JPH08328438A - Cleaning method and image forming device and device unit using the same - Google Patents

Abstract

PURPOSE: To provide a cleaning method, image forming device and device unit having high reliability. CONSTITUTION: The cleaning blade in the cleaning method and device for the toners remaining on the surface of an org. photoreceptor contg. inorg. or org. particles on the extreme surface layer is an elastic material. The hardness of the elastic material is 50 to 90, its Young's modulus (kg/cm<2> ) is 40 to 90, its 100% modulus (kg/cm<2> ) is 20 to 65, its 300% modulus (kg/cm<2> ) is 70 to 150, its tensile strength (kg/cm<2> ) is 240 to 500, its elongation (%) is 290 to 500, its repulsive elasticity (%) is 30 to 70, its tear strength (kg/cm<2> ) 25 to 75 and its permanent elongation (%) is <=4%. The thickness (t) of the free length part is 1 to 3mm, the free length (L) is 5 to 15mm and L/t ratio is 2 to 8 when the pressure contact force is set in a range of 10 to 50 (gf/cm).

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、電子写真複写機・同プ
リンター等静電転写プロセスを利用する画像形成装置の
クリーニング方法、装置ユニット及び画像形成装置に関
する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for cleaning an image forming apparatus, such as an electrophotographic copying machine and a printer, which utilizes an electrostatic transfer process, an apparatus unit and an image forming apparatus.

【０００２】[0002]

【従来の技術】無端走行する像担持体表面のトナー像を
転写材に転写し、この時転写にしない残留トナーを清掃
する工程をくりかえす画像形成装置において、残留トナ
ーを除去する手段として従来よりゴム質弾性材をクリー
ニングブレードとして用いている。このクリーニングブ
レードは、簡単な構成であって、トナー除去機能に優れ
ているので、広く実用化されている。2. Description of the Related Art In an image forming apparatus which repeats the step of transferring a toner image on the surface of an image carrier which travels endlessly to a transfer material and cleaning the residual toner which is not transferred at this time, rubber has been conventionally used as a means for removing the residual toner. The elastic material is used as a cleaning blade. This cleaning blade has a simple structure and is excellent in a toner removing function, and thus is widely put into practical use.

【０００３】この種のクリーニング素材としては耐摩耗
性に優れているポリウレタンゴムが多く使用されてお
り、その物性については、例えば特開昭５３−３２３９
号公報では６０〜９０°のゴム硬度、特開昭５４−１０
４８４０号公報ではｔａｎδ値が０．１５〜０．９５、
特開昭５９−２１８４７６号公報ではＴｇが−３５℃以
下で、ｔａｎδが０．３０以下、特開平３−２０７６８
号公報ではヤング率が３８〜５８ｋｇｆ／ｍ²で硬度
（ＪＩＳＡ）６０〜７０°、特開平５−３５１５６号公
報では反発弾性が６０〜８０％かつ硬度６５〜７０°、
特開平５−１５０６９７号公報では３００％モジュラス
１３０〜２５０ｋｇ／ｃｍ²かつ硬度（ＪＩＳＡ）が６
０〜７０、特開平６−２７４０７９号公報では反発弾性
が６２±８％、ヤング率５５ｋｇ／ｃｍ²以上かつｔａ
ｎδのピーク温度が−１３〜−１６℃である材料等を用
いているのが知られている。Polyurethane rubber, which is excellent in abrasion resistance, is often used as a cleaning material of this type, and the physical properties thereof are described in, for example, Japanese Patent Laid-Open No. 53-3239.
According to Japanese Patent Laid-Open No. 54-10, the rubber hardness is 60 to 90 °.
In the 4840 publication, the tan δ value is 0.15 to 0.95,
In JP-A-59-218476, Tg is −35 ° C. or lower and tan δ is 0.30 or lower.
In Japanese Patent Laid-Open No. 35-58156, Young's modulus is 38 to 58 kgf / m ² and hardness (JISA) is 60 to 70 °, and in Japanese Patent Laid-Open No. 5-35156, impact resilience is 60 to 80% and hardness is 65 to 70 °.
In Japanese Patent Laid-Open No. 5-150697, the 300% modulus is 130 to 250 kg / cm ² and the hardness (JISA) is 6
0 to 70, in JP-A-6-274079, impact resilience is 62 ± 8%, Young's modulus is 55 kg / cm ² or more and ta
It is known to use a material having a peak temperature of nδ of −13 to −16 ° C.

【０００４】又、圧接力、ブレード厚、ブレード長の規
定としては特開昭５３−３２３９号公報、同５３−９３
０３６号公報、特開平３−２０７６８号公報、同４−３
２８７８８号公報等に記載されているが、これらと力学
的物性値との関連が明確になされていないのが実情であ
って、クリーニング不良による画質の悪化、感光体との
共振による異音トラブル、ブレードめくれ、損傷等は依
然として発生しており、満足なブレードはないのが実情
である。その１つにはクリーニングプロセスはきわめて
複雑な力学的系であって、クリーニングブレードの物性
値やブレード厚等を２つ、３つ規定しても適正な条件を
規定しきれるものではない事による。Further, the pressure contact force, blade thickness and blade length are regulated by Japanese Patent Laid-Open Nos. 53-3239 and 53-93.
036, JP-A-3-20768, and 4-3
Although it is described in Japanese Patent No. 28788, etc., it is the fact that the relationship between these and the mechanical property values has not been clarified, and image quality is deteriorated due to poor cleaning, abnormal noise due to resonance with the photoconductor, Blade turning, damage, etc. are still occurring, and the reality is that there is no satisfactory blade. One of them is that the cleaning process is a very complicated mechanical system, and even if two or three physical values of the cleaning blade, blade thickness, etc. are specified, it is not possible to define proper conditions.

【０００５】又、クリーニング性は感光体表面の材質や
現像剤の組成、粒径にも大きく影響を受け、特に最近は
感光体の耐久性向上のため感光体の表面を加工する技術
が開発されている。これら技術とのかかわりからもクリ
ーニングブレードの物性値や形状を検討する必要性が出
て来ているが、現在まで殆どなされていないのが実情で
ある。Further, the cleaning property is greatly influenced by the material of the surface of the photoconductor, the composition of the developer and the particle size, and recently, a technique for processing the surface of the photoconductor has been developed in order to improve the durability of the photoconductor. ing. Although it is necessary to consider the physical property value and shape of the cleaning blade due to the relation with these techniques, the fact is that it has not been done so far until now.

【０００６】[0006]

【発明が解決しようとする課題】本発明の目的は、従来
少数の物性値で良好な範囲を定めていた素材に対して、
更に多くの管理特性項目や物性値を定めることにより、
高耐久化された感光体と組み合わせても信頼性の高い、
優れたクリーニングブレード、クリーニング方法を開発
し、それを適用した画像形成装置及び装置ユニットを提
供することにある。SUMMARY OF THE INVENTION The object of the present invention is to provide a material for which a good range has been determined with a small number of physical properties,
By defining more control characteristic items and physical property values,
Highly reliable, even when combined with a highly durable photoreceptor
An object of the present invention is to develop an excellent cleaning blade and cleaning method, and provide an image forming apparatus and an apparatus unit to which the cleaning blade and cleaning method are applied.

【０００７】[0007]

【課題を解決するための手段】本発明の目的は下記何れ
かの構成により達成することが出来る。The object of the present invention can be achieved by any of the following constitutions.

【０００８】（１） 形成されたトナー像を転写材へ転
写後の有機感光体からなる像担持体表面に残留するトナ
ー粉体を清掃除去するクリーニング方法において、該ク
リーニング方法がクリーニングブレードの一端を前記感
光体に圧接することにより行われ、且つ該ブレードの材
質が弾性体であり、該弾性体の硬度（ＪＩＳＡスケー
ル）が５０〜９０，ヤング率（ｋｇ／ｃｍ²）が４０〜
９０，１００％モジュラス（ｋｇ／ｃｍ²）が２０〜６
５，３００％モジュラス（ｋｇ／ｃｍ²）が７０〜１５
０，引っ張り強さ（ｋｇ／ｃｍ²）が２４０〜５００，
伸び（％）が２９０〜５００，反発弾性（％）が３０〜
７０，引裂強さ（ｋｇ／ｃｍ²）が２５〜７５及び永久
伸び（％）が４．０以下であり、かつ前記ブレードの感
光体表面への圧接力を１０〜５０（ｇｆ／ｃｍ）の範囲
に設定した際、自由長部の厚さ（ｔ）を１〜３ｍｍ、ブ
レードの自由長（Ｌ）を５〜１５ｍｍ及びＬ／ｔ比を２
〜８であることを特徴とするクリーニング方法。(1) In the cleaning method for cleaning and removing the toner powder remaining on the surface of the image carrier composed of the organic photoconductor after transferring the formed toner image to the transfer material, the cleaning method uses one end of the cleaning blade. The blade is made of an elastic body, the hardness (JISA scale) of the elastic body is 50 to 90, and the Young's modulus (kg / cm ² ) is 40 to 40.
90,100% modulus (kg / cm ² ) is 20-6
5,300% modulus (kg / cm ² ) 70 to 15
0, tensile strength (kg / cm ² ) 240-500,
Elongation (%) 290-500, impact resilience (%) 30-
70, a tear strength (kg / cm ² ) of 25 to 75, a permanent elongation (%) of 4.0 or less, and a pressure contact force of the blade to the photoreceptor surface of 10 to 50 (gf / cm). When the range is set, the thickness (t) of the free length portion is 1 to 3 mm, the free length (L) of the blade is 5 to 15 mm, and the L / t ratio is 2.
The cleaning method is characterized in that

【０００９】（２） 前記感光体の最表面層は無機粒子
又は有機粒子を含有することを特徴とする（１）記載の
クリーニング方法。(2) The cleaning method according to (1), wherein the outermost surface layer of the photoreceptor contains inorganic particles or organic particles.

【００１０】（３） 前記クリーニングブレードの材質
がポリウレタンゴム弾性体であることを特徴とする
（１）又は（２）記載のクリーニング方法。(3) The cleaning method according to (1) or (2), wherein the material of the cleaning blade is a polyurethane rubber elastic body.

【００１１】（４） 前記無機粒子が粒径０．０１〜１
０μｍの金属酸化物であることを特徴とする（２）記載
のクリーニング方法。(4) The inorganic particles have a particle size of 0.01 to 1
The cleaning method according to (2), which is a metal oxide having a thickness of 0 μm.

【００１２】（５） 前記有機粒子が粒径０．０１〜１
０μｍのフッ素又はケイ素含有樹脂であることを特徴と
する（２）記載のクリーニング方法。(5) The organic particles have a particle size of 0.01 to 1
The cleaning method according to (2), which is a resin containing 0 μm of fluorine or silicon.

【００１３】（６） 帯電手段及び現像手段の少なくと
も１つが有機感光体及びクリーニング手段を一体に支持
してユニットを形成し、装置本体に着脱自在の単一ユニ
ットとした装置ユニットにおいて、前記感光体は、その
最表面層に無機粒子又は有機粒子を含有し、並びに前記
クリーニング手段は、其の一端を該感光体に圧接し、そ
の材質がポリウレタン弾性体であり、該ポリウレタン弾
性体の硬度（ＪＩＳＡスケール）が５０〜９０，ヤング
率（ｋｇ／ｃｍ²）が４０〜９０，１００％モジュラス
（ｋｇ／ｃｍ²）が２０〜６５，３００％モジュラス
（ｋｇ／ｃｍ²）が７０〜１５０，引っ張り強さ（ｋｇ
／ｃｍ²）が２４０〜５００，伸び（％）が２９０〜５
００，反発弾性（％）が３０〜７０，引裂強さ（ｋｇ／
ｃｍ²）が２５〜７５及び永久伸び（％）が４．０以下
であり、かつ前記ブレードの圧接力を１０〜５０（ｇｆ
／ｃｍ）の範囲に設定した際、自由長部の厚さ（ｔ）を
１〜３ｍｍ、ブレードの自由長（Ｌ）を５〜１５ｍｍ及
びＬ／ｔ比を２〜８であることを特徴とする装置ユニッ
ト。(6) In a device unit in which at least one of the charging device and the developing device integrally supports the organic photoconductor and the cleaning device to form a unit, and which is a detachable single unit in the device body, the photoconductor Has inorganic particles or organic particles in its outermost surface layer, and the cleaning means presses one end of the cleaning means into contact with the photoreceptor, and the material thereof is a polyurethane elastic body, and the hardness of the polyurethane elastic body (JIS A Scale) 50 to 90, Young's modulus (kg / cm ² ) 40 to 90, 100% modulus (kg / cm ² ) 20 to 65, 300% modulus (kg / cm ² ) 70 to 150, tensile strength (Kg
/ Cm ² ) is 240 to 500, and elongation (%) is 290 to 5
00, impact resilience (%) 30-70, tear strength (kg /
cm ² ) is 25 to 75 and permanent elongation (%) is 4.0 or less, and the pressing force of the blade is 10 to 50 (gf).
/ Cm), the thickness (t) of the free length portion is 1 to 3 mm, the free length (L) of the blade is 5 to 15 mm, and the L / t ratio is 2 to 8. Device unit to be used.

