JP4407979B2 - Metal-coated yarn manufacturing sheet and metal-coated yarn and woven fabric - Google Patents
Metal-coated yarn manufacturing sheet and metal-coated yarn and woven fabric Download PDFInfo
- Publication number
- JP4407979B2 JP4407979B2 JP02079099A JP2079099A JP4407979B2 JP 4407979 B2 JP4407979 B2 JP 4407979B2 JP 02079099 A JP02079099 A JP 02079099A JP 2079099 A JP2079099 A JP 2079099A JP 4407979 B2 JP4407979 B2 JP 4407979B2
- Authority
- JP
- Japan
- Prior art keywords
- metal
- yarn
- coated
- sheet
- film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【0001】
【発明の属する技術分野】
本発明は、金属被覆糸およびこれを用いた布に関するもので、特に、優れた耐食性および柔軟性を有し、衣服などに好適に使用される金属被覆糸および布に関する。
【0002】
【従来の技術】
和服等に使用される織布の一種として、金銀色の模様を形成したものがある。このような織布は、通常、金糸または銀糸を横糸、絹糸を縦糸として織り、部分的に金糸または銀糸(以下、両者を合わせて金銀糸と称する)を織布の表面側に露出させて模様を形成したものである。
【0003】
前記金銀糸の多くは、プラスチック製のフィルムに銀を蒸着し、この銀被膜上に樹脂コーティングを施した金銀糸製造用シートを裁断して製造されている。図8〜図10は、それぞれ異なる従来の金銀糸製造用シートの断面を示している。これらの金銀糸製造用シートは、いずれも片面型シートと呼ばれるものであり、これら片面型シートを2枚用意し、金銀光沢を有する面を外側にして、接着剤で張り合わせた両面型シートも市販されている。本明細書中の金銀糸製造用シートとは、これら片面型シートおよび両面型シートの両者を総称するものとする。
【0004】
図8に示す片面型シートは、透明なPET等からなる樹脂フィルム41上に銀被膜42を蒸着し、さらに銀被膜42を保護するアクリル系樹脂の樹脂コーティング層43を形成したものである。また、図9のシートは、樹脂フィルム41の裏面に着色層7が形成されたものであり、図10のシートは、樹脂フィルム41と銀被膜42との間に着色層7が形成されたものである。着色層7は、例えば金糸の場合には赤色系の着色料を塗布乾燥して形成され、シートを銀被膜42の着色層7側から見ることにより、シートは金色に発色する。
これらの片面型シートを2枚用意し、金銀光沢を有する面を外側にして、支持層の両面に接着することにより両面型シートが得られる。
【0005】
上記の金銀糸製造用シートを細く裁断し、絹糸等の芯糸に螺旋状に巻き付ければ、金銀撚糸となる。
金銀織布には、通常このような撚糸が用いられている。
【0006】
【発明が解決しようとする課題】
ところで、近年、上記のような金銀糸は、和服のみならず洋服にも多用されるようになってきている。
しかしながら、上記のような金銀糸は、洋服に使用するには、剛直で柔軟性に欠けることが問題となっていた。
このような問題を解決するために、金銀糸製造用シートを構成している樹脂フィルムの厚さを薄くすることが考えられるが、前記樹脂フィルムの厚さを薄くすると、銀被膜上に樹脂コーティングを施す際の熱により、前記樹脂フィルムが変形し、皺になりやすくなるという不都合が生じる。
【0007】
さらに、洋服は、和服と比較して洗濯の頻度が高いうえ、汗などが直接付着することも多い。このため、和服では十分使用に耐える金銀糸も、洋服に使用すると変色しやすいという問題があった。
【0008】
本発明は、上記事情に鑑みてなされたもので、上記の問題を解決し、柔軟性および耐久性に優れた金属被覆糸製造用シートを提供することを課題とする。
また、上記金属被覆糸製造用シートを用いた金属被覆糸、織布、不織布を提供することを課題とする。
【0009】
上記課題を解決するため、本発明の金属被覆糸製造用シートは、厚さ8μm以下のフィルムと、このフィルム上に設けられた金属薄膜と、この金属薄膜上に設けられたコーティング層とを具備する金属被覆糸製造用シートであり、前記コーティング層は、主成分となる樹脂に、この樹脂との編目構造を形成する反応の開始温度が前記樹脂の硬化温度よりも低いシランカップリング剤が、0.05〜2%含有されてなり、前記樹脂と前記シランカップリング剤及び前記シランカップリング剤同士が結合していることを特徴とする。
【0010】
