JPH06312572A - Ink jet recording sheet - Google Patents
Ink jet recording sheetInfo
- Publication number
- JPH06312572A JPH06312572A JP5104111A JP10411193A JPH06312572A JP H06312572 A JPH06312572 A JP H06312572A JP 5104111 A JP5104111 A JP 5104111A JP 10411193 A JP10411193 A JP 10411193A JP H06312572 A JPH06312572 A JP H06312572A
- Authority
- JP
- Japan
- Prior art keywords
- recording
- ink
- recording sheet
- ink jet
- jet recording
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
【０００１】[0001]
【産業上の利用分野】本発明は、インクジェット記録シ
ートに関するものであり、更に詳しくは、インクの滲み
ムラがなくインクの吸収性に優れ、記録された画像の濃
度や鮮明性が高く、真円に近い記録ドットが得られる微
塗工タイプのインクジェット記録シートに関するもので
ある。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink jet recording sheet, and more specifically, it has excellent ink absorbency without uneven bleeding of ink, high density and sharpness of recorded image, and a perfect circle. The present invention relates to a slightly coated ink jet recording sheet that can obtain recording dots close to the above.
【０００２】インクジェット記録方式は、種々の作動原
理によりインクの微小液滴を飛翔させて紙等の記録シー
トに付着させ、画像、文字等の記録を行なうものである
が、高速、低騒音、多色化が容易、記録パターンの融通
性が大きい、現像−定着が不要等の特徴があり、漢字を
含め各種図形及びカラー画像等の記録装置として種々の
用途において急速に普及している。更に、多色インクジ
ェット方式により形成される画像は、製版方式による多
色印刷やカラー写真方式による印画に比較して、遜色の
ない記録を得ることが可能である。又、作成部数が少な
くて済む用途においては、写真技術によるよりも安価で
あることからフルカラー画像記録分野にまで広く応用さ
れつつある。The ink jet recording system is a system in which minute droplets of ink are ejected and adhered to a recording sheet such as paper by various operating principles to record images, characters, etc. It has features such as easy colorization, great flexibility in recording patterns, and no need for development-fixing, and is rapidly spreading in various applications as a recording device for various figures including Kanji and color images. Further, an image formed by a multicolor ink jet system can obtain a recording comparable to that of multicolor printing by a plate making system or printing by a color photographic system. Further, in applications requiring a small number of copies, it is being widely applied to the field of full-color image recording because it is cheaper than the photographic technique.
【０００３】このインクジェット記録方式で使用される
記録シートとしては、通常の印刷や筆記に使われる上質
紙やコーテッド紙を使うべく、装置やインク組成の面か
ら努力がなされてきた。しかし、装置の高速化・高精細
化或はフルカラー化等インクジェット記録装置の性能の
向上や用途の拡大に伴い、記録シートに対してもより高
度な特性が要求されるようになった。即ち、当該記録シ
ートとしては、印字ドットの濃度が高く、色調が明るく
鮮やかであること、インクの吸収が早くて印字ドットが
重なった場合においてもインクが流れ出したり滲んだり
しないこと、印字ドットの横方向への拡散が必要以上に
大きくなく、且つ周辺が滑らかでぼやけないこと等が要
求される。As a recording sheet used in this ink jet recording system, efforts have been made from the aspect of the apparatus and ink composition so as to use high-quality paper or coated paper used for ordinary printing and writing. However, as the performance of the inkjet recording apparatus has been improved and the applications have been expanded, such as speeding up, high definition, or full-color of the apparatus, more advanced characteristics have been required for the recording sheet. That is, as the recording sheet, the density of print dots is high, the color tone is bright and vivid, the ink does not run or bleed even when the print dots overlap and the print dots overlap. It is required that the diffusion in the direction is not unnecessarily large and that the periphery is smooth and not blurred.
【０００４】インクジェット記録シートの形態として
は、所謂、上質紙・ボンド紙等に代表される普通紙タイ
プと上質紙等の紙、合成紙、合成樹脂フィルム等の支持
体面上にインク受理層を設けた塗工タイプに大別され
る。As the form of the ink jet recording sheet, an ink receiving layer is provided on a support surface such as plain paper type represented by so-called high-quality paper / bonded paper, paper such as high-quality paper, synthetic paper, synthetic resin film and the like. It is roughly divided into coating type.
【０００５】塗工タイプには、１〜１０／ｍ2程度の低
塗工タイプ、１０〜２０ｇ／ｍ2程度の中塗工タイプ、
２０ｇ／ｍ2以上の高塗工タイプの各インクジェット記
録シートがある。特に、近年に至っては、低塗工タイプ
でも下限の塗工量０．５〜５ｇ／ｍ2の微塗工タイプが
普通紙に近いものとなり、外観的にも、取扱いとしても
好ましく、この微塗工タイプが望まれてきている。しか
し、カラー記録の場合は、イエロー、マゼンタ、シア
ン、ブラックの単色記録だけでなく、これらの色を重ね
て重色記録され、インク付着量が極めて多くなるため、
微塗工タイプの場合は、塗工層でインクが吸収しきれな
くなることから、比較的低サイズ度の原紙を使用して、
支持体の原紙自体で付着インクの一部を吸収させる必要
がでてきている。The coating type includes a low coating type of about 1 to 10 / m 2, a medium coating type of about 10 to 20 g / m 2 ,
There are high coating type inkjet recording sheets of 20 g / m 2 or more. In particular, in recent years, even a low coating type, a lower coating amount of 0.5 to 5 g / m 2 of a fine coating type is close to that of plain paper, which is preferable in terms of appearance and handling. The coating type has been desired. However, in the case of color recording, not only single color recording of yellow, magenta, cyan, and black but also superposition of these colors is performed for multi-color recording, and the amount of ink adhered is extremely large.
In the case of the light coating type, the ink cannot be completely absorbed in the coating layer, so use a base paper of a relatively low size,
It has become necessary to absorb a part of the attached ink by the base paper itself of the support.
【０００６】これらの問題を解決するために、特公平３
−２６６６５号公報には、坪量６０ｇ／ｍ2基準のステ
キヒトサイズ度が４秒以下の基紙上に、微粒シリカと水
溶性高分子バインダーとを含む塗工層を設けたインクジ
ェット記録用紙の例が開示され、特開昭５９−３８０８
７公報には、サイズ度が０〜１０秒である基材上に、イ
ンク吸収層を設けたインクジェット記録材の例が開示さ
れ、特開昭５９−９５１６号公報には、ステキヒトサイ
ズ度０〜５秒の原紙にポリビニルピロリドン等を含浸し
たインクジェット記録用紙の例が開示されている。To solve these problems, Japanese Patent Publication No.
