JPH0747600A - Syndiotactic polystyrene film - Google Patents
Syndiotactic polystyrene filmInfo
- Publication number
- JPH0747600A JPH0747600A JP5193647A JP19364793A JPH0747600A JP H0747600 A JPH0747600 A JP H0747600A JP 5193647 A JP5193647 A JP 5193647A JP 19364793 A JP19364793 A JP 19364793A JP H0747600 A JPH0747600 A JP H0747600A
- Authority
- JP
- Japan
- Prior art keywords
- film
- less
- white
- stretching
- syndiotactic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、記録紙などに用いる
際、オフセット印刷やグラビア印刷で使用するインクや
トナーの密着性の良好な白色フィルムに関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a white film having good adhesion to ink and toner used in offset printing or gravure printing when used for recording paper or the like.
【０００２】[0002]
【従来の技術】従来の白色フィルムの主原料としては、
ポリエチレン、ポリプロピレン、ポリエステルなどが用
いられており、それらの特徴を生かした用途展開が行わ
れている。白色フィルムを得る方法としては、フィルム
内部に二酸化チタンや炭酸カルシウムなどの無機顔料を
添加する方法が知られている。また、ポリエステルやポ
リプロピレンなどを主原料とした紙と類似した機能を有
するフィルムを得る方法として、従来（１）微細な空洞
をフィルム内部に多量に含有させる方法や通常の平坦な
フィルムを（２−１）サンドプラスト処理や（２−２）
ケミカルエッチング処理や（２−３）マット化処理（マ
ット剤をバインダーとともに積層する方法）などによっ
て粗面化する方法、などが開示されている。2. Description of the Related Art As a main raw material of a conventional white film,
Polyethylene, polypropylene, polyester, etc. are used, and their applications are being developed by making use of their characteristics. As a method of obtaining a white film, a method of adding an inorganic pigment such as titanium dioxide or calcium carbonate inside the film is known. In addition, as a method of obtaining a film having a function similar to that of paper mainly made of polyester or polypropylene, (1) a method of containing a large amount of fine voids inside the film or an ordinary flat film (2- 1) Sandplast processing and (2-2)
A method of roughening by chemical etching treatment, (2-3) matting treatment (a method of laminating a matting agent with a binder), and the like are disclosed.
【０００３】しかしながらポリエステルやポリプロピレ
ンなどを主原料とした白色フィルムは、主としてスチレ
ン系樹脂からなるトナーやインクとの密着性が良好では
ない。そのため表面に塗布層を設けたり、コロナ処理や
火炎処理といった表面処理を行うことにより密着性を上
げている。しかし、そのような処理を行うことはコスト
上昇や耐熱性の低下、また時間の経過とともに生じる性
能の低下といった問題を解決することは困難であった。
そのためには主原料をポリスチレン樹脂による白色フィ
ルムまたはシートが良好となる。だが、ポリスチレンフ
ィルムやシートを白色化するために単純に無機顔料など
を添加すると非常に脆くなるため、実際には使用不可能
であった。However, a white film mainly made of polyester, polypropylene or the like does not have good adhesion to a toner or ink mainly made of styrene resin. Therefore, the adhesion is improved by providing a coating layer on the surface or performing surface treatment such as corona treatment or flame treatment. However, it has been difficult to solve such problems that the cost increases, the heat resistance decreases, and the performance deteriorates with the passage of time by performing such treatment.
For that purpose, a white film or sheet made of polystyrene resin as a main material is preferable. However, simply adding an inorganic pigment or the like to whiten a polystyrene film or sheet makes it very brittle, and thus it was not practically usable.
【０００４】[0004]
【発明が解決しようとする課題】本発明は、前期の欠
点、即ち、トナーやインクの密着性を良好にする白色フ
ィルムに関する。SUMMARY OF THE INVENTION The present invention relates to a drawback of the previous term, that is, a white film which improves the adhesion of toner and ink.