また、上記課題を解決するため、本発明の金属被覆糸製造用シートは、厚さ8μm以下のフィルムと、このフィルム上に設けられた金属薄膜と、この金属薄膜上に設けられたコーティング層とを具備する金属被覆糸製造用シートであり、前記コーティング層は、第1コーティング層と第2コーティング層とからなり、前記第1コーティング層と前記第2コーティング層のいずれか一方または両方は、主成分となる樹脂に、この樹脂との編目構造を形成する反応の開始温度が前記樹脂の硬化温度よりも低いシランカップリング剤が、0.05〜2%含有されてなり、前記樹脂と前記シランカップリング剤及び前記シランカップリング剤同士が結合していることを特徴とする。
【0011】
上記の金属被覆糸製造用シートにおいては、前記金属薄膜と前記フィルムとの間と、前記金属薄膜と前記コーティング層との間の一方または両方に、Si,Al,Ba,Ca,Ce,In,Pb,Li,K,Mg,Na,Sn,Ti,Zn,Zr,Mo,Ta,W,Fe,Sr,V,Th,Sb,Pt,Bi,Y,Geおよびこれらの金属の酸化物,フッ化物,窒化物,炭化物から選択される1種または2種以上の物質からなる腐食防止層を形成してもよい。
また、上記の金属被覆糸製造用シートにおいては、前記金属薄膜と前記フィルムとの間に、アンダーコート層を形成してもよい。
さらに、上記の金属被覆糸製造用シートにおいては、装飾性を高めるために、前記金属薄膜を金銀光沢を有するものとしてもよい。ここでの金銀光沢を有するとは、金色または銀色の光沢を有することをいう。
【0012】
本発明の金属被覆平糸は、上記の金属被覆糸製造用シートが細く裁断されてなることを特徴とする。また、本発明の金属被覆撚糸は、上記の金属被覆平糸または上記の金銀被覆糸が、芯糸の外周に巻回されたことを特徴とする。
【0013】
【発明の実施の形態】
図1は、本発明の金属被覆糸製造用シートの一例を示した図である。
図1において、符号10は、金属被覆糸製造用シートを示している。この金属被覆糸製造用シート10は、フィルム1と、このフィルム1上に設けられた金属薄膜2と、この金属薄膜2上に設けられた第1コーティング層3aと第2コーティング層3bとからなるコーティング層3とからなるものである。
【0014】
フィルム1の材質は、特に限定されないが、例えば、ポリエステル、ポリエチレンテレフタレート、ナイロン、ポリ塩化ビニル、OPP(二軸延伸ポリプロピレン)、CPP(無延伸ポリプロピレン)、ビニロンなどの合成樹脂からなるフィルムなどが好適に用いられる。中でも、ポリエステルやポリエチレンテレフタレートは、熱的に安定であり、第1および第2コーティング層3a、3bの形成および取扱いが容易であり、好ましい。
【0015】
フィルム1の厚さは、8μm以下とするのが好ましい。より好ましくは、4〜7μm程度である。8μm程度を越える厚さとした場合、金属被覆糸20の柔軟性が不十分となるため好ましくない。
【0016】
金属薄膜2の種類は、特に限定されず、例えば、Cu、Ag、Zn、Sn、Ti、Al、Pd、Pb、Ni、Cr、Au、Pt、Fe、Co、Mo、Zrから選択される1種又は2種以上の合金が好適である。金属薄膜2の表面には、その金属のハロゲン化物、錯体、酸化物、硫化物などが形成されていてもよい。
【0017】
図1に示す金属被覆糸製造用シート10が金銀糸の製造に用いられる場合、金属薄膜2は、金色または銀色の光沢を有する、例えば、Cu、Ag、Zn、Su、Tiなどが好適に使用される。中でも、Agは、他の金属では得られ難いAg特有の深い光沢が得られるため好ましい。この場合、Agに、Sn、Gaのいずれかまたは双方を合計50wt%未満添加すると、銀薄膜そのものの耐食性が向上して変色を防ぐ効果が得られる。添加率が50wt%より多いと銀薄膜の光沢が変化して美観を低下させる。
【0018】
金属薄膜2の厚さは、特に限定されないが、100〜1500Å程度とすることが好ましい。より好ましくは300〜1000Å程度とされる。金属薄膜2の厚さが100Å程度未満であると、金属被覆糸製造用シート10の光沢および耐食性が低下するため好ましくない。一方、蒸着で形成する場合、金属薄膜2の厚さを1500Åより大きくしても、美観を向上させる効果や耐食性を向上させる効果が得られず、コストが上昇するのみであるので好ましくない。また、金属薄膜2の形成方法は、特に限定されないが、蒸着法などが好適である。
【0019】
第1および第2コーティング層3a、3bの材質は、特に限定されないが、例えば、ポリエステル樹脂、ブチラール樹脂、アクリル樹脂、エポキシ樹脂、ウレタン樹脂、尿素ーメラミン樹脂、アミノ樹脂、フェノール樹脂、塩化ビニル樹脂、ポリアセタール樹脂、ポリカーボネート樹脂、けい素樹脂、酢酸ビニル樹脂、フッ素樹脂、スチロール樹脂などの単独あるいは混合物などが好適に使用される。
【0020】
さらに、第1コーティング層3aと第2コーティング層3bのいずれか一方または両方には、主成分である樹脂にシランカップリング剤が含有されている。