JP-A-26665 discloses an example of an ink jet recording paper in which a coating layer containing fine silica particles and a water-soluble polymer binder is provided on a base paper having a basis weight of 60 g / m 2 and a Steckigt sizing degree of 4 seconds or less. Japanese Patent Laid-Open No. 59-3808.
JP-A-59-9516 discloses an example of an ink jet recording material in which an ink absorbing layer is provided on a substrate having a sizing degree of 0 to 10 seconds. JP-A-59-9516 discloses a Steckigt sizing degree of 0. An example of an inkjet recording paper in which polyvinyl pyrrolidone or the like is impregnated into a base paper for 5 seconds is disclosed.
【０００７】更に、インク吸収性が高く、良好な記録ド
ット形状が得られるインクジェット記録シートとして、
特開昭６０−６３１９１号公報がある。同公報は、被記
録材（インクジェット記録シート）の表層が充填材と繊
維質材料とが混在してなることを特徴としている。ここ
では、繊維質材料からなる基材と、該基材の表面にごく
薄く散布されたように付着した充填材粒子とを有すると
記載している。しかし、該公報では表層の充填材と繊維
質材料が混在している状態であって、基材を形成する繊
維質材料が表層で露呈している状態について触れていな
い。Further, as an ink jet recording sheet having high ink absorbency and capable of obtaining a good recording dot shape,
There is JP-A-60-63191. The publication is characterized in that the recording material (inkjet recording sheet) has a surface layer in which a filler and a fibrous material are mixed. Here, it is described that it has a base material made of a fibrous material and filler particles attached to the surface of the base material so as to be dispersed very thinly. However, in this publication, there is no mention of the state in which the surface layer filler and the fibrous material are mixed, and the fibrous material forming the base material is exposed in the surface layer.
【０００８】[0008]
【発明が解決しようとする課題】上述したとおり、イン
ク受理層が低塗工量の場合、比較的低サイズ度の原紙を
使用して支持体自体で付着インクの一部を吸収させてい
る。特に、支持体上に塗工されたインク受理層は、その
表面において、パルプ繊維の絡み合った凹凸に均一に塗
工されないためにパルプ繊維の露呈が甚だしい状態にあ
る。このため、付着インクは、インク受理層表面で所望
の形状の記録ドットを形成することなく、露呈したパル
プ繊維に沿って支持体、即ち原紙内部に浸透していき、
記録ドットが滲んで広がった形状を呈することになる。
言い替えれば、記録画像の鮮明性に欠けたものとなるの
である。As described above, when the ink receiving layer has a low coating amount, a base material having a relatively low size is used to absorb a part of the adhered ink by the support itself. In particular, since the ink receiving layer coated on the support is not uniformly coated on the concavo-convex pattern of pulp fibers on its surface, the exposure of pulp fibers is significant. Therefore, the adhered ink penetrates into the support, that is, the base paper inside along the exposed pulp fibers without forming recording dots having a desired shape on the surface of the ink receiving layer,
The recording dots have a blurred and spread shape.
In other words, the recorded image lacks sharpness.
【０００９】本発明の目的は、インクジェット記録シー
トでも、微塗工タイプのインクジェット記録シートであ
り、インクの滲みムラがなくインク吸収性に優れ、記録
された画像の濃度や鮮明性が高く、真円に近い記録ドッ
トが得られるインクジェット記録シートを得ることを目
的とするものである。An object of the present invention is to provide an ink jet recording sheet of a slightly coated type even with an ink jet recording sheet, which has excellent ink absorbency without uneven bleeding of ink, high density and sharpness of a recorded image, and The purpose of the present invention is to obtain an inkjet recording sheet from which recording dots close to a circle can be obtained.
【００１０】[0010]
【課題を解決するための手段】本発明者らは、上記に鑑
み鋭意研究した結果、インクの滲みがなくインク吸収性
に優れ、記録された画像の濃度が高く、真円に近い記録
ドットが得られるインクジェット記録シートを発明する
に至った。即ち、本発明のインクジェット記録シート
は、インクジェット記録シートにおいて、該記録シート
の記録面が、原紙面の交絡状態にあるパルプ繊維表面に
沿って超微粒子無機顔料を主体とする組成物で表面被覆
された該記録面で、該記録面に被覆されたパルプ繊維形
状を走査電子顕微鏡により視認することができ、且つ該
記録面のパルプ繊維の表面被覆率が７０％以上であるこ
とを特徴とするものである。Means for Solving the Problems As a result of intensive studies in view of the above, the present inventors have found that there is no ink bleeding, the ink absorbency is excellent, the density of a recorded image is high, and a recording dot close to a perfect circle is formed. The inventors have invented the resulting inkjet recording sheet. That is, the inkjet recording sheet of the present invention, in the inkjet recording sheet, the recording surface of the recording sheet is surface-coated with a composition mainly composed of ultrafine inorganic pigments along the pulp fiber surface in the entangled state of the base paper surface. Further, on the recording surface, the shape of the pulp fiber coated on the recording surface can be visually confirmed by a scanning electron microscope, and the surface coverage of the pulp fiber on the recording surface is 70% or more. Is.
【００１１】以下、本発明のインクジェット記録シート
について、詳細に説明する。本発明のインクジェット記
録シートは、支持体、即ち原紙面上にある記録面のパル
プ繊維の形状が十分に識別できる程度に表面被覆された
ものである。記録面の表面被覆は、パルプ繊維の表面に
沿って均一に超微粒子無機顔料で覆われており、パルプ
繊維表面の形状通りに薄く覆っている。記録面の表面被
覆率は、記録面のパルプ繊維表面を７０％以上覆ってい
るものであり、これにより本発明の目的とする特性を十
分に発揮することができる。好ましくは、８０％以上、
更に好ましくは、９０％以上である。その理由として、
記録面が均一に表面被覆されている場合、インクジェッ
トプリンターを使用して記録面にインクが与えられたと
き、記録面が均一に表面被覆されているため、インクの
記録面方向の広がりを起こさず、真円に近い記録ドット
を表現することができ、余剰インクが表面被覆面から原
紙の厚さ方向に浸透していくためである。一方、記録面
のパルプ繊維を覆う表面被覆率が、７０％未満では、イ
ンクが記録面方向に広がる比率が多くなり、結果として
記録ドットは、真円からはずれた形状となる。更に、原
紙への浸透も不規則となり、インクの滲みが現れる。The ink jet recording sheet of the present invention will be described in detail below. The ink jet recording sheet of the present invention is surface-coated so that the shape of pulp fibers on the support, that is, the recording surface on the raw paper surface can be sufficiently identified. The surface coating of the recording surface is uniformly covered with the ultrafine inorganic pigment along the surface of the pulp fiber, and is thinly covered according to the shape of the surface of the pulp fiber. The surface coverage of the recording surface is such that the pulp fiber surface of the recording surface is covered by 70% or more, so that the characteristics targeted by the present invention can be sufficiently exhibited. Preferably, 80% or more,
More preferably, it is 90% or more. The reason is
When the recording surface is uniformly coated, when the ink is applied to the recording surface using an inkjet printer, the recording surface is uniformly coated, so that the ink does not spread in the recording surface direction. This is because it is possible to represent a recording dot close to a perfect circle, and surplus ink permeates from the surface coating surface in the thickness direction of the base paper. On the other hand, if the surface coverage of the recording surface covering the pulp fibers is less than 70%, the rate at which the ink spreads in the recording surface direction increases, and as a result, the recording dots have a shape deviated from a perfect circle. Further, the penetration into the base paper becomes irregular, and ink bleeding appears.
