JPH08176327A - Treatment of surface of substrate - Google Patents

Treatment of surface of substrate

Info

Publication number
JPH08176327A
JPH08176327A JP31884294A JP31884294A JPH08176327A JP H08176327 A JPH08176327 A JP H08176327A JP 31884294 A JP31884294 A JP 31884294A JP 31884294 A JP31884294 A JP 31884294A JP H08176327 A JPH08176327 A JP H08176327A
Authority
JP
Japan
Prior art keywords
gas
substrate
metal electrodes
surface treatment
inert gas
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP31884294A
Other languages
Japanese (ja)
Inventor
Motokazu Yuasa
基和 湯浅
Junko Noguchi
順子 野口
Shigemasa Kawai
重征 河合
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sekisui Chemical Co Ltd
Original Assignee
Sekisui Chemical Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Sekisui Chemical Co Ltd filed Critical Sekisui Chemical Co Ltd
Priority to JP31884294A priority Critical patent/JPH08176327A/en
Publication of JPH08176327A publication Critical patent/JPH08176327A/en
Pending legal-status Critical Current

Abstract

PURPOSE: To provide a method for treating the surface of a plastic substrate, capable of imparting excellent hydrophilicity to the surface of the plastic substrate and maintaining the hydrophilicity over a long period. CONSTITUTION: The method for treating the surface of a substrate comprises the first process comprising disposing the plastic substrate between metal electrodes 4 and 5 wherein a solid dielectric substance 6 is disposed on at least one of the faced surfaces between the faced metal electrodes 4 and 5, maintaining an inert gas alone or the mixture of the inert gas with an oxygen- containing gas (a gas for treating the surface) at a pressure near to the atmospheric pressure, and subsequently applying an electric voltage between the metal electrodes 4 and 5 to activate the surface with the generated discharge plasma, and the second process comprising dipping the surface-activated substrate 7 in the solution of a hydrophilic monomer, and subsequently heating the substrate to react the hydrophilic monomer on the surface of the substrate.

Description

【発明の詳細な説明】Detailed Description of the Invention

【0001】[0001]

【産業上の利用分野】本発明は、基材の表面処理方法に
関する。
FIELD OF THE INVENTION The present invention relates to a surface treatment method for a substrate.

【0002】[0002]

【従来の技術】従来、プラスチック基材の表面を親水化
する方法は数多く提案されている。例えば、界面活性剤
を含有する組成物を基材表面に塗布する方法は挙げられ
るが、この方法では、水と接触すると界面活性剤が水に
より流失し親水性を維持できなくなるため、耐久性に問
題があった。また、大気圧下でコロナ放電処理し表面を
酸化する方法が広く知られ実用化されている。しかしな
がら、表面処理された酸化層の厚みはきわめて薄く、親
水性の耐久性に問題があった。
2. Description of the Related Art Conventionally, many methods for making a surface of a plastic substrate hydrophilic have been proposed. For example, a method of applying a composition containing a surfactant to the surface of a base material can be mentioned. In this method, when contacted with water, the surfactant is washed away by water and the hydrophilicity cannot be maintained. There was a problem. Further, a method of corona discharge treatment under atmospheric pressure to oxidize the surface is widely known and put into practical use. However, the thickness of the surface-treated oxide layer was extremely thin, and there was a problem in hydrophilic durability.

【0003】そこで、親水性の耐久性を向上させるため
に、0.01〜10Torr程度の低い圧力でグロー放
電プラズマによる基材表面を活性化し、アクリルアミド
等ののモノマー溶液中でモノマーをグラフト重合する方
法が、筏氏によってMacromolecules, 19, 1804 (1986)
に提案されている。しかしながら、低い圧力でグロー放
電プラズマを発生するためには、容器は高価な真空チャ
ンバーを必要とし、また真空排気装置を設置する必要が
ある。さらに、真空中で処理するため、大面積の基板を
処理しようとすると真空容器を大きくしなければなら
ず、かつ、真空排気装置も大出力のものが必要となる。
従って、設備自体が非常に高価なものになるという問題
点があった。その上、吸水率の高いプラスチック基板の
表面処理を行う場合は、真空引きに長時間を要し、処理
品がコスト高になるという問題点もあった。
Therefore, in order to improve the durability of hydrophilicity, the surface of the substrate is activated by glow discharge plasma at a low pressure of about 0.01 to 10 Torr, and the monomer is graft-polymerized in a monomer solution such as acrylamide. The Method by Macromolecules, 19 , 1804 (1986)
Has been proposed to. However, in order to generate glow discharge plasma at a low pressure, the container needs an expensive vacuum chamber, and an evacuation device needs to be installed. Further, since the processing is performed in a vacuum, when a large-area substrate is to be processed, the vacuum container must be made large, and the vacuum exhaust device must also have a large output.
Therefore, there is a problem that the equipment itself becomes very expensive. In addition, when the surface treatment of a plastic substrate having a high water absorption rate is performed, it takes a long time to evacuate and there is a problem that the cost of the treated product becomes high.

