JPH07132357A - Lubricating method for plunger tip of casting device - Google Patents
Lubricating method for plunger tip of casting deviceInfo
- Publication number
- JPH07132357A JPH07132357A JP5304666A JP30466693A JPH07132357A JP H07132357 A JPH07132357 A JP H07132357A JP 5304666 A JP5304666 A JP 5304666A JP 30466693 A JP30466693 A JP 30466693A JP H07132357 A JPH07132357 A JP H07132357A
- Authority
- JP
- Japan
- Prior art keywords
- lubricant
- plunger tip
- water
- pts
- heat insulating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、アルミニウム、マグネ
シウム等の非鉄金属の鋳造加工において、水溶性潤滑剤
の使用によってもチル層が生成せず、且つ、優れた潤滑
性が実現されるプランジャーチップの潤滑方法に関す
る。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a plunger which does not form a chill layer even when a water-soluble lubricant is used in casting of non-ferrous metals such as aluminum and magnesium, and has excellent lubricity. A method for lubricating chips.
【0002】[0002]
【従来の技術】鋳造装置におけるプランジャーチップの
潤滑方法としては、従来より、射出スリーブ内周面とプ
ランジャーチップとの間に潤滑剤を供給し、この間の摩
擦を低減して、溶湯をキャビティ内にスムーズに送り込
む方法が採られている。このような目的に使用されるプ
ランジャーチップ用潤滑剤としては、従来より不水溶性
潤滑剤と水溶性潤滑剤とが知られている。不水溶性潤滑
剤としては、例えば、 黒鉛等の粉体を使用する潤滑剤(特開平1−144
494号公報等)、また、水溶性潤滑剤としては、例え
ば、 鉱物油、油脂、脂肪酸エステル、固体潤滑剤、界面
活性剤よりなる潤滑剤(特開平2−248497号公
報)、等が知られている。2. Description of the Related Art As a method of lubricating a plunger tip in a casting apparatus, conventionally, a lubricant is supplied between the inner peripheral surface of the injection sleeve and the plunger tip to reduce the friction between them and to melt the molten metal into a cavity. The method of sending it inside smoothly is adopted. As the plunger tip lubricant used for such a purpose, a water-insoluble lubricant and a water-soluble lubricant have been conventionally known. As the water-insoluble lubricant, for example, a lubricant using powder such as graphite (Japanese Patent Laid-Open No. 1-144)
As the water-soluble lubricant, for example, mineral oil, oil and fat, fatty acid ester, solid lubricant, lubricant composed of a surfactant (JP-A-2-248497), and the like are known. ing.
【0003】しかし、前記の不水溶性潤滑剤は、オイ
ルを主成分とするため火災の危険性を有しているととも
に、機械周辺を汚すという問題点がある。これに対し
て、黒鉛を含有せず、白色固体潤滑剤を使用する不水溶
性潤滑剤(特開平2−215894号公報)、或いは粉
体を含有しない不水溶性潤滑剤(特開平2−22839
3号公報)なども提案されているが、前者は依然として
火災の危険性があり、後者は潤滑性が劣るという問題が
ある。一方、前記の水溶性潤滑剤は、不水溶性潤滑剤
に比較して潤滑性が劣り、プランジャーチップのかじり
が発生するという問題がある。However, since the water-insoluble lubricant contains oil as a main component, it has a risk of fire and also has a problem of contaminating the periphery of the machine. On the other hand, a water-insoluble lubricant containing no graphite and using a white solid lubricant (JP-A-2-215894), or a water-insoluble lubricant containing no powder (JP-A-2-22839).
No. 3) has been proposed, but the former still has a risk of fire and the latter has a problem that lubricity is inferior. On the other hand, the above water-soluble lubricant has a problem that the lubricity is inferior to that of the water-insoluble lubricant, and galling of the plunger tip occurs.
