JPH0636262A - Magnetic recording medium - Google Patents
Magnetic recording mediumInfo
- Publication number
- JPH0636262A JPH0636262A JP21380692A JP21380692A JPH0636262A JP H0636262 A JPH0636262 A JP H0636262A JP 21380692 A JP21380692 A JP 21380692A JP 21380692 A JP21380692 A JP 21380692A JP H0636262 A JPH0636262 A JP H0636262A
- Authority
- JP
- Japan
- Prior art keywords
- magnetic
- strength
- medium
- recording medium
- output
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【0001】[0001]
【産業上の利用分野】本発明は、磁気テープ等の磁気記
録媒体に関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a magnetic recording medium such as a magnetic tape.
【0002】[0002]
【従来の技術】例えば、8mm方式やVHS−C方式に代
表されるカメラ一体型VTRにおいては、小型軽量化を
図るために、テープカセットも小型のものが使用され
る。このため、記録時間を確保するのが困難であり、8
mm方式では最大2時間、VHS−C方式では標準モード
で20分の録画時間が限度であり、十分な記録時間が得ら
れない。2. Description of the Related Art For example, in a camera-integrated VTR represented by an 8 mm system and a VHS-C system, a small tape cassette is used in order to reduce the size and weight. Therefore, it is difficult to secure the recording time.
In the mm system, the maximum recording time is 2 hours, and in the VHS-C system, the recording time is 20 minutes in the standard mode.
【0003】そこで、このような録画再生時間の問題を
解消し、その記録容量を上げるための手段として、テー
プカセット内に収容される磁気テープとして厚さの薄い
ものを使用することにより、テープカセットの巻取りエ
リアの中に巻かれるテープの長さを長く(長尺化)し、
記録エリアの拡大を行うこと等がある。この際、同一シ
ステム上に異なる2種類の媒体、すなわち長尺化前(厚
物)と長尺化後(薄物)の媒体が存在することになる
が、理想的には、この両者ともに同じ特性を示すことが
望ましい。Therefore, as a means for solving such a problem of the recording / reproducing time and increasing the recording capacity, by using a magnetic tape having a small thickness as a magnetic tape accommodated in the tape cassette, a tape cassette is used. The length of the tape wound in the winding area of
For example, the recording area may be expanded. At this time, there are two different types of media on the same system, that is, a medium before lengthening (thick material) and a medium after lengthening (thin material), but ideally, both have the same characteristics. Is desirable.
【0004】しかし、現実には、同一システムで上記し
た2種類の媒体を使用すると、磁気ヘッドと媒体との接
触状況に違いが発生し、2つの媒体の出力特性に差が生
じることが多々報告されている。In reality, however, it is often reported that when the above-mentioned two types of media are used in the same system, the contact state between the magnetic head and the medium is different and the output characteristics of the two media are different. Has been done.
【0005】例えは、2つの媒体に厚みの異なるPET
(ポリエチレンテレフタレート)ベースフィルムを使用
し、ベースフィルムの厚みが厚物で10〜12μm、薄物で
5〜7μmであるとする。この時のベースフィルムの物
理特性は、下記の表−1に示す通りである。For example, the two media may have different thicknesses of PET.
It is assumed that a (polyethylene terephthalate) base film is used and the thickness of the base film is 10 to 12 μm for a thick material and 5 to 7 μm for a thin material. Physical properties of the base film at this time are as shown in Table 1 below.
【0006】 [0006]
【0007】そして、上記した2種類のPETベースフ
ィルムに磁性塗料を塗布し、作製された各媒体を、同一
システムにおいて評価すると、厚物の媒体に比べ、薄物
の媒体は出力が非常に不安定であることが確認された。
図1には、各種媒体について得られた出力波形をオシロ
スコープで示したが、上記の厚物が比較例1に、上記の
薄物が比較例2にそれぞれ相当している。When the above-mentioned two types of PET base films were coated with a magnetic coating material and each produced medium was evaluated in the same system, the output of the thin medium was very unstable as compared with that of the thick medium. Was confirmed.
In FIG. 1, output waveforms obtained for various media are shown by an oscilloscope. The thick material corresponds to Comparative Example 1 and the thin material corresponds to Comparative Example 2.