【０００５】[0005]
【課題を解決するための手段】すなわちこれらを解決す
るための手段としての本発明の主旨は、少なくとも１軸
に配向し、光線透過率が５０％以下であることを特徴と
するシンジオタクティックポリスチレンフィルムに関す
る。本発明における主原料となる樹脂は、シンジオタク
ティックポリスチレンが挙げられる。シンジオタクティ
ック構造を有するポリスチレンとは、立体規則性がシン
ジオタクティック構造すなわち、炭素−炭素結合からな
る形成された主鎖に対して側鎖であるフェニル基や置換
フェニル基が交互に反対方向に位置する立体構造を持つ
ものである。本発明におけるスチレン重合体は、分子量
については特に制限はないが、重量平均分子量が１万以
上３００万以下が望ましい（特開平３−１２４４２７号
公報）。That is, the gist of the present invention as a means for solving these problems is that the syndiotactic polystyrene is characterized in that it is oriented in at least one axis and has a light transmittance of 50% or less. Regarding film. Examples of the resin as the main raw material in the present invention include syndiotactic polystyrene. Polystyrene having a syndiotactic structure means that the stereoregularity is a syndiotactic structure, that is, a phenyl group or a substituted phenyl group, which is a side chain with respect to a main chain formed of carbon-carbon bonds, alternates in opposite directions. It has a three-dimensional structure. The styrene polymer in the present invention is not particularly limited in molecular weight, but a weight average molecular weight of 10,000 or more and 3,000,000 or less is desirable (JP-A-3-124427).
【０００６】本発明に用いられるフィルムは光線透過率
を５０％以下、好ましくは３０％以下、より好ましくは
２０％以下にしなくてはならない。そのための方法は特
に限定されるものではない。たとえば、表面に塗料を塗
る方法、紙や不織布などを貼る方法などがある。しか
し、好ましくは内部に無機粒子を含有する方法または内
部に多数の空洞を含有する方法である。The film used in the present invention must have a light transmittance of 50% or less, preferably 30% or less, more preferably 20% or less. The method therefor is not particularly limited. For example, there are a method of applying paint on the surface, a method of applying paper or a non-woven fabric, and the like. However, a method of containing inorganic particles inside or a method of containing a large number of cavities inside is preferable.
【０００７】本発明においては内部に含有する無機粒子
は特に限定されるものではなく、二酸化チタン、炭酸カ
ルシウム、硫酸バリウム、酸化亜鉛、二酸化珪素、炭酸
マグメシウム、炭酸ストロンチウム、酸化アルミニウ
ム、タルク、カオリン、ゼオライトおよびこれらの２次
凝集体などを一種類または二種類以上用いることができ
る。しかし、一般にこれらの無機粒子は表面エネルギー
が大きく、臨界表面張力は５０ｄｙｎｅ／ｃｍ以上であ
る。一方ポリスチレン樹脂のそれは約３３ｄｙｎｅ／ｃ
ｍであるため、両者の界面親和性の不良が原因によりフ
ィルムやシートが脆くなる。よって特に本発明において
重要なことは、これらの界面の親和性を良好にし、柔軟
性をよくすることである。親和性を良好にする方法は、
たとえば無機粒子を表面処理を行うことにより表面エネ
ルギーを下げることがあげられる。また特に有効な方法
は無機粒子を一度他の樹脂で予備混練して、シンジオタ
クティックポリスチレン樹脂の混合する方法である。そ
のための樹脂は表面エネルギーがシンジオタクティック
ポリスチレンよりも大きく無機粒子よりも小さいもので
ある、すなわち臨界表面張力が３４ｄｙｎｅ／ｃｍ以上
５０ｄｙｎｅ／ｃｍ以下のものであれば特に限定されな
い。たとえば、ポリエチレンテレフタレートやポリエチ
レン−２，６−ナフタレートなどのポリエステル樹脂、
ポリアクリル樹脂、ポリスルホン樹脂、ポリアミド樹
脂、ポリカーボネート樹脂などが挙げられる。In the present invention, the inorganic particles contained inside are not particularly limited, and include titanium dioxide, calcium carbonate, barium sulfate, zinc oxide, silicon dioxide, magnesium carbonate, strontium carbonate, aluminum oxide, talc, kaolin, One kind or two or more kinds of zeolite and secondary aggregates thereof can be used. However, generally, these inorganic particles have large surface energy and the critical surface tension is 50 dyne / cm or more. On the other hand, that of polystyrene resin is about 33 dyne / c
