JPH0782626A - Sheet for production of gold or silver thread, gold or silver thread and moven fabric having gold or silver decoration - Google Patents
Sheet for production of gold or silver thread, gold or silver thread and moven fabric having gold or silver decorationInfo
- Publication number
- JPH0782626A JPH0782626A JP5223711A JP22371193A JPH0782626A JP H0782626 A JPH0782626 A JP H0782626A JP 5223711 A JP5223711 A JP 5223711A JP 22371193 A JP22371193 A JP 22371193A JP H0782626 A JPH0782626 A JP H0782626A
- Authority
- JP
- Japan
- Prior art keywords
- silver
- gold
- sheet
- layer
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、服飾等に使用される金
銀糸を製造するためのシート、金銀糸、および金銀装飾
を有する織布に関するもので、特に、銀被膜の耐食性を
高めるための改良に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a sheet for producing gold and silver threads used for clothing and the like, a gold and silver thread, and a woven cloth having a gold and silver decoration, and more particularly to improving corrosion resistance of a silver coating. Regarding improvement.
【０００２】[0002]
【従来の技術】和服等に使用される織布の一種として金
銀色の模様を形成したものがある。このような織布は通
常、金糸または銀糸を横糸、絹糸を縦糸として織り、部
分的に金糸または銀糸（以下、両者を合わせて金銀糸と
称する）を織布の表面側に露出させて模様を形成したも
のである。2. Description of the Related Art A type of woven fabric used for Japanese clothes includes gold and silver patterns. Such woven fabrics are usually woven with gold or silver yarns as wefts and silk yarns as warp yarns, and the gold or silver yarns (hereinafter, both are collectively referred to as gold and silver yarns) are partially exposed on the surface side of the woven fabric to form a pattern. It was formed.
【０００３】前記金銀糸の多くは、プラスチック製のフ
ィルムに銀を蒸着し、この銀被膜上に樹脂コーティング
を施した金銀糸製造用シートを裁断して製造されてい
る。銀を使用しているのは、銀特有の深い光沢は他の金
属では得られ難いためである。図７〜図９は、それぞれ
異なる従来の金銀糸製造用シートの断面を示している。
これらの図に示すシートはいずれも片面型と呼ばれるも
ので、これら片面型シートのフィルム側を接着剤で張り
合わせた両面型シートも市販されている。本明細書中の
金銀糸製造用シートとは、これら片面型シートおよび両
面型シートの両者を総称するものとする。Most of the gold-silver yarns are manufactured by vapor-depositing silver on a plastic film and cutting a gold-silver yarn producing sheet having a resin coating on the silver film. The reason why silver is used is that the deep luster peculiar to silver is difficult to obtain with other metals. 7 to 9 show cross sections of different conventional gold-silver yarn manufacturing sheets.
The sheets shown in these figures are all called single-sided sheets, and double-sided sheets obtained by laminating the film side of these single-sided sheets with an adhesive are also commercially available. In the present specification, the gold-silver yarn production sheet is a generic term for both the single-sided sheet and the double-sided sheet.
【０００４】図７に示す片面型シートは、透明なＰＥＴ
等からなる樹脂フィルム１上に銀被膜２を蒸着し、さら
に銀被膜２を保護するアクリル系樹脂の樹脂コーティン
グ層３を形成したものである。また、図８のシートは樹
脂フィルム１の裏面に着色層４が形成されたもの、図９
のシートは樹脂フィルム１と銀被膜２の間に着色層４が
形成されたものである。着色層は、例えば金糸の場合に
は赤色系の着色料を塗布乾燥して形成され、これが銀被
膜２を通して透けることにより、シートは金色に発色す
る。The single-sided sheet shown in FIG. 7 is a transparent PET.
A silver film 2 is vapor-deposited on a resin film 1 made of, for example, and a resin coating layer 3 of an acrylic resin that protects the silver film 2 is further formed. Further, the sheet of FIG. 8 has the colored layer 4 formed on the back surface of the resin film 1, and FIG.
This sheet has a colored layer 4 formed between the resin film 1 and the silver coating 2. For example, in the case of a gold thread, the colored layer is formed by applying a red colorant and drying it, and the sheet is colored through the silver coating 2 when it is transparent.
【０００５】これら片面型シートのフィルム側を対向さ
せ、接着層および繊維層を介在させて張り合わせること
により、両面型シートが得られる。この両面型シートの
厚さは０．１ｍｍ程度であり、この両面シートをマイク
ロスリッター等で０．３ｍｍ程度の幅で細く裁断すれ
ば、金銀平糸が得られる。A double-sided sheet is obtained by making the film sides of these single-sided sheets face each other and laminating them with an adhesive layer and a fiber layer interposed therebetween. The thickness of this double-sided sheet is about 0.1 mm, and if this double-sided sheet is finely cut into a width of about 0.3 mm by a micro slitter or the like, gold and silver flat yarn can be obtained.