【0008】図1の結果から、薄物のベースフィルムを
使用すると、出力が非常に不安定となることが明らかで
あるが、これは磁気ヘッドに対する媒体の接触状態が不
安定であることによるものと思われる。From the results shown in FIG. 1, it is clear that the output becomes very unstable when a thin base film is used. This is because the contact state of the medium with the magnetic head is unstable. Seem.
【0009】しかしながら、媒体の記憶容量の拡大は、
今後も必要不可欠であり、媒体の薄物化はさらに進むと
考えられる。これを可能にするためにも、上記した2種
類の媒体間の出力特性の差の問題を解決する必要があ
る。However, the expansion of the storage capacity of the medium is
It will be indispensable in the future, and it is thought that the media will become thinner. In order to enable this, it is necessary to solve the problem of the difference in the output characteristics between the two types of media described above.
【0010】[0010]
【発明が解決しようとする課題】本発明の目的は、次の
(1)〜(4) を可能にする磁気記録媒体を提供することに
ある。The objects of the present invention are as follows.
It is to provide a magnetic recording medium capable of (1) to (4).
【0011】(1) 磁気記録媒体の薄物化に起因する特性
劣化を小さくできること。 (2) 磁気記録媒体の薄物化に起因する磁気ヘッドと媒体
の接触状況を改善できること。 (3) 同一システム上で、厚物媒体と薄物媒体の特性互換
性が確保できること。 (4) 磁気記録媒体の薄物化による記録容量の拡大が可能
となること。(1) It is possible to reduce characteristic deterioration due to thinning of the magnetic recording medium. (2) To improve the contact condition between the magnetic head and the medium due to the thinning of the magnetic recording medium. (3) It is possible to ensure compatibility of characteristics between thick media and thin media on the same system. (4) The recording capacity can be expanded by making the magnetic recording medium thinner.
【0012】[0012]
【課題を解決するための手段】即ち、本発明は、非磁性
支持上に磁性層が形成されている磁気記録媒体におい
て、前記非磁性支持体の縦方向強度として、破断強度が
40〜60Kg/mm2 、ヤング率が 800〜1000Kg/mm2 (特に
850〜1000Kg/mm2)、5%伸び荷重が15〜30Kg/mm2で
あり、かつ、前記非磁性支持体の縦方向強度とその横方
向強度との比(縦方向強度/横方向強度)が、破断強度
では 1.8以上(特に 2.0以上)、ヤング率では 1.8以上
(特に 2.0以上)、5%伸び荷重が 1.8以上(特に 2.0
以上)であることを特徴とする磁気記録媒体に係るもの
である。That is, according to the present invention, in a magnetic recording medium in which a magnetic layer is formed on a non-magnetic support, the breaking strength as the longitudinal strength of the non-magnetic support is
40-60Kg / mm 2 , Young's modulus 800-1000Kg / mm 2 (especially
850 to 1000 kg / mm 2 ), 5% elongation load is 15 to 30 kg / mm 2 , and the ratio of the longitudinal strength of the non-magnetic support to its lateral strength (longitudinal strength / lateral strength) However, the breaking strength is 1.8 or more (especially 2.0 or more), the Young's modulus is 1.8 or more (especially 2.0 or more), and the 5% elongation load is 1.8 or more (especially 2.0 or more).
The above) relates to the magnetic recording medium.
【0013】本発明において、前記非磁性支持体の縦方
向の破断伸度が20〜40%であり、前記非磁性支持体の縦
方向の破断伸度とその横方向の破断伸度との比(縦方向
の破断伸度/横方向の破断伸度)が0.25以下であること
が望ましい。In the present invention, the breaking elongation in the machine direction of the non-magnetic support is 20 to 40%, and the ratio of the breaking elongation in the machine direction to the breaking elongation in the cross direction of the non-magnetic support. It is desirable that (elongation at break in longitudinal direction / elongation at break in lateral direction) is 0.25 or less.
【0014】また、本発明は、非磁性支持体の厚みが5
〜10μmと薄物である磁気記録媒体に対して効果的であ
る。In the present invention, the thickness of the non-magnetic support is 5
This is effective for a magnetic recording medium that is as thin as -10 μm.
【0015】本発明者は、既述した出力特性の差が、媒
体に使用される非磁性支持体の厚みに依るものであると
の認識に立って、薄物であっても安定した出力を得るに
はその機械的強度を向上させ、特定の数値範囲内に設定
すべきことを突き止め、本発明に到達したものである。The present inventor recognizes that the difference in the output characteristics described above depends on the thickness of the non-magnetic support used for the medium, and obtains stable output even with a thin material. The present invention has reached the present invention by improving its mechanical strength and finding out that it should be set within a specific numerical range.
