JPH06328498A - Insertion molded item and manufacture thereof - Google Patents
Insertion molded item and manufacture thereofInfo
- Publication number
- JPH06328498A JPH06328498A JP14843993A JP14843993A JPH06328498A JP H06328498 A JPH06328498 A JP H06328498A JP 14843993 A JP14843993 A JP 14843993A JP 14843993 A JP14843993 A JP 14843993A JP H06328498 A JPH06328498 A JP H06328498A
- Authority
- JP
- Japan
- Prior art keywords
- insert
- mold
- insert material
- molded product
- female
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Description
【０００１】[0001]
【産業上の利用分野】この発明は、AV機器のフロントパ
ネルやボタン、自動車の計器パネル、弁当箱、お皿、カ
ップなどに用いられるインサート成形品とその製造方法
に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an insert-molded article used for front panels and buttons of AV equipment, instrument panels of automobiles, lunch boxes, plates, cups and the like, and a method for producing the same.
【０００２】[0002]
【従来の技術】従来、インサート成形品とその製造方法
としては、つぎに挙げるものがある。 （１）特開昭56-126142号公報に記載されたものがあ
る。この方法は、樹脂射出孔を有する凸部と溝部とが形
成された雄型と、凹部が形成された雌型とからなる射出
成形金型の雌型に、プレフォームされたインサート材を
装着し、雄型と雌型とを接合させて型閉めした後、キャ
ビティ内に溶融樹脂を射出し、溶融樹脂を冷却固化後、
成形品表面にインサート材が形成されたインサート成形
品を取り出すようにしたものである。2. Description of the Related Art Conventionally, there are the following insert molding products and their manufacturing methods. (1) There is one described in JP-A-56-126142. In this method, a preformed insert material is mounted on a female die of an injection molding die including a male die having a convex portion having a resin injection hole and a groove portion and a female die having a concave portion. After joining the male mold and the female mold and closing the mold, the molten resin is injected into the cavity, and the molten resin is cooled and solidified.
The insert molded product having the insert material formed on the surface of the molded product is taken out.
【０００３】（２）特開昭54-33561号公報に記載された
ものがある。この方法は、凸部と溝部とが形成された雄
型と、樹脂射出孔を有する凹部が形成された雌型とから
なる射出成形金型の雄型に、プレフォームされたインサ
ート材を装着し、雄型と雌型とを接合させて型閉めした
後、キャビティ内に溶融樹脂を射出し、溶融樹脂を冷却
固化後、成形品表面にインサート材が形成されたインサ
ート成形品を取り出すようにしたものである。(2) There is one described in JP-A-54-33561. In this method, a preformed insert material is attached to a male die of an injection molding die including a male die having a convex portion and a groove portion and a female die having a concave portion having a resin injection hole. After joining the male mold and the female mold and closing the mold, the molten resin was injected into the cavity, the molten resin was cooled and solidified, and the insert molded product with the insert material formed on the surface of the molded product was taken out. It is a thing.
【０００４】[0004]
【発明が解決しようとする課題】しかし、従来の製造方
法では、つぎのような問題点があった。（１）は、プレ
フォームされたインサート材が、雌型の凹部表面と同面
積かあるいは雌型の凹部表面より小面積の大きさである
ため、型閉めしても、インサート材の端縁は、雄型の溝
部まで入り込むことはなかった。However, the conventional manufacturing method has the following problems. In (1), since the preformed insert material has the same area as the female concave surface or a smaller area than the female concave surface, the edge of the insert material remains the same even when the mold is closed. , The male groove did not enter.
【０００５】（２）は、プレフォームされたインサート
材が、雌型の凹部表面と同面積の大きさであるため、型
閉めしても、インサート材の端縁は、雌型の溝部まで入
り込むことはなかった。In (2), since the preformed insert material has the same area as the surface of the concave portion of the female die, even if the die is closed, the edge of the insert material enters the groove portion of the female die. It never happened.
