JPH07197222A - Hot-dip plating device - Google Patents
Hot-dip plating deviceInfo
- Publication number
- JPH07197222A JPH07197222A JP35129193A JP35129193A JPH07197222A JP H07197222 A JPH07197222 A JP H07197222A JP 35129193 A JP35129193 A JP 35129193A JP 35129193 A JP35129193 A JP 35129193A JP H07197222 A JPH07197222 A JP H07197222A
- Authority
- JP
- Japan
- Prior art keywords
- plating bath
- plating
- treatment material
- slit
- immersion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、長尺な鋼板等の処理材
をメッキ浴中に浸漬し、その表面に金属を付着させてメ
ッキを施す浸漬メッキ装置に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an immersion plating apparatus in which a treatment material such as a long steel plate is dipped in a plating bath and a metal is attached to the surface of the plating bath for plating.
【０００２】[0002]
【従来の技術】例えば、鋼板に亜鉛メッキを施す工程で
は、高温で溶融した亜鉛からなるメッキ浴中に鋼板を浸
漬し、その表面に溶融した亜鉛を付着させ、これを硬化
させてメッキを施す浸漬メッキ装置が使用される。従来
のこの種のメッキ装置は、溶融した亜鉛を満たしたメッ
キ浴中に鋼板ガイド用のローラを設置し、このローラで
鋼板を案内しながら鋼板をメッキ浴中に連続的に引き込
み、その表面に溶融亜鉛を付着させる。その後、鋼板を
メッキ浴中から引き出し、亜鉛メッキを鋼板表面に定着
させるものである。2. Description of the Related Art For example, in the step of galvanizing a steel sheet, the steel sheet is dipped in a plating bath made of molten zinc at a high temperature, the molten zinc is adhered to the surface thereof, and this is hardened to perform plating. Immersion plating equipment is used. This type of conventional plating equipment installs a steel plate guide roller in a plating bath filled with molten zinc, and while guiding the steel plate with this roller, the steel plate is continuously drawn into the plating bath and its surface is Apply molten zinc. After that, the steel plate is pulled out from the plating bath to fix the zinc plating on the surface of the steel plate.
【０００３】[0003]
【発明が解決しようとしている課題】しかしながら、前
記従来の浸漬メッキ装置の場合、メッキ浴中にローラを
設置しこれを回転させる構造のため、高温のメッキ浴中
のローラやその軸受が早期に劣化、腐食し、寿命が短
い。さらに、メッキ浴の液面に浮遊する酸化物等が、メ
ッキ浴の液面から引き込まれる鋼板に付着してメッキ浴
中に引き込まれ、さらにローラの周面に巻き込まれる。
このため、ローラの周面に金属酸化物が付着し、ローラ
の周面の平坦度が悪くなり、メッキの品質が確保できな
くなる。However, in the case of the above-mentioned conventional immersion plating apparatus, since the roller is installed in the plating bath and is rotated, the roller and its bearing in the high temperature plating bath deteriorate early. Corrosion, short life. Further, oxides floating on the liquid surface of the plating bath adhere to the steel plate drawn from the liquid surface of the plating bath, are drawn into the plating bath, and are further wound around the peripheral surface of the roller.
Therefore, the metal oxide adheres to the peripheral surface of the roller, the flatness of the peripheral surface of the roller deteriorates, and the quality of plating cannot be ensured.
【０００４】このような理由から、従来の浸漬メッキ装
置では、頻繁にローラやその軸受等の補修や交換をしな
ければならない。ところが、メッキ浴中からローラを引
き上げてその補修をするのは、極めて手数がかかり、多
大な時間と費用を要する。そこで、本発明は、溶融金属
であるメッキ浴中にローラを設置せずに長尺な処理材を
メッキ浴中に引き込むことができ、しかもメッキ浴の液
面からではなく、その中間部から引き込むことができる
ようにし、その結果、ローラの保守を不要とし、且つ浮
遊酸化物等の影響の無い浸漬メッキ装置を提供すること
を目的とする。For these reasons, in the conventional immersion plating apparatus, the rollers and their bearings must be frequently repaired or replaced. However, it is extremely troublesome to pull up the roller from the plating bath to repair it, which requires a great deal of time and cost. Therefore, according to the present invention, a long treatment material can be drawn into the plating bath, which is a molten metal, without installing a roller, and moreover, it is drawn not from the liquid level of the plating bath but from the intermediate portion thereof. Therefore, it is an object of the present invention to provide an immersion plating apparatus that does not require roller maintenance and is free from the influence of floating oxides.