【０００６】一方、片面シートを細く裁断し、絹糸等の
芯糸に螺旋状に巻き付ければ、金銀撚糸となる。金銀織
布には通常このような撚糸が用いられるが、織り方によ
っては、前記平糸がそのまま使用される場合もある。On the other hand, a single-sided sheet is finely cut and spirally wound around a core thread such as silk thread to obtain a gold-silver twisted thread. Such twisted yarns are usually used for gold and silver woven fabrics, but the flat yarns may be used as they are depending on the weaving method.
【０００７】[0007]
【発明が解決しようとする課題】ところで、上記のよう
な金銀糸が近年では和服のみならず洋服にも多用される
ようになってきている。洋服の場合、和服に比して洗濯
の頻度が高いうえ、汗などが直接付着することも多いた
め、和服では十分使用に耐える金銀糸も、洋服に使用す
ると変色し易いという問題が生じた。By the way, in recent years, the gold and silver threads as described above have been widely used not only in Japanese clothes but also in Western clothes. Since clothes are washed more frequently than Japanese clothes and sweat and the like are often directly attached to the clothes, there is a problem that the gold and silver yarns that can be sufficiently used in Japanese clothes are easily discolored when used in the clothes.
【０００８】本発明者らは上記変色の原因を詳細に検討
し、その結果、空気中に含まれる酸素や硫化水素等の腐
食性ガスあるいは汗中の塩化物が、金銀糸の裁断面から
銀被膜とフィルムの界面、または樹脂コーティング層と
銀被膜の界面に沿って侵入し、銀被膜を剥離させながら
酸化，硫化または塩化していくことにより変色が進行す
ることを見いだした。The present inventors have examined in detail the cause of the above-mentioned discoloration, and as a result, corrosive gases such as oxygen and hydrogen sulfide contained in the air or chlorides in sweat have been found to be silver from the cut surface of the gold-silver thread. It has been found that discoloration progresses by invading along the interface between the film and the film or the interface between the resin coating layer and the silver film, and oxidizing, sulfiding or chlorinating while peeling off the silver film.
【０００９】本発明は上記事情に鑑みてなされたもの
で、裁断面からの腐食の進行を防止し得る金銀糸製造用
シート、金銀糸および金銀装飾を有する織布を提供する
ことを課題とする。The present invention has been made in view of the above circumstances, and an object of the present invention is to provide a sheet for producing a gold and silver thread, a gold and silver thread and a woven cloth having a gold and silver decoration, which can prevent the progress of corrosion from the cut surface. .
【００１０】[0010]
【課題を解決するための手段】図１ないし図６はそれぞ
れ、本発明に係る金銀糸製造用シートの具体例を示す断
面拡大図である。図１において符号１はフィルムで、こ
のフィルム１の片面上には、厚さ５〜２００オングスト
ロームのＹ2Ｏ3層１０、厚さ１００〜１５００オングス
トロームの銀被膜２、および樹脂コーティング層３が順
に積層して形成されている。1 to 6 are enlarged cross-sectional views showing specific examples of the sheet for producing a gold and silver yarn according to the present invention. In FIG. 1, reference numeral 1 is a film, and a Y 2 O 3 layer 10 having a thickness of 5 to 200 angstroms, a silver coating 2 having a thickness of 100 to 1500 angstroms, and a resin coating layer 3 are sequentially formed on one surface of the film 1. It is formed by stacking.
