JPH0553250A - Cartridge for photographic film - Google Patents

Abstract

PURPOSE:To make the dropping strength of a cartridge for a photographic film comparable to or higher than that of a conventional one as well as to enable sure detection of the cartridge with a photoelectric tube and clear view of the photographic film housed in the cartridge from the outside. CONSTITUTION:This cartridge for a photographic film is made of a resin compsn. contg. 65-95wt.% propylene-ethylene random copolymer resin, 5-35wt.% propylene-ethylene block copolymer resin, 0.01-2.0wt.% nucleus forming agent, 0.01-10wt.% lubricity improving substance and 0.01-1.0wt.% antioxidant.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】本発明は、写真フイルム用容器に
関するものである。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a photographic film container.

【０００２】[0002]

【従来の技術】写真フイルムパトローネ用容器は、初期
の頃は写真フイルムに悪影響を与えず、防湿・ガスバリ
ヤ性に優れているので金属薄葉素材が用いられていた。
しかし、大量使用されるようになると製造が面倒であ
り、且つ高価であるので熱可塑性樹脂を用いて射出成形
により製造されるようになった。そして、この熱可塑性
樹脂としては、金属の代替品との考えから高剛性のもの
─すなわち、メルト・フローレイトが低いポリスチレン
樹脂やホモポリプロピレン樹脂─が用いられていた。2. Description of the Related Art A container for a photographic film cartridge has a metal thin film material in its early days because it does not adversely affect the photographic film and has excellent moisture-proof and gas barrier properties.
However, when it is used in a large amount, the production is troublesome and expensive, so that it is produced by injection molding using a thermoplastic resin. As the thermoplastic resin, a highly rigid one, that is, a polystyrene resin or a homopolypropylene resin having a low melt flow rate, has been used because it is considered as a substitute for a metal.

【０００３】しかし近年、衝撃強度の向上、剛性確保、
透明容器化による透明性の向上等の観点から、メルト・
フローレイトの低いプロピレン・エチレンランダム共重
合体樹脂が用いられるようになり、各種樹脂組成の写真
フイルムパトローネ用容器が提案されている。例えば、
本発明者は成形サイクルを短縮し、かつ成形故障を無く
すことができる容器本体を提案し（特開昭60−163045号
公報）、また成形直後の空送性を改良するとともに射出
成形性を改良するために、脂肪酸アミド系滑剤を0.05〜
１重量％含ませた容器本体を提案した（特開昭61−7394
7号公報）。However, in recent years, improvement of impact strength, securing of rigidity,
From the viewpoint of improving transparency by making it a transparent container,
A propylene / ethylene random copolymer resin having a low flow rate has come to be used, and containers for photographic film cartridges having various resin compositions have been proposed. For example,
The present inventor has proposed a container body capable of shortening the molding cycle and eliminating molding failures (Japanese Patent Laid-Open No. 60-163045), and also improves the idling property immediately after molding and the injection moldability. In order to
A container body containing 1% by weight has been proposed (Japanese Patent Laid-Open No. 61-7394).
No. 7).

【０００４】その他、写真フイルムパトローネ容器の形
態としては、容器本体と蓋とが別体で構成されているも
の以外に、容器本体と蓋とがヒンジで一体に形成されて
いる容器も提案されていた（特開昭63−223640号公報、
実開平１−88940号公報）。In addition, as a form of the photographic film cartridge container, a container in which the container body and the lid are integrally formed by a hinge has been proposed in addition to the container body and the lid being separately configured. (JP-A-63-223640,
(Kaikaihei 1-88940).

【０００５】[0005]

【発明が解決しようとする課題】しかしながら、上述し
た写真フイルム用容器は光電管で検出する際、確実に検
出できない場合があった。また、すり傷やちりの付着が
目立ち外観上好ましいものでは無かった。さらに、落下
強度やアイゾット衝撃強度のさらなる向上も望まれてい
た。However, when the above-mentioned photographic film container is detected by the photoelectric tube, it may not be surely detected. In addition, scratches and dust adhesion were conspicuous and not preferable in appearance. Further, further improvements in drop strength and Izod impact strength have been desired.

【０００６】本発明は、以上の問題点を解決し、光電管
で確実に検出できるとともに内部に収納した写真フイル
ムパトローネを見ることもでき、しかも物理強度を維持
又は向上させることができる写真フイルム用容器を提供
するこを目的とする。The present invention solves the above-mentioned problems, enables reliable detection by a photocell, allows the user to see the photographic film cartridge stored inside, and is capable of maintaining or improving the physical strength of the photographic film container. The purpose is to provide.

【０００７】[0007]

【課題を解決するための手段】本発明は、上記目的を達
成するために鋭意研究し、光電管で検出できないのはヘ
イズ（厚さ1.0ｍ、ASTM D-1003 準拠) が小さ過ぎるこ
とを見出し、ヘイズが適当な範囲であれば光電管による
検出が確実にでき、かつ収納した写真フイルムもよく見
えることを見出した。そして本発明はさらに研究し、所
定の樹脂組成であれば衝撃白化が少なく、ヘイズが所定
の範囲になり、しかも落下強度が向上することを見出
し、本発明を完成させた。また、その樹脂組成に着色物
質を加えると、落下強度が著しく向上することも見出し
た。Means for Solving the Problems The present invention has been eagerly studied in order to achieve the above-mentioned object, and found that haze (thickness 1.0 m, conforming to ASTM D-1003) is too small to be detected by a photoelectric tube, It has been found that when the haze is in an appropriate range, the phototube can be surely detected, and the stored photographic film can be seen well. Then, the present invention was further studied, and it was found that, when a predetermined resin composition was used, impact whitening was less, haze was within a predetermined range, and drop strength was improved, and the present invention was completed. It was also found that adding a coloring substance to the resin composition significantly improves the drop strength.

【０００８】すなわち、本発明の写真フイルム用容器
は、プロピレン・エチレンランダム共重合体樹脂65〜95
重量％、プロピレン. エチレンブロック共重合体樹脂５
〜35重量％、造核剤0.01〜2.0重量％、滑性向上物質0.0
1〜10重量％及び酸化防止剤0.01〜1.0重量％含まれてい
ることを特徴として構成されている。That is, the photographic film container of the present invention comprises a propylene / ethylene random copolymer resin 65-95.
% By weight, propylene. Ethylene block copolymer resin 5
~ 35 wt%, nucleating agent 0.01 ~ 2.0 wt%, lubricity improving substance 0.0
The composition is characterized by containing 1 to 10% by weight and 0.01 to 1.0% by weight of an antioxidant.

【０００９】また、本発明の写真フイルム用容器は、プ
ロピレン・エチレンランダム共重合体樹脂65〜95重量
％、プロピレン. エチレンブロック共重合体樹脂５〜35
重量％、造核剤0.01〜2.0重量％、滑性向上物質0.01〜1
0重量％、酸化防止剤0.01〜1.0重量％及び着色物質0.01
〜29重量％含まれていることを特徴として構成されてい
る。The photographic film container of the present invention comprises a propylene / ethylene random copolymer resin 65 to 95% by weight and a propylene.ethylene block copolymer resin 5 to 35.
% By weight, 0.01 to 2.0% by weight of nucleating agent, 0.01 to 1 of lubricity improving substance
0% by weight, antioxidant 0.01-1.0% by weight and coloring substance 0.01
The composition is characterized by containing ~ 29% by weight.

【００１０】本発明の写真フイルム用容器は、プロピレ
ン・エチレンランダム共重合体樹脂が65〜95重量％含ま
れている。このプロピレン・エチレンランダム共重合体
樹脂はプロピレン含有率が90重量％以上、エチレン含有
率が10重量％以下のエチレンをランダム構造で共重合さ
せたポリプロピレン系樹脂である（ポリプロピレン樹脂
の１つ）。The photographic film container of the present invention contains 65 to 95% by weight of a propylene / ethylene random copolymer resin. This propylene / ethylene random copolymer resin is a polypropylene resin obtained by copolymerizing ethylene having a propylene content of 90% by weight or more and an ethylene content of 10% by weight or less in a random structure (one of polypropylene resins).

【００１１】重合適性、剛性、落下衝撃強度、透明度、
耐摩耗性、成形性等のバランスの点でエチレン含有率は
0.3〜８重量％が好ましく、1.0〜6.5重量％が特に好ま
しく、1.5〜5.0重量％が最も好ましい。含有率が0.3重
量％未満では落下衝撃強度が不足し、かつ透明度が向上
せず、また８重量％を越えると重合適性が悪化し、ロッ
クウェル硬度が小さく、摩耗による白粉が発生しやす
く、剛性も小さく、かつ傷、変形、座屈等も発生しやす
くなる。Polymerization suitability, rigidity, drop impact strength, transparency,
In terms of balance of wear resistance and moldability, ethylene content is
0.3 to 8% by weight is preferable, 1.0 to 6.5% by weight is particularly preferable, and 1.5 to 5.0% by weight is most preferable. If the content is less than 0.3% by weight, the drop impact strength will be insufficient and the transparency will not improve, and if it exceeds 8% by weight, the polymerization suitability will deteriorate, the Rockwell hardness will be small, and white powder due to abrasion tends to be generated, resulting in rigidity. Is small, and scratches, deformation, and buckling are likely to occur.

【００１２】プロピレン・エチレンランダム共重合体樹
脂のメルト・フローレイト（JIS K7210、以後ＭＦＲと
表示）は５〜80g/10分が好ましく、10〜60g/10分が特に
好ましく、15〜50g/10分が最も好ましい。５g/10分未満
では樹脂の流動性が悪く、成形故障が多発する。80g/10
分を越えると分子量が小さくなり、表面硬度が小さくな
り内外壁が摩耗しやすく、白粉が多発する。The melt flow rate (JIS K7210, hereinafter referred to as MFR) of the propylene / ethylene random copolymer resin is preferably 5 to 80 g / 10 minutes, particularly preferably 10 to 60 g / 10 minutes, particularly 15 to 50 g / 10 minutes. Minutes are most preferred. If it is less than 5 g / 10 minutes, the fluidity of the resin is poor and molding failures frequently occur. 80g / 10
If it exceeds the limit, the molecular weight becomes small, the surface hardness becomes small, the inner and outer walls are easily worn, and white powder frequently occurs.

【００１３】プロピレン・エチレンランダム共重合体樹
脂の曲げ弾性率（JIS K 7203）は、5000kg/cm²以上が好
ましく、8000kg/cm²以上が特に好ましく、10000kg/cm²
以上が最も好ましい。曲げ弾性率が5000kg/cm²未満であ
ると変性、座屈等が発生しやすくなり、成形サイクルも
長くなる。さらに、輸送中に耐圧縮性が小さいためパト
ローネの保護ができなくなったり、キャップがはずれた
りする故障が多発する。The flexural modulus (JIS K 7203) of the propylene / ethylene random copolymer resin is preferably 5000 kg / cm ² or more, particularly preferably 8000 kg / cm ² or more, 10000 kg / cm ²
The above is the most preferable. If the flexural modulus is less than 5000 kg / cm ² , denaturation and buckling are likely to occur, and the molding cycle becomes long. Further, since the compression resistance is low during transportation, the patrone cannot be protected, and the cap is often detached, resulting in frequent failures.

【００１４】以上のようなプロピレン・エチレンランダ
ム共重合体樹脂が65〜95重量％含まれている。プロピレ
ン・エチレンランダム共重合体樹脂が65重量％未満で
は、剛性及び表面硬度が小さく写真フイルムとの摩擦に
より写真フイルムのパーホレーション部分や先端に白粉
が付着しやすくなり、95重量％を越えるとアイゾット衝
撃強度が低下し、割れやクラックが発生しやすくなる。The propylene / ethylene random copolymer resin as described above is contained in an amount of 65 to 95% by weight. If the propylene / ethylene random copolymer resin is less than 65% by weight, the rigidity and surface hardness are small, and white powder easily adheres to the perforated portion or the tip of the photographic film due to friction with the photographic film. Izod impact strength decreases, and cracks and cracks are more likely to occur.