【0004】更に、上記水溶性潤滑剤では、潤滑剤中の
水の蒸発潜熱により射出スリーブ内周面等が冷却され、
スリーブ内周面の断熱性が低い場合には溶湯自体が有す
る熱の逸散も大きく、冷却されたスリーブ内周面に接す
る溶湯表面が凝固して金属の薄層(通常、チル層とい
う)が生成することがあり、このチル層がプランジャー
チップによって剥がされ鋳造品中に混入するため、鋳造
後の製品品位を損なうという問題もある。以上説明した
ように、非鉄金属の鋳造加工において、水溶性潤滑剤の
使用によってもチル層が生成せず、潤滑性に優れたプラ
ンジャーチップの潤滑方法は見出されていないのが実情
である。Further, in the above water-soluble lubricant, the inner peripheral surface of the injection sleeve is cooled by latent heat of vaporization of water in the lubricant,
When the inner peripheral surface of the sleeve has low heat insulation, the heat of the molten metal itself dissipates greatly, and the molten metal surface in contact with the cooled inner peripheral surface of the sleeve solidifies to form a thin metal layer (usually called a chill layer). There is a problem in that the chill layer may be formed, and the chill layer is peeled off by the plunger tip and mixed in the cast product, thereby impairing the product quality after casting. As described above, in the non-ferrous metal casting process, the chill layer is not formed even by the use of the water-soluble lubricant, and the method of lubricating the plunger tip having excellent lubricity has not been found. .
【0005】[0005]
【発明が解決しようとする課題】本発明は、上記問題点
を解決するものであり、水溶性潤滑剤の使用によっても
チル層の生成がなく、且つ、高潤滑性が維持され、火災
の危険性もなく、作業環境の良好なプランジャーチップ
の潤滑方法を提供することを課題とする。DISCLOSURE OF THE INVENTION The present invention solves the above-mentioned problems. Even when a water-soluble lubricant is used, a chill layer is not formed, high lubricity is maintained, and there is a risk of fire. It is an object of the present invention to provide a method for lubricating a plunger tip which has no working property and has a good working environment.
【0006】[0006]
【課題を解決するための手段】本発明者らは、非鉄金属
の鋳造加工における、チル層生成防止のための射出スリ
ーブ内周面用断熱剤の組成とその効果、及びプランジャ
ーチップ用水溶性潤滑剤の組成と潤滑性との関係、並び
にそれらを用いたプランジャーチップの潤滑方法につい
て鋭意検討した結果、潤滑剤を供給する前に、先ず、鋳
造装置の射出スリーブ内周面に断熱剤の皮膜を形成し、
次いで、その皮膜表面及び/又はプランジャーチップの
表面に潤滑剤を供給する方法により、水溶性潤滑剤を使
用した場合の従来の問題点、即ち、チル層の生成、不十
分な潤滑性等が解決されることを見出し、本発明を完成
するに至ったのである。The inventors of the present invention have found the composition and effect of a heat insulating agent for the inner peripheral surface of an injection sleeve for preventing the formation of a chill layer in the casting process of non-ferrous metal, and a water-soluble lubricant for a plunger tip. As a result of diligent studies on the relationship between the composition of the lubricant and the lubricity and the lubrication method of the plunger tip using them, first, before supplying the lubricant, first, a film of a heat insulating agent was formed on the inner peripheral surface of the injection sleeve of the casting machine. To form
Then, by the method of supplying the lubricant to the surface of the film and / or the surface of the plunger tip, the conventional problems when the water-soluble lubricant is used, that is, formation of a chill layer, insufficient lubricity, etc. The inventors have found that they can be solved and have completed the present invention.
【0007】即ち、本第1発明のプランジャーチップの
潤滑方法は、鋳造装置の射出スリーブ内周面に断熱剤の
皮膜を形成した後、潤滑剤を供給することを特徴とす
る。また、第2発明は、上記潤滑剤を上記断熱剤の皮膜
の表面及び/又は上記プランジャーチップの表面に供給
することを特徴とし、第3発明は、上記断熱剤が、
(a)無機粉体、(b)分散剤、(c)界面活性剤、及
び(d)水を含有することを特徴とする。第1〜2発明
をより具体的に説明すれば、上記「断熱剤」を予めスプ
レー等の方法で射出スリーブ内周面に展着して「皮膜」
を形成し、その皮膜上に上記「潤滑剤」をスプレー等で
塗布する、或いは断熱剤を展着した後に、潤滑剤をプラ
ンジャーチップ表面に滴下、又はアトマイザーにより空
気と共に高圧で吹き付けて供給する、更には、これらを
併用する等により、プランジャーチップの潤滑性を良好
なものとする方法などが挙げられる。That is, the plunger tip lubricating method according to the first aspect of the present invention is characterized in that the lubricant is supplied after forming a heat insulating agent film on the inner peripheral surface of the injection sleeve of the casting apparatus. A second invention is characterized in that the lubricant is supplied to the surface of the film of the heat insulating agent and / or the surface of the plunger tip, and the third invention is that the heat insulating agent is
It is characterized by containing (a) inorganic powder, (b) dispersant, (c) surfactant, and (d) water. The first and second inventions will be described in more detail. The "heat insulating agent" is spread on the inner peripheral surface of the injection sleeve in advance by a method such as spraying to form a "film".