【００１１】Ｙ2Ｏ3層１０の厚さが５オングストローム
未満であると、銀被膜２の耐食性を向上する効果が得ら
れず、２００オングストロームより厚くてもそれ以上耐
食性は向上しない。なお、５〜２００オングストローム
といったきわめて薄い蒸着膜では、Ｙ2Ｏ3層１０は必ず
しも緻密な膜とならず、多孔膜になっていると考えられ
る。それにも拘らず耐食性向上効果が得られるのは、
銀被膜２の蒸着時に銀原子がＹ2Ｏ3と化学的な結合を生
じ、Ｙ2Ｏ3層１０と接する銀被膜面にキンクやステップ
等の高活性部が生じにくくなる作用、およびＹ2Ｏ3層
１０の介在によって銀被膜２がフィルム１から剥離しに
くくなる作用、の相乗効果であると推測される。Ｙ2Ｏ3
層１０の厚さは、より好ましくは１０〜１００オングス
トロームである。Ｙ2Ｏ3層１０の形成方法は限定されな
いが、Ｙ2Ｏ3ターゲットの融点が高いことから、一般に
は電子ビーム加熱法が好適である。If the thickness of the Y 2 O 3 layer 10 is less than 5 angstroms, the effect of improving the corrosion resistance of the silver coating 2 cannot be obtained, and if it is more than 200 angstroms, the corrosion resistance is not improved any more. It is considered that the Y 2 O 3 layer 10 is not necessarily a dense film and is a porous film in an extremely thin deposited film of 5 to 200 Å. Nevertheless, the effect of improving corrosion resistance can be obtained
Silver atoms when the deposition silver coating 2 occurs a chemical bond and Y 2 O 3, action of highly active part is less likely to occur, such as kinks and steps silver coating surface in contact with the Y 2 O 3 layer 10, and Y 2 It is presumed that there is a synergistic effect that the silver coating 2 is less likely to be peeled from the film 1 due to the inclusion of the O 3 layer 10. Y 2 O 3
The thickness of layer 10 is more preferably 10-100 angstroms. The method for forming the Y 2 O 3 layer 10 is not limited, but the electron beam heating method is generally preferable because the melting point of the Y 2 O 3 target is high.
【００１２】フィルム１は、従来の金銀糸用シートと同
様の材質で形成されたもので、具体的にはポリエステ
ル，ポリエチレンテレフタレート，ポリ塩化ビニル，Ｏ
ＰＰ（二軸延伸ポリプロピレン），ＣＰＰ（無延伸ポリ
プロピレン）等のプラスチック等が好適で、厚さは一般
には２〜５０μｍ程度とされる。ただし、本発明ではフ
ィルムの材質や厚さは限定されない。The film 1 is made of the same material as a conventional gold / silver yarn sheet, and specifically, polyester, polyethylene terephthalate, polyvinyl chloride, O.
A plastic such as PP (biaxially stretched polypropylene) or CPP (unstretched polypropylene) is suitable, and the thickness thereof is generally about 2 to 50 μm. However, the material and thickness of the film are not limited in the present invention.
【００１３】銀被膜２は必ずしも純銀で形成されていな
くてもよく、他の金属元素、例えばＣｕ，Ａｌ，Ｐｂ，
Ｐｄ等を添加した銀合金で形成することも可能である。
特に銀被膜２にＳｎ，Ｇａのいずれかまたは双方を合計
０．４〜１２ｗｔ％添加した場合には、銀被膜そのもの
の耐食性が向上するため、Ｙ2Ｏ3層１０の効果と相まっ
て変色を防ぐ効果がいっそう向上できる。添加率が０．
４ｗｔ％未満では耐食性向上効果が得られず、１２ｗｔ
％より多いと銀被膜の光沢が変化し美観を低下させる。The silver coating 2 does not necessarily have to be formed of pure silver, but may be formed of another metal element such as Cu, Al, Pb,
It is also possible to use a silver alloy to which Pd or the like is added.
In particular, when one or both of Sn and Ga are added to the silver coating 2 in a total amount of 0.4 to 12 wt%, the corrosion resistance of the silver coating itself is improved, and the discoloration is prevented in combination with the effect of the Y 2 O 3 layer 10. The effect can be further improved. The addition rate is 0.
If it is less than 4 wt%, the effect of improving corrosion resistance cannot be obtained, and
%, The gloss of the silver coating changes and the aesthetics deteriorates.
【００１４】銀被膜２の厚さが１００オングストローム
未満では、銀光沢が低下して好ましくない。１５００オ
ングストロームより厚くする必要はなく、徒にコストが
上昇するのみである。銀被膜２の厚さはより好ましくは
５００〜１０００オングストロームとされる。また、銀
被膜２の形成方法は、公知のいかなる蒸着方法でも可能
である。When the thickness of the silver coating 2 is less than 100 angstroms, the silver luster is lowered, which is not preferable. It does not need to be thicker than 1500 angstroms, only costly. The thickness of the silver coating 2 is more preferably 500 to 1000 angstrom. The silver coating 2 can be formed by any known vapor deposition method.
【００１５】樹脂コーティング層３としては、アクリル
樹脂，エポキシ樹脂，ウレタン樹脂，尿素−メラミン樹
脂，アミノ樹脂，フェノール樹脂等の樹脂の単独または
混合物が好適であるが、必ずしもこれら材質に限定する
必要はない。The resin coating layer 3 is preferably made of a resin such as an acrylic resin, an epoxy resin, a urethane resin, a urea-melamine resin, an amino resin or a phenol resin, or a mixture thereof, but is not necessarily limited to these materials. Absent.