【０００６】したがって、（１）（２）のいずれにおい
ても、型閉めされた雄型と雌型との境界線にできる隙間
に、射出成形時の溶融樹脂が侵入して、成形品の表面に
樹脂バリが発生したり、雄型と雌型とのエッジのズレが
境界線で段差となり、その段差が成形品の表面に現わ
れ、見苦しいインサート成形品となってしまう。また、
成型品の表面の、型閉めされた雄型と雌型との境界線に
相当する部分よりも下まで、インサート材で覆うことが
できず、装飾が中途半端なインサート成形品しか得られ
ないという問題点があった。この発明の目的は、上記の
ような問題点を解決することにあり、樹脂バリや段差の
ない見栄えのよいインサート成形品を提供することを目
的とする。Therefore, in any of (1) and (2), the molten resin at the time of injection molding penetrates into the gap formed at the boundary line between the closed male and female molds, and the surface of the molded product is exposed. Resin burrs are generated, and a difference between the edges of the male mold and the female mold forms a step at the boundary line, and the step appears on the surface of the molded product, resulting in an unsightly insert molded product. Also,
It cannot be covered with the insert material even below the part corresponding to the boundary line between the closed male and female molds on the surface of the molded product, so that only the insert molded product with decoration halfway can be obtained. There was a problem. An object of the present invention is to solve the above problems, and an object of the present invention is to provide an insert-molded article which has no resin burrs and steps and has a good appearance.
【０００７】[0007]
【課題を解決するための手段】この発明のインサート成
形品は、射出成形時に型閉めされた雄型と雌型との境界
線に相当する部分が、インサート材で覆われた構成であ
る。The insert-molded product of the present invention has a structure in which a portion corresponding to a boundary line between a male mold and a female mold that are closed during injection molding is covered with an insert material.
【０００８】この発明のインサート成形品の製造方法
は、樹脂射出孔を有する凸部の周囲に溝部が形成された
雄型と、凹部が形成された雌型とからなる射出成形金型
のいずれか一方の型に、プレフォームされたインサート
材を装着し、雄型と雌型とを型閉めした後、キャビティ
内に溶融樹脂を射出し、溶融樹脂を冷却固化後、成形品
の外表面にインサート材が形成されたインサート成形品
を取り出すインサート成形品の製造方法において、プレ
フォームされたインサート材が、雌型の凹部表面よりも
大面積であって、インサート材の端縁部が雄型の溝部ま
で入り込む大きさであるように構成している。In the method for manufacturing an insert-molded product according to the present invention, any one of an injection molding die including a male mold having a groove formed around a convex portion having a resin injection hole and a female mold having a concave portion is formed. Attach the preformed insert material to one mold, close the male mold and the female mold, inject the molten resin into the cavity, cool and solidify the molten resin, and insert it on the outer surface of the molded product. In the method of manufacturing an insert-molded product in which an insert-molded product in which a material is formed is taken out, the preformed insert material has a larger area than the concave surface of the female die, and the edge of the insert material is a male-shaped groove portion. It is configured so that it can fit in.
【０００９】この発明のインサート成形品の製造方法
は、凸部の周囲に溝部が形成された雄型と、樹脂射出孔
を有する凹部が形成された雌型とからなる射出成形金型
のいずれか一方の型に、プレフォームされたインサート
材を装着し、雄型と雌型とを型閉めした後、キャビティ
内に溶融樹脂を射出し、溶融樹脂を冷却固化後、成形品
の内表面から外表面の一部にかけてインサート材が形成
されたインサート成形品を取り出すインサート成形品の
製造方法において、プレフォームされたインサート材
が、雄型の凸部表面と溝部内面とを合わせた面積よりも
大面積であって、インサート材の端縁部が雌型の凹部ま
で入り込む大きさであるように構成している。The insert-molded article manufacturing method according to the present invention is either an injection molding die comprising a male mold having a groove formed around a convex portion and a female mold having a concave portion having a resin injection hole. Attach the preformed insert material to one mold, close the male mold and the female mold, inject the molten resin into the cavity, cool and solidify the molten resin, and then remove from the inner surface of the molded product. In a method of manufacturing an insert-molded product that takes out an insert-molded product in which the insert material is formed over a part of the surface, the preformed insert material has a larger area than the combined area of the male convex surface and the groove inner surface. In addition, the end edge portion of the insert material is configured to fit into the female recess.