Is formed, and the above "lubricant" is applied to the film by spraying or the like, or after spreading the heat insulating agent, the lubricant is dropped on the surface of the plunger tip, or is sprayed at a high pressure with air by an atomizer and supplied. Further, a method of improving the lubricity of the plunger tip by using them in combination is included.
【0008】上記「無機粉体」としては、例えば、雲
母、タルク、カオリン、セリサイト、ジルコンフラワ
ー、ジルコンサンド、石英ガラス粉末、窒化ホウ素、フ
ッ化黒鉛等を使用できる。また、上記分散剤としては、
例えば、カルボキシメチルセルロース、メチルセルロー
ス、ヒドロオキシセルロース等のセルロースエーテル、
天然多糖類、及びモンモロリナイト鉱石群からなる群か
ら選ばれる1種又は2種以上を使用できる。As the above-mentioned "inorganic powder", for example, mica, talc, kaolin, sericite, zircon flour, zircon sand, quartz glass powder, boron nitride, fluorinated graphite and the like can be used. Further, as the dispersant,
For example, carboxymethyl cellulose, methyl cellulose, cellulose ether such as hydroxy cellulose,
One or more selected from the group consisting of natural polysaccharides and montmorillonite ore group can be used.
【0009】更に、上記「界面活性剤」は、本発明の潤
滑方法で使用する断熱剤中で、無機粉体を分散、湿潤す
るために使用する成分であり、具体的には、断熱剤全体
の均一な分散、混合を妨げないものであれば、脂肪族ア
ミン塩、ピリジニウム塩、イミダゾリニウム塩等のカチ
オン系界面活性剤、脂肪酸石鹸、アルキルベンゼンスル
ホン酸塩、アルキルナフタレンスルホン酸塩等のアニオ
ン系界面活性剤、及びポリオキシエチレンアルキルエー
テル、ポリオキシエチレンソルビタン脂肪酸エステル、
ポリエチレングリコール脂肪酸エステル等のノニオン系
界面活性剤などを使用できる。Further, the above-mentioned "surfactant" is a component used for dispersing and wetting the inorganic powder in the heat insulating agent used in the lubricating method of the present invention, and specifically, the whole heat insulating agent. If it does not hinder the uniform dispersion and mixing of cations, cationic surfactants such as aliphatic amine salts, pyridinium salts, imidazolinium salts, anions such as fatty acid soaps, alkylbenzene sulfonates, alkylnaphthalene sulfonates, etc. -Based surfactants, polyoxyethylene alkyl ethers, polyoxyethylene sorbitan fatty acid esters,
A nonionic surfactant such as polyethylene glycol fatty acid ester can be used.
【0010】本発明のプランジャーチップの潤滑方法に
使用される水溶性潤滑剤としては、(a)鉱油、油脂、
脂肪酸、及び脂肪酸エステルからなる群から選ばれる1
種又は2種以上、(b)ワックス、(c)高級脂肪酸金
属塩、(d)界面活性剤、並びに(e)水等を含有する
潤滑剤などを使用できる。潤滑剤は必ずしも上記各成分
全てを含有する必要はなく、例えば、(c)成分を欠い
たもの、(a)及び(b)成分を欠いたものであっても
使用できる。潤滑剤中の界面活性剤は、射出スリーブ内
周面及び/又はプランジャーチップ表面に固着した潤滑
剤を水洗して除去する際に、潤滑剤を可溶化する作用を
有する成分であり、潤滑剤全体の均一な混合、分散を妨
げない限り、上記断熱剤の場合と同様のものを使用でき
る。Examples of the water-soluble lubricant used in the method of lubricating the plunger tip of the present invention include (a) mineral oil, fats and oils,
1 selected from the group consisting of fatty acids and fatty acid esters
It is possible to use a lubricant containing one kind or two or more kinds, (b) wax, (c) higher fatty acid metal salt, (d) surfactant, and (e) water. The lubricant does not necessarily need to contain all of the above components, and for example, a lubricant lacking the component (c) or a lubricant lacking the components (a) and (b) can be used. The surfactant in the lubricant is a component having a function of solubilizing the lubricant when the lubricant adhered to the inner peripheral surface of the injection sleeve and / or the plunger tip surface is removed by washing with water. As long as it does not hinder the uniform mixing and dispersion of the whole, the same materials as those for the heat insulating agent can be used.
