality silica is disclosed and disclosed in JP-A-55
No. 146786 discloses an example using a water-soluble polymer coating layer. Further, in recent years, recording media having a coating layer using an alkali having a boehmite structure have been proposed, for example, US Pat. Nos. 4,879,166 and 5;
104730, JP-A-2-276670, 4
-37576 and 5-32037.

【０００４】これらのアルミナ水和物を用いた被記録媒
体は、アルミナ水和物が正電荷を持っているためにイン
ク染料の定着がよく、発色の良い画像が得られること、
従来シリカ化合物を用いることで発生していた黒色イン
クの茶変、耐光性などの問題点がないこと、さらに画質
特にカラー画質における画質の点で従来の被記録媒体に
比べ好ましいなどの長所がある。しかしながら、このア
ルミナ水和物の持つ長所を被記録媒体に十分発揮させる
ためには以下の問題点がある。In the recording medium using these alumina hydrates, since the alumina hydrate has a positive charge, the ink dye is well fixed and an image with good color development can be obtained.
It has the advantages that it does not have problems such as brown discoloration of black ink, light resistance, etc., which have been caused by using a conventional silica compound, and that it is preferable to conventional recording media in terms of image quality especially in color image quality. . However, in order to sufficiently bring out the advantages of this alumina hydrate to the recording medium, there are the following problems.

【０００５】１）一般にアルミナ水和物は、水性ゾル中
で良好な分散状態を保つために解膠剤として酸を添加す
ることが知られており、特開平４−６７９８５号公報、
同４−２７５９１７号公報には解膠剤や分散剤として鉱
酸やモノカルボン酸などの有機酸を添加して、良分散の
透明ゾルを得る方法が開示されている。しかしながらこ
れらのアルミナゾルから形成されたインク受容層は、酸
の影響で印字物の色味が変化してしまう問題点がある。
特に透明なインク受容層を得る場合には、分散性の劣る
微細な顔料粒子を用いる必要があるために、酸量が多く
なる傾向があり印字物の保存性に対しても影響が大き
い。1) It is generally known that an alumina hydrate is added with an acid as a deflocculant in order to maintain a good dispersed state in an aqueous sol, and JP-A-4-67985,
Japanese Unexamined Patent Publication No. 4-275917 discloses a method of obtaining a well-dispersed transparent sol by adding an organic acid such as a mineral acid or a monocarboxylic acid as a peptizer or a dispersant. However, the ink receiving layer formed from these alumina sols has a problem that the tint of the printed matter changes due to the influence of acid.
In particular, when a transparent ink receiving layer is to be obtained, it is necessary to use fine pigment particles having poor dispersibility, so that the amount of acid tends to increase and the storage stability of printed matter is greatly affected.

【０００６】２）特開昭６４−８０８６号公報、同６４
−１１８７７号公報では、印字物の耐光性や保存性を高
めるために、インク受容層を形成する塗工液のｐＨを７
以上にする方法が開示されている。しかしながら顔料と
してアルミナ水和物を用いた場合には、分散液のｐＨを
７以上にすると増粘傾向が著しく経時安定性が劣り、分
散液の固形分濃度を高くすることが困難であった。2) JP-A-64-8086 and 64-64
In JP-A-11877, the pH of the coating liquid for forming the ink receiving layer is set to 7 in order to improve the light resistance and the storage stability of the printed matter.
The above method is disclosed. However, when alumina hydrate is used as the pigment, when the pH of the dispersion is 7 or more, the viscosity tends to increase remarkably and the stability over time deteriorates, making it difficult to increase the solid content concentration of the dispersion.

【０００７】[0007]

【発明が解決しようとする課題】このような問題に対し
て本発明者が鋭意検討した結果、本発明は上記問題点を
解決する目的でなされたものであり、インク吸収性、画
像濃度、解像度、透明性、平滑性に優れ、かつ印字物の
色再現性や保存性を満足する被記録媒体が得られ、かつ
分散性や経時安定性にも優れた塗工液及びその製造方
法、これを用いた画像形成方法を提供するものである。As a result of intensive studies made by the present inventor with respect to such a problem, the present invention has been made for the purpose of solving the above problems, and ink absorption, image density, resolution. , A coating liquid excellent in transparency and smoothness, and capable of obtaining a recording medium satisfying color reproducibility and storability of printed matter, and also excellent in dispersibility and stability over time, and a method for producing the same, An image forming method used is provided.

【０００８】[0008]

【課題を解決するための手段】前記の目的は下記の手段
によって達成される。The above object can be achieved by the following means.

【０００９】すなわち、本発明は、アルミナ水和物を主
体としたインク受容層を有する被記録媒体用塗工液にお
いて、該インク受容層を形成せしめる塗工液がアルミナ
水和物を酸で解膠し、次いでアルカリを添加した分散液
と水溶性高分子とから成り、かつ該塗工液のｐＨが３〜
７であることを特徴とする被記録媒体用塗工液を提案す
るものであり、前記アルミナ水和物のＢＥＴ比表面積が
４０〜５００ｍ² ／ｇであること、アルミナ水和物を解
膠する酸が硝酸、塩酸、硫酸、シュウ酸、ギ酸、酢酸、
過塩素酸およびリン酸から選ばれる１種または２種以上
混合した酸であること、アルカリがアンモニア及びアミ
ン化合物であることを含む。That is, according to the present invention, in a coating liquid for a recording medium having an ink receiving layer mainly composed of alumina hydrate, the coating liquid for forming the ink receiving layer dissolves the alumina hydrate with an acid. It consists of a dispersion liquid in which a glue is added and then an alkali is added, and a water-soluble polymer, and the pH of the coating liquid is 3 to
A coating liquid for a recording medium is proposed, wherein the alumina hydrate has a BET specific surface area of 40 to 500 m ² / g, and the alumina hydrate is peptized. Acids are nitric acid, hydrochloric acid, sulfuric acid, oxalic acid, formic acid, acetic acid,
It includes one or a mixture of two or more selected from perchloric acid and phosphoric acid, and the alkali is ammonia and an amine compound.

