JPH0892075A - Plaster - Google Patents

Abstract

PURPOSE: To obtain a plaster having elasticity to come into close contact with the uneven surface of the human skin, exhibiting good tacky adhesiveness and feeling in use, peelable without giving pain to the skin and having little tendency to cause low-temperature scald in the case of thermotherapy by forming a tacky adhesive layer having a specific constitution on a substrate. CONSTITUTION: This plaster is composed of a substrate and a tacky adhesive layer made of a foamed tacky adhesive containing a hot-melt polymeric substance (e.g. styrene-butadiene-styrene block copolymer) and formed on the substrate at a thickness of preferably 80-1,000μm. The tacky adhesive is preferably composed of 10-30 pts.wt. of a hot-melt polymeric substance, 10-50 pts.wt. of an alicyclic petroleum resin as a tackifying agent, 15-45 pts.wt. of a softening agent and 1-8 pts.wt. of a water-absorbing polymer. The foaming of the tacky adhesive is preferably carried out by a physical foaming method comprising the mechanical mixing of a gas such as air under heating to uniformly disperse the gas and the foaming of the adhesive under atmospheric pressure.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、外皮に貼付されて患部
の治療や温熱効果を与える貼付剤に関するものであり、
特に、弾力性があって人体皮膚の凹凸面にも追従して密
着し、しかも粘着性及び使用感が良好である上、剥離時
の苦痛が無く、又、温熱を与えたとき、粘着剤層が発泡
体で形成されているので、熱伝導を制御して低温火傷が
生じ難い粘着剤層を備える貼付剤に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an adhesive patch which is applied to the outer skin to treat an affected area and has a heating effect.
In particular, it is elastic and adheres closely to the uneven surface of human skin, and has good adhesiveness and usability, and there is no pain during peeling, and when heat is applied, the adhesive layer Since it is formed of a foam, the patch is provided with an adhesive layer that controls heat conduction and hardly causes low-temperature burns.

【０００２】[0002]

【従来の技術】従来より、種々の目的で人体に適用され
る貼付剤には粘着剤が用いられているが、この粘着剤を
大別すると、ゴム系粘着剤とアクリル系粘着剤に分類さ
れる。2. Description of the Related Art Conventionally, adhesives have been used in patches applied to the human body for various purposes, but these adhesives are roughly classified into rubber adhesives and acrylic adhesives. It

【０００３】又、この貼付剤を大別すると、発熱体を備
えるものと、発熱体を備えないものとに分類される。The patches are roughly classified into those with a heating element and those without a heating element.

【０００４】この場合、発熱体としては、通気性フィル
ムで構成された開放部のないシート状袋体の内部に、発
熱体組成物、例えば鉄粉、活性炭及び塩類等からなる発
熱体組成物を封入してなるものが提案されている(特開
昭５０−５４１８８号公報、特開昭５３−４７１５４号
公報、特開昭５３−６０８８５号公報、特開昭５４−１
５５９８４号公報、特開昭５５−１４０６７号公報、特
開昭５５−１６６１４７号公報、特開昭６２−１０３０
１４号公報、実公昭５８−２２７３３号公報等)。In this case, as the heating element, a heating element composition such as iron powder, activated carbon and salts is provided inside a sheet-like bag having no opening and formed of a breathable film. Encapsulated products have been proposed (Japanese Patent Laid-Open Nos. 50-54188, 53-47154, 53-60885, and 54-1).
55984, JP-A-55-14067, JP-A-55-166147, and JP-A-62-1030.
14 gazette, Jitsuko 58-22733 gazette, etc.).

【０００５】[0005]

【発明が解決しようとする課題】これらの粘着剤を用い
て形成した粘着剤層には弾力性がなく、外皮の凹凸面に
追従し難いので密着性に欠けるのであり、しかも使用に
際し、突っ張り感が生じる等、使用感が悪いのである。The pressure-sensitive adhesive layer formed by using these pressure-sensitive adhesives has no elasticity, and it is difficult to follow the uneven surface of the outer skin, resulting in lack of adhesion. It has a bad usability such as occurrence of.

【０００６】又、発熱体を備える貼付剤の場合、この貼
付剤は外皮に直接当てて使用するものであり、使用者が
温度変化を敏感に感知しうると共に温度のバラツキがあ
って低温火傷が発生し易い。Further, in the case of a patch having a heating element, this patch is used by directly applying it to the outer skin, and the user can sensitively detect the temperature change and the temperature varies, which causes low-temperature burns. It is easy to occur.

【０００７】ところで、上記の粘着剤のうち、ゴム系粘
着剤を用いた貼付剤には初期タックがあり、低温、常温
時の粘着性が非常にすぐれているが、粘着後における粘
着力の経時変化が発生するのであり、特に、上記発熱体
による高温時の粘着力の経時変化が大であるなどの課題
がある。By the way, among the above-mentioned pressure-sensitive adhesives, a patch using a rubber-based pressure-sensitive adhesive has an initial tack, and the adhesiveness at low temperature and room temperature is very excellent. However, there is a problem in that the adhesive force due to the above-mentioned heating element changes at a high temperature over time.

【０００８】一方、アクリル系粘着剤を用いた貼付剤は
初期タックが乏しく、低温、常温時の粘着性に欠けるき
らいがある。On the other hand, a patch using an acrylic adhesive has a poor initial tack and tends to lack adhesiveness at low temperature and room temperature.

【０００９】本発明は、上記技術的課題を解決するため
に完成されたものであって、この種、貼付剤において、
粘着剤層がホットメルト型高分子物質を含有する粘着剤
の発泡体で形成されていることにより、弾力性があって
人体皮膚の凹凸面にも追従して密着し、しかも粘着性及
び使用感が良好である上、剥離時の苦痛が無く、又、温
熱を与えたとき、粘着剤層が発泡体で形成されているの
で、この発泡体が熱伝導を制御して低温火傷が生じ難い
貼付剤を提供することを目的とする。The present invention has been completed to solve the above technical problems, and in this type of patch,
The pressure-sensitive adhesive layer is made of a foam of pressure-sensitive adhesive containing a hot-melt type polymer substance, so that it has elasticity and adheres to the uneven surface of human skin to adhere to it. In addition, there is no pain when peeling, and when heat is applied, the adhesive layer is formed of foam, so this foam controls heat conduction and low-temperature burns are less likely to occur. The purpose is to provide an agent.

【００１０】[0010]

【課題を解決するための手段】本発明の貼付剤は、上記
目的を達成するために、支持体に粘着剤層を設けた貼付
剤において、この粘着剤層がホットメルト型高分子物質
を含有する粘着剤の発泡体で形成されている、との技術
的手段を講じたものである。Means for Solving the Problems In order to achieve the above object, the patch of the present invention is a patch in which a pressure-sensitive adhesive layer is provided on a support, and the pressure-sensitive adhesive layer contains a hot melt type polymer substance. It is formed of a foam of a pressure sensitive adhesive.

【００１１】以下、本発明を詳細に説明する。本発明で
用いられる支持体としては、後述する粘着剤層を保持し
得るフィルム状ないしシート状のものであれば特に限定
されるものではないが、具体的には、例えばポリエチレ
ン、ポリプロピレン、ポリブタジエン、エチレン酢酸ビ
ニル共重合体、ポリ塩化ビニル、ポリエステル、ポリア
ミド又はポリウレタン等の合成樹脂で形成された単層の
フィルム又はシート或いはこれらのフィルム又はシート
を２枚以上積層した積層体、多孔質体、発泡体、紙、布
及び不織布等が挙げられる。The present invention will be described in detail below. The support used in the present invention is not particularly limited as long as it is a film-like or sheet-like one capable of holding the pressure-sensitive adhesive layer described later, but specifically, for example, polyethylene, polypropylene, polybutadiene, A single-layer film or sheet formed of a synthetic resin such as ethylene-vinyl acetate copolymer, polyvinyl chloride, polyester, polyamide or polyurethane, or a laminated body, a porous body, or a foamed body in which two or more of these films or sheets are laminated. Examples thereof include bodies, papers, cloths and non-woven fabrics.

【００１２】又、本発明においては、粘着剤層がホット
メルト型高分子物質を含有する粘着剤の発泡体で形成さ
れている点、に最も大きな特徴を有する。Further, the present invention is most characterized in that the pressure-sensitive adhesive layer is formed of a pressure-sensitive adhesive foam containing a hot-melt type polymer substance.

【００１３】この粘着剤層の厚さとしては特に限定され
るものではないが、１０〜３０００μｍ、特に、５０〜
２０００μｍ、更に好ましくは８０〜１０００μｍとす
るのが好ましく、粘着剤層の厚さが、１０μｍ未満にな
ると所要の粘着力を得られない場合があり、一方、３０
００μｍを超えると使用感が悪くなるだけでなく、経済
性が悪くなるので好ましくない。The thickness of the pressure-sensitive adhesive layer is not particularly limited, but is 10 to 3000 μm, particularly 50 to
The thickness is preferably 2000 μm, more preferably 80 to 1000 μm. If the thickness of the pressure-sensitive adhesive layer is less than 10 μm, the required pressure-sensitive adhesive strength may not be obtained.
When it exceeds 00 μm, not only is the feeling of use deteriorated, but also the economy is deteriorated, which is not preferable.

【００１４】本発明においては、このように粘着剤層が
ホットメルト型高分子物質を含有する粘着剤の発泡体を
用いることによって、上記目的を達成できる。In the present invention, the above object can be achieved by using a foam of a pressure-sensitive adhesive whose pressure-sensitive adhesive layer contains a hot-melt type polymer substance.

【００１５】本発明において、ホットメルト型高分子物
質を含有する粘着剤としては、ホットメルト型高分子物
質を含有するものであれば良く、従って、他の成分、例
えば他の粘着剤、粘着賦与剤、老化防止剤、充填剤、粘
着調整剤、粘着改良剤、着色剤、消泡剤、増粘剤、改質
剤、防カビ剤、抗菌剤、殺菌剤、消臭剤又は脱臭剤等が
配合されていても良い意味である。In the present invention, the pressure-sensitive adhesive containing the hot-melt type polymer substance may be any one containing the hot-melt type polymer substance. Therefore, other components, for example, other pressure-sensitive adhesives and tackifiers. Agents, anti-aging agents, fillers, adhesion modifiers, adhesion improvers, colorants, defoamers, thickeners, modifiers, fungicides, antibacterial agents, bactericides, deodorants or deodorants, etc. It means that they may be mixed.

【００１６】又、この粘着剤の発泡体とは、化学的発泡
或いは物理的発泡に拘わらず、又、独立気泡、連続気泡
又は独立気泡と連続気泡が混在したものなど、いずれの
ものでも良いが、外皮に適用されるものであるので、常
温で粘着性を有するものであることを要する。Further, the foam of the pressure-sensitive adhesive may be any foam, regardless of chemical foaming or physical foaming, or closed cells, open cells or a mixture of closed cells and open cells. Since it is applied to the outer skin, it needs to have adhesiveness at room temperature.

【００１７】ところで、化学的発泡とは、無機系発泡剤
又は有機系発泡剤或いはこれらの混合物を用い、その分
解反応の際に発生する窒素ガスや炭酸ガス等を利用する
ものであり、物理的発泡とは、例えば加熱加圧下で空
気、炭酸ガス又は窒素ガスを混入し、大気圧下で発泡さ
せるものである。By the way, the chemical foaming is to use an inorganic foaming agent, an organic foaming agent, or a mixture thereof, and to utilize nitrogen gas, carbon dioxide gas, etc. generated during the decomposition reaction, and to physically The foaming is, for example, mixing air, carbon dioxide gas or nitrogen gas under heating and pressurization to foam under atmospheric pressure.

【００１８】これらのうち、特に、特公昭６０−３３５
０号公報、特開昭６２ー８７２６７号公報、特公昭６３
ー１７２９５号公報、特開平１ー５９０２３号公報及び
特公平２ー４８１９１号公報等の物理的発泡の方法が以
下に述べる理由より、望ましい。Of these, especially Japanese Examined Patent Publication No. 60-335.
No. 0, JP-A-62-87267, JP-B-63
For example, the physical foaming methods described in JP-A-17295, JP-A-1-59023 and JP-B-2-48191 are preferable for the following reasons.

【００１９】即ち、これらの方法は、ホットメルト型高
分子物質に空気又は窒素ガス等の気体を比較的低圧下で
機械的に、加熱混入して均一に分散した後、大気圧で発
泡させるものであるから、発泡剤を用いるものに比較し
て圧力条件、加熱温度条件等の設定が容易であり、しか
も空気又は窒素ガス等の小さな気泡を含む比較的均質な
発泡体が再現性良く得られる。That is, in these methods, a gas such as air or nitrogen gas is mechanically heated and mixed into a hot-melt type polymer substance under a relatively low pressure to uniformly disperse, and then foamed at atmospheric pressure. Therefore, it is easier to set pressure conditions, heating temperature conditions, etc., as compared with those using a foaming agent, and a relatively homogeneous foam containing small bubbles such as air or nitrogen gas can be obtained with good reproducibility. .