シランカップリング剤としては、主成分である樹脂とのネットワーク構造(編目構造)を形成する反応の開始温度が、前記樹脂の硬化温度よりも低いものが使用される。樹脂にシランカップリング剤を含有させることにより、樹脂を硬化させる際に、主成分である樹脂の硬化温度よりも低い温度で、樹脂の水酸基、アミノ基、イソシアネート基などの反応基やジエン類とシランカップリング剤とが結合するとともに、シランカップリング剤同士が結合して、樹脂の硬化を促進し、硬化後の緻密な樹脂膜を形成すると推定される。
【0021】
前記シランカップリング剤としては、RSiX3(ただし、 Rは、ビニル基、グリシドキシ基、メタクリル基、アミノ基、メルカプト基などの有機官能性基を示し、Xは、塩素およびアルコキシ基を示す。)の式で示されるものなどが好適に使用される。より好ましくは、上記Rが、グリシドキシ基またはアミノ基であるシランカップリング剤である。
シランカップリング剤の添加量は、0.05〜2%程度の範囲が好ましい。より好ましくは、0.1〜0.15%程度の範囲である。添加量が0.05%程度未満であると、主成分である樹脂の硬化温度を十分に低下させることができなくなり、前記フィルムが皺になりやすくなる。また、緻密な樹脂膜を形成する効果が不十分となり、十分な耐久性を得ることが困難となる。一方、2%を越える添加量としても、コストが上昇するのみであるので好ましくない。
【0022】
シランカップリング剤は、上述したように、第1コーティング層3aと第2コーティング層3bのいずれか一方または両方に含有されている。
例えば、前記シランカップリング剤が、第1および第2コーティング層3a、3bの両方に含有されているものとした場合、いずれか一方のみに含有されているものと比較して、より一層耐久性を向上させることが可能となる。
また、少なくとも第2コーティング層3bにシランカップリング剤が含有されているものとした場合、金属被覆糸製造用シート10の表面を形成する第2コーティング層3bが緻密な樹脂膜となり、金属被覆糸製造用シート10の第2コーティング層3b側の表面全体を保護することができ、効果的に耐久性を向上させることができる。
さらに、シランカップリング剤を第1コーティング層3aと第2コーティング層3bのいずれか一方のみに含有した場合においては、両方に含有したものと比較して、シランカップリング剤を含有する工程と、シランカップリング剤の使用量とを削減することができ、安価なものとすることができる。
【0023】
第1コーティング層3aの厚さは、0.05〜2.5μm程度とするのが好ましい。より好ましくは、0.1〜1.5μm程度である。2.5μm程度を越える厚さとした場合、金属被覆糸20の柔軟性が不十分となるため好ましくない。一方、0.05μm未満の厚さとした場合、十分な保護効果が得られず、耐久性が低下するため好ましくない。
また、第2コーティング層3bの厚さは、第1コーティング層3aと同等程度とすることが好ましい。
【0024】
このような金属被覆糸製造用シート10は、第1コーティング層3aと第2コーティング層3bのいずれか一方または両方に、シランカップリング剤が含有されているので、以下のような効果を有するものとなる。
(1)シランカップリング剤が含有されたコーティング層を、主成分である樹脂の硬化温度よりも低い温度で形成することができ、コーティング層を形成する際の熱によりフィルム1が皺になることを防止できる。したがって、従来12μm程度であったフィルム1の厚さを、8μm以下と薄くすることが可能となり、柔軟性に優れた金属被覆糸製造用シート10を得ることができる。
(2)前記樹脂とシランカップリング剤とのネットワーク構造(編目構造)が形成されることにより、緻密な樹脂膜を形成することができ、耐久性に優れた金属被覆糸製造用シート10が得られる。
【0025】
また、上記の金属被覆糸製造用シート10では、コーティング層3は、第1コーティング層3aと第2コーティング層3bの2層からなるものであるので、1層からなるものと比較して、金属薄膜2を長期にわたって保護することができ、より耐久性に優れたものとなる。
【0026】
このような金属被覆糸製造用シート10は、上述したように、優れた耐久性および柔軟性を有するので、洗濯や汗に強く、しなやかで、和服、洋服を問わず様々な用途に使用可能な金属被覆糸の材料として、好適に使用されるものとなる。
【0027】
本発明の金属被覆糸製造用シートの構造は、図1に示す例にのみ限定されるものではなく、以下に示すように用途などに応じて適宜変更してもよい。
図2に示す金属被覆糸製造用シートは、図1に示す金属被覆糸製造用シート10の金属薄膜2とフィルム1との間に腐食防止層5を設けたものである。
【0028】
腐食防止層5は、Si,Al,Ba,Ca,Ce,In,Pb,Li,K,Mg,Na,Sn,Ti,Zn,Zr,Mo,Ta,W,Fe,Sr,V,Th,Sb,Pt,Bi,Y,Geおよびこれらの金属の酸化物,フッ化物,窒化物,炭化物から選択される1種または2種以上の物質などによって形成することが可能である。中でも特に、ZnO,SnOx(0<x≦2)、Sn,Y2O3,ZrO2,TiO2,Crなどが耐食性に優れるため好適である。
【0029】
腐食防止層5の厚さは、耐食性向上効果とコストの点から5〜200Åであることが好ましい。腐食防止層5の厚さが5Å未満であると、金属薄膜2の耐食性を向上する効果が得られず、200Åより厚くても、それ以上耐食性は向上しない。