【００１０】また本発明はアルミナ水和物を酸で解膠
し、次いでアルカリを添加してｐＨを３〜７に調整した
分散液と水溶性高分子とを混合分散することを特徴とす
る被記録媒体用塗工液の製造方法及び基材上に塗工液を
塗工することによって得られる被記録媒体の製造方法に
おいて、該塗工液がアルミナ水和物を酸で解膠し、次い
でアルカリを添加してｐＨを３〜７に調整した後に水溶
性高分子を混合した分散液であることを特徴とする被記
録媒体の製造方法を提案するものである。Further, the present invention is characterized in that a hydrated alumina is peptized with an acid, and then an alkali is added to mix and disperse a dispersion liquid whose pH is adjusted to 3 to 7 and a water-soluble polymer. In a method for producing a recording medium coating liquid and a method for producing a recording medium obtained by applying a coating liquid onto a substrate, the coating liquid peptizes alumina hydrate with an acid, and then The present invention proposes a method for producing a recording medium, which is a dispersion liquid obtained by mixing a water-soluble polymer after adjusting the pH to 3 to 7 by adding an alkali.

【００１１】さらにインクの小滴を微細孔から吐出させ
て被記録媒体に付与して印字を行うインクジェット記録
方法において、請求項６に記載の方法によって得られる
被記録媒体を用いることを特徴とする画像形成方法を提
案するものであり、インクに熱エネルギーを作用させて
インクの小滴を形成することを含む。Further, in the ink jet recording method for performing printing by ejecting a small droplet of ink from a fine hole and applying it to the recording medium, the recording medium obtained by the method according to claim 6 is used. An image forming method is proposed, which comprises applying thermal energy to ink to form ink droplets.

【００１２】本発明で顔料として用いるアルミナ水和物
はインク吸収性や発色性、ビーディングに優れた被記録
媒体が得られる。そして本発明によるアルミナ水和物分
散液は、ｐＨを調整することで印字物の色味変化が極め
て少なく画像保存性に優れ、かつ高い透明性、平滑性を
有するインク受容層が得られる。また本発明によれば、
アルミナ水和物を酸で解膠したときに得られる優れた分
散性が、ｐＨ調整後もそのまま維持されるために、塗工
液の分散性や粘度安定性にも優れ、固形分濃度の高い分
散液の調製が可能となり、塗工適性や生産性にも効果が
絶大である。The alumina hydrate used as a pigment in the present invention can provide a recording medium excellent in ink absorbability, color developability and beading. By adjusting the pH, the alumina hydrate dispersion according to the present invention has an extremely small change in the tint of the printed matter, excellent image storability, and an ink receiving layer having high transparency and smoothness can be obtained. According to the present invention,
The excellent dispersibility obtained when deflocculating alumina hydrate with an acid is maintained as it is even after pH adjustment, so the dispersibility and viscosity stability of the coating liquid are also excellent, and the solid content is high. It becomes possible to prepare a dispersion liquid, which has a great effect on coating suitability and productivity.

【００１３】[0013]

【発明の実施の形態】以下に本発明で好ましく用いられ
るアルミナ水和物の物性について説明する。本発明に用
いられるアルミナ水和物は水酸化アルミニウムと称され
るものも含み、下記一般式により定義されるものであ
る。BEST MODE FOR CARRYING OUT THE INVENTION The physical properties of the alumina hydrate preferably used in the present invention will be described below. The alumina hydrate used in the present invention includes that called aluminum hydroxide and is defined by the following general formula.

【００１４】Ａｌ₂ Ｏ_3-n （ＯＨ）_2n・ｍＨ₂ Ｏ 式中、ｎは０，１，２または３の整数の内のいずれかを
表し、ｍは０〜１０、好ましくは０〜５の値を表す。ｍ
Ｈ₂ Ｏは多くの場合結晶格子の形成に関与しない脱離可
能な水相を表すものであるため、ｍは整数でない値をと
ることができる。また、この種のアルミナ水和物をか焼
するとｍは０の値に達することがある。本発明で被記録
媒体に含有されるアルミナ水和物の製造方法としては、
特に限定はされないが、例えばバイヤー法、明バン熱分
解法などのいずれの方法も採用することができる。特に
好ましくは、長鎖のアルミニウムアルコキシドに対して
酸を添加して加水分解する方法が挙げられる。例えば炭
素数が５以上のアルコキシドであり、さらに炭素数１２
〜２２のアルコキシドを用いると、後述のようなアルコ
ール分の除去、およびアルミナ水和物の形状制御が容易
になるために好ましい。上記方法はアルミナヒドロゲル
やカチオン性アルミナを製造する方法と比較して不純物
の混入が少なく、しかも長鎖のアルミニウムアルコキシ
ドは、加水分解後のアルコールが除去しやすいため、ア
ルミニウムイソプロポキシド等の短鎖アルコキシドを用
いる場合と比べ、脱アルコール化が完全に行なえるとい
う利点がある。Al ₂ O _3-n (OH) _2n · mH ₂ O In the formula, n represents any one of integers of 0, 1, 2 or 3, and m is 0-10, preferably 0-5. Represents the value of. m
In many cases, H ₂ O represents a detachable aqueous phase that does not participate in the formation of the crystal lattice, and therefore m can take a non-integer value. Also, when this type of alumina hydrate is calcined, m may reach a value of zero. The method for producing the alumina hydrate contained in the recording medium in the present invention includes:
Although not particularly limited, for example, any method such as the Bayer method or the Ming-bang thermal decomposition method can be adopted. Particularly preferred is a method in which an acid is added to a long-chain aluminum alkoxide to carry out hydrolysis. For example, an alkoxide having 5 or more carbon atoms and further 12 carbon atoms
It is preferable to use an alkoxide of 22 to facilitate the removal of the alcohol component and the shape control of the alumina hydrate as described below. Compared to the method for producing alumina hydrogel or cationic alumina, the above method has less impurities mixed in, and the long-chain aluminum alkoxide is easy to remove the alcohol after hydrolysis, so that a short-chain such as aluminum isopropoxide can be removed. Compared with the case of using an alkoxide, there is an advantage that dealcoholation can be performed completely.