【００２０】又、ホットメルト型高分子物質の中に、空
気もしくは窒素ガス、炭酸ガス等を無数の独立気泡とし
て混入させたものであり、その結果、そのものは体積が
１倍を超え数倍に膨張された発泡体であるが、この発泡
体の特性としては、本来の粘着性を維持することは勿
論、気泡の混入によって原料の削減、多孔質面や粗大面
に対する接着性の向上及びシール性の向上等の利点があ
るが、特に、このような粘着剤の発泡体を用いると、弾
力性が著しく向上して人体皮膚の凹凸面にも追従して密
着し、しかも粘着性及び使用感が良好である上、剥離時
の苦痛が無く、又、温熱を与えたとき、粘着剤層が発泡
体であり、この発泡体が熱伝導を制御して低温火傷が生
じ難い等、貼付剤に適用することによって、極めて多く
の利点を発現するのである。Further, air, nitrogen gas, carbon dioxide gas, etc. are mixed in the hot-melt type polymer substance as a myriad of independent bubbles, and as a result, the volume of the hot-melt type polymer substance exceeds 1 times and several times. Although it is an expanded foam, the properties of this foam are not only to maintain the original adhesiveness, but also to reduce the raw materials due to the inclusion of bubbles, to improve the adhesiveness to porous surfaces and rough surfaces, and to improve the sealing property. However, especially when such a foam of an adhesive is used, the elasticity is remarkably improved and the unevenness of human skin is followed and adhered, and the adhesiveness and usability are improved. It is good and has no pain at the time of peeling, and when it is heated, the adhesive layer is a foam, and this foam controls heat conduction and is unlikely to cause low-temperature burns. To realize a great number of advantages A.

【００２１】つまり、この粘着剤の発泡体は、粘着力が
大であり、貼付剤の粘着剤層として使用した場合には、
外皮との追従性が良好で、外皮との密着性が一層増大す
るのである。その結果、外皮の凹凸面に対しても弾力的
に順応して粘着するので、粘着強度の低下は生じ難いの
である。That is, the foam of this adhesive has a large adhesive force, and when used as an adhesive layer of a patch,
The followability with the outer skin is good, and the adhesion with the outer skin is further increased. As a result, even the uneven surface of the outer skin is elastically adapted and adheres, so that the adhesive strength is less likely to decrease.

【００２２】又、ホットメルト型高分子物質の発泡倍率
を制御することによって、弾力性、凹凸面への追従性や
密着性、更に粘着性及び使用感、剥離時の苦痛、断熱性
や熱伝導性等を容易に制御できるのである。Further, by controlling the expansion ratio of the hot-melt type polymer substance, the elasticity, the conformability to the uneven surface and the adhesiveness, the tackiness and the feeling of use, the pain at the time of peeling, the heat insulating property and the heat conduction. The sex and the like can be easily controlled.

【００２３】本発明で用いられるホットメルト型高分子
物質としては、上記目的を達成できるものであれば特に
限定されるものではないが、具体的には、例えばＡ−Ｂ
−Ａ型ブロック共重合体、飽和ポリエステル系高分子物
質、ポリアミド系高分子物質、アクリル系高分子物質、
ウレタン系高分子物質、ポリオレフィン系高分子物質又
はポリオレフィン系共重合体或いはこれらの変性体が挙
げられる。この変性体とは、ホットメルト型高分子物質
の成分の一部を他の成分に置き換えてホットメルト型高
分子物質の性質、例えばホットメルト型高分子物質の粘
着性の改善や安定性等を変えたものをいう。The hot-melt type polymer substance used in the present invention is not particularly limited as long as it can achieve the above object, and specifically, for example, AB.
-A type block copolymer, saturated polyester polymer substance, polyamide polymer substance, acrylic polymer substance,
Examples thereof include urethane-based polymer substances, polyolefin-based polymer substances, polyolefin-based copolymers and modified products thereof. With this modified product, some of the components of the hot-melt polymer substance are replaced with other components to improve the properties of the hot-melt polymer substance, such as improvement of the tackiness and stability of the hot-melt polymer substance. I say something changed.

【００２４】上記Ａ−Ｂ−Ａ型ブロック共重合体におい
て、Ａブロックはスチレン、メチルスチレン等のモノビ
ニル置換芳香族化合物Ａで、非弾性重合体ブロックであ
り、Ｂブロックはブタジエン、イソプレン等の共役ジエ
ンの弾性重合体ブロックであり、具体的には、例えばス
チレン−ブタジエン−スチレンブロック共重合体、スチ
レン−イソプレン−スチレンブロック共重合体等が挙げ
られるのであり、また、これらを混合して用いても良い
のである。In the ABA type block copolymer, the A block is a monovinyl-substituted aromatic compound A such as styrene and methylstyrene, which is an inelastic polymer block, and the B block is a conjugate of butadiene and isoprene. It is an elastic polymer block of a diene, and specific examples thereof include styrene-butadiene-styrene block copolymer, styrene-isoprene-styrene block copolymer, and the like. Is also good.

【００２５】Ａ−Ｂ−Ａ型ブロック共重合体の市販品の
例としては、具体的にはカリフレックスＴＲ−１１０
１、カリフレックスＴＲ−１１０７、カリフレックスＴ
Ｒ−１１１１(シェル化学製)、或いはフィリップペトロ
リアム製のソルプレン４１８等が挙げられる。Specific examples of commercially available ABA type block copolymers include Califlex TR-110.
1, Califlex TR-1107, Califlex T
R-1111 (manufactured by Shell Chemical Co., Ltd.) or Sorprene 418 manufactured by Philippe Petroleum, etc. may be mentioned.

【００２６】本発明において、粘着剤がホットメルト型
高分子物質、脂環族系石油樹脂及び軟化剤で形成されて
いるものが有益であり、この粘着剤は、上述の方法で発
泡される。In the present invention, it is advantageous that the pressure-sensitive adhesive is formed of a hot-melt type polymer substance, an alicyclic petroleum resin and a softening agent, and the pressure-sensitive adhesive is foamed by the above-mentioned method.

【００２７】本発明において、ホットメルト型高分子物
質としては、上述のものが挙げられる。このホットメル
ト型高分子物質は、粘着剤中の主ポリマーであり、これ
を用いて形成した粘着剤の発泡体は、優れた保形性を有
し、しかも初期タックがあり、常温時や加温時の粘着性
が良好で、且つ粘着後における粘着力が安定しているの
である。In the present invention, examples of the hot melt type polymer substance include those mentioned above. This hot-melt type polymer substance is the main polymer in the pressure-sensitive adhesive, and the foam of the pressure-sensitive adhesive formed using this has excellent shape-retaining property and also has an initial tack, and it is used at room temperature or at a high temperature. The adhesiveness at the time of warming is good, and the adhesive force after adhesion is stable.

【００２８】又、本発明において、脂環族系石油樹脂
は、粘着性賦与剤であり、ホットメルト型高分子物質と
の組合せにより、所要の粘着特性が得られる。Further, in the present invention, the alicyclic petroleum resin is a tackifier, and by combining it with a hot-melt type polymer substance, required tackiness properties can be obtained.

【００２９】脂環族系石油樹脂とは、環状骨格を持った
石油系樹脂であり、具体的には、例えばロジン、脱水系
ロジン、脱水素ロジンのグリセリンエステル類、ガムロ
ジンのグリセリンエステル類、水添ロジン、水添ロジン
のメチルエステル類、水添ロジンのグリセリンエステル
類、水添ロジンのペンタエリトリットロジン類、重合ロ
ジン、重合ロジンのグリセリンエステル類、クマロンイ
ンデン樹脂、水添石油樹脂、無水マレイン酸変性ロジ
ン、ロジン誘導体類又はＣ₅系石油樹脂等が挙げられる
のであり、貼付剤に所要の粘着力を賦与するために、単
独或いは２種以上を組み合わせて適宜用いられる。The alicyclic petroleum resin is a petroleum resin having a cyclic skeleton, and specific examples thereof include rosin, dehydrated rosin, dehydrogenated rosin glycerin esters, gum rosin glycerin esters, and water. Hydrogenated rosin, hydrogenated rosin methyl ester, hydrogenated rosin glycerin ester, hydrogenated rosin pentaerythritol rosin, polymerized rosin, polymerized rosin glycerin ester, coumarone indene resin, hydrogenated petroleum resin, anhydrous Examples thereof include maleic acid-modified rosin, rosin derivatives, C ₅ petroleum resins, and the like, and may be used alone or in combination of two or more in order to impart a required adhesive force to the patch.

【００３０】その具体的な市販品の例としては、例えば
アルコンＰ−８５、アルコンＰ−１００、アルコンＰ−
１２５(荒川化学製)等、クイントン(日本ゼオン製)、エ
スコレッツ３０００(エクソン製)等が挙げられる。Specific examples of commercially available products include, for example, Alcon P-85, Alcon P-100, and Alcon P-.
Examples thereof include 125 (manufactured by Arakawa Chemical Co., Ltd.), Quinton (manufactured by Zeon Corporation), Escolettes 3000 (manufactured by Exxon) and the like.

【００３１】又、本発明で用いられる軟化剤はホットメ
ルト型高分子物質を溶解ないし分散させて軟化させるも
のであり、ホットメルト型高分子物質と脂環族系石油樹
脂の組み合わせによって、適度の保形性や柔軟性更に粘
着力を発現させるのである。この軟化剤としては高級脂
肪酸、液化ゴム、鉱油等が挙げられる。Further, the softening agent used in the present invention is to dissolve or disperse the hot-melt type polymer substance to soften it, and the softening agent is appropriately mixed depending on the combination of the hot-melt type polymer substance and the alicyclic petroleum resin. The shape retention, flexibility, and adhesiveness are developed. Examples of the softening agent include higher fatty acids, liquefied rubber, mineral oil and the like.

【００３２】この軟化剤としては、例えばヤシ油、ヒマ
シ油、オリーブ油、ツバキ油、アーモンド油、パーシッ
ク油、ラッカセイ油、ゴマ油、大豆油、ミンク油、綿実
油、トウモロコシ油、サフラワー油、オレイン酸、流動
パラフィン等が挙げられる。Examples of the softener include coconut oil, castor oil, olive oil, camellia oil, almond oil, persic oil, peanut oil, sesame oil, soybean oil, mink oil, cottonseed oil, corn oil, safflower oil, oleic acid, Liquid paraffin and the like can be mentioned.

【００３３】ところで、この粘着剤には、所望により、
他の成分、例えば他の粘着剤、粘着賦与剤、老化防止
剤、充填剤、粘着調整剤、粘着改良剤、着色剤、消泡
剤、増粘剤、改質剤、防カビ剤、抗菌剤、殺菌剤、消臭
剤又は脱臭剤等が適宜適量配合されても良いのである。By the way, if desired, this adhesive may be
Other components, such as other adhesives, tackifiers, antiaging agents, fillers, tackifiers, tackifiers, colorants, defoamers, thickeners, modifiers, fungicides, antibacterial agents A bactericide, a deodorant, a deodorant, or the like may be appropriately mixed in an appropriate amount.

【００３４】本発明においては、密着性、粘着性、使用
感及び皮膚からの剥離性等の観点から、粘着剤層がホッ
トメルト型高分子物質５〜４０重量部、脂環族系石油樹
脂５〜５５重量部及び軟化剤５〜５５重量部で形成され
たものを発泡させた発泡体、特に、粘着剤層がホットメ
ルト型高分子物質１０〜３０重量部、脂環族系石油樹脂
１０〜５０重量部及び軟化剤１５〜４５重量部で形成さ
れており、このものを発泡させた発泡体が、弾力性があ
って人体皮膚の凹凸面にも追従して密着し、しかも粘着
性及び使用感が良好である上、剥離時の苦痛が無く、
又、温熱を与えたとき、低温火傷が生じ難いので望まし
い。In the present invention, from the viewpoints of adhesion, tackiness, feeling of use, peelability from the skin, etc., the pressure-sensitive adhesive layer comprises 5 to 40 parts by weight of hot-melt type polymer substance, alicyclic petroleum resin 5 ˜55 parts by weight and a softening agent formed by 5 to 55 parts by weight, and a foamed product obtained by foaming the softening agent, in particular, an adhesive layer containing 10 to 30 parts by weight of a hot-melt type polymer substance, and an alicyclic petroleum resin 10 to 10. It is composed of 50 parts by weight and 15 to 45 parts by weight of a softening agent, and the foamed product is elastic and adheres closely to the uneven surface of human body skin, and is adhesive and usable. The feeling is good and there is no pain when peeling,
Further, when heat is applied, low temperature burns are less likely to occur, which is desirable.

