JP3329524B2 - Inkjet recording sheet - Google Patents
Inkjet recording sheetInfo
- Publication number
- JP3329524B2 JP3329524B2 JP21571093A JP21571093A JP3329524B2 JP 3329524 B2 JP3329524 B2 JP 3329524B2 JP 21571093 A JP21571093 A JP 21571093A JP 21571093 A JP21571093 A JP 21571093A JP 3329524 B2 JP3329524 B2 JP 3329524B2
- Authority
- JP
- Japan
- Prior art keywords
- ink
- recording sheet
- jet recording
- ink jet
- base paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【０００１】[0001]
【産業上の利用分野】本発明は、インクジェット記録シ
ートに関するものであり、更に詳しくは、原紙の平滑性
に反映してインク受理層塗液の塗工性に優れ、インク受
理層面の塗工ムラがなく、且つインクの吸収性や鮮明性
に優れ、剛直性のある微塗工タイプのインクジェット記
録シートに関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to an ink jet recording sheet, and more particularly, to an ink receiving layer having excellent coating properties reflecting the smoothness of a base paper and coating unevenness on the surface of the ink receiving layer. The present invention relates to a fine-coating type ink jet recording sheet having no rigidity, excellent ink absorbency and clearness, and having rigidity.
【０００２】インクジェット記録方式は、種々の作動原
理によりインクの微小液滴を飛翔させて紙等の記録シー
トに付着させ、画像、文字等の記録を行なうものである
が、高速、低騒音、多色化が容易、記録パターンの融通
性が大きい、現像−定着が不要等の特徴があり、漢字を
含め各種図形及びカラー画像等の記録装置として種々の
用途において急速に普及している。又、多色インクジェ
ット方式により形成される画像は、製版方式による多色
印刷やカラー写真方式による印画に比較して、遜色のな
い記録を得ることが可能である。更に、作成部数が少な
くて済む用途においては、写真技術によるよりも安価で
あることからフルカラー画像記録分野にまで広く応用さ
れつつある。[0002] Ink jet recording is a method in which minute droplets of ink are made to fly and adhere to a recording sheet such as paper by various operating principles to record images, characters, and the like. It has features such as easy colorization, great flexibility in recording patterns, and no need for development-fixing, and is rapidly spreading in various applications as a recording device for various figures including Chinese characters and color images. Further, an image formed by the multi-color ink jet system can obtain a record comparable to multi-color printing by a plate making system or printing by a color photographic system. Further, in applications where the number of copies required is small, it is being widely applied to the field of full-color image recording because it is cheaper than the photographic technique.
【０００３】特に、近年では、ニーズの多様化に伴っ
て、インクジェット記録方式で印字された記録シート
が、価格表示用ラベル、商品表示（バーコード）用ラベ
ル、品質表示用ラベル、計量表示用ラベル、広告宣伝用
ラベル（ステッカー）等のラベル用途、或はＣＤ／ＡＴ
Ｍ、自動発券機等の金銭に係わる用途に使用されつつあ
る。これらの用途においては、インクジェット記録シー
ト自体の種々特性に加えて、十分な剛直性を有すること
が求められる。[0003] In recent years, in recent years, with the diversification of needs, recording sheets printed by the ink jet recording method have been used for price display labels, product display (barcode) labels, quality display labels, and weighing display labels. , Label applications such as advertising labels (stickers), or CD / AT
M, is being used for money related applications such as automatic ticketing machines. In these applications, the inkjet recording sheet is required to have sufficient rigidity in addition to various properties of the inkjet recording sheet itself.
【０００４】インクジェット記録方式で使用される記録
シートとしては、通常の印刷や筆記に使われる上質紙や
コーテッド紙を使うべく、装置やインク組成の面から努
力がなされてきた。しかし、装置の高速化・高精細化或
はフルカラー化等インクジェット記録装置の性能の向上
や用途の拡大に伴い、記録シートに対してもより高度な
特性が要求されるようになった。即ち、当該記録シート
としては、印字ドットの濃度が高く、色調が明るく鮮や
かであること、インクの吸収が早くて印字ドットが重な
った場合においてもインクが流れ出したり滲んだりしな
いこと、印字ドットの横方向への拡散が必要以上に大き
くなく、且つ周辺が滑らかでぼやけないこと等が要求さ
れる。As recording sheets used in the ink jet recording system, efforts have been made in terms of apparatuses and ink compositions in order to use high-quality paper and coated paper used for ordinary printing and writing. However, as the performance of the inkjet recording apparatus has been improved and the use thereof has been expanded, such as by increasing the speed and increasing the definition of the apparatus or by increasing the color, the recording sheet has been required to have higher properties. That is, the recording sheet has a high density of print dots, a bright and vivid color tone, quick absorption of ink, so that ink does not flow or bleed even when print dots overlap, It is required that the diffusion in the direction is not excessively large and that the periphery is smooth and not blurred.
【０００５】インクジェット記録シートの形態として
は、所謂、上質紙・ボンド紙等に代表される普通紙タイ
プと上質紙等の紙、合成紙、合成樹脂フィルム等の支持
体面上にインク受理層を設けた塗工タイプに大別され
る。[0005] The form of the ink jet recording sheet is a so-called plain paper type typified by high quality paper or bond paper, and an ink receiving layer provided on a support such as paper such as high quality paper, synthetic paper, synthetic resin film or the like. Coating type.
【０００６】塗工タイプには、１〜１０／ｍ2程度の低
塗工タイプ、１０〜２０ｇ／ｍ2程度の中塗工タイプ、
２０ｇ／ｍ2以上の高塗工タイプの各インクジェット記
録シートがある。特に、近年に至っては、低塗工タイプ
でも下限の塗工量０．５〜５ｇ／ｍ2の微塗工タイプが
普通紙に近いものとなり、外観的にも、取扱いとしても
好ましく、この微塗工タイプが望まれてきている。微塗
工タイプのインクジェット記録シートは、原紙に塗設さ
れるインク受理層の塗工量が少なく、インクジェット記
録シートの種々特性が、原紙に大きく依存することか
ら、均一なインク受理層を得るには、原紙の平滑性を高
くすることが最も好ましい手段である。即ち、原紙の平
滑性を高めることにより、インク受理層塗液の塗工が容
易となり、塗設されたインク受理層を均一な塗層とする
ことができる。The coating type includes a low coating type of about 1 to 10 / m 2, a medium coating type of about 10 to 20 g / m 2 ,
There is a high coating type ink jet recording sheet of 20 g / m 2 or more. In particular, in recent years, even with a low coating type, a fine coating type having a lower coating amount of 0.5 to 5 g / m 2 is closer to plain paper, and is preferable in appearance and handling. Coating type is desired. The finely coated type ink jet recording sheet has a small coating amount of the ink receiving layer applied to the base paper, and various properties of the ink jet recording sheet greatly depend on the base paper, so that a uniform ink receiving layer can be obtained. The most preferable means is to increase the smoothness of the base paper. That is, by increasing the smoothness of the base paper, the application of the ink receiving layer coating liquid becomes easy, and the applied ink receiving layer can be made a uniform coating layer.
【０００７】平滑性としては、地合等に起因する波長が
数ｍｍ以上の比較的大きな凹凸と、パルプ繊維の粗度等
の影響を受け易いそれ以下の微細な凹凸が対象になる。
比較的大きな凹凸の改良としては、原紙に用いるパルプ
の繊維長分布を所定の範囲内に調節する方法、パルプの
繊維長と保水度を所定の範囲に調節する方法等がある。[0007] The smoothness includes relatively large unevenness having a wavelength of several mm or more due to formation and the like, and fine unevenness less than that which is easily affected by the roughness of the pulp fiber.
As a method for improving relatively large irregularities, there are a method of adjusting the fiber length distribution of pulp used for base paper within a predetermined range, and a method of adjusting the fiber length and water retention of pulp within a predetermined range.
【０００８】又、微細な凹凸の改良としては、繊維壁厚
さの薄いパルプ繊維を選択することや原紙に種々のカレ
ンダー処理を行う方法等がある。As the improvement of fine irregularities, there is a method of selecting a pulp fiber having a small fiber wall thickness, a method of performing various calendering treatments on base paper, and the like.
【０００９】[0009]
【発明が解決しようとする課題】上述したとおり、微塗
工タイプのインクジェット記録シートでは、原紙の平滑
性を高め、インク受理層塗液の塗工性を向上させる目的
で、原紙について種々の試みがなされているが、これら
のいずれの方法によっても、大きさの異なる２種類の凹
凸を同時に改良しがたく、剛直度のような力学的性質に
悪影響を及ぼすことが多い等の問題点があった。As described above, in the case of the ink-jet recording sheet of the fine coating type, various attempts have been made for the base paper for the purpose of improving the smoothness of the base paper and improving the coatability of the coating liquid for the ink receiving layer. However, any of these methods has a problem that two types of irregularities having different sizes are hardly improved at the same time, and often adversely affect mechanical properties such as rigidity. Was.