このような腐食防止層5を設けることにより、より一層耐食性を高めることができる。
【0030】
前記腐食防止層5は、図2に示す例のように、金属薄膜2とフィルム1との間に設けることができるが、金属薄膜2と第1コーティング層3aとの間に設けてもよい。さらに、より一層耐食性を高めるために、金属薄膜2とフィルム1との間と、金属薄膜2と第1コーティング層3aとの間の両方に腐食防止層5を設けてもよい。
特に、金銀糸の製造に用いられる金属被覆糸製造用シートにおいて、腐食防止層5を金属薄膜2とフィルム1との間に設ける場合には、腐食防止層5の材質は、ZnOおよびSnOx(ただし0<x≦2)から選択される1種または2種の物質などが好ましい。これらの物質で形成された腐食防止層5は、透明度が高いため、フィルム1側から見た場合の金属薄膜2の光沢をほとんど阻害せず、良好な光沢が得られる。
【0031】
図3に示す金属被覆糸製造用シートは、フィルム1と金属薄膜2との間に、アンダーコート層6を設けたものである。アンダーコート層6の材質としては、第1および第2コーティング層3a、3bと同様の材質などが好ましく使用される。アンダーコート層6を設けることにより、フィルム1と金属薄膜2との接合強度を高めることができる。また、金属薄膜2の耐食性をより一層向上させることができる。
【0032】
上記の金属被覆糸製造用シートは、着色して使用される金属被覆糸製造用シートの場合には、図4に示すようにフィルム1の金属薄膜2側の面、または、フィルム1の金属薄膜2と反対側の面に、染料や顔料などを含有する着色層7を設けてもよい。
【0033】
また、上記の金属被覆糸製造用シートを2枚用意し、それらを接着することにより得られた両面型シートとしてもよい。両面型シートに用いられる2枚の金属被覆糸製造用シートは、同じ構成のものでもよいし、異なる構成のものでもよい。
図5に示す金属被覆糸製造用シートは、図1に示す金属被覆糸製造用シートを2枚用意し、これらのフィルム1側を対向させ、支持層8を挟んで接合した両面型シートである。
【0034】
支持層8としては和紙、洋紙、合成繊維の不織布などが使用可能であり、厚さは限定されないが5〜200μm程度のものが好適である。支持層8の厚さが5μm未満であると補強効果が低下し、200μmを越えるとシートが堅くなり、製造しにくくなる。また、このシートから製造した糸を衣服などに使用した場合に手触りが悪くなる。
支持層8を接着するための接着剤としては、塩化ビニル−酢酸ビニル系の共重合物接着剤、エポキシ系接着剤などの従来から使用されているいずれのものでもよい。
【0035】
上記の金属被覆糸製造用シートでは、コーティング層3を第1コーティング層3aと第2コーティング層3bの2層からなるものとしたが、シランカップリング剤を含有する1層からなるものとしてもよいし、上記の金属被覆糸製造用シートに、さらに1層以上のコーティング層を設けて3層以上としてもよく、特に限定されない。1層のみとした場合、コーティング層を形成するための手間やコストを削減することができ、3層以上とした場合、より一層耐久性を向上させることができる。
【0036】
なお、上記の金属被覆糸製造用シートの構成を用途などに応じて適宜組み合わせることが可能であるのは勿論である。
【0037】
本発明の金属被覆平糸10aは、図6に示すように、図1に示す金属被覆糸製造用シート10を、マイクロスリッターなどを用いて細く裁断したものである。前記金属被覆平糸10aの太さは限定されないが、一般には0.5mm以下の幅とされることが好ましい。このような金属被覆平糸10aは、上記の金属被覆糸製造用シート10を用いたものであるので、良好な耐久性および柔軟性を有する。
【0038】
本発明の金属被覆撚糸20aは、図7に示すように、図6に示す金属被覆平糸10aを、芯糸11の外周に螺旋状に巻回したものである。
芯糸11は、2本の糸11a、11bからなっている。芯糸11の材質としては、特に限定されないが、天然ゴム、ウレタンゴム、ブタジエンスチレンゴム、ブチルゴム、ニトリルゴム、クロロプレンゴム、シリコーンゴム、フッ素ゴム、ステレオゴムなどの一般的なゴムや、ナイロン、ポリエステル、レーヨン、キュープラ、絹、綿、アセテート系繊維、ビニロン、ビニリデン、アクリル、ポリエチレン、ポリプロピレン、ポリウレタン、炭素繊維、ガラス繊維、金属繊維などが好適に使用される。中でも、ゴムなどの伸縮性を有する材質は、より良好な柔軟性および伸縮性を有する金属被覆撚糸20aを得ることができるため好ましい。
このような金属被覆撚糸20aは、上記の金属被覆糸製造用シート10を用いたものであるので、良好な耐久性および柔軟性を有する。
【0039】
なお、芯糸11の構造は、図7に示す例にのみ限定されるものではなく、例えば、1本の糸からなるものとしてもよいし、3本以上の糸からなるものとしてもよく、用途などに応じて適宜変更してよい。また、芯糸11は、様々な繊維とともに金属被覆平糸10aを撚り合わせてなるものも使用できる。
【0040】