【0004】[0004]

【発明が解決しようとする課題】本発明は、上記欠点を
解決するためになされたものであり、その目的は、プラ
スチック基材表面上に優れた親水性を付与すると共に、
その親水性を長期間にわたって維持可能な表面処理方法
を提供することにある。
The present invention has been made to solve the above-mentioned drawbacks, and its purpose is to impart excellent hydrophilicity to the surface of a plastic substrate, and
It is to provide a surface treatment method capable of maintaining its hydrophilicity for a long period of time.

【0005】[0005]

【課題を解決するための手段】本発明の基材の表面処理
方法は、該基材表面に金属電極間に電圧を印加して発生
した放電プラズマを接触させ活性化させる第1の工程
と、基材表面の活性点で該水性モノマーと反応させる第
2の工程からなる。
The substrate surface treatment method of the present invention comprises a first step of contacting and activating a discharge plasma generated by applying a voltage between metal electrodes on the substrate surface, It comprises a second step of reacting with the aqueous monomer at the active sites on the substrate surface.

【0006】上記基材としては、ポリエチレン、アクリ
ル樹脂、ポリカーボネート、ポリエチレンテレフタレー
ト等の樹脂フィルム又はプレートが挙げられる。
Examples of the base material include resin films or plates of polyethylene, acrylic resin, polycarbonate, polyethylene terephthalate and the like.

【0007】上記第1の工程では、不活性ガス単体又は
不活性ガスと酸素含有ガス(以下、表面処理用ガスとい
う)との混合ガスを大気圧近傍の圧力に保ち、上記基材
表面に金属電極間に電圧を印加して発生した放電プラズ
マを接触させることにより、基材表面にラジカル層を形
成したり、過酸化層を形成し基材表面を活性化させる。
In the first step, an inert gas alone or a mixed gas of an inert gas and an oxygen-containing gas (hereinafter referred to as a surface-treating gas) is kept at a pressure near atmospheric pressure, and metal on the surface of the substrate is kept. By contacting the discharge plasma generated by applying a voltage between the electrodes, a radical layer is formed on the surface of the base material or a peroxide layer is formed to activate the surface of the base material.

【0008】上記不活性ガスとしては、例えば、ヘリウ
ム、ネオン、アルゴン、キセノン等の希ガスや窒素ガス
等が挙げられ、これらは単独で使用されても二種以上が
併用されてもよい。特に、不活性ガスとして、ヘリウム
ガスは準安定状態の寿命が長く、処理用ガスの励起に都
合がよく好ましい。上記不活性ガスとしては、ヘリウム
以外のものを用いる場合は、2体積%以下のアセトンや
メタノール等の有機物蒸気や、メタン、エタン等の炭化
水素を混合して使用するのが好ましい。
Examples of the above-mentioned inert gas include rare gases such as helium, neon, argon and xenon, and nitrogen gas. These may be used alone or in combination of two or more kinds. In particular, as the inert gas, helium gas is preferable because it has a long metastable life and is convenient for exciting the processing gas. When a gas other than helium is used as the above-mentioned inert gas, it is preferable to mix and use 2% by volume or less of an organic vapor such as acetone or methanol, or a hydrocarbon such as methane or ethane.

【0009】上記不活性ガス単体に代えて、不活性ガス
と表面処理用ガスとの混合ガスを使用してもよい。両者
の併用によりラジカル層や酸化層の形成が容易になるの
で好ましい。上記表面処理用ガスとしては、例えば、酸
素、オゾン、水蒸気、一酸化炭素、二酸化炭素、一酸化
窒素、二酸化窒素等の酸素含有ガスが挙げられ、これら
は単独で使用されても二種以上が併用されてもよい。
A mixed gas of an inert gas and a surface treatment gas may be used in place of the above-mentioned inert gas alone. The combination of the two is preferable because it facilitates the formation of the radical layer and the oxide layer. Examples of the surface treatment gas include oxygen-containing gases such as oxygen, ozone, water vapor, carbon monoxide, carbon dioxide, nitric oxide, and nitrogen dioxide, and two or more of them may be used alone. You may use together.