【0016】即ち、非磁性支持体の縦方向強度(長手方
向での強度)を上記した特定範囲に設定し、かつ、横方
向強度(幅方向での強度)との比も上記した特定範囲に
設定してはじめて、目的とする効果を得ることができる
のである。That is, the strength in the longitudinal direction (strength in the longitudinal direction) of the non-magnetic support is set to the above-mentioned specific range, and the ratio to the strength in the lateral direction (strength in the width direction) is also set to the above-specified range. Only after setting the desired effect can the desired effect be obtained.
【0017】縦方向強度、及び横方向強度との比につい
ては、破断強度、ヤング率、5%伸び荷重が上記した下
限値を下廻ると、非磁性支持体が薄物であるために、縦
方向の強度が小さくなりすぎて、磁気ヘッドに対する接
触が不良になってしまう。また、上記した上限値を超え
ると、却って実用的でない。As for the ratio of the strength in the longitudinal direction and the strength in the lateral direction, when the breaking strength, Young's modulus and 5% elongation load are below the lower limits mentioned above, the non-magnetic support is thin, and therefore the longitudinal direction. Becomes too small, resulting in poor contact with the magnetic head. On the other hand, if it exceeds the above-mentioned upper limit value, it is rather not practical.
【0018】非磁性支持体の機械的強度を上記した範囲
に設定するには、例えば、非磁性支持体を成形した後
に、その縦方向及び横方向に延伸する際の延伸率をコン
トロールすればよい。In order to set the mechanical strength of the non-magnetic support within the above range, for example, after the non-magnetic support is molded, the stretching ratio at the time of stretching in the machine direction and the transverse direction may be controlled. .
【0019】本発明の磁気記録媒体において使用可能な
非磁性支持体としては、ポリエチレンテレフタレート、
ポリエチレンナフタレート等のポリエステル類、ポリイ
ミド、ポリアミドイミド、ポリアラミド等が挙げられ
る。As the non-magnetic support usable in the magnetic recording medium of the present invention, polyethylene terephthalate,
Examples thereof include polyesters such as polyethylene naphthalate, polyimide, polyamide imide, and polyaramid.
【0020】上記非磁性支持体上に設けられる磁性層
は、磁性粉末と結合剤とを主体とする磁性塗料を非磁性
支持体表面に塗布することにより形成される磁性塗膜で
あるのが望ましい。The magnetic layer provided on the non-magnetic support is preferably a magnetic coating film formed by applying a magnetic paint mainly containing magnetic powder and a binder to the surface of the non-magnetic support. .
【0021】磁性層を磁性塗膜とする場合、磁性粉末、
結合剤等は従来公知のものがいずれも使用可能で、何等
限定されるものではない。When the magnetic layer is a magnetic coating film, magnetic powder,
Any conventionally known binder can be used as the binder, and the binder is not limited in any way.
【0022】磁性粉末としては、γ−Fe2O3 、コバルト
被着γ−Fe2O3 等の強磁性酸化鉄系粒子、強磁性二酸化
クロム系粒子、Fe、Co、Ni等の金属やこれらを含んだ合
金からなる強磁性金属系粒子、六角板状の六方晶系フェ
ライト微粒子等が例示される。As the magnetic powder, γ-Fe 2 O 3 , ferromagnetic iron oxide type particles such as γ-Fe 2 O 3 coated with cobalt, ferromagnetic chromium dioxide type particles, metals such as Fe, Co, Ni and the like are used. Examples thereof include ferromagnetic metal-based particles made of an alloy containing, hexagonal plate-shaped hexagonal ferrite fine particles, and the like.