【００３５】又、本発明の貼付剤においては、上述の粘
着剤に更に吸水性ポリマーが配合されたものを発泡させ
た発泡体、つまり用いられる粘着剤層がホットメルト型
高分子物質、脂環族系石油樹脂、軟化剤及び吸水性ポリ
マーで形成されたものを発泡させた発泡体が、この吸水
性ポリマーによって、皮膚からの汗や分泌物等の体液
を、吸収、吸着し、常に外皮表面を清潔に保つので衛生
面から望ましい。Further, in the patch of the present invention, a foamed product of the above-mentioned pressure-sensitive adhesive further mixed with a water-absorbing polymer, that is, the pressure-sensitive adhesive layer used is a hot-melt type polymer substance, an alicyclic ring. A foam made of a petroleum-based petroleum resin, a softening agent, and a water-absorbent polymer that has been foamed absorbs and adsorbs body fluids such as sweat and secretions from the skin by the water-absorbent polymer, and constantly coats the outer surface of the skin. It is desirable from a hygienic point of view to keep it clean.

【００３６】この粘着剤は、上述の粘着剤に更に吸水性
ポリマーが配合されたものであり、従って、用いられる
ホットメルト型高分子物質、脂環族系石油樹脂及び軟化
剤は上述の場合と同様であるので、重複説明を避けるた
めに省略する。This pressure-sensitive adhesive is a mixture of the above-mentioned pressure-sensitive adhesive with a water-absorbing polymer. Therefore, the hot-melt type polymer substance, alicyclic petroleum resin and softening agent used are the same as those described above. Since it is the same, it is omitted to avoid redundant description.

【００３７】この吸水性ポリマーとしては、自重の１０
倍以上、特に５０倍以上の水を吸収してゲル化するもの
であれば特に限定されるものではないが、特に、架橋結
合を導入して水に対する溶解性を制御した吸水性ポリマ
ーが望ましい。This water-absorbing polymer has a weight of 10
It is not particularly limited as long as it absorbs twice or more, especially 50 times or more of water and gels, but a water-absorbing polymer in which a cross-linking bond is introduced to control the solubility in water is particularly desirable.

【００３８】具体的には、特公昭４９−４３３９５号公
報に開示されている澱粉−ポリアクリロニトリル共重合
体、特公昭５１−３９６７２号公報に開示されている架
橋ポリアルキレンオキシド、特公昭５３−１３４９５号
公報に開示されているビニルエステル−エチレン系不飽
和カルボン酸共重合体ケン化物、特公昭５４−３０７１
０号公報に開示されている逆相懸濁重合法によって得ら
れる自己架橋ポリアクリル酸塩、特開昭５４−２００９
３号公報に開示されているポリビニルアルコール系重合
体と環状無水物との反応生成物、特開昭５９−８４３０
５号公報に開示されているポリアクリル酸塩架橋物、ポ
リアクリル酸ソーダ、ＣＭＣ、ポリビニルアルコール、
ポリビニルピロリドン、ポリビニルメチルエーテル、ア
ラビアゴム、ヒドロキシエチルセルロース、メチルセル
ロース、アルギン酸ソーダ、ペクチン、カルボキシビニ
ルポリマー、ゼラチン、ポリエチレンオキサイド等から
選ばれた１種または２種以上の混合物が挙げられる。Specifically, the starch-polyacrylonitrile copolymer disclosed in JP-B-49-43395 and the crosslinked polyalkylene oxide disclosed in JP-B-51-39672, JP-B-53-13495. Saponified vinyl ester-ethylenically unsaturated carboxylic acid copolymer disclosed in Japanese Patent Publication No. 54-3071
Self-crosslinked polyacrylic acid salt obtained by the reverse phase suspension polymerization method disclosed in JP-A-54-2009.
No. 3, a reaction product of a polyvinyl alcohol-based polymer and a cyclic anhydride, disclosed in JP-A-59-8430.
5, polyacrylic acid salt cross-linked products, sodium polyacrylate, CMC, polyvinyl alcohol,
One or a mixture of two or more selected from polyvinylpyrrolidone, polyvinyl methyl ether, gum arabic, hydroxyethyl cellulose, methyl cellulose, sodium alginate, pectin, carboxyvinyl polymer, gelatin, polyethylene oxide and the like can be mentioned.

【００３９】この吸水性ポリマーの市販品の例として
は、例えば三洋化成社製のサンウェットＩＭ−３００、
サンウェットＩＭ−３００ＭＰＳ、サンウェットＩＭ−
１０００又はサンウェットＩＭ−１０００ＭＰＳ等の
他、製鉄化学社製のアクアキープ４Ｓやアクアキープ４
ＳＨ等が挙げられるのであり、又、住友化学社製のスミ
カゲルＮＰ−１０２０、スミカゲルＮＰ−１０４０、ス
ミカゲルＳＰ−５２０及びスミカゲルＮ−１０４０等が
挙げられるのであり、更に、クラレ社製のＫＩゲル２０
１−ＫやＫＩゲルー２０１Ｋ−Ｆ２等が挙げられるので
あり、又、荒川化学社製のアラソープ８００やアラソー
プ８００Ｆ等が挙げられるのであり、これらのうち、吸
水性が高く、しかも加温しても粘着剤層のダレがなく、
粘着剤層の保形性が良好である等の理由より、三洋化成
社製のサンウェットＩＭ−３００ＭＰＳやサンウェット
ＩＭ−１０００ＭＰＳ、住友化学社製のスミカゲルＮＰ
−１０２０やスミカゲルＮＰ−１０４０、クラレ社製の
ＫＩゲル−２０１Ｋ−Ｆ２、荒川化学社製のアラソープ
８００Ｆ等が特に好ましい。Examples of commercial products of this water-absorbing polymer include, for example, Sanwet IM-300 manufactured by Sanyo Kasei Co.,
Sunwet IM-300MPS, Sunwet IM-
1000 or Sunwet IM-1000MPS, etc., as well as AquaKeep 4S and AquaKeep 4 manufactured by Steel Manufacturing Chemical Co., Ltd.
SH and the like, and Sumitomo Chemical Co., Ltd. Sumikagel NP-1020, Sumikagel NP-1040, Sumikagel SP-520 and Sumikagel N-1040, and the like, further, Kuraray Co., Ltd. KI gel 20.
Examples include 1-K and KI gel-201K-F2, and Arakawa 800 and Arasoap 800F manufactured by Arakawa Chemical Co., Ltd. Of these, water absorption is high and even when heated. There is no sagging of the adhesive layer,
Due to the good shape retention of the pressure-sensitive adhesive layer, for example, Sanyo Kasei's Sunwet IM-300MPS and Sunwet IM-1000MPS, Sumitomo Chemical's Sumikagel NP
-1020, Sumika gel NP-1040, KI gel-201K-F2 manufactured by Kuraray Co., Ltd., and Arasoap 800F manufactured by Arakawa Chemical Co., Ltd. are particularly preferable.

【００４０】本発明においては、密着性、粘着性、皮膚
からの汗や分泌物等の体液の吸収・吸着性、使用感及び
皮膚からの剥離性等の観点から、粘着剤層がホットメル
ト型高分子物質５〜４０重量部、脂環族系石油樹脂５〜
５５重量部、軟化剤５〜５５重量部及び吸水性ポリマー
０．５〜１０重量部で形成されたものを発泡させた発泡
体、特に、粘着剤層がホットメルト型高分子物質１０〜
３０重量部、脂環族系石油樹脂１０〜５０重量部、軟化
剤１５〜４５重量部及び吸水性ポリマー１〜８重量部で
形成されており、このものを発泡させた発泡体が、弾力
性があって人体皮膚の凹凸面にも追従して密着し、しか
も粘着性及び使用感が良好である上、剥離時の苦痛が無
く、加えて、吸水性ポリマーによって、皮膚からの汗や
分泌物等の体液を、吸収、吸着し、常に外皮表面を清潔
に保つので衛生面から望ましい。In the present invention, from the viewpoints of adhesion, adhesiveness, absorption / adsorption of body fluids such as sweat and secretions from the skin, feeling of use and releasability from the skin, the adhesive layer is a hot melt type. 5 to 40 parts by weight of polymer substance, 5 to alicyclic petroleum resin
55 parts by weight, 5 to 55 parts by weight of a softening agent and 0.5 to 10 parts by weight of a water-absorbing polymer are foamed, in particular, a pressure-sensitive adhesive layer is a hot-melt polymer substance 10 to 10 parts by weight.
30 parts by weight, 10 to 50 parts by weight of an alicyclic petroleum resin, 15 to 45 parts by weight of a softening agent and 1 to 8 parts by weight of a water-absorbing polymer are used. It adheres to the uneven surface of human skin and adheres well, and it has good adhesiveness and usability, and there is no pain during peeling. In addition, due to the water-absorbing polymer, sweat and secretions from the skin It is desirable from the viewpoint of hygiene because it absorbs and adsorbs body fluids such as the above and always keeps the outer skin surface clean.

【００４１】この場合、吸水性ポリマーが、粘着(剤)層
と親和性が悪く、均一に分散しない恐れが有るときに
は、界面活性剤で処理するのが望ましい。In this case, when the water-absorbent polymer has poor affinity with the adhesive (agent) layer and there is a risk that it will not be dispersed uniformly, it is desirable to treat with a surfactant.

【００４２】本発明で用いられる界面活性剤としては吸
水性ポリマーを処理することによって当該吸水性ポリマ
ーが粘着剤の粘着層中に分散し易くなるものであれば特
に限定されるものではなく、具体的には、陰イオン界面
活性剤、陽イオン界面活性剤、非イオン界面活性剤又は
両性界面活性剤が挙げられる。The surfactant used in the present invention is not particularly limited as long as the water-absorbent polymer can be easily dispersed in the pressure-sensitive adhesive layer by treating the water-absorbent polymer. Specific examples include anionic surfactants, cationic surfactants, nonionic surfactants or amphoteric surfactants.

【００４３】本発明で好適に用いられる界面活性剤とし
ては、例えばドデシル硫酸ナトリウム、ドデシルベンゼ
ンスルホン酸ナトリウム、カプロン酸ナトリウム、カプ
リル酸ナトリウム、アルキルナフタリンスルホン酸ナト
リウム、ラウリン酸ナトリウム、オレイン酸ナトリウ
ム、或いは、リン酸エステル塩型の界面活性剤、高級ア
ルコールリン酸モノエステルジナトリウム塩、高級アル
コールリン酸ジエステルナトリウム塩等の界面活性剤、
オレイン酸、リノール酸、リノレイン酸、ラウリン酸、
パルミチン酸、ミリスチン酸、ステアリン酸等の脂肪酸
やその金属塩、低重合度ポリカルボン酸の塩、例えば低
重合度ポリアクリル酸ソーダ、低重合度ポリアクリル酸
ブチル、低重合度ポリメタアクリル酸ソーダ、更に、ス
ルホン化ポリスチレン等の界面活性剤等が挙げられる。As the surfactant preferably used in the present invention, for example, sodium dodecyl sulfate, sodium dodecylbenzenesulfonate, sodium caproate, sodium caprylate, sodium alkylnaphthalenesulfonate, sodium laurate, sodium oleate, or , Phosphate ester type surfactants, higher alcohol phosphate monoester disodium salt, higher alcohol phosphate diester sodium salt and other surfactants,
Oleic acid, linoleic acid, linoleic acid, lauric acid,
Fatty acids such as palmitic acid, myristic acid, stearic acid and their metal salts, salts of low polymerization degree polycarboxylic acid, such as low polymerization degree polyacrylic acid sodium acrylate, low polymerization degree polybutyl acrylate, low polymerization degree polymethacrylic acid sodium salt Further, a surfactant such as sulfonated polystyrene may be used.

【００４４】又、この粘着剤には、所望により、他の成
分、例えば他の粘着剤、粘着賦与剤、老化防止剤、充填
剤、粘着調整剤、粘着改良剤、着色剤、消泡剤、増粘
剤、改質剤、防カビ剤、抗菌剤、殺菌剤、消臭剤又は脱
臭剤等が適宜適量配合されても良いのである。If desired, the adhesive may contain other components such as other adhesives, tackifiers, antiaging agents, fillers, tackifiers, tackifiers, coloring agents, defoamers, Thickeners, modifiers, antifungal agents, antibacterial agents, bactericides, deodorants, deodorants and the like may be added in appropriate amounts.