【００１２】本発明のインクジェット記録シートにおい
て、表面被覆された面は、原紙面のパルプ繊維に沿って
均一に覆った面であり、超微粒子無機顔料を主体とする
組成物を使用して被覆する。原紙を形成するパルプ繊維
の繊維径が数１０μｍのオーダーに対して、超微粒子無
機顔料の一次粒子径は、１００ｎｍ以下、好ましくは５
０ｎｍ以下である。粒子径が微小であればあるほど、パ
ルプ繊維への表面被覆が均一となり好ましい。これら超
微粒子無機顔料は、通常水中に一次粒子径を維持した状
態でコロイド状に分散しているものを使用する。In the ink jet recording sheet of the present invention, the surface coated surface is the surface uniformly covered along the pulp fiber of the base paper surface, and is coated using a composition mainly composed of ultrafine particle inorganic pigment. . The primary particle diameter of the ultrafine inorganic pigment is 100 nm or less, preferably 5 with respect to the fiber diameter of the pulp fiber forming the base paper of the order of several tens of μm.
It is 0 nm or less. The finer the particle size, the more uniform the surface coating on the pulp fiber, which is preferable. As these ultrafine particle inorganic pigments, those which are dispersed in water in a colloidal state while maintaining the primary particle size are used.
【００１３】本発明のインクジェット記録シートにおい
て、記録面のパルプ繊維表面の表面被覆について、その
表面被覆率を測定する手段としては、走査電子顕微鏡を
用いることができ、これより画像解析して面積率を算出
する。In the ink jet recording sheet of the present invention, a scanning electron microscope can be used as a means for measuring the surface coverage of the pulp fiber surface of the recording surface. To calculate.
【００１４】超微粒子無機顔料としては、以下のものを
例示することができる。例えば、シリカ（コロイダルシ
リカ）、アルミナ或はアルミナ水和物（アルミナゾル、
コロイダルアルミナ、カチオン性アルミニウム酸化物又
はその水和物、疑ベーマイト等）、表面処理カチオン性
コロイダルシリカ、珪酸アルミニウム、珪酸マグネシウ
ム、炭酸マグネシウム等が挙げられ、一次粒子が多孔性
であれば、なお好ましいが、非多孔性であっても塗工液
調製時に凝集したり、塗工乾燥時に更に凝集し、パルプ
繊維表面に多孔性の表面被覆面が形成されることが好ま
しい。特に、本発明においては、原紙表面のパルプ繊維
１本１本に繊維の幅の数１００分の１以下の平均粒子径
を有する超微粒子無機顔料を用いてパルプ繊維自体を被
覆することが好ましい。The following can be exemplified as the ultrafine particle inorganic pigment. For example, silica (colloidal silica), alumina or alumina hydrate (alumina sol,
Colloidal alumina, cationic aluminum oxides or hydrates thereof, pseudo-boehmite, etc.), surface-treated cationic colloidal silica, aluminum silicate, magnesium silicate, magnesium carbonate and the like, more preferably primary particles are porous. However, it is preferable that even if it is non-porous, it aggregates at the time of preparing the coating liquid or further aggregates at the time of drying the coating to form a porous surface-coated surface on the pulp fiber surface. In particular, in the present invention, it is preferable to coat the pulp fiber itself with an ultrafine particle inorganic pigment having an average particle diameter of several hundredths or less of the width of the fiber for each pulp fiber on the surface of the raw paper.
【００１５】更に、超微粒子無機顔料と併用することの
できる無機顔料は、従来公知の如何なるものも用いるこ
とができる。例えば、軽質炭酸カルシウム、重質炭酸カ
ルシウム、カオリン、タルク、硫酸カルシウム、硫酸バ
リウム、二酸化チタン、酸化亜鉛、硫化亜鉛、炭酸亜
鉛、サチンホワイト、珪酸アルミニウム、ケイソウ土、
珪酸カルシウム、合成非晶質シリカ、水酸化アルミニウ
ム、リトポン、ゼオライト、加水ハロイサイト、水酸化
マグネシウム等を挙げることができる。これら該無機顔
料の中でも、多孔性無機顔料が好ましく、多孔性合成非
晶質シリカ、多孔性炭酸マグネシウム、多孔性アルミナ
等が挙げられ、特に細孔容積の大きい多孔性合成非晶質
シリカが好ましい。又、スチレン系プラスチックピグメ
ント、アクリル系プラスチックピグメント、ポリエチレ
ン、マイクロカプセル、尿素樹脂、メラミン樹脂等の有
機顔料等を上記超微粒子無機顔料と共に併用することも
できる。Further, as the inorganic pigment that can be used in combination with the ultrafine particle inorganic pigment, any conventionally known inorganic pigment can be used. For example, light calcium carbonate, heavy calcium carbonate, kaolin, talc, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide, zinc sulfide, zinc carbonate, satin white, aluminum silicate, diatomaceous earth,
Examples thereof include calcium silicate, synthetic amorphous silica, aluminum hydroxide, lithopone, zeolite, hydrohaloysite, magnesium hydroxide and the like. Among these inorganic pigments, porous inorganic pigments are preferable, and porous synthetic amorphous silica, porous magnesium carbonate, porous alumina and the like can be mentioned, and particularly porous synthetic amorphous silica having a large pore volume is preferable. . Further, organic pigments such as styrene-based plastic pigments, acrylic-based plastic pigments, polyethylene, microcapsules, urea resins and melamine resins can be used together with the above ultrafine inorganic pigments.