【0010】上記不活性ガスと表面処理用ガスとの混合
ガスを使用する場合には、表面処理用ガスに対して体積
比50%以下のフッ素含有ガスを併用することにより、
活性化がより促進される。上記フッ素含有ガスとして
は、例えば、四フッ化炭素(CF4)、六フッ化炭素(C
6)、六フッ化プロピレン(C3 6)等のフッ化炭化水
素ガス;一塩素三フッ化炭素ガス(CClF3)等のハロ
ゲン化炭化水素ガス;六フッ化硫黄(SF6)等のフッ化
硫黄化合物などが挙げられる。特に、これらのフッ素含
有ガスの中で、安全性が高くフッ化水素等の有害なガス
を生成しない、四フッ化炭素、六フッ化炭素や六フッ化
プロピレンが好ましい。
When a mixed gas of the above-mentioned inert gas and surface treatment gas is used, a fluorine-containing gas having a volume ratio of 50% or less with respect to the surface treatment gas is used in combination.
Activation is promoted more. Examples of the fluorine-containing gas include carbon tetrafluoride (CF 4 ), carbon hexafluoride (C
F 6 ), fluorinated hydrocarbon gas such as propylene hexafluoride (C 3 F 6 ), halogenated hydrocarbon gas such as carbon monofluoride trifluoride gas (CClF 3 ), sulfur hexafluoride (SF 6 ), etc. And the like. Of these fluorine-containing gases, carbon tetrafluoride, carbon hexafluoride and propylene hexafluoride, which are highly safe and do not generate harmful gases such as hydrogen fluoride, are particularly preferable.

【0011】上記不活性ガスと表面処理用ガスとの混合
ガスにおいて、両者の混合比は、用いるガスの種類によ
って適宜決定されるが、表面処理用ガスの濃度は高くな
ると電圧を印加しても放電プラズマが発生し難くなるの
で、10体積%以下が好ましく、より好ましくは0.1
〜5体積%である。
In the mixed gas of the inert gas and the surface treatment gas, the mixing ratio of the two is appropriately determined depending on the kind of the gas used, but when the concentration of the surface treatment gas becomes higher, a voltage is applied. Since discharge plasma is less likely to be generated, it is preferably 10% by volume or less, more preferably 0.1% by volume or less.
~ 5% by volume.

【0012】本発明の第1の工程では、上記不活性ガス
と表面処理用ガスとの混合ガスは、大気圧近傍の圧力1
00〜800Torrに保たれるが、実際には圧力調整
が容易で、かつ装置が簡便になる、700〜780To
rrが好ましい。また、基材表面に放電プラズマを接触
させて活性化する際には、基材は加熱されても冷却され
てもよく、室温に保たれていてもよい。
In the first step of the present invention, the mixed gas of the inert gas and the surface-treating gas has a pressure of about 1 at atmospheric pressure.
It is maintained at 00-800 Torr, but in reality, pressure adjustment is easy and the device becomes simple, 700-780To
rr is preferred. When the discharge plasma is brought into contact with the surface of the substrate for activation, the substrate may be heated or cooled, or may be kept at room temperature.

【0013】上記活性化処理に要する時間は、印加電圧
の大きさや使用されるガスの種類や基材の種類で決定さ
れ、例えば、ポリエチレンフィルムをヘリウムガスを使
用して活性化処理する場合は、上記印加電圧の範囲では
15秒間程度が好ましい。以上の第1の工程によって、
基材の表面に活性点が形成される。
The time required for the activation treatment is determined by the magnitude of the applied voltage, the type of gas used and the type of base material. For example, when the polyethylene film is activated using helium gas, It is preferable that the applied voltage range be about 15 seconds. By the above first step,
Active sites are formed on the surface of the substrate.

【0014】本発明の処理方法の第1の工程を、図面を
参照しながら詳細に説明する。図1は、第1工程に使用
される装置を示し、この装置は、電源部1、処理容器
2、上部電極4及び下部電極5から構成されている。電
源部1は、kHz台の周波数の電圧を印加可能であり、
耐熱性の低い基材を処理する場合には、5〜30kHz
の低い周波数が好ましい。
The first step of the processing method of the present invention will be described in detail with reference to the drawings. FIG. 1 shows an apparatus used in the first step, which is composed of a power supply unit 1, a processing container 2, an upper electrode 4 and a lower electrode 5. The power supply unit 1 can apply a voltage having a frequency on the order of kHz,
When processing a substrate with low heat resistance, 5-30 kHz
Lower frequencies are preferred.