本発明の金銀被覆糸は、上記の金属被覆糸製造用シートを用いた金属被覆平糸と金属被覆撚糸とに限定されるものではなく、基体と、この基体上に設けられた金属薄膜と、この金属薄膜上に設けられたコーティング層とを具備してなり、前記コーティング層に、シランカップリング剤が含有された金銀被覆糸としてもよい。さらに、この金銀被覆糸を芯糸の外周に巻回してなる金属被覆撚糸としてもよい。
この場合、基体は、糸状の形状とされることが好ましく、基体上に設けられた層の構成および材質は、上記の金属被覆糸製造用シートのフィルム上に設けられた層の構成および材質と同様としてよい。また、前記基体を形成する材質は、上述したフィルム1と同様の材質などが好適に使用される。
【0041】
本発明の織布は、上記の金属被覆平糸10a、金属被覆撚糸20a、金属被覆糸から選択される少なくとも一種が、布体の中に織り込まれたものである。このような織布は、横糸と縦糸のどちらか一方または両方を上記の金属被覆平糸10aまたは金属被覆撚糸20aとして、織機にかけることによって得られる。
このような織布は、前記金属被覆平糸10a、金属被覆撚糸20a、金属被覆糸から選択される少なくとも一種が、布体の中に織り込まれてなるものであるので、従来の金銀糸を用いた織布と比較して、良好な柔軟性および耐久性を有する。また、前記金属被覆平糸10a、金属被覆撚糸20a、金属被覆糸として、金銀光沢を有する金銀糸を用いれば、金銀装飾を有する織布が得られる。
【0042】
本発明の不織布は、上記の金属被覆平糸10a、金属被覆撚糸20a、金属被覆糸から選択される少なくとも一種が、不織布を構成する繊維原料中に含まれてなるものである。このような不織布を製造するには、上記の金属被覆平糸10a、金属被覆撚糸20a、金属被覆糸から選択される少なくとも一種を繊維原料の全部または一部として、接着剤を含む不織布原料中に添加し、これを抄紙する方法などによって得られる。
このような不織布も、上記の金属被覆平糸20a、金属被覆撚糸20a、金属被覆糸から選択される少なくとも一種を用いたものであるので、従来の金銀糸12を用いた織布と比較して、良好な柔軟性および耐久性を有するものとなる。また、前記金属被覆平糸10a、金属被覆撚糸20a、金属被覆糸として、金銀光沢を有する金銀糸を用いれば、金銀装飾を有する不織布が得られる。
【0043】
本発明の織布や不織布は、良好な柔軟性および耐久性を有するものであるので、和服、洋服を問わず使用することが可能であり、例えば、着物、帯、アンダーウェア、アウターウェア、靴下などの衣服や、カーテン、布団カバー、シーツ、マット類、タオルなどの様々な用途に使用できる。
【0044】
【発明の効果】
以上説明したように、本発明の金属被覆糸製造用シートは、コーティング層に、シランカップリング剤が含有されているので、コーティング層の主成分である樹脂の硬化温度よりも低い温度でコーティング層を形成することができ、前記コーティング層の形成に伴う熱によって、フィルムが皺になることを防止することができる。したがって、フィルムの厚さを薄くすることが可能となり、柔軟性に優れた金属被覆糸が得られる。
また、前記樹脂とシランカップリング剤とのネットワーク構造(編目構造)が形成されることにより、緻密な樹脂膜を形成することができ、耐久性に優れた金属被覆糸が得られる。
【0045】
本発明の金属被覆糸、織布、不織布は、良好な柔軟性および耐久性を有するものであるので、和服、洋服を問わず様々な用途に使用することができる。
【図面の簡単な説明】
【図1】 本発明の金属被覆糸製造用シートの一例を示した断面図である。
【図2】 本発明の金属被覆糸製造用シートの他の例を示した断面図である。
【図3】 本発明の金属被覆糸製造用シートの他の例を示した断面図である。
【図4】 本発明の金属被覆糸製造用シートの他の例を示した断面図である。
【図5】 本発明の金属被覆糸製造用シートの他の例を示した断面図である。
【図6】 本発明の金属被覆平糸の一例を示した図である。
【図7】 本発明の金属被覆撚糸の一例を示した図である。
【図8】 従来の金銀糸製造用シートの一例を示した断面図である。
【図9】 従来の金銀糸製造用シートの他の例を示した断面図である。
【図10】 従来の金銀糸製造用シートの他の例を示した断面図である。
【符号の説明】
1 フィルム
2 金属薄膜
3 コーティング層
3a 第1コーティング層
3b 第2コーティング層
5 腐食防止層
6 アンダーコート層
7 着色層
8 支持層
10 金属被覆糸製造用シート
10a 金属被覆平糸
11 芯糸
20a 金属被覆糸[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a metal-coated yarn and a fabric using the same, and more particularly to a metal-coated yarn and a fabric that have excellent corrosion resistance and flexibility and are suitably used for clothes and the like.