【００１４】（７） 最表面層に無機或いは有機粒子を
含有する有機感光体からなる像担持体、像担持体を帯電
する手段及び転写後の像担持体上に残留するトナーをク
リーニングするクリーニング手段を備えた画像形成装置
において、該クリーニング手段が其の一端を像担持体に
圧接するクリーニングブレードであり、その材質がポリ
ウレタン弾性体であり、該ポリウレタン弾性体の硬度
（ＪＩＳＡスケール）が５０〜９０，ヤング率（ｋｇ／
ｃｍ²）が４０〜９０，１００％モジュラス（ｋｇ／ｃ
ｍ²）が２０〜６５，３００％モジュラス（ｋｇ／ｃ
ｍ²）が７０〜１５０，引っ張り強さ（ｋｇ／ｃｍ²）が
２４０〜５００，伸び（％）が２９０〜５００，反発弾
性（％）が３０〜７０，引裂強さ（ｋｇ／ｃｍ²）が２
５〜７５及び永久伸び（％）が４．０以下であり、かつ
前記ブレードの圧接力を１０〜５０（ｇｆ／ｃｍ）の範
囲に設定した際、自由長部の厚さ（ｔ）を１〜３ｍｍ、
ブレードの自由長（Ｌ）を５〜１５ｍｍ及びＬ／ｔ比を
２〜８であることを特徴とする画像形成装置。(7) An image carrier made of an organic photoreceptor containing inorganic or organic particles in the outermost surface layer, means for charging the image carrier, and cleaning means for cleaning toner remaining on the image carrier after transfer. In the image forming apparatus including the above, the cleaning means is a cleaning blade whose one end is brought into pressure contact with the image carrier, and the material thereof is a polyurethane elastic body, and the hardness (JISA scale) of the polyurethane elastic body is 50 to 90. , Young's modulus (kg /
cm ² ) is 40 to 90, 100% modulus (kg / c
m ² is 20 to 65,300% modulus (kg / c
m ² ) 70 to 150, tensile strength (kg / cm ² ) 240 to 500, elongation (%) 290 to 500, impact resilience (%) 30 to 70, tear strength (kg / cm ² ). Is 2
5 to 75 and a permanent elongation (%) of 4.0 or less, and when the pressure contact force of the blade is set to a range of 10 to 50 (gf / cm), the thickness (t) of the free length portion is 1 ~ 3 mm,
An image forming apparatus having a blade free length (L) of 5 to 15 mm and an L / t ratio of 2 to 8.

【００１５】本発明の如く、各物性値、ブレード厚、自
由長、圧接力等の適正範囲を見出したことにより、優れ
たクリーニングブレードと、表面強度の必ずしも充分で
ない像担持体例えば有機感光体の組み合わせを効率良く
得ることができる。As in the present invention, by finding the proper range of each physical property value, blade thickness, free length, pressure contact force, etc., an excellent cleaning blade and an image bearing member whose surface strength is not always sufficient, such as an organic photoreceptor, can be obtained. The combination can be efficiently obtained.

【００１６】なお本発明で用いられる物性値の測定はＪ
ＩＳＫ−６３０１加硫ゴム物理試験方法に準じる。The physical properties used in the present invention are measured by J
According to ISK-6301 vulcanized rubber physical test method.

【００１７】クリーニングブレードの硬度、ヤング率或
いは１００％モジュラスが低すぎると、像担持体表面に
圧接時の圧力不足や弾性体の腰が弱く、クリーニングブ
レードの接触面積が大きくなり、摩擦力が増加し、摺動
性が悪くなる。高すぎると、像担持体表面への傷の原因
となる。If the hardness, Young's modulus or 100% modulus of the cleaning blade is too low, the pressure is insufficient at the time of pressure contact with the surface of the image bearing member or the elastic body becomes weak, the contact area of the cleaning blade becomes large and the friction force increases. However, the slidability deteriorates. If it is too high, it may cause scratches on the surface of the image bearing member.

【００１８】３００％モジュラスが低すぎると、クリー
ニングブレードエッジは大きく変形する領域において、
繰り返して集中応力を受ける為、エッジの欠損が生じや
すい。又、高くなりすぎると感光体ドラムとクリーニン
グブレードとのなじみが悪く、接触不良によるクリーニ
ング不良を生じる。If the 300% modulus is too low, the cleaning blade edge will deform significantly in the area
Since repeated concentrated stress is applied, edge defects are likely to occur. On the other hand, if the temperature is too high, the contact between the photosensitive drum and the cleaning blade is poor, resulting in poor cleaning due to poor contact.

【００１９】本発明において１００％モジュラス又は３
００％モジュラスとはそれぞれ伸びが１００％又は３０
０％の時の引っ張り強さを意味する。In the present invention, 100% modulus or 3
00% modulus means 100% or 30% elongation
It means the tensile strength at 0%.

【００２０】引っ張り強さが小さすぎると、耐久性が低
くなり、伸びが小さすぎると、しなやかさが足りなくな
り追随性が悪化する。If the tensile strength is too small, the durability will be low, and if the elongation is too small, the flexibility will be insufficient and the followability will be deteriorated.

【００２１】反発弾性が低すぎると、高速度で走行する
感光体の表面に追随して弾性変形したエッジの復元速度
が遅く巻き込まれやすい。高すぎると、始動時に感光体
ドラムとクリーニングブレードとの間に摺擦音（鳴き）
が生じる。If the impact resilience is too low, the restoring speed of the edge elastically deformed following the surface of the photoconductor traveling at a high speed is slow and the air is easily caught. If it is too high, a rubbing noise (squeaking) will occur between the photoconductor drum and the cleaning blade when starting.
Occurs.

【００２２】引き裂き強さが小さいと過負荷により耐久
性が急速に悪化する。When the tear strength is small, the durability is rapidly deteriorated due to overload.

【００２３】永久伸びが大きすぎると、ブレードと感光
体との接触面積が時間、荷動力の増加とともに増し、ク
リーニング不良発生の原因となる。If the permanent elongation is too large, the contact area between the blade and the photosensitive member increases with the increase of time and load power, which causes defective cleaning.

【００２４】圧接力（Ｆ）が１０ｇｆ／ｃｍより小さい
場合には、感光体ドラムのクリーニングにムラが生じ、
また５０ｇｆ／ｃｍを超えると、ブレードが感光体ドラ
ムの表面を傷付けたり、異音を発生させ、駆動モータ等
の過負荷によりシステムに異常を来すため、適切な圧接
力（Ｆ）の範囲としては、１０ｇｆ／ｃｍ〜５０ｇｆ／
ｃｍが好ましく、更に好ましくは１０〜３５ｇｆ／ｃｍ
である。If the pressure contact force (F) is less than 10 gf / cm, the cleaning of the photosensitive drum becomes uneven,
If it exceeds 50 gf / cm, the blade may damage the surface of the photoconductor drum or generate abnormal noise, and the system may become abnormal due to overload of the drive motor. Therefore, the range of the appropriate pressure contact force (F) should be set. Is 10 gf / cm to 50 gf /
cm is preferable, and more preferably 10 to 35 gf / cm
Is.

【００２５】また、ブレードの自由長部の厚さｔ（ｍ
ｍ）が、１．０ｍｍ未満の場合には、熱可塑性樹脂例え
ばポリウレタンにおいて成形性が悪くなり、製造が困難
であると言うような問題があり、また３．０ｍｍより大
の場合には、ブレードの剛性により感光体ドラムを傷付
けると言う問題があるため、自由長部の厚さ（ｔ）は、
１．０ｍｍ〜３．０ｍｍの範囲が好適であり、更に好ま
しくは１．５〜２．５ｍｍである。更にブレードの自由
長Ｌ（ｍｍ）も、５．０ｍｍ未満の場合には、ブレード
の剛性により感光体ドラムを傷付けると言う問題があ
り、１５ｍｍより大の場合には、熱可塑性ウレタンが反
転し、十分なクリーニング性能が得られなくなると言う
ような問題があるため、ブレードの自由長（Ｌ）は５．
０ｍｍ〜１５ｍｍの範囲が好適である。更に好ましくは
８〜１２ｍｍであって、Ｌ／ｔ比は２〜８であるのが好
ましく更に好ましくは４〜６である。なお、ブレードが
階段状やテーパ状等で厚さが均一となっていない場合に
は、その平均厚さを自由長部の厚さｔ（ｍｍ）とするも
のである。ブレード自由長（Ｌ）はブレードの支持体か
ら自由端までの長さ（Ｌ）を意味する（図１、２のＬ参
照）。Further, the thickness t (m
When m) is less than 1.0 mm, there is a problem that the thermoplastic resin such as polyurethane has poor moldability and is difficult to manufacture, and when it is larger than 3.0 mm, the blade has a problem. The thickness of the free length (t) is
The range of 1.0 mm to 3.0 mm is suitable, and more preferably 1.5 to 2.5 mm. Further, when the free length L (mm) of the blade is less than 5.0 mm, there is a problem that the rigidity of the blade damages the photosensitive drum, and when it is more than 15 mm, the thermoplastic urethane is reversed, Since there is a problem that sufficient cleaning performance cannot be obtained, the free length (L) of the blade is 5.
A range of 0 mm to 15 mm is suitable. It is more preferably 8 to 12 mm, and the L / t ratio is preferably 2 to 8 and more preferably 4 to 6. When the blade has a stepped shape or a tapered shape and the thickness is not uniform, the average thickness thereof is taken as the thickness t (mm) of the free length portion. The blade free length (L) means the length (L) from the support of the blade to the free end (see L in FIGS. 1 and 2).

【００２６】上記は一般的な傾向であるが実際には上記
各力学的物性、ブレード厚、自由長、圧接力は相互に複
雑に関連し合っており実際の複写機を用いて適正値を定
める。Although the above is a general tendency, in reality, the above-mentioned mechanical properties, blade thickness, free length, and pressure contact force are intricately related to each other, and appropriate values are determined using an actual copying machine. .

【００２７】本発明において使用する弾性体としては前
記の諸特性を比較的容易に得られることからポリウレタ
ン弾性体が好ましい。ポリウレタン弾性体としては、一
般にイソシアネートとポリオール及び各種水素含有化合
物との付加反応を経て合成されるポリウレタンが用いら
れており、ポリオール成分として、ポリプロピレングリ
コール、ポリテトラメチレングリコール等のポリエーテ
ル系ポリオールや、アジペート系ポリオール、ポリカプ
ロラクタム系ポリオール、ポリカーボネート系ポリオー
ル等のポリエステル系ポリオールを用い、ポリイソシア
ネート成分として、トリレンジイソシアネート、４，
４′ジフェニルメタンジイソシアネート、ポリメチレン
ポリフェニルポリイソシアネート、トルイジンジイソシ
アネート、等の芳香族系ポリイソシアネート、ヘキサメ
チレンジイソシアネート、イソホロンジイソシアネー
ト、キシリレンジイソシアネート、ジシクロヘキシルメ
タンジイソシアネート等の脂肪族系ポリイソシアネート
を用いてウレタンプレポリマーを調製し、これに硬化剤
を加えて、所定の型内に注入し、架橋硬化させた後、常
温で熟成することによって製造されている。上記硬化剤
としては、通常、１，４−ブタンジオール等の二価アル
コールとトリメチロールプロパン、ペンタエリスリトー
ル等の三価以上の多価アルコールとが併用される。As the elastic body used in the present invention, a polyurethane elastic body is preferable because the above-mentioned various properties can be obtained relatively easily. As the polyurethane elastic body, polyurethane which is generally synthesized through an addition reaction of isocyanate and polyol and various hydrogen-containing compounds is used, and as a polyol component, polypropylene glycol, polyether polyol such as polytetramethylene glycol, or the like, Polyester polyols such as adipate-based polyols, polycaprolactam-based polyols and polycarbonate-based polyols are used, and tolylene diisocyanate, 4,
Urethane prepolymers using aromatic polyisocyanates such as 4'diphenylmethane diisocyanate, polymethylene polyphenyl polyisocyanate, toluidine diisocyanate, etc., hexamethylene diisocyanate, isophorone diisocyanate, xylylene diisocyanate, dicyclohexylmethane diisocyanate, etc. Is prepared, and a curing agent is added thereto, and the mixture is injected into a predetermined mold, cross-linked and cured, and then aged at room temperature. As the curing agent, dihydric alcohols such as 1,4-butanediol and trihydric or higher polyhydric alcohols such as trimethylolpropane and pentaerythritol are usually used in combination.

【００２８】更に、ポリウレタン弾性体には、上記の条
件を満たす範囲で炭素数４０〜１００の不飽和脂肪酸ア
ミドを含有させたり、シリコーンオイル含有層を設けた
りしてもよい。又、シリカ等の微粒子を混入させてもよ
い。Further, the polyurethane elastic material may contain an unsaturated fatty acid amide having 40 to 100 carbon atoms or a silicone oil-containing layer within a range satisfying the above conditions. Further, fine particles such as silica may be mixed.

【００２９】本発明のクリーニングブレードの形状は特
に限定されず種々のものが用いられるが、その具体例と
して図１に本発明で用いられるブレード例（ａ），
（ｂ），（ｃ）を示す。The shape of the cleaning blade of the present invention is not particularly limited and various ones may be used. As a specific example, the blade example (a) used in the present invention is shown in FIG.
(B), (c) is shown.

【００３０】又、図２に本発明で用いられるクリーニン
グブレードの断面図を示し、支持金具と一体的に形成さ
れた熱可塑性ウレタンからなるブレードを示し、図２に
おいて、ｔはブレードの支持端から自由端までの自由長
部の厚さ（ｍｍ）、Ｌはブレードの支持端までの自由長
（ｍｍ）の長さを示している。Further, FIG. 2 shows a sectional view of the cleaning blade used in the present invention, showing a blade made of thermoplastic urethane integrally formed with the support fitting, and in FIG. 2, t is from the supporting end of the blade. The thickness (mm) of the free length portion up to the free end, and L indicates the length of the free length (mm) up to the supporting end of the blade.