【0015】上記放電プラズマの発生は、電圧を電極に
印加することによって発生させるが、電界強度は、弱く
なると処理に時間がかかり過ぎ、強くなるとアーク放電
に移行する挙動を示すので、1〜40kV/cm程度が
好ましい。上記放電プラズマによる表面処理部(放電プ
ラズマ発生部)3は、対向する電極4、5の間の空間で
ある。
The discharge plasma is generated by applying a voltage to the electrodes. When the electric field strength becomes weak, it takes too long to process, and when it becomes strong, the electric field strength changes to arc discharge. / Cm is preferable. The surface treatment part (discharge plasma generation part) 3 by the discharge plasma is a space between the electrodes 4 and 5 facing each other.

【0016】上記処理容器2は、耐熱ガラス製のものが
使用されるが、電極との絶縁が保たれていれば、ステン
レス、アルミニウム、銅、アルミニウム等の金属製であ
ってもよい。この処理容器2内には、相対する一対の平
行平板型の上部電極4と下部電極5とが配設されてい
る。電極構造としては、平行平板型以外の、円筒対向平
板型、球対向平板型、双曲面対向平板型又は同軸円筒型
であってもよく、複数の細線と平板からなるものであっ
てもよい。上部電極4及び下部電極5の材質としては、
ステンレス、真鍮、アルミニウム、銅等が挙げられる。
The processing container 2 is made of heat resistant glass, but may be made of metal such as stainless steel, aluminum, copper or aluminum as long as the insulation with the electrodes is maintained. In the processing container 2, a pair of parallel plate type upper electrodes 4 and lower electrodes 5 which are opposed to each other are arranged. The electrode structure may be a cylinder facing flat plate type, a sphere facing flat plate type, a hyperboloid facing flat plate type or a coaxial cylinder type other than the parallel flat plate type, and may be composed of a plurality of fine wires and a flat plate. As the material of the upper electrode 4 and the lower electrode 5,
Examples include stainless steel, brass, aluminum and copper.

【0017】上記下部電極5の上部電極4に対向する側
には、その電極全体を覆うように固体誘電体6が配置さ
れている。電極の一部でも固体誘電体6で覆われていな
い部分があると、そこからアーク放電が起こるので好ま
しくない。また、上記固体誘電体6は、必ずしも、下部
電極5に配置される必要はなく、上部電極4に配置され
ていてもよく、上部電極4と下部電極5の両方に配置さ
れていてもよい。
On the side of the lower electrode 5 facing the upper electrode 4, a solid dielectric 6 is arranged so as to cover the entire electrode. If there is a part of the electrode that is not covered with the solid dielectric 6, arc discharge will occur from that part, which is not preferable. Further, the solid dielectric 6 does not necessarily have to be arranged on the lower electrode 5, and may be arranged on the upper electrode 4 or may be arranged on both the upper electrode 4 and the lower electrode 5.

【0018】上記固体誘電体6としては、ポリテトラフ
ルオロエチレン(PTFE)、ポリエチレンテレフタレ
ート(PET)等のプラスチック類;SiO2 、Al2
3、ZrO2 、TiO2 等の金属酸化物単体やこれら
の化合物が挙げられ、その形状は、シート状、フィルム
状のいずれであってもよい。
As the solid dielectric 6, plastics such as polytetrafluoroethylene (PTFE) and polyethylene terephthalate (PET); SiO 2 , Al 2
Examples thereof include simple metal oxides such as O 3 , ZrO 2 , and TiO 2 and compounds thereof, and the shape thereof may be a sheet shape or a film shape.

【0019】上記固体誘電体6の厚みは、薄くなると電
圧印加時に絶縁破壊が起こってアーク放電が発生し易く
なり、厚くなると放電プラズマを発生するのに高電圧を
要するので、0.05〜4mmが好ましい。
When the thickness of the solid dielectric 6 is thin, dielectric breakdown occurs when a voltage is applied and arc discharge easily occurs, and when it is thick, a high voltage is required to generate discharge plasma. Is preferred.

【0020】上部電極4と下部電極5の間の距離は、固
体誘電体6の厚み、基材7の厚み、印加電圧の大きさ、
ガス流量等によって適宜決定されるが、短くなると未使
用のガスが多くなって非能率的となり、長くなると放電
プラズマの均一性が損なわれるので、1〜30mmが好
ましい。
The distance between the upper electrode 4 and the lower electrode 5 depends on the thickness of the solid dielectric 6, the thickness of the base material 7, the magnitude of the applied voltage,
Although it is appropriately determined depending on the gas flow rate and the like, when the length is short, the amount of unused gas is large, which is inefficient, and when the length is long, the uniformity of the discharge plasma is impaired.