【０００５】[0005]
【課題を解決するための手段】すなわち、前記の目的を
達成するため、本発明による浸漬メッキ装置は、メッキ
浴槽中に満たされたメッキ浴に長尺な処理材を通し、そ
の表面に金属を付着させて、メッキを施す装置におい
て、処理材ａを通すスリット３を有するメッキ浴槽１
と、前記スリット３を通してメッキ浴槽１の中に処理材
ａが通過するよう案内する処理材ガイド１６と、前記ス
リット３の外側にメッキ浴槽１を囲むように巻かれ、交
流電流が流されるコイル４、５とを備えることを特徴と
するものである。[Means for Solving the Problems] That is, in order to achieve the above-mentioned object, an immersion plating apparatus according to the present invention passes a long treatment material through a plating bath filled in a plating bath and deposits metal on its surface. A plating bath 1 having a slit 3 for passing a treatment material a in an apparatus for applying and plating.
A treatment material guide 16 for guiding the treatment material a to pass through the slit 3 into the plating bath 1, and a coil 4 wound around the plating bath 1 on the outer side of the slit 3 and passing an alternating current. And 5 are provided.
【０００６】さらに、このような浸漬メッキ装置におい
て、前記メッキ浴槽１内のメッキ浴の液位を計測するレ
ベル計９と、溶融炉１からメッキ浴槽１に溶融金属を供
給する溶融金属供給ポンプ１０と、前記レベル計９によ
るメッキ浴の液位により、前記溶融金属供給ポンプ１０
を制御する制御器１５とを備えることを特徴とするもの
である。Further, in such an immersion plating apparatus, a level meter 9 for measuring the liquid level of the plating bath in the plating bath 1 and a molten metal supply pump 10 for supplying molten metal from the melting furnace 1 to the plating bath 1. And the molten metal supply pump 10 depending on the level of the plating bath by the level meter 9.
And a controller 15 for controlling the.
【０００７】これらの浸漬メッキ装置において、前記ス
リット３の手前の処理材ａの通過経路に、同処理材ａを
予熱する加熱部１７を配置するのが好ましい。さらに、
前記スリット３の後の処理材ａの通過経路には、同処理
材ａを加熱するガルバニール処置部２０を配置するのが
好ましい。In these immersion plating apparatuses, it is preferable to dispose a heating section 17 for preheating the treatment material a in the passage of the treatment material a before the slit 3. further,
It is preferable to dispose a galvannealing section 20 for heating the treatment material a in the passage of the treatment material a after the slit 3.
【０００８】[0008]
【作用】前記メッキ装置において、スリット３の外側に
メッキ浴槽１を囲むように巻かれたコイル４、５に交流
電流を流すと、コイル４、５の周囲に交番磁界が生じ
る。この状態で、メッキ浴槽１に導体であるメッキ浴を
満たすと、この交番磁界により、スリット３の内側のメ
ッキ浴には、前記交番磁界を打ち消す方向に渦電流が生
じる。このため、この渦電流と前記交番磁界との電磁作
用により、メッキ浴はメッキ浴槽１の中央へ向けて電磁
力、いわゆるローレンツ力を受け、スリット３から流出
するのが防止される。In the plating apparatus, when an alternating current is passed through the coils 4 and 5 wound around the plating bath 1 outside the slit 3, an alternating magnetic field is generated around the coils 4 and 5. When the plating bath 1 serving as a conductor is filled with the plating bath 1 in this state, an eddy current is generated in the plating bath inside the slit 3 in the direction canceling the alternating magnetic field due to the alternating magnetic field. Therefore, due to the electromagnetic action of the eddy current and the alternating magnetic field, the plating bath receives an electromagnetic force, a so-called Lorentz force, toward the center of the plating bath 1 and is prevented from flowing out from the slit 3.