Since it is m, the film or sheet becomes brittle due to the poor interface affinity between the two. Therefore, what is particularly important in the present invention is to improve the affinity and flexibility of these interfaces. The method to improve the affinity is
For example, the surface energy can be lowered by subjecting the inorganic particles to a surface treatment. A particularly effective method is a method in which the inorganic particles are once pre-kneaded with another resin and then the syndiotactic polystyrene resin is mixed. The resin for that purpose is not particularly limited as long as it has a surface energy larger than that of syndiotactic polystyrene and smaller than that of the inorganic particles, that is, has a critical surface tension of 34 dyne / cm or more and 50 dyne / cm or less. For example, polyester resins such as polyethylene terephthalate and polyethylene-2,6-naphthalate,
Examples thereof include polyacrylic resin, polysulfone resin, polyamide resin, and polycarbonate resin.
【０００８】該重合体混合物には、用途に応じて着色
剤、耐光剤、蛍光剤、帯電防止剤などを添加することも
可能である。こうして得た重合体混合物は、更に速度差
をもったロール間での延伸（ロール延伸）やクリップに
把持して拡げていくことによる延伸（テンター延伸）や
空気圧によって拡げることによる延伸（インフレーショ
ン延伸）などによって少なくとも１軸に配向処理する。
このときに分散された該ポリエステルに非相溶性の熱可
塑性樹脂とポリエステルとの界面で剥離が起こり重合体
混合物に空洞が多数発生する。It is possible to add a colorant, a light-proofing agent, a fluorescent agent, an antistatic agent, etc. to the polymer mixture depending on the application. The polymer mixture thus obtained is further stretched between rolls having different speeds (roll stretch), stretched by gripping and expanding with a clip (tenter stretch), and stretched by expanding by air pressure (inflation stretch). At least one axis is subjected to orientation treatment by, for example,
At this time, peeling occurs at the interface between the insoluble thermoplastic resin and the polyester dispersed in the polyester, and a large number of voids are generated in the polymer mixture.
【０００９】また本発明の目的であるオフセット印刷や
グラビア印刷で使用するインクやトナーの密着性を低下
させない範囲でフィルム表面に塗布層を設けることがで
きる。塗布層を設ける方法としては、グラビアコート方
式、キスコート方式、ディップ方式、スプレイコート方
式、カーテンコート方式、エアナイフコート方式、ブレ
ードコート方式、リバースロールコート方式など通常用
いられている方法が適用できる。塗布する段階として
は、配向処理を行う前の混合重合体物表面にあらかじめ
塗布する方法、１軸方向に配向した空洞含有フィルム表
面に塗布し、それを更に直角方向に配向させる方法、配
向処理の終了した空洞含有フィルム表面に塗布する方法
などのいずれの方法も可能である。Further, a coating layer can be provided on the surface of the film within a range that does not deteriorate the adhesiveness of the ink or toner used in the offset printing or gravure printing which is the object of the present invention. As a method for providing the coating layer, a commonly used method such as a gravure coating method, a kiss coating method, a dip method, a spray coating method, a curtain coating method, an air knife coating method, a blade coating method or a reverse roll coating method can be applied. As the step of applying, a method of previously applying to the surface of the mixed polymer before the orientation treatment, a method of applying to the surface of the uniaxially oriented cavity-containing film and further orienting it in the orthogonal direction, Any method such as coating on the surface of the finished void-containing film is possible.