【００３１】本発明者等は未反応の残存イソシアネート
が空気中の水分や、オゾン或いはトナー粒子中の活性水
素を有する化合物或いは紙粉中の水分により化学変化を
引き起こし、ブレード中に低分子の窒素含有モノマーを
生成せしめたり、感光体の最表面に含有された無機或い
は有機の粒子によりブレードに不均一で局部的な衝撃力
や摩擦熱が加わることにより、フリーラジカルが生じ、
残存イソシアネートやポリマーとの反応により低分子化
が進行し、ブレードの耐久性が急激に悪化し、それによ
り画質の劣化が起こることを突き止めた。The present inventors have found that unreacted residual isocyanate causes a chemical change due to moisture in the air, ozone or a compound having active hydrogen in toner particles or moisture in paper powder, and low molecular weight nitrogen in the blade. Free radicals are generated due to non-uniform and local impact force or frictional heat applied to the blade due to the formation of the contained monomer or the inorganic or organic particles contained on the outermost surface of the photoreceptor.
It was found that the reaction with the residual isocyanate and the polymer promotes the lowering of the molecular weight, and the durability of the blade deteriorates sharply, which causes the deterioration of the image quality.

【００３２】残存イソシアネートを低下せしめる方法は
使用するイソシアネートの種類や重合法、触媒、反応条
件、反応釜の形状、撹拌機の効率によるが、反応せしめ
た後２次加熱処理を長時間行うことによっても得られ
る。或いは触媒、高反応性イソシアネートを選定しても
よい。The method for reducing the residual isocyanate depends on the type of isocyanate used, the polymerization method, the catalyst, the reaction conditions, the shape of the reaction vessel, and the efficiency of the stirrer. However, after the reaction, the secondary heat treatment is carried out for a long time. Can also be obtained. Alternatively, a catalyst or a highly reactive isocyanate may be selected.

【００３３】本発明で用いられるポリウレタン弾性体中
のイソシアネート（ＮＣＯ）基量測定は、ＩＲ内部標準
法（ＣＨ₂：２８６０ｃｍ^-1、ＮＣＯ：２２３０ｃ
ｍ^-1）によった。The isocyanate (NCO) group content in the polyurethane elastomer used in the present invention is measured by IR internal standard method (CH ₂ : 2860 cm ^-1 , NCO: 2230c).
m ^-1 ).

【００３４】残存イソシアネートは全ポリウレタン弾性
体に対する重量比率にて、０．１５％以下がよく、特に
好ましくは０．１％以下がよい。０．１５％より大きい
とブレードの機械的損傷が大きく、高耐久性有機感光体
の繰り返し使用時の画像安定性を生かし切れない。The residual isocyanate is preferably 0.15% or less, particularly preferably 0.1% or less in terms of weight ratio to the total polyurethane elastic material. If it is more than 0.15%, the mechanical damage of the blade is large, and the image stability of the highly durable organic photoreceptor cannot be fully utilized when it is repeatedly used.

【００３５】本発明の電子写真感光体の最表面層に含有
される無機粒子としては、好ましくはモース硬度で４以
上の硬質の粒子とされ、電子写真性能に悪影響を与えな
いものとされる。The inorganic particles contained in the outermost surface layer of the electrophotographic photosensitive member of the present invention are preferably hard particles having a Mohs hardness of 4 or more, and do not adversely affect the electrophotographic performance.

【００３６】このような無機粒子としては、例えば酸化
セリウム、酸化クロム、酸化アルミニウム、酸化マグネ
シウム、酸化ケイ素、酸化錫、酸化ジルコニウム、酸化
鉄、酸化チタンなどの酸化物；硫酸カルシウム、硫酸バ
リウム、硫酸アルミニウムなどの硫酸塩；珪酸カルシウ
ム、珪酸マグネシウムなどの珪酸塩；チッ化ホウ素、チ
ッ化チタンなどのチッ化物；炭化ケイ素、炭化チタン、
炭化ホウ素、炭化タングステン、炭化ジルコニウムなど
の炭化物；ホウ化ジルコニウム、ホウ化チタンなどのホ
ウ化物などが挙げられ、これらのうち１種を、又は必要
に応じて２種以上が用いられる。この内好ましいものと
して、酸化アルミニウム、酸化チタン、酸化ジルコニウ
ム、酸化ケイ素等がある。Examples of such inorganic particles include oxides such as cerium oxide, chromium oxide, aluminum oxide, magnesium oxide, silicon oxide, tin oxide, zirconium oxide, iron oxide and titanium oxide; calcium sulfate, barium sulfate and sulfuric acid. Sulfates such as aluminum; silicates such as calcium silicate and magnesium silicate; nitrides such as boron nitride and titanium nitride; silicon carbide, titanium carbide,
Carbides such as boron carbide, tungsten carbide, and zirconium carbide; borides such as zirconium boride and titanium boride, and the like can be used, and one of these can be used, or two or more can be used as necessary. Among these, aluminum oxide, titanium oxide, zirconium oxide, silicon oxide and the like are preferable.

【００３７】この内酸化ケイ素としては、未然の珪石又
は水晶の微粉砕体で球状処理化によるものや、合成微粒
子シリカ等が挙げられる。合成微粒子シリカは出発物質
より（１）ケイ酸アルカリ法、（２）四塩化ケイ素法、
（３）金属シリコーン法、（４）アルコキシシラン法等
があるが、製造する方法として化学炎ＣＶＤ法（ＣＶ
Ｄ；Ｃｈｅｍｉｃａｌ Ｖａｐｏｒ Ｄｅｐｏｓｉｔｉ
ｏｎ）によるのが好ましい。Examples of the silicon oxide include those obtained by spheroidizing a previously pulverized silica stone or quartz and synthetic fine particle silica. Synthetic fine particle silica is composed of (1) alkali silicate method, (2) silicon tetrachloride method,
There are (3) metal silicone method, (4) alkoxysilane method, etc., but as a manufacturing method, chemical flame CVD method (CV
D; Chemical Vapor Depositi
on).

【００３８】本発明の電子写真感光体の最表面に含有さ
れる有機粒子としては、ポリエチレン、ポリプロピレ
ン、ポリブテン、ポリヘキセン等のオレイン系、ポリ塩
化ビニル、ポリ塩化ビニルデン、ポリ酢酸ビニル、アク
リル−スチレンコポリマー、ポリアクリロニトリル、ポ
リスチレン、ポリアクリル酸エステル、ポリメタクリレ
ート等のビニル系、或いはポリアセタール、メラミン、
ベンゾグアナミン、ポリアミド、ポリエステル、ポリエ
チレンテレフタレート等からなる粒子がある。The organic particles contained on the outermost surface of the electrophotographic photoreceptor of the present invention include olein series such as polyethylene, polypropylene, polybutene, polyhexene, polyvinyl chloride, polyvinyl chloride, polyvinyl acetate, acryl-styrene copolymer. , Vinyl type such as polyacrylonitrile, polystyrene, polyacrylic acid ester, polymethacrylate, or polyacetal, melamine,
There are particles made of benzoguanamine, polyamide, polyester, polyethylene terephthalate and the like.

【００３９】フッ素含有樹脂としては、ポリテトラフル
オロエチレン、ポリクロロトリフルオロエチレン、ポリ
フッ化ビニリデン、ポリジクロロジフルオロエチレン、
テトラフルオロエチレン−パーフルオロアルキルビニル
エーテル共重合体、テトラフルオロエチレン−ヘキサフ
ルオロプロピレン共重合体、テトラフルオロエチレン−
エチレン共重合体及びテトラフルオロエチレン−ヘキサ
フルオロプロピレン−パーフルオロアルキルビニルエー
テル共重合体からなる群から選ばれた１種または２種以
上から構成されているものがある。市販のフッ素原子含
有樹脂微粒子をそのまま用いることが可能であり、３０
００〜５００万の分子量のものが使用可能である。更に
その他のものとしてフロロカーボンがあり、例えばセフ
ボン−ＣＭＦ（セントラル硝子製）がある。As the fluorine-containing resin, polytetrafluoroethylene, polychlorotrifluoroethylene, polyvinylidene fluoride, polydichlorodifluoroethylene,
Tetrafluoroethylene-perfluoroalkyl vinyl ether copolymer, tetrafluoroethylene-hexafluoropropylene copolymer, tetrafluoroethylene-
Some are composed of one type or two or more types selected from the group consisting of ethylene copolymers and tetrafluoroethylene-hexafluoropropylene-perfluoroalkyl vinyl ether copolymers. It is possible to use commercially available fluorine atom-containing resin fine particles as they are.
Those having a molecular weight of 00 to 5,000,000 can be used. Further, there is fluorocarbon, for example, Cefbon-CMF (made by Central Glass).

【００４０】ケイ素含有有機ポリマーとしては、ジメチ
ルポリシロキサン、メトキシポリシロキサン、オルガノ
ポリシロキサン、オルガノシリカゾル等があり、例えば
トスパール（東芝シリコーン（株））、トレフイル（東
レダウコーティングシリコーン（株））がある。Examples of the silicon-containing organic polymer include dimethylpolysiloxane, methoxypolysiloxane, organopolysiloxane, and organosilica sol. For example, Tospearl (Toshiba Silicone Co., Ltd.) and Trefyl (Toray Dow Coating Silicone Co., Ltd.) are available. .

【００４１】これら粒子の粒径としては、０．０１〜１
０μｍがよく、好ましくは０．０５〜５μｍが良い。
０．０１μｍより小さいと微粒子添加の効果がなく、１
０μｍより大きいと画像劣化とクリーニング不良が起き
やすい。The particle size of these particles is 0.01 to 1
0 μm is preferable, and 0.05 to 5 μm is preferable.
If it is smaller than 0.01 μm, there is no effect of adding fine particles, and 1
If it is larger than 0 μm, image deterioration and cleaning failure are likely to occur.

【００４２】これら粒子は分散性向上の為、特開昭６０
−２１３９５８号の如くチタネート系又はシラン系カッ
プリング剤で表面処理されていてもよい。Since these particles improve the dispersibility, they are disclosed in JP-A-60
The surface may be treated with a titanate-based or silane-based coupling agent as described in JP-A-213958.

【００４３】本発明の感光体においては、電荷発生物質
（ＣＧＭ）として次の代表例で示されるような顔料が用
いられる。In the photoconductor of the present invention, the pigments represented by the following representative examples are used as the charge generating substance (CGM).

【００４４】(１) モノアゾ顔料、ビスアゾ顔料、トリ
アゾ顔料、金属錯塩アゾ顔料等のアゾ顔料 (２) ペリレン酸無水物、ペリレン酸イミド等のペリレ
ン顔料 (３) アントラキノン誘導体、アントアントロン誘導
体、ジベンズピレンキノン誘導体、ピラントロン誘導
体、ビオラントロン誘導体及びイソビオラントロン誘導
体等多環キノン顔料 (４) インジゴ誘導体及びチオインジゴ誘導体等のイン
ジゴイド顔料 (５) 金属フタロシアニン及び無金属フタロシアニン等
のフタロシアニン顔料 更に詳しく電荷発生物質について述べると、本発明にお
いて好ましく用いられる電荷発生物質としては、特開昭
59-184353号記載の多環キノン顔料、更に好ましくはジ
ブロムアンスアンスロン顔料、或いは特開平2-20877
号、同２−２８３３４３号、特開昭６３−３０１９５５
号、同５４−２２８３４号、同５７−４９９４９号、同
５９−２２９５６４号、同６３−３０１９５５号記載の
ビスアゾ顔料、特公平3-26384号記載のハロゲン置換型
ペリレン系顔料、特開昭62-54267号記載の非対称型ペリ
レン系顔料、特開昭54-126036号、同58-152247号、同59
-31957号、特開平2-251858号、同4-62560号、同5-6014
号記載のペリレン系顔料、特願平3-279764号記載のビス
イミダゾピリドノペリレン系顔料が良い。(1) Azo pigments such as monoazo pigments, bisazo pigments, triazo pigments, metal complex salt azo pigments, etc. (2) Perylene pigments such as perylene anhydride, perylene imide, etc. (3) Anthraquinone derivatives, anthanthrone derivatives, dibenz Polycyclic quinone pigments such as pyrenequinone derivatives, pyranthrone derivatives, violanthrone derivatives and isobiolanthrone derivatives (4) Indigoid pigments such as indigo derivatives and thioindigo derivatives (5) Phthalocyanine pigments such as metal phthalocyanines and metal-free phthalocyanines The charge generating substance preferably used in the present invention is described in
Polycyclic quinone pigments described in 59-184353, more preferably dibromoanthanthrone pigment, or JP-A 2-20877.
No. 2-283343, JP-A-63-301955.
Nos. 54-22834, 57-49949, 59-229564, and 63-301955, bisazo pigments described in JP-B-3-26384, halogen-substituted perylene pigments, JP-A-62-1 Asymmetrical perylene pigments described in 54267, JP-A Nos. 54-126036, 58-152247, and 59.
-31957, JP-A-2-251858, 4-62560, 5-6014
And the bisimidazopyridonoperylene-based pigments described in Japanese Patent Application No. 3-279764 are preferable.

【００４５】又、特開昭61-239248号記載のα型チタニ
ルフタロシアニン、同62-67094号記載のβ型チタニルフ
タロシアニン、同63-366号記載のＣ型チタニルフタロシ
アニン、特開平2-309362号記載のＩ型チタニルフタロシ
アニンがあり、更に好ましくは特願昭62-173640号記載
のＹ型チタニルフタロシアニンが良い。Further, α-type titanyl phthalocyanine described in JP-A-61-239248, β-type titanyl phthalocyanine described in 62-67094, C-type titanyl phthalocyanine described in 63-366, and JP-A-2-309362 are described. I-type titanyl phthalocyanine, more preferably Y-type titanyl phthalocyanine described in Japanese Patent Application No. 62-173640.

【００４６】本発明の電荷発生層に用いられるバインダ
としては、例えば次のものを挙げることができる。Examples of the binder used in the charge generation layer of the present invention include the following.