【０００９】この状態で、スリット３を通してメッキ浴
槽１の中に長尺板状或は線状の処理材ａを引き入れ、ス
リット３を通してメッキ浴槽１の中から処理材ａを引き
出すことができる。これにより、処理材ａをメッキ浴槽
１内のメッキ浴に浸漬することができ、処理材ａの浸漬
メッキが可能となる。In this state, a long plate-shaped or linear treatment material a can be drawn into the plating bath 1 through the slit 3, and the treatment material a can be drawn from the plating bath 1 through the slit 3. As a result, the treatment material a can be immersed in the plating bath in the plating bath 1, and the immersion plating of the treatment material a becomes possible.
【００１０】この浸漬メッキ装置では、処理材ａを真直
にした状態でスリット３を通してメッキ浴槽１の中間部
を通過させればよいので、処理材ａのメッキ浴槽１内で
の折返しのためにメッキ浴中にローラ等を設置する必要
がなく、メッキ浴槽１の外側にのみ処理材ガイド１６を
設ければ足りる。また、メッキ浴槽１内のメッキ浴の液
面から処理材ａをその中に引き入れるものではなく、メ
ッキ浴の液面より下の部分から引き入れるため、処理材
ａが液面に浮遊する酸化物をメッキ浴中に引き入れてし
まわない。このため、処理材ガイド１６に浮遊酸化物を
付着させることもなくなる。In this immersion plating apparatus, since it is sufficient to pass the intermediate portion of the plating bath 1 through the slit 3 in a state where the treatment material a is straightened, it is necessary to plate the treatment material a in order to turn it back inside the plating bath 1. It is not necessary to install rollers or the like in the bath, and it suffices to provide the treatment material guide 16 only outside the plating bath 1. In addition, the treatment material a is not drawn into the plating bath from the liquid surface of the plating bath, but from a portion below the liquid surface of the plating bath, so that the treatment material a is prevented from floating on the liquid surface. Don't pull it into the plating bath. Therefore, the floating oxide is not attached to the processing material guide 16.
【００１１】このような浸漬メッキ装置において、前記
メッキ浴槽１内のメッキ浴の液位を計測するレベル計９
により、溶融炉１２からメッキ浴槽１に溶融金属を供給
する溶融金属供給ポンプ１０を制御するものでは、メッ
キ浴槽１内のメッキ浴の液面を一定に保つことが出来、
安定したメッキが可能となる。In such an immersion plating apparatus, a level meter 9 for measuring the liquid level of the plating bath in the plating bath 1
Thus, in the one that controls the molten metal supply pump 10 that supplies the molten metal from the melting furnace 12 to the plating bath 1, the liquid level of the plating bath in the plating bath 1 can be kept constant,
Stable plating is possible.
【００１２】さらに、前記メッキ浴槽１のスリット３の
手前の処理材ａの通過経路に、同処理材ａを予熱する加
熱部１７を配置して、メッキ浴に浸漬する前に予め処理
材ａを予熱すると、処理材ａの表面へのメッキ付性がよ
くなる。さらに、前記スリット３の後の処理材ａの通過
経路に、同処理材ａを加熱するガルバニール処置部２０
を配置し、メッキ直後の処理材ａを加熱処理すると、い
わゆるガルバニール処理がなされ、メッキ付性が向上す
る。Further, a heating part 17 for preheating the treatment material a is arranged in the passage of the treatment material a before the slit 3 of the plating bath 1 to pretreat the treatment material a before dipping it in the plating bath. Preheating improves the ability of the treated material a to be plated on the surface. Further, in the passage of the processed material a after the slit 3, the galvannealing unit 20 for heating the processed material a is provided.
And heat treatment of the treated material a immediately after plating is performed, so-called galvannealing is performed, and the plating property is improved.
【００１３】[0013]
【実施例】次に、図面を参照しながら、本発明の実施例
について詳細に説明する。図１は、本発明の実施例によ
る浸漬メッキ装置を示す。メッキ浴である溶融金属を満
たすメッキ浴槽１は、その全周にわたってスリット３を
有している。このメッキ浴槽１の底部に排出口が設けら
れ、この排出口にドレンパイプ７が連結されている。こ
の排出口は栓２によって開閉される。Embodiments of the present invention will now be described in detail with reference to the drawings. FIG. 1 shows an immersion plating apparatus according to an embodiment of the present invention. The plating bath 1 which is a plating bath and which is filled with molten metal has slits 3 along the entire circumference thereof. An outlet is provided at the bottom of the plating bath 1, and a drain pipe 7 is connected to the outlet. This outlet is opened and closed by the plug 2.
