JPH0543850A - Production of double-coated self-adhesive tape - Google Patents

Abstract

PURPOSE:To produce the title tape which is free from shrinkage voids otherwise occurring when wound up into a roll. CONSTITUTION:The title tape 10 is prepd. by thermally drying a substrate 1 comprising nonwoven fabric contg. pulp mixed therein on a heating roll 2, etc., and transferring adhesive layers from transfer sheets 4 and 8 to both sides of the substrate 1. Thus, shrinkage of both the substrate 1 and the tape 10 can be kept low.

Description

【発明の詳細な説明】Detailed Description of the Invention

【０００１】[0001]

【産業上の利用分野】この発明は、パルプ混入不織布を
支持体とする両面粘着テープの製造方法に関する。BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a method for producing a double-sided pressure-sensitive adhesive tape using a pulp-containing nonwoven fabric as a support.

【０００２】[0002]

【従来の技術】紙・不織布は、安価であること、粘着剤
の含浸がよいこと、柔軟性が適度であるので被着体への
なじみがよいこと、等の利点を有しており、両面粘着テ
ープの支持体として広く使用されている。なかでも、パ
ルプ混入不織布は、安価で適度の強度を有し、支持体と
しての上記の特性を備えているので特に汎用されてい
る。2. Description of the Related Art Paper / nonwoven fabric has advantages such as low cost, good impregnation with an adhesive, and good adaptability to an adherend due to its moderate flexibility. Widely used as a support for adhesive tape. Among them, the pulp-mixed nonwoven fabric is particularly widely used because it is inexpensive, has a proper strength, and has the above-mentioned characteristics as a support.

【０００３】ところで、パルプ混入不織布、とりわけパ
ルプ混入率が高い不織布（例えばパルプが５０％程度混
入されたレーヨン不織布）を支持体として用いた両面粘
着テープは、これを紙管に巻いておくと、セパレーター
に面した部分が部分的に浮き上がった状態、いわゆる巣
が発生し易かった。By the way, a double-sided adhesive tape using a non-woven fabric containing pulp, particularly a non-woven fabric having a high pulp mixing rate (for example, rayon non-woven fabric containing about 50% pulp) as a support, is wound around a paper tube. A state in which the part facing the separator was partially lifted, that is, a so-called nest was easily generated.

【０００４】この巣の発生をなくすため、従来、両面粘
着テープを紙管に巻く際、巻き取りテンションを強くし
たり、タッチロールで両面粘着テープを紙管に強く圧着
するなどしていた。In order to eliminate the formation of the nest, conventionally, when the double-sided pressure-sensitive adhesive tape is wound around the paper tube, the winding tension is increased, or the double-sided pressure-sensitive adhesive tape is strongly pressed onto the paper tube with a touch roll.

【０００５】[0005]

【発明が解決しようとする課題】しかし、上記のような
手段によっても巣の発生を完全に無くすことはできなか
った。However, it has not been possible to completely eliminate the generation of nests even by the above means.

【０００６】この発明は、巻き取り時に支持体や両面粘
着テープに強い応力をかけることなく、巣の発生が抑制
された両面粘着テープの製造方法を提供することを目的
とする。An object of the present invention is to provide a method for producing a double-sided pressure-sensitive adhesive tape in which generation of cavities is suppressed without applying a strong stress to the support or the double-sided pressure-sensitive adhesive tape during winding.

【０００７】[0007]

【課題を解決するための手段】この発明者は、上記課題
について鋭意研究の結果、両面粘着テープが紙管に巻か
れて巻重体とされているとき、巣は、両面粘着テープの
伸縮によってセパレーターとその外側の粘着剤剤層とが
部分的に剥離して生成された空隙であって、特に支持体
のパルプ混入不織布の含水率が高いと、両面粘着テープ
の伸縮が大きく巣の発生が多いことを知見し、この発明
を完成した。As a result of earnest research on the above problems, the present inventor has found that when a double-sided pressure-sensitive adhesive tape is wound around a paper tube to form a wound body, a nest is formed by expansion and contraction of the double-sided pressure-sensitive adhesive tape. This is a void formed by the partial peeling of the adhesive layer on the outside with the adhesive layer, and especially when the moisture content of the pulp-mixed non-woven fabric of the support is high, the double-sided adhesive tape expands and contracts largely, and cavities often occur. Based on this finding, the present invention has been completed.