【００１０】又、パルプの１５０メッシュ通過分を所定
の値以下に調整する方法、重量繊維長と保水度が所定の
範囲内にあるパルプを原紙に使用する方法等では、比較
的大きい凹凸の改良には有効であるが、微細な凹凸の改
良には不十分である、剛直度が低下する等の問題があっ
た。In a method of adjusting the pulp passing through 150 mesh to a predetermined value or less, a method of using a pulp having a weight fiber length and a water retention within a predetermined range as a base paper, etc., improvement of relatively large unevenness is required. However, there are problems such as insufficient rigidity, and insufficient rigidity.
【００１１】更に、パルプとして繊維壁厚さの薄いメー
プルを使用する方法では、平滑性改良に関してはある程
度有効であるが、剛直度の低下が問題であった。又、カ
レンダーの加圧条件を変更する方法では、微細な凹凸は
改良できるが、比較的大きな凹凸の改良には不十分であ
り、剛直度の低下も著しかった。Further, the method of using maple having a small fiber wall thickness as pulp is effective to some extent in terms of improving smoothness, but has a problem in that rigidity is reduced. Further, the method of changing the pressing condition of the calender can improve fine irregularities, but it is insufficient for improvement of relatively large irregularities, and the rigidity is significantly reduced.
【００１２】上述したとおり、目的とする平滑性が良好
で、インク受理層塗液の塗工性の優れ、且つ十分な剛直
性を有するインクジェット記録シートの原紙とすること
ができなかった。As described above, it was not possible to obtain a base paper for an ink jet recording sheet having a desired smoothness, excellent coatability of the ink receiving layer coating liquid, and sufficient rigidity.
【００１３】即ち、本発明の目的は、インクジェット記
録シートでも、微塗工タイプのインクジェット記録シー
トであり、インク受理層塗液の塗工性に優れ、インク受
理層の塗工ムラがなく、且つインク吸収性や鮮明性に優
れ、剛直性を有するインクジェット記録シートを得るこ
とを目的とするものである。That is, an object of the present invention is to provide an ink jet recording sheet which is a finely coated type ink jet recording sheet, has excellent coating properties of the ink receiving layer coating liquid, has no coating unevenness of the ink receiving layer, and An object of the present invention is to obtain an ink jet recording sheet having excellent rigidity and excellent ink absorbency and sharpness.
【００１４】[0014]
【課題を解決するための手段】本発明者らは、上記に鑑
み鋭意研究した結果、インク受理層塗液の塗工性に優
れ、インク受理層の塗工ムラがなく、且つインク吸収性
や鮮明性に優れ、剛直性を有するインクジェット記録シ
ートを発明するに至った。即ち、本発明のインクジェッ
ト記録シートは、原紙上にインク受理層を塗設してなる
インクジェット記録シートにおいて、該原紙が、重量平
均繊維長が０．５５〜０．６５ｍｍであり、且つ道管要
素の長さ／幅が２．０以下である広葉樹パルプから構成
された該原紙であり、該インク受理層組成物が、主成分
として非球状カチオン性コロイダルシリカであることを
特徴とするものである。The present inventors have conducted intensive studies in view of the above, and as a result, have found that the coating properties of the ink receiving layer coating liquid are excellent, there is no coating unevenness of the ink receiving layer, and the ink absorbing property is high. The inventors have invented an ink jet recording sheet having excellent clarity and rigidity. That is, an ink jet recording sheet of the present invention is an ink jet recording sheet obtained by coating an ink receiving layer on a base paper, wherein the base paper has a weight average fiber length of 0.55 to 0.65 mm and a vascular element. A base paper composed of hardwood pulp having a length / width of 2.0 or less, wherein the ink receiving layer composition is a non-spherical cationic colloidal silica as a main component. .
【００１５】本発明のインクジェット記録シートにおい
て、広葉樹パルプの繊維粗度が、７．０〜１０．０ｍｇ
／１００ｍであることを特徴とするものである。In the ink jet recording sheet of the present invention, the hardwood pulp has a fiber roughness of 7.0 to 10.0 mg.
/ 100 m.
【００１６】本発明のインクジェット記録シートにおい
て、非球状カチオン性コロイダルシリカが、針状或は繊
維状のものであることを特徴とする。In the ink jet recording sheet of the present invention, the non-spherical cationic colloidal silica is acicular or fibrous.
【００１７】以下、本発明のインクジェット記録シート
について、詳細に説明する。本発明のインクジェット記
録シートにおいて、具体的には、先ず剛直度を維持しな
がら地合を改良するための条件について検討し、叩解後
のパルプの重量平均繊維長を０．５５〜０．６５ｍｍに
調節する必要があることを見い出した。次いで、微少な
凹凸の改良について検討した結果、広葉樹パルプに３〜
１５重量％含まれる道管要素の形態が微細な凹凸に大き
な影響を及ぼすことを見い出した。重量では少量の道管
要素も、原紙の表面に平行な面中で占める面積としては
３０％程度になりうるため、平滑性への影響が大きいも
のと思われる。更に、道管要素の長さ／幅が小さい方
が、表面の微細な凹凸を減少させる効果が大きいことを
見い出した。Hereinafter, the ink jet recording sheet of the present invention will be described in detail. In the ink jet recording sheet of the present invention, specifically, first, conditions for improving the formation while maintaining the rigidity are examined, and the weight-average fiber length of the pulp after beating is adjusted to 0.55 to 0.65 mm. I found that I needed to adjust. Next, as a result of examining the improvement of minute irregularities, it
It has been found that the form of the vascular element contained at 15% by weight has a great effect on fine irregularities. Even a small amount of a vascular element in terms of weight can occupy about 30% in a plane parallel to the surface of the base paper, so that the influence on smoothness is considered to be large. Further, it has been found that the smaller the length / width of the vascular element, the greater the effect of reducing fine irregularities on the surface.
【００１８】通常の印刷用紙等では、印刷時の道管ムケ
の原因になるため、長さ／幅が小さい道管要素は好まし
くないとされているが、インクジェット記録シート用原
紙の場合は、表面強度が印刷用紙ほど必要でないため、
このような道管要素を含む広葉樹パルプの使用が可能で
あり、むしろ積極的に使用することにより、平滑性を向
上させることが出来ることが明らかになった。道管要素
の形態の違いは、紙のＭＤ或はＣＤ方向の力学的性質に
はほとんど影響を及ぼさないため、剛直度を損なうこと
なく、平滑性の優れたインクジェット記録シート用原紙
を得ることが出来る。It is considered that a tubing element having a small length / width is not preferable for ordinary printing paper or the like because it causes tubing during printing. Because strength is not as necessary as printing paper,
It has been clarified that hardwood pulp containing such a vascular element can be used, and that the smoothness can be improved by positively using it. Since the difference in the form of the vascular element has little effect on the mechanical properties of the paper in the MD or CD directions, it is possible to obtain an ink jet recording sheet base paper having excellent smoothness without impairing the rigidity. I can do it.
【００１９】本発明の重量平均繊維長は、ＪＡＰＡＮ
ＴＡＰＰＩによる紙パルプ試験方法Ｎｏ．５２に準拠し
て測定した値である。叩解後のパルプの重量平均繊維長
を、０．５５〜０．６５ｍｍになるように調節する必要
がある。ここで、０．５５ｍｍ未満の場合は剛直度の低
下が大きく、０．６５ｍｍを超えると地合が悪化して波
長数ｍｍ以上の比較的大きい凹凸が悪化するため好まし
くない。The weight average fiber length of the present invention is JAPAN
Paper pulp test method No. by TAPPI. It is a value measured according to No. 52. It is necessary to adjust the weight average fiber length of the pulp after beating to be 0.55 to 0.65 mm. Here, if it is less than 0.55 mm, the rigidity is greatly reduced, and if it exceeds 0.65 mm, the formation deteriorates and relatively large unevenness having a wavelength of several mm or more deteriorates.
【００２０】叩解後の重量平均繊維長を調節する方法と
しては、上記範囲の繊維長の樹種から製造したパルプを
利用する方法と、叩解で繊維長を調節する方法がある
が、道管要素の長さ／幅の小さい樹種の繊維長がこの範
囲に入るとは限らないため、後者の叩解による方がより
実用的である。その手段としては、通常パルプの叩解に
使用される設備、即ちビーター、コニカルリファイナ
ー、ディスクリファイナー等をカッティング叩解が起こ
り易い条件に設定して使用することが出来る。As a method for adjusting the weight average fiber length after beating, there are a method using pulp produced from a tree species having a fiber length in the above range, and a method for adjusting the fiber length by beating. The latter is more practical, as the fiber length of tree species of small length / width does not always fall into this range. As the means, equipment normally used for beating pulp, that is, a beater, a conical refiner, a disc refiner, or the like can be used under conditions where cutting beating easily occurs.