【００４７】(１) ポリエステル (２) メタクリル樹脂 (３) アクリル樹脂 (４) ポリ塩化ビニル (５) ポリ塩化ビニリデン (６) ポリスチレン (７) ポリビニルアセテート (８) スチレン共重合樹脂 (例えば、スチレン-ブタヂエ
ン共重合体、スチレン-メタクリル酸メチル共重合体、
等) (９) アクリロニトリル系共重合体樹脂 (例えば、塩化
ビニリデン-アクリトロニトリル共重合体、等) (10) 塩化ビニル-酢酸ビニル共重合体 (11) 塩化ビニル-酢酸ビニル-無水マレイン酸共重合体 (12) シリコーン樹脂 (13) シリコーン-アルキッド樹脂 (14) フェノール樹脂 (例えば、フェノールーホルムア
ルデヒド樹脂、クレゾールホルムアルデヒド樹脂、等) (15) スチレン-アルキッド樹脂 (16) ポリ-N-ビニルカルバゾール (17) ポリビニルブチラール (18) ポリビニルホルマール (19) ポリヒドロキシスチレン これらのバインダは、単独で或いは２種以上の混合物と
して併用することができる。(1) Polyester (2) Methacrylic resin (3) Acrylic resin (4) Polyvinyl chloride (5) Polyvinylidene chloride (6) Polystyrene (7) Polyvinyl acetate (8) Styrene copolymer resin (for example, styrene- Butadiene copolymer, styrene-methyl methacrylate copolymer,
Etc.) (9) Acrylonitrile-based copolymer resin (for example, vinylidene chloride-acrytronitrile copolymer, etc.) (10) Vinyl chloride-vinyl acetate copolymer (11) Vinyl chloride-vinyl acetate-maleic anhydride copolymer Polymer (12) Silicone resin (13) Silicone-alkyd resin (14) Phenol resin (for example, phenol-formaldehyde resin, cresol formaldehyde resin, etc.) (15) Styrene-alkyd resin (16) Poly-N-vinylcarbazole ( 17) Polyvinyl butyral (18) Polyvinyl formal (19) Polyhydroxystyrene These binders can be used alone or as a mixture of two or more kinds.

【００４８】本発明に係る感光体の感光層に含有される
電荷輸送物質(CTM)としては、例えばオキサゾール誘導
体、オキサジアゾール誘導体、チアゾール誘導体、チア
ジアゾール誘導体、トリアゾール誘導体、イミダゾール
誘導体、イミダゾロン誘導体、イミダゾリン誘導体、ビ
スイミダゾリジン誘導体、スチリル化合物、ヒドラゾン
化合物、ベンジジン化合物、ピラゾリン誘導体、スチル
ベン化合物、アミン誘導体、オキサゾロン誘導体、ベン
ゾチアゾール誘導体、ベンズイミダゾール誘導体、キナ
ゾリン誘導体、ベンゾフラン誘導体、アクリジン誘導
体、フェナジン誘導体、アミノスチルベン誘導体、ポリ
-N-ビニルカルバゾール、ポリ-1-ビニルピレン、ポリ-9
-ビニルアントラセン等が挙げられこれらの電荷輸送物
質(CTM)は通常バインダーと共に層形成が行われる。Examples of the charge transport material (CTM) contained in the photosensitive layer of the photoreceptor according to the present invention include oxazole derivatives, oxadiazole derivatives, thiazole derivatives, thiadiazole derivatives, triazole derivatives, imidazole derivatives, imidazolone derivatives, imidazoline. Derivatives, bisimidazolidine derivatives, styryl compounds, hydrazone compounds, benzidine compounds, pyrazoline derivatives, stilbene compounds, amine derivatives, oxazolone derivatives, benzothiazole derivatives, benzimidazole derivatives, quinazoline derivatives, benzofuran derivatives, acridine derivatives, phenazine derivatives, aminostilbenes Derivative, poly
-N-vinylcarbazole, poly-1-vinylpyrene, poly-9
-Vinyl anthracene and the like are mentioned. These charge transport materials (CTM) are usually layered with a binder.

【００４９】これらの中で特に好ましい電荷輸送物質(C
TM)としては下記一般式で示される化合物のものがあげ
られる。Of these, particularly preferred charge transport materials (C
Examples of TM) include compounds represented by the following general formula.

【００５０】[0050]

【化１】 Embedded image

【００５１】（式中、Ar₁、Ar₂、Ar₄は各々置換、無置
換の芳香族炭化水素基または複素環基を表し、Ar₃は各
々置換、無置換の２価の芳香族炭化水素基又は複素環
基、Ｒ₂は水素原子もしくは各々置換、無置換の芳香族
炭化水素基または複素環基を表す。ｎは１もしくは２で
ある。Ar₄とＲ₂は互いに結合して環を形成してもよ
い。）(In the formula, Ar ₁ , Ar ₂ , and Ar ₄ each represent a substituted or unsubstituted aromatic hydrocarbon group or a heterocyclic group, and Ar ₃ represents a substituted or unsubstituted divalent aromatic hydrocarbon group. Group or heterocyclic group, R ₂ represents a hydrogen atom or a substituted or unsubstituted aromatic hydrocarbon group or heterocyclic group, n is 1 or 2. Ar ₄ and R ₂ are bonded to each other to form a ring. It may be formed.)

【００５２】[0052]

【化２】 Embedded image

【００５３】（式中、Ｒ₃、Ｒ₄は各々置換、無置換の芳
香族炭化水素基、複素環基またはアルキル基を表し、互
いに連結して環を形成してもよい。Ｒ₅は水素原子また
は各々置換、無置換の芳香族炭化水素基、複素環基もし
くはアルキル基を表し、Ar₅は各々置換、無置換の芳香
族炭化水素基または複素環基を表す。ｍは０もしくは１
である。）(In the formula, R ₃ and R ₄ each represent a substituted or unsubstituted aromatic hydrocarbon group, a heterocyclic group or an alkyl group, which may be linked to each other to form a ring. R ₅ is hydrogen. An atom or a substituted or unsubstituted aromatic hydrocarbon group, a heterocyclic group or an alkyl group is represented, Ar ₅ is a substituted or unsubstituted aromatic hydrocarbon group or a heterocyclic group, and m is 0 or 1.
Is. )

【００５４】[0054]

【化３】 Embedded image

【００５５】（式中、Ｙは各々ｌ価の置換、無置換はフ
ェニル基、ナフチル基、ピレニル基、フルオレニル基、
カルバゾリル基、ジフェニル基及び4,4′-アルキリデン
ジフェニル基を表し、Ar₆、Ar₇は各々置換、無置換の芳
香族炭化水素基または複素環基を表す。ｌは１〜３の整
数を表す。）(In the formula, Y is a monovalent substituted or unsubstituted phenyl group, naphthyl group, pyrenyl group, fluorenyl group,
It represents a carbazolyl group, a diphenyl group and a 4,4'-alkylidene diphenyl group, and Ar ₆ and Ar ₇ each represent a substituted or unsubstituted aromatic hydrocarbon group or a heterocyclic group. l represents an integer of 1 to 3. )

【００５６】[0056]

【化４】 [Chemical 4]

【００５７】（式中、Ar₈、Ar₉、Ar₁₀、Ar₁₁は各々置
換、無置換の芳香族炭化水素基または複素環基を表し、
Ar₁、Ar₂、Ar₃は前述の通りである。） これらの内、本発明の感光体に好ましく用いられる具体
的化合物例を以下に例示する。(In the formula, Ar ₈ , Ar ₉ , Ar ₁₀ and Ar ₁₁ each represent a substituted or unsubstituted aromatic hydrocarbon group or a heterocyclic group,
Ar ₁ , Ar ₂ and Ar ₃ are as described above. Among these, specific compound examples preferably used in the photoconductor of the present invention are illustrated below.

【００５８】[0058]

【化５】 Embedded image

【００５９】[0059]

【化６】 [Chemical 6]

【００６０】[0060]

【化７】 [Chemical 7]

【００６１】[0061]

【化８】 Embedded image

【００６２】[0062]

【化９】 [Chemical 9]

【００６３】[0063]

【化１０】 [Chemical 10]

【００６４】本発明に係る感光体の感光層及び積層構成
の場合の電荷発生層(CGL)、電荷輸送層(CTL)に含有され
るバインダー樹脂としては、ポリエステル樹脂、ポリス
チレン樹脂、メタクリル樹脂、アクリル樹脂、ポリ塩化
ビニル樹脂、ポリ塩化ビニリデン樹脂、ポリカーボネー
ト樹脂、ポリビニルブチラール樹脂、ポリビニルアセテ
ート樹脂、スチレン-ブタジエン樹脂、塩化ビニリデン-
アクリロニトリル共重合体樹脂、塩化ビニル-無水マレ
イン酸共重合体樹脂、ウレタン樹脂、シリコン樹脂エポ
キシ樹脂、シリコン-アルキッド樹脂、フェノール樹
脂、ポリシラン樹脂、ポリビニルカルバゾール等が挙げ
られる。The binder resin contained in the charge generating layer (CGL) and charge transporting layer (CTL) in the case of the photosensitive layer and the laminated structure of the photoreceptor according to the present invention includes polyester resin, polystyrene resin, methacrylic resin, acrylic resin. Resin, polyvinyl chloride resin, polyvinylidene chloride resin, polycarbonate resin, polyvinyl butyral resin, polyvinyl acetate resin, styrene-butadiene resin, vinylidene chloride-
Examples thereof include acrylonitrile copolymer resin, vinyl chloride-maleic anhydride copolymer resin, urethane resin, silicone resin epoxy resin, silicone-alkyd resin, phenol resin, polysilane resin, and polyvinylcarbazole.

【００６５】各感光体の最上層に含有されるバインダー
樹脂は好ましくは機械的衝撃に強く耐摩耗性が大であ
り、かつ電子写真性能を阻害しないものがよい。好まし
いバインダー樹脂としては下記一般式（Ｉ）、（II）、
（III）又は（IV）の構造単位を有するポリカーボネー
ト樹脂があげられる。The binder resin contained in the uppermost layer of each photoconductor is preferably one that is resistant to mechanical impact, has high abrasion resistance, and does not impair electrophotographic performance. Preferred binder resins include the following general formulas (I), (II),
A polycarbonate resin having the structural unit (III) or (IV) can be used.

【００６６】[0066]

【化１１】 [Chemical 11]

【００６７】（式中、Ｒ₁〜Ｒ₈は水素原子、ハロゲン原
子、各々置換若しくは無置換の炭素数１〜10のアルキル
基、シクロアルキル基又はアリール基、Ｚは４〜11の炭
素原子数を有する飽和又は不飽和の炭素環形成残基、Ｒ
₉は炭素原子数１〜９のアルキル基又はアリール基であ
る。）(Wherein, R _{1 to} R ₈ are hydrogen atoms, halogen atoms, substituted or unsubstituted alkyl groups having 1 to 10 carbon atoms, cycloalkyl groups or aryl groups, and Z is a carbon atom having 4 to 11 carbon atoms. A saturated or unsaturated carbocycle-forming residue having R, R
₉ is an alkyl group or an aryl group having 1 to 9 carbon atoms. )

【００６８】[0068]

【化１２】 [Chemical 12]

【００６９】（式中、Ｒ₁₁からＲ₁₈はそれぞれ独立して
水素原子、ハロゲン原子、アルキル基又はアリール基を
表す。）(In the formula, R ₁₁ to R ₁₈ each independently represents a hydrogen atom, a halogen atom, an alkyl group or an aryl group.)

【００７０】[0070]

【化１３】 [Chemical 13]

【００７１】（式中、Ｒ₂₁〜Ｒ₂₈はそれぞれ独立した水
素原子、ハロゲン原子、各々置換若しくは無置換の炭素
数１〜10アルキル基、シクロアルキル基、又はアリール
基を表す。）(In the formula, R _{21 to} R ₂₈ each independently represent a hydrogen atom, a halogen atom, a substituted or unsubstituted C 1-10 alkyl group, a cycloalkyl group, or an aryl group.)

【００７２】[0072]

【化１４】 Embedded image

【００７３】（式中、Ｒ₃₁〜Ｒ₄₆はそれぞれ独立して水
素原子、ハロゲン原子、各々置換、無置換アルキル基も
しくはアリール基を表し、ｋおよびｍは正の整数であっ
て、ｋ／ｍが１〜10になるように選択される。） なお前記一般式で示される構造単位を有するポリカーボ
ネート樹脂は好ましくは重量平均分子量30,000以上のも
のとされる。(In the formula, R _{31 to} R ₄₆ each independently represent a hydrogen atom, a halogen atom, a substituted or unsubstituted alkyl group or an aryl group, and k and m are positive integers and k / m Is selected to be 1 to 10.) The polycarbonate resin having the structural unit represented by the general formula is preferably one having a weight average molecular weight of 30,000 or more.