【0021】上記基材7は、図1では固体誘電体6上に
配置されているので、その片面(図の上面)のみがプラ
ズマ放電処理されるが、基材7の両面にプラズマ放電処
理を必要とする場合は、上部電極4と下部電極5の間の
表面処理部3に浮かせた状態で放電プラズマを接触させ
ればよい。
Since the base material 7 is disposed on the solid dielectric 6 in FIG. 1, only one surface (upper surface in the drawing) of the base material 7 is subjected to plasma discharge processing, but both surfaces of the base material 7 are subjected to plasma discharge processing. If necessary, the discharge plasma may be brought into contact with the surface treatment section 3 between the upper electrode 4 and the lower electrode 5 in a floating state.

【0022】上記放電プラズマ処理時には、表面処理用
ガスをガス導入管8から、不活性ガスをガス導入管9か
ら、それぞれ表面処理部3に供給する。なお、上部電極
4が多孔構造を有すると、表面処理用ガスを表面処理部
3に均一に供給することにより、均一な放電プラズマを
接触させることができるので好ましいが、表面処理部3
に表面処理用ガス及び不活性ガスを攪拌しながら供給し
たり、前記ガスを高速で基材7に吹きつけて供給するこ
とにより、均一な供給が可能であれば、必ずしも多孔構
造である必要はない。
At the time of the discharge plasma treatment, the surface treatment gas is supplied to the surface treatment section 3 from the gas introduction pipe 8 and the inert gas is supplied to the surface treatment unit 3 from the gas introduction pipe 9. It is preferable that the upper electrode 4 has a porous structure because the surface treatment gas can be uniformly supplied to the surface treatment unit 3 so that uniform discharge plasma can be brought into contact with the surface treatment unit 3.
If the surface treatment gas and the inert gas are supplied while being stirred or the gas is sprayed onto the base material 7 at a high speed to supply the gas, a porous structure is not necessarily required. Absent.

【0023】上記表面処理用ガス及び不活性ガスは、マ
スフローコントローラー(図示しない)によって、流量
が制御されており、過剰のガスは排出口10から排出さ
れる。なお、処理容器2内に表面処理用ガス及び不活性
ガスを導入する際には、該容器2内に残存する空気を排
気口11から排出するのが好ましい。
The flow rates of the surface treatment gas and the inert gas are controlled by a mass flow controller (not shown), and excess gas is discharged from the discharge port 10. When the surface treatment gas and the inert gas are introduced into the processing container 2, it is preferable that the air remaining in the container 2 be discharged from the exhaust port 11.

【0024】次に、本発明の処理方法の第2の工程につ
いて説明する。上記第2の工程では、第1の工程で得ら
れた表面活性化された基材を、親水性モノマーの溶液中
に浸漬し加熱することにより、基材表面の活性点で親水
性モノマーをラジカル反応させる。
Next, the second step of the processing method of the present invention will be described. In the second step, the surface-activated base material obtained in the first step is immersed in a solution of the hydrophilic monomer and heated to radically convert the hydrophilic monomer at the active sites on the surface of the base material. React.

【0025】上記親水性モノマーは、親水基として、例
えば、水酸基、スルホン酸又はスルホン酸塩基、1級、
2級あるいは3級アミノ基、アミド基、4級アンモニウ
ム塩基、カルボン酸あるいはカルボン酸塩基、ポリエチ
レングリコール鎖等を1つ以上もつもの、または重合後
化学反応によって重合体が親水性となる酢酸ビニル、ア
クリル酸エステル等が挙げられる。
The above-mentioned hydrophilic monomer has, as a hydrophilic group, for example, a hydroxyl group, a sulfonic acid or a sulfonate group, a primary,
A polymer having one or more secondary or tertiary amino group, amide group, quaternary ammonium salt group, carboxylic acid or carboxylate group, polyethylene glycol chain, or vinyl acetate whose polymer becomes hydrophilic by a chemical reaction after polymerization, Examples thereof include acrylic acid ester.

【0026】上記親水性モノマーとしては、具体的に、
(メタ)アクリル酸、(メタ)アクリルアミド、プロピ
オンアミド、(メタ)アクリル酸ナトリウム、アクリル
酸カリウム、スチレンスルホン酸ナトリウム、アクリル
酸メチオル、ポリエチレングリコールジ(メタ)アクリ
ル酸エステル、2−ヒドロキシエチルメタクリレート、
2−ヒドロキシメチルアクリレート等が挙げられ、これ
らは単独で用いられても二種以上が併用されてもよい。
Specific examples of the hydrophilic monomer include:
(Meth) acrylic acid, (meth) acrylamide, propionamide, sodium (meth) acrylate, potassium acrylate, sodium styrenesulfonate, methacrylic acid acrylate, polyethylene glycol di (meth) acrylic acid ester, 2-hydroxyethyl methacrylate,
2-Hydroxymethyl acrylate and the like are mentioned, and these may be used alone or in combination of two or more kinds.