【００１６】フィルム１とＹ2Ｏ3層１０との間には、こ
れらの接合強度を更に高めるためのアンダーコーティン
グ層が形成されていてもよく、その材質としては、樹脂
コーティング層３と同様の材質や、アミノ樹脂，イソシ
アネート樹脂，フェノール樹脂等が好適である。また、
金糸として使用する場合には、フィルム１のＹ2Ｏ3層１
０とは反対側の面、あるいはフィルム１とＹ2Ｏ3層１０
との間に、赤色系等の顔料を含有する透明な着色層を設
けてもよい。An undercoating layer may be formed between the film 1 and the Y 2 O 3 layer 10 to further enhance the bonding strength between them, and the material thereof is the same as that of the resin coating layer 3. Suitable materials are amino resins, isocyanate resins, phenol resins and the like. Also,
When used as a gold thread, Y 2 O 3 layer 1 of film 1
Surface opposite to 0, or film 1 and Y 2 O 3 layer 10
A transparent coloring layer containing a red pigment or the like may be provided between and.
【００１７】上記のようにして構成される片面型シート
を２枚用意し、これらのフィルム１側を対向させ、繊維
層を挟んでこれらを接着し、両面型シートとしてもよ
い。繊維層としては、和紙，洋紙，合成繊維の不織布等
からなり、厚さは１０〜２００μｍ程度、望ましくは１
５〜１００μｍのものが使用される。１０μｍよりも薄
いと十分な補強効果が得られず、２００μｍよりも厚い
と得られる布材が強張って手触りが悪化する。Two double-sided sheets may be prepared by preparing two single-sided sheets having the above-described structure, making these film 1 sides face each other, and adhering them with a fiber layer interposed therebetween. The fiber layer is made of Japanese paper, foreign paper, synthetic fiber non-woven fabric or the like, and has a thickness of about 10 to 200 μm, preferably 1
Those having a thickness of 5 to 100 μm are used. When the thickness is less than 10 μm, a sufficient reinforcing effect cannot be obtained, and when the thickness is more than 200 μm, the obtained cloth material is stretched and the touch is deteriorated.
【００１８】繊維層を接着するための接着剤としては、
塩化ビニル−酢酸ビニル系の共重合物接着剤，エポキシ
系接着剤など従来使用されているいずれでもよい。必要
であれば、同一の層構成からなる片面型シート同士を張
り合わせるだけでなく、層構成の異なる片面型シートを
張り合わせて両面型シートを形成してもよい。As an adhesive for adhering the fiber layers,
Any conventionally used adhesive such as a vinyl chloride-vinyl acetate based copolymer adhesive or an epoxy adhesive may be used. If necessary, not only the single-sided sheets having the same layer structure may be bonded to each other, but also the single-sided sheets having different layer structures may be bonded to form a double-sided sheet.
【００１９】さらにマイクロスリッター等を用いて、両
面型シートを例えば０．５ｍｍ以下の幅に切断すれば、
金銀平糸が得られる。また、片面シートを同様に裁断し
た金銀平糸を絹糸等の芯糸の周囲に螺旋状に巻き付けれ
ば、金銀撚糸が得られる。さらに、これらの金銀平糸ま
たは金銀撚糸を横糸(あるいは縦糸)とし、通常の絹糸等
の糸を縦糸(または横糸)として織機にかければ、金銀装
飾を有する織布が得られる。If a double-sided sheet is cut into a width of, for example, 0.5 mm or less using a micro slitter or the like,
Gold and silver flat yarn is obtained. Moreover, a gold-silver twisted yarn is obtained by spirally winding a gold-silver flat yarn obtained by similarly cutting a single-sided sheet around a core yarn such as silk yarn. Furthermore, when these gold-silver flat yarns or gold-silver twisted yarns are used as wefts (or warp yarns) and ordinary silk yarns or the like as warp yarns (or weft yarns) and applied to a loom, a woven fabric with gold-silver decoration is obtained.
【００２０】上記構成からなる金銀糸製造用シート，金
銀糸，織布によれば、フィルム１と銀被膜２の間にＹ2
Ｏ3層１０を蒸着形成したことにより、フィルム１と銀
被膜２との界面に沿って銀被膜２が腐食する現象を防ぐ
ことができ、長期に亙って変色を防止することが可能で
ある。According to the gold-silver yarn production sheet, the gold-silver yarn, and the woven fabric having the above-mentioned constitution, Y 2 is provided between the film 1 and the silver coating 2.
By forming the O 3 layer 10 by vapor deposition, it is possible to prevent the phenomenon that the silver coating 2 corrodes along the interface between the film 1 and the silver coating 2, and it is possible to prevent discoloration over a long period of time. .