【００７４】次に、前記各層を形成する際に用いられる
溶媒又は分散媒としては、n-ブチルアミン、ジエチルア
ミン、エチレンジアミン、イソプロパノールアミン、ト
リエタノールアミン、トリエチレンジアミン、N,N-ジメ
チルホルムアミド、アセトン、メチルエチルケトン、メ
チルイソプロピルケトン、シクロヘキサノン、ベンゼ
ン、トルエン、キシレン、クロロホルム、ジクロロメタ
ン、1,2-ジクロロエタン、1,2-ジクロロプロパン、1,1,
2-トリクロロエタン、1,1,1-トリクロロエタン、トリク
ロロエチレン、テトラクロロエタン、テトラヒドロフラ
ン、ジオキサン、メタノール、エタノール、イソプロピ
ナール、酢酸エチル、酢酸ブチル、ジメチルスルホキシ
ド、メチルセロソルブ等が挙げられる。本発明はこれら
に限定されるものではないが、ケトン系溶媒を用いた場
合に感度、繰り返し使用時に電位変化等が更に良好とな
る。また、これらの溶媒は単独或いは２種以上の混合溶
媒として用いることもできる。Next, as a solvent or a dispersion medium used in forming each of the layers, n-butylamine, diethylamine, ethylenediamine, isopropanolamine, triethanolamine, triethylenediamine, N, N-dimethylformamide, acetone, methylethylketone , Methyl isopropyl ketone, cyclohexanone, benzene, toluene, xylene, chloroform, dichloromethane, 1,2-dichloroethane, 1,2-dichloropropane, 1,1,
Examples thereof include 2-trichloroethane, 1,1,1-trichloroethane, trichloroethylene, tetrachloroethane, tetrahydrofuran, dioxane, methanol, ethanol, isopropinal, ethyl acetate, butyl acetate, dimethyl sulfoxide, and methyl cellosolve. The present invention is not limited to these, but when a ketone solvent is used, the sensitivity and potential change during repeated use are further improved. Further, these solvents can be used alone or as a mixed solvent of two or more kinds.

【００７５】又、本発明において、基体と電荷発生層の
間に必要に応じて中間層を設けることが出来る。前記中
間層は接着層又はブロッキング層等として機能するもの
で、上記バインダ樹脂の外に、例えばポリビニルアルコ
ール、エチルセルロース、カルボキシメチルセルロー
ス、塩化ビニル-酢酸ビニル共重合体、塩化ビニル-酢酸
ビニル-無水マレイン酸共重合体、カゼイン、アルコー
ル可溶性ナイロン、澱粉等が用いられる。Further, in the present invention, an intermediate layer may be provided between the substrate and the charge generating layer, if necessary. The intermediate layer functions as an adhesive layer or a blocking layer, and in addition to the binder resin, for example, polyvinyl alcohol, ethyl cellulose, carboxymethyl cellulose, vinyl chloride-vinyl acetate copolymer, vinyl chloride-vinyl acetate-maleic anhydride. Copolymers, casein, alcohol-soluble nylon, starch and the like are used.

【００７６】以下、本発明の電子写真感光体の層構成を
図３により説明する。The layer structure of the electrophotographic photosensitive member of the present invention will be described below with reference to FIG.

【００７７】図３（イ）は導電性支持体１上に中間層２
を介してＣＧＭを主成分とする電荷発生層（ＣＧＬ）
４、ＣＴＭを主成分とする第１の電荷輸送層（ＣＴＬ）
であるＣＴＬ３及びバインダー樹脂中に前記無機粒子或
いは有機粒子を第２のＣＴＬであるＣＴＬ５とをこの順
に積層して成る感光層６を有する感光体である。又図３
（ロ）は導電性支持体１上に中間層２を介して前記ＣＧ
Ｌ４及び前記無機粒子或いは有機粒子を含有するＣＴＬ
３をこの順に積層して成る感光層６を有する感光体であ
る。又図３（ハ）は導電性支持体１上に中間層２を介し
てＣＧＭとＣＴＭとを共に含有し、かつ前記無機粒子、
或いは有機粒子が含有された単層構成の感光層６を有す
る感光体である。又図３（ニ）は導電性支持体１上に前
記ＣＴＬ３及び前記無機粒子或いは有機粒子とを含有す
るＣＧＬ４をこの順に積層して成る感光層６を有する感
光体である。FIG. 3A shows an intermediate layer 2 on the conductive support 1.
Charge generation layer (CGL) whose main component is CGM
4. First charge transport layer (CTL) mainly composed of CTM
And a photosensitive layer 6 formed by laminating the above-mentioned inorganic particles or organic particles in a binder resin and CTL5 as a second CTL in this order. See also Figure 3
(B) is the CG on the conductive support 1 with the intermediate layer 2 interposed therebetween.
CTL containing L4 and the aforementioned inorganic particles or organic particles
3 is a photoreceptor having a photosensitive layer 6 formed by laminating 3 in this order. In addition, FIG. 3C shows that both CGM and CTM are contained on the conductive support 1 through the intermediate layer 2, and the inorganic particles,
Alternatively, it is a photoreceptor having a single-layer photosensitive layer 6 containing organic particles. Further, FIG. 3D shows a photosensitive member having a photosensitive layer 6 formed by laminating the CTL 3 and the CGL 4 containing the inorganic particles or the organic particles in this order on the conductive support 1.

【００７８】なお前記図３（イ）のＣＴＬ５、図３
（ロ）のＣＴＬ３、図３（ハ）の感光層６及び図３
（ニ）のＣＧＬ４は何れも本発明で言う最上層を形成す
るものであり、それぞれのバインダー樹脂に対する無機
粒子或いは有機粒子の量比は０．００１〜２．０とされ
る。The CTL5 shown in FIG.
(B) CTL3, photosensitive layer 6 of FIG. 3 (c), and FIG.
All of CGL4 of (d) form the uppermost layer in the present invention, and the amount ratio of the inorganic particles or the organic particles to each binder resin is 0.001 to 2.0.

【００７９】前記無機粒子のバインダー樹脂に対する量
比が０．００１より小さいと前記感光体の最上層の機械
的強度が不十分となり、又電子写真性能も劣化し易く、
２．０より大きいとクリーニング時、クリーニングブレ
ードの感光体に接する端面が摩耗、損傷してクリーニン
グ不良となると共に画像ボケが発生し易くなる。When the amount ratio of the inorganic particles to the binder resin is less than 0.001, the mechanical strength of the uppermost layer of the photoreceptor becomes insufficient and the electrophotographic performance is apt to deteriorate.
If it is larger than 2.0, the end surface of the cleaning blade in contact with the photosensitive member is worn or damaged during cleaning, resulting in poor cleaning and image blurring.

【００８０】又前記最上層に含有されるＣＴＭは、該最
上層が図３（イ）のＣＴＬ５又は図１（ニ）のＣＧＬ４
の場合は各層のバインダー樹脂に対して０．０１〜２．
０の量比で含有されるのが好ましく、前記ＣＴＭのバイ
ンダー樹脂に対する量比が０．０１より小さいと感光体
の繰り返し使用により残留電位の上昇や感度の低下を生
じ易く、２．０より大きいと、帯電電位低下、暗減衰の
増大及び感度低下を生じ易い。The CTM contained in the uppermost layer is the CTL5 in FIG. 3 (a) or the CGL4 in FIG. 1 (d).
In the case of 0.01 to 2.
It is preferable that the content of CTM is 0. When the ratio of CTM to the binder resin is less than 0.01, the residual potential and sensitivity are likely to increase due to repeated use of the photoconductor, and it is more than 2.0. As a result, a decrease in charging potential, an increase in dark decay, and a decrease in sensitivity are likely to occur.

【００８１】又前記図３（イ）のＣＴＬ５又は図３
（ニ）のＣＧＬ４に含有されるＣＴＭは下層のＣＴＬ３
のＣＴＭと同じでも異なってもよい。Further, the CTL5 of FIG.
CTM contained in CGL4 in (d) is CTL3 in the lower layer
CTM may be the same or different.

【００８２】なお前記最上層が図３（ロ）のＣＴＬ３又
は図３（ハ）の感光層６の場合は、既に所定量のＣＴＭ
が含有されているので、特に添加する必要はない。If the uppermost layer is the CTL 3 in FIG. 3B or the photosensitive layer 6 in FIG. 3C, a predetermined amount of CTM has already been added.
, It does not need to be added.

【００８３】又、図３（イ）のＣＴＬ５からＣＴＭを除
いたいわゆる保護層がある層構成であってもよい。又、
図３（ハ）や（ニ）の感光層６の中に粒子を含む、又
は、図３（ハ）や（ニ）の感光層６の上に粒子を含む保
護層があってもよい。A layer structure having a so-called protective layer obtained by removing CTM from the CTL 5 in FIG. 3A may be used. or,
There may be particles in the photosensitive layer 6 of FIGS. 3C and 3D, or there may be a protective layer containing particles on the photosensitive layer 6 of FIGS. 3C and 3D.

【００８４】本発明に係る感光体は、複写機、レーザー
プリンター、ＬＥＤプリンター、液晶シャッター式プリ
ンター等の電子写真装置一般に適用し得るものである
が、更には電子写真技術を応用したディスプレイ、記
録、軽印刷、製版、ファクシミリ等の装置にも広く適用
し得るものである。The photoconductor according to the present invention can be applied to general electrophotographic apparatuses such as copying machines, laser printers, LED printers and liquid crystal shutter printers. It can be widely applied to devices such as light printing, plate making, and facsimile.

【００８５】図４は本発明の電子写真感光体が組み込ま
れ電子写真装置の一例を示すデジタルカラー複写機の断
面図である。図中１０は感光体ドラムで矢印方向（時計
方向）に回転駆動され、帯電器１２により一様の帯電が
付与される。FIG. 4 is a sectional view of a digital color copying machine showing an example of an electrophotographic apparatus incorporating the electrophotographic photosensitive member of the present invention. In the figure, reference numeral 10 denotes a photosensitive drum which is rotationally driven in the direction of the arrow (clockwise), and is uniformly charged by the charger 12.

【００８６】前記感光体ドラム１０への一様帯電後、像
露光手段１３により画像信号に基づく像露光が行われ
る。前記像露光手段１３では、原稿走査光学系１３３に
より読み取られた画像信号により、図示しないレーザー
光源からのレーザービームを変調し、得られた変調レー
ザービームを高速回転するポリゴンミラー１３１により
前記感光体ドラム１０上を主走査し、かつ該感光体ドラ
ムの回転により副走査して、該感光体ドラム１０上に静
電潜像が形成される。After the photosensitive drum 10 is uniformly charged, the image exposing means 13 performs image exposure based on the image signal. In the image exposure means 13, the laser beam from a laser light source (not shown) is modulated by the image signal read by the document scanning optical system 133, and the obtained modulated laser beam is rotated at a high speed by the polygon mirror 131, and the photosensitive drum is rotated. An electrostatic latent image is formed on the photosensitive drum 10 by performing main scanning on the photosensitive drum 10 and sub-scanning by rotation of the photosensitive drum.

【００８７】まず感光体ドラムの１回転目に、前記原稿
走査光学系１３３によりＹ画像信号が読み取られ、該Ｙ
画像信号により変調されたレーザービームを用いて前記
感光体ドラム１０上に像露光して静電潜像を形成し、該
潜像はＹトナーを含むＹ現像剤が充填された現像器１４
Ｙにより現像され、前記感光体ドラム１０上にＹトナー
像が形成される。First, at the first rotation of the photosensitive drum, the Y image signal is read by the original scanning optical system 133, and the Y image signal is read.
An electrostatic latent image is formed by exposing the photosensitive drum 10 with a laser beam modulated by an image signal to form an electrostatic latent image, and the latent image is filled with a Y developer containing Y toner.
After being developed by Y, a Y toner image is formed on the photosensitive drum 10.

【００８８】次に前記感光体ドラム１０の２回転目に、
マゼンタ（Ｍ）画像信号が読み取られ、再帯電後の前記
感光体ドラム１０上に前記Ｍ画像信号に基づくレーザー
像露光が行われて静電潜像が形成され、Ｍトナーを含む
Ｍ現像剤が充填された現像器１４Ｍにより現像されて、
前記感光体ドラム１０上に前記Ｙトナー像に重ね合わせ
てＭトナー像が形成される。Next, in the second rotation of the photosensitive drum 10,
A magenta (M) image signal is read, laser image exposure based on the M image signal is performed on the photosensitive drum 10 after recharging, an electrostatic latent image is formed, and an M developer containing M toner is generated. It is developed by the filled developing device 14M,
An M toner image is formed on the photosensitive drum 10 by superimposing it on the Y toner image.

【００８９】以後同様にして感光体ドラム１０の３回転
目及び４回転目において、シアン（Ｃ）画像信号及び黒
（Ｋ）画像信号に基づく像露光が行われ、かつＣ現像剤
を収容した現像器１４Ｃ及びＫ現像剤を収容した現像器
１４Ｋによりそれぞれ現像されて、前記感光体ドラム１
０上に、前記Ｙトナー像及びＹトナー像に重ね合わせて
Ｃトナー像及びＫトナー像が形成される。Thereafter, similarly, at the third and fourth rotations of the photosensitive drum 10, image exposure based on the cyan (C) image signal and the black (K) image signal is performed, and the development containing the C developer is performed. The developing device 14C and the developing device 14K containing the K developing agent, respectively, develop the photosensitive drum 1.
On C, the C toner image and the K toner image are formed in superposition with the Y toner image and the Y toner image.

【００９０】前記のようにして得られた感光体ドラム１
０上の４色トナー像から成るカラートナー像は給紙装置
１６から給送され、タイミングローラ１７によりタイミ
ングを合わせて搬送された転写材Ｐ上に転写ローラ１８
の作用で一括転写され、次いで前記カラートナー像が転
写された転写材Ｐは分離ブラシにより除電されることに
より、前記感光体ドラム１０から分離され、定着装置２
０へ搬送され、熱ローラ２０１と加圧ローラ２０２との
圧接下に熱定着されてカラー画像が形成される。Photoreceptor drum 1 obtained as described above
A color toner image composed of four color toner images on the transfer roller 18 is fed from the paper feeding device 16 and is transferred onto the transfer material P by the timing roller 17 at the same timing.
The transfer material P on which the color toner images have been transferred is removed by the separating brush to be separated from the photoconductor drum 10, and the fixing device 2
The image is conveyed to 0 and is thermally fixed under pressure contact between the heat roller 201 and the pressure roller 202 to form a color image.