【００２１】本発明における道管要素の長さ／幅とは、
パルプに含まれる道管要素の光学顕微鏡像について、道
管要素の最大長（ＭＬ）と最大長に平行な２本の直線で
画像をはさんだ時の２直線間の最短距離（ＢＤ）の比
（ＭＬ／ＢＤ）を測定した値である。なお、繊維のカッ
ティングが起こり易い条件で叩解した場合、道管要素の
破壊等はほとんど起こらないため、叩解、未叩解いずれ
のパルプもほぼ同様の道管要素の長さ／幅の値を示し
た。測定は通常５０個の道管要素について行う。The length / width of a vascular element in the present invention is defined as
About the optical microscope image of the vascular element contained in the pulp, the ratio of the maximum length (ML) of the vascular element and the shortest distance (BD) between the two straight lines when the image is sandwiched by two straight lines parallel to the maximum length (ML / BD) is a measured value. It should be noted that, when beaten under conditions where fiber cutting is likely to occur, almost no destruction of the vessel elements and the like occur, so that both the beaten and unbeaten pulp showed almost the same length / width value of the vessel elements. . The measurement is usually performed on 50 vascular elements.
【００２２】本発明では、道管要素の長さ／幅が２．０
以下の広葉樹パルプを使用するものとする。広葉樹の樹
種により、道管要素の長さ／幅は１〜１０の範囲で異な
るが、本発明で使用する長さ／幅が２．０以下の樹種に
は、メリーナ、ユーカリ、アルビジア、オーク属等があ
る。道管要素についての条件を満たす樹種においても、
木繊維の形態は様々であるが、木繊維の繊維粗度が、
７．０〜１０．０ｍｇ／１００ｍであるような樹種を用
いると、特に平滑性と剛直度の優れたインクジェット記
録シート用原紙が得られる。なお、本発明の繊維粗度
は、繊維質量が既知の試料についてＪＡＰＡＮ ＴＡＰ
ＰＩによる紙パルプ試験方法Ｎｏ．５２に準拠して数平
均繊維長と繊維総数を測定し、それらの結果から数１に
より算出した値である。繊維粗度は繊維長軸に直角方向
の平均断面積にほぼ比例すると考えられる。In the present invention, the length / width of the vascular element is 2.0
The following hardwood pulp shall be used. The length / width of the vascular element varies from 1 to 10 depending on the species of hardwood, but the tree species having a length / width of 2.0 or less used in the present invention include Melina, Eucalyptus, Albizia, and Oak genus. Etc. Even for species that meet the requirements for vascular elements,
Although the form of wood fiber varies, the fiber roughness of wood fiber is
When a tree species of 7.0 to 10.0 mg / 100 m is used, a base paper for an ink jet recording sheet having particularly excellent smoothness and rigidity can be obtained. In addition, the fiber roughness of the present invention is measured by using JAPAN TAP for a sample whose fiber mass is known.
Paper pulp test method No. PI This is a value obtained by measuring the number average fiber length and the total number of fibers in accordance with No. 52, and calculating from the results according to Equation 1. It is considered that the fiber roughness is almost proportional to the average cross-sectional area in the direction perpendicular to the long axis of the fiber.
【００２３】[0023]
【数１】Ｃ＝Ｗ×１０5／（Ｎ×Ｌ） Ｃ：繊維粗度（ｍｇ／１００ｍ） Ｗ：繊維質量（ｍｇ） Ｎ：繊維総数（本） Ｌ：数平均繊維長（ｍｍ）C = W × 10 5 / (N × L) C: Fiber roughness (mg / 100 m) W: Fiber mass (mg) N: Total number of fibers (number) L: Number average fiber length (mm)
【００２４】本発明で使用する広葉樹パルプとしては、
クラフトパルプ、サルファイトパルプ、ケミサーモメカ
ニカルパルプ、ケミメカニカルパルプ等を単独或は数種
類併用して使用することできる。又、数種類の広葉樹パ
ルプの混合使用、或は少量の針葉樹パルプとの混合物も
用いることが出来る。The hardwood pulp used in the present invention includes:
Kraft pulp, sulfite pulp, chemi-thermomechanical pulp, chemimechanical pulp and the like can be used alone or in combination of several kinds. It is also possible to use a mixture of several kinds of hardwood pulp or a mixture with a small amount of softwood pulp.
【００２５】本発明のインクジェット記録シート用の原
紙は、長網抄紙機、ハイブリッド抄紙機、ツインワイヤ
ー抄紙機等で抄造され、必要とされる平滑性に応じてマ
シンカレンダー、ソフトカレンダー、スーパーカレンダ
ー、熱カレンダー等により平滑化処理される。The base paper for the ink jet recording sheet of the present invention is formed by a fourdrinier paper machine, a hybrid paper machine, a twin wire paper machine, or the like, and depending on the required smoothness, a machine calender, a soft calender, a super calender, It is smoothed by a heat calender or the like.
【００２６】本発明のインクジェット記録シートは、微
塗工タイプのインクジェット記録シートであり、原紙の
上に、インク受理層が塗工量０．５〜５ｇ／ｍ2と薄く
塗工され、原紙面の平滑性をそのまま反映した状態で微
塗工され、且つ剛直性を有するものである。微塗工の程
度は、原紙自体の表面がより平滑性を有するほど塗工ム
ラの少ないものとすることができる。即ち、原紙の平滑
性が高いほど、インク受理層塗液の塗工性が向上し、均
一にインク受理層を塗工することが可能となったのであ
る。又、剛直性あるインクジェット記録シートとするこ
とが可能となった。The ink jet recording sheet of the present invention is an ink jet recording sheet of a fine coating type, in which an ink receiving layer is thinly coated on a base paper with a coating amount of 0.5 to 5 g / m 2 , Is finely coated in a state that reflects the smoothness of the material as it is, and has rigidity. The degree of the fine coating can be such that the more uneven the surface of the base paper itself, the less uneven the coating. In other words, the higher the smoothness of the base paper, the better the coatability of the ink receiving layer coating liquid, and the more uniformly the ink receiving layer can be coated. In addition, a rigid ink jet recording sheet can be obtained.
【００２７】本発明のインクジェット記録シートは、上
述したような本発明の範囲内にある原紙にインク受理層
を微塗工したものであり、原紙の均一性に反映して平
滑、且つ均一なインク受理層とすることができる。イン
ク受理層が均一に塗工されている場合、インクジェット
プリンターを使用してインク受理層面にインクが与えら
れたとき、インク受理層面が均一に塗工されているた
め、インクのインク受理層面方向の広がりを起こさず、
真円に近い記録ドットを表現することができ、余剰イン
クがインク受理層面から原紙の厚さ方向に浸透していく
ためである。一方、本発明の範囲外の原紙では、インク
受理層面に塗工ムラを生じやすく、インクが記録面方向
に広がる比率が多くなり、結果として記録ドットは、真
円からはずれた形状となる。更に、原紙への浸透も不規
則となり、インクの滲みが現れる。The ink jet recording sheet of the present invention is obtained by slightly coating the ink receiving layer on the base paper within the scope of the present invention as described above, and reflects the uniformity of the base paper to obtain a smooth and uniform ink. It can be a receiving layer. When the ink receiving layer is uniformly coated, when the ink is applied to the ink receiving layer surface using an ink jet printer, the ink receiving layer surface is uniformly coated, so the ink in the ink receiving layer surface direction is Without spreading
This is because a recording dot close to a perfect circle can be expressed, and surplus ink permeates from the ink receiving layer surface in the thickness direction of the base paper. On the other hand, when the base paper is out of the range of the present invention, coating unevenness easily occurs on the surface of the ink receiving layer, and the ratio of ink spreading in the recording surface direction increases, and as a result, the recording dots deviate from a perfect circle. Further, the penetration into the base paper becomes irregular, and ink bleeding appears.
【００２８】本発明のインクジェット記録シートにおい
て、インク受理層面は、非球状カチオン性コロイダルシ
リカを主体とする組成物を使用することで、原紙面の平
滑性を反映した面とすることができる。非球状カチオン
性コロイダルシリカの粒子径について、原紙を形成する
パルプ繊維と比較すると、パルプ繊維の繊維幅が数１０
μｍのオーダーに対して、該コロイダルシリカの最大短
径は、５０ｎｍ以下、好ましくは３０ｎｍ以下である。
最大短径が微小であればあるほど、原紙面への塗工が均
一となり好ましい。又、該コロイダルシリカの長さは、
３００ｎｍ以下、好ましくは１００ｎｍ以下である。こ
れら非球状カチオン性コロイダルシリカは、通常水中に
一次粒子径を維持した状態でコロイド状に分散している
ものを使用する。In the ink jet recording sheet of the present invention, the surface of the ink receiving layer can be made to reflect the smoothness of the base paper surface by using a composition mainly composed of non-spherical cationic colloidal silica. Regarding the particle size of the non-spherical cationic colloidal silica, the fiber width of the pulp fiber is several tens of tens in comparison with the pulp fiber forming the base paper.