【００１５】また、本発明の写真フイルム用容器にはプ
ロピレン・エチレンブロック共重合体樹脂が５〜35重量
％も含まれている。このプロピレン・エチレンブロック
共重合体樹脂はプロピレン含有率が60重量％以上、エチ
レン含有率が40重量％以下のエチレンをブロック構造で
共重合させたポリプロピレン系樹脂である（ポリプロピ
レン樹脂の１つ）。Further, the photographic film container of the present invention contains 5 to 35% by weight of a propylene / ethylene block copolymer resin. This propylene / ethylene block copolymer resin is a polypropylene resin obtained by copolymerizing ethylene having a propylene content of 60% by weight or more and an ethylene content of 40% by weight or less in a block structure (one of polypropylene resins).

【００１６】重合適性、剛性、落下衝撃強度、耐摩耗
性、成形性、耐衝撃白化、着色物質との混合性等のバラ
ンスの点でエチレン含有率は１〜30重量％が好ましく、
２〜20重量％が特に好ましく、３〜10重量％が最も好ま
しい。含有率が１重量％未満では、落下衝撃強度向上効
果が小さく、ヘイズコントロール許容幅が小さくなる。The ethylene content is preferably 1 to 30% by weight from the viewpoint of the balance of polymerization suitability, rigidity, drop impact strength, abrasion resistance, moldability, impact whitening resistance, mixability with coloring substances, and the like.
2-20% by weight is particularly preferred, and 3-10% by weight is most preferred. When the content is less than 1% by weight, the drop impact strength improving effect is small and the haze control allowable range is small.

【００１７】また、30重量％を越えると重合適性が悪化
し、ロックウェル硬度が小さく、摩耗による白粉が発生
しやすく、剛性も小さく、かつ傷、変形、座屈等も発生
しやすくなる。On the other hand, if it exceeds 30% by weight, the suitability for polymerization is deteriorated, the Rockwell hardness is small, white powder due to abrasion is likely to occur, the rigidity is low, and scratches, deformation, buckling, etc. are likely to occur.

【００１８】プロピレン・エチレンブロック共重合体樹
脂のメルト・フローレイト（JIS K7210、以後ＭＦＲと
表示）は５〜80g/10分が好ましく、10〜60g/10分が特に
好ましく、15〜50g/10分が最も好ましい。5g/10 分未満
では樹脂の流動性が悪く、成形故障が多発する。80g/10
分を越えると分子量が小さくなり、表面硬度が小さくな
り内外壁が摩耗しやすく、白粉が多発する。なお、プロ
ピレン・エチレンランダム共重合体樹脂のＭＦＲとプロ
ピレン・エチレンブロック共重合体樹脂のＭＦＲの比
は、±90％以内であることが好ましい。The melt flow rate (JIS K7210, hereinafter referred to as MFR) of the propylene / ethylene block copolymer resin is preferably 5 to 80 g / 10 minutes, particularly preferably 10 to 60 g / 10 minutes, particularly 15 to 50 g / 10. Minutes are most preferred. If it is less than 5 g / 10 minutes, the fluidity of the resin is poor and molding failures frequently occur. 80g / 10
If it exceeds the limit, the molecular weight becomes small, the surface hardness becomes small, the inner and outer walls are easily worn, and white powder frequently occurs. The ratio of the MFR of the propylene / ethylene random copolymer resin and the MFR of the propylene / ethylene block copolymer resin is preferably within ± 90%.

【００１９】プロピレン・エチレンブロック共重合体樹
脂の23℃のノッチ付アイゾット衝撃強度(JIS K 7110)が
３kg・cm/cm²以上が好ましく、４kg・cm/cm²以上が特に
好ましく、５kg・cm/cm²以上が最も好ましい。23℃のノ
ッチ付アイゾット衝撃強度が３kg・cm/cm²未満では衝撃
強度向上効果が小さく、エチレン・ランダム共重合体樹
脂を65〜95重量％含む本発明の写真フイルム用容器とし
ては実用化困難、特に低温度条件下（10℃以下）での衝
撃強度が小さくなり、実用化困難になる。The propylene-ethylene block copolymer notched Izod impact strength of 23 ° C. of the resin (JIS K 7110) is preferably 3 kg · cm / cm ² or more, particularly preferably 4 kg · cm / cm ² or more, 5 kg · cm / cm ² or more is most preferable. If the notched Izod impact strength at 23 ° C. is less than 3 kg · cm / cm ² , the impact strength improving effect is small, and it is difficult to put it into practical use as a photographic film container of the present invention containing 65 to 95% by weight of an ethylene / random copolymer resin. In particular, the impact strength becomes small under low temperature conditions (10 ° C or less), which makes practical application difficult.

【００２０】以上のようなプロピレン・エチレンブロッ
ク共重合体樹脂が５〜35重量％含まれている。プロピレ
ン・エチレンブロック共重合体樹脂が５重量％未満で
は、アイゾット衝撃強度向上効果が小さく、割れやクラ
ックが発生しやすくなる。35重量％を越えると剛性及び
表面硬度が小さく、写真フイルムとの摩擦により写真フ
イルムのパーホレーション部分や先端に白粉が付着しや
すくなる。もっとも問題なのは衝撃により白化し、見栄
えが悪くなり商品価値を大きく低下させる。The propylene / ethylene block copolymer resin as described above is contained in an amount of 5 to 35% by weight. When the propylene / ethylene block copolymer resin is less than 5% by weight, the effect of improving the Izod impact strength is small, and cracks and cracks are likely to occur. If it exceeds 35% by weight, the rigidity and the surface hardness are small, and the white powder easily adheres to the perforated portion or the tip of the photographic film due to friction with the photographic film. The most problematic problem is that it is bleached by the impact, which makes it unattractive and greatly reduces the product value.

【００２１】造核剤は、結晶化速度向上、成形サイクル
短縮、剛性向上、透明度向上及び変形や白粉発生防止や
物理特性向上等のためのものである。The nucleating agent is for improving the crystallization rate, shortening the molding cycle, improving rigidity, improving transparency, preventing deformation and white powder generation, and improving physical properties.

【００２２】造核剤としては、有機造核剤と無機造核剤
がある。これらの代表例を以下に示す。Nucleating agents include organic nucleating agents and inorganic nucleating agents. Representative examples of these are shown below.

【００２３】有機造核剤は、カルボン酸、ジカルボン
酸、これらの塩及び無水物、芳香族スルホン酸の塩及び
エステル、芳香族ホスフィン酸、芳香族ホスホン酸、芳
香族カルボン酸、そのアルミニウム塩、芳香族リン酸金
属塩、炭素数８〜30のアルキルアルコール、多価アルコ
ールとアルデヒドの縮合物ならびにアルキルアミンなど
であり、例えばp-t-ブチル安息香酸アルミニウム、1,3・
2,4-ジベンジリデンソルビトール、次式で表されるジ置
換ベンジリデンソルビトール化合物Organic nucleating agents include carboxylic acids, dicarboxylic acids, salts and anhydrides thereof, salts and esters of aromatic sulfonic acids, aromatic phosphinic acids, aromatic phosphonic acids, aromatic carboxylic acids, aluminum salts thereof, Aromatic metal phosphates, alkyl alcohols having 8 to 30 carbon atoms, condensation products of polyhydric alcohols and aldehydes, and alkyl amines, such as pt-butyl aluminum benzoate, 1,3.
2,4-dibenzylidene sorbitol, a di-substituted benzylidene sorbitol compound represented by the following formula

【００２４】[0024]

【化１】 [Chemical 1]

【００２５】（式中、Ｒ₁及びＲ₂は炭素数１〜８のアル
キル、アルコキシ又はハロゲンであり、ｍ及びｎはいず
れも０〜３であってかつｍ＋ｎ≧１である。)、ステアリ
ル乳酸のカルシウム、マグネシウム等の金属塩、N-（2-
ヒドロキシエチル）−ステアリルアミン等の次式で表さ
れる化合物(Wherein R ₁ and R ₂ are alkyl, alkoxy or halogen having 1 to 8 carbon atoms, m and n are both 0 to 3 and m + n ≧ 1), stearyl lactic acid Calcium, magnesium and other metal salts, N- (2-
A compound represented by the following formula, such as hydroxyethyl) -stearylamine

【００２６】[0026]

【化２】 [Chemical 2]

【００２７】（式中、Ｒ₃は炭素数が８〜30のアルキル
基であり、ｋ及びｌはいずれも０〜10であってｋ＋ｌ≧
１である。)、1,2-ヒドロキシステアリン酸のリチウム
塩、ナトリウム塩、カリウム塩、カルシウム塩、マグネ
シウム塩等の金属塩、ステアリルアルコール、ラウリル
アルコール等のアルキルアルコール、安息香酸ソーダ、
安息香酸、セパチン酸などを含む。(Wherein R ₃ is an alkyl group having 8 to 30 carbon atoms, k and l are both 0 to 10 and k + l ≧
It is 1. ), 1,2-hydroxystearic acid lithium salt, sodium salt, potassium salt, calcium salt, metal salt such as magnesium salt, stearyl alcohol, alkyl alcohol such as lauryl alcohol, sodium benzoate,
Including benzoic acid and sepatic acid.

【００２８】無機造核剤は、水酸化リチウム、水酸化ナ
トリウム、水酸化カリウム等のアルカリ金属水酸化物、
酸化ナトリウム等のアルカリ金属酸化物、炭酸リチウ
ム、炭酸ナトリウム、炭酸カリウム、炭酸水素ナトリウ
ム、炭酸水素カリウム等のアルカリ金属炭酸塩、水酸化
カルシウム、水酸化マグネシウム、水酸化バリウム等の
アルカリ土類金属水酸化物、炭酸カルシウム、酸化カル
シウム等のアルカリ土類金属酸化物などである。The inorganic nucleating agent is an alkali metal hydroxide such as lithium hydroxide, sodium hydroxide or potassium hydroxide,
Alkali metal oxides such as sodium oxide, alkali metal carbonates such as lithium carbonate, sodium carbonate, potassium carbonate, sodium hydrogen carbonate and potassium hydrogen carbonate, alkaline earth metal waters such as calcium hydroxide, magnesium hydroxide and barium hydroxide. Examples thereof include oxides, alkaline earth metal oxides such as calcium carbonate and calcium oxide.

【００２９】造核剤は、これらに限定されるものではな
く、その他の公知の造核剤を用いることもできる。ま
た、造核剤は単独の場合に限らず、二種以上を併用する
こともできることはいうまでもない。The nucleating agent is not limited to these, and other known nucleating agents can be used. Needless to say, the nucleating agent is not limited to a single type, and two or more types can be used in combination.

【００３０】写真フイルムに悪影響を与えず、造核剤と
して添加効果の大きい有機造核剤として好ましい例を以
下に記載する。Preferred examples of the organic nucleating agent which does not adversely affect the photographic film and has a large addition effect as a nucleating agent are described below.

【００３１】1・3・2・4-ジ（メチルベンジリデン）ソルビ
トール、1・3・2・4-ジ（エチルベンジリデン）ソルビトー
ル、1・3・2・4-ジ（プロピルベンジリデン）ソルビトー
ル、1・3・2・4-ジ（メトキシベンジリデン）ソルビトー
ル、1・3・2・4-ジ（エトキシベンジリデン）ソルビトー
ル、1・3・2・4-ジ（P-メチルベンジリデン）ソルビトー
ル、1・3・2・4-ジ（P-クロルベンジリデン）ソルビトー
ル、1・3・2・4-ジ（P-メトキシベンジリデン）ソルビトー
ル、1・3・2・4-ジ（アルキルベンジリデン）ソルビトー
ル、1・3・2・4-ビス（メチルベンジリデン）ソルビトー
ル、アルミニウムベンゾエート等。1,3,2,4-di (methylbenzylidene) sorbitol, 1,3,2,4-di (ethylbenzylidene) sorbitol, 1,3,2,4-di (propylbenzylidene) sorbitol, 1, 3 ・ 2.4-Di (methoxybenzylidene) sorbitol, 1 ・ 3 ・ 2.4-di (ethoxybenzylidene) sorbitol, 1 ・ 3 ・ 2.4-di (P-methylbenzylidene) sorbitol, 1 ・ 3 ・ 2・ 4-di (P-chlorobenzylidene) sorbitol, 1 ・ 3 ・ 2 ・ 4-di (P-methoxybenzylidene) sorbitol, 1 ・ 3 ・ 2 ・ 4-di (alkylbenzylidene) sorbitol, 1 ・ 3 ・ 2 ・4-bis (methylbenzylidene) sorbitol, aluminum benzoate, etc.