【００１０】本発明においては、基本となる層の少なく
とも片面に他の層を積層したいわゆる複合フィルムとし
てもよい。その方法は特に限定されるものではなく、例
えば２軸延伸したシンジオタクティックポリスチレンフ
ィルムの少なくとも片面に溶融した熱可塑性樹脂をラミ
ネートする方法、１軸延伸したフィルムの少なくとも片
面に溶融した熱可塑性樹脂をラミネートし、その積層体
をさらに直角方向に延伸する方法、すでに延伸したフィ
ルムを接着剤や粘着剤で貼り合わせる方法など特に限定
されるものではない。しかし生産性を考慮すると、表層
と中心層の原料は別々の押出機から押出し、１つのダイ
スに導き未延伸シートを得た後、少なくとも１軸に配向
させる、いわゆる共押出法による積層がもっとも好まし
い。この場合、無機粒子、帯電防止剤、紫外線吸収剤、
蛍光増白剤、酸化防止剤などの添加物を表層と中心層と
で各々異なるものを含有することにより、要求特性に応
じたフィルムを得ることが容易になる。たとえば、滑り
性と隠蔽性（不透明性）を両立させるため、表層には中
心層よりも粒径の大きい粒子をいれたり、紫外線防止効
果と隠蔽性を両立させるため、表層には紫外線防止剤や
表面処理をしたルチル型二酸化チタン、中心層には二酸
化チタンや炭酸カルシウムなどを含有することなどが挙
げられる。In the present invention, a so-called composite film in which at least one surface of a basic layer is laminated with another layer may be used. The method is not particularly limited. For example, a method of laminating a molten thermoplastic resin on at least one surface of a biaxially stretched syndiotactic polystyrene film, a method of laminating a molten thermoplastic resin on at least one surface of a uniaxially stretched film. There is no particular limitation, such as a method of laminating and further stretching the laminated body in a direction perpendicular to the laminate, a method of laminating an already stretched film with an adhesive or a pressure-sensitive adhesive. However, from the viewpoint of productivity, it is most preferable to use a so-called co-extrusion method in which the raw materials for the surface layer and the central layer are extruded from different extruders, introduced into one die to obtain an unstretched sheet, and then oriented at least uniaxially. . In this case, inorganic particles, antistatic agent, ultraviolet absorber,
By containing different additives such as a fluorescent whitening agent and an antioxidant in the surface layer and the central layer, it becomes easy to obtain a film satisfying the required properties. For example, in order to achieve both slipping property and hiding property (opacity), particles having a particle size larger than that of the central layer may be added to the surface layer, and an ultraviolet ray inhibitor or a surface protection agent may be added to the surface layer in order to achieve both the ultraviolet protection effect and the hiding property. Examples thereof include surface-treated rutile titanium dioxide, and the central layer containing titanium dioxide, calcium carbonate, or the like.
【００１１】本発明においては好ましくは未延伸シート
を少なくとも１軸に延伸する。その方法は速度差をもっ
たロール間での延伸（ロール延伸）やクリップに把持し
て拡げていくことによる延伸（テンター延伸）や空気圧
によって拡げることによる延伸（インフレーション延
伸）などいずれでも構わない。しかし、機械的特性など
から考えると、最初にフィルムの流れ方向にあたる縦方
向に延伸し、次に横方向に延伸する逐次２軸延伸が好ま
しい。この縦、横方向の順に延伸する逐次二軸延伸を例
にとって、具体的に説明するが後のフィルムの特性を満
足するものであれば以下の方法に限定されるものではな
い。In the present invention, the unstretched sheet is preferably stretched uniaxially. The method may be stretching between rolls having different speeds (roll stretching), stretching by gripping a clip and expanding (tenter stretching), or stretching by expanding by air pressure (inflation stretching). However, from the viewpoint of mechanical properties and the like, sequential biaxial stretching is preferred in which the film is first stretched in the machine direction, which corresponds to the flow direction of the film, and then stretched in the transverse direction. The sequential biaxial stretching in which the machine direction and the transverse direction are sequentially stretched will be specifically described. However, the method is not limited to the following methods as long as the characteristics of the film to be described later are satisfied.