【００１０】[0010]
【作用】この発明では、射出成形金型に装着するプレフ
ォームされたインサート材が、雌型の凹部表面よりも大
面積であって、インサート材の端縁部が雄型の溝部まで
入り込む大きさのものを使用している（図２〜図５参
照）。According to the present invention, the preformed insert material to be mounted on the injection molding die has a larger area than the surface of the concave portion of the female die, and the edge portion of the insert material enters the groove portion of the male die. (See FIGS. 2 to 5).
【００１１】また、この発明では、射出成形金型に装着
するプレフォームされたインサート材が、雄型の凸部表
面と溝部内面とを合わせた面積よりも大面積であって、
インサート材の端縁部が雌型の凹部まで入り込む大きさ
をしている（図８〜図１０参照）。Further, in the present invention, the preformed insert material to be mounted on the injection molding die has a larger area than the combined area of the convex surface of the male mold and the inner surface of the groove,
The edge of the insert material is sized to fit into the female recess (see FIGS. 8 to 10).
【００１２】したがって、型閉めされた雄型と雌型との
境界線にできる隙間は、インサート材で塞がれてしまう
ので、その隙間には溶融樹脂が侵入しない（図４、図１
０参照）。また、雄型と雌型とのエッジのズレは、イン
サート材で覆われてしまう（図４、図１０参照）。ま
た、成型品の表面の、型閉めされた雄型と雌型との境界
線に相当する部分よりも下まで、インサート材が覆って
しまう（図１参照）。Therefore, the gap formed at the boundary between the closed male and female molds is closed by the insert material, so that the molten resin does not enter the gap (see FIGS. 4 and 1).
0). Further, the gap between the edges of the male mold and the female mold is covered with the insert material (see FIGS. 4 and 10). Further, the insert material covers the surface of the molded product even below the portion corresponding to the boundary line between the closed male and female dies (see FIG. 1).
【００１３】[0013]
【実施例】以下、図面を参照しながらこの発明を詳しく
説明する。この発明は、まず、樹脂射出孔１０を有する
凸部１１の周囲に溝部１２が形成された雄型１と、凹部
２０が形成された雌型２とからなる射出成形金型のいず
れか一方の型に、プレフォームされたインサート材３を
装着する。DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS The present invention will be described in detail below with reference to the drawings. In the present invention, first, either one of an injection mold including a male die 1 in which a groove 12 is formed around a convex portion 11 having a resin injection hole 10 and a female die 2 in which a concave portion 20 is formed. The preformed insert material 3 is attached to the mold.
【００１４】雄型１と雌型２とは、型閉めされることに
よって、雄型１の凸部１１と溝部１２と雌型２の凹部２
０とで、たとえば、容器形状の空間（以下、キャビティ
４と呼ぶ。）が形成されるようになっている。雄型１と
雌型２とは、雄型１と雌型２とのエッジがズレないよう
に型閉めされる金型でもよいし（図３参照）、雄型１と
雌型２とのエッジをずらして段差とした金型でもよい
（図１１参照）。The male die 1 and the female die 2 are closed to form a convex portion 11 and a groove portion 12 of the male die 1 and a concave portion 2 of the female die 2.
With 0, for example, a container-shaped space (hereinafter referred to as cavity 4) is formed. The male mold 1 and the female mold 2 may be molds that are closed so that the edges of the male mold 1 and the female mold 2 do not shift (see FIG. 3), or the edges of the male mold 1 and the female mold 2. It is also possible to use a mold in which the steps are shifted to form a step (see FIG. 11).