【0027】上記親水性モノマーは溶媒に溶かし溶液と
して用いられる。溶媒としては、メタノール、エタノー
ル、アセトン等の有機溶媒又は水が用いられる。溶液中
のモノマー濃度は、特に限定されないが、薄くなると反
応速度が遅くなって反応に要する時間が長くなり、濃く
なると未反応モノマーが大量に溶液中に残ることから、
効率的な反応を行うためには、モノマーの種類にもよる
が5〜30重量%が好ましい。
The hydrophilic monomer is dissolved in a solvent and used as a solution. As the solvent, an organic solvent such as methanol, ethanol or acetone or water is used. The concentration of the monomer in the solution is not particularly limited, but when it becomes thin, the reaction speed becomes slow and the time required for the reaction becomes long, and when it becomes thick, a large amount of unreacted monomer remains in the solution,
For efficient reaction, it is preferably 5 to 30% by weight, though it depends on the kind of the monomer.

【0028】第1の工程で表面の活性化して基材を上記
親水性モノマー溶液に浸漬し加熱することによって、ラ
ジカル反応が促進される。反応させる際の加熱温度は、
高ければ高いほど反応が促進されるので好ましいが、基
材に悪影響を及ぼすので基材の耐熱温度以下に加熱する
のが好ましい。親水性モモノマー溶液への浸漬時間は、
該モノマーの種類や濃度、加熱温度等により適宜決定さ
れる。上記反応により、基材表面に未反応モノマーやホ
モポリマー等が物理吸着する場合は、必要に応じて、水
や有機溶媒等で洗浄を行い、これを除去することができ
る。
In the first step, the radical reaction is promoted by activating the surface, immersing the substrate in the hydrophilic monomer solution and heating it. The heating temperature for the reaction is
The higher the temperature is, the more the reaction is promoted, which is preferable. However, since it adversely affects the base material, it is preferable to heat the base material to the heat resistant temperature or lower. The immersion time in the hydrophilic monomer monomer solution is
It is appropriately determined depending on the type and concentration of the monomer, the heating temperature and the like. When unreacted monomers, homopolymers and the like are physically adsorbed on the surface of the substrate by the above reaction, they can be removed by washing with water, an organic solvent or the like, if necessary.

【0029】[0029]

【実施例】以下、本発明を実施例に基いて説明する。 (実施例1) <第1の工程>図1に示した装置(金属電極80mm
φ)において、電極間距離7mmの電極空間中に、厚み
2mm、直径120mmの円板状TiO2 焼結体を装着
した下部電極上に基材として100mm□×3mm厚の
ポリカーボネート板(旭硝子社製「レキサン」)を設置
し、1Torrまで油回転ポンプで排気した。次いで、
Heガスを流量500sccmでガス導入管から容器内
に導入し、757Torrの大気圧とした。その後、1
5kHz、3.1kVの電圧を電極に印加し15秒間放
置し、基材表面に活性点を形成した。なお、電圧印加に
伴って放電プラズマの発光が観察された。 <第2の工程>第1の工程で処理されたポリカーボネー
ト板を、脱気した10重量%スチレンスルホン酸ナトリ
ウム水溶液に浸漬し、50℃で2時間反応を行った。反
応終了後、熱水による洗浄と水による超音波洗浄を行
い、親水性を有する表面処理品を得た。
The present invention will be described below with reference to examples. Example 1 <First Step> Device shown in FIG. 1 (metal electrode 80 mm
φ), a polycarbonate plate of 100 mm □ × 3 mm thickness (made by Asahi Glass Co., Ltd.) as a base material on the lower electrode on which a disk-shaped TiO 2 sintered body having a thickness of 2 mm and a diameter of 120 mm is mounted in an electrode space having a distance between electrodes of 7 mm. “Lexan”) was installed and the oil was evacuated to 1 Torr with an oil rotary pump. Then
He gas was introduced into the container from the gas introduction pipe at a flow rate of 500 sccm, and the atmospheric pressure was set to 757 Torr. Then 1
A voltage of 5 kHz and 3.1 kV was applied to the electrodes and left for 15 seconds to form active points on the surface of the base material. Note that the emission of discharge plasma was observed as the voltage was applied. <Second Step> The polycarbonate plate treated in the first step was immersed in a degassed 10 wt% sodium styrenesulfonate aqueous solution, and reacted at 50 ° C. for 2 hours. After completion of the reaction, washing with hot water and ultrasonic washing with water were performed to obtain a surface-treated product having hydrophilicity.