[0002]
[Prior art]
One type of woven fabric used in Japanese clothes and the like is one in which a gold-silver pattern is formed. Such woven fabric is usually woven with gold or silver yarn as weft and silk yarn as warp, and partially exposed with gold or silver yarn (hereinafter referred to as gold and silver yarn together) exposed on the surface side of the woven fabric. Is formed.
[0003]
Most of the gold and silver threads are manufactured by depositing silver on a plastic film and cutting a sheet for producing gold and silver threads having a resin coating on the silver film. 8-10 has shown the cross section of the sheet | seat for a different conventional gold and silver thread manufacture, respectively. These sheets for producing gold and silver thread are all called single-sided sheets, and two-sided sheets prepared by preparing two sheets of these single-sided sheets, with the surface having gold and silver gloss on the outside, and bonded together with an adhesive are also available on the market. Has been. The sheet for producing gold and silver thread in this specification is a collective term for both the single-sided sheet and the double-sided sheet.
[0004]
The single-sided sheet shown in FIG. 8 is obtained by depositing a
A double-sided sheet is obtained by preparing two of these single-sided sheets and bonding them to both sides of the support layer with the gold-silver glossy side facing outside.
[0005]
If the above sheet for producing gold and silver yarn is cut into thin pieces and wound spirally around a core yarn such as silk yarn, it becomes a gold and silver twisted yarn.
Such a twisted yarn is usually used for the gold and silver woven fabric.
[0006]
[Problems to be solved by the invention]
By the way, in recent years, gold and silver yarn as described above has been frequently used not only for Japanese clothes but also for clothes.
However, the gold and silver threads as described above have been problematic in that they are rigid and lack flexibility when used for clothes.
In order to solve such a problem, it is conceivable to reduce the thickness of the resin film constituting the sheet for producing gold and silver yarn. However, if the thickness of the resin film is reduced, the resin coating is formed on the silver coating. The inconvenience that the resin film is deformed and easily becomes wrinkles due to heat at the time of application.
[0007]
Furthermore, clothes are more frequently washed than Japanese clothes, and sweat is often attached directly. For this reason, there has been a problem that gold and silver threads that can be used sufficiently in Japanese clothes are likely to change color when used in clothes.
[0008]
This invention is made | formed in view of the said situation, and makes it a subject to solve the said problem and to provide the sheet | seat for metal-coated yarn manufacture excellent in a softness | flexibility and durability.
Another object of the present invention is to provide a metal-coated yarn, a woven fabric, and a non-woven fabric using the sheet for producing a metal-coated yarn.
[0009]
In order to solve the above problems, a sheet for producing metal-coated yarn of the present invention comprises a film having a thickness of 8 μm or less, a metal thin film provided on the film, and a coating layer provided on the metal thin film. A metal-coated yarn manufacturing sheet, wherein the coating layer has a resin having a main component, a silane coupling agent having a reaction start temperature that forms a stitch structure with the resin lower than the curing temperature of the resin, 0.05-2% is contained, The resin, the silane coupling agent, and the silane coupling agent are bonded to each other.
[0010]
Moreover, in order to solve the said subject, the sheet | seat for metal-coated thread | yarn manufacture of this invention is a film below 8 micrometers in thickness , the metal thin film provided on this film, and the coating layer provided on this metal thin film, The coating layer comprises a first coating layer and a second coating layer, and either one or both of the first coating layer and the second coating layer is a main sheet. The resin as a component contains 0.05 to 2% of a silane coupling agent having a reaction start temperature for forming a stitch structure with the resin lower than the curing temperature of the resin, and the resin and the silane The coupling agent and the silane coupling agent are bonded to each other.