【００１６】表面被覆する上で、超微粒子無機顔料と共
に使用されるバインダーとして、例えば、ポリビニルア
ルコール、酢酸ビニル、酸化澱粉、エーテル化澱粉、カ
ルボキシメチルセルロース、ヒドロキシエチルセルロー
ス等のセルロース誘導体、カゼイン、ゼラチン、大豆蛋
白、シリル変性ポリビニルアルコール等；無水マレイン
酸樹脂、スチレン−ブタジエン共重合体、メチルメタク
リレート−ブタジエン共重合体等の共役ジエン系共重合
体ラテックス；アクリル酸エステル及びメタクリル酸エ
ステルの重合体又は共重合体、アクリル酸及びメタクリ
ル酸の重合体又は共重合体等のアクリル系重合体ラテッ
クス；エチレン酢酸ビニル共重合体等のビニル系重合体
ラテックス；或いはこれらの各種重合体のカルボキシル
基等の官能基含有単量体による官能基変性重合体ラテッ
クス；メラミン樹脂、尿素樹脂等の熱硬化合成樹脂系等
の水性バインダー；ポリメチルメタクリレート、ポリウ
レタン樹脂、不飽和ポリエステル樹脂、塩化ビニル−酢
酸ビニルコポリマー、ポリビニルブチラール、アルキッ
ド樹脂等の合成樹脂系バインダーを挙げることができ、
少なくとも１種以上で使用することができる。又、従来
公知の染料を定着する目的として添加するカチオン性樹
脂を併用することもできる。As a binder used together with the ultrafine inorganic pigment for surface coating, for example, polyvinyl alcohol, vinyl acetate, oxidized starch, etherified starch, cellulose derivatives such as carboxymethyl cellulose, hydroxyethyl cellulose, casein, gelatin, soybean. Protein, silyl modified polyvinyl alcohol, etc .; Conjugated diene copolymer latex such as maleic anhydride resin, styrene-butadiene copolymer, methylmethacrylate-butadiene copolymer; polymer or copolymer of acrylic acid ester and methacrylic acid ester Acrylic polymer latex such as polymer, copolymer or copolymer of acrylic acid and methacrylic acid; vinyl polymer latex such as ethylene vinyl acetate copolymer; or functional group such as carboxyl group of these various polymers Polymer latex modified by functional group; water-based binder such as thermosetting synthetic resin such as melamine resin, urea resin; polymethylmethacrylate, polyurethane resin, unsaturated polyester resin, vinyl chloride-vinyl acetate copolymer, polyvinyl butyral, alkyd There may be mentioned synthetic resin binders such as resins,
At least one kind can be used. Also, a cationic resin added for the purpose of fixing a conventionally known dye can be used together.
【００１７】バインダーの総量は、目的とするインクジ
ェット記録シートの特性に合わせて、適宜調整すること
が出来るが、一般には、顔料１００重量％に対して、５
〜６０重量％である。更に、その他の添加剤として、顔
料分散剤、増粘剤、流動性改良剤、消泡剤、抑泡剤、離
型剤、発泡剤、浸透剤、着色染料、着色顔料、蛍光増白
剤、紫外線吸収剤、酸化防止剤、防腐剤、防バイ剤、耐
水化剤、湿潤紙力増強剤、乾燥紙力増強剤等を適宜配合
することもできる。The total amount of the binder can be appropriately adjusted according to the characteristics of the intended ink jet recording sheet, but in general, it is 5 per 100% by weight of the pigment.
-60% by weight. Furthermore, as other additives, a pigment dispersant, a thickener, a fluidity improver, a defoaming agent, a foam suppressor, a release agent, a foaming agent, a penetrant, a coloring dye, a coloring pigment, a fluorescent whitening agent, An ultraviolet absorber, an antioxidant, an antiseptic agent, an antifungal agent, a water resistance agent, a wet paper strength enhancer, a dry paper strength enhancer and the like can be appropriately blended.
【００１８】本発明において、表面被覆する方法は、塗
工或は含浸の方法があるが、表面被覆面の被覆量につい
ては、特に限定するものではない。通常、普通紙ライク
を指向する場合には、０．５〜５ｇ／ｍ2が好ましい
が、これ以上被覆してもよい。In the present invention, the method of coating the surface may be a coating or impregnation method, but the coating amount on the surface coated surface is not particularly limited. Usually, in the case of directing to a plain paper like, 0.5 to 5 g / m 2 is preferable, but more may be coated.
【００１９】本発明に係る原紙とは、ＬＢＫＰ、ＮＢＫ
Ｐ等の化学パルプ、ＧＰ、ＰＧＷＲＭＰ、ＴＭＰ、ＣＴ
ＭＰ、ＣＭＰ、ＣＧＰ等の機械パルプ、ＤＩＰ等の古紙
パルプ、等の木材パルプと従来公知の顔料を主成分とし
て、バインダー及びサイズ剤や定着剤、歩留まり向上
剤、カチオン化剤、紙力増強剤等の各種添加剤を１種以
上用いて混合し、長網抄紙機、円網抄紙機、ツインワイ
ヤ抄紙機等の各種装置で製造された原紙、更に、原紙
に、澱粉、ポリビニルアルコール等でのサイズプレスを
した原紙も含まれる。このような原紙に、そのまま表面
被覆しても良いし、平坦化をコントロールする目的で、
マシンカレンダー、ＴＧカレンダー、ソフトカレンダー
等のカレンダー装置を使用しても良い。The base paper according to the present invention means LBKP, NBK
Chemical pulp such as P, GP, PGWRMP, TMP, CT
Mechanical pulp such as MP, CMP and CGP, wood pulp such as waste paper pulp such as DIP, and conventionally known pigments as main components, and binder and sizing agent, fixing agent, yield improving agent, cationizing agent, paper strengthening agent A mixture of at least one kind of various additives such as, for example, a base paper manufactured by various devices such as a Fourdrinier paper machine, a cylinder paper machine, and a twin wire paper machine, and further, a base paper with starch, polyvinyl alcohol, etc. Includes size-pressed base paper. Such base paper may be surface-coated as it is, or for the purpose of controlling flattening,
A calendar device such as a machine calendar, a TG calendar or a soft calendar may be used.
【００２０】表面被覆する場合、塗工及び含浸する方法
としては、各種ブレードコータ、ロールコータ、エアー
ナイフコータ、バーコータ、ロッドコータ、ゲートロー
ルコータ、カーテンコータ、ショートドウェルコータ、
グラビアコータ、フレキソグラビアコータ、サイズプレ
ス等の各種装置をオンマシン或はオフマシンで用いるこ
とができる。しかし、本発明においては、ロッドコータ
又はゲートロールコータが好ましい。又、塗工又は含浸
後には、マシンカレンダー、ＴＧカレンダー、スーパー
カレンダー、ソフトカレンダー等のカレンダーを用いて
仕上げても良い。In the case of surface coating, various blade coaters, roll coaters, air knife coaters, bar coaters, rod coaters, gate roll coaters, curtain coaters, short dwell coaters,
Various machines such as a gravure coater, a flexo gravure coater, and a size press can be used on-machine or off-machine. However, in the present invention, a rod coater or a gate roll coater is preferable. Further, after coating or impregnation, finishing may be performed using a machine calendar, a TG calendar, a super calendar, a soft calendar or the like.