For the order of μm, the maximum minor axis of the colloidal silica is 50 nm or less, preferably 30 nm or less.
The smaller the maximum minor axis, the more uniform the coating on the base paper surface, which is preferable. The length of the colloidal silica is
It is 300 nm or less, preferably 100 nm or less. These non-spherical cationic colloidal silicas are usually those which are dispersed in water in a colloidal state while maintaining the primary particle diameter.
【００２９】本発明に用いられる非球状カチオン性コロ
イダルシリカとしては、該コロイダルシリカの表面をカ
チオン変性剤である金属酸化水和物を使用して被覆し、
カチオン変性にしたものである。本発明で言う非球状と
は、実質的に球状でないという意味であり、針状、柱
状、数珠状、棒状、板状、塊状、繊維状、紡錘状等各種
形態があるが、特に針状或は繊維状のものが好ましく用
いられる。As the non-spherical cationic colloidal silica used in the present invention, the surface of the colloidal silica is coated with a metal oxide hydrate as a cation modifier,
It is one modified by cation. The non-spherical as referred to in the present invention means that it is not substantially spherical, and has various shapes such as a needle shape, a column shape, a bead shape, a rod shape, a plate shape, a lump shape, a fiber shape, and a spindle shape. A fibrous material is preferably used.
【００３０】又、本発明のインクジェット記録シートに
用いられる非球状カチオン性コロイダルシリカとして
は、酸化アルミニウム水和物、酸化ジルコニウム水和
物、酸化錫水和物等の金属酸化水和物からなるカチオン
変性剤で被覆された該コロイダルシリカが好ましく用い
られ、特に酸化アルミニウム水和物でカチオン変性され
たものが好ましく用いられる。カチオン変性の方法とし
ては、米国特許第３，００７，８７８号明細書、特公昭
４７−２６９５９号公報等に記載の方法で行うことが出
来る。The non-spherical cationic colloidal silica used in the ink jet recording sheet of the present invention includes a cation comprising a metal oxide hydrate such as aluminum oxide hydrate, zirconium oxide hydrate and tin oxide hydrate. The colloidal silica coated with a modifying agent is preferably used, and in particular, a cation modified with aluminum oxide hydrate is preferably used. The cation can be modified by the method described in U.S. Pat. No. 3,007,878, Japanese Patent Publication No. 47-26959, and the like.
【００３１】本発明のインクジェット記録シートに用い
られる非球状カチオン性コロイダルシリカにおいて、カ
チオン変性剤である金属酸化水和物の被覆量としては、
シリカ（ＳｉＯ2換算）に対して、金属酸化物換算で１
〜３０重量％の範囲が有用である。カチオン変性剤の被
覆量が１重量％と少なすぎると、インクジェット記録用
シ−トのインク記録された画像の耐水性が顕著に悪化
し、逆に多過ぎると被覆面の皮膜物性が脆弱となってヒ
ビ割れを起こし、パルプ繊維表面の露呈が目立ってく
る。該被覆量として、好ましくは２．５〜２５重量％、
更に好ましくは５〜２０重量％である。又、非球状カチ
オン性コロイダルシリカの分散液中には、コロイド安定
剤等の目的で酢酸、クエン酸、硫酸、リン酸等の酸成分
を含有してもよい。In the non-spherical cationic colloidal silica used in the ink jet recording sheet of the present invention, the coating amount of the metal oxide hydrate as the cation modifier is as follows.
1 compared to silica (SiO 2 equivalent) in terms of metal oxide
A range of -30% by weight is useful. If the coating amount of the cationic modifier is too low, such as 1% by weight, the water resistance of the ink-recorded image of the ink-jet recording sheet will be remarkably deteriorated, and if it is too high, the physical properties of the coating surface will be weak. Cracks occur, and the surface of the pulp fiber is exposed. The coating amount is preferably 2.5 to 25% by weight,
More preferably, it is 5 to 20% by weight. The dispersion of the non-spherical cationic colloidal silica may contain an acid component such as acetic acid, citric acid, sulfuric acid, and phosphoric acid for the purpose of a colloid stabilizer.
【００３２】本発明のインクジェット記録シートには、
非球状カチオン性コロイダルシリカに加えて、超微粒子
無機顔料を併用することができる。超微粒子無機顔料と
しては、以下のものを例示することができる。例えば、
シリカ（コロイダルシリカ）、アルミナ或はアルミナ水
和物（アルミナゾル、コロイダルアルミナ、カチオン性
アルミニウム酸化物又はその水和物、疑ベーマイト
等）、表面処理カチオン性コロイダルシリカ、珪酸アル
ミニウム、珪酸マグネシウム、炭酸マグネシウム等が挙
げられ、一次粒子が多孔性であれば、なお好ましいが、
非多孔性であっても塗工液調製時に凝集したり、塗工乾
燥時に更に凝集し、パルプ繊維表面に多孔性の表面被覆
面が形成されることが好ましい。特に、本発明において
は、原紙表面のパルプ繊維１本１本に繊維の幅の数１０
０分の１以下の平均粒子径を有する非球状カチオン性コ
ロイダルシリカを用いてパルプ繊維自体を被覆すること
が好ましい。In the ink jet recording sheet of the present invention,
In addition to the non-spherical cationic colloidal silica, an ultrafine inorganic pigment can be used in combination. Examples of the ultrafine inorganic pigment include the following. For example,
Silica (colloidal silica), alumina or alumina hydrate (alumina sol, colloidal alumina, cationic aluminum oxide or its hydrate, pseudoboehmite, etc.), surface-treated cationic colloidal silica, aluminum silicate, magnesium silicate, magnesium carbonate And the like, if the primary particles are porous, more preferably,
Even if it is non-porous, it is preferable that it coagulates at the time of preparation of the coating liquid or coagulates at the time of coating and drying to form a porous surface coating surface on the pulp fiber surface. In particular, in the present invention, each pulp fiber on the base paper surface has a width of several tens of fibers.
It is preferable to coat the pulp fiber itself with a non-spherical cationic colloidal silica having an average particle size of 1/0 or less.
【００３３】更に、超微粒子無機顔料と併用することの
できる無機顔料は、従来公知の如何なるものも用いるこ
とができる。例えば、軽質炭酸カルシウム、重質炭酸カ
ルシウム、カオリン、タルク、硫酸カルシウム、硫酸バ
リウム、二酸化チタン、酸化亜鉛、硫化亜鉛、炭酸亜
鉛、サチンホワイト、珪酸アルミニウム、ケイソウ土、
珪酸カルシウム、合成非晶質シリカ、水酸化アルミニウ
ム、リトポン、ゼオライト、加水ハロイサイト、水酸化
マグネシウム等を挙げることができる。これら該無機顔
料の中でも、多孔性無機顔料が好ましく、多孔性合成非
晶質シリカ、多孔性炭酸マグネシウム、多孔性アルミナ
等が挙げられ、特に細孔容積の大きい多孔性合成非晶質
シリカが好ましい。又、スチレン系プラスチックピグメ
ント、アクリル系プラスチックピグメント、ポリエチレ
ン、マイクロカプセル、尿素樹脂、メラミン樹脂等の有
機顔料等を上記超微粒子無機顔料と共に併用することも
できる。Further, as the inorganic pigment which can be used in combination with the ultrafine inorganic pigment, any conventionally known inorganic pigment can be used. For example, light calcium carbonate, heavy calcium carbonate, kaolin, talc, calcium sulfate, barium sulfate, titanium dioxide, zinc oxide, zinc sulfide, zinc carbonate, satin white, aluminum silicate, diatomaceous earth,
Examples thereof include calcium silicate, synthetic amorphous silica, aluminum hydroxide, lithopone, zeolite, hydrohaloysite, and magnesium hydroxide. Among these inorganic pigments, porous inorganic pigments are preferable, and porous synthetic amorphous silica, porous magnesium carbonate, porous alumina, and the like can be mentioned. Particularly, porous synthetic amorphous silica having a large pore volume is preferable. . Further, organic pigments such as styrene-based plastic pigment, acrylic-based plastic pigment, polyethylene, microcapsules, urea resin, melamine resin and the like can be used together with the ultrafine inorganic pigment.