【００２１】次に図２に示す例は、銀被膜２と樹脂コー
ティング層３の間に、厚さ５〜２００オングストローム
のＹ2Ｏ3層１２を蒸着形成したことを特徴とする。この
例は、樹脂コーティング層３と銀被膜２との界面に沿っ
て腐食が進行するのを防止することを目的としたもので
ある。他の構成は、上記図１の例と同じである。図２の
構造を有する金銀糸製造用シート，金銀糸，織布によれ
ば、銀被膜２と樹脂コーティング層３の間にＹ2Ｏ3層１
２を蒸着形成したことにより、銀被膜２と樹脂コーティ
ング層３の界面に沿って銀被膜２が腐食する現象を防ぐ
ことができ、長期に亙って変色を防止できる。Next, the example shown in FIG. 2 is characterized in that a Y 2 O 3 layer 12 having a thickness of 5 to 200 angstroms is formed by vapor deposition between the silver coating 2 and the resin coating layer 3. This example is intended to prevent corrosion from proceeding along the interface between the resin coating layer 3 and the silver coating 2. Other configurations are the same as those in the example of FIG. According to the gold-silver yarn manufacturing sheet, the gold-silver yarn, and the woven fabric having the structure of FIG. 2, the Y 2 O 3 layer 1 is provided between the silver coating 2 and the resin coating layer 3.
By vapor-depositing No. 2, it is possible to prevent a phenomenon in which the silver coating 2 corrodes along the interface between the silver coating 2 and the resin coating layer 3, and it is possible to prevent discoloration over a long period of time.
【００２２】次に図３に示す例は、フィルム１と銀被膜
２の間、および銀被膜２と樹脂コーティング層３の間の
双方に、厚さ５〜２００オングストロームのＹ2Ｏ3層１
０，１２をそれぞれ蒸着形成したことを特徴とする。他
の構成は図１の例と同じである。図３の構造を有する金
銀糸製造用シート，金銀糸，織布によれば、フィルム１
と銀被膜２との界面、および銀銀被膜２と樹脂コーティ
ング層３の界面の双方に沿って銀被膜２が腐食する現象
を防ぐことができる。Next, in the example shown in FIG. 3, a Y 2 O 3 layer 1 having a thickness of 5 to 200 angstroms is provided both between the film 1 and the silver coating 2 and between the silver coating 2 and the resin coating layer 3.
It is characterized in that 0 and 12 are formed by vapor deposition. Other configurations are the same as those in the example of FIG. The gold-silver yarn manufacturing sheet, the gold-silver yarn, and the woven fabric having the structure shown in FIG.
It is possible to prevent the phenomenon in which the silver coating 2 corrodes along both the interface between the silver coating 2 and the silver coating 2, and the interface between the silver-silver coating 2 and the resin coating layer 3.
【００２３】次に図４に示す例は、フィルム１と銀被膜
２の間に厚さ５〜２００オングストロームのＹ2Ｏ3層１
０を蒸着形成するとともに、銀被膜２と樹脂コーティン
グ層３の間に厚さ５〜１００オングストロームのＳｎ層
１４を蒸着形成したことを特徴とする。このような構造
を有する金銀糸製造用シート，金銀糸，織布によれば、
フィルム１と銀被膜２との界面に沿って銀被膜２が腐食
する現象を防ぐことができるだけでなく、銀被膜２上に
形成したＳｎ層１６によって銀被膜２の耐食性を向上す
ることができ、これら効果の相乗によりさらに高い変色
防止効果が得られる。Next, in the example shown in FIG. 4, a Y 2 O 3 layer 1 having a thickness of 5 to 200 angstroms is provided between the film 1 and the silver coating 2.
0 is vapor-deposited and a Sn layer 14 having a thickness of 5 to 100 angstrom is vapor-deposited between the silver coating 2 and the resin coating layer 3. According to the gold-silver yarn manufacturing sheet, the gold-silver yarn, and the woven fabric having such a structure,
Not only can the corrosion of the silver coating 2 along the interface between the film 1 and the silver coating 2 be prevented, but the Sn layer 16 formed on the silver coating 2 can improve the corrosion resistance of the silver coating 2. By synergizing these effects, a higher discoloration preventing effect can be obtained.