【００１５】プレフォームされたインサート材３は、雌
型２の凹部２０表面よりも大面積であって、雄型１と雌
型２とが型閉めされたときに、インサート材３の端縁部
３３が雄型１の溝部１２まで入り込む大きさである。プ
レフォームは、真空成形や型押し成形などによって行わ
れる。インサート材３は、その端縁部３３が雄型１の溝
部１２の底部１２０に届く大きさでもよい。インサート
材３は、少なくとも、雄型１と雌型２との境界線５を覆
うものであればよい。The preformed insert material 3 has a larger area than the surface of the recess 20 of the female die 2, and when the male die 1 and the female die 2 are closed, the edge portion of the insert material 3 is closed. The size of 33 is large enough to enter the groove 12 of the male die 1. The preform is performed by vacuum forming, embossing or the like. The insert material 3 may have a size such that the end edge portion 33 thereof reaches the bottom portion 120 of the groove portion 12 of the male die 1. It is sufficient that the insert material 3 covers at least the boundary line 5 between the male die 1 and the female die 2.
【００１６】インサート材３の装着は、真空吸引孔２２
などによって、雄型１あるいは雌型２のいずれに装着し
てもよい（図２、図５参照）。A vacuum suction hole 22 is used to mount the insert material 3.
It may be attached to either the male die 1 or the female die 2 depending on the conditions (see FIGS. 2 and 5).
【００１７】インサート材３は、基体フィルム３０上
に、図柄層３１、接着層３２などが順次形成されたもの
がある（図６参照）。基体フィルム３０は、通常のイン
サート材の基体フィルムとして使用されるものであり、
ポリエチレンテレフタレート、ポリカーボネート、アク
リル、スチレンなどのプラスチックフィルムなどがあ
る。図柄層３１は、成形品表面に、模様、絵画、ロゴ、
文字、記号などを形成するために、印刷などの通常の形
成方法で形成される。図柄層３１は、真空蒸着によって
形成された金属層を有していてもよい。接着層３２は、
成形品６０の成形と同時に成形品表面にインサート材３
を接着させるためのものであり、成形品６０を構成する
樹脂と同系の樹脂を用いて、印刷などの通常の形成方法
で形成される。インサート材３は、アルミニウム、鉄、
ステンレスなどのプレフォームなどの金属箔や金属シー
トでもよい。As the insert material 3, there is one in which a design layer 31, an adhesive layer 32 and the like are sequentially formed on a base film 30 (see FIG. 6). The base film 30 is used as a base film of an ordinary insert material,
Examples include polyethylene terephthalate, polycarbonate, acrylic, styrene, and other plastic films. The pattern layer 31 is a pattern, a painting, a logo,
In order to form characters, symbols, etc., it is formed by an ordinary forming method such as printing. The pattern layer 31 may have a metal layer formed by vacuum vapor deposition. The adhesive layer 32 is
Simultaneously with molding of the molded product 60, the insert material 3 is formed on the surface of the molded product.
And is formed by a normal forming method such as printing using a resin similar to the resin forming the molded product 60. Insert material 3 is aluminum, iron,
A metal foil such as a preform such as stainless steel or a metal sheet may be used.
【００１８】つぎに、雄型１と雌型２とを型閉めした
後、キャビティ４内に溶融樹脂６を射出する（図４参
照）。溶融樹脂６を射出する時の樹脂の熱によって、イ
ンサート材３の接着層３２が溶融し、溶融樹脂６の冷却
固化にともなって接着層３２も冷却固化され成形品表面
に接着する。溶融樹脂６としては、アクリロニトリルス
チレン樹脂や、ポリカーボネート樹脂、ポリスチレン樹
脂、アクリル樹脂、ポリエステル樹脂などがある。Next, after closing the male mold 1 and the female mold 2, the molten resin 6 is injected into the cavity 4 (see FIG. 4). The adhesive layer 32 of the insert material 3 is melted by the heat of the resin when the molten resin 6 is injected, and the adhesive layer 32 is also cooled and solidified as the molten resin 6 is cooled and solidified, and adheres to the surface of the molded product. Examples of the molten resin 6 include acrylonitrile styrene resin, polycarbonate resin, polystyrene resin, acrylic resin, and polyester resin.