【００３２】特に、ジベンジリデンソルビトール化合物
が好ましい。Particularly, a dibenzylidene sorbitol compound is preferable.

【００３３】有機造核剤は、単独で用いても無機造核剤
との併用、有機造核剤の２種以上を併用することもでき
る。また、有機造核剤の表面を各種の脂肪酸、脂肪酸化
合物、カップリング剤、界面活性剤等で被覆することが
でき好ましい。The organic nucleating agent may be used alone, in combination with an inorganic nucleating agent, or in combination of two or more kinds of organic nucleating agents. Further, the surface of the organic nucleating agent can be coated with various fatty acids, fatty acid compounds, coupling agents, surfactants and the like, which is preferable.

【００３４】造核剤の添加量は、0.01〜2.0重量％であ
る。添加量が0.01重量％未満ではほとんど効果を発揮せ
ずブレンド経費がかかるだけであり、2.0重量％を越え
ても増量効果がなくコストアップになるだけであり、か
つ造核剤の種類によっては写真フイルムに悪影響を与え
たり、金型に付着したり、ブリードアウトしたり、落下
強度を大巾に低下させたりするので好ましくない。The amount of the nucleating agent added is 0.01 to 2.0% by weight. If the addition amount is less than 0.01% by weight, the effect is hardly exhibited and only the blending cost is required. If the addition amount is more than 2.0% by weight, there is no effect of increasing the amount and only the cost is increased. It is not preferable because it adversely affects the film, adheres to the mold, bleeds out, and greatly reduces the drop strength.

【００３５】造核剤をブレンドする方法としては、コン
パウンド方式やドライブレンド方式やマスターバッチ方
式等があるが、マスターバッチ方式が好ましい。カサが
高く、飛散しやすいのでそのまま配合することは困難で
あり、少量の分散剤か湿潤剤を入れて配合すると良い。
分散剤として効果があるものとしては無水カルボン酸、
高級脂肪酸等があり、オレイン酸アミド等の脂肪酸アミ
ド系の滑剤は特に好ましい。湿潤剤としてはＤＯＰ、Ｄ
ＨＰ等の可塑剤が使用できる。As a method of blending the nucleating agent, there are a compound method, a dry blend method, a master batch method and the like, but the master batch method is preferable. Since it has a high dryness and is easily scattered, it is difficult to mix it as it is.
Carboxylic anhydride, which is effective as a dispersant,
There are higher fatty acids and the like, and fatty acid amide-based lubricants such as oleic acid amide are particularly preferable. Wetting agents DOP, D
A plasticizer such as HP can be used.

【００３６】また高級脂肪酸、脂肪酸アミド、脂肪酸金
属塩等の脂肪酸や脂肪酸化合物の純品を有機造核剤の表
面にコーティングしたりブレンドして分散効果を高め、
ブリードアウトを防ぐことも好ましい。すなわち、これ
らの添加剤を添加することにより、剛性が大きくなり摩
耗による白粉の発生を減少させるとともに、有機造核剤
のブリードアウトによる白粉の発生を減少させる。さら
に、有機造核剤の悪臭を防止でき、かつ金型からの離形
性、静電気の発生防止及びブロッキング防止性を向上さ
せることができる。Further, pure products of fatty acids and fatty acid compounds such as higher fatty acids, fatty acid amides and fatty acid metal salts are coated or blended on the surface of the organic nucleating agent to enhance the dispersion effect,
It is also preferable to prevent bleed-out. That is, by adding these additives, the rigidity is increased and the generation of white powder due to wear is reduced, and the generation of white powder due to bleed-out of the organic nucleating agent is reduced. Furthermore, the malodor of the organic nucleating agent can be prevented, and the mold releasability from the mold, the prevention of static electricity generation, and the prevention of blocking can be improved.

【００３７】滑性向上物質は成形性向上、写真フイルム
の容器への出し入れをしやすくし、空送性、加工包装適
性を向上させる。さらに、金型からの離形性、静電気の
発生防止、ブロッキング防止性等を向上させる。さら
に、また本発明に必須の造核剤、酸化防止剤、２種のポ
リプロピレン樹脂、着色物質の分散、混練性を向上させ
る働きをする。The slipperiness-improving substance improves the moldability, makes it easier to put the photographic film in and out of the container, and improves the dry feeding property and suitability for processing and packaging. Further, the mold releasability from the mold, the prevention of static electricity generation, the prevention of blocking and the like are improved. Further, it also functions to improve the dispersibility and kneading property of the nucleating agent, antioxidant, two kinds of polypropylene resins and coloring substances which are essential to the present invention.

【００３８】例えば、各種滑剤、各種界面活性剤、各種
帯電防止剤、各種粒状樹脂等がある。For example, various lubricants, various surfactants, various antistatic agents, various granular resins and the like are available.

【００３９】市販の代表的滑剤名と製造メーカー名を以
下に記載する。 (1) 脂肪酸アミド系滑剤；飽和脂肪酸アミド系滑剤 ベヘニン酸アミド系滑剤；ダイヤミッドＫＮ（日本化
成）等 ステアリン酸アミド系滑剤；アーマイドＨＴ（ライオ
ン油脂）、アルフローＳ−10（日本油脂）、脂肪酸アマ
イドＳ（花王）、ダイヤミッド200(日本化成）、ダイヤ
ミッドAP−１（日本化成）、アマイドＳ・アマイドＴ
（日東化学）、ニュートロン−２（日本精化）等 パルミチン酸アミド系滑剤；ニュートロンＳ−18（日
本精化）、アマイドＰ（日東化学）等 ラウリン酸アミド系滑剤；アーマイドＣ（ライオン・
アクゾ）、ダイヤミッド（日本化成）等The names of typical commercially available lubricants and the names of manufacturers are described below. (1) Fatty acid amide lubricant; Saturated fatty acid amide lubricant Behenic acid amide lubricant; Diamid KN (Nippon Kasei), etc. Stearic acid amide lubricant; Armide HT (Lion fat), Alflo S-10 (Nippon fat), Fatty acid Amide S (Kao), Diamond Mid 200 (Nippon Kasei), Diamond Mid AP-1 (Nippon Kasei), Amide S, Amide T
(Nitto Kagaku), Neutron-2 (Nippon Seika), etc. Palmitic acid amide lubricant; Neutron S-18 (Nippon Seika), Amide P (Nitto Kagaku), etc. Lauric acid amide lubricant; Armide C (Lion.
Akzo), Diamond (Nihon Kasei), etc.

【００４０】不飽和脂肪酸アミド系滑剤 エルカ酸アミド系滑剤；アルフローＰ−10（日本油
脂）、ニュートロン−Ｓ（日本精化）、LUBROL（Ｉ・Ｃ
・Ｉ）、ダイヤミッドＬ−200(日本化成）等 オレイン酸アミド系滑剤；アーモスリップＣＰ（ライ
オン・アクゾ）、ニュートロン（日本精化）、ニュート
ロンＥ−18（日本精化）、アマイドＯ（日東化学）、ダ
イヤミッドＯ−200・ダイヤミッドＧ−200(日本化
成）、アルフローＥ−10（日本油脂）、脂肪酸アマイド
Ｏ（花王）等Unsaturated Fatty Acid Amide Lubricants Erucamide Amide Lubricants; Alflo P-10 (Nippon Yushi), Neutron-S (Nippon Seika), LUBROL (IC)
・ I), Diamid L-200 (Nippon Kasei), etc. Oleic acid amide lubricants; Armoslip CP (Lion Akzo), Neutron (Nippon Seika), Neutron E-18 (Nippon Seika), Amide O (Nitto Chemical), Diamid O-200, Diamid G-200 (Nippon Kasei), Alflo E-10 (Nippon Yushi), Fatty Acid Amide O (Kao), etc.

【００４１】ビス脂肪酸アミド系滑剤 メチレンビスベヘニン酸アミド系滑剤；ダイヤミッド
ＮＫビス（日本化成）等 メチレンビスステアリン酸アミド系滑剤；ダイヤミッ
ド200ビス（日本化成）、アーモワックス（ライオン・
アクゾ）、ビスアマイド（日東化学）等 メチレンビオオレイン酸アミド系滑剤；ルブロンＯ
（日本化成）等 エチレンビスステアリン酸アミド系滑剤；アーモスリ
ップＥＢＳ（ライオン・アクゾ）等 ヘキサメチレンビスステアリン酸アミド系滑剤；アマ
イド65（川研ファインケミカル）等 ヘキサメチレンビスオレイン酸アミド系滑剤；アマイ
ド60（川研ファインケミカル）等Bis-fatty acid amide lubricants Methylene bis-behenic acid amide lubricants; Diamid NK bis (Nippon Kasei), etc. Methylene bisstearic amide lubricants; Diamid 200 bis (Nippon Kasei), Armowax (Lion
Akzo), bisamide (Nitto Kagaku), etc. Methylenebiooleic acid amide lubricant; Lubron O
(Nippon Kasei) etc. Ethylenebisstearic acid amide lubricant; Armoslip EBS (Lion Akzo) etc. Hexamethylenebisstearic acid amide lubricant; Amide 65 (Kawaken Fine Chemicals) etc. Hexamethylenebisoleic acid amide lubricant; Amide 60 (Kawaken Fine Chemicals) etc.

【００４２】(2) シリコーン系滑剤；各種グレードのジ
メチルポリシロキサン及びその変性物（信越シリコー
ン、東レシリコーン）(2) Silicone-based lubricants; various grades of dimethylpolysiloxane and its modified products (Shin-Etsu Silicone, Toray Silicone)

【００４３】特に各種シリコンが樹脂流動性向上、滑性
向上等の効果を発揮させるだけでなく、着色物質と併用
すると着色物質の分散性向上、着色力向上等予想外の効
果を発揮するので好ましい。In particular, various silicons are preferable because they not only exhibit the effects of improving the resin fluidity and the lubricity, but also when used in combination with the coloring substance, they exhibit unexpected effects such as the improvement of the dispersibility of the coloring substance and the coloring power. ..

【００４４】(3) 非イオン界面活性剤系滑剤；エレクト
ロストリッパ-TS-２、エレクトロストリッパ-TS-３（花
王石鹸）等(3) Nonionic surfactant lubricants; Electrostripper-TS-2, Electrostripper-TS-3 (Kao soap), etc.

【００４５】(4) 炭化水素系滑剤；流動パラフィン、天
然パラフィン、マイクロワックス、合成パラフィン、ポ
リエチレンワックス、ポリプロピレンワックス、塩素化
炭化水素、フルオロカルボン(4) Hydrocarbon lubricants; liquid paraffin, natural paraffin, microwax, synthetic paraffin, polyethylene wax, polypropylene wax, chlorinated hydrocarbon, fluorocarbon

【００４６】(5) 脂肪酸系滑剤；高級脂肪酸（Ｃ₁₂以上
が好ましい）、オキシ脂肪酸(5) Fatty acid type lubricant; higher fatty acid (preferably C ₁₂ or more), oxy fatty acid

【００４７】(6) エステル系滑剤；脂肪酸の低級アルコ
ールエステル、脂肪酸の多価アルコールエステル、脂肪
酸のポリグリコールエステル、脂肪酸の脂肪アルコール
エステル(6) Ester lubricants: lower alcohol esters of fatty acids, polyhydric alcohol esters of fatty acids, polyglycol esters of fatty acids, fatty alcohol esters of fatty acids

【００４８】(7) アルコール系滑剤；多価アルコール、
ポリグリコール、ポリグリセロール(7) Alcohol lubricants; polyhydric alcohols,
Polyglycol, polyglycerol

【００４９】(8) 金属石けん；ラウリン酸、ステアリン
酸、リシノール酸、ナフテン酸、オレイン酸等の高級脂
肪酸とＬi、Ｍg、Ｃa、Ｓr、Ｂa、Ｚn、Ｃd、Ａl、Ｓ
n、Ｐb等の金属との化合物(8) Metal soap: higher fatty acids such as lauric acid, stearic acid, ricinoleic acid, naphthenic acid, oleic acid and Li, Mg, Ca, Sr, Ba, Zn, Cd, Al, S
Compounds with metals such as n and Pb

【００５０】以上のような滑性向上物質の添加量は0.01
〜10重量％であり、添加量が0.01重量％未満では添加効
果がほとんどなく、混練費アップになるだけであり、10
重量％を越えると、滑性向上効果の小さい脂肪酸や脂肪
酸金属塩であってもスクリューのスリップが発生し、樹
脂との混練性が悪化する。特に、脂肪酸アミドのように
滑性効果の大きい物質の場合は1.0重量％以下にしない
とスクリューのスリップが発生したり、ブリードアウト
による障害が発生する。The amount of the above-mentioned lubricity improving substance added is 0.01
10 to 10% by weight, and if the addition amount is less than 0.01% by weight, there is almost no effect of addition and only the kneading cost increases.
If the content exceeds 10% by weight, screw slippage occurs even with a fatty acid or a fatty acid metal salt having a small effect of improving lubricity, and the kneadability with the resin deteriorates. In particular, in the case of a substance such as fatty acid amide having a large slippery effect, if the content is not less than 1.0% by weight, screw slippage or bleed-out failure will occur.