【００１２】まず縦延伸はロール延伸により行う。この
時の延伸倍率は１．２〜６．０倍、延伸温度は９５〜１
４０℃の範囲で実施することが望ましい。延伸倍率が
１．２倍未満であると機械的強度が不足し、また６．０
倍を越えると後の横延伸が困難になりフィルムが得られ
ない。延伸温度が９５℃未満であるとシートが軟化せず
延伸が困難であり、１４０℃を越えると結晶化度が高く
なりすぎ後の横延伸が困難になる。延伸時のシートの加
熱方法は、加熱したロールでも、赤外線による加熱で
も、またその他の方法でも構わない。また予熱、延伸ロ
ールの任意の場所にガイドロールまたはニップロールを
用いてもよい。続く横延伸においてはテンター延伸が望
ましい。この時の延伸倍率は１．２〜６．０倍、延伸温
度は１００〜１４０℃の範囲で実施するのが望ましい。
延伸倍率が１．２倍未満であると機械的強度が不足し、
また６．０倍を越えると破断が生じやすくなる。延伸温
度が１００℃未満であるとシートが軟化せず延伸が困難
であり、１４０℃を越えると結晶化度が高くなりすぎ破
断が生じやすくなる。 また本発明においては、好まし
くは延伸終了後に１７０〜２７０℃、好ましくは２００
〜２７０℃において熱処理する。この時縦かつ／または
横方向に２％以上緩和させながら熱処理させることによ
り、より熱収縮率の小さいものが得られる。この熱収縮
率は好ましくは１５０℃で２％以下、より好ましくは
１．５％以下、さらに好ましくは１％以下とすることで
ある。First, longitudinal stretching is performed by roll stretching. At this time, the draw ratio is 1.2 to 6.0, and the draw temperature is 95 to 1.
It is desirable to carry out in the range of 40 ° C. If the draw ratio is less than 1.2 times, the mechanical strength will be insufficient and 6.0
If the number exceeds twice, lateral stretching later becomes difficult and a film cannot be obtained. If the stretching temperature is less than 95 ° C, the sheet will not be softened and stretching will be difficult, and if it exceeds 140 ° C, the crystallinity will be too high and lateral stretching afterwards will be difficult. The heating method of the sheet at the time of stretching may be a heated roll, infrared heating, or any other method. Further, a guide roll or a nip roll may be used at any place of the preheating and stretching rolls. In the subsequent transverse stretching, tenter stretching is desirable. At this time, the stretching ratio is preferably 1.2 to 6.0 and the stretching temperature is preferably 100 to 140 ° C.
If the draw ratio is less than 1.2 times, the mechanical strength is insufficient,
If it exceeds 6.0 times, fracture tends to occur. If the stretching temperature is less than 100 ° C, the sheet will not be softened and stretching will be difficult, and if it exceeds 140 ° C, the crystallinity will be too high and breakage will occur easily. In the present invention, it is preferably 170 to 270 ° C., preferably 200 after the stretching.
Heat treat at ~ 270 ° C. At this time, heat treatment is performed while relaxing 2% or more in the longitudinal direction and / or the transverse direction to obtain a material having a smaller heat shrinkage rate. This heat shrinkage ratio is preferably 2% or less at 150 ° C., more preferably 1.5% or less, still more preferably 1% or less.
【００１３】本発明のフィルムは加工性などを考慮する
と初期弾性率が４００kg/mm2以上、引張強さが１４kg/m
m2以上が好ましい。初期弾性率が４００kg/mm2未満、引
張強さが１４kg/mm2未満では印刷などの後加工時のトラ
ブルが生じ易くなる。本発明のフィルムは中心線平均粗
さが０．０５μｍ以上１．０μｍ以下、好ましくは０．
１μｍ以上０．５μｍ以下でなくてはならない。０．０
５未満では複写機内部での滑り性が不良となり、１．０
μｍを越えると印刷物などの外観が不良となる。In consideration of workability, the film of the present invention has an initial elastic modulus of 400 kg / mm 2 or more and a tensile strength of 14 kg / m.
m 2 or more is preferable. If the initial elastic modulus is less than 400 kg / mm 2 and the tensile strength is less than 14 kg / mm 2 , troubles during post-processing such as printing are likely to occur. The center line average roughness of the film of the present invention is 0.05 μm or more and 1.0 μm or less, preferably 0.