【００１５】上記方法によって得られたアルミナ水和物
は、水熱合成の工程を経て、粒子を成長させる（熟成工
程）。当該工程の条件を調整することにより、アルミナ
水和物の粒子形状を特定範囲に制御することができる。
熟成時間を適当に設定すると、粒子径が比較的均一なア
ルミナ水和物一次粒子が成長する。ここで得られたゾル
は、解膠剤として酸を添加することでそのまま分散液と
して用いることもできるが、本発明ではゾルをスプレー
ドライ等の方法により粉末化した後、酸を添加して分散
液とすることが好ましい。この場合アルミナ水和物の水
への分散性がより向上し、一次粒子まで分散される。The alumina hydrate obtained by the above method undergoes a hydrothermal synthesis step to grow particles (ripening step). The particle shape of the alumina hydrate can be controlled within a specific range by adjusting the conditions of the step.
When the aging time is appropriately set, alumina hydrate primary particles having a relatively uniform particle size grow. The sol obtained here can be used as a dispersion as it is by adding an acid as a deflocculant, but in the present invention, the sol is pulverized by a method such as spray drying, and then an acid is added to disperse the sol. It is preferably a liquid. In this case, the dispersibility of the alumina hydrate in water is further improved, and even the primary particles are dispersed.

【００１６】本発明で用いられるアルミナ水和物として
はＢＥＴ比表面積が４０〜５００ｍ ² ／ｇであることが
好ましい。ＢＥＴ比表面積が４０ｍ² ／ｇ未満の場合で
はアルミナ水和物の粒子が大きいためにインク受容層の
透明性が損なわれ、画像濃度が低下し、印字物が白くモ
ヤのかかったような画像になりやすい。また、ＢＥＴ比
表面積が５００ｍ² ／ｇを超えた場合ではアルミナ水和
物の解膠に必要な酸の量が多くなり、アルカリを添加し
てｐＨを調整すると分散液が増粘し易くなる。より好ま
しくは５０〜２５０ｍ² ／ｇの範囲であって、インク吸
収性やビーディング、平滑性などに優れている。As the alumina hydrate used in the present invention
Has a BET specific surface area of 40 to 500 m ^Two / G
preferable. BET specific surface area is 40m^Two If less than / g
Has large particles of alumina hydrate,
Transparency is impaired, image density is reduced, and printed matter is white.
The image tends to be dull. Also, the BET ratio
Surface area is 500m^Two Hydration of alumina when the amount exceeds / g
The amount of acid required to peptize the object increases,
When the pH is adjusted by adjusting the pH, the dispersion liquid easily thickens. More preferred
50-250m^Two / G range,
Excellent in yield, beading and smoothness.

【００１７】本発明に用いられるアルミナ水和物を解膠
する酸としては、硝酸、塩酸、硫酸、シュウ酸、ギ酸、
酢酸、過塩素酸およびリン酸から選ばれる１種または２
種以上混合した酸が好ましい。これらの酸はアルミナ水
和物を容易に一次粒子まで解膠することができ、良分散
の均一な分散液が得られる。そのために塗工した際に透
明性や平滑性、皮膜性などに優れたインク受容層が得ら
れる。酸の添加量としては、特に限定はないがアルミナ
水和物を解膠分散するのに十分な量であれば良く、アル
ミナ水和物の重量に対して酸を０．０５〜１０ｍｅｑ／
ｇ（ｍｅｑ：ミリモル当量）添加するのが好ましい。Acids for peptizing the alumina hydrate used in the present invention include nitric acid, hydrochloric acid, sulfuric acid, oxalic acid, formic acid,
One or two selected from acetic acid, perchloric acid and phosphoric acid
Acids mixed with one or more species are preferred. These acids can easily deflocate the alumina hydrate to the primary particles, and a uniform dispersion with good dispersion can be obtained. Therefore, when applied, an ink receiving layer having excellent transparency, smoothness, film-forming property and the like can be obtained. The addition amount of the acid is not particularly limited as long as it is sufficient to peptize and disperse the alumina hydrate, and the acid is added in an amount of 0.05 to 10 meq / weight of the alumina hydrate.
It is preferable to add g (meq: millimol equivalent).

【００１８】該アルミナ水和物に上記酸を添加した分散
液はｐＨが低く、これを塗工して形成されるインク受容
層はインクの変色が起こり易い。そこで本発明では、該
アルミナ水和物を酸で十分に解膠せしめた後に、アルカ
リを添加しｐＨを３〜７に調整することによって、この
問題点を解決するに至った。本発明によれば塗工液の分
散性を損ねることなく、高い分散性を維持しながらｐＨ
を調整することが可能であり、これによって印字物の色
再現性や保存性が大幅に向上することができる。より好
ましくはｐＨの範囲としては３．５〜６で、分散液の経
時安定性が高い。The dispersion obtained by adding the above-mentioned acid to the alumina hydrate has a low pH, and the ink receiving layer formed by coating this is likely to cause discoloration of the ink. Therefore, in the present invention, this problem is solved by sufficiently peptizing the alumina hydrate with an acid and then adding an alkali to adjust the pH to 3 to 7. According to the present invention, the pH is maintained while maintaining high dispersibility without impairing the dispersibility of the coating liquid.
The color reproducibility and storability of the printed matter can be significantly improved. More preferably, the pH range is 3.5 to 6, and the temporal stability of the dispersion is high.