【００１４】スリット３の外側には、メッキ浴槽１を囲
むようにして巻かれたコイル４、５が配置され、図示の
コイル４、５は、スリット３の中央の上下に各々１つず
つ配置されている。さらに、前記スリット３及びコイル
４、５の間を通して、メッキ浴槽１を水平に横断するよ
う鋼板或は鋼線等の長尺な処理材ａを案内、移動させる
ことができるように、コイル４、５の外側に処理材ガイ
ド１６が配置されている。Outside the slit 3, coils 4 and 5 wound so as to surround the plating bath 1 are arranged, and the illustrated coils 4 and 5 are arranged one above and one below the center of the slit 3. . Further, through the slit 3 and the coils 4 and 5, it is possible to guide and move a long treatment material a such as a steel plate or a steel wire so as to horizontally traverse the plating bath 1, A treatment material guide 16 is arranged on the outer side of 5.
【００１５】スリット３の下側に、メッキ浴槽１の全周
を囲むように、樋６が設けられ、この樋６の一部にドレ
ンパイプ２１が接続されている。前記メッキ浴槽１のド
レンパイプ７と樋６のドレンパイプ２１との下端は、何
れもドレンポット８に臨んでおり、ドレンポット８は、
その下方からヒータ１１で加熱される。A gutter 6 is provided below the slit 3 so as to surround the entire circumference of the plating bath 1, and a drain pipe 21 is connected to a part of the gutter 6. The lower ends of the drain pipe 7 of the plating bath 1 and the drain pipe 21 of the gutter 6 both face the drain pot 8, and the drain pot 8 is
The heater 11 is heated from below.
【００１６】前記メッキ浴槽１とは別に、処理材ａにメ
ッキを施す金属を溶融する溶融炉１２が設けられ、この
溶融炉１２内では、例えばインゴット等がヒータ１３に
より加熱され、溶融される。この溶融炉１２にはレベル
計１４が設けられ、このレベル計１４で計測される溶融
金属の液位が所定のレベル以下となると、それに応じた
量のインゴットが自動または手動により溶融炉１２に投
入され、溶融される。In addition to the plating bath 1, a melting furnace 12 for melting the metal to be plated on the treatment material a is provided. In the melting furnace 12, for example, an ingot is heated by a heater 13 and melted. The melting furnace 12 is provided with a level meter 14, and when the level of the molten metal measured by the level meter 14 falls below a predetermined level, an amount of ingot corresponding to the level is automatically or manually charged into the melting furnace 12. And melted.
【００１７】この溶融炉１２内の溶融金属は、電磁ポン
プ等の溶融金属供給ポンプ１０により、前記メッキ浴槽
１に供給される。メッキ浴槽１にはレベル計９が設けら
れ、そのメッキ浴の液位が計測される。そして、この液
位の計測結果が制御器１５に入力され、これにより前記
溶融金属供給ポンプ１０が制御される。すなわち、レベ
ル計９により計測された液位により、溶融金属ポンプ１
０の出力を連続的にコントロールする。これにより、メ
ッキ液槽１内のメッキ浴は、常時一定の量に維持され
る。なお、メッキ浴槽１の中のメッキ浴の液位は、スリ
ット３から必要以上に高くせず、メッキを行うのに必要
最小限の高さとする。これにより、コイル４、５の出力
を必要以上に大きくさせる必要がなくなる。The molten metal in the melting furnace 12 is supplied to the plating bath 1 by a molten metal supply pump 10 such as an electromagnetic pump. A level meter 9 is provided in the plating bath 1 to measure the liquid level of the plating bath. Then, the measurement result of the liquid level is input to the controller 15, which controls the molten metal supply pump 10. That is, the molten metal pump 1 is determined by the liquid level measured by the level meter 9.
0 output is continuously controlled. As a result, the plating bath in the plating solution tank 1 is constantly maintained at a constant amount. In addition, the liquid level of the plating bath in the plating bath 1 is not raised more than necessary from the slit 3 and is set to the minimum required for plating. This eliminates the need to increase the output of the coils 4 and 5 more than necessary.