【００４５】本発明においては、粘着剤に経皮吸収性の
薬物を配合することにより、局所治療効果を向上させた
り、全身治療効果を向上させたり、温熱効果によって循
環が活発になった血液などに薬物を吸収させて一層効果
的に生体内の各部に薬物を循環させることができるの
で、各部位の投与効果を一層高める上ですこぶる好まし
い。In the present invention, by mixing a transdermal drug into the adhesive, the local therapeutic effect or systemic therapeutic effect is improved, or the blood whose circulation is activated by the thermal effect is activated. Since it is possible to absorb the drug into the body and circulate the drug to each part of the body more effectively, it is extremely preferable in order to further enhance the administration effect of each part.

【００４６】本発明で用いられる薬物としては、経皮吸
収性のものであれば特に限定されるものではないが、具
体的には、例えば皮膚刺激剤、鎮痛消炎剤、中枢神経作
用剤（睡眠鎮静剤、抗てんかん剤、精神神経用剤）、利
尿剤、血圧降下剤、冠血管拡張剤、鎮咳去痰剤、抗ヒス
タミン剤、不整脈用剤、強心剤、副腎皮質ホルモン剤、
局所麻酔剤等が挙げられる。これら薬効成分は、一種又
は必要に応じて二種以上配合されて用いられる。The drug used in the present invention is not particularly limited as long as it is transdermally absorbable, and specifically, for example, a skin stimulant, an analgesic / anti-inflammatory agent, a central nervous system acting agent (sleeping agent). Sedative, antiepileptic agent, neuropsychiatric drug), diuretic, antihypertensive, coronary vasodilator, antitussive expectorant, antihistamine, arrhythmic agent, cardiotonic agent, corticosteroid,
Examples include local anesthetics. These medicinal components are used alone or in admixture of two or more if necessary.

【００４７】この薬物の含有量としては薬効を期待でき
る範囲であれば特に限定されるものではないが、薬理効
果や経済性更に粘着力等の観点より、経皮吸収性の薬物
の含有量が粘着剤１００重量部に対し０．０１〜２５重
量部、特に０．５〜１５重量部の範囲で適宜決定され
る。The content of this drug is not particularly limited as long as the drug effect can be expected, but from the viewpoint of pharmacological effect, economical efficiency, adhesive strength, etc., the content of the transdermal drug is It is appropriately determined in the range of 0.01 to 25 parts by weight, particularly 0.5 to 15 parts by weight, relative to 100 parts by weight of the adhesive.

【００４８】本発明においては、粘着剤が架橋されてい
るものが、以下に述べる理由より、至極有益である。In the present invention, the one in which the pressure-sensitive adhesive is crosslinked is extremely useful for the reasons described below.

【００４９】即ち、粘着剤が架橋されていると、熱安定
性が向上し、加温時のダレやべたつき更に糊残りが極め
て少なくなって使用感が良好になり、しかも加温時の粘
着力や保形性も良好になり、更に薬物の保持性が向上す
る。That is, when the pressure-sensitive adhesive is cross-linked, the thermal stability is improved, the sag and stickiness during heating and the adhesive residue are extremely reduced, and the usability is improved, and the adhesive strength during heating is improved. Also, the shape retention is improved, and the drug retention is further improved.

【００５０】この粘着剤の架橋方法としては特に限定さ
れるものではないが、具体的には、例えば紫外線や電子
線等の照射線を、得られた粘着剤の発泡体に直接照射し
たり、支持体又はライナーの上で直接、照射線架橋を行
ったり、あらかじめ別の装置で照射線架橋を行い、転移
により粘着剤の発泡体を支持体上に転着しても良いので
ある。The method of crosslinking the pressure-sensitive adhesive is not particularly limited, but specifically, for example, the obtained foam of the pressure-sensitive adhesive is directly irradiated with irradiation rays such as ultraviolet rays and electron beams, Irradiation cross-linking may be carried out directly on the support or liner, or irradiation-cross-linking may be carried out in advance by another device, and the foam of the pressure-sensitive adhesive may be transferred onto the support by transfer.

【００５１】照射線架橋としては、例えば特公昭６２−
３９１８４号公報に準じて行うことができる。そして、
例えば、紫外線の場合、通常３００〜６８０nmで５〜３
０分間照射、電子線の場合、通常１〜２０Ｍradで、照
射時間０．０１〜５秒である。勿論、粘着剤に種々の化
学的架橋剤を加え、化学的に架橋しても良いのである。Examples of radiation cross-linking include Japanese Patent Publication No. 62-
It can be performed according to Japanese Patent No. 39184. And
For example, in the case of ultraviolet rays, it is usually 5 to 3 at 300 to 680 nm.
In the case of irradiation for 0 minutes and electron beam, the irradiation time is usually 1 to 20 Mrad and the irradiation time is 0.01 to 5 seconds. Of course, various chemical cross-linking agents may be added to the pressure-sensitive adhesive to chemically cross-link it.

【００５２】ところで、本発明においては、粘着剤を上
述の方法で架橋し、次いで、これを発泡させたものを支
持体又はライナーの上に形成しても良いのである。By the way, in the present invention, the pressure-sensitive adhesive may be crosslinked by the above-mentioned method, and then the foamed product may be formed on the support or liner.

【００５３】本発明においては、粘着剤がホットメルト
型高分子物質とアクリル系粘着剤の混合物からなるもの
が、これらの混合比を変更することによって、種々の粘
着力や発泡状態の異なる粘着剤が得られるので望まし
い。In the present invention, the pressure-sensitive adhesive is composed of a mixture of a hot-melt type polymer substance and an acrylic pressure-sensitive adhesive. By changing the mixing ratio of these, pressure-sensitive adhesives having various adhesive strengths and foaming states can be obtained. It is desirable because

【００５４】この場合、ホットメルト型高分子物質とア
クリル系粘着剤の混合比は、ホットメルト型高分子物質
７０〜９９重量％とアクリル系粘着剤１〜３０重量％の
範囲から、貼付剤の用途や形態、つまり後述する発熱体
を具備するものか否か等によって、任意に決定される。In this case, the mixing ratio of the hot-melt type polymeric substance and the acrylic pressure-sensitive adhesive is in the range of 70 to 99% by weight of the hot-melt type polymeric substance and 1 to 30% by weight of the acrylic pressure-sensitive adhesive. It is arbitrarily determined depending on the use and form, that is, whether or not it has a heating element described later.

【００５５】本発明において、上述の貼付剤には発熱体
を積層し、この発熱体で温熱効果を発現させるように構
成したものが有益である。In the present invention, it is advantageous that the above-mentioned patch is constructed by laminating a heating element and exhibiting a heating effect by this heating element.

【００５６】この発熱体としては外皮に適用されて温熱
効果を発現するものであれば特に限定されるものではな
いが、具体的には、例えば化学的な反応熱を利用するも
の、抵抗体に電力を供給して発生するジュール熱を利用
するもの、等が挙げられる。The heating element is not particularly limited as long as it is applied to the outer skin and exerts a heating effect. Specifically, for example, a heating element using chemical reaction heat or a resistor is used. Examples include those that use Joule heat generated by supplying electric power.

【００５７】発熱体において、化学的な反応熱を利用す
るものとしては空気の存在下で発熱する、いわゆる発熱
カイロ等が挙げられる。この発熱体組成物としては、例
えば特公昭６０−１２３８１号公報、特公昭６１−８１
１６号公報及び特公昭６３−２４０３０号公報等、種々
のものが提案されているが、特に、その組成としては鉄
粉系、反応助剤、水及び保水剤から構成されるもので、
空気の存在下で発熱する物質が好ましい。具体的には還
元鉄粉、活性炭、保水剤、塩化ナトリウムや塩化カリウ
ム等の塩化物等の発熱体組成物を適宜配合したものであ
る。Examples of the heating element that utilizes the heat of chemical reaction include a so-called heating warmer that generates heat in the presence of air. Examples of the heating element composition include Japanese Patent Publication No. 60-12381 and Japanese Patent Publication No. 61-81.
No. 16 and Japanese Patent Publication No. 63-24030 have been proposed, but in particular, the composition is composed of iron powder, a reaction aid, water and a water retention agent,
Substances that exotherm in the presence of air are preferred. Specifically, a reduced iron powder, activated carbon, a water retention agent, and a heating element composition such as chloride such as sodium chloride or potassium chloride are appropriately mixed.

【００５８】この場合、発熱体の温度条件としては低温
火傷を発生しない範囲に制御することが重要であり、こ
の観点から、粘着剤層(発泡体)の表面温度が３８〜４３
℃に制御するのが好ましい。In this case, it is important to control the temperature condition of the heating element within a range that does not cause low-temperature burn. From this viewpoint, the surface temperature of the pressure-sensitive adhesive layer (foam) is 38 to 43.
It is preferable to control the temperature to ° C.

【００５９】ところで、遠赤外線効果を発現させるうえ
で、発熱体組成物中に遠赤外線照射用のセラミックスの
含有や、発熱体と粘着剤層(発泡体)の間に遠赤外線照射
用セラミックス層を設けてもよいのである。By the way, in order to exert the far infrared ray effect, the ceramics for far infrared ray irradiation are contained in the heating element composition, or the ceramic layer for far infrared ray irradiation is provided between the heating element and the adhesive layer (foam). It may be provided.

【００６０】このようにして得られた温熱型の貼付剤
は、冬期において、単に、人体に温熱を供給して快適に
過ごすことができるだけでなく、局所のこり、疼痛及び
冷え等を伴う症状、例えば肩こり、筋肉痛、筋肉のこ
り、腰痛、手足の冷え、神経痛、リューマチ、打ち身、
捻挫等の疾患に使用され、温熱による治療効果を充分に
期待できるのである。The heat-type patch obtained in this manner can not only simply supply heat to the human body and spend a comfortable time in the winter season, but also cause symptoms such as local stiffness, pain and chill, for example, Stiff neck, muscle aches, stiff muscles, back pain, cold limbs, neuralgia, rheumatism, bruises,
It is used for diseases such as sprains, and the therapeutic effect of heat can be expected sufficiently.

【００６１】本発明で用いられる発熱体としては特に限
定されるものではないが、特に、以下に述べる発熱体
が、低温火傷の発生がなく安全であり、又、優れた温熱
効果を比較的長時間にわたって提供できるうえ、使用中
に異臭がなく、しかも発熱体組成物の偏りがないので使
用感が優れる結果、至極有益である。The heating element used in the present invention is not particularly limited, but in particular, the heating element described below is safe without the occurrence of low-temperature burns and has an excellent heating effect for a relatively long time. It can be provided over a period of time, has no offensive odor during use, and has no bias in the composition of the heating element.

【００６２】即ち、本発明で好適に用いられる発熱体と
しては、少なくとも片面通気性フィルムで構成された開
放部のない偏平状袋体の内部に、鉄粉４０〜７５重量
％、活性炭１〜１０重量％、塩化ナトリウム等の塩化物
１〜１０重量％、水１０〜４０重量％及び保水剤１〜４
０重量％からなる発熱体組成物を封入してなり、且つ上
記通気性フィルムの透湿量がＡＳＴＭ法（Ｅ−９６−８
０Ｄ法）で５０〜８００ｇ／ｍ²・２４ｈｒのものであ
る。That is, as a heating element preferably used in the present invention, 40 to 75% by weight of iron powder and 1 to 10% of activated carbon are contained in a flat bag body having at least one open-air permeable film and having no open portion. % By weight, chloride such as sodium chloride 1 to 10% by weight, water 10 to 40% by weight and water retention agent 1 to 4
A heating element composition consisting of 0% by weight is enclosed, and the breathable film has a moisture permeability of ASTM method (E-96-8).
OD method) of 50 to 800 g / m ² · 24 hr.

【００６３】この場合において、発熱体からの温熱を一
層厳格に制御して、一層安全で、しかも一層優れた温熱
効果を確保するために、特に、通気性フィルムの透湿量
がＡＳＴＭ法（Ｅ−９６−８０Ｄ法）で５０〜８００ｇ
／ｍ²・２４ｈｒのものが望ましい。In this case, in order to more strictly control the heat from the heating element to ensure a safer and more excellent heat effect, the moisture permeability of the breathable film is particularly determined by the ASTM method (E -96-80D method) 50-800 g
/ M ² · 24 hr is desirable.

【００６４】このように、透湿度で通気性フィルムを管
理するのは、温度が安定するだけでなく、発熱時間もほ
ぼ一定化するからである。Thus, the reason why the breathable film is controlled by the moisture permeability is that not only the temperature becomes stable but also the heat generation time becomes almost constant.