【００５１】酸化防止剤は、２種類のポリプロピレン樹
脂と滑剤や界面活性剤等の滑性向上物質の熱による劣化
を防止する。The antioxidant prevents the deterioration of the two kinds of polypropylene resins and the lubricity-improving substances such as lubricants and surfactants due to heat.

【００５２】酸化防止剤の代表例を以下に記載する。 (イ) フェノール系酸化防止剤 6-t-ブチル-3-メチルフェニール誘導体、2・6-ジ-t-ブチ
ル-Pクレゾールt-t-ブチルフェノール）、2・2'-メチレ
ンビス-(4-エチル-6-t-ブチルフェノール）、4・4'-ブチ
リデンビス（6-t-ブチル-m-クレゾール）、4・4'-チオビ
ス（6-t-ブチル-m-クレゾール）、4・4-ジヒドロキシジ
フェニルシクロヘキサン、アルキル化ビスフェノールス
チレン化フェノール、2・6-ジ-t-ブチル-4-メチルフェノ
ール、n-オクタデシル-3-(3'・5'-ジ-t-ブチル-4'-ヒド
ロキシフェニル）プロピネート、2・2'-メチレンビン（4
-メチル-6-t-ブチルフェノール）、4・4'-チオビス（3-
メチル-6-t-ブチルフェニール）、4・4'-ブチリデンビス
（3-メチル-6-t-ブチルフェノール）、ステアリル−β
（3・5-ジ-4-ブチル-4-ヒドロキシフェニル）プロピオネ
ート、1・1・3-トリス（2-メチル-4ヒドロキシ-5-t-ブチ
ルフェニル）ブタン、1・3・5トリメチル-2・4・6-トリス
（3・5-ジ-t-ブチル-4ヒドロキシベンジル）ベンゼン、
テトラキス〔メチレン-3（3'・5'-ジ-t-ブチル-4'-ヒド
ロキシフェニル）プロピオネート〕メタン等 (ロ) ケトンアミン縮合系酸化防止剤 6-エトキシ-2・2・4-トリメチル-1・2-ジヒドロキノリン、
2・2・4-トリメチル-1・2-ジヒドロキノリンの重合物、ト
リメチルジヒドロキノリン誘導体等 (ハ) アリルアミン系酸化防止剤 フェニル-α-ナフチルアミン、N-フェニル-β-ナフチル
アミン、N-フェニル-N'-イソプロピル-P-フェニレンジ
アミン、N・N'-ジフェニル-P-フェニレンジアミン、N・N'
-ジ-β-ナフチル-P-フェニレンジアミン、N-(3'-ヒドロ
キシブチリデン)-1-ナフチルアミン等 (ニ) イミダゾール系酸化防止剤 2-メルカプトベンゾイミダゾール、2-メルカプトベンゾ
イミダゾールの亜鉛塩、2-メルカプトメチルベンゾイミ
ダゾール等 (ホ) ホスファイト系酸化防止剤 アルキル化アリルホスファイト、ジフェニルイソデシル
フォスファイト、トリス（ノニルフェニル）ホスファイ
ト、亜リン酸ソーダ、トリノニルフェニルフォスファイ
ト、トリフェニルフォスファイト等 (ヘ) チオ尿素系酸化防止剤 チオ尿素誘導体、1・3-ビス（ジメチルアミノプロピル)-
2-チオ尿素等 (ト) その他空気酸化に有用な酸化防止剤 チオジプロピオン酸ジラウリル等 (チ) 硫黄系酸化防止剤 ジラウリルチオジプロピオネート、シミリスチルチオジ
プロピオネート、ラウリルステアリルチオジプロピオネ
ート、ジステアリルチオジプロピオネート等Representative examples of antioxidants are listed below. (A) Phenolic antioxidant 6-t-butyl-3-methylphenyl derivative, 2,6-di-t-butyl-P cresol tt-butylphenol), 2,2'-methylenebis- (4-ethyl-6) -t-butylphenol), 4.4'-butylidene bis (6-t-butyl-m-cresol), 4.4'-thiobis (6-t-butyl-m-cresol), 4.4-dihydroxydiphenylcyclohexane, Alkylated bisphenol Styrenated phenol, 2,6-di-t-butyl-4-methylphenol, n-octadecyl-3- (3 '・ 5'-di-t-butyl-4'-hydroxyphenyl) propinate, 2・ 2'-Methylenebin (4
-Methyl-6-t-butylphenol), 4'-thiobis (3-
Methyl-6-t-butylphenyl), 4,4'-butylidenebis (3-methyl-6-t-butylphenol), stearyl-β
(3 ・ 5-di-4-butyl-4-hydroxyphenyl) propionate, 1 ・ 1.3-tris (2-methyl-4hydroxy-5-t-butylphenyl) butane, 1 ・ 3 ・ 5 trimethyl-2・ 4.6-Tris (3.5-di-t-butyl-4hydroxybenzyl) benzene,
Tetrakis [methylene-3 (3 '・ 5'-di-t-butyl-4'-hydroxyphenyl) propionate] methane etc. (b) Ketone amine condensation type antioxidant 6-ethoxy-2 ・ 2 ・ 4-trimethyl-1・ 2-dihydroquinoline,
Polymers of 2,2,4-trimethyl-1,2-dihydroquinoline, trimethyldihydroquinoline derivatives, etc. (c) Allylamine antioxidants Phenyl-α-naphthylamine, N-phenyl-β-naphthylamine, N-phenyl-N '-Isopropyl-P-phenylenediamine, N ・ N'-diphenyl-P-phenylenediamine, N ・ N'
-Di-β-naphthyl-P-phenylenediamine, N- (3'-hydroxybutylidene) -1-naphthylamine, etc. (d) Imidazole antioxidant 2-mercaptobenzimidazole, zinc salt of 2-mercaptobenzimidazole, 2-Mercaptomethylbenzimidazole, etc. (e) Phosphite antioxidants Alkylated allylphosphite, diphenylisodecylphosphite, tris (nonylphenyl) phosphite, sodium phosphite, trinonylphenylphosphite, triphenylphosphite Fight, etc. (f) Thiourea-based antioxidants Thiourea derivatives, 1,3-bis (dimethylaminopropyl)-
2-Thiourea, etc. (G) Other antioxidants useful for air oxidation Dilauryl thiodipropionate, etc. (H) Sulfur-based antioxidants Dilauryl thiodipropionate, Simyristyl thiodipropionate, Lauryl stearyl thiodipropioate Nate, distearyl thiodipropionate, etc.

【００５３】次に、代表的な市販の酸化防止剤商品名を
以下に記載する。 (1) フェノール系酸化防止剤；SUMILIZER BHT(住友）、
IRGANOX 1076（チバガイギー）、MARK AO-50（アデカ・
アーガス）、SUMILIZER BP-76(住友）、TOMINOX SS（吉
富）、IRGANOX 565(チバガイギー）、NONOX WSP(ＩＣ
Ｉ）、SANTONOX（Monsanto）、SUMILIZER WX R（住
友）、ANTAGECRYSTAL(川口）、IRGANOX 1035（チバガイ
ギー）、ANTAGE W-400（川口）、NOCLIZER NS-6(大内新
興）、IRGANOX 1425 WL(チバガイギー）、MARKAO-80
（アデカ・アーガス）、SUMILIZER GA-80(住友）、TOPA
NOL CA（ＩＣＩ）、MARK AO-30（アデカ・アーガス）、
MARKAO-20(アデカ・アーガス）、IRGANOX3114（チバガ
イギー）、MARK AO-330(アデカ・アーガス）、IRGANOX
1330（チバガイギー）、CYANOX 1790(ＡＣＣ）、IRGANO
X 1010（チバガイギー）、MARK AO-60（アデカ・アーガ
ス）、SUMILIZER BP-101（住友）、TOMINOX TT（吉富）
等Next, typical commercial products of antioxidants are listed below. (1) Phenolic antioxidant; SUMILIZER BHT (Sumitomo),
IRGANOX 1076 (Ciba-Geigy), MARK AO-50 (Adeka
Argus), SUMILIZER BP-76 (Sumitomo), TOMINOX SS (Yoshitomi), IRGANOX 565 (Ciba Geigy), NONOX WSP (IC
I), SANTONOX (Monsanto), SUMILIZER WX R (Sumitomo), ANTAGECRYSTAL (Kawaguchi), IRGANOX 1035 (Ciba Geigy), ANTAGE W-400 (Kawaguchi), NOCLIZER NS-6 (Ouchi Shinko), IRGANOX 1425 WL (Ciba Geigy) , MARKAO-80
(Adeka Argus), SUMILIZER GA-80 (Sumitomo), TOPA
NOL CA (ICI), MARK AO-30 (Adeka Argus),
MARKAO-20 (Adeka Argus), IRGANOX3114 (Ciba Geigy), MARK AO-330 (Adeka Argus), IRGANOX
1330 (Ciba Geigy), CYANOX 1790 (ACC), IRGANO
X 1010 (Ciba Geigy), MARK AO-60 (Adeka Argus), SUMILIZER BP-101 (Sumitomo), TOMINOX TT (Yoshitomi)
etc

【００５４】(2) 燐系酸化防止剤；IRGAFOS 168(チバガ
イギー）、MARK 2112(アデカ・アーガス）、WESTON 618
（ボルグワーナー）、MARK PEP-8（アデカ・アーガ
ス）、ULTRANOX 626（ボルグ・ワーナー）、MARK PEP-2
4G（アデカ・アーガス）、MARK PEP-36(アデカ・アーガ
ス）、HCA(三光）等(2) Phosphorus antioxidants: IRGAFOS 168 (Ciba Geigy), MARK 2112 (Adeka Argus), WESTON 618
(Borg Warner), MARK PEP-8 (Adeka Argus), ULTRANOX 626 (Borg Warner), MARK PEP-2
4G (Adeka Argus), MARK PEP-36 (Adeka Argus), HCA (Sanko), etc.

【００５５】(3) チオエーテル系酸化防止剤；DLTDP "Y
OSHITOMI"(吉富）、SUMILIZER TPL(住友）、ANTIOX L
（日油）、DMTD"YOSHITOMI"（吉富）、SUMILIZER TPM
(住友）、ANTIOX M（日油）、DSTP "YOSHITOMI"（吉
富）、SUMILIZER TPS(住友）、ANTIOX S（日油）、SEEN
OX 412S(シプロ）、MARK AO-412S（アデカ・アーガ
ス）、SUMILIZER TP-D（住友）、MARK AO-23（アデカ・
アーガス）、SANDSTAB P-EPQ（サンド）、IRGAFOS P-EP
Q FF（チバガイギー）、IRGANOX 1222（チバガイギ
ー）、MARK 329K(アデカ・アーガス）、WES TON399（ボ
ルグ・ワーナー）、MARK 260（アデカ・アーガス）、MA
RK 522A(アデカ・アーガス）等(3) Thioether type antioxidant; DLTDP "Y
OSHITOMI "(Yoshitomi), SUMILIZER TPL (Sumitomo), ANTIOX L
(NOF), DMTD "YOSHITOMI" (Yoshitomi), SUMILIZER TPM
(Sumitomo), ANTIOX M (NOF), DSTP "YOSHITOMI" (Yoshitomi), SUMILIZER TPS (Sumitomo), ANTIOX S (NOF), SEEN
OX 412S (Cipro), MARK AO-412S (Adeka Argus), SUMILIZER TP-D (Sumitomo), MARK AO-23 (Adeka
Argus), SANDSTAB P-EPQ (Sand), IRGAFOS P-EP
Q FF (Ciba Geigy), IRGANOX 1222 (Ciba Geigy), MARK 329K (Adeka Argus), WES TON399 (Borg Warner), MARK 260 (Adeka Argus), MA
RK 522A (Adeka Argus) etc.