[0011]
In the metal-coated yarn manufacturing sheet, Si, Al, Ba, Ca, Ce, In, and / or between the metal thin film and the film and one or both of the metal thin film and the coating layer, Pb, Li, K, Mg, Na, Sn, Ti, Zn, Zr, Mo, Ta, W, Fe, Sr, V, Th, Sb, Pt, Bi, Y, Ge and oxides of these metals, fluorine You may form the corrosion prevention layer which consists of 1 type, or 2 or more types of substances selected from a chemical compound, nitride, and carbide.
In the metal-coated yarn manufacturing sheet, an undercoat layer may be formed between the metal thin film and the film.
Furthermore, in the above-mentioned sheet for producing a metal-coated yarn, the metal thin film may have a gold-silver luster in order to enhance the decorativeness. The term “having gold-silver gloss” as used herein means having a gold or silver gloss.
[0012]
The metal-coated flat yarn of the present invention is characterized in that the metal-coated yarn manufacturing sheet is cut into thin pieces . Also, metallization twisting of the present invention, the metal coated flat yarn or the gold and silver covering yarn, characterized in that the wound on the outer periphery of the core yarn.
[0013]
DETAILED DESCRIPTION OF THE INVENTION
FIG. 1 is a view showing an example of a metal-coated yarn manufacturing sheet according to the present invention.
In FIG. 1, the code |
[0014]
The material of the
[0015]
The thickness of the
[0016]
The type of the metal
[0017]
When the metal-coated
[0018]
The thickness of the metal
[0019]
The material of the first and second coating layers 3a and 3b is not particularly limited. For example, polyester resin, butyral resin, acrylic resin, epoxy resin, urethane resin, urea-melamine resin, amino resin, phenol resin, vinyl chloride resin, Polyacetal resin, polycarbonate resin, silicon resin, vinyl acetate resin, fluororesin, styrene resin or the like alone or a mixture is preferably used.
[0020]
Furthermore, one or both of the
As the silane coupling agent, one having a starting temperature of reaction for forming a network structure (stitch structure) with the resin as the main component is lower than the curing temperature of the resin. By containing a silane coupling agent in the resin, when the resin is cured, the resin has a reactive group such as a hydroxyl group, an amino group, an isocyanate group, and dienes at a temperature lower than the curing temperature of the resin as the main component. It is presumed that the silane coupling agent is bonded to each other and the silane coupling agents are bonded to each other to accelerate the curing of the resin and form a dense resin film after curing.
[0021]
As the silane coupling agent, RSiX 3 (wherein R represents an organic functional group such as a vinyl group, a glycidoxy group, a methacryl group, an amino group, and a mercapto group, and X represents a chlorine and alkoxy group). Those represented by the formula are preferably used. More preferably, it is a silane coupling agent in which R is a glycidoxy group or an amino group.
The addition amount of the silane coupling agent is preferably in the range of about 0.05 to 2%. More preferably, it is about 0.1 to 0.15% of range. When the addition amount is less than about 0.05%, the curing temperature of the resin as the main component cannot be sufficiently lowered, and the film tends to become wrinkled. In addition, the effect of forming a dense resin film becomes insufficient, and it becomes difficult to obtain sufficient durability. On the other hand, an addition amount exceeding 2% is not preferable because it only increases the cost.
[0022]
As described above, the silane coupling agent is contained in one or both of the
For example, when the silane coupling agent is contained in both the first and second coating layers 3a and 3b, it is more durable than that contained in only one of them. Can be improved.
When at least the
Furthermore, in the case where the silane coupling agent is contained only in one of the
[0023]
The thickness of the
Moreover, it is preferable that the thickness of the
[0024]
Such a metal-coated
(1) The coating layer containing the silane coupling agent can be formed at a temperature lower than the curing temperature of the resin as the main component, and the
(2) By forming a network structure (stitch structure) between the resin and the silane coupling agent, a dense resin film can be formed, and a
[0025]
In the metal-coated
[0026]
Such a
[0027]
The structure of the sheet for producing a metal-coated yarn of the present invention is not limited to the example shown in FIG. 1 and may be appropriately changed according to the application as shown below.
The sheet for producing metal-coated yarn shown in FIG. 2 is obtained by providing a
[0028]
The
[0029]
The thickness of the
By providing such a
[0030]
The
In particular, in the metal-coated yarn manufacturing sheet used for the production of gold and silver yarn, when the
[0031]
The metal-coated yarn manufacturing sheet shown in FIG. 3 has an undercoat layer 6 provided between the
[0032]
In the case of the metal-coated yarn manufacturing sheet used by coloring, the metal-coated yarn manufacturing sheet described above is the surface of the
[0033]
Moreover, it is good also as a double-sided sheet | seat obtained by preparing two sheets for said metal-coated yarn manufacture, and adhere | attaching them. The two metal-coated yarn manufacturing sheets used for the double-sided sheet may have the same configuration or different configurations.