【０００８】この発明の両面粘着テープの製造方法は、
パルプ混入不織布を支持体とし、該支持体の両面に粘着
剤を塗工して両面粘着テープを製造するにあたり、支持
体を乾燥した後に粘着剤を塗工することを特徴としてい
る。The method for producing the double-sided adhesive tape of the present invention is
When a non-woven fabric containing pulp is used as a support and a pressure-sensitive adhesive is applied to both surfaces of the support to produce a double-sided pressure-sensitive adhesive tape, the support is dried and then the pressure-sensitive adhesive is applied.

【０００９】パルプ混入不織布としては、従来から両面
粘着テープの支持体として用いられているパルプ混入不
織布、例えば、パルプが５０％程度混入されたレーヨン
不織布などがあげられる。また、粘着剤もゴム系、アク
リル系、ビニル系、シリコン系などの従来から用いられ
ているものが用いられる。Examples of the pulp-containing nonwoven fabric include a pulp-containing nonwoven fabric which has been conventionally used as a support for a double-sided pressure-sensitive adhesive tape, for example, a rayon nonwoven fabric containing about 50% pulp. Also, as the adhesive, those conventionally used such as rubber, acrylic, vinyl, and silicone are used.

【００１０】パルプ混入不織布を乾燥する方法として
は、乾燥炉を通過させる方法、加熱ロールに接触させる
ことにより加熱して乾燥する方法などがあげられるが、
これに限定されるものでない。この乾燥度合いについて
は、パルプ混入不織布の含水率が３％以下、好ましくは
２％以下となるように乾燥するのが好ましい。Examples of the method for drying the pulp-containing nonwoven fabric include a method of passing it through a drying furnace and a method of heating by drying by contact with a heating roll.
It is not limited to this. Regarding the degree of drying, it is preferable to dry the nonwoven fabric containing pulp so that the moisture content thereof is 3% or less, preferably 2% or less.

【００１１】[0011]

【作用】粘着剤の塗工前にパルプ混入不織布が乾燥され
るので、支持体の含水率が低いものとなって支持体及び
両面粘着テープの伸縮が小さくなり巣の発生が防がれ
る。Since the non-woven fabric mixed with pulp is dried before the application of the pressure-sensitive adhesive, the water content of the support becomes low and the expansion of the support and the double-sided pressure-sensitive adhesive tape becomes small, thus preventing generation of cavities.

【００１２】[0012]

【実施例】この発明の実施例を図面を参照して説明す
る。図１は、この発明の両面粘着テープの製造方法の説
明図である。Embodiments of the present invention will be described with reference to the drawings. FIG. 1 is an explanatory view of the method for producing the double-sided pressure-sensitive adhesive tape of the present invention.