【００１９】また本発明で用いられるアルカリとしては
特に限定はないが、アンモニアや、メチルアミン、エチ
ルアミン、プロピルアミン、ジメチルアミン、ジエチル
アミン、ジプロピルアミン、トリメチルアミン、トリエ
チルアミン、アリルアミン、ジアリルアミンなどのアミ
ン化合物は特にアルミナ水和物の凝集が少ないために、
インク受容層の平滑性や透明性が高く、印字濃度に優れ
ているので好ましい。本発明の被記録媒体において、上
記顔料と組み合わせて使用するバインダーとしては、水
溶性高分子物質が好ましい。例えば、ポリビニルアルコ
ールまたはその変生体（カチオン変性、アニオン変性、
シラノール変性）、澱粉またはその変生体（酸化、エー
テル化）、ゼラチンまたはその変性体、カゼインまたは
その変性体、カルボキシメチルセルロース、アラビヤゴ
ム、ヒドロキシエチルセルロース、ヒドロキシプロピル
メチルセルロース、などのセルロース誘導体、ＳＢＲラ
テックス、ＮＢＲラテックス、メチルメタクレート−ブ
タジエン共重合体などの共役ジエン系共重合体ラテック
ス、官能基変性重合体ラテックス、エチレン酢酸ビニル
共重合体などのビニル系共重合体ラテックス、ポリビニ
ルピロリドン、無水マレイン酸またはその共重合体、ア
クリル酸エステル共重合体等が好ましい。これらのバイ
ンダーは、単独あるいは複数種混合で用いることができ
る。The alkali used in the present invention is not particularly limited, but ammonia and amine compounds such as methylamine, ethylamine, propylamine, dimethylamine, diethylamine, dipropylamine, trimethylamine, triethylamine, allylamine and diallylamine are used. In particular, because there is little aggregation of alumina hydrate,
It is preferable because the ink receiving layer has high smoothness and transparency and excellent printing density. In the recording medium of the present invention, the binder used in combination with the pigment is preferably a water-soluble polymer substance. For example, polyvinyl alcohol or a modified organism thereof (cation-modified, anion-modified,
Silanol-modified), starch or its modified body (oxidation, etherification), gelatin or its modified product, casein or its modified product, carboxymethyl cellulose, arabic gum, hydroxyethyl cellulose, hydroxypropylmethyl cellulose, and other cellulose derivatives, SBR latex, NBR latex , A conjugated diene-based copolymer latex such as a methylmethacrylate-butadiene copolymer, a functional group-modified polymer latex, a vinyl-based copolymer latex such as an ethylene vinyl acetate copolymer, polyvinylpyrrolidone, maleic anhydride or a copolymer thereof. Polymers, acrylic acid ester copolymers and the like are preferable. These binders can be used alone or in combination of two or more.

【００２０】前記顔料とバインダーの混合比は、重量比
で１：１〜３０：１、より好ましくは、５：１〜２０：
１の範囲から任意に選択できる。バインダーの量が上記
範囲より少ない場合は、インク受容層の機械的強度が不
足して、ひび割れや粉落ちが発生し易く、上記範囲を超
える場合は、細孔容積が少なくなってインク吸収性が低
下する。The mixing ratio of the pigment and the binder is 1: 1 to 30: 1 by weight, more preferably 5: 1 to 20 :.
It can be arbitrarily selected from the range of 1. When the amount of the binder is less than the above range, the mechanical strength of the ink receiving layer is insufficient, and cracking and powder falling easily occur, and when the amount exceeds the above range, the pore volume becomes small and the ink absorbency is low. descend.

【００２１】顔料およびバインダーを含む分散液には、
必要に応じて分散剤、増粘剤、ｐＨ調整剤、潤滑剤、界
面活性剤、消泡剤、耐水化剤、離形剤、発泡剤、浸透
剤、着色染料、蛍光増白剤、紫外線吸収剤、酸化防止
剤、防腐剤、防バイ剤等を添加することも可能である。The dispersion containing the pigment and the binder includes
Dispersants, thickeners, pH adjusters, lubricants, surfactants, defoamers, waterproofing agents, release agents, foaming agents, penetrants, coloring dyes, optical brighteners, UV absorption as required. It is also possible to add agents, antioxidants, preservatives, antifungal agents and the like.

【００２２】耐水化剤としてはハロゲン化第四級アンモ
ニウム塩、第四級アンモニウム塩ポリマー等の公知の材
料のなかから自由に選択して用いることができる。The waterproofing agent can be freely selected from known materials such as halogenated quaternary ammonium salts and quaternary ammonium salt polymers.

【００２３】インク受容層は、顔料とバインダーを含む
分散液を塗工装置を用いて、支持体上に塗布、乾燥する
方法により形成される。塗工方法としては、特に制限は
ないが、ブレードコート方式、エアーナイフ方式、ロー
ルコート方式、ブラッシュコート方式、グラビアコート
方式、キスコート方式、エクストルージョン方式、スラ
イドホッパー（スライドビード）方式、カーテンコート
方式、スプレー方式などを用いることができる。The ink receiving layer is formed by a method in which a dispersion containing a pigment and a binder is applied onto a support using a coating apparatus and dried. The coating method is not particularly limited, but may be blade coating method, air knife method, roll coating method, brush coating method, gravure coating method, kiss coating method, extrusion method, slide hopper (slide bead) method, curtain coating method. A spray method or the like can be used.

【００２４】被記録媒体の塗工量は、０．５〜６０ｇ／
ｍ² 、より好ましくは、５〜４５ｇ／ｍ² であるが、良
好なインク吸収性、解像性を得るには、１５μｍ以上、
好ましくは２０μｍ以上のインク受容層の厚みにする必
要がある。支持体としては適度のサイジングを施した
紙、無サイズ紙、レジンコート紙などの紙類、熱可塑性
フィルムのようなシート状物質及び布帛が使用でき、特
に制限はない。The coating amount of the recording medium is 0.5 to 60 g /
m ² , more preferably 5 to 45 g / m ² , but 15 μm or more to obtain good ink absorption and resolution.
The thickness of the ink receiving layer is preferably 20 μm or more. As the support, suitable sized paper, non-sized paper, resin-coated paper, sheet-like material such as thermoplastic film, and cloth can be used, and there is no particular limitation.