【００２４】次に図５に示す例は、フィルム１と銀被膜
２の間に厚さ５〜１００オングストロームのＳｎ層１６
を蒸着形成するとともに、銀被膜２と樹脂コーティング
層３の間に厚さ５〜２００オングストロームのＹ2Ｏ3層
１２を蒸着形成したことを特徴とする。このような構造
を有する金銀糸製造用シート，金銀糸，織布によれば、
フィルム１と銀被膜２との界面に沿って銀被膜２が腐食
する現象を防ぐことができるだけでなく、銀被膜２上に
形成したＳｎ層１６によって銀被膜２の耐食性を向上す
ることができ、これら効果の相乗によりさらに高い変色
防止効果が得られる。Ｓｎ層１６による耐食性向上効果
のメカニズムは明確ではないが、Ｓｎの還元作用により
銀の酸化（硫化、塩化を含む）が防止されるものと推測
される。Next, in the example shown in FIG. 5, the Sn layer 16 having a thickness of 5 to 100 angstroms is provided between the film 1 and the silver coating 2.
And a Y 2 O 3 layer 12 having a thickness of 5 to 200 angstroms is vapor deposited between the silver coating 2 and the resin coating layer 3. According to the gold-silver yarn manufacturing sheet, the gold-silver yarn, and the woven fabric having such a structure,
Not only can the corrosion of the silver coating 2 along the interface between the film 1 and the silver coating 2 be prevented, but the Sn layer 16 formed on the silver coating 2 can improve the corrosion resistance of the silver coating 2. By synergizing these effects, a higher discoloration preventing effect can be obtained. Although the mechanism of the effect of improving the corrosion resistance by the Sn layer 16 is not clear, it is presumed that the reduction action of Sn prevents the oxidation (including sulfurization and chloride) of silver.
【００２５】次に図６に示す例は、Ｙ2Ｏ3層１０の蒸着
と、銀被膜２の蒸着を一部重複して行うことにより、Ｙ
2Ｏ3層１０と銀被膜２との境界をなくし、これによりフ
ィルム１に対する銀被膜２の接合性をより向上したもの
である。上記のように一部重複した蒸着を行うには、同
一の蒸着装置内においてＹ2Ｏ3と銀を連続蒸着すればよ
い。Ｙ2Ｏ3の蒸着量は、単体として蒸着した際に、厚さ
５〜２００オングストロームとなる量であればよい。Next, in the example shown in FIG. 6, the deposition of the Y 2 O 3 layer 10 and the deposition of the silver coating 2 are partially overlapped to obtain Y
By eliminating the boundary between the 2 O 3 layer 10 and the silver coating 2, the bondability of the silver coating 2 to the film 1 is further improved. In order to carry out vapor deposition that partially overlaps as described above, Y 2 O 3 and silver may be vapor-deposited continuously in the same vapor deposition apparatus. The amount of Y 2 O 3 vapor deposited may be such that it has a thickness of 5 to 200 Å when vapor-deposited as a simple substance.
【００２６】[0026]
【実施例】次に、実施例を挙げて本発明の効果を実証す
る。厚さ１２μｍ×幅５２０ｍｍ×長さ６０００ｍｍの
ＰＥＴ製フィルムを、半連続巻き取り式蒸着機にセット
し、電子ビーム加熱方式により、所定厚さのＹ2Ｏ3層、
６００オングストロームの銀被膜、およびＳｎ層を適宜
形成し、さらに蒸着面にアクリル樹脂コーティング剤を
塗布して、厚さ１．０μｍのアクリル樹脂コーティング
層を形成した。得られた各種金銀糸製造用シートを６×
７ｃｍに裁断して試料片とし、以下の耐汗性試験および
耐硫化性試験、並びに目視による光沢評価を行った。EXAMPLES Next, the effects of the present invention will be demonstrated with reference to examples. A PET film having a thickness of 12 μm × a width of 520 mm × a length of 6000 mm was set on a semi-continuous winding type vapor deposition machine, and a Y 2 O 3 layer having a predetermined thickness was set by an electron beam heating method.
A 600 angstrom silver film and a Sn layer were appropriately formed, and an acrylic resin coating agent was applied to the vapor deposition surface to form an acrylic resin coating layer having a thickness of 1.0 μm. 6 × the obtained sheets for manufacturing various gold and silver yarns
A sample piece was cut into 7 cm, and the following sweat resistance test and sulfidation resistance test, and visual gloss evaluation were performed.
【００２７】耐汗性試験：試料を下記組成からなる耐汗
性試験液に４０℃で４時間浸漬し、フィルム側から目視
することにより銀被膜の変色程度を５段階に評価した。
評価１が全面変色、評価５が全く変色なしであることを
示す。 （耐汗性試験液組成） 酢酸：１０ｇ リン酸三ナトリウム：１６ｇ 工業用食塩：１６ｇ 蒸留水：８００ｍｌSweat resistance test: A sample was dipped in a sweat resistance test solution having the following composition for 4 hours at 40 ° C., and visually observed from the film side to evaluate the degree of discoloration of the silver coating in five levels.