【００２１】本発明で云う水性インクとは、下記の着色
剤、液媒体、その他の添加剤からなる記録液体である。
着色剤としては、直接染料、酸性染料、塩基性染料、反
応性染料或は食品用色素等の水溶性染料が挙げられる。The aqueous ink referred to in the present invention is a recording liquid containing the following colorant, liquid medium and other additives.
Examples of the colorant include water-soluble dyes such as direct dyes, acid dyes, basic dyes, reactive dyes and food dyes.
【００２２】水性インクの溶媒としては、水及び水溶性
の各種有機溶剤、例えば、メチルアルコール、エチルア
ルコール、ｎ−プロピルアルコール、イソプロピルアル
コール、ｎ−ブチルアルコール、sec−ブチルアルコー
ル、tert−ブチルアルコール、イソブチルアルコール等
の炭素数１〜４のアルキルアルコール類；ジメチルホル
ムアミド、ジメチルアセトアミド等のアミド類；アセト
ン、ジアセトンアルコール等のケトン又はケトンアルコ
ール類；テトラヒドロフラン、ジオキサン等のエーテル
類；ポリエチレングリコール、ポリプロピレングリコー
ル等のポリアルキレングリコール類；エチレングリコー
ル、プロピレングリコール、ブチレングリコール、トリ
エチレングリコール、1,2,6 −ヘキサントリオール、チ
オジグリコール、ヘキシレングリコール、ジエチレング
リコール等のアルキレン基が２〜６個のアルキレングリ
コール類；グリセリン、エチレングリコールメチルエー
テル、ジエチレングリコールメチル（又はエチル）エー
テル、トリエチレングリコール、モノメチルエーテル等
の多価アルコールの低級アルキルエーテル類等が挙げら
れる。これらの多くの水溶性有機溶剤の中でも、ジエチ
レングリコール等の多価アルコール、トリエチレングリ
コールモノメチルエーテル、トリエチレングリコールモ
ノエチルエーテル等の多価アルコールの低級アルキルエ
ーテルが好ましい。 その他の添加剤としては、例え
ば、ＰＨ調節剤、金属封鎖剤、防カビ剤、粘度調整剤、
表面張力調整剤、湿潤剤、界面活性剤、及び防錆剤等が
挙げられる。As the solvent for the aqueous ink, water and various water-soluble organic solvents such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol, C1-C4 alkyl alcohols such as isobutyl alcohol; amides such as dimethylformamide and dimethylacetamide; ketones or ketone alcohols such as acetone and diacetone alcohol; ethers such as tetrahydrofuran and dioxane; polyethylene glycol, polypropylene glycol Polyalkylene glycols such as ethylene glycol, propylene glycol, butylene glycol, triethylene glycol, 1,2,6-hexanetriol, thiodiglycol, hex Alkylene glycols having 2 to 6 alkylene groups such as len glycol and diethylene glycol; lower alkyl ethers of polyhydric alcohols such as glycerin, ethylene glycol methyl ether, diethylene glycol methyl (or ethyl) ether, triethylene glycol and monomethyl ether Is mentioned. Among these many water-soluble organic solvents, polyhydric alcohols such as diethylene glycol and lower alkyl ethers of polyhydric alcohols such as triethylene glycol monomethyl ether and triethylene glycol monoethyl ether are preferable. Other additives include, for example, a pH adjusting agent, a sequestering agent, an antifungal agent, a viscosity adjusting agent,
Surface tension adjusting agents, wetting agents, surfactants, rust preventives and the like can be mentioned.
【００２３】本発明におけるインクジェット記録シート
は、インクジェット記録シートとしての使用に留まら
ず、記録時に液状であるインクを使用するどのような記
録シートとして用いることもできる。例えば、熱溶融性
物質、染顔料等を主成分とする熱溶融性インクを樹脂フ
ィルム、高密度紙、合成紙等の薄い支持体上に塗工した
インクシートを、その裏面より加熱し、インクを溶融さ
せて転写する熱転写記録用受像シート、熱溶融性インク
を加熱溶融して微小液滴化、飛翔記録するインクジェッ
ト記録シート、油溶性染料を溶媒に溶解したインクを用
いたインクジェット記録シート、光重合型モノマー及び
無色又は有色の染顔料を内包したマイクロカプセルを用
いた感光感圧型ドナーシートに対応する受像シート等が
挙げられる。The ink jet recording sheet according to the present invention is not limited to use as an ink jet recording sheet, but may be used as any recording sheet using a liquid ink during recording. For example, an ink sheet in which a heat-fusible ink containing a heat-fusible substance, a pigment or the like as a main component is coated on a thin support such as a resin film, high-density paper, or synthetic paper is heated from the back surface of the ink sheet, An image-receiving sheet for thermal transfer recording that melts and transfers ink, an inkjet recording sheet that heat-melts a heat-melting ink to form fine droplets, and flight recording, an inkjet recording sheet that uses an ink in which an oil-soluble dye is dissolved, An image receiving sheet corresponding to a light and pressure sensitive donor sheet using microcapsules containing a polymerizable monomer and a colorless or colored dye / pigment may be mentioned.
【００２４】これらの記録シートの共通点は、記録時に
インクが液体状態である点である。液状インクは、硬
化、固化又は定着までに、記録シートのインク受理層の
深さ方向又は水平方向に対して浸透又は拡っていく。上
述した各種記録シートは、それぞれの方式に応じた吸収
性を必要とするもので、本発明のインクジェット記録シ
ートを上述した各種の記録シートとして利用しても何ら
制限しない。更に、複写機・プリンター等に広く使用さ
れている電子写真記録方式のトナーを加熱定着する記録
シートとして、本発明におけるインクジェット記録シー
トを使用することもできる。The common point of these recording sheets is that the ink is in a liquid state at the time of recording. The liquid ink penetrates or spreads in the depth direction or the horizontal direction of the ink receiving layer of the recording sheet before being cured, solidified, or fixed. The various recording sheets described above require absorptivity according to their respective methods, and the inkjet recording sheet of the present invention may be used as the various recording sheets described above without any limitation. Further, the ink jet recording sheet of the present invention can be used as a recording sheet for heating and fixing toner of an electrophotographic recording system which is widely used in copying machines, printers and the like.