【００１８】このような構成からなるメッキ装置におい
て、スリット３の外側にメッキ浴槽１を囲むように巻か
れたコイル４、５に交流電流を流すと、コイル４、５の
周囲に交番磁界が生じる。いま、図２において、上側と
下側のコイル４、５に紙面の手前から奥へ電流が流れる
と、図２に点線で示した矢印の方向に磁界が形成され
る。他方、コイル４、５にこれと逆方向に電流が流れる
と、前記点線の矢印と反対の方向に磁界が発生する。こ
れにより、コイル４、５の周りには、交互に方向の異な
る磁界が発生する。In the plating apparatus having such a structure, when an alternating current is passed through the coils 4 and 5 wound around the plating bath 1 outside the slit 3, an alternating magnetic field is generated around the coils 4 and 5. . Now, in FIG. 2, when a current flows through the upper and lower coils 4 and 5 from the front to the back of the drawing, a magnetic field is formed in the direction of the arrow shown by the dotted line in FIG. On the other hand, when a current flows through the coils 4 and 5 in the opposite direction, a magnetic field is generated in the direction opposite to the dotted arrow. As a result, magnetic fields of different directions are alternately generated around the coils 4 and 5.
【００１９】この状態で、メッキ浴槽１に導体であるメ
ッキ浴を満たすと、この交番磁界により、スリット３の
内側のメッキ浴には、前記交番磁界を打ち消す方向に渦
電流が生じる。例えば、図２に示す方向に磁界が発生し
たときは、スリット３の奥側のメッキ浴には、紙面奥か
ら手前に向けて電流が流れる。この電流は、磁界の向き
が交互に変わる毎に逆向きとなる。このため、この渦電
流と前記交番磁界との電磁作用により、メッキ浴はメッ
キ浴槽１の中央へ向けて電磁力、いわゆるローレンツ力
を受け、スリット３から流出するのが防止される。な
お、スリット３の下部では、その上部に比べてメッキ浴
の圧力が高いため、上側のコイル４より下側のコイル５
の出力を若干大きくする必要がある。When the plating bath 1 which is a conductor is filled with the plating bath in this state, an eddy current is generated in the plating bath inside the slit 3 in the direction of canceling the alternating magnetic field due to the alternating magnetic field. For example, when a magnetic field is generated in the direction shown in FIG. 2, a current flows in the plating bath on the back side of the slit 3 from the back side of the paper toward the front side. This current becomes opposite every time the direction of the magnetic field changes alternately. Therefore, due to the electromagnetic action of the eddy current and the alternating magnetic field, the plating bath receives an electromagnetic force, a so-called Lorentz force, toward the center of the plating bath 1 and is prevented from flowing out from the slit 3. Since the pressure of the plating bath is higher in the lower part of the slit 3 than in the upper part, the coil 5 below the upper coil 4
It is necessary to increase the output of.
【００２０】この状態では、図１に示すように、処理材
ガイド１６側からスリット３を通してメッキ浴槽１の中
に長尺板状或は線状の処理材ａを引き入れ、他方のスリ
ット３から処理材ガイド１６を通してメッキ浴槽１の中
から処理材ａを引き出すことができる。これにより、処
理材ａをメッキ浴槽１内のメッキ浴に浸漬することがで
き、処理材ａの浸漬メッキが可能となる。なお、メッキ
液槽１のスリット３から一部漏れたメッキ浴は、樋６で
受けられ、ドレンパイプ２１を通ってドレンポット８で
受けられる。In this state, as shown in FIG. 1, a long plate-shaped or linear processing material a is drawn into the plating bath 1 from the processing material guide 16 side through the slit 3 and processed from the other slit 3. The treatment material a can be pulled out from the plating bath 1 through the material guide 16. As a result, the treatment material a can be immersed in the plating bath in the plating bath 1, and the immersion plating of the treatment material a becomes possible. The plating bath partially leaked from the slit 3 of the plating liquid tank 1 is received by the gutter 6, passes through the drain pipe 21, and is received by the drain pot 8.