【0011】上記の鉱油、油脂、脂肪酸及び脂肪酸エス
テルは、プランジャーチップ用水溶性潤滑剤において、
特に低温領域での潤滑性を発揮するための成分である。
上記油脂としては、例えば、ナタネ油、大豆油、ヤシ
油、パーム油、牛脂、豚脂等の動植物油脂等が挙げられ
る。また、上記脂肪酸としては、例えば、ヤシ油脂肪
酸、オレイン酸、ステアリン酸、ラウリン酸、パルミチ
ン酸、牛脂脂肪酸等が挙げられる。更に、上記脂肪酸エ
ステルとしては、例えば、上記脂肪酸の一価アルコール
エステル又は多価アルコールエステル等が挙げられる。
これらのうち、耐熱性、他成分との溶解性の観点から、
ヤシ油脂肪酸、オレイン酸、ステアリン酸等とトリメチ
ロールプロパン、ネオペンチルアルコールとのエステル
が好ましい。The above-mentioned mineral oil, fats and oils, fatty acids and fatty acid esters are used in a water-soluble lubricant for plunger tips.
Especially, it is a component for exerting lubricity in a low temperature range.
Examples of the fats and oils include animal and vegetable fats and oils such as rapeseed oil, soybean oil, coconut oil, palm oil, beef tallow and lard. Examples of the fatty acid include coconut oil fatty acid, oleic acid, stearic acid, lauric acid, palmitic acid, beef tallow fatty acid and the like. Furthermore, examples of the fatty acid ester include monohydric alcohol esters and polyhydric alcohol esters of the fatty acids.
Of these, from the viewpoint of heat resistance and solubility with other components,
Esters of coconut oil fatty acid, oleic acid, stearic acid and the like with trimethylolpropane and neopentyl alcohol are preferable.
【0012】また、上記のワックスとしては、天然若し
くは合成の炭化水素ワックス及びロウ、並びにそれらの
酸化物や酸変性物等を挙げることができる。ここで、天
然ワックスとしては、例えば、密ロウ、鯨ロウ、水添鯨
ロウ、カルナバワックス、キャンデリアワックス、木ロ
ウ、ぬかロウ等の動植物性ワックス、パラフィンワック
ス、マイクロクリスタリンワックス、モンタンワック
ス、セリシンワックス等の鉱物性ワックスなどを挙げる
ことができる。Examples of the above waxes include natural and synthetic hydrocarbon waxes and waxes, and oxides and acid modified products thereof. Examples of the natural wax include animal waxes such as beeswax, spermaceti wax, hydrogenated spermaceti wax, carnauba wax, candelia wax, wood wax, bran wax, paraffin wax, microcrystalline wax, montan wax, sericin. Mineral wax such as wax can be used.
【0013】更に、上記の高級脂肪酸金属塩は、プラン
ジャーチップ用水溶性潤滑剤において、高温領域での油
膜切れを防止し、高温において潤滑性を発揮する成分で
あり、例えば、ヤシ油脂肪酸、オレイン酸、ステアリン
酸、ラウリン酸、パルミチン酸、牛脂脂肪酸等の高級脂
肪酸と、ナトリウム、カリウム、マグネシウム、リチウ
ム、カルシウム、アルミニウム、亜鉛等の金属との塩な
どを使用できる。尚、本発明のプランジャーチップの潤
滑方法に使用される水溶性潤滑剤は、上記の各成分以外
に、防食剤、増粘剤、湿潤剤、防腐・防黴剤、消泡剤等
の任意添加剤を適宜添加して使用できる。Further, the above-mentioned higher fatty acid metal salt is a component which prevents oil film breakage in a high temperature region and exhibits lubricity at a high temperature in a water-soluble lubricant for a plunger tip, such as coconut oil fatty acid and olein. A salt of a higher fatty acid such as an acid, stearic acid, lauric acid, palmitic acid, or beef tallow fatty acid with a metal such as sodium, potassium, magnesium, lithium, calcium, aluminum or zinc can be used. The water-soluble lubricant used in the method for lubricating the plunger tip of the present invention may be any of anticorrosion agents, thickeners, wetting agents, antiseptic / antifungal agents, defoaming agents, etc., in addition to the above components. Additives can be appropriately added and used.