【００２５】[0025]
【作用】本発明のインクジェット記録シートは、微塗工
タイプのインクジェット記録シートであり、該記録シー
トの記録面が、原紙の交絡状態にあるパルプ繊維に沿っ
てパルプ繊維表面を表面被覆したもので、記録面に被覆
されたパルプ繊維形状を走査電子顕微鏡により視認する
ことができ、記録面のパルプ繊維表面の表面被覆率が７
０％以上であることを特徴とし、インクの滲みムラがな
くインク吸収性に優れる。これは、インクが該記録シー
トの記録面に与えられたとき、記録面方向に広がらず、
表面被覆面に浸透し、余剰インクが原紙の厚さ方向に浸
透することによるものであり、真円に近い記録ドットの
形状を得ることができる。又、記録された画像の濃度及
び鮮明性の高いインクジェット記録シートを得ることが
できる。The ink jet recording sheet of the present invention is a fine coating type ink jet recording sheet, and the recording surface of the recording sheet is obtained by surface-coating the pulp fiber surface along the pulp fibers in the entangled state of the base paper. The shape of the pulp fiber coated on the recording surface can be visually confirmed by a scanning electron microscope, and the surface coverage of the pulp fiber surface on the recording surface is 7
It is characterized in that it is 0% or more, and there is no unevenness of ink bleeding and the ink absorbability is excellent. This is because when ink is applied to the recording surface of the recording sheet, it does not spread in the recording surface direction,
This is because the ink penetrates into the surface-covered surface and the excess ink permeates in the thickness direction of the base paper, and it is possible to obtain the shape of the recording dot close to a perfect circle. Further, it is possible to obtain an ink jet recording sheet having a recorded image with high density and sharpness.
【００２６】[0026]
【実施例】以下に、本発明の実施例を挙げて説明する
が、本発明はこれらの例に限定されるものではない。
又、実施例において示す「部」及び「％」は、特に明示
しない限り重量部及び重量％を示す。なお、超微粒子無
機顔料については、水分散液として使用したが、いずれ
も固形分で表示した。EXAMPLES Examples of the present invention will be described below, but the present invention is not limited to these examples.
Further, “parts” and “%” shown in the examples represent parts by weight and% by weight, unless otherwise specified. The ultrafine-particle inorganic pigment was used as an aqueous dispersion, but all are shown by solid content.
【００２７】実施例１ ［原紙の作製］濾水度４５０ｍｌｃｆｓのＬＢＫＰ８３
部、濾水度４８０ｍｌｃｓｆのＮＢＫＰ８部からなるパ
ルプスラリーに、カチオン澱粉０．８部、硫酸バンド
０．４部、カオリン９部、アルキルケテンダイマー０．
１部を添加して、パルプスラリーをｐＨ８．２に調整
し、長網抄紙機で抄造乾燥し、マシンカレンダー仕上げ
をして、坪量８５ｇ／ｍ2の原紙を作製した。なお、作
製した原紙のステキヒトサイズ度は、２５秒であった。Example 1 [Preparation of base paper] LBKP83 having a freeness of 450 mlcfs
Part, a pulp slurry consisting of 8 parts of NBKP having a freeness of 480 mlcsf, 0.8 parts of cationic starch, 0.4 parts of sulfuric acid band, 9 parts of kaolin, 0 parts of alkyl ketene dimer.
The pulp slurry was adjusted to pH 8.2 by adding 1 part, paper-making dried with a Fourdrinier paper machine, and machine calendering was performed to prepare a base paper having a basis weight of 85 g / m 2 . The prepared paper had a Steckigt sizing degree of 25 seconds.
【００２８】［インクジェット記録シートの作製］上記
により作製した原紙に、表面被覆面の組成物として、コ
ロイダルシリカ（スノーテックス−ＹＬ、日産化学製、
一次粒子径５０〜８０ｎｍ）１００部、接着剤としてポ
リビニルアルコール（ＰＶＡ１１７、クラレ社製）３０
部、染料定着剤としてカチオン性樹脂（ポリフィックス
６０１、カチオン荷電量６．９ｍｅｑ．／ｇ、昭和高分
子社製）３０部を主成分とする固形分濃度１０％の水性
分散液をロッドコータを用いて乾燥固形分１ｇ／ｍ2と
なるように塗工、乾燥し、カレンダー仕上げしてインク
ジェット記録シートを作製した。[Preparation of Inkjet Recording Sheet] Colloidal silica (Snowtex-YL, manufactured by Nissan Kagaku,
100 parts of primary particle diameter 50 to 80 nm, polyvinyl alcohol (PVA117, manufactured by Kuraray Co., Ltd.) 30 as an adhesive agent
Part, an aqueous dispersion having a solid content concentration of 10% and containing 30 parts of a cationic resin (Polyfix 601, cation charge amount of 6.9 meq./g, Showa Polymer Co., Ltd.) as a dye fixing agent as a main component was applied to a rod coater. An ink jet recording sheet was prepared by applying the coating composition to a dry solid content of 1 g / m 2 , drying, and calendering.
【００２９】実施例２ 実施例１で作製した原紙に、カチオン性コロイダルシリ
カ（スノーテックス−ＡＫ（３）、日産化学社製、一次
粒子径１０〜２０ｎｍ）１００部、接着剤としてポリビ
ニルアルコール（ＰＶＡ１１７、クラレ社製）３０部、
染料定着剤としてカチオン性樹脂（スミレーズレジン１
００１、カチオン荷電量３．５ｍｅｑ．／ｇ、住友化学
社製）３０部を主成分とする固形分濃度１０％の水性分
散液をロッドコータを用いて乾燥固形分２ｇ／ｍ2とな
るように塗工、乾燥し、カレンダー仕上げしてインクジ
ェット記録シートを作製した。Example 2 100 parts of cationic colloidal silica (Snowtex-AK (3), Nissan Chemical Co., Ltd., primary particle size 10 to 20 nm) was added to the base paper prepared in Example 1 and polyvinyl alcohol (PVA117 was used as an adhesive. , Kuraray Co., Ltd.) 30 parts,
Cationic resin as dye fixing agent (Sumiraz resin 1
001, cation charge amount 3.5 meq. / G, manufactured by Sumitomo Chemical Co., Ltd.) and an aqueous dispersion having a solid content of 10% as a main component of 30 parts is coated with a rod coater to a dry solid content of 2 g / m 2 , dried, and calendered. To prepare an inkjet recording sheet.