【0023】結合剤としては、塩化ビニル、酢酸ビニ
ル、ビニルアルコール、塩化ビニリデン、アクリル酸エ
ステル、メタクリル酸エステル、スチレン、ブタジエ
ン、アクリロニトリル等の重合体、あるいはこれらの二
種以上を組み合わせた共重合体、ポリウレタン樹脂、ポ
リエステル樹脂、エポキシ樹脂等が例示される。これら
の結合剤には、磁性粉末の分散性を改善するために、ス
ルホン酸基やカルボキシル基、リン酸基等の親水性基が
導入されてもよい。As the binder, a polymer of vinyl chloride, vinyl acetate, vinyl alcohol, vinylidene chloride, acrylic acid ester, methacrylic acid ester, styrene, butadiene, acrylonitrile, or the like, or a copolymer of two or more kinds thereof is combined. , Polyurethane resin, polyester resin, epoxy resin and the like. A hydrophilic group such as a sulfonic acid group, a carboxyl group, or a phosphoric acid group may be introduced into these binders in order to improve the dispersibility of the magnetic powder.
【0024】磁性塗膜には、前記磁性粉末、結合剤の
他、添加剤として分散剤、研磨剤、帯電防止剤、防錆剤
等が加えられてもよい。In addition to the above magnetic powder and binder, a dispersant, an abrasive, an antistatic agent, a rust preventive, etc. may be added to the magnetic coating film.
【0025】なお、本発明の磁気記録媒体は、磁性層上
に防錆剤や潤滑剤よりなるトップコート層が設けられた
り、非磁性支持体上の磁性層を形成しなかった方の面に
バックコート層が設けられているものであってもよい。In the magnetic recording medium of the present invention, a topcoat layer made of a rust preventive or a lubricant is provided on the magnetic layer, or the magnetic layer on the non-magnetic support is not formed. A back coat layer may be provided.
【0026】図5は、本発明の磁気記録媒体の一例とし
て(VTR用の磁気テープ)を示すものである。即ち、
非磁性支持体1の一方の面に、磁性粉、結合剤等を含有
した磁性層2を有している。また他方の面に、非磁性粉
末と結合剤とを主体とするバックコート層3を有してい
てもよい。FIG. 5 shows a (VTR magnetic tape) as an example of the magnetic recording medium of the present invention. That is,
A magnetic layer 2 containing magnetic powder, a binder, etc. is provided on one surface of the non-magnetic support 1. Further, the other surface may have a back coat layer 3 mainly composed of a non-magnetic powder and a binder.
【0027】[0027]
【実施例】以下、本発明を具体的な実施例により説明す
るが、本発明は以下の実施例に限定されるものでない。EXAMPLES The present invention will be described below with reference to specific examples, but the present invention is not limited to the following examples.
【0028】下記組成の磁性塗料を調製した。 Co被着γ−Fe2O3 100重量部 N−3127(ポリウレタン) 13重量部(固形量) VAGH(塩ビ系共重合体) 9重量部(固形量) Al2O3 20重量部 カーボンブラック 4重量部 ブチルステアレート 1重量部 ミリスチン酸 1重量部 メチルエチルケトン 110重量部 シロクヘキサノン 110重量部A magnetic paint having the following composition was prepared. Co deposited γ-Fe 2 O 3 100 parts by weight N-3127 (polyurethane) 13 parts by weight (solid amount) VAGH (vinyl chloride copolymer) 9 parts by weight (solid amount) Al 2 O 3 20 parts by weight carbon black 4 Parts by weight Butyl stearate 1 part by weight Myristic acid 1 part by weight Methyl ethyl ketone 110 parts by weight Sirochexanone 110 parts by weight
【0029】即ち、以上の材料をボールミルポットに仕
込み、約48時間混合した後、これを濾過、脱泡し、ポリ
イソシアネート硬化剤7重量部を添加、約30分攪拌し、
磁性塗料を作成した。これを下記の表−2、表−3の比
較例、実施例に示す特性を持ったPETベースフィルム
に塗布厚 1.5μmとなるようにドクターブレード法によ
り塗布し、約80℃で乾燥後、表面処理を行い、60℃の恒
温槽で約20時間硬化し、所定幅にスリッティングし、検
討用サンプルテープを作成した。That is, the above materials were placed in a ball mill pot, mixed for about 48 hours, filtered and defoamed, added with 7 parts by weight of a polyisocyanate curing agent, stirred for about 30 minutes,
Magnetic paint was created. This was applied to a PET base film having the characteristics shown in Tables 2 and 3 below by a doctor blade method so that the coating thickness would be 1.5 μm, and dried at about 80 ° C. The sample tape was treated, cured in a constant temperature bath at 60 ° C. for about 20 hours, and slitted to a predetermined width to prepare a sample tape for study.