Evaluation 1 indicates that the entire surface is discolored, and evaluation 5 indicates that there is no discoloration at all. (Sweat resistance test liquid composition) Acetic acid: 10 g Trisodium phosphate: 16 g Industrial salt: 16 g Distilled water: 800 ml
【００２８】耐硫化性試験：試料を下記組成からなる耐
硫化性試験液に４０℃で５時間浸漬し、変色程度を５段
階で評価した。評価１が全面変色、評価５が全く変色な
しであることを示す。 （耐硫化性試験液） 「六−０ハップ」（硫化物を含有する武藤＜金正＞製薬
品株式会社製入浴剤の商品名）の１０ｗｔ％水溶液（＜
＞内は漢字１字）。 上記各試験の結果を表１に示す。試料番号中の「実」は
本発明の実施例であることを示し、「比」は本発明の範
囲から外れた比較例を示す。光沢評価は、１…不適、２
…やや劣る、３…可、４…やや優れる、５…優れる、で
表している。Sulfuration resistance test: A sample was immersed in a sulfurization resistance test liquid having the following composition for 5 hours at 40 ° C., and the degree of discoloration was evaluated in 5 grades. Evaluation 1 indicates that the entire surface is discolored, and evaluation 5 indicates that there is no discoloration at all. (Sulfidation resistance test liquid) 10 wt% aqueous solution of "6--0 Happ" (trade name of bath salt manufactured by Mutoh <Kinmasa> Chemicals Co., Ltd. containing sulfide) (<
> Is one kanji). The results of each of the above tests are shown in Table 1. In the sample numbers, "real" indicates that the present invention is an example, and "ratio" indicates a comparative example that is out of the range of the present invention. Gloss evaluation is 1 ... inappropriate, 2
… Slightly inferior, 3 ... Acceptable, 4 ... Slightly excellent, 5 ... Excellent.
【００２９】[0029]
【表１】 [Table 1]
【００３０】上表から明らかなように、本発明の実施例
３〜７，９，１０，１２ではいずれも優れた耐汗性およ
び耐硫化性を示し、光沢も優れていた。これに対し、比
較例１，２，１３では耐汗性および耐硫化性が低く、比
較例８，１１では光沢が低下した。As is clear from the above table, Examples 3 to 7, 9, 10, and 12 of the present invention all showed excellent sweat resistance and sulfidation resistance, and had excellent gloss. In contrast, Comparative Examples 1, 2 and 13 had low sweat resistance and sulfidation resistance, and Comparative Examples 8 and 11 had low gloss.
【００３１】[0031]
【発明の効果】以上説明したように、本発明に係る金銀
糸製造用シート，金銀糸および金銀装飾を有する織布に
よれば、汗や酸素、硫化水素に接した場合にもシート裁
断面からの腐食の進行を防止することができ、長期に亙
って変色を防ぐことができる。As described above, according to the gold-silver yarn manufacturing sheet, the gold-silver yarn and the woven fabric having the gold-silver decoration according to the present invention, the sheet cut surface can be cut even when it is contacted with sweat, oxygen or hydrogen sulfide. It is possible to prevent the progress of corrosion and prevent discoloration over a long period of time.
【図１】本発明に係る金銀糸製造用シートの一例を示す
断面拡大図である。FIG. 1 is an enlarged cross-sectional view showing an example of a gold-silver yarn manufacturing sheet according to the present invention.
【図２】本発明に係る金銀糸製造用シートの一例を示す
断面拡大図である。FIG. 2 is an enlarged cross-sectional view showing an example of a gold-silver yarn manufacturing sheet according to the present invention.
【図３】本発明に係る金銀糸製造用シートの一例を示す
断面拡大図である。FIG. 3 is an enlarged cross-sectional view showing an example of a gold-silver yarn manufacturing sheet according to the present invention.
【図４】本発明に係る金銀糸製造用シートの一例を示す
断面拡大図である。FIG. 4 is an enlarged cross-sectional view showing an example of the gold-silver yarn manufacturing sheet according to the present invention.
【図５】本発明に係る金銀糸製造用シートの一例を示す
断面拡大図である。FIG. 5 is an enlarged cross-sectional view showing an example of the gold-silver yarn manufacturing sheet according to the present invention.
【図６】本発明に係る金銀糸製造用シートの一例を示す
断面拡大図である。FIG. 6 is an enlarged cross-sectional view showing an example of the gold-silver yarn manufacturing sheet according to the present invention.
【図７】従来の金銀糸製造用シートの一例を示す断面拡
大図である。FIG. 7 is an enlarged cross-sectional view showing an example of a conventional gold / silver yarn manufacturing sheet.