【００５６】(4) 金属不活性化剤；NAUGARD XL-1（ユニ
ロイヤル）、NARK CDA-1（アデカ・アーガス）、MARK C
DA-6（アデカ・アーガス）、LRGANOX MD-1024(チバガイ
ギー）、CUNOX(三井東圧）等(4) Metal deactivator; NAUGARD XL-1 (Uniroyal), NARK CDA-1 (Adeka Argus), MARK C
DA-6 (Adeka Argus), LRGANOX MD-1024 (Ciba Geigy), CUNOX (Mitsui Toatsu), etc.

【００５７】以上のような酸化防止剤の添加量は、0.01
〜1.0重量％である。添加量が0.01重量％未満である
と、２種類のポリプロピレン樹脂と滑性向上物質の熱に
よる劣化を防止することが困難である。The amount of the above antioxidant added is 0.01
~ 1.0% by weight. If the added amount is less than 0.01% by weight, it is difficult to prevent the deterioration of the two kinds of polypropylene resins and the lubricity improving substance due to heat.

【００５８】また、1.0重量％を越えると酸化、還元作
用を利用している写真フイルムに悪影響を及ぼし、カブ
リの発生、感度異常等の品質異常が発生する。On the other hand, if it exceeds 1.0% by weight, the photographic film utilizing the oxidation and reduction effects is adversely affected, causing fog and abnormal quality such as abnormal sensitivity.

【００５９】着色物質は、主として写真フイルム用容器
の落下強度を向上させるためのものである。本発明に用
いる着色物質の代表例を以下に記載する。The coloring substance is mainly for improving the drop strength of the photographic film container. Representative examples of the coloring substance used in the present invention are described below.

【００６０】(1) 無機化合物 A. 酸化物…シリカ、ケイ藻土、アルミナ、酸化チタ
ン、酸化鉄、酸化亜鉛、酸化マグネシウム、酸化アンチ
モン、バリウムフェライト、ストロンチウムフェライ
ト、酸化ベリリウム、軽石、軽石バルーン、アルミナ繊
維等 B. 水酸化物…水酸化アルミニウム、水酸化マグネシウ
ム、塩基性炭酸マグネシウム等 C. 炭酸塩…炭酸カルシウム、炭酸マグネシウム、ドロ
マイト、ドーソナイト等 D. （亜）硫酸塩…硫酸カルシウム、硫酸バリウム、硫
酸アンモニウム、亜硫酸カルシウム等 E. ケイ酸塩…タルク、クレー、マイカ、アスベスト、
ガラス繊維、ガラスバルーン、ガラスビーズ、ケイ酸カ
ルシウム、モンモリロナイト、ベントナイト等 F. 炭素…カーボンブラック、グラファイト、炭素繊
維、炭素中空球等 G. その他…鉄粉、銅粉、鉛粉、錫粉、ステンレス粉、
パール顔料、アルミニウム粉、硫化モリブデン、ポロン
繊維、炭化ケイ素繊維、黄銅繊維、チタン酸カリウム、
チタン酸ジルコン酸鉛、ホウ酸亜鉛、メタホウ酸バリウ
ム、ホウ酸カルシウム、ホウ酸ナトリウム、アルミニウ
ムペースト、タルク等(1) Inorganic Compound A. Oxide ... Silica, diatomaceous earth, alumina, titanium oxide, iron oxide, zinc oxide, magnesium oxide, antimony oxide, barium ferrite, strontium ferrite, beryllium oxide, pumice stone, pumice balloon, Alumina fibers, etc. B. Hydroxide: Aluminum hydroxide, magnesium hydroxide, basic magnesium carbonate, etc. C. Carbonate: Calcium carbonate, magnesium carbonate, dolomite, dawsonite, etc. D. (Sub) sulfate: Calcium sulfate, barium sulfate , Ammonium sulfate, calcium sulfite, etc. E. Silicates ... Talc, clay, mica, asbestos,
Glass fibers, glass balloons, glass beads, calcium silicate, montmorillonite, bentonite, etc. F. Carbon: carbon black, graphite, carbon fibers, carbon hollow spheres, etc. G. Others: iron powder, copper powder, lead powder, tin powder, stainless steel powder,
Pearl pigment, aluminum powder, molybdenum sulfide, polon fiber, silicon carbide fiber, brass fiber, potassium titanate,
Lead zirconate titanate, zinc borate, barium metaborate, calcium borate, sodium borate, aluminum paste, talc, etc.

【００６１】(2) 有機化合物 木粉（松、樫、ノコギリクズなど）、殻繊維（アーモン
ド、ピーナッツ、モミ殻など）、着色した各種の繊維例
えば木綿、ジュート、紙細片、セロハン片、ナイロン繊
維、ポリプロピレン繊維、デンプン、芳香族ポリアミド
繊維等(2) Organic compounds Wood powder (pine, oak, sawdust, etc.), shell fiber (almond, peanut, fir shell, etc.), various colored fibers such as cotton, jute, paper strips, cellophane strips, nylon fibers , Polypropylene fiber, starch, aromatic polyamide fiber, etc.

【００６２】これらの着色物質のなかで、滑剤や界面活
性剤等のブリードアウト量を減少させることができるの
でカーボンブラックが好ましい。カーボンブラックの原
料による分類例をあげるとガスブラック、ファーネスブ
ラック、チャンネルブラック、アントラセンブラック、
アセチレンブラック、ケッチェンカーボンブラック、サ
ーマルブラック、ランプブラック、油煙、松煙、アニマ
ルブラック、ベジタブルブラック等がある。本発明では
遮光性、コスト、物性向上の目的ではファーネスカーボ
ンブラックが望ましく、高価であるが帯電防止効果を有
する着色物質としてはアセチレンカーボンブラック、変
性副生カーボンブラックであるケッチェンカーボンブラ
ックが望ましい。必要により前者と後者を必要特性に従
ってミックスすることも望ましい。着色物質をポリエチ
レン系ポリマーに配合する形態は上記のように種々ある
が、マスターバッチ法がコスト、作業場の汚染防止等の
点で望ましい。公知文献の特公昭40-26196号では有機溶
媒に溶解した重合体の溶液中にカーボンブラックを分散
せしめて、重合体−カーボンブラックのマスターバッチ
をつくる方法を、特公昭43-10362号にはカーボンブラッ
クをポリエチレンに分散してマスターバッチをつくる方
法を述べている。Among these coloring substances, carbon black is preferable because it can reduce the bleed-out amount of the lubricant, the surfactant and the like. Examples of carbon black materials classified by gas black, furnace black, channel black, anthracene black,
There are acetylene black, Ketjen carbon black, thermal black, lamp black, oil smoke, pine smoke, animal black, vegetable black and the like. In the present invention, furnace carbon black is preferable for the purpose of improving the light-shielding property, cost and physical properties, and acetylene carbon black and Ketjen carbon black which is a modified by-product carbon black are preferable as expensive coloring substances having an antistatic effect. If necessary, it is also desirable to mix the former and the latter according to the required characteristics. Although there are various forms of mixing the coloring substance with the polyethylene-based polymer as described above, the masterbatch method is preferable in terms of cost, prevention of contamination of the workplace, and the like. In Japanese Patent Publication No. 40-26196, which is a publicly known document, there is disclosed a method of dispersing a carbon black in a solution of a polymer dissolved in an organic solvent to form a polymer-carbon black masterbatch. It describes how to disperse black in polyethylene to make a masterbatch.

【００６３】また、写真フイルムに対しカブリの発生が
なく、感光度の増減の発生が少なく、遮光能力が大き
く、L-LDPE樹脂フイルムに添加した場合でもカーボンブ
ラックの固り（ブツ）の発生やフィッシュアイ等フイル
ム中にピンホールが発生しにくい点で、カーボンブラッ
クの中でも特にpH6.0〜9.0、平均粒子径10〜120ｍμ、
揮発成分が2.0％以下、吸油量が50ml/100ｇ以上のファ
ーネスカーボンブラックが好ましい。チャンネルカーボ
ンブラックは高価な上に、写真フイルムにカブリを発生
させるものが多く好ましくない。どうしても使用する必
要がある場合でも写真性に及ぼす影響を調査して選択す
べきである。Further, there is no fog on the photographic film, there is little increase or decrease in the photosensitivity, the light-shielding ability is large, and even when added to the L-LDPE resin film, the solidification of the carbon black occurs. Among the carbon blacks, pH 6.0-9.0, average particle size 10-120mμ, because pinholes are less likely to occur in the film such as fish eyes,
Furnace carbon black having a volatile component of 2.0% or less and an oil absorption of 50 ml / 100 g or more is preferable. Channel carbon black is not preferable because it is expensive and often causes fog on the photographic film. Even if it must be used, it should be investigated and selected for its effect on photographic properties.

【００６４】また、好ましいカーボンブラックの実際の
製品としては、例えば三菱化成製のカーボンブラック＃
20(B)、＃30(B)、＃33(B)、＃40(B)、＃44(B)、＃45
(B)、＃50、＃55、＃100、＃600、＃2200(B)、＃2400
(B)、ＭＡ８、ＭＡ11、ＭＡ100等が挙げられる。The actual product of the preferred carbon black is, for example, carbon black # manufactured by Mitsubishi Kasei.
20 (B), # 30 (B), # 33 (B), # 40 (B), # 44 (B), # 45
(B), # 50, # 55, # 100, # 600, # 2200 (B), # 2400
(B), MA8, MA11, MA100 and the like.

【００６５】海外の製品としては、例えばキャボット社
のBlack Pearls 2、46、70、71、74、80、81、607等、R
egal 300、330、400、660、991、SRF-S等、Vulcan 3、
６等、Sterling 10、ＳＯ、Ｖ、Ｓ、FT−FF、MT−FF等
が挙げられる。As overseas products, for example, Black Pearls 2, 46, 70, 71, 74, 80, 81, 607, etc. of Cabot Co., R
egal 300, 330, 400, 660, 991, SRF-S, Vulcan 3,
6 etc., Sterling 10, SO, V, S, FT-FF, MT-FF and the like.

【００６６】さらに、アシュランドケミカル社のUnited
R、BB、15、102、3001、3004、3006、3007、3008、300
9、3011、3012、XC−3016、XC−3017、3020等が挙げら
れるが、これらに限定されるものではない。Further, United of Ashland Chemical Co.
R, BB, 15, 102, 3001, 3004, 3006, 3007, 3008, 300
Examples include, but are not limited to, 9, 3011, 3012, XC-3016, XC-3017, and 3020.

【００６７】着色物質の添加量は0.01〜29重量％、好ま
しくは0.05〜15重量％、特に好ましくは0.1〜５重量％
の範囲である。添加量が0.01重量％未満であると、落下
強度の向上の程度が著しくなく、着色濃度が小さく着色
物質添加効果が発生せず、また添加量が29重量％を越え
ると樹脂の流動性が悪化し、ショートショットやウェル
ドラインの発生が多くなる。外観も悪くなり、落下衝撃
強度も悪化する。The amount of the coloring substance added is 0.01 to 29% by weight, preferably 0.05 to 15% by weight, particularly preferably 0.1 to 5% by weight.
The range is. If the addition amount is less than 0.01% by weight, the drop strength is not significantly improved, the coloring concentration is small and the effect of adding the coloring substance does not occur, and if the addition amount exceeds 29% by weight, the fluidity of the resin deteriorates. However, short shots and weld lines often occur. The appearance also deteriorates, and the drop impact strength also deteriorates.

【００６８】光電管検出が可能で、かつ内容物を見るこ
とができる本発明の写真フイルム用容器はヘイズが17〜
70％であり、好ましくは20〜65％であり、特に好ましく
は25〜60％である。The container for photographic film of the present invention capable of detecting a phototube and seeing the contents has a haze of 17 to
It is 70%, preferably 20 to 65%, and particularly preferably 25 to 60%.