【0030】(実施例2) <第1の工程>図1に示した装置(金属電極80mm
φ)において、電極間距離5mmの電極空間中に、厚み
2mm、120mm□の石英ガラスを装着した下部電極
上に基材として100mm□×50μm厚のポリエチレ
ンテレフタレートフィルム(東レ社製「ルミラーT5
0」)を設置し、1Torrまで油回転ポンプで排気し
た。次いで、O2 ガスを流量15sccmで多孔構造の
上部電極から、また、Heガスを流量985sccmで
ガス導入管から容器内にそれぞれ導入し、757Tor
rの大気圧とした。その後、15kHz、4.1kVの
電圧を電極に印加して15秒間放置し、基材表面を活性
化した。なお、電圧印加に伴って放電プラズマの発光が
観察された。 <第2の工程>第1の工程で活性化処理されたフィルム
を、脱気した10重量%アクリルアミド水溶液中に浸漬
し、70℃で4時間反応を行った。反応終了後、熱水に
よる洗浄と水による超音波洗浄を行い、親水性を有する
表面処理品を得た。
Example 2 <First Step> The apparatus shown in FIG. 1 (metal electrode 80 mm
φ), a polyethylene terephthalate film having a thickness of 2 mm and a quartz glass of 120 mm □ mounted on a lower electrode having a thickness of 100 mm □ × 50 μm as a substrate (“Lumirror T5 manufactured by Toray Industries, Inc.”).
0 ”) was installed and exhausted to 1 Torr with an oil rotary pump. Then, O 2 gas was introduced into the container at a flow rate of 15 sccm from the upper electrode having a porous structure, and He gas was introduced at a flow rate of 985 sccm from the gas introduction pipe into the container, and 757 Tor was obtained.
The atmospheric pressure was r. Then, a voltage of 15 kHz and 4.1 kV was applied to the electrodes and left for 15 seconds to activate the substrate surface. Note that the emission of discharge plasma was observed as the voltage was applied. <Second Step> The film activated in the first step was immersed in a degassed 10 wt% acrylamide aqueous solution, and reacted at 70 ° C. for 4 hours. After completion of the reaction, washing with hot water and ultrasonic washing with water were performed to obtain a surface-treated product having hydrophilicity.

【0031】(実施例3) <第1の工程>図1に示した装置(金属電極80mm
φ)において、電極間距離5mmの電極空間中に、12
0mm□×1mm厚のポリテトラフルオロエチレンを装
着した下部電極上に基材として100mm□×50μm
厚のポリエチレンフィルム(積菱包装社製「IIーF」)
を設置し、1Torrまで油回転ポンプで排気した。次
いで、流量7sccmのO2 ガスと流量3sccmのC
4 ガスとの混合ガスを多孔構造の上部電極から、ま
た、Heガスを流量990sccmでガス導入管から容
器内に導入し、757Torrの大気圧とした。その
後、15kHz、3.8kVの電圧を電極に印加し15
秒間放置し、基材表面を活性化した。なお、電圧印加に
伴って放電プラズマの発光が観察された。 <第2の工程>第1の工程で活性化処理されたフィルム
を、脱気した10重量%アクリルアミド水溶液中に浸漬
し、50℃で2時間反応を行った。反応終了後、熱水に
よる洗浄と水による超音波洗浄を行い、親水性を有する
表面処理品を得た。
Example 3 <First Step> The apparatus shown in FIG. 1 (metal electrode 80 mm
φ), 12 in the electrode space with a distance between the electrodes of 5 mm
100 mm □ × 50 μm as a base material on the lower electrode equipped with 0 mm □ × 1 mm thick polytetrafluoroethylene
Thick polyethylene film ("II-F" manufactured by Sekiryo Packaging Co., Ltd.)
Was installed, and the oil was evacuated to 1 Torr by an oil rotary pump. Next, O 2 gas with a flow rate of 7 sccm and C with a flow rate of 3 sccm
A mixed gas with F 4 gas was introduced into the container from the upper electrode having a porous structure, and He gas was introduced into the container from the gas introduction pipe at a flow rate of 990 sccm to make the atmospheric pressure 757 Torr. After that, a voltage of 15 kHz and 3.8 kV was applied to the electrodes, and
The substrate surface was activated by leaving it for a second. Note that the emission of discharge plasma was observed as the voltage was applied. <Second Step> The film activated in the first step was immersed in a degassed 10 wt% acrylamide aqueous solution and reacted at 50 ° C. for 2 hours. After completion of the reaction, washing with hot water and ultrasonic washing with water were performed to obtain a surface-treated product having hydrophilicity.