【００９１】転写後の感光体ドラム１０は除電器２３に
より除電された後、クリーニング装置２２の弾性クリー
ニングブレード２２１により清掃され、ＬＥＤ等の除電
ランプ（ＰＣＬ）１１により除電されて次の像形成に備
えられる。After the transfer, the photosensitive drum 10 is destaticized by the destaticizer 23, cleaned by the elastic cleaning blade 221 of the cleaning device 22, and decharged by the destaticizing lamp (PCL) 11 such as an LED to form the next image. Be prepared.

【００９２】なお２２２はトナーガイドローラであり、
該ガイドローラ及び前記弾性クリーニングブレードは不
使用時前記感光体ドラム１０から離間される。Numeral 222 is a toner guide roller,
The guide roller and the elastic cleaning blade are separated from the photosensitive drum 10 when not in use.

【００９３】又本発明の電子写真装置では、帯電器１
２、ＰＣＬ１１、クリーニング装置２２、除電器２３、
分離ブラシ１９、転写ローラ１８及び感光体ドラム１０
がカートリッチとしてユニット化して一体的に支持さ
れ、装置本体１００に着脱自在に装着されている。In the electrophotographic apparatus of the present invention, the charger 1
2, PCL 11, cleaning device 22, static eliminator 23,
Separation brush 19, transfer roller 18, and photosensitive drum 10
Is united as a cart rich and integrally supported, and is detachably attached to the apparatus main body 100.

【００９４】又前記潜像器１４Ｙ，１４Ｍ，１４Ｃ及び
１４Ｋに充填される現像剤はフェライトをコアとしてそ
のまわりに絶縁性樹脂をコーティングしたキャリアと、
ポリエステルを主材料として色に応じた顔料と荷電制御
剤、シリカ、酸化チタン等を加えたトナーとからなるも
ので、現像剤は層形成手段によって現像スリーブ141上
に100〜600μmの層厚（現像剤）に規制されて現像域へ
と搬送され、感光体ドラム10と現像スリーブ141との間
に直流或いは交流バイアス電圧をかけて現像が行われ
る。The developer filled in the latent imagers 14Y, 14M, 14C and 14K is a carrier having ferrite as a core and an insulating resin coated around the core.
It is composed of polyester as a main material, a pigment according to color, and a toner to which a charge control agent, silica, titanium oxide, etc. are added, and the developer has a layer thickness of 100 to 600 μm (developing layer on the developing sleeve 141 by a layer forming means. The developer is regulated by the agent) and conveyed to the developing area, and a DC or AC bias voltage is applied between the photosensitive drum 10 and the developing sleeve 141 to perform the development.

【００９５】なお前記説明では、デジタルカラー複写機
を説明したが、これをコンピューター、ファクシミリ、
その他の外部通信手段から画像信号を入力して、カラー
プリンターとして使用してもよく、又モノクロ画像信号
を入力してモノクロ複写機又はモノクロプリンターとし
て使用してもよい。In the above description, the digital color copying machine has been described, but it may be a computer, a facsimile,
An image signal may be input from other external communication means and used as a color printer, or a monochrome image signal may be input and used as a monochrome copying machine or a monochrome printer.

【００９６】前記本発明の感光体は該感光体上に各色ト
ナー像を形成する度に転写材上に転写し、該転写材上で
各色トナー像を重ね合わせてカラー画像を形成するタイ
プのカラー複写機又はカラープリンターに適用してもよ
い。The photoconductor of the present invention is a color type in which a toner image of each color is transferred onto a transfer material each time it is formed on the photoconductor, and the toner images of the respective colors are superposed on the transfer material to form a color image. It may be applied to a copying machine or a color printer.

【００９７】又感光体周縁に帯電器、露光器及び現像器
を複数組配置して１パスでカラー画像を形成するカラー
複写機又はカラープリンターに適用してもよい。Further, it may be applied to a color copying machine or a color printer in which a plurality of sets of charging devices, exposing devices and developing devices are arranged around the periphery of the photoconductor to form a color image in one pass.

【００９８】又本発明の感光体はアナログの白黒複写機
に適用できるのは勿論である。Further, it goes without saying that the photoconductor of the present invention can be applied to an analog monochrome copying machine.

【００９９】なお、前記図４のデジタルカラー複写機で
は、帯電器１２、ＰＣＬ１１、クリーニング装置２２、
除電器２３、分離ブラシ１９、転写ローラ１８及び感光
体ドラム等の像形成手段をユニット化しているが、感光
体と、他の少なくとも１つの像形成手段とをユニット化
するようにしてもよい。In the digital color copying machine shown in FIG. 4, the charger 12, the PCL 11, the cleaning device 22,
Although the image forming means such as the static eliminator 23, the separating brush 19, the transfer roller 18 and the photoconductor drum are unitized, the photoconductor and at least one other image forming unit may be unitized.

【０１００】本発明における「着脱自在」とは、ユーザ
ーサイドで容易にメンテナンスできる程度に取り外した
り清掃、交換が出来る事を意味する。The term "detachable" in the present invention means that the user can remove, clean, or replace the product so that the user can easily perform maintenance.

【０１０１】[0101]

【実施例】以下、実施例を挙げて本発明を詳細に説明す
るが、本発明の態様はこれに限定されない。The present invention will be described in detail below with reference to examples, but the embodiments of the present invention are not limited thereto.

【０１０２】《クリーニングブレードの作製》Ｋｏｎｉ
ｃａＵ−ＢＩＸ４０４５複写機を用い、弾性体の硬度，
ヤング率（ｋｇ／ｃｍ²），１００％モジュラス（ｋｇ
／ｃｍ²），３００％モジュラス（ｋｇ／ｃｍ²），引っ
張り強さ（ｋｇ／ｃｍ²），伸び（％），反発弾性
（％），引裂強さ（ｋｇ／ｃｍ²），永久伸び（％）、
圧接力（ｇｆ／ｃｍ）、自由長部の厚さ（ｔ）、自由長
（Ｌ）、Ｌ／ｔ比を変えてクリーニングブレードを表１
の如く設定した。<< Preparation of Cleaning Blade >> Koni
Using a caU-BIX4045 copier, the hardness of the elastic body,
Young's modulus (kg / cm ² ), 100% modulus (kg
/ Cm ² ), 300% modulus (kg / cm ² ), tensile strength (kg / cm ² ), elongation (%), impact resilience (%), tear strength (kg / cm ² ), permanent elongation (%) ),
Table 1 shows cleaning blades with different pressure contact forces (gf / cm), free length thickness (t), free length (L), and L / t ratio.
I set it like.

【０１０３】[0103]

【表１】 [Table 1]

【０１０４】《積層感光体試料の作製》 感光体１ アルミニウムドラム基体上に下記の層を順次積層し、感
光体１を作製した。<< Preparation of Laminated Photoreceptor Sample >> Photoreceptor 1 A photoreceptor 1 was prepared by sequentially laminating the following layers on an aluminum drum substrate.

【０１０５】 下引層（ＤＣＣ） ポリアミド樹脂（ＣＭ−８０００ 東レ社製） ３０ｇ メタノール １０００ｍｌ からなる液を基体上に乾燥後膜厚が０．２μｍになるよ
う塗布した。Undercoat layer (DCC) Polyamide resin (CM-8000, manufactured by Toray Industries, Inc.) 30 g A solution of 1000 ml of methanol was applied onto a substrate so that the film thickness after drying was 0.2 μm.

【０１０６】 電荷発生層（ＣＧＬ） ペリレン顔料（ＣＧＭ−１） ２５０ｇ ポリビニルブチラール（エスレックスＢＬ−Ｓ 積水化学社製） ５０ｇ メチルエチルケトン ６５００ｍｌ シクロヘキサン １５００ｍｌ 上記組成物をサンドミルを用いて２０時間分散した。こ
の液を用いて上記下引層上に浸漬塗布し、乾燥後膜厚が
０．５μｍになるようにした。Charge Generation Layer (CGL) Perylene Pigment (CGM-1) 250 g Polyvinyl butyral (S-lex BL-S Sekisui Chemical Co., Ltd.) 50 g Methyl ethyl ketone 6500 ml Cyclohexane 1500 ml The above composition was dispersed for 20 hours using a sand mill. This solution was applied onto the above-mentioned undercoat layer by dip coating, and the film thickness after drying was adjusted to 0.5 μm.

【０１０７】 電荷輸送層（ＣＴＬ） 電荷輸送物質（ＣＴＭ Ｔ−２） １６０ｇ ポリカーボネート（パンライトＴＳ−２０５０ 帝人化成社製）２４０ｇ シリコーンオイル（ＫＦ−５４ 信越化学社製） ０．４ｇ シリコーン粒子 ８０ｇ （トスパール１０５ 体積平均粒径０．５μｍ 東芝シリコーン社製） メチレンクロライド １７００ｍｌ 上記の溶解液を用いて、上記の電荷発生層上に浸漬塗布
して１００℃、６０分乾燥し、乾燥後膜厚が２８μｍに
なるようにした。Charge Transport Layer (CTL) Charge Transport Material (CTM T-2) 160 g Polycarbonate (Panlite TS-2050 manufactured by Teijin Chemicals Ltd.) 240 g Silicone oil (KF-54 manufactured by Shin-Etsu Chemical Co., Ltd.) 0.4 g Silicone particles 80 g ( TOSPEARL 105 Volume average particle diameter 0.5 μm, manufactured by Toshiba Silicone Co., Ltd.) Methylene chloride 1700 ml. The above solution was applied onto the above charge generation layer by dip coating and dried at 100 ° C. for 60 minutes, and the film thickness after drying was 28 μm. I tried to become.

【０１０８】[0108]

【化１５】 [Chemical 15]

【０１０９】感光体２ 感光体１の電荷輸送層中のシリコーン粒子の代わりに酸
化チタン（ルチル型０．５μｍ）を用いた以外感光体１
と同様に作製した。Photosensitive member 2 Photosensitive member 1 except that titanium oxide (rutile type 0.5 μm) was used in place of the silicone particles in the charge transport layer of photosensitive member 1.
Was prepared in the same manner as in.

【０１１０】感光体３ 感光体１の電荷輸送層中のシリコーン粒子の代わりに酸
化アルミニウム（０．２μｍ）を用いた以外感光体１と
同様に作製した。Photoreceptor 3 Photoreceptor 1 was prepared in the same manner as photoreceptor 1 except that aluminum oxide (0.2 μm) was used instead of the silicone particles in the charge transport layer of photoreceptor 1.

【０１１１】感光体４ アルミニウムドラム基体上に下記の層を順次積層し、感
光体４を作製した。Photoreceptor 4 A photoreceptor 4 was prepared by sequentially laminating the following layers on an aluminum drum substrate.

【０１１２】 下引層（ＤＣＣ） メトキシメチル化ナイロン ２ｇ （ダイアミドＸ−１８７４Ｍ ダイセル化学社製） メタノール ８００ｍｌ ブタノール ２００ｍｌ からなる液を基体上に乾燥後膜厚が０．２μｍになるよ
う塗布した。Undercoat layer (DCC) 2 g of methoxymethylated nylon (Daiamide X-1874M manufactured by Daicel Chemical Industries, Ltd.) A solution of 800 ml of methanol and 200 ml of butanol was applied onto a substrate so as to have a thickness of 0.2 μm after drying.

【０１１３】 電荷発生層（ＣＧＬ） フルオレノン系ビスアゾ化合物（ＣＧＭ−２） ２５ｇ ポリビニルブチラール（エスレックスＫＰ−II 積水化学社製） １０ｇ メチルイソプロピルケトン １４３０ｍｌ 上記組成物をサンドミルを用いて３０時間分散した。こ
の液を用いて上記下引層上に浸漬塗布し、乾燥後膜厚が
０．５μｍになるようにした。Charge Generation Layer (CGL) Fluorenone Bisazo Compound (CGM-2) 25 g Polyvinyl butyral (S-Rex KP-II Sekisui Chemical Co., Ltd.) 10 g Methyl isopropyl ketone 1430 ml The above composition was dispersed for 30 hours using a sand mill. This solution was applied onto the above-mentioned undercoat layer by dip coating, and the film thickness after drying was adjusted to 0.5 μm.

【０１１４】 第一電荷輸送層（ＣＴＬ） 電荷輸送物質（ＣＴＭ Ｔ−１） ７５ｇ ポリカーボネート（Ｚ−２００ 三菱瓦斯化学社製） ２４０ｇ シリコーンオイル（ＫＦ−５４ 信越化学社製） ０．０５ｇ １，２−ジクロロエタン ５００ｍｌ 上記の溶解液を用いて、上記の電荷発生層上に浸漬塗布
して１００℃、６０分乾燥し、乾燥後膜厚が２０μｍに
なるようにし第一電荷輸送層を形成した。First charge transport layer (CTL) Charge transport material (CTM T-1) 75 g Polycarbonate (Z-200 manufactured by Mitsubishi Gas Chemical Co., Inc.) 240 g Silicone oil (KF-54 manufactured by Shin-Etsu Chemical Co., Ltd.) 0.05 g 1,2 -Dichloroethane 500 ml The above-mentioned solution was applied onto the above charge generation layer by dip coating and dried at 100 ° C for 60 minutes to form a first charge transport layer having a thickness of 20 µm after drying.

【０１１５】 第二電荷輸送層（ＣＴＬ） 電荷輸送物質（ＣＴＭ Ｔ−１） ３３．３ｇ ポリカーボネート（Ｚ−２００ 三菱瓦斯化学社製） ５０ｇ テトラフルオロエチレン粒子 （ルブロンＬ−５ ダイキン工業社製） ４０ｇ １，２−ジクロロエタン １０００ｍｌ 上記の溶解分散液を用いて、上記の第一電荷輸送層上に
円形量規制型塗布機にて塗布し、１００℃、６０分乾燥
し、乾燥後膜厚が５μｍになるようにし第二電荷輸送層
を形成した。Second charge transport layer (CTL) Charge transport material (CTM T-1) 33.3 g Polycarbonate (Z-200 manufactured by Mitsubishi Gas Chemical Co., Inc.) 50 g Tetrafluoroethylene particles (Lubron L-5 manufactured by Daikin Industries, Ltd.) 40 g 1,2-Dichloroethane 1000 ml Using the above dissolution dispersion, it was applied on the above first charge transport layer by a circular amount control type coating machine and dried at 100 ° C. for 60 minutes, and the film thickness after drying was 5 μm. And a second charge transport layer was formed.