【００６９】本発明の写真フイルム用容器は、曲げ弾性
率が5000〜25000Kg/cm²であることが好ましい。The flexural modulus of the photographic film container of the present invention is preferably 5000 to 25000 Kg / cm ² .

【００７０】本発明の写真フイルム用容器は、例えば、
図１に示すような蓋が容器本体に嵌合する型式の写真フ
イルムパトローネ用容器、図２に示すような蓋が容器本
体に被嵌する型式の写真フイルムパトローネ用容器、図
３に示すような蓋と容器本体がヒンジで一体となってい
る型式の写真フイルムパトローネ用容器（なお、図３に
示す写真フイルムパトローネ用容器は図４に示すように
シュリンクフイルムで被覆してもよい）、図５に示すよ
うな蓋と容器本体がヒンジで一体となっている型式の写
真フイルムパトローネ用容器、図６に示すような蓋と容
器本体がヒンジで一体となっているマイクロフイルム用
遮光容器、図７に示すような蓋と容器本体がロック嵌合
型式の写真フイルム用遮光容器、図８に示すような外面
が矩形で内面が円形の写真フイルムパトローネ用容器、
図９に示すような写真フイルムの先端がプラスチックパ
トローネ本体内に巻き込まれた写真フイルムパトローネ
用容器等に適用される。The photographic film container of the present invention is, for example,
A container for a photographic film cartridge whose lid as shown in FIG. 1 fits into the container body, a container for a photographic film cartridge as shown in FIG. 2 in which the lid fits over the container body, as shown in FIG. A container for a photo film cartridge in which the lid and the container body are integrated by a hinge (note that the container for a photo film cartridge shown in FIG. 3 may be covered with a shrink film as shown in FIG. 4), FIG. A photo film cartridge container of the type in which the lid and the container body are integrated by a hinge as shown in Fig. 6, a light-shielding container for a microfilm in which the lid and the container body are integrated by a hinge as shown in Fig. 6, As shown in Fig. 8, the lid and the container body are lock-fitting type light-shielding containers for photo films, as shown in Fig. 8, a photo film container with a rectangular outer surface and a circular inner surface,
The tip of the photographic film as shown in FIG. 9 is applied to a container for a photographic film cartridge in which a plastic cartridge body is wound.

【００７１】蓋と容器本体がヒンジで一体となっている
型式の写真フイルムパトローネ用容器の場合は、容器本
体と蓋との平均高さの比が５：５〜50：１、特に６：４
〜9.5：0.5の割合が好ましい。また、写真フイルムパト
ローネ用容器の場合、写真フイルムパトローネとして
は、例えば、写真フイルムの先端が露出しているＪＩＳ
型写真フイルムのパトローネ及び特開平２−272538号公
報、特開平３−37645号公報、特開平３−126029号公
報、米国特許第 4,634,306号、第 4,832,275号明細書、
第 4,887,776号明細書等に開示されている、未使用状態
では写真フイルムの先端までもプラスチックパトローネ
本体内に巻き込んでおくようにし、使用時にはスプール
を回転させることによって写真フイルムの送り出しを行
うようにしたパトローネ等がある。In the case of a container for a photographic film cartridge in which the lid and the container body are integrated by a hinge, the average height ratio of the container body and the lid is 5: 5 to 50: 1, especially 6: 4.
A ratio of ˜9.5: 0.5 is preferred. In the case of a photographic film cartridge container, the photographic film cartridge may be, for example, a JIS film whose tip is exposed.
Patrolne of mold photo film and JP-A-2-272538, JP-A-3-37645, JP-A-3-126029, US Pat. Nos. 4,634,306, 4,832,275,
As disclosed in the specification of No. 4,887,776 etc., in the unused state, even the tip of the photographic film is rolled up in the main body of the plastic patrone, and when used, the photographic film is sent out by rotating the spool. There are Patrone and others.

【００７２】写真フイルムパトローネ用容器をシュリン
クフイルムで被包した場合は、衝撃強度が大きいので輸
送中における破損防止ができ、内容物を確実に保護でき
る。さらに、シュリンクフイルム自体にクッション性が
あるので、外部からの衝撃に対して内容物を保護する。
また、写真フイルムパトローネ用容器をシュリンクフイ
ルムで被包する場合、容器本体の底面と蓋の天面を被包
する面積を容器断面積の98％以下に収縮させ、容器本体
と蓋にオリジナルシール特性を持たせ、さらに図４に代
表例を示す易開封部を設けることが好ましい。When the photographic film cartridge container is wrapped with a shrink film, it has a high impact strength, so that it can be prevented from being damaged during transportation and the contents can be surely protected. Furthermore, since the shrink film itself has a cushioning property, the contents are protected from an external impact.
When a photo film cartridge container is wrapped with a shrink film, the area covering the bottom of the container body and the top surface of the lid is shrunk to 98% or less of the container cross-sectional area, and the original sealing characteristics are applied to the container body and the lid. It is preferable to provide an easy-opening portion having a typical example shown in FIG.

【００７３】また、本発明の写真フイルム用容器の樹脂
組成物は、ＶＴＲブックケース用展開板、フロッピーデ
ィスク用ケースの展開板、インスタントフイルム用パッ
ク、明室装填用マガジン、プラスチックパトローネ、帯
状製品用、コア、ディスク、カートリッジ、食品容器、
電気製品、自動車部品、写真フイルム用スプール、住宅
材料等に用いることができる。Further, the resin composition of the photographic film container of the present invention is used for a VTR book case developing plate, a floppy disk case developing plate, an instant film pack, a bright room loading magazine, a plastic cartridge, a strip-shaped product. , Core, disc, cartridge, food container,
It can be used for electrical products, automobile parts, spools for photographic films, housing materials, etc.

【００７４】[0074]

【作用】本発明の写真フイルム用容器では、プロピレン
・エチレンランダム共重合体樹脂が透明度向上、造核剤
添加効果促進（透明度向上、結晶化速度向上、成形サイ
クル短縮、剛性向上、表面硬度向上等）、衝撃落下強度
向上、衝撃白化抑制等を向上させ、プロピレン・エチレ
ンブロック共重合体樹脂が衝撃落下強度や低温度下の衝
撃落下強度向上、ヘイズコントロール、剛性向上、着色
物質の混練適性を向上させている。In the photographic film container of the present invention, the propylene / ethylene random copolymer resin has improved transparency and accelerated nucleating agent addition effect (improved transparency, improved crystallization speed, shortened molding cycle, improved rigidity, improved surface hardness, etc.). ), Improved impact drop strength, improved impact whitening control, etc., propylene / ethylene block copolymer resin improves impact drop strength and impact drop strength at low temperatures, haze control, rigidity improvement, and improved kneading suitability for coloring substances I am letting you.

【００７５】造核剤が透明度、剛性、結晶化速度、耐摩
耗性、表面硬度を向上させ、変形や座屈の発生を防止
し、成形サイクルを短縮させている。The nucleating agent improves transparency, rigidity, crystallization rate, wear resistance and surface hardness, prevents deformation and buckling, and shortens the molding cycle.

【００７６】滑性向上物質が金型からの離形性、静電気
防止性、ブロッキング防止性等を向上させると共に、成
形サイクルを短縮させている。さらに造核剤、酸化防止
剤、２種のポリプロピレン樹脂、着色物質の表面被覆等
の作用により分散、混練性を向上させ、さらにまた耐摩
耗性、包装作業性を改良している。The lubricity improving substance improves the mold releasability from the mold, the antistatic property, the antiblocking property and the like, and shortens the molding cycle. Further, the action of a nucleating agent, an antioxidant, two kinds of polypropylene resins, the surface coating of a coloring substance and the like improves the dispersibility and kneading property, and further improves the abrasion resistance and the packaging workability.

【００７７】酸化防止剤が、２種類のポリプロピレン樹
脂と滑剤や界面滑性剤、防曇物質等の滑性向上物質の加
熱による品質劣化を防止している。The antioxidant prevents the deterioration of the quality of the two kinds of polypropylene resin and the lubricity improving substance such as the lubricant, the interfacial lubricant and the antifogging substance due to the heating.

【００７８】また、着色物質が遮光性向上、印刷適性向
上、識別性向上（容器をあけて見なくても色により内容
物を識別）と落下強度等の物理強度を極めて向上させ
る。Further, the coloring substance improves the light-shielding property, the printability, the discrimination property (the contents are discriminated by the color even when the container is not opened and seen) and the physical strength such as the drop strength is remarkably improved.

【００７９】[0079]

【実施例】【Example】

実施例１ エルカ酸アミド0.1重量％（容器本体全体に対しては0.0
8重量％）、1・3, 2・4ジ（メチルベンジリデン）ソルビ
トール0.15重量％（容器本体全体に対しては0.12重量
％）及びフェノール系酸化防止剤0.1重量％（容器本体
全体に対しては0.08重量％）含み、かつＭＦＲが35g/10
分、密度(JIS K 7112)が0.90g/cm³、曲げ弾性率が10300
kg/cm²、23℃アイゾット衝撃強度が3.5kg・cm/cm²そし
てヘイズが13％でエチレン含有率が2.1 重量％のプロピ
レン・エチレンランダム共重合体樹脂80重量％と、ＭＦ
Ｒが27g/10分、密度が0.90g/cm³、曲げ弾性率が12100kg
/cm²、23℃アイゾット衝撃強度が5.7kg・cm/cm²そして
ヘイズが83％でエチレン含有率が3.7重量％のプロピレ
ン・エチレンブロック共重合体樹脂20重量％とからなる
プロピレン・エチレン共重合体樹脂組成物を用いた。Example 1 0.1% by weight of erucic acid amide (0.0 for the whole container body)
8% by weight), 1,3,2,4 di (methylbenzylidene) sorbitol 0.15% by weight (0.12% by weight for the whole container body) and phenolic antioxidant 0.1% by weight (for the entire container body) 0.08 wt%) and MFR 35g / 10
Min, density (JIS K 7112) 0.90 g / cm ³ , flexural modulus 10300
80% by weight of propylene / ethylene random copolymer resin having kg / cm ² , 23 ° C Izod impact strength of 3.5 kg · cm / cm ^2, haze of 13% and ethylene content of 2.1% by weight, and MF
R is 27 g / 10 minutes, density is 0.90 g / cm ³ , flexural modulus is 12100 kg
/ cm ^2, 23 ℃ Izod impact strength propylene-ethylene copolymer 5.7 kg · cm / cm ² and haze ethylene content of 83% consists of 20% by weight of 3.7% by weight of propylene-ethylene block copolymer resin Weight A combined resin composition was used.

【００８０】そして、型締圧150tのトグル式射出成形機
｛住友重機製ネスタール（商品名）｝及びキャビティ数
24ヶのホットランナー型式の金型を用い、樹脂温度220
℃で、図１に示す写真フイルムパトローネ用容器本体を
作成した。なお、周壁部の厚さは0.7mmとした。A toggle type injection molding machine with a mold clamping pressure of 150 tons {Nestal (trade name) manufactured by Sumitomo Heavy Industries) and the number of cavities
Resin temperature of 220 using 24 hot runner model dies
The container body for the photographic film cartridge shown in FIG. The thickness of the peripheral wall was 0.7 mm.

【００８１】この容器本体は、周壁部のヘイズが46％で
あり、光電管により通過検出ができるとともに、内部に
収納した写真フイルムパトローネの印刷を外側から見る
ことができた。また、36枚撮りの35mm写真フイルムを収
納後低密度ポリエチレン製キャップを嵌合した状態で、
５ｍの高所からコンクリート床へ落下させて落下強度を
試験したが(100回）、割れたものは無かった。さらに、
成形サイクルを10秒以下にしても成形故障が殆ど発生せ
ず、爪で強くおしても白化現象がなく、輸送後のすり傷
が目立たず、嵌合強度、圧縮強度及び防湿性も後述する
比較例１より優れていた。In this container body, the haze of the peripheral wall was 46%, the passage could be detected by the photoelectric tube, and the printing of the photographic film cartridge stored inside could be seen from the outside. Also, after storing the 35mm photo film of 36 shots, with the low density polyethylene cap fitted,
Drop strength was tested by dropping from a height of 5 m onto a concrete floor (100 times), but no cracks were found. further,
Even if the molding cycle is 10 seconds or less, molding failure hardly occurs, even if it is strongly pressed with a nail, there is no whitening phenomenon, scratches after transportation are not noticeable, fitting strength, compression strength and moisture resistance are also comparative examples described later. Better than 1.