【0014】[0014]
【作用】本発明では、鋳造装置の射出スリーブ内周面に
予め断熱剤の皮膜を形成することにより、その後供給さ
れる水溶性潤滑剤中の水の蒸発潜熱によって、射出スリ
ーブ内周面が冷却され、溶湯の温度が部分的に低下した
としても、射出スリーブ内周面及び溶湯から奪われた熱
の射出スリーブ外部への逸散が抑えられる。そのため、
溶湯表面の温度低下が小さく、チル層が生成せず、供給
される潤滑剤の性能が十分に発揮され、優れた潤滑性が
維持されるものである。According to the present invention, by forming a film of a heat insulating agent on the inner peripheral surface of the injection sleeve of the casting apparatus in advance, the inner peripheral surface of the injection sleeve is cooled by latent heat of vaporization of water in the water-soluble lubricant supplied thereafter. Even if the temperature of the molten metal is partially lowered, the heat taken away from the inner peripheral surface of the injection sleeve and the molten metal is prevented from escaping to the outside of the injection sleeve. for that reason,
The temperature drop on the surface of the molten metal is small, a chill layer is not formed, the performance of the supplied lubricant is fully exhibited, and excellent lubricity is maintained.
【0015】[0015]
【実施例】以下、実施例及び比較例により本発明を具体
的に説明する。 (1) 断熱剤及び潤滑剤の調製及び組成 実施例及び比較例に使用した断熱剤及び潤滑剤は、表1
に示す組成成分を混合して調製した。尚、表中の組成に
関する数値は、何れも断熱剤又は潤滑剤の全量を100
重量部とした場合の重量部を表す。また、表1におい
て、各成分は具体的にはそれぞれ以下のものを使用し
た。EXAMPLES The present invention will be specifically described below with reference to Examples and Comparative Examples. (1) Preparation and composition of heat insulating agent and lubricant The heat insulating agent and lubricant used in Examples and Comparative Examples are shown in Table 1.
It was prepared by mixing the composition components shown in. In addition, the numerical values relating to the composition in the table are 100% of the total amount of the heat insulating agent or the lubricant.
The parts by weight are shown when the parts are parts by weight. Further, in Table 1, each component specifically used the following.
【0016】a) タルク:日本タルク株式会社製、商品
名「ミクロエースP4」(平均粒径;1.5μm) b) 窒化ホウ素:三井東圧化学株式会社製、商品名「M
BN−050」(平均粒径;0.1〜0.2μm) c) 分散剤:カルボキシメチルセルロース d) 界面活性剤A:三洋化成工業株式会社製、商品名
「ノニポールSN60」 e) 界面活性剤B:三洋化成工業株式会社製、商品名
「ノニポールSN85」 f) 界面活性剤C:ソルビタンモノオレエート g) 鉱油:日本石油株式会社製、商品名「SAE30」
(40℃における動粘度;100mm2 /s) h) ワックス:アライドケミカル社製、商品名「ACポ
リエチレン629」(酸化ポリエチレンワックス、酸
価;16) i) 高級脂肪酸金属塩:ステアリン酸カルシウムA) Talc: Nippon Talc Co., Ltd., trade name "Microace P4" (average particle size: 1.5 μm) b) Boron nitride: Mitsui Toatsu Chemical Co., Ltd., trade name "M
BN-050 "(average particle size; 0.1 to 0.2 μm) c) Dispersant: carboxymethyl cellulose d) Surfactant A: Sanyo Chemical Industries, Ltd., trade name" Nonipol SN60 "e) Surfactant B : Sanyo Chemical Industry Co., Ltd., trade name "Nonipol SN85" f) Surfactant C: sorbitan monooleate g) Mineral oil: Nippon Oil Co., Ltd., trade name "SAE30"
(Kinematic viscosity at 40 ° C .; 100 mm 2 / s) h) Wax: Allied Chemical Co., trade name “AC polyethylene 629” (oxidized polyethylene wax, acid value; 16) i) Higher fatty acid metal salt: calcium stearate
【0017】[0017]
【表1】 [Table 1]
【0018】(2)性能試験 図1に示す試験装置によって、溶解ルツボ3中の温度7
80℃のアルミニウム溶湯1中に、外周面及び底面に表
1に示す断熱剤をスプレーで塗布して皮膜を形成した
後、形成された断熱剤皮膜上に、同様にスプレーによっ
て表1の潤滑剤を塗布して潤滑剤皮膜を形成した治具5