【０１１６】[0116]

【化１６】 Embedded image

【０１１７】感光体５ 感光体４のルブロンＬ−５の代わりに合成したテトラフ
ルオロエチレン粒子（０．２μｍ）を用いた以外感光体
４と同様に作製した。Photosensitive member 5 Photosensitive member 4 was prepared in the same manner as photosensitive member 4 except that synthesized tetrafluoroethylene particles (0.2 μm) were used instead of Lubron L-5.

【０１１８】感光体６ 感光体４のルブロンＬ−５の代わりに合成したテトラフ
ルオロエチレン粒子（０．５μｍ）を用いた以外感光体
４と同様に作製した。Photosensitive member 6 Photosensitive member 4 was prepared in the same manner as photosensitive member 4 except that synthesized tetrafluoroethylene particles (0.5 μm) were used instead of Lubron L-5.

【０１１９】感光体７ 感光体４のルブロンＬ−５の代わりに合成したテトラフ
ルオロエチレン粒子（０．８μｍ）を用いた以外感光体
４と同様に作製した。Photosensitive member 7 Photosensitive member 4 was prepared in the same manner as photosensitive member 4 except that synthesized tetrafluoroethylene particles (0.8 μm) were used instead of Lubron L-5.

【０１２０】感光体８ 感光体４の電荷輸送物質（Ｔ−１）の代わりにＴ−２０
を用いた以外感光体４と同様に作製した。Photoreceptor 8 T-20 instead of the charge transport material (T-1) of photoreceptor 4
Was prepared in the same manner as the photoconductor 4 except that was used.

【０１２１】感光体９ アルミニウムドラム基体上に下記の層を順次積層し、感
光体９を作製した。Photoreceptor 9 A photoreceptor 9 was prepared by successively laminating the following layers on an aluminum drum substrate.

【０１２２】 下引層（ＤＣＣ） ポリアミド樹脂（ＣＭ−８０００ 東レ社製） ３０ｇ メタノール １０００ｍｌ からなる液を基体上に乾燥後膜厚が０．２μｍになるよ
う塗布した。Undercoat layer (DCC) Polyamide resin (CM-8000, manufactured by Toray Industries, Inc.) 30 g A solution of 1000 ml of methanol was applied onto a substrate so that the film thickness after drying was 0.2 μm.

【０１２３】 電荷発生層（ＣＧＬ） Ｙ型チタニルフタロシアニン顔料（ＣＧＭ−３） １０ｇ ポリビニルブチラール（ＸＹＨＬ ユニオン・カーバイト社製） １０ｇ メチルエチルケトン １０００ｍｌ 上記組成物をサンドミルを用いて２０時間分散した。こ
の液を用いて上記下引層上に浸漬塗布し、乾燥後膜厚が
０．５μｍになるようにした。Charge Generation Layer (CGL) Y-type titanyl phthalocyanine pigment (CGM-3) 10 g Polyvinyl butyral (XYHL Union Carbide Co.) 10 g Methyl ethyl ketone 1000 ml The above composition was dispersed for 20 hours using a sand mill. This solution was applied onto the above-mentioned undercoat layer by dip coating, and the film thickness after drying was adjusted to 0.5 μm.

【０１２４】[0124]

【化１７】 [Chemical 17]

【０１２５】 第一電荷輸送層（ＣＴＬ） 電荷輸送物質（ＣＴＭ Ｔ−１１） ３０ｇ ポリカーボネート（Ｚ−２００ 三菱瓦斯化学社製） ４０ｇ シリコーンオイル（ＫＦ−５４ 信越化学社製） ０．０１ｇ １，２−ジクロロエタン ２００ｍｌ 上記の溶解液を用いて、上記の電荷発生層上に浸漬塗布
して１００℃、６０分乾燥し、乾燥後膜厚が２０μｍに
なるよう第一電荷輸送層を形成した。First charge transport layer (CTL) Charge transport material (CTM T-11) 30 g Polycarbonate (Z-200 manufactured by Mitsubishi Gas Chemical Co., Inc.) 40 g Silicone oil (KF-54 manufactured by Shin-Etsu Chemical Co., Ltd.) 0.01 g 1,2 -Dichloroethane 200 ml Using the above-mentioned solution, the above charge generation layer was applied by dip coating and dried at 100 ° C for 60 minutes to form a first charge transport layer having a thickness of 20 µm after drying.

【０１２６】 第二電荷輸送層（ＣＴＬ） 電荷輸送物質（ＣＴＭ Ｔ−１１） ３．０ｇ ポリカーボネート（Ｚ−２００ 三菱瓦斯化学社製） ５０ｇ シリカ粒子（ＳＯ−Ｃ１ アドマチック社製 ０．２μｍ） １０ｇ １，２−ジクロロエタン １０００ｍｌ 上記の溶解分散液を用いて、上記の第一電荷輸送層上に
円形量規制型塗布機にて塗布し、１００℃、６０分乾燥
し、乾燥後膜厚が５μｍになるようにし第二電荷輸送層
を形成した。Second charge transport layer (CTL) Charge transport material (CTM T-11) 3.0 g Polycarbonate (Z-200 manufactured by Mitsubishi Gas Chemical Co., Inc.) 50 g Silica particles (SO-C1 manufactured by Admatic Co., Ltd. 0.2 μm) 10 g 1 , 2-Dichloroethane 1000 ml Using the above-mentioned dissolution dispersion, it is applied on the above-mentioned first charge transport layer by a circular amount control type coating machine and dried at 100 ° C for 60 minutes to give a film thickness of 5 µm after drying. Thus, the second charge transport layer was formed.

【０１２７】感光体１０ 感光体９のシリカ粒子の代わりにシリカ粒子（ＳＯ−Ｃ
２ アドマチック社製０．５μｍ）を用いた以外感光体
９と同様に作製した。Photoreceptor 10 Instead of the silica particles of the photoreceptor 9, silica particles (SO-C
2 was prepared in the same manner as the photoconductor 9 except that 0.5 μm manufactured by Admatic Co., Ltd. was used.

【０１２８】感光体１１ 感光体９のシリカ粒子の代わりに疎水化されたシリカ粒
子（アエロジルＲ９７２ 日本アエロジル社製 ０．０
１６μｍ）を用いた以外感光体９と同様に作製した。Photoreceptor 11 Hydrophobized silica particles (Aerosil R972 manufactured by Nippon Aerosil Co., Ltd. 0.0 instead of the silica particles of the photoreceptor 9)
16 μm) was used and manufactured in the same manner as the photoconductor 9.

【０１２９】感光体１２ 感光体９のシリカ粒子の代わりに、トリメチルシリルメ
トキシシランから成るシランカップリング剤で疎水化さ
れたシリカ粒子（ＳＯ−Ｃ１ アドマチック社製 ０．
２μｍ）を用いた以外感光体９と同様に作製した。Photoreceptor 12 Instead of the silica particles of the photoreceptor 9, silica particles hydrophobized with a silane coupling agent composed of trimethylsilylmethoxysilane (SO-C1 manufactured by Admatic Co., Ltd.
2 μm) was used, and the same procedure as for the photoconductor 9 was performed.

【０１３０】感光体１３ アルミニウムドラム基体上に下記の層を順次積層し、感
光体１３を作製した。Photoreceptor 13 A photoreceptor 13 was prepared by sequentially laminating the following layers on an aluminum drum substrate.

【０１３１】 下引層（ＤＣＣ） 部分メトキシメチル化６ナイロン ２ｇ （ラッカマイド５００３ 大日本化学工業社製） メタノール ８００ｍｌ １−ブタノール ２００ｍｌ からなる液を基体上に乾燥後膜厚が０．３μｍになるよ
う塗布した。Undercoat layer (DCC) Partially methoxymethylated 6-nylon 2 g (Laccamide 5003, manufactured by Dainippon Chemical Industry Co., Ltd.) Methanol 800 ml 1-Butanol 200 ml A solution was dried on a substrate so that the film thickness would be 0.3 μm. Applied.

【０１３２】 電荷発生層（ＣＧＬ） 臭化アンスアンスロン（ＣＧＭ−４） ６０ｇ ポリビニルブチラール（エスレックスＢＸ−１ 積水化学社製）１５ｇ １，２−ジクロロエタン １０００ｍｌ 上記組成物をサンドミルを用いて５０時間分散した。こ
の液を用いて上記下引層上に浸漬塗布し、乾燥後膜厚が
１μｍになるようにした。Charge Generation Layer (CGL) Anthanthrone Bromide (CGM-4) 60 g Polyvinyl Butyral (S-Rex BX-1 Sekisui Chemical Co., Ltd.) 15 g 1,2-Dichloroethane 1000 ml The above composition was dispersed for 50 hours using a sand mill. did. This solution was applied onto the above-mentioned undercoat layer by dip coating, and dried to a film thickness of 1 μm.

【０１３３】 第一電荷輸送層（ＣＴＬ） 電荷輸送物質（ＣＴＭ Ｔ−１４） １５０ｇ ポリカーボネート（Ｚ−２００ 三菱瓦斯化学社製） ２００ｇ シリコーンオイル（ＫＦ−５４ 信越化学社製） ０．０６５ｇ １，２−ジクロロエタン １０００ｍｌ 上記の溶解液を用いて、上記の電荷発生層上に浸漬塗布
して１００℃、６０分乾燥し、乾燥後膜厚が２０μｍに
なるようにし第一電荷輸送層を形成した。First charge transport layer (CTL) Charge transport material (CTM T-14) 150 g Polycarbonate (Z-200 manufactured by Mitsubishi Gas Chemical Co., Inc.) 200 g Silicone oil (KF-54 manufactured by Shin-Etsu Chemical Co., Ltd.) 0.065 g 1,2 -Dichloroethane 1000 ml The above-mentioned solution was applied onto the above charge generation layer by dip coating and dried at 100 ° C for 60 minutes to form a first charge transport layer having a thickness of 20 µm after drying.

【０１３４】 第二電荷輸送層（ＣＴＬ） 電荷輸送物質（ＣＴＭ Ｔ−１４） ３０ｇ ポリカーボネート（Ｚ−２００ 三菱瓦斯化学社製） ６０ｇ シリカ粒子（ＳＯ−Ｃ１ アドマチック社製 ０．２μｍ） １２ｇ １，２−ジクロロエタン １０００ｍｌ 上記の溶解分散液を用いて、上記の第一電荷輸送層上に
円形量規制型塗布機にて塗布し、１００℃、６０分乾燥
し、乾燥後膜厚が５μｍになるようにし第二電荷輸送層
を形成した。Second charge transport layer (CTL) Charge transport material (CTM T-14) 30 g Polycarbonate (Z-200 manufactured by Mitsubishi Gas Chemical Co., Inc.) 60 g Silica particles (SO-C1 0.2 μm manufactured by Admatic Co.) 12 g 1,2 -Dichloroethane 1000 ml Using the above-mentioned dissolved dispersion liquid, it is applied on the above-mentioned first charge transport layer by a circular amount control type coating machine, dried at 100 ° C for 60 minutes, and dried to a film thickness of 5 µm. A second charge transport layer was formed.

【０１３５】比較感光体１ 感光体１の電荷輸送層からトスパール１０５を除いた以
外感光体１と同様に作製した。Comparative Photoreceptor 1 Manufactured in the same manner as in Photoreceptor 1 except that Tospearl 105 was omitted from the charge transport layer of Photoreceptor 1.

【０１３６】比較感光体２ 感光体４の第二電荷輸送層からルブロンＬ−５を除いた
以外感光体４と同様に作製した。Comparative Photoreceptor 2 Manufactured in the same manner as in Photoreceptor 4 except that Lubron L-5 was omitted from the second charge transport layer of Photoreceptor 4.

【０１３７】比較感光体３ 感光体９の第二電荷輸送層からシリカ粒子（ＳＯ−Ｃ
１）を除いた以外感光体９と同様に作製した。Comparative Photoreceptor 3 Silica particles (SO-C
A photoconductor 9 was prepared in the same manner as the photoconductor 9 except that 1) was omitted.

【０１３８】比較感光体４ 感光体１３の第二電荷輸送層からシリカ粒子（ＳＯ−Ｃ
１）を除いた以外感光体１３と同様に作製した。Comparative Photoreceptor 4 From the second charge transport layer of photoreceptor 13 to silica particles (SO-C
The photoconductor 13 was manufactured in the same manner as the photoconductor 13 except that 1) was omitted.

【０１３９】特性評価 ＫｏｎｉｃａＵ−ＢＩＸ４０４５複写機（コニカ社製
有機感光体、クリーニングブレード感光体へカウンター
方向突き当て、クリーニング器・感光体・現像器をユニ
ット化）を用いた。表１に示す如くクリーニングブレー
ドの物性、設置条件を変えて作成したクリーニングブレ
ード試料と、感光体１〜１３及び比較感光体１〜４を表
２の如く組み合わせて１０万コピーの実写テストを行い
表２に１０万コピー後のブレード物性の変化を示す。Characteristic Evaluation Konica U-BIX 4045 Copier (Konica Corporation)
The cleaning device, the photoconductor, and the developing device were unitized by abutting against the organic photoconductor and the cleaning blade photoconductor in the counter direction. As shown in Table 1, the cleaning blade samples prepared by changing the physical properties and installation conditions of the cleaning blade, the photoconductors 1 to 13 and the comparative photoconductors 1 to 4 were combined as shown in Table 2, and a 100,000-copy actual copying test was conducted. 2 shows changes in the physical properties of the blade after 100,000 copies.