【００２１】次に、図３で示す実施例について説明する
と、この実施例では、処理材ａを通すメッキ液槽１の手
前と先とに、各々処理材ａを前処理及び後処理するため
の手段が設けられている。処理材ａを前処理する手段
は、加熱部１７であり、ヒータ１８により、メッキ浴槽
１に引き込まれる前の処理材ａを予熱し、メッキ付性を
良好とする。この加熱部１７は、微量のＯ2 を含むＳＦ
6 ガス、炭酸ガス及びＮ2 ガスの混合ガス雰囲気とする
のがよい。Next, the embodiment shown in FIG. 3 will be described. In this embodiment, the pretreatment and the posttreatment of the treatment material a are performed before and after the plating solution tank 1 through which the treatment material a is passed. Means are provided. The means for pre-treating the treated material a is the heating unit 17, and the heater 18 preheats the treated material a before being drawn into the plating bath 1 to improve the plating property. This heating unit 17 is an SF containing a slight amount of O 2.
A mixed gas atmosphere of 6 gas, carbon dioxide gas and N 2 gas is preferable.
【００２２】処理材ａを後処理する手段は、第一に、処
理材ａの通過経路の上下に配置されたノズル１９であ
り、このノズル１９から処理材ａの表面に空気またはＮ
2 ガスを高圧で吹き付ける。この高圧ガスの吹き付けに
より、処理材ａの表面に付着したメッキ層を均一化する
ものである。第二に、直火加熱、熱風吹付或は誘導加熱
等の加熱器２２で処理材ａを急速加熱し、処理材ａの金
属成分、例えばＦｅを、表面のメッキ層、例えばＺｎメ
ッキ層に拡散させ、メッキ層をＦｅ−Ｚｎ合金化させ
る、いわゆるガルバニール処理を行うものである。これ
により、処理材ａ表面へのメッキの付着性が良好とな
る。The means for post-treating the treated material a is, firstly, nozzles 19 arranged above and below the passage of the treated material a. From this nozzle 19, air or N is applied to the surface of the treated material a.
2 Blow gas at high pressure. By spraying this high-pressure gas, the plating layer attached to the surface of the treated material a is made uniform. Secondly, the treatment material a is rapidly heated by the heater 22 such as direct fire heating, hot air blowing or induction heating, and the metal component of the treatment material a, for example Fe, is diffused into the surface plating layer, for example the Zn plating layer. Then, a so-called galvannealing process is performed in which the plated layer is made into an Fe—Zn alloy. Thereby, the adhesion of the plating on the surface of the treated material a becomes good.
【００２３】なお、前記の実施例では、スリット３がメ
ッキ浴槽１の全周にわたって設けられているため、最初
に処理材ａをメッキ浴層１の側方からその中央部に引き
入れることができる点で有利である。他方、スリット３
がメッキ浴槽１の全周にわたって設けられておらず、処
理材ａを通すに充分な一部にのみ設けられている場合
は、最初に処理材ａをメッキ浴層１の中に引き入れる操
作に難点がある。しかし、この場合でも、予めスリット
を通して処理材ａをメッキ浴層に通しておいてから、そ
のメッキ浴層にメッキ浴を満たせば、同様にしてメッキ
が行える。In the above embodiment, since the slit 3 is provided over the entire circumference of the plating bath 1, the treatment material a can be first drawn into the plating bath layer 1 from the side to the center thereof. Is advantageous. On the other hand, slit 3
Is not provided over the entire circumference of the plating bath 1, but is provided only in a part sufficient to pass the treatment material a, it is difficult to first draw the treatment material a into the plating bath layer 1. There is. However, even in this case, if the treatment material a is passed through the plating bath layer through the slits in advance and the plating bath layer is filled with the plating bath, plating can be performed in the same manner.
【００２４】[0024]
【発明の効果】以上説明した通り、本発明によれば、溶
融金属であるメッキ浴中にローラを設置せずに、長尺な
処理材をメッキ浴中に引き込むことができる。しかも、
メッキ浴の液面からではなく、その中間部から処理材を
メッキ浴中に引き込むことができる。この結果、ローラ
の保守が不要となり、且つ浮遊酸化物等の影響の無い浸
漬メッキ装置が得られる。As described above, according to the present invention, a long processing material can be drawn into a plating bath which is a molten metal without installing a roller in the plating bath. Moreover,
It is possible to draw the treatment material into the plating bath not from the liquid surface of the plating bath but from an intermediate portion thereof. As a result, maintenance of the roller becomes unnecessary, and an immersion plating apparatus free from the influence of floating oxides can be obtained.