【００６５】即ち、このように、温度範囲を３８〜４３
℃という微妙な範囲に設定するには、発熱体組成物の組
成と、フィルムを通気度で管理するのではなく、透湿度
で管理する必要があり、しかも通気性フィルムの透湿度
をＡＳＴＭ法(Ｅ−９６−８０Ｄ法)で５０〜８００g／m
²・２４hrとすることにより、空気(酸素)と発熱体組成
物との酸化反応による発熱と、水の蒸散等による放熱の
バランスによって温度が制御されるのである。That is, in this way, the temperature range is 38 to 43.
In order to set in a delicate range of ℃, it is necessary to control not the composition of the heating element composition and the air permeability of the film but the moisture permeability, and the moisture permeability of the breathable film is controlled by the ASTM method ( E-96-80D method) 50-800 g / m
By setting the time to ² · 24 hours, the temperature is controlled by the balance between the heat generation due to the oxidation reaction of air (oxygen) and the heat generating composition and the heat radiation due to evaporation of water.

【００６６】又、透湿度を上記範囲にコントロールする
ことにより、空気(酸素)と発熱体組成物との酸化反応に
よって酸素が消費され(減圧状態)、一方、発熱によって
蒸気圧が上昇するが、この両方の相殺によっても偏平状
袋体内は減圧状態になり(蒸気圧の上昇より空気中の酸
素の消費による体積の減少の方が大)、このため発熱体
組成物は偏平状袋体によって押圧されるので発熱体組成
物が固定され、偏りがなく、従って、温熱型の貼付剤の
形状が一定で、しかも貼付剤全面の温度が均一になるの
で、優れた温熱型の貼付剤が得られるのである。By controlling the water vapor transmission rate within the above range, oxygen is consumed by the oxidation reaction between air (oxygen) and the heating element composition (reduced pressure state), while the vapor pressure rises due to heat generation. Due to both of these cancellations, the flat bag body is in a reduced pressure state (the volume decrease due to the consumption of oxygen in the air is larger than the vapor pressure increase), so that the heating element composition is pressed by the flat bag body. Since the heating element composition is fixed and there is no bias, the shape of the heat-sensitive adhesive patch is constant and the temperature of the entire surface of the adhesive patch is uniform, so that an excellent heat-sensitive adhesive patch can be obtained. Of.

【００６７】事実、このように水蒸気透過性を制御した
通気性フィルムを用いると、使用中の温度変化が小さ
く、しかもロット間のバラツキが極めて小さく安定した
温度特性が再現性良く得られる。In fact, when the breathable film having the controlled water vapor permeability is used, the temperature change during use is small, the variation between lots is extremely small, and stable temperature characteristics can be obtained with good reproducibility.

【００６８】本発明に用いられる偏平状袋体は片面が通
気性フィルムで構成された開放部のないものであって、
該通気性フィルムの透湿量がＡＳＴＭ法(Ｅ−９６−８
０Ｄ法)で５０〜８００g／m²・２４hrの範囲のものであ
る。The flat bag used in the present invention has an open portion, one side of which is made of a breathable film,
The moisture permeability of the breathable film is determined by the ASTM method (E-96-8
OD method) in the range of 50 to 800 g / m ² · 24 hr.

【００６９】又、上記偏平状袋体においてその他面は上
記の通気性フィルムと同様のものを用いて形成してもよ
く、或いは他のフィルムやシートを用いて形成してもよ
いのであり、通気性や透湿性の有無は問わない。The other surface of the flat bag may be made of the same material as the breathable film, or may be made of another film or sheet. It does not matter whether it has moisture permeability or moisture permeability.

【００７０】上記偏平状袋体を形成する高分子材料とし
ては、例えばポリエチレン、ポリプロピレン、ナイロ
ン、ポリエステル、ポリ塩化ビニル、ポリ塩化ビニリデ
ン、ポリウレタン、ポリスチレン、エチレン−酢酸ビニ
ル共重合体ケン化物、エチレン−酢酸ビニル共重合体、
天然ゴム、再生ゴム、合成ゴム等が挙げられる。As the polymer material forming the flat bag, for example, polyethylene, polypropylene, nylon, polyester, polyvinyl chloride, polyvinylidene chloride, polyurethane, polystyrene, saponified ethylene-vinyl acetate copolymer, ethylene- Vinyl acetate copolymer,
Examples include natural rubber, recycled rubber, synthetic rubber and the like.

【００７１】又、上記偏平状袋体は、目的に応じて２層
以上の樹脂層で形成されたものでもよいが、その素材の
選択に当たり、ヒートシール性があり、簡単に熱融着で
きるものを選ぶのが好ましい。この場合、２層以上の樹
脂層が熱融着できないときには、その間にホットメルト
系の接着フィルムを介在させてこれらの樹脂層を接合し
てもよいが、このように構成することにより、片面の通
気性フィルムの透湿性が失われないように注意すること
を要する。The flat bag may be formed of two or more resin layers according to the purpose, but it has heat sealability and can be easily heat-sealed when selecting the material. Is preferred. In this case, when two or more resin layers cannot be heat-sealed, a hot-melt adhesive film may be interposed therebetween to bond these resin layers. Care must be taken not to lose the breathability of the breathable film.

【００７２】ところで、上記偏平状袋体を補強するため
に織布もしくは不織布からなる通気性補強用フィルムを
用いるのが好ましいが、かかる通気性補強用フィルム
は、例えば、ナイロン、ビニロン、ポリエステル、レー
ヨン、アセテート、アクリル、ポリエチレン、ポリプロ
ピレン、ポリ塩化ビニル等の人工繊維、綿、麻、絹等の
天然繊維から選ばれる１種または２種以上の素材を用い
て形成される。In order to reinforce the flat bag body, it is preferable to use a breathable reinforcing film made of woven or non-woven fabric. Examples of such breathable reinforcing film include nylon, vinylon, polyester and rayon. , One or more materials selected from artificial fibers such as acetate, acryl, polyethylene, polypropylene, polyvinyl chloride, and natural fibers such as cotton, hemp, and silk.

【００７３】上記ＡＳＴＭ法(Ｅ−９６−８０Ｄ法)とは
以下に述べる方法である。即ち、カップ内径(直径)６．
１８cm、高さ１．５cmの容器内に純水２０mlを入れ、該
容器の上面を通気性フィルムで閉蓋してロウで固定し、
これを恒温(３２．２℃)、恒湿(５０％)の中に２４時間
放置する。次いで、この容器内の水の減少量を測定し、
放出(蒸散)した水の量を[g／m²・２４hr]に換算して表
示する。The above-mentioned ASTM method (E-96-80D method) is the method described below. That is, the cup inner diameter (diameter) 6.
20 ml of pure water was placed in a container of 18 cm and height of 1.5 cm, the upper surface of the container was covered with a breathable film and fixed with wax,
This is left for 24 hours in a constant temperature (32.2 ° C.) and a constant humidity (50%). Then, measure the amount of water loss in this container,
The amount of water released (transpiration) is converted into [g / m ² · 24 hr] and displayed.

【００７４】通気性フィルムの透湿量が、５０g／m²・
２４hr未満であると発熱量が少な過ぎて温湿布効果が乏
しくなるので好ましくなく、一方、８００g／m²・２４h
rを超えると温度が上昇して最高温度が５０℃を超える
場合があり、このため、低温火傷の危険性があるのでこ
の場合も好ましくなく、従って、通気性フィルムの透湿
量が、好ましくは７５〜７００ｇ／ｍ²・２４ｈｒ、特
に、１００〜４５０ｇ／ｍ²・２４ｈｒの範囲のものが
最も望ましい。The moisture permeability of the breathable film is 50 g / m ² ·
If it is less than 24 hours, the calorific value is too small and the hot compress effect becomes poor, which is not preferable. On the other hand, 800 g / m ² · 24 h
If it exceeds r, the temperature may rise and the maximum temperature may exceed 50 ° C., which is not preferable because there is a risk of low-temperature burns. Therefore, the moisture permeability of the breathable film is preferably The range of 75 to 700 g / m ² · 24 hr, particularly 100 to 450 g / m ² · 24 hr is most desirable.

【００７５】又、本発明に用いられる発熱体組成物は、
空気の存在下で発熱反応を起こすものが用いられるが、
この発熱体組成物としては、例えば、鉄粉と、該鉄粉の
酸化反応を起こさせたり、pＨの調整及び触媒作用を有
する活性炭、鉄粉表面の酸化皮膜を破壊し、鉄粉の酸化
反応を円滑に進行させるための塩化ナトリウム、更に
水、及び該水によるベトツキをなくするために用いられ
る保水剤からなる。The heating element composition used in the present invention is
The one that causes an exothermic reaction in the presence of air is used,
Examples of the heating element composition include iron powder, an oxidation reaction of the iron powder, activated carbon having pH adjustment and a catalytic action, and destruction of an oxide film on the surface of the iron powder, and an oxidation reaction of the iron powder. It further comprises sodium chloride for smoothly advancing water, water, and a water retention agent used for eliminating stickiness due to the water.

【００７６】上記発熱体組成物はその成分比率が鉄４０
〜７５重量％、活性炭１〜１０重量％、塩化ナトリウム
等の塩化物１〜１０重量％、水１０〜４０重量％、保水
剤１〜４０重量％からなるものであり、この範囲以外で
は、低温やけどを生じることがなく安全で、しかも長時
間にわたって優れた温湿布効果を発現する貼付剤を得ら
れないのである。The composition ratio of the heating element composition is 40% iron.
.About.75% by weight, activated carbon 1 to 10% by weight, chlorides such as sodium chloride 1 to 10% by weight, water 10 to 40% by weight, and water retention agent 1 to 40% by weight. It is not possible to obtain a patch that is safe without burns and that has an excellent warm compress effect over a long period of time.

【００７７】この場合、上記発熱体組成物は上記偏平状
袋体に均一に封入されるが、その充填量は２００〜５０
００g／m²の範囲とするのが望ましく、その充填量が、
２００g／m²未満であると発熱体組成物の充填量が少な
過ぎて所望の温度を長時間に亘って維持できず優れた温
熱効果が得られないのであり、一方、５０００g／m²を
超えると発熱体組成物の充填量が過剰になって袋詰めが
困難になったり、貼付剤が厚くなり過ぎて使用感や携帯
性が悪くなるうえ、不経済であるから好ましくない。In this case, the heating element composition is uniformly enclosed in the flat bag, and the filling amount is 200 to 50.
It is desirable that the range is 00 g / m ² , and the filling amount is
If it is less than 200 g / m ² , the filling amount of the heating element composition is too small to maintain a desired temperature for a long time and an excellent heating effect cannot be obtained. On the other hand, it exceeds 5000 g / m ² . When the filling amount of the heating element composition becomes excessive, bagging becomes difficult, and the patch becomes too thick, resulting in poor usability and portability and is uneconomical.

【００７８】ところで、上記発熱体組成物中の各成分は
製法、用途によって種々のものがあるが、使捨てカイロ
に用いられるものであれば、種類、形状、純度を問わ
ず、使用が可能である。By the way, each component in the above-mentioned heating element composition has various kinds depending on the production method and application, but if it is used in a disposable body warmer, it can be used regardless of type, shape and purity. is there.

【００７９】又、上記保水剤としては、保水性が高く、
発熱体組成物においてそのベトツキを無くするものであ
れば特に限定されるものではないが、具体的には、例え
ばバーミキュライト、シリカ粉、木粉、吸水性ポリマー
のうち少なくとも一種が挙げられる。The water retention agent has a high water retention property,
The heating element composition is not particularly limited as long as it eliminates stickiness, and specific examples thereof include at least one of vermiculite, silica powder, wood powder, and water-absorbing polymer.

【００８０】次に、本発明の貼付剤の製造方法について
説明する。又、この粘着剤の発泡方法としては、ホット
メルト型高分子物質、脂環族系石油樹脂及び軟化剤など
を所定の割合で混合機に投入し、例えば窒素気流中で６
０〜２５０℃の温度で充分に撹拌して均一な液状混合物
とし、この液状混合物を化学的発泡或いは物理的発泡に
よって粘着剤の発泡体を得る。Next, the method for producing the patch of the present invention will be described. As a method of foaming the pressure-sensitive adhesive, a hot-melt type polymer substance, an alicyclic petroleum resin, a softening agent, etc. are charged into a mixer at a predetermined ratio and, for example, 6
The mixture is thoroughly stirred at a temperature of 0 to 250 ° C. to form a uniform liquid mixture, and the liquid mixture is chemically or physically foamed to obtain a foam of an adhesive.

【００８１】この場合、独立気泡、連続気泡又は独立気
泡と連続気泡が混在したものなど、いずれのものでも良
いが、この発泡体は、外皮に適用されるものであるの
で、常温で粘着性を有するものであることを要する。In this case, any of closed cells, open cells, or a mixture of closed cells and open cells may be used, but since this foam is applied to the outer skin, it does not have adhesiveness at room temperature. It is necessary to have it.