【００８２】実施例２ 実施例１のプロピレン・エチレンランダム共重合体樹脂
（エルカ酸アミド等を含む）とプロピレン・エチレンブ
ロック共重合体樹脂との混合割合を、プロピレン・エチ
レンランダム共重合体樹脂90重量％、プロピレン・エチ
レンブロック共重合体樹脂10重量％に変更したプロピレ
ン・エチレン共重合体樹脂組成物を用いた。そして、実
施例１と同一の成形条件（成形機、金型、樹脂温度）
で、図１に示す写真フイルム用容器本体を作成した。Example 2 The mixing ratio of the propylene / ethylene random copolymer resin (including erucic acid amide etc.) and the propylene / ethylene block copolymer resin of Example 1 was changed to 90% by weight of the propylene / ethylene random copolymer resin. A propylene / ethylene copolymer resin composition was used which was changed to 10% by weight of propylene / ethylene block copolymer resin. Then, the same molding conditions as in Example 1 (molding machine, mold, resin temperature)
Then, the main body of the photographic film container shown in FIG. 1 was prepared.

【００８３】この容器本体は、周壁部のヘイズが32％で
あり、光電管により通過検出ができるとともに、内部に
収納した写真フイルムパトローネの印刷を外側から見る
ことができた。また、36枚撮りの35mm写真フイルムを収
納後低密度ポリエチレン製キャップを嵌合した状態で、
５ｍの高所からコンクリート床へ落下させて落下強度を
試験したが(100回）、割れたものは無かった。さらに、
成形サイクルを10秒以下にしても成形故障が殆ど発生せ
ず、爪で強くおしても白化現象がなく、輸送後のすり傷
が目立たず、嵌合強度、圧縮強度及び防湿性も後述する
比較例１より優れていた。The container main body had a haze of 32% on the peripheral wall portion, and the passage could be detected by the photoelectric tube, and the printing of the photographic film cartridge stored inside could be seen from the outside. Also, after storing the 35mm photo film of 36 shots, with the low density polyethylene cap fitted,
Drop strength was tested by dropping from a height of 5 m onto a concrete floor (100 times), but no cracks were found. further,
Even if the molding cycle is 10 seconds or less, molding failure hardly occurs, even if it is strongly pressed with a nail, there is no whitening phenomenon, scratches after transportation are not noticeable, fitting strength, compression strength and moisture resistance are also comparative examples described later. Better than 1.

【００８４】実施例３ 実施例１のプロピレン・エチレンランダム共重合体樹脂
94.7重量％、実施例１のプロピレン・エチレンブロック
共重合体樹脂５重量％そしてアルミニウムペースト0.3
重量％からなるプロピレン・エチレン共重合体樹脂組成
物を用いた。そして、実施例１と同一の成形条件（成形
機、金型、樹脂温度）で、図１に示す写真フイルム用容
器本体を作成した。Example 3 Propylene / ethylene random copolymer resin of Example 1
94.7% by weight, 5% by weight of the propylene / ethylene block copolymer resin of Example 1 and 0.3 of aluminum paste
A propylene / ethylene copolymer resin composition consisting of wt% was used. Then, under the same molding conditions (molding machine, mold, resin temperature) as in Example 1, the photographic film container body shown in FIG. 1 was prepared.

【００８５】この容器本体２は、ヘイズが100％であっ
た。また、36枚撮りの35mm写真フイルムを収納後低密度
ポリエチレン製キャップを嵌合した状態で、５ｍの高所
からコンクリート床へ落下させて落下強度を試験したが
(100回）、割れたものは無かった。さらに、成形サイク
ルを10秒以下にしても成形故障が殆ど発生しなかった。
この容器本体は、外観が優れ曲面印刷性に優れ、太陽光
下に長時間放置しても容器内の温度上昇が小さく、熱変
形も発生しなかった。This container body 2 had a haze of 100%. Also, the drop strength was tested by storing a 35mm photo film of 36 shots and dropping it onto a concrete floor from a height of 5m with the low density polyethylene cap fitted.
(100 times), there were no cracks. Further, even if the molding cycle was set to 10 seconds or less, almost no molding failure occurred.
This container body had an excellent appearance and excellent printability on a curved surface, and even when left in sunlight for a long time, the temperature rise in the container was small and thermal deformation did not occur.

【００８６】実施例４ 実施例１のプロピレン・エチレンランダム共重合体樹脂
85重量％、実施例１のプロピレン・エチレンブロック共
重合体樹脂13.8重量％、酸化チタン１重量％、エルカ酸
アミド0.1重量％そしてフェノール系酸化防止剤0.1重量
％からなるプロピレン・エチレン共重合体樹脂組成物を
用いた。Example 4 Propylene / ethylene random copolymer resin of Example 1
Propylene / ethylene copolymer resin consisting of 85% by weight, 13.8% by weight of propylene / ethylene block copolymer resin of Example 1, 1% by weight of titanium oxide, 0.1% by weight of erucic acid amide and 0.1% by weight of phenolic antioxidant. The composition was used.

【００８７】そして、型締圧150tのトグル式射出成形機
｛住友重機製ネスタール（商品名）｝を用い、図３に示
す角型の身蓋一体式の写真フイルム用容器を作成した。
なお、周壁部の厚さは0.7mm、ヒンジの厚さは0.5mm 、
容器本体と蓋の長さの比は８：２とした。さらに防湿
性、オリジナルシール性を確保するために、図４に示す
ように取扱い説明、注意書き、ＣＩマーク等を印刷した
塩化ビニリデンコートポリプロピレン樹脂製シュリンク
フイルムで被包した。Then, using a toggle type injection molding machine with a mold clamping pressure of 150 tons {Nestal (trade name) manufactured by Sumitomo Heavy Industries, Ltd.}, a rectangular lid-integrated photographic film container shown in FIG. 3 was prepared.
The thickness of the peripheral wall is 0.7 mm, the thickness of the hinge is 0.5 mm,
The ratio of the length of the container body to the length of the lid was 8: 2. Further, in order to secure the moisture-proof property and the original sealing property, the film was wrapped with a shrink film made of vinylidene chloride-coated polypropylene resin on which a handling instruction, a cautionary note, a CI mark and the like are printed as shown in FIG.

【００８８】この写真フイルム用容器は、ヘイズが100
％であった。また、36枚撮りの35mm写真フイルムを収納
した状態で、５ｍの高所からコンクリート床へ落下させ
て落下強度を試験したが(100回）、割れたものは無かっ
た。また、爪で強くおしても白化現象がなく、耐圧縮
性、防湿性、耐熱性が良好であった。この容器本体は、
外観が白色で印刷適性も優れ、太陽光下に長時間放置し
ても容器内の温度上昇が小さく写真フイルムの品質を維
持でき、熱変性も発生しない従来の紙製の化粧小箱を必
要としない優れたものであった。This photographic film container has a haze of 100.
%Met. In addition, a drop strength was tested by dropping a 35 mm photo film of 36 shots from a height of 5 m onto a concrete floor (100 times), but no cracks were found. Further, even if it was strongly pressed with a nail, there was no whitening phenomenon, and the compression resistance, moisture resistance and heat resistance were good. This container body is
The appearance is white, the printability is excellent, the temperature inside the container does not rise even if left in the sun for a long time, the quality of the photographic film can be maintained, and the conventional paper cosmetic small box that does not undergo thermal denaturation is required. Not excellent.

【００８９】実施例５ 実施例１のプロピレン・エチレンランダム共重合体樹脂
85重量％、実施例１のプロピレン・エチレンブロック共
重合体樹脂13.8重量％、ファーネスカーボンブラック１
重量％、エルカ酸アミド0.1重量％そしてフェノール系
酸化防止剤0.1重量％からなるプロピレン・エチレン共
重合体樹脂組成物を用いた。Example 5 Propylene / ethylene random copolymer resin of Example 1
85% by weight, propylene / ethylene block copolymer resin of Example 1 13.8% by weight, furnace carbon black 1
A propylene / ethylene copolymer resin composition consisting of 0.1% by weight of erucic acid amide and 0.1% by weight of phenolic antioxidant was used.

【００９０】そして、型締圧150tのトグル式射出成形機
（住友重機製ネスタール−商品名）を用い、図６に示す
身蓋一体式のマイクロフイルム用遮光容器を作成した。
なお、周壁部の厚さは1.2mm、ヒンジの厚さは0.6mm 、
容器本体と蓋の長さの比は85：15とした。さらに防湿
性、オリジナルシール性を確保するために、製品の内
容、取扱い説明、注意書き、ＣＩマーク等を印刷した塩
化ビニリデンコート二軸延伸ポリプロピレン樹脂製シュ
リンクフイルムで被包した。Then, a toggle-type injection molding machine (Nestal manufactured by Sumitomo Heavy Industries, Ltd.) having a mold clamping pressure of 150 t was used to prepare the lid-integrated microfilm light-shielding container shown in FIG.
The thickness of the peripheral wall is 1.2 mm, the thickness of the hinge is 0.6 mm,
The ratio of the length of the container body to the length of the lid was 85:15. Further, in order to secure the moisture-proof property and the original sealability, the product was covered with a vinylidene chloride-coated biaxially stretched polypropylene resin shrink film on which content of contents, handling instructions, notes, CI mark and the like were printed.

【００９１】この包装体は、１ｍの高さからコンクリー
トの床へ落下させても、割れが発生しなかった。また、
防湿性、オリジナルシール性等が向上し、全体が同一の
樹脂組成物で作成されているので、リサイクルが可能で
あった。This package did not crack when dropped from a height of 1 m onto a concrete floor. Also,
The moisture resistance and the original sealability were improved, and since the whole was made of the same resin composition, it was recyclable.

【００９２】実施例６ 実施例４と同一のプロピレン・エチレン共重合体樹脂組
成物を用い、実施例と同一の射出成形条件で図９に示す
外面が矩形で、内面が未使用状態では写真フイルムの先
端までもプラスチックパトローネ本体内に巻き込んでお
くようにし、使用時にはスプールを回転させることによ
って写真フイルムの送り出しを行う特開平３−126029号
公報や特開平３−177835号公報等で開示されているタイ
プのパトローネの形状をした身蓋一体式の写真フイルム
用容器を作成した。容器本体と蓋の長さ（厚さ）の比は
50：２とした。さらに、防湿性オリジナルシール性を有
する取扱い説明を印刷した実施例４と同一のシュリンク
フイルムで被包した。この写真フイルム用容器はヘイズ
が100％であった。また、36枚撮りの写真フイルムを収
納した状態で、５ｍの高所からコンクリート床へ落下さ
せて落下強度を試験したが(100回）、割れたものは無か
った。また、爪で強くおしても白化現象がなく、耐圧縮
性、防湿性、耐熱性が良好であった。この容器本体は、
外観が白色で印刷適性も優れ、太陽光下に長時間放置し
ても容器内の温度上昇が小さく、店頭に長期間小箱なし
で展示されていても写真フイルムの品質を維持でき、容
器本体の熱変形も発生しない優れた容器であった。Example 6 The same propylene / ethylene copolymer resin composition as in Example 4 was used, and under the same injection molding conditions as in Example, the outer surface shown in FIG. 9 was rectangular and the inner surface was a photographic film when unused. Is disclosed in Japanese Patent Laid-Open No. 3-126029, Japanese Patent Laid-Open No. 3-177835, and the like, in which the photo film is sent out by rotating the spool at the time of use so that even the tip of the photo film is wound in the plastic cartridge body. A lid-integrated photographic film container in the shape of a type of cartridge was created. The ratio of the length (thickness) of the container body to the lid is
It was set to 50: 2. Further, the shrink film was wrapped with the same shrink film as in Example 4 on which a handling instruction having a moisture-proof original sealing property was printed. The haze of this photographic film container was 100%. In addition, when the photo film of 36 sheets was stored, the drop strength was tested by dropping it from a height of 5 m onto a concrete floor (100 times), but no cracks were found. Further, even if it was strongly pressed with a nail, there was no whitening phenomenon, and the compression resistance, moisture resistance and heat resistance were good. This container body is
The white appearance and excellent printability, the temperature rise inside the container is small even if left in the sun for a long time, and the quality of the photo film can be maintained even if it is displayed in the store for a long time without a small box, and the container body It was an excellent container that did not undergo thermal deformation.