【００２５】熱可塑性フィルムの場合はポリエステル、
ポリスチレン、ポリ塩化ビニル、ポリメチルメタクリレ
ート、酢酸セルロース、ポリエチレン、ポリカーボネー
トなどの透明フィルムや、アルミナ水和物やチタンホワ
イトの充填または微細な発泡による不透明化したシート
を用いることもできる。Polyester in the case of a thermoplastic film,
It is also possible to use a transparent film of polystyrene, polyvinyl chloride, polymethylmethacrylate, cellulose acetate, polyethylene, polycarbonate or the like, or an opaque sheet filled with alumina hydrate or titanium white or finely foamed.

【００２６】また、上記支持体とインク受容層との接着
性を良好にするために、コロナ処理等の表面処理を行っ
たり、易接着層を下引き層として設けても良い。さらに
カールを防止するために支持体の裏面あるいは所定の部
位に樹脂層や顔料層等のカール防止層を設けることもで
きる。Further, in order to improve the adhesion between the support and the ink receiving layer, a surface treatment such as corona treatment may be carried out, or an easily adhesive layer may be provided as an undercoat layer. Further, in order to prevent curling, a curl preventing layer such as a resin layer or a pigment layer may be provided on the back surface of the support or at a predetermined portion.

【００２７】本発明の記録方法に使用されるインクは、
主として色材（染料もしくは顔料）、水溶性有機溶剤及
び水を含むものである。染料としては、例えば直接染
料、酸性染料、塩基性染料、反応性染料、食用色素など
に代表される水溶性染料が好ましく、被記録媒体との組
み合わせで定着性、発色性、鮮明性、安定性、耐光性そ
の他の要求される性能を満たす画像を与えるものであれ
ばいずれでも使用できる。The ink used in the recording method of the present invention is
It mainly contains a coloring material (dye or pigment), a water-soluble organic solvent and water. As the dye, for example, a water-soluble dye represented by a direct dye, an acid dye, a basic dye, a reactive dye, an edible dye, or the like is preferable, and in combination with a recording medium, fixability, color development, clarity, and stability. Any material can be used as long as it gives an image that satisfies the required performance, such as light resistance.

【００２８】水溶性染料は、一般に水または水と有機溶
剤からなる溶媒中に溶解して使用するものであり、これ
らの溶媒成分としては、好ましくは水と水溶性の各種有
機溶剤などとの混合物が使用されるが、インク中の水分
含有量が、２０〜９０重量％、好ましくは６０〜９０重
量％の範囲内となるように調整するのが好ましい。上記
水溶性の有機溶剤としては、例えばメチルアルコール、
エチルアルコール、ｎ−プロピルアルコール、イソプロ
ピルアルコール、ｎ−ブチルアルコール、ｓｅｃ−ブチ
ルアルコール、ｔｅｒｔ−ブチルアルコール、イソブチ
ルアルコールなどの炭素数が１〜４のアルキルアルコー
ル類、ジメチルホルムアミド、ジメチルアセトアミドな
どのアミド類、アセトン、ジアセトンアルコールなどの
ケトンまたはケトンアルコール類、テトラヒドロフラ
ン、ジオキサンなどのエーテル類、ポリエチレングリコ
ール、ポリプロピレングリコールなどのポリアルキレン
グリコール類、エチレングリコール、プロピレングリコ
ール、１、２、６−ヘキサントリオール、チオジグリコ
ール、ヘキシレングリコール、ジエチレングリコールな
どのアルキレン基が２〜６個の炭素数を含むアルキレン
グリコール類、グリセリン；エチレングリコールメチル
エーテル、ジエチレングリコールメチルエーテル、ジエ
チレングリコールエチルエーテル、トリエチレングリコ
ールモノメチルエーテル、トリエチレングリコールモノ
エチルエーテルなどの多価アルコールの低級アルキルエ
ーテル類などが挙げられる。The water-soluble dye is generally used by dissolving it in water or a solvent consisting of water and an organic solvent, and the solvent component thereof is preferably a mixture of water and various water-soluble organic solvents. Is used, but it is preferable to adjust the water content in the ink to be in the range of 20 to 90% by weight, preferably 60 to 90% by weight. Examples of the water-soluble organic solvent include methyl alcohol,
Alkyl alcohols having 1 to 4 carbon atoms such as ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol and isobutyl alcohol, amides such as dimethylformamide and dimethylacetamide. , Ketones or ketone alcohols such as acetone and diacetone alcohol, ethers such as tetrahydrofuran and dioxane, polyalkylene glycols such as polyethylene glycol and polypropylene glycol, ethylene glycol, propylene glycol, 1,2,6-hexanetriol, thio Alkylene glycols having an alkylene group of 2 to 6 carbon atoms, such as diglycol, hexylene glycol, and diethylene glycol; Phosphorus, ethylene glycol methyl ether, diethylene glycol methyl ether, diethylene glycol ethyl ether, triethylene glycol monomethyl ether, such as lower alkyl ethers of polyhydric alcohols such as triethylene glycol monoethyl ether.

【００２９】これらの多くの水溶性有機溶剤の中でも、
エチレングリコール、ジエチレングリコールなどの多価
アルコール、トリエチレングリコールモノメチルエーテ
ル、トリエチレングリコールモノエチルエーテルなどの
多価アルコールの低級アルキルエーテル類が好ましい。
多価アルコール類は、インク中の水が蒸発し、水溶性染
料が析出することに基づくノズルの目詰まり減少を防止
するための潤滑剤としての効果が大きいため、特に好ま
しい。Among these many water-soluble organic solvents,
Preferred are polyhydric alcohols such as ethylene glycol and diethylene glycol, and lower alkyl ethers of polyhydric alcohols such as triethylene glycol monomethyl ether and triethylene glycol monoethyl ether.
Polyhydric alcohols are particularly preferable because they have a great effect as a lubricant for preventing a decrease in nozzle clogging due to evaporation of water in the ink and precipitation of a water-soluble dye.