The metal-coated yarn manufacturing sheet shown in FIG. 5 is a double-sided sheet in which two metal-coated yarn manufacturing sheets shown in FIG. 1 are prepared, these
[0034]
As the support layer 8, Japanese paper, Western paper, synthetic fiber non-woven fabric or the like can be used, and although the thickness is not limited, a layer of about 5 to 200 μm is preferable. If the thickness of the support layer 8 is less than 5 μm, the reinforcing effect is reduced, and if it exceeds 200 μm, the sheet becomes stiff and difficult to manufacture. Moreover, when the yarn manufactured from this sheet is used for clothes or the like, the touch becomes worse.
As an adhesive for adhering the support layer 8, any conventionally used adhesive such as a vinyl chloride-vinyl acetate copolymer adhesive or an epoxy adhesive may be used.
[0035]
In the metal-coated yarn manufacturing sheet, the
[0036]
Of course, the structure of the sheet for producing metal-coated yarn can be appropriately combined depending on the use.
[0037]
As shown in FIG. 6, the metal-coated flat yarn 10 a of the present invention is obtained by cutting the metal-coated
[0038]
As shown in FIG. 7, the metal-coated
The
Such a metal-coated
[0039]
The structure of the
[0040]
The gold-silver coated yarn of the present invention is not limited to a metal-coated flat yarn and a metal-coated twisted yarn using the above-mentioned sheet for producing a metal-coated yarn, but a substrate, a metal thin film provided on the substrate, A coating layer provided on the metal thin film, and the coating layer may be a gold-silver coated yarn containing a silane coupling agent. Furthermore, it is good also as a metal covering twisted thread | yarn formed by winding this gold-silver covering thread | yarn around the outer periphery of a core thread | yarn.
In this case, the substrate is preferably formed in a thread shape, and the configuration and material of the layer provided on the substrate are the same as the configuration and material of the layer provided on the film of the metal-coated yarn manufacturing sheet. The same may be applied. Further, as the material for forming the substrate, the same material as that of the
[0041]
The woven fabric of the present invention is one in which at least one selected from the metal-coated flat yarn 10a, the metal-coated
Since such a woven fabric is one in which at least one selected from the metal-coated flat yarn 10a, the metal-coated
[0042]
The nonwoven fabric of the present invention is one in which at least one selected from the metal-coated flat yarn 10a, the metal-coated
Since such a non-woven fabric is also one using at least one selected from the above-mentioned metal-coated
[0043]
Since the woven fabric and the nonwoven fabric of the present invention have good flexibility and durability, they can be used regardless of Japanese clothes or clothes. For example, kimonos, belts, underwear, outerwear, socks It can be used for various purposes such as clothes, curtains, futon covers, sheets, mats, towels, etc.
[0044]
【The invention's effect】
As described above, the sheet for producing metal-coated yarn of the present invention contains a silane coupling agent in the coating layer, so that the coating layer is at a temperature lower than the curing temperature of the resin that is the main component of the coating layer. The film can be prevented from wrinkling due to the heat accompanying the formation of the coating layer. Therefore, the thickness of the film can be reduced, and a metal-coated yarn excellent in flexibility can be obtained.
Further, by forming a network structure (stitch structure) between the resin and the silane coupling agent, a dense resin film can be formed, and a metal-coated yarn excellent in durability can be obtained.
[0045]
Since the metal-coated yarn, woven fabric, and non-woven fabric of the present invention have good flexibility and durability, they can be used for various applications regardless of Japanese clothes or clothes.
[Brief description of the drawings]
FIG. 1 is a cross-sectional view showing an example of a sheet for producing a metal-coated yarn of the present invention.
FIG. 2 is a cross-sectional view showing another example of the sheet for producing metal-coated yarn of the present invention.
FIG. 3 is a cross-sectional view showing another example of the sheet for producing metal-coated yarn of the present invention.
FIG. 4 is a cross-sectional view showing another example of the metal-coated yarn manufacturing sheet of the present invention.
FIG. 5 is a cross-sectional view showing another example of the sheet for producing metal-coated yarn of the present invention.
FIG. 6 is a view showing an example of a metal-coated flat yarn of the present invention.
FIG. 7 is a view showing an example of a metal-coated twisted yarn of the present invention.
FIG. 8 is a cross-sectional view showing an example of a conventional sheet for producing gold and silver thread.
FIG. 9 is a cross-sectional view showing another example of a conventional sheet for producing gold and silver thread.
FIG. 10 is a cross-sectional view showing another example of a conventional sheet for producing gold and silver thread.
[Explanation of symbols]
DESCRIPTION OF
Claims (6)