【００９３】さらに、身・蓋共同一樹脂組成を用いてい
るので回収し再生利用も可能で、従来の高価な紙製の化
粧小箱を必要としない（角形をしているので展示適性＝
積み重ね可能を有し、印刷適性もある。容器本体に印刷
しなくても実施例のようにシュリンクフイルムに印刷し
てもよい。)現在の産業廃棄物問題も解消可能なすぐれた
容器である。Further, since the body / lid joint resin composition is used, it can be recovered and reused, and the conventional expensive paper cosmetic small box is not required (the square shape makes it suitable for exhibition).
It is stackable and printable. Instead of printing on the container body, it may be printed on the shrink film as in the embodiment. This is an excellent container that can solve the current industrial waste problem.

【００９４】さらに、また内面が写真フイルムパトロー
ネの形状で空間を有するので、写真フイルムパトローネ
のガタつきが少なく、運搬中の振動によっても従来の容
器のように容器内で回転したりすることがないので白粉
や傷の発生が少ない優れた容器である。身と蓋を別体に
した容器、外面を他の形状の矩形にした容器（コーナー
を直角にしたもの、Ｒをつけたもの、コーナーカットを
した８角形にしたもの）及び樹脂組成として請求項１〜
６はもちろん、密度が0.940g/cm³以上の高密度ポリエチ
レン樹脂（エチレン・αオレフィン共重合体樹脂も含
む）、プロピレン・αオレフィン共重合体樹脂（αオレ
フィンはエチレン、ブテン-1、ヘキセン-1、４メチルペ
ンテン-1、オクテン-1等）の少なくとも１種を70重量％
以上含むポリオレフィン系樹脂組成でも実施例６に用い
た外面が矩形で内面が写真フイルムパトローネの形状
（少なくとも写真フイルムパトローネを収納可能な寸法
の空間を有することが必須。写真フイルムパトローネよ
り寸法を大きくした場合は突起をもうけて写真フイルム
パトローネの働きを抑制してもよい）の場合は、衝撃を
吸収できる構造なので十分利用できるようになった。Further, since the inner surface has a space in the shape of a photographic film cartridge, the photographic film cartridge has less rattling and does not rotate in the container due to vibration during transportation unlike a conventional container. Therefore, it is an excellent container with less white powder and scratches. Claims as a container in which the body and the lid are separated, a container in which the outer surface is a rectangular shape of another shape (corners with right angles, R's, corner cut octagons) and resin composition 1 to
6 as well as high density polyethylene resin with a density of 0.940 g / cm ³ or more (including ethylene / α-olefin copolymer resin), propylene / α-olefin copolymer resin (α-olefin is ethylene, butene-1, hexene- 70% by weight of at least one of 1,4 methylpentene-1, octene-1, etc.)
Even in the polyolefin resin composition containing the above, the outer surface used in Example 6 was rectangular and the inner surface had the shape of a photographic film cartridge (at least it is necessary to have a space capable of storing the photographic film cartridge. The size was made larger than that of the photographic film cartridge. If you want to suppress the action of the photographic film cartridge by providing a projection), in the case of a structure that can absorb the impact, it has become fully usable.

【００９５】比較例１ 実施例１のプロピレン・エチレンランダム共重合体樹脂
を用い、実施例１と同一の成形条件で同一の写真フイル
ム用容器本体を作成した。Comparative Example 1 Using the propylene / ethylene random copolymer resin of Example 1, the same photographic film container body was prepared under the same molding conditions as in Example 1.

【００９６】この容器本体は、周壁部のヘイズが９％で
あり、内部に収納した写真フイルムパトローネの印刷を
外側から見ることができるが、光電管による通過検出が
できなかった。また、36枚撮りの35mm写真フイルムを収
納後低密度ポリエチレン製キャップを嵌合した状態で、
５ｍの高所からコンクリート床へ落下させて落下強度を
試験したが(100回）、５％の割れが発生した。さらに、
輸送後のすり傷及びちりの付着が目立つものであった。In this container body, the haze of the peripheral wall portion was 9%, and the printing of the photographic film cartridge stored inside could be seen from the outside, but the passage detection by the photoelectric tube could not be detected. Also, after storing the 35mm photo film of 36 shots, with the low density polyethylene cap fitted,
Drop strength was tested from a height of 5 m onto a concrete floor (100 times), and 5% cracking occurred. further,
Scratches and dust adhesion after transportation were noticeable.

【００９７】比較例２ 実施例１のプロピレン・エチレンブロック共重合体樹脂
を用い、実施例１と同一の成形条件で同一の写真フイル
ム用容器本体を作成した。Comparative Example 2 Using the propylene / ethylene block copolymer resin of Example 1, the same photographic film container body was prepared under the same molding conditions as in Example 1.

【００９８】この容器本体は、周壁部のヘイズが66％で
あり、光電管による通過検出ができるが、内部に収納し
た写真フイルムパトローネの印刷を外部からみることは
できなかった。また、36枚撮りの35mm写真フイルムを収
納後低密度ポリエチレン製キャップを嵌合した状態で、
５ｍの高所からコンクリート床へ落下させて落下強度を
試験したが(100回）、割れは発生しなかったが白化が多
発し商品価値のないものであった。また、つめで強く押
すと白化するものであった。また、成形故障の発生も多
かった。In this container body, the haze of the peripheral wall was 66%, and the passage of light could be detected by the photoelectric tube, but the printing of the photographic film cartridge stored inside could not be seen from the outside. Also, after storing the 35mm photo film of 36 shots, with the low density polyethylene cap fitted,
Although it was dropped from a height of 5 m onto a concrete floor and tested for drop strength (100 times), cracking did not occur, but whitening frequently occurred and it was of no commercial value. Also, it was bleached when pressed firmly with the pawl. In addition, there were many molding failures.

【００９９】[0099]

【発明の効果】本発明は、落下衝撃強度を維持又は向上
させつつ、光電管による検出が確実にできるとともに、
収納物を外側から見ることが出来る。また、着色物質を
添加した場合は、落下強度を極めて大きくするこができ
る。Industrial Applicability The present invention enables reliable detection by a photoelectric tube while maintaining or improving drop impact strength, and
You can see the contents from the outside. Further, when a coloring substance is added, the drop strength can be extremely increased.

【図面の簡単な説明】[Brief description of drawings]

【図１】本発明の写真フイルム用容器が適用される身蓋
嵌合式写真フイルムパトローネ用容器の断面図。FIG. 1 is a sectional view of a lid-fitting type photographic film cartridge container to which the photographic film container of the present invention is applied.

【図２】本発明の写真フイルム用容器が適用される他の
身蓋嵌合式写真フイルムパトローネ用容器の断面図。FIG. 2 is a sectional view of another lid-fitting type photographic film cartridge container to which the photographic film container of the present invention is applied.

【図３】本発明の写真フイルム用容器が適用される身蓋
がヒンジで一体化されている写真フイルムパトローネ用
容器の断面図。FIG. 3 is a cross-sectional view of a photographic film cartridge container in which a lid to which the photographic film container of the present invention is applied is integrated by a hinge.

【図４】本発明の写真フイルム用容器が適用される身蓋
がヒンジで一体化されている写真フイルムパトローネ用
容器をシュリンクフイルムで被包した包装体の斜視図。FIG. 4 is a perspective view of a package in which a container for a photo film patrone to which a container for a photo film of the present invention is integrated with a hinge is wrapped with a shrink film.

【図５】本発明の写真フイルム用容器が適用される身蓋
がヒンジで一体化されている写真フイルムパトローネ用
容器の断面図。FIG. 5 is a cross-sectional view of a container for a photographic film cartridge in which a body lid to which the photographic film container of the present invention is applied is integrated by a hinge.

【図６】本発明の写真フイルム用容器が適用される身蓋
がヒンジで一体化されているマイクロフイルム用遮光容
器の断面図。FIG. 6 is a cross-sectional view of a microfilm light-shielding container in which a body lid to which the photographic film container of the present invention is applied is integrated by a hinge.

【図７】本発明の写真フイルム用容器が適用される身蓋
ロック嵌合式遮光容器の斜視図。FIG. 7 is a perspective view of a lid lock-fitting type light-shielding container to which the photographic film container of the present invention is applied.

【図８】本発明の写真フイルム用容器が適用される外面
が矩形で内面が円形の写真フイルム用パトローネ用容器
本体の斜視図。FIG. 8 is a perspective view of a container body for a photographic film cartridge having a rectangular outer surface and a circular inner surface to which the photographic film container of the present invention is applied.

【図９】本発明の写真フイルム用容器が適用される写真
フイルムの先端がプラスチック製パトローネ本体内に巻
き込まれたタイプの写真フイルムパトローネ用容器の斜
視図。FIG. 9 is a perspective view of a photographic film cartridge container of a type in which the tip of the photographic film to which the photographic film container of the present invention is applied is wound inside a plastic cartridge body.

Claims (7)

【特許請求の範囲】[Claims] 【請求項１】 プロピレン・エチレンランダム共重合体
樹脂65〜95重量％、プロピレン. エチレンブロック共重
合体樹脂５〜35重量％、造核剤0.01〜2.0重量％、滑性
向上物質0.01〜10重量％及び酸化防止剤0.01〜1.0重量
％含まれていることを特徴とする写真フイルム用容器1. A propylene / ethylene random copolymer resin 65 to 95% by weight, propylene. An ethylene block copolymer resin 5 to 35% by weight, a nucleating agent 0.01 to 2.0% by weight, and a lubricity improving substance 0.01 to 10% by weight. % And 0.01 to 1.0% by weight of an antioxidant are included in the photographic film container. 【請求項２】 プロピレン・エチレンランダム共重合体
樹脂65〜95重量％、プロピレン. エチレンブロック共重
合体樹脂５〜35重量％、造核剤0.01〜2.0重量％、滑性
向上物質0.01〜10重量％、酸化防止剤0.01〜1.0重量％
及び着色物質0.01〜29重量％含まれている写真フイルム
用容器2. A propylene / ethylene random copolymer resin 65 to 95% by weight, propylene. An ethylene block copolymer resin 5 to 35% by weight, a nucleating agent 0.01 to 2.0% by weight, and a lubricity improving substance 0.01 to 10% by weight. %, Antioxidant 0.01-1.0% by weight
And a photographic film container containing 0.01 to 29% by weight of coloring substances 【請求項３】 造核剤が、ソルビトール系有機化合物で
ある請求項１又は２に記載の写真フイルム用容器3. The photographic film container according to claim 1, wherein the nucleating agent is a sorbitol-based organic compound. 【請求項４】 滑性向上物質が、１種以上の滑剤である
請求項１又は２に記載の写真フイルム用容器4. The photographic film container according to claim 1, wherein the lubricity-improving substance is one or more lubricants. 【請求項５】 プロピレン・エチレンランダム共重合体
樹脂とプロピレン.エチレンブロック共重合体樹脂との
メルト・フロー・レイトの比が、±90％以内である請求
項１又は２に記載の写真フイルム用容器5. The photographic film according to claim 1, wherein the ratio of the melt flow rate of the propylene / ethylene random copolymer resin and the propylene.ethylene block copolymer resin is within ± 90%. container 【請求項６】 容器本体の曲げ弾性率が5000〜25000kg/
cm²である請求項１又は請求項２に記載の写真フイルム
用容器6. The flexural modulus of the container body is 5000 to 25000 kg /
The container for photographic film according to claim 1 or ^2, which has a size of cm ^2. 【請求項７】 容器本体が高密度ポリエチレン樹脂及び
プロピレン・αオレフィン共重合体樹脂の少なくとも１
種を70重量％以上含み、外面が矩形で内面が略写真フイ
ルムパトローネの形状をしたことを特徴とする写真フイ
ルム用容器7. The container body comprises at least one of a high-density polyethylene resin and a propylene / α-olefin copolymer resin.
A photographic film container characterized by containing at least 70% by weight of seeds, the outer surface of which is rectangular and the inner surface of which is roughly the shape of a photographic film cartridge.