【００１３】図１において、１は支持体、２は加熱ロー
ル、３及び９は転写ロール、４及び８は転写シート、５
及び７は乾燥炉である。支持体１は、例えばパルプが５
０％程度混入されたレーヨン不織布からなるパルプ混入
不織布であり、８０〜１００℃に加熱された加熱ロール
２に送られる。この加熱ロール２により支持体１は加熱
され、その含水率が３％以下、好ましく２％以下に乾燥
されて転写ロール３に送られる。一方、転写シート４
は、図２に示されるとおり、工程紙（セパレーター）４
１に粘着剤層４２が塗工されることにより形成されてお
り、転写ロール３に送られる。工程紙４１は図示してい
ないが両面がシリコーン系離型剤などで離型処理されて
いる。この離型処理面は、粘着剤層４２側の離型処理面
の剥離力が他面の剥離力よりもやや重くされている。ま
た、５は粘着剤乾燥炉である。In FIG. 1, 1 is a support, 2 is a heating roll, 3 and 9 are transfer rolls, 4 and 8 are transfer sheets, 5
And 7 are drying ovens. The support 1 has, for example, 5 pulp.
This is a pulp-mixed non-woven fabric made of rayon non-woven fabric mixed with about 0%, and sent to the heating roll 2 heated to 80 to 100 ° C. The support 1 is heated by the heating roll 2, dried to a water content of 3% or less, preferably 2% or less, and sent to the transfer roll 3. On the other hand, the transfer sheet 4
2 is a process paper (separator) 4 as shown in FIG.
It is formed by coating the pressure-sensitive adhesive layer 42 on 1 and is sent to the transfer roll 3. Although not shown, both sides of the process paper 41 are release-treated with a silicone release agent or the like. With respect to the release-treated surface, the peeling force of the release-treated surface on the pressure-sensitive adhesive layer 42 side is set to be slightly heavier than the peeling force of the other surface. Further, 5 is an adhesive drying oven.

【００１４】転写ロール３において、転写シート４の粘
着剤層４２面が支持体１に接し、支持体１と転写シート
４とが積層され、支持体１の片面に粘着剤層４２が積層
された、図３に示されるとおりの中間テープ６が形成さ
れる。In the transfer roll 3, the adhesive layer 42 side of the transfer sheet 4 is in contact with the support 1, the support 1 and the transfer sheet 4 are laminated, and the adhesive layer 42 is laminated on one side of the support 1. The intermediate tape 6 as shown in FIG. 3 is formed.

【００１５】続いて、転写ロール９において、中間テー
プ６の下面、すなわち支持体１の粘着剤が塗工されてい
ない面に、転写シート４と同様の転写シート８の粘着剤
層８２が転写され、両面粘着テープ１０が形成される。Subsequently, in the transfer roll 9, the adhesive layer 82 of the transfer sheet 8 similar to the transfer sheet 4 is transferred to the lower surface of the intermediate tape 6, that is, the surface of the support 1 on which the adhesive is not applied. The double-sided adhesive tape 10 is formed.

【００１６】すなわち、シリコーン系離型剤などで離型
処理された工程紙８１の離型処理面に粘着剤が図示して
ない塗工装置により塗工され、粘着剤乾燥炉７で乾燥さ
れた転写シート８は、転写ロール９に送られる。この転
写ロール９において、転写シート８は支持体１の下面に
粘着剤層８２が接して積層されると共に工程紙８１は剥
離される。その結果、粘着剤剤層８２は支持体１に転写
され、両面粘着テープ１０が形成される。That is, a pressure-sensitive adhesive is applied to the release-treated surface of the process paper 81 which has been release-treated with a silicone-based release agent by a coating device (not shown) and dried in the pressure-sensitive adhesive drying oven 7. The transfer sheet 8 is sent to the transfer roll 9. In the transfer roll 9, the transfer sheet 8 is laminated with the pressure-sensitive adhesive layer 82 in contact with the lower surface of the support 1, and the process paper 81 is peeled off. As a result, the pressure-sensitive adhesive layer 82 is transferred to the support 1, and the double-sided pressure-sensitive adhesive tape 10 is formed.

【００１７】このようにして、図４に示されるとおり、
支持体１の両面に粘着剤層４２、８２が形成され、粘着
剤層４２がセパレーター（工程紙）４１で保護された両
面粘着テープ１０が得られ、セパレーター４１を外側に
して紙管１１に巻かれ、巻重体とされる。なお、両面粘
着テープ１０を紙管１１に巻くときには、特に巻きテン
ションを強くしたり、タッチロールで押圧するなどして
堅く巻くことなく通常の巻き方によった。Thus, as shown in FIG.
The double-sided pressure-sensitive adhesive tape 10 in which the pressure-sensitive adhesive layers 42 and 82 are formed on both sides of the support 1 and the pressure-sensitive adhesive layer 42 is protected by the separator (process paper) 41 is obtained, and the separator 41 is placed outside and wound around the paper tube 11. He is regarded as a rolled body. When the double-sided pressure-sensitive adhesive tape 10 is wound around the paper tube 11, the usual winding method is used without increasing the winding tension or pressing with a touch roll to tightly wind it.