【００３０】インクには可溶化剤を加えることもでき
る。代表的な可溶化剤は、含窒素複素環式ケトン類であ
り、その目的とする作用は、水溶性染料の溶媒に対する
溶解性を飛躍的に向上させることにある。例えばＮ−メ
チル−２−ピロリドン、１、３−ジメチル−２−イミダ
ゾリジノンが好ましく用いられる。さらに特性の改善の
ために、粘度調整剤、界面活性剤、表面張力調整剤、ｐ
Ｈ調整剤、比抵抗調整剤、保存安定剤などの添加剤を加
えて用いることもできる。A solubilizing agent may be added to the ink. Typical solubilizers are nitrogen-containing heterocyclic ketones, and their intended action is to dramatically improve the solubility of the water-soluble dye in a solvent. For example, N-methyl-2-pyrrolidone and 1,3-dimethyl-2-imidazolidinone are preferably used. In order to further improve the properties, a viscosity modifier, a surfactant, a surface tension modifier, p
Additives such as an H adjuster, a specific resistance adjuster, and a storage stabilizer can also be added and used.

【００３１】前記被記録媒体に上記インクを付与して記
録を行う方法としては、インクジェット記録方法が好ま
しく、該記録方法はインクをノズルより効果的に離脱さ
せて、被記録媒体にインクを付与し得る方法であればい
かなる方法でも良い。特に特開昭５４−５９９３６号公
報に記載されている方法で、熱エネルギーの作用を受け
たインクが急激な体積変化を生じ、この状態変化による
作用力によって、インクをノズルから吐出させるインク
ジェット方式は有効に使用することができる。An ink jet recording method is preferable as a method for recording by applying the ink to the recording medium, and the recording method applies the ink to the recording medium by effectively separating the ink from the nozzles. Any method may be used as long as it can be obtained. In particular, according to the method described in Japanese Patent Application Laid-Open No. 54-59936, an ink jet method in which ink subjected to the action of thermal energy causes a sudden volume change, and the ink is ejected from a nozzle by the action force due to this state change. Can be used effectively.

【００３２】[0032]

【実施例】以下、実施例を示し、本発明をさらに具体的
に説明するが、本発明がこれらに限定されるものではな
い。EXAMPLES The present invention will be described in more detail below with reference to examples, but the present invention is not limited thereto.

【００３３】アルミナ水和物の製造法 米国特許明細書第４２４２２７１号に記載された方法で
アルミニウムドデキシドを製造した。つぎに米国特許明
細書第４２０２８７０号に記載された方法で前記アルミ
ニウムアルコキシドを加水分解してアルミナスラリーを
製造した。このアルミナスラリーをアルミナ水和物固形
分が７．９％になるまで水を加え、さらに表１に示すそ
れぞれの熟成条件でコロイダルゾルを得た。このコロイ
ダルゾルを７５℃でスプレー乾燥してアルミナ水和物
（Ａ，Ｂ，Ｃ，Ｄ）を得た。これらアルミナ水和物のＢ
ＥＴ比表面積をＢｒｕｎａｕｅｒらの方法により計算し
求めた。その結果を表１に示す。 Method for Producing Alumina Hydrate Aluminum dodoxide was produced by the method described in US Pat. No. 4,242,271. Next, the aluminum alkoxide was hydrolyzed by the method described in U.S. Pat. No. 4,202,870 to produce an alumina slurry. Water was added to this alumina slurry until the alumina hydrate solid content became 7.9%, and colloidal sols were obtained under the respective aging conditions shown in Table 1. This colloidal sol was spray-dried at 75 ° C. to obtain alumina hydrate (A, B, C, D). B of these alumina hydrates
The ET specific surface area was calculated and determined by the method of Brunauer et al. Table 1 shows the results.

【００３４】[0034]

【表１】 実施例（１〜５） イオン交換水５６重量部に対し、アルミナ水和物（Ａ〜
Ｄ）１４重量部および種々の１規定濃度の酸水溶液を１
４重量部添加後、分散機（特殊機化（株）製、Ｔ．Ｋ．
オートホモミクサーＭ型）にて解膠、分散し、次いでｐ
Ｈメーター（（株）堀場製作所製、Ｄ−１２）で計測し
ながら徐々に種々の１０％アミン水溶液を混合攪拌して
所定のｐＨに調整した。これに１０％ポリビニルアルコ
ール水溶液（日本合成化学（株）製、ゴーセノールＧＨ
−１７Ｒ）を１５重量部をそれぞれ添加、分散して塗工
液を得た。塗工液の分散安定性を後述の方法で測定し
た。これを白色ポリエステルフィルム（東レ（株）製、
ルミラーＸ−２１、厚み１００μｍ）と透明ポリエステ
ルフィルム（東レ（株）製、１００Ｑ８０Ｄ、厚み１０
０μｍ、透過率８８．７４％）の上にそれぞれバーコー
トし、１００℃で乾燥して厚さ３０μｍのインク受容層
を形成する被記録媒体を得た。インク受容層の物性をそ
れぞれ後述の方法で測定した。結果を表２に示す。[Table 1] Example (1 to 5) Alumina hydrate (A to
D) 1 part by weight of 14 parts by weight and various 1N concentration aqueous acid solutions
After adding 4 parts by weight, a disperser (manufactured by Tokushu Kika Co., Ltd., TK.
Peptide and disperse with an auto homomixer M type), then p
While measuring with an H meter (D-12, manufactured by Horiba, Ltd.), various 10% amine aqueous solutions were gradually mixed and stirred to adjust to a predetermined pH. 10% polyvinyl alcohol aqueous solution (Nippon Gosei Kagaku KK, Gohsenol GH)
Each of 15 parts by weight of -17R) was added and dispersed to obtain a coating liquid. The dispersion stability of the coating liquid was measured by the method described below. This is a white polyester film (manufactured by Toray Industries, Inc.,
Lumirror X-21, thickness 100 μm) and transparent polyester film (manufactured by Toray Industries, Inc., 100Q80D, thickness 10)
0 μm, transmittance 88.74%) was bar-coated on each and dried at 100 ° C. to obtain a recording medium on which an ink receiving layer having a thickness of 30 μm was formed. The physical properties of the ink receiving layer were measured by the methods described below. Table 2 shows the results.