It must be 1 μm or more and 0.5 μm or less. 0.0
If it is less than 5, the slipperiness inside the copying machine becomes poor and 1.0
If it exceeds μm, the appearance of printed matter or the like becomes poor.
【００１４】かくして得られた白色フィルムまたはシー
トは、従来提案されている白色フィルムにくらべてオフ
セット印刷やグラビア印刷で使用するインクやトナーの
密着性が良好であるため、印刷物や情報記録紙に好適な
基材をして提供できる。またこの他にもラベル、ポスタ
ー、カード、記録用紙、包装材料、インクジェット用
紙、ビデオプリンター受像紙、バーコードラベル、バー
コードプリンター受像紙、感熱記録紙、地図、無塵紙、
表示板、印画紙、化粧紙、壁紙、離型紙、カレンダー、
磁気カード、トレーシング紙、感圧記録紙、複写用紙、
臨床検査紙などに用いることができる。The white film or sheet thus obtained has good adhesion to inks and toners used in offset printing and gravure printing, as compared with conventionally proposed white films, and is therefore suitable for printed matter and information recording paper. It can be provided as a base material. In addition to these, labels, posters, cards, recording paper, packaging materials, inkjet paper, video printer image receiving paper, bar code labels, bar code printer image receiving paper, thermal recording paper, maps, dust-free paper,
Display board, photographic paper, decorative paper, wallpaper, release paper, calendar,
Magnetic card, tracing paper, pressure sensitive recording paper, copy paper,
It can be used as clinical test paper.
【００１５】[0015]
【作用】本発明において、シンジオタクティックポリス
チレン樹脂を用いるのはオフセット印刷やグラビア印刷
などで使用するインクやトナーの密着性を良好にするた
めである。本発明において、好ましくは該重合体混合物
を少なくとも一軸に配向するのは、適切な強度をもたす
ためである。In the present invention, the syndiotactic polystyrene resin is used in order to improve the adhesiveness of the ink or toner used in offset printing or gravure printing. In the present invention, the polymer mixture is preferably oriented at least uniaxially in order to have appropriate strength.
【００１６】実施例 次に本発明の実施例および比較例を示す。本発明に用い
る測定・評価方法を以下に示す。 １）中心線平均粗さ ＪＩＳ−Ｂ６０１−１９８２により測定したExamples Next, examples and comparative examples of the present invention will be shown. The measurement / evaluation methods used in the present invention are shown below. 1) Center line average roughness Measured according to JIS-B601-1982
【００１７】２）初期弾性率 ＡＳＴＭ Ｄ−８８２−８１（Ａ法）により測定した。2) Initial elastic modulus It was measured by ASTM D-882-81 (method A).
【００１８】３）引張強さ ＪＩＳ−Ｃ２３１８−１９７５により測定した。3) Tensile Strength Measured according to JIS-C2318-1975.
【００１９】４）熱収縮率 フィルムを幅１０ｍｍ、長さ２５０ｍｍとり、２００ｍ
ｍ間隔で印をつけ５ｇの一定張力下で固定し印の間隔Ａ
を測る。続いて、無張力下で３０分間、１５０℃の雰囲
気中のオーブンにいれた後の印の間隔Ｂを求め、以下の
式により熱収縮率とした4) Heat shrinkage rate: A film having a width of 10 mm and a length of 250 mm is 200 m
Mark at m intervals and fix under a constant tension of 5 g, and mark intervals A
Measure Subsequently, the space B between the marks after being placed in an oven in an atmosphere of 150 ° C. for 30 minutes under no tension was determined, and the heat shrinkage rate was calculated by the following formula.