【００３４】インク受理層を塗工する上で、非球状カチ
オン性コロイダルシリカと共に使用されるバインダーと
して、例えば、ポリビニルアルコール、酢酸ビニル、酸
化澱粉、エーテル化澱粉、カルボキシメチルセルロー
ス、ヒドロキシエチルセルロース等のセルロース誘導
体、カゼイン、ゼラチン、大豆蛋白、シリル変性ポリビ
ニルアルコール等；無水マレイン酸樹脂、スチレン−ブ
タジエン共重合体、メチルメタクリレート−ブタジエン
共重合体等の共役ジエン系共重合体ラテックス；アクリ
ル酸エステル及びメタクリル酸エステルの重合体又は共
重合体、アクリル酸及びメタクリル酸の重合体又は共重
合体等のアクリル系重合体ラテックス；エチレン酢酸ビ
ニル共重合体等のビニル系重合体ラテックス；或いはこ
れらの各種重合体のカルボキシル基等の官能基含有単量
体による官能基変性重合体ラテックス；メラミン樹脂、
尿素樹脂等の熱硬化合成樹脂系等の水性バインダー；ポ
リメチルメタクリレート、ポリウレタン樹脂、不飽和ポ
リエステル樹脂、塩化ビニル−酢酸ビニルコポリマー、
ポリビニルブチラール、アルキッド樹脂等の合成樹脂系
バインダーを挙げることができ、少なくとも１種以上で
使用することができる。又、従来公知の染料を定着する
目的として添加するカチオン性樹脂を併用することもで
きる。In coating the ink receiving layer, as a binder used together with the non-spherical cationic colloidal silica, for example, a cellulose derivative such as polyvinyl alcohol, vinyl acetate, oxidized starch, etherified starch, carboxymethyl cellulose, hydroxyethyl cellulose, etc. , Casein, gelatin, soy protein, silyl-modified polyvinyl alcohol, etc .; conjugated diene copolymer latex such as maleic anhydride resin, styrene-butadiene copolymer, methyl methacrylate-butadiene copolymer; acrylate and methacrylate Acrylic polymer latex such as polymer or copolymer of acrylic acid and methacrylic acid; Vinyl polymer latex such as ethylene-vinyl acetate copolymer; Functional group-modified polymer latex according to the functional group-containing monomers such as Bokishiru group; melamine resins,
Aqueous binder such as thermosetting synthetic resin such as urea resin; polymethyl methacrylate, polyurethane resin, unsaturated polyester resin, vinyl chloride-vinyl acetate copolymer,
Synthetic resin binders such as polyvinyl butyral and alkyd resin can be mentioned, and at least one kind can be used. Further, a cationic resin added for the purpose of fixing a conventionally known dye can also be used in combination.
【００３５】バインダーの総量は、目的とするインクジ
ェット記録シートの特性に合わせて、適宜調整すること
が出来るが、一般には、顔料１００重量％に対して、５
〜６０重量％である。更に、その他の添加剤として、顔
料分散剤、増粘剤、流動性改良剤、消泡剤、抑泡剤、離
型剤、発泡剤、浸透剤、着色染料、着色顔料、蛍光増白
剤、紫外線吸収剤、酸化防止剤、防腐剤、防バイ剤、耐
水化剤、湿潤紙力増強剤、乾燥紙力増強剤等を適宜配合
することもできる。The total amount of the binder can be appropriately adjusted in accordance with the desired properties of the target ink jet recording sheet.
６０60% by weight. Further, as other additives, a pigment dispersant, a thickener, a fluidity improver, an antifoaming agent, a foam inhibitor, a release agent, a foaming agent, a penetrant, a coloring dye, a coloring pigment, a fluorescent brightening agent, An ultraviolet absorber, an antioxidant, an antiseptic, an antibacterial agent, a waterproofing agent, a wet paper strength enhancer, a dry paper strength enhancer, and the like can be appropriately blended.
【００３６】本発明において、インク受理層を塗工する
方法は、塗工或は含浸の方法があるが、インク受理層面
の塗工量については、特に限定するものではない。通
常、普通紙ライクを指向する場合には、０．５〜５ｇ／
ｍ2が好ましいが、これ以上塗工してもよい。In the present invention, the method for coating the ink receiving layer includes a coating method and an impregnating method, but the coating amount on the ink receiving layer surface is not particularly limited. Normally, when oriented to plain paper like, 0.5 to 5 g /
Although m 2 is preferable, coating may be performed further.
【００３７】本発明のインクジェット記録シートにおい
て、上述した原紙に、そのままインク受理層を設けても
良いし、平坦化をコントロールする目的で、マシンカレ
ンダー、ＴＧカレンダー、ソフトカレンダー等のカレン
ダー装置を使用して、インク受理層を設けても良い。In the ink jet recording sheet of the present invention, an ink receiving layer may be directly provided on the above-mentioned base paper, or a calendar device such as a machine calendar, a TG calendar, or a soft calendar may be used for the purpose of controlling flattening. Thus, an ink receiving layer may be provided.
【００３８】インク受理層を塗工する方法としては、各
種ブレードコータ、ロールコータ、エアーナイフコー
タ、バーコータ、ロッドコータ、ゲートロールコータ、
カーテンコータ、ショートドウェルコータ、グラビアコ
ータ、フレキソグラビアコータ、サイズプレス等の各種
装置をオンマシン或はオフマシンで用いることができ
る。しかし、本発明においては、特にサイズプレス、ロ
ッドコータ、ゲートロールコータ、エアーナイフコータ
が好ましい。又、塗工後には、マシンカレンダー、ＴＧ
カレンダー、スーパーカレンダー、ソフトカレンダー等
のカレンダーを用いて仕上げても良い。As a method for coating the ink receiving layer, various blade coaters, roll coaters, air knife coaters, bar coaters, rod coaters, gate roll coaters,
Various devices such as a curtain coater, a short dwell coater, a gravure coater, a flexographic gravure coater, and a size press can be used on-machine or off-machine. However, in the present invention, a size press, a rod coater, a gate roll coater, and an air knife coater are particularly preferred. After coating, machine calendar, TG
The finishing may be performed using a calendar such as a calendar, a super calendar, and a soft calendar.
【００３９】本発明で云う水性インクとは、下記の着色
剤、液媒体、その他の添加剤からなる記録液体である。
着色剤としては、直接染料、酸性染料、塩基性染料、反
応性染料或は食品用色素等の水溶性染料が挙げられる。The aqueous ink referred to in the present invention is a recording liquid comprising the following colorant, liquid medium, and other additives.
Examples of the coloring agent include a direct dye, an acid dye, a basic dye, a reactive dye, and a water-soluble dye such as a food colorant.
【００４０】水性インクの溶媒としては、水及び水溶性
の各種有機溶剤、例えば、メチルアルコール、エチルア
ルコール、ｎ−プロピルアルコール、イソプロピルアル
コール、ｎ−ブチルアルコール、sec−ブチルアルコー
ル、tert−ブチルアルコール、イソブチルアルコール等
の炭素数１〜４のアルキルアルコール類；ジメチルホル
ムアミド、ジメチルアセトアミド等のアミド類；アセト
ン、ジアセトンアルコール等のケトン又はケトンアルコ
ール類；テトラヒドロフラン、ジオキサン等のエーテル
類；ポリエチレングリコール、ポリプロピレングリコー
ル等のポリアルキレングリコール類；エチレングリコー
ル、プロピレングリコール、ブチレングリコール、トリ
エチレングリコール、1,2,6 −ヘキサントリオール、チ
オジグリコール、ヘキシレングリコール、ジエチレング
リコール等のアルキレン基が２〜６個のアルキレングリ
コール類；グリセリン、エチレングリコールメチルエー
テル、ジエチレングリコールメチル（又はエチル）エー
テル、トリエチレングリコール、モノメチルエーテル等
の多価アルコールの低級アルキルエーテル類等が挙げら
れる。これらの多くの水溶性有機溶剤の中でも、ジエチ
レングリコール等の多価アルコール、トリエチレングリ
コールモノメチルエーテル、トリエチレングリコールモ
ノエチルエーテル等の多価アルコールの低級アルキルエ
ーテルが好ましい。その他の添加剤としては、例えば、
ＰＨ調節剤、金属封鎖剤、防カビ剤、粘度調整剤、表面
張力調整剤、湿潤剤、界面活性剤、及び防錆剤等が挙げ
られる。As the solvent for the aqueous ink, water and various water-soluble organic solvents such as methyl alcohol, ethyl alcohol, n-propyl alcohol, isopropyl alcohol, n-butyl alcohol, sec-butyl alcohol, tert-butyl alcohol, Alkyl alcohols having 1 to 4 carbon atoms such as isobutyl alcohol; amides such as dimethylformamide and dimethylacetamide; ketones or ketone alcohols such as acetone and diacetone alcohol; ethers such as tetrahydrofuran and dioxane; polyethylene glycol and polypropylene glycol Polyalkylene glycols such as ethylene glycol, propylene glycol, butylene glycol, triethylene glycol, 1,2,6-hexanetriol, thiodiglycol, hexyl Alkylene glycols having 2 to 6 alkylene groups such as lene glycol and diethylene glycol; lower alkyl ethers of polyhydric alcohols such as glycerin, ethylene glycol methyl ether, diethylene glycol methyl (or ethyl) ether, triethylene glycol and monomethyl ether; Is mentioned. Among these many water-soluble organic solvents, polyhydric alcohols such as diethylene glycol, and lower alkyl ethers of polyhydric alcohols such as triethylene glycol monomethyl ether and triethylene glycol monoethyl ether are preferable. As other additives, for example,
Examples include a pH adjuster, a metal sequestering agent, a fungicide, a viscosity adjuster, a surface tension adjuster, a wetting agent, a surfactant, and a rust inhibitor.