【００８２】ところで、化学的発泡とは、粘着剤に無機
系発泡剤又は有機系発泡剤或いはこれらの混合物を混入
し、その分解反応の際に発生する窒素ガスや炭酸ガス等
を利用するものであり、物理的発泡とは、粘着剤である
液状混合物に、例えば加熱加圧下で空気、炭酸ガス又は
窒素ガスを混入し、次いで、大気圧下で発泡させるもの
である。By the way, the chemical foaming is a method in which an inorganic foaming agent, an organic foaming agent or a mixture thereof is mixed in an adhesive and nitrogen gas or carbon dioxide gas generated during the decomposition reaction is used. The physical foaming is to mix air, carbon dioxide gas or nitrogen gas into a liquid mixture which is an adhesive, for example, under heating and pressurization, and then foam the mixture under atmospheric pressure.

【００８３】これらのうち、特に、以下に述べる物理的
発泡させたものが望ましい。即ち、まず、ホットメルト
型高分子物質、脂環族系石油樹脂、軟化剤、粘着付与剤
及び充填剤等を所定の割合で混合機に投入し、窒素気流
中で６０〜２５０℃の温度で充分に撹拌して均一な液状
混合物とする。Of these, those physically foamed as described below are particularly desirable. That is, first, a hot-melt polymer substance, an alicyclic petroleum resin, a softening agent, a tackifier, a filler and the like are charged into a mixer at a predetermined ratio, and the mixture is heated in a nitrogen stream at a temperature of 60 to 250 ° C. Stir well to form a homogeneous liquid mixture.

【００８４】この場合、所望により、経皮吸収性の薬物
を所定の割合で配合しても良いのである。In this case, a transdermal drug may be blended in a predetermined ratio, if desired.

【００８５】次に、この液状混合物に、窒素ガス等の気
体を、例えば１５〜２００Ｋｇ／ｃｍ²、好ましくは２
０〜１００Ｋｇ／ｃｍ²の加圧下で機械的に加熱混入し
て分散した後、スプレーガン(スプレーエアー圧０．５
〜１０Ｋｇ／ｃｍ²、特に、１〜５Ｋｇ／ｃｍ²)で、支
持体或いはライナーの上に、吐出させ大気圧で発泡させ
て粘着剤の発泡体を得るのである。Next, a gas such as nitrogen gas is added to this liquid mixture, for example, 15 to 200 Kg / cm ² , preferably 2
After mechanically heating and mixing under pressure of 0 to 100 Kg / cm ² to disperse, spray gun (spray air pressure 0.5
10 to 10 kg / cm ² , particularly 1 to 5 kg / cm ² ) is discharged onto a support or a liner and foamed at atmospheric pressure to obtain a foamed adhesive.

【００８６】又、ホットメルト型高分子物質、脂環族系
石油樹脂、軟化剤、粘着付与剤及び充填剤、更に、所望
により、経皮吸収性の薬物等を所定の割合で混合機に投
入し、窒素気流中で６０〜２５０℃の温度で充分に撹拌
して均一な液状混合物とし、この液状混合物と窒素ガス
等の気体をノズルの中で混合し、これを、ガンで支持体
或いはライナーの上に、吐出させ大気圧で発泡させて粘
着剤の発泡体を得るものである。Further, a hot-melt type polymer substance, an alicyclic petroleum resin, a softening agent, a tackifier and a filler, and, if desired, a percutaneously absorbable drug and the like are put in a mixer at a predetermined ratio. Then, the mixture is thoroughly stirred in a nitrogen stream at a temperature of 60 to 250 ° C. to form a uniform liquid mixture, and this liquid mixture and a gas such as nitrogen gas are mixed in a nozzle, and this is mixed by a gun with a support or liner. Then, it is discharged and foamed at atmospheric pressure to obtain a foam of the adhesive.

【００８７】更に、上述の方法で液状混合物を、一旦剥
離処理の施された紙、フィルム等に展延し、その後、支
持体に圧着転写して貼付剤を製造しても良いのである。Furthermore, the liquid mixture may be spread on a paper, a film or the like which has been once subjected to a peeling treatment by the above-mentioned method, and then pressure-transferred to a support to produce a patch.

【００８８】このようにして得られた粘着剤の発泡体に
は窒素ガス等の気体からなる多数の気泡が混在し、その
結果、そのものは体積が１倍を超え数倍に膨張した発泡
体であるが、この発泡体の特性としては、本来の粘着性
を維持するものである。In the foam of the pressure-sensitive adhesive thus obtained, a large number of bubbles composed of a gas such as nitrogen gas are mixed, and as a result, the foam itself is a foam whose volume exceeds 1 time and expands several times. However, the characteristic of this foam is that it retains its original tackiness.

【００８９】又、本発明においては、ホットメルト型高
分子物質、脂環族系石油樹脂、軟化剤、粘着付与剤及び
充填剤等を所定の割合で混合機に投入し、窒素気流中で
６０〜２５０℃の温度で充分に撹拌して均一な液状混合
物とし、この液状混合物を、上述の方法で、支持体或い
はライナーの上に、吐出、発泡させて粘着剤の発泡体を
得た後、この粘着剤の発泡体上に、例えば経皮吸収性の
薬物を溶解した溶液を含浸、乾燥させてもよいのであ
る。Further, in the present invention, the hot-melt type polymeric substance, the alicyclic petroleum resin, the softening agent, the tackifier, the filler and the like are put in a mixer at a predetermined ratio, and the mixture is mixed in a nitrogen stream at 60. After sufficiently stirring at a temperature of ˜250 ° C. to form a uniform liquid mixture, the liquid mixture is discharged and foamed onto a support or a liner by the above-mentioned method to obtain a foam of an adhesive, The foam of the adhesive may be impregnated with a solution having a transdermal drug dissolved therein and dried.

【００９０】この支持体としてはポリエチレン、ポリプ
ロピレン、ポリエステル等の合成樹脂製のフィルム又は
シート、紙、布、不織布等が挙げられる。又、ライナー
とは剥離処理をほどこした剥離紙、セロファン又はポリ
エチレン、ポリプロピレン、ポリエステル等の合成樹脂
製のフィルム又はシート等が挙げられる。Examples of the support include films or sheets made of synthetic resin such as polyethylene, polypropylene and polyester, paper, cloth, non-woven fabric and the like. Examples of the liner include release paper that has been subjected to a release treatment, cellophane, or a film or sheet made of a synthetic resin such as polyethylene, polypropylene or polyester.

【００９１】又、本発明において、温熱型の貼付剤は、
上述の貼付剤に、発熱体を積層することによって得られ
るのである。In the present invention, the heat-type patch is
It is obtained by laminating a heating element on the above-mentioned patch.

【００９２】この発熱体としては、外皮に適用されて温
熱効果を発現するものであれば特に限定されるものでは
ないが、具体的には、例えば化学的な反応熱を利用する
もの、抵抗体に電力を供給して発生するジュール熱を利
用するもの、等が挙げられるが、特に、低温火傷の発生
がなく安全であり、又、優れた温熱効果を比較的長時間
にわたって提供できるうえ、使用中に異臭がなく、しか
も発熱体組成物の偏りがない等の理由より、少なくとも
片面通気性フィルムで構成された開放部のない偏平状袋
体の内部に、鉄粉４０〜７５重量％、活性炭１〜１０重
量％、塩化ナトリウム等の塩化物１〜１０重量％、水１
０〜４０重量％及び保水剤１〜４０重量％からなる発熱
体組成物を封入してなり、且つ上記通気性フィルムの透
湿量がＡＳＴＭ法（Ｅ−９６−８０Ｄ法）で５０〜８０
０ｇ／ｍ²・２４ｈｒのものが有益である。The heating element is not particularly limited as long as it is applied to the outer skin and exerts a heating effect. Specifically, for example, one using chemical reaction heat, a resistor Examples include those that use Joule heat generated by supplying electric power to the product. Especially, it is safe without the occurrence of low-temperature burns, and can provide an excellent thermal effect for a relatively long period of time. Due to the fact that there is no strange odor therein and there is no bias of the heating element composition, at least 40 to 75% by weight of iron powder and activated carbon are contained inside a flat bag body having no open portion and formed of at least one side breathable film. 1-10% by weight, chloride such as sodium chloride 1-10% by weight, water 1
A heating element composition composed of 0 to 40% by weight and a water retention agent of 1 to 40% by weight is enclosed, and the moisture permeability of the breathable film is 50 to 80 by the ASTM method (E-96-80D method).
Those of 0 g / m ² · 24 hr are useful.

【００９３】このようにして得られた温熱型の貼付剤
は、冬期において、単に、人体に温熱を供給して寒さを
凌ぎ、快適に過ごすことができるだけでなく、局所のこ
り、疼痛及び冷え等を伴う症状、例えば肩こり、筋肉
痛、筋肉のこり、腰痛、手足の冷え、神経痛、リューマ
チ、打ち身、捻挫等の疾患に使用され、温熱による治療
効果を充分に期待できるのである。The heat-type patch obtained in this manner not only simply supplies heat to the human body in winter to overcome the cold and allows a comfortable stay, but also causes local stiffness, pain and chills. It is used for accompanying symptoms such as stiff shoulders, muscle aches, stiff muscles, back pain, cold hands and feet, neuralgia, rheumatism, bruises, and sprains, and the therapeutic effect of heat can be expected sufficiently.

【００９４】ところで、このようにして得られた、貼付
剤における粘着剤の発泡体の露出面には剥離処理を施し
た剥離紙、セロファン又はポリエチレン、ポリプロピレ
ン等のプラスチックフィルムを積層して被覆される。By the way, the exposed surface of the foam of the pressure-sensitive adhesive in the adhesive patch thus obtained is laminated and covered with a release-treated release paper, cellophane or a plastic film such as polyethylene or polypropylene. .

【００９５】この貼付剤は１個或いは２個以上の単位で
気密性の包装材に密封包装され、流通に供される。The patch is hermetically packed in an airtight packing material in units of one piece or two pieces or more, and is provided for distribution.

【００９６】[0096]

【作用】本発明は、貼付剤における粘着剤層がホットメ
ルト型高分子物質を含有する粘着剤の発泡体で形成され
ている。In the present invention, the pressure-sensitive adhesive layer in the patch is formed of a pressure-sensitive adhesive foam containing a hot-melt type polymer substance.

【００９７】そして、この粘着剤の発泡体は、そのもの
は体積が１倍を超え数倍に膨張された発泡体であるが、
この発泡体の特性としては、本来の粘着性を維持するこ
とは勿論、気泡の混入によって原料の削減、凹凸面や粗
面に対する密着性が向上するのであるが、特に、このよ
うな粘着剤の発泡体を用いると、弾力性が著しく向上し
て人体皮膚の凹凸面にも追従して密着し、しかも粘着性
及び使用感が良好である上、粘着剤の発泡体で形成され
ているので、剥離時のクッション性によって体毛を引っ
張る等の物理的作用が緩和される結果、剥離時の苦痛が
無いか或いは極めて少ない作用を有するのである。The foam of this adhesive is a foam whose volume is more than 1 time and expanded several times.
As the characteristics of this foam, not only maintaining the original tackiness, but also the inclusion of air bubbles reduces the amount of raw materials and improves the adhesion to uneven and rough surfaces. When a foam is used, the elasticity is remarkably improved, the uneven surface of the human body is also closely followed and adhered, and the adhesiveness and the feeling of use are good, and since it is formed of a foam of an adhesive, As a result of cushioning at the time of peeling, physical effects such as pulling body hair are alleviated, so that there is no or very little pain at the time of peeling.

【００９８】つまり、この粘着剤の発泡体は、粘着力が
大であり、貼付剤の粘着剤層として使用した場合には、
外皮との追従性が良好で、外皮との密着性が一層増大す
るのである。その結果、外皮の凹凸面に対しても弾力的
に順応して粘着するので、粘着強度の低下は生じ難いの
である。That is, the foam of this pressure-sensitive adhesive has a large adhesive force, and when used as a pressure-sensitive adhesive layer of a patch,
The followability with the outer skin is good, and the adhesion with the outer skin is further increased. As a result, even the uneven surface of the outer skin is elastically adapted and adheres, so that the adhesive strength is less likely to decrease.

【００９９】本発明において、粘着剤の発泡体に経皮吸
収性の薬物を配合することにより、局所治療効果を向上
させたり、全身治療効果を向上させることができる作用
を有するのである。In the present invention, by incorporating a transdermal drug into the foam of the adhesive, it is possible to improve the local therapeutic effect and the systemic therapeutic effect.