【００１９】最後に、溶融樹脂６の冷却固化を待って、
射出成形金型の型開きを行い、立体の成形品６０の外表
面６１にインサート材３が形成されたインサート成形品
を取り出す（図１参照）。得られたインサート成形品
は、型閉めされた雄型１と雌型２との境界線５に相当す
る部分が、インサート材３で覆われたものである（図１
参照）。Finally, waiting for the cooling and solidification of the molten resin 6,
The injection molding die is opened, and the insert-molded product having the insert material 3 formed on the outer surface 61 of the three-dimensional molded product 60 is taken out (see FIG. 1). The obtained insert-molded product has a portion corresponding to the boundary line 5 between the closed male mold 1 and female mold 2 covered with the insert material 3 (FIG. 1).
reference).
【００２０】なお、雄型１と雌型２として、雄型と雌型
とのエッジをずらして段差とした金型を用いた場合で
も、型閉めされた雄型と雌型との境界線にできる隙間に
は、射出成形時の溶融樹脂が侵入せず、成形品の表面に
樹脂バリが発生しないものとなる（図１２参照）。Even when the male mold 1 and the female mold 2 are molds in which the edges of the male mold and the female mold are offset from each other, the boundary line between the male mold and the female mold is closed. The molten resin at the time of injection molding does not enter the gap formed, and resin burrs do not occur on the surface of the molded product (see FIG. 12).
【００２１】この発明では、凸部１１の周囲に溝部１２
が形成された雄型１と、樹脂射出孔２１を有する凹部２
０が形成された雌型とからなる射出成形金型を用いても
よい（図８〜図１０参照）。According to the present invention, the groove 12 is formed around the protrusion 11.
Male mold 1 in which the resin is formed, and recess 2 having resin injection hole 21
You may use the injection mold which consists of the female mold in which 0 was formed (refer FIGS. 8-10).
【００２２】この場合は、まず、射出成形金型のいずれ
か一方の型に、プレフォームされたインサート材３を装
着する（図８参照）。プレフォームされたインサート材
３は、雄型１の凸部１１表面と溝部１２内面とを合わせ
た面積よりも大面積であって、インサート材３の端縁部
３３が雌型２の凹部２０まで入り込む大きさであり、少
なくとも、型閉めされた雄型１と雌型２との境界線５を
覆うものであればよい。In this case, first, the preformed insert material 3 is mounted on either one of the injection molding dies (see FIG. 8). The preformed insert material 3 has a larger area than the total area of the surface of the convex portion 11 of the male die 1 and the inner surface of the groove portion 12, and the end edge portion 33 of the insert material 3 reaches the concave portion 20 of the female die 2. It may be of any size as long as it can enter, and at least covers the boundary line 5 between the closed male mold 1 and female mold 2.
【００２３】以下、雄型１と雌型２とを型閉めした後
（図９参照）、キャビティ４内に溶融樹脂６を射出し
（図１０参照）、溶融樹脂６を冷却固化後、成形品６０
の内表面６２から外表面６１にかけてインサート材３が
形成されたインサート成形品を取り出す。得られたイン
サート成形品は、型閉めされた雄型１と雌型２との境界
線５に相当する部分が、インサート材３で覆われたもの
である（図７参照）。After the male mold 1 and the female mold 2 are closed (see FIG. 9), the molten resin 6 is injected into the cavity 4 (see FIG. 10), the molten resin 6 is cooled and solidified, and then a molded product is obtained. 60
The insert-molded product having the insert material 3 formed thereon is taken out from the inner surface 62 to the outer surface 61. The obtained insert-molded product has a portion corresponding to the boundary line 5 between the closed male mold 1 and female mold 2 covered with the insert material 3 (see FIG. 7).