【００１８】このようにして、得られた両面粘着テープ
の巻重体には巣の発生はなかった。一方、加熱ロール２
をなくしたこと以外、上記の方法と同様にして得た両面
粘着テープの巻重体には、何箇所かに巣の発生がみられ
た。In this way, no nest was formed in the obtained double-sided pressure-sensitive adhesive tape roll. On the other hand, heating roll 2
With the double-sided pressure-sensitive adhesive tape wound body obtained in the same manner as described above, except that the above was eliminated, cavities were observed at several places.

【００１９】上記の実施例においては、支持体１が加熱
ロール２に接触して加熱乾燥される方法が採られている
が、乾燥手段として加熱ロール２を用いることの他、図
５に示されるとおり、乾燥炉２ａ内を通過させることに
より支持体１を乾燥させることもできる。In the above-mentioned embodiment, a method is employed in which the support 1 is brought into contact with the heating roll 2 to be heated and dried, but in addition to using the heating roll 2 as a drying means, it is shown in FIG. As described above, the support 1 can be dried by passing through the drying furnace 2a.

【００２０】[0020]

【発明の効果】この発明の両面粘着テープの製造方法
は、パルプ混入不織布からなる支持体を乾燥した後に粘
着剤を塗工するものであるから、支持体の含水率が低い
ものとなって支持体及び両面粘着テープの伸縮が小さく
抑えられ、巣の発生が防がれる。In the method for producing a double-sided pressure-sensitive adhesive tape of the present invention, since the pressure-sensitive adhesive is applied after drying the support made of pulp-containing nonwoven fabric, the support has a low water content and is thus supported. The expansion and contraction of the body and the double-sided adhesive tape are suppressed to a small extent, and the formation of nests is prevented.

【図面の簡単な説明】[Brief description of drawings]

【図１】この発明の両面粘着テープの製造方法の説明図
である。FIG. 1 is an explanatory view of a method for producing a double-sided pressure-sensitive adhesive tape of the present invention.

【図２】図１に示す転写シートの断面図である。FIG. 2 is a sectional view of the transfer sheet shown in FIG.

【図３】図１に示す中間テープの断面図である。FIG. 3 is a cross-sectional view of the intermediate tape shown in FIG.

【図４】図１に示す両面粘着テープの断面図である。FIG. 4 is a cross-sectional view of the double-sided adhesive tape shown in FIG.

【図５】支持体の別の乾燥方法の説明図である。FIG. 5 is an explanatory view of another method of drying the support.

【符号の説明】[Explanation of symbols]

１ 支持体 ２ 加熱ロール ３、９ 転写ロール ４、８ 転写シート ６ 中間テープ １０ 両面粘着テープ １１ 紙管 1 Support 2 Heating Roll 3, 9 Transfer Roll 4, 8 Transfer Sheet 6 Intermediate Tape 10 Double-sided Adhesive Tape 11 Paper Tube

Claims (2)

【特許請求の範囲】[Claims] 【請求項１】 パルプ混入不織布を支持体とし、該支持
体の両面に粘着剤を塗工して両面粘着テープを製造する
にあたり、支持体を乾燥した後に粘着剤を塗工すること
を特徴とする両面粘着テープの製造方法。1. A non-woven fabric mixed with pulp is used as a support, and when a pressure sensitive adhesive is applied to both sides of the support to produce a double-sided pressure-sensitive adhesive tape, the pressure-sensitive adhesive is applied after the support is dried. Method for producing double-sided adhesive tape. 【請求項２】 支持体を３％以下に乾燥することを特徴
とする請求項１記載の両面粘着テープの製造方法。2. The method for producing a double-sided adhesive tape according to claim 1, wherein the support is dried to 3% or less.