【0030】なお、各例において、使用したベースフィ
ルムの機械的物性値は、その成形時の延伸率を長手又は
幅方向でコントロールすることにより制御した。また、
そのヤング率は引張試験により求め、5%伸び荷重はフ
ィルムを引張って5%伸ばしたときの荷重を測定する
等、各機械的物性値は公知の測定方法で求めた。ベース
フィルムの厚みは、その成形厚により調整した。In each example, the mechanical properties of the base film used were controlled by controlling the stretching ratio during molding in the longitudinal or width direction. Also,
The Young's modulus was determined by a tensile test, and the 5% elongation load was determined by a known measurement method such as measuring the load when the film was stretched and stretched by 5%. The thickness of the base film was adjusted by its molding thickness.
【0031】 [0031]
【0032】 [0032]
【0033】 [0033]
【0034】以上のようにしてサンプルを作成し、これ
らのサンプルで検討を行った。比較例1は従来の厚物媒
体であり、比較例2、3、実施例1はベースフィルム厚
5〜7μm(例えば7μm)の薄物媒体である。また、
比較例2、3、実施例1は、縦方向強度と縦/横強度バ
ランスを任意に変えてあり、その違いにより出力特性が
どのように変わるか、従来の厚物媒体に比べどうである
かを検討した。比較例4、5、実施例2は、ベースフィ
ルム厚7〜9μm(例えば9μm)の媒体である。Samples were prepared as described above, and examinations were conducted on these samples. Comparative Example 1 is a conventional thick medium, and Comparative Examples 2 and 3 and Example 1 are thin mediums having a base film thickness of 5 to 7 μm (for example, 7 μm). Also,
In Comparative Examples 2 and 3 and Example 1, the longitudinal strength and the longitudinal / horizontal strength balance are arbitrarily changed, and how the output characteristics are changed due to the difference and how compared with the conventional thick medium. It was investigated. Comparative Examples 4 and 5 and Example 2 are media having a base film thickness of 7 to 9 μm (for example, 9 μm).
【0035】出力特性は次のようにして出力波形から評
価した。 出力波形:固定ヘッドを使用した磁気記録媒体記録再生
機を使用し、各サンプルテープをそれぞれ記録再生し、
その時の出力波形をオシロスコープで観察した。各出力
波形は図1、図2に示した。 出力レベル:図1中に示したように、各サンプルにおい
て完全に当たりが取れている状態を 100%とし、これを
基準に、当たり不良による出力の落ち込み部をXとした
とき、これが基準に対して何%の出力であるかを算出し
た。結果は図3、図4にそれぞれ示した。なお、図3、
図4に示した傾向は、他のパラメータにおいても同様で
ある。The output characteristics were evaluated from the output waveform as follows. Output waveform: Using a magnetic recording medium recording / reproducing device with a fixed head, recording / reproducing each sample tape,
The output waveform at that time was observed with an oscilloscope. Each output waveform is shown in FIGS. Output level: As shown in Fig. 1, the state where each sample is completely hit is 100%, and when the output drop due to a hit is X, this is relative to the reference. The percentage of output was calculated. The results are shown in FIGS. 3 and 4, respectively. Note that FIG.
The tendency shown in FIG. 4 is the same for other parameters.
【0036】図1及び図3の結果から、次のことが明ら
かである。 (1) 比較例1は非常に安定していることがわかる。これ
に対して、一般的に使用されている薄物ベースフィルム
を使用した比較例2、3は比較例1に比べ不安定であ
り、これはベースフィルムの厚み違いによるヘッドと媒
体の接触状態の変化によるものである。From the results shown in FIGS. 1 and 3, the following is clear. (1) It can be seen that Comparative Example 1 is very stable. On the other hand, Comparative Examples 2 and 3 using a commonly used thin base film are more unstable than Comparative Example 1, because the change in the contact state between the head and the medium due to the difference in the thickness of the base film. It is due to.
【0037】(2) これに比べて実施例1は比較例2、3
と同じ厚みにもかかわらず、安定した出力波形が得ら
れ、比較例1の厚物媒体と比較しても同等の出力波形で
るあことがわかる。比較例2、3、実施例1の違いは、
ベースフィルムの物性のみであり、実施例1に使用した
ベースフィルムの物性が有効であることがわかる。(2) In comparison with this, Example 1 is Comparative Examples 2 and 3
It can be seen that a stable output waveform is obtained despite the same thickness as, and the output waveform is equivalent to that of the thick medium of Comparative Example 1. Differences between Comparative Examples 2 and 3 and Example 1 are:
It can be seen that the physical properties of the base film used in Example 1 are effective only in the physical properties of the base film.