【００２４】[0024]
【発明の効果】この発明のインサート成形品とその製造
方法は、以上のような構成と作用なので、つぎのような
効果を奏する。射出成形金型の雄型と雌型との境界線に
できる隙間には、溶融樹脂が侵入しないので、成形品の
側部に樹脂バリが発生しない。The insert-molded article and the method for producing the same according to the present invention have the following effects because they have the above-described configurations and operations. Since the molten resin does not enter the gap formed at the boundary between the male mold and the female mold of the injection molding die, resin burrs do not occur on the side portions of the molded product.
【００２５】また、射出成形金型の雄型と雌型との境界
線は、インサート材で覆われているので、インサート材
の厚みにより、雄型と雌型とのエッジのズレに起因して
生じる段差が緩和され、その段差が成形品の側部に現わ
れることはない。また、成型品の表面の、型閉めされた
雄型と雌型との境界線に相当する部分よりも下まで、イ
ンサート材で覆われたインサート成形品が得られる。Further, since the boundary line between the male mold and the female mold of the injection molding die is covered with the insert material, due to the thickness of the insert material, it is caused by the deviation of the edge between the male mold and the female mold. The resulting step is mitigated and the step does not appear on the side of the molded product. In addition, an insert-molded product is obtained in which the surface of the molded product is covered with the insert material to a position below the portion corresponding to the boundary line between the closed male and female molds.
【００２６】したがって、樹脂バリや段差が表面に現わ
れない見栄えのよいインサート成形品が得られる。Therefore, it is possible to obtain a good-looking insert-molded article in which resin burrs and steps are not visible on the surface.
【図１】 この発明のインサート成形品の一実施例を示
す断面図である。FIG. 1 is a sectional view showing an embodiment of an insert-molded product of the present invention.
【図２】 この発明のインサート成形品の製造方法の一
工程を示す断面図である。FIG. 2 is a cross-sectional view showing one step of a method for manufacturing an insert-molded product according to the present invention.
【図３】 この発明のインサート成形品の製造方法の一
工程を示す断面図である。FIG. 3 is a cross-sectional view showing one step of a method for manufacturing an insert-molded product of the present invention.
【図４】 この発明のインサート成形品の製造方法の一
工程を示す断面図である。FIG. 4 is a cross-sectional view showing a step of the method for manufacturing the insert-molded product of the present invention.
【図５】 この発明のインサート成形品の製造方法の一
工程を示す断面図である。FIG. 5 is a cross-sectional view showing one step of a method for manufacturing an insert-molded product of the present invention.
【図６】 この発明のインサート成形品の製造方法で用
いるインサート材の一例を示す断面図である。FIG. 6 is a cross-sectional view showing an example of an insert material used in the method for manufacturing an insert-molded product of the present invention.
【図７】 この発明の別のインサート成形品の一実施例
を示す断面図である。FIG. 7 is a sectional view showing an embodiment of another insert-molded product of the present invention.
【図８】 この発明の別のインサート成形品の製造方法
の一工程を示す断面図である。FIG. 8 is a cross-sectional view showing a step of a method for producing another insert-molded product of the present invention.
【図９】 この発明の別のインサート成形品の製造方法
の一工程を示す断面図である。FIG. 9 is a cross-sectional view showing a step in a method for producing another insert-molded product of the present invention.
【図１０】 この発明の別のインサート成形品の製造方
法の一工程を示す断面図である。FIG. 10 is a cross-sectional view showing a step of a method for producing another insert-molded product of the present invention.
【図１１】 この発明のさらに別のインサート成形品の
製造方法の一工程を示す断面図である。FIG. 11 is a cross-sectional view showing a step of a method for producing an insert-molded article according to still another aspect of the present invention.