【００３０】実施例３ 実施例１で作製した原紙に、アルミナ水和物（カタロイ
ドＡＳ−３、触媒化成工業社製、一次粒子径約１０ｎ
ｍ）１００部、接着剤としてポリビニルアルコール（Ｐ
ＶＡ１１７、クラレ社製）３０部、染料定着剤としてカ
チオン性樹脂（ポリフィックス６０１、カチオン荷電量
６．９ｍｅｑ．／ｇ、昭和高分子社製）３０部を主成分
とする固形分濃度１５％の水性分散液をエアーナイフコ
ータを用いて乾燥固形分５ｇ／ｍ2となるように塗工、
乾燥し、カレンダー仕上げしてインクジェット記録シー
トを作製した。Example 3 On the base paper prepared in Example 1, an alumina hydrate (Cataloid AS-3, manufactured by Catalysts & Chemicals Co., Ltd., primary particle diameter of about 10 n) was used.
m) 100 parts, polyvinyl alcohol (P
VA117, manufactured by Kuraray Co., Ltd.), 30 parts, 30 parts of a cationic resin (Polyfix 601, cation charge amount of 6.9 meq./g, Showa Polymer Co., Ltd.) as a dye fixing agent, and a solid content concentration of 15% Coating the aqueous dispersion with an air knife coater to a dry solid content of 5 g / m 2 ,
An ink jet recording sheet was prepared by drying and calendering.
【００３１】実施例４ 実施例３で使用した水性分散液の固形分濃度を１０％と
し、実施例１の原紙を使用して、サイズプレスを用いて
乾燥固形分が０．５ｇ／ｍ2となるように塗工、乾燥
し、カレンダー仕上げしてインクジェット記録シートを
作製した。Example 4 The solid content concentration of the aqueous dispersion used in Example 3 was 10%, and the dry solid content was 0.5 g / m 2 by using the base paper of Example 1 and a size press. An ink jet recording sheet was prepared by applying the above coating, drying, and calendering.
【００３２】実施例５ 実施例３で使用した水性分散液の固形分濃度を１０％と
し、実施例１の原紙を使用して、ゲートロールコータを
用いて乾燥固形分が２ｇ／ｍ2となるように塗工、乾燥
し、カレンダー仕上げしてインクジェット記録シートを
作製した。Example 5 The solid content concentration of the aqueous dispersion used in Example 3 was set to 10%, and the base paper of Example 1 was used to obtain a dry solid content of 2 g / m 2 using a gate roll coater. Thus, the ink jet recording sheet was prepared by coating, drying and calendering.
【００３３】比較例１ 実施例１で作製した原紙に、コロイダルシリカ（スノー
テックスＰＳＴ−３、日産化学社製、一次粒子径３００
±３０ｎｍ）１００部、接着剤としてポリビニルアルコ
ール（ＰＶＡ１１７、クラレ社製）３０部、染料定着剤
としてカチオン性樹脂（ポリフィックス６０１、カチオ
ン荷電量６．９ｍｅｑ．／ｇ、昭和高分子社製）３０部
を主成分とする固形分濃度１０％の水性分散液をロッド
コータを用いて乾燥固形分２ｇ／ｍ2となるように塗
工、乾燥し、カレンダー仕上げしてインクジェット記録
シートを作製した。Comparative Example 1 Colloidal silica (Snowtex PST-3, manufactured by Nissan Kagaku Co., Ltd., primary particle size 300) was applied to the base paper prepared in Example 1.
± 30 nm) 100 parts, polyvinyl alcohol (PVA117, Kuraray Co., Ltd.) 30 parts as an adhesive, cationic resin (Polyfix 601, cation charge amount 6.9 meq./g, Showa Polymer Co., Ltd.) 30 as a dye fixing agent 30 Parts was used as a main component, and an aqueous dispersion having a solid content concentration of 10% was applied using a rod coater to a dry solid content of 2 g / m 2 , dried, and calendered to prepare an inkjet recording sheet.
【００３４】比較例２ 実施例１で作製した原紙に、シリカ（ニップシルＥ２２
０Ａ、日本シリカ工業製、平均粒子径１．０μｍ）１０
０部、接着剤としてポリビニルアルコール（ＰＶＡ１１
７、クラレ社製）３０部、染料定着剤としてカチオン性
樹脂（ポリフィックス６０１、カチオン荷電量６．９ｍ
ｅｑ．／ｇ、昭和高分子社製）３０部を主成分とする固
形分濃度１０％の水性分散液をゲートロールコータを用
いて乾燥固形分２ｇ／ｍ2となるように塗工、乾燥し、
カレンダー仕上げしてインクジェット記録シートを作製
した。Comparative Example 2 The base paper prepared in Example 1 was coated with silica (Nipsil E22
0A, manufactured by Nippon Silica Industry Co., Ltd., average particle size 1.0 μm) 10
0 parts, polyvinyl alcohol (PVA11 as an adhesive
7, Kuraray Co., Ltd. 30 parts, cationic resin as a dye fixing agent (Polyfix 601, cationic charge amount 6.9 m)
eq. / G, manufactured by Showa High Polymer Co., Ltd.), and an aqueous dispersion having a solid content of 10% as a main component is applied using a gate roll coater to a dry solid content of 2 g / m 2, and dried.
An ink jet recording sheet was prepared by calendering.
【００３５】比較例３ 比較例２で使用した水性分散液を固形分濃度１５％と
し、実施例１の原紙を使用し、エアーナイフコータを用
いて乾燥固形分５ｇ／ｍ2となるように塗工、乾燥し、
カレンダー仕上げしてインクジェット記録シートを作製
した。Comparative Example 3 The aqueous dispersion used in Comparative Example 2 was applied to a solid content concentration of 15%, the base paper of Example 1 was used, and the dry solid content was applied to 5 g / m 2 using an air knife coater. Work, dry,
An ink jet recording sheet was prepared by calendering.
【００３６】比較例４ 実施例１で作製した原紙をそのまま比較例３のインクジ
ェット記録シートとした。Comparative Example 4 The base paper prepared in Example 1 was used as it is as an ink jet recording sheet of Comparative Example 3.
【００３７】上記の実施例１〜５及び比較例１〜４で作
製したインクジェット記録シートについて、以下の方法
に基づいて評価し、その結果を表１に示した。The ink jet recording sheets prepared in Examples 1 to 5 and Comparative Examples 1 to 4 were evaluated by the following method, and the results are shown in Table 1.
【００３８】［インク吸収性］インク吸収性及び画像の
鮮明性は、重色ベタ印字部分の境界、例えば、赤印字
（マゼンタ＋イエロー）と緑印字（シアン＋イエロー）
の境界部分のインクのにじみ具合いを、目視で判定し
た。赤印字部分と緑印字部分が重ならず、分離している
場合を特性良好とし、重なりが大きくなって黒線状にな
る場合を特性不良とした。インク吸収性の悪いものは、
著しく画像品位（画像の鮮明性）を損なうため、他の特
性、例えば、画像濃度等が良くても、何等意味をなさな
い。なお、評価基準として、Ａは特性が良好、Ｂは実用
上問題ない範囲で良好、Ｃは実用上問題あり、Ｄは特性
が不良を示す。[Ink Absorbency] Ink absorptivity and image sharpness are determined by the boundaries of solid color solid print portions, for example, red print (magenta + yellow) and green print (cyan + yellow).