を浸漬し、治具温度が600℃に達するまでの時間(断
熱性)を調べた。尚、図中2は溶湯を溶融状態に保つた
めの電気炉、4は潤滑剤及び断熱剤皮膜、並びに治具壁
を介して、治具内部へ伝わる熱による昇温を測定するた
めのシース型熱電対、6は電気炉と溶解ルツボとの間の
空間の熱の外部への逸散を防止するため、空間上部にド
ーナツ状に嵌装されたガラスウール、7は熱電対によっ
て測定された温度を径時的に記録するためのレコーダー
である。(2) Performance test Using the test apparatus shown in FIG. 1, the temperature in the melting crucible 3 was reduced to 7
The heat insulating agent shown in Table 1 was applied by spraying on the outer peripheral surface and the bottom surface of the molten aluminum 1 at 80 ° C. to form a film, and then the lubricant of Table 1 was also sprayed on the formed heat insulating agent film. 5 with a lubricant applied to form a lubricant film
Was immersed, and the time until the jig temperature reached 600 ° C. (heat insulating property) was examined. In the figure, 2 is an electric furnace for keeping the molten metal in a molten state, 4 is a sheath type for measuring the temperature rise due to the heat transmitted to the inside of the jig through the lubricant and heat insulating agent coating, and the jig wall. A thermocouple, 6 is a glass wool that is fitted in a donut shape at the upper part of the space to prevent the heat in the space between the electric furnace and the melting crucible from escaping to the outside, and 7 is the temperature measured by the thermocouple. It is a recorder for recording the time.
【0019】また、試験片(材質:SPCC−SB、寸
法;20×160×1mm)に上記と同様にして断熱剤
の皮膜を形成した後、その皮膜表面に表1の潤滑剤を塗
布し、バウデン摩擦試験機を使用して潤滑性(摩擦係
数)を調べた。尚、比較例1では、治具表面に断熱剤皮
膜のみを形成し、比較例2〜5では、断熱剤皮膜は形成
せず、治具表面に直接潤滑剤皮膜を形成して試験をし
た。断熱性試験条件及び潤滑性試験条件を下記に示し、
結果を表2に示す。Further, after forming a heat insulating agent film on the test piece (material: SPCC-SB, size: 20 × 160 × 1 mm) in the same manner as described above, the lubricant of Table 1 is applied to the surface of the film, Lubricity (friction coefficient) was examined using a Bowden friction tester. In Comparative Example 1, only the heat insulating agent film was formed on the jig surface, and in Comparative Examples 2 to 5, the heat insulating agent film was not formed, and the lubricant film was directly formed on the jig surface for the test. The heat insulation test conditions and lubricity test conditions are shown below,
The results are shown in Table 2.
【0020】 断熱性 溶湯温度:780℃ 溶湯材質:ADC12 治具材質:SKD61 治具寸法:φ13.8×95 潤滑性 鋼球:SUJ−2 試験温度:200℃ 荷重:0.5Kgf 滑り速度:4.0mm/s 滑り距離:30mmAdiabatic property Molten metal temperature: 780 ° C. Molten metal material: ADC12 Jig material: SKD61 Jig size: φ13.8 × 95 Lubricity Steel ball: SUJ-2 Test temperature: 200 ° C. Load: 0.5 Kgf Sliding speed: 4 0.0mm / s Sliding distance: 30mm
【0021】[0021]
【表2】 [Table 2]
【0022】表2の結果より、各実施例では600℃に
達するまでの時間が長く、断熱性が高いことが分かる。
また、摩擦係数が小さく潤滑性も優れていることが分か
る。これに対して、比較例1では、断熱剤の付着量は各
実施例と同等であり、断熱性も同程度に優れているが、
潤滑剤を使用していないため、焼き付いてしまってい
る。また、比較例2〜5では、潤滑剤の付着量は各実施
例よりも多く、摩擦係数の値も殆ど同じであるが、断熱
剤を使用していないため、各実施例の半分強の時間で6
00℃にまで達しており、断熱性に劣ることが分かる。
尚、本発明においては、前記具体的実施例に示すものに
限られず、目的、用途に応じて本発明の範囲内で種々変
更した実施例とすることができる。From the results of Table 2, it can be seen that in each Example, the time required to reach 600 ° C. is long and the heat insulating property is high.