【００３５】[0035]

【表２】 塗工液および被記録媒体物性の評価・測定方法 １）塗工液の分散安定性 分散液を調製した直後の初期粘度と、その液を２５℃で
７日間密閉容器中に静置保存した後の経時粘度をＢ型回
転粘度計（ＴＯＫＩＭＥＣ社製，ＶＩＳＣＯＭＥＴＥ
Ｒ）を用いて下記の条件で測定し、経時粘度／初期粘度
を求めた。[Table 2] Method for evaluating and measuring physical properties of coating liquid and recording medium 1) Dispersion stability of coating liquid After initial storage viscosity of the dispersion liquid and its liquid being stored in a closed container at 25 ° C for 7 days Viscosity with time of type B rotational viscometer (manufactured by TOKIMEC, VISCOMETE
R) was measured under the following conditions to determine the viscosity with time / initial viscosity.

【００３６】ローター：Ｎｏ．１、回転数：３０ｒｐ
ｍ、測定温度：２５℃ ２）インク受容層の塗膜状態 白色基材上にインク受容層を設けた被記録媒体に対して
目視により評価した。平滑面が得られ良好なものを○、
粗面あるいは不溶物付着等のよる欠陥を生じたものを×
とした。Rotor: No. 1, rotation speed: 30 rp
m, measurement temperature: 25 ° C. 2) Coating state of ink receiving layer A recording medium having an ink receiving layer on a white base material was visually evaluated. Good one with a smooth surface
Those that have defects such as rough surfaces or insoluble matter adhesion x
And

【００３７】３）インク受容層の透明性 透明基材上にインク受容層を設けた被記録媒体に対して
ヘイズメーター（日本電色工業（株）製、ＮＨＤ−１０
０１ＤＰ）を用いて透過率を測定した。3) Transparency of ink receiving layer A haze meter (manufactured by Nippon Denshoku Industries Co., Ltd., NHD-10) for a recording medium provided with an ink receiving layer on a transparent substrate.
01DP) was used to measure the transmittance.

【００３８】４）印字特性 １ｍｍに１６本の割合のノズル間隔で、１２８本のノズ
ルを供えたインクジェットヘッドをＹ、Ｍ、Ｃ、Ｂｋの
４色分備えたバブルジェットプリンターを用い、下記組
成のインクにより、白色基材上にインク受容層を設けた
被記録媒体に対してインクジェット記録を行なって、イ
ンク吸収性、画像濃度、解像性、ビーディング、色再現
性、記録保存性について評価した。4) Printing characteristics Using a bubble jet printer equipped with ink jet heads provided with 128 nozzles at a nozzle spacing of 16 nozzles per 1 mm for four colors Y, M, C and Bk, the following composition was used. Inkjet recording was performed on a recording medium having an ink receiving layer on a white base material with an ink, and the ink absorbency, image density, resolution, beading, color reproducibility, and record storability were evaluated. .

【００３９】（ａ）インク吸収性 下記組成のＹ、Ｍ、Ｃ、Ｂｋそれぞれのインクを単色ま
たは多色でベタ印字した後の被記録媒体表面のインクの
乾燥状態を記録部に指で触れて調べた。単色印字でのイ
ンク量を１００％とした。インク量３００％でインクが
指に付着しないものを◎、インク量２００％でインクが
指に付着しないものを○、インク量１００％でインクが
指に付着しないものを△とした。(A) Ink Absorption Absorbency of ink on the surface of a recording medium after solid printing of each of Y, M, C, and Bk inks having the following compositions with a single color or multiple colors is touched with a finger on the recording portion. Examined. The ink amount in monochromatic printing was set to 100%. When the ink amount was 300%, the ink did not adhere to the finger, ⊚, when the ink amount was 200%, the ink did not adhere to the finger, ◯, and when the ink amount was 100%, the ink did not adhere to the finger, Δ.

【００４０】（ｂ）画像濃度 下記組成のＭインクでベタ印字した画像の画像濃度を、
マクベス反射濃度計ＲＤ−１２５５を用いて評価した
（いずれの実施例においても４色中、Ｍの画像濃度が最
も低かった）。(B) Image Density The image density of the image solidly printed with the M ink having the following composition is
Evaluation was carried out using a Macbeth reflection densitometer RD-1255 (in any of the examples, the image density of M was the lowest among the four colors).

【００４１】（ｃ）解像性 下記組成のＹ、Ｍ、Ｃ、Ｂｋそれぞれのインクを単色ま
たは多色でベタ印字した後の被記録媒体表面のドットに
じみを目視によって評価した。単色印字でのインク量を
１００％とした。インク量３００％で発生してしなけれ
ば◎、インク量２００％で発生していなければ○、イン
ク量１００％で発生していなければ△とした。(C) Resolution The dot bleeding on the surface of the recording medium after solid printing of each of the inks of Y, M, C and Bk having the following compositions in a single color or multiple colors was visually evaluated. The ink amount in monochromatic printing was set to 100%. When the ink amount did not occur at 300%, the result was ⊚, when the ink amount did not occur at 200%, the result was ◯, and when the ink amount did not occur at 100%, the result was Δ.

【００４２】（ｄ）ビーディング 下記組成のＹ、Ｍ、Ｃ、Ｂｋそれぞれのインクを単色ま
たは多色でベタ印字した後の印字部での粒状の濃度ムラ
を目視により評価した。インク量３００％で発生してい
なければ◎、インク量２００％で発生していなければ
○、インク量１００％で発生していなければ△とした。(D) Beading Each of the Y, M, C, and Bk inks having the following compositions was solid-printed in a single color or multiple colors, and the granular density unevenness in the printed portion was visually evaluated. When the ink amount was not generated at 300%, it was rated as ⊚, when it was not generated at the ink amount of 200%, it was rated as ◯, and when it was not generated at the ink amount of 100%, it was rated as Δ.