【００４１】本発明におけるインクジェット記録シート
は、インクジェット記録シートとしての使用に留まら
ず、記録時に液状であるインクを使用するどのような記
録シートとして用いることもできる。例えば、熱溶融性
物質、染顔料等を主成分とする熱溶融性インクを樹脂フ
ィルム、高密度紙、合成紙などの薄い支持体上に塗布し
たインクシートを、その裏面より加熱し、インクを溶融
させて転写する熱転写記録用受像シート、熱溶融性イン
クを加熱溶融して微小液滴化、飛翔記録するインクジェ
ット記録シート、油溶性染料を溶媒に溶解したインクを
用いたインクジェット記録シート、光重合型モノマー及
び無色又は有色の染顔料を内包したマイクロカプセルを
用いた感光感圧型ドナーシートに対応する受像シート等
が挙げられる。The ink-jet recording sheet of the present invention can be used not only as an ink-jet recording sheet but also as any recording sheet using a liquid ink during recording. For example, a heat-fusible substance, a heat-fusible ink containing a dye or pigment as a main component, is applied on a thin support such as a resin film, high-density paper, or synthetic paper, and then heated from the back surface of the ink sheet, and the ink is heated. An image-receiving sheet for thermal transfer recording, which is melted and transferred, an ink-jet recording sheet, which heats and melts a hot-melt ink to form fine droplets, and performs flight recording; an ink-jet recording sheet, which uses an ink in which an oil-soluble dye is dissolved in a solvent; And an image receiving sheet corresponding to a photosensitive pressure-sensitive donor sheet using microcapsules containing a type monomer and a colorless or colored dye or pigment.
【００４２】これらの記録シートの共通点は、記録時に
インクが液体状態である点である。液状インクは、硬
化、固化又は定着までに、記録シートのインク受理層の
深さ方向又は水平方向に対して浸透又は拡っていく。上
述した各種記録シートは、それぞれの方式に応じた吸収
性を必要とするもので、本発明のインクジェット記録シ
ートを上述した各種の記録シートとして利用しても何ら
制限しない。更に、複写機・プリンター等に広く使用さ
れている電子写真記録方式のトナーを加熱定着する記録
シートとして、本発明におけるインクジェット記録シー
トを使用することもできる。The common feature of these recording sheets is that the ink is in a liquid state at the time of recording. The liquid ink permeates or spreads in the depth direction or the horizontal direction of the ink receiving layer of the recording sheet until it hardens, solidifies or fixes. The above-mentioned various recording sheets require absorptivity according to each system, and there is no limitation even if the inkjet recording sheet of the present invention is used as the above-mentioned various recording sheets. Furthermore, the ink jet recording sheet of the present invention can be used as a recording sheet for heating and fixing an electrophotographic recording toner widely used in a copying machine, a printer, and the like.
【００４３】[0043]
【作用】本発明のインクジェット記録シートにおいて、
重量平均繊維長が０．５５〜０．６５ｍｍであり、且つ
道管要素の長さ／幅が２．０以下である広葉樹パルプか
ら構成されたインクジェット記録シート用原紙は、剛直
度と平滑性が優れ、又、広葉樹パルプの繊維粗度が、
７．０〜１０．０ｍｇ／１００ｍである場合に、特に優
れた効果が得られ、該原紙上に主成分として非球状カチ
オン性コロイダルシリカからなるインク受理層を塗工す
ることで、インク受理層塗液の塗工性に優れ、インク受
理層面の塗工ムラがなく、且つインクの吸収性や鮮明性
に優れ、剛直性を有する微塗工タイプのインクジェット
記録シートとすることができる。In the ink jet recording sheet of the present invention,
Base paper for an ink jet recording sheet composed of hardwood pulp having a weight average fiber length of 0.55 to 0.65 mm and a length / width of a vascular element of 2.0 or less has rigidity and smoothness. Excellent, and the fiber roughness of hardwood pulp,
When the content is 7.0 to 10.0 mg / 100 m, a particularly excellent effect is obtained. By coating the ink receiving layer composed of non-spherical cationic colloidal silica as a main component on the base paper, the ink receiving layer An ink jet recording sheet of a fine coating type having excellent coating properties of the coating liquid, no coating unevenness on the surface of the ink receiving layer, excellent ink absorbency and clearness, and having rigidity can be obtained.
【００４４】[0044]
【実施例】以下に、本発明の実施例を挙げて説明する
が、本発明はこれらの例に限定されるものではない。
又、実施例において示す「部」及び「％」は、特に明示
しない限り重量部及び重量％を示す。EXAMPLES The present invention will be described below with reference to examples of the present invention, but the present invention is not limited to these examples.
Further, “parts” and “%” shown in Examples are parts by weight and% by weight unless otherwise specified.
【００４５】実施例１〜３ ［原紙の作製］ユーカリ材より製造したＢＫＰをダブル
ディスクリファイナーの回転数を変化させて叩解し、カ
ナダ標準濾水度が３３０ｍｌで、重量平均繊維長が０．
５５ｍｍ（実施例１）、０．６０ｍｍ（実施例２）、並
びに０．６５ｍｍ（実施例３）と異なるパルプを得た。
なお、このユーカリパルプの道管要素の長さ／幅は１．
５、繊維粗度は８．１ｍｇ／１００ｍであった。叩解パ
ルプそれぞれ１００部に対し、カチオン澱粉（ケイト
Ｆ、王子ナショナル社製）を０．７部、及びアルキルケ
テンダイマーサイズ剤（ハーコン１１−２、ディック−
ハーキュレス社製）を０．１部添加し、長網抄紙機で坪
量８５ｇ／ｍ2からなる３種のインクジェット記録シー
ト用原紙を製造した。Examples 1 to 3 [Preparation of base paper] BKP produced from eucalyptus wood was beaten by changing the number of revolutions of a double disc refiner, and the Canadian standard freeness was 330 ml and the weight average fiber length was 0.1.
Pulp different from 55 mm (Example 1), 0.60 mm (Example 2) and 0.65 mm (Example 3) was obtained.
The length / width of the vascular element of this eucalyptus pulp is 1.
5. The fiber roughness was 8.1 mg / 100 m. 0.7 parts of cationic starch (Kate F, manufactured by Oji National Co., Ltd.) and alkyl ketene dimer sizing agent (Harcon 11-2, Dick-
0.1 part of Hercules Co., Ltd.), and three types of base paper for ink jet recording sheet having a basis weight of 85 g / m 2 were produced by a fourdrinier paper machine.
【００４６】［インクジェット記録シートの作製］上記
により作製した３種のインクジェット記録シート用原紙
に、インク受理層組成物として、針状のコロイドダルシ
リカをシリカ（ＳｉＯ2 換算）に対しＡｌ2Ｏ3換算で約
６．２重量％の酸化アルミニウム水和物により変性した
針状のカチオン変性コロイダルシリカの１０％水分散液
（粒径；幅１０〜２０ｎｍ×長さ５０〜２００ｎｍ）１
０００部、接着剤としてポリビニルアルコールの１０％
水溶液（ＰＶＡ１１７、クラレ社製）３００部、染料定
着剤としてカチオン性樹脂の６０％水溶液（ポリフィッ
クス６０１、カチオン荷電量６．９ｍｅｑ．／ｇ、昭和
高分子社製）５０部を主成分とする固形分濃度１０％の
水性分散液をロッドコータを用いて、塗工速度３００ｍ
／分で乾燥固型分１ｇ／ｍ2となるように塗工、乾燥
し、カレンダー仕上げして実施例１〜３のインクジェッ
ト記録シートを作製した。[Preparation of Ink-Jet Recording Sheet] In the three kinds of base paper for ink-jet recording sheet prepared as described above, acicular colloidal dal silica was added as an ink-receiving layer composition to silica (SiO 2 equivalent) Al 2 O 3. A 10% aqueous dispersion of acicular cation-modified colloidal silica modified with about 6.2% by weight of aluminum oxide hydrate (particle size: width 10 to 20 nm × length 50 to 200 nm) 1
000 parts, 10% of polyvinyl alcohol as adhesive
A main component is 300 parts of an aqueous solution (PVA117, manufactured by Kuraray Co., Ltd.) and 50 parts of a 60% aqueous solution of a cationic resin as a dye fixing agent (Polyfix 601, 6.9 meq./g of cationic charge, manufactured by Showa Kogyo KK). An aqueous dispersion having a solid concentration of 10% was applied using a rod coater at a coating speed of 300 m.
/ Min, and dried and solidified to give a dry solid content of 1 g / m 2 , followed by calendering to produce inkjet recording sheets of Examples 1 to 3.