【００２０】（Ａ−Ｂ）／Ａ×１００（％） ５）光線透過率 ＪＩＳ−Ｋ６７１４に準じ、ポイック積分球式Ｈ．Ｔ．
Ｒメーター（日本精密光学製）を用い、フィルムの光線
透過率を測定した。この値が小さいほど隠ぺい性が高
い。(A−B) / A × 100 (%) 5) Light transmittance According to JIS-K6714, Poic integrating sphere formula H.264. T.
The light transmittance of the film was measured using an R meter (manufactured by Nippon Seimitsu Optical Co., Ltd.). The smaller this value is, the higher the hiding property is.
【００２１】６）コピー適性 通常のＰＰＣ複写機でコピーを行い、外観の良好なもの
を○、不良なものを×とした。6) Applicability of copying: Copying was carried out by a normal PPC copying machine, and a product having a good appearance was evaluated as ◯, and a product having a poor appearance was evaluated as x.
【００２２】実施例１ 固有粘度０．６２のポリエチレンテレフタレート樹脂５
０重量％とアナターゼ型二酸化チタン５０重量％を２軸
スクリュー押出機を用いて、２８５℃で予備混練しマス
ターバッチペレット（ＭＢ）を作成した。このＭＢ２０
重量％を重量平均分子量４３万のシンジオタクティック
ポリスチレン樹脂８０重量％と混合し、２軸スクリュー
押出機中に投入し、３１０℃で溶融し、Ｔ−ダイスより
押出し冷却ロールに静電密着することにより厚さ約１０
００μｍの未延伸シートを得た。このシートを１１０℃
で３．３倍縦方向にロール延伸し、続いて横方向に１２
０℃で３．５倍延伸し、２５０℃で４％緩和しながら熱
固定することにより最終的に１００μｍの白色シンジオ
タクティックポリスチレンフィルムを得た。Example 1 Polyethylene terephthalate resin 5 having an intrinsic viscosity of 0.62
Masterbatch pellets (MB) were prepared by pre-kneading 0% by weight and 50% by weight of anatase type titanium dioxide at 285 ° C. using a twin screw extruder. This MB20
% By weight, mixed with 80% by weight of syndiotactic polystyrene resin having a weight average molecular weight of 430,000, charged in a twin-screw extruder, melted at 310 ° C., electrostatically adhered to a cooling roll extruded from a T-die. Thickness is about 10
An unstretched sheet of 00 μm was obtained. This sheet is 110 ℃
Roll stretching 3.3 times in the machine direction and then 12 in the transverse direction.
A 100-μm white syndiotactic polystyrene film was finally obtained by stretching 3.5 times at 0 ° C. and heat setting at 250 ° C. while relaxing by 4%.
【００２３】比較例１ 重量平均分子量４３万のシンジオタクティックポリスチ
レン樹脂５０重量％とアナターゼ型二酸化チタン５０重
量％を２軸スクリュー押出機を用いて、３１０℃で予備
混練しマスターバッチペレット（ＭＢ）を作成した。こ
のＭＢ２０重量％を重量平均分子量４３万のシンジオタ
クティックポリスチレン樹脂８０重量％と混合し、２軸
スクリュー押出機中に投入し、３１０℃で溶融し、Ｔ−
ダイスより押出し冷却ロールに静電密着することにより
厚さ約１０００μｍの未延伸シートを得た。その後実施
例１と全く同様の方法において最終厚み１００μｍの白
色シンジオタクティックポリスチレンフィルムを得た。Comparative Example 1 50% by weight of syndiotactic polystyrene resin having a weight average molecular weight of 430,000 and 50% by weight of anatase type titanium dioxide were pre-kneaded at 310 ° C. using a twin-screw extruder to prepare master batch pellets (MB). It was created. 20% by weight of this MB was mixed with 80% by weight of syndiotactic polystyrene resin having a weight average molecular weight of 430,000, charged into a twin-screw extruder and melted at 310 ° C.
An unstretched sheet having a thickness of about 1000 μm was obtained by extruding from a die and electrostatically adhering to a cooling roll. Then, in the same manner as in Example 1, a white syndiotactic polystyrene film having a final thickness of 100 μm was obtained.