【００４３】（ｅ）色再現性 下記組成のＣインクの最大吸収波長λ１とシアンインク
により印字した被記録媒体の印字部の最大吸収波長λ２
とを分光光度計（（株）日立製作所製、日立自記分光光
度計Ｕ−３４１０）を用いて測定し、各色の最大吸収波
長の変化量（ΔλＣ）の絶対値を求めた。(E) Color Reproducibility The maximum absorption wavelength λ1 of the C ink having the following composition and the maximum absorption wavelength λ2 of the printing portion of the recording medium printed with the cyan ink.
Were measured using a spectrophotometer (Hitachi Autograph U-3410, manufactured by Hitachi, Ltd.), and the absolute value of the change amount (ΔλC) of the maximum absorption wavelength of each color was obtained.

【００４４】（ｆ）記録保存性 下記のＢｋインクをベタ印字した後に該被記録媒体を一
ヶ月間室内で放置した。この印字部の放置前後での色度
差ΔＥをＪＩＳ−８７３０により求めた。(F) Recording storability After solid printing of the following Bk ink, the recording medium was left indoors for one month. The chromaticity difference ΔE before and after leaving the printed portion was determined according to JIS-8730.

【００４５】 インク組成 染料 ５部 エチレングリコール １０部 ポリエチレングリコール １０部 水 ７５部 インク染料 Ｙ：Ｃ．Ｉ．ダイレクトイエロー８６ Ｍ：Ｃ．Ｉ．アシッドレッド３５ Ｃ：Ｃ．Ｉ．ダイレクトブルー１９９ Ｂｋ：Ｃ．Ｉ．フードブラック２Ink composition Dye 5 parts Ethylene glycol 10 parts Polyethylene glycol 10 parts Water 75 parts Ink dye Y: C.I. I. Direct Yellow 86 M: C.I. I. Acid Red 35 C: C.I. I. Direct Blue 199 Bk: C.I. I. Food black 2

【００４６】[0046]

【発明の効果】アルミナ水和物の水性ゾルに酸を加えて
解膠させた後にアルカリを添加してｐＨを３〜７に調整
した分散液を用いてインク受容層を形成することによっ
て、印字物の色再現性や保存性に優れるとともにインク
吸収性、ビーディング、画像濃度に優れ、かつ高い透明
性と平滑性を有する被記録媒体が得られる。また塗工液
の分散性や経時保存性にも優れている。EFFECTS OF THE INVENTION By adding an acid to an aqueous sol of alumina hydrate to peptize it, and then adding an alkali to form an ink-receiving layer using a dispersion having a pH adjusted to 3 to 7, A recording medium having excellent color reproducibility and storability, excellent ink absorbency, beading, image density, and high transparency and smoothness can be obtained. It is also excellent in dispersibility of the coating liquid and storage stability over time.

Claims (8)

【特許請求の範囲】[Claims] 【請求項１】 アルミナ水和物を主体としたインク受容
層を有する被記録媒体用塗工液において、該インク受容
層を形成せしめる塗工液がアルミナ水和物を酸で解膠
し、次いでアルカリを添加した分散液と水溶性高分子と
から成り、かつ該塗工液のｐＨが３〜７であることを特
徴とする被記録媒体用塗工液。1. A coating liquid for a recording medium having an ink receiving layer mainly composed of alumina hydrate, wherein the coating liquid for forming the ink receiving layer peptizes the alumina hydrate with an acid, and then A coating liquid for a recording medium, which comprises a dispersion liquid to which an alkali is added and a water-soluble polymer, and has a pH of 3 to 7. 【請求項２】 前記アルミナ水和物のＢＥＴ比表面積が
４０〜５００ｍ² ／ｇである請求項１に記載の被記録媒
体用塗工液。2. The coating liquid for a recording medium according to claim 1, wherein the BET specific surface area of the alumina hydrate is 40 to 500 m ² / g. 【請求項３】 アルミナ水和物を解膠する酸が硝酸、塩
酸、硫酸、シュウ酸、ギ酸、酢酸、過塩素酸およびリン
酸から選ばれる１種または２種以上混合した酸である請
求項１に記載の被記録媒体用塗工液。3. The acid for deflocculating alumina hydrate is one or a mixture of two or more selected from nitric acid, hydrochloric acid, sulfuric acid, oxalic acid, formic acid, acetic acid, perchloric acid and phosphoric acid. 1. The coating liquid for a recording medium according to 1. 【請求項４】 アルカリがアンモニア及びアミン化合物
である請求項１に記載の被記録媒体用塗工液。4. The coating liquid for a recording medium according to claim 1, wherein the alkali is ammonia and an amine compound. 【請求項５】 アルミナ水和物を酸で解膠し、次いでア
ルカリを添加してｐＨを３〜７に調整した分散液と水溶
性高分子とを混合分散することを特徴とする被記録媒体
用塗工液の製造方法。5. A recording medium characterized by deflocculating alumina hydrate with an acid, and then adding an alkali to adjust the pH to 3 to 7 and mixing and dispersing the water-soluble polymer. For producing coating fluid for use in manufacturing. 【請求項６】 基材上に塗工液を塗工することによって
得られる被記録媒体の製造方法において、該塗工液がア
ルミナ水和物を酸で解膠し、次いでアルカリを添加して
ｐＨを３〜７に調整した後に水溶性高分子を混合した分
散液であることを特徴とする被記録媒体の製造方法。6. A method for producing a recording medium obtained by applying a coating liquid onto a substrate, wherein the coating liquid peptizes alumina hydrate with an acid, and then an alkali is added. A method for producing a recording medium, which is a dispersion in which a water-soluble polymer is mixed after adjusting the pH to 3 to 7. 【請求項７】 インクの小滴を微細孔から吐出させて被
記録媒体に付与して印字を行うインクジェット記録方法
において、請求項６に記載の方法によって得られる被記
録媒体を用いることを特徴とする画像形成方法。7. A recording medium obtained by the method according to claim 6, wherein a recording medium obtained by the method according to claim 6 is used in an ink jet recording method in which droplets of ink are ejected from fine holes and applied to the recording medium. Image forming method. 【請求項８】 インクに熱エネルギーを作用させてイン
クの小滴を形成する請求項７に記載の画像形成方法。8. The image forming method according to claim 7, wherein thermal energy is applied to the ink to form small droplets of the ink.