Further, it can be seen that the coefficient of friction is small and the lubricity is excellent. On the other hand, in Comparative Example 1, the amount of the heat insulating agent attached is the same as that in each Example, and the heat insulating property is also excellent to the same degree.
Since no lubricant is used, it has burned in. Further, in Comparative Examples 2 to 5, the amount of lubricant adhered is larger than that in each example and the friction coefficient values are almost the same, but since a heat insulating agent is not used, the time is a little over half of each example. In 6
It can be seen that the temperature reaches up to 00 ° C and the heat insulating property is poor.
The present invention is not limited to the specific examples described above, and various modifications may be made within the scope of the present invention depending on the purpose and application.
【0023】[0023]
【発明の効果】本発明のプランジャーチップの潤滑方法
によって非鉄金属の鋳造加工を行えば、射出スリーブ内
周面の断熱性に優れるため、水溶性潤滑剤の使用によっ
てもチル層の生成がなく、そのため供給される潤滑剤の
性能が十分に発揮され、不水溶性潤滑剤を使用した場合
と同等の潤滑性が実現され、焼け等の発生もない。更
に、本発明では、水溶性潤滑剤を使用しているため、火
災の危険性が全くなく、また、装置周辺のオイルによる
汚損という問題もない。EFFECTS OF THE INVENTION When a non-ferrous metal is cast by the plunger tip lubrication method of the present invention, the inner peripheral surface of the injection sleeve is excellent in heat insulation. Therefore, even if a water-soluble lubricant is used, a chill layer is not formed. Therefore, the performance of the supplied lubricant is sufficiently exerted, the lubricity equivalent to the case of using the water-insoluble lubricant is realized, and the occurrence of burning etc. does not occur. Further, in the present invention, since the water-soluble lubricant is used, there is no risk of fire and there is no problem of contamination by oil around the device.
【図1】本発明のプランジャーチップの潤滑方法におけ
る、射出スリーブ内周面の断熱性を評価するための試験
装置の横断面図である。FIG. 1 is a cross-sectional view of a test device for evaluating the heat insulating property of an inner peripheral surface of an injection sleeve in a method of lubricating a plunger tip of the present invention.
1;溶湯、2;電気炉、3;溶解ルツボ、4;シース型
熱電対、5;治具、6;ガラスウール、7;レコーダー1; molten metal, 2; electric furnace, 3; melting crucible, 4; sheath type thermocouple, 5; jig, 6; glass wool, 7; recorder
フロントページの続き (72)発明者 横井 光義 愛知県刈谷市昭和町1丁目1番地 日本電 装株式会社内 (72)発明者 吉川 澄 愛知県刈谷市昭和町1丁目1番地 日本電 装株式会社内Front page continued (72) Inventor Mitsuyoshi Yokoi, 1-1, Showa-cho, Kariya city, Aichi prefecture, Nihon Denso Co., Ltd. (72) Inventor, Sumi Yoshikawa, 1-1, Showa-machi, Kariya city, Aichi prefecture, Nihondenso Co., Ltd.
Claims (3)
の皮膜を形成した後、水溶性潤滑剤を供給することを特
徴とするプランジャーチップの潤滑方法。1. A method for lubricating a plunger tip, which comprises supplying a water-soluble lubricant after forming a film of a heat insulating agent on the inner peripheral surface of an injection sleeve of a casting apparatus.
の表面及び/又は上記プランジャーチップの表面に供給
することを特徴とする請求項1記載のプランジャーチッ
プの潤滑方法。2. The method for lubricating a plunger tip according to claim 1, wherein the water-soluble lubricant is supplied to the surface of the film of the heat insulating agent and / or the surface of the plunger tip.
分散剤、(c)界面活性剤、及び(d)水を含有するこ
とを特徴とする請求項1又は2記載のプランジャーチッ
プの潤滑方法。3. The heat insulating agent is (a) inorganic powder, (b)
The method for lubricating a plunger tip according to claim 1 or 2, further comprising a dispersant, (c) a surfactant, and (d) water.