【図１】本発明の実施例である浸漬メッキ装置の概略縦
断側面図である。FIG. 1 is a schematic vertical sectional side view of an immersion plating apparatus which is an embodiment of the present invention.
【図２】同実施例の浸漬メッキ装置の要部拡大側面図で
ある。FIG. 2 is an enlarged side view of an essential part of the immersion plating apparatus of the same embodiment.
【図３】本発明の他の実施例である浸漬メッキ装置の概
略縦断側面図である。FIG. 3 is a schematic vertical sectional side view of an immersion plating apparatus which is another embodiment of the present invention.
１ メッキ浴槽 ３ スリット ４ コイル ５ コイル ９ レベル計 １０ 溶融金属供給ポンプ １５ 制御器 １６ 処理材ガイド １７ 加熱部 ２０ ガルバニール処置部 ａ 処理材 1 Plating Bath 3 Slit 4 Coil 5 Coil 9 Level Meter 10 Molten Metal Supply Pump 15 Controller 16 Processing Material Guide 17 Heating Section 20 Galvanile Treatment Section a Processing Material
───────────────────────────────────────────────────── フロントページの続き (72)発明者 浅葉 信 茨城県日立市滑川本町三丁目19番５号 助 川電気工業株式会社内 ─────────────────────────────────────────────────── ─── Continuation of the front page (72) Inventor Shin Asaba 3-19-5 Namerikawahonmachi, Hitachi City, Ibaraki Prefecture Sukegawa Electric Industry Co., Ltd.
Claims (4)
尺な処理材を通し、その表面に金属を付着させて、メッ
キを施す浸漬メッキ装置において、処理材（ａ）を通す
スリット（３）を有するメッキ浴槽（１）と、前記スリ
ット（３）を通してメッキ浴槽（１）の中に処理材
（ａ）が通過するよう案内する処理材ガイド（１６）
と、前記スリット（３）の外側にメッキ浴槽（１）を囲
むように巻かれ、交流電流が流されるコイル（４）、
（５）とを備えることを特徴とする浸漬メッキ装置。1. A slit (3) through which a treatment material (a) is passed in an immersion plating apparatus in which a long treatment material is passed through a plating bath filled in a plating bath and a metal is attached to the surface of the treatment material to perform plating. And a treatment material guide (16) for guiding the treatment material (a) to pass through the slit (3) into the plating bath (1).
And a coil (4) wound around the outside of the slit (3) so as to surround the plating bath (1) and supplied with an alternating current,
(5) An immersion plating apparatus comprising:
（３）の手前の処理材（ａ）の通過経路に、同処理材
（ａ）を予熱する加熱部（１７）が配置されていること
を特徴とする浸漬メッキ装置。2. The heating unit (17) according to claim 1, wherein a heating unit (17) for preheating the treatment material (a) is arranged in a passage path of the treatment material (a) before the slit (3). Characteristic immersion plating equipment.
リット（３）の後の処理材（ａ）の通過経路に、同処理
材（ａ）を加熱するガルバニール処置部（２０）が配置
されていることを特徴とする浸漬メッキ装置。3. The galvanneale treatment unit (20) for heating the treatment material (a) according to claim 1 or 2, wherein the treatment material (a) passes through the passage after the slit (3). Immersion plating equipment characterized by
記メッキ浴槽（１）内のメッキ浴の液位を計測するレベ
ル計（９）と、溶融炉（１２）からメッキ浴槽（１）に
溶融金属を供給する溶融金属供給ポンプ（１０）と、前
記レベル計（９）によるメッキ浴の液位により、前記溶
融金属供給ポンプ（１０）を制御する制御器（１５）と
を備えることを特徴とする浸漬メッキ装置。4. The level gauge (9) for measuring the liquid level of the plating bath in the plating bath (1) according to any one of claims 1 to 3, and the plating bath (1) from the melting furnace (12). And a controller (15) for controlling the molten metal supply pump (10) according to the level of the plating bath by the level meter (9). Characteristic immersion plating equipment.