【0032】(比較例1)市販のコロナ放電処理装置
(春日電機社製「形式HFSS−103」)でポリエチ
レンフィルム(積菱包装社製「IIーF」)を30kVの
電圧を印加して15秒間コロナ放電処理した。
(Comparative Example 1) A polyethylene film ("II-F" manufactured by Sekiryo Packaging Co., Ltd.) was applied with a voltage of 30 kV using a commercially available corona discharge treatment device ("Model HFSS-103" manufactured by Kasuga Denki Co., Ltd.). Corona discharge treatment was performed for a second.

【0033】上記実施例及び比較例で使用された基材及
び実施例及び比較例で得られた表面処理品につき接触角
を測定し、その測定結果を表1に示した。接触角の測定
には、2mmの水滴を1cm間隔で滴下し、協和界面科
学社製「接触角測定装置(商品名:CA−D)」を使用
し、静的接触角を測定した。尚、表面処理品について
は、処理直後及び60℃のオーブン中で7日間放置後に
それぞれ測定した。
The contact angles of the substrates used in the above Examples and Comparative Examples and the surface-treated products obtained in Examples and Comparative Examples were measured, and the measurement results are shown in Table 1. To measure the contact angle, a 2 mm water droplet was dropped at 1 cm intervals, and a static contact angle was measured using a "contact angle measuring device (trade name: CA-D)" manufactured by Kyowa Interface Science Co., Ltd. The surface-treated product was measured immediately after the treatment and after standing in an oven at 60 ° C. for 7 days.

【0034】[0034]

【表1】 [Table 1]

【0035】[0035]

【発明の効果】本発明の基材の表面処理方法は、上述の
通りであり、プラスチック基材表面上に優れた親水性を
付与することができ、その親水性が長期間にわたって維
持されるので、プラスチック成形体の印刷性向上のため
の表面処理や接着性向上のためのアンカー層の形成なら
びに眼鏡や鏡等の防曇材として好適に用いられる。
Industrial Applicability The surface treatment method for a substrate of the present invention is as described above, and it is possible to impart excellent hydrophilicity to the surface of a plastic substrate and the hydrophilicity is maintained for a long period of time. It is preferably used as a surface treatment for improving printability of a plastic molded body, forming an anchor layer for improving adhesiveness, and as an antifogging material for spectacles, mirrors and the like.

【図面の簡単な説明】[Brief description of drawings]

【図1】本発明の表面処理方法の第1の工程で使用され
る装置を示す概要図である。
FIG. 1 is a schematic view showing an apparatus used in a first step of a surface treatment method of the present invention.

【符号の説明】 1 電源 2 耐熱性ガラス容器 3 表面処理部 4 上部電極 5 下部電極 6 固体誘電体 7 基材 8、9 ガス導入管 10 排出口 11 排気口[Explanation of symbols] 1 power supply 2 heat-resistant glass container 3 surface treatment part 4 upper electrode 5 lower electrode 6 solid dielectric 7 base material 8, 9 gas inlet pipe 10 exhaust port 11 exhaust port

Claims (1)

【特許請求の範囲】[Claims] 【請求項1】プラスチック基材を対向する金属電極間の
少なくとも一方の対向面に固体誘電体が配設された金属
電極間に配置して、不活性ガス単体又は不活性ガスと酸
素含有ガス(表面処理用ガス)との混合ガスを大気圧近
傍の圧力に保ち、該基材表面に金属電極間に電圧を印加
して発生した放電プラズマを接触させ活性化させる第1
の工程と、表面が活性化された基材を親水性モノマーの
溶液に浸漬し加熱することにより、該基材表面で該親水
性モノマーを反応させる第2の工程からなることを特徴
とする基材の表面処理方法。
1. A plastic substrate is disposed between metal electrodes having a solid dielectric disposed on at least one opposing surface between opposing metal electrodes, and an inert gas alone or an inert gas and an oxygen-containing gas ( A mixed gas with a surface treatment gas) is kept at a pressure near atmospheric pressure, and a discharge plasma generated by applying a voltage between the metal electrodes is brought into contact with the surface of the base material to activate the first plasma.
And a second step of reacting the hydrophilic monomer on the surface of the substrate by immersing the substrate whose surface is activated in a solution of the hydrophilic monomer and heating the substrate. Surface treatment method for wood.
JP31884294A 1994-12-21 1994-12-21 Treatment of surface of substrate Pending JPH08176327A (en)