【０１００】本発明においては、貼付剤の片面に発熱体
が積層されていると、この発熱体により、冬期におい
て、単に、人体に温熱を供給して快適に過ごすことがで
きるだけでなく、局所のこり、疼痛及び冷え等を伴う症
状、例えば肩こり、筋肉痛、筋肉のこり、腰痛、手足の
冷え、神経痛、リューマチ、打ち身、捻挫等の疾患に使
用され、温熱による治療効果を充分に期待できる作用を
有するのである。In the present invention, when a heating element is laminated on one surface of the patch, this heating element not only allows the human body to be heated by the heat in winter, but also has a local residue. It is used for symptoms such as pain and cold, such as stiff shoulders, muscle aches, stiff muscles, back pain, cold hands and feet, neuralgia, rheumatism, bruises, sprains, etc., and has the effect of being able to fully expect the therapeutic effect of heat. Of.

【０１０１】この場合、粘着剤層が粘着剤の発泡体で形
成されているので、上記作用に加えて、この発泡体が熱
伝導を制御して低温火傷が生じ難くなる作用を有するの
である。In this case, since the pressure-sensitive adhesive layer is formed of the foam of the pressure-sensitive adhesive, in addition to the above-mentioned function, this foam has the function of controlling heat conduction and making low temperature burn less likely to occur.

【０１０２】この温熱型の貼付剤において、粘着剤の発
泡体に経皮吸収性の薬物が配合されていることにより、
温熱効果によって、循環が活発になった血液などに薬物
を吸収させて一層効果的に生体内の各部に薬物を循環さ
せることができるので、局所治療効果を一層向上させた
り、全身治療効果を一層向上させて、薬理効果を一層高
める作用を有するのである。In this warm type patch, since the transdermal drug is mixed in the foam of the adhesive,
The thermal effect makes it possible to more effectively circulate the drug in various parts of the living body by absorbing the drug into the blood that has become active in circulation, thus further improving the local therapeutic effect and the systemic therapeutic effect. It has the effect of further improving the pharmacological effect.

【０１０３】この場合、この温熱によって、皮膚からの
発汗等が活発になるが、粘着剤層に吸水性ポリマーが配
合されていることにより、この吸水性ポリマーによって
汗等の体液を円滑に吸収、吸着し、常に外皮表面を清潔
に保つので、ムレや痒みがなく、しかも衛生的である作
用を有するのである。In this case, sweating from the skin is activated by this heat, but since the water-absorbent polymer is mixed in the adhesive layer, the water-absorbent polymer smoothly absorbs body fluid such as sweat, Since it is adsorbed and the skin surface is always kept clean, there is no stuffiness or itchiness, and it has a hygienic effect.

【０１０４】[0104]

【実施例】以下、本発明を実施例に基づき詳細に説明す
るが、本発明はこれに限定されるものではない。The present invention will be described below in detail with reference to examples, but the present invention is not limited to these examples.

【０１０５】実施例１ スチレンーイソプレンースチレンブロック共重合体３３
重量部、水素添加石油樹脂２８．５重量部、テルペン系
樹脂７．５重量部、パラフィン系オイル１８．５重量
部、アロマ系オイル６．５重量部、酸化チタン３重量
部、亜鉛華２．５重量部及びトリスノニルフェニルーフ
ォスファイト０．５重量部からなる粘着剤を窒素気流中
で１６５℃の温度で充分に撹拌して均一な液状混合物と
した。Example 1 Styrene-isoprene-styrene block copolymer 33
1 part by weight, hydrogenated petroleum resin 28.5 parts by weight, terpene resin 7.5 parts by weight, paraffin oil 18.5 parts by weight, aroma oil 6.5 parts by weight, titanium oxide 3 parts by weight, zinc oxide 2. An adhesive consisting of 5 parts by weight and 0.5 parts by weight of trisnonylphenyl-phosphite was sufficiently stirred in a nitrogen stream at a temperature of 165 ° C. to form a uniform liquid mixture.

【０１０６】次に、この液状混合物に、窒素ガスを、例
えば７１Ｋｇ／ｃｍ²の加圧下で機械的に加熱混入して
分散した後、スプレーガン(スプレーエアー圧 ２Ｋｇ／
ｃｍ²の条件下)で、支持体(厚さ２５μｍのポリエチレ
ン製フィルムの片面にレーヨン繊維含有量６０重量％で
且つ厚さ４０μｍのレーヨン・ポリエステル混合不織布
をラミネートしたもの)の不織布側に吐出させ大気圧で
発泡させて厚さ２５０μｍの粘着剤層(粘着剤の発泡体)
を得た。発泡倍率は約２倍であった。Next, nitrogen gas was mechanically heated and mixed into the liquid mixture under pressure of, for example, 71 Kg / cm ² to disperse the mixture, and then spray gun (spray air pressure 2 Kg / cm ² ).
under a condition of cm ² ) and discharge it to the non-woven fabric side of the support (a 25 μm-thick polyethylene film laminated with a rayon / polyester mixed non-woven fabric having a rayon fiber content of 60 wt% and a thickness of 40 μm on one side). 250 μm thick adhesive layer foamed at atmospheric pressure (adhesive foam)
Got The expansion ratio was about 2 times.

【０１０７】次いで、上記粘着剤層上に、塩酸リドカイ
ンゼリーを塗工して、塩酸リドカイン含有粘着層を形成
した。この場合、塩酸リドカイン含有粘着剤層全体中の
塩酸リドカイン含有量は１重量％になるように調整し
た。Then, lidocaine hydrochloride jelly was applied onto the pressure-sensitive adhesive layer to form a lidocaine hydrochloride-containing pressure-sensitive adhesive layer. In this case, the content of lidocaine hydrochloride in the entire pressure-sensitive adhesive layer containing lidocaine hydrochloride was adjusted to 1% by weight.

【０１０８】かくして、本発明の貼付剤を得た。この貼
付剤の大きさは、縦９．５ｃｍ、横１３．０ｃｍとし
た。Thus, the patch of the present invention was obtained. The size of this patch was 9.5 cm in length and 13.0 cm in width.

【０１０９】実施例２ 表フィルムである透湿性フィルムの製造 ポリエチレン製の透湿性基材フィルム（厚さ４０μｍ）
の片面に、ポリエステル製多孔質補強用基材（厚さ６０
μｍ）をラミネートしたものを用いた［透湿度がＡＳＴ
Ｍ法（Ｅ−９６−８０Ｄ法）で７５０ｇ／ｍ²・２４ｈ
ｒ］。Example 2 Production of moisture-permeable film which is a surface film Moisture- permeable substrate film made of polyethylene (thickness: 40 μm)
On one side of the, polyester porous reinforcing substrate (thickness 60
(The water vapor transmission rate is AST
M method (E-96-80D method) 750 g / m ² · 24h
r].

【０１１０】 裏フィルムの製造 厚さ２５μｍのポリエチレン製フィルムの片面にレーヨ
ン繊維含有量６０重量％で且つ厚さ４０μｍのレーヨン
・ポリエステル混合不織布をラミネートしたものを用い
た。 Production of Back Film A polyethylene film having a thickness of 25 μm was laminated on one side with a rayon / polyester mixed non-woven fabric having a rayon fiber content of 60% by weight and a thickness of 40 μm.

【０１１１】上記の表フィルムと裏フィルムを重ね合わ
せるにあたり、裏フィルムにおけるポリエチレン製フィ
ルム側と、表フィルムにおける透湿性基材フィルムとが
接触するように積層し、つまり不織布が露出するように
積層し、その積層体の三周縁部をヒートシールして一方
端開放の偏平状袋体を形成し、この偏平状袋体の内部に
後述する空気の存在によって発熱する発熱体組成物を充
填し（１６６６．７ｇ／ｍ²）、この開放部をヒートシ
ールして発熱体構造物を得た。When the front film and the back film are laminated, they are laminated so that the polyethylene film side of the back film and the moisture-permeable substrate film of the front film are in contact with each other, that is, the nonwoven fabric is exposed. The three peripheral edges of the laminate are heat-sealed to form a flat bag body having one open end, and the flat bag body is filled with a heating element composition that generates heat due to the presence of air (1666). 0.7 g / m ² ), the open portion was heat-sealed to obtain a heating element structure.

【０１１２】発熱体組成物の成分 鉄粉６０重量％、活性炭３重量％、塩化ナトリウム３重
量％、保水剤３重量％及び水３１重量％の組成物 Components of heating element composition Composition of 60% by weight of iron powder, 3% by weight of activated carbon, 3% by weight of sodium chloride, 3% by weight of water retention agent and 31% by weight of water.

【０１１３】上記偏平状袋体における裏フィルムの露出
面側、つまりレーヨン・ポリエステル混合不織布側に実
施例１と同様にして厚さ２５０μｍの粘着剤層(粘着剤
の発泡体)を得た。A pressure-sensitive adhesive layer (pressure-sensitive adhesive foam) having a thickness of 250 μm was obtained in the same manner as in Example 1 on the exposed surface side of the back film in the flat bag, that is, the rayon / polyester mixed nonwoven fabric side.

【０１１４】次いで、上記粘着剤層上に、塩酸リドカイ
ンゼリーを塗工して、塩酸リドカイン含有粘着層を形成
した。この場合、塩酸リドカイン含有粘着剤層全体中の
塩酸リドカイン含有量は１重量％になるように調整し
た。Next, lidocaine hydrochloride jelly was applied onto the pressure-sensitive adhesive layer to form a lidocaine hydrochloride-containing pressure-sensitive adhesive layer. In this case, the content of lidocaine hydrochloride in the entire pressure-sensitive adhesive layer containing lidocaine hydrochloride was adjusted to 1% by weight.

【０１１５】かくして、本発明の温熱型の貼付剤を得
た。この温熱型の貼付剤の大きさは、縦９．５ｃｍ、横
１３．０ｃｍとした。[0115] Thus, the thermosensitive patch of the present invention was obtained. The size of this warm type patch was 9.5 cm in length and 13.0 cm in width.

【０１１６】比較例１ 実施例１と同様の粘着剤を用い、公知の方法で、粘着剤
層を形成した以外は、実施例１と同様にして貼付剤を得
た。Comparative Example 1 A patch was obtained in the same manner as in Example 1 except that the same pressure-sensitive adhesive as in Example 1 was used and the pressure-sensitive adhesive layer was formed by a known method.

【０１１７】即ち、この貼付剤における粘着剤層は全く
発泡させていないものを用い、又、粘着剤層の厚さを１
２０μｍとした。That is, the pressure-sensitive adhesive layer in this patch was not foamed at all, and the thickness of the pressure-sensitive adhesive layer was 1
It was set to 20 μm.

【０１１８】比較例２ 実施例２と同様の粘着剤を用い、公知の方法で、粘着剤
層を形成した以外は、実施例２と同様にして発熱型の貼
付剤を得た。Comparative Example 2 An exothermic patch was obtained in the same manner as in Example 2 except that the same adhesive as in Example 2 was used and the adhesive layer was formed by a known method.

【０１１９】即ち、この発熱型の貼付剤における粘着剤
層は全く発泡させていないものを用い、又、粘着剤層の
厚さを１２０μｍとした。That is, the pressure-sensitive adhesive layer in this exothermic patch was not foamed at all, and the thickness of the pressure-sensitive adhesive layer was 120 μm.

【０１２０】上記の実施例１・２及び比較例１・２の各
貼付剤を用い、下肢痛を訴えるパネラー(男性７人、女
性８人 年令５５〜６５才)に適用し、粘着性、使用
感、人体皮膚の凹凸面への追従性、下肢痛の自覚症状、
剥離時の苦痛及び低温火傷について試験を行った。Using each patch of Examples 1 and 2 and Comparative Examples 1 and 2 described above, it was applied to panelists (7 males, 8 females aged 55 to 65 years old) who complain of lower limb pain, Feeling of use, conformability to uneven surface of human body, subjective symptoms of lower limb pain,
Tests were performed for peeling pain and low temperature burns.

【０１２１】この場合、下肢痛の箇所に１枚貼着し、こ
れを毎日張り替えつつ１週間続けた。In this case, one piece was attached to the site of lower limb pain, and this was reattached every day and continued for one week.

【０１２２】その結果、粘着性は実施例及び比較例共に
良好であり、しかも実施例１・２のものは剥離の際の苦
痛を訴える人はいなかったが、比較例１・２のものは剥
離の際の苦痛を１５名中１２名が訴えた。As a result, the tackiness was good in both Examples and Comparative Examples, and no one complained of the pain during peeling in Examples 1 and 2, but peeling in Comparative Examples 1 and 2. Twelve out of fifteen complained of the suffering.