【0038】(3) また、比較例2、3、実施例1は縦/
横の強度バランスが次のような関係になっている。 これに対し、それぞれの出力波形は、 出力波形・・・良い=実施例1>比較例3>比較例2=
悪い の関係にあり、破断伸度の縦/横強度バランスは弱い
程、その他の縦/横強度バランスは強い程、出力波形は
良い傾向になる。(3) Further, Comparative Examples 2 and 3 and Example 1 are vertical /
The horizontal strength balance has the following relationship. On the other hand, the respective output waveforms are good as the output waveforms = good example 1> comparative example 3> comparative example 2 =
There is a bad relationship, and the weaker the longitudinal / lateral strength balance of elongation at break, and the stronger the other longitudinal / lateral strength balance, the better the output waveform.
【0039】(4) また、この縦/横強度バランスがそれ
ぞれのパラメーターで下記の条件になったとき、薄物媒
体は厚物媒体と同等の出力波形が得られることが明らか
になった。 (4) Further, it has been clarified that when the vertical / horizontal strength balance satisfies the following conditions for each parameter, the thin medium can obtain an output waveform equivalent to that of the thick medium.
【0040】更に、図2及び図4の結果からは、次のこ
とが明らかである。 (5) ベースフィルム厚を9μmとしたとき、上記に比べ
て比較的厚いために出力波形が不安定となり易いが、実
施例2のように本発明の条件を満たすことによってかな
り改善されることが分かる。Furthermore, from the results shown in FIGS. 2 and 4, the following is clear. (5) When the thickness of the base film is 9 μm, the output waveform is likely to be unstable because it is relatively thicker than the above, but it can be considerably improved by satisfying the conditions of the present invention as in the second embodiment. I understand.
【0041】(6) 実施例2は比較例4、5と同じ厚みに
もかかわらず、より安定した出力波形が得られ、実施例
2に使用したベースフィルムの物性が、有効であること
が分かる。(6) In Example 2, a more stable output waveform was obtained despite the same thickness as in Comparative Examples 4 and 5, and it can be seen that the physical properties of the base film used in Example 2 are effective. .
【0042】(7) また、比較例4、5、実施例2は縦/
横の強度バランスが次のような関係になっている。 これに対し、それぞれの出力波形は、 出力波形・・・良い=実施例2>比較例5>比較例4=
悪い の関係にあり、縦/横強度バランスは強いほど、出力波
形は良い傾向になる。(7) In addition, Comparative Examples 4 and 5 and Example 2 are vertical /
The horizontal strength balance has the following relationship. On the other hand, the respective output waveforms are output waveforms ... Good = Example 2> Comparative Example 5> Comparative Example 4 =
There is a bad relationship, and the stronger the vertical / horizontal strength balance, the better the output waveform.
【0043】(8) また、この縦/横強度バランスがそれ
ぞれのパラメーターで下記の条件になったとき、薄物媒
体の出力波形が向上することが明らかになった。 (8) Further, it was revealed that the output waveform of the thin medium is improved when the vertical / horizontal strength balance satisfies the following conditions for each parameter.
【0044】以上のことから、本発明の条件を満たした
ベースフィルムに磁性塗料を塗布することにより、記録
媒体の薄物化に起因する出力劣化を小さくでき、薄物化
による磁気ヘッドと媒体の接触状態を改善することがで
きる。これにより、同一システム上での厚物媒体と薄物
媒体の出力特性の互換性が確保でき、さらには磁気記録
媒体の薄物化による記録容量の拡大が可能となる。From the above, by applying the magnetic paint to the base film satisfying the conditions of the present invention, it is possible to reduce the output deterioration due to the thinning of the recording medium, and the contact state between the magnetic head and the medium due to the thinning. Can be improved. As a result, the compatibility of the output characteristics of the thick medium and the thin medium on the same system can be ensured, and the recording capacity can be expanded by making the magnetic recording medium thinner.