【００２４】比較例２ 固有粘度０．６２のポリエチレンテレフタレート樹脂９
０重量％にアナターゼ型二酸化チタンを１０重量％混合
し、２軸スクリュー押出機で２８５℃で溶融し、Ｔ−ダ
イスより押出冷却ロールに静電密着することにより厚さ
約１０００μｍの未延伸シートを得た。その後１００℃
で３．３倍縦延伸し、１２０℃で３．５倍横延伸し、２
３５℃で４％緩和しながら熱固定し、最終厚み１００μ
ｍの空洞含有ポリエステル系フィルムを得た。Comparative Example 2 Polyethylene terephthalate resin 9 having an intrinsic viscosity of 0.62
Anatase type titanium dioxide was mixed with 0% by weight of 10% by weight, melted at 285 ° C. by a twin screw extruder, and electrostatically adhered to an extrusion cooling roll from a T-die to form an unstretched sheet having a thickness of about 1000 μm. Obtained. Then 100 ° C
Longitudinally stretched 3.3 times, then at 120 ° C 3.5 times horizontally stretched,
Heat set while relaxing 4% at 35 ° C, final thickness 100μ
A m-containing polyester film was obtained.
【００２５】[0025]
【発明の効果】本発明の白色シンジオタクティックポリ
スチレンフィルムはこれまでの白色フィルムに比べ、オ
フセット印刷やグラビア印刷で使用するインクやトナー
の密着性が良好であるためラベル、ポスター、印刷用
紙、オフセット印刷、商業印刷、感熱記録紙、昇華転写
記録紙、プリンター用印字基材などに特に優れ、配送伝
票、電子白板、感圧紙、ＰＳ板、印刷板、包装用材料な
どにも優れた基材である。EFFECTS OF THE INVENTION The white syndiotactic polystyrene film of the present invention has better adhesion to inks and toners used in offset printing and gravure printing than conventional white films, and therefore has good adhesiveness to labels, posters, printing papers and offsets. Especially excellent for printing, commercial printing, thermal recording paper, sublimation transfer recording paper, printing base materials for printers, etc., and also excellent base materials for delivery slips, electronic white boards, pressure sensitive paper, PS boards, printing boards, packaging materials, etc. is there.
【００２６】[0026]
【表１】 [Table 1]
───────────────────────────────────────────────────── フロントページの続き (51)Int.Cl.6 識別記号 庁内整理番号 ＦＩ 技術表示箇所 Ｂ２９Ｋ 105:16 Ｂ２９Ｌ 7:00 (72)発明者 奥平 正 滋賀県大津市堅田二丁目１番１号 東洋紡 績株式会社総合研究所内─────────────────────────────────────────────────── ─── Continuation of front page (51) Int.Cl. 6 Identification number Reference number in the agency FI Technical display location B29K 105: 16 B29L 7:00 (72) Inventor Tadashi Okuhira 2-1-1 Katata, Otsu City, Shiga Prefecture No. Toyobo Co., Ltd.
Claims (3)
５０％以下であることを特徴とする白色シンジオタクテ
ィックポリスチレン系フィルム。1. A white syndiotactic polystyrene film, which is at least uniaxially oriented and has a light transmittance of 50% or less.
率が２％以下、表面粗さが０．０５μｍ以上１．０μｍ
以下であることを特徴とする請求項１記載の白色シンジ
オタクティックポリスチレン系フィルム。2. The film according to claim 1, which has a heat shrinkage of 2% or less and a surface roughness of 0.05 μm or more and 1.0 μm.
The white syndiotactic polystyrene film according to claim 1, wherein:
部に多数の無機粒子を含有し、その無機粒子の周囲が熱
可塑性樹脂で覆われていることを特徴とする請求項１ま
たは２記載の白色シンジオタクティックポリスチレン系
フィルム。3. The film according to claim 1, wherein the film contains a large number of inorganic particles, and the periphery of the inorganic particles is covered with a thermoplastic resin. White syndiotactic polystyrene film.