【０１２３】又、実施例１・２のものは粘着剤層に弾力
性があり、人体皮膚の凹凸面に対する追従性が良好で使
用感が良好であると主張したものが１５名中１３名いた
が、比較例１・２のものは全員が人体皮膚の凹凸面に対
する追従性が悪く使用感が悪いと主張した。Also, in Examples 1 and 2, 13 out of 15 claimed that the pressure-sensitive adhesive layer had elasticity and the conformability to the uneven surface of human skin was good and the usability was good. However, all of Comparative Examples 1 and 2 claimed that they had poor followability to the uneven surface of human skin and had a bad feeling in use.

【０１２４】更に、薬理効果において、実施例１と比較
例１、実施例２と比較例２では差異が認められなかった
が、温熱型の貼着剤（実施例２及び比較例２）の方が顕
著な効果が認められた。Further, in the pharmacological effect, no difference was observed between Example 1 and Comparative Example 1 and between Example 2 and Comparative Example 2, but the thermal adhesive patch (Example 2 and Comparative Example 2) However, the remarkable effect was recognized.

【０１２５】低温火傷において、実施例２では低温火傷
は全く認められなかったが、比較例２のものは１５名中
９名の人に低温火傷が認められた。Regarding low-temperature burns, low-temperature burns were not observed at all in Example 2, but in Comparative Example 2, 9 out of 15 people had low-temperature burns.

【０１２６】ところで、実施例２及び比較例２を皮膚
(下肢)に貼着し、この皮膚(下肢)側に固定した５本の熱
電対を用いて当該皮膚(下肢)部の温度変化を理化工業株
式会社のＳＢＲ１８７−３５ＣＡにて記録したところ、
実施例２のものは４０．５〜４１．２℃の範囲であった
が、比較例２のものは４１．８〜４３．１℃の範囲であ
ることが認められた。By the way, Example 2 and Comparative Example 2 were used for the skin.
When the temperature change of the skin (lower limb) part was recorded by SBR187-35CA of Rika Kogyo Co., Ltd. using 5 thermocouples fixed to the (lower limb) and fixed to the skin (lower limb) side,
It was confirmed that the temperature of the example 2 was in the range of 40.5 to 41.2 ° C, while that of the comparative example 2 was in the range of 41.8 to 43.1 ° C.

【０１２７】以上の実験から、本発明の温熱型の貼付剤
は、皮膚の最高温度が制御できるので、冬期において、
単に、人体に温熱を供給して快適に過ごすことができる
だけでなく、局所のこり、疼痛及び冷え等を伴う症状、
例えば肩こり、筋肉痛、筋肉のこり、腰痛、手足の冷
え、神経痛、リューマチ、打ち身、捻挫等の疾患に使用
され、温熱による治療効果を充分に期待できるのであ
る。From the above-mentioned experiments, since the maximum temperature of the skin can be controlled in the warm type patch of the present invention, in the winter season,
Simply supplying heat to the human body for a comfortable stay, as well as local symptoms such as stiffness, pain and coldness,
For example, it is used for diseases such as stiff shoulders, muscle aches, stiff muscles, low back pain, cold limbs, neuralgia, rheumatism, bruises, and sprains, and the therapeutic effect of heat can be expected sufficiently.

【０１２８】[0128]

【発明の効果】本発明は、貼付剤における粘着剤層がホ
ットメルト型高分子物質を含有する粘着剤の発泡体で形
成されているのであるが、この発泡体の特性としては、
本来の粘着性を維持することは勿論、気泡の混入によっ
て、弾力性が著しく向上し、人体皮膚の凹凸面にも弾力
的に順応して追従して密着するのであり、しかも粘着性
及び使用感が良好である上、粘着剤の発泡体で形成され
ているので、剥離時のクッション性によって体毛を引っ
張る等の物理的作用が緩和される結果、剥離時の苦痛が
無いか或いは極めて少ないのであり、これらの結果、貼
付剤として至極有益である。INDUSTRIAL APPLICABILITY In the present invention, the pressure-sensitive adhesive layer in the patch is formed of a foam of a pressure-sensitive adhesive containing a hot-melt type polymer substance.
In addition to maintaining the original adhesiveness, the inclusion of air bubbles significantly improves the elasticity and elastically adapts and conforms to the uneven surface of human body skin as well. In addition, since it is formed of a foam of an adhesive, the cushioning property at the time of peeling relaxes the physical action such as pulling the body hair, resulting in no or very little pain at the time of peeling. As a result of these, it is extremely useful as a patch.

【０１２９】本発明において、粘着剤の発泡体に経皮吸
収性の薬物を配合することにより、局所治療効果を向上
させたり、全身治療効果を向上させることができる結
果、医薬品として至極有益である。In the present invention, by incorporating a transdermal drug into the foam of the adhesive, the local therapeutic effect and the systemic therapeutic effect can be improved, which is extremely beneficial as a pharmaceutical. .

【０１３０】本発明においては、貼付剤の片面に発熱体
が積層されていると、この発熱体により、冬期におい
て、単に、人体に温熱を供給して快適に過ごすことがで
きるだけでなく、局所のこり、疼痛及び冷え等を伴う症
状、例えば肩こり、筋肉痛、筋肉のこり、腰痛、手足の
冷え、神経痛、リューマチ、打ち身、捻挫等の疾患に使
用されると、温熱による治療効果を発現するのである。In the present invention, when a heating element is laminated on one surface of the patch, the heating element not only allows the human body to be warmed up in winter, but also has a local residue. When it is used for symptoms such as pain and cold, such as stiff neck, muscle aches, stiff muscles, low back pain, cold hands and feet, neuralgia, rheumatism, bruises and sprains, a therapeutic effect due to heat is exhibited.

【０１３１】この場合、粘着剤層が粘着剤の発泡体で形
成されているので、上記作用に加えて、この発泡体が熱
伝導を制御して低温火傷が生じ難くなり、安全性が著し
く高いのである。In this case, since the pressure-sensitive adhesive layer is formed of the pressure-sensitive adhesive foam, in addition to the above-mentioned function, this foam controls heat conduction to prevent low-temperature burns from occurring, resulting in extremely high safety. Of.

【０１３２】この温熱型の貼付剤において、粘着剤の発
泡体に経皮吸収性の薬物が配合されていることにより、
温熱効果によって、循環が活発になった血液などに薬物
を吸収させて一層効果的に生体内の各部に薬物を循環さ
せることができるので、局所治療効果を一層向上させた
り、全身治療効果を一層向上させて、薬理効果を一層高
める結果、医薬品として至極有益である。In this warm type patch, since the transdermally absorbable drug is mixed in the foam of the adhesive,
The thermal effect makes it possible to more effectively circulate the drug in various parts of the living body by absorbing the drug into the blood that has become active in circulation, thus further improving the local therapeutic effect and the systemic therapeutic effect. As a result of further improvement and further enhancement of the pharmacological effect, it is extremely beneficial as a medicine.

【０１３３】この場合、この温熱によって、皮膚からの
発汗等が活発になるが、粘着剤層に吸水性ポリマーが配
合されていることにより、この吸水性ポリマーによって
汗等の体液を円滑に吸収、吸着し、常に外皮表面を清潔
に保つので、ムレや痒みがなく、しかも至極衛生的であ
る。In this case, sweating from the skin is activated by the heat, but since the water-absorbent polymer is mixed in the adhesive layer, the water-absorbent polymer smoothly absorbs body fluid such as sweat, Adsorbs and keeps the skin surface clean at all times, so there is no stuffiness or itching and it is extremely hygienic.

Claims (13)

【特許請求の範囲】[Claims] 【請求項１】 支持体に粘着剤層を設けた貼付剤におい
て、この粘着剤層がホットメルト型高分子物質を含有す
る粘着剤の発泡体で形成されていることを特徴とする貼
付剤。1. A patch having a pressure-sensitive adhesive layer provided on a support, wherein the pressure-sensitive adhesive layer is formed of a foam of a pressure-sensitive adhesive containing a hot-melt polymer substance. 【請求項２】 ホットメルト型高分子物質がＡ−Ｂ−Ａ
型ブロック共重合体、飽和ポリエステル系高分子物質、
アクリル系高分子物質、ウレタン系高分子物質、ポリア
ミド系高分子物質、ポリオレフィン系高分子物質又はポ
リオレフィン系共重合体或いはこれらの変性体である請
求項１に記載の貼付剤。2. A hot melt type polymer material is ABA.
Type block copolymer, saturated polyester polymer material,
The patch according to claim 1, which is an acrylic polymer substance, a urethane polymer substance, a polyamide polymer substance, a polyolefin polymer substance, a polyolefin copolymer, or a modified product thereof. 【請求項３】 粘着剤がホットメルト型高分子物質、脂
環族系石油樹脂及び軟化剤で形成されている請求項１又
は２に記載の貼付剤。3. The patch according to claim 1, wherein the adhesive is formed of a hot melt type polymer substance, an alicyclic petroleum resin and a softening agent. 【請求項４】 粘着剤層がホットメルト型高分子物質５
〜４０重量部、脂環族系石油樹脂５〜５５重量部及び軟
化剤５〜５５重量部で形成されている請求項３に記載の
貼付剤。4. The hot melt type polymer substance 5 having an adhesive layer.
The patch according to claim 3, wherein the patch is formed by 40 parts by weight, 5 to 55 parts by weight of an alicyclic petroleum resin and 5 to 55 parts by weight of a softening agent. 【請求項５】 粘着剤層がホットメルト型高分子物質、
脂環族系石油樹脂、軟化剤及び吸水性ポリマーで形成さ
れている請求項１又は２に記載の貼付剤。5. The adhesive layer is a hot-melt type polymer substance,
The patch according to claim 1 or 2, which is formed of an alicyclic petroleum resin, a softening agent, and a water-absorbing polymer. 【請求項６】 粘着剤層がホットメルト型高分子物質５
〜４０重量部、脂環族系石油樹脂５〜５５重量部、軟化
剤５〜５５重量部及び吸水性ポリマー０．５〜１０重量
部で形成されている請求項５に記載の貼付剤。6. The hot melt type polymer substance 5 having an adhesive layer.
The patch according to claim 5, wherein the patch is formed by 40 parts by weight, 5 to 55 parts by weight of an alicyclic petroleum resin, 5 to 55 parts by weight of a softening agent, and 0.5 to 10 parts by weight of a water absorbing polymer. 【請求項７】 吸水性ポリマーが界面活性剤で処理され
ている請求項５又は６に記載の貼付剤。7. The patch according to claim 5, wherein the water-absorbent polymer is treated with a surfactant. 【請求項８】 粘着剤層に経皮吸収性の薬物が含有され
ている請求項１ないし７のいずれか１項に記載の貼付
剤。8. The patch according to any one of claims 1 to 7, wherein the adhesive layer contains a percutaneously absorbable drug. 【請求項９】 経皮吸収性の薬物の含有量が粘着剤１０
０重量部に対し０．０１〜２５重量部である請求項８に
記載の貼付剤。9. A pressure sensitive adhesive 10 containing a percutaneously absorbable drug.
The patch according to claim 8, which is 0.01 to 25 parts by weight with respect to 0 parts by weight. 【請求項１０】 粘着剤が架橋されている請求項１ない
し９のいずれか１項に記載の貼付剤。10. The patch according to claim 1, wherein the adhesive is crosslinked. 【請求項１１】 請求項１ないし１０のいずれか１項に
記載の貼付剤には発熱体が積層されている貼付剤。11. A patch having a heating element laminated on the patch according to any one of claims 1 to 10. 【請求項１２】 発熱体が、少なくとも片面通気性フィ
ルムで構成された開放部のない偏平状袋体の内部に、鉄
粉４０〜７５重量％、活性炭１〜１０重量％、塩化物１
〜１０重量％、水１０〜４０重量％及び保水剤１〜４０
重量％からなる発熱体組成物を封入してなり、且つ上記
通気性フィルムの透湿量がＡＳＴＭ法（Ｅ−９６−８０
Ｄ法）で５０〜８００ｇ／ｍ²・２４ｈｒのものである
請求項１１に記載の貼付剤。12. An exothermic heating element comprising a flat bag having at least one open-sided air-permeable film and having no open portion, wherein 40 to 75% by weight of iron powder, 1 to 10% by weight of activated carbon and 1 chloride of chloride are contained.
-10 wt%, water 10-40 wt% and water retention agent 1-40
A heating element composition composed of 10% by weight is enclosed, and the moisture permeability of the breathable film is ASTM method (E-96-80).
The patch according to claim 11, which has a D method of 50 to 800 g / m ² · 24 hr. 【請求項１３】 発熱体組成物の充填量が２００〜５０
００ｇ／ｍ²である請求項１２に記載の貼付剤。13. The heating element composition is loaded in an amount of 200 to 50.
The patch according to claim 12, which is 00 g / m ² .