【００４７】比較例１及び比較例２ 実施例１において、広葉樹パルプの重量平均繊維長を
０．５３ｍｍ（比較例１）及び０．６８ｍｍ（比較例
２）に変化させる以外は、実施例１と同様にして比較例
１及び比較例２のインクジェット記録シートを製造し
た。Comparative Example 1 and Comparative Example 2 The procedure of Example 1 was repeated except that the weight-average fiber length of the hardwood pulp was changed to 0.53 mm (Comparative Example 1) and 0.68 mm (Comparative Example 2). In the same manner, the ink jet recording sheets of Comparative Examples 1 and 2 were produced.
【００４８】実施例４及び実施例５ ［原紙の作製］実施例１において、ユーカリパルプの代
わりに道管要素の長さ／幅が１．３で繊維粗度が９．５
ｍｇ／１００ｍであるアルビジア（実施例４）、或は道
管要素の長さ／幅が２．０で繊維粗度が９．０のホワイ
トオーク（実施例５）を用い、叩解により重量平均繊維
長を０．６０ｍｍに調節する以外は、実施例１と同様に
して実施例４及び実施例５のインクジェット記録シート
用原紙を得た。Examples 4 and 5 [Preparation of base paper] In Example 1, instead of eucalyptus pulp, the length / width of the vessel element was 1.3 and the fiber roughness was 9.5.
mg / 100 m of Albizia (Example 4) or white oak with a length / width of vascular element of 2.0 and fiber roughness of 9.0 (Example 5), and beaten to obtain a weight-average fiber. Except that the length was adjusted to 0.60 mm, base papers for ink jet recording sheets of Examples 4 and 5 were obtained in the same manner as in Example 1.
【００４９】［インクジェット記録シートの作製］上記
により作製した実施例４及び実施例５のインクジェット
記録シート用原紙に、インク受理層組成物として、柱状
のカチオン性コロイダルシリカの１０％水分散液（粒
径；幅４０ｎｍ×長さ１００〜３００ｎｍ）１０００
部、接着剤としてポリビニルアルコールの１０％水溶液
（ＰＶＡ１１７、クラレ社製）３００部、染料定着剤と
してカチオン性樹脂の６０％水溶液（ポリフィックス６
０１、カチオン荷電量６．９ｍｅｑ．／ｇ、昭和高分子
社製）５０部を主成分とする固形分濃度１５％の水性分
散液をエアーナイフコータを用いて、塗工速度３００ｍ
／分で乾燥固型分３ｇ／ｍ2となるように塗工、乾燥
し、カレンダー仕上げして実施例４及び実施例５のイン
クジェット記録シートを作製した。[Preparation of Inkjet Recording Sheet] A 10% aqueous dispersion (particles) of columnar cationic colloidal silica was used as an ink receiving layer composition on the base paper for ink jet recording sheets of Examples 4 and 5 prepared as described above. Diameter; width 40 nm x length 100-300 nm) 1000
Parts, 300 parts of a 10% aqueous solution of polyvinyl alcohol (PVA117, manufactured by Kuraray) as an adhesive, and 60% aqueous solution of a cationic resin (Polyfix 6) as a dye fixing agent
01, cation charge amount of 6.9 meq. / G, manufactured by Showa Polymer Co., Ltd.) 50 parts by weight of an aqueous dispersion having a solid content of 15% using an air knife coater at a coating speed of 300 m.
/ Min, and dried and solidified to give a dry solid content of 3 g / m 2 , followed by calendering to produce inkjet recording sheets of Examples 4 and 5.
【００５０】比較例３及び比較例４ 実施例４において、パルプとして道管要素の長さ／幅が
３．１で繊維粗度が９．０のカバ（比較例３）、或は道
管要素の長さ／幅が４．６で繊維粗度が６．９のメープ
ル（比較例４）から製造したパルプを用いる以外は、実
施例４と同様にして比較例３及び比較例４のインクジェ
ット記録シート用原紙を得た。次いで、実施例４と同様
にして比較例３及び比較例４のインクジェット記録シー
トを製造した。COMPARATIVE EXAMPLE 3 AND COMPARATIVE EXAMPLE 4 A pulp having a length / width of 3.1 and a fiber roughness of 9.0 as a pulp (Comparative Example 3); Ink jet recording of Comparative Examples 3 and 4 in the same manner as in Example 4 except that pulp manufactured from maple having a length / width of 4.6 and a fiber roughness of 6.9 (Comparative Example 4) was used. A sheet base paper was obtained. Subsequently, the ink jet recording sheets of Comparative Examples 3 and 4 were manufactured in the same manner as in Example 4.
【００５１】実施例６〜９ 実施例４において、パルプとして、ユーカリ・グランデ
ィス、ユーカリ・マクラータ等ユーカリ属の中での種の
違いにより、道管要素の長さ／幅が１．２〜１．５、繊
維粗度が６．５ｍｇ／１００ｍ（実施例６）、７．０ｍ
ｇ／１００ｍ（実施例７）、１０．０ｍｇ／１００ｍ
（実施例８）、並びに１１．０ｍｇ／１００ｍ（実施例
９）と異なるユーカリパルプを用いる以外は、実施例４
と同様にして実施例６〜９のインクジェット記録シート
用原紙を得た。次いで、実施例４と同一のインク受理層
組成物を用い、実施例４と同様にして、実施例６〜９の
インクジェット記録シートを製造した。Examples 6 to 9 In Example 4, the length / width of the vascular element was 1.2 to 1.1 depending on the species of eucalyptus such as Eucalyptus grandis and Eucalyptus maculata as pulp. 5. Fiber roughness is 6.5 mg / 100m (Example 6), 7.0m
g / 100m (Example 7), 10.0mg / 100m
Example 8 and Example 4 except that eucalyptus pulp different from 11.0 mg / 100 m (Example 9) was used.
In the same manner as in the above, base papers for ink jet recording sheets of Examples 6 to 9 were obtained. Next, using the same ink receiving layer composition as in Example 4, the ink jet recording sheets of Examples 6 to 9 were produced in the same manner as in Example 4.
【００５２】比較例５ 実施例４で作製したインクジェット記録シート用原紙を
用い、インク受理層組成物として、球状のコロイダルシ
リカの４０％水分散液（一次粒子径３００±３０ｎｍ）
２５０部、接着剤としてポリビニルアルコールの水溶液
（ＰＶＡ１１７、クラレ社製）３００部、染料定着剤と
してカチオン性樹脂の６０％水溶液（ポリフィックス６
０１、カチオン荷電量６．９ｍｅｑ．／ｇ、昭和高分子
社製）５０部を主成分とする固形分濃度１０％の水性分
散液をゲートロールコータを用いて、塗工速度３００ｍ
／分で乾燥固型分２ｇ／ｍ2となるように塗工、乾燥
し、カレンダー仕上げしてインクジェット記録シートを
作製した。Comparative Example 5 A 40% aqueous dispersion of spherical colloidal silica (primary particle diameter 300 ± 30 nm) was used as the ink receiving layer composition, using the base paper for an ink jet recording sheet prepared in Example 4.
250 parts, aqueous solution of polyvinyl alcohol (PVA117, manufactured by Kuraray) as an adhesive, 300 parts, 60% aqueous solution of a cationic resin as a dye fixing agent (Polyfix 6)
01, cation charge amount of 6.9 meq. / G, manufactured by Showa Polymer Co., Ltd.) 50 parts by weight of an aqueous dispersion having a solid content of 10% using a gate roll coater at a coating speed of 300 m
/ Min, and dried and solid-coated at 2 g / m 2 to obtain an ink jet recording sheet.
【００５３】以上、実施例１〜９及び比較例１〜５で作
製したインクジェット記録シートについて、下記の評価
方法により評価し、その結果をまとめて表１に示す。な
お、実験に供試した各樹種の道管要素含有量は、いずれ
も５〜７重量％であり、極端な差は認められなかった。The ink jet recording sheets prepared in Examples 1 to 9 and Comparative Examples 1 to 5 were evaluated by the following evaluation methods. The results are shown in Table 1. The vascular element content of each tree species used in the experiment was 5 to 7% by weight, and no extreme difference was observed.
【００５４】［地合］地合は、原紙地合の視覚評価結果
であり、最も均一なものをＡ、不均一なものをＣとする
３段階に評価した。[Formation] The formation is a visual evaluation result of the base paper formation, and was evaluated in three grades, where A is the most uniform and C is the non-uniform one.
【００５５】［Ｒａ］Ｒａは、ＪＩＳ Ｂ ０６０１に
準拠して触針式表面粗さ計を用いて測定した原紙の表面
粗さ（μｍ）の値である。数値が小さいほど微細な表面
の凹凸が少ないことを表す。[Ra] Ra is the value of the surface roughness (μm) of the base paper measured using a stylus type surface roughness meter in accordance with JIS B0601. The smaller the value, the smaller the fine surface irregularities.