【図８】従来の金銀糸製造用シートの一例を示す断面拡
大図である。FIG. 8 is an enlarged cross-sectional view showing an example of a conventional gold-silver yarn manufacturing sheet.
【図９】従来の金銀糸製造用シートの一例を示す断面拡
大図である。FIG. 9 is an enlarged cross-sectional view showing an example of a conventional gold-silver yarn manufacturing sheet.
───────────────────────────────────────────────────── フロントページの続き (72)発明者 古内 哲哉 福島県会津若松市扇町128の７ 三菱伸銅 株式会社若松製作所内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Tetsuya Furuuchi 128-7 Ogimachi, Aizuwakamatsu, Fukushima Mitsubishi Shindoh Co., Ltd. Wakamatsu Manufacturing Co., Ltd.
Claims (8)
に設けられた厚さ１００〜１５００オングストロームの
銀被膜と、この銀被膜上に設けられた樹脂コーティング
層とを具備する金銀糸製造用シートにおいて、 前記フィルムと前記銀被膜の間に、厚さ５〜２００オン
グストロームのＹ2Ｏ3層を蒸着形成したことを特徴とす
る金銀糸製造用シート。1. A sheet for producing gold and silver yarns, comprising a synthetic resin film, a silver coating having a thickness of 100 to 1500 angstroms provided on the film, and a resin coating layer provided on the silver coating. 2. A sheet for producing a gold-silver yarn, wherein a Y 2 O 3 layer having a thickness of 5 to 200 angstrom is formed by vapor deposition between the film and the silver coating.
に設けられた厚さ１００〜１５００オングストロームの
銀被膜と、この銀被膜上に設けられた樹脂コーティング
層とを具備する金銀糸製造用シートにおいて、 前記銀被膜と前記樹脂コーティング層の間に、厚さ５〜
２００オングストロームのＹ2Ｏ3層を蒸着形成したこと
を特徴とする金銀糸製造用シート。2. A sheet for producing a gold and silver thread, comprising a synthetic resin film, a silver coating having a thickness of 100 to 1500 angstroms provided on the film, and a resin coating layer provided on the silver coating. In the above, between the silver coating and the resin coating layer, a thickness of 5 to
A gold-silver yarn manufacturing sheet, characterized in that a Y 2 O 3 layer having a thickness of 200 Å is formed by vapor deposition.
前記銀被膜と前記樹脂コーティング層の間に、厚さ５〜
２００オングストロームのＹ2Ｏ3層をさらに蒸着形成し
たことを特徴とする金銀糸製造用シート。3. The gold-silver yarn manufacturing sheet according to claim 1, wherein
Between the silver coating and the resin coating layer, a thickness of 5 to
A gold-silver yarn manufacturing sheet, further comprising a 200 Å Y 2 O 3 layer formed by vapor deposition.
おいて、前記銀被膜と前記樹脂コーティング層の間に、
厚さ５〜１００オングストロームのＳｎ層をさらに蒸着
形成したことを特徴とする金銀糸製造用シート。4. The sheet for producing a gold-silver yarn according to claim 1 or 2, wherein between the silver coating and the resin coating layer,
A gold-silver yarn manufacturing sheet, characterized in that a Sn layer having a thickness of 5 to 100 angstroms is further formed by vapor deposition.
おいて、前記銀被膜と前記フィルムの間に、厚さ５〜１
００オングストロームのＳｎ層をさらに蒸着形成したこ
とを特徴とする金銀糸製造用シート。5. The sheet for producing a gold-silver yarn according to claim 1 or 2, wherein a thickness of 5 to 1 is provided between the silver coating and the film.
A gold-silver yarn production sheet, further comprising a Sn layer of 00 angstrom formed by vapor deposition.
糸製造用シートを一対、前記フィルム側を対向させ、こ
れらの間に繊維層を介在させた状態で張り合わせ、この
複合シートを細く裁断してなる金銀平糸。6. A composite sheet obtained by laminating a pair of sheets for producing a gold-silver yarn according to claim 1, 2, 3, 4 or 5 with the film sides facing each other and interposing a fiber layer therebetween. Gold and silver flat yarns made by cutting finely.
糸製造用シートを細く裁断し、芯糸の外周に巻回したこ
とを特徴とする金銀撚糸。7. A gold-silver twisted yarn, characterized in that the gold-silver yarn production sheet according to claim 1, 2, 3, 4 or 5 is finely cut and wound around an outer periphery of a core yarn.
記載の金銀撚糸を布体の中に織り込んだことを特徴とす
る金銀装飾を有する織布。8. The gold-silver flat yarn according to claim 6, or claim 7.
A woven fabric having a gold-silver decoration, characterized in that the described gold-silver twisted yarn is woven into a fabric body.