The degree of ink bleeding at the boundary portion of was visually determined. When the red printed portion and the green printed portion did not overlap and were separated, the characteristics were good, and when the overlapping was large and a black line was formed, the characteristics were bad. If the ink absorption is poor,
Since the image quality (image sharpness) is remarkably impaired, it does not make any sense even if other characteristics such as image density are good. In addition, as an evaluation criterion, A indicates a good characteristic, B indicates a good practically acceptable range, C indicates a practical problem, and D indicates a poor characteristic.
【００３９】［画像濃度］画像濃度は、ブラックインク
でベタ印字した部分を、反射濃度計（マクベスＲＤ９１
８；マクベス社製）を用いて測定した。数値が高いほど
画像濃度が高く良好であるが、通常１．２０以上あれば
良好である。[Image Density] The image density is a reflection densitometer (Macbeth RD91) for a solid printed portion of black ink.
8: manufactured by Macbeth). The higher the value, the higher the image density and the better, but normally, 1.20 or more is good.
【００４０】［記録面の表面被覆率］記録面の表面被覆
率（％）は、走査電子顕微鏡によりインクジェット記録
シートのパルプ繊維表面において、使用した素材の金属
元素のＸ線像図を撮影し、画像解析装置を用いてパルプ
繊維表面の表面被覆率を面積率として測定した。[Surface Coverage of Recording Surface] The surface coverage (%) of the recording surface was determined by taking an X-ray image of the metal element of the material used on the pulp fiber surface of the ink jet recording sheet with a scanning electron microscope. The surface coverage of the pulp fiber surface was measured as an area ratio using an image analyzer.
【００４１】［ドット形状係数］インクジェットプリン
タ（ＩＯ−７２０：シャープ株式会社製）を用いて、ブ
ラックインクから成る単色ドットを印字して、画像解析
装置により、ドットの周囲長Ｌ及びドットの面積Ａを測
定し、下記の数１により定義するドット形状係数Ｃを算
出した。ドット形状係数Ｃが１．０の場合、真円とし
て、１．０から離れて大きくなるほど、ドットの滲み出
し等により、ドット形状が不規則であることを示す。[Dot shape factor] An ink jet printer (IO-720: manufactured by Sharp Corporation) is used to print a single color dot made of black ink, and an image analyzer analyzes the dot perimeter L and the dot area A. Was measured, and the dot shape factor C defined by the following equation 1 was calculated. When the dot shape factor C is 1.0, the larger the distance from 1.0 as a perfect circle, the more irregular the dot shape due to dot bleeding.
【００４２】[0042]
【数１】Ｃ＝Ｌ2／（４π×Ａ） ここで、Ｃはドット形状係数、Ｌはドットの周囲長、Ａ
はドットの面積を表す。## EQU1 ## C = L 2 / (4π × A) where C is the dot shape factor, L is the perimeter of the dot, and A
Represents the area of a dot.
【００４３】[0043]
【表１】 [Table 1]
【００４４】表１の結果より、実施例１〜５及び比較例
１〜４のインクジェット記録シートにおいて、実施例に
おける該記録シートは、使用した超微粒子無機顔料の粒
子径が小さく、表面被覆率が本発明の範囲内に入ってお
り、いずれもインク吸収性、鮮明性、画像濃度共に良好
であった。又、ドット形状係数も小さく、真円に近い記
録ドット形状を示していた。一方、比較例１〜３では、
使用した粒子径が大きいために表面被覆率が低く、画像
濃度が低く、ドット形状係数が大きく、不良であった。
比較例３では、被覆量が５ｇ／ｍ2と多いが、使用した
無機顔料の粒子径が大きいために、表面被覆率として低
い結果であった。特に、実施例２、実施例５、比較例
１、並びに比較例２を比較すると、表面被覆において２
ｇ／ｍ2と被覆量が同一であるが、使用した無機顔料の
粒子径に依存して、パルプ繊維への被覆率が悪くなって
いることを示した。From the results shown in Table 1, in the ink jet recording sheets of Examples 1 to 5 and Comparative Examples 1 to 4, the recording sheets in Examples had a small particle size of the ultrafine inorganic pigment used and a surface coverage ratio. It was within the range of the present invention, and all were good in ink absorbency, sharpness, and image density. Also, the dot shape coefficient was small and the recording dot shape was close to a perfect circle. On the other hand, in Comparative Examples 1 to 3,
Since the particle size used was large, the surface coverage was low, the image density was low, the dot shape factor was large, and the result was poor.
In Comparative Example 3, the coating amount was as large as 5 g / m 2 , but the surface coverage was low because the particle size of the inorganic pigment used was large. In particular, comparing Example 2, Example 5, Comparative Example 1, and Comparative Example 2, it was found that 2 in the surface coating.
Although the coverage was the same as g / m 2 , it was shown that the coverage on the pulp fiber was poor depending on the particle size of the inorganic pigment used.
【００４５】[0045]
【発明の効果】本発明のインクジェット記録シートは、
超微粒子無機顔料を主体とする組成物で原紙面のパルプ
繊維表面を表面被覆してなる記録面を有し、記録面に被
覆されたパルプ繊維形状を電子顕微鏡により視認でき、
且つ表面被覆率が７０％以上とすることでインク滲みム
ラがなくインク吸収性に優れ、画像の濃度及び鮮明性が
高く、真円に近い記録ドット形状が得られるインクジェ
ット記録シートである。The ink jet recording sheet of the present invention is
It has a recording surface formed by surface-coating the pulp fiber surface of the raw paper surface with a composition mainly composed of ultrafine particle inorganic pigment, and the pulp fiber shape coated on the recording surface can be visually confirmed by an electron microscope,
Further, when the surface coverage is 70% or more, there is no unevenness of ink bleeding, excellent ink absorbency, high image density and sharpness, and a recording dot shape close to a perfect circle can be obtained.
Claims (1)
記録シートの記録面が、原紙面の交絡状態にあるパルプ
繊維表面に沿って超微粒子無機顔料を主体とする組成物
で表面被覆された該記録面で、該記録面に被覆されたパ
ルプ繊維形状を走査電子顕微鏡により視認することがで
き、且つ該記録面の被覆されたパルプ繊維の表面被覆率
が７０％以上であることを特徴とするインクジェット記
録シート。1. An inkjet recording sheet, wherein the recording surface of the recording sheet is surface-coated with a composition mainly comprising ultrafine inorganic pigments along the pulp fiber surface which is in an entangled state with the base paper surface. An ink jet recording sheet characterized in that the shape of pulp fibers coated on the recording surface can be visually confirmed by a scanning electron microscope, and the surface coverage of the pulp fibers coated on the recording surface is 70% or more. .