【0045】[0045]
【発明の作用効果】本発明は上記した如く、非磁性支持
体の縦方向強度として、破断強度を40〜60Kg/mm2 、ヤ
ング率を 800〜1000Kg/mm2 、5%伸び荷重を15〜30Kg
/mm2とし、かつ、前記非磁性支持体の縦方向強度とそ
の横方向強度との比(縦方向強度/横方向強度)を、破
断強度では 1.8以上、ヤング率では 1.8以上、5%伸び
荷重では 1.8以上としたので、記録媒体の薄物化に起因
する出力劣化を小さくでき、薄物化による磁気ヘッドと
媒体の接触状態を改善することができる。これにより、
同一システム上での厚物媒体と薄物媒体の出力特性の互
換性が確保でき、さらには磁気記録媒体の薄物化による
記録容量の拡大が可能となる。As described above, the present invention has a breaking strength of 40 to 60 kg / mm 2 , a Young's modulus of 800 to 1000 kg / mm 2 , and a 5% elongation load of 15 to 15 as longitudinal strength of the non-magnetic support. 30 kg
/ Mm 2 , and the ratio of the longitudinal strength of the non-magnetic support to its transverse strength (longitudinal strength / lateral strength) is 1.8 or more for breaking strength, 1.8 or more for Young's modulus and 5% elongation. Since the load is 1.8 or more, the output deterioration due to the thinning of the recording medium can be reduced, and the contact state between the magnetic head and the medium due to the thinning can be improved. This allows
The compatibility of the output characteristics of the thick medium and the thin medium on the same system can be ensured, and the recording capacity can be expanded by making the magnetic recording medium thinner.
【図1】サンプル4種について得られた出力波形図であ
る。FIG. 1 is an output waveform diagram obtained for four types of samples.
【図2】他のサンプル3種について得られた出力波形図
である。FIG. 2 is an output waveform chart obtained for three other samples.
【図3】図1の各サンプルについてのベースフィルム強
度の縦/横バランスによる出力レベル変化を示すグラフ
である。FIG. 3 is a graph showing changes in output level according to vertical / horizontal balance of base film strength for each sample of FIG.
【図4】図2の各サンプルについてのベースフィルム強
度の縦/横バランスによる出力レベル変化を示すグラフ
である。FIG. 4 is a graph showing changes in output level according to vertical / horizontal balance of base film strength for each sample of FIG.
【図5】本発明を適用した磁気記録媒体の一構成例を示
す概略断面図である。FIG. 5 is a schematic cross-sectional view showing one structural example of a magnetic recording medium to which the present invention is applied.
【符号の説明】 1・・・非磁性支持体 2・・・磁性層 3・・・バックコート層[Explanation of reference numerals] 1 ... Non-magnetic support 2 ... Magnetic layer 3 ... Back coat layer
Claims (3)
る磁気記録媒体において、 前記非磁性支持体の縦方向強度として、 破断強度が40〜60Kg/mm2 、 ヤング率が 800〜1000Kg/mm2 、 5%伸び荷重が15〜30Kg/mm2であり、かつ、 前記非磁性支持体の縦方向強度とその横方向強度との比
(縦方向強度/横方向強度)が、 破断強度では 1.8以上、 ヤング率では 1.8以上、 5%伸び荷重では 1.8以上であることを特徴とする磁気
記録媒体。1. A magnetic recording medium having a magnetic layer formed on a non-magnetic support, wherein the breaking strength of the non-magnetic support is 40 to 60 kg / mm 2 , and Young's modulus is 800 to 1000 kg. / Mm 2 , 5% elongation load is 15 to 30 kg / mm 2 , and the ratio of the longitudinal strength of the non-magnetic support to its lateral strength (longitudinal strength / lateral strength) is the breaking strength. Is 1.8 or higher, Young's modulus is 1.8 or higher, and 5% elongation load is 1.8 or higher.
40%であり、前記非磁性支持体の縦方向の破断伸度とそ
の横方向の破断伸度との比(縦方向の破断伸度/横方向
の破断伸度)が0.25以下である、請求項1に記載した磁
気記録媒体。2. The breaking elongation in the longitudinal direction of the non-magnetic support is 20 to.
40%, and the ratio of the breaking elongation in the longitudinal direction of the non-magnetic support to the breaking elongation thereof in the lateral direction (longitudinal breaking elongation / lateral breaking elongation) is 0.25 or less. The magnetic recording medium according to item 1.
る、請求項1又は2に記載した磁気記録媒体。3. The magnetic recording medium according to claim 1, wherein the non-magnetic support has a thickness of 5 to 10 μm.