【０１４０】評価項目と基準 １．ブレードめくれ … 初期摺動時の反転の状況を複
写機本体から上記ユニットを取り出して観察 ２．感 光 体 傷 … １０万枚実写通紙後の適正濃
度の実写テストで感光体ドラム円周方向の黒線がベタ白
部に有るかどうか観察 ３．クリーニング性 … クリーニング後の感光体面上
の残留トナーの有無を肉眼にて観察 ４．ブレード耐久性 … １０万枚実写通紙後のブレー
ドエッヂ部の摩耗を観察５．画質 … 標準
チャートの実写プリントグレードを観察 ６．感光体層の減耗量… 初期と１０万枚実写通紙後の
感光体の構成層厚の差を膜厚計で測定 結果を表２に示す。Evaluation items and criteria 1. Blade flip-up ... Observation of the state of reversal during initial sliding by removing the above unit from the copier body. Scratch on photosensitizer: Observe whether there is a black line in the solid white area in the circumferential direction of the photoconductor drum in a real-image test with an appropriate density after 100,000 sheets have been actually printed. Cleanability ... Visual observation of the presence or absence of residual toner on the surface of the photoconductor after cleaning. Blade durability: Observes the wear of the blade edge after 100,000 sheets have been printed. Image quality: Observe the actual print grade of the standard chart. Amount of depleted photoreceptor layer: Table 2 shows the results of measuring the difference in the thickness of the constituent layers of the photoreceptor between the initial stage and the actual sheet after 100,000 sheets have been passed.

【０１４１】 ○： 実用的に問題なし △： 実用にはやや問題あり ×： 実用上きわめて問題◯: No problem in practical use Δ: Some problem in practical use ×: Extremely problematic in practical use

【０１４２】[0142]

【表２】 [Table 2]

【０１４３】本発明のブレードは圧接力、自由長、厚
さ、Ｌ／ｔ比が規定内にあり、かつ各力学的特性値が定
めた範囲内にあるものを用いることにより、ブレードめ
くれがなく、感光体表面を傷付けず、クリーニング性が
良好であり、ブレードの耐久性及び作動性に勝る。しか
も、感光層の耐減耗性、画質が良いことがわかった。As the blade of the present invention, a blade having a pressure contact force, a free length, a thickness and an L / t ratio within the stipulated range and each mechanical characteristic value within the defined range is used to prevent the blade from being turned over. The surface of the photoconductor is not damaged, the cleaning property is good, and the durability and operability of the blade are excellent. Moreover, it was found that the photosensitive layer had good wear resistance and good image quality.

【０１４４】[0144]

【発明の効果】本発明により、クリーニングブレードの
物性値及び画像形成装置本体への取り付け条件が所定の
範囲に入っているか細かくチェックする必要はあるが、
高耐久化された有機感光体との組み合わせにおいても信
頼性の高い、優れたクリーニングブレード及びそれを用
いたクリーニング装置、ユニットを提供することが出来
る。According to the present invention, it is necessary to carefully check whether the physical property values of the cleaning blade and the conditions for attaching the cleaning blade to the main body of the image forming apparatus are within a predetermined range.
It is possible to provide an excellent cleaning blade that is highly reliable even in combination with a highly durable organic photoreceptor, and a cleaning device and a unit using the cleaning blade.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明のクリーニングブレード形状例の概要断
面図。FIG. 1 is a schematic cross-sectional view of a cleaning blade shape example of the present invention.

【図２】本発明のクリーニングブレード取付け方、自由
長とその部分の厚さを説明する断面図。FIG. 2 is a cross-sectional view illustrating how to attach the cleaning blade of the present invention, the free length, and the thickness of that portion.

【図３】本発明に係わる感光体の層構成を示す断面図。FIG. 3 is a cross-sectional view showing a layer structure of a photoreceptor according to the present invention.

【図４】本発明に係わる電子写真画像形成装置の断面
図。FIG. 4 is a sectional view of an electrophotographic image forming apparatus according to the present invention.

【符号の説明】[Explanation of symbols]

１ 導電性支持体 ２ 中間層 ３ 第１電荷輸送層（ＣＴＬ） ４ 電荷発生層（ＣＧＬ） ５ 第二電荷輸送層（ＣＴＬ） ６ 感光層 １０ 感光体ドラム １２ スコロトロン帯電器 １３ 像露光手段 １４ 現像器 １７ 給紙ローラ １８ 転写ローラ １９ 分離ブラシ ２０ 定着装置 ２１ 排紙ローラ ２２ クリーニング装置 ３０ 像保持部部材（感光体ドラム）、帯電手段、現像
手段及びクリーニング手段を一体化されている着脱可能
なカートリッジ。1 Conductive Support 2 Intermediate Layer 3 First Charge Transport Layer (CTL) 4 Charge Generation Layer (CGL) 5 Second Charge Transport Layer (CTL) 6 Photosensitive Layer 10 Photoreceptor Drum 12 Scorotron Charger 13 Image Exposure Means 14 Development Device 17 Paper Feed Roller 18 Transfer Roller 19 Separation Brush 20 Fixing Device 21 Paper Ejection Roller 22 Cleaning Device 30 Image Retaining Member (Photoreceptor Drum), Charging Means, Developing Means, and Cleaning Means Removable Cartridge .

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 形成されたトナー像を転写材へ転写後の
有機感光体からなる像担持体表面に残留するトナー粉体
を清掃除去するクリーニング方法において、該クリーニ
ング方法がクリーニングブレードの一端を前記感光体に
圧接することにより行われ、且つ該ブレードの材質が弾
性体であり、該弾性体の硬度（ＪＩＳＡスケール）が５
０〜９０，ヤング率（ｋｇ／ｃｍ²）が４０〜９０，１
００％モジュラス（ｋｇ／ｃｍ²）が２０〜６５，３０
０％モジュラス（ｋｇ／ｃｍ²）が７０〜１５０，引っ
張り強さ（ｋｇ／ｃｍ²）が２４０〜５００，伸び
（％）が２９０〜５００，反発弾性（％）が３０〜７
０，引裂強さ（ｋｇ／ｃｍ²）が２５〜７５及び永久伸
び（％）が４．０以下であり、かつ前記ブレードの感光
体表面への圧接力を１０〜５０（ｇｆ／ｃｍ）の範囲に
設定した際、自由長部の厚さ（ｔ）を１〜３ｍｍ、ブレ
ードの自由長（Ｌ）を５〜１５ｍｍ及びＬ／ｔ比を２〜
８であることを特徴とするクリーニング方法。1. A cleaning method for cleaning and removing toner powder remaining on the surface of an image carrier made of an organic photoconductor after transferring a formed toner image onto a transfer material, wherein the cleaning method comprises: The blade is made of an elastic material, and the hardness (JISA scale) of the elastic material is 5
0-90, Young's modulus (kg / cm ² ) 40-90,1
00% modulus (kg / cm ² ) is 20 to 65,30
0% modulus (kg / cm ² ) 70 to 150, tensile strength (kg / cm ² ) 240 to 500, elongation (%) 290 to 500, impact resilience (%) 30 to 7
0, a tear strength (kg / cm ² ) of 25 to 75, a permanent elongation (%) of 4.0 or less, and a pressure contact force of the blade to the photoreceptor surface of 10 to 50 (gf / cm). When the range is set, the thickness (t) of the free length portion is 1 to 3 mm, the free length (L) of the blade is 5 to 15 mm, and the L / t ratio is 2 to
8. A cleaning method characterized by being 8. 【請求項２】 前記感光体の最表面層は無機粒子又は有
機粒子を含有することを特徴とする請求項１記載のクリ
ーニング方法。2. The cleaning method according to claim 1, wherein the outermost surface layer of the photoreceptor contains inorganic particles or organic particles. 【請求項３】 前記クリーニングブレードの材質がポリ
ウレタンゴム弾性体であることを特徴とする請求項１又
は２記載のクリーニング方法。3. The cleaning method according to claim 1, wherein the material of the cleaning blade is a polyurethane rubber elastic body. 【請求項４】 前記無機粒子が粒径０．０１〜１０μｍ
の金属酸化物であることを特徴とする請求項２記載のク
リーニング方法。4. The particle size of the inorganic particles is 0.01 to 10 μm.
3. The cleaning method according to claim 2, wherein the cleaning agent is the metal oxide. 【請求項５】 前記有機粒子が粒径０．０１〜１０μｍ
のフッ素又はケイ素含有樹脂であることを特徴とする請
求項２記載のクリーニング方法。5. The organic particles have a particle size of 0.01 to 10 μm.
The cleaning method according to claim 2, wherein the fluorine- or silicon-containing resin is used. 【請求項６】 帯電手段及び現像手段の少なくとも１つ
が有機感光体及びクリーニング手段を一体に支持してユ
ニットを形成し、装置本体に着脱自在の単一ユニットと
した装置ユニットにおいて、前記感光体は、その最表面
層に無機粒子又は有機粒子を含有し、並びに前記クリー
ニング手段は、其の一端を該感光体に圧接し、その材質
がポリウレタン弾性体であり、該ポリウレタン弾性体の
硬度（ＪＩＳＡスケール）が５０〜９０，ヤング率（ｋ
ｇ／ｃｍ²）が４０〜９０，１００％モジュラス（ｋｇ
／ｃｍ²）が２０〜６５，３００％モジュラス（ｋｇ／
ｃｍ²）が７０〜１５０，引っ張り強さ（ｋｇ／ｃｍ²）
が２４０〜５００，伸び（％）が２９０〜５００，反発
弾性（％）が３０〜７０，引裂強さ（ｋｇ／ｃｍ²）が
２５〜７５及び永久伸び（％）が４．０以下であり、か
つ前記ブレードの圧接力を１０〜５０（ｇｆ／ｃｍ）の
範囲に設定した際、自由長部の厚さ（ｔ）を１〜３ｍ
ｍ、ブレードの自由長（Ｌ）を５〜１５ｍｍ及びＬ／ｔ
比を２〜８であることを特徴とする装置ユニット。6. An apparatus unit in which at least one of a charging means and a developing means integrally supports an organic photoconductor and a cleaning means to form a unit, and which is a detachable single unit in an apparatus body, wherein the photoconductor is The outermost surface layer contains inorganic particles or organic particles, and the cleaning means presses one end of the cleaning means into contact with the photoconductor, and the material is a polyurethane elastic body, and the hardness of the polyurethane elastic body (JIS A scale ) Is 50 to 90, Young's modulus (k
g / cm ² ) is 40 to 90, 100% modulus (kg
/ Cm ² ) is 20 to 65,300% modulus (kg /
cm ² ) is 70 to 150, tensile strength (kg / cm ² )
Is 240 to 500, elongation (%) is 290 to 500, impact resilience (%) is 30 to 70, tear strength (kg / cm ² ) is 25 to 75, and permanent elongation (%) is 4.0 or less. And, when the pressure contact force of the blade is set in the range of 10 to 50 (gf / cm), the thickness (t) of the free length portion is 1 to 3 m.
m, the free length (L) of the blade is 5 to 15 mm and L / t
A device unit having a ratio of 2 to 8. 【請求項７】 最表面層に無機或いは有機粒子を含有す
る有機感光体からなる像担持体、像担持体を帯電する手
段及び転写後の像担持体上に残留するトナーをクリーニ
ングするクリーニング手段を備えた画像形成装置におい
て、該クリーニング手段が其の一端を像担持体に圧接す
るクリーニングブレードであり、その材質がポリウレタ
ン弾性体であり、該ポリウレタン弾性体の硬度（ＪＩＳ
Ａスケール）が５０〜９０，ヤング率（ｋｇ／ｃｍ²）
が４０〜９０，１００％モジュラス（ｋｇ／ｃｍ²）が
２０〜６５，３００％モジュラス（ｋｇ／ｃｍ²）が７
０〜１５０，引っ張り強さ（ｋｇ／ｃｍ²）が２４０〜
５００，伸び（％）が２９０〜５００，反発弾性（％）
が３０〜７０，引裂強さ（ｋｇ／ｃｍ²）が２５〜７５
及び永久伸び（％）が４．０以下であり、かつ前記ブレ
ードの圧接力を１０〜５０（ｇｆ／ｃｍ）の範囲に設定
した際、自由長部の厚さ（ｔ）を１〜３ｍｍ、ブレード
の自由長（Ｌ）を５〜１５ｍｍ及びＬ／ｔ比を２〜８で
あることを特徴とする画像形成装置。7. An image carrier comprising an organic photoreceptor containing inorganic or organic particles in the outermost surface layer, a means for charging the image carrier, and a cleaning means for cleaning the toner remaining on the image carrier after transfer. In the provided image forming apparatus, the cleaning means is a cleaning blade whose one end is brought into pressure contact with the image carrier, and the material thereof is a polyurethane elastic body, and the hardness of the polyurethane elastic body (JIS
A scale) is 50 to 90, Young's modulus (kg / cm ² )
Is 40 to 90, 100% modulus (kg / cm ² ) is 20 to 65,300% modulus (kg / cm ² ) is 7
0-150, tensile strength (kg / cm ² ) 240-
500, elongation (%) 290-500, impact resilience (%)
Is 30 to 70, tear strength (kg / cm ² ) is 25 to 75
And the permanent elongation (%) is 4.0 or less, and when the pressure contact force of the blade is set in the range of 10 to 50 (gf / cm), the thickness (t) of the free length portion is 1 to 3 mm, An image forming apparatus having a blade free length (L) of 5 to 15 mm and an L / t ratio of 2 to 8.