【図１２】 この発明のさらに別のインサート成形品の
製造方法の一工程を示す断面図である。FIG. 12 is a cross-sectional view showing a step of a method for producing an insert-molded article according to still another aspect of the present invention.
１ 雄型 １０ 樹脂射出孔 １１ 凸部 １２ 溝部 １２０ 底部 １３ 真空吸引孔 ２ 雌型 ２０ 凹部 ２１ 樹脂射出孔 ２２ 真空吸引孔 ３ インサート材 ３０ 基体フィルム ３１ 絵柄層 ３２ 接着層 ３３ 端縁部 ４ キャビティ ５ 境界線 ６ 溶融樹脂 ６０ 成形品 ６１ 外表面 ６２ 内表面 DESCRIPTION OF SYMBOLS 1 Male type 10 Resin injection hole 11 Convex part 12 Groove part 120 Bottom part 13 Vacuum suction hole 2 Female type 20 Recessed part 21 Resin injection hole 22 Vacuum suction hole 3 Insert material 30 Base film 31 Picture layer 32 Adhesive layer 33 Edge part 4 Cavity 5 Boundary line 6 Molten resin 60 Molded product 61 Outer surface 62 Inner surface
Claims (3)
の境界線に相当する部分が、インサート材で覆われてい
ることを特徴とするインサート成形品。1. An insert-molded product, characterized in that a portion corresponding to a boundary line between a male mold and a female mold that are closed during injection molding is covered with an insert material.
形成された雄型と、凹部が形成された雌型とからなる射
出成形金型のいずれか一方の型に、プレフォームされた
インサート材を装着し、雄型と雌型とを型閉めした後、
キャビティ内に溶融樹脂を射出し、溶融樹脂を冷却固化
後、成形品の外表面にインサート材が形成されたインサ
ート成形品を取り出すインサート成形品の製造方法にお
いて、プレフォームされたインサート材が、雌型の凹部
表面よりも大面積であって、インサート材の端縁部が雄
型の溝部まで入り込む大きさであることを特徴とするイ
ンサート成形品の製造方法。2. An injection molding die comprising a male mold having a groove formed around a convex portion having a resin injection hole and a female mold having a concave portion, which has been preformed. After mounting the insert material and closing the male and female molds,
In the method of manufacturing an insert-molded product, in which the molten resin is injected into the cavity, the molten resin is cooled and solidified, and then the insert-molded product having the insert material formed on the outer surface of the molded product is taken out, the preformed insert material is A method for manufacturing an insert-molded product, which has a larger area than the surface of the concave portion of the mold and has a size such that the edge portion of the insert material enters the groove portion of the male mold.
樹脂射出孔を有する凹部が形成された雌型とからなる射
出成形金型のいずれか一方の型に、プレフォームされた
インサート材を装着し、雄型と雌型とを型閉めした後、
キャビティ内に溶融樹脂を射出し、溶融樹脂を冷却固化
後、成形品の内表面から外表面の一部にかけてインサー
ト材が形成されたインサート成形品を取り出すインサー
ト成形品の製造方法において、プレフォームされたイン
サート材が、雄型の凸部表面と溝部内面とを合わせた面
積よりも大面積であって、インサート材の端縁部が雌型
の凹部まで入り込む大きさであることを特徴とするイン
サート成形品の製造方法。3. A male mold in which a groove is formed around the convex portion,
Either one of the injection molds consisting of the female mold in which the concave portion having the resin injection hole is formed, the preformed insert material is mounted, and after the male mold and the female mold are closed,
Injecting molten resin into the cavity, cooling and solidifying the molten resin, and then taking out the insert molded product with insert material formed from the inner surface to part of the outer surface of the molded product. The insert material is larger in area than the combined area of the male convex surface and the groove inner surface, and the edge of the insert material is sized to fit into the female concave portion. Molded article manufacturing method.