【００５６】［平滑性］平滑性は、インク受理層と塗工
した後のインクジェット記録シートについて行った標準
見本に対する視覚評価の結果である。最も平滑性の優れ
たものをＡ、劣ったものをＤとして４段階に評価した。
平滑性の優れたインクジェット記録シート用原紙として
は、Ｃ以上（Ａ、Ｂ、Ｃ）、好ましくはＢ以上が必要で
ある。[Smoothness] Smoothness is a result of a visual evaluation of a standard sample performed on an ink jet recording sheet after coating with an ink receiving layer. The sample with the most excellent smoothness was evaluated as A, and the sample with the poorest smoothness was evaluated as D, in four grades.
The base paper for an ink jet recording sheet having excellent smoothness requires C or more (A, B, C), preferably B or more.
【００５７】［剛直性］剛直度は、ＪＩＳ Ｐ８１４３
に準拠して測定した、自重曲げ法によるインクジェット
記録シート用原紙の縦（ＭＤ）方向のこわさ測定値であ
る。インクジェット記録シートとしては、１００ｇ・ｃ
ｍ以上、好ましくは１１０ｇ・ｃｍ以上であることが好
ましい。[Rigidity] The rigidity is measured according to JIS P8143.
Is the stiffness measured in the machine direction (MD) of the base paper for ink jet recording sheet by the self-weight bending method, measured in accordance with the above formula. 100 g · c as an inkjet recording sheet
m or more, preferably 110 g · cm or more.
【００５８】［塗工性］塗工性は、原紙上に各種コータ
を用いて、インク受理層組成物を塗工速度３００ｍ／分
で塗工したインクジェット記録シートについて評価し
た。なお、評価基準として、塗工ムラが少ない順に表
し、Ａは特性が良好、Ｂは実用上問題ない範囲で良好、
Ｃは実用上問題ありとした。[Coatability] The coatability was evaluated on an ink jet recording sheet obtained by applying the ink receiving layer composition at a coating speed of 300 m / min on a base paper using various coaters. As evaluation criteria, coating unevenness is represented in ascending order, A is good in characteristics, B is good in a practically acceptable range,
C was regarded as having a practical problem.
【００５９】［インク吸収性及び鮮明性］インク吸収性
及び画像の鮮明性は、重色ベタ印字部分の境界、例え
ば、赤印字（マゼンタ＋イエロー）と緑印字（シアン＋
イエロー）の境界部分のインクのにじみ具合いを、目視
で判定した。赤印字部分と緑印字部分が重ならず、分離
している場合を特性良好とし、重なりが大きくなって黒
線状になる場合を特性不良とした。インク吸収性の悪い
ものは、著しく画像品位（画像の鮮明性）を損なうた
め、他の特性、例えば、画像濃度等が良くても、何等意
味をなさない。なお、評価基準として、Ａは特性が良
好、Ｂは実用上問題ない範囲で良好、Ｃは実用上問題あ
り、Ｄは特性が不良を示す。[Ink Absorbing Property and Sharpness] The ink absorbing property and the sharpness of the image are determined by the boundaries between the solid printing portions, for example, red printing (magenta + yellow) and green printing (cyan +
The bleeding condition of the ink at the boundary portion of (yellow) was visually determined. The case where the red printed portion and the green printed portion did not overlap and were separated was regarded as good characteristics, and the case where the overlap became large and became a black line was regarded as poor characteristics. A material having poor ink absorbability significantly impairs image quality (image clarity), so that even if other characteristics, for example, image density and the like are good, it has no meaning. As evaluation criteria, A shows good characteristics, B shows good results in practically acceptable range, C shows practical problems, and D shows poor characteristics.
【００６０】[0060]
【表１】 [Table 1]
【００６１】表１の結果、実施例１〜３を比較例１〜２
と比較することにより、重量平均繊維長が０．５５〜
０．６５ｍｍである広葉樹パルプを原紙に使用すること
により、地合と微細な凹凸の優れた原紙が得られ、イン
ク受理層塗工後のインクジェット記録シートの平滑性と
剛直度も優れていることが明らかである。重量平均繊維
長が０．５５ｍｍ未満の場合には、十分な剛直度が得ら
れていない。又、実施例４〜５を比較例３〜４と比較す
ることにより、繊維長が同一であっても、道管要素の長
さ／幅が２．０以下の場合に、微細な凹凸が少ない原紙
が得られ、インクジェット記録シートの平滑性も優れて
いることがわかる。更に、実施例６〜９から、繊維粗度
が７．０〜１０．０ｍｇ／１００ｍの場合、特に平滑性
と剛直度の優れたインクジェット記録シートの得られる
ことが明らかである。比較例５は、実施例４で作製した
インクジェット記録シート用原紙に、本発明外のインク
受理層組成物を使用した例であるが、他の特性は優れて
いるものの鮮明性に劣った。As shown in Table 1, Examples 1 to 3 were compared with Comparative Examples 1 and 2.
By comparison with, the weight average fiber length is 0.55 to
By using 0.65 mm hardwood pulp for the base paper, a base paper with excellent formation and fine irregularities can be obtained, and the smoothness and rigidity of the ink jet recording sheet after coating the ink receiving layer are also excellent. Is evident. When the weight average fiber length is less than 0.55 mm, sufficient rigidity is not obtained. In addition, by comparing Examples 4 to 5 with Comparative Examples 3 and 4, even when the fiber length is the same, when the length / width of the vascular element is 2.0 or less, there are few fine irregularities. It can be seen that a base paper was obtained, and the ink jet recording sheet was also excellent in smoothness. Further, from Examples 6 to 9, it is clear that when the fiber roughness is 7.0 to 10.0 mg / 100 m, an ink jet recording sheet having particularly excellent smoothness and rigidity can be obtained. Comparative Example 5 is an example in which the ink receiving layer composition other than the present invention was used for the base paper for the ink jet recording sheet prepared in Example 4, but the other characteristics were excellent, but the sharpness was poor.
【００６２】[0062]
【発明の効果】以上から、本発明のインクジェット記録
シート用原紙、即ち重量平均繊維長が０．５５〜０．６
５ｍｍであり、且つ道管要素の長さ／幅が２．０以下で
ある広葉樹パルプから構成される該原紙を用い、該原紙
上に、インク受理層を塗工したインクジェット記録シー
トは、インク受理層面の塗工ムラがなく、インクの吸収
性や鮮明性に優れ、剛直性のある微塗工タイプのインク
ジェット記録シートが得られた。As described above, the base paper for an ink jet recording sheet of the present invention, that is, the weight average fiber length is 0.55 to 0.6
An ink jet recording sheet having a base paper composed of hardwood pulp having a length / width of 5 mm or less and a length / width of a vascular element of 2.0 or less, and an ink receiving layer coated on the base paper is an ink receiving sheet. There was no unevenness in coating on the layer surface, excellent ink absorbency and sharpness, and a rigid coating type ink jet recording sheet having rigidity was obtained.
───────────────────────────────────────────────────── フロントページの続き (56)参考文献 特開 昭60−219084（ＪＰ，Ａ) 特開 平５−96844（ＪＰ，Ａ) 特開 昭60−219083（ＪＰ，Ａ) 特開 昭60−260377（ＪＰ，Ａ) 特開 平４−12880（ＪＰ，Ａ) 特開 平５−51469（ＪＰ，Ａ) 特開 平６−92011（ＪＰ，Ａ) (58)調査した分野(Int.Cl.7，ＤＢ名) B41M 5/00 ──────────────────────────────────────────────────続 き Continuation of the front page (56) References JP-A-60-219084 (JP, A) JP-A-5-96844 (JP, A) JP-A-60-219083 (JP, A) JP-A 60-19084 260377 (JP, A) JP-A-4-12880 (JP, A) JP-A-5-51469 (JP, A) JP-A-6-92011 (JP, A) (58) Fields investigated (Int. 7 , DB name) B41M 5/00
Claims (3)
ンク受理層を塗設してなるインクジェット記録シートに
おいて、該原紙が、重量平均繊維長が０．５５〜０．６
５ｍｍであり、且つ道管要素の長さ／幅が２．０以下で
ある広葉樹パルプから構成された該原紙であり、該イン
ク受理層組成物が、主成分として非球状カチオン性コロ
イダルシリカであることを特徴とするインクジェット記
録シート。1. An ink-jet recording sheet comprising a base paper and an ink receiving layer having a coating amount of 0.5 to 5 g / m 2 , wherein the base paper has a weight average fiber length of 0.1 g / m 2 . 55-0.6
The base paper is composed of hardwood pulp having a length / width of 5 mm or less and a length / width of a vascular element is 2.0 or less, and the ink receiving layer composition is a non-spherical cationic colloidal silica as a main component. An ink jet recording sheet, characterized in that:
０．０ｍｇ／１００ｍであることを特徴とする請求項１
記載のインクジェット記録シート。2. The hardwood pulp has a fiber roughness of 7.0-1.
2. The amount is 0.0 mg / 100 m.
The ink jet recording sheet according to the above.
針状或は繊維状のものであることを特徴とする請求項１
記載のインクジェット記録シート。3. The non-spherical cationic colloidal silica,
2. A needle-like or fibrous shape.
The ink jet recording sheet according to the above.